OA16486A - Composite membranes for membrane distillation and related methods of manufacture. - Google Patents

Abstract

The present invention provides composite membranes for membrane distillation and related methods of manufacture. In particular, there is provided a composite hydrophilic/hydrophobic membrane comprising a hydrophilic polymer layer and a hydrophobic polymer layer comprising fluorinated surface-modifying macromolecules, wherein said composite membrane has a high vapour flux. There is also provided methods of manufacturing and optimizing the composite membranes and a membrane distillation system comprising the composite membranes.

Description

COMPOSITE MEMBRANES FOR MEMBRANE DISTILLATION AND RELATED METHODS OF MANUFACTURE

FIELD OF THE INVENTION [001] The présent invention pertains to the field of membranes for membrane distillation. More particularly, the présent invention pertains to the field of hydrophobic/hydrophilic composite membranes.

BACKGROUND OF THE INVENTION [002] Membrane distillation (MD) is a thermally driven séparation process that has been investigated widely for many applications including, but are not limited to, water desalination, food industry and removal ofvolatile organic compounds from water [1]. Many recent review articles hâve documented most of the research that was done in MD [1-6].

[003] The principle of MD is based on applying a thermal gradient between both sides of a porous hydrophobie membrane that acts as a physical support separating a hot feed solution from a cooling chamber containing either a Liquid or a gas depending on the used MD configuration. For instance, in direct contact membrane distillation (DCMD), a cold liquid solution is allowed to flow through the permeate side of the membrane in order to condense the vapour that has migrated through the membrane pores from the hot feed solution. Other MD configurations can be used to recover and condense the migrated vapour molécules: vacuum membrane distillation (VMD), sweeping gas membrane distillation (SGMD) and air gap membrane distillation (AGMD) [1-6].

[004] The main advantages of MD, compared to other desalination processes, are the high selectivity for non-volatile compounds (100% rétention of ions, macromolecules, colloids, etc.). In addition, it provides the possibility of working at low températures, which allows coupling to low-grade, waste or alternative energy sources [7]. In spite of those obvious advantages, MD process is not commercialized yet for large scale desalination plants. The reasons behind that are the relatively lower MD flux compared to the production of the well established commercialized desalination processes such as reverse osmosis and the membrane wetting which diminishes the durability of MD membranes. In other words, there is a lack of adequately designed MD membranes, which should hâve low conductive heat flux (i.e., low heat loss by conduction through the membrane matrix) and high mass flux in order to increase the membrane flux as well as small pore size to decrease the danger of membrane wetting.

[005] The membranes that hâve been used in MD are, generally, porous membranes made of hydrophobie material such as polypropylene (PP), poly(vinylidene fluoride) (PVDF) and polytetrafluoroethylene (PTFE), available in capillary or flat-sheet forms, although these membranes were marketed for microfiltration and ultrafiltration processes [6].

[006] Recently, in MD research, more attention has gone into preparing membranes specifically for the MD applications [7-19], The objective of the research was either to increase membrane durability or improve perméation flux. For example, Peng et al. [7] prepared composite fiat sheet MD membrane by casting a hydrophilic polymer on PVDF hydrophobie substrate. The membrane was tested by DCMD configuration and the results were compared to the PVDF uncoated substrate. The coated membrane durability was improved compared to the uncoated membrane; although the flux decreased by about 9% (a flux of 23.7 kg/m².h was achieved by the new membrane at feed and codant températures of 70°C and 12°C, respectively). Feng et al. [8] prepared asymmetric flat-sheet membranes from poly(vinylidene fluoride-co-tetrafluoroethylene) by the phase inversion method. Those membranes were tested by DCMD configuration and the results were compared to PVDF flat-sheet membranes prepared by the same procedure. Their new membranes exhibited higher flux than those of the PVDF membranes. They also prepared membranes from poly(vinylidene fluoride-co-hexafluoro propylene) [9] and found that the DCMD performance of these membranes was better than that of the PVDF membrane. Li and Sirkar [10] and Song et al. [11] designed novel hollow fiber membrane and device for desalination by VMD and DCMD. The membranes were commercial polypropylene (PP) membranes coated with plasma polymerized silicone fiuoropolymer. Permeate fluxes as high as 71 kg/m².h at 85°C feed température using VMD configuration were achieved. The same type of membranes was used for larger scale DCMD desalination device [12], Bonyadi and Chung [13] used the co-extrusion method to préparé dual layer hydrophilic/hydrophobic hollow fiber membranes for MD. PVDF was used as a host polymer in the spinning dope, where hydrophobie and hydrophilic surfactants were added. A flux as high as 55 kg/m².h at inlet feed and permeate températures of 90°C and 16.5°C, respectively, was achieved using DCMD configuration.

[007] In sériés of publications [15-19], the requirements of higher flux MD membranes were clearly identified. As a resuit, the concept of hydrophobic/hydrophilic composite membranes for MD was first presented by Khayet et al. [15,16]. It was shown that this type of membrane satisfies ail the requirements of higher flux MD membranes [16,17]. The hydrophobic/hydrophilic membrane was prepared by phase inversion method in a single casting step. A hydrophilic base polymer was blended with a hydrophobie surface modifying macromolecules (SMMs). During the casting step, the SMMs migrated to the air/polymer interface since they hâve lower surface energy [20]. Consequently, the membrane top-layer became hydrophobie while the bottom layer became hydrophilic. There remains a need for high flux membranes for use in MD.

[008] This background information is provided for the purpose of making known information believed by the applicant to be of possible relevance to the présent invention. No admission is necessarily intended, nor should be construed, that any of the preceding information constitutes prior art against the présent invention.

SUMMARY OF THE INVENTION [009] An object of the présent invention is to provide composite membranes for membrane distillation and related methods of manufacture that overcome the above-mentioned drawbacks.

[010] As a first aspect of the invention, there is provided a composite hydrophilic/hydrophobic membrane comprising a hydrophilic polymer layer, a hydrophobie polymer layer and fluorinated surface-modifying macromolecules (SMM). Preferably, the hydrophilic polymer layer is selected from the group consisting of polysulfone, polyether sulfone, polyetherimide, polyvinylidenfluoride and cellulose acetate. Preferably, the fluorinated surface-modifying macromolecules (SMM) consist of oligomeric fluoropolymers synthesized using polyuréthane chemistry and tailored with fluorinated end-groups. Preferably, the fluorinated SMM is blended with the hydrophilic polymer layer, and the SMM is selected from the group consisting of poly(urethane propylene glycol) and poly(urea dimethylsiloxane urethane).

[011] When the SMM is a poly(urethane propylene glycol), it is preferably prepared using a two step polymerization method comprising a first polymerization step to form a polyuréthane pre-polymer from 4,4’methylene bis(pheny)isocyanate) (MDI) and polypropylene glycol (PPG), and a second polymerization step to end-cap the polyuréthane pre-polymer by the addition of 2-(perfluoroalkyl)ethanol. In this case, the ratio of MDI:PPG:FAE is preferably about 3:2:2.

[012] When the SMM is a poly(urea dimethylsiloxane urethane), it is preferably prepared using a two step polymerization method comprising a first polymerization step to form a polyurea pre-polymer from 4,4’methylene bis(phenylisocyanate) (MDI) and α,ω- v\/

-316486

Aminopropyl poly(dimethyl siloxane) (PDMS), and a second polymerization step to end-cap the polyurea pre-polymer by the addition of 2-(perfluoroalkyl)ethanol (FAE). In this case, the ratio of MDI:PDMS:FAE is preferably about 2:1:2, about 3:2:2 or about 4:3:3.

[013] Preferably, the composite membrane has a flux and a morphology conceived to maximize the flux, where the morphology is preferably conceived by compiling mathematical parameters reflectmg various characteristics of the morphology.

[014] Preferably, the mathematical parameters comprise parameters representing a thickness, a porosity density and a thermal conductivity of the hydrophobie layer, and a thickness, a porosity density and a thermal conductivity of the hydrophilic layer.

[015] Preferably, the morphology is conceived in accordance with:

where fi reflects the morphology.

[016] Preferably, the composite membrane has a high vapour flux.

[017] As a second aspect of the invention, there is provided a membrane distillation System comprising a composite membrane as described hereinbefore.

[018] Preferably, the system is selected from the group consisting of a direct contact membrane distillation system, a vacuum membrane distillation system, a sweeping gas membrane distillation system and an air gap membrane distillation system.

[019] As a further aspect of the invention, there is provided a method of manufacturing a composite hydrophilic/hydrophobic membrane comprising a hydrophilic polymer layer and a hydrophobie polymer layer, the method comprising the steps of blending a host hydrophilic polymer with fluorinated surface-modifying macromolecules (SMM) and a non-solvent additive in a solvent, casting the hydrophilic polymer blend and allowing the solvent to evaporate at room température for a predetermined time, and immersing the cast film produced in step (b) in water to allow gélation.

[020] Preferably, the method of manufacturing a composite membrane further comprises maximizing porosity and minimizing thickness of the hydrophobie polymer layer of the composite membrane in order to increase flux of the composite membrane.

[021] Preferably, the method of manufacturing a composite membrane further comprises maximizing thickness, porosity and thermal conductivity of the hydrophilic polymer layer.

-416486 [022] Preferably, the host hydrophilic polymer comprises at least one of polysulfone, polyethersulfone, polytherimide polyvinylidenefluoride and cellulose acetate.

[023] Preferably, the SMM is selected from the group consisting of poly(urethane propylene glycol) and poly(urca dîmethylsiloxanc urethane).

[024] Preferably, the non-solvent additive is selected from the group consisting of γbutyrolactone and éthanol.

[025] Preferably, the solvent is selected from the group consisting of N,Ndimethylacetamide and 1 -methyl -2-pyrrolidinone.

[026] As a further further aspect of the présent invention, there is provided a method of optimizing the MD performance of a composite hydrophilic/hydrophobic membrane comprising a hydrophilic polymer layer and a hydrophobie polymer layer, the method comprising the steps of maximizing porosity of the top hydrophobie layer of the composite membrane, minimizing the thickness of the top hydrophobie layer of the composite membrane, and maximizing the thickness, the porosity and the thermal conductivity of the bottom hydrophilic layer.

-516486

BRIEF DESCRIPTION OF THE DRAWINGS [027] Further features and advantages of the présent invention will become apparent from the following detailed description, taken in combination with the appended drawings, in which:

[028] Figure 1 is a schematic of the DCMD mechanism of transport through a porous composite hydrophobic/hydrophilic membrane;

(029] Figure 2 shows the effect of polyetherimide concentration on both experimental and theoretical permeate flux at infinité stirring rate and bulk températures of 45 and 35°C;

[030] Figure 3 demonstrates the effect of increasing the hydrophilic sub-layer thickness on the DCMD flux of the hydrophobic/hydrophilic composite membrane ((a) Laboratory made membranes, (b) Commercial membranes);

[031] Figure 4 graphically depicts the effect of the hydrophobie top-Iayer porosity, e_h on the DCMD flux of the hydrophobic/hydrophilic membranes;

[032] Figure 5 graphically depicts the effect of hydrophilic sub-layer porosity, on the DCMD flux of the hydrophobic/hydrophilic membranes;

[033] Figure 6 graphically depicts the effect of the thermal conductivity of the hydrophilic sub-layer, k_Si on the DCMD flux of the composite hydrophobic/hydrophilic membranes;

[034] Figure 7 graphically depicts the effect of the thermal conductivity of the hydrophilic sub-layer on the DCMD flux of the composite hydrophobic/hydrophilic membranes at different boundary layers’ heat transfer coefficients;

[035] Figure 8 depicts the chemical structures of two prepared surface modifying macromolecules;

[036] Figure 9 shows SEM photographs of the cross-section of SMM/PEI membranes: (a) Ml; (b) M2; (c) M3; (d) M4; (e) M5; (f) M7;

[037] Figure 10 graphically depicts the effect of SMM type on SMM/PEI membrane performance in DCMD: (a) feed température effect on DCMD flux of dîstilled water feed solution; (b) water vapour flux of 0.5 M NaCI feed solution at 7)-of 65°C and T_p of 15°C;

[038] Figure 11 graphically depicts the effect of SMM concentration on SMM/PEI membrane performance in DCMD: (a) feed température effect on DCMD flux of distilled water feed solution; (b) water vapour flux of 0.5 M NaCI feed solution at 7/of 65°C and T_p of 15°C;

[039] Figure 12 graphically depicts the effect of solvent type on SMM/PEI membrane performance in DCMD: (a) feed température effect on DCMD flux of distilled water feed solution; (b) water vapour flux of 0.5 M NaCI feed solution at Tyof 65°C and T_p of 15°C; [040] Figure 13 graphically depicts the effect of évaporation time effect on SMM/PEI membrane performance in DCMD: (a) feed température effect on DCMD flux of distilled water feed solution; (b) water vapour flux of 0.5 M NaCI feed solution at 7/of 65°C and T_p of 15°C;

[041] Figure 14 is a schematic diagram of the gas perméation and liquid entry pressure of water tests setup;

[042] Figure 15 is a schematic diagram of the experimental DCMD set-up [16] used in Example 3;

[043] Figure 16 depicts SEM pictures of the cross-section of the prepared membranes: (a) Ml; (b) M2; (c) M3, (d) M4; (e) M5; (f) M6; (g) M7;

[044] Figure 17 graphically depicts the effect of SMM type on SMM/PS membrane performance in DCMD: (a) mean température effect on DCMD flux of distilled water feed at stirring rate of 500 rpm; (b) water vapour flux of 0.5 M NaCI feed solution at T_m of 45°C and stirring rate of 500 rpm;

[045] Figure 18 graphically depicts the effect of hydrophilic polymer concentration on SMM/PS membrane performance in DCMD: (a) mean température effect on DCMD flux of distilled water feed at stirring rate of 500 rpm; (b) water vapour flux of 0.5 M NaCI feed solution at T_ra of 45°C and stirring rate;

[046] Figure 19 graphically depicts the effect of solvent type on SMM/PS membrane performance in DCMD: (a) mean température effect on DCMD flux of distilled water feed at stirring rate of 500 rpm; (b) water vapour flux of 0.5 M NaCI feed solution at T_m of 45°C and stirring rate of 500 rpm;

[047] Figure 20 graphically depicts the effect of non-solvent concentration on SMM/PS membrane performance in DCMD: (a) mean température effect on DCMD flux of distilled water feed at stirring rate of 500 rpm; (b) water vapour flux of 0.5 M NaCI feed solution at Tm of 45°C and stirring rate of 500 rpm;

[048] Figure 21 depicts SEM pictures of the cross-section of nSMM2/PES and nSMM2/PEI membranes: (a) Ml; (b) M2;

[049] Figure 22 depicts AFM images of the top surface of nSMM2/PES and nSMM2/PEI membranes: (a) Ml; (b) M2;

[050] Figure 23 shows the probability density function gencrated for the pore size measured from the AFM images;

[051] Figure 24 graphically depicts the DCMD flux results of nSMM2/PES and nSMM2/PEI membranes: (a) mean température effect on DCMD flux of distilled water feed solution; (b) water vapour flux of 0.5 M NaCl feed solution at Tm of 45°C;

[052] Figure 25 depicts SEM pictures of the cross-section of the prepared membranes from Example 5: (a) Ml; (b) M2; and (c) M3; and [053] Figure 26 graphically depicts the effect of SMM type on membrane performance in

DCMD from Example 5; (a) feed température effect on DCMD flux of distilled water feed solution; (b) water vapour flux of 0.5 M NaCl feed solution at 7}-of 65°C and T_p of 15 °C. 0/

-816486

DETAILED DESCRIPTION OF THE INVENTION [054] Unless defined otherwise, ali technical and scientific terms used herein have the same meaning as commonÎy understood by one of ordinary skill in the art to which this invention belongs.

]055] As used in the spécification and daims, the singular forms “a”, “an” and the “the” include plural references unless the context clearly dictâtes otherwise. The term “comprising” as used herein will be understood to mean that the list following is nonOexhaustive and may or may not include any other additional suitable items, for example one or more further feature(s), component(s) and/or ingredient(s) as appropriate.

[056J In general, membranes for use in MD should allow a high flow rate. Further, a good porous membrane should be highly permeable, have low thermal conductivity, high liquid entry pressure of water (LEP_W\ which is the minimum pressure of water that must be applied onto pure water before water overcomes the hydrophobie forces of the membrane and pénétrâtes into the membrane pores), in addition it should have good thermal stability and excellent chemical résistance to feed streams.

[057] To provide the above characteristics, high flux membranes useful in MD should be designed to have a high hydrophobicity and relativeiy small pore sizes. However, while still being small, the membrane pores should be as large as possible in order to reduce barrier résistance. Further, the membranes should be as thin as possible, to minimize the barrier résistance to mass transfer, while being sufficiently thick to minimize température polarization by lowering the heat conductance of the membrane. The présent invention provides high flux composite membranes that are useful in MD and are designed to balance these requirements.

[058] As used herein, the term “flux” refers to the quantity of vapour crossing the hydrophobie layer of the composite membrane pores présent in a given membrane area during a period of time. The term “high flux” or “high vapour flux”, as used herein, refers to a flux of about 50 kg/m² h at 60°C feed température, or higher.

Composite Membranes:

[059] The composite membranes of the présent invention comprise a hydrophilic layer and a hydrophobie layer. The hydrophobie layer prevents water pénétration into its pores and is relativeiy thin, thereby minimizing résistance to mass transfer. The heat conductance of the composite membrane of the présent invention can be reduced through the use of a relativeiy thick hydrophilic sublayer.

[060] The composite membranes are prepared usîng fluorinated surface-modifying macromolecules (SMMs), which migrate to the air-film surface during membrane formation according to thermodynamic principles and form an amphipathic structure (hydrophobic/hydrophilic/hydrophobic). The SMMs used in the préparation of these membranes are oligomeric fluoropolymers synthesized using polyuréthane chemistry and tailored with fluorinated end-groups.

[061] The hydrophilic bulk membrane phase is prepared using a polymeric material that can be blended with the SMMs. Suitable polymers include, but are not limited to, polysulfone, polyether sulfone, polyetherimide polyvinylidenfluoride and cellulose acetate.

Manufacture of Composite Membranes [062] In accordance with an advantageous embodiment of the présent invention, the composite membranes of the présent invention are manufacture using a phase inversion method in which a host hydrophilic polymer is blended with the SMMs in a single casting step. Alternative methods can be used to préparé the composite membranes, however, SMM surface migration is critical to préparation of the membranes of the présent invention and the phase inversion method is the simplest and cheapest method currently known.

[063] Phase inversion is a process in which a polymer is transformed from a liquid to a solid state. There are a number of methods to achieve phase inversion. Among others, the dry-wet phase inversion technique and the température induced phase séparation (TIPS) are most commonly used in the industrial membrane manufacturing. The dry-wet phase inversion technique was applied by Loeb and Sourirajan in their development of the first cellulose acetate membrane for seawater desalination. Therefore, this method is often called the LoebSourirajan method.

