KR920008931B1 - Video tape - Google Patents
Video tape Download PDFInfo
- Publication number
- KR920008931B1 KR920008931B1 KR1019900003745A KR900003745A KR920008931B1 KR 920008931 B1 KR920008931 B1 KR 920008931B1 KR 1019900003745 A KR1019900003745 A KR 1019900003745A KR 900003745 A KR900003745 A KR 900003745A KR 920008931 B1 KR920008931 B1 KR 920008931B1
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive
- video tape
- magnetic material
- tape
- mixed
- Prior art date
Abstract
Description
[발명의 명칭][Name of invention]
비디오 테이프video tape
[발명의 상세한 설명]Detailed description of the invention
본 발명은 비디오 테이프에 관한 것으로, 특히 통상적인 비디오 테이프의 기능을 충분히 수행하면서 동시에 비디오 크리닝 테이프의 기능을 수행할 수 있는 비디오 테이프에 관한 것이다.TECHNICAL FIELD The present invention relates to a video tape, and more particularly, to a video tape capable of performing a function of a video cleaning tape while fully performing a function of a conventional video tape.
일반적으로 사용되고 있는 비디오 크리닝 테이프는 비자성지지체와, 그비자성지지체의 상면에 형성되는 연마제등을 포함한 비자성층으로 구성되어 있으며, 상기 비자 성층은 브이씨알의 헤드를 크리닝하는 연마제와, 상기 연마제를 비자성지지체상에 고착시킬 수 있는 접착제(binder)와 더불어 크리닝 테이프의 기능에 필요한 첨가제로 구성되어 있다.A video cleaning tape generally used is composed of a nonmagnetic support, a nonmagnetic layer including an abrasive formed on an upper surface of the nonmagnetic support, and the nonmagnetic layer comprises an abrasive for cleaning the head of V-Cal, and the abrasive. It consists of an additive necessary for the function of the cleaning tape, together with a binder which can adhere on a nonmagnetic support.
상기한 바와 같은 비디오 크리닝 테이프는 외부신호를 기록할 수 없는 구조로서 일반적인 비디오 테이프로는 사용할 수 없는 단점이 있는 것이며, 단지 헤드를 크리닝하는 기능만 수행할 뿐이었다.The video cleaning tape as described above has a disadvantage in that external signals cannot be recorded and cannot be used as a general video tape, and only the head cleaning function is performed.
만일, 이와 같은 비디오 크리닝 테이프를 일반적인 비디오 테이프로 사용할 경우에는 S/N가 현저하게 낮아 일반적인 비디오 테이프 보다 화질이 현격하게 떨어지게 되는 현상이 발생하게 되는 것이다.If such a video cleaning tape is used as a general video tape, the S / N is remarkably low, resulting in a sharp drop in image quality than a general video tape.
본 발명은 상기한 바와 같은 종래의 문제점을 해소하기 위하여 창안한 것으로, 이하, 본 발명을 보다 상세하게 설명하면 다음과 같다.The present invention was devised to solve the above-mentioned conventional problems. Hereinafter, the present invention will be described in more detail as follows.
최근 자기기록분야, 특히 비디오 테이프 분야는 자기기록매체의 고성능화, 고신뢰성의 요구가 높아짐에 따라 내구성 및 내환경성에 대한 문제가 더욱 중요시되고 있는 실정이다.Recently, in the magnetic recording field, particularly in the video tape field, as the demand for high performance and high reliability of the magnetic recording medium increases, problems regarding durability and environmental resistance become more important.
상기한 내구성이란 다양한 환경에서의 장시간 사용에 기초를 둔 전자기적, 치수형상적, 기계강도적, 화학적, 그리고 주행성능의 특성 열화정도에 대한 것으로, 특히 비디오 테이프의 경우에는 테이프와 헤드, 데이프와 실린더 사이에서의 고속접촉이 수반 되므로 비디오 테이프의 구성 성분상 헤드 오염이 발생되는 것은 필연적이다 하겠으며, 연속녹화작업을 하는 복사장치(duplicator)에서의 상기한 바와 같은 문제는 한층 엄격한 상황에 놓이게 되는 것이다.The durability described above refers to the degree of deterioration of the characteristics of electromagnetic, dimensional, mechanical, chemical, and driving performance based on long-term use in various environments, and especially in the case of video tape, tape, head, tape and tape. It is inevitable that head contamination occurs due to the high speed contact between the cylinders, and the above problem in the duplicator with continuous recording is subject to a more severe situation. .
