RU2175035C2 - Ballistic protection cloth and pack based on ballistic protection cloth - Google Patents

Abstract

FIELD: textile industry. SUBSTANCE: cloth is manufactured from high-strength aramide threads of equal linear density in warp and weft directions, similar longitudinal configuration and equal number of threads per unit of width in both directions and twisting rate not exceeding 4. Cloth is manufactured by satin, twill or wafer weave of single threads and satin, twill, calico or wafer weave of 2-6 threads in warp and weft directions. Regular satin weave has pattern repeat of 5-10 with constant shift of from 2 to 7 and irregular satin weave has pattern of 4 to 10 with variable shift of from 1 to 8. Twill weave has 1-8 warp overlappings and 2-8 weft overlappings. Wafer weave pattern repeat has 4-16 threads. Pack of ballistic protection cloth has front and rear cloth layers arranged in succession and manufactured from high-strength aramide threads. Layers are arranged so that front and rear layers with respect to source of destructive force are manufactured from cloths having threads reinforced 2-6 times in warp and weft directions. Cloth pattern repeat and thread reinforcement in cloths in direction from front to rear layers is decreasing, with separating layers being arranged in front of rear layers and/or between rear layers, and/or behind rear layers. Cloth of such structure has improved puncture resistance. EFFECT: wider operational capabilities, increased efficiency and enhanced reliability in operation. 3 cl, 3 dwg, 1 tbl, 5 ex

Description

Изобретение относится к текстильной промышленности, в частности к разработке защитных тканей специального назначения, предназначенных для изготовления бронежилетов, защитной одежды и других целей. The invention relates to the textile industry, in particular to the development of protective fabrics for special purposes, intended for the manufacture of body armor, protective clothing and other purposes.

Известны баллистически стойкие ткани из арамидных нитей, используемые для изготовления средств индивидуальной броневой защиты, в частности бронежилетов [1, 2, 3]. Known ballistic resistant fabrics from aramid yarns used for the manufacture of personal protective equipment, in particular body armor [1, 2, 3].

Однако эти ткани обладают недостаточно высокими эксплуатационными свойствами при применении в пакетах для баллистической защиты. However, these fabrics do not have high operational properties when used in bags for ballistic protection.

Техническим решением, наиболее полно иллюстрирующим подход к решению проблемы создания защитной ткани, является ткань для баллистической защиты полотняного переплетения из высокопрочной арамидной нити равной линейной плотности по основе и утку, выполненная с одинаковой продольной конфигурацией и равным количеством нитей на единицу ширины в обоих направлениях, при этом коэффициент крутки нитей не превышает 4 [3]. The technical solution that most fully illustrates the approach to solving the problem of creating a protective fabric is a fabric for ballistic protection of linen weaving from high-strength aramid yarn of equal linear density on the basis and a weft made with the same longitudinal configuration and equal number of threads per unit width in both directions, with this coefficient of twisting of the threads does not exceed 4 [3].

Недостатком данного решения является высокое усилие при перемещении нитей в плоскости ткани. В результате воздействия баллистического снаряда происходит поперечное разрушение нити с малым поглощением энергии средства поражения, что в свою очередь требует увеличения числа слоев ткани в пакете для повышения стойкости изделия. The disadvantage of this solution is the high force when moving the threads in the plane of the fabric. As a result of the impact of a ballistic projectile, the yarn with transverse destruction occurs with a small absorption of energy of the means of destruction, which in turn requires an increase in the number of tissue layers in the bag to increase the durability of the product.

Технический результат, достигаемый изобретением, заключается в повышении эксплуатационных характеристик, к которым относятся увеличение сопротивления пробитию и эффективное гашение динамического воздействия при обстреле в сочетании с низкой массой и хорошей гибкостью структуры. The technical result achieved by the invention is to increase operational characteristics, which include an increase in penetration resistance and effective damping of dynamic impact during firing in combination with low weight and good flexibility of the structure.

