LU88506A1 - Method and installation for sorting heterogeneous plastics - Google Patents

Description

PROCEDE ET INSTALLATION DE TRIAGE DE MATIERES PLASTIQUES HETEROGENESMETHOD AND PLANT FOR SORTING HETEROGENEOUS PLASTIC MATERIALS

La présent invention concerne un procédé de triage de matières plastiques hétérogènes. On propose aussi une installation pour la mise en oeuvre de ce procédé de triage.The present invention relates to a method for sorting heterogeneous plastics. An installation is also proposed for the implementation of this sorting process.

Les matières plastiques jouissent d'une grande popularité car elles offrent de nombreux avantages et peuvent remplacer avantageusement d'autres matériaux classiques tels que le papier, le bois, le verre et le métal dans beaucoup d' applications.Plastics are very popular because they offer many advantages and can advantageously replace other conventional materials such as paper, wood, glass and metal in many applications.

Parmi les matières plastiques les plus utilisées, on trouve le polyéthylène à basse densité (LDPE), le polyéthylène à haute densité (HDPE), le polystyrène (PS) , le polychlorure de vinyle (PVC) et le polypropylène (PP) . Une grande partie de ces matières plastiques se retrouve après une courte utilisation dans les poubelles et doit être mise à la décharge ou incinérée. Les matières plastiques occupent un pourcentage en poids de plus en plus élevé dans les ordures ménagères et on s'est posé la question si on ne pouvait pas réutiliser ces matières plastiques à des fins utiles. Cependant, à fin de pouvoir réutiliser les matières plastiques efficacement et économiquement, il faut les trier selon le type de produit de façon à obtenir des produits homogènes. En effet, les différentes matières plastiques ne sont pas toutes compatibles entre elles. Par exemple, il suffit de quelques pour-cents de PVC pour rendre inutilisable le LDPE.Among the most used plastics are low density polyethylene (LDPE), high density polyethylene (HDPE), polystyrene (PS), polyvinyl chloride (PVC) and polypropylene (PP). A large part of these plastics is found after a short use in the bins and must be landfilled or incinerated. Plastics are occupying an increasing percentage by weight in household waste and the question has been asked if these plastics could not be reused for useful purposes. However, in order to reuse plastics efficiently and economically, they must be sorted according to the type of product so as to obtain homogeneous products. Indeed, the different plastics are not all compatible with each other. For example, a few percent of PVC is enough to make LDPE unusable.

Les différents types de matières plastiques se ressemblent fortement de sorte que même pour un expert il est pratiquement impossible de les distinguer à l’oeil nu. Par conséquent, il est difficile de trier rapidement et efficacement les différents types de matières plastiques. Ces difficultés ont, jusqu'à présent, fortement limité le recyclage des matières plastiques hétérogènes.The different types of plastics are very similar so that even for an expert it is practically impossible to distinguish them with the naked eye. Therefore, it is difficult to quickly and efficiently sort the different types of plastics. These difficulties have so far severely limited the recycling of heterogeneous plastics.

Le but de la présente invention est de proposer un procédé de triage de matières plastiques hétérogènes automatique, simple et efficace.The aim of the present invention is to propose an automatic, simple and efficient sorting process for heterogeneous plastics.

