KR20220126228A - Colored photosensitive resin composition, color filter and display device comprising the same - Google Patents

Colored photosensitive resin composition, color filter and display device comprising the same Download PDF

Info

Publication number
KR20220126228A
KR20220126228A KR1020220028080A KR20220028080A KR20220126228A KR 20220126228 A KR20220126228 A KR 20220126228A KR 1020220028080 A KR1020220028080 A KR 1020220028080A KR 20220028080 A KR20220028080 A KR 20220028080A KR 20220126228 A KR20220126228 A KR 20220126228A
Authority
KR
South Korea
Prior art keywords
pigment
resin composition
photosensitive resin
color material
colored photosensitive
Prior art date
Application number
KR1020220028080A
Other languages
Korean (ko)
Inventor
김수호
김정식
이현보
Original Assignee
동우 화인켐 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 동우 화인켐 주식회사 filed Critical 동우 화인켐 주식회사
Priority to CN202210426380.XA priority Critical patent/CN116736632A/en
Publication of KR20220126228A publication Critical patent/KR20220126228A/en

Abstract

The present invention relates to a colored photosensitive resin composition which comprises:(A) a coloring material; (B) an alkali-soluble resin; (C) a photopolymerizable compound; (D) a photopolymerization initiator and (E) a solvent, wherein the (A) coloring material includes: at least one coloring material selected from a group consisting of red, blue, and purple; and a black pigment and when a film is formed to a thickness of 0.5 to 3 μm, the transmittance in the spectrum wavelength of 380 to 780 nm is 80% or more, a color filter prepared using the same, and a display device comprising the color filter.

Description

착색 감광성 수지 조성물, 이를 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자{COLORED PHOTOSENSITIVE RESIN COMPOSITION, COLOR FILTER AND DISPLAY DEVICE COMPRISING THE SAME}Colored photosensitive resin composition, a color filter manufactured using the same, and a display device comprising the color filter

본 발명은 착색 감광성 수지 조성물, 이를 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자에 관한 것이다.The present invention relates to a colored photosensitive resin composition, a color filter manufactured using the same, and a display device including the color filter.

최근에는 플렉서블(flexible) 소재인 플라스틱 등과 같이 유연한 기판에 표시부, 배선 등을 형성하여, 종이처럼 휘어져도 화상 표시가 가능한 플렉서블 디스플레이 소자가 최근 각광을 받고 있다.Recently, a flexible display device capable of displaying an image even if it is bent like paper by forming a display unit and wiring on a flexible substrate such as plastic, which is a flexible material, has recently been in the spotlight.

플렉서블 디스플레이 소자는 컴퓨터의 모니터 및 TV 뿐만 아니라 개인 휴대 기기까지 그 적용 범위가 다양하며, 특히 유기 발광 표시 장치(Organic Light Emitting Display; OLED)는 액정 표시 장치(Liquid Crystal Display; LCD)와 달리 별도의 광원이 필요하지 않으므로 상대적으로 얇은 두께로 구현이 가능하다는 점에서, 플렉서블 디스플레이 소자와 관련하여 유기발광소자에 대한 연구가 활발히 진행되고 있다.Flexible display devices have a wide range of applications, not only to computer monitors and TVs, but also to personal portable devices. In particular, organic light emitting displays (OLEDs) are different from liquid crystal displays (LCDs). Since a light source is not required, it can be implemented with a relatively thin thickness, so research on an organic light emitting device is being actively conducted in relation to a flexible display device.

한편, 플렉서블 디스플레이 소자가 실제로 적용되기 위해서는 현재의 다양한 디스플레이 제품과 비교하였을 때 풀 컬러의 구현이 가능하고, 소비 전력이 작아야 하며, 실외에서도 쉽게 읽힐 수 있어야 한다.On the other hand, in order for the flexible display device to be actually applied, it should be able to realize full color, have low power consumption, and be easily readable even outdoors when compared to various current display products.

이러한 의미에서 유기 발광 소자는 풀 컬러의 구현 가능성과 낮은 소비 전력, 빠른 응답 속도의 장점을 갖고 있기 때문에 플렉서블 디스플레이 소자의 광원으로서 가장 유용한 자원이 되고 있다. 현재의 유기 발광 소자는 유기 발광 소자를 산소와 수분으로부터 보호하기 위한 캡슐 배리어(encapsulation barrier)층과 실외에서도 쉽게 읽힐 수 있도록(outdoor readability) 하기 위하여 높은 명암비(contrast ratio)를 유지하도록 편광판(polarizer)을 필요로 한다.In this sense, the organic light emitting diode has the advantages of full color realization possibility, low power consumption, and fast response speed, so it is becoming the most useful resource as a light source for a flexible display device. Current organic light emitting devices include an encapsulation barrier layer to protect the organic light emitting device from oxygen and moisture, and a polarizer to maintain a high contrast ratio for outdoor readability. need.

그러나, 상기 편광판은 휘어지지 않고 딱딱한 특성을 갖기 때문에 이를 플렉서블 디스플레이 소자에 적용하는 경우 유연성이 감소하게 되는 문제점이 발생할 수 있다. 반면, 편광판을 적용하지 않는 경우, 외부광이 플렉서블 디스플레이 소자로 투과되어 들어온 후 다시 반사되어 나가면서 원래의 유기 발광 소자에서 나오는 광과 혼색이 되면서 외부 광원 하에서의 명암비가 크게 감소하게 된다.However, since the polarizing plate does not bend and has a hard characteristic, when it is applied to a flexible display device, a problem of reduced flexibility may occur. On the other hand, when the polarizing plate is not applied, the external light is transmitted through the flexible display device and then reflected again, and the color is mixed with the light emitted from the original organic light emitting device, and the contrast ratio under the external light source is greatly reduced.

이에 따라, 최근 편광판의 특성을 개선하거나 편광판을 대체하기 위한 조성물을 개발하고자 하는 연구가 활발히 진행되고 있다.Accordingly, recent studies to improve the characteristics of the polarizing plate or to develop a composition for replacing the polarizing plate are being actively conducted.

한편, 종래 디스플레이는 전면 화면을 넓게 쓰면서도 카메라를 장착 하기 위해, 디스플레이 일부를 깍아내고 카메라 장착을 위한 구멍을 뚫는, 노치 디자인이나 홀 디스플레이 형태로 제조 되어, 화면이 불완전한 형태로 구현되었다. 이에, 최근에는 이러한 노치나 홀을 별도로 구성하지 않고도 풀스크린의 화면을 구현하면서도 카메라를 장착하기 위해, 노치나 홀 없이 카메라를 디스플레이 아래 장착하는 언더 디스플레이 카메라(UDC)에 대한 수요가 늘어나고 있다. 이러한 언더 디스플레이 카메라(UDC)는 카메라 화질을 높이기 위해 고투명 및 저반사의 소재가 절연막으로써 검토되어야 한다.On the other hand, the conventional display is manufactured in the form of a notch design or a hole display in which a part of the display is cut out and a hole is drilled for mounting a camera in order to mount a camera while using a wide front screen, and the screen is implemented in an incomplete form. Accordingly, in recent years, in order to mount a camera while implementing a full-screen screen without separately configuring such a notch or hole, there is an increasing demand for an under-display camera (UDC) in which the camera is mounted under the display without a notch or hole. In such an under-display camera (UDC), a high-transparency and low-reflection material should be considered as an insulating film in order to improve the camera quality.

또한, 저온 공정을 사용하여 제조된 디스플레이는 이전의 고온 공정을 사용하여 제조된 디스플레이와 비교하여 큰 특징을 가지게 된다. 일반적으로 재료의 신뢰성을 높이기 위하여 고온공정을 통해 패턴의 신뢰성을 높이는 것이 일반적이지만, 최근 개발되고 있는 디스플레이들의 경우 열에 취약하기 때문에 고온 공정을 진행하는 것이 어렵다. 때문에 저온 공정에서도 공정성 문제가 없는 수지 조성물에 대한 요구가 커지고 있다.In addition, a display manufactured using a low temperature process has great characteristics compared to a display manufactured using a previous high temperature process. In general, it is common to increase the reliability of the pattern through a high-temperature process in order to increase the reliability of the material. Therefore, there is a growing demand for a resin composition having no processability problem even in a low-temperature process.

대한민국 공개특허 제10-2013-0134498호에서는 적색 착색제와 녹색 착색제를 포함하는 착색제, 바인더 수지 및 블록 이소시아네이트기를 함유하는 잉크 조성물을 제시하고 있다. 그러나, 고색재현성을 구현함에 있어 색재의 선택범위가 제한되는 단점과 더불어 다양한 색영역의 구현이 부족하며, 추가로 패턴 형성성에 있어 선뜯김 및 언더컷과 같은 공정성이 부족한 문제가 있다. Korean Patent Laid-Open No. 10-2013-0134498 discloses an ink composition containing a colorant including a red colorant and a green colorant, a binder resin, and a block isocyanate group. However, in realizing high color reproducibility, there is a problem in that the selection range of a color material is limited, the implementation of various color gamuts is insufficient, and there is a problem that fairness such as line tearing and undercut is insufficient in pattern formation.

이에, 편광판을 대체하면서도, 저온경화성 특성이 우수한 언더 디스플레이 카메라 구현을 위한 절연막에 적합한 수지 조성물의 개발이 필요한 실정이다.Accordingly, there is a need to develop a resin composition suitable for an insulating film for realizing an under-display camera having excellent low-temperature curing characteristics while replacing a polarizing plate.

대한민국 공개특허 제10-2013-0134498호(2013.12.10. 공개)Republic of Korea Patent Publication No. 10-2013-0134498 (published on Dec. 10, 2013)

본 발명은 종래 고색(회색)의 재현성 및 공정성 부족 문제점을 해결하고, 편광판 대체가 가능하면서도 저온경화성 및 외광반사방지 효과가 매우 우수하며, 언더 디스플레이 카메라(UDC) 구현에 적합한 착색 감광성 수지 조성물을 제공하는 것을 목적으로 한다.The present invention solves the problem of lack of reproducibility and fairness of the conventional high color (gray), while being able to replace a polarizing plate, has excellent low-temperature curing and external light reflection prevention effects, and provides a colored photosensitive resin composition suitable for under-display camera (UDC) implementation aim to do

또한, 본 발명은 상기 착색 감광성 수지 조성물을 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자를 제공하는 것을 목적으로 한다.Another object of the present invention is to provide a color filter manufactured using the colored photosensitive resin composition and a display device including the color filter.

상기 목적을 달성하기 위해, 본 발명은 (A) 색재; (B) 알칼리 가용성 수지; (C) 광중합성 화합물; (D) 광중합 개시제 및 (E) 용제를 포함하고,In order to achieve the above object, the present invention is (A) a color material; (B) alkali-soluble resin; (C) a photopolymerizable compound; (D) a photoinitiator and (E) a solvent,

상기 (A) 색재는 적색, 청색 및 자색으로 이루어진 군으로부터 선택되는 1 종 이상의 색재와, 흑색 안료를 포함하며,The (A) color material includes at least one color material selected from the group consisting of red, blue and purple, and a black pigment,

0.5 내지 3 ㎛의 두께로 막 형성시, 380 nm 내지 780 nm의 스펙트럼 파장에서의 투과율이 80 % 이상인 것을 특징으로 하는, 착색 감광성 수지 조성물을 제공한다.It provides a colored photosensitive resin composition, characterized in that the transmittance at a spectral wavelength of 380 nm to 780 nm is 80% or more when the film is formed to a thickness of 0.5 to 3 μm.

또한, 본 발명은 상기 착색 감광성 수지 조성물을 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자를 제공한다.In addition, the present invention provides a color filter manufactured using the colored photosensitive resin composition and a display device including the color filter.

본 발명의 착색 감광성 수지 조성물, 이를 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자는 우수한 명암비, 색순도 및 반사율 효과를 제공할 수 있고, 저온경화성 및 외광반사방지 효과 역시 우수하여 디스플레이 소자에 있어 편광판을 대체할 수 있으며, 언더 디스플레이 카메라(UDC) 구현에 적합하여, 종래 착색 감광성 수지 조성물의 고색의 회색 재현성 및 공정성 부족 문제를 해결할 수 있다.The colored photosensitive resin composition of the present invention, a color filter manufactured using the same, and a display device including the color filter can provide excellent contrast ratio, color purity, and reflectance effects, and low-temperature curing and external light reflection prevention effects are also excellent. It can replace a polarizing plate in the present invention, and is suitable for implementing an under display camera (UDC), thereby solving the problem of insufficient gray reproducibility and fairness of the conventional colored photosensitive resin composition.

또한, 본 발명에 따른 착색 감광성 수지 조성물, 이를 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자는 0.5 내지 3 ㎛의 두께로 막 형성시, 380 nm 내지 780 nm의 스펙트럼 파장에서의 투과율이 80 % 이상을 가짐으로써, OLED 광원 수명의 과도한 단축을 방지할 수 있고, 광원의 효율을 높일 수 있다.In addition, the color photosensitive resin composition according to the present invention, a color filter manufactured using the same, and a display device including the color filter have transmittance at a spectral wavelength of 380 nm to 780 nm when a film is formed to a thickness of 0.5 to 3 μm. By having this 80% or more, excessive shortening of the lifetime of the OLED light source can be prevented, and the efficiency of the light source can be increased.

본 발명은 우수한 명암비, 색순도 및 반사율 효과를 제공할 수 있고, 저온경화성 및 외광반사방지 효과 역시 우수하여 디스플레이 소자에 있어 편광판을 대체할 수 있으며, 종래 착색 감광성 수지 조성물의 고색의 회색 재현성 및 공정성 부족 문제를 해결하여, 언더 디스플레이 카메라(UDC) 구현에 적합한 착색 감광성 수지 조성물, 이를 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자에 관한 것이다.The present invention can provide excellent contrast ratio, color purity and reflectance effect, and can replace a polarizing plate in a display device due to its excellent low-temperature curing and external light reflection prevention effects, and lack of gray reproducibility and fairness of conventional colored photosensitive resin compositions By solving the problem, a colored photosensitive resin composition suitable for implementing an under display camera (UDC), a color filter manufactured using the same, and a display device including the color filter are provided.

또한, 본 발명은 380 내지 780 nm의 스펙트럼 파장에서의 80 % 이상의 (광)투과율을 가짐으로써, OLED 광원 수명의 과도한 단축을 방지할 수 있고, 광원의 효율을 높일 수 있는 착색 감광성 수지 조성물, 이를 이용하여 제조된 컬러필터 및 상기 컬러필터를 포함하는 디스플레이 소자에 관한 것이다.In addition, the present invention has a (light) transmittance of 80% or more at a spectral wavelength of 380 to 780 nm, thereby preventing excessive shortening of the life of the OLED light source and increasing the efficiency of the light source. It relates to a color filter manufactured by using the color filter and a display device including the color filter.

이하 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.

<착색 감광성 수지 조성물><Colored photosensitive resin composition>

본 발명의 착색 감광성 수지 조성물은 (A) 색재; (B) 알칼리 가용성 수지; (C) 광중합성 화합물; 및 (D) 광중합 개시제를 포함하며, (E) 용제를 더 포함할 ㅅ수 있다.The coloring photosensitive resin composition of this invention is (A) a color material; (B) alkali-soluble resin; (C) a photopolymerizable compound; and (D) a photopolymerization initiator, and (E) a solvent may be further included.

(A) 색재(A) Color material

본 발명의 착색 감광성 수지 조성물은 (A) 색재로 적색 색재, 청색 색재 및 자색 색재로 이루어진 군으로부터 선택되는 1종 이상의 색재와 흑색 안료를 필수적으로 포함한다.The colored photosensitive resin composition of the present invention essentially includes at least one color material selected from the group consisting of a red color material, a blue color material and a purple color material and a black pigment as the color material (A).

구체적으로, 본 발명의 착색 감광성 수지 조성물은 상기 색재와 흑색 안료를혼합하여 사용함으로써, 두께가 0.5 내지 3 ㎛인 막을 형성했을 때, 상기 막의 두께 방향에서 380 내지 780 nm 파장대의 (광)투과율이 80 % 이상일 수 있으며, 반사율이 10 % 이하일 수 있다.Specifically, in the colored photosensitive resin composition of the present invention, when a film having a thickness of 0.5 to 3 μm is formed by mixing the color material and the black pigment, the (light) transmittance in the 380 to 780 nm wavelength band in the thickness direction of the film is It may be 80% or more, and the reflectance may be 10% or less.

또한, 바람직하게 본 발명의 착색 감광성 수지 조성물은, 두께가 0.5 내지 3 ㎛인 막을 형성했을 때, 550 내지 590 nm의 스펙트럼 파장에서의 투과율이 80 % 이상일 수 있다. Preferably, the colored photosensitive resin composition of the present invention may have a transmittance of 80% or more at a spectral wavelength of 550 to 590 nm when a film having a thickness of 0.5 to 3 μm is formed.

종래 착색 감광성 수지 조성물의 경우 투과율을 낮추지 못하여 외광반사율이 지나치게 높거나, 외광반사방지 효과를 주기 위하여 가시광선 파장대 영역인 380 내지 780 nm에서 투과율이 지나치게 낮추어 OLED 광원의 효율이 오히려 감소하고, 광원의 수명이 과도하게 소모되는 문제가 있다.In the case of the conventional colored photosensitive resin composition, the transmittance cannot be lowered, so the external light reflectance is too high, or the transmittance is too low in the visible ray wavelength range of 380 to 780 nm to give an external light reflection prevention effect. There is a problem that the lifespan is excessively consumed.