Для достижения данного технического результата ткань для баллистической защиты из высокопрочной арамидной нити равной линейной плотности по основе и утку с одинаковой продольной конфигурацией и равным количеством нитей на единицу ширины в обоих направлениях с коэффициентом крутки нитей, не превышающим 4, выполнена атласным или сатиновым, саржевым, вафельным переплетением одиночных нитей или атласным или сатиновым, саржевым, полотняным, вафельным переплетением из усиленных в 2-6 раз нитей по основе и утку. При этом правильное атласное или сатиновое переплетение имеет раппорт переплетения от 5 до 10 с постоянным сдвигом от 2 до 7, а неправильное атласное или сатиновое переплетение имеют раппорт переплетения от 4 до 10 с переменным сдвигом от 1 до 8, саржевое переплетение имеет число основных перекрытий от 1 до 8 и число уточных перекрытий от 2 до 8, число нитей в раппорте вафельного переплетения составляет от 4 до 16. To achieve this technical result, the fabric for ballistic protection from high-strength aramid yarn of equal linear density on the warp and weft with the same longitudinal configuration and equal number of threads per unit width in both directions with a twist coefficient of threads not exceeding 4 is made of satin or satin, twill, wafer weave of single threads or satin or satin, twill, linen, waffle weave from 2-6 times reinforced warp and weft threads. In this case, the correct satin or satin weave has a repeat pattern of 5 to 10 with a constant shift from 2 to 7, and the wrong satin or satin weave has a repeat pattern of 4 to 10 with a variable shift of 1 to 8, the twill weave has the number of main overlap from 1 to 8 and the number of weft overlaps from 2 to 8, the number of threads in the wafer weave pattern is from 4 to 16.

Известен пулезащитный тканевый пакет, который содержит тканевые слои на основе арамидных нитей Кевлар [4, 5, 6]. Known bulletproof fabric package, which contains tissue layers based on aramid yarns Kevlar [4, 5, 6].

Известны также пулезащитные тканевые пакеты, выполненные из слоев ткани на основе высокомодульных арамидных нитей, таких как СВМ и ПФТА (полипарафенилентерефталамид) [2, 7, 8, 9]. Also known are bulletproof fabric bags made of fabric layers based on high modulus aramid filaments, such as CBM and PFTA (polyparaphenylene terephthalamide) [2, 7, 8, 9].

Наиболее близким техническим решением является пулезащитный пакет, содержащий расположенные друг за другом слои из разнородных синтетических тканей, лицевые слои которых выполнены из нитей на основе высокомодульных полиамидных нитей с пределом прочности при растяжении не ниже 2000 мН/м² и относительным удлинением при разрыве не менее 1%, а тыльные слои выполнены из полиамидных нитей с пределом прочности при растяжении не ниже 600 мН/м² при относительном удлинении при разрыве не менее 10%, при этом соотношение лицевых и тыльных слоев ткани находится в пределах 2:(1-4) по массе [9].The closest technical solution is a bulletproof package, containing successive layers of heterogeneous synthetic fabrics, the front layers of which are made of threads based on high modulus polyamide fibers with a tensile strength of at least 2000 mN / m ² and an elongation at break of at least 1 %, and rear layers are made of polyamide yarns with a tensile strength of not less than 600 mN / m ^2, with a tensile elongation at break of not less than 10%, wherein the ratio of the front and back fabric layers on oditsya in the range 2: (1-4) by weight of [9].

Однако известный защитный пакет обладает недостаточно высокими защитными свойствами. However, the known protective package has insufficiently high protective properties.

Другим техническим результатом изобретения является создание пакета на основе предлагаемых тканей с высокой баллистической стойкостью при хорошей гибкости структуры. Another technical result of the invention is the creation of a package based on the proposed fabric with high ballistic resistance with good flexibility of the structure.

Для этого предлагается баллистический защитный тканевый пакет, содержащий последовательно расположенные фронтальные и тыльные слои ткани вышеописанных структур из высокопрочной арамидной нити, при этом слои расположены так, что фронтальные по отношению к средству поражения слои выполнены из тканей, имеющих по основе и утку усиленные в 2-6 раз нити, причем раппорт переплетения тканей и усиление нитей в них в направлении от фронтальных к тыльным слоям уменьшается. Фронтальный слой состоит из протяженных фрагментов ткани, выполненных в виде полос и уложенных параллельно с перекрытием без закрепления между собой. Размещенные за фронтальным слоем слои выполнены из ткани, имеющей прорези, расположенные в шахматном порядке, причем размер прорезей и шаг их расположения по основе и утку скоррелированы с калибром средства поражения, а последующий по направлению к тылу слой состоит из фрагментов ткани, скрепленных между собой внахлест, после которых расположены тыльные слои из цельнокроеных фрагментов ткани по форме пакета, причем раппорт переплетения тканей и усиление нитей в направлении от фронтальных слоев к тыльным уменьшается и перед тыльными слоями и/или между ними и/или после них расположены разделительные прокладки. For this purpose, a ballistic protective fabric package is proposed that contains successively located frontal and back layers of fabric of the above structures from high-strength aramid filament, the layers being arranged so that the layers that are frontal to the means of destruction are made of fabrics having a warp and weft reinforced in 2- 6 times the filament, and the rapport of the weave of fabrics and the strengthening of the filaments in them in the direction from the front to the back layers decreases. The frontal layer consists of extended tissue fragments made in the form of strips and laid in parallel with the overlap without fixing each other. The layers located behind the front layer are made of fabric having staggered slits, the size of the slots and the step of their location along the base and weft are correlated with the caliber of the means of destruction, and the subsequent layer towards the rear consists of fragments of fabric bonded together with an overlap , after which the back layers of whole-cut tissue fragments are arranged in the shape of a packet, and the rapport of the weave of fabrics and the strengthening of the threads in the direction from the front layers to the back decreases even in front of the back layers and / or between them and / or after them there are separation pads.

