PL3619040T3 - Sposób wytwarzania blachy stalowej, ocynkowanej z przeżarzaniem, odpornej na kruchość wywołaną przez ciekły metal - Google Patents
Sposób wytwarzania blachy stalowej, ocynkowanej z przeżarzaniem, odpornej na kruchość wywołaną przez ciekły metalInfo
- Publication number
- PL3619040T3 PL3619040T3 PL18722194T PL18722194T PL3619040T3 PL 3619040 T3 PL3619040 T3 PL 3619040T3 PL 18722194 T PL18722194 T PL 18722194T PL 18722194 T PL18722194 T PL 18722194T PL 3619040 T3 PL3619040 T3 PL 3619040T3
- Authority
- PL
- Poland
- Prior art keywords
- manufacturing
- steel sheet
- liquid metal
- galvannealed steel
- metal embrittlement
- Prior art date
Links
- 229910000831 Steel Inorganic materials 0.000 title 1
- 229910001338 liquidmetal Inorganic materials 0.000 title 1
- 238000004519 manufacturing process Methods 0.000 title 1
- 238000000034 method Methods 0.000 title 1
- 239000010959 steel Substances 0.000 title 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
- C23C28/021—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material including at least one metal alloy layer
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/011—Layered products comprising a layer of metal all layers being exclusively metallic all layers being formed of iron alloys or steels
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
- B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
- B23K11/00—Resistance welding; Severing by resistance heating
- B23K11/10—Spot welding; Stitch welding
- B23K11/11—Spot welding
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/012—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of aluminium or an aluminium alloy
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B32—LAYERED PRODUCTS
- B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
- B32B15/00—Layered products comprising a layer of metal
- B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
- B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0273—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C10/00—Solid state diffusion of only metal elements or silicon into metallic material surfaces
- C23C10/28—Solid state diffusion of only metal elements or silicon into metallic material surfaces using solids, e.g. powders, pastes
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
- C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
- C23C2/0224—Two or more thermal pretreatments
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
- C23C2/06—Zinc or cadmium or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/261—After-treatment in a gas atmosphere, e.g. inert or reducing atmosphere
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
- C23C2/26—After-treatment
- C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
- C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
- C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
- C23C28/025—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only with at least one zinc-based layer
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/10—Electroplating with more than one layer of the same or of different metals
- C25D5/12—Electroplating with more than one layer of the same or of different metals at least one layer being of nickel or chromium
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of workpieces
- C25D5/48—After-treatment of electroplated surfaces
- C25D5/50—After-treatment of electroplated surfaces by heat-treatment
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D7/00—Electroplating characterised by the article coated
