PL2682495T3 - Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania - Google Patents

Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania

Info

Publication number
PL2682495T3
PL2682495T3 PL12752196T PL12752196T PL2682495T3 PL 2682495 T3 PL2682495 T3 PL 2682495T3 PL 12752196 T PL12752196 T PL 12752196T PL 12752196 T PL12752196 T PL 12752196T PL 2682495 T3 PL2682495 T3 PL 2682495T3
Authority
PL
Poland
Prior art keywords
dip
coated
steel sheet
based system
manufacturing same
Prior art date
Application number
PL12752196T
Other languages
English (en)
Inventor
Kentaro Hirata
Yukio Katagiri
Susumu Fujiwara
Kazuaki Hosomi
Masaaki URANAKA
Original Assignee
Nisshin Steel Co., Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nisshin Steel Co., Ltd. filed Critical Nisshin Steel Co., Ltd.
Publication of PL2682495T3 publication Critical patent/PL2682495T3/pl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B60—VEHICLES IN GENERAL
    • B60R—VEHICLES, VEHICLE FITTINGS, OR VEHICLE PARTS, NOT OTHERWISE PROVIDED FOR
    • B60R13/00—Elements for body-finishing, identifying, or decorating; Arrangements or adaptations for advertising purposes
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C22C18/04—Alloys based on zinc with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C23/00—Alloys based on magnesium
    • C22C23/02—Alloys based on magnesium with aluminium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C23/00—Alloys based on magnesium
    • C22C23/04—Alloys based on magnesium with zinc or cadmium as the next major constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
PL12752196T 2011-02-28 2012-02-28 Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania PL2682495T3 (pl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
JP2011043334 2011-02-28
PCT/JP2012/054926 WO2012118073A1 (ja) 2011-02-28 2012-02-28 溶融Ｚｎ－Ａｌ－Ｍｇ系めっき鋼板および製造方法
EP12752196.1A EP2682495B1 (en) 2011-02-28 2012-02-28 STEEL SHEET HOT-DIP-COATED WITH Zn-Al-Mg-BASED SYSTEM, AND PROCESS OF MANUFACTURING SAME

Publications (1)

Publication Number Publication Date
PL2682495T3 true PL2682495T3 (pl) 2019-06-28

Family

ID=46758004

Family Applications (1)

Application Number Title Priority Date Filing Date
PL12752196T PL2682495T3 (pl) 2011-02-28 2012-02-28 Blacha stalowa powlekana zanurzeniowo systemem na bazie Zn-Al-Mg i sposób jej wytwarzania

Country Status (12)

Country Link
US (1) US9592772B2 (pl)
EP (2) EP2682495B1 (pl)
JP (1) JP5936390B2 (pl)
KR (1) KR102099588B1 (pl)
CN (1) CN103415641B (pl)
AU (1) AU2012224032B2 (pl)
CA (1) CA2826225C (pl)
ES (1) ES2712631T3 (pl)
HU (1) HUE043883T2 (pl)
PL (1) PL2682495T3 (pl)
TR (1) TR201903572T4 (pl)
WO (1) WO2012118073A1 (pl)