Ce but est atteint par le procédé selon la présente invention caractérisé en ce que les matières plastiques hétérogènes sont d'abord mouillées et homogénéisées dans une première solution de densité d = 1 kg/1, en ce qu'un mélange de produits dont la densité est supérieure à 1 kg/1 est extrait de ladite solution par décantation tandis qu'un mélange de produits dont la densité est inférieure à l kg/1 en est extrait par flottation, en ce que ledit mélange de produits dont la densité est supérieure à 1 kg/1 est ensuite mouillé et homogénéisé dans une deuxième solution de densité d = 1,2 kg/1, en ce que les produits dont la densité est supérieure à 1,2 kg/1 sont extraits de cette deuxième solution par sédimentation et puis stockés tandis que les produits dont la densité est comprise entre l kg/1 et 1,2 kg/1 sont extraits par flottation et puis stockés, le mélange de produits dont la densité est inférieure à 1 kg/1 quant à lui, est soumis à un mouillage et à une homogénéisation dans une troisième solution dont la densité d = 0,93 kg/1, en ce que les produits dont la densité est comprise entre 0,93 kg/1 et 1 kg/1 sont extraits pare décantation et stockés tandis que les produits dont la densité est inférieure 0,93 kg/1 qui sont extraits par flottation sont soumis à un mouillage et à une homogénéisation dans une quatrième solution de densité d = 0,91 kg/1, les produits dont la densité est inférieure à 0,91 kg/1 sont extraits par flottation et puis stockés tandis que les produits dont la densité est comprise entre 0,91 kg/1 et 0,93 kg/1 sont extraits par décantation et puis stockés.This object is achieved by the method according to the present invention, characterized in that the heterogeneous plastics are first wetted and homogenized in a first solution with a density d = 1 kg / 1, in that a mixture of products whose density is greater than 1 kg / 1 is extracted from said solution by decantation while a mixture of products whose density is less than 1 kg / 1 is extracted therefrom by flotation, in that said mixture of products whose density is greater than 1 kg / 1 is then wetted and homogenized in a second solution with a density d = 1.2 kg / 1, in that the products whose density is greater than 1.2 kg / 1 are extracted from this second solution by sedimentation and then stored while the products whose density is between 1 kg / 1 and 1.2 kg / 1 are extracted by flotation and then stored, the mixture of products whose density is less than 1 kg / 1 is subject to wetting and homogenization in a third solution whose density d = 0.93 kg / 1, in that the products whose density is between 0.93 kg / 1 and 1 kg / 1 are extracted by decantation and stored while that the products whose density is less than 0.93 kg / 1 which are extracted by flotation are subjected to wetting and homogenization in a fourth solution with density d = 0.91 kg / 1, the products whose density is lower at 0.91 kg / 1 are extracted by flotation and then stored while the products whose density is between 0.91 kg / 1 and 0.93 kg / 1 are extracted by decantation and then stored.

Les produits dont la densité est supérieure à 1,2 kg/1 consistent en du PVC dont la densité se situe entre 1.38 et 1,58 kg/1.Products with a density greater than 1.2 kg / 1 consist of PVC with a density between 1.38 and 1.58 kg / 1.

Les produits dont la densité est comprise entre 1 kg/1 et 1,2 kg/1 se composent de PS qui a une densité comprise entre 1,05 et 1,059 kg/1.Products with a density between 1 kg / 1 and 1.2 kg / 1 consist of PS which has a density between 1.05 and 1.059 kg / 1.

Les produits dont la densité est comprise entre 0,93 kg/1 et 1 kg/1 comprennent du HDPE dont la densité varie entre 0,945 kg/1 et 0,959 kg/1.Products with a density between 0.93 kg / 1 and 1 kg / 1 include HDPE with a density between 0.945 kg / 1 and 0.959 kg / 1.

Les produits dont la densité est comprise entre 0,91 kg/1 et 0,93 kg/1 consistent en du LDPE, la densité du LDPE variant entre 0,910 et 0,925 kg/1.Products with a density between 0.91 kg / 1 and 0.93 kg / 1 consist of LDPE, the density of LDPE varying between 0.910 and 0.925 kg / 1.

Finalement les produits dont la densité est inférieure à 0,91 kg/1 sont en PP dont la densité se situe entre 0,904 et 0,907 kg/1.Finally, the products whose density is less than 0.91 kg / 1 are made of PP whose density is between 0.904 and 0.907 kg / 1.

Selon un premier mode de réalisation, les matières plastiques séparées sont séchées après chaque étape de séparation.According to a first embodiment, the separated plastics are dried after each separation step.

Selon un autre mode de réalisation, les solutions sont recirculées après avoir été filtrées, et après que leur densité ait été contrôlée et ajustée si nécessaire.According to another embodiment, the solutions are recirculated after being filtered, and after their density has been checked and adjusted if necessary.

Afin de garantir le bon fonctionnement de l'installation, il est recommandé d'extraire toutes les matières étrangères tels que les métaux, le papier, le bois etc des matières plastiques à traiter.In order to guarantee the proper functioning of the installation, it is recommended to extract all foreign materials such as metals, paper, wood, etc. from the plastics to be treated.

