KR910007978A - 랜덤 공중합체의 제조방법 - Google Patents
랜덤 공중합체의 제조방법 Download PDFInfo
- Publication number
- KR910007978A KR910007978A KR1019900017400A KR900017400A KR910007978A KR 910007978 A KR910007978 A KR 910007978A KR 1019900017400 A KR1019900017400 A KR 1019900017400A KR 900017400 A KR900017400 A KR 900017400A KR 910007978 A KR910007978 A KR 910007978A
- Authority
- KR
- South Korea
- Prior art keywords
- range
- psi
- hexene
- hydrogen
- propylene
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (17)
- 중합화 조건하, 약 50℃내지 약 90℃의 온도에서, 단량체 및, 임의로는, 수소를 일단계 반응 존(zone)에서 기체상으로 (i) 마그네슘; 티타늄; 할로겐 (이는 염소, 브롬, 또는 요오드이다). 또는 이의 혼합물; 및 폴리카복실산 에스테르(이는 인접한 탄소원자에 결합된 2개의 공면에스테르 그룹을 함유한다)를 함유하는 고체 촉매 전구체; (ii) 하이드로루알루미늄 공촉매; 및 (iii) 하나 이상의 실리콘-산소-탄소 그룹을 함유하는 실리콘 화합물로 이루어진 촉매 시스템과 접촉시킴을 특징으로 하여 (여기에서, (a) 알루미늄대 티타늄의 원자비는 약 10내지 약 300의 범위이고, (b) 알루미늄대 실리콘 화합물의 몰비는 약 0.5내지 약 10의 범위이며, (c) 프로필렌의 부분압은 약 50내지 약 400psi이하의 범위이며, (d) 1-헥센의 부분압은 약 1내지 약 15psi의 범위이며, (e) 수소가 존재하는 경우, 수소의 부분압은 약 80psi이하의 범위이고, (f) 가스 표면 속도는 초당 약 1내지 약 3ft의 범위이며, (g) 1-헥센대 프로필렌의 몰비는 약 0.01:1 내지 약 0.08:1의 범위이다), 프로필렌 및 1-헥센을 함유하는 단량체의 혼합물을 공중합시키는 방법.
- 제1항에 있어서, 알루미늄대 실리콘 화합물의 몰비가 약 1내지 약 5의 범위인 방법.
- 제1항에 있어서, 반응 존 내의 온도가 약 60℃내지 약 80℃의 범위인 방법.
- 제1항에 있어서, 프로필렌 부반압이 약 60 내지 약 400psi의 범위인 방법.
- 제1항에 있어서, 1-헥센의 부분압이 약 4내지 약 12psi의 범위인 방법.
- 제1항에 있어서, 공정은 유동층내에서 연속적으로 수행하는 방법.
- 제1항에 있어서, 일반식(I)의 마그네슘 화합물을 할로탄화수소 및 폴리카복실산 에스테르(이는 인접한 탄소원자에 결합된 2개의 공면 에스테르 그룹을 합유한다)의 존재하에서 2개 이상의 할로겐 원자를 함유하는 할로겐화된 사가 티타늄 화합물로 할로겐화시켜 고형 촉매 전구체를 수득하는 방법.MgPR' (I)상기식에서, R은 알콕사이드 또는 아릴옥사이드 그룹이고, R'는 R 또는 할로겐이다.
- 제1항에 있어서, 하이드로카르빌 알루미늄 공촉매가 트리알킬알루미늄인 방법.
- 제1항에 있어서, 실리콘 화합물이 일반식(II)인 방법.RaSiYbXc(Ⅱ)상기식에서, R은 탄소수 1내지 20의 하이드로카르빌이고, Y는 -OR 또는 -OCOR이며, X는 수소, 염소, 브롬 또는 요오드이고, R 및 Y는 각각 동일하거나 상이하며, a는 0내지 3의 정수이고, b는 1내지 4의 정수이며, c는 0 또는 1이고, a+b+c는 4이다.
- 제8항에 있어서, 마그네슘 화합물이 마그네슘 디에톡사이드이고, 할로겐화된 시가 티타늄 화합물이 사염화티타늄이며, 할로탄화수소가 클로로벤젠이고, 폴리카복실산이 디이소부틸 프탈레이트인 방법.
- 제1항에 있어서, 실리콘 화합물이 디페닐 디메톡시실란인 방법.
- 제1항에 있어서, 실리콘 화합물이 디-이소부틸 디메톡시실란인 방법.
- 제1항에 있어서, 실리콘 화합물이 n-프로필트리메톡시실란인 방법.
- 중합화 조건하, 약 60℃내지 약 80℃의 온도에서, 단량체 및 수소를 일단계 반응 존에서 기체상으로 (i) 마그네슘; 티타늄; 할로겐 (이는 염소, 브롬, 또는 요오드이다). 또는 이의 혼합물; 및 폴리카복실산 에스테르(이는 인접한 탄소원자에 결합된 2개의 공연에스테르 그룹을 함유한다)를 함유하는 고체 촉매 전구체; (ii) 하이드로카르빌알루미늄 공촉매; 및 (iii) 하나 이상의 실리콘-산소-탄소 그룹을 함유하는 실리콘 화합물로 이루어진 촉매 시스템과 접촉시킴을 특징으로 하여 (여기에서, (a) 알루미늄대 티타늄의 원자비는 약 20내지 약 100의 범위이고, (b) 알루미늄대 실리콘 화합물의 몰비는 약 1내지 약 5의 범위이며, (c) 프로필렌의 부분압은 약 60내지 약220psi의 범위이며, (d) 1-헥센의 부분압은 약 4내지 약 12psi의 범위이며, (e) 수소가 존재하는 경우, 수소부분압은 0.05내지 약 80psi이하의 범위이고, (f) 가스 표면 속도는 초당 약 1내지 약 2ft의 범위이며, (g) 1-헥센대 프로필렌의 몰비는 약 0.04:1 내지 약 0.08:1의 범위이다), 프로필렌 및 1-헥센을 함유하는 단량체의 혼합물을 공중합시키는 방법.
- 제1항에 따른 방법으로 생성되는 공중합체.
- DSC 융점이 약 140℃이상이고 할선 굴곡 계수가 약 100,000psi이하임을 특징으로 하는, 제14항에 따른 방법으로 생성되는 공중합체.
- DSC 융점이 약 140℃이상이고 할선 굴곡 계수가 약 75,000psi이하임을 특징으로 하는, 제14항에 따른 방법으로 생성되는 공중합체.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.