Families Citing this family (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5372217B2 (ja) * 2012-02-24 2013-12-18 日新製鋼株式会社 アーク溶接構造部材の製造法
JP6049516B2 (ja) * 2013-03-26 2016-12-21 日新製鋼株式会社 溶接構造部材用高強度めっき鋼板およびその製造法
CN105940131A (zh) * 2013-12-19 2016-09-14 日新制钢株式会社 加工性优异的热浸Zn-Al-Mg系镀层钢板及其制造方法
US20150231726A1 (en) * 2014-02-19 2015-08-20 Nisshin Steel Co., Ltd. METHOD FOR PRODUCING ARC-WELDED Zn-Al-Mg ALLOY COATED STEEL PLATE STRUCTURAL MEMBER
KR101758529B1 (ko) * 2014-12-24 2017-07-17 주식회사 포스코 인산염 처리성과 스폿 용접성이 우수한 아연합금도금강판 및 그 제조방법
EP3561138B1 (en) 2014-12-24 2023-11-15 POSCO Co., Ltd Zinc alloy plated steel material having excellent weldability
JP6209175B2 (ja) * 2015-03-03 2017-10-04 日新製鋼株式会社 めっき表面外観およびバーリング性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板の製造方法
CA2979169C (en) 2015-04-08 2018-01-02 Nippon Steel & Sumitomo Metal Corporation Zn-al-mg coated steel sheet, and method of producing zn-al-mg coated steel sheet
JP6114785B2 (ja) * 2015-05-29 2017-04-12 日新製鋼株式会社 溶接部外観と溶接強度に優れた溶融Ｚｎ系めっき鋼板のアーク溶接方法、および溶接部材の製造方法
CN105256196A (zh) * 2015-10-23 2016-01-20 首钢总公司 一种铝锌镁镀层钢板及其制备方法
JP2017145441A (ja) * 2016-02-16 2017-08-24 日新製鋼株式会社 黒色表面被覆高強度鋼板およびその製造方法
KR101899674B1 (ko) * 2016-12-19 2018-09-17 주식회사 포스코 저온역 버링성이 우수한 고강도 강판 및 이의 제조방법
WO2018234839A1 (en) 2017-06-20 2018-12-27 Arcelormittal ZINC COATED STEEL SHEET HAVING HIGH STRENGTH POINTS WELDABILITY
KR102010079B1 (ko) 2017-09-13 2019-08-12 주식회사 포스코 도장 후 선영성이 우수한 강판 및 그 제조방법
KR102031465B1 (ko) * 2017-12-26 2019-10-11 주식회사 포스코 가공 후 내식성 우수한 아연합금도금강재 및 그 제조방법
KR102142766B1 (ko) 2018-08-31 2020-08-07 주식회사 포스코 내식성 및 가공성이 우수한 용융도금강판 및 이의 제조방법
KR102276742B1 (ko) 2018-11-28 2021-07-13 주식회사 포스코 도금 밀착성 및 내부식성이 우수한 아연도금강판 및 이의 제조방법
JP2021055135A (ja) * 2019-09-27 2021-04-08 日本製鉄株式会社 溶融Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
CN115103923A (zh) * 2020-02-13 2022-09-23 日本制铁株式会社 接合部件及其制造方法
CN112575275A (zh) * 2020-12-03 2021-03-30 攀钢集团研究院有限公司 高成形性的热浸镀锌铝镁合金镀层钢板及其制备方法
US11441039B2 (en) * 2020-12-18 2022-09-13 GM Global Technology Operations LLC High temperature coatings to mitigate weld cracking in resistance welding
CN115074576A (zh) * 2022-06-13 2022-09-20 首钢集团有限公司 一种锌铝镁合金锭、镀层、镀层钢及其制备方法

Family Cites Families (15)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP3392154B2 (ja) * 1991-03-29 2003-03-31 日新製鋼株式会社 耐火用高張力溶融Ｚｎ−Ａ１合金めっき鋼板の製造方法
JPH05263145A (ja) 1992-03-05 1993-10-12 Nippon Steel Corp バーリング性の優れた高強度合金化溶融亜鉛メッキ鋼板の製造方法
KR100257900B1 (ko) * 1995-03-23 2000-06-01 에모토 간지 인성이 우수한 저항복비 고강도 열연강판 및 그 제조방법
DE60143989D1 (de) * 2000-09-12 2011-03-17 Jfe Steel Corp Schmelztauchbeschichtetes stahlblech mit hoher zugfestigkeit und herstellungsverfahren hierfür
KR100486753B1 (ko) * 2000-10-31 2005-05-03 제이에프이 스틸 가부시키가이샤 고장력 열연강판 및 그 제조방법
JP3715220B2 (ja) * 2001-06-22 2005-11-09 日新製鋼株式会社 耐食性に優れたＺｎ−Ａｌ−Ｍｇ系溶融めっき鋼材
JP3821043B2 (ja) 2002-04-30 2006-09-13 Ｊｆｅスチール株式会社 溶接性に優れた溶融亜鉛系めっき高張力熱延鋼板ならびにその製造方法および加工方法
KR101019791B1 (ko) * 2002-12-24 2011-03-04 신닛뽄세이테쯔 카부시키카이샤 용접 열영향부의 내연화성과 버링성이 우수한 고강도 강판
JP4635525B2 (ja) * 2003-09-26 2011-02-23 Ｊｆｅスチール株式会社 深絞り性に優れた高強度鋼板およびその製造方法
JP4721221B2 (ja) * 2004-09-01 2011-07-13 日新製鋼株式会社 耐溶融金属脆化割れ性に優れたＺｎ−Ａｌ−Ｍｇ合金めっき鋼板
JP4776951B2 (ja) 2005-03-11 2011-09-21 新日本製鐵株式会社 溶接性に優れた溶接用亜鉛系合金めっき鋼材
KR100968013B1 (ko) * 2005-08-05 2010-07-07 제이에프이 스틸 가부시키가이샤 고장력강판 및 그 제조방법
JP5264235B2 (ja) * 2008-03-24 2013-08-14 日新製鋼株式会社 耐溶融金属脆化割れ性に優れた高降伏比型Ｚｎ−Ａｌ−Ｍｇ系めっき鋼板およびその製造方法
BRPI0822700A2 (pt) * 2008-05-15 2015-07-07 Siemens Vai Metals Technologies S A S Sistema e método para orientação de um dispositivo de secagem de um produto de galvanização
WO2010104086A1 (ja) * 2009-03-10 2010-09-16 日新製鋼株式会社 耐溶融金属脆化割れ性に優れた亜鉛系合金めっき鋼材

