KR20240003480A - Pt alloy composition and Manufacturing method thereof - Google Patents
Pt alloy composition and Manufacturing method thereof Download PDFInfo
- Publication number
- KR20240003480A KR20240003480A KR1020220081062A KR20220081062A KR20240003480A KR 20240003480 A KR20240003480 A KR 20240003480A KR 1020220081062 A KR1020220081062 A KR 1020220081062A KR 20220081062 A KR20220081062 A KR 20220081062A KR 20240003480 A KR20240003480 A KR 20240003480A
- Authority
- KR
- South Korea
- Prior art keywords
- platinum
- alloy
- alloy composition
- mass
- iridium
- Prior art date
Abstract
본 발명은 백금(Pt) 합금 조성물 및 그 제조방법에 관한 것이다.
본 발명에 따른 백금(Pt) 합금 조성물은 강도가 극대화되어 외부 충격으로부터 저항성이 높아짐으로써 주얼리 산업에서 가장 중요한 핵심 기술인 디자인 자유도 측면에서 기존 합금 소재로는 표현할 수 없었던 더욱 섬세한 디자인 형상화가 가능하다. The present invention relates to a platinum (Pt) alloy composition and a method for manufacturing the same.
The platinum (Pt) alloy composition according to the present invention maximizes strength and increases resistance to external shock, enabling more detailed design shaping that could not be expressed with existing alloy materials in terms of design freedom, which is the most important core technology in the jewelry industry.
Description
본 발명은 백금(Pt) 합금 조성물 및 그 제조방법에 관한 것이다. The present invention relates to a platinum (Pt) alloy composition and a method for manufacturing the same.
귀금속 소재로 다양하게 사용되고 있는 백금(Platinum, Pt)과 금(Gold, Au)은 높은 용융점과 무른 성질로 인하여 별도의 가공기술이 요구되는 소재로써 백금 합금 소재인 Pt 950, 금 합금 소재인 Au 995는 제품에 손상을 입기가 쉽고 세밀한 형상을 표현하기 위하여 가는 선을 가공하였을 경우 변형과 끊어짐이 쉽게 일어나는 기술적 문제로 인하여 정밀 세공이 어려운 디자인적인 문제와 이로 인한 중량증가 및 원가 상승의 기술적 문제점을 가지고 있다.Platinum (Pt) and gold (Au), which are widely used as precious metal materials, require separate processing technology due to their high melting point and soft nature. Pt 950 is a platinum alloy material, and Au 995 is a gold alloy material. The product is prone to damage, and when thin lines are processed to express detailed shapes, deformation and breakage occur easily. Due to this, there are design problems that make precise machining difficult, and technical problems of increased weight and cost due to this. there is.
그리고, 99.9% 이상 순도의 순수 백금은 높은 용융점으로 인한 가공의 어려움과 무름 특성(Hv 37~108)으로 인하여 쉽게 스크래치가 생기는 등의 문제점이 있으며, 순금 또한 무름 특성(Hv 20~58) 때문에 정교한 주얼리 제작에 한계가 존재하고 있다.In addition, pure platinum with a purity of 99.9% or higher has problems such as difficulty in processing due to its high melting point and scratches easily due to its brittle nature (Hv 37~108). Pure gold also has its brittle nature (Hv 20~58), making it difficult to process, and has problems such as being easily scratched. There are limits to jewelry production.
또한, Pt 합금으로 Pt 850, Pt 900, Pt 950이 있으며, 첨가되는 합금용 금속에 대해서는 특별한 규정이 없으나, 일반적으로 Pd, Ru, Ag 또는 Ir 등의 금속이 Pt 합금에 이용되고 있다. 백금 제품의 소재로 가장 많이 사용되는 것은 Pt 950이지만 현재 시판되고 있는 Pt 950 합금을 사용한 백금 합금 제품들은 낮은 강도(strength)로 인하여 백금 주얼리 시장에서 요구되는 강도를 충족시키지 못하여 외부 충격에 약한 단점이 있고 다양한 디자인의 고품질 제품 개발에 걸림돌이 되는 상황에 있다. In addition, Pt alloys include Pt 850, Pt 900, and Pt 950. There are no special regulations on the alloy metals added, but metals such as Pd, Ru, Ag, or Ir are generally used in Pt alloys. The most commonly used material for platinum products is Pt 950, but currently commercially available platinum alloy products using Pt 950 alloy do not meet the strength required in the platinum jewelry market due to their low strength, making them vulnerable to external shocks. and is an obstacle to the development of high-quality products with diverse designs.
