NL1000871C2 - Cement-bound constructional component - Google Patents

Cement-bound constructional component Download PDF

Info

Publication number
NL1000871C2
NL1000871C2 NL1000871A NL1000871A NL1000871C2 NL 1000871 C2 NL1000871 C2 NL 1000871C2 NL 1000871 A NL1000871 A NL 1000871A NL 1000871 A NL1000871 A NL 1000871A NL 1000871 C2 NL1000871 C2 NL 1000871C2
Authority
NL
Netherlands
Prior art keywords
building element
filler
building
cement
composition
Prior art date
Application number
NL1000871A
Other languages
Dutch (nl)
Inventor
Pieter De Bruin
Original Assignee
De Bruin Eisinga Anna Geziena
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by De Bruin Eisinga Anna Geziena filed Critical De Bruin Eisinga Anna Geziena
Priority to NL1000871A priority Critical patent/NL1000871C2/en
Application granted granted Critical
Publication of NL1000871C2 publication Critical patent/NL1000871C2/en

Abstract

The component is baked or dried in a mould to form a block. The filler material consists of sand and mostly whole seashells. The bonding material can include seashell(sic) lime. One or more of the block surfaces can be polished, and a heater element can be mounted in or on it, with connections to a central-heating system. The mixture used can contain a colouring agent.

Description

55

BOUWELEMENTBUILDING ELEMENT

De uitvinding betreft een mengsel ter vervaardiging van steenachtige bouwelementen, welke samenstelling althans cement bevattend bindmiddel en vulmiddel bevat, en 10 in een mal te bakken, te persen of te drogen is om het bouwelement te vervaardigen. Verder betreft de uitvinding een bouwelement, dat is vervaardigd uit een in een mal gebakken, geperst of gedroogd mengsel van althans cement bevattend bindmiddel en vulmiddel.The invention relates to a mixture for the production of stony building elements, which composition contains at least cement-containing binder and filler, and which can be baked, pressed or dried in a mold to produce the building element. The invention furthermore relates to a construction element, which is manufactured from a mold baked, pressed or dried mixture of binder and filler containing at least cement.

15 Een dusdanige samenstelling en bouwelement zijn algemeen bekend. Veelal, zoals in het geval van een beton-muur, bevat het vulmiddel zand, waaraan kiezels zijn toegevoegd om de structurele integriteit van het bouwelement te verhogen. De kwaliteit van het toegepaste zand, in 20 het bijzonder de mate van grofheid hiervan, de kwaliteit van het cement, en de mengverhoudingen van deze componenten, en tevens het soort gebruikte kiezels zijn bepalende factoren voor het gebruik, waarvoor het bouwelement geschikt is. Dit gebruik is afhankelijk van de sterkte van 25 het bouwelement. Een betonmuur behoort bijvoorbeeld een grotere sterkte te bezitten dan een dakpan.Such a composition and building element are generally known. Usually, as in the case of a concrete wall, the filler contains sand, to which pebbles have been added to increase the structural integrity of the building element. The quality of the sand used, in particular the degree of coarseness thereof, the quality of the cement, and the mixing ratios of these components, as well as the type of pebbles used, are determining factors for the use for which the construction element is suitable. This use depends on the strength of the building element. For example, a concrete wall should have greater strength than a roof tile.

Bouwelementen van het bekende soort hebben als nadeel, dat de produktie van cement en hieraan toe te voegen kalk, en de winning van zand en, wanneer van toepassing, 30 kiezels op grote bezwaren met betrekking tot het milieu stuiten.Construction elements of the known type have the drawback that the production of cement and lime to be added thereto, and the extraction of sand and, if applicable, pebbles encounter major environmental concerns.

