NL8503546A - LAMINATED SUBSTRATE AND ARTICLE MADE THEREFROM INCLUDING FLORORATED POLYETHYLENE. - Google Patents
LAMINATED SUBSTRATE AND ARTICLE MADE THEREFROM INCLUDING FLORORATED POLYETHYLENE. Download PDFInfo
- Publication number
- NL8503546A NL8503546A NL8503546A NL8503546A NL8503546A NL 8503546 A NL8503546 A NL 8503546A NL 8503546 A NL8503546 A NL 8503546A NL 8503546 A NL8503546 A NL 8503546A NL 8503546 A NL8503546 A NL 8503546A
- Authority
- NL
- Netherlands
- Prior art keywords
- layer
- polyethylene
- adhesive
- fluorinated polyethylene
- paper
- Prior art date
Description
ί « VO 7546ί «VO 7546
Gelamineerd substraat en daaruit vervaardigd voorwerp, waarin gefluoreerd polyethyleen is opgenomen.Laminated substrate and article made therefrom incorporating fluorinated polyethylene.
De onderhavige uitvinding heeft in algemene zin betrekking op de techniek van het vervaardigen van houders en betreft meer in het bijzonder een samenvouwbare toedieningshouder met een gelamineerde wand-constructie in het lichaamsgedeelte ervan, waarbij permeatie en 5 absorptie van produkt, alsmede zuurstofabsorptie in alle, daarvoor gevoelige gebieden van de houderstructuur in hoofdzaak verhinderd worden.The present invention relates generally to the technique of manufacturing containers and more particularly relates to a collapsible administration container having a laminated wall construction in its body portion, permeation and absorption of product, as well as oxygen absorption in all, previously sensitive areas of the container structure are substantially prevented.
Samenvouwbare tubes van uit metaal en kunststof bestaande materialen zijn sedert lange tijd bekend op het gebied van verpakking.Collapsible tubes made of metal and plastic materials have long been known in the field of packaging.
10 Geëxtrudeerde metalen tubes zijn van nature bros en herhaald gebruik resulteert niet zelden in wandscheuren, zodat vanuit een andere plaats dan de in wezen stijve toedieningsopening produkt wordt afgescheiden.Extruded metal tubes are brittle by nature and repeated use often results in wall cracks so that product is separated from a location other than the substantially rigid delivery opening.
Van de uit de stand der techniek bekende metalen tubes zijn aluminium tubes, hoewel deze waarschijnlijk het minst bros zijn, in hun toe-15 passingen enigszins beperkt, daar het tot nu toe niet mogelijk is geweest op de inwendige oppervlakken ervan een geheel bevredigende bekledingslaag aan te brengen wanneer dit vereist is om aantasting en corrosie van het metaal door een alkalische of zure inhoud en contaminatie van de inhoud door de reactieprodukten te verhinderen. Ondanks de 20 betrekkelijk brosse aard van een metalen tube, maakt de genoemde verrichting vein het inwendig bekleden een extra bewerkingsstap noodzakelijk, die de prijs van het eind-voorwerp noodzakelijkerwijze hoger maakt.Of the metal tubes known in the art, aluminum tubes, although probably the least brittle, are somewhat limited in their applications, as hitherto it has not been possible to obtain a completely satisfactory coating on the internal surfaces thereof. when required to prevent attack and corrosion of the metal by an alkaline or acidic content and contamination of the content by the reaction products. Despite the relatively brittle nature of a metal tube, the said internal coating operation necessitates an additional processing step, which necessarily increases the price of the final article.