더욱이 현재 주얼리 제조시 핵심공정인 캐스팅(casting) 공정은 피막 및 불순물 제거를 위하여 Pt950 제품은 불산 환경에서 약 120분, Au995 제품은 황산(혹은 염산)에서 약 10분 정도의 후처리 공정이 필요하여 작업자들은 인체 유해물질에 장시간 노출되고 있는 문제점이 있다.Moreover, the casting process, which is currently a core process in jewelry manufacturing, requires a post-treatment process of about 120 minutes in a hydrofluoric acid environment for Pt950 products and about 10 minutes in sulfuric acid (or hydrochloric acid) for Au995 products to remove films and impurities. There is a problem in that workers are exposed to substances hazardous to the human body for long periods of time.
한편, 백금(Pt) 950과 순금 99.5% 금속 소재 Au 995의 경우 저중량으로도 충분한 내구성 유지가 가능하여 생산단가를 낮출 수 있는 소재의 고강도화 기술과 디자인 자유도를 극대화할 수 있는 신소재 기술 개발이 요구되고 있다.Meanwhile, in the case of platinum (Pt) 950 and Au 995, a metal material made of 99.5% pure gold, it is possible to maintain sufficient durability even at low weight, requiring the development of high-strength materials that can reduce production costs and new material technologies that can maximize design freedom. there is.
본 발명의 과제는 강도를 극대화하여 외부 충격으로부터 저항성이 높아짐으로써 주얼리 산업에서 가장 중요한 핵심 기술인 디자인 자유도 측면에서 기존 합금 소재로는 표현할 수 없었던 더욱 섬세한 디자인 형상화가 가능한 백금(Pt) 합금 조성물 및 그 제조방법을 제공하는 것이다. The object of the present invention is to provide a platinum (Pt) alloy composition and its It provides a manufacturing method.
상기한 과제를 달성하기 위해 본 발명은,In order to achieve the above task, the present invention,
백금(Pt) 95 질량% 이상, 루테늄(Ru), 이리듐(Ir) 및 은(Ag)으로 이루어진 군에서 선택된 1종 이상의 합금용 금속 3.7 내지 4.8 질량%와, 레늄(Re) 0.2 내지 1 질량%를 함유하는 것을 특징으로 하는, 백금(Pt) 합금 조성물을 제공한다.95% by mass or more of platinum (Pt), 3.7 to 4.8% by mass of one or more alloy metals selected from the group consisting of ruthenium (Ru), iridium (Ir), and silver (Ag), and 0.2 to 1% by mass of rhenium (Re) Provided is a platinum (Pt) alloy composition, characterized in that it contains.
또한 본 발명은Additionally, the present invention
백금(Pt), 루테늄(Ru), 이리듐(Ir) 및 은(Ag)으로 이루어진 군에서 선택된 1종 이상의 합금용 금속과 레늄(Re)을 고주파 발진기와 유도코일이 구비된 용해챔버에 넣고, 100-400 KHz로 고주파를 인가하여 귀금속 백금(Pt), 루테늄(Ru), 이리듐(Ir) 및 은(Ag)으로 이루어진 군에서 선택된 1종 이상의 합금용 금속과 레늄(Re)을 용해시키는 단계를 포함하는 백금(Pt) 합금 조성물의 제조방법을 제공한다. One or more alloy metals selected from the group consisting of platinum (Pt), ruthenium (Ru), iridium (Ir), and silver (Ag) and rhenium (Re) are placed in a melting chamber equipped with a high-frequency oscillator and an induction coil, 100 Including the step of dissolving rhenium (Re) and one or more alloy metals selected from the group consisting of noble metals platinum (Pt), ruthenium (Ru), iridium (Ir), and silver (Ag) by applying high frequency at -400 KHz. A method for producing a platinum (Pt) alloy composition is provided.
