KR20220113860A - Self-heating scalp functional cosmetic composition containing beauty salt and zeolite components and method for manufacturing the same - Google Patents

Abstract

The present invention relates to a functional cosmetic composition containing a zeolite component and a method for preparing the same. The present invention helps blood circulation, helps smooth discharge of cellulite, and is rich in minerals, which is good for moisturizing and exfoliating the skin. Also, the composition has cosmetic salt that is excellent for moisturizing, whitening, wrinkle alleviation, inflammation removal, and pore contraction, and has excellent waste removal with fine dust and heavy metal adsorption. The composition promotes the circulation of the skin cycle to improve skin conditions, and increases adsorption surface area by increasing the pore volume. The cosmetic composition of the present invention comprises cosmetic salt; zeolite; and cosmetic raw materials. The manufacturing method of the cosmetic composition comprises the steps of: a powder preparing step of preparing a fine zeolite powder or a ceramic powder containing zeolite; a cosmetic step of preparing cosmetic salt; and a composition raw material mixing step of mixing 3 to 10 parts by weight of the prepared powder, 2 to 5 parts by weight of cosmetic salt, and cosmetic raw materials as the remainder, wherein the fine zeolite powder or ceramic powder is treated by irradiating gamma rays.

Description

미용소금과 제올라이트 성분을 함유하는 자가 발열 두피 기능성 화장료 조성물 및 이의 제조 방법{Self-heating scalp functional cosmetic composition containing beauty salt and zeolite components and method for manufacturing the same}Self-heating scalp functional cosmetic composition containing beauty salt and zeolite components and method for manufacturing the same

본 발명은 기능성 화장료 조성물 및 이의 제조 방법에 관한 것으로, 더욱 상세하게는 피부 보습이 탁월하고, 미세먼지와 중금속 흡착력을 가져 노폐물 제거가 뛰어나고, 피부 주기의 순환을 촉진하여 피부 상태를 개선하며,세공 용적을 높여 흡착 표면적을 높이고, pH를 낮춰 피부 자극성이 거의 없는 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물 및 이의 제조 방법에 관한 것이다.The present invention relates to a functional cosmetic composition and a method for manufacturing the same, and more particularly, it has excellent skin moisturizing ability, has fine dust and heavy metal adsorption power, so it is excellent in removing waste products, and improves skin condition by promoting circulation of the skin cycle, The present invention relates to a functional cosmetic composition containing cosmetic salt and zeolite ingredients that have little skin irritation by increasing the volume to increase the adsorption surface area and lowering the pH, and to a method for preparing the same.

두피 스케일링은 열을 가해 피부의 신진대사와 혈액순환을 활달하게 하는 것이며, 피부 온도가 높아지면서 모공이 열리게 되므로 모공 속의 오래된 미세 먼지, 피지 노폐물, 또는 노화된 각질 세포를 제거하여 청결한 두피로 만들어 주고 두피를 유연하게 하여 거칠어짐을 방지하여 준다. 제올라이트 등의 세공성 토양구성광물을 흡착제로 사용하여 모공 속의 미세 먼지, 피지, 노폐물 등을 제거하기 위한 화장료 조성물이 종래 개발된 바 있다. 대한민국 등록특허공보 10-1659456에는 초미세먼지 차단용 기능성 크림이 개시되어 있다. 상기 공개특허는 맥반석, 제올라이트, 일라이트, 버미큘라이트 중 어느 1종 이상으로 선택되는 팽창성 광물입자를 포함하는 기능성크림을 개시하고 있다. 그러나 대한민국 등록특허공보 10-1659456에는 맥반석, 제올라이트, 일라이트, 버미큘라이트 등의 토양구성 광물은 세공을 가져 흡착제로 이용가치가 있지만, 그 세공에는 수분함량이 높고 미생물이 존재할 가능성이 커 화장료 조성물의 재료로 사용하기에는 부적합하다. 또한, 이들 토양구성광물은 약한 알칼리성을 띄고 있어 피부에 오래 적용해 있을 때 오히려 자극을 유발할가능성이 있다. 한편, 화장료 조성물이 사용되는 대표적인 제품으로는 클렌져가 있는데, 클렌져는 단순한 클렌징 기능에서 벗어나, 인체의 피부에 사용되는 만큼 보다 탁월한 기능을 갖는 연구가 이루어지고 있다.Scalp scaling activates the skin's metabolism and blood circulation by applying heat, and as the skin temperature rises, the pores open. It makes the scalp flexible and prevents roughness. A cosmetic composition for removing fine dust, sebum, waste, etc. in pores by using porous soil constituents such as zeolite as an adsorbent has been previously developed. Korean Patent No. 10-1659456 discloses a functional cream for blocking ultrafine dust. The above publication discloses a functional cream containing expandable mineral particles selected from any one or more of elvan, zeolite, illite, and vermiculite. However, in Korean Patent No. 10-1659456, soil constituent minerals such as elvan, zeolite, illite, and vermiculite have pores and are valuable as adsorbents, but the pores have a high moisture content and there is a high possibility that microorganisms are present in the pores, so the material of the cosmetic composition unsuitable for use as In addition, these soil constituent minerals have weak alkalinity, and may cause irritation when applied to the skin for a long time. On the other hand, there is a cleanser as a representative product in which the cosmetic composition is used, and research is being conducted on the cleanser to have a superior function as much as it is used on the skin of the human body, away from a simple cleansing function.