Üit polyethyleen en andere kunststoffen gevormde tubes hebben 25 bij het verpakken van vele produkten een wijdverbreid commercieel succes ondervonden; wanneer echter daarin bepaalde andere produkten aanwezig waren, bleken deze na een zekere tijd in kwaliteit achteruit te gaan. Kunststoffen, zoals bijvoorbeeld polyethyleen, zijn in zekere mate doorlatend wanneer zij gebruikt worden in de wanddikten die voor 30 tubulaire houders worden toegepast en van de etherische oliën, die in de meeste tandreinigingsmiddelen voor het op smaak brengen aanwezig zijn, wordt het volume tijdens opslag van de houder kleiner, waardoor het ï - ; 3 4 Ö 5 -2- tandreinigingsmiddel minder aangenaam van smaak wordt.Ook absorbeert de uit'kunststof bestaande houderwand gedurende een. bepaalde tijdsperiode zuurstof en kan hij tenslotte het produkt doen ontleden, hetgeen werkelijk het geval bleek te zijn met fluoride-bevattende tandpasta's.Tubes formed from polyethylene and other plastics have enjoyed widespread commercial success in packaging many products; however, when certain other products were contained therein, these were found to deteriorate in time. Plastics, such as, for example, polyethylene, are permeable to some degree when used in the wall thicknesses used for tubular containers, and of the essential oils contained in most flavoring dentifrices, the volume during storage the holder smaller, making it ï -; 3 4 Ö 5 -2- dentifrice becomes less pleasant in taste. Also the container wall made of plastic absorbs during a. oxygen for a certain period of time and can finally decompose the product, which has been found to be the case with fluoride containing toothpastes.
5 Een ander nadeel van de kunststof-tube is gelegen in het onvermogen van het oppervlak om drukmateriaal of decoratief materiaal gemakkelijk op te nemen. Bovendien bezitten kunststof-tubes bijvoorbeeld diè, welke uit polyethyleen zijn vervaardigd, een geheugen-effeet; d.w.z., dat zij, wanneer zij samengeknepen zijn, niet samengeperst blijven, hetgeen 10 voor tandreinigingsmiddel-tubes een bijzonder nadeel betekent.Another drawback of the plastic tube lies in the inability of the surface to easily absorb printing material or decorative material. In addition, plastic tubes, for example, those made of polyethylene, have a memory effect; that is, when squeezed, they do not remain compressed, which is a particular drawback for dentifrice tubes.
Om de bovenvermelde problemen tegen te gaan, heeft men bijgevolg voorgesteld een metalen folie als versperring tussen het produkt en het uit polyethyleen bestaande tube-lichaam aan te brengen. Dit zou het comprimeerbaarheidsprobleem in zoverre tegengaan, dat de metaal-laag 15 haar comprimeerbaarheid op de kunststof zou opleggen. Bovendien zou de uit metaalfolie bestaande versperring tussen het produkt en het uit polyethyleen bestaande tube-lichaam het genoemde verlies aan etherische oliën en de absorptie van zuurstof verhinderen. Voorgesteld is, de metalen versperring als een tussenlaag tussen bekledingslagen van 20 polyethyleen uit te voeren en daarvan door middel van warmte met of zonder geschikte lijmen een laminaat te vormen. Ofschoon echter een structuur van dit algemene karakter effectief is voor het verhinderen van enige produkt-permeatie en zuurstofabsorptie door het tube-lichaam heen, en in het bijzonder wanneer de binnenste thermoplastische laag 25. een copolymeer is van ethyleen en een daarmee copolymeriseerbaar monomeer met een polaire groep, blijft de mogelijkheid van produktachteruitgang bestaan, hoewel in een veel geringere mate.To counteract the above-mentioned problems, it has therefore been proposed to provide a metal foil as a barrier between the product and the polyethylene tube body. This would counteract the compressibility problem in that the metal layer 15 would impose its compressibility on the plastic. In addition, the metal foil barrier between the product and the polyethylene tube body would prevent said essential oil loss and oxygen absorption. It has been proposed to design the metal barrier as an intermediate layer between coating layers of polyethylene and to laminate it by heat with or without suitable adhesives. However, although a structure of this general character is effective in preventing any product permeation and oxygen absorption through the tube body, and especially when the inner thermoplastic layer 25 is a copolymer of ethylene and a copolymerizable monomer having a polar group, the possibility of product decline remains, although to a much lesser extent.