De uitvinding heeft als doel een mengsel en een bouwelement te verschaffen, die zijn vervaardigd uit natuurlijke grondstoffen, en het bovengenoemde bezwaar op 35 te heffen, waarbij de samenstelling en het bouwelement volgens de uitvinding zich onderscheiden doordat het vulmiddel zand en in hoofdzaak gehele schelpen bevat.The object of the invention is to provide a mixture and a building element, which are manufactured from natural raw materials, and to eliminate the above drawback, wherein the composition and the building element according to the invention are distinguished in that the filler contains sand and substantially whole shells .

10 00 87 1 .10 00 87 1.

22

Wanneer schelpen aan het zand zijn toegevoegd om tezamen hiermee de grove toeslag te vormen, waarbij deze schelpen op een zeer eenvoudige en milieuvriendelijk wijze kunnen worden gewonnen, verkrijgen de bouwelementen een 5 sterkte, die vergelijkbaar is met die van bouwelementen met kiezels.When shells have been added to the sand to form together with it the coarse aggregate, whereby these shells can be extracted in a very simple and environmentally friendly manner, the building elements acquire a strength comparable to that of building elements with pebbles.

Volgens een ander aspect van de uitvinding bevat het bindmiddel schelpkalk. Het schelpkalk vormt tezamen met het cement het bindmiddel. Het schelpkalk kan op eenvoudi-10 ge en milieuvriendelijke wijze worden verkregen door bewerking van gewonnen schelpen. Deze wijze van kalkwin-ning is vanuit een ecologisch standpunt veruit te verkiezen boven bekende kalkwinningswijzen.According to another aspect of the invention, the binder contains shell lime. The shell lime, together with the cement, forms the binder. The shell lime can be obtained in a simple and environmentally friendly manner by processing extracted shells. From an ecological point of view, this method of lime extraction is by far preferable to known lime extraction methods.

De uitvinding zal hieronder nader worden toegelicht 15 aan de hand van voorbeelden van samenstellingen, waaruit verschillende soorten bouwelementen kunnen worden vervaardigd.The invention will be further elucidated below on the basis of examples of compositions from which different types of building elements can be manufactured.

VOORBEELD 1 20EXAMPLE 1 20

Dit voorbeeld betreft gevelstenen met breukvlak, die worden vervaardigd in overeenstemming met de uitvinding. Dergelijke gevelstenen worden als volgt gefabriceerd. Een mengsel met de hieronder beschreven samenstelling wordt in 25 een mal gestort, waarbij deze mal is gevormd door een vlakke bak met een op de bodem hiervan aangebracht patroon opstaande richels. Het patroon richels komt overeen met de afmetingen van de stenen. De bak wordt tot boven het niveau van de richels volgestort. Bij voorkeur is de 30 hoogte van de door de samenstelling gevormde, gestorte laag slechts enigszins groter dan het niveau van de richels. Na gedurende een periode te zijn gedroogd wordt de geharde laag langs de met het richel-patroon overeenkomende breukvlakken gebroken, waardoor de afzonderlijke stenen 35 worden verkregen.This example concerns facing bricks, which are manufactured in accordance with the invention. Such facing bricks are manufactured as follows. A mixture with the composition described below is poured into a mold, this mold being formed by a flat tray with a pattern of upright ridges arranged on the bottom thereof. The pattern of ledges matches the dimensions of the stones. The bucket is poured above the level of the ledges. Preferably, the height of the deposited layer formed by the composition is only slightly greater than the level of the ridges. After being dried for a period of time, the cured layer is broken along the fracture surfaces corresponding to the ridge pattern, whereby the individual stones are obtained.

Voor deze gevelstenen is de verhouding tussen het volume van het vulmiddel (V) en het volume van het bindmiddel (B) bepaald op V : B = 5,4 : 1 .For these facing bricks, the ratio between the volume of the filler (V) and the volume of the binder (B) is set at V: B = 5.4: 1.

10 00 87 1.10 00 87 1.

33

Het vulmiddel is samengesteld uit zand en schelpen, waarbij 60 % van het volume van het vulmiddel bestaat uit zand, waarvoor bij voorkeur gebruik wordt gemaakt van grof zeezand, en 40 % van het volume van het vulmiddel bestaat 5 uit schelpen.The filler is composed of sand and shells, with 60% of the volume of the filler consisting of sand, preferably using coarse sea sand, and 40% of the volume of the filler consisting of shells.