본 발명에 따른 백금(Pt) 합금 조성물은 강도가 극대화되어 외부 충격으로부터 저항성이 높아짐으로써 주얼리 산업에서 가장 중요한 핵심 기술인 디자인 자유도 측면에서 기존 합금 소재로는 표현할 수 없었던 더욱 섬세한 디자인 형상화가 가능하다. The platinum (Pt) alloy composition according to the present invention maximizes strength and increases resistance to external shock, enabling more detailed design shaping that could not be expressed with existing alloy materials in terms of design freedom, which is the most important core technology in the jewelry industry.
도 1은 본 발명의 실시 예에 따른 유도가열 기반의 고주파 합금 용해로의 설치 상태를 보인 구성도이다.
도 2는 도 1의 유도가열 기반의 고주파 합금 용해로를 보인 정면도이다.
도 3은 도 1의 유도가열 기반의 고주파 합금 용해로를 보인 평면도이다.
도 4는 도 1의 유도가열 기반의 고주파 합금 용해로에 대한 사시도이다.Figure 1 is a configuration diagram showing the installation state of an induction heating-based high-frequency alloy melting furnace according to an embodiment of the present invention.
Figure 2 is a front view showing the induction heating-based high-frequency alloy melting furnace of Figure 1.
Figure 3 is a plan view showing the induction heating-based high-frequency alloy melting furnace of Figure 1.
Figure 4 is a perspective view of the induction heating-based high-frequency alloy melting furnace of Figure 1.
이하 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.
본 발명에 따른 백금(Pt) 합금 조성물은, 귀금속 백금(Pt)와, 루테늄(Ru), 이리듐(Ir) 및 은(Ag)으로 이루어진 군에서 선택된 1종 이상의 합금용 금속과 레늄(Re)을 함유한다.The platinum (Pt) alloy composition according to the present invention includes the precious metal platinum (Pt), one or more alloy metals selected from the group consisting of ruthenium (Ru), iridium (Ir), and silver (Ag), and rhenium (Re). Contains.
백금(Pt)는 Pt 합금의 주성분으로 95 질량% 이상으로 함유되어 Pt950을 얻을 수 있다. 백금 합금 Pt950은 경도가 낮아 사용 중 상처가 나기 쉽고, 변형이 생겨 가공이 어렵다. 이에 본 발명에서는 강도 개선을 위해 루테늄(Ru), 이리듐(Ir) 및 은(Ag)으로 이루어진 군에서 선택된 1종 이상과, 레늄(Re)을 첨가한다. 이때 목표로 하는 강도를 얻기 위해 필요한 1종 이상의 합금용 금속과 레늄(Re)의 첨가를 위해 백금(Pt)의 함유량은 95.3 질량% 이하인 것이 바람직하다. Platinum (Pt) is the main component of Pt alloy and is contained in more than 95% by mass to obtain Pt950. Platinum alloy Pt950 has low hardness, so it is easy to get scratched during use and is difficult to process due to deformation. Accordingly, in the present invention, at least one selected from the group consisting of ruthenium (Ru), iridium (Ir), and silver (Ag), and rhenium (Re) are added to improve strength. At this time, in order to add one or more alloy metals and rhenium (Re) necessary to obtain the target strength, the platinum (Pt) content is preferably 95.3% by mass or less.
본 발명의 일 실시예에 있어서, 백금(Pt) 합금 조성물은 레늄(Re) 0.20 내지 1 질량% 함유한다. 상기 레늄(Re)는 PtRe간 금속간 화합물 형성으로 인해 백금 합금의 경도를 개선하기 위해 첨가한다. 이때 레늄(Re)의 함량이 상기 범위 미만이면, 첨가 효과가 없어 레늄(Re)을 첨가하였음에도 경도 개선 효과가 미미하고, 이와 반대로 상기 범위를 초과하면, 가공성이 저하된다. In one embodiment of the present invention, the platinum (Pt) alloy composition contains 0.20 to 1% by mass of rhenium (Re). The rhenium (Re) is added to improve the hardness of the platinum alloy due to the formation of an intermetallic compound between PtRe. At this time, if the content of rhenium (Re) is less than the above range, there is no effect of addition, so the effect of improving hardness is minimal despite the addition of rhenium (Re). Conversely, if it exceeds the above range, processability deteriorates.