Такое градиентное построение пакета наряду с повышенным рассеиванием энергии при обстреле препятствует раздавливанию нитей за счет их равнозначного перемещения в ткани вдоль основы и утка с быстро нарастающим подключением массы пакета до полной остановки баллистического снаряда. This gradient construction of the package, along with increased energy dissipation during shelling, prevents the threads from being crushed due to their equivalent movement into the fabric along the warp and weft with a rapidly increasing mass of the package until the ballistic projectile stops completely.

Разделительные прокладки могут быть выполнены из тканевых, вспененных материалов или из их сочетания. Separation pads can be made of fabric, foam or a combination thereof.

На фиг. 1 показана схема строения защитного пакета. Защитный пакет содержит фронтальные слои 1, содержащие протяженные фрагменты ткани, выполненные в виде полос и уложенные параллельно с перекрытием без закрепления между собой, как показано на фиг. 2а и 2б. Прилегающий к фронтальному слой 2 выполнен из ткани, имеющей прорези, расположенные в шахматном порядке, причем их размер и расположение скоррелированы с калибром средства поражения. Как показано на фиг. 3, следующий по направлению к тылу слой 3 состоит из фрагментов ткани, скрепленных между собой внахлест. Тыльные слои 4 изготовлены из цельнокроеных фрагментов ткани по форме пакета, после которых расположена разделительная прокладка 5. In FIG. 1 shows a structure diagram of a protective bag. The protective bag contains frontal layers 1 containing extended tissue fragments made in the form of strips and laid in parallel with the overlap without being fixed to each other, as shown in FIG. 2a and 2b. Adjacent to the frontal layer 2 is made of fabric having slits arranged in a checkerboard pattern, their size and location being correlated with the caliber of the weapon. As shown in FIG. 3, the layer 3 next to the rear consists of tissue fragments that are overlapped together. The back layers 4 are made of one-piece fabric fragments in the form of a bag, after which there is a spacer 5.

Для подтверждения технического результата были изготовлены ткани следующих переплетений:
- саржа 1/2х3^*, 1/2х4, 2/2х4, 1/3х3, 3/3х2, 2/2, 3/5, 4/4, 5/5, 6/6:
- правильный атлас 5/2, 8/3, 10/7;
- неправильный атлас 4/1,2,3,2, 6/2,3,4,4,3,2;
- полотно (рогожка) 1х2, 1х3, 1х4, 1х6:
- вафельная ткань с раппортом из 4, 6, 8, 10 нитей;
- комбинированная неразрезная двухполотная основоворсовая ткань из капроновой мононити диаметром 0,2 мм и хлопчатобумажной нити линейной плотности 32 текс;
- неразрезная двухполотная основоворсовая ткань из капроновой мононити диаметром 0,15 мм и из комплексной нити СВМ линейной плотности 29,4 текс.To confirm the technical result, the following weave fabrics were made:
- twill 1 / 2x3 ^* , 1 / 2x4, 2 / 2x4, 1 / 3x3, 3 / 3x2, 2/2, 3/5, 4/4, 5/5, 6/6:
- the correct atlas 5/2, 8/3, 10/7;
- irregular atlas 4 / 1,2,3,2, 6 / 2,3,4,4,3,2;
- canvas (matting) 1x2, 1x3, 1x4, 1x6:
- waffle fabric with a rapport of 4, 6, 8, 10 threads;
- Combined continuous two-web warp cloth made of kapron monofilament with a diameter of 0.2 mm and cotton thread of linear density 32 tex;
- continuous two-sheet warp-cloth from kapron monofilament with a diameter of 0.15 mm and from a composite thread of CBM with a linear density of 29.4 tex.

