RU2015143094A - Синтетический цинковый гекторит и его гидротермическое получение - Google Patents
Синтетический цинковый гекторит и его гидротермическое получение Download PDFInfo
- Publication number
- RU2015143094A RU2015143094A RU2015143094A RU2015143094A RU2015143094A RU 2015143094 A RU2015143094 A RU 2015143094A RU 2015143094 A RU2015143094 A RU 2015143094A RU 2015143094 A RU2015143094 A RU 2015143094A RU 2015143094 A RU2015143094 A RU 2015143094A
- Authority
- RU
- Russia
- Prior art keywords
- acid
- source
- hydroxide
- lithium
- substituted
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B33/00—Silicon; Compounds thereof
- C01B33/20—Silicates
- C01B33/32—Alkali metal silicates
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K8/00—Cosmetics or similar toiletry preparations
- A61K8/02—Cosmetics or similar toiletry preparations characterised by special physical form
- A61K8/0241—Containing particulates characterized by their shape and/or structure
- A61K8/0254—Platelets; Flakes
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K8/00—Cosmetics or similar toiletry preparations
- A61K8/18—Cosmetics or similar toiletry preparations characterised by the composition
- A61K8/19—Cosmetics or similar toiletry preparations characterised by the composition containing inorganic ingredients
- A61K8/25—Silicon; Compounds thereof
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K8/00—Cosmetics or similar toiletry preparations
- A61K8/18—Cosmetics or similar toiletry preparations characterised by the composition
- A61K8/19—Cosmetics or similar toiletry preparations characterised by the composition containing inorganic ingredients
- A61K8/27—Zinc; Compounds thereof
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61Q—SPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
- A61Q1/00—Make-up preparations; Body powders; Preparations for removing make-up
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61Q—SPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
- A61Q19/00—Preparations for care of the skin
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01G—COMPOUNDS CONTAINING METALS NOT COVERED BY SUBCLASSES C01D OR C01F
- C01G9/00—Compounds of zinc
- C01G9/006—Compounds containing, besides zinc, two ore more other elements, with the exception of oxygen or hydrogen
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C14/00—Glass compositions containing a non-glass component, e.g. compositions containing fibres, filaments, whiskers, platelets, or the like, dispersed in a glass matrix
- C03C14/004—Glass compositions containing a non-glass component, e.g. compositions containing fibres, filaments, whiskers, platelets, or the like, dispersed in a glass matrix the non-glass component being in the form of particles or flakes
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C8/00—Enamels; Glazes; Fusion seal compositions being frit compositions having non-frit additions
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J5/00—Manufacture of articles or shaped materials containing macromolecular substances
- C08J5/18—Manufacture of films or sheets
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K3/00—Use of inorganic substances as compounding ingredients
- C08K3/34—Silicon-containing compounds
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/0015—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings
- C09C1/0018—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings uncoated and unlayered plate-like particles
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/0015—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings
- C09C1/0024—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings comprising a stack of coating layers with alternating high and low refractive indices, wherein the first coating layer on the core surface has the high refractive index
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C1/00—Treatment of specific inorganic materials other than fibrous fillers; Preparation of carbon black
- C09C1/0015—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings
- C09C1/0024—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings comprising a stack of coating layers with alternating high and low refractive indices, wherein the first coating layer on the core surface has the high refractive index
- C09C1/003—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings comprising a stack of coating layers with alternating high and low refractive indices, wherein the first coating layer on the core surface has the high refractive index comprising at least one light-absorbing layer
- C09C1/0039—Pigments exhibiting interference colours, e.g. transparent platelets of appropriate thinness or flaky substrates, e.g. mica, bearing appropriate thin transparent coatings comprising a stack of coating layers with alternating high and low refractive indices, wherein the first coating layer on the core surface has the high refractive index comprising at least one light-absorbing layer consisting of at least one coloured inorganic material
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D11/00—Inks
- C09D11/02—Printing inks
- C09D11/03—Printing inks characterised by features other than the chemical nature of the binder
- C09D11/037—Printing inks characterised by features other than the chemical nature of the binder characterised by the pigment
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D11/00—Inks
- C09D11/30—Inkjet printing inks
- C09D11/32—Inkjet printing inks characterised by colouring agents
- C09D11/322—Pigment inks
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/60—Additives non-macromolecular
- C09D7/61—Additives non-macromolecular inorganic
