KR910000935A - 탄성 반응이 개선된 플루오로실리콘 조성물 - Google Patents
탄성 반응이 개선된 플루오로실리콘 조성물 Download PDFInfo
- Publication number
- KR910000935A KR910000935A KR1019900008814A KR900008814A KR910000935A KR 910000935 A KR910000935 A KR 910000935A KR 1019900008814 A KR1019900008814 A KR 1019900008814A KR 900008814 A KR900008814 A KR 900008814A KR 910000935 A KR910000935 A KR 910000935A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- group
- rubber composition
- fluorosilicone
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (14)
- (A) (1)플루오실리콘 환식 삼량체 100 중량부, (2) (a)하기 식(Ⅰ)의 비닐 말단 폴리실록산 20-96중량% 및 (b)하기 식(Ⅱ)의 실록산 4-80중량%로 이루어지는 쇄 개질제 혼합물 약0.5-2.0 중량부 (3) 1,3,5 - 트리메틸-1,3,5,-트리비닐 실록산 환식 삼량체 약 0.045-0.065중량부 및 (4)NaOH 10ppm을 제공하기에 충분한 양의 플루오로실라놀산 나트륨의 반응 생성물 100중량부와 (B) 약 3.2중량%의 비닐기를 갖는 폴리디메틸실록산검 약 1-10 중량부로 이루어지는 것을 특징으로 하는 플루오로실리콘 고무 조성물.상기 각 식에서, Vi는 비닐기이고, R은 C1-4알킬기 및 페닐기로 이루어지는 군에서 선택된 기이며, R은 R 또는 -(CH2)2-R2기이고, 이때 R2는 탄소 원자수가 1-4개인 퍼플루오로알킬기이며, X는 30-45, Y는 15-30 및 Z는 3-6이다.
- 제1항에 있어서, 플루오로실리콘 환식 삼량체가 메틸-3,3,3-트리플루오로프로필실록산 환식 삼량체인 것을 특징으로 하는 플루오로실리콘 고무 조성물.
- 제1항에 있어서, 기소제가 성분 A(1) 100중량부 당 약 3-10 중량부의 양으로 추가 첨가되는 것을 특징으로 하는 플루오로실리콘 고무 조성물.
- 제3항에 있어서, 기소제가 알콜시 말단 폴리디메틸실록산인 것을 특징으로 하는 플루오로실리콘 고무 조성물.
- 제4항에 있어서, a, 발연 실리카 약 10-200 중량부, b, 비닐 실라잔 약 0.02-1.0 중량부 및 c. 플루오로실리콘 텔로머릭 실록사놀 유체 약 14-25 중량부로 이루어지는 혼합물이 추가로 첨가되는 것을 특징으로 하는 플루오로실리콘 고무 조성물.
- 제5항에 있어서, 회토류 옥토산염이 약 0.25-2.0 중량부의 양으로 추가 첨가되는 것을 특징으로 하는 플루오로실리콘 고무 조성물.
- 제5항에 있어서, a.옥토산철 약 0.01-0.1 중량부 및 b. TiO₂약 0.3-2.0 중량부로 이루어지는 혼합물이 추가로 첨가되는 것을 특징으로 하는 플루오로실리콘 고무 조성물.
- (A) (1) 플루오실리콘 환식 삼량체 100 중량부, (2) 상기 (A) (1)의 성분 100 중량부 당 (a)하기 식(Ⅰ)의 비닐 말단 폴리실록산 20-96 중량% 및 (b)하기 식(Ⅱ)의 실록산 4-80중량%로 이루어지는 쇄 개질제용 혼합물 약 0.5-2.0 중량부. (3)1,3,5,-트리메틸-1,3,5,-트리비닐실록산 환식 삼량체 약 0.045-0.065중량부 및 (4)NaOH 10ppm을 제공하기에 충분한 양의 플루오로실라놀산 나트륨으로 이루어지는 기재 고분자 조성물 반응기에 첨가시키고, (B) 상기 (A)의 기재 고분자 조성물을 약 118-135℃로 가열하여 반응을 개시시키며, (C) 상기 (A) 공저의 기재 고분자중에, 3.2중량%의 비닐기를 갖는 폴리디메틸실록산 검 약 1-10 중량부를 혼합시키는 것을 특징으로 하는 플루오로실리콘 고무 조성물의 제조방법.상기 각 식에서, Vi 는 비닐기에고, R은 C1-4알킬기 및 페닐기로 이루어지는 군에서 선택된 기이며, R'은 R 또는 -(CH2)2-R2기이고, 이때 R2탄소 원자수가 1-4개인 퍼플루오로알킬기이며, X는 30-45, Y는 15-30 및 Z는 3-6이다.
- 제8항에 있어서, 플루오로실리콘 환식 삼량체가 메틸-3,3,3-트리플루오로프로필 환식 삼량체인 것을 특징으로 하는 제조 방법.
- 제8항에 있어서, 플루오로실리콘 고무 조성물중에, 가소제가 상기 성분(A) (1) 100 중량부 당 약 3-10 중량부의 양으로 추가 혼합되는 것을 특징으로 하는 제조 방법.
- 제10항에 있어서, 가소제가 알콕시 말단 폴리디메틸실록산인 것을 특징으로 하는 제조 방법.
- 제11항에 있어서, 플루오로실리콘 고무 조성물중에, a. 발연 실리카 약 10-200 중량부, b. 비닐 실라잔 약 0.02-1.0 중량부 및 c. 플루오로실리콘 텔로머릭 실록사놀 유체 약 14-25 중량부로 이루어지는 혼합물이 추가로 혼합되는 것을 특징으로 하는 제조 방법.
- 제12항에 있어서, 플루오로실리콘 고무 조성물중에 회토류 옥토산염이 약 0.25-2.0 중량부의 양으로 추가 혼합되는 것을 특징으로 하는 제조 방법.
- 제12항에 있어서, 플루오로실리콘 고무 조성물중에, a. 옥토산철 약 0.01-0.1 중량부 및 b. TiO₂약 0.3-2.0 중량부로 이루어지는 혼합물이 추가로 혼합되는 것을 특징으로 하는 제조 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.