대한민국 등록특허공보 10-1659456Republic of Korea Patent Publication No. 10-1659456 대한민국 공개특허공보 10-2007-0006549Korean Patent Publication No. 10-2007-0006549 대한민국 공개특허공보 10-2011-0124457Republic of Korea Patent Publication No. 10-2011-0124457 대한민국 등록특허공보 10-09670739Republic of Korea Patent Publication No. 10-09670739

따라서, 상기한 종래의 문제점을 해결하기 위한 본 발명은, 피부 보습이 탁월하고, 미세먼지와 중금속 흡착력을 가져 노폐물 제거가 뛰어나고, 피부 주기의 순환을 촉진하여 두피 상태를 개선할 수 있는 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물 및 이의 제조 방법을 제공하는데 그 목적이 있다. 또한, 본 발명은 세공 용적을 높여 흡착 표면적을 높이고, 내부 세공의 미생물을 제거하고 pH를 낮춰 피부자극성이 거의 없으며 수분공급 성능이 뛰어난 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물 및 이의 제조 방법을 제공하는데 다른 목적이 있다. 또한, 본 발명은 미용소금과 제올라이트 성분이 갖는 기능에 더불어, 보조 기능성 물질의 성분을 통해 항균,항여드름, 피지조절 활성화를 도모할 수 있어 두피 건강에 더욱 도움을 줄 수 있는 기능성 화장료 조성물 및 이의 제조 방법을 제공하는데 또 다른 목적이 있다. 본 발명의 해결과제는 이상에서 언급한 것들에 한정되지 않으며, 언급되지 아니한 다른 해결과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다Therefore, the present invention for solving the above problems of the prior art is excellent in moisturizing the skin, has fine dust and heavy metal adsorption power, so it is excellent in removing wastes, and it is a cosmetic salt that can improve the scalp condition by promoting the circulation of the skin cycle and An object of the present invention is to provide a functional cosmetic composition containing a zeolite component and a method for preparing the same. In addition, the present invention provides a functional cosmetic composition containing beauty salt and zeolite ingredients with excellent moisture supply performance, which has little skin irritation by increasing the pore volume and increasing the adsorption surface area, removing microorganisms in the internal pores, and lowering the pH, and a method for manufacturing the same It serves another purpose to provide. In addition, the present invention provides a functional cosmetic composition that can further help scalp health by promoting antibacterial, anti-acne, and sebum control activation through components of auxiliary functional substances in addition to the functions of beauty salt and zeolite components, and functional cosmetic compositions thereof Another object is to provide a manufacturing method. The problems to be solved of the present invention are not limited to those mentioned above, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.