그러나 본 발명에 따른 착색 감광성 수지 조성물은 편광판을 대체할 수 있을 만큼의 외광반사방지 효과를 제공함과 동시에 80 % 이상의 투과율을 제공함에 따라 디스플레이의 밝기를 유지시킬 수 있으며, 이로 인해 광원의 수명 및 효율을 극대화할 수 있는 장점이 있다.However, the colored photosensitive resin composition according to the present invention provides an anti-reflection effect sufficient to replace a polarizing plate and at the same time provides a transmittance of 80% or more, thereby maintaining the brightness of the display, and thus the lifespan and efficiency of the light source has the advantage of maximizing

적색 색재, 청색 색재 및/또는 자색 색재Red colorant, blue colorant and/or purple colorant

상기 색재는 안료 및 염료 중 하나 이상을 포함할 수 있다.The color material may include at least one of a pigment and a dye.

상기 안료로는 구체적으로 색지수(The society of Dyers and Colourists 출판)에서 피그먼트로 분류되어 있는 화합물을 들 수 있고, 보다 구체적으로는 이하와 같은 색지수(C.I.) 번호의 안료인 것이 바람직하지만, 반드시 이들로 한정되는 것은 아니다.Specifically, the pigment may include a compound classified as a pigment in the color index (published by The Society of Dyers and Colorists), and more specifically, a pigment having the following color index (C.I.) number is preferable, It is not necessarily limited to these.

그러나, 녹색과 황색 색재의 경우 본 발명에 따른 적색 색재, 청색 색재 또는 자색 색재에 비하여 반사율이 떨어지고, 또한 파장이 평탄(Flat)하지 않은 문제가 발생할 수 있음을 실험을 통해 확인하였다.However, in the case of green and yellow color materials, it was confirmed through experiments that the reflectance was lower than that of the red color material, the blue color material or the purple color material according to the present invention, and also the problem that the wavelength was not flat may occur.

본 발명에 포함되는 적색 색재는 적색 안료 및 적색 염료 중 하나 이상을 포함할 수 있다.The red color material included in the present invention may include at least one of a red pigment and a red dye.

본 발명의 적색 안료로는, 예를 들어, C.I. 피그먼트 레드 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 215, 216, 224, 242, 254, 255 및 264로 이루어진 군으로부터 선택되는 1종 이상일 수 있으며, C.I. 피그먼트 레드 179, C.I. 피그먼트 레드 177, C.I. 피그먼트 레드 209, C.I. 피그먼트 레드 242 및 C.I. 피그먼트 레드 254가 바람직하다.As the red pigment of the present invention, for example, C.I. Pigment Red 9, 97, 105, 122, 123, 144, 149, 166, 168, 176, 177, 180, 192, 215, 216, 224, 242, 254, one selected from the group consisting of 255 and 264 or more, and C.I. Pigment Red 179, C.I. Pigment Red 177, C.I. Pigment Red 209, C.I. Pigment Red 242 and C.I. Pigment Red 254 is preferred.

본 발명의 적색 염료로는, 예를 들어, C.I. 솔벤트 염료로서, C.I. 솔벤트 레드 8, 45, 49, 89, 111, 122, 125, 130, 132, 146 및 179 등;As the red dye of the present invention, for example, C.I. As a solvent dye, C.I. solvent red 8, 45, 49, 89, 111, 122, 125, 130, 132, 146 and 179 and the like;

C.I. 애시드 염료로서, C.I.애시드 레드 1, 4, 8, 14, 17, 18, 26, 27, 29, 31, 34, 35, 37, 42, 44, 50, 51, 52, 57, 66, 73, 80, 87, 88, 91, 92, 94, 97, 103, 111, 114, 129, 133, 134, 138, 143, 145, 150, 151, 158, 176, 182, 183, 198, 206, 211, 215, 216, 217, 227, 228, 249, 252, 257, 258, 260, 261, 266, 268, 270, 274, 277, 280, 281, 195, 308, 312, 315, 316, 339, 341, 345, 346, 349, 382, 383, 394, 401, 412, 417, 418, 422 및 426 등;C.I. As an acid dye, C.I. Acid Red 1, 4, 8, 14, 17, 18, 26, 27, 29, 31, 34, 35, 37, 42, 44, 50, 51, 52, 57, 66, 73, 80 , 87, 88, 91, 92, 94, 97, 103, 111, 114, 129, 133, 134, 138, 143, 145, 150, 151, 158, 176, 182, 183, 198, 206, 211, 215 , 216, 217, 227, 228, 249, 252, 257, 258, 260, 261, 266, 268, 270, 274, 277, 280, 281, 195, 308, 312, 315, 316, 339, 341, 345 , 346, 349, 382, 383, 394, 401, 412, 417, 418, 422 and 426 and the like;

C.I.다이렉트 염료로서, C.I.다이렉트 레드 79, 82, 83, 84, 91, 92, 96, 97, 98, 99, 105, 106, 107, 172, 173, 176, 177, 179, 181, 182, 184, 204, 207, 211, 213, 218, 220, 221, 222, 232, 233, 234, 241, 243, 246 및 250 등;As a C.I. Direct dye, C.I. Direct Red 79, 82, 83, 84, 91, 92, 96, 97, 98, 99, 105, 106, 107, 172, 173, 176, 177, 179, 181, 182, 184, 204, 207, 211, 213, 218, 220, 221, 222, 232, 233, 234, 241, 243, 246 and 250, and the like;

C.I. 모단토 염료로서, C.I.모단토 레드 1, 2, 3, 4, 9, 11, 12, 14, 17, 18, 19, 22, 23, 24, 25, 26, 30, 32, 33, 36, 37, 38, 39, 41, 43, 45, 46, 48, 53, 56, 63, 71, 74, 85, 86, 88, 90, 94 및 95; 등의 염료를 들 수 있다.C.I. As a modanto dye, C.I. modanto red 1, 2, 3, 4, 9, 11, 12, 14, 17, 18, 19, 22, 23, 24, 25, 26, 30, 32, 33, 36, 37 , 38, 39, 41, 43, 45, 46, 48, 53, 56, 63, 71, 74, 85, 86, 88, 90, 94 and 95; Dyes, such as these are mentioned.

본 발명의 적색 색재로 바람직하게는, C.I. 피그먼트 레드 177, C.I. 피그먼트 레드 179, C.I. 피그먼트 레드 209, C.I. 피그먼트 레드 242 및 C.I. 피그먼트 레드 254로 이루어진 군으로부터 선택되는 1종 이상을 포함할 수 있다. Preferably, as the red color material of the present invention, C.I. Pigment Red 177, C.I. Pigment Red 179, C.I. Pigment Red 209, C.I. Pigment Red 242 and C.I. It may include one or more selected from the group consisting of Pigment Red 254.

본 발명에 포함되는 청색 색재는 청색 안료 및 청색 염료 중 하나 이상을 포함할 수 있다.The blue color material included in the present invention may include at least one of a blue pigment and a blue dye.

본 발명의 청색 안료로는, 예를 들어, C.I. 피그먼트 블루 15(15:3, 15:4, 15:6 등), 21, 28, 60, 64 및 76으로 군으로부터 선택되는 1종 이상일 수 있으며, 그 중에서도C.I. 피그먼트 블루 15:3, C.I. 피그먼트 블루 15:4, C.I. 피그먼트 블루 15:6, C.I. 피그먼트 블루 16, C.I. 피그먼트 블루 21, C.I. 피그먼트 블루 28, C.I. 피그먼트 블루 60, C.I. 피그먼트 블루 64 및 C.I. 피그먼트 블루 76이 바람직하다.As the blue pigment of the present invention, for example, C.I. Pigment Blue 15 (15:3, 15:4, 15:6, etc.), 21, 28, 60, 64 and 76 may be at least one selected from the group, among which C.I. Pigment Blue 15:3, C.I. Pigment Blue 15:4, C.I. Pigment Blue 15:6, C.I. Pigment Blue 16, C.I. Pigment Blue 21, C.I. Pigment Blue 28, C.I. Pigment Blue 60, C.I. Pigment Blue 64 and C.I. Pigment Blue 76 is preferred.

본 발명의 청색 염료로는, 예를 들어, C.I. 솔벤트 염료로서, C.I. 솔벤트 블루 35, 37, 59 및 67 등;As the blue dye of the present invention, for example, C.I. As a solvent dye, C.I. solvent blue 35, 37, 59 and 67, etc.;

C.I. 애시드 염료로서, C.I.애시드 블루 1, 7, 9, 15, 18, 23, 25, 27, 29, 40, 42, 45, 51, 62, 70, 74, 80, 83, 86, 87, 90, 92, 96, 103, 112, 113, 120, 129, 138, 147, 150, 158, 171, 182, 192, 210, 242, 243, 256, 259, 267, 278, 280, 285, 290, 296, 315, 324:1, 335 및 340 등;C.I. As an acid dye, C.I. Acid Blue 1, 7, 9, 15, 18, 23, 25, 27, 29, 40, 42, 45, 51, 62, 70, 74, 80, 83, 86, 87, 90, 92 , 96, 103, 112, 113, 120, 129, 138, 147, 150, 158, 171, 182, 192, 210, 242, 243, 256, 259, 267, 278, 280, 285, 290, 296, 315 , 324:1, 335 and 340 and the like;

C.I.다이렉트 염료로서, C.I.다이렉트 블루 38, 44, 57, 70, 77, 80, 81, 84, 85, 86, 90, 93, 94, 95, 97, 98, 99, 100, 101, 106, 107, 108, 109, 113, 114, 115, 117, 119, 137, 149, 150, 153, 155, 156, 158, 159, 160, 161, 162, 163, 164, 166, 167, 170, 171, 172, 173, 188, 189, 190, 192, 193, 194, 196, 198, 199, 200, 207, 209, 210, 212, 213, 214, 222, 228, 229, 237, 238, 242, 243, 244, 245, 247, 248, 250, 251, 252, 256, 257, 259, 260, 268, 274, 275 및 293 등;As a C.I. Direct dye, C.I. Direct Blue 38, 44, 57, 70, 77, 80, 81, 84, 85, 86, 90, 93, 94, 95, 97, 98, 99, 100, 101, 106, 107, 108, 109, 113, 114, 115, 117, 119, 137, 149, 150, 153, 155, 156, 158, 159, 160, 161, 162, 163, 164, 166, 167, 170, 171, 172, 173, 188, 189, 190, 192, 193, 194, 196, 198, 199, 200, 207, 209, 210, 212, 213, 214, 222, 228, 229, 237, 238, 242, 243, 244, 245, 247, 248, 250, 251, 252, 256, 257, 259, 260, 268, 274, 275 and 293, and the like;

C.I. 모단토 염료로서, C.I.모단토 블루 1, 2, 3, 7, 8, 9, 12, 13, 15, 16, 19, 20, 21, 22, 23, 24, 26, 30, 31, 32, 39, 40, 41, 43, 44, 48, 49, 53, 61, 74, 77, 83 및 84 등을 들 수 있다.C.I. As a modanto dye, C.I. modanto blue 1, 2, 3, 7, 8, 9, 12, 13, 15, 16, 19, 20, 21, 22, 23, 24, 26, 30, 31, 32, 39 , 40, 41, 43, 44, 48, 49, 53, 61, 74, 77, 83 and 84.

본 발명의 청색 색재로 바람직하게는, C.I. 피그먼트 블루 15:3, C.I. 피그먼트 블루 15:4, C.I. 피그먼트 블루 15:6, C.I. 피그먼트 블루 16, C.I. 피그먼트 블루 21, C.I. 피그먼트 블루 28, C.I. 피그먼트 블루 60, C.I. 피그먼트 블루 64 및 C.I. 피그먼트 블루 76으로 이루어진 군으로부터 선택되는 1종 이상을 포함할 수 있다. Preferably, as the blue color material of the present invention, C.I. Pigment Blue 15:3, C.I. Pigment Blue 15:4, C.I. Pigment Blue 15:6, C.I. Pigment Blue 16, C.I. Pigment Blue 21, C.I. Pigment Blue 28, C.I. Pigment Blue 60, C.I. Pigment Blue 64 and C.I. It may include one or more selected from the group consisting of Pigment Blue 76.

본 발명에 포함되는 자색 색재는 자색 안료 및 자색 염료 중 하나 이상을 포함할 수 있다.The purple color material included in the present invention may include at least one of a purple pigment and a purple dye.

본 발명의 자색 안료로는, 예를 들어, C.I. 피그먼트 바이올렛 14, 19, 23, 32, 33, 36 및 38로 이루어진 군으로부터 선택되는 1종 이상일 수 있으며, C.I. 피그먼트 바이올렛 14, C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 바이올렛 29, C.I. 피그먼트 바이올렛 32, C.I. 피그먼트 바이올렛 33, C.I. 피그먼트 바이올렛 36, C.I. 피그먼트 바이올렛 37 및 C.I. 피그먼트 바이올렛 38가 바람직하다.As the purple pigment of the present invention, for example, C.I. Pigment Violet may be at least one selected from the group consisting of 14, 19, 23, 32, 33, 36 and 38, and C.I. Pigment Violet 14, C.I. Pigment Violet 19, C.I. Pigment Violet 23, C.I. Pigment Violet 29, C.I. Pigment Violet 32, C.I. Pigment Violet 33, C.I. Pigment Violet 36, C.I. Pigment Violet 37 and C.I. Pigment Violet 38 is preferred.

본 발명의 자색 염료로는, 예를 들어, C.I. 애시드 염료로서, C.I.애시드 바이올렛 6B, 7, 9, 17 및 19 등;As the purple dye of the present invention, for example, C.I. As acid dyes, C.I. Acid Violet 6B, 7, 9, 17 and 19, etc.;

C.I.다이렉트 염료로서, C.I.다이렉트 바이올렛 47, 52, 54, 59, 60, 65, 66, 79, 80, 81, 82, 84, 89, 90, 93, 95, 96, 103 및 104 등;As a C.I. direct dye, C.I. Direct Violet 47, 52, 54, 59, 60, 65, 66, 79, 80, 81, 82, 84, 89, 90, 93, 95, 96, 103 and 104 and the like;

C.I. 모단토 염료로서, C.I.모단토 바이올렛 1, 2, 4, 5, 7, 14, 22, 24, 30, 31, 32, 37, 40, 41, 44, 45, 47, 48, 53 및 58 등을 들 수 있다.C.I. As modanto dye, C.I. modanto violet 1, 2, 4, 5, 7, 14, 22, 24, 30, 31, 32, 37, 40, 41, 44, 45, 47, 48, 53 and 58, etc. can be heard

본 발명의 자색 색재로 바람직하게는 C.I. 피그먼트 바이올렛 14, C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 바이올렛 29, C.I. 피그먼트 바이올렛 32, C.I. 피그먼트 바이올렛 33, C.I. 피그먼트 바이올렛 36, C.I. 피그먼트 바이올렛 37 및 C.I. 피그먼트 바이올렛 38로 이루어진 군으로부터 선택되는 1종 이상을 포함할 수 있다. As the purple colorant of the present invention, preferably C.I. Pigment Violet 14, C.I. Pigment Violet 19, C.I. Pigment Violet 23, C.I. Pigment Violet 29, C.I. Pigment Violet 32, C.I. Pigment Violet 33, C.I. Pigment Violet 36, C.I. Pigment Violet 37 and C.I. It may include one or more selected from the group consisting of Pigment Violet 38.

상기 적색 색재, 청색 색재 및/또는 자색 색재는 본 발명의 착색 감광성 수지 조성물 총 중량에 대하여 0.1 내지 3 중량%, 바람직하게는 0.3 내지 1.2 중량%으로 포함될 수 있다. 상기 범위로 포함되는 경우, 외광 반사 방지 효과와 시인성 측면에서 유리하고 투과율 80 % 이상 및 반사율 10% 이하를 유지할 수 있다. 그러나, 상기 범위를 초과하여 포함되는 경우, 반사율을 떨어지고, 단파장 투과율이 증가하여 평탄(Flat)한 투과스펙트럼을 형성하기 어려운 문제가 발생할 수 있다.The red color material, blue color material and/or purple color material may be included in an amount of 0.1 to 3 wt%, preferably 0.3 to 1.2 wt%, based on the total weight of the colored photosensitive resin composition of the present invention. When included in the above range, it is advantageous in terms of an external light reflection prevention effect and visibility, and can maintain a transmittance of 80% or more and a reflectance of 10% or less. However, when it is included in excess of the above range, it may be difficult to form a flat transmission spectrum due to a decrease in reflectance and an increase in short-wavelength transmittance.

흑색 안료black pigment

본 발명의 색재에 포함되는 흑색 안료는 가시광 파장대의 광을 흡수하기 위하여 사용될 수 있다.The black pigment included in the color material of the present invention may be used to absorb light in the visible wavelength band.

상기 흑색 안료는 흑색 유기 안료를 단독으로 사용하거나, 흑색 유기 안료와 흑색 무기 안료를 혼합하여 사용할 수 있다. 흑색 유기 안료를 포함하는 경우, 착색 감광성 수지 조성물의 보다 낮은 유전율을 가지기 때문에 바람직하다. 또한, 흑색 무기 안료만을 단독으로 포함하는 경우, 흑색 유기 안료에 비하여 유전율이 높기 때문에 절연막 생성에 문제가 발생할 수 있어, 바람직하지 않다.As the black pigment, a black organic pigment may be used alone or a black organic pigment and a black inorganic pigment may be mixed. When a black organic pigment is included, since it has a lower dielectric constant of a coloring photosensitive resin composition, it is preferable. In addition, when only the black inorganic pigment is included alone, since the dielectric constant is higher than that of the black organic pigment, a problem may occur in the formation of the insulating film, which is not preferable.

상기 흑색 유기 안료는 적색, 청색 및 녹색 안료를 혼합한 안료, C.I. 피그먼트 블랙 1, C.I. 피그먼트 블랙 7 등의 유기카본 블랙, 락탐 블랙, 페릴렌 블랙, 시아닌 블랙 및 아닐린 블랙으로 이루어진 군에서 선택되는 1종 이상을 사용할 수 있으나, 이에 제한되는 것은 아니다.The black organic pigment is a pigment mixed with red, blue and green pigments, C.I. Pigment Black 1, C.I. At least one selected from the group consisting of organic carbon black such as pigment black 7, lactam black, perylene black, cyanine black, and aniline black may be used, but is not limited thereto.