본 발명의 일 실시예에 있어서, 백금(Pt) 합금 조성물은 루테늄(Ru), 이리듐(Ir) 및 은(Ag)으로 이루어진 군에서 선택된 1종 이상의 합금용 금속 3.7 내지 4.8 질량% 함유한다. 상기 루테늄(Ru)과 이리듐(Ir)은 금속 경화제로 백금(Pt) 합금의 경도를 개선하기 위해 첨가되며, 광범위한 첨가량 범위에 걸쳐 백금(Pt) 합금의 특성을 저하시키지 않고, 경도 개선이 가능하다. 상기 은(Ag)는 루테늄(Ru), 이리듐(Ir), 레늄(Re) 등과의 합금을 형성하여 백금(Pt)의 강도를 개선하기 위해 첨가한다. 이때 합금용 금속의 함량이 상기 범위 미만이면, Pt950을 얻기 위해 상대적으로 레늄(Re)의 첨가량이 증가하여 가공성이 저하되고, 상기 범위를 초과하면 레늄(Re)의 첨가량이 감소하여 적절한 경도 개선 효과를 나타낼 수 없다. In one embodiment of the present invention, the platinum (Pt) alloy composition contains 3.7 to 4.8 mass% of one or more alloy metals selected from the group consisting of ruthenium (Ru), iridium (Ir), and silver (Ag). The ruthenium (Ru) and iridium (Ir) are added as a metal hardener to improve the hardness of the platinum (Pt) alloy, and the hardness can be improved without deteriorating the properties of the platinum (Pt) alloy over a wide range of addition amounts. . The silver (Ag) is added to improve the strength of platinum (Pt) by forming an alloy with ruthenium (Ru), iridium (Ir), rhenium (Re), etc. At this time, if the content of alloy metal is less than the above range, the amount of rhenium (Re) added is relatively increased to obtain Pt950, which reduces workability, and if it exceeds the above range, the amount of rhenium (Re) added is reduced, resulting in an appropriate improvement in hardness. cannot be expressed.
본 발명의 일 실시예에 있어서, 백금(Pt) 합금 조성물은 루테늄(Ru) 3.0 내지 3.5 질량%로 첨가된다. 이때 루테늄(Ru)의 함량이 상기 범위 미만이면, 첨가 효과가 없어 경도 개선 효과가 미미하고, 이와 반대로 상기 범위를 초과하면, 가공성이 저하된다. In one embodiment of the present invention, 3.0 to 3.5% by mass of ruthenium (Ru) is added to the platinum (Pt) alloy composition. At this time, if the content of ruthenium (Ru) is less than the above range, there is no effect of addition, so the effect of improving hardness is minimal. Conversely, if it exceeds the above range, processability deteriorates.
본 발명의 일 실시예에 있어서, 백금(Pt) 합금 조성물은 이리듐(Ir) 0.4 내지 0.9 질량%로 첨가된다. 상기 이리듐(Ir)의 함량이 상기 범위 미만이면, 첨가 효과가 없어 경도 개선 효과가 미미하고, 이와 반대로 상기 범위를 초과하면, 가공성이 저하된다. In one embodiment of the present invention, 0.4 to 0.9% by mass of iridium (Ir) is added to the platinum (Pt) alloy composition. If the content of iridium (Ir) is less than the above range, there is no effect of addition, so the effect of improving hardness is minimal. Conversely, if it exceeds the above range, processability deteriorates.