Also Published As

Publication number Publication date
US20130337287A1 (en) 2013-12-19
TR201903572T4 (tr) 2019-04-22
CN103415641A (zh) 2013-11-27
EP2682495A4 (en) 2016-03-16
KR102099588B1 (ko) 2020-04-10
ES2712631T3 (es) 2019-05-14
US9592772B2 (en) 2017-03-14
AU2012224032A1 (en) 2013-09-12
KR20140002740A (ko) 2014-01-08
EP2682495B1 (en) 2019-01-02
JP5936390B2 (ja) 2016-06-22
CA2826225C (en) 2020-07-21
JP2012193452A (ja) 2012-10-11
HUE043883T2 (hu) 2019-09-30
AU2012224032B2 (en) 2017-03-16
WO2012118073A1 (ja) 2012-09-07
EP3470541A1 (en) 2019-04-17
EP2682495A1 (en) 2014-01-08
CA2826225A1 (en) 2012-09-07
CN103415641B (zh) 2016-01-06

Similar Documents

Publication Publication Date Title
HUE043883T2 (hu) Zn-Al-Mg-alapú rendszerrel tûzi bevonatolt acéllemez, valamint eljárás annak gyártására
EP2896715A4 (en) COMPOSITE STRUCTURAL STEEL PLATE AND METHOD FOR THE PRODUCTION THEREOF
ZA201307377B (en) Steel sheet for hot-stamped member and method of production of same.
EP2765212A4 (en) HIGH-RESISTANCE STEEL PLATE AND MANUFACTURING METHOD THEREFOR
EP2799562A4 (en) HOT-ROLLED STEEL SHEET AND PROCESS FOR PRODUCING THE SAME
EP2881484A4 (en) COLD-ROLLED STEEL PLATE, MANUFACTURING METHOD AND HOT-COATED MOLDING BODY
ZA201402216B (en) Galvanized steel sheet and method of manufacturing the same
EP2631307A4 (en) STEEL PLATE AND MANUFACTURING METHOD FOR STEEL PLATE
EP2692452A4 (en) STAINLESS STEEL SHEET AND MANUFACTURING METHOD THEREOF
EP2799568A4 (en) FINE HIGH-STRENGTH STEEL SHEET AND MANUFACTURING METHOD THEREOF
PL2692895T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
IL231591A (en) Preserved benzyl indazoles, a process for their preparation and use
EP2843081A4 (en) METHOD FOR PRODUCING BLACK-PLATED STEEL SHEET, AND METHOD FOR PRODUCING BLACK-PLATED STEEL SHEET MOLDED ARTICLE
PL2982772T3 (pl) Wyrób formowany przez wytłaczanie na gorąco, blacha stalowa cienka walcowana na zimno i sposób wytwarzania wyrobu formowanego przez wytłaczanie na gorąco
EP2716783A4 (en) HOT-ROLLED STEEL SHEET AND PROCESS FOR PRODUCING THE SAME
PL2698444T3 (pl) Blacha stalowa walcowana na gorąco i sposób jej wytwarzania
EP2902520A4 (en) HOT ROLLED STEEL SHEET AND PROCESS FOR PRODUCING THE SAME
EP2684972A4 (en) STEEL PLATE FOR HOT IMPORTS, PRODUCTION METHOD THEREFOR, AND METHOD FOR PRODUCING HIGH-STRENGTH PARTS
ZA201307002B (en) Hot-rolled steel sheet and associated production method
EP2677054A4 (en) DUPLEX STAINLESS STEEL AND PROCESS FOR PRODUCTION THEREOF
PL2816132T3 (pl) Blacha stalowa cienka, blacha stalowa cienka powlekana galwanicznie, sposób wytwarzania blachy stalowej cienkiej oraz sposób wytwarzania blachy stalowej cienkiej powlekanej galwanicznie
EP2843082A4 (en) METHOD FOR PRODUCING A BLACK PLATED STEEL PLATE AND METHOD FOR PRODUCING A FORM BODY FROM BLACK PLATED STEEL PLATE
PL2818568T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
PL2818569T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
EP2770075A4 (en) ORIENTED ELECTROMAGNETIC STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME