MX2017015841A - Acero de alta resistencia y metodo de fabricacion. - Google Patents

Acero de alta resistencia y metodo de fabricacion.

Info

Publication number
MX2017015841A
MX2017015841A MX2017015841A MX2017015841A MX2017015841A MX 2017015841 A MX2017015841 A MX 2017015841A MX 2017015841 A MX2017015841 A MX 2017015841A MX 2017015841 A MX2017015841 A MX 2017015841A MX 2017015841 A MX2017015841 A MX 2017015841A
Authority
MX
Mexico
Prior art keywords
martensite
surface area
less
fraction
ferrite
Prior art date
Application number
MX2017015841A
Other languages
English (en)
Inventor
Drillet Josee
Hebert Veronique
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MX2017015841A publication Critical patent/MX2017015841A/es

Abstract

La invención se refiere a una hoja de acero laminada en frío y recocida de espesor entre 0.7 mm y 2 mm, resistencia mecánica que varía de 1,180 MPa a 1,320 MPa, en donde la relación de expansión de orificio Ac% es mayor a 20% y el ángulo de flexión es mayor o igual a 40° y en donde la composición química comprende, siendo el contenido expresado como porcentaje en peso: 0.09% = C = 0.11%, 2.6% = Mn = 2.8%, 0. 20% = Si = 0.55%, 0. 25% = Cr < 0.5%, 0.025% = Ti = 0.040%, 0.0015% = B = 0.0025%, 0.005% = Al = 0.18%, 0.08% = Mo = 0.15%, 0.020% = Nb = 0.040%, 0.002% = N = 0.007%, 0.0005% = S = 0.005%, 0.001% = P = 0.020%, Ca = 0.003%, siendo el resto hierro e impurezas inevitables resultantes del proceso. La hoja tiene una microestructura que comprende martensita y/o bainita inferior y dicha martensita que comprende martensita fresca y/o martensita templada automáticamente, siendo la suma de las fracciones superficiales de martensita y bainita inferior entre 40% y 70%, de 15% a 45% de la fracción de superficie de bainita de bajo contenido de carburo, de 5% a menos de 20% de la fracción de superficie de ferrita, la fracción de ferrita no recristalizada con respecto a la fracción de ferrita total siendo menos del 15% y menos del 5% de la fracción de superficie de austenita residual en forma de islotes, la fracción de granos austeníticos antiguos en donde el tamaño es menor que al menos un micrómetro que representa del 40% al 60% de la población total de dichos granos austeníticos antiguos.
MX2017015841A 2015-06-10 2016-06-09 Acero de alta resistencia y metodo de fabricacion. MX2017015841A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2015/000891 WO2016198906A1 (fr) 2015-06-10 2015-06-10 Acier a haute résistance et procédé de fabrication
PCT/IB2016/000780 WO2016198940A2 (fr) 2015-06-10 2016-06-09 Acier à haute résistance et procédé de fabrication

Publications (1)

Publication Number Publication Date
MX2017015841A true MX2017015841A (es) 2018-06-06

Family

ID=53762217

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017015841A MX2017015841A (es) 2015-06-10 2016-06-09 Acero de alta resistencia y metodo de fabricacion.

Country Status (12)

Country Link
US (1) US10697052B2 (es)
EP (1) EP3307921A2 (es)
JP (1) JP6971856B2 (es)
KR (1) KR102140928B1 (es)
CN (1) CN107614732B (es)
BR (1) BR112017025366B1 (es)
CA (1) CA2987691C (es)
MA (1) MA42495A (es)
MX (1) MX2017015841A (es)
RU (1) RU2689826C1 (es)
UA (1) UA118420C2 (es)
WO (2) WO2016198906A1 (es)

Families Citing this family (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016198906A1 (fr) * 2015-06-10 2016-12-15 Arcelormittal Acier a haute résistance et procédé de fabrication
MY198084A (en) * 2015-10-30 2023-07-31 Cancer Research Tech Ltd Expansion of non-haematopoietic tissue-resident ()()t cells and uses of these cells
WO2019092482A1 (en) * 2017-11-10 2019-05-16 Arcelormittal Cold rolled heat treated steel sheet and a method of manufacturing thereof
WO2019130713A1 (ja) 2017-12-27 2019-07-04 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
KR102415150B1 (ko) 2018-02-05 2022-06-29 주식회사 엘지에너지솔루션 배터리 모듈, 이를 포함하는 배터리 팩 및 자동차
US20210189517A1 (en) * 2018-05-22 2021-06-24 Thyssenkrupp Steel Europe Ag Sheet Metal Part Formed from a Steel Having a High Tensile Strength and Method for Manufacturing Said Sheet Metal Part
CN109100378B (zh) * 2018-07-24 2021-01-01 华北理工大学 一种低碳贝氏体钢中残余奥氏体的分析方法
DE102018122901A1 (de) * 2018-09-18 2020-03-19 Voestalpine Stahl Gmbh Verfahren zur Herstellung ultrahochfester Stahlbleche und Stahlblech hierfür
WO2020096555A2 (en) * 2018-11-08 2020-05-14 Coşkunöz Kalip Maki̇na Sanayi̇ Ve Ti̇caret Anoni̇m Şi̇rketi̇ Steel production method providing high energy absorption with mn partitioning and rapid heating
BR112021005688B1 (pt) * 2018-11-30 2023-05-02 Arcelormittal Chapa de aço, método para a produção de uma chapa de aço e uso
MX2021008306A (es) * 2019-01-09 2021-08-05 Jfe Steel Corp Lamina de acero laminada en frio de alta resistencia y metodo de produccion para la misma.
KR102503913B1 (ko) * 2019-01-30 2023-02-27 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
WO2020250009A1 (en) * 2019-06-12 2020-12-17 Arcelormittal A cold rolled martensitic steel and a method of martensitic steel thereof
JP6947327B2 (ja) * 2019-07-31 2021-10-13 Ｊｆｅスチール株式会社 高強度鋼板、高強度部材及びそれらの製造方法
MX2022001203A (es) * 2019-07-31 2022-02-22 Jfe Steel Corp Lamina de acero de alta resistencia, miembro de alta resistencia, y metodos para la fabricacion de los mismos.
KR20220049534A (ko) * 2019-08-07 2022-04-21 유나이테드 스테이츠 스틸 코포레이션 고 연성의 아연-코팅된 강 시트 제품
WO2021116741A1 (en) * 2019-12-13 2021-06-17 Arcelormittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
BR112022011703A2 (pt) * 2019-12-18 2022-09-06 Arcelormittal Chapa de aço laminada a frio e recozida e método de fabricação de uma chapa de aço laminada a frio e recozida
WO2022008949A1 (en) * 2020-07-06 2022-01-13 Arcelormittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
CN112899577B (zh) * 2021-01-18 2021-12-24 北京科技大学 一种Fe-Mn系高强度高阻尼合金的制备方法
CN115181895B (zh) * 2021-04-02 2023-09-12 宝山钢铁股份有限公司 1180MPa级别低碳低合金热镀锌Q&P钢及快速热处理热镀锌制造方法
CN118048578A (zh) * 2022-11-17 2024-05-17 育材堂（苏州）材料科技有限公司 一种低碳的高韧性热冲压成形构件及钢板

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6159312A (en) 1997-12-19 2000-12-12 Exxonmobil Upstream Research Company Ultra-high strength triple phase steels with excellent cryogenic temperature toughness
DE10146791A1 (de) * 2001-09-20 2003-04-10 Sms Demag Ag Verfahren und Vorrichtung zum Beschichten der Oberfläche von strangförmigem metallischem Gut
JP2003253385A (ja) * 2002-02-28 2003-09-10 Jfe Steel Kk 高速変形特性および曲げ特性に優れた冷延鋼板およびその製造方法
JP4788291B2 (ja) 2005-10-27 2011-10-05 Ｊｆｅスチール株式会社 伸びフランジ成形性に優れた高強度溶融亜鉛めっき鋼板の製造方法
JP4772497B2 (ja) 2005-12-27 2011-09-14 新日本製鐵株式会社 穴拡げ性に優れた高強度冷延薄鋼板及びその製造方法
WO2007129676A1 (ja) 2006-05-10 2007-11-15 Sumitomo Metal Industries, Ltd. 熱間プレス成形鋼板部材およびその製造方法
DE102006047060A1 (de) * 2006-05-18 2007-11-22 Thyssenkrupp Steel Ag Mit einem Korrosionsschutzsystem versehenes Stahlblech und Verfahren zum Beschichten eines Stahlblechs mit einem solchen Korrosionsschutzsystem
JP5365216B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
EP2123786A1 (fr) 2008-05-21 2009-11-25 ArcelorMittal France Procédé de fabrication de tôles d'aciers dual phase laminées à froid à trés haute résistance et tôles ainsi produites
WO2010013848A1 (ja) 2008-07-31 2010-02-04 Ｊｆｅスチール株式会社 低温靭性に優れた厚肉高張力熱延鋼板およびその製造方法
JP4924730B2 (ja) * 2009-04-28 2012-04-25 Ｊｆｅスチール株式会社 加工性、溶接性および疲労特性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
FI20095528A (fi) 2009-05-11 2010-11-12 Rautaruukki Oyj Menetelmä kuumavalssatun nauhaterästuotteen valmistamiseksi sekä kuumavalssattu nauhaterästuote
JP5412182B2 (ja) 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5434960B2 (ja) * 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
WO2012052626A1 (fr) 2010-10-21 2012-04-26 Arcelormittal Investigacion Y Desarrollo, S.L. Tole d'acier laminee a chaud ou a froid, don procede de fabrication et son utilisation dans l'industrie automobile
PL2716783T3 (pl) 2011-05-25 2019-01-31 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka walcowana na gorąco i sposób jej wytwarzania
US9745639B2 (en) 2011-06-13 2017-08-29 Kobe Steel, Ltd. High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
ES2648415T5 (es) 2012-03-30 2021-02-15 Voestalpine Stahl Gmbh Chapa de acero de alta resistencia laminada en frío y procedimiento de fabricación de dicha chapa de acero
WO2015088523A1 (en) 2013-12-11 2015-06-18 ArcelorMittal Investigación y Desarrollo, S.L. Cold rolled and annealed steel sheet
JP5858032B2 (ja) * 2013-12-18 2016-02-10 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
WO2015185956A1 (en) * 2014-06-06 2015-12-10 ArcelorMittal Investigación y Desarrollo, S.L. High strength multiphase galvanized steel sheet, production method and use
WO2016198906A1 (fr) * 2015-06-10 2016-12-15 Arcelormittal Acier a haute résistance et procédé de fabrication