Het bindmiddel is samengesteld uit cement en schelpkalk, waarbij de verhouding tussen het volume van het cement (C) en het volume van de schelpkalk (S) is bepaald op C : S = 2 : 1 .The binder is composed of cement and shell lime, the ratio between the volume of the cement (C) and the volume of the shell lime (S) being determined at C: S = 2: 1.

10 Proeven hebben uitgewezen, dat de gevelstenen met breukvlak met de hierboven beschreven samenstelling minimaal een druksterkte van 25 N/mm2 hebben, na gedurende 28 dagen te zijn gedroogd. Deze druksterkte voldoet aan heden aan dergelijke stenen gestelde eisen, en derhalve zijn 15 deze stenen goed geschikt om toegepast te worden. De stenen behoeven derhalve niet noodzakelijkerwijs te worden gebakken.Tests have shown that the facing bricks with fracture surface with the above-described composition have a minimum compressive strength of 25 N / mm 2 after being dried for 28 days. This compressive strength meets the requirements of such bricks today, and therefore these bricks are well suited for application. The stones therefore do not necessarily have to be baked.

VOORBEELD 2 20EXAMPLE 2 20

Dit voorbeeld betreft gevelstenen met een uitgewassen zichtvlak, die worden vervaardigd in overeenstemming met de uitvinding.This example concerns facing bricks with a washed-out visible surface, which are manufactured in accordance with the invention.

Deze stenen worden als volgt gefabriceerd. Eerst 25 wordt een met die van voorbeeld 1 vergelijkbare bak tot het niveau van de richels volgestort met een gebruikelijk mengsel van cement en kalk met zand en kiezels. Hierover wordt een mengsel met een hierna beschreven samenstelling gestort en wordt vloeistof, bij voorkeur water, over de op 30 deze wijze gevormde deklaag gespoeld om deze deklaag te vereffenen. Deze deklaag is bedoeld om het aanzicht van de steen te vormen in de ingemetselde toestand van de steen.These stones are manufactured as follows. First, a bin comparable to that of Example 1 is filled up to the level of the ridges with a usual mixture of cement and lime with sand and pebbles. A mixture of a composition described below is poured over this and liquid, preferably water, is rinsed over the top layer formed in this way in order to equalize this top layer. This coating is intended to form the appearance of the stone in the bricked state of the stone.

Voor de deklaag van deze gevelstenen is de verhouding tussen het volume van het vulmiddel (V) en het volume van 35 het bindmiddel (B) bepaald op V : B = 4,3 : 1 .For the top layer of these facing bricks, the ratio between the volume of the filler (V) and the volume of the binder (B) is determined at V: B = 4.3: 1.

Het vulmiddel is samengesteld uit zand en schelpen, waarbij 23 % van het volume van het vulmiddel bestaat uit zand, waarvoor bij voorkeur gebruik wordt gemaakt van fijn 10 00 87 1 .The filler is composed of sand and shells, 23% of the volume of the filler being sand, preferably using fine 10 00 87 1.

4 zeezand, en 77 % van het volume van het vulmiddel bestaat uit schelpen.4 sea sand, and 77% of the filler volume consists of shells.

Het bindmiddel is samengesteld uit cement en schelpkalk, waarbij de verhouding tussen het volume van het 5 cement (C) en het volume van de schelpkalk (S) is bepaald op C : S = 2 : 1 , hetgeen gelijk is aan de betreffende verhouding bij het hierboven beschreven voorbeeld 1.The binder is composed of cement and shell lime, the ratio between the volume of the cement (C) and the volume of the shell lime (S) being determined at C: S = 2: 1, which is equal to the respective ratio at the example 1 described above.