상기 적색 색재, 청색 색재 및 자색 색재로 이루어진 군으로부터 선택되는 1종 이상의 색재와 흑색 안료의 중량비는 0.4:0.6 내지 0.1:0.9 일 수 있다. 흑색 안료의 함량이 증가하는 경우 반사율 측면에서 유리하나, 투과율이 저하되는 문제가 나타날 수 있기에 색재와 흑색 안료의 중량비를 상기 중량비 범위로 포함하는 경우, 감소된 투과율을 높여줌과 동시에 전파장 영역에서 굴곡이 있지 않은 평탄한 투과율을 갖는 파장을 생성할 수 있어 바람직하다.The weight ratio of the at least one color material selected from the group consisting of the red color material, the blue color material, and the purple color material to the black pigment may be 0.4:0.6 to 0.1:0.9. When the content of the black pigment is increased, it is advantageous in terms of reflectance, but a problem of a decrease in transmittance may occur. It is preferable because it is possible to generate a wavelength having a flat transmittance that is not there.

상기 (A) 색재는 본 발명의 착색 감광성 수지 조성물 총 중량에 대하여 0.1 내지 3 중량%으로 포함될 수 있다. 상기 범위로 포함되는 경우, 외광 반사 방지 효과와 시인성 측면에서 유리하고 투과율 80 %이상 유지할 수 있다. 색재가 3 중량%을 초과하여 포함되는 경우, 투과율 저하 문제가 발생하여 화면의 밝기를 저하 시키게 된다.The (A) colorant may be included in an amount of 0.1 to 3% by weight based on the total weight of the colored photosensitive resin composition of the present invention. When included in the above range, it is advantageous in terms of an external light reflection prevention effect and visibility, and a transmittance of 80% or more can be maintained. When the color material is included in excess of 3 wt%, a problem of lowering transmittance occurs, thereby lowering the brightness of the screen.

추가 안료 또는 염료additional pigments or dyes

본 발명에 따른 (A) 색재는 본 발명의 목적을 해치지 않는 범위 내에서 당 분야에 통상적으로 사용되는 유기 안료, 무기 안료, 염료 등을 더 포함할 수 있다.(A) color material according to the present invention may further include organic pigments, inorganic pigments, dyes, etc. commonly used in the art within a range that does not impair the object of the present invention.

유기 안료로는 인쇄 잉크, 잉크젯 잉크 등에 사용되는 각종의 안료를 사용할 수 있으며, 구체적으로는 수용성 아조 안료, 불용성 아조 안료, 프탈로시아닌 안료, 퀴나크리돈 안료, 이소인돌리논 안료, 이소인돌린 안료, 페리렌 안료, 페리논 안료, 디옥사진 안료, 안트라퀴논 안료, 디안트라퀴노닐 안료, 안트라피리미딘 안료, 안탄트론 (anthanthrone) 안료, 인단트론 (indanthrone) 안료, 프라반트론 안료, 피란트론 (pyranthrone) 안료 또는 디케토피로로피롤 안료 등을 들 수 있다.As the organic pigment, various pigments used in printing inks, inkjet inks, etc. can be used, and specifically, water-soluble azo pigments, insoluble azo pigments, phthalocyanine pigments, quinacridone pigments, isoindolinone pigments, isoindoline pigments, Perylene pigment, perinone pigment, dioxazine pigment, anthraquinone pigment, dianthraquinonyl pigment, anthrapyrimidine pigment, anthanthrone pigment, indanthrone pigment, pravanthrone pigment, pyranthrone ) pigment or diketopyrroropyrrole pigment.

상기 무기 안료로서는 금속 산화물이나 금속 착염 등의 금속 화합물을 들 수 있고, 구체적으로는 철, 코발트, 알루미늄, 카드뮴, 납, 구리, 티탄, 마그네슘, 크롬, 아연 또는 안티몬 등의 금속의 산화물 또는 복합 금속 산화물 등을 들 수 있다.Examples of the inorganic pigment include metal compounds such as metal oxides and metal complex salts, and specifically, oxides or composite metals of metals such as iron, cobalt, aluminum, cadmium, lead, copper, titanium, magnesium, chromium, zinc or antimony. oxides and the like.

상기 유기 안료 및 무기 안료로는 구체적으로 색지수 (The society of Dyers and Colourists 출판)에서 피그먼트로 분류되어 있는 화합물을 들 수 있고, 보다 구체적으로는 이하와 같은 색지수 (C.I.) 번호의 안료를 들 수 있지만, 반드시 이들로 한정되는 것은 아니다:Examples of the organic and inorganic pigments include compounds classified as pigments in the color index (published by The Society of Dyers and Colorists), and more specifically, pigments having the following color index (C.I.) numbers. include, but are not necessarily limited to:

상기 염료는 유기 용제에 대한 용해성을 가지거나 분산 가능한 것이라면 제한 없이 사용할 수 있다. 바람직하게는 유기 용제에 대한 용해성을 가지면서 알칼리 현상액에 대한 용해성 및 내열성, 내용제성 등의 신뢰성을 확보할 수 있는 염료를 사용하는 것이 바람직하다.The dye may be used without limitation as long as it has solubility in organic solvents or is dispersible. Preferably, it is preferable to use a dye having solubility in an organic solvent and ensuring reliability such as solubility in an alkali developer, heat resistance, and solvent resistance.

상기 염료로는 설폰산이나 카복실산 등의 산성기를 갖는 산성 염료, 산성 염료와 질소 함유 화합물의 염, 산성 염료의 설폰아미드체 등과 이들의 유도체에서 선택된 것을 사용할 수 있으며, 이외에도 아조계, 크산텐계, 프탈로시아닌계의 산성염료 및 이들의 유도체도 선택할 수 있다.As the dye, an acid dye having an acid group such as sulfonic acid or carboxylic acid, a salt of an acid dye and a nitrogen-containing compound, a sulfonamide compound of an acid dye, and derivatives thereof may be used. In addition, azo-based, xanthene-based, phthalocyanine Acid dyes and derivatives thereof can also be selected.

안료 분산제pigment dispersant

상기 안료 분산제는 안료의 탈응집 및 안정성 유지를 위해 첨가되는 것으로서 당해 분야에서 일반적으로 사용되는 것을 제한 없이 사용할 수 있다. 예를 들면, 양이온계, 음이온계, 비이온계, 양성, 폴리에스테르계, 폴리아민계 등의 계면활성제 등을 들 수 있고, 이들은 각각 단독으로 또는 2종 이상을 조합하여 사용할 수 있다.The pigment dispersant is added for deagglomeration and stability of the pigment, and those generally used in the art may be used without limitation. For example, surfactants, such as cationic, anionic, nonionic, amphoteric, polyester, polyamine, etc. are mentioned, These can be used individually or in combination of 2 or more types, respectively.

상기 양이온계 계면 활성제의 구체적인 예로는 스테아릴아민 염산염 및 라우릴트리메틸암모늄클로라이드 등의 아민염 또는 4급 암모늄염 등을 들 수 있다.Specific examples of the cationic surfactant include amine salts such as stearylamine hydrochloride and lauryltrimethylammonium chloride, or quaternary ammonium salts.

상기 음이온계 계면 활성제의 구체적인 예로는 라우릴알코올 황산에스테르나트륨 및 올레일알코올 황산에스테르나트륨 등의 고급 알코올 황산에스테르염류, 라우릴황산나트륨 및 라우릴황산암모늄 등의 알킬황산염류, 도데실벤젠술폰산나트륨 및 도데실나프탈렌술폰산나트륨 등의 알킬아릴술폰산염류 등을 들 수 있다.Specific examples of the anionic surfactant include higher alcohol sulfate ester salts such as sodium lauryl alcohol sulfate ester and sodium oleyl alcohol sulfate ester, alkyl sulfates such as sodium lauryl sulfate and ammonium lauryl sulfate, sodium dodecylbenzenesulfonate and Alkyl aryl sulfonates, such as sodium dodecyl naphthalene sulfonate, etc. are mentioned.

상기 비이온계 계면 활성제의 구체적인 예로는 폴리옥시에틸렌 알킬에테르, 폴리옥시에틸렌 아릴에테르, 폴리옥시에틸렌 알킬아릴에테르, 그 밖의 폴리옥시에틸렌 유도체, 옥시에틸렌/옥시프로필렌 블록 공중합체, 소르비탄지방산 에스테르, 폴리옥시에틸렌 소르비탄지방산에스테르, 폴리옥시에틸렌 소르비톨지방산에스테르, 글리세린지방산에스테르, 폴리옥시에틸렌 지방산에스테르 및 폴리옥시에틸렌 알킬아민 등을 들 수 있다.Specific examples of the nonionic surfactant include polyoxyethylene alkyl ether, polyoxyethylene aryl ether, polyoxyethylene alkyl aryl ether, other polyoxyethylene derivatives, oxyethylene/oxypropylene block copolymer, sorbitan fatty acid ester, Polyoxyethylene sorbitan fatty acid ester, polyoxyethylene sorbitol fatty acid ester, glycerol fatty acid ester, polyoxyethylene fatty acid ester, polyoxyethylene alkylamine, etc. are mentioned.

그 외에 폴리옥시에틸렌 알킬에테르류, 폴리옥시에틸렌 알킬페닐에테르류, 폴리에틸렌글리콜 디에스테르류, 소르비탄지방산 에스테르류, 지방산변성 폴리에스테르류, 3급아민변성 폴리우레탄류 및 폴리에틸렌 이민류 등을 들 수 있다.Other examples include polyoxyethylene alkyl ethers, polyoxyethylene alkylphenyl ethers, polyethylene glycol diesters, sorbitan fatty acid esters, fatty acid-modified polyesters, tertiary amine-modified polyurethanes, and polyethylene imines. have.

또한, 상기 안료 분산제는 부틸메타아크릴레이트(BMA) 또는 N,N-디메틸아미노에틸메타아크릴레이트(DMAEMA)를 포함하는 아크릴레이트계 분산제 (이하, 아크릴레이트계 분산제)를 포함하는 것이 바람직하다. 상기 아크릴레이트계 분산제는 리빙 제어방법에 의해 제조된 것을 사용하는 것이 바람직하며, 시판품으로는 DISPER BYK-2000, DISPER BYK-2001, DISPER BYK-2070 또는 DISPER BYK-2150 등을 들 수 있으며, 상기 아크릴레이트계 분산제는 각각 단독 또는 2종 이상을 혼합하여 사용할 수 있다.In addition, the pigment dispersant preferably includes an acrylate-based dispersant (hereinafter, acrylate-based dispersant) including butyl methacrylate (BMA) or N,N-dimethylaminoethyl methacrylate (DMAEMA). It is preferable to use the acrylate-based dispersant prepared by the living control method, and commercially available products include DISPER BYK-2000, DISPER BYK-2001, DISPER BYK-2070 or DISPER BYK-2150. The rate-based dispersant may be used alone or in combination of two or more.

상기 안료 분산제는 아크릴레이트계 분산제 이외에 다른 수지 타입의 안료 분산제를 사용할 수도 있다. 상기 다른 수지 타입의 안료 분산제로는 공지된 수지 타입의 안료 분산제, 특히 폴리우레탄, 폴리아크릴레이트로 대표되는 폴리카르복실산에스테르, 불포화폴리아미드, 폴리카르복실산, 폴리카르복실산의 (부분적)아민 염, 폴리카르복실산의 암모늄 염, 폴리카르복실산의 알킬아민 염, 폴리실록산, 장쇄 폴리아미노아미드 포스페이트 염, 히드록실기-함 폴리카르복실산의 에스테르 및 이들의 개질 생성물, 또는 프리(free) 카르복실기를 갖는 폴리에스테르와 폴리(저급 알킬렌이민)의 반응에 의해 형성된 아미드 또는 이들의 염과 같은 유질의 분산제; (메트)아크릴산-스티렌 코폴리머, (메트)아크릴산-(메트)아크릴레이트 에스테르 코폴리머, 스티렌-말레산 코폴리머, 폴리비닐 알코올 또는 폴리비닐 피롤리돈과 같은 수용성 수지 또는 수용성 폴리머 화합물; 폴리에스테르; 개질 폴리아크릴레이트; 에틸렌 옥사이드/프로필렌 옥사이드의 부가생성물; 및 포스페이트 에스테르 등을 들 수 있다.As the pigment dispersant, a pigment dispersant of a resin type other than the acrylate-based dispersant may be used. The pigment dispersants of the other resin types include known resin type pigment dispersants, in particular polyurethane, polycarboxylic acid esters typified by polyacrylates, unsaturated polyamides, polycarboxylic acids, polycarboxylic acids (partially) amine salts, ammonium salts of polycarboxylic acids, alkylamine salts of polycarboxylic acids, polysiloxanes, long-chain polyaminoamide phosphate salts, esters of hydroxyl-containing polycarboxylic acids and modified products thereof, or free ) oily dispersants such as amides or salts thereof formed by the reaction of a polyester having a carboxyl group with poly (lower alkyleneimine); water-soluble resins or water-soluble polymer compounds such as (meth)acrylic acid-styrene copolymer, (meth)acrylic acid-(meth)acrylate ester copolymer, styrene-maleic acid copolymer, polyvinyl alcohol or polyvinyl pyrrolidone; Polyester; modified polyacrylates; adducts of ethylene oxide/propylene oxide; and phosphate esters.

상기 다른 수지타입의 안료 분산제의 시판품으로는 양이온계 수지 분산제로서는, 예를 들면, BYK(빅) 케미사의 상품명: DISPER BYK-160, DISPER BYK-161, DISPER BYK-162,DISPER BYK-163, DISPER BYK-164, DISPER BYK-166, DISPER BYK-171, DISPER BYK-182,DISPER BYK-184; BASF사의 상품명: EFKA-44, EFKA-46, EFKA-47, EFKA-48,EFKA-4010, EFKA-4050, EFKA-4055, EFKA-4020, EFKA-4015, EFKA-4060, EFKA-4300, EFKA-4330, EFKA-4400, EFKA-4406, EFKA-4510, EFKA-4800 ; Lubrizol사의 상품명:SOLSPERS-24000, SOLSPERS-32550, NBZ-4204 /10; 카와켄 파인 케미컬사의 상품명: 히노액트(HINOACT) T-6000, 히노액트 T-7000, 히노액트 T-8000; 아지노모토사의 상품명: 아지스퍼(AJISPUR) PB-821, 아지스퍼 PB-822, 아지스퍼 PB-823; 쿄에이샤 화학사의 상품명: 플로렌 (FLORENE) DOPA-17HF, 플로렌 DOPA-15BHF, 플로렌 DOPA-33, 플로렌 DOPA-44 등을 들 수 있다.As a commercially available product of the above-mentioned other resin type pigment dispersant, as a cationic resin dispersant, for example, BYK (Big) Chemi Corporation's trade names: DISPER BYK-160, DISPER BYK-161, DISPER BYK-162, DISPER BYK-163, DISPER BYK-164, DISPER BYK-166, DISPER BYK-171, DISPER BYK-182, DISPER BYK-184; BASF trade names: EFKA-44, EFKA-46, EFKA-47, EFKA-48, EFKA-4010, EFKA-4050, EFKA-4055, EFKA-4020, EFKA-4015, EFKA-4060, EFKA-4300, EFKA- 4330, EFKA-4400, EFKA-4406, EFKA-4510, EFKA-4800; Trade names from Lubrizol: SOLSPERS-24000, SOLSPERS-32550, NBZ-4204/10; Kawaken Fine Chemicals' trade names: HINOACT T-6000, HINOACT T-7000, HINOACT T-8000; Trade names of Ajinomoto Corporation: AJISPUR PB-821, AJISPUR PB-822, AJISPUR PB-823; Trade names of Kyoeisha Chemical Corporation: FLORENE DOPA-17HF, fluorene DOPA-15BHF, fluorene DOPA-33, fluorene DOPA-44, etc. are mentioned.

상기 아크릴레이트계 분산제 이외에 다른 수지 타입의 안료 분산제는 각각 단독 또는 2종 이상을 혼합하여 사용할 수 있으며, 아크릴레이트계 분산제와 병용하여 사용할 수도 있다.In addition to the acrylate-based dispersant, other resin-type pigment dispersants may be used alone or in combination of two or more, or may be used in combination with an acrylate-based dispersant.

상기 안료 분산제는 상기 색재 고형분 100 중량부에 대하여 1 내지 50 중량부, 바람직하게는 5 내지 30 중량부로 포함될 수 있다. 안료 분산제의 함량이 상기 범위 내인 경우 균일한 입경의 분산된 안료를 얻을 수 있기 때문에 바람직하다. 분산제의 함량이 50 중량부 초과이면 점도가 높아질 수 있으며, 1 중량부 미만이면 안료의 미립화가 어렵거나, 분산 후 겔화 등의 문제를 야기할 수 있다.The pigment dispersant may be included in an amount of 1 to 50 parts by weight, preferably 5 to 30 parts by weight, based on 100 parts by weight of the colorant solid content. When the content of the pigment dispersant is within the above range, it is preferable because it is possible to obtain a dispersed pigment having a uniform particle size. If the content of the dispersant is more than 50 parts by weight, the viscosity may increase, and if it is less than 1 part by weight, it may be difficult to atomize the pigment, or it may cause problems such as gelation after dispersion.