Also Published As

Publication number Publication date
CN107614732B (zh) 2020-07-10
BR112017025366A2 (pt) 2018-08-07
MA42495A (fr) 2018-05-30
CN107614732A (zh) 2018-01-19
JP6971856B2 (ja) 2021-11-24
KR102140928B1 (ko) 2020-08-05
WO2016198906A1 (fr) 2016-12-15
WO2016198940A3 (fr) 2017-10-19
BR112017025366B1 (pt) 2024-01-30
RU2689826C1 (ru) 2019-05-29
WO2016198940A2 (fr) 2016-12-15
UA118420C2 (uk) 2019-01-10
KR20180014093A (ko) 2018-02-07
CA2987691A1 (en) 2016-12-15
US10697052B2 (en) 2020-06-30
JP2018521222A (ja) 2018-08-02
EP3307921A2 (fr) 2018-04-18
US20180171459A1 (en) 2018-06-21
CA2987691C (en) 2021-05-25

Similar Documents

Publication Publication Date Title
MX2017015841A (es) Acero de alta resistencia y metodo de fabricacion.
MX2019003282A (es) Lamina de acero de alta resistencia y alta conformabilidad laminada en frio y tratada termicamente y metodo de fabricacion.
UA114877C2 (uk) Двічі відпалений сталевий лист з високою механічною міцністю і пластичністю, спосіб виготовлення і використання такого листа
MX2022004076A (es) Acero para conformado en caliente y pieza conformada en caliente fabricada de tal acero.
MX2016001013A (es) Hoja de acero que tiene propiedades mecanicas de resistencia y ductibilidad muy altas, metodo de fabricacion y uso de tales hojas.
MX2013013106A (es) Lamina de acero con altas propiedades de resistencia mecanica, ductilidad y de formacion, metodo de produccion de la misma y uso de dichas láminas.
UA118036C2 (uk) Високоміцна сталь та спосіб виготовлення
MX2019007165A (es) Lamina de acero templada y recubierta que tiene excelente conformabilidad y metodo para fabricar la misma.
MX2018008561A (es) Lamina de acero de alta resistencia que tiene excelente conformabilidad y un metodo de fabricacion de la misma.
UA117865C2 (uk) Високоміцна багатофазна сталь, спосіб її одержання та застосування
MX2019007169A (es) Hoja de acero revestida y templada con excelente capacidad de formacion y un metodo para fabricar la misma.
MX2016009745A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
MX2015011027A (es) Hoja de acero laminada en caliente y metodo para fabricar la misma.
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
MX2017000496A (es) Hoja de acero laminada en caliente y metodo de fabricacion relacionado.
MX2016001723A (es) Lamina de acero laminada en frio de alta resistencia y metodo para la fabricacion de la misma.
WO2016098964A8 (ko) 재질 불균일이 작고 성형성이 우수한 고강도 냉연강판, 용융아연도금강판, 및 그 제조 방법
MX2015014099A (es) Hoja de acero laminada en caliente y metodo de fabricacion de la misma.
WO2008145871A3 (fr) Procede de fabrication de tôles d&#39;acier laminees a froid et recuites a tres haute resistance, et tôles ainsi produites
UA113404C2 (xx) Гарячекатаний сталевий лист та спосіб його виготовлення
MX2018009735A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
PH12017500557A1 (en) Steel sheet for cans and method for manufacturing steel sheet for cans
MX2017000185A (es) Metodo para la fabricacion de una hoja de acero de alta resistencia que tiene formabilidad y ductilidad mejoradas y hoja obtenida.
MX2021002972A (es) Hoja de acero laminado en caliente con una alta proporcion de expansion de agujero y proceso de fabricacion de la misma.
MX2017011144A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.