본 발명의 일 실시예에 있어서, 백금(Pt) 합금 조성물은 은(Ag) 0.1 내지 0.5 질량%로 첨가된다. 상기 은(Ag)의 함량이 상기 범위 미만이면, 첨가 효과가 없어 은(Ag)을 첨가하였음에도 경도 개선 효과가 미미하고, 이와 반대로 상기 범위를 초과하면, 가공성이 저하된다. In one embodiment of the present invention, 0.1 to 0.5% by mass of silver (Ag) is added to the platinum (Pt) alloy composition. If the content of silver (Ag) is less than the above range, there is no effect of addition, so the effect of improving hardness is minimal despite the addition of silver (Ag). Conversely, if it exceeds the above range, processability deteriorates.
본 발명의 일 실시예에 있어서, 백금(Pt) 합금 조성물의 비커스 경도(Hv)는, 190 이상의 값, 구체적으로 190 내지 200 사이의 값을 가질 수 있다. 또한, 상기 백금(Pt) 합금 조성물의 인장강도(N)는 100 이상의 값, 구체적으로 100 내지 110 사이의 값을 가질 수 있다. In one embodiment of the present invention, the Vickers hardness (Hv) of the platinum (Pt) alloy composition may have a value of 190 or more, specifically a value between 190 and 200. In addition, the tensile strength (N) of the platinum (Pt) alloy composition may have a value of 100 or more, specifically a value between 100 and 110.
본 발명의 일 실시예에 따르면, 첨가되는 합금용 금속의 3000 ℃가 넘는 높은 용융점까지 가열이 필요하므로, 100-400 KHz 고주파 용해로를 이용하여 귀금속 및 합금용 원소를 용융함으로써 합금을 제조한다. According to one embodiment of the present invention, since the added alloy metal needs to be heated to a high melting point of over 3000°C, the alloy is manufactured by melting the noble metal and alloy elements using a 100-400 KHz high-frequency melting furnace.
본 발명의 일 실시예에 따른 유도가열 기반의 고주파 합금 용해로는 도 1 내지 도 4에 도시된 바와 같이 용해로를 이루는 바디(100)와 상기 바디(100)의 내측에 제공되는 용해챔버(200)와, 고주파 전류를 공급하는 고주파 발진기(400)와 상기 용해챔버(200)의 외벽에 설치되며 상기 고주파 발진기(400)와 단자로 연결되어 고주파를 발생시키는 유도코일(300)과 상기 용해챔버(200)에 설치되어 재료의 용융온도를 센싱하는 복수개의 적외선 센서(500) 및 센싱값을 통해 각 구성부품을 제어하는 제어부(600)를 포함하여 구성되어 있다.The high-frequency alloy melting furnace based on induction heating according to an embodiment of the present invention includes a body 100 forming a melting furnace as shown in FIGS. 1 to 4, a melting chamber 200 provided inside the body 100, and , a high-frequency oscillator 400 that supplies high-frequency current, and an induction coil 300 and the dissolution chamber 200 that are installed on the outer wall of the dissolution chamber 200 and are connected to the high-frequency oscillator 400 through a terminal to generate high frequencies. It is installed and consists of a plurality of infrared sensors 500 that sense the melting temperature of the material and a control unit 600 that controls each component through the sensing value.
바디(100)는, 용해로의 외관을 이루며 내측에 용해챔버(200)가 설치되어 있다.The body 100 has the appearance of a melting furnace and a melting chamber 200 is installed on the inside.
용해챔버(200)는, 대략 3000 ℃에서 견딜수 있는 세라믹 소재로 이루어지며, 내부는 진공 상태를 유지하고 있고, 벽체의 외주면에 유도코일(300)이 감겨지는 형태로 설치되어 있다.The dissolution chamber 200 is made of a ceramic material that can withstand approximately 3000°C, the interior is maintained in a vacuum state, and an induction coil 300 is wound around the outer peripheral surface of the wall.
유도코일(300)은, 상기 용해챔버(200)의 외측 벽면에 감겨지는 형태로 구비되어 상기 고주파 발진기(400)로부터의 전원 인가시 상기 용해챔버(200) 내의 재료를 유도가열을 통해 급속 가열시키게 된다.The induction coil 300 is provided in a form wound around the outer wall of the dissolution chamber 200 to rapidly heat the material in the dissolution chamber 200 through induction heating when power is applied from the high-frequency oscillator 400. do.
