RU2109618C1 - Method of vibration treatment of easily deformable metal parts - Google Patents

Abstract

FIELD: mechanical engineering; instrumentation engineering. SUBSTANCE: parts being treated are placed in container the height or diameter of which does not exceed 20 amplitudes. Then abrasive and cleaning medium in the form of soft granulated material, for example polyvinylchloride plastic compound, are placed in container. Vibrator imparts oscillatory motion to container at frequency of 46-50 Hz and amplitude of 2.5-3.0 mm. EFFECT: enhanced surface treatment of parts. 1 tbl

Description

Изобретение относится к поверхностной обработке деталей и может найти применение в машиностроении и приборостроении для отделочной и упрочняющей обработки металлических и легкодеформируемых деталей малых масс и размеров. The invention relates to the surface treatment of parts and can find application in mechanical engineering and instrumentation for finishing and hardening processing of metal and easily deformable parts of small masses and sizes.

Известен способ сухой вибрационной обработки деталей толщиной до 0,5 мм, осуществляемый на установке с вибропроводом и тороидальным контейнером. Обрабатываемые детали и образцы помещают в контейнер, которому посредством вибропровода придают эллиптические колебания с частотой 45-50 Гц и амплитудами 2,5-3 мм. Авт.св.1726212 кл. B 24 B 31/06, 1992. A known method of dry vibration processing of parts with a thickness of up to 0.5 mm, carried out on the installation with a vibroconductor and a toroidal container. The parts and samples to be processed are placed in a container, to which elliptical vibrations with a frequency of 45-50 Hz and amplitudes of 2.5-3 mm are imparted by means of a vibroconductor. Auth. St. 1726212 cl. B 24 B 31/06, 1992.

Задачей, на решение которой направлено заявляемое изобретение, является интенсификация процесса обработки металлических легкодеформируемых деталей с исключением деформации последних. The task to which the invention is directed is the intensification of the processing of metal easily deformable parts with the exception of deformation of the latter.

Технический результат, который может быть получен при осуществлении изобретения - чистота процесса обработки и увеличение сил трения между обрабатываемыми деталями и поверхностью контейнера. The technical result that can be obtained by carrying out the invention is the purity of the processing process and the increase in friction between the workpieces and the surface of the container.

Для этого в способе сухой обработки вибрационной металлических легкодеформируемых деталей, включающем наполнение контейнера обрабатываемыми деталями и придания ему колебательных движений, согласно изобретению последние выбирают частотой 46-50 Гц и амплитудой 2,5-3 мм и используют контейнер с размером в плоскости одной из составляющих колебания не более 20 амплитуд с очищающей средой в виде мягкого гранулированного материала типа поливинилхлоридного пластиката и/или пенорезины. For this, in the method of dry processing of vibrating metal easily deformable parts, including filling the container with machined parts and giving it oscillatory movements, according to the invention, the latter are selected with a frequency of 46-50 Hz and an amplitude of 2.5-3 mm and use a container with a size in the plane of one of the components of the vibration no more than 20 amplitudes with a cleaning medium in the form of soft granular material such as polyvinyl chloride plastic compound and / or foam rubber.

Экспериментальные исследования показали, что заявленные условия выполнения способа обеспечивают мягкий режим обработки (исключают деформации деталей) и в то же время происходит интенсивное соударение обрабатываемых деталей между собой, внутренней поверхностью контейнера и очищающей средой, т.е. возникающие в процессе обработки силы трения обеспечивают как процесс обработки деталей, так и очистку их, т.к. отходы обработки вкрапливаются в мягкий гранулированный материал, который в свою очередь становится дополнительным абразивным материалом. Experimental studies have shown that the claimed conditions for the implementation of the method provide a soft processing mode (exclude deformation of parts) and at the same time there is an intensive collision of the processed parts between themselves, the inner surface of the container and the cleaning medium, i.e. friction forces arising during processing provide both the processing of parts and their cleaning, because processing waste is embedded in soft granular material, which in turn becomes an additional abrasive material.

При снижении режима вибрации и увеличения высоты контейнера или диаметра контейнера более 20 амплитуд процесс обработки деталей практически отсутствует. With a decrease in the vibration mode and an increase in the height of the container or the diameter of the container over 20 amplitudes, the processing of parts is practically absent.

При увеличении режимов вибрации происходит резкое возрастание температуры и возможно спекание и залипание деталей и очищающей среды. With an increase in vibration modes, a sharp increase in temperature occurs and sintering and sticking of parts and a cleaning medium are possible.

Обработка по предлагаемому способу осуществляется следующим образом. Processing by the proposed method is as follows.

Обрабатываемые детали помещают в контейнер, имеющий высоту (вертикальная составляющая колебания) или диаметр (горизонтальная составляющая колебания) не более 20 амплитуд, затем в контейнер закладывают абразив и очищающую среду, например гранулированный пластикат. Общий объем заполнения контейнера примерно 70-80%. Масса очищающей среды определяется в зависимости от наличия заусенцев и загрязненности деталей и может составлять 1/50-1/10 от массы деталей. Форма контейнера может быть в виде параллелепипеда или цилиндра. Контейнер закрепляют на площадке вибратора и придают ему колебательные движения частотой 46-50 Гц и амплитудой 2,5-3 мм. Время обработки зависит от материала деталей, количества заусенцев и массы деталей. The parts to be processed are placed in a container having a height (vertical component of vibration) or a diameter (horizontal component of vibration) of no more than 20 amplitudes, then an abrasive and a cleaning medium, for example, granular plastic compound, are placed in the container. The total filling volume of the container is approximately 70-80%. The mass of the cleaning medium is determined depending on the presence of burrs and contamination of the parts and may be 1 / 50-1 / 10 of the mass of the parts. The shape of the container may be in the form of a parallelepiped or a cylinder. The container is fixed on the platform of the vibrator and gives it oscillatory movements with a frequency of 46-50 Hz and an amplitude of 2.5-3 mm. Processing time depends on the material of the parts, the number of burrs and the mass of the parts.

Примеры конкретного выполнения способа представлены в таблице. Examples of specific performance of the method are presented in the table.

Claims (1)

Способ вибрационной обработки металлических легкодеформируемых деталей, при котором контейнер заполняют обрабатываемыми деталями и очищающей средой, при этом контейнеру сообщают колебания с частотами 46 - 50 Гц и амплитудами 2,5 - 3,0 мм, отличающийся тем, что используют контейнер с размером в плоскости колебания, преимущественно вертикальной, не более 20 амплитуд, а в качестве очищающей среды берут поливинилхлоридный пластикат и/или пенорезину. The method of vibration processing of metal easily deformable parts, in which the container is filled with machined parts and a cleaning medium, while the container is informed of vibrations with frequencies of 46-50 Hz and amplitudes of 2.5-3.0 mm, characterized in that they use a container with a dimension in the plane of oscillation , mainly vertical, not more than 20 amplitudes, and as a cleaning medium take polyvinyl chloride plastic compound and / or foam rubber.