Il est préférable de broyer préalablement la matière plastique à traiter en des particules d'une taille plus ou moins homogène afin de faciliter la décantation des particules.It is preferable to grind the plastic material to be treated beforehand into particles of a more or less homogeneous size in order to facilitate the settling of the particles.

Un des grands avantages de ce procédé est qu'il permet de séparer efficacement des matières plastiques hétérogènes en leur constituants respectifs et cela d'une manière simple, efficace et peu onéreuse. Les produits obtenus par ce procédé sont des produits homogènes et propres à partir desquels on peut produire de nouveaux emballages, ou d'autres objets utiles. Ces produits peuvent être retravaillés facilement car leurs propriétés mécaniques et leurs caractéristiques physico-chimiques correspondent à celles des produits vierges respectifs.One of the great advantages of this process is that it makes it possible to efficiently separate heterogeneous plastics into their respective constituents and this in a simple, efficient and inexpensive manner. The products obtained by this process are homogeneous and clean products from which we can produce new packaging, or other useful objects. These products can be easily reworked because their mechanical properties and their physico-chemical characteristics correspond to those of the respective virgin products.

La présente invention propose aussi une installation pour la mise en oeuvre du procédé caractérisé par un premier moyen de décantation rempli d'une première solution de densité d = 1 kg/1, un moyen d'évacuation des produits dont la densité est supérieure à 1 kg/1 vers un premier moyen d'homogénéisation et de mouillage comprenant une solution dont la densité d = 1,2 kg/1, un moyen de transport pour transvaser ledit produit et la deuxième solution dans un deuxième moyen de séparation, une conduite pour évacuer les produits dont la densité est supérieure à 1,2 kg/1 vers un premier silo de stockage, une conduite d'évacuation des produits dont la densité est comprise entre 1 kg/1 et 1,2 kg/1 vers un deuxième moyen de stockage, une conduite d'évacuation des produits dont la densité est inférieure à 1 kg/1 du premier moyen de décantation vers une troisième unité de mouillage et d'homogénéisation comprenant une solution dont la densité d = 0,93 kg/1, une conduite d'évacuation des produits dont la densité est comprise entre 0,93 kg/1 et 1 kg/1 vers un troisième moyen de stockage, une conduite d'évacuation des produits dont la densité est inférieure à 0,93 kg/1 vers un quatrième moyen de homogénéisation et de mouillage comprenant une solution dont la densité d = 0,91 kg/1, une conduite d'évacuation du mélange de solution et de particules vers un quatrième moyen de séparation, une conduite d'évacuation des produits dont la densité est comprise entre 0,91 kg/1 et 0,93 kg/1 vers un quatrième moyen de stockage, une conduite d'évacuation des produits dont la densité est inférieure à 0,91 g/1 du quatrième moyen de séparation un cinquième moyen de stockage.The present invention also provides an installation for implementing the process characterized by a first decantation means filled with a first solution with a density d = 1 kg / 1, a means for removing products whose density is greater than 1 kg / 1 to a first means of homogenization and wetting comprising a solution whose density d = 1.2 kg / 1, a means of transport for decanting said product and the second solution in a second means of separation, a line for evacuate products whose density is greater than 1.2 kg / 1 to a first storage silo, an evacuation pipe for products whose density is between 1 kg / 1 and 1.2 kg / 1 to a second means storage, an evacuation pipe for products whose density is less than 1 kg / 1 from the first decantation means to a third wetting and homogenization unit comprising a solution whose density d = 0.93 kg / 1, a cond a product discharge line with a density between 0.93 kg / 1 and 1 kg / 1 to a third storage means, a product discharge line with a density less than 0.93 kg / 1 to a fourth means of homogenization and wetting comprising a solution whose density d = 0.91 kg / 1, a line for discharging the mixture of solution and particles to a fourth means of separation, a line for discharging the products of which the density is between 0.91 kg / 1 and 0.93 kg / 1 to a fourth storage means, a product evacuation pipe whose density is less than 0.91 g / 1 from the fourth separation means a fifth means of storage.