(B) 알칼리 가용성 수지(B) alkali-soluble resin

알칼리 가용성 수지는 현상 공정에서 이용되는 알칼리 현상액에 대해서 가용성을 부여하는 성분으로 알칼리 현상액에 용해 가능하다면 제한 없이 사용 가능하다. 상기 알칼리 가용성 수지는 패턴을 형성할 때의 현상 처리 공정에서 이용되는 알칼리 현상액에 대해서 가용성을 가지고, 저온경화성 특성을 향상시키기 위해, (b1) 카르복실기를 갖는 에틸렌성 불포화 단량체를 공중합하여 제조하는 것이 바람직하다.The alkali-soluble resin is a component that imparts solubility to the alkali developer used in the developing process, and can be used without limitation as long as it can be dissolved in the alkali developer. The alkali-soluble resin has solubility with respect to the alkali developer used in the developing process at the time of forming the pattern, and in order to improve low-temperature curability characteristics, it is preferable to prepare by copolymerizing (b1) an ethylenically unsaturated monomer having a carboxyl group. do.

상기 알칼리 가용성 수지의 산가는 30 내지 200 mgKOH/g인 것이 바람직하다. 알칼리 가용성 수지의 산가가 30 mgKOH/g 미만인 경우 감광성 수지 조성물이 충분한 현상속도를 확보하기 어려우며, 200 mgKOH/g를 초과하는 경우 기판과의 밀착성이 감소되어 패턴의 단락이 발생하기 쉬우며 색재와의 상용성이 문제가 발생하여 감광성 수지 조성물 내의 색재가 석출되거나 감광성 수지 조성물의 저장안정성이 저하되어 점도가 상승하기 쉽다.It is preferable that the acid value of the alkali-soluble resin is 30 to 200 mgKOH/g. If the acid value of the alkali-soluble resin is less than 30 mgKOH/g, it is difficult for the photosensitive resin composition to secure a sufficient development speed. The compatibility problem occurs, the color material in the photosensitive resin composition is precipitated, or the storage stability of the photosensitive resin composition is lowered, and the viscosity tends to increase.

상기 알칼리 가용성 수지의 중량 평균 분자량(예를 들면, 표준 물질로서 폴리스티렌을 사용하여 겔 침투 크로마토그래피(GPC)로 측정)은 약 3,000 내지 50,000, 바람직하게는 5,000 내지 30,000일 수 있다. 상기 분자량 범위 내에서 현상 공정에서의 막 손실이 억제되고 및 패턴 안정성이 향상될 수 있다.The weight average molecular weight of the alkali-soluble resin (eg, measured by gel permeation chromatography (GPC) using polystyrene as a standard material) may be about 3,000 to 50,000, preferably 5,000 to 30,000. Within the molecular weight range, film loss in the developing process may be suppressed and pattern stability may be improved.

(b1) 카르복실기를 갖는 에틸렌성 불포화 단량체(b1) an ethylenically unsaturated monomer having a carboxyl group

카르복실기를 갖는 에틸렌성 불포화 단량체의 구체적인 예로는 아크릴산, 메타아크릴산, 크로톤산 등의 모노카르복실산류; 푸마르산, 메사콘산, 이타콘산 등의 디카르복실산류; 및 상기 디카르복실산의 무수물; ω-카르복시폴리카프로락톤모노(메타)아크릴레이트 등의 양 말단에 카르복실기와 수산기를 갖는 폴리머의 모노(메타)아크릴레이트류 등을 들 수 있으며, 아크릴산 및 메타아크릴산이 바람직하다.Specific examples of the ethylenically unsaturated monomer having a carboxyl group include monocarboxylic acids such as acrylic acid, methacrylic acid, and crotonic acid; dicarboxylic acids such as fumaric acid, mesaconic acid, and itaconic acid; and an anhydride of said dicarboxylic acid; Polymer mono(meth)acrylates having a carboxyl group and a hydroxyl group at both terminals, such as ω-carboxypolycaprolactone mono(meth)acrylate, etc. are mentioned, and acrylic acid and methacrylic acid are preferable.

또한, 상기 카르복실기를 갖는 에틸렌성 불포화 단량체와 (b2) 공중합 가능한 불포화 단량체를 중합하여 상기 알칼리 가용성 수지를 제조할 수 있다.In addition, the alkali-soluble resin may be prepared by polymerizing the ethylenically unsaturated monomer having a carboxyl group and an unsaturated monomer copolymerizable with (b2).

(b2) 공중합 가능한 불포화 단량체(b2) copolymerizable unsaturated monomers

상기 공중합이 가능한 불포화 중합 단량체의 구체적인 예로는,Specific examples of the copolymerizable unsaturated polymerization monomer include,

글리시딜기를 갖는 불포화 단량체인 글리시딜메타아크릴레이트;glycidyl methacrylate which is an unsaturated monomer having a glycidyl group;

2-히드록시에틸(메타)아크릴레이트, 2-히드록시프로필(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 2-히드록시-3-페녹시프로필 (메타)아크릴레이트, N-히드록시에틸 아크릴아마이드 등의 히드록시에틸(메타)아크릴레이트류 등의 수산기를 갖는 에틸렌성 불포화 단량체;2-hydroxyethyl (meth) acrylate, 2-hydroxypropyl (meth) acrylate, 4-hydroxybutyl (meth) acrylate, 2-hydroxy-3-phenoxypropyl (meth) acrylate, N -ethylenically unsaturated monomers having a hydroxyl group such as hydroxyethyl (meth)acrylates such as hydroxyethyl acrylamide;

스티렌, 비닐톨루엔, α-메틸스티렌, p-클로로스티렌, o-메톡시스티렌, m-메톡시스티렌, p-메톡시스티렌, o-비닐벤질메틸에테르, m-비닐벤질메틸에테르, p-비닐벤질메틸에테르, o-비닐벤질글리시딜에테르, m-비닐벤질글리시딜에테르, p-비닐벤질글리시딜에테르 등의 방향족 비닐 화합물;Styrene, vinyltoluene, α-methylstyrene, p-chlorostyrene, o-methoxystyrene, m-methoxystyrene, p-methoxystyrene, o-vinylbenzylmethyl ether, m-vinylbenzylmethyl ether, p-vinyl aromatic vinyl compounds such as benzyl methyl ether, o-vinyl benzyl glycidyl ether, m-vinyl benzyl glycidyl ether, and p-vinyl benzyl glycidyl ether;

N-시클로헥실말레이미드, N-벤질말레이미드, N-페닐말레이미드, N-o-히드록시페닐말레이미드, N-m-히드록시페닐말레이미드, N-p-히드록시페닐말레이미드, N-o-메틸페닐말레이미드, N-m-메틸페닐말레이미드, N-p-메틸페닐말레이미드, N-o-메톡시페닐말레이미드, N-m-메톡시페닐말레이미드, N-p-메톡시페닐말레이미드 등의 N-치환 말레이미드계 화합물;N-cyclohexylmaleimide, N-benzylmaleimide, N-phenylmaleimide, N-o-hydroxyphenylmaleimide, N-m-hydroxyphenylmaleimide, N-p-hydroxyphenylmaleimide, N-o-methylphenylmaleimide, N-m -N-substituted maleimide compounds, such as methylphenylmaleimide, N-p-methylphenylmaleimide, N-o-methoxyphenylmaleimide, N-m-methoxyphenylmaleimide, and N-p-methoxyphenylmaleimide;

메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, n-프로필(메타)아크릴레이트, i-프로필(메타)아크릴레이트, n-부틸(메타)아크릴레이트, i-부틸(메타)아크릴레이트, sec-부틸(메타)아크릴레이트, t-부틸(메타)아크릴레이트 등의 알킬(메타)아크릴레이트류; 시클로펜틸(메타)아크릴레이트, 시클로헥실(메타)아크릴레이트, 2-메틸시클로헥실(메타)아크릴레이트, 트리시클로[5.2.1.0 2,6 ]데칸-8-일(메타)아크릴레이트, 2-디시클로펜타닐옥시에틸(메타)아크릴레이트, 이소보르닐(메타)아크릴레이트 등의 지환족(메타)아크릴레이트류;Methyl (meth) acrylate, ethyl (meth) acrylate, n-propyl (meth) acrylate, i-propyl (meth) acrylate, n-butyl (meth) acrylate, i-butyl (meth) acrylate, alkyl (meth)acrylates such as sec-butyl (meth)acrylate and t-butyl (meth)acrylate; Cyclopentyl (meth) acrylate, cyclohexyl (meth) acrylate, 2-methylcyclohexyl (meth) acrylate, tricyclo [5.2.1.0 2,6 ] decan-8-yl (meth) acrylate, 2- alicyclic (meth)acrylates such as dicyclopentanyloxyethyl (meth)acrylate and isobornyl (meth)acrylate;

페닐(메타)아크릴레이트, 벤질(메타)아크릴레이트 등의 아릴(메타)아크릴레이트류;aryl (meth)acrylates such as phenyl (meth)acrylate and benzyl (meth)acrylate;

3-(메타크릴로일옥시메틸)옥세탄, 3-(메타크릴로일옥시메틸)-3-에틸옥세탄, 3-(메타크릴로일옥시메틸)-2-트리플루오로메틸옥세탄, 3-(메타크릴로일옥시메틸)-2-페닐옥세탄, 2-(메타크릴로일옥시메틸)옥세탄, 2-(메타크릴로일옥시메틸)-4-트리플루오로메틸옥세탄 등의 불포화 옥세탄 화합물; 등이 있으나, 이에 한정되지 않는다.3-(methacryloyloxymethyl)oxetane, 3-(methacryloyloxymethyl)-3-ethyloxetane, 3-(methacryloyloxymethyl)-2-trifluoromethyloxetane; 3-(methacryloyloxymethyl)-2-phenyloxetane, 2-(methacryloyloxymethyl)oxetane, 2-(methacryloyloxymethyl)-4-trifluoromethyloxetane, etc. of unsaturated oxetane compounds; and the like, but is not limited thereto.

상기 공중합 가능한 불포화 단량체 각각 단독으로 또는 2종 이상을 조합하여 사용할 수 있다.Each of the above copolymerizable unsaturated monomers may be used alone or in combination of two or more.

상기 알칼리 가용성 수지는 착색 감광성 수지 조성물 총 중량에 대하여 10 내지 80 중량%로 포함될 수 있으며, 바람직하게는 15 내지 50 중량%, 보다 바람직하게는 20 내지 30 중량%로 포함될 수 있다. 상기 알칼리 가용성 수지가 상기 범위 내로 포함되는 경우, 현상액에의 용해성이 충분하여 패턴 형성이 용이하며, 현상시에 노광부의 화소 부분의 막 감소가 방지되어 비화소 부분의 누락성이 양호해지므로 바람직하다.The alkali-soluble resin may be included in an amount of 10 to 80% by weight, preferably 15 to 50% by weight, more preferably 20 to 30% by weight based on the total weight of the colored photosensitive resin composition. When the alkali-soluble resin is included within the above range, it is preferable because the solubility in the developer is sufficient to facilitate pattern formation, and the film reduction of the pixel portion of the exposed portion is prevented during development, so that the omission of the non-pixel portion is improved. .

(C) 광중합성 화합물(C) photopolymerizable compound

상기 광중합성 화합물은 하기 (D) 광중합 개시제의 작용으로 중합할 수 있는 화합물로, 단관능 단량체, 2관능 단량체 또는 다관능 단량체를 사용할 수 있으며, 바람직하게는 2관능 이상의 다관능 단량체를 사용할 수 있다.The photopolymerizable compound is a compound that can be polymerized by the action of the photopolymerization initiator (D) below, and may be a monofunctional monomer, a bifunctional monomer or a polyfunctional monomer, and preferably a polyfunctional monomer having a bifunctional or higher function may be used. .

상기 단관능 단량체의 구체적인 예로는, 노닐페닐카르비톨아크릴레이트, 2-히드록시-3-페녹시프로필아크릴레이트, 2-에틸헥실카르비톨아크릴레이트, 2-히드록시에틸 아크릴레이트 또는 N-비닐피롤리돈 등이 있으나, 이에 한정되는 것은 아니다. Specific examples of the monofunctional monomer include nonylphenyl carbitol acrylate, 2-hydroxy-3-phenoxypropyl acrylate, 2-ethylhexyl carbitol acrylate, 2-hydroxyethyl acrylate, or N-vinyl acrylate. Rollidone, and the like, but is not limited thereto.

상기 2관능 단량체의 구체적인 예로는, 1,6-헥산디올디(메타) 아크릴레이트, 에틸렌글리콜디(메타)아크릴레이트, 네오펜틸글리콜디(메타) 아크릴레이트, 트리에틸렌글리콜디(메타)아크릴레이트, 비스페놀 A의 비스(아크릴로일옥시에틸)에테르 또는 3-메틸펜탄디올디(메타)아크릴레이트 등이 있으나, 이에 한정되는 것은 아니다.Specific examples of the bifunctional monomer include 1,6-hexanediol di (meth) acrylate, ethylene glycol di (meth) acrylate, neopentyl glycol di (meth) acrylate, and triethylene glycol di (meth) acrylate. , bis (acryloyloxyethyl) ether of bisphenol A, or 3-methylpentanediol di (meth) acrylate, but is not limited thereto.

상기 다관능 단량체의 구체적인 예로는, 트리메틸올프로판 트리(메타)아크릴레이트, 에톡실레이티드 트리메틸올프로판 트리(메타)아크릴레이트, 프로폭실레이티드 트리메틸올프로판 트리(메타)아크릴레이트, 펜타에리스리톨 트리(메타)아크릴레이트, 펜타에리스리톨 테트라(메타)아크릴레이트, 디펜타에리스리톨 펜타(메타)아크릴레이트, 에톡실레이티드 디펜타에리스리톨 헥사(메타)아크릴레이트, 프로폭실레이티드 디펜타에리스리톨 헥사(메타)아크릴레이트 또는 디펜타에리스리톨 헥사(메타)아크릴레이트 등이 있으나, 이에 한정되는 것은 아니다.Specific examples of the polyfunctional monomer include trimethylolpropane tri(meth)acrylate, ethoxylated trimethylolpropane tri(meth)acrylate, propoxylated trimethylolpropane tri(meth)acrylate, pentaerythritol tri (meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol penta(meth)acrylate, ethoxylated dipentaerythritol hexa(meth)acrylate, propoxylated dipentaerythritol hexa(meth) acrylate or dipentaerythritol hexa(meth)acrylate, but is not limited thereto.

또한, 상기 광중합성 화합물은 착색 감광성 수지 조성물 총 중량에 대하여 5 내지 50 중량%로 포함될 수 있으며, 바람직하게는 7 내지 45 중량%, 보다 바람직하게는 10 내지 20 중량%로 포함될 수 있다. 상기 광중합성 화합물이 상기 범위 내로 포함되는 경우, 화소부의 강도와 평활성이 양호하게 되기 때문에 바람직하다.In addition, the photopolymerizable compound may be included in an amount of 5 to 50% by weight, preferably 7 to 45% by weight, more preferably 10 to 20% by weight based on the total weight of the colored photosensitive resin composition. When the photopolymerizable compound is contained within the above range, it is preferable because the strength and smoothness of the pixel portion are improved.

(D) 광중합 개시제(D) photoinitiator

본 발명에서의 상기 광중합 개시제는 가시광선, 자외선, 원자외선, 전자선, X선 등의 방사선의 노광에 의해, 상기 광중합성 화합물의 중합을 개시할 수 있는 라디칼을 발생하는 화합물이다.The photopolymerization initiator in the present invention is a compound that generates a radical capable of initiating polymerization of the photopolymerizable compound by exposure to radiation such as visible light, ultraviolet light, far ultraviolet light, electron beam, or X-ray.

상기 광중합 개시제는, 예를 들어, 아세토페논계 화합물, 벤조페논계 화합물, 비이미다졸계 화합물, 트리아진계 화합물, 옥심에스테르계 화합물 및 티오크산톤계 화합물 등을 들 수 있다.Examples of the photopolymerization initiator include an acetophenone-based compound, a benzophenone-based compound, a biimidazole-based compound, a triazine-based compound, an oxime ester-based compound, and a thioxanthone-based compound.

본 발명에 있어서, 광중합 개시제는 단독으로 또는 2종 이상을 혼합하여 사용할 수 있으며 옥심에스테르계 화합물을 1종 이상 사용하는 것이 바람직하다.In the present invention, the photopolymerization initiator may be used alone or in mixture of two or more, and it is preferable to use one or more oxime ester compounds.

상기 아세토페논계 화합물의 구체적인 예로는 디에톡시아세토페논, 2-히드록시-2-메틸-1-페닐프로판-1-온, 벤질디메틸케탈, 2-히드록시-1-[4-(2-히드록시에톡시)페닐]-2-메틸프로판-1-온, 1-히드록시시클로헥실페닐케톤, 2-메틸-1-(4-메틸티오페닐)-2-모르폴리노프로판-1-온, 2-벤질-2-디메틸아미노-1-(4-모르폴리노페닐)부탄-1-온, 2-히드록시-2-메틸-1-[4-(1-메틸비닐)페닐]프로판-1-온, 2-(4-메틸벤질)-2-(디메틸아미노)-1-(4-모르폴리노페닐)부탄-1-온 등을 들 수 있다.Specific examples of the acetophenone-based compound include diethoxyacetophenone, 2-hydroxy-2-methyl-1-phenylpropan-1-one, benzyldimethyl ketal, 2-hydroxy-1-[4-(2-hydroxyl) oxyethoxy)phenyl]-2-methylpropan-1-one, 1-hydroxycyclohexylphenylketone, 2-methyl-1-(4-methylthiophenyl)-2-morpholinopropan-1-one; 2-Benzyl-2-dimethylamino-1-(4-morpholinophenyl)butan-1-one, 2-hydroxy-2-methyl-1-[4-(1-methylvinyl)phenyl]propane-1 -one, 2-(4-methylbenzyl)-2-(dimethylamino)-1-(4-morpholinophenyl)butan-1-one, etc. are mentioned.

