PL424691A1 - Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych - Google Patents
Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznychInfo
- Publication number
- PL424691A1 PL424691A1 PL424691A PL42469118A PL424691A1 PL 424691 A1 PL424691 A1 PL 424691A1 PL 424691 A PL424691 A PL 424691A PL 42469118 A PL42469118 A PL 42469118A PL 424691 A1 PL424691 A1 PL 424691A1
- Authority
- PL
- Poland
- Prior art keywords
- max
- group
- steel
- fasteners
- cold forging
- Prior art date
Abstract
Przedmiotem zgłoszenia jest sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych, w którym stosuje się stal o strukturze wielowazowej z efektem TRIP z fazą w postaci austenitu szczątkowego w granicach od 6 do 11% uzyskanego poprzez termomechaniczne walcowanie z kontrolowanym chłodzeniem, przy czym stosuje się stal o składzie chemicznym grupy pierwszej, dla której zawartość poszczególnych pierwiastków wynosi: C = 0,06 - 0,12%; Si = 0,2 - 0,5%; Mn = 0,0 - 1,5%; Cr = 0,0 - 0,3%; P = max 0,025%, S = max 0,025%, albo grupy drugiej, dla której zawartość poszczególnych pierwiastków wynosi: C = 0,06 - 0,14%; Si = 0,8 - 1,2%; Mn = 1,6 - 1,9%; Cr = 0,0 - 0,15%; P = max 0,025%, S = max 0,025%, natomiast średnicę materiału wsadowego oraz gniot sumaryczny podczas operacji ciągnienia jedno lub wieloetapowego dobiera się tak, aby spełniona była zależność Rm = 1142 z 0,1831 dla stali z grupy pierwszej oraz Rm = 1081 z 0,1567 dla stali z grupy drugiej, z możliwym odchyleniem ±50 MPa, gdzie Rm oznacza oczekiwaną wytrzymałość na rozciąganie drutu.
Priority Applications (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| PL424691A PL424691A1 (pl) | 2018-02-27 | 2018-02-27 | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych |
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| PL424691A PL424691A1 (pl) | 2018-02-27 | 2018-02-27 | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| PL424691A1 true PL424691A1 (pl) | 2019-09-09 |
Family
ID=67844624
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| PL424691A PL424691A1 (pl) | 2018-02-27 | 2018-02-27 | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych |
Country Status (1)
| Country | Link |
|---|---|
| PL (1) | PL424691A1 (pl) |
Citations (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3926687A (en) * | 1973-09-10 | 1975-12-16 | Nippon Steel Corp | Method for producing a killed steel wire rod |
| US4613385A (en) * | 1984-08-06 | 1986-09-23 | Regents Of The University Of California | High strength, low carbon, dual phase steel rods and wires and process for making same |
| US5338380A (en) * | 1985-08-29 | 1994-08-16 | Kabushiki Kaisha Kobe Seiko Sho | High strength low carbon steel wire rods and method of producing them |
| CN106311781A (zh) * | 2016-09-28 | 2017-01-11 | 邢台钢铁有限责任公司 | 一种超低碳钢拉拔细丝的方法 |
-
2018
- 2018-02-27 PL PL424691A patent/PL424691A1/pl unknown
Patent Citations (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US3926687A (en) * | 1973-09-10 | 1975-12-16 | Nippon Steel Corp | Method for producing a killed steel wire rod |
| US4613385A (en) * | 1984-08-06 | 1986-09-23 | Regents Of The University Of California | High strength, low carbon, dual phase steel rods and wires and process for making same |
| US5338380A (en) * | 1985-08-29 | 1994-08-16 | Kabushiki Kaisha Kobe Seiko Sho | High strength low carbon steel wire rods and method of producing them |
| CN106311781A (zh) * | 2016-09-28 | 2017-01-11 | 邢台钢铁有限责任公司 | 一种超低碳钢拉拔细丝的方法 |
Non-Patent Citations (1)
| Title |
|---|
| WIEWIÓRKOWSKA S, MUSKALSKI Z, THE APPLICATION OF LOW AND MEDIUM CARBON STEEL WITH MULTIPHASE TRIP STRUCTURE IN DRAWING INDUSTRY PROCEDIA MANUFACTURING, 2015 * |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| MX2018004772A (es) | Miembro prensado en caliente y metodo de fabricacion del mismo. | |
| UA118699C2 (uk) | Спосіб отримання високоміцного сталевого листа з покриттям, що має покращену міцність і пластичність, та отриманий лист | |
| MX2020003923A (es) | Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma. | |
| TWI616538B (zh) | 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法 | |
| UA117865C2 (uk) | Високоміцна багатофазна сталь, спосіб її одержання та застосування | |
| IN2014CN02685A (pl) | ||
| AU2015205937B2 (en) | Pearlitic steel rail with high strength and toughness and producing method thereof | |
| BR112017000021A2 (pt) | método para fabricar uma folha de aço e folha de aço | |
| WO2011121118A3 (de) | Stahl, stahlflachprodukt, stahlbauteil und verfahren zur herstellung eines stahlbauteils | |
| WO2012002638A3 (ko) | 초고강도 철근 및 그 제조방법 | |
| MX2013005011A (es) | Hoja de acero laminado de frio de alta resistencia que tiene capacidad de embuticion profunda y capacidad de temple en horno excelentes y metodo para su fabricacion. | |
| MX366776B (es) | Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma. | |
| BR122019019513B1 (pt) | Folha de aço descoberta e folha de aço revestida | |
| MX2017008296A (es) | Laminas de acero galvanizado de alta resistencia y metodos para fabricar las mismas. | |
| MX356324B (es) | Método para la fabricación de acero martensítico con límite de elasticidad muy alto y placa o pieza obtenida por tal método. | |
| RU2011147484A (ru) | Высокопрочный, высоковязкий тонкий стальной пруток и способ его изготовления | |
| RU2017143579A (ru) | Коррозионностойкая сталь, способ изготовления указанной стали и ее применение | |
| MY173780A (en) | Steel sheet for can and method for manufacturing the same | |
| MX2016014963A (es) | Tira de acero que tiene alta resistencia y alta plasticidad, la tira de acero tiene un recubrimiento a base de zinc en caliente. | |
| RU2017141034A (ru) | Низколегированная особо высокопрочная сталь третьего поколения | |
| MY192536A (en) | High-mn steel and method for manufacturing same | |
| MX2018011606A (es) | Chapa de acero galvanizada de alta resistencia y metodo para producir la misma. | |
| PL424691A1 (pl) | Sposób wytwarzania drutu ciągniętego, zwłaszcza do zastosowania jako materiał wsadowy do kucia na zimno elementów złącznych | |
| CN102433507A (zh) | 低屈强比易焊接高强钢板及其制备工艺 | |
| MX2019009600A (es) | Lamina de acero laminada en frio y metodo para fabricar la misma. |