Selon un premier mode de réalisation avantageux les produits sont amenés et traitées dans des moyens de séchage avant d'être transvasé dans les moyens de mouillage et d'homogénéisation.According to a first advantageous embodiment, the products are brought and treated in drying means before being transferred to the wetting and homogenization means.

Préférablement les moyens de séchage sont des tamis vibrants.Preferably the drying means are vibrating screens.

Avantageusement, des bassins de récupération sont aménagés en dessous des différents tamis pour récolter les solutions.Advantageously, recovery basins are arranged below the various sieves to collect the solutions.

De préférence, l'installation comprend également un circuit de recirculation séparé pour chacune des solutions utilisées comprenant une installation de filtrage, des moyens de dosage des composantes de chaque solution et des moyens pour ajuster la densité.Preferably, the installation also comprises a separate recirculation circuit for each of the solutions used comprising a filtering installation, means for dosing the components of each solution and means for adjusting the density.

Selon un autre mode de réalisation préféré, le premier moyen de décantation est équipé d'une bande de transport située au fond du premier bassin de décantation et d'une deuxième bande de transport située en partie en dessous du niveau de liquide. La première bande de transport permet d'évacuer les produits à densité plus élevée que la solution tandis que la deuxième bande de transport permet de récolter les produits flottant à la surface.According to another preferred embodiment, the first settling means is equipped with a conveyor belt located at the bottom of the first settling tank and a second conveyor belt located partly below the liquid level. The first conveyor belt allows products with higher density than the solution to be removed, while the second conveyor belt allows products floating on the surface to be collected.

Selon encore un autre mode de réalisation préféré, les deuxième, troisième et quatrième moyens de séparation sont des hydrocyclones.According to yet another preferred embodiment, the second, third and fourth separation means are hydrocyclones.

D'autres caractéristiques et particularités ressortiront de la description détaillée d'un mode de réalisation avantageux, présenté ci-dessous, à titre d'illustration, en référence à la figure annexée dans laquelle : la Figure l montre un vue schématique générale d'une installation de triage de matières plastiques hétérogènes. La matière plastique hétérogène est déversée dans un bassin de décantation 5 lequel est rempli d'une solution de densité d = 1 kg/1. Cette solution se compose d'eau et d'un agent tensioactif qui favorise le mouillage des particules en matière plastique. Si la densité des particules est supérieure à 1 kg/1, les particules descendent vers le fond du bassin tandis que si la densité des particules est inférieure à 1 kg/1, les particules flottent à la surface du liquide. Les particules de densité supérieure à 1 kg/1 tombent sur une bande de transport 10 aménagée au fond du bassin 5 et sont amenées via une conduite 12 sur un tamis vibrant 15 pour y être égouttées. Ce tamisage permet de réduire l'humidité résiduelle des particules jusqu'à environ 5%. Les particules ainsi obtenues se compose de PVC et de PS, car la densité de ces deux matériaux est supérieure à 1 kg/1. Ces particules sont ensuite transportées dans une conduite 17 vers une unité d' homogénéisation et de mouillage 20 dans laquelle se trouve une solution de densité d = 1,2 kg/1. Cette solution se compose, de préférence, d'eau, d'un agent tensioactif et d'une quantité appropriée de hydrochlorure de sodium ou d'un autre sel adéquat. Les particules et une partie de ladite solution sont ensuite amenées dans un hydrocyclone 25 via une conduite 22. Les particules qui ont une densité supérieure à 1,2 kg/1 se rassembleront au fond de 1'hydrocyclone 25 et seront évacuées moyennant une conduite 2 7 vers un deuxième tamis vibrant 30 pour y être séchées. Ces particules, qui se composent de particules de PVC, sont ensuite stockées dans un silo 35 et peuvent être réutilisées après avoir été broyées en une poudre fine si nécessaire. Les particules qui ont une densité inférieure à 1,2 kg/1 mais supérieure à 1 kg/1 sont évacuées de la partie supérieure de 1'hydrocyclone 25 par une conduite 37 et séchées sur un tamis vibrant 4 0 puis stockées dans un silo 45. Ces particules se composent de PS.Other characteristics and particularities will emerge from the detailed description of an advantageous embodiment, presented below, by way of illustration, with reference to the appended figure in which: Figure 1 shows a general schematic view of a sorting plant for heterogeneous plastics. The heterogeneous plastic is poured into a settling tank 5 which is filled with a solution of density d = 1 kg / 1. This solution consists of water and a surfactant which promotes the wetting of plastic particles. If the density of the particles is greater than 1 kg / 1, the particles descend to the bottom of the basin while if the density of the particles is less than 1 kg / 1, the particles float on the surface of the liquid. The particles of density greater than 1 kg / 1 fall on a conveyor belt 10 arranged at the bottom of the tank 5 and are brought via a line 12 on a vibrating screen 15 to be drained there. This sieving reduces the residual moisture of the particles up to about 5%. The particles thus obtained consist of PVC and PS, because the density of these two materials is greater than 1 kg / 1. These particles are then transported in a line 17 to a homogenization and wetting unit 20 in which there is a solution of density d = 1.2 kg / 1. This solution preferably consists of water, a surfactant and an appropriate amount of sodium hydrochloride or other suitable salt. The particles and part of said solution are then brought into a hydrocyclone 25 via a line 22. The particles which have a density greater than 1.2 kg / 1 will collect at the bottom of the hydrocyclone 25 and will be evacuated by means of a line 2 7 to a second vibrating sieve 30 to be dried there. These particles, which consist of PVC particles, are then stored in a silo 35 and can be reused after being ground into a fine powder if necessary. The particles which have a density of less than 1.2 kg / l but greater than 1 kg / l are removed from the upper part of the hydrocyclone 25 by a line 37 and dried on a vibrating sieve 40 and then stored in a silo 45 These particles consist of PS.