상기 본 발명의 목적들 및 다른 특징들을 달성하기 위한 본 발명의 일 관점에 따르면, 화장료 조성물로서, 미용소금과, 제올라이트, 및 화장품 원료를 포함하는 것을 특징으로 하는 미용소금과 제올라이트 성분을 함유 하는 기능성 화장료 조성물이 제공된다. 본 발명의 일 관점에 있어서, 상기 미용소금은 2중량% 내지 5중량%이고, 상기 제올라이트는 3중량% 내지 10 중량%이며, 화장품 원료 85중량% 내지 95중량%로 하는 조성 비율로 이루어지며, 상기 제올라이트는 0.3㎛ ~ 0.6 ㎛의 크기로 분쇄된 분말인 것이 바람직하다. 본 발명의 일 관점에 있어서, 상기 제올라이트는 감마선을 조사하여 처리된 것이고, 미생물 함량이 0 내지 50CFU/g이며, pH가 7 내지 7.2이며, 수분함량이 5중량% 내지 15중량%인 것이 바람직하다. 본 발명의 다른 관점에 따르면, 화장료 조성물로서, 미용소금과, 규소와 게르마늄의 비율인 Si/Ge 비가 중량 비로 5.0 내지 6.0인 게르마늄실리케이트 제올라이트와 장석 및 석영으로 이루어진 세라믹 분말, 및 화장품 원 료를 포함하고, 상기 미용소금은 2중량% 내지 5중량%이고, 상기 세라믹 분말은 3중량% 내지 10중량%이며, 화장품 원료를 85중량% 내지 95중량%로 하는 조성 비율로 이루어지고, 상기 세라믹 분말은 감마선을 조사하여 처리된 것이고, 미생물 함량이 0 내지 50CFU/g이며, pH가 7 내지 7.2이며, 수분함량이 5 내지 15%이며, 상기 세라믹 분말은 총 중량 기준으로, 게르마늄실리케이트 제올라이트 40중량% 내지 75중량%, 장석 10중량% 내지 30중량 %, 및 석영 15중량% 내지 30중량%로 이루어진 것을 특징으로 하는 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물이 제공된다. 본 발명의 다른 관점에 있어서, 상기 화장품 원료는 계면활성제를 포함하며, 상기 계면활성제는 코코-글루코사이드(Coco-glucoside), 데실글루코사이드(Decyl Glucoside), 포타슘코코에이트(Potassium Cocoate)에서 선택되는 하나의 천연 계면활성제인 것이 바람직하다. 본 발명의 다른 관점에 있어서, 상기 기능성 화장료 조성물은 미역 추출물, 코코넛 추출물, 구주소나무잎 추출물, 쇠비름 추출물, 동백나무꽃 추출물, 병풀 추출물 중 적어도 하나의 부가기능 추출물과, 하이드롤라이즈드 콜라겐 및 베타글루칸 중 적어도 하나 이상의 보조 기능성 물질, 및 호호바씨 오일 및 시어버터 중 적어도 하나의 수분유지 기능성 물질 중 적어도 하나를 더 포함할 수 있다. 본 발명의 다른 관점에 있어서, 상기 부가기능 추출물은 기능성 화장료 조성물의 100중량부에 대하여 3중량부 내지 7중량부로 혼합되며, 상기 보조 기능성 물질은 기능성 화장료 조성물의 100중량부에 대하여 2중량부 내지 4중량부로 혼합되며, 상기 수분유지 기능성물질은 기능성 화장료 조성물의 100중량부에 대하여 2중량부 내지 4 중량부로 혼합되는 것이 바람직하다. 본 발명의 또 다른 관점에 따르면, 화장료 조성물의 제조 방법으로서, 제올라이트 미세분말 또는 제올라이트를 포함하는 세라믹 분말을 마련하는 분말 마련 단계; 미용소금을 마련하는 미용소금 마련 단계; 및 상기 마련된 분말 3중량% 내지 약 10중량%와, 미용소금 2중량% 내지 5중량% 및 화장품 원료를 85중량% 내지 95중량% 로 하여 혼합하는 조성원료 혼합 단계;를 포함하고, 상기 제올라이트 미세분말 또는 세라믹 분말은 감마선을 조 사하여 처리된 것으로 이루어지는 것을 특징으로 하는 미용소금과 제올라이트 성분을 함유하는 기능성 화장 료 조성물의 제조 방법이 제공된다. 본 발명의 또 다른 관점에 있어서, 상기 분말 마련 단계에서 제올라이트 분말은 0.3㎛ ~ 0.6㎛의 크기로 분쇄된 분말로 마련되고, 상기 제올라이트 분말 또는 세라믹 분말은 pH가 7 내지 7.2이고, 상기 조성원료 혼합단계 이 전에서의 수분함량이 5% 내지 15%이며, 상기 조성원료 혼합 단계는 코코-글루코사이드(Coco-glucoside), 데실글루코사이드(Decyl Glucoside), 포타슘코코에이트(Potassium Cocoate)에서 선택되는 하나의 천연 계면활성제가 혼합 되는 것을 포함하는 것을 특징으로 하는 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 방법이 제공된다. 본 발명의 또 다른 관점에 있어서, 상기 조성원료 혼합 단계는 미역 추출물, 코코넛 추출물, 구주소나무잎 추출물, 쇠비름 추출물, 동백나무꽃 추출물, 병풀 추출물 중 적어도 하나의 부가기능 추출물과, 하이드롤라이즈드 콜라겐 및 베타글루칸 중 적어도 하나 이상의 보조 기능성 물질 및 호호바씨 오일 및 시어버터 중 적어도 하나의 수분유지 기능성 물질 중 적어도 하나가 혼합되는 것을 포함할 수 있다. 본 발명의 또 다른 관점에 있어서, 상기 부가기능 추출물은 기능성 화장료 조성물의 100중량부에 대하여 3중량 부 내지 7중량부로 혼합되며, 상기 보조 기능성 물질은 기능성 화장료 조성물의 100중량부에 대하여 2중량부 내 지 4중량부로 혼합되며, 상기 수분유지 기능성물질은 기능성 화장료 조성물의 100중량부에 대하여 2중량부 내지 4중량부로 혼합되는 것이 바람직하다. According to one aspect of the present invention for achieving the above objects and other features of the present invention, as a cosmetic composition, it is a cosmetic composition comprising a cosmetic salt, a zeolite, and a cosmetic raw material, characterized in that it contains a cosmetic salt and a zeolite component. A cosmetic composition is provided. In one aspect of the present invention, the cosmetic salt is 2% to 