상기 유도가열이란, 도전성이 있는 물체를 변화하는 자계 가운데 넣어 가열하는 방법을 말하며, 가열되는 물체는 반드시 전도성이 있어야 한다. The induction heating refers to a method of heating a conductive object by placing it in a changing magnetic field, and the object to be heated must be conductive.
고주파 유도 가열은, 전원 공급에 의해 고주파 발진기(400)로부터 공급되는 고주파 전류가 유도코일(300)을 따라 흐르면, 유도코일(300)에 의해 감겨져 중심부에 위치한 피가열체의 재료에 전자 유도 작용으로 인한 와전류(EddyCurrent) 및 히스테리시스(Hysteresis)의 열 손실에 의해 피가열체의 재료 표면이 급속하게 가열된다.In high-frequency induction heating, when a high-frequency current supplied from the high-frequency oscillator 400 by power supply flows along the induction coil 300, it is wound by the induction coil 300 and produces an electromagnetic induction effect on the material of the object to be heated located at the center. The surface of the material to be heated is rapidly heated due to heat loss due to eddy current and hysteresis.
고주파 발진기(400)는, 공지의 고주파 전류를 공급하는 발진기가 적용될 수 있으며 백금 등의 합금이 용해될 수 있도록 100-400 KHz로 고주파를 발생시키게 된다.The high-frequency oscillator 400 may be an oscillator that supplies a known high-frequency current and generates a high frequency of 100-400 KHz so that alloys such as platinum can be dissolved.
이에 따라 용해챔버(200) 내의 피가열체인 재료는 고주파 전류에 의한 전자 유도 작용을 통해 용해되게 된다.Accordingly, the material to be heated in the dissolution chamber 200 is melted through electromagnetic induction by high-frequency current.
적외선 센서(600)는, 초고온 온도의 측정이 가능하며, 상기 용해챔버(200)에 복수개로 설치되어 재료의 용융온도를 센싱하게 된다.The infrared sensor 600 is capable of measuring extremely high temperatures, and is installed in plural numbers in the melting chamber 200 to sense the melting temperature of the material.
이상에서와 같이 구성되는 본 발명에 따른 유도가열 기반의 고주파 합금 용해로를 통해 재료를 용해시키는 과정을 살펴보면 다음과 같다.The process of melting the material through the induction heating-based high-frequency alloy melting furnace according to the present invention configured as described above is as follows.
도 1에 도시된 바와 같이 바디(100) 내의 용해챔버(200)에 백금 등의 합금 재료를 넣고 고주파 발진기(400)를 동작시킨다. 그러면 유도코일(300)을 통해 대략 100-400 KHz 용량의 고주파 전류가 발생되어 재료를 가열시키게 된다. 이후 재료가 용융이 시작된 후 적정 온도가 되면 적외선 센서(600)가 온도값을 센싱하여 출력하고 제어부(600)는 입력된 센싱값과 기 저장된 온도값을 통해 고주파 발진기(400)를 제어하여 안정되게 용융된 재료를 얻을 수 있게 된다. As shown in FIG. 1, an alloy material such as platinum is placed in the dissolution chamber 200 within the body 100, and the high-frequency oscillator 400 is operated. Then, a high-frequency current of approximately 100-400 KHz is generated through the induction coil 300 to heat the material. After the material begins to melt and reaches an appropriate temperature, the infrared sensor 600 senses and outputs the temperature value, and the control unit 600 controls the high-frequency oscillator 400 through the input sensing value and the previously stored temperature value to stabilize the temperature. Molten material can be obtained.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예 및 실험예를 제시한다. 그러나 하기의 실시예는 본 발명을 보다 쉽게 이해하기 위하여 제공되는 것일 뿐, 실시예에 의해 본 발명의 내용이 한정되는 것은 아니다.Below, preferred examples and experimental examples are presented to aid understanding of the present invention. However, the following examples are provided only to make the present invention easier to understand, and the content of the present invention is not limited by the examples.
