KR880010007A - 복분해 중합된 공중합체 - Google Patents

복분해 중합된 공중합체 Download PDF

Info

Publication number
KR880010007A
KR880010007A KR1019880001518A KR880001518A KR880010007A KR 880010007 A KR880010007 A KR 880010007A KR 1019880001518 A KR1019880001518 A KR 1019880001518A KR 880001518 A KR880001518 A KR 880001518A KR 880010007 A KR880010007 A KR 880010007A
Authority
KR
South Korea
Prior art keywords
mol
content
dicyclopentadiene
monomers
cyclic compound
Prior art date
Application number
KR1019880001518A
Other languages
English (en)
Other versions
KR920002617B1 (ko
Inventor
시게요시 하라
젠 이찌로 엔도
히로시 데라
Original Assignee
나까오 마스로오
데이진 가부시끼가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 나까오 마스로오, 데이진 가부시끼가이샤 filed Critical 나까오 마스로오
Publication of KR880010007A publication Critical patent/KR880010007A/ko
Application granted granted Critical
Publication of KR920002617B1 publication Critical patent/KR920002617B1/ko

Abstract

내용 없음.

Description

복분해 중합된 공중합체
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (54)

  1. (a) 하기식(I-a)와 (I-b)의 단량체를 함유하는 혼합물로부터 유도된 반복단위 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물로부터 유도된 반복단위 97 내지 0몰%로 이루어짐을 특징으로 하는 복분해 중합된 가교결합 공중합체.
  2. 제1항에 있어서, 단량체 (I-a) 및 (I-b)로부터 유도된 반복단위의 함량이 3 내지 80몰%인 공중합체.
  3. 제2항에 있어서, 단량체 (I-a) 및 (I-b)로부터 유도된 반복단위의 함량이 5 내지 50몰%인 공중합체.
  4. 제1항에 있어서, 시클릭 화합물(b)가 그의 총몰량을 기준으로 30몰%이상의 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 공중합체.
  5. 제4항에 있어서, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 50몰%이상인 공중합체.
  6. 제1항에 있어서, 디시클로펜타디엔으로부터 유도된 반복 단위의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 98 내지 50몰%인 공중합체.
  7. (a)하기식 (I-a)와 (I-b)의 단량체를 함유하는 혼합물 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물 97 내지 0몰%를 함유하는 단량체 혼합물을 복분해 중합반응 촉매 시스템의 존재하에서 복분해 중합시키는 것으로 이루어짐을 특징으로 하는 가교결합 공중합체의 제조방법.
  8. 제7항에 있어서, 단량체 (I-a) 및 (I-b)의 함량이 3 내지 80몰%인 방법.
  9. 제8항에 있어서, 단량체 (I-a) 및 (I-b)의 함량이 5 내지 50몰%인 방법.
  10. 제7항에 있어서, 시클릭화합물(b)가 그의 총몰량을 기준으로 30몰%이상의, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 방법.
  11. 제10항에 있어서, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 50몰%이상인 방법.
  12. 제7항에 있어서, 디시클로펜타디엔의 함량이 시클릭화합물(b)의 총몰량을 기준으로 98 내지 50몰%인 방법.
  13. 제7항에 있어서, (I-a)와 (I-b)를 함유하는 혼합물이 디엘스-알더 첨가 반응이 발생할 수 있는 조건하에서 시클로펜타디엔과 시클로옥타디엔과의 약 2：1몰비의 혼합물을 열처리하여 제조된 반응 생성물로부터 유도되는 방법.
  14. 제13항에 있어서, 디시클로펜타디엔이 시클로펜타디엔의 전구체로서 사용되는 방법.
  15. (a)하기식 (I-a)와 (I-b)의 단량체를 함유하는 혼합물 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물 97 내지 0몰%로 이루어진 복분해 중합성 단량체와 복분해 중합성 촉매 시스템을 함유하는 반응성 액체 혼합물을 금형에 도입하여 그 내부에서 괴상으로 복분해 중합시켜 성형품을 제조함을 특징으로 하는 성형품의 제조방법.
  16. 제15항에 있어서, 단량체 (I-a)와 (I-b)의 함량이 3 내지 80몰%인 방법.
  17. 제15항에 있어서, 시클릭화합물(b)가 그의 총몰량을 기준으로 30몰%이상의, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 방법.
  18. 제17항에 있어서, 적어도 하나의 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 50몰%이상인 방법.
  19. 제15항의 방법에 의하여 제조된 성형품.
  20. (a)하기식(I-a)와 (I-b)의 단량체를 함유하는 혼합물 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물 97 내지 0몰%로 이루어진 복분해 중합성 단량체를 함유함을 특징으로 하는 다수부분 중합성 조성물.
  21. 제20항에 있어서, 단량체 (I-a)와 (I-b)의 함량이 3 내지 80몰%인 조성물.
  22. 제21항에 있어서, 단량체 (I-a)와 (I-b)의 함량이 5 내지 50몰%인 조성물.