상기 벤조페논계 화합물로서는, 예를 들면 벤조페논, o-(메톡시카보닐)벤조페논, 4-페닐벤조페논, 4-(4-메틸페닐티오)벤조페논, 3,3',4,4'-테트라(tert-부틸 퍼옥시카보닐)벤조페논, 2,4,6-트리메틸벤조페논 등이 있다.Examples of the benzophenone compound include benzophenone, o-(methoxycarbonyl)benzophenone, 4-phenylbenzophenone, 4-(4-methylphenylthio)benzophenone, 3,3′,4,4′ -tetra(tert-butyl peroxycarbonyl)benzophenone, 2,4,6-trimethylbenzophenone, and the like.

상기 비이미다졸 화합물의 구체적인 예로는 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라페닐-1,2'-비이미다졸, 2,2'-비스(2,3-디클로로페닐)-4,4',5,5'-테트라페닐-1,2'-비이미다졸, 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라(알콕시페닐)-1,2'-비이미다졸, 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라(트리알콕시페닐)-1,2'-비이미다졸, 2,2-비스(2,6-디클로로페닐)-4,4’5,5’-테트라페닐-1,2’-비이미다졸 또는 4,4',5,5' 위치의 페닐기가 카르보알콕시기에 의해 치환되어 있는 이미다졸 화합물 등을 들 수 있다. 이들 중에서 2,2'-비스(2-클로로페닐)-4,4',5,5'-테트라페닐-1,2'-비이미다졸, 2,2'-비스(2,3-디클로로페닐)-4,4',5,5'-테트라페닐-1,2'-비이미다졸, 2,2-비스(2,6-디클로로페닐)-4,4’5,5’-테트라페닐-1,2’-비이미다졸이 바람직하게 사용된다.Specific examples of the biimidazole compound include 2,2'-bis(2-chlorophenyl)-4,4',5,5'-tetraphenyl-1,2'-biimidazole, 2,2'-bis (2,3-dichlorophenyl)-4,4',5,5'-tetraphenyl-1,2'-biimidazole, 2,2'-bis(2-chlorophenyl)-4,4',5 ,5'-tetra(alkoxyphenyl)-1,2'-biimidazole, 2,2'-bis(2-chlorophenyl)-4,4',5,5'-tetra(trialkoxyphenyl)-1 ,2'-biimidazole, 2,2-bis(2,6-dichlorophenyl)-4,4'5,5'-tetraphenyl-1,2'-biimidazole or 4,4',5, The imidazole compound etc. in which the phenyl group at the 5'-position is substituted by the carboalkoxy group are mentioned. Among them, 2,2'-bis(2-chlorophenyl)-4,4',5,5'-tetraphenyl-1,2'-biimidazole, 2,2'-bis(2,3-dichlorophenyl) )-4,4',5,5'-tetraphenyl-1,2'-biimidazole, 2,2-bis(2,6-dichlorophenyl)-4,4'5,5'-tetraphenyl- 1,2'-biimidazole is preferably used.

상기 트리아진계 화합물의 구체적인 예로는 2,4-비스(트리클로로메틸)-6-(4-메톡시페닐)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-(4-메톡시나프틸)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-피페로닐-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-(4-메톡시스티릴)-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(5-메틸퓨란-2-일)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(퓨란-2-일)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(4-디에틸아미노-2-메틸페닐)에테닐]-1,3,5-트리아진, 2,4-비스(트리클로로메틸)-6-[2-(3,4-디메톡시페닐)에테닐]-1,3,5-트리아진 등을 들 수 있다.Specific examples of the triazine-based compound include 2,4-bis(trichloromethyl)-6-(4-methoxyphenyl)-1,3,5-triazine, 2,4-bis(trichloromethyl)-6 -(4-Methoxynaphthyl)-1,3,5-triazine, 2,4-bis(trichloromethyl)-6-piperonyl-1,3,5-triazine, 2,4-bis (trichloromethyl)-6-(4-methoxystyryl)-1,3,5-triazine, 2,4-bis(trichloromethyl)-6-[2-(5-methylfuran-2- yl)ethenyl]-1,3,5-triazine, 2,4-bis(trichloromethyl)-6-[2-(furan-2-yl)ethenyl]-1,3,5-triazine , 2,4-bis(trichloromethyl)-6-[2-(4-diethylamino-2-methylphenyl)ethenyl]-1,3,5-triazine, 2,4-bis(trichloromethyl )-6-[2-(3,4-dimethoxyphenyl)ethenyl]-1,3,5-triazine etc. are mentioned.

상기 옥심에스테르계 화합물은 o-에톡시카르보닐-α-옥시이미노-1-페닐프로판-1-온, 1,2-옥타디온,-1-(4-페닐치오)페닐,-2-(o-벤조일옥심), 에타논,-1-(9-에틸)-6-(2-메틸벤조일-3-일)-,1-(o-아세틸옥심) 등을 포함하며, 상용되는 제품으로 CGI-124(시바가이기사), CGI-224(시바가이기사), Irgacure OXE-01(BASF사), Irgacure OXE-02(BASF사), N-1919(아데카사), NCI-831(아데카사) 등을 들 수 있다.The oxime ester compound is o-ethoxycarbonyl-α-oxyimino-1-phenylpropan-1-one, 1,2-octadione,-1-(4-phenylthio)phenyl,-2-(o -benzoyloxime), ethanone,-1-(9-ethyl)-6-(2-methylbenzoyl-3-yl)-,1-(o-acetyloxime), etc. 124 (Shiva Geigisa), CGI-224 (Chiba Geigisa), Irgacure OXE-01 (BASF), Irgacure OXE-02 (BASF), N-1919 (Adecas), NCI-831 (Adecas), etc. can be heard

상기 티오크산톤계 화합물로서는, 예를 들면 2-이소프로필티오크산톤, 2,4-디에틸티오크산톤, 2,4-디클로로티오크산톤, 1-클로로-4-프로폭시티오크산톤 등이 있다.Examples of the thioxanthone-based compound include 2-isopropylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone, 1-chloro-4-propoxythioxanthone, and the like. There is this.

또한, 상기 광중합 개시제는 본 발명의 적외선 투과 감광성 수지 조성물의 감도를 향상시키기 위해서, 광중합 개시 보조제를 더 포함할 수 있다. 본 발명에 따른 적외선 투과 감광성 수지 조성물은 광중합 개시 보조제를 함유함으로써, 감도가 더욱 높아져 생산성을 향상시킬 수 있다.In addition, the photopolymerization initiator may further include a photopolymerization initiation adjuvant in order to improve the sensitivity of the infrared transmitting photosensitive resin composition of the present invention. The infrared transmitting photosensitive resin composition according to the present invention contains a photopolymerization initiation auxiliary, thereby further increasing the sensitivity and improving productivity.

상기 광중합 개시 보조제로는, 예를 들어, 아민 화합물, 카르복실산 화합물 및 티올기를 가지는 다관능 티올 화합물로 이루어진 군으로부터 선택되는 1종 이상의 화합물이 바람직하게 사용될 수 있다.As the photopolymerization initiation adjuvant, for example, at least one compound selected from the group consisting of an amine compound, a carboxylic acid compound, and a polyfunctional thiol compound having a thiol group may be preferably used.

상기 아민 화합물로는 방향족 아민 화합물을 사용하는 것이 바람직하며, 구체적으로 트리에탄올아민, 메틸디에탄올아민, 트리이소프로판올아민 등의 지방족 아민 화합물, 4-디메틸아미노벤조산메틸, 4-디메틸아미노벤조산에틸, 4-디메틸아미노벤조산이소아밀, 4-디메틸아미노벤조산2-에틸헥실, 벤조산2-디메틸아미노에틸, N,N-디메틸파라톨루이딘, 4,4'-비스(디메틸아미노)벤조페논(통칭: 미힐러 케톤), 4,4'-비스(디에틸아미노)벤조페논 등을 사용할 수 있다.It is preferable to use an aromatic amine compound as the amine compound, and specifically, an aliphatic amine compound such as triethanolamine, methyldiethanolamine, and triisopropanolamine, methyl 4-dimethylaminobenzoate, ethyl 4-dimethylaminobenzoate, 4- Dimethylaminobenzoic acid isoamyl, 4-dimethylaminobenzoic acid 2-ethylhexyl, benzoic acid 2-dimethylaminoethyl, N,N-dimethylparatoluidine, 4,4'-bis(dimethylamino)benzophenone (common name: Michler ketone) ), 4,4'-bis(diethylamino)benzophenone, and the like can be used.

상기 카르복실산 화합물은 방향족 헤테로아세트산류인 것이 바람직하며, 구체적으로 페닐티오아세트산, 메틸페닐티오아세트산, 에틸페닐티오아세트산, 메틸에틸페닐티오아세트산, 디메틸페닐티오아세트산, 메톡시페닐티오아세트산, 디메톡시페닐티오아세트산, 클로로페닐티오아세트산, 디클로로페닐티오아세트산, N-페닐글리신, 페녹시아세트산, 나프틸티오아세트산, N-나프틸글리신, 나프톡시아세트산 등을 들 수 있다.The carboxylic acid compound is preferably aromatic heteroacetic acid, specifically phenylthioacetic acid, methylphenylthioacetic acid, ethylphenylthioacetic acid, methylethylphenylthioacetic acid, dimethylphenylthioacetic acid, methoxyphenylthioacetic acid, dimethoxyphenylthio Acetic acid, chlorophenylthioacetic acid, dichlorophenylthioacetic acid, N-phenylglycine, phenoxyacetic acid, naphthylthioacetic acid, N-naphthylglycine, naphthoxyacetic acid, etc. are mentioned.

상기 티올기를 가지는 다관능 티올 화합물로는, 예를 들어, 2-머캅토벤조티아졸, 1,4-비스(3-머캅토부티릴옥시)부탄, 1,3,5-트리스(3-머캅토부틸옥시에틸)-1,3,5-트리아진-2,4,6(1H,3H,5H)-트리온, 트리메틸올프로판트리스(3-머갑토프로피오네이트), 펜타에리트리톨테트라키스(3-머캅토부틸레이트), 펜타에리트리톨테트라키스(3-머캅토프로피오네이트), 디펜타에리트리톨헥사키스(3-머캅토프로피오네이트), 테트라에틸렌글리콜비스(3-머캅토프로피오네이트) 등을 들 수 있다.Examples of the polyfunctional thiol compound having a thiol group include 2-mercaptobenzothiazole, 1,4-bis(3-mercaptobutyryloxy)butane, 1,3,5-tris(3-mer). Captobutyloxyethyl)-1,3,5-triazine-2,4,6(1H,3H,5H)-trione, trimethylolpropanetris(3-mercaptopropionate), pentaerythritol tetrakis (3-mercaptobutylate), pentaerythritol tetrakis (3-mercaptopropionate), dipentaerythritol hexakis (3-mercaptopropionate), tetraethylene glycol bis (3-mercaptopropionate) cionate) and the like.

상기 광중합 개시제는 본 발명의 착색 감광성 수지 조성물의 총 중량에 대해서 0.1 내지 40 중량%, 바람직하게는 0.1 내지 10 중량%로 포함될 수 있다. 상기 광중합 개시제가 상기 범위로 포함되는 경우, 착색 감광성 수지 조성물이 고감도화되어 노광 시간이 단축되므로 생산성이 향상되며 높은 해상도를 유지할 수 있으며. 화소부의 강도와 화소부의 표면에서의 평활성이 양호해질 수 있다.The photopolymerization initiator may be included in an amount of 0.1 to 40 wt%, preferably 0.1 to 10 wt%, based on the total weight of the colored photosensitive resin composition of the present invention. When the photopolymerization initiator is included in the above range, the colored photosensitive resin composition is highly sensitive and the exposure time is shortened, so that productivity is improved and high resolution can be maintained. The intensity of the pixel portion and smoothness on the surface of the pixel portion can be improved.

또한 상기 광중합 개시 보조제를 포함하는 경우, 전체 광중합 개시제 중 10 내지 100 중량%, 바람직하게는 20 내지 100 중량%로 포함할 수 있다. 상기 광중합 개시 보조제가 상기 범위로 포함되는 경우, 착색 감광성 수지 조성물의 감도가 더 높아지고, 상기 조성물을 사용하여 형성되는 컬러필터의 생산성이 향상되는 효과를 제공할 수 있다.In addition, when the photopolymerization initiation aid is included, it may be included in an amount of 10 to 100% by weight, preferably 20 to 100% by weight of the total photopolymerization initiator. When the photopolymerization initiation adjuvant is included in the above range, the sensitivity of the colored photosensitive resin composition may be increased, and productivity of a color filter formed using the composition may be improved.

(E) 용제(E) solvent

본 발명의 용제는 프로필렌글리콜 모노메틸에테르 아세테이트가 바람직하나 상기 착색 감광성 수지 조성물을 용해시키는 것이라면 특별히 제한하지 않고 추가로 사용 가능하다.The solvent of the present invention is preferably propylene glycol monomethyl ether acetate, but as long as it dissolves the colored photosensitive resin composition, it is not particularly limited and may be additionally used.

상기 추가로 사용 가능한 용제는 특히 에테르류, 방향족 탄화수소류, 케톤류, 알코올류, 에스테르류 또는 아미드류 등이 바람직하다. 구체적으로 에틸렌글리콜 모노메틸 에테르, 에틸렌글리콜 모노에틸 에테르, 에틸렌글리콜 모노프로필 에테르, 에틸렌글리콜 모노부틸 에테르, 디에틸렌글리콜 디메틸 에테르, 디에틸렌글리콜 디에틸 에테르, 디에틸렌글리콜 디프로필 에테르, 디에틸렌글리콜 디부틸 에테르, 프로필렌글리콜 모노메틸 에테르, 프로필렌글리콜 모노에틸 에테르, 프로필렌글리콜 모노프로필 에테르, 프로필렌글리콜 모노부틸 에테르, 디프로필렌글리콜 디메틸 에테르, 디프로필렌글리콜 디에틸 에테르, 디프로필렌글리콜 디프로필 에테르 및 디프로필렌글리콜 디부틸 에테르 등의 에테르류; 벤젠, 톨루엔, 크실렌 및 메시틸렌 등의 방향족 탄화수소류; 메틸에틸케톤, 아세톤, 메틸아밀케톤, 메틸이소부틸케톤 및 시클로헥사논 등의 케톤류; 에탄올, 프로판올, 부탄올, 헥사놀, 시클로헥산올, 에틸렌글리콜 및 글리세린 등의 알코올류; 3-에톡시프로피온산에틸, 3-메톡시 프로피온산메틸, 메틸셀로솔브 아세테이트, 에틸셀로솔브 아세테이트, 에틸아세테이트, 부틸아세테이트, 아밀아세테이트, 메틸락테이트, 에틸락테이트, 부틸락테이트, 3-메톡시 부틸아세테이트, 3-메틸-3-메톡시-1-부틸아세테이트, 메톡시펜틸아세테이트, 에틸렌글리콜 모노아세테이트, 에틸렌글리콜 디아세테이트, 에틸렌글리콜 모노메틸에테르 아세테이트, 에틸렌글리콜 모노에틸에테르 아세테이트, 디에틸렌글리콜 모노아세테이트, 디에틸렌글리콜 디아세테이트, 디에틸렌글리콜 모노부틸에테르 아세테이트, 프로필렌글리콜 모노아세테이트, 프로필렌글리콜 디아세테이트, 프로필렌글리콜 모노에틸에테르 아세테이트, 에틸렌 카보네이트, 프로필렌 카보네이트 및 γ-부티로락톤 등의 에스테르류 등을 들 수 있다. 상기 용제는 예시한 용제로 이루어진 군으로부터 선택되는 1종 또는 2종 이상을 혼합하여 사용할 수 있다.The solvent that can be used in addition is particularly preferably ethers, aromatic hydrocarbons, ketones, alcohols, esters or amides. Specifically, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, ethylene glycol monopropyl ether, ethylene glycol monobutyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol dipropyl ether, diethylene glycol di Butyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol monobutyl ether, dipropylene glycol dimethyl ether, dipropylene glycol diethyl ether, dipropylene glycol dipropyl ether and dipropylene glycol ethers such as dibutyl ether; aromatic hydrocarbons such as benzene, toluene, xylene and mesitylene; ketones such as methyl ethyl ketone, acetone, methyl amyl ketone, methyl isobutyl ketone and cyclohexanone; alcohols such as ethanol, propanol, butanol, hexanol, cyclohexanol, ethylene glycol and glycerin; 3-Ethoxy ethyl propionate, 3-methoxymethyl propionate, methyl cellosolve acetate, ethyl cellosolve acetate, ethyl acetate, butyl acetate, amyl acetate, methyl lactate, ethyl lactate, butyl lactate, 3-methyl Toxybutyl acetate, 3-methyl-3-methoxy-1-butyl acetate, methoxypentyl acetate, ethylene glycol monoacetate, ethylene glycol diacetate, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, diethylene glycol Esters such as monoacetate, diethylene glycol diacetate, diethylene glycol monobutyl ether acetate, propylene glycol monoacetate, propylene glycol diacetate, propylene glycol monoethyl ether acetate, ethylene carbonate, propylene carbonate and γ-butyrolactone can be heard The solvent may be used one or a mixture of two or more selected from the group consisting of the exemplified solvents.

바람직하게 상기 용제 중 도포성, 건조성면에서 비점이 100 내지 200 ℃인 유기 용제를 사용할 수 있고, 보다 바람직하게는 알킬렌글리콜 알킬에테르 아세테이트류, 케톤류, 3-에톡시프로피온산 에틸이나, 3-메톡시프로피온산 메틸 등의 에스테르류를 사용할 수 있으며, 더욱 바람직하게는 프로필렌글리콜 모노메틸에테르 아세테이트, 프로필렌글리콜 모노에틸에테르 아세테이트, 시클로헥사논, 3-에톡시프로피온산 에틸, 3-메톡시프로피온산 메틸 등을 사용할 수 있다. 이들 용제는 각각 단독으로 또는 2 종류 이상 혼합하여 사용할 수 있다.Preferably, an organic solvent having a boiling point of 100 to 200° C. in terms of applicability and dryness among the solvents may be used, and more preferably, alkylene glycol alkyl ether acetates, ketones, 3-ethoxypropionate ethyl, or 3-methyl Esters such as methyl oxypropionate may be used, and more preferably, propylene glycol monomethyl ether acetate, propylene glycol monoethyl ether acetate, cyclohexanone, 3-ethoxypropionate ethyl, 3-methoxypropionate methyl, etc. may be used. can These solvents can be used individually or in mixture of 2 or more types, respectively.

