RO119784B1 - Recipient for storing a liquid meant for alimentary consumption and process for making the same - Google Patents

Recipient for storing a liquid meant for alimentary consumption and process for making the same Download PDF

Info

Publication number
RO119784B1
RO119784B1 ROA200300568A RO200300568A RO119784B1 RO 119784 B1 RO119784 B1 RO 119784B1 RO A200300568 A ROA200300568 A RO A200300568A RO 200300568 A RO200300568 A RO 200300568A RO 119784 B1 RO119784 B1 RO 119784B1
Authority
RO
Romania
Prior art keywords
layer
weight
minutes
polyethylene
powder
Prior art date
Application number
ROA200300568A
Other languages
Romanian (ro)
Inventor
Ionel Scîrleţ
Original Assignee
Valrom Industrie S.R.L.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Valrom Industrie S.R.L. filed Critical Valrom Industrie S.R.L.
Priority to ROA200300568A priority Critical patent/RO119784B1/en
Priority to PCT/RO2004/000011 priority patent/WO2005000026A1/en
Priority to EP04775194A priority patent/EP1643840A1/en
Publication of RO119784B1 publication Critical patent/RO119784B1/en

Abstract

The invention relates to a recipient for storing a liquid meant for alimentary consumption, which comprises an active layer of polyethylene, which comprises silver ions, said layer being protected by an outer layer, made up only of polyethylene, which consists in that the active layer has a thickness of 0.05...1 mm and has a content of 0.005...0.3% by weight of a powder containing Ag+ ions with biocide activity, deriving from AgCl, deposited on an inert TiO2 support, and the outer layer, when it exists, has a thickness of 1...2 mm and is in intimate contact with the active layer. According to the invention, the process for preparing the recipient consists in mixing 1.5...9.0 parts by weight of low density polyethylene with 0.3% by weight biocide powder which is previously homogenized for 20 minutes, the mixture is introduced into a die in a rotary movement, which is maintained at temperature for 25 min, for depositing the polyethylene layer on the walls, is cooled slowly under ventilation, the rotary movement is stopped and the resulting mono-layer recipient is extracted. According to the invention, the process for making the bi-layered recipient consists in that 7.5 parts by weight of low density polyethylene needed for forming an outer layer, are introduced into a heated die which is a rotating and maintained in the oven for 10 min, afterwards in the die there is introduced a mixture of low density polyethylene, with biocide powder, it is maintained for further 5 min, at temperature, for forming the inner layer, it is cooled slowly under ventilation, then the rotary movement is stopped and the resulting bi-layered recipient is extracted.

Description

Invenția se referă la un recipient pentru stocarea unui lichid destinat consumului alimentar, monostrat sau bistrat, și la un procedeu de realizare a acestuia prin formare rotațională.The invention relates to a container for storing a liquid intended for food consumption, monolayer or bistro, and to a process for making it by rotational formation.

Este cunoscută realizarea recipientelor din materiale termoplastice, în general, din polietilenă și copolimeri de etilenă, care se poate face prin extrudare-suflare și formare rotațională. Față de procedeul prin extrudare-suflare, formarea rotațională prezintă câteva avantaje majore: permite formarea de articole de mari dimensiuni, la un preț competitiv; matrițele au un cost relativ scăzut; produsele nu prezintă eforturi mecanice reziduale.It is known the manufacture of containers made of thermoplastic materials, generally of polyethylene and ethylene copolymers, which can be done by extrusion-blowing and rotational formation. Compared to the extrusion-blowing process, the rotational formation presents some major advantages: it allows the formation of large items, at a competitive price; the molds have a relatively low cost; the products have no residual mechanical stress.

în formarea rotațională, materia primă sub formă de pulbere este introdusă într-o matriță închisă, care se rotește simultan după două axe. Matrița este introdusă într-un cuptor și încălzită astfel încât materialul se topește și aderă la pereții matriței. După topirea materialului, matrița este scoasă din cuptor, răcită până când piesa revine în stare solidă și apoi este extrasă din matriță. Atât etapa de formare în cuptor, cât și cea de răcire se execută cu matrița aflată în mișcare de rotație după cele două axe, pentru a fixa materialul de pereții matriței.In rotational formation, the raw material in powder form is introduced into a closed mold, which rotates simultaneously along two axes. The mold is inserted into an oven and heated so that the material melts and adheres to the walls of the mold. After the material has melted, the mold is removed from the oven, cooled until the part returns to solid state and is then extracted from the mold. Both the formation stage in the oven and the cooling stage are executed with the mold in rotation motion after the two axes, to fix the material to the walls of the mold.