- C25D7/06—Wires; Strips; Foils
- C25D7/0614—Strips or foils
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D3/00—Electroplating: Baths therefor
- C25D3/02—Electroplating: Baths therefor from solutions
- C25D3/12—Electroplating: Baths therefor from solutions of nickel or cobalt
-
- C—CHEMISTRY; METALLURGY
- C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
- C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
- C25D3/00—Electroplating: Baths therefor
- C25D3/02—Electroplating: Baths therefor from solutions
- C25D3/22—Electroplating: Baths therefor from solutions of zinc
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Mechanical Engineering (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Electrochemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Oil, Petroleum & Natural Gas (AREA)
- Coating With Molten Metal (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Electroplating Methods And Accessories (AREA)
- Laminated Bodies (AREA)
- Solid-Phase Diffusion Into Metallic Material Surfaces (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/IB2017/000520 WO2018203097A1 (en) | 2017-05-05 | 2017-05-05 | A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet |
EP18722194.0A EP3619040B1 (en) | 2017-05-05 | 2018-04-25 | A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet |
PCT/IB2018/000429 WO2018203126A1 (en) | 2017-05-05 | 2018-04-25 | A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet |
Publications (1)
Publication Number | Publication Date |
---|---|
PL3619040T3 true PL3619040T3 (pl) | 2022-04-25 |
Family
ID=59101514
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PL18722194T PL3619040T3 (pl) | 2017-05-05 | 2018-04-25 | Sposób wytwarzania blachy stalowej, ocynkowanej z przeżarzaniem, odpornej na kruchość wywołaną przez ciekły metal |
Country Status (16)
Country | Link |
---|---|
US (2) | US11654653B2 (pl) |
EP (1) | EP3619040B1 (pl) |
JP (2) | JP2020521041A (pl) |
KR (2) | KR20190126441A (pl) |
CN (1) | CN110573335B (pl) |
BR (1) | BR112019021226B1 (pl) |
CA (1) | CA3059297C (pl) |
ES (1) | ES2911187T3 (pl) |
HU (1) | HUE059412T2 (pl) |
MA (1) | MA49080B1 (pl) |
MX (1) | MX2019013153A (pl) |
PL (1) | PL3619040T3 (pl) |
RU (1) | RU2729236C1 (pl) |
UA (1) | UA123755C2 (pl) |
WO (2) | WO2018203097A1 (pl) |
ZA (1) | ZA201906479B (pl) |
Families Citing this family (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2018203097A1 (en) * | 2017-05-05 | 2018-11-08 | Arcelormittal | A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet |
CA3076464C (en) * | 2017-10-24 | 2022-07-12 | Arcelormittal | A method for the manufacture of a galvannealed steel sheet |
CN111356783B (zh) * | 2017-11-17 | 2023-03-21 | 安赛乐米塔尔公司 | 用于制造抗液态金属脆化的锌涂覆的钢板的方法 |
CN110184537B (zh) * | 2019-05-24 | 2020-10-30 | 武汉钢铁有限公司 | 一种低碳含钴高强度桥索钢及生产方法 |
US11548091B2 (en) * | 2019-10-10 | 2023-01-10 | GM Global Technology Operations LLC | Pretreatment of weld flanges to mitigate liquid metal embrittlement cracking in resistance welding of galvanized steels |
KR102510214B1 (ko) * | 2020-10-29 | 2023-03-16 | 현대제철 주식회사 | 액체금속취성을 방지하는 철-니켈 합금층을 포함한 핫스탬핑 용융아연도금 강재, 핫스탬핑 부품 및 그 제조방법 |
US11441039B2 (en) * | 2020-12-18 | 2022-09-13 | GM Global Technology Operations LLC | High temperature coatings to mitigate weld cracking in resistance welding |
CN114686651A (zh) * | 2020-12-31 | 2022-07-01 | 通用汽车环球科技运作有限责任公司 | 具有降低的液态金属致脆(lme)敏感性的锌涂覆的钢 |
JP7304476B1 (ja) * | 2021-12-27 | 2023-07-06 | Jfeテクノリサーチ株式会社 | 鋼板の抵抗スポット溶接部における液体金属脆性割れ感受性の評価方法 |