[064] According to the Loeb-Sourirajan method, a polymer solution is prepared by mixing polymer, solvent and sometimes even nonsolvent. The solution is then cast on a suitable surface by a doctor blade to a thickness of about 250 μτη. After partial évaporation of the solvent, the cast film is immersed in a bath of nonsolvent medium, often called gélation medium. Due to a sequence of two desolvation steps, i.e., évaporation of solvent and solventnonsolvent exchange in the gélation bath, solidification of polymer film takes place. It is désirable to choose a solvent of strong dissolving power with high volatility. During the first step of desolvation by solvent évaporation, a thin skin layer of solid polymer is formed V instantly at the top of the cast film due to the loss of solvent. In the solvent-nonsolvent exchange process that follows, nonsolvent diffuses into, while solvent diffuses out of, the polymer solution film through the thin solid layer.

[065] At some point in the process, the content of solvent in the solution film becomes so low that the solvent no longer is able to hold polymer in one phase. Phase séparation takes place at this point, forming droplets of one liquid phase dispersed in the other continuons liquid phase. The point of phase séparation, and the size and the number of the dispersed droplets dépend on the nature of solvent and nonsolvent and the polymer solution composition. The control of the number and the size of the droplets will eventually control the structure of the porous substrate.

[066] The thin layer of solid polymer that forms during the first évaporation step becomes the top skin layer that will govem the selectivity and the flux of the membrane, while the porous structure that forms during the solvent-nonsolvent extraction step becomes the porous sublayer, providing the mechanical strength. Hence, the membrane obtained by the dry-wet phase inversion process is an întegrally skinned asymmetric membrane. The top skin layer can also be made porous by lowering the polymer concentration in the casting solution and the solvent évaporation period. This is called hereafter porous skin layer. Ultrafiltration membranes hâve a porous skin layer. The asymmetric membranes can also be made in tubular form using a casting bob assembly and hollow fibers can be spun using a hollow fiber spinneret.

Optimization of the Composite Membranes:

[067] The présent invention further provides a method of optimizing hydrophobic/hydrophilic composite membranes for MD. The method of optimization is usefiil in preparing membranes having a higher flux.

[068] A criterion parameter (fi) reflecting the hydrophobie top-layer and hydrophilic sublayer morphology was identified. It has been found that the criterion parameter (fi) should be lower than unity in order to improve the permeate flux by increasing the hydrophilic sublayer thickness while the total membrane thickness is kept constant. Consequently, with fi less than l, an increase in hydrophilic sub-layer thickness resulted in a dramatic increase in the calculated DCMD theoretical flux. Moreover, the theoretical flux increased with increasing both the hydrophobie and hydrophilic layers’ porosities, but it was more pronounced for the hydrophobie top-layer porosity. Further, it was surprisingly found that the

4116486

DCMD flux could be improved by an order of magnitude if the hydrophilic sub-layer’s thermal conductivity was 26 W/m.K when assuming an infinité stirring rate at both thermal boundary layers.

[069] Based on these fîndings, there is provided a method that makes use of the requîred characteristics of the hydrophobic/hydrophiiic composite membranes to improve their performance in MD, In particular, it has now been found that the following three criteria can be used to optimize a composite membrane:

- the porosity of the top hydrophobie layer as well as the bottom hydrophilic layer should be as high as possible;

- the thickness of the top hydrophobie layer should be as low as possible; and

- the thermal conductivity of the bottom hydrophilic layer should be as high as possible. [070] As a resuit, a composite membrane can be prepared with characteristics for improved MD performance using a method comprising the steps of:

1. maximizing porosity of the top hydrophobie layer of the composite membrane;

2. minimizing the thickness of the top hydrophobie layer of the composite membrane; and

3. maximizing the thickness, the porosity and the thermal conductivity of the bottom hydrophilic layer.

Application of the Composite Membranes:

[071] The composite membranes of the présent invention are particularly useful in membrane distillation.

[072J Under different MD configurations, the proposed composite membranes can be used for seawater desalination, wastewater treatment, food processing, concentration of pharmaceutical products, Volatile organic compounds (VOCs) removal from water, ethanol/water séparation etc.

[073] To gain a better understanding of the invention described herein, the following examples are set forth. It should be understood that these examples are for illustrative purposes only. Therefore, they should not limit the scope of this invention in any way.

EXAMPLE 1; Process for Optimizing Composite Membranes for Membrane Distillation [074) It is documented that 61% of MD studies included modeling as the basis for investi gating the MD process performance [6]. Most MD publications hâve focused on modeling the DCMD process since it is the most suitable configuration for desalination, which is the most common application of MD. DCMD modeling can be split into two domains: i) heat and mass transfer analysis of the process and ii) the effect of membrane characteristics. The studies of the first domain focused, mainly, on predicting the permeate flux, heat and mass transfer coefficients, heat and mass résistances and température and concentration polarization coefficients [4, 32, 36-40 and 42]. The other studies are related to the second domain and focused on the investigation of the effect of membrane characteristics such as membrane thickness, porosity and pore size distribution on the membrane performance [9,10,13-17,41 and 43-47].

[075] Commercial microporous hydrophobie membranes, available in capillary or flat-sheet forms, hâve been used in most MD research, El-Bourawi et al. [6] summarized most of the commercial membranes commonly used in MD processes together with some of their characteristics. Those membranes were mainly made of polypropyiene (PP), polyvinylidene fluoride (PVDF) and polytetrafluoroethylene (PTFE). It should be noted that ail those commercial membranes were marketed for microfiltration or ultrafiltration purposes, but hâve been used in MD because of their hydrophobicity and adéquate pore sizes. On the other hand, only a few authors hâve designed novel membranes and modules for MD [9,10,13-19, 44,45], [076] In recent publications [15-19 and 45], the use of hydrophobic/hydrophilic composite membranes for MD has been adopted. Higher flux MD membrane requirements were identified based on the physical understanding of the MD process. Consequently, a thinhydrophobic/thick-hydrophilic membrane approach was developed and experimentaily proven.

[077] The concept of composite hydrophobic/hydrophilic membrane is based on better understanding of the requirements for high flux MD membranes. Briefly, the concept dictâtes that a thinner hydrophobie layer combined with a thick hydrophilic sub-layer will increase the flux since the mass transfer résistance will decrease. On the other hand, the température polarization effect will decrease because of the thick hydrophilic sub-layer [21].

[078] The objective of the présent Example was to study the hydrophobic/hydrophilic composite membrane performance from a theoretical view point, in order to develop an understanding of the hydrophobic/hydrophilic composite membrane concept, to assist in the design of high flux hydrophobic/hydrophilic membranes for desalination by DCMD. A mathematical model describing the effects of both the hydrophobie top-layer and the hydrophilic sub-layer characteristics on the DCMD process performance was developed. Four different surface modifying macromolecules (SMMs) blended polyetherimide (PEI) membranes and two commercial PTFE membranes were considered [16 and 17]. Based on the model and investigations, the characteristics of the hydrophobie top-layer and the hydrophilic sub-layer of the composite hydrophobic/hydrophilic membrane, required for enhancement ofthe DCMD water vapour flux, were identified.

Experimental Data;

(079] Two commercial polytetrafluoroethylene membranes supported by a polypropylène net, TF200 (pore size 0.22 pm; 0.8 porosity) and TF450 (pore size 0.45 pm; 0.8 porosity) supplied by Gelman Company and four laboratory made hydrophobic/hydrophilic composite membranes (M12, M15, M17 and M20 [16]) were used in this study. The details of membrane préparation procedure are available elsewhere [16], Those membranes were named as M12, M15, M17 and M20 based on the variation of the polyetherimide (PEI, Ultem®1000, General Electric Company) concentration in the casting solution from 12 to 20 wt % maintaining the concentration of the surface modifying macromolecules (SMMs) at 2 wt. %.

[080] Ail membranes used in the présent study were characterized by the measurement of thickness, δ, advancing contact angle, θ_α, liquid entry pressure of water, LEP_W and gas perméation test. The gas perméation data were used to obtain the mean pore diameter, d_pt, the effective porosity of the hydrophobie top-layer, e/Lp [16 and 17]. The other surface (i.e., the hydrophilic layer) was investigated using Atomic Force Microscopy (AFM), which allows the détermination of data for the surface porosity of the porous hydrophilic sub-layer, and the roughness of both the top layer and sub-layer of the membranes. Details of the experimental procedures hâve been described previously [16 and 17].

[081] Table 1 shows the membrane characterization results for both the commercial and the laboratory made membranes. These results are used in this study to discuss the effect of the hydrophobic/hydrophilic layers characteristics on the DCMD performance of the composite membranes,

Table 1: Membrane thickness (<5), advancing contact angle of the top surface (0_fl), liquid entry pressure of water (LEP/), mean pore size (d_Pil), effective porosity of the hydrophobie top-layer (c/Lp), surface porosity of hydrophobie top-layer (¾). surface porosity of hydrophilic sub-layer (fj), and mean roughness, R_m, of the SMM/PEI membranes (M12, Ml5, M17 and M20) and the commercial PTFE membranes (TF200, TF450).

'“e | ÛÎ o	Top: 42.9 |	; Bottom: 73.8	Top: 38.6 |	Bottom: 90.4	| Top: 31.2 |	Bottom: 66.2	| Top: 28.0 |	Bottom: 72.4	t t	a 1 1 f 1
	m		o	d	d	Ό
	7.6	m 'O	4.3	5.2	ch en	0.8
					en	en
		CM	d	1—4	oo	un
- /*>	CM	KO	OO	un		KO
G sp	Ch	1—4 CM	24.	d	43.	44
	d	oc		M*		d
		o	OO	Ch	·—d	o
	rn		d	un	00	OK
	d		o	un	d	en
d	1—4	m		00
CO		Tt	Tt	d	d
									KO	d
		KO		Ό	Ch	00
C 'g'	00	t	un	d	00	00
. «i H	ri	O\	un	d	ch	1—4
^3 ·Ο·	n	#—4			1—1
¢0
s 0-
		o	m	oo	KO	Ch
S Ξ		d	r—<	en	d	M-
q o	en	't	•O	ko	d
		m				Ch		Ό
		ΜΊ		\o		un
		00		00		oo		00	KO	en
	d		d		«n				en	00
	d	fi	ko	fi	d	r<	un	f
	Ch	σ.	o.	G	Q.	R	»—4	4—4
	o		o		o	g		, *,
	ü	ts	ô.	tJ	ü	ç	eu	Q.
	O	o	o	o	o	o	o	o	,o	O
	H	«	H	m	H	m	H	m	H	H
	d	i—4	m	<n	^4	d
	σ.	d	m	d	00	o
	ô	d	Tf		M·’	o
un	Un	un	wn	«n	KO
i?
« ©s
J—« M £ flu CL·	n		d	o
		Ψ—4	d
ω S									M
X>									o	o
e	d	un	d	o	o CM	m ^1*
s	•—4 s	Ml	^-4 S			s	Üu H

Theoretical Approach:

[082] The System studied consisted of a composite hydrophobic/hydrophilic membrane maintained between hot pure water, named hereafter the feed side, and cold pure water, the permeate side. The hydrophobie side of the membrane was brought into contact with the hot feed water, while the hydrophilic-layer of the membrane was maintained in contact with cold water which penetrated into the pores of the hydrophilic-layer. On the other hand, the pores of the hydrophobic-layer are maintained dry unless the applied transmembrane pressure exceeds the liquid entry pressure of water (LEPw) of the membrane. At this point, lîquid/vapour interfaces are formed at both ends of the pores of the hydrophobie layer, as shown in Figure 1.

[083] The température drop established across the hydrophobic-layer créâtes a vapour pressure différence, which is the driving force in DCMD process. In this case, évaporation takes place at the hot feed side and after water vapour is transported through the pores of the hydrophobic-layer, condensation takes place at the vapour/liquid interface formed at the boundary between the hydrophobie and the hydrophilic layers.

[084] In the system described above, both mass and heat transfers occur simultaneously across the membrane. Consequently, the températures at the membrane surfaces differ from those at the bulk liquid phases, leading to a decrease of the driving force and réduction of the DCMD flux (i.e. température polarization effect).

Heat transfer t [085] The following heat transfer flux is involved in the DCMD system as described previously:

[086] Through the feed solution boundary layer:

Q_f = h_f(T_bf -T_mf) ...

Through the hydrophobie top layer:

Q_t=Wf

Through the hydrophilic sub-layer:

Q_t=hAT„_tP-T_JiP)

Through the permeate solution boundary layer:

(2) (3)

- 1646486

8_Ρ W» (4)

At steady state, the overall heat transfer flux through the whole DCMD system, Q, is givenby

Q=Q_/=Q_i=Q,=Q_P (5) [087] In the above équations, h is the heat transfer coefficient, is the permeate flux, ΔΗ_ν is the latent heat of vaporization and T is the absolute température. The subscripts specifying the location of the température, b, f, p, m and s refer to the bulk solution, feed, permeate, hydrophobie top-layer of the membrane and its hydrophilic sub-layer, respectively.

[088] Therefore, from the above équations, the heat flux can be written as follows:

(6)

As a resuit the overall heat transfer coefficient (ί/) for the DCMD process may be written as:

(7) i

--1--r . rr--<---~' h, _hA K *,

[089] The heat transfer coefficients, hf and h_p can be estimated with the help of the known empirical corrélations of the dimensionless numbers and the correction factor used to express the température dependence of the water viscosity.

(8)

Where Nu, Re, and Pr are Nusselt, Reynolds and Prandtl numbers, respectively; a, b, c and d are characteristics constants of the liquid flow régime; pt, and μ™ are the water dynamic viscosity at the bulk and at the corresponding side of the membrane, respectively [16 and 17].

-17”16486 [090] The heat transfer coefficient of the hydrophilîc sub-layer, h_s, can be calculated from the thermal conductivities of the hydrophilîc membrane polymer (k_s) and water in the pores (U

(9) where & and % are the thickness and porosity of the hydrophilic-layer of the composite membrane, respectively.

[091[ The heat transfer coefficient of the hydrophobie top-layer, ht, can be calculated from the thermal conductivities of the hydrophobie membrane polymer (k_t) and the gas présent inside the pores (k_g).

k'_t k^+kfll-sj (10) where St and E_t are the thickness and porosity of the hydrophobie top-layer of the composite membrane, respectively.

Mass Transfer;

[092] In DCMD process, the permeate flux of liquid water, can be related to the transmembrane liquid pressure as follows [6,8,11,21,25]:

Λ - - Pm.p) (Π) where Pmj- and p^p are the partial pressures of water at the feed and permeate calculated at the températures T_m/and Τ„_ιΡ> respectively; and B„ is the net DCMD membrane permeability. [093] The vapour pressures within the membrane are not dïrectly measurable. Therefore, it would be more convenient to express Eq. (11) in terms of températures. For the small transmembrane bulk température différences Tb,_p 10 K) used in this study, the following expression can be used as indicated by Schofield et al. [6].

J.

(12)

Where K’ is defined as

-18(13) where T_m is the mean température, (Tbj- + Tb,_p)f2, and (dp/dT) can be evaluated from the Clausius-Clapeyron équation together with Antoine équation used to calculate the vapour pressure of water [l ,21 ].

3841 ' ^-45, (14) [094] Various types of mechanisms hâve been proposed for the vapeurs transport in DCMD: Knudsen mechanism, molecular diffusion mechanism, and/or the combination thereof [l], The goveming quantity that provides a guideline in determîning which mechanism is operative under a gîven experimental condition is the Knudsen number, Kn, defined as the ratio of the mean free path (Â) of the transported molécules to the membrane pore size (i.e. Kn = Md_pff [095] Accordingly, the membrane permeability (5_m) can be evaluated depending on the flow mechanism as follows

- Knudsen mechanism * 3 τ,δ₍ RT ) (15) where sj, r_h r_Pit, δ are the porosity, pore tortuosity, pore size and thickness of the membrane hydrophobic-layer, respectively; M is the molecular weight of water, R is the gas constant and T is the absolute température.

- Molecular diffusion mechanism

B^d - ^ε' ^{PD M} t,δ, P_a RT (16) where P_a is the air pressure, P is the total pressure inside the pore which is assumed constant and equal to the sum of the partial pressures of air and water vapor, and D is the water diffusion coefficient. The value of PD (Pa m²/s) for water-air can be calculated from the following expression [8].

PD = 1.895 10'^s T^tm

- Combined Knudsen/ordinary-diffusion mechanism (17)

08) rfi, ( π ΡΤΊ'” ! τ,δ, P_a RT J ^{+ ε}. ^{PD M}

Mathematical model describing the effect of the hydrophobic/hydrophilic composite membrane characteristics on the permeate flux:

[096] It is very important to develop a valid mathematical model for the hydrophobic/hydrophilic membrane for membrane distillation (MD), which will provide a guideline for the future development of highly efficient MD membranes. The model will allow us to optimize the different parameters that affect the performance of hydrophobic/hydrophilic membranes.

[097] As a resuit of the performed heat transfer analysis, Eq. (2) can be rewritten as:

Substituting Q in Eq. (19) with UÇhj- Tf,,_p) and rearranging:

V (19) (20) δ,

Substituting the water vapour flux (Λ) in Eq. (20) with Eq. (12):

(21)

Substituting (T*/- T„_tP) in Eq. (21) with Eq. (12) and rearranging, the water vapour flux can be expressed as:

(22) [098J If infinité stirring rate is assumed at both feed and permeate solutions, the heat transfer coefficients of the boundary layers become infinity. When the overall heat transfer coefficient and vapour flux that correspond to the infinité heat transfer coefficients are given as U_v and J® , respectively, Eq. (7) becomes:

1

-2016486 (24)

By substituting h_s, h_t and Λ, in Eq. (23) with appropriate expressions:

λ-¹

1 k', , K'Aff, ⁺ k', l^r ⁵t ^δ _ί)

From Eqs. (22) and (24), the following équation can be obtained:

“H

K'

JZ

K.f ~^Tb.p i i kl Κ'ΔΗ„ ⁺ Jt; A ^δ. ^δ,.

k' + K'AH_r (25)

Further rearrangement of Eq. (25) yields,

fl»

H¹

J

k'_t +Κ'ΔΗ_ν k'_tK'

(26)

When a constant value of ô is assumed for the total thickness of the hydrophobic/hydrophilic composite membrane, δ,=δ-δ,

Substituting S_t of Eq. (26) with Eq. (27):

J: ⁺ k'_t

Further rearrangement of Eq. (28) yields:

• ~ ¢+^(/, -i) where (27) (28) (29) k'_t+K'AH_r k’

(30)

Substituting and K' in Eq. (30) with Eqs. (9), (10) and (13), respectively, one can obtain the foilowing expression for/ :

(31)

Accordingly, fi reflects only the morphology of the hydrophobie top-layer and the hydrophilic sub-layer (i.e. r_Pilt $) and their thermal conductivities.

Resuit and Discussion:

Theoretical validation of the hydrophobic/hydrophilic membrane concept :

[099] Equation (29) shows that if the quantity fi_t given by Eq. (31), is smaller than 1, an increase in the hydrophilic sub-layer thickness, ô_s, will enhance the DCMD flux through the composite hydrophobic/hydrophilic membrane, . Otherwise, the DCMD flux will exhibit a decreasing trend when the hydrophilic sub-layer thickness is increased. Since f₍ is obviously a positive value, the criteria for the increase of J* with an increase of £ is, O^/^l (32) [0100] This is not unexpected since having the quantity/ lower than one means an increase in either the hydrophilic sub-layer porosity or thermal conductivity and/or an increase in the hydrophobie top-layer porosity, which will eventually decrease the barrier résistance to the mass flux through the membrane.