- C09D7/62—Additives non-macromolecular inorganic modified by treatment with other compounds
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/66—Additives characterised by particle size
- C09D7/69—Particle size larger than 1000 nm
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
- C09K21/00—Fireproofing materials
- C09K21/02—Inorganic materials
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
- D21H17/63—Inorganic compounds
- D21H17/67—Water-insoluble compounds, e.g. fillers, pigments
- D21H17/68—Water-insoluble compounds, e.g. fillers, pigments siliceous, e.g. clays
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K2800/00—Properties of cosmetic compositions or active ingredients thereof or formulation aids used therein and process related aspects
- A61K2800/10—General cosmetic use
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K2800/00—Properties of cosmetic compositions or active ingredients thereof or formulation aids used therein and process related aspects
- A61K2800/40—Chemical, physico-chemical or functional or structural properties of particular ingredients
- A61K2800/41—Particular ingredients further characterized by their size
- A61K2800/412—Microsized, i.e. having sizes between 0.1 and 100 microns
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K2800/00—Properties of cosmetic compositions or active ingredients thereof or formulation aids used therein and process related aspects
- A61K2800/40—Chemical, physico-chemical or functional or structural properties of particular ingredients
- A61K2800/42—Colour properties
- A61K2800/43—Pigments; Dyes
-
- A—HUMAN NECESSITIES
- A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
- A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
- A61K2800/00—Properties of cosmetic compositions or active ingredients thereof or formulation aids used therein and process related aspects
- A61K2800/40—Chemical, physico-chemical or functional or structural properties of particular ingredients
- A61K2800/58—Metal complex; Coordination compounds
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/20—Particle morphology extending in two dimensions, e.g. plate-like
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/20—Particle morphology extending in two dimensions, e.g. plate-like
- C01P2004/22—Particle morphology extending in two dimensions, e.g. plate-like with a polygonal circumferential shape
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/61—Micrometer sized, i.e. from 1-100 micrometer
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C2200/00—Compositional and structural details of pigments exhibiting interference colours
- C09C2200/10—Interference pigments characterized by the core material
- C09C2200/102—Interference pigments characterized by the core material the core consisting of glass or silicate material like mica or clays, e.g. kaolin
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C2200/00—Compositional and structural details of pigments exhibiting interference colours
- C09C2200/10—Interference pigments characterized by the core material
- C09C2200/102—Interference pigments characterized by the core material the core consisting of glass or silicate material like mica or clays, e.g. kaolin
- C09C2200/1025—Interference pigments characterized by the core material the core consisting of glass or silicate material like mica or clays, e.g. kaolin comprising at least one metal layer adjacent to core material, e.g. core-M or M-core-M
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C2200/00—Compositional and structural details of pigments exhibiting interference colours
- C09C2200/30—Interference pigments characterised by the thickness of the core or layers thereon or by the total thickness of the final pigment particle
- C09C2200/302—Thickness of a layer with high refractive material
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09C—TREATMENT OF INORGANIC MATERIALS, OTHER THAN FIBROUS FILLERS, TO ENHANCE THEIR PIGMENTING OR FILLING PROPERTIES ; PREPARATION OF CARBON BLACK ; PREPARATION OF INORGANIC MATERIALS WHICH ARE NO SINGLE CHEMICAL COMPOUNDS AND WHICH ARE MAINLY USED AS PIGMENTS OR FILLERS
- C09C2200/00—Compositional and structural details of pigments exhibiting interference colours
- C09C2200/30—Interference pigments characterised by the thickness of the core or layers thereon or by the total thickness of the final pigment particle
- C09C2200/303—Thickness of a layer with low refractive material
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Health & Medical Sciences (AREA)
- Materials Engineering (AREA)
- Inorganic Chemistry (AREA)
- Wood Science & Technology (AREA)
- Animal Behavior & Ethology (AREA)
- Veterinary Medicine (AREA)
- Public Health (AREA)
- General Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Birds (AREA)
- Epidemiology (AREA)
- General Chemical & Material Sciences (AREA)
- Medicinal Chemistry (AREA)
- Manufacturing & Machinery (AREA)
- Polymers & Plastics (AREA)
- Dispersion Chemistry (AREA)
- Geochemistry & Mineralogy (AREA)
- Nanotechnology (AREA)
- Ceramic Engineering (AREA)
- Dermatology (AREA)
- Silicates, Zeolites, And Molecular Sieves (AREA)
- Cosmetics (AREA)
- Pigments, Carbon Blacks, Or Wood Stains (AREA)
- Paints Or Removers (AREA)
- Inks, Pencil-Leads, Or Crayons (AREA)
Claims (87)
1. Пластина синтетического цинкового гекторита формулы (1)
где
I представляет собой межслойный моновалентный катион, выбранный из группы, включающей K+, Na+, Li+, NH4 + и их смесей, предпочтительно Li+, Na+ и их смесей;
и
X независимо представляет собой фторид или гидроксид, предпочтительно гидроксид;
индекс x равно числу в интервале от >0 до 1 и включая 1;
и Zn и Li больше 0;
и пластина синтетического цинкового гекторита характеризуется диаметром, равным =>2 микрон.
