KR950013334A - Process for preparing processable conductive colloidal polymer - Google Patents

Process for preparing processable conductive colloidal polymer Download PDF

Info

Publication number
KR950013334A
KR950013334A KR1019930021514A KR930021514A KR950013334A KR 950013334 A KR950013334 A KR 950013334A KR 1019930021514 A KR1019930021514 A KR 1019930021514A KR 930021514 A KR930021514 A KR 930021514A KR 950013334 A KR950013334 A KR 950013334A
Authority
KR
South Korea
Prior art keywords
colloidal polymer
hydration
conductive colloidal
acrylate
emulsion
Prior art date
Application number
KR1019930021514A
Other languages
Korean (ko)
Other versions
KR970004756B1 (en
Inventor
첸 슈안
첸 치쳉
Original Assignee
칭 파아오 후
내쇼날 사이언스 카운실
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 칭 파아오 후, 내쇼날 사이언스 카운실 filed Critical 칭 파아오 후
Priority to KR1019930021514A priority Critical patent/KR970004756B1/en
Publication of KR950013334A publication Critical patent/KR950013334A/en
Application granted granted Critical
Publication of KR970004756B1 publication Critical patent/KR970004756B1/en

Abstract

본 발명은 수화반응 매개물에서 가공성 도전 콜로이드 폴리머를 제조하는 방법에 관한 것이다. 수화매개물에서 희석된 폴리머릭 에멀젼은 수화매개물에서 콜로이드 폴리머를 합성하는 동안 방향족 헤테로 사이클릭 모노머에 대한 스테리 안정제로서 사용된다.The present invention relates to a process for preparing a processable conductive colloidal polymer in a hydration medium. Diluted polymeric emulsions in the hydration media are used as steri stabilizers for aromatic heterocyclic monomers during the synthesis of the colloidal polymers in the hydration media.

합성된 콜로이드 폴리머는 스테릭 안정제와 혼합되는 용매에서 더 분산된다. 분산액은 기판을 금속화하도록 비전도 기판위에 코팅될 수 있으며, 플라스틱과 섬유에 대해서 정전기 방지코팅제로서 사용될 수 있다.The synthesized colloidal polymer is further dispersed in a solvent mixed with a steric stabilizer. The dispersion may be coated onto a nonconductive substrate to metallize the substrate and may be used as an antistatic coating agent for plastics and fibers.

Description

가공성 도전 콜로이드 폴리머의 제조방법Process for preparing processable conductive colloidal polymer

본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음Since this is an open matter, no full text was included.

제1도는 응용실시예 1의 콜로이드층을 스캐닝 일렉트론 마이크로스코피(이후, SEM으로 통칭함)로 관찰했을때의 사진.1 is a photograph when the colloid layer of Application Example 1 is observed by scanning electron microscopy (hereinafter collectively referred to as SEM).

제2도는 응용예 1의 구리층을 SEM으로 관찰했을때의 사진.2 is a photograph when the copper layer of Application Example 1 is observed by SEM.

Claims (27)