Ook voor dit voorbeeld hebben proeven uitgewezen, dat de gevelstenen met een uitgewassen zichtvlak met de hier-10 boven beschreven samenstelling minimaal een druksterkte van 25 N/mm2 hebben, na gedurende 28 dagen te zijn gedroogd. Deze druksterkte voldoet aan heden aan dergelijke stenen gestelde eisen, en derhalve zijn deze stenen goed geschikt om toegepast te worden.For this example as well, tests have shown that the facing bricks with a washed face with the composition described above have a minimum compressive strength of 25 N / mm 2 after being dried for 28 days. This compressive strength satisfies the requirements of such bricks today, and therefore these bricks are well suited for application.

1515

De hierboven beschreven voorbeelden van de uitvinding hebben beide betrekking op produktie van stenen, die na voltooiing bijvoorbeeld naar een bouwplaats kunnen worden getransporteerd om aldaar te worden gebruikt. Het is 20 echter evenwel mogelijk voor het vervaardigen van een muur van een gebouw een bekisting op de bouwplaats vol te storten met een samenstelling volgens de onderhavige uitvinding. In dit geval is echter een samenstelling met die van de voorbeelden afwijkende verhoudingen vereist, 25 teneinde een voor deze toepassing gewenste sterkte te verkrijgen.The examples of the invention described above both relate to the production of bricks, which after completion can be transported, for example, to a construction site for use there. However, it is possible, for the manufacture of a wall of a building, to fill in a formwork on the construction site with a composition according to the present invention. In this case, however, a composition with ratios different from those of the examples is required in order to obtain a strength desired for this application.

In een uitvoeringsvorm van de uitvinding zijn bouwelementen gepolijst, waardoor deze als decoratief afwer-kingselement in een bouwwerk kunnen worden toegepast.In one embodiment of the invention, building elements are polished, so that they can be used as a decorative finishing element in a building.

30 Gepolijste bouwelementen zijn bijvoorbeeld toepasbaar als gevel- of wandbeplatingen, dakpannen, vloertegels, vensterbanken of drempels. Gepolijste bouwelementen volgens de onderhavige uitvinding kunnen tevens worden toegepast als bijvoorbeeld decoratieve gebruiksobjecten, zoals keu-35 kenbladen of tafelbladen.Polished building elements can be used, for example, as facade or wall cladding, roof tiles, floor tiles, window sills or thresholds. Polished building elements according to the present invention can also be used as, for example, decorative utensils, such as kitchen tops or table tops.

Verder is toepassing van een samenstelling volgens de uitvinding mogelijk als sierpleister, welke op een bestaande muur of vloer aangebracht kan worden om een ander 10 00 871.Furthermore, use of a composition according to the invention is possible as a decorative plaster, which can be applied to an existing wall or floor for another 10 00 871.

5 decoratief effect te bewerkstelligen, dat bijvoorbeeld vergelijkbaar is met ruw granol, waarbij echter de schelpen in de structuur duidelijk waarneembaar zijn.5 to achieve a decorative effect, which is comparable, for example, to crude granol, but the shells are clearly visible in the structure.

Tevens zijn toepassingen van een bouwelement volgens 5 de uitvinding buitenshuis mogelijk, bijvoorbeeld als trottoirtegel, trottoirband of klinker. De samenstelling kan tevens worden toegepast bij het vervaardigen van uiterst duurzame tuinmeubels, waarbij dergelijke meubels tevens gepolijst kunnen zijn.Applications of a building element according to the invention are also possible outdoors, for example as a curb tile, curb or clinker. The composition can also be used in the manufacture of extremely durable garden furniture, whereby such furniture can also be polished.