2. Пластина по п. 1, где соединение формулы (1) выбирается из группы, состоящей из:
3. Пластина по п. 1, где пластина характеризуется значением d50 в интервале от =>2 до около 60 микрон, наиболее предпочтительно от около 3 до около 50 микрон, в частности пластины могут характеризоваться значением d50, равным по меньшей мере 3 микрон.
4. Пластина по п. 1 или 2, где пластина пропускает по меньшей мере 92% света, предпочтительно 95% света и наиболее предпочтительно 98% света.
5. Способ получения пластины гекторита формулы (I) по любому одному из пп. 1-4, включающий стадии:
получение реакционной смеси, содержащей
I источник, выбранный из группы, состоящей из Na+, K+, NH4 + и Li+, предпочтительно Li+, Na+ и их смесей;
источник лития;
источник кремния;
источник цинка;
необязательно источник фторида и/или источник гидроксида, предпочтительно источник гидроксида и необязательно источник фторида, наиболее предпочтительно источник гидроксида;
модификатор формы, выбранный из группы, включающей
слабую органическую кислоту, слабую неорганическую кислоту или сахар,
и
необязательно затравочные кристаллы предварительно образованного гекторита,
гидротермическая обработка указанной реакционной смеси при основных условиях при температуре в интервале от около 125 до около 250°С, предпочтительно 150°С до около 225°С
и
давлении в интервале от около 50 до около 400 пси, предпочтительно от около 100 пси до около 220 пси;
с образованием пластины синтетического гекторита формулы (1); и
необязательно отделение образованной пластины.
6. Способ получения пластины гекторита формулы (1) по любому одному из пп. 1-4, включающий стадии:
получение реакционной смеси, содержащей I источник, выбранный из группы, состоящей из Na+, K+, NH4 + и Li+, предпочтительно Li+, Na+ их смесей;
источник лития;
источник кремния;
источник цинка;
необязательно источник фторида и/или источник гидроксида, предпочтительно источник гидроксида и необязательно источник фторида, наиболее предпочтительно источник гидроксида;
и
необязательно затравочные кристаллы предварительно образованного гекторита,
гидротермическая обработка указанной реакционной смеси при основных условиях при температуре в интервале от около 125 до около 250°С, предпочтительно 150°С до около 225°С
и
давлении в интервале от около 50 до около 400 пси, предпочтительно от около 100 пси до около 220 пси;
с образованием пластины синтетического гекторита формулы (1);
и
необязательно отделение образованной пластины, где источником кремния является коллоидный диоксид кремния.
7. Способ по п. 6, где реакционная смесь дополнительно содержит модификатор формы, где модификатор формы представляет собой слабую органическую кислоту, слабую неорганическую кислоту или сахар.