Les particules qui n'ont pas sédimentées dans le premier bassin 5 et qui ont par conséquent une densité inférieure à 1 kg/1, sont récoltées à la surface du liquide par une deuxième bande de transport 50 aménagé en partie en dessous du niveau de la solution et puis séchées sur un tamis vibrant 55. Ces particules séchées sont ensuite déversées moyennant une conduite 57 dans une deuxième unité de mouillage et d'homogénéisation 60 dans laquelle se trouve un liquide d'une densité d = 0,93 kg/1. Cette solution se compose, de préférence, d'eau, d'un agent tensioactif et d'une quantité appropriée d'éthanol. Le mélange de particules et de liquide est transvasé à l'aide d'une conduite 62 dans un deuxième hydrocyclone 65 et lea.The particles which have not sedimented in the first tank 5 and which consequently have a density of less than 1 kg / 1, are collected on the surface of the liquid by a second conveyor belt 50 arranged partly below the level of the solution and then dried on a vibrating screen 55. These dried particles are then poured by means of a pipe 57 into a second wetting and homogenization unit 60 in which there is a liquid with a density d = 0.93 kg / 1. This solution preferably consists of water, a surfactant and an appropriate amount of ethanol. The mixture of particles and liquid is transferred using a line 62 into a second hydrocyclone 65 and lea.

particules qui ont une densité comprise entre 0,93 et 1 kg/1 sont évacuées via le fond de 1'hydrocyclone 65 par une conduite 67 et sont séchées sur un tamis 70 avant d'être stockées dans un silo 75. Ces particules se composent de HDPE.particles which have a density between 0.93 and 1 kg / 1 are evacuated via the bottom of the hydrocyclone 65 by a line 67 and are dried on a sieve 70 before being stored in a silo 75. These particles are composed of HDPE.

Les particules qui ont une densité inférieure à 0.93 kg/1 flottent à la surface de la solution contenue dans 1'hydrocyclone 65 et sont évacuées par une conduite 77 vers un autre tamis vibrant 80 et séchées.The particles which have a density of less than 0.93 kg / 1 float on the surface of the solution contained in the hydrocyclone 65 and are evacuated via a line 77 to another vibrating screen 80 and dried.