본 발명의 목적은 상기한 바와 같은 비디오 테이프의 통상적인 역할을 수행하면서 동시에 비디오 크리닝 테이프의 역할을 하는 비디오 테이프를 제공함에 있는 것이다.It is an object of the present invention to provide a video tape which performs the usual role of a video tape as described above and at the same time serves as a video cleaning tape.
본 발명에 의한 비디오 테이프는 기존의 비디오 크리닝 테이프를 기본으로하여 제조된다.The video tape according to the present invention is manufactured on the basis of the existing video cleaning tape.
즉, 비자성지지체의 상면에 접착제, 첨가제등이 혼합된 코팅층을 통상의 방법으로 형성하되, 상기 코팅층에 자기기록 및 재생을 할 수 있도록 자성체를 혼합하여, 그 자성체가 혼합된 코팅층이 형성되는 부분을 이용하여 테이프의 크리닝 기능을 수행함은 물론, 자기기록 및 재생을 할 수 있는 복합테이프로 형성한 것이다.That is, a coating layer in which an adhesive, an additive, etc. is mixed on the upper surface of the nonmagnetic support is formed by a conventional method, and a portion of the coating layer in which the magnetic material is mixed is formed by mixing magnetic materials to enable magnetic recording and reproduction on the coating layer. By performing the cleaning function of the tape, as well as to form a composite tape capable of magnetic recording and reproduction.
상기 자성체는 경도가 높은 CrO2자성체가 사용되고, 그 CrO2의 입자크기(BET)는 15~40㎡/g인 것이 사용되며, 더욱 좋기로는 20~35㎡/g이다.CrO 2 magnetic material having high hardness is used as the magnetic material, and the particle size (BET) of the CrO 2 is 15 to 40 m 2 / g, and more preferably 20 to 35 m 2 / g.
또한, 본발명에 의한 비디오 테이프의 코팅층을 구성하는 접착제로는 카르복실(carboxyl)기와, 하이드록실(hydroxyl)기를 일정비율로 함유한 비닐(vinyl)계 공중합체와, 하이드록실기를 함유하는 지방족 폴리 우레탄(Aliphatic Polyurethane) 수지를 적정비율로 혼합하여 사용하며, 그 혼합접착제에 폴리이소시아네이트(Polyisocyanate)수지를 혼합접착제량에 대하여 20~100w%로 사용하고, 더욱 좋기로는 40~70wt%이다.In addition, the adhesive constituting the coating layer of the videotape according to the present invention is a vinyl copolymer containing a carboxyl group, a hydroxyl group at a predetermined ratio, and an aliphatic containing a hydroxyl group. Polyurethane (Aliphatic Polyurethane) resin is used by mixing in an appropriate ratio, the polyisocyanate (Polyisocyanate) resin is used in the mixed adhesive 20 to 100% by weight based on the amount of the mixed adhesive, more preferably 40 to 70wt%.
한편, 상기한 바와 같은 본발명에 의한 복합테이프는 일반적으로 사용되는 비디오 테이프에 그비디오 테이프 전체길이의 30% 이내로 비디오 테이프의 양단부 또는 중간부중 하나 이상을 선택하여 연결사용할 경우, 비디오 테이프의 통상적인 역할을 충분하게 수행하면서 동시에 크리닝 효과도 충분히 발휘함을 알 수 있었다.On the other hand, the composite tape according to the present invention as described above is generally used when the one or more of the end or middle portion of the video tape is connected to the commonly used video tape within 30% of the total length of the video tape, While fulfilling the role sufficiently, the cleaning effect was also shown to be sufficient.
상기한 바와 같은 본 발명에 의한 비디오 테이프는 본 발명의 일실시예와 종래 기술에 의한 비교예 1,2의 S/N 및 헤드 오염상태을 비교함으로써 그 특성을 보다 쉽게 이해할 수 있을 것이다.As described above, the video tape according to the present invention may be more easily understood by comparing the S / N and head contamination states of Comparative Examples 1 and 2 according to one embodiment of the present invention and the prior art.