8. Способ по п. 5, где модификатор формы представляет собой слабую органическую кислоту или слабую неорганическую кислоту, их соль или гидрат,
и слабая органическая кислота, ее соль или гидрат, представляет собой соединение формулы (I)
если m+p равно 1:
А представляет собой разветвленный или неразветвленный, замещенный или незамещенный С1-С10 алкил, разветвленный или неразветвленный, замещенный или незамещенный С2-С10 алкенил, замещенный или незамещенный С7-С9 фенилалкил или замещенный или незамещенный С6-С10 арил,
где линейный или разветвленный незамещенный C1-С10 алкил, линейный или разветвленный С2-С10 алкенил может быть замещен С(O)ОН, С(O)O-Х+, NH2, галогеном, ОН, -С(O)Н или прерываться -О-, -NR2 - или -С(О)-,
С7-С9 фенилалкил или С6-С10 арил может быть замещен одним или более С(O)ОН, С(O)O-X(+)n, NH2, галогеном, ОН или -С(O)Н,
R представляет собой водород, или RO представляет собой О-X(+)n,
R2 представляет собой водород или линейный или разветвленный С1-С10-алкил, замещенный одним или более С(O)ОН, С(O)O-Х(+)n, галогеном, NH2, -С(О)- или ОН; n равно 1-3,
и
Х(+)n представляет собой органический или неорганический катион, например, аммоний, замещенный аммоний, такой как, например, метиламмоний, диметиламмоний, триметиламмоний, этаноламмоний, катионы металлов, например, катион щелочного металла, катион щелочноземельного металла или другие катионы металлов, например, Na+, Li+, K+, Cs+, Rb+, Fr+, Mg++, Sr++, Ba++, Be++, Ca++, P+++, B+++ или Al+++.
если m+p равно двум или более,
А представляет собой разветвленный или неразветвленный, замещенный или незамещенный C1-С10 алкилен, разветвленный или неразветвленный, замещенный или незамещенный С2-С10 алкилиден, замещенный или незамещенный С7-С9 алкилфенилен или С6-С10 арилен,
где линейный или разветвленный C1-С10 алкилен, линейный или разветвленный С2-С10 алкилиден может быть замещен С(O)ОН, С(O)O-X+, NH2, галогеном, ОН, -С(O)Н и/или прерываться -О-, -NR2- или -С(О)-,
и
С7-С9 алкилфенилен или С6-С12 арилен включает одно или более замещение NHR2, ОН, СООН, галогеном, СОО-Х(+)n или -С(O)Н,
где R, RO, R2 и Х(+)n имеют значения, как определено выше,
и
слабая неорганическая кислота выбирается из группы, состоящей из борной кислоты, фосфорной кислоты (Н3РО4), трифосфатов, их солей или гидратов.
9. Способ по п. 8, где
m+p равно двум или более,
А представляет собой разветвленный или неразветвленный, замещенный или незамещенный C1-C8 алкилен,
замещение разветвленного или неразветвленного C1-C8 алкилена включает одного или более замещение посредством ОН, СООН, СОО-Х(+)n как определено выше,
предпочтительно разветвленный или неразветвленный C1-C8 алкилен замещен ОН и СООН или СОО-Х(+)n,
и слабая неорганическая кислота представляет собой борную кислоту, ее соли или гидраты.
10. Способ по п. 7, где модификатор формы представляет собой слабую органическую кислоту и выбирается из группы, состоящей из следующих: муравьиная кислота, уксусная кислота, акриловая кислота, бензойная кислота, щавелевая кислота, фталевая кислота, изофталевая кислота, терефталевая кислота, малоновая кислота, метил малоновая кислота, сукциновая кислота, молочная кислота, аспаргиновая кислота, глутаровая кислота, адипиновая кислота, пимелиновая кислота, яблочная кислота, малеиновая кислота, винная кислота, тартроновая кислота, муциновая кислота, глюконовая кислота, лимонная кислота, изолимонная кислота, ацетиллимонная кислота, пробковая кислота, себациновая кислота, азелаиновая кислота, 1,2,3-пропантрикарбоновая кислота, 1,1,3,3-пропантетракарбоновая кислота, 1,1,2,2-этантетракарбоновая кислота, 1,2,3,4-бутантетракарбоновая кислота, 1,2,2,3-пропантетракарбоновая кислота, 1,3,3,5 пентантетракарбоновая кислота, этилендиаминтетрауксусная кислота, этиленгликольбис-тетрауксусная кислота, дигликолевая кислота, этилендиаминтетрапропионовая кислота, иминдиуксусная кислота, 1,2-пропилендиаминтетрауксусная кислота, N-метил, -этил, -пропил и -бутил иминдиуксусная кислота, 1,3-пропилендиаминтетрауксусная кислота, N-гидроксиэтилэтилендиаминтриуксусная кислота, триэтилентетраамингексауксусная кислота, диэтилентриаминпентауксусная кислота, аминокислоты, такие как глицин, аланин, валин, лейцин, тирозин, тореонин, серин, глутаминовая кислота, лизин и их соли или гидраты,
предпочтительно слабая органическая кислота выбирается из группы, состоящей из следующего: яблочная кислота, адипиновая кислота, винная кислота, щавелевая кислота, тартроновая кислота, лимонная кислота, изолимонная кислота, пимелиновая кислота, азелаиновая кислота, дигликолевая кислота, муциновая кислота, малоновая кислота, метилмалоновая кислота, глутаровая кислота, сукциновая кислота, аспаргиновая кислота, пробковая кислота, себациновая кислота, глутаминовая кислота, их соли и гидраты,
наиболее предпочтительно слабая органическая кислота выбирается из группы, состоящей из следующего: яблочная кислота, винная кислота, щавелевая кислота, лимонная кислота, изолимонная кислота, муциновая кислота, их соли и гидраты,
или
модификатор формы представляет собой слабую неорганическую кислоту, выбранную из группы, состоящей из борной кислоты, фосфорной кислоты (Н3РО4), пирофосфатоа, трифосфата и их солей или гидратов, предпочтительно модификатор формы представляет собой слабую неорганическую кислоту и представляет собой борную кислоту, ее соли или гидраты.
