KR20240059375A - A method for treating a substrate - Google Patents
A method for treating a substrate Download PDFInfo
- Publication number
- KR20240059375A KR20240059375A KR1020220140564A KR20220140564A KR20240059375A KR 20240059375 A KR20240059375 A KR 20240059375A KR 1020220140564 A KR1020220140564 A KR 1020220140564A KR 20220140564 A KR20220140564 A KR 20220140564A KR 20240059375 A KR20240059375 A KR 20240059375A
- Authority
- KR
- South Korea
- Prior art keywords
- substrate
- process gas
- film
- processing method
- substrate processing
- Prior art date
Abstract
본 발명은 기판을 처리하는 방법을 제공한다. 일 실시예에 의한 기판 처리 방법은 챔버 내에 공정 가스를 공급하여 기판을 처리하되, 상기 공정 가스 중 일부는 플라즈마 상태로 여기되고, 상기 플라즈마는 기판 상에 형성된 하드 마스크 막을 기판으로부터 제거하고, 상기 공정 가스 중 다른 일부는 기판 상에 형성된 박막과 반응하여 상기 박막의 표면에 패시베이션 막(Passivation film)을 형성하되, 상기 공정 가스는 CHF 계열의 가스일 수 있다.The present invention provides a method for processing a substrate. A substrate processing method according to an embodiment processes a substrate by supplying a process gas into a chamber, wherein some of the process gas is excited into a plasma state, the plasma removes the hard mask film formed on the substrate from the substrate, and the process gas is excited to a plasma state. Another part of the gas reacts with the thin film formed on the substrate to form a passivation film on the surface of the thin film, and the process gas may be a CHF-based gas.
Description
본 발명은 기판 처리 방법에 관한 것으로, 더욱 상세하게는 기판 상에 형성된 하드 마스크 막을 제거하는 기판 처리 방법에 관한 것이다.The present invention relates to a substrate processing method, and more particularly, to a substrate processing method for removing a hard mask film formed on a substrate.
일반적으로, 반도체 소자는 포토리소그래피 공정, 에칭 공정, 증착 공정 및/또는 이온주입 공정의 단위 공정에 의해 제조될 수 있다. 포토리소그래피 공정은 기판 상에 포토레지스트 막을 형성하는 공정이다. 포토레지스트 막은 기판을 선택적으로 노출시키는 마스크 패턴으로 기능할 수 있다. 또한, 포토레지스트 막의 하측에는 하드 마스크 막이 형성될 수 있다. 하드 마스크 막은 기판에 형성된 회로 패턴의 붕괴를 막는 등의 기능을 수행할 수 있다. 포토레지스트 막과 하드 마스크 막은 이온주입 공정 또는 에칭 공정을 수행한 이후에 스트립(Strip)과 같은 방법으로 기판으로부터 순차적으로 제거될 수 있다.In general, semiconductor devices can be manufactured by unit processes of a photolithography process, an etching process, a deposition process, and/or an ion implantation process. The photolithography process is a process of forming a photoresist film on a substrate. The photoresist film can function as a mask pattern that selectively exposes the substrate. Additionally, a hard mask film may be formed below the photoresist film. The hard mask film can perform functions such as preventing the collapse of the circuit pattern formed on the substrate. The photoresist film and the hard mask film can be sequentially removed from the substrate using a strip method after performing an ion implantation process or an etching process.
에칭 타겟의 증가와 고 선택비를 가지는 미세한 패턴을 요하는 최근의 트랜드에 따라, 하드 마스크 막의 에칭에 대한 내성을 증가시키고 있다. 예컨대, 하드 마스크 막에 메탈(예컨대, 카본, 브론, 및/또는 텅스텐)을 첨가(doping)하여 하드 마스크 막의 프로파일의 라인 거칠기(Line roughness)를 개선하고, 동시에 에칭에 대한 내성을 향상시킬 수 있다. 다만, 이와 같이 하드 마스크 막에 메탈을 첨가하는 경우, 에칭 공정 등이 완료된 이후에 기판 상에서 하드 마스크 막을 용이하게 제거하기 어렵다. 또한, 메탈이 첨가된 하드 마스크 막을 제거하기 위해 더 높은 온도를 형성하고, 더 강한 밀도의 플라즈마를 발생시키는 경우, 하드 마스크 막 뿐만 아니라 기판 상에 형성된 절연막도 손상된다. 절연막이 손상되는 경우, 선택비(selectivity)가 저하되어 기판의 수율이 저하되는 결과로 이어진다.In accordance with recent trends requiring an increase in etching targets and fine patterns with high selectivity, the resistance of hard mask films to etching is increasing. For example, doping a metal (e.g., carbon, bronze, and/or tungsten) to the hard mask film can improve the line roughness of the profile of the hard mask film and at the same time improve resistance to etching. . However, when metal is added to the hard mask film like this, it is difficult to easily remove the hard mask film from the substrate after the etching process, etc. is completed. Additionally, when a higher temperature is generated and a stronger density plasma is generated to remove the metal-added hard mask film, not only the hard mask film but also the insulating film formed on the substrate is damaged. If the insulating film is damaged, selectivity decreases, resulting in a decrease in substrate yield.
본 발명은 기판을 효율적으로 처리할 수 있는 기판 처리 방법을 제공하는 것을 일 목적으로 한다.One object of the present invention is to provide a substrate processing method that can efficiently process a substrate.
또한, 본 발명은 기판 상에 형성된 하드 마스크 막을 효율적으로 제거할 수 있는 기판 처리 방법을 제공하는 것을 일 목적으로 한다.Another object of the present invention is to provide a substrate processing method that can efficiently remove a hard mask film formed on a substrate.
또한, 본 발명은 기판 상에 형성된 절연막을 손상시키는 것을 최소화하면서, 특정 물질이 첨가된 하드 마스크 막을 효율적으로 제거할 수 있는 기판 처리 방법을 제공하는 것을 일 목적으로 한다.Another object of the present invention is to provide a substrate processing method that can efficiently remove a hard mask film to which a specific material has been added while minimizing damage to the insulating film formed on the substrate.
본 발명이 해결하고자 하는 과제가 상술한 과제들로 한정되는 것은 아니며, 언급되지 아니한 과제들은 본 명세서 및 첨부된 도면으로부터 본 발명의 속하는 기술 분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다.The problems to be solved by the present invention are not limited to the above-mentioned problems, and problems not mentioned can be clearly understood by those skilled in the art from this specification and the attached drawings. will be.
본 발명은 기판을 처리하는 방법을 제공한다. 일 실시예에 의한 기판 처리 방법은 챔버 내에 공정 가스를 공급하여 기판을 처리하되, 상기 공정 가스 중 일부는 플라즈마 상태로 여기되고, 상기 플라즈마는 기판 상에 형성된 하드 마스크 막을 기판으로부터 제거하고, 상기 공정 가스 중 다른 일부는 기판 상에 형성된 박막과 반응하여 상기 박막의 표면에 패시베이션 막(Passivation film)을 형성하되, 상기 공정 가스는 CHF 계열의 가스일 수 있다.The present invention provides a method for processing a substrate. A substrate processing method according to an embodiment processes a substrate by supplying a process gas into a chamber, wherein some of the process gas is excited into a plasma state, the plasma removes the hard mask film formed on the substrate from the substrate, and the process gas is excited to a plasma state. Another part of the gas reacts with the thin film formed on the substrate to form a passivation film on the surface of the thin film, and the process gas may be a CHF-based gas.
일 실시예에 의하면, 상기 방법은, 상기 챔버 내로 상기 공정 가스를 공급하는 동안, 제1스텝과 제2스텝을 일 사이클로 복수 회 반복하고, 상기 제1스텝은, 상기 플라즈마를 발생시키는 전극에 제1전압을 인가하고, 상기 제2스텝은, 상기 전극에 상기 제1전압보다 낮은 제2전압을 인가할 수 있다.According to one embodiment, the method repeats the first step and the second step multiple times in one cycle while supplying the process gas into the chamber, and the first step is performed by applying a pressure to the electrode that generates the plasma. One voltage may be applied, and the second step may apply a second voltage lower than the first voltage to the electrode.
일 실시예에 의하면, 상기 제1스텝은, 상기 일 사이클 내에서, 상기 제2스텝보다 선행할 수 있다.According to one embodiment, the first step may precede the second step within one cycle.
일 실시예에 의하면, 상기 제2스텝은, 상기 일 사이클 내에서, 상기 제1스텝보다 선행할 수 있다.According to one embodiment, the second step may precede the first step within the one cycle.
일 실시예에 의하면, 상기 하드 마스크 막은 메탈이 포함될 수 있다.According to one embodiment, the hard mask layer may include metal.
일 실시예에 의하면, 상기 메탈은, 텅스텐, 카본, 그리고 브론 중 적어도 어느 하나를 포함할 수 있다.According to one embodiment, the metal may include at least one of tungsten, carbon, and bronze.
일 실시예에 의하면, 상기 박막은, 실리콘 산화막과 실리콘 질화막 중 적어도 어느 하나를 포함할 수 있다.According to one embodiment, the thin film may include at least one of a silicon oxide film and a silicon nitride film.
일 실시예에 의하면, 상기 박막은, 상기 실리콘 산화막과 상기 실리콘 질화막이 교대로 적층될 수 있다.According to one embodiment, the thin film may be formed by alternately stacking the silicon oxide film and the silicon nitride film.
일 실시예에 의하면, 상기 챔버 내에 상기 공정 가스를 공급하는 동안, 상기 챔버 내로 공급되는 상기 공정 가스의 단위 시간당 공급 유량이 변경될 수 있다.According to one embodiment, while supplying the process gas into the chamber, the supply flow rate per unit time of the process gas supplied into the chamber may be changed.
또한, 본 발명은 질화막과 산화막이 교대로 적층된 박막과, 상기 박막의 상측에 적층되고 메탈 성분을 함유하는 하드 마스크 막을 포함하는 기판을 처리하는 방법을 제공한다. 일 실시예에 의한 기판 처리 방법은, CHF 계열의 공정 가스를 챔버 내로 공급하여 상기 하드 마스크 막을 제거하되, 상기 챔버 내로 상기 공정 가스를 공급하는 동안 상기 공정 가스를 여기시키는 고주파 전압의 세기를 변경시키는 스텝을 복수 회 반복할 수 있다.Additionally, the present invention provides a method for processing a substrate including a thin film in which nitride films and oxide films are alternately stacked, and a hard mask film containing a metal component and stacked on top of the thin film. A substrate processing method according to an embodiment includes supplying a CHF-based process gas into a chamber to remove the hard mask film, and changing the intensity of a high-frequency voltage that excites the process gas while supplying the process gas into the chamber. Steps can be repeated multiple times.
일 실시예에 의하면, 상기 공정 가스 중 일부는 상기 고주파 전압에 의해 플라즈마 상태로 여기되고, 상기 플라즈마는 상기 하드 마스크 막을 기판으로부터 제거하고, 상기 공정 가스 중 다른 일부는 상기 박막과 반응하여 상기 박막의 표면에 패시베이션 막을 형성할 수 있다.According to one embodiment, some of the process gas is excited into a plasma state by the high frequency voltage, the plasma removes the hard mask film from the substrate, and another part of the process gas reacts with the thin film to form the thin film. A passivation film can be formed on the surface.
일 실시예에 의하면, 상기 스텝은 제1스텝과 제2스텝을 포함하고, 상기 제1스텝은, 상기 플라즈마를 발생시키는 전극에 제1전압을 인가하고, 상기 제2스텝은, 상기 전극에 상기 제1전압보다 낮은 제2전압을 인가하되, 상기 제1스텝에서는, 상기 하드 마스크 막의 제거 속도가 상기 패시베이션 막의 형성 속도보다 우세하고, 상기 제2스텝에서는, 상기 패시베이션 막의 형성 속도가 상기 하드 마스크 막의 제거 속도보다 우세할 수 있다.According to one embodiment, the step includes a first step and a second step, the first step applies a first voltage to the electrode that generates the plasma, and the second step applies the first voltage to the electrode. A second voltage lower than the first voltage is applied, wherein in the first step, the removal rate of the hard mask film is superior to the formation rate of the passivation film, and in the second step, the formation rate of the passivation film is superior to that of the hard mask film. It may be superior to the rate of removal.
일 실시예에 의하면, 상기 제1스텝은 상기 제2스텝보다 선행할 수 있다.According to one embodiment, the first step may precede the second step.
일 실시예에 의하면, 상기 제2스텝은 상기 제1스텝보다 선행할 수 있다.According to one embodiment, the second step may precede the first step.
일 실시예에 의하면, 상기 메탈은, 텅스텐, 카본, 그리고 브론 중 적어도 어느 하나를 포함할 수 있다.According to one embodiment, the metal may include at least one of tungsten, carbon, and bronze.
일 실시예에 의하면, 상기 챔버 내에 상기 공정 가스를 공급하는 동안, 상기 챔버 내로 공급되는 상기 공정 가스의 단위 시간당 공급 유량이 변경될 수 있다.According to one embodiment, while supplying the process gas into the chamber, the supply flow rate per unit time of the process gas supplied into the chamber may be changed.
본 발명의 일 실시예에 의하면, 기판을 효율적으로 처리할 수 있다.According to an embodiment of the present invention, a substrate can be processed efficiently.
또한, 본 발명의 일 실시예에 의하면, 메탈이 첨가된 하드 마스크 막을 이용하여 고 선택비의 특성을 만족하도록 기판을 처리하되, 메탈이 첨가된 하드 마스크 막을 기판으로부터 용이하게 제거할 수 있다.In addition, according to an embodiment of the present invention, a substrate is processed to satisfy high selectivity characteristics using a metal-added hard mask film, and the metal-added hard mask film can be easily removed from the substrate.
또한, 본 발명의 일 실시예에 의하면, 기판 상에 형성된 절연막을 손상시키는 것을 최소화하면서, 메탈이 첨가된 하드 마스크 막을 효율적으로 제거할 수 있다.Additionally, according to an embodiment of the present invention, it is possible to efficiently remove the metal-added hard mask film while minimizing damage to the insulating film formed on the substrate.
본 발명의 효과가 상술한 효과들로 한정되는 것은 아니며, 언급되지 아니한 효과들은 본 명세서 및 첨부된 도면으로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확히 이해될 수 있을 것이다.The effects of the present invention are not limited to the effects described above, and effects not mentioned can be clearly understood by those skilled in the art from this specification and the attached drawings.
도 1은 일 실시예에 따른 기판 처리 장치를 개략적으로 보여주는 단면도이다.
도 2는 일 실시예에 따른 기판 처리 장치에서 처리되는 기판을 개략적으로 보여주는 일부 확대도이다.
도 3은 일 실시예에 따른 기판 처리 방법의 플로우 차트이다.
도 4는 일 실시예에 따른 제1스텝이 수행되는 기판의 모습을 개략적으로 보여주는 일부 확대도이다.
도 5는 일 실시예에 따른 제2스텝이 수행되는 기판의 모습을 개략적으로 보여주는 일부 확대도이다.
도 6은 공정 가스 유량과 선택비의 상관관계를 개략적으로 보여주는 그래프이다.
도 7은 다른 실시예에 따른 기판 처리 방법의 플로우 차트이다.1 is a cross-sectional view schematically showing a substrate processing apparatus according to an embodiment.
Figure 2 is a partially enlarged view schematically showing a substrate being processed in a substrate processing apparatus according to an embodiment.
3 is a flow chart of a substrate processing method according to one embodiment.
Figure 4 is a partial enlarged view schematically showing the appearance of the substrate on which the first step is performed according to one embodiment.
Figure 5 is a partial enlarged view schematically showing the appearance of the substrate on which the second step is performed according to one embodiment.
Figure 6 is a graph schematically showing the correlation between process gas flow rate and selectivity.
7 is a flow chart of a substrate processing method according to another embodiment.
이하, 본 발명의 실시 예를 첨부된 도면들을 참조하여 더욱 상세하게 설명한다. 본 발명의 실시 예는 여러 가지 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 서술하는 실시예로 인해 한정되어지는 것으로 해석되어서는 안된다. 본 실시예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다. 따라서 도면에서의 구성 요소의 형상 등은 보다 명확한 설명을 강조하기 위해서 과장된 것이다.Hereinafter, embodiments of the present invention will be described in more detail with reference to the attached drawings. Embodiments of the present invention may be modified in various forms, and the scope of the present invention should not be construed as being limited by the embodiments described below. This example is provided to more completely explain the present invention to those with average knowledge in the art. Therefore, the shapes of components in the drawings are exaggerated to emphasize a clearer explanation.
제1, 제2 등의 용어는 다양한 구성 요소들을 설명하는데 사용될 수 있지만, 상기 구성 요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성 요소를 다른 구성 요소로부터 구별하는 목적으로 사용될 수 있다. 예를 들어, 본 발명의 권리 범위로부터 이탈되지 않은 채 제1 구성 요소는 제2 구성 요소로 명명될 수 있고, 유사하게 제2 구성 요소도 제1 구성 요소로 명명될 수 있다.Terms such as first, second, etc. may be used to describe various components, but the components should not be limited by the terms. The above terms may be used for the purpose of distinguishing one component from another component. For example, a first component may be referred to as a second component, and similarly, the second component may also be referred to as a first component without departing from the scope of the present invention.
도 1은 일 실시예에 따른 기판 처리 장치를 개략적으로 보여주는 단면도이다.1 is a cross-sectional view schematically showing a substrate processing apparatus according to an embodiment.
기판 처리 장치(10)에서는 후술하는 일 실시예에 의한 기판 처리 방법이 수행될 수 있다. 일 실시예에 의한 기판 처리 장치(10)에서는, 플라즈마를 이용하여 기판(W)을 처리할 수 있다. 예컨대, 기판 처리 장치(10)에서는, 플라즈마를 이용하여 기판(W) 상에 형성된 하드 마스크 막을 제거하는 하드 마스크 스트립(Strip) 공정이 수행될 수 있다. 기판 처리 장치(10)에서 처리되는 기판(W)에 대한 상세한 설명은 후술한다.The
기판 처리 장치(10)는 하우징(100), 지지 유닛(200), 배플 유닛(300), 가스 공급 유닛(400), 전원 유닛(500), 그리고 제어기(600)를 포함할 수 있다.The
하우징(100)은 내부에 처리 공간(101)을 가진다. 처리 공간(101)은 기판(W)이 처리되는 공간으로 기능한다. 하우징(100)의 일 측벽에는 기판(W)이 반입 또는 반출되는 개구(미도시)가 형성된다. 또한, 하우징(100)의 바닥에는 처리 공간(101)의 내부 분위기를 배기하는 배기 홀(미도시)이 형성될 수 있다. 하우징(100)의 천정에는 후술하는 배플 유닛(300)이 삽입될 수 있다. 또한, 하우징(100)은 접지될 수 있다.The
지지 유닛(200)은 기판(W)을 지지한다. 지지 유닛(200)은 처리 공간(101)에 배치된다. 일 실시예에 의하면, 지지 유닛(200)은 정전기력을 이용하여 기판(W)을 지지하는 ESC일 수 있다. 지지 유닛(200)의 내부에는, 지지된 기판(W)의 온도를 조절하는 온도 조절부(미도시)가 배치될 수 있다. 예컨대, 온도 조절부(미도시)는 히터 및/또는 냉각 유체가 유동하는 냉각 유로일 수 있다. 또한, 지지 유닛(200)은 기판(W)을 상하 방향으로 이동할 수 있다. 지지 유닛(200)은 기판(W)을 상하 방향으로 이동시켜, 후술하는 배플 유닛(300)과 기판(W) 사이의 간격을 조절할 수 있다. 또한, 지지 유닛(200)은 접지될 수 있다.The
배플 유닛(300)은 처리 공간(101)으로 공정 가스를 공급한다. 배플 유닛(300)은 대체로 원통 형상을 가질 수 있다. 배플 유닛(300)은 하우징(100)의 천정에 삽입될 수 있다. 배플 유닛(300)은 내부 공간(301)을 가진다. 배플 유닛(300)의 하면에는 공정 가스가 통과하는 복수의 배플 홀(310)이 형성된다. 배플 유닛(300)의 상부(upper portion)에는, 후술하는 가스 라인(440)이 연결되는 포트가 형성될 수 있다. 공정 가스는 가스 라인(440)과 포트를 순차적으로 통과하여 내부 공간(301)으로 유입된다. 내부 공간(301)으로 유입된 공정 가스는 배플 홀(310)을 통해 처리 공간(101)으로 공급된다.The
가스 공급 유닛(400)은 처리 공간(101)으로 공정 가스를 공급한다. 일 실시예에 의한 가스 공급 유닛(400)이 공급하는 공정 가스는, CHF 계열의 가스를 포함할 수 있다. 예컨대, 공정 가스는, CHF, CHF2, CH2F2, 또는 CHF3 가스를 포함할 수 있다.The
가스 공급 유닛(400)은 가스 소스(420), 가스 라인(440), 그리고 유량 조절기(460)를 포함할 수 있다.The
가스 소스(420)는 공정 가스를 저장한다. 가스 라인(440)의 일단은 가스 소스(420)와 연결된다. 또한, 가스 라인(440)의 타단은 전술한 배플 유닛(300)의 상부에 형성된 포트와 연결된다. 가스 라인(440)에는 유량 조절기(460)가 설치될 수 있다. 유량 조절기(460)는 가스 라인(440)을 거쳐 내부 공간(301)으로 유입되는 공정 가스의 유량을 조절할 수 있다. 일 실시예에 의하면, 유량 조절기(460)는 레귤레이터 또는 유량 조절 밸브 중 어느 하나일 수 있다. 다만, 이에 한정되는 것은 아니고, 유량 조절기(460)는 가스 라인(440)을 유동하는 공정 가스의 유량을 변경시킬 수 있는 공지된 다양한 장치로 변경될 수 있다.
전원 유닛(500)은 전원(520)과 정합기(540)를 포함할 수 있다. 일 실시예에 의하면, 전원(520)은 고주파 전원일 수 있다. 전원(520)은 배플 유닛(300)과 전기적으로 연결될 수 있다. 전원(520)은 고주파 전압을 배플 유닛(300)에 인가할 수 있다. 이에, 배플 유닛(300)은 상부 전극으로 기능할 수 있다. 또한, 전술한 바와 같이, 지지 유닛(200)은 접지되어 하부 전극으로 기능할 수 있다. 고주파 전압이 인가되는 배플 유닛(300)과 접지된 지지 유닛(200)은 처리 공간(101)에 전계(Electric Field)를 형성할 수 있다. 처리 공간(101)에 공급된 공정 가스는, 처리 공간(101)에 형성된 전계에 의해 플라즈마 상태로 여기된다. 정합기(540)는 배플 유닛(300)에 인가되는 고주파 전압의 임피던스를 매칭시킨다.The
제어기(600)는 기판 처리 장치(10)에 포함되는 구성들을 제어한다. 제어기(600)는 기판 처리 장치(10)의 제어를 실행하는 마이크로프로세서(컴퓨터)로 이루어지는 프로세스 컨트롤러와, 오퍼레이터가 기판 처리 장치(10)를 관리하기 위해서 커맨드 입력 조작 등을 행하는 키보드나, 기판 처리 장치(10)의 가동 상황을 가시화해서 표시하는 디스플레이 등으로 이루어지는 유저 인터페이스와, 기판 처리 장치(10)에서 실행되는 처리를 프로세스 컨트롤러의 제어로 실행하기 위한 제어 프로그램이나, 각종 데이터 및 처리 조건에 따라 각 구성부에 처리를 실행시키기 위한 프로그램, 즉 처리 레시피가 저장된 기억부를 구비할 수 있다. 또한, 유저 인터페이스 및 기억부는 프로세스 컨트롤러에 접속되어 있을 수 있다. 처리 레시피는 기억 부 중 기억 매체에 기억되어 있을 수 있고, 기억 매체는, 하드 디스크이어도 되고, CD-ROM, DVD 등의 가반성 디스크나, 플래시 메모리 등의 반도체 메모리 일 수도 있다.The controller 600 controls components included in the
도 2는 일 실시예에 따른 기판 처리 장치에서 처리되는 기판을 개략적으로 보여주는 일부 확대도이다.Figure 2 is a partially enlarged view schematically showing a substrate being processed in a substrate processing apparatus according to an embodiment.
일 실시예에 의한 기판(W)은 전 공정의 수행이 완료된 기판(W)일 수 있다. 또한, 일 실시예에 의한 기판(W)은 포토레지스트 막이 제거된 상태일 수 있다. 기판(W) 상에는 하드 마스크 막(700)과 박막(800)이 형성될 수 있다. 일 실시예에 의한 박막(800)은, 산화막, 질화막, 실리콘 산화막, 실리콘 질화막, 그리고 폴리 실리콘 막 중 적어도 하나를 포함할 수 있다. 선택적으로, 박막(800)은 자연 산화막이나 화학적으로 생성된 산화막일 수 있다.The substrate W according to one embodiment may be a substrate W on which all processes have been completed. Additionally, the substrate W according to one embodiment may have the photoresist film removed. A
도 2에 도시된 바와 같이, 기판(W) 상에는 실리콘 산화막(820)과 실리콘 질화막(840)이 적층될 수 있다. 보다 구체적으로, 기판(W) 상에는 실리콘 산화막(820)과 실리콘 질화막(840)이 교번적으로 적층될 수 있다. 다만, 이에 한정되는 것은 아니고, 기판(W) 상에는 자연 산화막이나 화학적으로 생성된 산화막, 폴리 실리콘 막 등이 더 형성될 수 있다. 또한, 박막(800)들 내에는, 유전율을 감소시키기 위한 복수 개의 Pore 들이 형성될 수 있다.As shown in FIG. 2, a
하드 마스크 막(700)은 박막(800)들의 상측에 위치한다. 일 실시예에 의한 하드 마스크 막(700)은 메탈을 포함할 수 있다. 보다 구체적으로, 일 실시예에 의한 하드 마스크 막(700)은, 메탈이 첨가(Doped)된 하드 마스크 막일 수 있다. 즉, 일 실시예에 의한 하드 마스크 막(700)은 MDC(Metal doped carbon) 일 수 있다. 일 실시예에 의한, 메탈은, 텅스텐(Wolfram), 카본(Carbon), 그리고 브론(Boron) 중 적어도 하나를 포함할 수 있다.The
이하에서는, 일 실시예에 의한 기판 처리 방법에 대해 설명한다. 이하에서 설명하는 기판 처리 방법은, 도 1에서 설명한 기판 처리 장치(10)에서 수행될 수 있다. 이에, 이하에서는 도 1에 도시된 참조 부호를 그대로 인용하여 일 실시예에 의한 기판 처리 방법을 설명한다. 또한, 이하에서 설명하는 기판 처리 방법은, 상술한 제어기(600)가 기판 처리 장치(10)에 포함되는 구성들을 제어하여 수행될 수 있다.Below, a substrate processing method according to an embodiment will be described. The substrate processing method described below may be performed in the
도 3은 일 실시예에 따른 기판 처리 방법의 플로우 차트이다. 도 4는 일 실시예에 따른 제1스텝이 수행되는 기판의 모습을 개략적으로 보여주는 일부 확대도이다. 도 5는 일 실시예에 따른 제2스텝이 수행되는 기판의 모습을 개략적으로 보여주는 일부 확대도이다. 도 6은 공정 가스 유량과 선택비의 상관관계를 개략적으로 보여주는 그래프이다.3 is a flow chart of a substrate processing method according to one embodiment. Figure 4 is a partial enlarged view schematically showing the appearance of the substrate on which the first step is performed according to one embodiment. Figure 5 is a partial enlarged view schematically showing the appearance of the substrate on which the second step is performed according to one embodiment. Figure 6 is a graph schematically showing the correlation between process gas flow rate and selectivity.
일 실시예에 의한 기판 처리 방법은, 플라즈마를 이용하여 기판(W) 상에 형성된 하드 마스크 막(700)을 제거하는 하드 마스크 스트립(Strip) 공정을 포함할 수 있다. 일 실시예에 의한 기판 처리 방법은, 제1스텝(S10)과 제2스텝(S20)을 포함할 수 있다.A substrate processing method according to an embodiment may include a hard mask strip process of removing the
제1스텝(S10)과 제2스텝(S20)에서는, 각각 처리 공간(101)에 CHF 계열의 공정 가스를 공급한다. 또한, 전원 유닛(500)은 배플 유닛(300)에 고주파 전압을 인가하여, 처리 공간(101)에 전계를 형성시킨다. 이에, 처리 공간(101)에 공급된 공정 가스 중 일부는, 플라즈마 상태로 여기된다. 처리 공간(101)에 발생한 플라즈마는 이온과 라디칼을 포함한다.In the first step S10 and the second step S20, a CHF-based process gas is supplied to the
일 실시예에 의한 공정 가스는 CHF 계열의 가스로 제공되므로, 처리 공간(101)에 발생한 플라즈마에는, 불소 음이온(F-)이 포함될 수 있다. 플라즈마에 포함되는 불소 음이온(F-)이 하드 마스크 막(700)과 반응한다. 상술한 바와 같이, 하드 마스크 막(700)은 메탈을 포함하므로, 불소 음이온(F-)과 메탈이 반응하여 MFx의 반응물을 생성한다. 생성된 MFx 반응물은 가스 상태로 기화되어 기판(W)으로부터 제거된다.Since the process gas according to one embodiment is provided as a CHF-based gas, the plasma generated in the
또한, 처리 공간(101)에 공급된 공정 가스 중 다른 일부는 플라즈마 상태로 여기되지 않고, 기판(W)에 작용한다. 보다 구체적으로 CHF 계열의 가스는 기판(W) 상에 형성된 실리콘 산화막(820) 및 실리콘 질화막(840)과 반응하여 (CHF3)n의 패시베이션 막(900, Passivation film)을 형성한다. 즉, CHF 계열의 가스는, 실리콘 산화막(820) 및 실리콘 질화막(840)과 반응하여, 실리콘 산화막(820) 및 실리콘 질화막(840)의 표면에 패시베이션 막(900)을 형성한다. 패시베이션 막(900)은 실리콘 산화막(820) 및 실리콘 질화막(840)을 보호할 수 있다. 보다 구체적으로, 패시베이션 막(900)은 처리 공간(101)에 형성된 플라즈마에 의해 실리콘 산화막(820) 및 실리콘 질화막(840)이 식각되는 것을 최소화할 수 있다.Additionally, another part of the process gas supplied to the
또한, 처리 공간(101)에 공정 가스를 공급하는 동안, 처리 공간(101)에 공급되는 공정 가스의 단위 시간당 공급 유량을 변경시킬 수 있다. 도 6에 도시된 바와 같이, 공정 가스의 단위 시간당 공급 유량을 증가시킬수록, 기판(W)의 선택비(Selectivity)가 증가한다.Additionally, while supplying the process gas to the
보다 구체적으로, 공정 가스의 단위 시간당 공급 유량을 증가시킬수록, 기판(W)에 작용하는 공정 가스의 양이 증가한다. 이에, 실리콘 산화막(820) 및 실리콘 질화막(840)의 표면에 형성되는 패시베이션 막(900)의 두께가 증가한다. 이로 인해, 실리콘 산화막(820) 및 실리콘 질화막(840)이 플라즈마에 의해 식각되는 것이 최소화될 수 있다.More specifically, as the supply flow rate of the process gas per unit time increases, the amount of the process gas acting on the substrate W increases. Accordingly, the thickness of the
또한, 공정 가스의 단위 시간당 공급 유량을 증가시킬수록, 기판(W)에 작용하는 플라즈마의 양이 증가한다. 이에, 기판(W) 상에 형성된 하드 마스크 막(700)이 플라즈마에 의해 보다 많은 양의 하드 마스크 막(700)이 제거될 수 있다. 즉, 공정 가스의 단위 시간당 공급 유량을 증가시킬수록, 실리콘 산화막(820) 및 실리콘 질화막(840)은 플라즈마에 의해 식각되는 양이 줄고, 하드 마스크 막(700)이 제거되는 양이 증가하므로, 기판(W)의 선택비가 증가한다. 이에, 공정에서 요구되는 기판(W)의 선택비에 따라 처리 공간(101)으로 공급하는 공정 가스의 단위 시간당 공급 유량을 적절하게 변경시킬 수 있다.Additionally, as the supply flow rate of the process gas per unit time increases, the amount of plasma acting on the substrate W increases. Accordingly, a greater amount of the
제1스텝(S10)에서, 전원 유닛(500)은 배플 유닛(300)에 제1고주파 전압을 인가할 수 있다. 제2스텝(S20)에서, 전원 유닛(500)은 배플 유닛(300)에 제2고주파 전압을 인가할 수 있다. 제1고주파 전압은 제2고주파 전압보다 상대적으로 큰 값을 가질 수 있다.In the first step S10, the
또한, 일 실시예에 의하면, 제1스텝(S10)은 제2스텝(S20)보다 선행하여 수행될 수 있다. 즉, 전원 유닛(500)은 배플 유닛(300)에 제1고주파 전압을 인가한 이후에, 제2고주파 전압을 인가할 수 있다. 또한, 제1스텝(S10)과 제2스텝(S20)은 일 사이클로 수행되고, 해당 사이클은 복수 회 수행될 수 있다. 제1스텝(S10)과 제2스텝(S20)을 이루는 사이클을 설정 횟수만큼 반복 수행할 수 있다. 설정 횟수는, 공정 레시피에 따라 결정된다. 예컨대, 처리 공간(101)에 반입되는 기판(W) 상에 형성된 하드 마스크 막(700)의 두께 정보에 따라, 설정 횟수가 결정될 수 있다. 하드 마스크 막(700)의 두께 정보에 따른 설정 횟수는, 제어기(600)에 미리 기억되어 있을 수 있다.Additionally, according to one embodiment, the first step (S10) may be performed prior to the second step (S20). That is, the
제1스텝(S10)에서 상대적으로 큰 값을 가지는 제1고주파 전압이 배플 유닛(300)에 인가되므로, 처리 공간(101)에 형성되는 전계의 세기가 세다. 이에, 처리 공간(101)에 공급된 공정 가스 중, 플라즈마로 여기되는 공정 가스의 비율이 제2스텝(S20)보다 높아진다. 이와 반대로, 처리 공간(101)에 공급된 공정 가스 중, 플라즈마로 여기되지 않고 공정 가스 상태로 존재하는 비율이 제2스텝(S20)보다 낮아진다. 도 4에 도시된 바와 같이, 제1스텝(S10)을 수행하는 동안 처리 공간(101)에는, 플라즈마에 포함되는 불소 음이온(A1)의 개수가, 공정 가스(A2)의 개수보다 상대적으로 많을 수 있다.Since the first high-frequency voltage having a relatively large value is applied to the
이와 반대로, 제2스텝(S20)에서 상대적으로 작은 값을 가지는 제2고주파 전압이 배플 유닛(300)에 인가되므로, 처리 공간(101)에 형성된 전계의 세기가 약하다. 이에, 처리 공간(101)에 공급된 공정 가스 중, 플라즈마로 여기되는 공정 가스의 비율이 제1스텝(S10)보다 낮아진다. 이와 달리, 처리 공간(101)에 공정 가스 상태로 존재하는 비율이 제1스텝(S10)보다 높아진다. 도 5에 도시된 바와 같이, 제2스텝(S20)을 수행하는 동안, 처리 공간(101)에는, 플라즈마에 포함되는 불소 음이온(A1)의 개수가, 공정 가스(A2)의 개수보다 상대적으로 작아질 수 있다.On the contrary, since the second high-frequency voltage having a relatively small value is applied to the
이에, 하드 마스크 막(700)과 플라즈마는, 제2스텝(S20)보다 제1스텝(S10)에서 상대적으로 높은 빈도로 반응한다. 이에 따라, 제1스텝(S10)에서는, 제2스텝(S20)에서보다 더 많은 양의 하드 마스크 막(700)이 기판(W)으로부터 제거된다. 이와 달리, 공정 가스와 박막(800)은, 제1스텝(S10)보다 제2스텝(S20)에서 상대적으로 높은 빈도로 반응한다. 보다 구체적으로, 공정 가스는 제1스텝(S10)에서, 보다 높은 빈도로 실리콘 산화막(820) 및 실리콘 질화막(840)의 표면과 반응한다. 이에, 패시베이션 막(900)은 제1스텝(S10)보다 제2스텝(S20)에서 더 두껍게 형성된다. 즉, 제1스텝(S10)에서는, 플라즈마에 의한 하드 마스크 막(700)의 제거 속도가, 패시베이션 막(900)의 형성 속도보다 우세할 수 있다. 이와 달리, 제2스텝(S20)에서는, 패시베이션 막(900)의 형성 속도가, 플라즈마에 의한 하드 마스크 막(700)의 제거 속도보다 우세할 수 있다.Accordingly, the
상술한 실시예에 의하면, 하드 마스크 막(700)은 메탈을 포함하므로, 전 공정에서의 하드 마스크 막의 에칭에 대한 내성을 증가시킬 수 있다. 또한, 제1스텝(S10)을 제2스텝(S20)보다 선행하여, 메탈을 포함하는 하드 마스크 막(700)을 보다 효율적으로 제거할 수 있다. 즉, 제1스텝(S10)을 제2스텝(S20)보다 선행하면, 메탈을 포함하는 하드 마스크 막(700)의 제거 측면에서 보다 효율적일 수 있다.According to the above-described embodiment, since the
또한, 처리 공간(101)에 공급되는 공정 가스가 박막(800)의 표면에 패시베이션 막(900)을 형성하므로, 플라즈마로 하드 마스크 막(700)을 기판(W)으로부터 제거함과 동시에, 플라즈마에 의해 박막(800)들이 식각되는 것을 최소화할 수 있다. 이에, 높은 선택비(Selectivity)를 가지는 기판(W)을 얻을 수 있다.In addition, since the process gas supplied to the
