RU1820926C - Woven binding tape for rubber products - Google Patents

Abstract

Использование: текстильно-галантерейна  промышленность дл  изол ционного бинтовочного материала дл  опрессовке рукавных резиновых изделий высокого давлени . Сущность изобретени : лента содержит термостойкие капроновые основные и уточные нити, переплетенные между собой. Отношение величины поверхностного заполнени  ленты к количеству перекрытий основных и уточных нитей находитс  в пределах 1 : (6 - 8). ЈUsage: textile and haberdashery industry for insulating bandage material for crimping high-pressure hose rubber products. SUMMARY OF THE INVENTION: The tape comprises heat-resistant kapron warp and weft yarns intertwined. The ratio of the surface filling of the tape to the number of overlaps of the warp and weft yarns is within the range of 1: (6-8). Ј

Description

Изобретение относитс  к текстильной промышленности, а именно к текстильно-галантерейным издели м технического назначени , и может быть использовано в качестве.изол ционного материала при обмотке изделий, в особенности при ohрее- совке резинотехнических изделий.The invention relates to the textile industry, in particular to textile haberdashery products for technical use, and can be used as insulation material for wrapping products, in particular when wiring rubber products.

Целью изобретени   вл етс  повышение эксплуатационных характеристик.The aim of the invention is to improve performance.

Указанна  цель достигаетс  тем, что ткана  винтовочна  лента дл  резинотехнических изделий содержит переплетенные между собой синтетические основные и уточные нити, представл ющие собой термостойкие капроновые нити, при этом отношение величины поверхностного заполнени  тканой ленты к количеству перекрытий основных и уточных нитей в 1 см ленты находитс  в пределах 1 : (6 - 8)This goal is achieved by the fact that the fabric of a rifle tape for rubber products contains interwoven synthetic warp and weft threads, which are heat-resistant nylon threads, while the ratio of the surface filling of the woven tape to the number of overlapping warp and weft threads in 1 cm of tape is limits 1: (6 - 8)

Изобретение по сн етс  примером тканевой ленты:The invention is illustrated by an example of a fabric tape:

Ширина ленты, мм70 ± 2Width of a tape, mm70 ± 2

Материал, термостойкийHeat resistant material

капрон100%kapron100%

Масса, 1 п.м,8.68 ± 0,6Weight, 1 l.m, 8.68 ± 0.6

Толщина ленты, ммДо 0,3Tape thickness, mm Up to 0.3

Число нитей, 1 смThe number of threads, 1 cm

основа35 ± 1,5 уток 18x2 ± 1warp 35 ± 1,5 ducks 18x2 ± 1

Линейна  плотностьLinear density

нити, тексthreads, tex

основа23.5 (42,55) уток 11 (90,9)warp 23.5 (42.55) weft 11 (90.9)

В ленте при ее эксплуатации основные и уточные нити испытывают различные на- гружени , от гощенные процессом вулканизации и агрессивностью резиновой смеси.During its operation, the main and weft threads in the tape undergo various stresses, enriched by the vulcanization process and the aggressiveness of the rubber compound.