De aandacht wordt gevestigd op de volgende stand van de techniek: In het U.S. octrooischrift 3.295.725 is een tube beschreven, 30 waarbij de voordelen van een aluminium-tube gecombineerd worden met de voordelen van een kunststof-tube. Deze tube is een gelamineerde samen-vouwbare toedienings-houder, die zowel een metalen versperring als een uit polyethyleen bestaande binnenwand bevat. De thermoplastische laag wordt in algemene zin omschreven als bestaande uit polyalkeen en een 35 copolymeer van een alkeen en een polaire groep bevattend monomeer, dat daarmee copolymeriseerbaar is. Dit laminaat overwint de bovenbeschreven ** -fj *}, #7 & 9 jfc -¾ ?) ^ n -3- è „ beperkingen, behalve voor wat betreft de absorptie van de etherische oliën _uit de tandreinigingsmiddelen.Attention is drawn to the following prior art: In the U.S. U.S. Patent 3,295,725 discloses a tube combining the advantages of an aluminum tube with the advantages of a plastic tube. This tube is a laminated collapsible administration container containing both a metal barrier and a polyethylene inner wall. The thermoplastic layer is generally described as consisting of polyolefin and a copolymer of an olefin and a polar group-containing monomer which is copolymerizable therewith. This laminate overcomes the above-described limitations, except for the absorption of the essential oils from the dentifrices.
In het Canadese octrooischrift 728.525 is ook de ontwikkeling beschreven van een gelamineerde tube, die een binnenlaag van poly-5 ethyleen bevat.Hierbij werd het probleem van de absorptie van smaakstof-olie door de thermoplastische wand ingezien.Canadian Patent 728,525 also describes the development of a laminated tube containing an inner layer of poly-ethylene, recognizing the problem of flavor oil absorption through the thermoplastic wall.
Volgens een andere octrooipublikatie zijn polymeren, die een oppervlaktebehandeling hebben ondergaan, onderzocht voor wat betreft de daaruit vervaardigde voorwerpen. Met betrekking tot het onderzoek 10 van films en houders heeft men volgens het Ü.S. octrooischrift 4.142.032 opgemerkt, dat de eigenschappen van de versperring verbeterd worden door oppervlaktebehandeling met zowel fluor als broom.According to another patent publication, surface treated polymers have been investigated for the articles made therefrom. With regard to the investigation of films and holders, according to the US U.S. Patent 4,142,032 noted that the barrier properties are improved by surface treatment with both fluorine and bromine.
Hierbij werd echter geen tube vervaardigd; het voorwerp bezat geen aluminium; en de eigenschappen van dit polymeer als smaakstof-versperring 15 werden niet onderkend.However, no tube was manufactured for this; the object had no aluminum; and the properties of this polymer as a flavor barrier 15 were not recognized.
Bij de U.S. octrooischriften 4.2926.151, 4.110.518, 4.020.223, 3.647.613 en 4.404.256 betrof het ook vervaardigde voorwerpen, waarbij polymeren waren betrokken, waarvan het oppervlak met fluor was behandeld.At the U.S. Pat. Nos. 4,2926,151, 4,110,518, 4,020,223, 3,647,613 and 4,404,256 also concerned manufactured articles involving polymers whose surface had been treated with fluorine.
In het eerstgenoemde van deze octrooischriften wordt aangetoond, dat de 20 behandeling de oppervlakken ontvankelijk maakte voor lijmen, bekledings- lagen, verven, inkten, decoraties en dergelijke; in het U.S. octrooischrift 4.110.518 wordt getoond, dat het oppervlak zich gedraagt als een elektrische isolator; bij de behandeling volgens het U.S. octrooischrift 4.020.223 werden eigenschappen verleend met betrekking tot het los-25 laten van olievlekken; de behandeling volgens U.S.octrooischrift 3.647.613 verschafte bestandheid tegen oplosmiddelen. Geen van deze voorwerpen waren echter tubes; geen van deze voorwerpen bevatten een aluminium-laag; en in geen van deze octrooischriften wordt melding gemaakt van de bestandheid van deze voorwerpen tegen smaakstof.In the former of these patents it is shown that the treatment made the surfaces susceptible to adhesives, coatings, paints, inks, decorations and the like; in the U.S. U.S. Patent 4,110,518 shows that the surface behaves like an electrical insulator; in the treatment according to the U.S. U.S. Pat. No. 4,020,223 granted oil spill release properties; the treatment of U.S. Patent 3,647,613 provided solvent resistance. None of these objects, however, were tubes; none of these objects contain an aluminum layer; and none of these patents disclose the flavor resistance of these articles.