[0101] It should be noted that the numerical value of Ô, has absoiutely no effect on fi, even though it appears in Eq. (31), since Ô_t in Eq. (31) is cancelled by ô_t that appears in the denominator of B_m according to Eqs. (15), (16) and (18). Morcover, the change of the hydrophobie material will hâve only little effect on fi because most of the hydrophobie polymers hâve similar thermal conductivities [26].

[0102] In order to validate the physical concept of hydrophobic/hydrophilic membrane by using the presented DCMD model équations, simulation was made for DCMD configuration using water as feed. The DCMD flux was calculated for different thicknesses of the hydrophilic sub-layer, <5,, while maîntaining the total thickness δ = 60 pm. The DCMD

-2216486 >

operating conditions were assumed to be the same as those used in the earlîer publication [6], 45°C for the bulk feed température (Tf) and 35 °C for the bulk permeate température (7λ._ρ)· In addition, infinité stirring rates were assumed on both the feed and permeate membrane sides. On the other hand, as it is indicated in [21], the permeate flux was measured at 5 different stirring rates and extrapolation to an infinité stirring rate was carried out.

[0103] Table 2 shows ail the necessary membrane parameters requîred for the calculation. The membrane characterization parameters such as the porosities (ε₍) and (ç,) and the pore diameter (d_Pit) were obtained from gas perméation tests and atomic force microscopy as reported in [21], It is found that both porosities and pore diameters are substantially larger for 10 the commercial membranes. k_s values were calculated from Eq. (9), k_t value was set equal to

0.032 W/m.K as reported in earlier paper [21] and K values were calculated by Eqs. (13) to (18). In addition to the above membrane characterization parameters the following numerical t « f values were used for the calculation of A,, k, andK,

Table 2: Mass transfer mechanism and the estimated values of k'_ltk'_lt K' and the function f_it for both the laboratory made membranes (Ml 2, M15, M17 and M20) and the commercial membranes (TF200 and TF450).

Membrane	PEI (wt%)	a;° (W/m.K)	K (W/m.K)	Kn	Mass Transfer Mechanism	K’ (10'9kg/m.s.K)	ft
M12	12	0.032	0.218	6.02	Knudsen Model	2.82	0.176
M15	15	0.032	0.211	7.08	Knudsen Model	2.52	0.179
M17	17	0.032	0.201	8.88	Knudsen Model	2.30	0.185
M20	20	0.032	0.2056	11.23	Knudsen Model	1.58	0.173
TF200	0.1432	0.29907	0.69	Transition Région Model	20.97	0.637
TF450	0.15	0.2835	0.33	Transition Région Model	27.6	0.749

^a Values for M12 to M20 were taken from Khayet et al. [17].

[0104] The value 2405.55 kJ/kg was used for the latent heat of vaporization (AH_V), 0.0269 W/m.K was used for the gas thermal conductivity (A_x), 0.626 W/m.K was used for the water thermal conductivity (kf, 0.25 W/m.K was used for the SMMs thermal conductivity (AJ, which was considered to be equal to the thermal conductivity of PTFE. The thermal conductivity (A,) of PEI and PP was 0.1297 W/m.K and 0.135 W/m.K, respectively.

[0105] It should be noted that k_s values are higher for the commercial membranes than for the laboratory made membranes. This is because of the larger porosity of the commercial membranes. It must be pointed out that K’ values are an order of magnitude higher for the commercial membranes. This is because of the smaller pore diameters and lower porosities of the hydrophobie S MM layers of the laboratory membranes compared to the commercial membranes.

[0106] Table 2 also shows that the mass transfer of water vapour through the pores of the hydrophobie top-layer is govemed by the Knudsen mechanism for the laboratory-made membranes. On the other hand, the transition mechanism is the prevailing mechanism in the case of the commercial membranes. This was determined b y evaluating Knudsen number (Kn). The mean free path, Â, was estimated under the given operating conditions as 137.7 nm. [0107] The calculated fi values that are also shown m Table 2 satisfy the condition given by Eq. (32) for both the laboratory made membranes and the commercial membranes.

[0108] The agreement of the model calculation by Eq. (29) with the experimental results was examined. The experimental values corresponding to the infinité stirring rate were obtained by extrapolation as mentioned earlier [21], Figure 2 shows the theoretical and experimental flux values for the different PEI concentrations. Agreement is reasonable, showing the validity of the model. The flux decreases as the PEI concentration increases due to the decrease in the average pore diameter [0109] In Fig. 3 it is noticed that the DCMD flux increases with an increase in the hydrophilic sub-layer thickness (J,), or a decrease in the hydrophobie layer thickness (<5J. It can be also seen that the effect of on the DCMD flux (Λ) is stronger for the laboratory prepared membranes (M12-M20) than for the commercial membranes (TF200 and TF 450). This is because of the smaller fi values for the laboratory made membranes.

Discussion on the improvement of the laboratory made membranes:

1. Hydrophobie layer porosity

-2416486 [0110] Increase in the hydrophobie layer porosity will obviously hâve a positive effect on the DCMD flux for the following two reasons.

a) - It will increase the coefficient B_m according to Eqs. (15), (16) and (17) and consequently JC in Eq. (29).

b) - Jt, will decrease according to Eq. (10) because of the low value of Âg compared to k_t. However, this effect is currently ignored because of the very low value of k_t, which is 0.032 W/m K as stated earlier.

[OUI] To know the effect of the porosity of the hydrophobie top-layer, calculation was made by increasing the hydrophobie layer porosity from 0.2 to 0.6 while the other parameters were maintained constant as follows: d_pt = 17.53 nm; e_s = 0.1587, δ = 52.3 pm and δ_$ = 47.07 pm (i.e. 90% of the total composite membrane thickness as stated elsewhere [22]).

[0112] It should be noted that d_Pit and e_s are the average of the four laboratory made membranes (SMMs blended PEI membranes). The results of the calculation are given in Fig.

4. As it is shown, the DCMD flux increases as the porosity of the top hydrophobie layer increases. The DCMD flux was tripled when the hydrophobie top layer porosity was increased from 0.2 to 0.6. Therefore, this should be incorporated in the design of novel high flux DCMD membranes.

[0113] Physically, the increase of the hydrophobie top-layer porosity will increase the permeate flux because of two reasons: (i) the air entrapped within the membrane pores has lower thermal conductivity than the polymeric material of the membrane and (fl) the available surface area for évaporation is increased.

2. Hydrophilic layer porosity [0114] Increase of the hydrophilic sub-layer porosity will cause an increase in DCMD flux since k₃ will increase according to Eq. (9) because of the higher value of k_w than k_s. This will decrease thejÇ value as indicated by Eq. (30) leading to an increase of the DCMD flux. The calculation was made by increasing the hydrophilic sub-layer porosity from 0.1 to 0.6 while the other parameters were maintained constant as follows: d_Pil = 17.53 nm, e₍ = 0.2197, δ = 52.3 pm and δ₃ = 47.07 pm.

[0115] It should be noted that the values of d_{p l} and e_f are the average values of the laboratory prepared membranes. The results of the calculation are given in Fig 5. As expected, Figure 5 shows the increase of the DCMD flux with the increase of the hydrophilic sub-layer porosity, e,. More specifically, increasing the hydrophilic sub-layer porosity from 0.1 to 0.6 causes a DCMD flux increase by 60%. Therefore, this should also be considered in the composite hydrophobic/hydrophilic membrane design.

[0116] It must be pointed out that the DCMD flux through the composite hydrophobic/hydrophilic membranes is more sensitive to the increase of the hydrophobie toplayer porosity than the increase of the hydrophilic sub-layer porosity.

[0117] 3. Thermal conductivity of the hydrophilic sub-layer

The increase of the thermal conductivity of the hydrophilic sub-layer material (PEI in the présent study, k_t) will increase the thermal conductivity of the whole hydrophilic layer (Ai’) as stated in Eq. (9). This will decrease fi (see Eq. (30)) and increase the DCMD flux as may be expected from Eq. (29).

[0118] The theoretical calculation was made considering the laboratory made membranes (M12, M15, Ml 7 and M20). The results of the calculation are shown in Fig. 6. As expected, the DCMD flux increases considerably with an increase in k_s, approaching an asymptotïc value for each membrane. This is due to the fact that the thermal conductivity of the hydrophilic sub-layer, Ai, results in a dramatîc decrease of the f value. If one can decrease this value (/j) until it approaches zéro the permeate flux will be many times larger than any known MD flux.

[0119] Figure 6 also shows that the DCMD flux may approach 90 kg/m2.h at the given operating conditions, when the hydrophilic/hydrophobic membrane is properly designed and the température polarization can be removed. A hydrophilic sub-layer thermal conductivity of 26 W/m K is enough to achieve the maximum attainable flux.

[0120] From Fig. 6, it can be concluded that the hydrophilic sub-layer thermal conductivity should be as high as possible. The reason is that the température gradient across the hydrophobie layer (in Fig. 1) becomes steeper with an increase in the thermal conductivity of the hydrophilic layer, as a resuit, the température polarization defined as indicated in Eq. (33) also increases.

Tr—τ ppfj_ ~ T -T

W ^tb._P Ç33) [0121] It is worth mentioning that the thermal conductivity of polymers does not reach the desired value. It is recommended to choose material that has a thermal conductivity far greater than those ofpolymers.

-2616486 [0122] 4. Stirring rate effect on the optimal thermal conductivity

Finite heat transfer coefficients would be doser to reality of practical applications. For this case, combination of Eqs. (7), (22) and (30) yields:

(34)

Where hf and h_p are the heat transfer coefficients of the boundary layers on the feed and permeate side, respectively. Further assuming hf = h_p = h, Eq. (34) is rewritten as:

K (35) [0123] Simulation was conducted for various heat transfer coefficients ranging from 5000 to 50 000 W/m².K, while maintaining ail other parameters the same as those used in section 4.2.3. Membrane M12 was specifically chosen for the simulation. The results are shown in Fig. 7. It is obvious that the simulated flux values are far lower than those achieved for infinité heat transfer coefficient, although the flux increases as heat conductivity (fe) increases. The effect of the increasing fe value becomes more pronounced as h increases. For example an increase of fe from 0.13 to 26 W/m.K improved the permeate flux by 53.2% and 334.1% for the h value of 5 000 W/m².K and 50 000 W7m².K, respectively. Another observation that can be obtainaed from Fig.7 is that the flux value levels off more quickly, meaning at the lower fe value, as the heat transfer coefficient decreases.

Conclusions [0124] As set out above a new set of mathematical équations were derived to describe the performance of hydrophobic/hydrophilic composite membranes. A parameter fi reflecting the morphology of the hydrophobie top-layer and the hydrophilic sub-layer (i.e. the surface porosity, e_t, and the mean pore radius, r_Piti of the hydrophobie top-layer, and the surface porosity of the hydrophilic sub-layer, $) has been defined. It has been shown that the parameter fi should be lower than unïty în order to increase the MD flux when the hydrophillic sub-layer thickness is decreased. Otherwise, it will lead to a decrease in the MD flux. Simulation using the proposed mathematical model showed that the increase in the porosities of both hydrophobie top-layer and hydrophilic sub-layer will increase the MD flux. Moreover, the increase of the thermal conductivity of the hydrophilic sub-layer will increase the MD flux reaching asymptotic values at about 26 W/m.K of the hydrophilic-layer thermal conductivity.

Nomenclature

Symbols a Characteristic constant for empirical corrélation (Eq. 8)

B_m net DCMD permeability (kg m² s'¹ Pa'¹) mean pore size of the hydrophobie top-layer (nm) *7 1

D water diffusion coefficient (m s ) fi factor defined in Eq. (30) h heat transfer coefficient (W m‘² K'¹)

J_w DCMD flux (kg m'² h¹)

J® DCMD flux at infinité stirring rate (kg m² h'¹) k thermal conductivity (W m'¹ K'¹) k_t top-layer thermal conductivity (W m’¹ K'¹) k_s sub-layer thermal conductivity (W m* K' )

K membrane permeability (kg m'¹ s'¹ K⁴)

Kn Knudsen number

LEPw liquid entiy pressure of water (Pa)

M molecular weight of water (kg kmol⁴)

Nu Nusselt number p Partial vapour pressure of water (Pa)

P total pressure (Pa)

P_a air pressure (Pa)

Pr Prandtl number

Q heat flux (W m’²)

T absolute température (K)

T_m absolute mean température (K) r_p,_t mean pore radius of the hydrophobie top-layer (nm)

R gas constant (J mol⁴ K⁴)

Re Reynolds number

U Overall heat transfer coefficient (W m’² K⁴)

-2816486

U* Overall heat transfer coefficient at infinité stirring rate (W m'² K'¹)

Greek letters δ total membrane thickness (pm) (¾ hydrophilic sub-layer thickness (pm) δ hydrophobie top-layer thickness (pm) ε porosity (%) ε/τ effective porosity (%) λ mean free path (nm) μ water dynamic viscosity (kg m'¹ s'¹)

Θ water contact angle (°) τ pore tortuosity

ΔΗ_ν latent heat of vaporization (kJ/kg)

Subscripts a advancing contact angle b bulk f feed g gas m membrane mf hydrophobie surface of the membrane at the feed side

m.p interface hydrophobic/hydrophilic of the membrane p pore s hydrophilic sub-layer

s.p hydrophobie surface of the membrane at the permeate side t hydrophobie top-layer w water

Superscripts b Characteristic constant for empirical corrélation (Eq. 8) c Characteristic constant for empirical corrélation (Eq. 8) d Characteristic constant for empirical corrélation (Eq. 8)

-2916486

K Knudsen

D molecular-diffusion

C combined Knudsen/ordinary-diffusion

EXAMPLE 2: Préparation and Characterization of Hydrophobic/Hydrophilic

Polyetherimide Composite Membranes for Desalination bv Direct Contact.Membrane

Distillation [0125] The objective of this Example is to identify and discuss the effects of hydrophobic/hydrophilic membrane préparation conditions on the membrane morphology and desalination DCMD performance of these membranes. The membrane performance was related to the membrane morphology as well as to the membrane préparation factors such as, SMMs type, SMMs concentration, évaporation time and solvent type. Two different types of SMMs were synthesized and characterized. Polyetherimide (PEI) was used as the host hydrophilic polymer. Different membranes were prepared and characterized using the gas perméation test, the measurement of the liquid entry pressure of water (LEP_w)_t the scanning électron microscopy (SEM), the contact angle (CA) and the X-ray photoelectron spectroscopy (XPS) analysis. Finally, ail the membranes were tested by DCMD with feed distilled water and 0.5 M NaCl solution. The results were compared to those of the commercial PTFE membrane (FGLP 1425, Millipore Corporation USA). The prepared membranes seem promising for practical application in desalination by DCMD.

Experimental

Materials [0126] Ail chcmicals used in this work and their chemîcal abstract service (CAS) number are enhsted in Table 3. The weight average molecular weight (À/_w) of the polyetherimide (PEI) is 15 kDa and its glass transition température (T_g) is 216.8 °C. The commercial membrane used is polytetrafluoroethylene, PTFE, (FGLP 1425) having a porosity of 0.70 and a nominal pore size of 0.25 pm supplied by the Millipore Corporation, Billerica, MA, USA.

-3016486

Table 3. Materials Employed in this Example

Material description	CAS number	Source
4,4'-Methylene bis(phenyl isocyanate) (MDI, 98%)	101-68-8	Sigma-Aldrich, Inc., St. Louis, MO, USA
Poly(propylene glycol) (PPG, typical Mn 425 Dalton)	25322-69-4	Aldrich Chemical Company Inc., Milwaukee, WI, USA
α,ω-Aminopropyl poly(dimethyl siloxane) (PDMS) of average molecular weight 900	106214-84-0	Shin-Etsu Chemical Co. Ltd., Tokyo,Japan
Zonyl fluorotelomer intermediate, 2(Perfluoroalkyl)ethanol, (FAE, BA-L of average Mn 443 and 70 wt% fluorine	678-39-7	DuPont product supplied by Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Ν,Ν-Dimethylacetamide (DMAc, anhydrous 99.8%)	127-19-5	Sigma-Aldrich, Inc., St. Louis, MO, USA
l-Methyl-2-pyirolidinone (NMP, anhydrous 99.5%)	112-14-1	Sigma-Aldrich, Inc., St. Louis, MO, USA
γ-Butyrolactone (GBL, 99+%)	96-48-0	Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Tetrahydrofuran (THF, HPLC grade 99.9%)	109-99-9	Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Polyetherimide (PEI, Ultem 1000, Naturel Pallet) Spécifie gravity: 1,27	61128-46-9	General Electric Co., Pittsfield, MA, USA

SMMs synthesis [0127] The SMMs were synthesized using a two-step solution polymerization method [22 and 23]. The solvent À/jV-dimethylacetamide (DMAc) was distilled at about 25°C under a pressure of 133.3 Pa (1.0 Torr). Methylene bis(p-phenyl isocyanate) (diphenylmethane diisocyanate, MDI) was also distilled at 150°C under 66.7 Pa (0.5 Torr). Polypropylène glycol (PPG), α,ω-aminopropyl poly(dimethyl siloxane) (PDMS) and 2(perfluoroalkyl)ethanol (FAE) were degassed for 24 h under 66.7 Pa. The first polymerization step was conducted in a solution with a predetermined composition to form polyuréthane for the reaction of MDI with PPG or polyurea for the reaction of MDI with PDMS as a prepolymer. In the second polymerization step, the pre-polymer was end-capped by the addition of FAE, resulting in a solution of SMM. The composition of SMMs are: MDI:PPG:FAE = 3:2:2 or MDI:PDMS:FAE = 3:2:2. The prepared SMMs are named hereafter as PUP and

-31 16486

PUDU based on their chemical structure, which is shown in Figure 8 (i.e., goly(urethane propylene glycol), PUP and poly(urea dimethylsiloxane urethane), PUDU, both ends capped byFAE.

SMMs characterization [0128] The elemental analysis of fluorine content in the two prepared SMMs was carried out using standard method in ASTM D3761. An accurate weight (10-50 mg) of sample was placed into oxygen flask bomb combustion (Oxygen Bomb Calorimeter, Gallenkamp). After pyro-hydrolysis, the fluorine (ion) was measured by an ion chromatography (Ion Chromatograph, Dionex DX1000).

[0129] The glass transition température (T_g) was examined by differential scanning calorimeter (DSC) equipped with universal analysis 2000 program (DSC Q1000, TA Instruments, New Castle, DE). About 10 mg of polymer was crimped into aluminum pan. The SMMs were annealed at 280 °C for 10 min, then quenched to -50 °C and scanned at a heating rate of 10 °C/min. The T_g value was recorded at the midpoint of the corresponding heat capacity transition.

[0130] The weight average molecular weight (M_w) and the number average molecular weight (Àf_n) of the synthesized SMMs were measured by gel perméation chromatography (GPC) using Waters Associâtes GPC chromatograph equipped with Waters 410 refractive index detector. Three Waters UltraStyragel™ packed columns were installed in sériés. The tetrahydrofuran (THF) was filtered and used at 40 °C and a flow rate of 0.3 ml/min. First, the calibration of the system was performed using polystyrène (Shodex, Tokyo, Japan) standards with different molecular weights between 1.3xlO^J and 3.15xl0⁶ g/mol. The standards and SMM samples were prepared in a THF aqueous solution (0.2 w/v %) and filtered prior to injection through 0.45 pm filter to remove high molecular weight components. Millenium 32 software (Waters) was used for data acquisition.

