KR960013901B1 - Method for manufacturing stocking using nylon yarn - Google Patents

Abstract

The method is designed to knit a sock after coating a spandex using yarn with 4.5 - 5 of flatness. The method includes the steps of : manufacturing nylon hetero sectional yarn having 4.5 - 5 of flatness; manufacturing coated yarn by coating a spandex with nylon flat yarn; and knitting a sock. The method enables to manufacture socks having excellent operability, appearance and feeling.

Description

나이론편평사를 사용한 스타킹의 제조방법 및 그에 의해 수득되는 스타킹Manufacturing method of stockings using nylon flat yarn and stockings obtained by

제1도는 본 발명의 실시예에 이용되는 방사구금의 단면도.1 is a cross-sectional view of the spinneret used in the embodiment of the present invention.

제2도는 제1도의 방사구금에 의해 제조된 나이론 필라멘트사의 단면도.2 is a cross-sectional view of the nylon filament yarn produced by the spinneret of FIG.

제3도 (a), (b)는 본 발명의 제2도에 도시된 필라멘트사의 광택효과를 나타내주는 구성도.Figure 3 (a), (b) is a block diagram showing the gloss effect of the filament yarn shown in Figure 2 of the present invention.

제4도의 (a)는 본 발명의 나이론 편평사로 스판덱스를 피복한 피복사의 단면도, (b)는 종래의 나이론 라운드사로 스판덱스를 피복한 피복사의 단면도이다.(A) is sectional drawing of the coated yarn which covered the spandex with the nylon flat yarn of this invention, (b) is sectional drawing of the coated yarn which covered the spandex with the conventional nylon round yarn.

* 도면의 주요부분에 대한 부호의 설명* Explanation of symbols for main parts of the drawings

L : 슬릿의 길이 W : 슬릿의 폭L: length of slit W: width of slit

R : 슬릿 끝의 반경 1 : 스판덱스R: radius of slit tip 1: spandex

2 : 나이론 편평사 3 : 나이론 라운드사2: nylon flat yarn 3: nylon round yarn

본 발명은 나이론 편평사를 이용한 스타킹의 제조방법에 관한 것이다. 좀 더 상세하게는 편평도가 4.5∼5인 나이론 편평사를 사용하여 스판덱스를 피복한 후 편직하는 것을 특징으로 하는 스타킹의 제조방법에 관한 것이다.The present invention relates to a method for producing stockings using nylon flat yarn. More specifically, the present invention relates to a method for manufacturing stockings, wherein the knitting is performed after coating the spandex using a nylon flat yarn having a flatness of 4.5 to 5.

근래 스타킹의 시장은 1세대인 레그 스타킹(Reg Stocking)의 시대를 지나 2세대인 써포트 스타킹(Support Stocking)이 전체 스타킹 시장의 70%정도를 점하고 있으며, 최근에는 전체 피복사를 사용한 조끼타입 스타킹도 선을 보이고 있다.Recently, the market of stockings has passed the era of the first generation of Reg Stocking, and the second generation of Support Stocking occupies about 70% of the overall stocking market. The road is showing the line.

스타킹은 여성의 레그부위에 착용되는 것이기 때문에 스타킹 제조용사의 개발에 있어서는 촉감, 외관 및 신축성등을 개선하는 것이 핵심 과제이다.Since stockings are worn on the legs of women, it is a key task to improve the feel, appearance and elasticity in the development of stockings manufacturing companies.

종래의 이러한 기술적 과제를 해결하기 위한 방법으로 스타킹용 사의 굵기를 가늘게 즉, 15/5로 스타킹을 편직하던 것을 12/5로 편직하는 방법이 있다. 그러나 이 방법에 의한 경우는 촉감 개선에 한계가 있고, 사의 제조공정성이 저하되는 문제점이 있다.As a method for solving the conventional technical problem, there is a method of narrowing the thickness of the yarn for stockings, that is, knitting the stockings at 15/5 by 12/5. However, in this method, there is a limit to the improvement of the feel, there is a problem that the manufacturing processability of the yarn is lowered.

종래의 스타킹 제조에 사용되는 피복사에 있어서 피복되는 나이론은 원형 단면인 나이론 라운드사가 대부분이었는데, 사의 단면이 변형되지 않은 라운드사만으로는 외관의 개선에 한계가 있음이 지적되어 왔다.In the coated yarn used in the manufacture of the conventional stocking, most of the nylon covered yarns were circular cross-sections. However, it has been pointed out that the round yarns of which the cross-sections of the yarns are not deformed have limitations in appearance improvement.

한편 편평사 제조용 방사구금이 일본 공개특허 공고 소화 55-122074호 및 국내특허 공고 86-397, 91-3166등에 소개되어 있으나 이러한 방사구금을 이용하여 섬유를 제조하는 경우에는 사단면이 불균일하고 제조된 사의 무성도 불균일하여 스타킹 제조에는 이용되지 못하였다.Meanwhile, spinnerets for manufacturing flat yarns are introduced in Japanese Patent Laid-Open No. 55-122074 and Korean Patent Nos. 86-397, 91-3166. However, when fabricating fibers using such spinnerets, the cross section is uneven and manufactured. The asexuality of the yarn was also uneven so that it could not be used to manufacture stockings.