^* - цифра, следующая за знаком умножения после обозначения раппорта переплетения ткани, указывает на усиление основных и уточных нитей в соответствующее число раз в пределах раппорта ткани. ^* - the figure following the multiplication sign after the designation of the fabric weave repeat indicates the reinforcement of the warp and weft yarns an appropriate number of times within the fabric repeat.

Из полученных тканей были изготовлены баллистические защитные пакеты, приведенные в примерах. The ballistic protective bags shown in the examples were made from the resulting fabrics.

Пример 1. Наружный (фронтальный) слой пакета размером 300х400 мм состоит из полос саржи 2/2 шириной 22 мм, уложенных вдоль большей оси пакета с перекрытием 8 мм. За ним следуют два слоя саржи 2/2 со сквозными прямыми прорезями длиной 15 мм, расположенными в шахматном порядке вдоль большей оси пакета, причем расстояние между прорезями в ряду равно 12 мм и расстояние между рядами - 12 мм и расположение слоев ткани исключает совпадение прорезей. Следующие 12 слоев состоят из квадратных фрагментов саржи 2/2х3, размером 120х120 мм, уложенных в каждом слое внахлест с соседними фрагментами, с перекрытием 25 мм и закрепленные в слое прямой швейной строчкой из хлопчатобумажной нити линейной плотности 16,7 текс. Затем располагаются 6 цельнокроеных слоев вафельной ткани с раппортом из 10 нитей. После вафельной ткани находятся 12 цельнокроеных слоев саржи 3/3х2 и затем 6 цельнокроеных слоев саржи 6/6. На тыльной стороне располагается разделительная прокладка из пенополиэтилена толщиной 12 мм, армированного неразрезной двухполотной основоворсовой тканью из капроновой мононити диаметром 0,15 мм. Вес 1 м² пакета составляет 6,8 кг,
Пример 2. Наружный слой пакета размером 300х400 мм состоит из полос саржи 3/5 шириной 20 мм, уложенных поперек большей оси пакета с перекрытием 7 мм. За ним следуют два слоя саржи 3/5 со сквозными прямыми прорезями длиной 12 мм, расположенными в шахматном порядке поперек большей оси пакета. Причем расстояние между прорезями в ряду равно 15 мм и расстояние между рядами - 12 мм и расположение слоев ткани исключает совпадение прорезей. Следующие 18 слоев состоят из квадратных фрагментов саржи 1/2х3 размером 150х150 мм, уложенных в каждом слое внахлест с соседними фрагментами с перекрытием 30 мм и закрепленными в слое швейной строчкой зигзаг из хлопчатобумажной нити линейной плотности 25 текс. Далее следуют 6 цельнокроеных слоев саржи 1/3х3, а затем 6 цельнокроеных слоев саржи 1/2х4 и 6 цельнокроеных слоев неправильного атласа 6/2, 3, 4, 4, 3, 2. На тыльной стороне пакета располагается разделительная прокладка из пенополиэтилена толщиной 15 мм, армированного неразрезной двухполотной основоворсовой тканью из нити СВМ линейной плотности 29,4 текс. Вес 1 м² пакета составляет 6,2 кг.Example 1. The outer (front) layer of a packet 300 × 400 mm in size consists of 2/2 twill strips 22 mm wide, laid along the major axis of the packet with an overlap of 8 mm. It is followed by two layers of twill 2/2 with straight through slits 15 mm long, staggered along the major axis of the package, with the distance between the slots in a row equal to 12 mm and the distance between the rows 12 mm and the location of the fabric layers eliminates the coincidence of the slots. The next 12 layers consist of square fragments of twill 2 / 2x3, size 120x120 mm, overlapped in each layer with adjacent fragments, with an overlap of 25 mm and fixed in a layer with a straight sewing stitch from cotton thread with a linear density of 16.7 tex. Then there are 6 whole-cut layers of waffle fabric with a rapport of 10 threads. After the wafer cloth, there are 12 whole-cut layers of twill 3 / 3x2 and then 6 whole-cut layers of twill 6/6. On the back there is a dividing pad made of 12 mm thick polyethylene foam reinforced with a continuous two-sheet warp cloth made of nylon monofilament with a diameter of 0.15 mm. The weight of 1 m ² package is 6.8 kg,
Example 2. The outer layer of a bag measuring 300x400 mm consists of 3/5 twill strips 20 mm wide, laid across the larger axis of the bag with an overlap of 7 mm. It is followed by two 3/5 serge layers with 12 mm straight through slots, staggered across the larger axis of the packet. Moreover, the distance between the slots in the row is 15 mm and the distance between the rows is 12 mm and the location of the fabric layers eliminates the coincidence of the slots. The next 18 layers consist of square fragments of twill 1 / 2x3 with a size of 150x150 mm, overlapped in each layer with adjacent fragments with an overlap of 30 mm and fixed in a layer with a sewing stitch of 25 tex cotton linear thread. This is followed by 6 whole-cut layers of twill 1 / 3x3, and then 6 whole-cut layers of twill 1 / 2x4 and 6 whole-cut layers of irregular satin 6/2, 3, 4, 4, 3, 2. On the back of the bag there is a 15 mm thick spacer strip mm reinforced with continuous two-sheet warp cloth of CBM thread of linear density 29.4 tex. The weight of 1 m ² package is 6.2 kg.