30 Het is daarom een belangrijk oogmerk van de onderhavige uit vinding een samenvouwbare toedieningshouder te verschaffen met een gelamineerde wandconstructie in het lichaamsgedeelte.It is therefore an important object of the present invention to provide a collapsible administration container with a laminated wall construction in the body portion.
Een ander oogmerk van de uitvinding is gelegen in het verschaffen van een tubulaire houder, waarbij in het lichaamsgedeelte ervan een 35 veelvoud aan vasthechtende lagen aanwezig is, waarvan één der genoemde lagen een versperring tegen produktmigratie en zuurstofabsorptie - v 3 C -ΪΌ «Another object of the invention is to provide a tubular container, in the body portion of which there are a plurality of adhesive layers, one of said layers of which is a barrier against product migration and oxygen absorption.
* V* V
* -4- verschaft, zoals een metalen folie, en een andere van de genoemde lagen bestaat uit een gefluoreerd polyethyleen of mengsel daarvan, dat varieert in dichtheid en kristalliniteit. De laatstgenoemde laag wordt toegepast als binnenste laag en bij voorkeur ook als buitenste laag 5 waarbij daartussenin verschillende extra laminae zijn aangebracht.* -4- provided, such as a metal foil, and another of said layers consists of a fluorinated polyethylene or mixture thereof, which varies in density and crystallinity. The latter layer is used as the innermost layer and preferably also as the outer layer 5, with various additional laminae arranged in between.
Dergelijke extra lagen omvatten papier en geschikte hecht- en lijm-middelen zoals een copolymeer van ethyleen en acrylzuur.Such additional layers include paper and suitable adhesives and adhesives such as a copolymer of ethylene and acrylic acid.
De samenvouwbare toedieningshouder volgens de onderhavige uitvinding kan geconstrueerd worden uit het gelamineerde substraat 10 volgens de onderhavige uitvinding door middel van gebruikelijke en bekende apparaten. Voorbeelden van een dergelijke installatie en methode kunnen gevonden worden in ü.S. octrooischrift 3.832.964.The collapsible administration container of the present invention can be constructed from the laminated substrate 10 of the present invention by conventional and known devices. Examples of such an installation and method can be found in US. U.S. Patent 3,832,964.
Een ander oogmerk van de onderhavige uitvinding is het verschaffen van een methode voor de produktie van gelamineerde tubes, 15 waarbij van een versperringslaag en een daaraan gelamineerd gefluoreerd polyethyleen een tubulair lichaam wordt gevormd; het gelamineerde tube-lichaam wordt dan op een vormgevend element naast een zich ook daarop bevindend versperringselement geplaatst.Another object of the present invention is to provide a method for the production of laminated tubes, whereby a tubular body is formed from a barrier layer and a fluorinated polyethylene laminated thereto; the laminated tube body is then placed on a molding element next to a barrier element also thereon.
Andere oogmerken en voordelen van de uitvinding zullen duidelijker 20 worden naarmate de beschrijving vordert.Other objects and advantages of the invention will become more apparent as the description progresses.
In de tekeningen, waarin steeds dezelfde getallen worden gebruikt om dezelfde delen aan te duiden.- fig. 1 is een dwarsdoorsnede van een fragmentarisch gedeelte van een gelamineerd substraat volgens de onderhavige uitvinding; 25 fig. 2 is een zijaanzicht van een samenvouwbare toedienings houder, waarin de nieuwe opvattingen volgens deze uitvinding belichaamd zijn, waarbij de delen van de lichaamswanden weggebroken zijn om de gelamineerde structuur vollediger te illustreren.In the drawings, in which the same numbers are always used to indicate the same parts. Fig. 1 is a cross-sectional view of a fragmentary portion of a laminated substrate according to the present invention; FIG. 2 is a side view of a collapsible administration container embodying the novel views of the present invention, with the parts of the body walls broken away to more fully illustrate the laminated structure.