Family Cites Families (19)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2561331B2 (ja) * | 1988-11-07 | 1996-12-04 | 川崎製鉄株式会社 | 溶融ZnめっきCr含有鋼帯の製造方法 |
CN1204284C (zh) * | 2000-12-29 | 2005-06-01 | 新日本制铁株式会社 | 具有优异的镀层附着性和冲压成形性的高强度热浸镀锌钢板及其制造方法 |
US20080283154A1 (en) | 2004-01-14 | 2008-11-20 | Hirokazu Taniguchi | Hot dip galvanized high strength steel sheet excellent in plating adhesion and hole expandability and method of production of same |
KR100968620B1 (ko) * | 2005-04-20 | 2010-07-08 | 신닛뽄세이테쯔 카부시키카이샤 | 고강도 합금화 용융 아연 도금 강판의 제조 방법 |
JP4510688B2 (ja) * | 2005-04-20 | 2010-07-28 | 新日本製鐵株式会社 | 高強度高延性合金化溶融亜鉛メッキ鋼板の製造方法 |
JP2008144264A (ja) * | 2006-11-16 | 2008-06-26 | Jfe Steel Kk | 高強度溶融亜鉛めっき鋼板及び高強度合金化溶融亜鉛めっき鋼板の製造方法 |
US20120100391A1 (en) | 2010-10-21 | 2012-04-26 | Posco | Hot-dip galvanized steel sheet having excellent plating qualities, plating adhesion and spot weldability and manufacturing method thereof |
KR20120041544A (ko) | 2010-10-21 | 2012-05-02 | 주식회사 포스코 | 도금성, 도금밀착성 및 스폿용접성이 우수한 용융아연도금강판 및 그 제조방법 |
JP5273324B1 (ja) | 2011-07-29 | 2013-08-28 | 新日鐵住金株式会社 | 曲げ性に優れた高強度亜鉛めっき鋼板およびその製造方法 |
CA2850045C (en) * | 2011-09-30 | 2016-04-12 | Nippon Steel & Sumitomo Metal Corporation | Galvanized steel sheet and method of manufacturing the same |
EP2762592B1 (en) | 2011-09-30 | 2018-04-25 | Nippon Steel & Sumitomo Metal Corporation | High-strength hot-dipped galvanized steel sheet and high-strength alloyed hot-dipped galvanized steel sheet, each having tensile strength of 980 mpa or more, excellent plating adhesion, excellent formability and excellent bore expanding properties, and method for producing same |
JP5720856B2 (ja) | 2012-08-07 | 2015-05-20 | 新日鐵住金株式会社 | 熱間成形用亜鉛系めっき鋼板 |
US10040270B2 (en) * | 2013-05-20 | 2018-08-07 | Nippon Steel & Sumitomo Metal Corporation | Galvannealed steel sheet and manufacturing method thereof |
EP3040133B1 (en) | 2013-08-29 | 2017-03-01 | JFE Steel Corporation | Method of manufacturing hot press formed part, and hot press formed part |
KR101585721B1 (ko) | 2013-12-21 | 2016-01-14 | 주식회사 포스코 | 용접성이 우수한 아연도금강판 및 이의 제조 방법 |
KR101568543B1 (ko) | 2013-12-25 | 2015-11-11 | 주식회사 포스코 | 액체금속취화에 의한 크랙 저항성이 우수한 용융아연도금강판 |
WO2016016676A1 (fr) | 2014-07-30 | 2016-02-04 | ArcelorMittal Investigación y Desarrollo, S.L. | Procédé de fabrication de tôles d'acier, pour durcissement sous presse, et pièces obtenues par ce procédé |
WO2018203097A1 (en) * | 2017-05-05 | 2018-11-08 | Arcelormittal | A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet |
CA3076464C (en) * | 2017-10-24 | 2022-07-12 | Arcelormittal | A method for the manufacture of a galvannealed steel sheet |
-
2017
- 2017-05-05 WO PCT/IB2017/000520 patent/WO2018203097A1/en active Application Filing
-
2018
- 2018-04-25 BR BR112019021226-4A patent/BR112019021226B1/pt active IP Right Grant
- 2018-04-25 KR KR1020197031718A patent/KR20190126441A/ko not_active IP Right Cessation
- 2018-04-25 UA UAA201911639A patent/UA123755C2/uk unknown
- 2018-04-25 WO PCT/IB2018/000429 patent/WO2018203126A1/en active Application Filing
- 2018-04-25 RU RU2019139205A patent/RU2729236C1/ru active
- 2018-04-25 MA MA49080A patent/MA49080B1/fr unknown
- 2018-04-25 PL PL18722194T patent/PL3619040T3/pl unknown
- 2018-04-25 MX MX2019013153A patent/MX2019013153A/es unknown
- 2018-04-25 CA CA3059297A patent/CA3059297C/en active Active
- 2018-04-25 EP EP18722194.0A patent/EP3619040B1/en active Active
- 2018-04-25 CN CN201880028753.XA patent/CN110573335B/zh active Active
- 2018-04-25 KR KR1020207025680A patent/KR20200108102A/ko not_active IP Right Cessation