Пример 3. Наружный слой пакета размером 300х400 мм состоит из полос атласа 5/2 шириной 25 мм, уложенных вдоль большей оси пакета с перекрытием 10 мм. За ним следуют два слоя атласа 5/2 со сквозными прямыми прорезями длиной 15 мм, расположенными в шахматном порядке вдоль большей оси пакета, причем расстояние между прорезями в ряду равно 15 мм и расстояние между рядами 15 мм и расположение слоев исключает совпадение прорезей. Следующие 12 слоев состоят из квадратных фрагментов саржи 2/2х3 размером 130х130 мм, уложенных в каждом слое внахлест с соседними фрагментами с перекрытием 35 мм и закрепленными в слое швейной строчкой зигзаг из хлопчатобумажной нити линейной плотности 16,7 текс. Следующие 12 слоев состоят из квадратных фрагментов саржи 1/2х3 размером 110х110 мм, уложенных в каждом слое внахлест с соседними фрагментами с перекрытием 20 мм и закрепленными в слое швейной строчкой зигзаг из хлопчатобумажной нити линейной плотности 16,7 текс. Далее уложены 6 цельнокроеных слоев атласа 10/7. Следующие 8 цельнокроеных слоев состоят из вафельной ткани с раппортом из 10 нитей, после которых находится разделительная прокладка из комбинированной неразрезной двухполотной основоворсовой ткани толщиной 15 мм, выполненной из капроновой мононити диаметром 0,2 мм, причем коренные и уточные нити выполнены из хлопчатобумажной нити линейной плотности 32 текс. Масса 1 м² пакета составляет 6,5 кг.Example 3. The outer layer of a packet of 300x400 mm in size consists of 5/2 satin stripes with a width of 25 mm laid along the major axis of the packet with an overlap of 10 mm. It is followed by two 5/2 satin layers with through straight slits 15 mm long, staggered along the major axis of the packet, with the distance between the slots in a row equal to 15 mm and the distance between the rows 15 mm and the location of the layers eliminating the coincidence of the slots. The next 12 layers consist of square fragments of twill 2 / 2x3 in size 130x130 mm, overlapped in each layer with adjacent fragments with an overlap of 35 mm and fixed in a layer with a sewing stitch zigzag of cotton thread of linear density 16.7 tex. The next 12 layers consist of square fragments of twill 1 / 2x3 in size 110x110 mm, overlapped in each layer with adjacent fragments with an overlap of 20 mm and fixed in a layer with a sewing stitch zigzag of cotton thread of linear density 16.7 tex. Next, 6 whole-cut atlas 10/7 layers are laid. The next 8 whole-cut layers consist of a waffle fabric with a rapport of 10 threads, after which there is a separation pad of a combined continuous two-web warp cloth 15 mm thick made of 0.2 mm diameter nylon monofilament, and the warp and weft threads are made of linear density cotton thread 32 tex. The weight of 1 m ² package is 6.5 kg.

