RU2006136225A - Раствор для покрытия поверхностей - Google Patents
Раствор для покрытия поверхностей Download PDFInfo
- Publication number
- RU2006136225A RU2006136225A RU2006136225/04A RU2006136225A RU2006136225A RU 2006136225 A RU2006136225 A RU 2006136225A RU 2006136225/04 A RU2006136225/04 A RU 2006136225/04A RU 2006136225 A RU2006136225 A RU 2006136225A RU 2006136225 A RU2006136225 A RU 2006136225A
- Authority
- RU
- Russia
- Prior art keywords
- solution
- coating surfaces
- coating
- boehmite particles
- particles
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/02—Emulsion paints including aerosols
- C09D5/024—Emulsion paints including aerosols characterised by the additives
- C09D5/028—Pigments; Filters
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/02—Emulsion paints including aerosols
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/43—Thickening agents
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/60—Additives non-macromolecular
- C09D7/61—Additives non-macromolecular inorganic
- C09D7/62—Additives non-macromolecular inorganic modified by treatment with other compounds
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D7/00—Features of coating compositions, not provided for in group C09D5/00; Processes for incorporating ingredients in coating compositions
- C09D7/40—Additives
- C09D7/70—Additives characterised by shape, e.g. fibres, flakes or microspheres
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Wood Science & Technology (AREA)
- Dispersion Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Paints Or Removers (AREA)
- Compounds Of Alkaline-Earth Elements, Aluminum Or Rare-Earth Metals (AREA)
- Materials For Medical Uses (AREA)
- Pretreatment Of Seeds And Plants (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
Claims (52)
1. Раствор для покрытия поверхностей, который содержит
основу раствора и частицы бемита, имеющиеся в основе раствора и представляющие собой анизотропно фасонированные частицы, имеющие коэффициент формы по меньшей мере 3:1.
2. Раствор для покрытия поверхностей по п.1, в котором основа раствора представляет собой раствор на водной основе.
3. Раствор для покрытия поверхностей по п.2, в котором раствор на водной основе дополнительно содержит полимеры в эмульсии, а раствор для покрытия поверхности представляет собой латексную краску.
4. Раствор для покрытия поверхностей по п.3, в котором латексная краска представляет собой акриловую краску.
5. Раствор для покрытия поверхностей по п.1, который имеет растекание и распределение по поверхности с образованием ровной пленки, составляющее по меньшей мере около 6 мил.
6. Раствор для покрытия поверхностей по п.1, который имеет устойчивость против образования потеков больше чем 7 мил.
7. Раствор для покрытия поверхностей по п.6, который имеет устойчивость против образования потеков от 7 до 12 мил.
8. Раствор для покрытия поверхностей по п.2, который не содержит соединяющего загустителя.
9. Раствор для покрытия поверхностей по п.1, содержащий от 0,1 до 20% частиц бемита от веса раствора.
10. Раствор для покрытия поверхностей по п.9, содержащий от 0,5 до 10% частиц бемита от веса раствора.
11. Раствор для покрытия поверхностей по п.10, содержащий от 0,5 до 2% частиц бемита от веса раствора.
12. Раствор для покрытия поверхностей по п.1, который имеет время высыхания до затвердевания для касания меньше чем 30 мин.
13. Раствор для покрытия поверхностей по п.1, в котором частицы бемита имеют наибольший размер, составляющий по меньшей мере около 50 нм.
14. Раствор для покрытия поверхностей по п.13, в котором частицы бемита имеют наибольший размер в диапазоне от 100 до 1000 нм.
15. Раствор для покрытия поверхностей по п.1, в котором коэффициент формы частиц бемита составляет не меньше чем 6:1.
16. Раствор для покрытия поверхностей по п.1, в котором частицы бемита имеют вторичный коэффициент формы, который не превышает 3:1.
17. Раствор для покрытия поверхностей по п.1, в котором частицы бемита имеют площадь поверхности, составляющую по меньшей мере 10 м2/г.
18. Раствор для покрытия поверхностей по п.17, в котором частицы бемита имеют площадь поверхности, составляющую по меньшей мере 75 м2/г.
19. Раствор для покрытия поверхностей по п.18, в котором частицы бемита имеют площадь поверхности, составляющую от 100 до 350 м2/г.
20. Раствор для покрытия поверхностей по п.1, который восстанавливает 80% вязкости низкого сдвига в течение времени меньше чем 1,5 с.