De thermoplastische stof volgens de onderhavige uitvinding 30 is gefluoreerd polyethyleen.The thermoplastic material of the present invention is fluorinated polyethylene.
Thans wordt eerst verwezen naar fig. 1 van de tekeningen waarin een substraat 10 in dwarsdoorsnede wordt getoond, waarbij de componenten onthuld worden van de sandwich, die de gelamineerde configuratie gaat samenstellen.Reference is now first made to Fig. 1 of the drawings in which a substrate 10 is shown in cross-section, revealing the components of the sandwich which will assemble the laminated configuration.
35 Men zal begrijpen dat de onderste laag 11 uit een gefluoreerd polyethyleen bestaat. De daarbovenop liggende tweede laag 12 is een hechtende laag, die de gefluoreerd-polyethyleen-laag 11 ver- O o b 4 ö * i -5- bindt met de derde laag 13, die een metalen folie, zoals aluminiumfolie -is. De vierde laag 14 bestaat weer uit een lijm, die het andere oppervlak van de metaalfolielaag 13 hechtend aan een papierlaag 15 vastmaakt. De bovenste laag 16 bestaat uit gefluoreerd polyethyleen.It will be understood that the bottom layer 11 consists of a fluorinated polyethylene. The superimposed second layer 12 is an adhesive layer which bonds the fluorinated polyethylene layer 11 to the third layer 13 which is a metal foil, such as aluminum foil. The fourth layer 14 again consists of an adhesive which adheres the other surface of the metal foil layer 13 to a paper layer 15. The top layer 16 is made of fluorinated polyethylene.
5 De gefluoreerde polyethylenen zijn bijzonder geschikt, omdat zij zeer zwakke smaakstof-absorptie-kenmerken hebben, zoals blijkt uit de volgende tabellen, waarin gefluoreerde polyethylenen vergeleken worden met polyethyleen, waarbij de dikten van de lagen of bekleding dezelfde zijn:The fluorinated polyethylenes are particularly suitable because they have very weak flavor absorption characteristics, as can be seen from the following tables comparing fluorinated polyethylenes with polyethylene, the thicknesses of the layers or coating being the same:
10 TABEL A10 TABLE A
Relatieve smaakstofabsorptie in polymeren uit smaakstof bevattend tandreinigingsmiddel k__Relative flavor absorption in flavor-containing polymeric dentifrice k__
22,2°C 32,2°C 48,9°C22.2 ° C 32.2 ° C 48.9 ° C
Aluminium 0,4 0 0,4 15 Polyethyleen met hoge dichtheid,dat een oppervlaktebehandeling met fluor had ondergaan 22 37 90 HD-3 (Air Products)Aluminum 0.4 0 0.4 15 High density polyethylene that has been surface treated with fluorine 22 37 90 HD-3 (Air Products)
Polyethyleen met hoge dichtheid 20 HD-0 (Air Products) 98 94 100High density polyethylene 20 HD-0 (Air Products) 98 94 100
Polyethyleen met lage dichtheid LD-0 (Air Products) 100 94 111 x Alle getallen ten opzichte van polyethyleen met lage dichtheid bij 22,2°C arbitrair op 100 gesteld; hoe lager het getal des te 25 minder smaakstof geabsorbeerd is.Low Density Polyethylene LD-0 (Air Products) 100 94 111 x All numbers relative to Low Density Polyethylene at 22.2 ° C arbitrarily set to 100; the lower the number, the less flavor is absorbed.
8 -ï ij o o 9 ï> t -6-8 -ï ij o o 9 ï> t -6-
TABEL BTABLE B
Polymeer-absorptie van onversneden smaakstofoliePolymer absorption of uncut flavoring oil
Absorptie (%)Absorption (%)
Aluminium 0Aluminum 0
Polyethyleen met hoge dichtheid,waarvan het oppervlak jj]et-fluor was behandeld HD-3 (Air Products) 3,3.High density polyethylene, the surface of which was treated with fluorine HD-3 (Air Products) 3.3.