이외에도 많은 이형단면사 제조용 방사구금이 소개된바 있으나, 이들도 상기의 문제점을 완전히 해결하지는 못하였다.In addition, many spinnerets for manufacturing a release section yarn have been introduced, but these have not completely solved the above problems.

본 발명의 목적은 상기한 바와 같은 문제점을 해결하여 촉감, 외관 및 신축성이 향상된 스타킹을 제조하는 방법을 제공하는 것이다.SUMMARY OF THE INVENTION An object of the present invention is to provide a method of manufacturing a stocking with improved touch, appearance and elasticity by solving the above problems.

즉, 본 발명은 제1도에 도시된 바와 같은 하기 식(Ⅰ)의 조건을 만족시키는 방사구금을 이용하여 사단면이 편평한 나이론 이형단면사를 제조하고, 이와 같이 제조된 나이론 편평사로 스판덱스를 피복하여 피복사를 만든 후 편직하는 것을 특징으로 하는 스타킹의 제조방법을 제공하는 것이다. 상기 나이론 편평사는 편평도가 4.5∼5인 것이 바람직하다.In other words, the present invention is to produce a nylon hetero-section yarn with a flat cross section using a spinneret that satisfies the conditions of the following formula (I) as shown in Figure 1, and covers the spandex with a nylon flat yarn prepared as described above To provide a method for producing stockings characterized in that the knitting yarn after making the yarn. Preferably, the nylon flat yarn has a flatness of 4.5 to 5.

(단, 상기식에서 W:슬릿 폭, L:슬릿길이, R:슬릿끝의 반경이다.)(Wherein, W is the slit width, L is the slit length, and R is the radius of the slit tip.)

이하 본 발명을 도면을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

본 발명의 실시예에 이용되는 편평사 제조용 방사구금을 더욱 상세하게 설명하면 슬릿폭(W)은 0.08㎜∼1.1㎜가 바람직하다. 만일 슬릿폭이 0.08㎜이하이면 방사성이 불량해지고, 1.1㎜이상이면 제조되는 스타킹의 촉감이 저하되고 염색성이 떨어진다.When explaining the spinneret for manufacturing flat yarn used in the Example of this invention in more detail, 0.08 mm-1.1 mm are preferable for the slit width W. If the slit width is 0.08 mm or less, the radioactivity is poor. If the slit width is 1.1 mm or more, the feel of the stocking to be produced is lowered and the dyeability is poor.

슬릿길이(L)와 슬릿폭(W)과의 비(L/W)는 광택효과에 관계되는 것으로, 9∼11의 범위내인 것이 바람직한데, 만약 이 범위를 벗어날 경우 방사후 원사 편평도가 4.5∼5의 범위를 벗어나 광택효과를 충분히 발휘할 수 없게 된다.The ratio between the slit length (L) and the slit width (W) (L / W) is related to the gloss effect, and is preferably in the range of 9 to 11, if it is out of this range, the yarn flatness after spinning is 4.5 It becomes out of the range of -5 and cannot fully exhibit a gloss effect.

또한 슬릿끝의 반경(R)과 슬릿폭(W)과의 비(W/R) 및 슬릿길이(L)와 슬릿끝의 반경(R)과의 비(R/L)가 각각 본 발명에서 제시하는 적정범위인 1.3∼1.5, 0.6∼0.08을 벗어날 경우 본 발명의 제2도에 도시된 바와 같은 단면을 갖는 필라멘트사를 얻을 수 없다.In addition, the ratio of the radius R of the slit (R) to the slit width (W) and the ratio of the slit length (L) and the radius (R) of the slit tip (R / L) are presented in the present invention. If it is outside the appropriate range of 1.3 to 1.5, 0.6 to 0.08, it is not possible to obtain a filament yarn having a cross section as shown in FIG.

상술한 바와 같은 특징을 갖는 본 발명의 방사구금으로부터 제조되는 필라멘트사는 두께가 균일하고 사단면이 제2도에 도시된 바와 같이 편평하게 되어 촉감이 우수하고, 광택이 뛰어난 장점을 갖는다.The filament yarn produced from the spinneret of the present invention having the features as described above has an advantage that the thickness is uniform and the cross section is flat as shown in FIG.

제2도에 도시된 본 발명의 나이론 필라멘트사의 광택효과를 살펴보면 제3도에 도시된 바와같이 일정방향의 빛을 조사함에 대하여 강렬하게 반사하는 부분과 약하게 반사하는 부분을 공유하여 특이한 광택효과를 발현하게 된다. 즉 편평한 부분은 빛을 강렬하게 반사하고(제3도(가)) 둥근부분은 난반사등에 의하여 빛을 약하게 반사한다(제3도(나)).Referring to the gloss effect of the nylon filament yarn of the present invention shown in FIG. 2, as shown in FIG. Done. That is, the flat part reflects light intensely (Fig. 3 (a)) and the round part reflects light weakly by diffuse reflection (Fig. 3 (b)).