Principalul dezavantaj al recipientelor din materiale termoplastice este că apa sau alte lichide nu pot fi stocate fără circulație pe o durată mai mare de 20 zile, datorită dezvoltării de bacterii, alge și ciuperci. Soluțiile cunoscute până acum folosesc în general compuși organici cu conținut de clor, care însă au viteză mare de migrare, datorită moleculei mici, sunt sensibili la temperatură și prezintă risc crescut pentru mediu.The main disadvantage of the containers made of thermoplastic materials is that the water or other liquids cannot be stored without circulation for more than 20 days, due to the development of bacteria, algae and fungi. The solutions known so far generally use chlorine-containing organic compounds, which, however, have a high migration rate due to the small molecule, are temperature sensitive and present an increased risk to the environment.

Problema tehnică, pe care o rezolvă invenția, este realizarea unui recipient din materiale termoplastice, monostrat sau bistrat, folosind un agent bactericid (biocid) anorganic, compus dintr-un amestec de dioxid de titan ca material inert și clorură de argint ca agent activ.The technical problem, which is solved by the invention, is the manufacture of a container of thermoplastic materials, monolayer or bistrate, using an inorganic bactericidal (biocide) agent, composed of a mixture of titanium dioxide as an inert material and silver chloride as the active agent.

Recipientul pentru stocarea unui lichid destinat consumului alimentar, conform invenției, care este constituit dintr-un strat activ din polietilenă care are în compoziție ioni de argint, care strat poate fi protejat de către un strat exterior realizat numai din polietilenă, constă în aceea că stratul activ are o grosime de 0,05...1 mm și are un conținut de 0,005...0,3% în greutate pulbere care conține ioni de Ag+ cu activitate biocidă proveniți din AgCI depusă pe un suport inert din TiO2, iar stratul exterior, atunci când acesta există, are o grosime de 1...2 mm și este în contact intim cu stratul activ.The container for storing a liquid for food consumption according to the invention, which is made up of an active layer of polyethylene having silver ions, which layer can be protected by an outer layer made only of polyethylene, consists in that the layer active has a thickness of 0.05 ... 1 mm and a content of 0.005 ... 0.3% by weight of powder containing Ag + ions with biocidal activity coming from AgCI deposited on an inert TiO 2 support , and the outer layer, when it exists, has a thickness of 1 ... 2 mm and is in close contact with the active layer.

Pulberea cu activitate biocidă este constituită dintr-un suport inert din dioxid de titan și din clorură de argint în raport în greutate dioxid de titan:clorură de argint de 8:2.The powder with biocidal activity consists of an inert support of titanium dioxide and silver chloride in weight ratio titanium dioxide: silver chloride of 8: 2.

Procedeul de realizare a unui recipient pentru stocarea unui lichid destinat consumului alimentar, conform invenției, constă în aceea că se amestecă 1,5...9,0 părți în greutate polietilenă de joasă densitate cu 0,3% în greutate pulbere biocidă omogenizată în prealabil timp de 20 min, se introduce amestecul într-o matriță care se menține la o temperatură de 230°C, timp de 25 min, matriță aflată în mișcare de rotație în jurul celor două axe de rotație, primară și secundară, cu o viteză de rotație de 8,0 rot/min și respectiv de 2,1 rot/min, se menține matrița în cuptor timp de 5 min, pentru a se depune stratul de polietilenă pe pereți, se răcește lent timp de 40 min sub ventilație, se oprește mișcarea de rotație și se extrage recipientul monostrat rezultat.The process of making a container for storing a liquid for food consumption according to the invention consists in mixing 1.5 to 9.0 parts by weight of low density polyethylene with 0.3% by weight of biocidal powder homogenized in prior to 20 minutes, the mixture is introduced into a mold that is maintained at a temperature of 230 ° C, for 25 minutes, the mold is rotating around the two axes of rotation, primary and secondary, with a speed of rotation of 8.0 rot / min and 2.1 rot / min respectively, keep the mold in the oven for 5 minutes, to deposit the polyethylene layer on the walls, cool slowly for 40 minutes under ventilation, stops the rotation movement and extracts the resulting monolayer container.