Пример 4. Наружный слой пакета размером 300х400 мм состоит из равноплотных лент саржевого переплетения 1/2 шириной 22 мм из нити СВМ 29,4 текс по основе и 58,8 текс по утку, уложенных вдоль большей оси пакета параллельно с перекрытием 9 мм без закрепления между собой, причем с одного края все ленты пристрочены строчкой зигзаг из хлопчатобумажной нити линейной плотности 25 текс к ткани полотняного переплетения из нити Русар 58,8 текс, усиленной в 4 раза. За ним следует 2 слоя полотна, усиленного в 2 раза, со сквозными прямыми прорезями длиной 12 мм, расположенными в шахматном порядке вдоль большей оси пакета, причем расстояние между прорезями в ряду равно 12 мм и расстояние между рядами 12 мм и расположение слоев исключает совпадение прорезей. Следующие 6 слоев состоят из квадратных фрагментов саржи 2/2х3 размером 120х120 мм, уложенных в каждом слое внахлест с соседними фрагментами с перекрытием 30 мм и закрепленными в слое швейной строчкой зигзаг из хлопчатобумажной нити линейной плотности 16,7 текс. Следующие 6 слоев состоят из квадратных фрагментов саржи 1/2х4 размером 120х120 мм, уложенных в каждом слое внахлест с соседними фрагментами с перекрытием 30 мм и закрепленными в слое швейной строчкой зигзаг из хлопчатобумажной нити линейной плотности 16,7 текс. Следующие 6 слоев состоят из квадратных фрагментов саржи 1/2х3 размером 120х120 мм, уложенных в каждом слое внахлест с соседними фрагментами с перекрытием 30 мм и закрепленными в слое швейной строчкой зигзаг из хлопчатобумажной нити линейной плотности 16,7 текс. За ними следует разделительная прокладка из комбинированной неразрезной двухполотной основоворсовой ткани толщиной 12 мм, выполненной из капроновой мононити диаметром 0,2 мм, причем коренные и уточные нити объемной ткани выполнены из хлопчатобумажной нити линейной плотности 32 текс. Следующие 6 цельнокроеных слоев состоят из саржи 6/6. Далее следует 6 цельнокроеных слоев саржи 5/5. На тыльной стороне находятся 6 цельнокроеных слоев вафельной ткани с раппортом из 4 нитей. Масса 1 м² пакета составляет 6,2 кг.Example 4. The outer layer of a bag with a size of 300x400 mm consists of equal-weight 1/2 twill ribbons 1/2 with a width of 22 mm from a CBM thread of 29.4 tex on the warp and 58.8 tex on the weft, laid along the major axis of the bag in parallel with an overlap of 9 mm without fixing between each other, and from one edge all the ribbons are sewn together with a zigzag stitch from cotton thread of linear density 25 tex to plain fabric from Rusar 58.8 tex reinforced 4 times. It is followed by 2 layers of the web reinforced by 2 times, with through straight slits 12 mm long, arranged in a checkerboard pattern along the greater axis of the package, with the distance between the slots in a row equal to 12 mm and the distance between the rows of 12 mm and the location of the layers eliminates the coincidence of the slots . The next 6 layers consist of square fragments of twill 2 / 2x3 in size 120x120 mm, overlapped in each layer with adjacent fragments with an overlap of 30 mm and fixed in a layer with a sewing stitch zigzag of cotton thread of linear density 16.7 tex. The next 6 layers consist of square fragments of twill 1 / 2x4, size 120x120 mm, overlapped in each layer with adjacent fragments with an overlap of 30 mm and fixed in a layer with a sewing stitch zigzag of cotton thread of linear density 16.7 tex. The next 6 layers consist of square fragments of twill 1 / 2x3 with a size of 120x120 mm, overlapped in each layer with adjacent fragments with an overlap of 30 mm and fixed in a layer with a sewing stitch zigzag of cotton thread of linear density 16.7 tex. They are followed by a separation pad of a combined continuous two-sheet warp cloth 12 mm thick made of nylon monofilament with a diameter of 0.2 mm, and the warp and weft threads of the bulk fabric are made of cotton thread with a linear density of 32 tex. The next 6 whole layers are composed of 6/6 twill. Followed by 6 all-cut layers of twill 5/5. On the back there are 6 whole-cut layers of waffle fabric with a rapport of 4 threads. The weight of 1 m ² package is 6.2 kg.