수화매개물내에 가공된 도전 콜로이드 폴리머 제조방법에 있어서, (a) 스테릭 안정제로서 폴리머릭 에멀젼을 제조하는 단계, (b) 수화분산매개물로 폴리머릭 에멀젼을 희석하는 단계, (c) 피롤, N-치환 피롤, 베타-치환 피롤, 티오펜, 아닐린, 푸란으로 이루어진 그룹에서 선택된 방향족 헤테로 사이클릭 모노머를 방향족 헤테로 사이클릭 모노머용 산화제와 희석된 폴리머릭 에멀젼으로 이루어진 수화매개물내에 혼합물과 산화적으로 중합하는 단계와, 그리고 (d) 수화물로부터 가공성 도전 콜로이드 폴리머를 분리하는 단계로 이루어진 가공성 도전 콜로이드 폴리머 제조방법.A process for preparing a conductive colloidal polymer processed in a hydration medium, comprising: (a) preparing a polymeric emulsion as a steric stabilizer, (b) diluting the polymeric emulsion with a hydration dispersion medium, (c) pyrrole, N- Oxidative polymerization of an aromatic heterocyclic monomer selected from the group consisting of substituted pyrrole, beta-substituted pyrrole, thiophene, aniline and furan with a mixture in a hydration medium consisting of an oxidizing agent for an aromatic heterocyclic monomer and a diluted polymeric emulsion And (d) separating the processable conductive colloidal polymer from the hydrate. 제1항에 있어서, 폴리머릭 에멀젼이 폴리(비닐 아세테이트)의 에멀젼인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method of claim 1 wherein the polymeric emulsion is an emulsion of poly (vinyl acetate). 제1항에 있어서, 폴리머릭 에멀젼이 아크릴레이트의 에멀젼인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method of claim 1, wherein the polymeric emulsion is an emulsion of acrylate. 제3항에 있어서, 아크릴레이트가 폴리(메틸 메타크릴레이트-코-부틸 아크릴레이트)인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.4. A process according to claim 3, wherein the acrylate is poly (methyl methacrylate-co-butyl acrylate). 제3항에 있어서, 아크릴레이트가 폴리(메틸 케타크릴레이트-코-부틸 아크릴레이트-코-아크릴산)인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.4. The process for producing a processible conductive colloidal polymer according to claim 3, wherein the acrylate is poly (methyl methacrylate-co-butyl acrylate-co-acrylic acid). 제3항에 있어서, 아크릴레이트가 폴리(메틸 메타크릴레이트-코-부틸 아크릴레이트-코-비닐 아세테이트)인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.4. A process according to claim 3, wherein the acrylate is poly (methyl methacrylate-co-butyl acrylate-co-vinyl acetate). 제1항에 있어서, 수화분산 매개물이 물인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method of claim 1 wherein the hydration dispersion medium is water. 제1항에 있어서, 수화분산 매개물이 산성수화용액인 것을 특징으로 하는 가공성 도전 콜로이드 폴리어 제조방법.The method of claim 1, wherein the hydration dispersion medium is an acidic hydration solution. 제1항에 있어서, 산화제가 철염, 구리염, 과황산염, 할로겐, 질산은, 니크롬산염, 과망간산염, 망간산염, 과요오드산염, 세슘염(2V)으로 이루어진 그룹으로부터 선택되는 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The processable conductivity according to claim 1, wherein the oxidizing agent is selected from the group consisting of iron salt, copper salt, persulfate, halogen, silver nitrate, nichromate, permanganate, manganate, periodate, cesium salt (2V). Method for preparing colloidal polymer. 제9항에 있어서, 산화제가 염화철인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.10. The method of claim 9, wherein the oxidant is iron chloride. 제1항에 있어서. 방향족 헤테로사이클릭 모노머가 피롤인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method of claim 1. A process for producing a processible conductive colloidal polymer, wherein the aromatic heterocyclic monomer is pyrrole. 제1항에 있어서, 여과에 의해 분리되는 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method for producing a processible conductive colloidal polymer according to claim 1, which is separated by filtration. 수화물에 있는 가공성 도전 콜로이드 폴리머 제조방법에 있어서, (a) 스테릭 안정제내에 있는 폴리머릭 에멀젼을 제조하는 단계, (b) 수화분산 매개물로 폴리머릭 에멀젼을 희석하는 단계, (c) 피롤, N-치환 피롤, 베타-치환 피롤, 티오펜, 아닐린, 푸란으로 이루어진 그룹에서 선택된 방향족 헤테로 사이클릭 모노머와 방향족 헤테로 사이클릭 모노머에 대한 산화제와 희석된 폴리머릭 에멀젼을 함유한 혼합물을 수화매개물에서 산화적으로 중합하는 단계, (d) 수화매개물로부터 가공성 도전 콜로이드 폴리머를 분리하는 단계와, 그리고 (e) 폴리머 에멀젼내에 폴리머와 혼합되는 용매에서 얻어진 가공성 도전 콜로이드 폴리머를 분산하는 단계들로 이루어진 가공성 도전 콜로이드 폴리머 제조방법.A process for preparing a processable conductive colloidal polymer in hydrate, comprising: (a) preparing a polymeric emulsion in a steric stabilizer, (b) diluting the polymeric emulsion with a hydration dispersion medium, (c) pyrrole, N- A