10 Het is gebleken, dat een steen, een te storten muur van een gebouw of een dergelijke volgens de uitvinding, dat wil zeggen de samenstelling volgens de uitvinding na uitharden hiervan, goede isolerende eigenschappen heeft. Met voordeel kan een dusdanig bouwelement derhalve zijn 15 voorzien van een verwarmingselement, dat bij voorkeur is aangesloten op een in het gebouw aanwezige centrale ver-warmingsinstallatie. Wanneer het een in het dusdanige bouwelement aangebracht elektrisch verwarmingselement betreft, behoeft dit slechts te worden verbonden met het 20 spanningsnet. Het verwarmingselement behoeft echter niet noodzakelijkerwijs in het binnenste van het bouwelement te zijn aangebracht, maar kan hier tevens dicht tegen zijn geplaatst. In beide gevallen vervult het bouwelement onder invloed van het verwarmingselement en tezamen hiermee de 25 functie van een warmtebron.It has been found that a stone, a wall of a building to be poured or the like according to the invention, that is to say the composition according to the invention after curing thereof, has good insulating properties. Advantageously, such a building element can therefore be provided with a heating element, which is preferably connected to a central heating installation present in the building. If it concerns an electric heating element arranged in such a building element, this need only be connected to the voltage network. However, the heating element does not necessarily have to be arranged in the interior of the building element, but can also be placed close to it. In both cases the building element fulfills the function of a heat source under the influence of the heating element and together with this.

In het bijzonder, wanneer het bouwelement een decoratieve eigenschap bezit, kan deze eigenschap worden versterkt, doordat aan het mengsel volgens de uitvinding kleurstof is toegevoegd. Op deze wijze kan de kleur van de 30 schelpen in de samenstelling en derhalve in de uit de samenstelling vervaardigde bouwelementen worden geaccentueerd. Tevens kan op deze wijze een op de kleurschakering van verscheidene soorten marmer gelijkend uiterlijk van het bouwelement worden bewerkstelligd.In particular, if the building element has a decorative property, this property can be enhanced by the addition of dye to the mixture according to the invention. In this way, the color of the shells can be accentuated in the composition and, therefore, in the building elements manufactured from the composition. It is also possible in this way to achieve an appearance of the building element, similar to the color shading of various types of marble.

35 Verder zal duidelijk zijn, dat ook alleen het gebruik van schelpkalk in het bindmiddel, waarbij het vulmiddel geheel in overeenstemming met de bekende techniek bijvoor- 10 00 87 1 .It will further be clear that also only the use of shell lime in the binder, wherein the filler is entirely in accordance with the known technique, for example, 00 87 1.

6 beeld kiezels of alleen zand bevat, binnen het kader van de onderhavige uitvinding ligt.6 image containing pebbles or sand only, is within the scope of the present invention.

10 00 87 1 .10 00 87 1.

Claims (8)