Procedeul de realizare a unui recipient pentru stocarea unui lichid destinat consumului alimentar, conform invenției, bistrat, constă în aceea că 7,5 părți în greutate polietilenă de joasă densitate necesară formării unui strat exterior se introduc într-o matriță încălzită la o temperatură de 230’C, matriță aflată în mișcare de rotație, se menține în cuptor timp de 10 min, după care se introduce în matriță un amestec de 1,5 părți în greutate polietilenă de joasă densitate cu 0,1% în greutate pulbere biocidă omogenizată în prealabil timp de 20 min, se menține încă 5 min la temperatura de 230’C, pentru formarea stratului interior, se răcește lent sub ventilație timp de 20 min, după care se oprește mișcarea de rotație și se extrage recipientul bistrat rezultat.The process of making a container for storing a liquid for food consumption according to the invention, bistrate, consists in the fact that 7.5 parts by weight of low density polyethylene required to form an outer layer are introduced into a mold heated to a temperature of 230 'C, a rotating mold, is kept in the oven for 10 minutes, after which a mixture of 1.5 parts by weight of low density polyethylene with 0.1% by weight homogenized biocidal powder is introduced into the mold. for 20 minutes, keep for another 5 minutes at 230'C, for the formation of the inner layer, cool slowly under ventilation for 20 minutes, after which the rotation movement is stopped and the resulting bistable container is extracted.

RO 119784 Β1RO 119784 Β1

Față de utilizarea biocizilor organici, folosirea acestui recipient cu amestec biocid în 1 stratul de contact activ prezintă următoarele avantaje:Compared to the use of organic biocides, the use of this biocidal mixture container in 1 active contact layer has the following advantages:

- poate fi folosit cu oricare din materiile prime utilizate în formarea rotațională, polietilenă3 liniară, polietilenă de joasă densitate, polietilenă de înaltă densitate, polipropilenă etc;- can be used with any of the raw materials used in rotational formation, linear polyethylene3, low density polyethylene, high density polyethylene, polypropylene etc;

- activitate ridicată asupra unui spectru larg de microorganisme, cum ar fi, bacterii, alge,5 ciuperci;- high activity on a wide spectrum of microorganisms, such as bacteria, algae, 5 fungi;

- nivel de toxicitate foarte scăzut;7- very low level of toxicity; 7

- nu ridică probleme de sănătate fiind non-iritant și non-alergic;- it does not raise health problems being non-irritating and non-allergic;

- impact minim asupra mediului;9- minimal impact on the environment; 9

- stabil termic până la 450’C și într-un domeniu larg de pH;- thermally stable up to 450'C and in a wide pH range;

- concentrația de echilibru este de 3 părți pe milion în apă și ionii de argint sunt eliberați 11 pe măsură ce se consumă, asigurând astfel o durată mare de activitate;- the equilibrium concentration is 3 parts per million in water and the silver ions are released 11 as they are consumed, thus ensuring a long duration of activity;

- impact minim asupra caracteristicilor materialului de bază;13- minimal impact on the characteristics of the basic material; 13

- performanță excelentă în strat subțire.- excellent performance in thin layer.

Studii de laborator prin metoda stratului subțire asupra unor culturi de bacterii (Staphylo-15 coccus aureus și Escherichia Coli) arată o reducere de 99,6% pentru Staphylococcus aureus și 95,2% pentru Escherichia Coli, la 24 h de la aplicare.17Laboratory studies using the thin-layer method on bacterial cultures (Staphylo-15 coccus aureus and Escherichia Coli) show a 99.6% reduction for Staphylococcus aureus and 95.2% for Escherichia Coli, 24 hours after application.17

Amestecul de dioxid de titan ca material inert și clorură de argint ca agent activ, în proporție de 8:2 raport în greutate, trebuie să fie foarte bine omogenizat și măcinat foarte fin, rezi- 19 duul pe sita de 45 pm fiind de maximum 0,02%.The mixture of titanium dioxide as an inert material and silver chloride as the active agent, in a ratio of 8: 2 by weight ratio, must be very well homogenized and ground very finely, the residue on the 45 pm sieve being a maximum of 0 , 02%.