Membrane Préparation [0131] SMM modified PEI membranes were prepared in a single casting step by the phase inversion method [25,27 and 36]. y-Butyrolactone (GBL) was used as a non-solvent additive. A predetermined amount of PEI was dissolved in a DMAc/GBL or a NMP/GBL mixture. The PEI concentration in the casting solution was maintained at 12 wt%, while the amount of GBL was maintained at 10 wt%. Two different types of SMMs, PUP and PUDU, were added to the PEI solution in different concentrations in a range of 0.5-2 wt%. The resulting mixtures were stirred in an orbital shaker at room température for at least 48 h. Prior to their use, ail the resulting polymer solutions were filtered through a 0.5 pm Teflon® filter and degassed at room température. The polymer solutions were cast on a smooth glass plate to a thickness of 0.30 mm using a casting rod at room température. The solvent was then evaporated at ambient température for a predetermined period before the cast films together with the glass plates were immersed for 1 h in distilled water at room température. During gélation, it was observed that the membranes peeled off from the glass plate spontaneously. Ail the membranes were then dried at ambient conditions for 3 days. Table 4 shows the prepared membranes, their materials of construction and préparation conditions.

Table 4. Membrane préparation details: Casting solution composition and préparation conditions

T. Membrane code	SMMtype	Solvent	SMM concentration (wt%)	Evaporation time (min)
MO	-	NMP	0	0
Ml	PUP	NMP	1.5	0
M2	PUDU	NMP	1.5	0
M3	PUP	NMP	1.0	0
M4	PUP	NMP	2.0	0
M5	PUDU	DMAc	1.5	0
M6	PUDU	NMP	1.5	2
M7	PUDU	NMP	1.5	4

* PEI concentration: 12 wt%; GBL concentration: 10 wt%; solvent: 78 wt%; gélation bath température: 20°C.

Membrane Characterization

1. Measurement of Gas Perméation test and Liquid Entry Pressure of Water (LEP_W) [0132] Measurement of liquid entry pressure of water (LEP_W) and the gas perméation test were carried out for the prepared surface modified PEI membranes. The gas perméation test was performed prior to the measurement of LEP_W. Figure 14 shows a schematic diagram of the testing setup. The effective area of the membrane was 9.6 cm². First, the equipment was made ready for the gas perméation test by filling the pressure vessel with nitrogen at a pressure of 5 bars. Then the stainless steel membrane holder inlet valve was opened and the inlet nitrogen pressure was controlled by the help of the pressure gauge. The flux of the nitrogen flowing from the bottom of the membrane was measured by air flow meter.

[0133] In the présent study, the perméation flux of nitrogen through each dry membrane was measured at various transmembrane pressures, in the range of 10-100 kPa. In general, the gas permeance, B, for a porous medium contains both a diffiisive term and a viscous term, the contribution of which dépends on the applied pressure as reported by Carman [24]:

3\xMRT) L_p fytRT L_p

where R is the gas constant, T is the absolute température, M is the molecular weight of the gas, μ is the gas viscosity, P„ is the mean pressure within the membrane pore, r is the membrane pore radius, fis the porosity, and L_p is the effective pore length.

[0134] Throughout ail the conducted gas perméation experiments, it was noticed that the gas permeance was independent of pressure, which means that the gas permeance is independent of P_m. Therefore, diffiisive mechanism seems to dominate the gas transport through the membrane pores revealing the fact that the prepared membranes in this study have small pore sizes. Accordingly, the gas permeance will be described after omitting the viscous term of Eq. (34) as [16 and 17]:

ί=4—Γ3\jMRT) L_p (35) [0135] This test was therefore useful in evaluating the pore size/effective porosity ratio (rfÆp). Some of the gas perméation experiments were duplicated using different membrane sheets made from the same casting solution batch in order to evaluate the variance of the obtained value from batch to batch. Moreover, for each membrane, the measurement of the gas flow rate was made three times at a given gas pressure and the obtained values were averaged to obtain the membrane permeance value.

[0136] The equipment was then made ready for the measurement of the LEPw; the pressure vessel was filled with 2L of water. Then, pressure was applied from the nitrogen cylinder on water. The pressure was increased by 0.1 bar each time until the water penetrated through the membrane and left the filtration cell. As soon as the water started to flow, pressure was recorded and this was considered as the liquid entry pressure of water (LEPw) for that membrane. The experiment was done three times using three different sheets made from the casting solution batches. The results were averaged to obtain the LEPw.

-3416486

2. Scanning Electron Microscopy (SEM) [0137] The cross-section of the SMMs blended PEI membranes was analyzed by scanning électron microscopy, SEM, (JSM-6400 JEOL, Japon). The membranes were eut into pièces (3 mm width and 10 mm length) and subsequently immersed in liquid nitrogen réservoir for 5 s. While keeping the pièces in the liquid nitrogen, those were broken into two pièces by pulling from both ends. One of the broken pièces was mounted on métal plate with carbon paste and gold-coated prior to use. The cross-section of the membranes at the broken parts was final ly examined by SEM.

3. X-ray Photoelectron Spectroscopy (XPS) [0138] The elemental composition at the surface of each SMM blended membrane was determined by X-ray photoelectron spectroscopy (XPS, Kratos Axis HS X-ray photoelectron

A spectrometer, Manchester, UK). Each membrane was eut into samples of 1 cm from random positions of the membrane. Monochromatized Al Ko X-radiation was used for excitation and a 180° hemispherical analyzer with a three channel detector was employed. The X-ray gun was operated at 15 kV and 20 mA. The pressure in the analyzer chamber was 1.33x1 θ’⁴ to 1.33x10'⁵ Pa. The size of the analyzed area was about 1 mm². Ail the membrane samples were analyzed for fluorine content at both top and bottom sides.

4. Measurement of Contact Angle (CA) [0139] The contact angle (CA) of the SMMs blended membranes was measured to study their hydro-phobicity /-philicity. The CA measurements were executed using the VCAOptima (AST products, Inc., MA, USA). Samples of 4 cm² area (2 x 2 cm) at random positions were prepared from each membrane. The samples were then placed on the glass sample plate and fixed with scotch tape. The equipment syringe filled with distilled water was installed to stand vertically. Two microlitres of water were deposited on the membrane surface. The CA was measured at five different spots on each membrane sample for both top and bottom surfaces.

DCMD Experiments [0140] The prepared SMMs blended PEI membranes were tested by the DCMD setup shown in a previous study [36]. The performance of each membrane was compared to that of the.-yx/— commercial PTFE membrane in terms of water vapour flux and NaCl séparation factor. The membrane modules are a system of three circular stainless steel cells each composed of two cylindrical chambers. Each cell has an O-ring to prevent water leakage, one inlet and one outlet at the feed side and one inlet and one outlet at the permeate side, respectively. The diameter of each cell is approximately 10 cm, which results in a total effective area (of three cells), of 235.6 cm². Each cell has two supportive compartments with a thickness of 2.5 to 3 cm. The feed chamber is connected to a heating system through its jacket to control the température of the liquid feed. The permeate chamber is connected to a cooling system to control the température of the permeate side stream. The membranes were placed between the two chambers (feed side and permeate side). The feed and permeate flow rate were held constant at 2 l/min for each cell (the total flow rate was 6 1/min). The inlet and outlet températures of both the feed and permeate solutions were measured, after steady state was reached, using thermocouples connected to a digital meter with an accuracy of ± 0.05°C. The MD module cells together with ail tubes were insulated to prevent heat loss. The permeate flux was measured by monitoring the water level in both the feed and permeate cylindrical graduated containers. The loss in the amount of water in the feed container should be equal to the gain in the amount of water in the permeate container when there is no leakage of water in the DCMD setup.

[0141] Different sets of DCMD experiments were carried using as a feed distilled water and 0.5 M NaCl aqueous solution. When distilled water was used as feed, the feed température was varied from 35 to 65°C, while the permeate température was maintained at 11-15°C. When 0.5 M NaCl solution was used as feed, the feed température was 65°C and the permeate température was 15°C.

Results and Discussion

Charactcrizatîon of SMMs and SMMs blended PEI membranes [0142] The values of T_g. M_w and M_n for the SMMs (PUP and PUDU) are given in Table 3. The précisé T_g value could not be obtained for the PUDU as the sample was heated up to 280 °C due to the limitation of higher température of the equipment. According to the SMMs chemical composition presented in Fig. 8, the value of m, number of repeat unit of CF2, was calculated from the molecular weight of 2-(perfluoroalkyl)ethanol (FAE) to be 7.58. The values of the n, number of repeat unit of propylene glycol, and y, number of repeat unit of dim ethyl siloxane, were calculated from the average molecular weight of PPG and of PDMS to be 7.02 and 9.81, respectively. The value of q, number of repeat unit of urethane or urea was calculated from the weight averaged molecular weight of each SMM to be 50.60 and

22.58 for PUP and PUDU, respectively.

SMM type	F (wt%)	T, (°C)	Mh-(10* g/mol)	M„ (10* g/ mol)
PUP	11.45	19.35	3.61	1.09
PUDU	11.75	>280	2.71	1.28

[0143] The contact angle (CA) data of ail membranes are shown in Table 6. It was observed that the CA of the top side of the prepared membranes was higher than that of the bottom side. The higher CA of the membrane M2 compared to that of the membrane Ml prepared 10 under the same conditions except the SMMs type indicates that the hydrophobicity of the

SMMs PUDU is greater than that of PUP. As expected from the SMMs concentrations, the CA of the blended membranes using PUP follows the order: M4 > Ml > M3. These results were observed for other SMMs membranes prepared with other host polymers [13 and 31].

Table 6. Top and bottom contact angles (CA) of the prepared membranes.

Membrane	CA(#°)
MO	Top: 80.04 ±4.55
Bottom: 72.83 ± 2.62
Ml	Top: 89.31 ±3.91
Bottom: 78.69 ±2.80
M2	Top: 91.93 ±0.52
Bottom: 67.76 ±3.29
M3	Top: 88.36 ±2.59
Bottom: 64.99 ± 4.43
M4	Top: 96.28 ±2.72
Bottom: 80.03 ±4.45
M5	Top: 100.6 ±3.18
Bottom: 74.4 ±4.17
M6	Top: 104 ±4.57

-3716486

Membrane	CA(0°)
	Bottom: 80.4 ± 4.30
M7	Top: 121.2 + 3.21
Bottom: 78.1 ± 4.04

[0144] With an increase in solvent évaporation time, the CA of the membranes follows the order: M7 > M6 > M5, which is also expected since the SMMs migrate more with the increased évaporation time. This resuit was also observed previously for other SMMs blended membranes [13,25,45 and 50], [0145] The results of the XPS analysis for both PEI and SMMs blended PEI membranes are presented in Table 7. Fluorine was not detected in the PEI membrane. This is expected since fluorine is associated to SMMs. For ail the SMMs blended PEI membranes, fluorine contents of the top side membranes were found to be higher than those of the bottom side indicating SMMs migration towards the top-layer of the membranes. For the same SMMs concentration, 10 the PUDU blended PEI membrane (M2) exhibits more fluorine than the PUP blended PEI membrane (Ml). This is related to the fluorine concentration, which is higher for PUDU compared to PUP, as indicated in Table 5. It must be pointed out here that when the PUP concentration was varied in the PEI polymer casting solution, the CA of the corresponding membranes (M3, Ml and M2) together with the fluorine content increased with increasing 15 the SMM concentration as shown in Tables 6 and 7, respectîvely. This resuit was also observed previously for other SMMs blended membranes [13,25, 45 and 50].

Table 7. XPS results of some of the prepared membranes for both top and bottom sides.

Membrane	F (mass conc., %)
MO	Top: 0.00
Bottom: 0.00
Ml	Top: 23.70
Bottom: 0.21
M2	Top: 28.93
Bottom: 7.68
M3	Top: 9.16
Bottom: 2.05
M4	Top: 27.17
Bottom: 7.07

[0146] The SEM images of the membranes cross-section are shown in Figure 9. As can be seen, ail the membranes are of asymmetric structure with finger-like structure at the top surface, whereas the structure of the bottom surface varies depending on the SMMs type, SMMs concentration, solvent type and solvent évaporation time.

[0147J The data for the LEP_W and (τε/Lp) are summarized in Table 8. This data is discussed below together with the DCMD data.

Table 8. Liquid entry pressure of water (LEP„) and product of average pore size and effective porosity per unit effective pore length (erÆ_p) of the laboratory prepared membranes.

Membrane	LEPW (bar)	er/Lp
Ml	3.7	7.09 10s
M2	4.0	1.53 10s
M3	5.2	5.48 ÎO'7
M4	4.9	6.03 10“*
M5	5.1	1.10 ίο·*
M6	4.7	3.84 10*6
M7	5.5	4.20 10'7

Membrane performance

1. SMMs type effect [0148] Ml (PUP) and M2 (PUDU) membranes were chosen to compare the SMM type effects on the morphology and DCMD performance (see Table 4 for membrane préparation conditions). Figure 10 shows the DCMD fluxes of the above membranes along with those of the commercial membrane (FGLP 1425). Figure 10a shows the DCMD flux versus feed inlet température when distilled water was used as feed. Figure 10b shows the DCMD flux of the same membranes when using 0.5M NaCI aqueous solution as feed. As can be observed, both the commercial membrane and the SMMs blended PEI membranes exhibit an exponential increase of the DCMD flux with an increase in the feed inlet température. Both Fig. 10a and 10b show that the order in the DCMD flux is Ml > M2 > FGLP 1425. The prepared SMMs blended PEI membranes showed higher permeate fluxes than the commercial membrane, and the PUP blended membrane (Ml) is superior to PUDU blended PEI membranes for DCMD application. In particular, the DCMD flux of the membrane Ml was found to be 55 % higher than that of the commercial membrane. λ/

-3916486 [0149] The permeate flux when using NaCl aqueous solution as feed was 25 to 30 % lower than that obtained when distilled water was used as feed, reflecting the lower vapour pressure of the sait solution. Another reason for the decrease in the DCMD flux is the concentration polarization due to the presence of NaCl soluté in the feed membrane side [16]. Referring to the experiments with sait solution, the soluté séparation factor is defined as:

100 (36) where C_p and Cy are the NaCl concentration in the permeate and in the bulk feed solution, respectively. It was observed that a was above 99 % for the three tested membranes. This indicates that the SMMs blended membranes Ml and M2 are promising MD membranes as reported in previous studies [16-18]. On the other hand, the membrane MO, prepared without blending SMMs, did not show any sait rejection capacity, indicating that SMMs blending is essential for preparing MD membranes.

[0150] According to Table 6 and 7 the CA and fluorine content are both higher for M2 membrane surface than Ml membrane surface. Therefore, M2 membrane is more hydrophobie than Ml membrane. Moreover, Table 8 shows that Ml membrane’s LEP_V value is smaller than that of the membrane M2, indicating that either Ml membrane is more hydrophilic and/or Ml membrane has a larger maximum pore size than M2 membrane, according to the Laplace équation [24]. Both cases can be applied since Ml membrane is more hydrophilic and has larger value of the ratio (zr/Lp) than the membrane M2. It can be therefore conciuded that the membrane exhibiting higher ratio (et/L_p) will hâve higher DCMD flux. This is not unexpected since an increase in the ratio (zr/Lp) means an increase in either the porosity and/or pore radius or a decrease in effective pore length. Considering that the value of the ratio (zr/L_p) was obtained from the gas perméation experiments, a parallel relationship was found between the gas transport and vapour transport.

[0151] SEM pi ctures of the cross-section of the two different SMM/PEI membranes are presented in Figure 9a and Figure 9b. Both images show an asymmetric membrane structure with a dense top-layer supported by a finger-like structure undemeath. However, the bottom parts of both membranes are quite different. The finger-like structure of the membrane M2 (Fig. 9b) reached the bottom side, where it formed large and fully developed macro-voids. On the other hand, at the bottom of the Ml membrane (Fig. 9a) a sponge like structure was

-4016486 formed together with large macro-voids. The higher permeate flux of membranes exhibiting sponge-like structure than that of membranes having finger-like structure was documented [20]. Therefore higher flux of sponge-like Ml membrane than finger-like M2 membrane seems naturel. However, this interprétation is ignoring the contribution of the top skin layer to the DCMD mass transport. In fact, it is the skin layer that is controlling the overall membrane transport. While not wishing to be bound by theory, it is thought that the porous sub-layer only provides mechanical support. The above observation (of the relationship between the structure of the sub-layer and the DCMD flux) suggests that the porous sub-layer also is contributing to the membrane transport as liquid water pénétrâtes inside its void-space,

2. SMMs concentration effect [0152] MO (0 wt%), M3 (1.0 wt%), Ml (1.5 wt%) and M4 (2.0 wt%) membranes were chosen to study the effect of the SMM concentration (see Table 4). Figure 11 shows the DCMD fluxes of the above membranes along with those of the commercial membrane (FGLP 1425). Figure lia shows DCMD flux versus feed inlet température from the DCMD experiments with distilled water as feed. Figure 11b shows the performance of the membranes for DCMD with 0.5 M aqueous NaCl solution as feed. The data for MO membrane was not included since it failed to act as MD membrane. For ail other membranes the séparation factor, a, was found to be more than 99 %. h Figure lia DCMD flux increases exponentially with the feed température, similar to Figure 10a.

[0153J Comparing the permeate flux data, Ml membranes showed the best performance among the tested membranes, despite the fact that M4 and M3 showed flux enhancement by 40 and 20 %, respectively, compared to the commercial membrane.

[0154] According to Table 8, the increasing order in LEP_W values was; Ml (3.7 bar) < M4 (4.9 bar) < M3 (5.2 bar), indicating that Ml membrane has the largest maximum pore size according to Laplace équation [24] and/or less hydrophobie (i.e., smaller top-layer CA). The decreasing in o7L_p values was, on the other hand, Ml (7.09 x ΙΟ'⁵) > M4 (6.03 x ΙΟ^-6) > M3 (5.48 x 10'⁷). This trend validâtes the conclusion that the membranes with higher a-/L_p values exhibit higher fluxes.

[0155] The surface fluorine contents of the membranes are shown in Table 7. The observed order is M3 (9.16 %) < Ml (23.70 %) < M4 (27.17 %), which shows that the fluorine content of the top surface of the membrane increases with an increase in the SMM concentration. The CAs are M3 (88.4°) < Ml (89.3°) < M4 (96.3°), confirming the highest hydrophobicity of M4 membrane.

[0156] SEM pictures of the cross-section of the M3 and M4 membranes are presented in Figures 9c and 97d respectively (see Figure 9a for Ml membrane cross-section structure). Generally, the structures are very similar, consisting of a bottom layer of fully developed macro-pores with a sponge-like structure, an intermediate layer with fînger-like structure and a skin layer on the top. Hence, the PUP concentration in the dope did not affect the membrane structure, while affecting the cr/L_p value. The latter parameter reflects the structure of the skin layer, the detailed structure of which can not be observed by SEM.

[0157] Another important thing is that ail the above membranes exhibited higher fluxes than PTFE commercial membrane (FGLP 1425), regardless the SMM concentration. This is probably due to the sponge-like structure, which seems favourable for higher flux membranes in MD and to the smaller thickness of the top hydrophobie layer as reported in previous studies [16 and 17].