Пример 5. Наружная сторона пакета размером 300х400 мм состоит из 6 цельнокроеных слоев саржи 2/2х4. Следующие 6 цельнокроеных слоев содержат саржу 1/2х4, после которой расположены 12 цельнокроеных слоев саржи 1/2х3. Следующие 6 цельнокроеных слоев состоят из ткани полотняного переплетения, усиленной в 4 раза, после которой расположены 6 цельнокроеных слоев ткани вафельного переплетения с раппортом из 6 нитей. Следующие 6 цельнокроеных слоев состоят из саржи 6/6, после которой расположены 6 цельнокроеных слоев саржи 5/5 и затем разделительная прокладка, представляющая собой плетеный мат толщиной 8 мм из полипропиленовой нити линейной плотности 140 текс. Масса 1 м² пакета составляет 7,5 кг.Example 5. The outer side of the package with a size of 300x400 mm consists of 6 whole-cut layers of twill 2 / 2x4. The next 6 whole layers contain twill 1 / 2x4, after which there are 12 whole layers twill 1 / 2x4. The next 6 whole-cut layers consist of 4-fold linen fabric reinforced after which there are 6 whole-cut layers of waffle-weave fabric with a rapport of 6 threads. The next 6 whole-cut layers consist of 6/6 twill, after which there are 6 whole-cut 5/5 twill layers and then a spacer, which is an 8 mm thick woven mat of 140 tex linear density polypropylene yarn. The weight of 1 m ² package is 7.5 kg.

Баллистическая стойкость защитных пакетов оценивалась по результатам огнестрельных испытаний на пластилиновом блоке из пистолета Токарева (ТТ) пулей калибра 7,62 мм с металлическим сердечником с дистанции 5 м перпендикулярно к поверхности пакета при скорости пули 450-460 м/с. The ballistic resistance of the protective bags was evaluated by the results of fire tests on a plasticine block from a Tokarev pistol (TT) with a 7.62 mm bullet with a metal core from a distance of 5 m perpendicular to the surface of the bag at a bullet speed of 450-460 m / s.

Результаты испытаний приведены в таблице. The test results are shown in the table.

Данные таблицы показывают, что предлагаемые ткани из арамидных нитей и баллистические пакеты на их основе в соответствии с формулой изобретения обладают высокими пулезащитными свойствами, что позволяет уменьшить массу бронежилета и повысить его эргономические характеристики. These tables show that the proposed fabric from aramid yarns and ballistic packages based on them in accordance with the claims have high bulletproof properties, which reduces the weight of the bulletproof vest and increase its ergonomic characteristics.

Приведенные примеры конкретного выполнения ткани и защитного баллистического пакета не ограничивают притязания заявителя, изложенные в формуле изобретения. The above examples of specific performance of the fabric and the protective ballistic package do not limit the claims of the applicant set forth in the claims.

Источники информации
1. Пат. РФ N 2041986 кл. D 03 D 15/00, 1995 г.Sources of information
1. Pat. RF N 2041986 cl. D 03 D 15/00, 1995

2. Пат. РФ N 2042915 кл. F 41 H 1/02, 1995 г. 2. Pat. RF N 2042915 class. F 41 H 1/02, 1995

3. Пат. РФ N 2126856 кл. D 03 D 15/00, 1999 г. 3. Pat. RF N 2126856 class. D 03 D 15/00, 1999

4. Пат. США N 4413357, кл. F 41 H 1/02, 1983 г. 4. Pat. USA N 4413357, class. F 41 H 1/02, 1983

5. Пат США N 83097, кл. F 41 H 1/02, 1980 г. 5. US Pat. N 83097, cl. F 41 H 1/02, 1980

6. Заявка ФРГ N 3328415, кл. F 41 H1/02, 1985 г. 6. Application of Germany N 3328415, CL F 41 H1 / 02, 1985

7. Пат. РФ N 1792517 кл. F 41 H 1/02, 1993 г. 7. Pat. RF N 1792517 class. F 41 H 1/02, 1993

8. Пат. РФ N 1799450 кл. F 41 H 1/02, 1994 г. 8. Pat. RF N 1799450 cells F 41 H 1/02, 1994

9. Пат. РФ N 2098739 кл. F 41 H 1/02, 1988 г. 9. Pat. RF N 2098739 cells F 41 H 1/02, 1988

Claims (3)