Realizarea recipientelor folosind acest biocid se face prin introducerea lui în materia 21 primă sub formă de pulbere, într-o concentrație variind între 0,005% masic pentru un strat cu grosimea de 50 pm și 0,3% pentru un strat cu grosimea de 3 mm, omogenizarea foarte bună 23 și realizarea propriu-zisă a produsului. Datorită faptului că activitatea biocidului se manifestă la interfața dintre perete și lichid, este mai economică și mai eficientă folosirea lui în produse 25 cu pereți în strat dublu, biocidul fiind introdus doar în stratul interior care poate avea o grosime de circa 0,5...1 mm. 27Containers using this biocide are made by introducing it into the raw material as a powder, in a concentration ranging from 0.005% by mass for a layer with a thickness of 50 µm and 0.3% for a layer with a thickness of 3 mm, very good homogenization 23 and the actual production of the product. Due to the fact that the activity of the biocide is manifested at the interface between the wall and the liquid, it is more economical and efficient to use it in products 25 with double layer walls, the biocide being introduced only in the inner layer which can have a thickness of about 0.5. .1 mm. 27

Se dau, în continuare, două exemple de realizare din polietilenă liniară de joasă densitate, prin formare rotațională, a unui recipient conform invenției, pentru apă potabilă, cu o capa- 29 citate de 5001, de formă cilindrică, cu o grosime a peretelui de circa 3 mm. Primul exemplu este cu perete monostrat și al doilea cu perete în strat dublu. 31Following are two examples of low density linear polyethylene, by rotational formation, of a container according to the invention, for drinking water, with a capacity of 5001, of cylindrical shape, with a wall thickness of about 3 mm. The first example is with monolayer wall and the second with double layer wall. 31

Exemplul 1. Se cântăresc 9 kg polietilenă liniară de joasă densitate (LLDPE) și 27 g biocid (amestec dioxid de titan:clorură de argint în proporție de 8:2 masic) și se omogenizează 33 foarte bine într-un amestecător de pulberi uscate.Example 1. Weigh 9 kg of low density linear polyethylene (LLDPE) and 27 g of biocide (titanium dioxide mixture: silver chloride at 8: 2 mass) and mix 33 very well in a dry powder mixer.

Se introduce amestecul în matriță și se închide matrița.35Insert the mixture into the mold and close the mold.35

Se setează temperatura cuptorului la 230’C, se lasă să termostateze și se introduce matrița în cuptor. Matrița este continuu în mișcare de rotație, turația pe axa primară fiind de 837 rot/min, iar pe axa secundară de 2,1 rot/min.Set the oven temperature to 230'C, allow to thermostat and insert the mold into the oven. The mold is continuously rotating, the speed on the primary axis being 837 rpm and on the secondary axis 2.1 rpm.

După 10 min, circa 3 min pentru fiecare 1 mm grosime de perete, când tot materialul 39 este topit, se scoate matrița din cuptor.After 10 minutes, about 3 minutes for every 1 mm wall thickness, when all the material 39 is melted, remove the mold from the oven.

După scoaterea din cuptor, matrița se răcește lent, circa 20 min, folosind un ventilator 41 de capacitate corespunzătoare. Pe tot parcursul fazei de răcire, matrița este în mișcare de rotație.43After removing from the oven, the mold is cooled slowly, about 20 minutes, using a fan of 41 capacity. Throughout the cooling phase, the mold is rotating.43

După răcire, când materialul a revenit în stare solidă, se oprește mișcarea de rotație, se deschide matrița și se scoate produsul.45After cooling, when the material has returned to its solid state, the rotation movement is stopped, the mold is opened and the product is removed.

Se curăță produsul de resturile aflate la planurile de îmbinare ale matriței.The product is cleaned from the debris found on the molding plans of the mold.