[본 발명의 실시예]Embodiment of the Invention
1) CrO₂: 100(중량율)1) CrO₂: 100 (weight ratio)
2) 비닐계공중합체 : 12(중량율)2) Vinyl copolymer: 12 (weight ratio)
(OH, -COOH기 포함)(Including OH and -COOH groups)
3) 폴리우레탄 수지 : 8(중량율)3) Polyurethane resin: 8 (weight ratio)
4) 폴리이소시아네이트수지 : 10(중량율)4) Polyisocyanate resin: 10 (weight ratio)
5) 분산제 : 1(중량율)5) Dispersant: 1 (weight ratio)
6) 윤활제 : 3(중량율)6) Lubricant: 3 (weight ratio)
7) 솔벤트 : 272(중량율)7) Solvent: 272 (weight)
[비교예 1]Comparative Example 1
1) Co-γ-Fe O(Hc : 700 Oe) : 50(중량율)1) Co-γ-Fe O (Hc: 700 Oe): 50 (weight ratio)
2) 연마제 : α-A2O3: 50(중량율)2) Abrasive: α-A 2 O 3 : 50 (weight ratio)
3) 비닐계공중합체 : 12(중량율)3) Vinyl copolymer: 12 (weight ratio)
(-OH,-COOH기 포함)(Including -OH and -COOH groups)
4) 폴리우레탄수지 : 8(중량율)4) Polyurethane resin: 8 (weight ratio)
5) 폴리이소시아네이트 : 10(중량율)5) Polyisocyanate: 10 (weight ratio)
6) 분산체 : 1(중량율)6) Dispersion: 1 (weight ratio)
7) 윤활제 : 3(중량율)7) Lubricant: 3 (weight ratio)
8) 솔벤트 : 272(중량율)8) Solvent: 272 (weight)
[비교예 2]Comparative Example 2
일반적으로 사용되는 비디오 테이프Commonly used video tape
*결과*result
1) S/N1) S / N
2) 오염상태2) Pollution
%C : 극히 양호% C: Extremely good
○: 양호○: good
△ : 소량 오염△: small amount of contamination
S : 과량 오염S: excessive pollution
상기한 바와 같은 본발명의 비디오 테이프 및 종래 기술에 의한 비디오 테이프의 S/N 및, 실린더 오염상태 비교 실험에 의하면 본 발명에 의한 비디오 테이프의 S/N가 비교예 1, 2보다 월등히 우수한 값을 보이고 있음을 알 수 있으며 S/N실험에서는 비교예 1이 가장 낮은 값을 보이고 있다.According to the comparative experiments of the S / N of the video tape of the present invention and the video tape according to the prior art, and the cylinder contamination state, the S / N of the video tape according to the present invention was much better than those of Comparative Examples 1 and 2. It can be seen that Comparative Example 1 shows the lowest value in the S / N experiment.
상기한 바와 같은 형상은 본 발명의 자성체인 CrO2가 연마제의 역할을 하면서 탁월한 자성체의 효과도 발휘하기 때문이다.The shape as described above is because CrO 2, which is the magnetic body of the present invention, also plays a role of an abrasive, and also exhibits the effect of an excellent magnetic body.
또한, 헤드 및 헤드 실린더 오염상태 실험에서는 본 발명에 의한 비디오 테이프가 비교예 1과 같은 수준을 나타내 보이고 있음을 알 수 있으며, 이것 역시 CrO2자성체가 연마제의 효과를 발휘하기 때문인 것이다.In addition, in the head and head cylinder contamination state experiment, it can be seen that the video tape according to the present invention shows the same level as in Comparative Example 1, which is also because the CrO 2 magnetic body exhibits the effect of the abrasive.
이상에서 설명한 바와 같은 본 발명에 의한 비디오 테이프는 코팅층에 자성체로서 일반 크롬연마제(Cr2O3)와 경도가 비슷한 CrO2자성체를 사용함과 아울러 적정비율의 접착제를 혼합 사용함으로써 기존 비디오 테이프 보다 S/N 가 높고 동시에 헤드의 크리닝 기능을 수행할 수 있는 효과가 있다.As described above, the video tape according to the present invention uses a CrO 2 magnetic material having a similar hardness to that of a general chromium polishing agent (Cr 2 O 3 ) as a magnetic material in the coating layer, and uses an appropriate ratio of adhesive to mix S / N is high and there is an effect that can perform the cleaning function of the head at the same time.
Claims (1)