이하에서는, 다른 실시예에 따른 기판 처리 방법에 대해 설명한다. 이하에서 설명하는 일 실시예에 의한 기판 처리 방법은, 추가적으로 설명하는 경우 외에는 상술한 기판 처리 방법과 동일 또는 유사한 메커니즘으로 수행되므로, 중복되는 내용에 대한 설명은 생략한다.Below, a substrate processing method according to another embodiment will be described. The substrate processing method according to an embodiment described below is performed using the same or similar mechanism as the substrate processing method described above except in cases where it is additionally described, and therefore description of overlapping content will be omitted.
도 7은 다른 실시예에 따른 기판 처리 방법의 플로우 차트이다.7 is a flow chart of a substrate processing method according to another embodiment.
일 실시예에 의한 기판 처리 방법은, 제2스텝(S30)을 수행한 이후에 제1스텝(S40)을 수행할 수 있다. 일 실시예에 의한 제2스텝(S30)은 상술한 제2스텝(S20)과 동일 또는 유사하고, 제1스텝(S40)은 상술한 제1스텝(S10)과 동일 또는 유사하다. 즉, 일 실시예에 의한 기판 처리 방법에서는, 제2스텝(S30)이 제1스텝(S40)보다 선행하여 수행될 수 있다. 이 경우, 패시베이션 막(900)을 선행적으로 박막(800)들의 표면에 형성함으로써, 박막(800)들이 플라즈마에 의해 식각되는 것을 보다 효율적으로 예방할 수 있다. 즉, 제2스텝(S30)을 제1스텝(S40)보다 선행하면, 선택비 측면에서 보다 효율적일 수 있다.In the substrate processing method according to one embodiment, the first step (S40) may be performed after the second step (S30) is performed. The second step (S30) according to one embodiment is the same as or similar to the above-described second step (S20), and the first step (S40) is the same as or similar to the above-described first step (S10). That is, in the substrate processing method according to one embodiment, the second step S30 may be performed before the first step S40. In this case, by previously forming the
이상의 상세한 설명은 본 발명을 예시하는 것이다. 또한 전술한 내용은 본 발명의 바람직한 실시 형태를 나타내어 설명하는 것이며, 본 발명은 다양한 다른 조합, 변경 및 환경에서 사용할 수 있다. 즉 본 명세서에 개시된 발명의 개념의 범위, 저술한 개시 내용과 균등한 범위 및/또는 당업계의 기술 또는 지식의 범위내에서 변경 또는 수정이 가능하다. 전술한 실시예는 본 발명의 기술적 사상을 구현하기 위한 최선의 상태를 설명하는 것이며, 본 발명의 구체적인 적용 분야 및 용도에서 요구되는 다양한 변경도 가능하다. 따라서 이상의 발명의 상세한 설명은 개시된 실시 상태로 본 발명을 제한하려는 의도가 아니다. 또한 첨부된 청구범위는 다른 실시 상태도 포함하는 것으로 해석되어야 한다.The above detailed description is illustrative of the present invention. Additionally, the foregoing is intended to illustrate preferred embodiments of the present invention, and the present invention can be used in various other combinations, modifications, and environments. That is, changes or modifications are possible within the scope of the inventive concept disclosed in this specification, the scope equivalent to the written disclosure, and/or the technology or knowledge in the art. The above-described embodiments illustrate the best state for implementing the technical idea of the present invention, and various changes required for specific application fields and uses of the present invention are also possible. Accordingly, the detailed description of the invention above is not intended to limit the invention to the disclosed embodiments. Additionally, the appended claims should be construed to include other embodiments as well.
100: 하우징
200: 지지 유닛
300: 배플 유닛
400: 가스 공급 유닛
500: 전원 유닛
600: 제어기
S10, S40: 제1스텝
S20, S30: 제2스텝100: housing
200: support unit
300: Baffle unit
400: gas supply unit
500: Power unit
600: Controller
S10, S40: 1st step
S20, S30: 2nd step
Claims (16)
챔버 내에 공정 가스를 공급하여 기판을 처리하되,
상기 공정 가스 중 일부는 플라즈마 상태로 여기되고, 상기 플라즈마는 기판 상에 형성된 하드 마스크 막을 기판으로부터 제거하고,
상기 공정 가스 중 다른 일부는 기판 상에 형성된 박막과 반응하여 상기 박막의 표면에 패시베이션 막(Passivation film)을 형성하되,
상기 공정 가스는 CHF 계열의 가스인 것을 특징으로 하는 기판 처리 방법.In the method of processing the substrate,
Process the substrate by supplying process gas into the chamber,
Some of the process gas is excited into a plasma state, and the plasma removes the hard mask film formed on the substrate from the substrate,
Another part of the process gas reacts with the thin film formed on the substrate to form a passivation film on the surface of the thin film,
A substrate processing method, wherein the process gas is a CHF series gas.