Recipientul este gata pentru a fi folosit în exploatare.47The container is ready for use in operation.47

RO 119784 Β1RO 119784 Β1

Exemplul 2. Se cântăresc două porții de polietilenă liniară de joasă densitate (LLDPE), una de 7,5 kg care va forma stratul exterior și una de 1,5 kg care va forma stratul interior. Separat, se cântăresc 1,5 g biocid (amestec dioxid de titan:clorură de argint în proporție de 8:2 masic). Se omogenizează foarte bine cele 1,5 kg polietilenă cu cele 1,5 g biocid.Example 2. Weigh two portions of low density linear polyethylene (LLDPE), one 7.5 kg which will form the outer layer and one 1.5 kg which will form the inner layer. Separately, weigh 1.5 g biocide (titanium dioxide mixture: silver chloride in 8: 2 mass ratio). The 1.5 kg polyethylene is well homogenized with the 1.5 g biocide.

Se introduc cele 7,5 kg polietilenă în matriță și se închide matrița.Put the 7.5 kg polyethylene into the mold and close the mold.

Se setează temperatura cuptorului la 230’C, se lasă să termostateze și se introduce matrița în cuptor. Matrița este continuu în mișcare de rotație, turația pe axa primară fiind de 8 rot/min, iar pe axa secundară de 2,1 rot/min.Set the oven temperature to 230'C, allow to thermostat and insert the mold into the oven. The mold is continuously rotating, the speed on the primary axis being 8 rot / min, and on the secondary axis 2.1 rot / min.

După 10 min (circa 3 min pentru fiecare 1 mm grosime de perete), când tot materialul care va forma stratul exterior este topit, se scoate matrița din cuptor.After 10 minutes (about 3 minutes for every 1 mm wall thickness), when all the material that will form the outer layer is melted, remove the mold from the oven.

Se scoate dopul de aerisire, se introduce amestecul polietilenă-biocid în matriță, se reintroduce dopul de aerisire și se introduce matrița în cuptor.Remove the vent plug, insert the polyethylene-biocidal mixture into the mold, re-insert the vent plug and insert the mold into the oven.

Se lasă matrița în cuptor circa 5 min astfel încât tot materialul care formează stratul interior să se topească.Leave the mold in the oven for about 5 minutes so that all the material that forms the inner layer melts.

Se scoate matrița din cuptor și se răcește lent circa 20 min, folosind un ventilator de capacitate corespunzătoare. Pe tot parcursul fazei de răcire, matrița este în mișcare de rotație.Remove the mold from the oven and chill slowly for about 20 minutes, using a suitable capacity fan. Throughout the cooling phase, the mold is rotating.

După răcire, când materialul a revenit în stare solidă, se oprește mișcarea de rotație, se deschide matrița și se scoate produsul.After cooling, when the material has returned to solid state, the rotation movement stops, the mold is opened and the product is removed.

Se curăță produsul de resturile aflate la planurile de îmbinare ale matriței.The product is cleaned from the debris found on the molding plans of the mold.

Recipientul este gata pentru a fi folosit în exploatare.The container is ready for use in operation.

Pentru stratul interior, se poate folosi același material ca și pentru stratul exterior, sau de preferat un material cu caracteristici elastice, cum ar fi o polietilenă cu conținut ridicat de α-olefină, care să îmbunătățească rezistența la șoc.For the inner layer, the same material as the outer layer may be used, or preferably a material with elastic characteristics, such as a high-α-olefin polyethylene, which improves shock resistance.

Claims (5)