0000

к о о к оk o o o o o

оэoe

Нити основы испытывают наибольшее ленты только основные нити, определ ю- нагружение в продольном направлении, по- щие получение основозастилочной, двух- этому их плотность и толщина значительно сторонней и двухлицевой ленты, выше уточних нитей. Уточные нити, проло-Возможен также просчет и создание женные в зёв попарно, создают эластичной, 5 ленты исход  из задаваемой плотности по прилегающей к рукаву застил, испытыва  основе и утку и линейной плотности нитей при этом см тие и изгиб, от гощенный тре- основы и утка в теке, но с об зательным нием. Поэтому соотношение плотности выходом на рекомендуемые соотношени , уточных нитей к плотности основных нитей Следовательно если величина поверх- находитс  в пределах 1 : (1,8 - 2,1), а соот- Ю. ностного заполнени  будет ниже 80%, то ношение линейной плотности уточных ни- лента может иметь рыхлую структуру со тей в текс к линейной плотности основных слабой св зностью и недостаточной каркас- нитей втекс находитс  в пределах 1 :{1,9- ностью, что будет способствовать сниже- 2,2}. Элементы перекрыти  нитей основы и нию эксплуатационных характеристик, что утка подвержены еще интенсивным истира- 15 недопустимо. Если поверхностное заполне- ющим воздействи м как о поверхность ру- ние будет выше 90%, то могут встретитс  кава, так и по поверхности друг друга в трудности при выработке ленты на лентот- процессе бинтовки и разбинтовки, а также кацком станке и к неоправданному увеличе- воздействи м, способствующим раздвижке нию расхода сырь / нитей, поэтому создание максимального ко- 20 Если количество перекрытий основных личества опорных точек - мест перекры- и уточных нитей в ленте будет Менее 420 тий  вл етс  одним из главных условий (соотношение 1 : 6). то уменьшитс  количе- проектировани  новой тканой ленты и уста- ство полей трени , за счет чего увеличива- новленное соотношение величины поверх- етс  удельна  нагрузка на каждое ностного заполнени  ткани к количеству 25 перекрытие основных и уточных нитей, что перекрытий основных и уточных нитей в может привести к повреждению отдельно- пределах 1 :{6- 8) применимо ко всем ши- сти волокон и потере прочности ленты, ее ринам выпускаемых тканых лент и диамет- св зности, а значит, к уменьшению ее хоров обрабатываемых рукавов этого димости, что допустить нельз . Если коли- назначени , при этом поверхностное зарол- 30 чество перекрытий будет больше 700 нение тканой ленты должно находитьс  в (соотношение 1:8), то увеличитс  количест- пределах80-90%. во полей трени . Эту ленту трудно сработать Пор док конструировани  тканой лен- на ткацком станке. Возрастет стоимость ты, упом нутой в примере. . выработки ленты, увеличитс  расход сырь . Проектировщик ткани, задавшись при- 35 Лента, будет неоправданно жесткой, что родой волокна, име  ввиду применени  ни- может встретить трудности при ее заправке тей основы и утка из 100% термостойкого в бинтовочный станок и выполнение бинтов- . капрона, зна  его свойства и прогнозиру  ки и разбинтовки издели , что допустить поведение нитей в услови х выработки лен- нельз . The warp threads experience the greatest tapes, only the warp threads, determining the load in the longitudinal direction, helping to obtain the warp filament, therefore their density and thickness are significantly sided and double-faced tape, higher than the weft threads. Weft yarns, spliced. It is also possible to miscalculate and create wives in the throat in pairs, create an elastic, 5 tape based on a given density on the adjacent to the sleeve sheathed, testing the warp and weft and the linear density of the yarns with the wrinkling and bending of the weathered base and a duck in a tech, but with a mandatory one. Therefore, the ratio of density to the recommended ratios of weft yarns to the density of the main yarns. Therefore, if the value of the surface is within 1: (1.8 - 2.1), and the corresponding filling is below 80%, then wearing linear density the weft nipple can have a loose structure with tex to linear linear density of the main weak connectivity and insufficient Vtex skeletons is within 1: {1.9-, which will contribute to a decrease of 2.2}. Elements of overlapping warp and performance characteristics that the weft is subject to still intense abrasion - 15 is unacceptable. If the surface filling effect is higher than 90%, the cava may be encountered, as well as on each other’s surface, it is difficult to develop the tape on the tape process of bandaging and disassembling, as well as on the skating machine and to an unjustified increase - influences contributing to the spread of the feed / thread consumption, therefore, creating the maximum amount of 20 If the number of overlap of the main number of reference points - places of overlapping and weft threads in the tape will be Less than 420 ct is one of the main conditions (ratio 1: 6) . this will reduce the amount of designing of a new woven tape and the tolerance of friction fields, due to which the increased ratio of the magnitude of the specific load on each tissue filling to the number of 25 overlaps of the main and weft threads, which can overlap the main and weft threads in lead to damage separately within 1: {6-8) applies to all fiber widths and loss of strength of the tape, its rins of woven tapes and diameter, and, therefore, to a decrease in its choirs of processed sleeves of this range, which is an allowance the thread cannot be. If the number of appointments, while the surface number of overlaps is greater than 700, the woven tape should be in (1: 8 ratio), then the number will increase within 80-90%. in the fields fr. It is difficult to work this tape. The order of constructing a woven linen on a loom. The value of you mentioned in the example will increase. . tape production, raw material consumption will increase. The fabric designer, having set himself on the 35 Tape, will be unjustifiably tough that the kind of fiber, having in mind the use of it, will encounter difficulties when refueling the warp and weft from 100% heat-resistant into a bandage machine and making bandages -. kapron, knowing its properties and predicting and disassembling the product, which allows the behavior of threads under conditions of production of lennels.