11. Способ по п. 5, где модификатор формы представляет собой сахар и выбирается из группы, включающей глюкозу, фруктозу, галактозу, сахарозу, мальтозу, сорбит, лактозу, маннит, инозитол, ксилитол, треит, эритрит, адонит (рибитол), арабит (лукситол), дульцит (галактитол), мальтит, изомальт, рибозу, ксилозу и маннозу.
12. Способ по любому одному из пп. 5-11, где количество модификатора формы, добавляемое в реакционную смесь, находится в интервале от около 0.5 до около 10% ммоль, предпочтительно от около 1 до около 7% ммоль, и наиболее предпочтительно от около 1.5 до около 5% ммоль на основе теоретически вычисленного продукта (гекторита).
13. Способ по любому одному из пп. 5-11, где источник цинка выбирается из группы, включающей элементарный цинк Zn0, ZnSO4, Zn(NO3)2, ZnCl2, Zn(С2Н3O2)2 (ацетат цинка), ZnCO3, Zn(CHO2)2 (формиат цинка), ZnBr2, оксид цинка, Zn0, ZnI2 и их гидраты.
14. Способ по любому одному из пп. 5-11, где необязательный источник фторида выбирается из группы, включающей HF, NH4F, NaF, K2SiF6, KF и MgF2, и необязательный источник гидроксида выбирается из группы, состоящей из гидроксида калия, гидроксида натрия, гидроксида лития, аммония гидроксида, трипропиламмония гидроксида и тетраметиламмония гидроксида, предпочтительно источник гидроксида присутствует.
15. Способ по любому одному из пп. 5-11, где источник лития выбирается из группы, включающей ацетат лития, бромид лития, иодид лития, хлорид лития, фторид лития, карбонат лития, цитрат лития, формиат лития, гексафторфосфат лития, гексафтортитанат лития, гидроксид лития, оксид лития и их гидраты.
16. Пигмент, содержащий пластину цинкового гекторита по любому одному из пп. 1-4.
17. Пигмент, содержащий пластину гекторита по любому одному из пп. 1-4,
(a) слой диэлектрического вещества, в частности оксида металла, имеющего высокий показатель преломления; и/или
(b) слой металла, в частности тонкий полупрозрачный слой металла.
18. Пигмент по п. 17, где пигмент дополнительно содержит в дополнение к слою (а), имеющему высокий показатель преломления, и/или слою металла (b), оксидный слой (с) с низким показателем преломления и слой (d) с высоким показателем преломления, где различие между высоким и низким показателями преломления составляет по меньшей мере 0,1.
19. Пигмент по п. 17 или 18, где оксид металла слоя (а) с высоким показателем преломления представляет собой ТiO2, ZrO2, Fe2О3, Fe3O4, Сr2О3, ZnO, смесь этих оксидов, титанат железа, гидрат оксида железа, субоксид титана или смесь и/или смешанную фазу этих соединений.
20. Краска, чернила для струйной печати, покрытия, печатная краска, пластмасса, косметическое средство, глазурь для керамики и стекла, содержащие пигменты по любому одному из пп. 16-19 или любую из пластин по любому одному из пп. 1-4.