Revendicăriclaims 1. Recipient pentru stocarea unui lichid destinat consumului alimentar, care este constituit dintr-un strat activ din polietilenă care are în compoziție ioni de argint, care strat poate fi protejat de către un strat exterior realizat numai din polietilenă, caracterizat prin aceea că stratul activ are o grosime de 0,05...1 mm și are un conținut de 0,005...0,3% în greutate pulbere care conține ioni de Ag+ cu activitate biocidă, proveniți din AgCI, depusă pe un suport inert din TiO2 , iar stratul exterior, atunci când acesta există, are o grosime de 1...2 mm și este în contact intim cu stratul activ.1. Container for storing a liquid intended for food consumption, which consists of an active layer of polyethylene having silver ions, which layer can be protected by an outer layer made only of polyethylene, characterized in that the active layer It has a thickness of 0.05 ... 1 mm and has a content of 0.005 ... 0.3% by weight of powder containing Ag + ions with biocidal activity, coming from AgCI, deposited on an inert TiO 2 support. , and the outer layer, when it exists, has a thickness of 1 ... 2 mm and is in close contact with the active layer. 2. Recipient conform revendicării 1, caracterizat prin aceea că pulberea cu activitate biocidă este constituită dintr-un suport inert din dioxid de titan și din clorură de argint în raport în greutate dioxid de titan : clorură de argint de 8 : 2.2. Container according to claim 1, characterized in that the powder with biocidal activity consists of an inert support of titanium dioxide and silver chloride in weight ratio of titanium dioxide: silver chloride of 8: 2. 3. Procedeu de realizare a unui recipient monostrat, definit în revendicările 1 și 2, caracterizat prin aceea că se amestecă 1,5...9,0 părți în greutate polietilenă de joasă densitate cu 0,3% în greutate pulbere cu activitate biocidă, omogenizată în prealabil timp de 20 min, se introduce amestecul într-o matriță care se menține la o temperatură de 230’C, timp de 25 min, aflată în mișcare de rotație în jurul celor două axe de rotație, primară și secundară, cu o viteză de rotație de 8,0 rot/min și respectiv de 2,1 rot/min, se menține matrița în cuptor timp de 5 min, pentru a se depune stratul de polietilenă pe pereți, se răcește lent timp de 40 min sub ventilație, se oprește mișcarea de rotație și se extrage recipientul monostrat rezultat.Process for making a monolayer container, defined in claims 1 and 2, characterized in that 1.5 to 9.0 parts by weight of low density polyethylene with 0.3% by weight of biocidal activity powder are mixed. , homogenized beforehand for 20 minutes, the mixture is introduced into a mold which is maintained at a temperature of 230'C, for 25 minutes, which is rotating around the two axes of rotation, primary and secondary, with a rotation speed of 8.0 rot / min and 2.1 rot / min respectively, keep the mold in the oven for 5 minutes, to deposit the polyethylene layer on the walls, cool slowly for 40 minutes under ventilation , stop the rotation movement and extract the resulting monolayer container. 4. Procedeu de realizare a unui recipient bistrat, definit în revendicările 1 și 2, caracterizat prin aceea că 7,5 părți în greutate polietilenă de joasă densitate necesară formării unui strat exterior se introduc într-o matriță încălzită la o temperatură de 230‘C, aflată în mișcare de4. Process for making a bistable container, as defined in claims 1 and 2, characterized in that 7.5 parts by weight of low density polyethylene required to form an outer layer are introduced into a mold heated to a temperature of 230'C. , in motion by RO 119784 Β1 rotație, se menține în cuptor timp de 10 min, după care se introduce în matriță un amestec de 1 1,5 părți în greutate polietilenă de joasă densitate cu 0,1 % în greutate pulbere cu activitate biocidă, omogenizată în prealabil timp de 20 min, se menține încă 5 min la temperatura de 230’C, 3 pentru formarea stratului interior, se răcește lent sub ventilație timp de 20 min, după care se oprește mișcarea de rotație și se extrage recipientul bistrat rezultat. 5RO 119784 Β1 rotation, kept in the oven for 10 minutes, after which a mixture of 1 1.5 parts by weight of low density polyethylene with 0.1% by weight powder with biocidal activity, homogenized previously was introduced into the mold. for 20 minutes, keep for another 5 minutes at 230'C, 3 for the formation of the inner layer, cool slowly under ventilation for 20 minutes, after which the rotation movement is stopped and the resulting bistable container is extracted. 5 5. Procedeu conform revendicărilor 3 și 4, caracterizat prin aceea că pulberea cu activitate biocidă este constituită dintr-un suport inert din dioxid de titan pe care este depusă pul- 7 bere din clorură de argint în raport în greutate dioxid de titan : clorură de argint de 8:2.5. Process according to claims 3 and 4, characterized in that the powder with biocidal activity is constituted by an inert support of titanium dioxide on which silver chloride powder is deposited in weight ratio of titanium dioxide: chloride of chloride. 8: 2 silver.
ROA200300568A 2003-06-30 2003-06-30 Recipient for storing a liquid meant for alimentary consumption and process for making the same RO119784B1 (en)