3. Solvent type effect [01581 M2 (NMP) and M5 (DMAc) were chosen for the comparison of SMM/PE1 membranes prepared with different solvents. Other membrane préparation parameters were kept unchanged (see Table 4). Figure 12 shows the DCMD fluxes of the above membranes along with those of the commercial membrane (FGLP 1425). Figure 12a shows the permeate DCMD flux versus feed inlet température from the DCMD experiments with distilled water as feed. Figure 12b shows the performance of the membranes for DCMD with 0.5 M aqueous NaCl solution as feed. For both M2 and M5 membranes the séparation factor, a, was found to be more than 99 %. Again in Figure 12a the DCMD flux of ail tested membranes increases exponentially with the feed température, similar to Figure 10a.

[0159] The M2 membrane exhibited higher fluxes than M5 membrane (and the commercial membrane). The flux increased by around 11 % from M5 membrane to M2 membrane. M2 membrane showed lower LEPw than the M5 membrane indicating that M2 membrane may hâve larger maximum pore size according to Laplace équation [24] or M5 membrane is more hydrophobie. In fact, CA of M5 membrane (100.6°) is higher than that of M2 membrane (91.93°). Moreover, the order of the effective porosity/pore size ratio (£rÆ_p) order was: M2 > M5, which further validâtes our earlier conclusion that the membrane with higher (er/Ζ,ρ) exhibits higher DCMD flux.

[0160] The SEM cross-sectional picture of M5 membrane is shown in Figure 9e, while that of M2 is presented in Figure 97b. Both membranes consist of a bottom layer of fully faA developed macro-pores with a finger-like structure, an intermediate layer of finger-like structure, and a skin layer on the top. However, the macro-pores of M5 membrane are smaller. This could further explain the higher flux of M5 compared to that of M2 membrane.

4. Evaporation time effect [0161} The effect of the évaporation time was studied by M2 (0 min), M6 (2 min) and M7 (4 min) membranes, while keeping the other membrane préparation parameters unchanged (see Table 4). Figure 13 shows the DCMD fluxes of the above membranes along with those of the commercial membrane (FGLP 1425). Figure 13a shows DCMD flux versus feed inlet température from the DCMD experiments with dîstilled water as feed. Figure 13b shows the performance of the membranes for DCMD with 0.5 M aqueous NaCl solution as feed. For ail the above membranes the séparation factor, a, was found to be more than 99 %. In Figure 13a, for ail tested membranes the DCMD flux increases exponentially with the feed température, similar to the trends shown in previous Figures. The permeate flux decreased dramatically from M2 to M7 membranes, in other words with an increase in the évaporation time. More specifically, the DCMD flux decreased by 60 % and 85 % for the évaporation time of two minutes (M6) and four minutes (M7), respectively, from zéro évaporation time (M2).

[0162] Comparing LEP_W values, the increasing order is M2 (4.0 bar) < M6 (4.7 bar) < M7 (5.5 bar), indicating that the membrane M2 has the largest maximum pore size according to Laplace équation [24] and/or the lowest CA. The observed increasing order in the CA is M2 (91.93) < M6 (104°) < M7 (121.2°) (see Table 7). As the évaporation time increases the hydrophobicity of the membrane surface increases. Suk et al. [23 and 25] studied the effect of évaporation time on SMM migration toward the top-layer and similar behaviour was obtained. As for er/L_p values, the observed decreasing order is M2 > M6 > M7. This trend as well validâtes the conclusion that membranes with higher sr/L_p will exhibit higher permeate DCMD flux. The DCMD experiments presented in this Example indicate that no time is necessary to make the membrane surface sufficiently hydrophobie to be used for MD.

[0163] SEM picture of the cross-section of M7 membrane is presented in Figure 9f, while that of M2 membrane is presented in Figure 9b. Both membranes consist of a bottom layer of fully developed macro-voids with a finger-like structure, an intermediate layer with fingerlike structure, and a skin layer on the top. The size and number of macro-voids decreased with an increase in the évaporation time and the sponge-like structure between macro-voids 4/^ became thicker. The macro-voids were almost totally eliminated when the évaporation time was 4 minutes. This also may explain the dramatic decrease in DCMD flux with évaporation time increase. It must be pointed out that a thicker sponge-like structure was maintained in the membrane M7. Hence, it is supposed to hâve a high permeate flux. Despite that, this membrane exhibited a permeate flux lower than that of the membrane M2 prepared without évaporation time. This also means that sr/L_p value that govems the DCMD flux is not a property of the porous sub-layer, but a property of the top skin layer.

Conclusions [0164] This Example provides means for improving the performance of the composite hydrophobic/hydrophilic PEI membranes in MD. This was achieved through studying the effect of different membrane préparation parameters such as SMMs type, SMMs concentration, Solvent type and évaporation time before gélation.

[0165] A better and instructive understanding of hydrophobic/hydrophilic membranes performance in MD has been obtained by findïng the relationship between the membrane morphology and its performance in MD. The linkage between the membrane characteristics and the membrane performance was cohérent. It was verified that the top skin layer (the hydrophobie layer) characteristics highly influence the DCMD flux. Those characteristics are mainly the liquid. entry pressure of water and the product of average pore size and effective porosity per unit effective pore length (rs/L_p). Moreover it was shown that the cross-sectional structure of the membrane played a rôle in enhancing the DCMD flux in such a way that the membranes with sponge-like structure and/or larger macro-voids at the bottom layer (the hydrophilic layer) exhibited higher fluxes. Among the tested membrane préparation conditions, it was found that the membranes with PUP based SMMs are better than those with PUDU based SMMs, NMP was better solvent for membrane préparation than DMAc, membranes prepared with no évaporation time exhibited higher permeate fluxes than those of évaporation time before gélation and, finally, membranes with 1.5 wt% SMMs produced higher permeate fluxes than the membranes prepared with other different SMMs concentrations. Ail of these valuable findings were explained via the above presented understanding.

[0166] Generally, most of the SMMs modified PEI membranes exhibited higher permeate fluxes than those obtained using the commercial PTFE membrane, although the SMMs modified PEI membranes bave considerably lower pore size and porosity. Moreover, the v-/ séparation factor was found to be higher than 99% for ail the tested membranes. It was proved that the SMMs are necessary to produce workable membranes in MD.

EXAMPLE 3: Préparation and Characterization of Hydrophobic/Hydrophilic Polysulfone Composite Membranes for Desalination by Direct Contact Membrane Distillation [0167] The objective of this Example wass to introduce polysulfone (PS), which is widely used in preparing reverse osmosis (RO), ultrafiltration (UF) and microfiltration (MF) membranes [21], as a possible membrane material for manufacturing membrane distillation membranes for the first time. To this end; hydrophobic/hydrophilic membranes were prepared by the phase inversion method using PS as the host hydrophilic polymer, whereas the hydrophobie layer was formed via the migration of the hydrophobie SMM toward the air/polymer interface while the SMM blended polysulfone dope was cast into a film. Moreover, this Example identifies and discusses the effects of hydrophobic/hydrophilic membrane préparation conditions on the membrane morphology and desalination DCMD performance of the prepared membranes. The membrane performance was related to the membrane morphology as well as to the membrane préparation factors such as, SMM type, PS concentration, non-solvent concentration and solvent type. Three different types of SMMs were synthesized, characterized and blended to PS for membrane préparation. Membranes so prepared were characterized using the gas penneation test, the measurement of the liquid entry pressure of water (LEPw), the scanning électron microscopy (SEM), and the contact angle (CA) measurement. Finally, ail the membranes were tested by DCMD with feed distilled water and 0.5 M NaCl solution. The results were compared to those of the commercial PTFE membrane (FGLP 1425, Millipore Corporation USA). The prepared membranes are usefol in desalination by DCMD.

Experimental

Mate riais [0168] Ail chemicals used in this work and their chemical abstract service (CAS) number are enlisted in Table 7.1. The average molecular weight of the polysulfone (PS) is 79000 g/mol and its glass transition température (T_g) is 185°C. The commercial membrane used is polytetrafluoroethylene, PTFE, (FGLP 1425) having a porosity of 0.70 and a nominal pore size of 0.25 pm supplied by Millipore Corporation, Billerica, MA, USA.

Table 9. Materials Used in this Example

-4516486

Material description	CAS number	Source
4,4-Methylene bis(phenyl isocyanate) (MDI, 98%)	101-68-8	Sigma-Aldrich, Inc., St. Louis, MO, USA
α,ω-Aminopropyl poly(dimethyl siloxane) (PDMS) of average molecular weight 900	106214-84-0	Shin-Etsu Chemical Co. Ltd., Tokyo, Japan
Zonyl BA-L™ (BAL) of average Mn 443 and 70 wt% fluorine	678-39-7	DuPont product supplied by Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Æ.V-Dimethylacetamide (DMAc, anhydrous 99.8%)	127-19-5	Sigma-Aldrich, Inc., St Louis, MO, USA
l-Methyl-2-pyrrolidinone (NMP, anhydrous 99.5%)	112-14-1	Sigma-Aldrich, Inc., St. Louis, MO, USA
Ethanol (anhydrous, 99+%)	64-17-5	Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Tetrahydrofiiran (THF, HPLC grade 99.9%)	109-99-9	Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Polysulfone (PS, UDEL™ 3500) Spécifie gravity: 1.24	25154-01-2	Solvay Advanced Polymer, LLC, Alpharetta, Georgia, USA

SMMs synthesis [0169] The SMMs were synthesîzed using the two-step solution polymerization method described above [22 and 23]. In this example, the first polymerization step was conducted in a solution of a predetermined composition to form polyurea by the reaction of MDI with PDMS as a pre-polymer. In the second polymerization step, the pre-polymer was end-capped by the addition of FAE, resulting in a solution of SMM having the PUDU structure shown in Figure 6.

[0170] The composition of SMMs were altered such that the ratio of MDI:PDMS:FAE was (i) 2:1:2, (ii) 3:2:2 and (iii) 4:3:3. The prepared SMMs are named hereafter as nSMMl, nSMM2 and nSMM3, respectively, based on the PDMS stoichiometirc number.

SMMs charactcrization [0171] The elemental analysis of fluorine content in the three prepared SMMs was carried W—

-4616486 out using standard method in ASTM D3761. An accurate weight (10-50 mg) of sample was placed into oxygen flask bomb combustion (Oxygen Bomb Calorimeter, Gallenkamp). After pyro-hydrolysis, the fluorine (ion) was measured by an ion chromatography (Ion Chromatograph, Dionex DX1000).

[0172] The glass transition température (T_g) of synthesized SMMs were examined by differential scanning calorimeter and the weight average molecular weight of the synthesized SMMs was measured by gel perméation chromatography (GPC) as described above in Example 2.

Membrane préparation [0173] SMM modified PS membranes were prepared in a single casting step by the phase inversion method [15-16]. Ethanol was used as a non-solvent additive. A predetermined amount of PS was dissolved in a NMP/ethanol or a DMAc/ethanol mixture. The PS concentration in the casting solution was varied in a range of 10-14 wt%, two different éthanol concentrations were used; 10 and 20 wt %. Three different types of SMMs, nSMMl, nSMM2 and nSMM3 were added to the PS solution with a maintained concentration of 1.5 wt%. The resulting mixtures were stirred in an orbital shaker at room température for at least 48 h prior to their use. The resulting polymer solutions were filtered through a 0.5 pm Teflon® filter and degassed at room température. The polymer solutions were cast on a smooth glass plate to a thickness of 0.30 mm using a casting rod at room température. The resulted cast films together with the glass plates were immersed for 1 h in distilled water at room température. During gélation, it was observed that the membranes peeled off from the glass plate spontaneously. Ail the membranes were then dried at ambient conditions for 3 days. Table 10 shows the prepared membranes, their materials of construction and préparation conditions.

Table 10. Membrane préparation details: casting solution composition and préparation conditions*

Membrane code	SMM type	Solvent	Polymer Concentration	Ethanol Concentration
Ml	nSMMl	NMP	10	10
M2	nSMM2	NMP	10	10
M3	nSMM3	NMP	10	10
M4	nSMMl	NMP	12	10

Membrane code	SMM type	Solvent	Polymer Concentration	Ethanol Concentration
M5	nSMMl	NMP	14	10
M6	nSMMl	DMAc	10	10
M7	nSMMl	NMP	10	20

No évaporation time and gélation bath température: 20°C

Membrane characterization

1. Measurement of gas perméation test and liquid entry pressure of water (LEPw) [0174] Measurement of liquid entry pressure of water (LEPw) and the gas perméation test were carried out for the prepared surface modified PS membranes, essentially as described above in Example 2.

[0175] As in Example 2, the perméation flux of nitrogen through each dry membrane was measured at various transmembrane pressures, in the range of 10-100 kPa. In general, the gas permeance, B, for a porous medium contains both a difTiisive term and a viscous term, the contribution of which dépends on the applied pressure as required by Equation 34 above.

[0176] Similarly, throughout ail the gas perméation experiments, it was noticed that the gas permeance was independent of pressure (P_m). Accordingly, the gas permeance will be described after omitting the viscous term of Eq. (34) as [16 and 17], to get Eq. (35), which was useful in evaluating the ratio (rs/Lp).

[0177] As in Example 2, some of the gas perméation experiments were duplicated using different membrane sheets made from the same casting solution batch in order to evaluate the variance of the obtained values from batch to batch. Moreover, for each membrane, the measurement of the gas flow rate was made three times at a given gas pressure and the average value is reported as the membrane permeance.

[0178] The measurements for the ££P_W were then carried out as explained in Example2. The experiment was done three times using three different sheets made from the casting solution batches. The results were averaged to obtain the final LEP_W value of each membrane.

2. Scanning Electron Microscopy (SEM) [0179] The cross-section of the SMMs blended PS membranes was analyzed by SEM using the same system and technique as set out in Example 2. —

-4816486

3. Measurement of Contact Angle (CA) [0180] The contact angle (CA) of the SMMs blended membranes was measured to study their hydro-phobicity /-philicity using the same system and technique as set out in Example 2.

DCMD experiments [0181] The laboratory system used to conduct the DCMD experiments for the SMMs blended PS membranes is presented in Figure 15. The central part of the system is a stainless steel cell composed of two cylindrical chambers. One of the chambers is connected to a heating system through its jacket to control the température of the liquid feed. The other chamber is connected to a cooling system to control the température of the permeate. The membrane is placed between the two chambers (feed side and permeate side). The hot feed solution is brought into contact with the hydrophobie top layer of the membrane and the cold permeate solution is in contact with the hydrophilic part of the membrane. The effective membrane area is 2.75 x 10'³ m². The bulk feed and permeate températures are measured, after steady state is reached, inside each chamber by a pair of sensors connected to a digital meter with an accuracy of ± 0.1 °C. Both the feed and permeate liquids are stirred inside the cell by graduated magnetic stirrers. The DCMD flux is calculated in every case by measuring the condensate collected in the permeate chamber for a predetermined period. The experiments are conducted first for pure water to détermine the water vapour permeability of the membranes. Subsequently, aqueous solution of 0.5 M sodium chloride is employed as feed.

[0182] The experiments were carried out under a température différence between the feed and permeate of 10°C. When distilled water was used as feed, the mean température was varied from 20 to 45°C, while the stirring rate was maintained at 500 rpm. When 0.5M NaCl solution was used as feed, the mean température was 45°C and the stirring rate was 500 rpm. The concentration of both feed and permeate solutions is determined by a conductivity meter (712 QMetrohm). The soluté séparation factor, a , is calculated using the foilowing expression:

a

*100% (36) where C_p and Cf are the NaCl concentration in the permeate and in the bulk feed solution, respectively. χΖ'

-4916486

Results and Discussion

SMMs characterization [0183] The précisé T_g values could not be obtained for the SMMs (nSMMl, nSMM2 and nSMM3) as the samples were heated up to 280 °C due to the limitation of higher température of the equipment. According to the SMMs chemical structure presented in Figure 8, the value of m, the number of the repeating unit, CF2, was calculated from the molecular weight of (FAE). The value of y, the number of repeating unit, dimethylsiloxane, was calculated from the average molecular weight of PDMS. q, the number of the repeating unit, urea, was estimated for each SMM based on its fluorine content. The values of T_g, weight average molecular weight (M_w), fluorine content (F wt°/o), m, y, and q for the SMMs are given in Table 11.

Table 11. SMMs characterization results

SMM	F(wt%)	(104 g/mol)	TiCC)	m	y	?
nSMMl	16.21%	2.95	>280	7.58	9.81	2.306
nSMM2	11.75%	2.71	>280	7.58	9.81	3.557
nSMM3	10.06%	3.30	>280	7.58	9.81	4.320

Membrane characterization [0184] The contact angle (CA) data of ail membranes are shown in Table 12. It was observed that the CA of the top side of the prepared membranes is higher than their bottom side; indicating that the hydrophobicity of the membrane top Iayer is higher than that of the bottom sub-layer. This is attributed to the fact that the hydrophobie SMM tends to migrate toward the membrane top surface during gélation in order to minimize the interfacial energy according to the thermodynamic principles [15, 16,20, 22, 23 and 25).

[0185] The CA of the SMMs blended membranes where nSMMl, nSMM2 and nSMM3 were used as surface modifying macromolecules; follows the order: Ml (96.66°) > M2 and M3 (100.4° and 100.52°, respectively).

[0186] The membrane with higher hydrophilic polymer concentration exhibited higher contact angle at the membrane top surface. The CA of the blended membranes using nSMMl as surface modifying macromolecules but with different PS concentrations; follows the order: M5 > M4 > Ml. Furtheimore, the SMM blended PS membrane where DMAc was used as

-5016486 solvent (M6) exhibited higher CA than Ml. Similar trend was also observed from the nonsolvent concentration point of view (M7 > Ml).

Table 12. CA results of the prepared membrane for both top and bottom sides

Membrane	CA(0°)
Ml	Top: 96.66 ±3.84
Bottom: 84.60 ± 0.42
M2	Top: 100.40 ±0.91
Bottom: 78.87 ± 4.35
M3	Top: 100.52 ± 5.92
Bottom: 84.70 ±1.68
M4	Top: 100.50 ± 6.34
Bottom: 77.28 ±5.07
M5	Top: 102.95 ± 3.42
Bottom: 82.85 ± 3.64
M6	Top: 101.64 ±4.42
Bottom: 82.23 ±2.25
M7	Top: 103.60 ±2.20
Bottom: 86.85± 2.48

[0187] The SEM images of the membrane cross-sections are shown in Figure 16. As can be seen, ail the membranes are of asymmetric structure with a dense top-layer supported by a finger-like structure undemeath. However, the bottom parts of the membranes are different. The finger-like structure of the membrane Ml, M2 and M3 (Figure 16a, Figure 16b and 10 Figure 16c, respectively) reaches the bottom side, where small macro-voids were formed in vertical direction. It was noticed that at the bottom of the membrane; the macro-voids were separated by vertical sponge-like polymer layers.

[0188] From polymer concentration point of view; the SEM images of Ml, M4 and M5 membranes (see Figure 16a, Figure 16d and Figure 16e) showed that the size of the macro15 voids at the bottom layer decreased with increasïng polymer concentration. On the other hand, the structure of the top and the intermediate layer remained unaltered; i.e., a similar top dense layer is supported by a finger-like structure undemeath.