Ces particules sont transférées dans une troisième unité d'homogénéisation et de mouillage 85 dans laquelle se trouve une solution d'une densité d = 0,91 kg/1. Cette solution se compose d'eau , d'un agent tensioactif et d'éthanol. Le mélange de particules et de solution est transvasé au moyen d'une conduite 87 dans un troisième hydrocyclone 90 et les particules sont séparés suivant qu'elles ont une densité supérieure ou inférieure à la solution. Les particules ayant une densité comprise entre 0,91 et 0,93 kg/1 sont évacuées via une conduite 72 et sont séchées sur un tamis 95 puis stockées dans un silo 100. Les particules ayant une densité inférieure 0,91 kg/1 sont évacuées de la partie supérieure de 1'hydrocyclone par une conduite $7. Ces particules en PP sont séchées sur un tamis 105 et puis stockées dans un silo 110.These particles are transferred to a third homogenization and wetting unit 85 in which there is a solution with a density d = 0.91 kg / 1. This solution consists of water, a surfactant and ethanol. The mixture of particles and solution is transferred by means of a line 87 into a third hydrocyclone 90 and the particles are separated according to whether they have a density higher or lower than the solution. The particles having a density of between 0.91 and 0.93 kg / 1 are discharged via a line 72 and are dried on a sieve 95 and then stored in a silo 100. The particles having a density below 0.91 kg / 1 are evacuated from the upper part of the hydrocyclone via a pipe $ 7. These PP particles are dried on a sieve 105 and then stored in a silo 110.

Pour que l'installation fonctionne correctement, il est impératif de surveiller et d'ajuster constamment la densité des différentes solutions utilisées pour effectuer la séparation des produits.For the installation to function properly, it is imperative to constantly monitor and adjust the density of the different solutions used to separate the products.

La première solution de densité d = 1 kg/1 est récoltée dans des bassins de rétention 115 respectivement 120 situés en dessous des tamis 15 respectivement 55. Cette solution est traitée dans une unité de filtrage et d'ajustage de la densité 125 et puis reconduite dans le bassin de décantation 5. Les trois autres solution de densité d = 1,2 ; d = 0.9 3 respectivement d = 0,91 kg/1 sont collectées séparément dans des bassins de rétention 130, 135, 140, 145, 150 et 155 situés en dessous des différents des tamis respectifs 30, 40, 70, 80, 95, 105 et recyclées dans des unités de filtrage et d'ajustage de la densité 160 pour la solution dont la densité d = 1,2 kg/1; 165 pour la solution dont la densité d = 0,93 kg/1, respectivement 170 pour la solution dont la densité d = 0,91 kg/1. Après ajustage de leur densité, les différentes solutions sont ramenées dans les unités de mouillage et d'homogénéisation 20, 60 et 85 correspondantes.The first solution with a density d = 1 kg / 1 is collected in retention basins 115 respectively 120 located below the sieves 15 respectively 55. This solution is treated in a filtering and density adjustment unit 125 and then returned in the settling tank 5. The other three solutions with density d = 1.2; d = 0.9 3 respectively d = 0.91 kg / 1 are collected separately in retention basins 130, 135, 140, 145, 150 and 155 located below the different sieves 30, 40, 70, 80, 95, 105 and recycled into filtering and density adjustment units 160 for the solution whose density d = 1.2 kg / 1; 165 for the solution whose density d = 0.93 kg / 1, respectively 170 for the solution whose density d = 0.91 kg / 1. After adjusting their density, the different solutions are brought back to the corresponding wetting and homogenization units 20, 60 and 85.

Dans les différentes unités de filtrage et d'ajustage de la densité 125, 160, 165, et 170, les solutions sont filtrées et la concentration des différents constituants, sel, éthanol, eau et agents tensioactifs est contrôlée et ajustée si nécessaire.In the various filtering and density adjustment units 125, 160, 165, and 170, the solutions are filtered and the concentration of the various constituents, salt, ethanol, water and surfactants is checked and adjusted if necessary.