5 Polyethyleen met hoge dichtheid HD-0 (Air Products) 4,85 High density polyethylene HD-0 (Air Products) 4.8
Polyethyleen met lage dichtheid LD-0 (Air Products) 7,9Low density polyethylene LD-0 (Air Products) 7.9
Polyethyleen met lage dichtheid 10 NA (USI) 10,0 lonomeerLow density polyethylene 10 NA (USI) 10.0 lonomer
Surlyn 1707 (DuPont) 15,7 lonomeerSurlyn 1707 (DuPont) 15.7 lonomer
Surlyn 1605 (DuPont) 19,0 15 lonomeerSurlyn 1605 (DuPont) 19.0 15 lonomer
Surlyn 1706 (DuPont) 24,3 -·, -· · -J / -¾ Q } U 0 0 } 0 -7-Surlyn 1706 (DuPont) 24.3 -, - · -J / -¾ Q} U 0 0} 0 -7-
TABEL CTABLE C
Polymeer-absorptie van onversneden, smaakstofolie % geabsorbeerde smaakstofPolymer absorption of uncut flavoring oil% absorbed flavoring
Polyethyleen met lage dichtheid^, 5 waarvan het oppervlak met fluor is behandeld, No. 74 2,6Low-density polyethylene, the surface of which has been treated with fluorine, No. 74 2.6
Polyethyleen met lage dichtheid^,waarvan het oppervlak met fluor$.s behandeld, No.76 2,6Low-density polyethylene, the surface of which is treated with fluorine, No. 76, 2.6
Polyethyleen met lage dichtheid1 5,5 10 Polyethyleen met lage dichtheid (controle) ^ 5,6 _+ 0,14^ (c)Low density polyethylene1 5.5 10 Low density polyethylene (control) ^ 5.6 _ + 0.14 ^ (c)
Ionomeer 7,4Ionomer 7.4
Ionomeer ^ 12,2 (a) Het polyethyleen met lage dichtheid is Lupolen 1804H (BASF) (b) Tenite 154 (Eastman) 15 (c) Surlyn 8940 (DuPont) (d) Surlyn 8920 (DuPont) (e) n=3Ionomer ^ 12.2 (a) The low density polyethylene is Lupolen 1804H (BASF) (b) Tenite 154 (Eastman) 15 (c) Surlyn 8940 (DuPont) (d) Surlyn 8920 (DuPont) (e) n = 3
TABEL DTABLE D
Verlies van smaakstof uit smaakstof bevattend tandreinigingsmiddel door _absorptie in de polymeren_Loss of flavor from a dentifrice-containing dentifrice due to absorption into the polymers
Smaakstofverlies x 20 -Flavor loss x 20 -
Polyethyleen met lage dichtheid ^, waarvan het oppervlak met fluor is behandeld, No. 76 56Low-density polyethylene, the surface of which has been treated with fluorine, No. 76 56
Polyethyleen met lage dichtheid^,waarvan 25 het oppervlak met fluor is behandeld,No.74 64Low density polyethylene, 25 of which are surface treated with fluorine, No. 74 64
Ionomeer ^ 88 (o)Ionomer ^ 88 (o)
Ionomeer 96Ionomer 96
Polyethyleen met lage dichtheid (controle) ^ 100Low density polyethylene (control) ^ 100
Polyethyleen met lage dichtheid 136 30 * Ten opzichte van polyethyleen met lage dichtheid (BASF)(controle), waarvan het verlies arbitrair op 100 is gesteld; hoe lager het getal, des te minder smaakstof-verlies uit het tandreinigingsmiddel.Low density polyethylene 136 30 * Relative to low density polyethylene (BASF) (control), the loss of which is arbitrarily set at 100; the lower the number, the less flavor loss from the dentifrice.
« Γ· -δία) _LDPE is Lupolen 1804 (BASF) (b) Surlyn 8920 (DuPont) (c) Surlyn 8940 (DuPont) (d) Tenite 154 (Eastman) 5 Er is rekening mee gehouden, dat in het kader van de uitvinding de lijmen een copolymeer van ethyleen en acrylzuur of methacrylzuur, of natrium- of zinkzouten daarvan in een verdunningsmiddelsysteem kunnen zijn.«Γ · -δία) _LDPE is Lupolen 1804 (BASF) (b) Surlyn 8920 (DuPont) (c) Surlyn 8940 (DuPont) (d) Tenite 154 (Eastman) 5 It has been taken into account that under the The glues may be a copolymer of ethylene and acrylic acid or methacrylic acid, or sodium or zinc salts thereof in a diluent system.