실시예 1: 귀금속 백금(Pt) 합금의 제조Example 1: Preparation of precious metal platinum (Pt) alloy
아래와 같은 방법에 의하여 귀금속 백금(Pt) 합금을 제조하였다. 하기 조성의 성분을 균일하게 혼합하여 고주파 발진기와 유도코일이 구비된 용해챔버에 넣고 100-400 KHz 용량의 고주파를 인가하여 약 3000℃ 정도로 용해시킨 후, 진공 분위기에서 주형에 주입하고 냉각하여 귀금속 백금 합금을 얻었다. 하기 표 1에 표시된 수치는 원료가 되는 금속을 혼합하여 용융시킨 후 응고된 시료에 대해 EDS(Energy Dispersive X-ray Spectroscopy)를 이용하여 조성물 분석한 결과를 나타낸 것이다. The noble metal platinum (Pt) alloy was manufactured by the method below. Mix the ingredients of the following composition uniformly, put them in a melting chamber equipped with a high-frequency oscillator and an induction coil, apply high-frequency waves of 100-400 KHz to dissolve them at about 3000°C, then inject them into a mold in a vacuum atmosphere and cool them to produce precious metal platinum. alloy was obtained. The values shown in Table 1 below show the results of composition analysis using EDS (Energy Dispersive X-ray Spectroscopy) on the solidified sample after mixing and melting the raw metals.
실험예Experiment example 1: One: 비커스Vickers 경도의 측정 Measurement of hardness
상기 실시예 및 비교예의 백금(Pt) 합금에 대해 ASTM E384에 근거하여 미소 경도계를 이용하여 n = 3의 평균치에 대한 비커스 경도를 측정하고 그 결과를 아래 표 2에 나타내었다. For the platinum (Pt) alloys of the above examples and comparative examples, the Vickers hardness was measured for the average value of n = 3 using a micro hardness tester based on ASTM E384, and the results are shown in Table 2 below.
실험예 2: 인장강도의 측정Experimental Example 2: Measurement of tensile strength
상기 실시예 및 비교예의 백금(Pt) 합금에 대해 ASTM A370에 근거하여 인장강도를 측정하였으며, 그 결과를 아래 표 3에 나타내었다. The tensile strength of the platinum (Pt) alloys of the above examples and comparative examples was measured based on ASTM A370, and the results are shown in Table 3 below.
Claims (6)
백금(Pt) 95 질량% 이상, 루테늄(Ru), 이리듐(Ir) 및 은(Ag)으로 이루어진 군에서 선택된 1종 이상의 합금용 금속 3.7 내지 4.8 질량%와, 레늄(Re) 0.2 내지 1 질량%를 함유하는 것을 특징으로 하는, 백금(Pt) 합금 조성물. A precious metal alloy for jewelry containing platinum,
95% by mass or more of platinum (Pt), 3.7 to 4.8% by mass of one or more alloy metals selected from the group consisting of ruthenium (Ru), iridium (Ir), and silver (Ag), and 0.2 to 1% by mass of rhenium (Re) A platinum (Pt) alloy composition, characterized in that it contains.
루테늄(Ru) 3.0 내지 3.5 질량%를 함유하는 것을 특징으로 하는 백금(Pt) 합금 조성물. The method of claim 1, wherein the platinum (Pt) alloy composition is
A platinum (Pt) alloy composition characterized by containing 3.0 to 3.5 mass% of ruthenium (Ru).
이리듐(Ir) 0.4 내지 0.9 질량%를 함유하는 것을 특징으로 하는 백금(Pt) 합금 조성물. The method of claim 1, wherein the platinum (Pt) alloy composition is
A platinum (Pt) alloy composition comprising 0.4 to 0.9% by mass of iridium (Ir).
은(Ag) 0.1 내지 0.5 질량%를 함유하는 것을 특징으로 하는 백금(Pt) 합금 조성물. The method of claim 1, wherein the platinum (Pt) alloy composition is
A platinum (Pt) alloy composition characterized by containing 0.1 to 0.5 mass% of silver (Ag).