상기 방법은,
상기 챔버 내로 상기 공정 가스를 공급하는 동안, 제1스텝과 제2스텝을 일 사이클로 복수 회 반복하고,
상기 제1스텝은, 상기 플라즈마를 발생시키는 전극에 제1전압을 인가하고,
상기 제2스텝은, 상기 전극에 상기 제1전압보다 낮은 제2전압을 인가하는 것을 특징으로 하는 기판 처리 방법.According to paragraph 1,
The above method is,
While supplying the process gas into the chamber, the first step and the second step are repeated multiple times in one cycle,
The first step applies a first voltage to the electrode that generates the plasma,
The second step is a substrate processing method characterized in that a second voltage lower than the first voltage is applied to the electrode.
상기 제1스텝은, 상기 일 사이클 내에서, 상기 제2스텝보다 선행하는 것을 특징으로 하는 기판 처리 방법.According to paragraph 2,
A substrate processing method, characterized in that the first step precedes the second step within the one cycle.
상기 제2스텝은, 상기 일 사이클 내에서, 상기 제1스텝보다 선행하는 것을 특징으로 하는 기판 처리 방법.According to paragraph 2,
A substrate processing method, characterized in that the second step precedes the first step within the one cycle.
상기 하드 마스크 막은 메탈이 포함된 것을 특징으로 하는 기판 처리 방법.According to paragraph 1,
A substrate processing method, wherein the hard mask film contains metal.
상기 메탈은, 텅스텐, 카본, 그리고 브론 중 적어도 어느 하나를 포함하는 것을 특징으로 하는 기판 처리 방법.According to clause 5,
A substrate processing method, wherein the metal includes at least one of tungsten, carbon, and bronze.
상기 박막은,
실리콘 산화막과 실리콘 질화막 중 적어도 어느 하나를 포함하는 것을 특징으로 하는 기판 처리 방법.According to paragraph 1,
The thin film is,
A substrate processing method comprising at least one of a silicon oxide film and a silicon nitride film.
상기 박막은,
상기 실리콘 산화막과 상기 실리콘 질화막이 교대로 적층되는 것을 특징으로 하는 기판 처리 방법.In clause 7,
The thin film is,
A substrate processing method characterized in that the silicon oxide film and the silicon nitride film are alternately stacked.
상기 챔버 내에 상기 공정 가스를 공급하는 동안,
상기 챔버 내로 공급되는 상기 공정 가스의 단위 시간당 공급 유량이 변경되는 것을 특징으로 하는 기판 처리 방법.According to paragraph 1,
While supplying the process gas into the chamber,
A substrate processing method, characterized in that the flow rate per unit time of the process gas supplied into the chamber is changed.
CHF 계열의 공정 가스를 챔버 내로 공급하여 상기 하드 마스크 막을 제거하되, 상기 챔버 내로 상기 공정 가스를 공급하는 동안 상기 공정 가스를 여기시키는 고주파 전압의 세기를 변경시키는 스텝을 복수 회 반복하는 것을 특징으로 하는 기판 처리 방법.A method of processing a substrate including a thin film in which nitride films and oxide films are alternately stacked, and a hard mask film stacked on top of the thin film and containing a metal component,
The hard mask film is removed by supplying a CHF-based process gas into the chamber, and the step of changing the strength of the high frequency voltage that excites the process gas while supplying the process gas into the chamber is repeated multiple times. Substrate processing method.
상기 공정 가스 중 일부는 상기 고주파 전압에 의해 플라즈마 상태로 여기되고, 상기 플라즈마는 상기 하드 마스크 막을 기판으로부터 제거하고,
상기 공정 가스 중 다른 일부는 상기 박막과 반응하여 상기 박막의 표면에 패시베이션 막을 형성하는 것을 특징으로 하는 기판 처리 방법.According to clause 10,
Some of the process gas is excited into a plasma state by the high frequency voltage, and the plasma removes the hard mask film from the substrate,
Another part of the process gas reacts with the thin film to form a passivation film on the surface of the thin film.
상기 스텝은 제1스텝과 제2스텝을 포함하고,
상기 제1스텝은, 상기 플라즈마를 발생시키는 전극에 제1전압을 인가하고,
상기 제2스텝은, 상기 전극에 상기 제1전압보다 낮은 제2전압을 인가하되,
상기 제1스텝에서는, 상기 하드 마스크 막의 제거 속도가 상기 패시베이션 막의 형성 속도보다 우세하고,
상기 제2스텝에서는, 상기 패시베이션 막의 형성 속도가 상기 하드 마스크 막의 제거 속도보다 우세한 것을 특징으로 하는 기판 처리 방법.According to clause 11,
The step includes a first step and a second step,
The first step applies a first voltage to the electrode that generates the plasma,
The second step applies a second voltage lower than the first voltage to the electrode,
In the first step, the removal rate of the hard mask film is superior to the formation rate of the passivation film,
In the second step, the formation rate of the passivation film is superior to the removal rate of the hard mask film.
상기 제1스텝은 상기 제2스텝보다 선행하는 것을 특징으로 하는 기판 처리 방법.According to clause 12,
A substrate processing method, characterized in that the first step precedes the second step.
상기 제2스텝은 상기 제1스텝보다 선행하는 것을 특징으로 하는 기판 처리 방법.According to clause 12,
A substrate processing method, characterized in that the second step precedes the first step.
상기 메탈은, 텅스텐, 카본, 그리고 브론 중 적어도 어느 하나를 포함하는 것을 특징으로 하는 기판 처리 방법.According to clause 10,
A substrate processing method, wherein the metal includes at least one of tungsten, carbon, and bronze.
상기 챔버 내에 상기 공정 가스를 공급하는 동안,
상기 챔버 내로 공급되는 상기 공정 가스의 단위 시간당 공급 유량이 변경되는 것을 특징으로 하는 기판 처리 방법.According to clause 10,
While supplying the process gas into the chamber,
A substrate processing method, characterized in that the flow rate per unit time of the process gas supplied into the chamber is changed.