[0189] M6 membrane (Figure 16f), prepared with DMAc as solvent, exhibited completely different structure from that membranes prepared with NMP as solvent (Figure 16a). In the

-5116486

M6 membrane, the top layer was a dense layer supported by a short finger-like structure undemeath, followed by a sponge-like structure at the intermediate and bottom layers of the membrane.

[0190] Both Ml and M7 membrane, in which the non-solvent additive concentration was altered (see Figure 16a and Figure 16g), exhibited similar structures with a top dense layer supported by a finger-like structure undemeath. However, the macro-voids size was smaller in M7 than Ml. Moreover, the vertical sponge-like polymer layers that separate the macrovoids at the bottom of the membrane was more pronounced in M7 membrane.

[0191] The data for the LEP_W and (re/L_p) are summarized in Table 13. The data is discussed below, together with the DCMD data.

Table 13. Liquid entry pressure of water (LEPw) and (oÆ_F) of the prepared membranes

Membrane	LEPw (bar)	sr/Lp
Ml	2.9	1.15 10^
M2	3.3	6.97 10'5
M3	3.6	4.93 10'5
M4	4.4	3.02 10'6
M5	4.6	5.48 10’7
M6	3.2	1.65 10^
M7	3.3	5.48 10‘7

Membrane performance

1. SMMs type effect [0192] Ml (nSMMl), M2 (nSMM2) and M3 (nSMM3) membranes were chosen to compare the SMM type effects on the DCMD performance (see Table 10 for membrane préparation conditions). Figure 17 shows the DCMD fluxes ofthe above membranes alongwith those of the commercial membrane (FGLP 1425). Figure 17a shows the DCMD flux versus the average température of feed and permeate solutions (T_m) when distilled water was used as feed, while Figure 17b shows the DCMD flux of the same membranes when using 0.5M NaCI aqueous solution as feed.

(0193| It is well documented that température is the operatïng variable that affects the MD flux the most due to the exponentiel increase of vapour pressure with température according to the Antoine équation [1-6]. As shown in Figure 17a; both the commercial membrane and the SMMs blended PS membranes exhibit an exponential increase of the DCMD flux with an increase in T_m.

[0194J Both Figures 17a and 17b show that the order in the DCMD flux is Ml > M2 > M3 > FGLP 1425. In other words, the prepared SMMs blended PS membranes showed higher permeate fluxes than the commercial membrane. In particular, the DCMD flux of the membranes Ml, M2 and M3 was found, on average within the tested températures, to be (43 ± 8.51) %, (35 ± 8.30) % and (31 ± 6.63) %, respectively, higher than that ofthe commercial membrane as shown in Figure 15a.

[0195] According to Table 13, the LEPw of those membranes under investigation followed the order of M3 > M2 > Ml. This indicates that the order of maximum pore size according to Laplace équation [26] might be Ml > M2 > M3, which agréés with the flux order. Moreover, Table 13 shows that the decreasing order of the ratio (rs/Lf) is Ml > M2 > M3, which is again the same order of the permeate flux. As observed with the polyetherimide composite membranes described above, the membrane exhibiting higher (er/L_p) ratio will hâve higher DCMD flux. This is expected since an increase in the ratio (firZL_p) means an increase in either the porosity and/or pore radius or a decrease in effective pore length.

[0196] As can be observed in Figure 17b; smaller permeate fluxes were obtained in the presence of sodium chloride. The flux of Ml and FGLP 1425 decreased by 13-15 % compared to that obtained when distilled water was used as feed. While, the flux décliné in case of M2 and M3 was around 26%. Generally, it is expected to observe a flux décliné in presence of NaCl, since the water vapour pressure decreases, which results in lower driving force for vapor transport. Moreover, a boundary layer develops next to the feed membrane surface, where the NaCl concentration increases toward the membrane surface due to concentration polarization. The presence of the concentration boundary layer and the température boundary layer together reduces the driving force.

[0197] The soluté séparation factor defined as:

100 (37) where C_p and Cf are the NaCl concentration in the permeate and in the bulk feed solution, respectively, was higher than 99.9% (the permeate conductivity was always smaller than 25

-5316486

PCT/CA2011/000093 pS/cm ïn ail the tested membranes) for ail the tested membranes. This indicates that the SMMs blended membranes Ml, M2 and M3 are useful for MD processes.

2. Polymer concentration effect [0198] Ml (10 wt%), M4 (12 wt%) and M5 (14 wt%) membranes were chosen to study the effect of the hydrophilic host polymer (PS) concentration on the DCMD flux (see Table 10). Figure 18 shows the DCMD fluxes of the above membranes along with those of the commercial membrane (FGLP 1425). Figure 18a shows the DCMD flux versus the average température of feed and permeate solutions (T_m) when distilled water was used as feed, while Figure 18b shows the DCMD flux of the same membranes when using 0.5M NaCI aqueous solution as feed.

[0199] Comparing the permeate flux data; Ml membranes showed the best performance among the tested membranes. As stated earlier, the Ml membrane showed (43 ± 8.51) % flux enhancement compared to the commercial membrane. Conversely, M4 and M5 membranes DCMD exhibited fluxes lower, on average of the tested température range, by (43 ± 3.69 and 94 ± 1.64) % than that of the commercial membrane, respectively.

[0200] According to Table 13, the increasing order in the LEPw values was; Ml < M4 < M5, indicating that Ml membrane has the largest maximum pore size according to Laplace équation [26] and/or less hydrophobie (i.e. smaller top-layer CA). The decreasing order in the er/Lp values was, on the other hand, Ml > M4 > M5. This trend validâtes our earlier conclusion that the membranes with higher sr/L_p values will exhibit higher fluxes.

[0201] It can be concluded that increasing the polymer concentration leads to a sîgnificant decrease in the permeate flux, which is attributable to either the decrease in the maximum pore size or the decrease in the er/L_p ratio. Similar trend was observed when a different polymer was used [16 and 23].

[0202] In the presence of NaCI (see Figure 18b); the flux decreased compared to those values obtained when distilled water was used as feed. The flux décliné in the case of M4 and M5 membrane was 66% and 43%, respectively. Once again, this could be explained by the formation of the concentration boundary layer, which contributes together with the thermal boundary layer in the flux décliné.

[0203] The soluté séparation factor was higher than 99.9% for ail the above membranes. The permeate conductivity was around 12 pS/cm for M4 and M5 membrane, while it was around 23 pS/cm for the commercial and Ml membrane.

-5416486

3. Solvent type effect [0204] Ml (NMP) and M6 (DMAc) were chosen for the comparison of SMM/PS membranes prepared using different solvents. Other membrane préparation parameters were kept unchanged (see Table 10). Figure 19 shows the DCMD fluxes of the above membranes along with those of the commercial membrane (FGLP 1425). Figure 19a shows the DCMD flux versus the average température of feed and permeate solutions (Tn) when distilled water was used as feed, while Figure 19b shows the DCMD flux of the same membranes when using 0.5M NaCl aqueous solution as feed.

[0205] As shown in Figure 19a; both the commercial membrane and the SMM blended PS membranes exhibit an exponentiel increase of the DCMD flux with an increase in T_m as discussed above in the section regarding SMMs type effect.

[0206] Ml membrane showed a flux that is superior to that of the commercial or M6 membrane. In particular; the decreasing order of the flux was Ml > FGLP 1425 > M6. The M6 membrane’s flux was lower, on average of the tested température range, than that of the commercial membrane by around (53 ± 2.73) %. This decreasing order agréés with the increasing order of the LEPw of the SMM blended PS membranes, respectively as shown in Table 13. More specifically; the increasing order in LEPw ws Ml (2.9 bar) < M6 (3.2 bar). This validâtes our earlier conclusion that the membranes with lower LEPw exhibit higher fluxes since they hâve larger maximum pore sizes. Furthermore, the decreasing order of the flux agréés with the decreasing order of the ratio (érÆ_p); i.e. Ml (1.15 10⁴) > M6 (1.65 10⁴). This further validâtes our earlier conclusion of the relationship between the ratio (er/Lf) and the permeate flux.

[0207] It is worth mentioning that, although M6 membrane exhibited a more profound sponge like structure at the intermediate and bottom sub-layer than that of Ml membrane (see Figure 16a (Ml) and Figure 16f (M6)), which is more favorable in MD [13], the trend in the flux was the opposite. This suggests that the flux is more affected by the top skin layer properties including the (£r/Z_p) ratio and LEPw.

[0208] In presence of NaCl, the flux decreased compared to those values obtained when distilled water was used as feed (see Figure 19b). The flux décliné in case of M6 membrane was 58%. Once again, this could be explained by the formation of the concentration boundary layer. Most importantly, the soluté séparation factor was higher than 99.9% for ail membranes involved with the permeate conductivity of around 12 pS/cm and 23 pS/cm for vs/

-5516486

M6 and Ml membrane, respectively.

4. Non-solvent (Ethanol) concentration effect [0209] Ml (10% Ethanol) and M7 (20% éthanol) were chosen for the comparison of SMM/PS membranes prepared with different non-solvent concentrations. Other membrane préparation parameters were kept unchanged (see Table 10). Figure 20 shows the DCMD fluxes of the above membranes along with those of the commercial membrane (FGLP 1425). Figure 20a shows the DCMD flux versus the average température of feed and permeate solutions (T_m) when distilled water was used as feed, while Figure 20b shows the DCMD flux of the same membranes when using 0.5M NaCl aqueous solution as feed.

[0210] As shown in Figure 20a, both the commercial membrane and the SMM blended PS membranes exhibit an exponential increase of the DCMD flux with an increase in T_m due to the reason discussed earlier in the section relatïng to the SMMs type effect.

[0211] Ml membrane showed a flux that was superior to that of the commercial or M7 membranes. In particular; the decreasing order of the flux was Ml > FGLP 1425 > M7. The M7 mcmbrane’s flux was lower than that of the commercial membrane, in the tested température range, than that of the commercial membrane by around (23 ± 5.39) %. This decreasing order agréés with the increasing order of the LEPw of the SMM blended PS membranes, respectively as shown in Table 13. More specifically; the LEPw increasing order was Ml (2.9 bar) < M7 (3.3 bar). This, again, validâtes our earlier conclusion that the membranes with lower LEPw exhibit higher fluxes since they hâve larger maximum pore sizes. Furthermore, the decreasing order of flux agréés with the decreasing order of the ratio (srÆp); i.e. Ml (1.15 10^-4) > M7 (5.48 10'⁷). This further validâtes the earlier conclusion of the relationship between the ratio (£r/L_p) and the permeate flux.

[0212] Although the non-solvent additives is used to enhance the pore size and/or porosity of the membrane [27] and to achieve better permeate flux, the trend shown in Figure 20 is the opposite. As a conclusive remark; it is not necessary to enhance the permeate flux by increasing the éthanol concentration. Z.-L. Xu and F. Qusay [28] found that increasing the éthanol concentration from 0 to 15 wt% in polyethersulfone ultrafiltration hollow fibers decreased the mean pore size and caused an increase in the pore density. On the other hand; they also reported that the opposite occurred when increasing the éthanol concentration above 15 wt %.In the presence of NaCl, the flux decreased compared to those values obtained when distilled water was used as feed (see Figure 20b). The flux décliné in case of M7 membrane vV was 38%. Once again, this could be explained by the formation of the concentration boundary layer. The soluté séparation factor was higher than 99.9% for ail the membranes involved with the permeate conductivity around 18 pS/cm and 23 pS/cm for M7 and Ml membrane, respectively.

Conclusions [0213] This Example demonstrates that polysulfone (PS) use as a manufacturing material for membrane distillation (MD) membranes. This was achieved by blending PS, which is a hydrophilic polymer, with three different types of surface modifying macromolecules. The effects of different membrane préparation parameters such as SMMs type, hydrophilic polymer concentration, solvent type and non-solvent additive concentration on the membrane characteristics and performance in DCMD were clearly identified.

[0214] It was found that the characteristics of the top skin layer that govems the DCMD are able to explain the reported flux trends. Those characteristics are the product of average pore size and effective porosity per unit effective pore length (rz/L_p) and the liquid entry pressure of water (LEPw). In other words, membranes with higher rtfLp and lower LEPw produced higher permeate fluxes.

[0215] Among the tested membrane préparation conditions, it was found that nSMMl/PS membrane is better than those membranes prepared with nSMM2 and nSMM3, NMP was better solvent for membrane préparation than DMAc, membranes prepared with lower hydrophilic polymer (PS) concentration exhibited higher permeate fluxes than those of higher PS concentration, and finally, membranes with 10 wt% non-solvent additive (Ethanol) concentration produced higher permeate fluxes than the membranes prepared with 20 wt% Ethanol concentration.

[0216] Generally, SMM/PS membranes are promising as novel MD membranes. Some of the SMMs modified PS membranes exhibited higher permeate fluxes than those obtained using the commercial PTFE membrane, although the SMMs modified PS membranes hâve considerably lower pore size and porosity.

[0217] Most importantly, the séparation factor was found to be higher than 99.9% for ali of the tested membranes.

EXAMPLE 4: Comparas the Desalination Performance of SMM Blended Polycthersulfone to S MM Blended Polyetherimide Membranes by Direct Contact Membrane Distillation [0218] In this Example, nSMM was used to préparé SMM blended PES and PEI composite membranes. The membranes were prepared by a single casting step via the phase inversion method as described in an earlier study [16]. The membranes were characterized using a wide variety of characterization techniques including; gas perméation test, measurement of the liquid entry pressure of water (LEPw), scanning electronic microscopy (SEM), Atomic Force microscopy (AFM) and contact angle measurement (CA).

[0219] The main objective of this Example was to study the effect of the hydrophilic polymer type on the membrane characteristics as well as its DCMD performance when distilled water or 0.5M NaCl solution was used as a feed. The results were compared to those of the commercial PTFE membrane (FGLP 1425, Millipore Corporation USA). The prepared membranes are useful for practical application in desalination by DCMD. This Example 15 further provides a link between the characteristics of the composite hydrophobic/hydrophilic composite membrane and the DCMD performance. This improves the overall understanding of the principle of the hydrophobic/hydrophilic composite membrane in membrane distillation.

Experimental

Materials [0220] Ail chemicals used in this work and their chemîcal abstract service (CAS) number are enlisted in Table 14. The weight average molecular weight (Af_w) of the polyetherimide (PEI) and the polyethersulfone used in this study are 15 and 30.8 kDa, respectively. The commercial membrane used is polytetrafluoroethylene, PTFE, (FGLP 1425) having a 25 porosity of 0.70 and a nominal pore size of 0.25 pm supplied by the Millipore Corporation, Billerica, MA, USA.

Table 14. Materials used in this Example.

Material description	CAS number	Source
4,4'-Methylene bis(phenyl isocyanate) (MDI, 98%)	101-68-8	Sigma-Aldrich, Inc., St. Louis, MO, USA
α,ω-Aminopropyl poly(dimethyl siloxane) (PDMS) of average	106214-84-0	Shin-Etsu Chemîcal Co. Ltd., Tokyo, Japan

-5816486

Material description	CAS number	Source
molecular weight 900
Zonyl fluorotelomer intermediate, 2(Perfluoroalkyl)ethanol, (FAE, BA-L of average Mn 443 and 70 wt% fluorine	678-39-7	DuPont product supplied by Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Ν,Ν-Dimethylacetamide (DMAc, anhydrous 99.8%)	127-19-5	Sigma-Aldrich, Inc., St. Louis, MO, USA
l-Methyl-2-pyrrolidinone (NMP, anhydrous 99.5%)	112-14-1	Sigma-Aldrich, Inc., St. Louis, MO, USA
y-Butyrolactone (GBL, 99+%)	96-48-0	Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Ethanol (anhydrous, 99+%)	64-17-5	Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Tetrahydrofuran (THF, HPLC grade 99.9%)	109-99-9	Aldrich Chemical Company, Inc., Milwaukee, WI, USA
Polyetherimide (PEI, Ultem 1000, Natural Ballet) Spécifie gravity: 1.27	61128-46-9	General Electric Co., Pittsfield, MA, USA
Poiyethersulfone (PES, Radel A300PNT)	25667-42-9	Amoco Polymer Inc., Alpharetta, Georgia, USA

SMMs Synthesis and Characterization (0221] The SMMs were synthesized using a two-step solution polymerization method [23] as described above in Example 2. The first polymerization step was conducted in a solution with 5 a predetermined composition to form polyurea as a prepoiymer from the reaction of MDI with PDMS. In the second step, the pre-polymer was end-capped by the addition of FAE, resulting in a solution of SMM. The ratio of monomers for the synthesis of S MM was: MDI:PDMS:FAE = 3:2:2. The prepared SMM is referred to hereafter as nSMM2 and has the PUDU structure shown in Figure 8.

[0222J The synthesized SMM was characterized for fluorine content, glass transition température and weight and number average molecular weights as described above in Exampies 2 and 3. As above, the values for m, y, and q, for the repeating units shown in the chemical structure of the SMM (see Figure 8), were calculated from the average molecular weight of FAE, PDMS and SMM, respectively.

Membrane Préparation [0223] SMM modified PES and PEI membranes were prepared in a single casting step by the phase inversion method [16]. γ-Butyrolactone (GBL) was used as a non-solvent additive for PEI and Ethanol (EtOH) was used in case of PES. NMP was used as solvent. A predetermined amount of PES or PEI was dissolved in a NMP/ETOH or NMP/GBL mixture. The polymer (PES or PEI) concentration in the casting solution was maintained at 12 wt%, while the amount of non-solvent additive (EtOH or GBL) was maintained at 10 wt%. The added SMM concentration was 1.5 wt%. The resulting mixtures were stirred in an orbital shaker at room température for at least 48 h. Prior to use, ail polymer solutions were filtered through a 0.5 pm Teflon® filter and degassed at room température. The polymer solutions were cast on a smooth glass plate to a thickness of 0.30 mm using a casting rod at room température. The cast films together with the glass plates were immersed for 1 h in distilled water at room température. During gélation, it was observed that the membranes peeled off from the glass plate spontaneously. Ail the membranes were then dried at ambient conditions for 3 days. Two membranes were prepared, Ml, which is made of PES as host polymer, and M2 based on PEI as host polymer.

Membrane Characterization

1. Measurement of Gas Perméation test and Liquid Entry Pressure of Water (LEPw) [0224] Measurement of liquid entry pressure of water (LEPw) and the gas perméation test were carried out for the prepared surface modified membranes. The gas peimeation test was performed prior to the measurement of LEPw. The details of the systern and method are provided above in Examples 2 and 3, and the references cited therein.

[0225] As in Examples 2 and 3, throughout ail the gas perméation expérimenta, it was noticed that the gas permeance was independent of P_m. Therefore, the diffusive mechanism seems to dominate the gas transport through the membrane pores revealing the fact that the prepared membranes in this Example hâve small pore sizes. Accordingly, the gas permeance is given, by ignoring the viscous term of Eq. (34), to get Eq. (35), which was useful in evaluating the ratio (re/Lp).

[0226] Also, as in Examples 2 and 3, some of the gas perméation experiments were duplicated using different membrane sheets made from the same casting solution batch in order to evaluate the variance of the obtained values from batch to batch. Moreover, for each membrane, the measurement of the gas flow rate was made three times at a given gas — pressure and the resulting values were averaged to obtain the membrane permeance value.

