KR950032748A - 폴리테트라플루오로에틸렌 고강도 섬유 및 그의 제조방법 - Google Patents
폴리테트라플루오로에틸렌 고강도 섬유 및 그의 제조방법 Download PDFInfo
- Publication number
- KR950032748A KR950032748A KR1019950014030A KR19950014030A KR950032748A KR 950032748 A KR950032748 A KR 950032748A KR 1019950014030 A KR1019950014030 A KR 1019950014030A KR 19950014030 A KR19950014030 A KR 19950014030A KR 950032748 A KR950032748 A KR 950032748A
- Authority
- KR
- South Korea
- Prior art keywords
- polytetrafluoroethylene
- strength fiber
- high strength
- monofilament
- producing
- Prior art date
Abstract
본 발명은 0.5GPa 이상의 강도를 가지는 폴리테트라플루오로에틸렌(PTEE)고강도 섬유를 제공한다.이것은 페이스트 압출에 의해 PTEE계중합체의 모노필라멘트를 형성시키고, 모노필라멘트를 신축이 자유로운 상태로 열처리하고, 이어서 섬유를 형성하도록 열처리된 모노필라멘트를 연신하여 제조된 고강도 섬유로서 PTEE분자쇄가 섬유의 축방향에 평행한 방향으로 배열되는 것을 특징으로 한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 PTEE 고강도 섬유의 DSC를 나타내는 그래프이다.
Claims (24)
- 페이스트 압출에 의해 형성된 폴리테트라플루오로에틸렌계 중합체의 모노필라멘트를 신축이 자유로운 상태로 열처리한 후 이어서 연신하여 얻어지는 폴리테트라플르오로에틸렌 고강도 섬유로서, 상기한 폴리테트라플루오로에틸렌의 분자쇄가 상기 섬유의 축방향에 대해 평행한 방향으로 배열되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유.
- 제1항에 있어서, 상기한 신축이 자유로운 상태로 열처리한 후의 모노필라멘트의 결정화도가 26% 이상인 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유.
- 페이스트 압출에 의해 형성된 폴리테트라플루오로에틸렌계 중합체의 모노필라멘트를 연신하여 얻어지며 직경이 50㎛이하인 폴리테트라플루오로에틸렌 고강도 섬유로서, 상기 폴리테트라플루오로에틸렌의 인장 파단강도가 0.5GPa 이상인 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유.
- 페이스트 압출에 의해 형성된 폴리테트라플루오로에틸렌계 중합체의 모노필라멘트를 26%이상의 결정화도로 만들기 위해 신축이 자유로운 상태로 열처리한 후 이어서 연신하여 얻어지는 직경50㎛이하인 폴리테트라플루오로에틸렌 고강도 섬유로서, 이 폴리테트라플루오로에틸렌의 인장파단 강도가 0.5GPa 이상인 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유.
- 제3항 또는 제4항에 있어서, 상기한 폴리테트라플루오로에틸렌의 인장파단 강도가 1GPa 내지, 4.2GPa인 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유.
- 폴리테트라플루오로에틸렌계 중합체 빌렛을 페이스트 압출하여 모노필라멘트를 형성시키는 단계와, 상기 모노필라멘트를 신축이 자유로운 상태로 열처리하는 단계와 상기 열처리된 모노필라멘트를 서냉하는 단계와, 상기 열처리된 모노필라멘트를 연신하여 섬유를 형성시키는 단계를 포함하여 이루어지는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제6항에 있어서, 상기한 빌렛이 압출조제로 미리 습윤 처리된 폴리테트라플루오로에틸레 미세분말을 압축하여 형성되는 것임을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제7항에 있어서, 상기한 폴리테트라플루오로에틸렌계 미세분말이 0.1㎛ 내지 0.5㎛범위의 일차 입자직경을 가지는 것임을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제6항에 있어서, 상기한 신축이 자유로운 상태로 열처리가 340℃이상의 온도에서 수행되는 것을 특징으로하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제9항에 있어서, 상기한 신축이 자유로운 상태로 열처리가 340℃ 이상의 온도에서 30분 이상 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제6항에 있어서, 상기한 냉각처리가 10℃/분 이하의 냉각속도로 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제11항에 있어서, 상기한 냉각처리가 열처리 온도로부터 폴리테트라플루오로에틸렌의 유리 전이온도, Tg(122℃)까지 10℃/분 이하의 냉각속도로 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제6항에 있어서, 상기한 냉각처리가 5℃/분 이하의 냉각속도로 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제13항에 있어서,상기한 냉각처리가 열처리 온도로부터 폴리테트라플루오로에틸렌의 유리 전이온도, Tg(122℃)까지 5℃/분 이하의 냉각속도로 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제6항에 있어서, 상기한 연신처리가 340℃이상의 온도에서 50㎜/초 이상의 연신속도로 50배 이상 연신되게 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제6항에 있어서, 상기한 연신처리가 360℃이상의 온도에서 50㎜/초 이상의 연신속도로 50배 이상 연신하기 위해 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제6항에 있어서, 상기한 연신처리가 열처리된 모노필라멘트가 척크 사이에 설치되어 380∼390℃에서 5분 이상 예열된 후의 온도와 같은 온도에서 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 폴리테트라플루오로에틸렌게중합체 빌렛을 30℃이상의 온도에서 300이상의 리덕션비로 페이스트 압출하여 직경이 0.5㎛인 모노필라멘트를 형성시키는 단계와; 상기한 모노필라멘트를 340℃이상의 온도에서 신축이 자유로운 상태로 열처리하는 단계와, 상기 열처리된 모노필라멘트를 5℃/분 이하의 냉각속도로 서서히 냉각하는 단계와 상기 열처리된 모노필라멘트를 340℃ 이상의 온도에서 50㎜/초 이상의 연산속도로 50배 이상으로 연신하여 직경이 50㎛인 섬유를 형성시키는 단계와; 상기 연신처리 후에 즉시 섬유를 냉각시키는 단계를 포함하여 이루어지는 것을 특징으로 하는 폴리테트라에틸렌 고강도섬유의 제조방법.
- 제18항에 있어서, 상기한 신축이 자유로운 상태의 열처리가 350℃이상의 온도에서 30분 이상 수행되는 것을 특징으로 하는폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제18항 또는 제19항에 있어서, 상기한 신축이 자유로운 상태의 열처리한 후의 상기 모노필라멘트의 결정화도가 26% 이상인 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제18항에 있어서, 상기한 연신처리가 360℃이상의 온도에서 50㎜/초 이상의 연신속도로 50배 이상 연신하도록 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제18항에 있어서, 상기한 연신처리가 열처리된 모노필라멘트가 척크사이에 설치되어 380∼390℃에서 5분 이상 예열된 후의 온도와 같은 온도에서 수행되는 것을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.
- 제18항에 있어서, 상기한 빌렛이 압출조제로 미리 습윤처리된 폴리테트라플루오로에틸렌계 미세분말을 압축하여 형성되는 것임을 특징으로 하는 폴리테트라플루오로에틸렌 고강도섬유의 제조방법.
- 제18항에 있어서, 상기한 폴리테트라플루오로에틸렌계 미세분말이 0.1㎛내지 0.5㎛범위의 일차 입자직경을 가지는 것임을 특징으로 하는 폴리테트라플루오로에틸렌 고강도 섬유의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.