De metaalfolie is bij voorkeur aluminium-folie.The metal foil is preferably aluminum foil.
10 Het is wenselijk, dat de papierlaag uit kraft-papier bestaat.It is desirable that the paper layer consists of kraft paper.
Het diktebereik van elk van de lagen is als volgt: Gefluoreerd-polyethyleen-laag 11: 0,0127 mm tot 0,0762 mm, bij voorkeur 0,0254 mm.The thickness range of each of the layers is as follows: Fluorinated polyethylene layer 11: 0.0127 mm to 0.0762 mm, preferably 0.0254 mm.
Hechtingslaag 12: voldoende om hechting te garanderen. Metaalfolie- 15 laag 13: 0,0127 mm tot 0,0508 mm, bij voorkeur 0,0254 mm .Bonding layer 12: sufficient to ensure bonding. Metal foil layer 13: 0.0127 mm to 0.0508 mm, preferably 0.0254 mm.
Hechtingslaag 14 : voldoende om hechting te garanderen Papierlaag 15 : 0,0381 mm tot 0,0635 mm, bij voorkeur 0,0508 mm. Gefluoreerd-polyethyleen-laag 16: 0,0889 mm tot 0,1270 mm, bij voorkeur 0,1016 mm.Bonding layer 14: sufficient to ensure bonding. Paper layer 15: 0.0381 mm to 0.0635 mm, preferably 0.0508 mm. Fluorinated polyethylene layer 16: 0.0889 mm to 0.1270 mm, preferably 0.1016 mm.
20 De bovenste gefluoreerd-polyethyleen-laag 16 is aan de papierlaag 15 vastgehecht door aan het substraat voldoende warmte en druk toe te dienen. Voor het geval, dat toediening van warmte en druk niet geschikt is moet een geschikte lijm worden gebruikt.The upper fluorinated polyethylene layer 16 is adhered to the paper layer 15 by applying sufficient heat and pressure to the substrate. In the event that application of heat and pressure is not suitable, a suitable adhesive must be used.
Fig. 2 is een voorbeeld van de gelamineerde structuur van een 25 samenvouwbare houder, waarbij de lagen"zijn weergegeven als in fig. 1 met laag 11 als de binnenste en waarbij de andere lagen uit dezelfde materialen bestaan en zich in dezelfde volgorde bevinden als hierin getoond wordt.Fig. 2 is an example of the laminated structure of a collapsible container, wherein the layers "are shown as in FIG. 1 with layer 11 as the innermost and the other layers are the same materials and are in the same order as shown herein .
Aangenomen wordt, dat uit het voorafgaande duidelijk blijkt, 30 dat aanvraagster een samenvouwbare houder-structuur heeft verschaft, die de tot dusverre volgens de stand van de techniek onopgeloste problemen aanzienlijk verkleint. Het gelamineerde substraat en het gelamineerde schouderstuk 20 elimineert produkt-permeatie en zuurstof-absorptie in aanzienlijke mate.It is believed that it is clear from the foregoing that Applicant has provided a collapsible container structure which substantially reduces the problems solved hitherto. The laminated substrate and the laminated shoulder pad 20 substantially eliminate product permeation and oxygen absorption.
O / . ^ * *3 -9- — . Λί pe buitenlaag, bestaande uit een gefluoreerd-polyethyleen is een thermoplastische laag, die tijdens een kant-zomingsstap kan smelten en een adequate bescherming aan de tussenlaag van papier en de tussenlaag van metaalfolie kan bieden. De zoomtechniek bij een 5 samenvouwbare tandreinigingsmiddel-tube van het hierin beschreven algemene type kan aan het ü.S. octrooischrift 3.295.725 worden ontleend.O /. ^ * * 3 -9- -. A fluorinated polyethylene outer layer is a thermoplastic layer that can melt during a side-summer step and provide adequate protection to the paper interlayer and metal foil interlayer. The zoom technique on a collapsible dentifrice tube of the general type described herein can be performed on the U.S. No. 3,295,725 are derived.