상기 용제의 함량은 착색 감광성 수지 조성물의 총 중량이 100 중량%가 되도록 하는 잔량으로 포함될 수 있다. 구체적으로, 본 발명에서 "잔량"은 본 발명의 필수 성분 및 그 외 추가 성분들을 더 포함한 조성물의 총 중량이 100 중량%가 되도록 하는 잔량을 의미하며, 상기 "잔량"의 의미로 인해 본 발명의 착색 감광성 수지 조성물에 추가 성분이 포함되지 않는 것으로 한정되지 않는다. 예를 들어, 상기 용제는 착색 감광성 수지 조성물 총 중량에 대하여 50 내지 95 중량%, 바람직하게는 50 내지 60 중량%로 포함될 수 있으나, 이에 제한되는 것은 아니다.The content of the solvent may be included in a residual amount such that the total weight of the colored photosensitive resin composition is 100% by weight. Specifically, in the present invention, "residual amount" means a remaining amount such that the total weight of the composition further including the essential components and other additional components of the present invention is 100% by weight, and due to the meaning of the "residual amount", the It is not limited to the thing which an additional component is not included in the coloring photosensitive resin composition. For example, the solvent may be included in an amount of 50 to 95 wt%, preferably 50 to 60 wt%, based on the total weight of the colored photosensitive resin composition, but is not limited thereto.

(( F) 크산텐계 화합물F) Xanthene-based compounds

본 발명에 따른 착색 감광성 수지 조성물은 크산텐계 화합물을 추가로 더욱 포함할 수 있다.The colored photosensitive resin composition according to the present invention may further include a xanthene-based compound.

상기 크산텐계 화합물은 분자 내에 크산텐 골격을 가진 화합물로서, 착색 감광성 수지 조성물의 저장 안정성을 더욱 향상시킬 수 있다.The xanthene-based compound is a compound having a xanthene skeleton in a molecule, and may further improve storage stability of the colored photosensitive resin composition.

상기 크산텐계 화합물로는, 예를 들어, C.I.애시드 레드 51, 52, 87, 91, 92, 94, 289, 388, C.I.애시드 바이올렛 9, 30, C.I.베이직 레드 1(로다민 6G), 2, 3, 4, 8, C.I.베이직 레드 10(로다민 B), 11, C.I.베이직 바이올렛 10, 11, 25, C.I.솔벤트 레드 218, C.I.모던 레드 27, C.I.리액티브 레드 36(로즈벤갈 B), 설포로다민 B, 설포로다민 G 등을 들 수 있으나 이에 한정되는 것은 아니며 이들 염료는 각각 단독으로 또는 2종 이상을 조합하여 사용할 수 있다.As the xanthene-based compound, for example, C.I. Acid Red 51, 52, 87, 91, 92, 94, 289, 388, C.I. Acid Violet 9, 30, C.I. Basic Red 1 (Rhodamine 6G), 2, 3 , 4, 8, C.I. Basic Red 10 (Rhodamine B), 11, C.I. Basic Violet 10, 11, 25, C.I. Solvent Red 218, C.I. Modern Red 27, C.I. Reactive Red 36 (Rose Bengal B), Sulforodamine B and sulforodamine G may be mentioned, but are not limited thereto, and these dyes may be used alone or in combination of two or more.

보다 바람직하게는, C.I.애시드 레드 52, C.I.애시드 레드 289, C.I.애시드 레드 91, C.I.애시드 레드 92, C.I.애시드 레드 94 및 로다민 B(Rhodamine B)로 이루어진 군으로부터 선택되는 1 종 이상을 포함하는 것이 바람직하다.More preferably, C.I. Acid Red 52, C.I. Acid Red 289, C.I. Acid Red 91, C.I. Acid Red 92, C.I. Acid Red 94 and Rhodamine B. desirable.

상기 크산텐계 화합물은 상기 (A) 색재 총 중량에 대하여 1 내지 20 중량%로 포함되는 것이 바람직하다. 크산텐계 화합물은 투과율 및 내열성이 우수하지만, 용제에 대한 용해도 및 상용성이 부족하여 충분한 양을 착색 감광성 수지 조성물 내에 사용하기가 어렵다. 상기 크산텐계 화합물이 상기 범위 미만으로 포함될 경우에는 투과도 및 저장안정성 개선 효과를 기대하기가 어렵고, 상기 범위를 초과할 경우에는 크산텐계 화합물의 용해도가 저하되어 도막 내에 석출 등 이물이 발생하기 쉽고, 명암비가 떨어지며, 착색 감광성 수지 조성물의 저장 안정성이 떨어질 수 있다.The xanthene-based compound is preferably included in an amount of 1 to 20% by weight based on the total weight of the color material (A). Although the xanthene-based compound has excellent transmittance and heat resistance, it is difficult to use a sufficient amount in the colored photosensitive resin composition due to lack of solubility and compatibility with a solvent. When the xanthene-based compound is included in less than the above range, it is difficult to expect the effect of improving the transmittance and storage stability, and when it exceeds the above range, the solubility of the xanthene-based compound is lowered and foreign substances such as precipitation in the coating film are easy to occur, and the contrast ratio falls, and the storage stability of the colored photosensitive resin composition may be deteriorated.

(G) 첨가제(G) additives

본 발명의 착색 감광성 수지 조성물은 상기 성분 외에 본 발명의 목적을 해치지 아니하는 범위에서 당업자의 필요에 따라 레벨링제, 충진제, 다른 고분자 화합물, 밀착 촉진제, 자외선 흡수제, 응집 방지제 등의 당 기술 분야에서의 공지의 첨가제를 더욱 포함할 수 있다.The colored photosensitive resin composition of the present invention, in addition to the above components, is a leveling agent, filler, other high molecular compound, adhesion promoter, ultraviolet absorber, anti-aggregation agent, etc. A known additive may be further included.

상기 레벨링제로는 실리콘계 계면활성제, 불소계 계면활성제 및 불소 원자를 갖는 실리콘계 계면활성제를 들 수 있다. 이들은 측쇄에 중합성기를 가질 수 있다.The leveling agent may include a silicone-based surfactant, a fluorine-based surfactant, and a silicone-based surfactant having a fluorine atom. They may have a polymerizable group in the side chain.

상기 실리콘계 계면활성제로는 분자 내에 실록산 결합을 갖는 계면활성제를 들 수 있다. 구체적으로는 도레이실리콘 DC3PA, SH7PA, DC11PA, SH21PA, SH28PA, SH29PA, SH30PA, SH8400(Dow Corning Toray Co., Ltd.), KP321, KP322, KP323, KP324, KP326, KP340, KP341(Shin-Etsu Silicone 社), TSF400, TSF401, TSF410, TSF4300, TSF4440, TSF4445, TSF4446, TSF4452 및 TSF4460(Momentive Performance Materials japan LLC)등을 들 수 있다.Examples of the silicone-based surfactant include a surfactant having a siloxane bond in a molecule. Specifically, Toray Silicones DC3PA, SH7PA, DC11PA, SH21PA, SH28PA, SH29PA, SH30PA, SH8400 (Dow Corning Toray Co., Ltd.), KP321, KP322, KP323, KP324, KP326, KP340, KP341 (Shin-Etsu Silicone) ), TSF400, TSF401, TSF410, TSF4300, TSF4440, TSF4445, TSF4446, TSF4452 and TSF4460 (Momentive Performance Materials Japan LLC).

상기 불소계 계면활성제로는 분자 내에 플루오로카본쇄를 갖는 계면 활성제를 들 수 있다. 구체적으로는 Fluorad FC4430, FC431(Sumitomo 3M Ltd.), Megaface F142D, 동 F171, 동 F172, 동 F173, 동 F177, 동 F183, 동 F554, 동 R30, 동 RS-718-K(DIC Corporation), EFTOP EF301, 동 EF303, 동 EF351, 동 EF352 (Mitsubishi Materials Electronic Chemicals Co., Ltd.), SURFLON S381, 동 S382, 동 SC101, 동 SC105(Asahi Glass Co., Ltd. 제) 및 E5844(Daikin fine Chemical Laboratory)등을 들 수 있다.Examples of the fluorine-based surfactant include a surfactant having a fluorocarbon chain in the molecule. Specifically, Fluorad FC4430, FC431 (Sumitomo 3M Ltd.), Megaface F142D, Dong F171, Dong F172, Dong F173, Dong F177, Dong F183, Dong F554, Dong R30, Dong RS-718-K (DIC Corporation), EFTOP EF301, copper EF303, copper EF351, copper EF352 (Mitsubishi Materials Electronic Chemicals Co., Ltd.), SURFLON S381, copper S382, copper SC101, copper SC105 (manufactured by Asahi Glass Co., Ltd.) and E5844 (Daikin fine chemical laboratory) ) and the like.

불소 원자를 갖는 실리콘계 계면활성제로는 분자 내에 실록산 결합 및 플루오로카본쇄를 갖는 계면활성제를 들 수 있다. 구체적으로는 Megaface R08, 동 BL20, 동 F475, 동 F477 및 F443 (DIC Corporation)등을 들 수 있다.Examples of the silicone-based surfactant having a fluorine atom include a surfactant having a siloxane bond and a fluorocarbon chain in the molecule. Specific examples thereof include Megaface R08, copper BL20, copper F475, copper F477 and F443 (DIC Corporation).

상기 충진제는 구체적으로, 유리, 실리카, 알루미나 등을 사용할 수 있으나, 이에 한정되는 것은 아니다.Specifically, the filler may be used, such as glass, silica, alumina, but is not limited thereto.

상기 다른 고분자 화합물은 구체적으로 에폭시 수지, 말레이미드 수지 등의 경화성 수지, 폴리비닐알코올, 폴리아크릴산, 폴리에틸렌글리콜 모노알킬에테르, 폴리플루오로알킬아크릴레이트, 폴리에스테르, 폴리우레탄 등의 열가소성 수지 등을 사용할 수 있으나, 이에 한정되는 것은 아니다. Specific examples of the other high molecular compounds include curable resins such as epoxy resins and maleimide resins, and thermoplastic resins such as polyvinyl alcohol, polyacrylic acid, polyethylene glycol monoalkyl ether, polyfluoroalkyl acrylate, polyester, and polyurethane. However, the present invention is not limited thereto.

상기 밀착 촉진제는 구체적으로, 비닐트리메톡시실란, 비닐트리에톡시실란, 비닐트리스(2-메톡시에톡시)실란, N-(2-아미노에틸)-3-아미노프로필메틸디메톡시실란, N-(2-아미노에틸)-3-아미노프로필트리메톡시실란, 3-아미노프로필트리에톡시실란, 3-글리시독시프로필트리메톡시실란, 3-글리시독시프로필메틸디메톡시실란, 2-(3,4-에폭시시클로헥실)에틸트리메톡시실란, 3-클로로프로필메틸디메톡시실란, 3-클로로프로필트리메톡시실란, 3-메타크릴옥시프로필트리메톡시실란, 3-머캅토프로필트리메톡시실란, 3-이소시아네이트프로필트리메톡시실란 및 3-이소시아네이트프로필트리에톡시실란 으로 이루어진 군으로부터 선택된 단독 또는 이들의 혼합물을 사용할 수 있다.The adhesion promoter is specifically, vinyltrimethoxysilane, vinyltriethoxysilane, vinyltris(2-methoxyethoxy)silane, N-(2-aminoethyl)-3-aminopropylmethyldimethoxysilane, N -(2-aminoethyl)-3-aminopropyltrimethoxysilane, 3-aminopropyltriethoxysilane, 3-glycidoxypropyltrimethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 2- (3,4-epoxycyclohexyl)ethyltrimethoxysilane, 3-chloropropylmethyldimethoxysilane, 3-chloropropyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-mercaptopropyltri One or a mixture thereof selected from the group consisting of methoxysilane, 3-isocyanatepropyltrimethoxysilane and 3-isocyanatepropyltriethoxysilane may be used.

상기 자외선 흡수제는 구체적으로, 2-(3-tert-부틸-2-히드록시-5-메틸페닐)-5-클로로벤조티리아졸, 알콕시벤조페논 등을 사용할 수 있으나, 이에 제한되는 것은 아니다.Specifically, the ultraviolet absorber may be 2-(3-tert-butyl-2-hydroxy-5-methylphenyl)-5-chlorobenzothiazole, alkoxybenzophenone, or the like, but is not limited thereto.

상기 응집 방지제는 구체적으로 폴리아크릴산 나트륨 등을 사용할 수 있으나, 이에 제한되는 것은 아니다.The aggregation inhibitor may be specifically sodium polyacrylate, but is not limited thereto.

<컬러필터 및 디스플레이 소자><Color filter and display element>

본 발명은 상기 착색 감광성 수지 조성물로 제조되는 컬러필터 및 디스플레이 소자를 제공한다.The present invention provides a color filter and a display device made of the colored photosensitive resin composition.

상기 컬러 필터의 두께는 목적이나 용도 등에 따라 적절히 조정할 수 있으며, 일반적으로 0.1 내지 30 ㎛, 바람직하게는 1 내지 8 ㎛일 수 있다.The thickness of the color filter may be appropriately adjusted depending on the purpose or use, and may be generally 0.1 to 30 µm, preferably 1 to 8 µm.

상기 착색 감광성 수지 조성물을 기판 상에 도포하고 건조시켜 착색막을 형성할 수 있다. 도포 후 가열건조(프리베이크), 또는 감압 건조 후에 가열하여 용제 등의 휘발 성분을 휘발시키며, 상기 가열 온도는 70 내지 200 ℃, 바람직하게는 80 내지 130 ℃이다.The colored photosensitive resin composition may be applied on a substrate and dried to form a colored film. After application, heating and drying (pre-baking) or drying under reduced pressure to volatilize volatile components such as solvent, the heating temperature is 70 to 200 ℃, preferably 80 to 130 ℃.

기판은 컬러필터 자체 기판, 고체 촬상 소자 또는 디스플레이 장치 등에 컬러필터가 위치되는 부위일 수도 있으며, 특별히 제한되지 않는다. 상기 기판은 유리, 실리콘(Si), 실리콘 산화물(SiOx) 또는 고분자 기판일 수 있으며, 상기 고분자 기판은 폴리에테르설폰(polyethersulfone, PES) 또는 폴리카보네이트(polycarbonate, PC) 등일 수 있다.The substrate may be a region in which the color filter is located, such as a color filter itself substrate, a solid-state imaging device, or a display device, and is not particularly limited. The substrate may be glass, silicon (Si), silicon oxide (SiOx), or a polymer substrate, and the polymer substrate may be polyethersulfone (PES) or polycarbonate (PC).

상기 도포 방법으로는 롤 코팅, 스핀 코팅, 슬릿 코팅, 잉크젯 프린팅 등과 같은 코팅 방법 혹은 프린팅 공정 등에 의해 실시될 수 있다.The coating method may be carried out by a coating method such as roll coating, spin coating, slit coating, inkjet printing, or a printing process.

이후, 상기 착색막을 노광 및 현상하여 각 화소에 대응하는 착색 패턴이 형성될 수 있다.Thereafter, the colored layer may be exposed and developed to form a colored pattern corresponding to each pixel.

상기 노광 공정은 상기 화소 영역을 선택적으로 노출시키는 마스크를 사용한 자외선 노광(예를 들면, g-라인, h-라인, i-라인, KrF 광원 사용)을 포함할 수 있다. 이후, 비노광 영역을 현상액을 사용하여 선택적으로 제거함으로써 목적으로 하는 패턴 형상을 갖는 상기 착색 패턴을 형성할 수 있다.The exposure process may include UV exposure (eg, using a g-line, h-line, i-line, or KrF light source) using a mask selectively exposing the pixel region. Thereafter, the colored pattern having a desired pattern shape can be formed by selectively removing the unexposed area using a developer.

상기 현상액은 예를 들면, 무기 또는 유기 알칼리성 화합물을 포함할 수 있다. 상기 무기 알칼리성 화합물의 예로서 수산화나트륨, 수산화칼륨, 인산수소이나트륨, 인산이수소나트륨, 인산수소이암모늄, 인산이수소암모늄, 인산이수소칼륨, 규산나트륨, 규산칼륨, 탄산나트륨, 탄산칼륨, 탄산수소나트륨, 탄산수소칼륨, 붕산나트륨, 붕산칼륨, 암모니아 등을 들 수 있다. 상기 유기 알칼리성 화합물의 예로서 테트라메틸암모늄히드록시드, 2-히드록시에틸트리메틸암모늄히드록시드, 모노메틸아민, 디메틸아민, 트리메틸아민, 모노에틸아민, 디에틸아민, 트리에틸아민, 모노이소프로필아민, 디이소프로필아민, 에탄올아민 등을 들 수 있다. 이들은 단독으로 또는 2종 이상 조합하여 사용할 수 있다.The developer may include, for example, an inorganic or organic alkaline compound. Examples of the inorganic alkaline compound include sodium hydroxide, potassium hydroxide, disodium hydrogen phosphate, sodium dihydrogen phosphate, diammonium hydrogen phosphate, ammonium dihydrogen phosphate, potassium dihydrogen phosphate, sodium silicate, potassium silicate, sodium carbonate, potassium carbonate, sodium hydrogen carbonate , potassium hydrogen carbonate, sodium borate, potassium borate, ammonia, and the like. Examples of the organic alkaline compound include tetramethylammonium hydroxide, 2-hydroxyethyltrimethylammonium hydroxide, monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monoisopropyl An amine, diisopropylamine, ethanolamine, etc. are mentioned. These can be used individually or in combination of 2 or more types.