[0227] The measurements for the LEPw were then carried out as explaïned above and elsewhere [14]. The experiment was done three times using three different sheets made each casting solution batch. The results were averaged to obtain the final LEPw value of each membrane.

2. Scanning Electron Microscopy (S EM) [0228] The cross-section of the SMMs blended PS membranes was analyzed by SEM using the same System and technique as set out in Example 2.

3. Atomic Force Microscopy (AFM) Observation [0229] The morphology of the top surface (i.e., the hydrophobie surface) of the SMM/PES and SMM/PEI membranes was studied by atomic force microscopy (AFM). Details of the tapping mode (TM)-AFM technique are given elsewhere [33]. The membrane top surface was characterized in terms of the roughness, pore size and size of nodule aggregates.

[0230] Pore sizes and nodule/nodular aggregate sizes were measured by visual inspection of line profiles from the obtained AFM images. To obtain the pore sizes and nodule/nodular aggregate sizes, cross-sectional line profiles were selected to traverse micron Scan surface areas of the TM-AFM images. The diameters of nodules (i.e., light région or bright area, high peaks) or pores (i.e., dark area, low valleys, dépréssion) were measured by a pair of cursors along the reference line. The horizontal distance between each pair of cursors was taken as the diameter of the nodule/nodular aggregate or pore.

[0231] The sizes of the pores or nodule/nodular aggregates are based on the average of at least 30 measurements. The roughness parameters obtained from AFM images should not be considered as the absolute roughness value. In the présent study, the same tip was used for ail experiments and ail captured surfaces were treated in the same way. The évaluation of the roughness parameters of each membrane sample was based on various micron scan areas (i.e., 1 * 1 pm²). The pore size distribution was calculated by the method described by Singh et al. [34].

4. Measurement of Contact Angle (CA) [0232] The contact angle (CA) of both SMM/PES and SMM/PEI membranes was measured to study their hydro-phobicity /-philicity using the same System and technique as set out in '

-61 16486

Example 2.

DCMD Experiments [0233] The prepared S MM blended PES and PEI membranes were tested by the DCMD setup shown in a previous study [16] and detailed above in Example 3.

Results and Discussion

SMM and Membrane Characterization [0234] The SMM characteristics, including the glass transition température (Tg), weight average molecular weight (M_w), number average molecular weight (A/„), fluorine content and the number of the structural repeating units are given in Table 15.

Table 15. Surface Modifying Macromolecules (SMM) characteristics

Glass transition température, Tg (°C)	> 280
Weight average molecular weight, Mw (104 g/mol)	2.71
Number average molecular weight, M„( 104 g/mol)	1.28
Fluorine Content, F (wt%)	11.75
CF2 repeating unit, m	7.58
Dimethylsîloxane repeating unit, y	9.81
Urea repeating unit, q	22.58

|0235] The précisé glass transition température (T_g) value could not be obtained for the SMM as the sample could be heated up to 280 °C due to the limitation of higher température of the equipment. According to the SMMs chemical composition presented in Figure 8, the value of m, the number of repeat unit of CF2, was calculated from the FAE molecular weight. The value of y, the number of repeat unit of dimethylsîloxane, was calculated from the average molecular weight of PDMS. The value of q, the number of the urea repeat unit was calculated from the SMM weight average molecular weight.

[0236] The prepared SMM/PES and SMM/PEI membranes are called hereafter Ml and M2, respectively. The resulting contact angle (CA) data from these membranes are shown in Table 16. it was observed that the CA of the top side of the prepared membranes is higher than their bottom side. The CA of the top side was nearly equal to or higher than 90° indicating that the top layer is sufficiently hydrophobie. In contrast, the CA of the membranes’ bottom side was lower than 90° indicating the hydropholicity of the bottom layer. This is evidence of formation of composite hydrophobic/hydrophilic membranes by the phase inversion method, in which hydrophobie nSMM is blended to a hydrophilic polymer.

Table 16. Top and bottom contact angles (CA) of the prepared membranes.

Membrane	CA(0°)
Ml	Top: 89.76 ±3.34
Bottom: 62.69 ± 3.82
M2	Top: 91.93 ±0.52
Bottom: 67.76 ± 3.29

[0237] The SEM images of the membranes cross-section are shown in Figure 21. As can be seen, ail the membranes are of asymmetric structure with a dense top-layer supported by a finger-like structure undemeath. However, the bottom parts of the membranes are different. The finger-like structure of the membrane Ml (Fig. 21a) reaches the bottom side, where small macro-voids were formed in vertical direction. On the other hand, for the M2 membrane (Fig. 21b), the finger-like structure became more irregular in the middle of the cross-section and large macro-voids were formed in horizontal direction.

[0238] AFM images of the SMM/PES (Ml) and SMM/PEI (M2) top side membranes are shown in Figure 22. The bright side is the highest point (nodule) and the dark région is the lowest point (pore). For analyzing the top surface characteristics, AFM image analysis program was used. Table 17 shows the prepared membranes’ top surface characteristics from the AFM analysis, including the mean pore size, the surface roughness and the mean nodule size.

Table 17. AFM analysis results of the prepared membranes’ top surface

Surface Characteristics	Ml	M2
Mean pore size (dp, nm)	21.50	22.38
Mean nodule size (nm)	33.30	29.58
Surface roughness (Λ, nm)	9.8	10.32
Géométrie standard déviation (σρ)	1.18	1.28

[0239] As shown in Table 17, Ml membrane exhibited smaller mean pore size and larger nodule size compared to that of M2 membrane. From the mean pore size (d_p) and the géométrie standard déviation (σ_ρ) data, the pore size distribution of the laboratory made membranes can be expressed by the probability density fonction. [34]

WJ ₌ i [_ oq-uxq,)³] dd; tQlnapVZ* ^βΧ*^,[ ïÇbu^)¹ J (38) [0240] The pore size distribution of Ml and M2 membranes are shown in Figure 23. As can be seen, Ml membrane exhibited narrower pore size distribution than M2 membrane. The data for the LEPw and product of average pore size and effective porosity per unit effective pore length (?έ/Λ_ρ) are summarized in Table 18.

Table 18. Liquid entry pressure of water (LEPJ) and product of average pore size and effective porosity per unît effective pore length (er/L_p) of the laboratory prepared membranes.

Membrane	LEPW (bar)	et/Lp
Ml	3.1	6.97 10‘5
M2	4.0	1.53 10’5

Membrane performance [0241] Figure 24 shows the DCMD fluxes of the prepared Ml (PES) and M2 (PEI) membranes along with those of the commercial membrane (FGLP 1425). Figure 24a shows the DCMD flux versus the average température of feed and permeate solutions (Tm) when distilled water was used as feed, while Figure 24b shows the DCMD flux of the same membranes when using 0.5M NaCI aqueous solution as feed.

[0242] It is well documented that température is the operating variable that affects the MD flux the most due to the exponentiel increase of vapour pressure with température according to the Antoine équation [1-6, and 32]. As shown in Figure 24a; both the commercial membrane and the SMM blended PES and PEI membranes exhibit an exponential increase of the DCMD flux with an increase in Tm.

[0243] Both Figures 24a and 24b show that the order in the DCMD flux is Ml > M2 > FGLP 1425. In other words, the prepared SMM blended PES or PEI membranes showed higher permeate fluxes than the commercial membrane. In particular, the DCMD flux of the membranes Ml and M2 was found, on average within the tested températures, to be 40% and

-6416486

8%, respectively, higher than that of the commercial membrane as shown in Figure 24a. [0244] According to Table 18, the LEPw of the membranes under investigation followed the order of M2 > Ml. This indicates that the order of the maximum pore size, according to Laplace équation [13], should be Ml > M2, when the hydrophobicity of both membranes are equal. Moreover, Table 18 shows that the decreasing order of the ratio (re/Lf) is Ml > M2. The orders both in maximum pore size and (re/Lf) agréé with the order in the permeate flux. It can be therefore concluded that the membrane exhibitîng higher (re/Lf) ratio will hâve higher DCMD flux. This is expected since an increase in the ratio (re/L_p) means an increase in either the porosity and/or pore radius or a decrease in effective pore length.

[0245] According to the AFM data (see Table 17), Ml membrane exhibited smaller mean pore size compared to M2 membrane. This contradicts the reported permeate flux resuit. But according to re/L_p values then this flux enhancement is due to the increase of the effective porosity ratio, e/L_p, which is greater for Ml membrane.

[0246] As can be observed in Figure 24b; smaller permeate fluxes were obtained in the presence of sodium chloride. The flux of Ml, M2 and FGLP 1425 decreased by 13-15 % compared to that obtained when distilled water was used as feed. Generally, it is expected to observe a flux décliné in presence of NaCl, since the water vapour pressure decreases, which results in lower driving force for vapor transport. Moreover, a boundary layer develops next to the feed membrane surface, where the NaCl concentration increases toward the membrane surface due to concentration polarization. The presence of the concentration boundary layer and the température boundary layer together reduces the driving force.

[0247] The soluté séparation factor defined earlier in Eq. (37) was higher than 99.9% (the permeate conductivity was always smaller than 25 pS/cm in ail the tested membranes) for ail the tested membranes. This indicates that the SMMs blended membranes Ml and M2 are useful for MD processes.

Conclusions [0248] The data presented in this Example provides a better and instructive understanding of hydrophobic/hydrophilic membranes performance in MD by finding the relationship between the membrane morphology and its performance in MD. In particular, the higher product of average pore size and effective porosity per unit effective pore length (re/L_p) membranes produced higher fluxes. Membranes with higher liquid entry pressure of water (smaller maximum pore size) exhibiter higher fluxes. \>/^-6516486 [0249] Among the tested membrane préparation conditions it was found that the SMM/PES performed better membrane than SMM/PEI membranes.

[0250] Overall, both iaboratory-made membranes performed better than the commercial PTFE membrane, although they have considerably lower pore size and porosity. Moreover, 5 the séparation factor was higher than 99.9% for ail the tested membranes. Furthermore, it was proved that the SMMs are necessary to produce workable membranes in MD.

EXAMPLE 5: Effect of Surface Modifying Macromoleculcs Stoichiometric Ratio on Composite Hydrophobic/Hvdrophilic Membranes Char acteris tics and Performance in

Membrane Distillation

-6616486 [0251] The présent Example provides further improvement of the MD membranes performance by changing the nSMM structures. To this end, the stoichîometric ratio of nSMM components was altered systematically in nSMM synthesis:

1. nSMMl: 2(MDI):1(PDMS):2(FAE)

2. nSMM2:3(MDI):2(PDMS):2(FAE)

3. nSMM3:4(MDI):3(PDMS):3(FAE).

[0252] Furthermore, the newly developed SMMs were blended with PEI host polymer to préparé composite hydrophobic/hydrophilic membranes. This was done in a single casting step by the phase inversion method.

[0253] The membranes were characterized using gas perméation test, measurement of the liquid entry pressure of water (LEPw), scanning electronic microscopy (SEM), and contact angle measurement (CA). The effects of the SMM type on the membrane morphology were identified, which enabled us to link the membrane morphology to the membrane performance.

|0254] The membranes were further tested by DCMD for desalination of 0.5 M NaCl solution and the results were compared to commercial polytetraflouroethylene (PTFE) membranes (FGLP 1425, Millipore Corporation, USA).

Experimental

Materials [0255] Ail chemicals used in this work and their chemical abstract service (CAS) number are described in Example 2 above, and listed in Table 3.

SMMs synthesis and characterization [0256] The SMMs were synthesized using a two-step solution polymerization method as described above in Example 2. The ratio of the components of the SMMs were MDI:PDMS:FAE = 2:1:2, 3:2:2 and 4:3:3. The prepared SMMs are named hereafter as nSMMl, nSMM2 and nSMM3, respectively, based on the PDMS stoichîometric number. The chemical structure of the synthesized SMMs is shown in Figure 8 as PUDU.

[0257] The synthesized SMM was characterized for fluorine content, glass transition température and weight and number average molecular weights as described above in Examples -6716486 and 3.

Membrane Préparation [0258] SMM modifîed PEI membranes were prepared in a single casting step by the phase inversion method [15 and 16]. γ-Butyrolactone (GBL) was used as a non-solvent additive. A predetermined amount of PEI was dissolved in a NMP/GBL mixture. The PEI concentration in the casting solution was maintained at 12 wt%, while the amount of GBL was maintained at 10 wt%. Three different types of SMMs, nSMMl, nSMM2 and nSMM3, were added to the PEI solution in a concentration of 1.5 wt%. The resulting mixtures were stirred in an orbital shaker at room température for at least 48 h. Prior to their use, ail the resulted polymer solutions were filtered through a 0.5 pm Teflon® filter and degassed at room température. The polymer solutions were cast on a smooth glass plate to a thickness of 0.30 mm using a casting rod at room température. The solvent was then evaporated at ambient température for a predetermined period before the cast films together with the glass plates were immersed for 1 h in distilled water at room température. During gélation, it was observed that the membranes peeled off from the glass plate spontaneously. Ail the membranes were then dried at ambient conditions for 3 days. Table 19 shows the prepared membranes, their materials of construction and préparation conditions.

Table 19: Prepared membranes codes and the type of SMM used*.

Membrane Code	SMM type
MO	No SMMs
Ml	nSMMl
M2	nSMM2
M3	nSMM3

* PEI concentration: 12 wt%; GBL concentration: 10 wt%; NMP solvent: 76.5 wt%; SMMs: 1.5 wt%, gélation bath température; 20°C, évaporation time: 0 minute.

Membrane Characterization

1. Measurement of Gas Perméation test and Liquid Entry Pressure of Water (LEPw) [0259J Measurement of liquid entry pressure of water (LEPw) and the gas perméation test were carried out for the prepared surface modifîed membranes. The gas perméation test was performed prior to the measurement tâ LEPw. The details of the system and method are provided above in Exampies 2 and 3, and the référencés cited therein.

-6816486 [0260] As in Examples 2 and 3, throughout ail the gas perméation experiments, it was noticed that the gas permeance was independent of P„. Therefore, the difiusive mechanism seems to dominate the gas transport through the membrane pores revealing the fact that the prepared membranes in this Example hâve small pore sizes. Accordingly, the gas permeance is given, by 5 ignoring the viscous term of Eq. (34), to get Eq. (35), which was useful in evaluating the ratio (re/Lp).

[0261] Also, as in Examples 2 and 3, some of the gas perméation experiments were duplicated using different membrane sheets made from the same casting solution batch in order to evaluate the variance of the obtained values from batch to batch. Moreover, for each membrane, the 10 measurement of the gas flow rate was made three times at a given gas pressure and the resulting values were averaged to obtain the membrane permeance value.

[0262] The measurements for the LEPw were then carried out as explained above and el sewhere [14]. The experiment was done three times using three different sheets made each casting solution batch. The results were averaged to obtain the final LEPw value of each membrane.

2. Scanning Electron Microscopy (SEM) [0263] The cross-section of the SMMs blended PS membranes was analyzed by SEM using the same system and technique as set out in Example 2.

3. X-ray Photoelectron Spectroscopy (XPS) [0264] The elemental composition at the surface of each SMM blended membrane was determined by X-ray photoelectron spectroscopy using the same system and technique as set out in Example 2.

4. Measurement of Contact Angle (CA) [0265] The contact angle (CA) of the SMMs blended membranes was measured to study their hydro-phobicity /-philicity using the same system and technique as set out in Example 2.

DCMD Experiments [0266] The prepared SMMs blended PEI membranes were tested by the DCMD setup shown in a previous study [36]. The experiments were performed using the system and method described

-6916486 above in Example 2.

Results and Discussion

SMMs Characterization [0267] The précisé T_g values could not be obtained for the SMMs (nSMMl, nSMM2 and nSMM3) as the samples were heated up to 280 °C due to the limitation of higher température of the equipment. According to the SMMs chemical structure presented in Figure 8, the value of m, repeating unit of CF₂, was calculated from the molecular weight of (BAL). The values of y, repeating unit of dimethylsiloxane, were calculated from the average molecular weight of PDMS. q, repeating unit of the urea value was estimated for each SMM using two different méthodologies; the SMMs molecular weight (^_w() and fluorine content (çr_wt%). The values of T_gi number average molecular weight (M_w), fluorine content (F wt%), m, y, q^t and qrwt% for the SMMs are given in Table 20.

Table 20. SMMs characterization results

SMM	F(wt%)	M„ (10* g/mol)	r4CC)	M	y	qMwt	qpwtii
nSMMl	16.21%	2.95	>280	7.58	9.81	24.67	2.306
nSMM2	11.75%	2.71	>280	7.58	9.81	22.58	3.557
nSMM3	10.06%	3.30	>280	7.58	9.81	27.71	4.320

Membrane Characterization [0268| The contact angle (CA) data of ail membranes are shown in Table 21. It was observed that the CA of the top side of the prepared membranes was higher than their bottom side. The higher CA of the membrane Ml and M3 compared to that of the membrane M2 prepared under the same conditions indicates that the hydrophobicity of the membranes prepared with nSMM 1 (Ml) and nSMM3 (M3) is greater than that of the membrane prepared with nSMM2 (M2).

Table 21. Top and bottom contact angle (CA) of the prepared membranes

Membrane

CA (0°)

-7016486

Membrane	CA(0“)
MO	Top; 80.04 ±4.55
Bottom: 72.83 ± 2.62
Ml	Top: 93.55 ± 1.054
Bottom: 62.84 ± 3.05
M2	Top: 91.93 ±0.52
Bottom: 67.76 ±3.29
M3	Top: 100.17 ±3.62
Bottom: 73.80 ±4.08

[0269] The results of the XPS analysis for both PEI and SMMs blended PEI membranes are presented in Table 22. Fluorine was not detected in the PEI membrane. This is expected since fluorine is associated to SMMs. For ail the SMMs blended PEI membranes, fluorine contents were found to be higher at the top side than the bottom side îndicating SMMs’ migration towards the top side. The nSMMl blended PEI membrane (Ml) exhibits more fluorine than the nSMM2 and nSMM3 blended PEI membrane (M2 and M3), respectively. This is related to the order in the fluorine contents of SMMs, i.e. nSMMl > nSMM2 >nSMM3 (Table 20). It is worth tnentioning that the fluorine content at the top side of nSMMl and nSMM2 blended PEI 10 membranes was significantly higher than the bottom side. On the other hand, nSMM3 blended

PEI membrane exhibited only a small différence between the top and the bottom side. This indicates that the migration of nSMMl and nSMM2 to the top-layer was much faster than nSMM3. The fast migration of nSMM2 to the top-layer is reported in [25].

Table 22. XPS results of the prepared membranes for both top and bottom sides

Membrane	F (mass cône., %)
MO	Top: 0.00
Bottom: 0.00
Ml	Top: 30.80
Bottom: 4.62
M2	Top: 28.93
Bottom: 7.68
M3	Top: 5.82
Bottom: 4.89

-7l 16486 [0270] The SEM images of the membrane cross-sections are shown in Figure 25. As can be seen, ail the membranes are of asymmetric structure with a dense top-layer supported by a finger-like structure undemeath. However, the bottom parts of the membranes are different. The finger-)ike structure of the membrane Ml and M3 (Figure 25a and Figure 25c, respectively) reaches the bottom side, where small macro-voids were formed in vertical direction. On the other hand, for the M2 membrane (Figure 25b), the finger-like structure became more irregular in the middle of the cross-section and large macro-voids were formed in horizontal direction.