De buitenlaag van gefluoreerd polyethyleen en papier kan echter worden geëlimineerd, indien defolieversperring voldoende dikte heeft om weerstand te bieden aan beschadiging, en door een thermoplastisch 10 materiaal in de overslag-kantzoom te laten vloeien tijdens het lassen daarvan wanneer een dergelijk systeem wordt gebruikt.However, the fluorinated polyethylene and paper outer layer can be eliminated if the film barrier has sufficient thickness to resist damage, and to flow a thermoplastic material into the wrap-over seam during welding when such a system is used.
Voorts kan in een uit drie lagen bestaand laminaat, dat uit papier, folie en gefluoreerd polyethyleen op de beschreven wijze is gevormd, de buitenlaag van papier zijn. Daar de buitenste en binnenste 15 laag bij voorkeur uit hetzelfde materiaal bestaat, worden de gevouwen randen van de uit het substraat vervaardigde tube gemakkelijk door hitte aan elkaar gehecht.Een geschikte lijm kan worden toegepast wanneer het aaneenhechten door hitte niet mogelijk is. Deze modificatie geldt als extra modificatie naast het eerder genoemde vier-laags-laminaat, 20 bestaande uit, van buiten naar binnen gefluoreerd polyethyleen, papier, folie en gefluoreerd polyethyleen.Furthermore, in a three-layer laminate formed of paper, foil and fluorinated polyethylene in the manner described, the outer layer may be of paper. Since the outer and inner layers preferably consist of the same material, the folded edges of the tube made of the substrate are easily heat-bonded together. A suitable adhesive can be used when heat-bonding is not possible. This modification is an additional modification in addition to the aforementioned four-layer laminate, consisting of fluorinated polyethylene from the outside to the inside, paper, foil and fluorinated polyethylene.
Er is rekening mee gehouden, dat zo nodig tussen de laminae geschikte lijmen zullen worden gebruikt.It has been taken into account that suitable adhesives will be used between the laminae if necessary.
Gefluoreerd polyethyleen kan ook worden gebruikt voor het 25 schouderstuk, de dop, de hals, de zuiger en bij de constructie van toedieningskleppen voor andere tandreinigingsmiddel-toedieningsinrich-tingen, in het bijzonder in samenhang met de inwendige delen, die aan het zich er in bevindende tandreinigingsmiddel zijn blootgesteld en, wederom, zullen natuurlijk, waar dit vereist is, verenigbare lijmen 30 worden gebruikt.Fluorinated polyethylene can also be used for the yoke, cap, neck, plunger and in the construction of delivery valves for other dentifrice delivery devices, particularly in connection with the internals contained therein dentifrice and, again, compatible adhesives 30 will of course be used where required.
Wanneer het materiaal als een film wordt gegoten op de binnen-oppervlakken van fiber drums, die voor opslag van een tandreinigingsmiddel, waaraan smaakstof is toegevoegd, worden toegepast, zal dat materiaal bovendien het verlies aan smaakstof binnenin de druis vertragen, waarbij 35 de opslagduur wordt verlengd.Moreover, when the material is cast as a film on the inner surfaces of fiber drums used for storage of a dentifrice, to which flavoring has been added, that material will retard the loss of flavor within the grout, thereby increasing the storage time. extended.
Verscheidene modificaties van de uitvinding zijn hierin beschreven en deze en andere wijzigingen kunnen natuurlijk tot stand worden gebrachtSeveral modifications of the invention have been described herein, and these and other modifications can of course be accomplished
Λ ΓΛ *sr -* JΛ ΓΛ * sr - * J
öDü v ·; : ü 4 * -10- zonder van de nieuwe opvattingen van de onderhavige bijdrage af te wijken.öDü v ·; : ü 4 * -10- without departing from the new views of the present contribution.
-¾ W f3* f 9 3 ö ^ ^-¾ W f3 * f 9 3 ö ^ ^
Claims (10)