  23. 제20항에 있어서, 시클릭화합물(b)가 그의 총몰량을 기준으로 30몰%이상의, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 조성물.
  24. 제23항에 있어서, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 50%이상인 조성물.
  25. 제20항에 있어서, 디시클로펜타디엔의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 98 내지 50몰%인 조성물.
  26. 제20항에 있어서, (I-a)와 (I-b)를 함유하는 혼합물이 디엘스-알더 첨가 반응이 발생할 수 있는 조건하에서 시클로펜타디엔과 시클로옥타디엔과의 약 2：1몰비의 혼합물을 열처리하여 제조한 반응 생성물로 부터 유도되는 조성물.
  27. 제26항에 있어서, 디시클로펜타디엔이 시클로펜타디엔의 전구체로서 사용되는 조성물.
  28. (a)하기식 (Ⅱ-a)와 (Ⅱ-b)의 단량체를 함유하는 혼합물로부터 유도된 반복단위 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물로부터 유도된 반복단위 97 내지 0몰%로 이루어진을 특징으로 하는 복분해 중합된 가교결합 공중합체.
  29. 제28항에 잇어서, 단량체 (Ⅱ-a) 및 (Ⅱ-b)로부터 유도된 반복단위의 함량이 3 내지 80몰%인 공중합체.
  30. 제29항에 있어서, 단량체 (Ⅱ-a) 및 (Ⅱ-b)로부터 유도된 반복단위의 함량이 5 내지 50몰%인 공중합체.
  31. 제28항에 있어서, 시클릭 화합물(b)가 그의 총몰량을 기준으로 30몰%이상의, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 공중합체.
  32. 제31항에 있어서, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 50몰%이상인 공중합체.
  33. 제28항에 있어서, 디시클로펜타디엔으로 부터 유도된 반복단위의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 98 내지 50몰%인 공중합체.
  34. (a)하기식 (Ⅱ-a)와 (Ⅱ-b)의 단량체를 함유하는 혼합물 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물 97 내지 0몰%를 함유하는 단량체 혼합물을 복분해 중합반응 촉매시스템의 존재하에 복분해 중합시키는 것으로 이루어짐을 특징으로 하는 가교결합 공중합체의 제조방법.
  35. 제34항에 있어서, 단량체 (Ⅱ-a)와 (Ⅱ-b)의 함량이 3 내지 80몰%인 방법.
  36. 제35항에 있어서, 단량체 (II-a)와 (II-b)의 함량이 5 내지 50몰%인 방법.
  37. 제34항에 있어서, 시클릭 화합물(b)가 그의 총몰량을 기준으로 30몰%이상의, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 방법.
  38. 제37항에 있어서, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 50몰%이상인 방법.
  39. 제34항에 있어서, 디시클로펜타디엔의 함량이 시클릭화합물(b)의 총몰량을 기준으로 98 내지 50몰%인 방법.
  40. 제34항에 있어서, (Ⅱ-a)와 (Ⅱ-b)를 함유하는 혼합물이 디엘스-알더 첨가반응이 발생할 수 있는 조건하에서 시클로펜타디엔과 1,5-헥사디엔과의 약 2：1몰비의 혼합물을 열처리하여 제조된 반응 생성물로부터 유도되는 방법.
  41. 제40항에 있어서, 디시클로펜타디엔이 시클로펜타디엔의 전구체로서 사용되는 방법.
  42. (a)하기식 (Ⅱ-a)와 (Ⅱ-b)의 단량체를 함유하는 혼합물 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물 97 내지 0몰%로 이루어진 복분해 중합성 단량체와 복분해 중합성 촉매 시스템의 함유하는 반응성 액체 혼합물을 금형에 도입하고, 그 내부에서 괴상으로 복분해 중합시켜 성형품을 제조함을 특징으로 하는 성형품의 제조방법.
  43. 제42항에 있어서, 단량체 (Ⅱ-a)와 (Ⅱ-b)의 함량이 3 내지 80몰%인 방법.
  44. 제42항에 있어서, 시클릭 화합물(b)가 그의 총몰량을 기준으로 30몰%이상의, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 방법.
  45. 제44항에 있어서, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로 옥텐중 적어도 하나의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 50몰%이상인 방법.
  46. 제42항의 방법에 의하여 제조된 성형품.
  47. (a)하기식 (Ⅱ-a)와 (Ⅱ-b)의 단량체를 함유하는 혼합물 3 내지 100몰%, 및 (b)1종 이상의 복분해 중합성 시클릭 화합물 97 내지 0몰%로 이루어진 복분해 중합성 단량체를 함유함을 특징으로 하는 다수부분 중합성 조성물.
  48. 제47항에 있어서, 단량체 (Ⅱ-a)와 (Ⅱ-b)의 함량이 3 내지 80몰%인 조성물.
  49. 제48항에 있어서, 단량체 (Ⅱ-a)와 (Ⅱ-b)의 함량이 5 내지 50몰%인 조성물.
  50. 제47항에 있어서, 시클릭 화합물(b)가 그의 총몰량을 기준으로 30몰%이상의, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나를 함유하는 조성물.
  51. 제50항에 있어서, 디시클로펜타디엔, 시클로펜타디엔 올리고머 및 1,4-메타노-1,4-디히드로-5H-벤조시클로옥텐중 적어도 하나의 함량이 시클릭화합물(b)의 총몰량을 기준으로 50%이상인 조성물.
  52. 제47항에 있어서, 디시클로펜타디엔의 함량이 시클릭 화합물(b)의 총몰량을 기준으로 98 내지 50몰%인 조성물.
  53. 제47항에 있어서, (Ⅱ-a)와 (Ⅱ-b)를 함유하는 혼합물이 디엘스-알더 첨가 반응이 발생할 수 있는 조건하에서 시클로펜타디엔과 1,5-헥사디엔의 약 2：1몰비의 혼합물을 열처리하여 제조된 반응 생성물로 부터 유도되는 조성물.
  54. 제53항에 있어서, 디시클로펜타디엔이 시클로펜타디엔의 전구체로서 사용되는 조성물.
    ※참고사항:최초출원 내용에 의하여 공개하는 것임.
KR1019880001518A 1987-02-16 1988-02-15 복분해 중합된 공중합체 KR920002617B1 (ko)