Claims (10)

1. Procédé de triage de matières plastiques hétérogènes caractérisé en ce que les matières plastiques hétérogènes sont d'abord mouillées et homogénéisées dans une première solution de densité d = 1 kg/1, en ce qu'un mélange de produits dont la densité est supérieure à 1 kg/1 est extrait de ladite solution par décantation tandis qu'un mélange de produits dont la densité est inférieure à 1 kg/1 en est extrait par flottation, en ce que ledit mélange de produits dont la densité est supérieure à 1 kg/1 est ensuite mouillé et homogénéisé dans une deuxième solution de densité d = 1,2 kg/1, en ce que les produits dont la densité est supérieure à 1,2 kg/1 sont extraits de cette deuxième solution par sédimentation et puis stockés tandis que les produits dont la densité est comprise entre 1 kg/1 et 1,2 kg/1 sont extraits par flottation et puis stockés, le mélange de produits dont la densité est inférieure à 1 kg/1 quant à lui, est soumis à un mouillage et à une homogénéisation dans une troisième solution dont la densité d = 0,93 kg/1, en ce que les produits dont la densité est comprise entre 0,93 kg/1 et 1 kg/1 sont extraits par décantation et stockés tandis que les produits dont la densité est inférieure 0,93 kg/1 qui sont extraits par flottation sont soumis à un mouillage età une homogénéisation dans une quatrième solution de densité d = 0,91 kg/1, les produits dont la densité est inférieure à 0,91 kg/1 sont extraits par flottation et puis stockés tandis que les produits dont la densité est comprise entre 0,91 kg/1 et 0,93 kg/1 sont extraits par décantation et puis stockés-1. A method of sorting heterogeneous plastics, characterized in that the heterogeneous plastics are first wetted and homogenized in a first solution with a density d = 1 kg / 1, in that a mixture of products whose density is higher to 1 kg / 1 is extracted from said solution by decantation while a mixture of products whose density is less than 1 kg / 1 is extracted from it by flotation, in that said mixture of products whose density is greater than 1 kg / 1 is then wetted and homogenized in a second solution with a density d = 1.2 kg / 1, in that the products whose density is greater than 1.2 kg / 1 are extracted from this second solution by sedimentation and then stored while products whose density is between 1 kg / 1 and 1.2 kg / 1 are extracted by flotation and then stored, the mixture of products whose density is less than 1 kg / 1 is subjected to a mo uillage and homogenization in a third solution whose density d = 0.93 kg / 1, in that the products whose density is between 0.93 kg / 1 and 1 kg / 1 are extracted by decantation and stored while that the products whose density is less than 0.93 kg / 1 which are extracted by flotation are subjected to wetting and homogenization in a fourth solution with density d = 0.91 kg / 1, the products whose density is less than 0.91 kg / 1 are extracted by flotation and then stored while products with a density between 0.91 kg / 1 and 0.93 kg / 1 are extracted by decantation and then stored - 2. Procédé selon la revendication 1 caractérisé en ce que les matières plastiques séparées sont séchées à chaque étape de séparation.2. Method according to claim 1 characterized in that the separated plastics are dried at each separation step. 3. Procédé selon l'une quelconque des revendications 1 ou 2 caractérisé en ce que les solutions sont recirculées. après avoir été filtrés, et après que leur densité ait été contrôlée et ajustée si nécessaire.3. Method according to any one of claims 1 or 2 characterized in that the solutions are recirculated. after being filtered, and after their density has been checked and adjusted if necessary. 4. Installation pour la mise en oeuvre du procédé selon l'une quelconque des revendications 1 à 3 caractérisé par un premier moyen de décantation (5) rempli d'une première solution de densité d = 1 kg/1, un moyen d'évacuation (7) des produits dont la densité est supérieure à 1 kg/1 vers un premier moyen d'homogénéisation et de mouillage (20) comprenant une solution dont la densité d = 1,2 kg/1, un moyen de transport (22) pour transvaser ledit produit et la deuxième solution dans un deuxième moyen de séparation (30) , une conduite (27j pour évacuer les produits dont la densité est supérieure à 1,2 kg/1 vers un premier moyen de stockage (35) , une conduite d'évacuation (37) des produits dont la densité est comprise entre 1 kg/1 et 1,2 kg/1 vers un deuxième moyen de stockage (45), une conduite d'évacuation des produits dont la densité est inférieure à 1 kg/1 du premier moyen de décantation (5) vers une troisième unité de mouillage et d'homogénéisation (60) comprenant une solution de densité d =0,93kg/1, une conduite