Claims (1)

ты на лентоткацком станке, их контакт с 40 Изобретение значительно улучшает экс- изделием при бинтовке и разбинтовке, а плуатационные характеристики тканой лен- также режим работы при вулканизации ру- ты. Ее ходимость по отношению к кавов высокого давлени  задаетс  соотно- прототипу возросла более чем в 3 раза, при шением величины поверхностного этом материалоемкость - масса одного nor. заполнени  тканой ленты к количеству в ней 45 м ленты снижена в 1,33- 1,66 раза, перекрытий основных и уточных нитей. ЭтоФормула изобретени  соотношение равно 1:7,4. Исход  из напр - Ткана  бинтовочна  лента дл  резино- женности технологического процесса ткаче- технических изделий, содержаща  перепле- ства и режимов эксплуатации ленты тенные между собой синтетические поверхностное заполнение ленты установ- 50 основные и -уточные нити, о т л и ч а ю - лено 86%, а количество перекрытий - 627. щ а  с   тем, что, с целью улучшени  эксплу- Установив плотность основных нитей на см атационных характеристик, основные и ширины ленты, равную 35 нитей/см, и, по- уточные нити представл ют собой термо- делив 627:35 18 нитей/см, получают плот- стойкие капроновые нити, при этом отноше- ность уточных нитей на см, что находитс  в 55 ние величины поверхностного заполнени  пределах соотношени  плотности уточных тканой ленты к количеству перекрытий ос- нитей к плотности основных нитей и равно новных и уточных нитей в 1 см ленты нахо- 1 : 1,94. Здесь выведены на поверхность дитс  в пределах 1 :(б-8).you are on a tape loom, their contact with 40. The invention significantly improves the product during bandaging and unbinding, and the performance characteristics of woven linen are also the mode of operation during vulcanization of rut. Its mileage with respect to high-pressure cava is set according to the prototype increased by more than 3 times, while the surface consumption is increased, the material consumption is the mass of one nor. filling the woven tape to the amount of 45 m of tape in it is reduced by 1.33-1.66 times, overlap of the warp and weft threads. This claims is a ratio of 1: 7.4. Proceeding from, for example, Tkana, a bandage tape for rubberizing the technological process of weaving and technical products, containing interweaving and operating modes of the tape, woven synthetic fibers, surface filling of the tape, 50 main and daily filaments, 86%, and the number of overlappings - 627. The reason is that, in order to improve operation, Having established the density of the main threads on the fabrication characteristics, the main and tape widths equal to 35 threads / cm, and by thermally dividing 627: 35 18 threads / cm, semi dense nylon yarns are measured, the ratio of weft yarns per cm, which is 55 times the surface filling, within the ratio of the density of weft woven tapes to the number of overlapping stitches to the density of warp yarns and equal and weft yarns of 1 cm the tape is- 1: 1.94. Here dits are brought to the surface within 1: (b-8).