- 2018-04-25 US US16/605,473 patent/US11654653B2/en active Active
- 2018-04-25 JP JP2019560237A patent/JP2020521041A/ja active Pending
- 2018-04-25 HU HUE18722194A patent/HUE059412T2/hu unknown
- 2018-04-25 ES ES18722194T patent/ES2911187T3/es active Active
-
2019
- 2019-10-02 ZA ZA2019/06479A patent/ZA201906479B/en unknown
-
2022
- 2022-03-15 JP JP2022039900A patent/JP7358542B2/ja active Active
-
2023
- 2023-04-06 US US18/131,622 patent/US20230241865A1/en active Pending
Also Published As
Publication number | Publication date |
---|---|
ZA201906479B (en) | 2020-08-26 |
US20200123674A1 (en) | 2020-04-23 |
HUE059412T2 (hu) | 2022-11-28 |
KR20190126441A (ko) | 2019-11-11 |
UA123755C2 (uk) | 2021-05-26 |
WO2018203126A1 (en) | 2018-11-08 |
JP2022091820A (ja) | 2022-06-21 |
JP2020521041A (ja) | 2020-07-16 |
CA3059297C (en) | 2021-12-28 |
RU2729236C1 (ru) | 2020-08-05 |
BR112019021226B1 (pt) | 2023-05-02 |
ES2911187T3 (es) | 2022-05-18 |
MA49080B1 (fr) | 2022-03-31 |
MX2019013153A (es) | 2020-02-05 |
JP7358542B2 (ja) | 2023-10-10 |
CA3059297A1 (en) | 2018-11-08 |
BR112019021226A2 (pt) | 2020-04-28 |
KR20200108102A (ko) | 2020-09-16 |
CN110573335A (zh) | 2019-12-13 |
EP3619040A1 (en) | 2020-03-11 |
US20230241865A1 (en) | 2023-08-03 |
CN110573335B (zh) | 2021-09-14 |
EP3619040B1 (en) | 2022-03-09 |
WO2018203097A1 (en) | 2018-11-08 |
MA49080A (fr) | 2020-03-18 |
US11654653B2 (en) | 2023-05-23 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
ZA201906479B (en) | A method for the manufacturing of liquid metal embrittlement resistant galvannealed steel sheet | |
ZA202002400B (en) | A method for the manufacturing of liquid metal embrittlement resistant zinc coated steel sheet | |
ZA201903144B (en) | Tempered and coated steel sheet having excellent formability and a method of manufacturing the same | |
HUE053698T2 (hu) | Eljárás foszfatálható alkatrész elõállítására alumínium alapú fémes bevonattal bevont acéllemezbõl kiindulva | |
ZA201903329B (en) | Tempered and coated steel sheet having excellent formability and a method of manufacturing the same | |
HUE049700T2 (hu) | Eljárás alkatrész elõállítására alumínium bázisú fémbevonattal bevont acéllemezbõl | |
EP3438307A4 (en) | HOT GALVANIZED STEEL SHEET | |
ZA202001574B (en) | A method for the manufacture of a coated steel sheet | |
PL3181248T3 (pl) | Sposób i układ do wytwarzania arkusza blaszanego | |
PL3149217T3 (pl) | Blacha stalowa zaopatrzona w protektorową katodową powłokę ochronną zawierającą lantan | |
PL3697936T3 (pl) | Sposób wytwarzania stalowego elementu konstrukcyjnego zaopatrzonego w metalową powłokę chroniącą przed korozją | |
PL3642371T3 (pl) | Sposób wytwarzania stalowego elementu konstrukcyjnego zaopatrzonego w metalową powłokę chroniącą przed korozją | |
ZA202002381B (en) | A hot-dip coated steel substrate | |
ZA202002314B (en) | A hot-dip coated steel sheet | |
SG11201610389TA (en) | A method of coating a sheet of steel | |
ZA202002310B (en) | A galvannealed steel sheet | |
EP3396005A4 (en) | Mn-CONTAINING HOT-DIP GALVANNEALED STEEL SHEET AND MANUFACTURING METHOD THEREFOR | |
PL3728696T3 (pl) | Sposób wytrawiania blach stalowych | |
ZA202001535B (en) | A method for the manufacture of a coated steel sheet | |
ZA201806336B (en) | Method for producing a metallic coated steel sheet | |
GB2577004B (en) | Method of aligning a flat or profiled metal sheet | |
ZA202001632B (en) | A method for the manufacture of a galvannealed steel sheet | |
HUE056714T2 (hu) | Eljárás bevonatolt acéllemez gyártására |