d'évacuation (67) des produits dont la densité est comprise entre 0,93 kg/1 et 1 kg/1 vers un troisième moyen de stockage (75), une conduite d'évacuation (77) des produits dont la densité est inférieure à 0,93 kg/1 vers un quatrième moyen de homogénéisation et de mouillage (85) comprenant une solution dont la densitéd = 0,91 kg/1, une conduite d'évacuation (87) du mélange de solution et de particules vers un quatrième moyen de séparation (70), une conduite d'évacuation (72) des produits dont la densité est comprise entre 0,91 kg/1 et 0,93 kg/1 vers un quatrième moyen de stockage (100), une conduite d'évacuation (77) des produits dont la densité est inférieure à 0,91 g/1 du quatrième moyen de séparation (70) vers un cinquième moyen de stockage (110).4. Installation for the implementation of the method according to any one of claims 1 to 3 characterized by a first decantation means (5) filled with a first solution of density d = 1 kg / 1, a means of evacuation (7) products whose density is greater than 1 kg / 1 to a first means of homogenization and wetting (20) comprising a solution whose density d = 1.2 kg / 1, a means of transport (22) for transferring said product and the second solution into a second separation means (30), a pipe (27d for discharging products whose density is greater than 1.2 kg / 1 to a first storage means (35), a pipe evacuation (37) of products whose density is between 1 kg / 1 and 1.2 kg / 1 to a second storage means (45), an evacuation pipe for products whose density is less than 1 kg / 1 from the first settling means (5) to a third wetting and homogenization unit (60 ) comprising a solution of density d = 0.93 kg / 1, a discharge pipe (67) for products whose density is between 0.93 kg / 1 and 1 kg / 1 to a third storage means (75) , a discharge pipe (77) for products whose density is less than 0.93 kg / 1 to a fourth means of homogenization and wetting (85) comprising a solution whose density d = 0.91 kg / 1, a evacuation pipe (87) of the mixture of solution and particles to a fourth separation means (70), an evacuation pipe (72) for products whose density is between 0.91 kg / 1 and 0.93 kg / 1 to a fourth storage means (100), an evacuation pipe (77) for products whose density is less than 0.91 g / 1 from the fourth separation means (70) to a fifth storage means ( 110). 5. Installation selon la revendication 4 caractérisé par des moyens de séchage pour les produits après chaque étape de séparation.5. Installation according to claim 4 characterized by drying means for the products after each separation step. 6. Installation selon l’une quelconque des revendications 4 ou 5 caractérisé en ce que les moyens de séchage sont des tamis vibrants (15), (30) , (40), (55) , (70), (80), (95)et (105).6. Installation according to any one of claims 4 or 5 characterized in that the drying means are vibrating screens (15), (30), (40), (55), (70), (80), ( 95) and (105). 7. Installation selon l'une quelconque des revendications 4 à 6 caractérisé par des bassins de rétention ( 115), (120), (130), (135), (140), (145), (150), (155) pour les solutions situés en dessous des différents tamis (15), (30), (40), (55), (70), (80), (95)et (105).7. Installation according to any one of claims 4 to 6 characterized by retention basins (115), (120), (130), (135), (140), (145), (150), (155) for solutions located below the different sieves (15), (30), (40), (55), (70), (80), (95) and (105). 8. Installation selon l'une quelconque des revendications 4 à 7 caractérisé par un circuit de recirculation séparé pour chacune des solutions utilisées comprenant une installation de filtrage, de dosage, et d'ajustage de la densité (125), (160), (165), (170).8. Installation according to any one of claims 4 to 7 characterized by a separate recirculation circuit for each of the solutions used comprising a filtering, dosing and density adjustment installation (125), (160), ( 165), (170). 9. Installation selon l'une quelconque des revendications 4 à 8 caractérisé par une bande de transport (10) situé au fond du premier bassin de décantation et par une deuxième bande de transport (50) située en partie en dessous du niveau du liquide.9. Installation according to any one of claims 4 to 8 characterized by a conveyor belt (10) located at the bottom of the first settling tank and by a second conveyor belt (50) located partly below the level of the liquid. 10. Installation selon l’une quelconque des revendications 4 à 9 caractérisé en ce que les deuxième Î25) . troisième (65) et auatrième (70) movens de séoaration sont des hydrocyclones.10. Installation according to any one of claims 4 to 9 characterized in that the second Î25). third (65) and fourth (70) seoaration movens are hydrocyclones.