상기 현상 공정 이후, 추가 가열 경화 공정(포스트베이크, 후 소성)을 통하여 상기 착색 패턴을 보다 단단하게 경화시킬 수 있으며, 이 때 가열 온도는 90 내지 180℃일 수 있고, 가열 시간은 5 내지 180 분, 바람직하게는 15 내지 90 분일 수 있으나, 이에 한정되는 것은 아니다.After the developing process, the coloring pattern may be more firmly cured through an additional heat curing process (post-baking, post-baking), in which case the heating temperature may be 90 to 180° C., and the heating time is 5 to 180 minutes. , It may preferably be 15 to 90 minutes, but is not limited thereto.

상술한 공정에 의해 제조된 착색 패턴을 포함하는 컬러필터는 색재로 적색, 청색 및 자색으로 이루어진 군으로부터 선택되는 1종 이상의 색재와, 흑색 안료(바람직하게는 흑색 유기 안료)를 포함함으로서 편광판을 대체할 수 있을 만큼 반사율이 낮고, 외광반사 효과가 우수하며, 디스플레이의 시인성을 높일 수 있는 이점이 있다.The color filter including the coloring pattern manufactured by the above-described process replaces the polarizing plate by including at least one color material selected from the group consisting of red, blue and purple as a color material, and a black pigment (preferably a black organic pigment) There are advantages in that the reflectance is as low as possible, the external light reflection effect is excellent, and the visibility of the display can be increased.

또한, 본 발명은 상기 컬러필터를 포함하는 디스플레이 소자를 제공한다.In addition, the present invention provides a display device including the color filter.

상기 디스플레이 소자는 CCD 이미지 센서, CMOS 이미지 센서 등과 같은 고체촬상소자, 광원 등과 같은 발광 장치, 화상표시장치 등과 같이 통상적으로 디스플레이 소자에 포함될 수 있는 그 밖의 구성들을 포함할 수 있다. The display device may include a solid-state image sensor such as a CCD image sensor and a CMOS image sensor, a light emitting device such as a light source, an image display device, and the like, and other components that may be typically included in a display device.

본 발명의 상기 디스플레이 소자는 플렉서블 디스플레이 소자일 수 있으며, 특히 언더 디스플레이 카메라(UDC)가 구현된 디스플레이 소자일 수 있다. The display device of the present invention may be a flexible display device, and in particular, a display device in which an under display camera (UDC) is implemented.

이하, 본 발명을 구체적으로 설명하기 위해 실시예를 들어 상세하게 설명하기로 한다. 그러나, 본 발명에 따른 실시예는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 상술하는 실시예에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다.Hereinafter, examples will be given to describe the present invention in detail. However, the embodiments according to the present invention may be modified in various other forms, and the scope of the present invention should not be construed as being limited to the embodiments described below. The embodiments of the present invention are provided to more completely explain the present invention to those of ordinary skill in the art.

<안료 분산 조성물의 제조><Preparation of pigment dispersion composition>

제조예 1. 안료 분산 조성물 M1Preparation Example 1. Pigment Dispersion Composition M1

유기카본블랙 15 중량부, 분산제로서 아지스파 PB821(아지노모또 파인테크노 가부시끼가이샤) 6 중량부, 용매로서 프로필렌 글리콜모노메틸에테르아세테이트 79 중량부를 비드밀로 12 시간 동안 혼합/분산하여 안료 분산 조성물 M1을 제조하였다.15 parts by weight of organic carbon black, 6 parts by weight of Ajispa PB821 (Ajinomoto Fine Techno Co., Ltd.) as a dispersant, and 79 parts by weight of propylene glycol monomethyl ether acetate as a solvent Mix/disperse with a bead mill for 12 hours to disperse the pigment dispersion composition M1 was prepared.

제조예 2. 안료 분산 조성물 M2Preparation Example 2. Pigment Dispersion Composition M2

안료로서 C.I. 피그먼트 레드 177 12.0 중량부, 안료 분산제로서 DISPERBYK-2001 (BYK사 제조) 5.0 중량부, 용제로서 4-하이드록시-4-메틸-2-펜탄온 13.0 중량부, 프로필렌글리콜메틸에테르아세테이트 70.0 중량부를 비드밀에 의해 12 시간 동안 혼합/분산하여 안료 분산 조성물 M2를 제조하였다.As a pigment, C.I. Pigment Red 177 12.0 parts by weight, DISPERBYK-2001 (manufactured by BYK) 5.0 parts by weight as a pigment dispersant, 13.0 parts by weight of 4-hydroxy-4-methyl-2-pentanone as a solvent, 70.0 parts by weight of propylene glycol methyl ether acetate A pigment dispersion composition M2 was prepared by mixing/dispersing for 12 hours by a bead mill.

제조예 3. 안료 분산 조성물 M3Preparation Example 3. Pigment Dispersion Composition M3

안료로서 C.I. 피그먼트 레드 254 12.0 중량부, 안료 분산제로서 DISPERBYK-2001 (BYK사 제조) 5.0 중량부, 용제로서 4-하이드록시-4-메틸-2-펜탄온 13.0 중량부, 프로필렌글리콜메틸에테르아세테이트 70.0 중량부를 비드밀에 의해 12 시간 동안 혼합/분산하여 안료 분산 조성물 M3을 제조하였다.As a pigment, C.I. Pigment Red 254 12.0 parts by weight, DISPERBYK-2001 (manufactured by BYK) 5.0 parts by weight as a pigment dispersant, 13.0 parts by weight of 4-hydroxy-4-methyl-2-pentanone as a solvent, 70.0 parts by weight of propylene glycol methyl ether acetate A pigment dispersion composition M3 was prepared by mixing/dispersing for 12 hours by a bead mill.

제조예 4. 안료 분산 조성물 M4Preparation Example 4. Pigment Dispersion Composition M4

안료로서 C.I. 피그먼트 블루 15:6 12.0 중량부, 안료분산제로서 DISPERBYK-2001(BYK사 제조) 4.0 중량부, 용매로서 프로필렌글리콜메틸에테르아세테이트 44 중량부 및 프로필렌글리콜메틸에테르 40 중량부를 비드밀에 의해 12시간 동안 혼합/분산하여 안료 분산 조성물 M4를 제조하였다As a pigment, C.I. Pigment Blue 15:6 12.0 parts by weight, DISPERBYK-2001 (manufactured by BYK) 4.0 parts by weight as a pigment dispersant, 44 parts by weight of propylene glycol methyl ether acetate and 40 parts by weight of propylene glycol methyl ether as a solvent by a bead mill for 12 hours Mixing/dispersing to prepare pigment dispersion composition M4

제조예 5. 안료 분산 조성물 M5Preparation 5. Pigment dispersion composition M5

안료로서 C.I. 피그먼트 바이올렛 23 13 중량부, 안료분산제로서 DISPERBYK-2001(BYK사 제조) 7 중량부, 용매로서 프로필렌글리콜메틸에테르아세테이트 76 중량부 및 프로필렌글리콜메틸에테르 4 중량부를 비드밀에 의해 12 시간 동안 혼합/분산하여 안료 분산 조성물 M5를 제조하였다.As a pigment, C.I. 13 parts by weight of Pigment Violet 23, 7 parts by weight of DISPERBYK-2001 (manufactured by BYK) as a pigment dispersant, 76 parts by weight of propylene glycol methyl ether acetate and 4 parts by weight of propylene glycol methyl ether as a solvent Mixed/mixed by a bead mill for 12 hours The dispersion was carried out to prepare a pigment dispersion composition M5.

제조예 6. 안료 분산 조성물 M6Preparation Example 6. Pigment Dispersion Composition M6

안료로서 C.I. 피그먼트 그린 58 12.0 중량부, 안료 분산제로서 DISPERBYK-2001 (BYK사 제조) 5.0 중량부, 용제로서 4-하이드록시-4-메틸-2-펜탄온 13.0 중량부, 프로필렌글리콜메틸에테르아세테이트 70.0 중량부를 비드밀에 의해 12 시간 동안 혼합/분산하여 안료 분산 조성물 M6을 제조하였다.As a pigment, C.I. Pigment Green 58 12.0 parts by weight, DISPERBYK-2001 (manufactured by BYK) 5.0 parts by weight as a pigment dispersant, 13.0 parts by weight of 4-hydroxy-4-methyl-2-pentanone as a solvent, 70.0 parts by weight of propylene glycol methyl ether acetate A pigment dispersion composition M6 was prepared by mixing/dispersing for 12 hours by a bead mill.

제조예 7. 안료 분산 조성물 M7Preparation Example 7. Pigment Dispersion Composition M7

안료로서 C.I. 피그먼트 옐로우 150 12.0 중량부, 안료 분산제로서 DISPERBYK-2001 (BYK사 제조) 5.0 중량부, 용제로서 4-하이드록시-4-메틸-2-펜탄온 13.0 중량부, 프로필렌글리콜메틸에테르아세테이트 70.0 중량부를 비드밀에 의해 12 시간 동안 혼합/분산하여 안료 분산 조성물 M7을 제조하였다.As a pigment, C.I. Pigment Yellow 150 12.0 parts by weight, DISPERBYK-2001 (manufactured by BYK) 5.0 parts by weight as a pigment dispersant, 13.0 parts by weight of 4-hydroxy-4-methyl-2-pentanone as a solvent, 70.0 parts by weight of propylene glycol methyl ether acetate A pigment dispersion composition M7 was prepared by mixing/dispersing for 12 hours by a bead mill.

제조예 8. 안료 분산 조성물 M8Preparation 8. Pigment Dispersion Composition M8

안료로서 C.I. 피그먼트 블루 16 12.0 중량부, 안료분산제로서 DISPERBYK-2001(BYK사 제조) 4.0 중량부, 용매로서 프로필렌글리콜메틸에테르아세테이트 44 중량부 및 프로필렌글리콜메틸에테르 40 중량부를 비드밀에 의해 12시간 동안 혼합/분산하여 안료 분산 조성물 M8를 제조하였다As a pigment, C.I. 12.0 parts by weight of Pigment Blue 16, 4.0 parts by weight of DISPERBYK-2001 (manufactured by BYK) as a pigment dispersant, 44 parts by weight of propylene glycol methyl ether acetate and 40 parts by weight of propylene glycol methyl ether as a solvent Mixed/mixed by a bead mill for 12 hours A pigment dispersion composition M8 was prepared by dispersing

제조예 9. 안료 분산 조성물 M9Preparation 9. Pigment Dispersion Composition M9

안료로서 C.I. 피그먼트 바이올렛 37 13 중량부, 안료분산제로서 DISPERBYK-2001(BYK사 제조) 7 중량부, 용매로서 프로필렌글리콜메틸에테르아세테이트 76 중량부 및 프로필렌글리콜메틸에테르 4 중량부를 비드밀에 의해 12 시간 동안 혼합/분산하여 안료 분산 조성물 M9를 제조하였다.As a pigment, C.I. 13 parts by weight of Pigment Violet 37, 7 parts by weight of DISPERBYK-2001 (manufactured by BYK) as a pigment dispersant, 76 parts by weight of propylene glycol methyl ether acetate and 4 parts by weight of propylene glycol methyl ether as a solvent Mixed/mixed by a bead mill for 12 hours The dispersion was carried out to prepare a pigment dispersion composition M9.

합성예 1. 알칼리 가용성 수지의 합성Synthesis Example 1. Synthesis of alkali-soluble resin

교반기, 온도계 환류 냉각관, 적하 로트 및 질소 도입관을 구비한 플라스크에 프로필렌글리콜모노메틸에테르 아세테이트 120 중량부, 프로필렌글리콜모노메틸에테르 80 중량부, AIBN 2 중량부, 아크릴산 13.0 중량부, 벤질메타아크릴레이트 10 중량부, 스티렌 57.0 중량부, 메틸메타아크릴레이트 20 중량부 및 n-도데실머캅토 3 중량부를 투입하고 질소 치환하였다. 그 후 교반하며 반응액의 온도를 110 ℃로 상승시키고 6 시간 반응하였다. 이렇게 합성된 알칼리 가용성 수지의 고형분 산가는 100.2 ㎎KOH/g 이며 GPC로 측정한 중량 평균 분자량 Mw는 약 6,000이었다.120 parts by weight of propylene glycol monomethyl ether acetate, 80 parts by weight of propylene glycol monomethyl ether, 2 parts by weight of AIBN, 13.0 parts by weight of acrylic acid, benzyl methacrylic in a flask equipped with a stirrer, thermometer reflux cooling tube, dropping funnel and nitrogen introduction tube 10 parts by weight of the rate, 57.0 parts by weight of styrene, 20 parts by weight of methyl methacrylate and 3 parts by weight of n-dodecyl mercapto were added and nitrogen substituted. Thereafter, the temperature of the reaction solution was raised to 110° C. with stirring, followed by reaction for 6 hours. The alkali-soluble resin thus synthesized had a solid content acid value of 100.2 mgKOH/g and a weight average molecular weight Mw of about 6,000 as measured by GPC.

<착색 감광성 수지 조성물의 제조><Production of colored photosensitive resin composition>

하기 표 1 및 2의 조성으로 실시예 및 비교예에 따른 착색 감광성 수지 조성물을 제조하였다.Colored photosensitive resin compositions according to Examples and Comparative Examples were prepared with the compositions shown in Tables 1 and 2 below.

구분
(중량%)division
(weight%) 실시예Example 1One 22 33 44 55 66 77 88 99 1010 1111 1212 AA A1A1 1.851.85 1.801.80 1.441.44 1.851.85 2.382.38 2.112.11 1.851.85 1.851.85 1.851.85 0.880.88 0.880.88 0.880.88 A2A2 1.041.04 0.330.33 0.660.66 0.490.49 0.660.66 0.330.33 A3A3 0.990.99 A4A4 0.960.96 0.500.50 0.330.33 0.660.66 A5A5 0.710.71 A6A6 A7A7 A8A8 0.220.22 0.110.11 0.330.33 A9A9 0.220.22 0.330.33 0.110.11 BB 29.1029.10 29.1829.18 29.3729.37 29.1529.15 29.2129.21 29.1829.18 29.1529.15 29.1529.15 29.1529.15 29.3429.34 29.3429.34 29.3429.34 CC 10.6410.64 10.6610.66 10.7110.71 10.6510.65 10.6610.66 10.6610.66 10.6510.65 10.6510.65 10.6510.65 10.6710.67 10.6710.67 10.6710.67 DD 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 EE 57.1657.16 57.1957.19 57.5657.56 57.1557.15 57.2157.21 57.1857.18 57.1557.15 57.1557.15 57.1557.15 58.4658.46 58.4658.46 58.4658.46 계total 100100 100100 100100 100100 100100 100100 100100 100100 100100 100100 100100 100100

구분division 비교예comparative example (중량%)(weight%) 1One 22 33 44 55 66 77 88 99 1010 AA A1A1 2.792.79 1.851.85 1.851.85 1.581.58 1.321.32 0.950.95 0.950.95 3.083.08 3.083.08 3.083.08 A2A2 1.221.22 1.521.52 A3A3 A4A4 A5A5 A6A6 0.990.99 A7A7 0.990.99 A8A8 1.11.1 0.760.76 0.510.51 1.021.02 A9A9 1.11.1 0.760.76 1.021.02 0.510.51 BB 29.1929.19 29.1529.15 29.1529.15 29.1429.14 29.1229.12 29.1529.15 29.0829.08 28.1628.16 28.2528.25 28.2528.25 CC 10.6510.65 10.6510.65 10.6510.65 10.6510.65 10.6510.65 10.6510.65 10.6110.61 10.5510.55 10.3910.39 10.3910.39 DD 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 0.210.21 EE 57.1657.16 57.1557.15 57.1557.15 57.257.2 57.1857.18 57.9457.94 58.0558.05 56.4856.48 56.5456.54 56.5456.54 계total 100100 100100 100100 100100 100100 100100 100100 100100 100100 100100

(A): 안료 분산 조성물(A): pigment dispersion composition

A1: 제조예 1의 안료 분산 조성물 M1, 유기카본블랙A1: Pigment dispersion composition M1 of Preparation Example 1, organic carbon black

A2: 제조예 2의 안료 분산 조성물 M2, 피그먼트 레드 177A2: Pigment dispersion composition M2 of Preparation Example 2, Pigment Red 177

A3: 제조예 3의 안료 분산 조성물 M3, 피그먼트 레드 254A3: Pigment dispersion composition M3 of Preparation Example 3, Pigment Red 254

A4: 제조예 4의 안료 분산 조성물 M4, 피그먼트 블루 15:6A4: Pigment dispersion composition M4 of Preparation Example 4, Pigment Blue 15:6

A5: 제조예 5의 안료 분산 조성물 M5, C.I. 피그먼트 바이올렛 23A5: Pigment dispersion composition M5 of Preparation Example 5, C.I. Pigment Violet 23

A6: 제조예 6의 안료 분산 조성물 M6, C.I. 피그먼트 그린 58A6: Pigment dispersion composition M6 of Preparation Example 6, C.I. Pigment Green 58

A7: 제조예 7의 안료 분산 조성물 M7, C.I. 피그먼트 옐로우 150A7: Pigment dispersion composition M7 of Preparation Example 7, C.I. Pigment Yellow 150

A8: 제조예 8의 안료 분산 조성물 M8, C.I. 피그먼트 블루 16A8: Pigment dispersion composition M8 of Preparation Example 8, C.I. Pigment Blue 16

A9: 제조예 9의 안료 분산 조성물 M9, C.I. 피그먼트 바이올렛 37 A9: Pigment dispersion composition M9 of Preparation Example 9, C.I. Pigment Violet 37

(B) 알칼리 가용성 수지: 합성예 1의 알칼리 가용성 수지(B) alkali-soluble resin: alkali-soluble resin of Synthesis Example 1

(C) 광중합성 화합물: 디펜타에리스리톨헥사아크릴레이트(KAYARD DPHA; 닛본 카야쿠 ㈜제조)(C) Photopolymerizable compound: dipentaerythritol hexaacrylate (KAYARD DPHA; manufactured by Nippon Kayaku Co., Ltd.)