21. Раствор для покрытия поверхностей по п.1, у которого рН превышает 7,0.
22. Раствор для покрытия поверхностей, который содержит частицы бемита, которые представляют собой анизотропно фасонированные частицы, имеющие коэффициент формы, составляющий по меньшей мере около 3:1, и наибольший размер, составляющий по меньшей мере 50 нм.
23. Раствор для покрытия поверхностей по п.22, который имеет растекание и распределение по поверхности с образованием ровной пленки свыше 6 мил.
24. Раствор для покрытия поверхностей по п.22, который имеет устойчивость против образования потеков, составляющую по меньшей мере 7 мил.
25. Раствор для покрытия поверхностей по п.22, который не содержит соединяющего загустителя.
26. Раствор для покрытия поверхностей по п.22, в котором частицы бемита составляют от 0,5 до 2% от веса раствора.
27. Раствор для покрытия поверхностей по п.22, который имеет время высыхания до затвердевания для касания меньше чем 30 мин.
28. Раствор для покрытия поверхностей по п.22, в котором частицы бемита имеют наибольший размер от 100 до 1000 нм.
29. Раствор для покрытия поверхностей по п.22, в котором частицы бемита имеют коэффициент формы, составляющий по меньшей мере 6:1.
30. Раствор для покрытия поверхностей по п.22, в котором частицы бемита имеют вторичный коэффициент формы, не превышающий 3:1.
31. Раствор для покрытия поверхностей по п.22, в котором частицы бемита имеют площадь поверхности, составляющую по меньшей мере 10 м2/г.
32. Раствор для покрытия поверхностей по п.31, в котором частицы бемита имеют площадь поверхности, составляющую по меньшей мере 75 м2/г.
33. Раствор для покрытия поверхностей по п.32, в котором частицы бемита имеют площадь поверхности, составляющую ориентировочно от 100 до 350 м2/г.
34. Раствор для покрытия поверхностей по п.22, который восстанавливает 80% вязкости низкого сдвига в течение времени меньше чем 15 с.
35. Способ получения раствора для покрытия поверхностей, который включает в себя следующие операции: активирование частиц бемита для образования активного раствора, причем частицы бемита представляют собой главным образом анизатропно фасонированные частицы; образование растирочного раствора с использованием активного раствора и
образование покровного раствора с использованием растирочного раствора.
36. Способ по п.35, в котором активирование частиц бемита происходит в активном растворе, имеющем реологию уменьшения сдвига.
37. Способ по п.35, в котором активирование частиц бемита предусматривает добавление основы.
38. Способ по п.37, в котором основа представляет собой гидроксид аммония.
39. Способ по п.35, в котором активирование частиц бемита предусматривает увеличение рН активного раствора до величины, составляющей по меньшей мере 7,0,
40. Способ по п.35, в котором активирование частиц бемита предусматривает добавление частиц, имеющих заряд, противоположный заряду частиц бемита.
41. Способ по п.35, в котором образование растирочного раствора предусматривает добавление пигмента.
42. Способ по п.35, в котором активирование частиц бемита предусматривает добавление соли.
43. Способ по п.35, в котором анизотропно фасонированные частицы бемита имеют коэффициент формы, составляющий по меньшей мере около 3:1.
44. Способ по п.35, в котором покровный раствор имеет растекание и распределение по поверхности с образованием ровной пленки, превышающее 6 мил.
45. Способ по п.35, в котором покровный раствор имеет устойчивость против образования потеков, составляющую по меньшей мере 7 мил.
46. Способ по п.35, в котором покровный раствор не содержит соединяющего загустителя.
47. Способ по п.35, в котором частицы бемита составляют от 0,5 до 2% от веса покровного раствора.
48. Способ по п.35, в котором покровный раствор имеет время высыхания до затвердевания для касания меньше чем 30 мин.
49. Способ по п.35, в котором частицы бемита имеют наибольший размер, составляющий по меньшей мере около 50 нм.
50. Способ по п.35, в котором частицы бемита имеют площадь поверхности, составляющую по меньшей мере 10 м2/г.
51. Способ по п.35, в котором покровный раствор восстанавливает 80% вязкости низкого сдвига в течение времени меньше чем 15 с.
52. Раствор для покрытия поверхностей, полученный способом по п.35.