mixture containing an aromatic heterocyclic monomer selected from the group consisting of substituted pyrrole, beta-substituted pyrrole, thiophene, aniline, and furan and an oxidant for the aromatic heterocyclic monomer and a diluted polymeric emulsion is oxidatively hydrated in the hydration medium. Preparing a processable conductive colloidal polymer comprising: polymerizing, (d) separating the processable conductive colloidal polymer from the hydration medium, and (e) dispersing the processable conductive colloidal polymer obtained in a solvent mixed with the polymer in a polymer emulsion. Way. 제13항에 있어서, 폴리머릭 에멀젼이 폴리(비닐 아세테이트)의 에멀젼인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.15. The method of claim 13, wherein the polymeric emulsion is an emulsion of poly (vinyl acetate). 제13항에 있어서, 폴리머릭 에멀젼이 아크릴레이트의 에멀젼인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법,The process for producing a processible conductive colloidal polymer according to claim 13, wherein the polymeric emulsion is an emulsion of acrylate, 제15항에 있어서, 아크릴레이트가 폴리(메틸 메타크릴레이트-코-부틸 아크릴레이트)인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.16. The process of claim 15 wherein the acrylate is poly (methyl methacrylate-co-butyl acrylate). 제15항에 있어서, 아크릴레이트가 폴리(메틸 메케타크릴레이트-코-부틸 아크릴레이트-코-아크릴산)인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.16. The method of claim 15, wherein the acrylate is poly (methyl methacrylate-co-butyl acrylate-co-acrylic acid). 제15항에 있어서, 아크릴레이트가 폴리(메틸 메타크릴레이트-코-부틸 아크릴레이트-코-비닐 아세테이트)인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.16. The process of claim 15 wherein the acrylate is poly (methyl methacrylate-co-butyl acrylate-co-vinyl acetate). 제13항에 있어서, 수화분산 매개물이 물인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method of claim 13 wherein the hydration dispersion medium is water. 제13항에 있어서, 수화분산 매개물이 산성수화용액인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The process for producing a processible conductive colloidal polymer according to claim 13, wherein the hydration dispersion medium is an acidic hydration solution. 제13항에 있어서, 산화제가 과황산염, 할로겐화물, 질산염, 니크롬산염, 과망간산염, 망간산염, 과요오드산염의 철염, 구리염, 세슘염(IV)으로 이루어진 그룹으로부터 선택되는 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.14. Processability according to claim 13, wherein the oxidizing agent is selected from the group consisting of persulfates, halides, nitrates, nichromates, permanganates, manganates, perioates, copper salts, cesium salts (IV). Method for preparing a conductive colloidal polymer. 제21항에 있어서, 산화제가 염화철인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.22. The method of claim 21, wherein the oxidant is iron chloride. 제13항에 있어서, 방향족 헤테로 사이클릭 모노머가 피롤인 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The process for producing a processible conductive colloidal polymer according to claim 13, wherein the aromatic heterocyclic monomer is pyrrole. 제13항에 있어서, 여과에 의해 분리되는 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method for producing a processible conductive colloidal polymer according to claim 13, which is separated by filtration. 제13항에 있어서, 단계(e)에서 사용된 용매가 메탄올, 벤젠, 톨루엔, 클로로포름, DMF, 아세톤, 부타논과 에스테르로 이루어진 그룹으로부터 선택되는 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method of claim 13, wherein the solvent used in step (e) is selected from the group consisting of methanol, benzene, toluene, chloroform, DMF, acetone, butanone and esters. 제25항에 있어서, 단계(e)에서 사용된 용매가 메탄올이라는 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.27. The process of claim 25, wherein the solvent used in step (e) is methanol. 제25항에 있어서, 단계(e)에서 사용된 용매가 부타논이라는 것을 특징으로 하는 가공성 도전 콜로이드 폴리머 제조방법.The method of claim 25, wherein the solvent used in step (e) is butanone. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.※ Note: The disclosure is based on the initial application.
KR1019930021514A 1993-10-16 1993-10-16 Manufacturing method of conductive colloid polymer KR970004756B1 (en)