RU2132317C1 - Method of decorative building paste producing - Google Patents
Method of decorative building paste producing Download PDFInfo
- Publication number
- RU2132317C1 RU2132317C1 RU97102601A RU97102601A RU2132317C1 RU 2132317 C1 RU2132317 C1 RU 2132317C1 RU 97102601 A RU97102601 A RU 97102601A RU 97102601 A RU97102601 A RU 97102601A RU 2132317 C1 RU2132317 C1 RU 2132317C1
- Authority
- RU
- Russia
- Prior art keywords
- pigment
- white
- portland cement
- sand
- specific surface
- Prior art date
Abstract
Description
Изобретение относится к строительным материалам и может быть использовано в технологии приготовления композиции для отделочных работ. The invention relates to building materials and can be used in the technology of preparing compositions for decoration.
Известен способ приготовления отделочных растворов путем смешения раствора полимера, белого цемента, заполнителя и пигмента. Этот способ является наиболее близким по технической сущности и достигаемому эффекту к предлагаемому, он описан в авторском свидетельстве SU N 250004, 1969 г. A known method of preparing finishing solutions by mixing a polymer solution, white cement, aggregate and pigment. This method is the closest in technical essence and the achieved effect to the proposed, it is described in the copyright certificate SU N 250004, 1969
Технической задачей является повышение прочностных показателей и снижение расхода пигмента при сохранении декоративных свойств. The technical task is to increase strength indicators and reduce pigment consumption while maintaining decorative properties.
Техническая задача достигается тем, что способ изготовления декоративных строительных растворов включает смешение белого портландцемента, пигмента и активированного песка, причем белый портландцемент предварительно размалывают совместно с пластификатором до удельной поверхности 4500 - 5000 см2/г, после чего вводят оболочковый пигмент и осуществляют домол в течение 10 - 15 мин, а затем полученный продукт смешивают с активированным белым песком, имеющим удельную поверхность 4500 - 5000 см2/г в течение 10 - 15 мин.The technical problem is achieved by the fact that the method of manufacturing decorative mortar includes mixing white Portland cement, pigment and activated sand, and white Portland cement is pre-milled together with a plasticizer to a specific surface of 4500-5000 cm 2 / g, after which sheath pigment is introduced and milling is carried out for 10-15 minutes, and then the resulting product is mixed with activated white sand having a specific surface area of 4500-5000 cm 2 / g for 10-15 minutes.
В качестве пигмента используют оболочковый пигмент, в качестве белого песка - Люберецкий песок, в качестве белого портландцемента - белый портландцемент Щуровского цементного завода. Shell pigment is used as a pigment, Lyubertsy sand as white sand, White Portland cement of the Schurovsky cement plant as white portland cement.
Предложенный способ осуществляют следующим образом. The proposed method is as follows.
Белый портландцемент и пластификатор C-3 размалывают до удельной поверхности 4500 - 5000 см2/г. Затем оболочковый пигмент вводят в продукт помола и осуществляют домол в течение 10 - 15 мин, что позволяет равномерно распределиться пигменту в смеси.White Portland cement and plasticizer C-3 are ground to a specific surface area of 4,500-5,000 cm 2 / g. Then, the shell pigment is introduced into the grinding product and milling is carried out for 10-15 minutes, which allows the pigment to be evenly distributed in the mixture.
Белый песок активируют путем помола до удельной поверхности 4500 - 5000 см2/г и смешивают с предварительно полученной смесью в течение 10 - 15 мин до однородного состояния. В полученный продукт при механическом смешивании вводят заполнитель - белый песок в заданном соотношении.White sand is activated by grinding to a specific surface of 4500-5000 cm 2 / g and mixed with the previously prepared mixture for 10-15 minutes until smooth. When the product is mixed mechanically, an aggregate is introduced - white sand in a predetermined ratio.
Пример 1. Белый портландцемент и пластификатор С-3 размалывают до Sуд - 4500 см2/г. Домол с оболочковым пигментом, количество которого равно 0,15%, осуществляется в течение 10 мин. Затем вводят белый песок Sуд - 5000 см2/г и перемешивают в течение 12 мин, а затем смешивают с заполнителем - белым песком.Example 1. White Portland cement and plasticizer C-3 are ground to S beats - 4500 cm 2 / g. A domol with a shell pigment, the amount of which is 0.15%, is carried out for 10 minutes. Then introduce white sand S beats - 5000 cm 2 / g and mix for 12 minutes, and then mix with aggregate - white sand.
Расход пигмента снижается на 35%, прочность при сжатии при твердении 1 сут равна 7,1 МПа, 28 сут - 43 МПа. The pigment consumption is reduced by 35%, the compressive strength during hardening for 1 day is 7.1 MPa, 28 days - 43 MPa.
Пример 2. Белый портландцемент и С-3 размалывают до Sуд - 5000 см2/г, домол с оболочковым пигментом, количество которого равно 0,18%, осуществляют в течение 12 мин. Вводят активированный белый песок Sуд - 4500 см2/г и перемешивают смесь в течение 10 мин, а затем полученную смесь смешивают с заполнителем - белым песком.Example 2. White Portland cement and C-3 are ground to S beats of 5000 cm 2 / g, a mantle with shell pigment, the amount of which is 0.18%, is carried out for 12 minutes. Activated white sand S beats - 4500 cm 2 / g is introduced and the mixture is stirred for 10 minutes, and then the resulting mixture is mixed with aggregate - white sand.
Прочность при сжатии в 1 сут составляет 8,9 МПа, в 28 сут - 42,8 МПа, расход пигмента снизился на 25%. The compressive strength in 1 day is 8.9 MPa, in 28 days - 42.8 MPa, pigment consumption decreased by 25%.
Пример 3. Белый портландцемент и пластификатор С-3 измельчают до Sуд - 4800 см2/г, домалывают с оболочковым пигментом, количество которого равно 0,16%, в течение 15 мин. Затем вводят предварительно активированный белый песок с Sуд - 4500 см2/г и перемешивают смесь в течение 15 мин, а затем полученную композицию смешивают с заполнителем - белым песком в соотношении 1 : 3 и в/ц = 0,4. Прочность при сжатии в 1 сут твердения равна 10,5 МПа, в 28 сут твердения - 45,3 МПа.Example 3. White Portland cement and plasticizer C-3 are crushed to S beats - 4800 cm 2 / g, crushed with shell pigment, the amount of which is 0.16%, for 15 minutes Then preactivated white sand is introduced with S beats - 4500 cm 2 / g and the mixture is stirred for 15 minutes, and then the resulting composition is mixed with aggregate - white sand in a ratio of 1: 3 and w / c = 0.4. The compressive strength in 1 day of hardening is 10.5 MPa, in 28 days of hardening - 45.3 MPa.
Аналогичные результаты могут быть получены и при использовании других типов пластификаторов. Similar results can be obtained using other types of plasticizers.
Таким образом, использование предложенного способа позволяет снизить расход пигмента и повысить прочностные показатели декоративного строительного раствора. Thus, the use of the proposed method can reduce the consumption of pigment and increase the strength characteristics of decorative mortar.
Claims (1)