PL94509B1 - Okladzina stalowa walcow szarpiacych - Google Patents
Okladzina stalowa walcow szarpiacych Download PDFInfo
- Publication number
- PL94509B1 PL94509B1 PL1974176592A PL17659274A PL94509B1 PL 94509 B1 PL94509 B1 PL 94509B1 PL 1974176592 A PL1974176592 A PL 1974176592A PL 17659274 A PL17659274 A PL 17659274A PL 94509 B1 PL94509 B1 PL 94509B1
- Authority
- PL
- Poland
- Prior art keywords
- steel
- cladding
- nickel
- rollers
- chromium
- Prior art date
Description
Przedmiotem wynalazku jest okladzina stalowa walców szarpiacych w przedzarkach przedzacych metoda
wolnego konca, które to walce posiadaja beben i stalowy drut pilowy nieruchomo osadzony na tym bebnie jako
okladzine. ¦
Okladzina walców szarpiacych w przedzarkach ulega szybkiemu zuzyciu. Czesto zywotnosc jednej
okladziny przy przeróbce wlókien sztucznych wynosi zaledwie dwa tygodnie. Dotychczas starano sie
przedluzyc zywotnosc okladzin calkowicie stalowych walców szarpacza przez zastosowanie stali
martenzytycznych cwysokiej wytrzymalosci jako materialu drutu pilowego,, Mimo zastosowania takich
srodków nie udalo sie przedluzyc zywotnosci ponad wyzej podany okres*
Celem wynalazku jest opracowanie okladziny o zywotnosci znacznie wiekszej niz dotychczas stosowane.
Cel ten osiagnieto dzieki temu, ze okladzina wykonana jest ze stali chemicznie odpornej. Korzystnym jest
wykonanie okladziny ze stali zawierajacej co najmniej 12% chromu lub tez ze stali austenitycznej
chromo-niklowej. Przeprowadzone badania wykazaly, ze korzystnym jest dodawanie do stali molibdenu.
Szczególnie korzystnym jest gdy okladzina wykonana jest ze stali austenitycznej z zawartoscia 12 do 19%
chromu, 7 do 15% niklu i 2 do 3% molibdenu.
Przeprowadzone badania wykazaly, ze chemicznie odporne stale austenityczne wykazuja przy przeróbce
wlókien syntetycznych znacznie wieksza zywotnosc niz okladziny wykonywane dotychczas ze stali o wysokiej
wytrzymalosci.
Przeprowadzono próbe porównawcza z walcem szarpiacym, którego calkowicie stalowe obicie mialo drut
pilowy ze stali weglistej o twardosci Rockwella od 60 do 64. Ten walec szarpiacy zostal zastosowany do
przerobu wlókien akrylu. Po 160 godzinach pracy pokazaly sie na przednich krawedziach zebów rowki i dziury
na skutek czego calkowicie stalowe obicie nie nadawalo sie do dalszego uzytku po takim okresie pracy. Przy
dalszej pracy okazalo sie, ze zeby zostaly prawidlowo odpilowane. Nastepnie przeprowadzono druga próbe ze
stala chromowo-niklowa o zawartosci chromu od 17 do 19% i zawartosci niklu od 8 do 10% i z zawartoscia wegla
nizsza od 0,12%. Drut pilowy wykonany z tego materialu zostal po procesie walcowania poddany obróbce
cieplnej przy temperaturze 1100°C i zaraz potem szybko schlodzony w wodzie dla uzyskania lepszej struktury2 94 509
ziarn. Do szarpacza dano do przerobu ponownie wlókno akrylu i to na okres pracy 500 godzin. Po tym okresie
pracy na zebach nie byly jeszcze widoczne jakiekolwiek zmiany, tak ze próbe przerwana «
Zastosowana stal chromowo-niklowa jest w porównaniu ze stala weglista zastosowana, w pierwszym
przykladzie wzglednie miekka, poniewaz tego materialu nie mozna praktycznie zahartowac. Pomimo tego
uzyskano wielokrotne przedluzenie okresu zywotnosci obicia. Z. tego mozna wyciagnac wniosek, ze zywotnosc
nie tyle zalezy od twardosci zastosowanego rodzaju stali, co od jej chemicznej odpornosci. Stanowi to
przeciwstawienie dotychczasowych staran przedluzenia zywotnosci . okladzin walców szarpiacych przez
podwyzszenie twardosci stali. Jakkolwiek te dotychczas przedsiebrane srodki dawaly przedluzenie zywotnosci
okladzin, to mozna bylo ja bardzo znacznie przedluzyc przez zastosowanie srodków wedlug wynalazku.
To korzystne oddzialywanie wystepuje juz przy zastosowaniu prostych stali chromowych. Jednak
korzystniej jest zastosowac stale chromowo-niklowe, które sa szczególnie odporne na korozje. Tego rodzaju stale
chromowo-niklowe posiadaja zawartosc chromu w ilosci okolo 18% i zawartosc niklu 8%, jednak dla dalszego
ulepszenia odpornosci chemicznej moga byc zastosowane stale bardziej wysoko-stopowe i zawierajace jeszcze
dalsze skladniki stopowe, jak na przyklad molibden, tytan i niob. »
Mozna równiez zastosowac utwardzone dyspersyjnie stale nierdzewne, które na ogól posiadaja dodatek
glinu. '
Claims (1)
1. Zastrzezenie patentowe Okladzina stalowa, szczególnie walców szarpiacych przedzarek przedzacych metoda wolnego konca do wlókien syntetycznych, które to walce posiadaja beben z nieruchomo na nim osadzonym drutem pilowym, znamienna tym, ze drut pilowy jest wykonany z austenitycznej stali kwasoodpomej, zawierajacej od 12 do 19% chromu, 7 do 15% niklu i 2 do 3% molibdenu. « Prac. Poligraf. UP PRL naklad 120+18 Cena 10 zl