본 발명은 상기 나이론 편평사로 스판덱스를 피복하여 제4도의 (가)에 도시된 바와 같은 단면을 갖는 피복사를 제조한 후 편직하는 것을 특징으로 하는 스타킹의 제조방법에 관한 것이다.The present invention relates to a method for producing stockings, wherein the spandex is coated with nylon flat yarn to produce a coated yarn having a cross section as shown in Fig. 4A.

본 발명에 의한 편평사로 스판덱스를 피복하는 경우는 제4도 (나)에 도시된 바와같은 동일한 데니어에서 라운드사로 피복하는 경우에 비해서 표면적이 넓으므로 우수한 피복효과를 가지며 이형단면으로 인해 광택이 우수하고 촉감이 부드러운 효과를 얻을 수 있다.In the case of covering the spandex with the flat yarn according to the present invention, the surface area is wider than that of the round denier at the same denier as shown in FIG. 4 (b), and thus has excellent coating effect and excellent gloss due to the release cross section. The touch feels soft.

또한 라운드사의 세데니어화 경향에 따라 피복효과의 미비에 의한 스판덱스 부분돌출에 기인하는 편직작업성의 저하 및 불균일 염색등의 문제점을 해결할 수 있다.In addition, according to the tendency of rounded dendenization, problems such as deterioration of knitting workability and nonuniform dyeing due to partial spread of spandex due to insufficient coating effect can be solved.

즉, 본 발명에 의하여 편직작업성, 외관 및 촉감이 우수한 스타킹을 제조할 수 있다.That is, according to the present invention, it is possible to produce stockings excellent in knitting workability, appearance and feel.

이하 실시예를 들어 본 발명을 상세히 설명한다.The present invention will be described in detail with reference to the following Examples.

실시예 1Example 1

상대점도가 3.03인 나이론 6칩을 하기 표(1)에 표현된 조건을 만족시키고 제1도에 도시된 단면을 갖는 구멍이 6개 있는 방사구금을 통하여 방사온도 282℃, 토출량 4.6g/분, 권취속도 940m/분으로 방사한 후 연신비 2.92로 연신하여 합성섬유를 제조하고, 그 결과를 하기 표 1에 나타내었다.Spinning temperature 282 ° C., discharge amount 4.6 g / min, through a spinneret with six holes having a cross section shown in FIG. After spinning at a winding speed of 940 m / min to draw a draw ratio of 2.92 to prepare a synthetic fiber, the results are shown in Table 1 below.

비교예 1Comparative Example 1

상대점도가 3.03인 나이론 6칩을 하기 표(1)에 나타난 조건을 만족시키고 제1도에 도시된 단면을 갖는 구멍이 6개 있는 방사구금을 통하여 방사온도 282℃, 토출량 4.6g/분, 권취속도 940m/분으로 방사한 후 연신비 2.92로 연신하여 합성섬유를 제조하고 제조된 사로 스판덱스를 피복한 후 면직하여 스타킹을 제조하였으며 그 결과를 하기 표(1)에 나타내었다.A nylon 6 chip with a relative viscosity of 3.03 meets the conditions shown in Table (1) below and spins through a spinneret with six holes with a cross section shown in Figure 1, spinning temperature of 282 ° C, discharge rate of 4.6g / min, winding After spinning at a speed of 940 m / min and stretched at a draw ratio of 2.92 to prepare a synthetic fiber, coated with a prepared yarn spandex and then cotton to prepare a stocking is shown in Table (1).

비교예 2Comparative Example 2

상대점도 3.03인 나이론 6칩을 라운드 타입의 구멍이 6개 있는 방사구금을 통하여 방사온도 282℃, 토출량 4.6g/분, 권취속도 940m/분으로 방사한 후 연신비 2.92로 연신하여 합성섬유를 제조하였으며 그 결과를 하기 표1에 함께 나타내었다.A synthetic fiber was prepared by spinning a nylon 6 chip with a relative viscosity of 3.03 at a spinning temperature of 282 ° C, a discharge rate of 4.6g / min, and a winding speed of 940m / min through a spinneret with six round holes. The results are shown in Table 1 together.

Claims (1)

하기식(1)의 조건을 만족시키는 방사구금을 이용하여 편평도가 4.5∼5이고 사단면이 편평한 나이론 이형단면사를 제조하고, 이와같이 제조된 나이론 편평사로 스판덱스를 피복하여 피복사를 만든 후, 편직하는 것을 특징으로 하는 스타킹의 제조방법By using a spinneret that satisfies the conditions of the following formula (1), a nylon shaped cross-section yarn is produced with a flatness of 4.5 to 5 and a flat cross section, and the coated yarn is made by covering the spandex with the nylon flat yarn thus prepared, and then knitting. Manufacturing method of stockings characterized in that (단, 상기식에서 W:슬릿 폭, L:슬릿길이, R:슬릿끝의 반경이다.)(Wherein, W is the slit width, L is the slit length, and R is the radius of the slit tip.)