[0271] The data for the LEPw and product of average pore size and effective porosity per unit effective pore length (rs/L_p) are summarized in Table 23. The increasing order in LEPw values was; M2 (4.0 bar) < Ml (4.5 bar) < M3 (4.7 bar). According to the Lapiace équation [27], the above order should be the same as the order in the decreasing pore size and/or in the increasing hydrophobicity. It is found that both are satisfied when looking into the sr/L_p values in Table 23 (M2 (1.53 x 10 ^s) > Ml (6.02 x 10^-6) > M3 (2.74 x 10^)) and the CA data in Table 21 (M2 (91.93°) < Ml (93.55°) <M3 (100.17°)).

Table 23: Liquid entry pressure of water (LEPw) and sr/L_p of prepared membranes

Membrane	LEP„ (bar)	&/Lf
Ml	4.5	6.02 10’6
M2	4.0	1.53 10'5
M3	4.7	2.74 W6

Membrane Performance ⁴ [0272] Figure 26 shows the DCMD fluxes of the prepared membranes along with those of the commercial membrane (FGLP 1425). Figure 26a shows the DCMD flux versus feed inlet température when distilled water was used as feed. Figure 26b shows the DCMD flux of those membranes when using 0.5M NaCI aqueous solution as feed. As can be observed, both the commercial membrane and the SMMs blended PEI membranes exhibit an exponential increase of the DCMD flux with an increase in the feed inlet température. Both Figures 26a and 26b show that the order in the DCMD flux is M2 > FGLP 1425 > Ml > M3. The nSMM2 blended PEI membrane (M2) showed ca 10 % higher permeate fluxes than the commercial membrane. On the other hand, Ml and M3 exhibited lower fluxes than that of the commercial membrane by 42% and 72%, respectively. \/xZ^

-7216486 [0273] The permeate flux for the NaCl aqueous solution was 25 to 30 % lower than the distilled water flux, reflecting the lower vapor pressure of the sait solution. Another reason for the decrease in the DCMD flux is the concentration polarization due to the presence of NaCl soluté in the feed membrane side [16]. Referring to the studies using the sait solution, the soluté séparation factor (defined by Eq. (37)) was above 99 % for both the prepared and the commercial membranes. This indicates that the SMMs blended membranes Ml, M2 and M3 are promising MD membranes as reported in previous studies [16-18], It is interesting to note that the order in the DCMD flux is M2 >M1 >M3, which is precisely the decreasing order in (τε/Lp). It can therefore be concluded that the higher sr/L_p, the higher the flux will be. This is consistent with the fact that increasing {rz/L_p) coïncides with an increase b either porosity or pore radius or a decrease b effective pore length, which. will naturally lead to a decrease in the barrier résistance. Nevertheless, the parallel relationship found between the gas transport and vapour transport is documented b an earlier study [14], [0274] Furthermore, the reported flux results match well with the LEPw and CA measurements, since the membrane with lowest LEPw and CA exhibited the highest flux due to the fact that it has the largest maximum pore size as was discussed earlier.

[0275] Accordbg to the SEM pictures shown in Figure 25, the macro-voids size of M2 membrane was larger than those of Ml and M3 membranes. This might hâve reduced the barrier résistance toward mass transfer and enhanced the flux as a resuit.

Référencés [1] . K.W. Lawson, D.R. Lloyd, Membrane distillation, J. Membr. Sci., 124 (1997) 1-25.

[2] , J.I. Mengual, L. Pena, Membrane distillation, Current Topic Colloid Interface Sci., I (1997) 17-29.

[3] . A. Burgoyne, M.M. Vahdati, Direct contact membrane distillation, Sep. Sci Technol., 35 (2000) 1257-1284.

[4] , A.M. Alklaibi, N. Lior, Membrane-distillation desalïnation: Status and potential,

Desalbation, 171 (2004) 111-131.

[5] . E. Curcio, E. Drioli, Membrane distillation and related operations - a review, Sep. Purif.

Rev., 34 (2005) 35-86.

-7316486 [6] . M.S. El-Bourawi, Z. Ding, R. Ma, M. Khayet, A Framework for better understanding membrane distillation séparation process, J. Membr. Sci., 285 (2006) 4-29.

[7] . P. Peng, A.G. Fane, X. Li, Desalination by membrane distillation adopting a hydrophilic membrane, Desalination 173 (2005) 45-54.

[8] .C. Feng, B. Shi, G. Li, Y. Wu, Préparation and properties of microporous membrane from poly(vinylidene fluoride-co-tetrafluoroethylene) (F2.4) for membrane distillation, J. Membr. Sci., 237 (2004) 15-24.

[9] .C. Feng, R. Wang, B. Shi, G. Li, Y. Wu, Factors affecting pore structure and performance of poly(vinylidene fluoride-co-hexafluoro propylene) asymmetric porous membrane, J. Membr. Sci., 277 (2006) 55-64.

[10] . B. Li, K.K. Sirkar, Novel membrane and device for vacuum membrane distillation-based desalination process, J. Membr. Sci., 257 (2005) 60-75.

[11] , L. Song, B. Li, K.K. Sirkar, J.L. Girlon, Direct contact membrane distillation-based desalination: Novel membranes, devices, larger-scale studies, and a model, Ind. Eng. Chem. Res., 46 (2007) 2307-2323.

[12] . J. Girlon, L. Song, K.K. Sirkar, Design for cascade of crossflow direct contact membrane distillation, Ind. Eng. Chem. Res., 46 (2007) 2324-2334.

[13] . S. Bonyadi, T. S. Chung, Flux enhancement in membrane distillation by fabrication of dual layer hydrophilic-hydrophobic hollow fiber membranes, J. Membr. Sci., 306 (2007) 134-146.

[14] . M. Khayet, T. Matsuura, Préparation and characterization of Polyvinylidene fluoride membranes for membrane distillation, Ind. Eng. Chem. Res., 40 (2001) 5710-5718.

[15] . M. Khayet, T. Matsuura, Application of surface modifying macromolecules for the préparation of membranes for membrane distillation, Desalination, 158 (2003) 51-56.

[16] . M. Khayet, J.I. Mengual, T. Matsuura, Porous hydrophobic/hydrophilic composite membranes: Application in desalination using direct contact membrane distillation, J. Membr. Sci., 252 (2005) 101-113.

[17] . M. Khayet, T. Matsuura, J. I. Mengual, Porous hydrophobic/hydrophilic composite membranes: Estimation of the hydrophobie layer thickness, J. Membr. Sci., 266 (2005) 68-79.

[18] . M. Khayet, T. Matsuura, J. I. Mengual, M. Qtaishat, Design of novel direct contact membrane distillation membranes, Desalination, 192(2006) 105-111.

-7416486 [19] . M. Khayet, T. Matsuura, M.R. Qtaishat, J.I. Mengual, Porous hydrophobic/hydrophilic composite membranes: Préparation and application in DCMD desalination at higher températures, Desalination, 199 (2006) 180-181.

[20] . M. Khayet, D.E. Suk, R.M. Narbaitz, J.P. Santerre, T. Matsuura, Study on surface modification by surface-modifying macromolecules and its applications in membraneseparation processes, J. Appl. Polym. Sci., 89 (2003) 2902-2916.

[21] . A.L. Ahmad, M. Sarif, S. Ismail, Development of an integrally skinned ultrafiltration membrane for wastewater treatment: effect of different formulations of PSfTNMP/PVP on flux and rejection, Desalination, 179 (2005) 256-263.

[22] . Y. Fang, V.A. Pham, T. Matsuura, J.P. Santerre, R.M. Narbaitz, Effect of surface- modifying macromolecules and solvent évaporation time on the performance of polyethersulfone membranes for the séparation of chloroform/water mixtures by pervaporation, J. Appl. Polym. Sci., 54 (1994) 1937-1943.

[23] . D.E. Suk, T. Matsuura, H.B. Park, Y.M. Lee, Synthesis of a new type of surface modifying macromolecules (nSMM) and characterization and testing of nSMM blended membranes for membrane distillation, J. Membr. Sci., 277 (2006) 177-185.

[24] . P.C. Carman, “Flow of gases through porous media”, Butterworth Publication, London,

UK, 1956.

[25] . D.E. Suk, G. Chowdhury, T. Matsuura, R.M. Narbaitz, P. Santerre, G. Pleizier, Y.

Deslandes, Study on the kinetics of surface migration of surface modifying macromolecules in membrane préparation, Macromolecules, 35 (2002) 3017-3021.

[26] . T. Matsuura, “Synthetic membranes and membranes séparation processes”, CRC Press,

Boca Raton, FL, 1994.

[27] . M. Mulder, “Basic Principles of Membrane Technology”, Kluwer Academie Publisher,

Boston, MA, (1996).

[28] . Zhen-Liang Xu, F. Alsalhy Qusay, Polyethersulfone (PES) hollo fiber ultrafiltration membranes preapred by PES/non-solvent/NMP solution, J. Membr. Sci., 233 (2004) 101-

111.

[29] , D. Rana, T. Matsuura, R.M. Narbaitz, C, Feng, Development and characterization of novel hydrophilic surface modifying macromolecule for polymeric membranes, J. Membr. Sci., 249 (2005) 103-112.

-7516486 [30] . D. Rana, T. Matsuura, R.M. Narbaitz, Novel hydrophilic surface modifying macromolecules for polymeric membranes: Polyuréthane ends capped by hydroxy group, J. Membr. Sci., 282 (2006) 205-216.

[31] . M. Khayet, T. Matsuura, Surface modification of membranes for the séparation of volatile organic compounds from water by pervaporation, Desalination, 148 (2002) 3137.

[32] , L. Martinez, F.J. Florido-Diaz, A. Hernandez, P. Prâdanos, Characterization of three hydrophobie porous membranes used in membrane distillation: Modelling and évaluation of their water vapour penneabilities, J. Membr. Sci., 203 (2002) 15-27.

[33] , J. Barzin, C. Feng, K.C. Khulbe, T. Matsuura, S. S. Madaeni, H. Mirzadeh,

Characterization of polyethersulfone hemodialysis membrane by ultrafiltration and atomic force microscopy, J. Membr. Sci. 237 (2004) 77-85.

[34] , S. Singh, K.C. Khulbe, T. Matsuura, P. Ramamurthy, Membrane characterization by soluté transport and atomic force micrscopy, J. Membr. Sci. 142 (1998) 111-127.

[35] . Y. Fang, V.A. Pham, T. Matsuura, J.P. Santerre, R.M. Narbaitz, Effect of surface- modifying macromolecules and solvent évaporation time on the performance of polyethersulfone membranes for the séparation of chloroform/water mixtures by pervaporation, J. Appl. Polym. Sci., 54 (1994) 1937-1943.

[36] . M. Qtaishat, T. Matsuura, B. Kruczek, M. Khayet, Heat and mass transfer analysis in direct contact membrane distillation, Desalination, 219 (2008) 272-292.

[37] . F. A. Banat, F. Abu Al-Rub, K. Bani-Melhem, Desalination by vacuum membrane distillation: sensitivity analysis, Sep. & Pur. Tech., 33 (2003) 75-85.

[38] . M. Khayet, M.P. Godino, J.I. Mengual, Modelling transport mechanism through a porous partition, J. Non-Equi. Therm., 26 (2001) 1-14.

[39] . R.W. Schofield, A.G. Fane, C.J.D. Fell, Heat and mass transfer in membrane distillation,

J. Membr. Sci., 33 (1987) 299-313.

[40] . M. Khayet, T. Matsuura, Pervaporation and vacuum membrane distillation processes:

Modeling and experiments, AIChE J., 50 (2004) 1679-1712.

[41] . J. Phattaranawik, R. Jiraratananon, A.G. Fane, Effect of pore size distribution and air flux on mass transport in direct contact membrane distillation, J. Membr, Sci., 215 (2003) 7585.

-7616486 [42] . L. Martinez, J.M. Rodriguez-Maroto, On transport résistances in direct contact membrane distillation, J. Membr. Sci., 295 (2007) 28-39.

[43] . F. Laganà, G. Barbiéri, and E. Drioli, Direct contact membrane distillation: modelling and concentration experiments, J. Membr. Sci., 166 (2000) 1-11.

[44] . M. Tomaszewska, Préparation and properties of flat-sheet membranes from polyvinylidene fluoride for membrane distillation, Desalination, 104 (1996) 1-11.

[45] . M. Khayet, Membrane Surface modification and characterization by X-ray photoelectron spectroscopy, atomic force microscopy and contact angle measurements, Appl. Surf. Sci., 238 (2004) 269-272.

[46] . A.O. Imdakem, T. Matsuura, A Monte Carlo simulation model for membrane distillation process: direct contact (MD), J. Membr. Sci., 237(2004) 51-59.

[47] . A.O. ïmdakem, T. Matsuura, Simulation of heat and mass transfer in direct contact membrane distillation (MD): The effect of membrane physical properties, J. Membr. Sci., 262(2005)117-128.

[48] . M. Khayet, A. Velâzquez, J.I. Mengual, Modelling mass transport through a porous partition: Effect of pore size distribution, J. Non-Equilibrium Thermodynamics 29 (2004) 279-299.

[49] . C.A. Speraty, Physical Constants of fluoropolymers, Polymer Handbook, 3^rf Ed., Wiley,

New York, 1989.

[50] . M. Khayet, C.Y. Feng, T. Matsuura, Morphological study of fluorinated asymmetric polyetherimîde ultrafiltration membranes by surface modifying macromolecules, J. Membr. Sci., 213 (2003) 159-180.

[0276] Ail publications, patents and patent applications mentioned in this Spécification are indicative of the level of skill of those skilled in the art to which this invention pertains and are herein incorporated by reference to the same extent as if each individual publication, patent, or patent applications was specifîcally and individually indicated to be incorporated by reference.

[0277] The invention being thus described, it will be obvious that the same may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the invention, and ail such modifications as would be obvious to one skilled in the art are intended to be included within the scope of

-77the claims.

„„ 22 JWL 2013, EKEME USAGHTSarl rCÂMÉKOüN

YAQWfc

TéL- FâxTf

Claims (5)

1. A composite hydrophilic/hydrophobic membrane comprising a hydrophilic polymer layer, a hydrophobie polymer layer and fluorinated surface-modifying macromolecules (SMM).

2. The composite membrane as claimed in claim l, wherein said hydrophilic polymer layer is selected from the group consisting of polysulfone, polyether sulfone, polyetherimide, polyvinylidenfluoride and cellulose acetate.

3. The composite membrane as claimed in any one of claims 1 to 2, wherein said fluorinated surface-modifying macromolecules (SMM) consîst of oligomeric fluoropolymers synthesized using polyuréthane chemistry and tailored with fluorinated end-groups.

4. The composite membrane as claimed in any one of claims 1 to 3, wherein said fluorinated SMM is blended with said hydrophilic polymer layer.

5. The composite membrane as claimed in claim 4, wherein said SMM is selected from the group consisting of poly(urethane propylene glycol) and poly(urea dimethylsiloxane urethane).

6. The composite membrane as claimed in claim 5, wherein said SMM is a poly(urethane propylene glycol) prepared using a two step polymerization method comprising a first polymerization step to form a polyuréthane pre-polymer ftom 4,4’methylene bis(phenylisocyanate) (MDI) and polypropylene glycol (PPG), and a second polymerization step to end-cap the polyuréthane pre-polymer by the addition of 2-(perfluoroaIkyI) éthanol.

7. The composite membrane of claim 6, wherein the ratio of MDI:PPG:FAE is about 3:2:2.

8. The composite membrane as claimed in claim 5, wherein said SMM is a poly(urea dimethylsiloxane urethane) prepared using a two step polymerization method comprising a first polymerization step to form a polyurea pre-polymer from 4,4’methylene bis(phenylisocyanate) (MDI) and α,ω-Ammopropyl poly(dimethyl siloxane) (PDMS), and a second polymerization step to end-cap the polyurea prepolymer by the addition of 2-(perfluoroalkyl)ethanol (FAE).

9. The composite membrane as claimed ïn claim 8, wherein the ratio of MDI:PDMS:FAE is about 2:1:2, about 3:2:2 or about 4:3:3.

10. The composite membrane as claimed in any one of ciaims 1 to 9, wherein said composite membrane has a flux and a morphology conceived to maximize said flux.

11. The composite membrane as claimed in claim 10, wherein said morphology is conceived by compiling mathematical parameters reflecting various characteristics of said morphology.

12. The composite membrane as claimed in claim 11, wherein said mathematical parameters comprise parameters representing a thickness, a porosity density and a thermal conductivity of said hydrophobie layer, and a thickness, a porosity density and a thermal conductivity of said hydrophilic layer.

13. The composite membrane as claimed in claim 12, wherein said morphology is conceived in accordance with:

where/î reflects said morphology.

14. The composite membrane as claimed in any one of ciaims 1 to 13, wherein said composite membrane has a high vapour flux.

15. A membrane distillation systern comprising the composite membrane of any one of ciaims 1 to 14.

-7916486

16. The membrane distillation system as claimed in claim 15, wherein said system is selected from the group consisting of a direct contact membrane distillation system, a vacuum membrane distillation system, a sweeping gas membrane distillation system and an air gap membrane distillation system.

17. A method of manufacturing a composite hydrophilic/hydrophobic membrane comprising a hydrophilic polymer layer and a hydrophobie polymer layer, said method comprising the steps of:

(a) blending a host hydrophilic polymer with fluorinated surface-modifying macromolecules (SMM) and a non-solvent additive in a solvent;

(b) casting said hydrophilic polymer blend and allowing said solvent to evaporate at room température for a predetermined time; and (c) immersing said cast film produced in step (b) in water to allow gélation.

18. The method of manufacturing a composite membrane as claimed in claim 17, further comprising maximizing porosity and minimizing thickness of said hydrophobie polymer layer of said composite membrane in order to increase flux of said composite membrane.

19. The method of manufacturing a composite membrane as claimed in any one of claims 17 to 18, further comprising maximizing thickness, porosity and thermal conductivity of said hydrophilic polymer layer.

20. The method of manufacturing a composite membrane as claimed in any one of claims 17 to 19, wherein said host hydrophilic polymer comprises at least one of polysulfone, polyethersulfone, polytherimide polyvinyltdenefiuoride and cellulose acetate.

21. The method of manufacturing a composite membrane as claimed in any one of claims 17 to 20, wherein said SMM is selected from the group consisting of poly(urethane propylene glycol) and poly(urca dimethylsîloxane urethane).

22. The method of manufacturing a composite membrane as claimed in any one of claims 17 to 21, wherein said non-solvent additive is selected from the group consisting of γbutyrolactone and éthanol. U—>

-8016486

23. The method of manufacturing a composite membrane as claimed in any one of claims

17 to 22, wherein said solvent is selected from the group consisting of N,Ndimethylacetamide and l-methyl-2-pyrrolidinone..

5 24. A method of optimizing the MD performance of a composite hydrophi lic/hydrophobic membrane comprising a hydrophilic polymer layer and a hydrophobie polymer layer, said method comprising the steps of :

(a) maximizing porosity of the top hydrophobie layer of the composite membrane;

(b) minimizing the thickness of the top hydrophobie layer of the composite membrane;

and (c) maximizing the thickness, the porosity and the thermal conductivity of the bottom hydrophilic layer.