(D) 광중합 개시제: 2-O-벤조일옥심-1-[4-(페닐티오)페닐]-1,2-옥탄디온 (OXE-01; BASF제조)(D) photoinitiator: 2-O-benzoyloxime-1-[4-(phenylthio)phenyl]-1,2-octanedione (OXE-01; manufactured by BASF)

(E) 용제 (프로필렌글리콜모노메틸에테르아세테이트)(E) solvent (propylene glycol monomethyl ether acetate)

<실험예><Experimental example>

상기 실시예 및 비교예에서 제조된 착색 감광성 수지 조성물을 이용하여 컬러필터를 제조하였다.A color filter was prepared using the colored photosensitive resin composition prepared in Examples and Comparative Examples.

실험예 1. 막 두께 측정Experimental Example 1. Film thickness measurement

구체적으로, 상기 각각의 착색 감광성 수지 조성물을 스핀 코팅법으로 2 인치각의 유리 기판(코닝社 제조, 「EAGLE XG」) 위에 도포한 다음, 가열판 위에 놓고 100 ℃의 온도에서 3 분간 유지하여 박막을 형성시켰다. 이어서 상기 박막 위에 투과율을 1 내지 100 %의 범위에서 계단상으로 변화시키는 패턴과 3 x 3 cm 노광부 패턴을 갖는 시험 포토마스크를 올려놓고 시험 포토마스크와의 간격을 100 ㎛로 하여 자외선을 조사하였다. 이때, 자외선 광원은 g, h, i 선을 모두 함유하는 1KW의 고압 수은등을 사용하여 100 mJ/㎠의 조도로 조사하였으며, 특별한 광학 필터는 사용하지 않았다. 상기 자외선이 조사된 박막을 THMA 2.38 % 수용액 현상 용액에 2 분 동안 담궈 현상하였다. 상기 박막이 도포된 유리판을 증류수를 사용하여 세척한 다음, 질소 가스를 불어서 건조하고, 100 ℃의 가열 오븐에서 60분간 가열하여 컬러필터를 제조하였다. 막두께는 막두께 측정장치(DEKTAK 6M; Veeco社 제조)를 사용하여 측정하였으며, 측정된 막 두께는 1.5 ㎛이었다.Specifically, each of the above colored photosensitive resin compositions was coated on a 2-inch square glass substrate (“EAGLE XG”, manufactured by Corning) by spin coating, placed on a heating plate, and maintained at a temperature of 100° C. for 3 minutes to form a thin film. formed. Then, a test photomask having a pattern of changing the transmittance in a range of 1 to 100% and a pattern of 3 x 3 cm exposed part was placed on the thin film, and ultraviolet rays were irradiated with an interval of 100 μm between the test photomask. . At this time, the ultraviolet light source was irradiated with an illuminance of 100 mJ/cm 2 using a 1KW high-pressure mercury lamp containing all of the g, h, and i lines, and no special optical filter was used. The thin film irradiated with ultraviolet light was immersed in a THMA 2.38% aqueous solution developing solution for 2 minutes to develop. The glass plate coated with the thin film was washed with distilled water, dried by blowing nitrogen gas, and heated in a heating oven at 100° C. for 60 minutes to prepare a color filter. The film thickness was measured using a film thickness measuring device (DEKTAK 6M; manufactured by Veeco), and the measured film thickness was 1.5 μm.

실험예 2. 특성 평가Experimental Example 2. Characteristic evaluation

2.1 투과율 측정2.1 Transmittance Measurement

분광은 상기 실험예 1과 시험 포토마스크를 사용하지 않은 것 이외는 동일하게 컬러필터를 제조한 후, 색도계(올림푸스社 제조, OSP-200)를 이용하여 투과율을 측정하였으며, 그 결과를 하기 표 2에 나타내었다. 또한, 색도계(올림푸스社 제조, OSP-200)를 이용하여 380 nm ~ 780 nm 범위의 가시광 영역에서의 스펙트럼 투과율을 측정하였으며, 그 결과를 표 3에 나타내었다.For spectroscopy, a color filter was prepared in the same manner as in Experimental Example 1 and the test photomask was not used, and then transmittance was measured using a colorimeter (manufactured by Olympus, OSP-200), and the results are shown in Table 2 below. shown in In addition, the spectral transmittance in the visible light region in the range of 380 nm to 780 nm was measured using a colorimeter (manufactured by Olympus, OSP-200), and the results are shown in Table 3.

2.2 반사율 측정2.2 Reflectance Measurement

상기 실험예 1과 시험 포토마스크를 사용하지 않은 것 이외는 동일하게 컬러필터를 제조한 후 코팅 면에 2 도 정반사율을 적분구 반사율 측정기 (코니카미놀타社, Spectrophotometer CM-3700d)를 통해 측정하였으며, 그 결과를 하기 표 3에 나타내었다. After preparing the color filter in the same manner as in Experimental Example 1 and that the test photomask was not used, the 2 degree specular reflectance on the coated surface was measured using an integrating sphere reflectance meter (Konica Minolta, Spectrophotometer CM-3700d), The results are shown in Table 3 below.

2.3 내광성 평가2.3 Light fastness evaluation

얻어진 도막을 내광성 시험기(선테스트 CPS+, 도요세이키社제)로 크세논 램프광을 48 시간 조사했다. 조사 전후에서 xy 색도좌표(x, y) 및 Y를 측정하고, 상기 측정값으로부터 JIS Z 8730:2009에 기재되는 방법으로 색차 △Eab*를 계산하고, 결과를 표 3에 나타냈다. △Eab*는 작을수록 색변화가 작은것을 의미하며, △Eab*가 3 이하인 경우, 그 도막은 컬러필터로서 실용상 문제 없다고 할 수 있다. 또한, 도막의 광성이 양호하면 같은 착색 경화성 수지 조성물로 제작된 패턴도 내광성은 양호하다고 할 수 있다.The obtained coating film was irradiated with a xenon lamp light with a light resistance tester (Suntest CPS+, manufactured by Toyo Seiki Co., Ltd.) for 48 hours. The xy chromaticity coordinates (x, y) and Y were measured before and after irradiation, and the color difference ΔEab* was calculated from the measured values by the method described in JIS Z 8730:2009, and the results are shown in Table 3. When ΔEab* is smaller, the color change is smaller, and when ΔEab* is 3 or less, it can be said that the coating film has practically no problem as a color filter. Moreover, if the light property of a coating film is favorable, it can be said that the light resistance of the pattern produced with the same colored curable resin composition is also favorable.

구성composition 막두께film thickness 반사율(%)reflectivity(%) 투과율(%)Transmittance (%) 내광성light fastness 전체 투과율total transmittance 380nm380nm 550nm550nm 650nm650nm (△Eab)(ΔEab) (%)(%) 실시예 1Example 1 1.5um1.5um 9.639.63 72.972.9 78.578.5 86.186.1 1.81.8 80.480.4 실시예 2Example 2 1.5um1.5um 9.629.62 72.572.5 80.780.7 80.280.2 1.51.5 80.380.3 실시예 3Example 3 1.5um1.5um 9.739.73 77.877.8 80.680.6 87.987.9 1.61.6 80.880.8 실시예 4Example 4 1.5um1.5um 9.899.89 77.377.3 8080 8787 1.41.4 82.182.1 실시예 5Example 5 1.5um1.5um 9.559.55 81.581.5 73.473.4 89.789.7 22 80.280.2 실시예 6Example 6 1.5um1.5um 9.69.6 72.872.8 79.479.4 85.185.1 1.81.8 80.880.8 실시예 7Example 7 1.5um1.5um 9.629.62 7373 79.979.9 83.283.2 1.71.7 80.580.5 실시예 8Example 8 1.5um1.5um 9.639.63 73.473.4 79.879.8 84.384.3 1.51.5 80.880.8 실시예 9Example 9 1.5um1.5um 9.619.61 72.672.6 8080 8282 1.51.5 80.380.3 실시예10Example 10 1.5um1.5um 9.589.58 77.977.9 78.778.7 84.484.4 0.90.9 80.380.3 실시예11Example 11 1.5um1.5um 9.559.55 78.278.2 80.180.1 83.383.3 0.70.7 80.680.6 실시예12Example 12 1.5um1.5um 9.429.42 78.278.2 80.180.1 83.383.3 0.10.1 80.880.8 비교예 1Comparative Example 1 1.5um1.5um 9.59.5 6969 78.278.2 81.181.1 2.12.1 78.778.7 비교예 2Comparative Example 2 1.5um1.5um 10.4510.45 76.776.7 84.884.8 8181 3.13.1 84.384.3 비교예 3Comparative Example 3 1.5um1.5um 10.8210.82 7777 84.984.9 8787 33 8585 비교예 4Comparative Example 4 1.5um1.5um 10.110.1 79.579.5 80.880.8 88.788.7 1.71.7 82.882.8 비교예 5Comparative Example 5 1.5um1.5um 10.1510.15 8282 81.381.3 90.590.5 1.61.6 83.683.6 비교예 6Comparative Example 6 1.5um1.5um 10.3310.33 85.785.7 88.488.4 82.382.3 1.51.5 86.186.1 비교예 7Comparative Example 7 1.5um1.5um 10.1810.18 83.483.4 77.477.4 9191 1.21.2 81.381.3 비교예 8Comparative Example 8 1.5um1.5um 8.558.55 64.864.8 67.267.2 73.573.5 1.31.3 67.967.9 비교예 9Comparative Example 9 1.5um1.5um 8.458.45 64.364.3 65.465.4 7474 1.21.2 67.267.2 비교예 10Comparative Example 10 1.5um1.5um 8.528.52 64.764.7 67.567.5 72.372.3 1.51.5 68.168.1

상기 표 3을 참조하면, 본원발명에 따른 흑색 안료 및 색재를 포함하는 실시예의 경우, 내광성이 우수하고, 각 파장영역 및 전체 파장에서의 투과율 및 반사율의 범위를 만족하는 것을 확인할 수 있다.Referring to Table 3, it can be confirmed that, in the case of Examples including the black pigment and the color material according to the present invention, the light resistance is excellent and the transmittance and reflectance ranges in each wavelength region and all wavelengths are satisfied.

그러나, 흑색 안료만을 포함하는 경우, 흑색 안료와 녹색 또는 황색 색재를 포함하는 경우 및 적색 색재의 함량이 과도한 경우, 본원발명에 따른 투과율 및 반사율 범위를 만족하지 못하는 것을 확인할 수 있다.However, when only the black pigment is included, when the black pigment and the green or yellow color material are included, and when the content of the red color material is excessive, it can be seen that the transmittance and reflectance ranges according to the present invention are not satisfied.

Claims (15)

(A) 색재; (B) 알칼리 가용성 수지; (C) 광중합성 화합물; (D) 광중합 개시제 및 (E) 용제를 포함하고,
상기 (A) 색재는 적색 색재, 청색 색재 및 자색 색재로 이루어진 군으로부터 선택되는 1종 이상의 색재와, 흑색 안료를 포함하며,
0.5 내지 3 ㎛의 두께인 막을 형성했을 때, 380 nm 내지 780 nm의 스펙트럼 파장에서의 전체 투과율이 80 % 이상인 것을 특징으로 하는, 착색 감광성 수지 조성물.
(A) colorant; (B) alkali-soluble resin; (C) a photopolymerizable compound; (D) a photoinitiator and (E) a solvent,
The (A) color material includes at least one color material selected from the group consisting of a red color material, a blue color material and a purple color material, and a black pigment,
A colored photosensitive resin composition, characterized in that when a film having a thickness of 0.5 to 3 µm is formed, the total transmittance at a spectral wavelength of 380 nm to 780 nm is 80% or more.
 제 1 항에 있어서,
상기 착색 감광성 수지 조성물로 형성된 착색 패턴의 반사율이 10 % 이하인 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
The colored photosensitive resin composition, characterized in that the reflectance of the colored pattern formed of the colored photosensitive resin composition is 10% or less.
 제 1 항에 있어서,
0.5 내지 3 ㎛의 두께로 막 형성시, 550 내지 590 nm의 스펙트럼 파장에서의 투과율이 80 % 이상인 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
When the film is formed to a thickness of 0.5 to 3 μm, the color photosensitive resin composition, characterized in that the transmittance at a spectral wavelength of 550 to 590 nm is 80% or more.
 제 1 항에 있어서,
상기 적색 색재, 청색 색재 및/또는 자색 색재는 본 발명의 착색 감광성 수지 조성물 총 중량에 대하여 0.3 내지 1.2 중량%로 포함되는 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
The red color material, the blue color material and / or the purple color material is characterized in that contained in 0.3 to 1.2% by weight based on the total weight of the colored photosensitive resin composition of the present invention, the colored photosensitive resin composition.
 제 1 항에 있어서,
착색 감광성 수지 조성물의 총 중량에 대하여,
상기 (A) 색재는 0.1 내지 3 중량%로 포함되는 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
With respect to the total weight of the colored photosensitive resin composition,
The (A) color material is characterized in that contained in 0.1 to 3% by weight, the colored photosensitive resin composition.
 제 1 항에 있어서,
상기 적색 색재는 C.I. 피그먼트 레드 177, C.I. 피그먼트 레드 179, C.I. 피그먼트 레드 209, C.I. 피그먼트 레드 242 및 C.I. 피그먼트 레드 254로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
The red color material is characterized in that it comprises one or more selected from the group consisting of CI pigment red 177, CI pigment red 179, CI pigment red 209, CI pigment red 242 and CI pigment red 254, A colored photosensitive resin composition.
 제 1 항에 있어서,
상기 청색 색재는 C.I. 피그먼트 블루 15:3, C.I. 피그먼트 블루 15:4, C.I. 피그먼트 블루 15:6, C.I. 피그먼트 블루 16, C.I. 피그먼트 블루 21, C.I. 피그먼트 블루 28, C.I. 피그먼트 블루 60, C.I. 피그먼트 블루 64 및 C.I. 피그먼트 블루 76으로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
The blue color material is CI Pigment Blue 15:3, CI Pigment Blue 15:4, CI Pigment Blue 15:6, CI Pigment Blue 16, CI Pigment Blue 21, CI Pigment Blue 28, CI Pigment Blue 60, CI Pigment Blue 64, and CI Pigment Blue 76 comprising at least one selected from the group consisting of, the colored photosensitive resin composition.
 제 1 항에 있어서,
상기 자색 색재는 C.I. 피그먼트 바이올렛 14, C.I. 피그먼트 바이올렛 19, C.I. 피그먼트 바이올렛 23, C.I. 피그먼트 바이올렛 29, C.I. 피그먼트 바이올렛 32, C.I. 피그먼트 바이올렛 33, C.I. 피그먼트 바이올렛 36, C.I. 피그먼트 바이올렛 37 및 C.I. 피그먼트 바이올렛 38로 이루어진 군으로부터 선택되는 1종 이상을 포함하는 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
The purple color material is CI Pigment Violet 14, CI Pigment Violet 19, CI Pigment Violet 23, CI Pigment Violet 29, CI Pigment Violet 32, CI Pigment Violet 33, CI Pigment Violet 36, CI Pigment Violet 37 and at least one selected from the group consisting of CI Pigment Violet 38, the colored photosensitive resin composition.
 제 1 항에 있어서,
상기 흑색 안료는 흑색 유기 안료인 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
The said black pigment is a black organic pigment, The coloring photosensitive resin composition characterized by the above-mentioned.
 제 9 항에 있어서,
상기 흑색 유기 안료는 적색, 청색 및 녹색 안료를 혼합한 안료, C.I. 피그먼트 블랙 1, C.I. 피그먼트 블랙 7, 유기 카본 블랙, 락탐 블랙, 페릴렌 블랙, 시아닌 블랙 및 아닐린 블랙으로 이루어진 군에서 선택되는 1종 이상을 포함하는 것을 특징으로 하는, 착색 감광성 수지 조성물.
10. The method of claim 9,
The black organic pigment is a pigment mixed with red, blue and green pigments, CI Pigment Black 1, CI Pigment Black 7, organic carbon black, lactam black, perylene black, cyanine black and aniline black selected from the group consisting of One or more types are included, The coloring photosensitive resin composition characterized by the above-mentioned.
 제 1 항에 있어서,
적색 색재, 청색 색재 및 자색 색재로 이루어진 군으로부터 선택되는 1종 이상의 색재와 흑색 안료의 중량비는 0.4:0.6 내지 0.1:0.9 인 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
The weight ratio of at least one color material selected from the group consisting of a red color material, a blue color material and a purple color material and a black pigment is 0.4:0.6 to 0.1:0.9, the colored photosensitive resin composition.
 제 1 항에 있어서,
크산텐계 화합물을 추가로 포함하는 것을 특징으로 하는, 착색 감광성 수지 조성물.
The method of claim 1,
A colored photosensitive resin composition, characterized in that it further comprises a xanthene-based compound.
 청구항 1 내지 12 중 어느 한 항의 착색 감광성 수지 조성물을 이용하여 제조된 컬러필터.
A color filter manufactured using the colored photosensitive resin composition of any one of claims 1 to 12.
 청구항 13의 컬러필터를 포함하는 디스플레이 소자.
A display device comprising the color filter of claim 13 .
 제 14 항에 있어서,
상기 디스플레이 소자는 플렉서블 디스플레이 소자인 것을 특징으로 하는, 디스플레이 소자.
15. The method of claim 14,
The display element is a flexible display element, characterized in that the display element.
KR1020220028080A 2021-03-08 2022-03-04 Colored photosensitive resin composition, color filter and display device comprising the same KR20220126228A (en)