1. Samenstelling ter vervaardiging van steenachtige bouwelementen, welke samenstelling althans cement bevat- 5 tend bindmiddel en vulmiddel bevat, en in een mal te bakken of te drogen is om het bouwelement te vervaardigen, met het kenmerk, dat het vulmiddel zand en in hoofdzaak gehele schelpen bevat.1. Composition for the manufacture of stony building elements, which composition contains at least cement containing binder and filler, and can be baked or dried in a mold to produce the building element, characterized in that the filler is sand and substantially whole contains shells. 2. Samenstelling volgens conclusie 1, met het ken-10 merk, dat het bindmiddel schelpkalk bevat.2. A composition according to claim 1, characterized in that the binder contains shell lime. 3. Bouwelement, dat is vervaardigd uit een in een mal gebakken of gedroogd mengsel van althans cement bevattend bindmiddel en vulmiddel, met het kenmerk, dat het vulmiddel zand en in hoofdzaak gehele schelpen bevat.3. Building element, which is manufactured from a mold-baked or dried mixture of at least cement-containing binder and filler, characterized in that the filler contains sand and substantially whole shells. 4. Bouwelement volgens conclusie 3, met het kenmerk, dat het bindmiddel schelpkalk bevat.Building element according to claim 3, characterized in that the binder contains shell lime. 5. Bouwelement volgens conclusie 3 of 4, gekenmerkt door ten minste één gepolijst oppervlak.Building element according to claim 3 or 4, characterized by at least one polished surface. 6. Bouwelement volgens één van de conclusies 3 tot en 20 met 5, gekenmerkt door ten minste één verwarmingselement, dat in of aan het bouwelement is aangebracht.Building element according to one of claims 3 to 20 with 5, characterized by at least one heating element which is arranged in or on the building element. 7. Bouwelement volgens conclusie 6, met het kenmerk, dat het verwarmingselement verbindbaar is met leidingen, zoals buizen voor geleiding van verwarmingswater van de 25 centrale verwarmingsinstallatie.7. Building element according to claim 6, characterized in that the heating element is connectable to pipes, such as pipes for conducting heating water of the central heating installation. 8. Bouwelement volgens één van de voorgaande conclusies, met het kenmerk, dat het mengsel een kleurstof bevat. 10 00 87 1 . SAMENWERKINGSVERDRAG (PCT) RAPPORT BETREFFENDE NIEUWHEIDSONDERZOEK VAN INTERNATIONAAL TYPE IDENTIFIKAT1E VAN DE NATIONALE AANVRAGE Kenmerk van 0« aanvrager o! van d· gemacnogde W-1/OD61 Nederlandse aanvrage nr. tndienngsdaum '1000871 21 juli 1995 In ge roe pen voortangsdaum Aanvrager (Naam) DE BRUIN-EISINGA, Anna Gezina Datum van het verzoek voor een onderzoek van mtamalonaal type Door de Insante voor intamatonaai Onderzoek (ISA) aan het verzoek voor een onderzoek van internationaal type toegekend nr. SN 26213 NL I. CLASSIFICATIE VAN HET ONDERWERP (bij toepassing van verschillende dassiAcases, alle dassilieattesymbolen opgeven) volgens de mama tuna te classificatie (IPC) int.Cl.6: C 04 B 14/28, E 04 C 2/04 II. ONDERZOCHTE GEBIEDEN VAN DE TECHNIEK __ Onderzochte minimum documentatie__ Classificatiesysteem Classificatiesymbolen Int.Cl.6; C 04 B, E 04 C Onderzochte andere documentatie dan de minimum documontane voor zover detgeijke documenten m de onderzochte gebieden zin opgenomen III. I 1 GEEN ONDERZOEK MOGELUK VOOR BEPAALDE CONCLUSIES (opmerkingen op aanvullingsblad) IV·! . ! GEBREK AAN EENHEID VAN UITVINDING (opmerkingen op aanvullingsblad) /0 Form PCT/ISA/201(a) 08 1994Building element according to one of the preceding claims, characterized in that the mixture contains a dye. 10 00 87 1. COOPERATION TREATY (PCT) REPORT ON NEWNESS RESEARCH OF INTERNATIONAL TYPE IDENTIFIKAT1E OF THE NATIONAL APPLICATION Characteristic of 0 «applicant o! van d · modified W-1 / OD61 Dutch application no. tndienngsdaum '1000871 21 July 1995 Involved voorangsdaum Applicant (Name) DE BRUIN-EISINGA, Anna Gezina Date of the request for an examination of mtamalonal type By the Insante for intamatonaai Study (ISA) assigned to the request for an study of international type no. SN 26213 EN I. SUBJECT CLASSIFICATION (when using different dassiAcases, indicate all badassie symbols) according to the mama tuna classification (IPC) int.Cl.6 : C 04 B 14/28, E 04 C 2/04 II. FIELDS OF TECHNIQUE EXAMINED __ Minimum documentation examined__ Classification system Classification symbols Int.Cl.6; C 04 B, E 04 C Examined documentation other than minimum documontane insofar as the equivalent documents are included in the areas under investigation III. I 1 NO RESEARCH AT ALL FOR CERTAIN CONCLUSIONS (comments on supplementary sheet) IV ·! . ! LACK OF UNIT OF INVENTION (comments on supplement sheet) / 0 Form PCT / ISA / 201 (a) 08 1994
NL1000871A 1995-07-21 1995-07-21 Cement-bound constructional component NL1000871C2 (en)