1. Ткань для баллистической защиты из высокопрочных арамидных нитей равной линейной плотности по основе и утку с одинаковой продольной конфигурацией, равным количеством нитей на единицу ширины в обоих направлениях и коэффициентом крутки, не превышающим 4, отличающаяся тем, что она выполнена атласным или сатиновым, саржевым, вафельным переплетением одиночных нитей или атласным или сатиновым, саржевым, полотняным, вафельным переплетением из в 2 - 6 нитей по основе и утку, при этом правильное атласное или сатиновое переплетение имеет раппорт от 5 до 10 с постоянным сдвигом от 2 до 7, а неправильное атласное или сатиновое переплетение имеет раппорт от 4 до 10 с переменным сдвигом от 1 до 8, саржевое переплетение имеет число основных перекрытий от 1 до 8 и число уточных перекрытий от 2 до 8, число нитей в раппорте вафельного переплетения составляет от 4 до 16. 1. Fabric for ballistic protection from high-strength aramid threads of equal linear density on the warp and weft with the same longitudinal configuration, an equal number of threads per unit width in both directions and a twist coefficient not exceeding 4, characterized in that it is made of satin or satin, twill , single-strand wafer or satin or satin, twill, linen, wafer weave of 2 to 6 warp and weft, with the correct satin or satin weave t 5 to 10 with a constant shift from 2 to 7, and the wrong satin or satin weave has a rapport from 4 to 10 with a variable shift from 1 to 8, the twill weave has the number of main overlaps from 1 to 8 and the number of weft overlaps from 2 to 8 , the number of threads in the wafer weave pattern is 4 to 16. 2. Баллистический защитный тканевый пакет, содержащий последовательно расположенные фронтальные и тыльные слои тканей из высокопрочных арамидных нитей, отличающийся тем, что ткань для баллистической защиты выполнена из высокопрочных арамидных нитей равной линейной плотности по основе и утку с одинаковой продольной конфигурацией, равным количеством нитей на единицу ширины в обоих направлениях и коэффициентом крутки, не превышающим 4, атласным или сатиновым, саржевым, вафельным переплетением одиночных нитей или атласным или сатиновым, саржевым, полотняным, вафельным переплетением из в 2 - 6 нитей по основе и утку, при этом правильное атласное или сатиновое переплетение имеет раппорт от 5 до 10 с постоянным сдвигом от 2 до 7, а неправильное атласное или сатиновое переплетение имеет раппорт от 4 до 10 с переменным сдвигом от 1 до 8, саржевое переплетение имеет число основных перекрытий от 1 до 8 и число уточных перекрытий от 2 до 8, число нитей в раппорте вафельного переплетения составляет от 4 до 16, причем слои расположены так, что фронтальные и тыльные слои по отношению к средству поражения выполнены из тканей, имеющих по основе и утку усиленные в 2 - 6 раз нити, причем раппорт переплетения тканей и усиление нитей в них в направлении от фронтальных к тыльным слоям уменьшается и перед тыльными слоями и/или между ними и/или после них расположены разделительные прокладки. 2. Ballistic protective fabric package containing sequentially located front and back layers of fabric from high strength aramid yarns, characterized in that the fabric for ballistic protection is made of high strength aramid yarns of equal linear density on the base and weft with the same longitudinal configuration, equal number of threads per unit width in both directions and with a twist coefficient not exceeding 4, satin or satin, twill, waffle weaving of single threads or satin or satin, arzhevym, linen, waffle weaving from 2 to 6 threads on the warp and weft, while the correct satin or satin weave has a rapport from 5 to 10 with a constant shift from 2 to 7, and the wrong satin or satin weave has a rapport from 4 to 10 with a variable shift from 1 to 8, the twill weave has the number of main overlaps from 1 to 8 and the number of weft overlaps from 2 to 8, the number of threads in the wafer weave repeat is from 4 to 16, the layers being arranged so that the front and back layers are in relation to the medium time The stitches are made of fabrics having warp and weft reinforced by 2-6 times, the rapport of the weaving of fabrics and the strengthening of the threads in them in the direction from the front to the back layers decrease and are located in front of the back layers and / or between them and / or after them separation pads. 3. Баллистический защитный тканевый пакет по п.2, отличающийся тем, что фронтальные слои состоят из протяженных фрагментов ткани, выполненных в виде полос и уложенных параллельно с перекрытием без закрепления между собой, прилегающие к фронтальным слои выполнены из ткани, имеющей прорези, расположенные в шахматном порядке с размером и шагом, скоррелированным с калибром средства поражения, а последующие в направлении к тылу слои состоят из фрагментов ткани, скрепленных между собой внахлест, после которых расположены тыльные слои из цельнокроеных фрагментов ткани по форме пакета. 3. Ballistic protective fabric package according to claim 2, characterized in that the frontal layers consist of extended tissue fragments made in the form of strips and laid in parallel with the overlap without fixing each other, adjacent to the frontal layers are made of fabric having slots located in staggered with size and pitch, correlated with the caliber of the means of destruction, and the subsequent layers towards the rear consist of tissue fragments that are overlapped together, after which the rear layers of whole swarming tissue fragments shaped package.