5% by weight, the zeolite is 3% to 10% by weight, and the composition ratio is 85% to 95% by weight of the cosmetic raw material, The zeolite is preferably a powder pulverized to a size of 0.3 μm to 0.6 μm. In one aspect of the present invention, the zeolite is processed by irradiating gamma rays, the microbial content is 0 to 50 CFU / g, the pH is 7 to 7.2, it is preferable that the moisture content is 5 wt% to 15 wt% . According to another aspect of the present invention, as a cosmetic composition, it includes cosmetic salt, a germanium silicate zeolite having a Si/Ge ratio of silicon and germanium in a weight ratio of 5.0 to 6.0, a ceramic powder made of feldspar and quartz, and a cosmetic raw material and the cosmetic salt is 2 wt% to 5 wt%, the ceramic powder is 3 wt% to 10 wt%, and the cosmetic raw material is composed of a composition ratio of 85 wt% to 95 wt%, and the ceramic powder is It is treated by irradiation with gamma rays, the microbial content is 0 to 50 CFU / g, the pH is 7 to 7.2, the moisture content is 5 to 15%, and the ceramic powder is, based on the total weight, germanium silicate zeolite 40 wt% to There is provided a functional cosmetic composition containing a cosmetic salt and a zeolite component, characterized in that it consists of 75% by weight, 10% by weight to 30% by weight of feldspar, and 15% by weight to 30% by weight of quartz. In another aspect of the present invention, the cosmetic raw material includes a surfactant, and the surfactant is one selected from coco-glucoside, decyl glucoside, and potassium cocoate. It is preferred that it is a natural surfactant. In another aspect of the present invention, the functional cosmetic composition is an additional functional extract of at least one of a seaweed extract, a coconut extract, an extract of guava extract, a purslane extract, a camellia flower extract, and a Centella asiatica extract, and hydrolyzed collagen and beta It may further include at least one of at least one auxiliary functional material of glucan, and at least one of at least one water retention functional material of jojoba seed oil and shea butter. In another aspect of the present invention, the additional functional extract is mixed in 3 parts by weight to 7 parts by weight based on 100 parts by weight of the functional cosmetic composition, and the auxiliary functional material is 2 parts by weight to 100 parts by weight of the functional cosmetic composition. It is mixed in 4 parts by weight, and the moisture-retaining functional material is preferably mixed in an amount of 2 to 4 parts by weight based on 100 parts by weight of the functional cosmetic composition. According to another aspect of the present invention, there is provided a method for preparing a cosmetic composition, comprising: a powder preparation step of preparing a zeolite fine powder or a ceramic powder containing zeolite; beauty salt preparation step of preparing beauty salt; and 3 wt% to about 10 wt% of the powder, 2 wt% to 5 wt% of cosmetic salt, and 85 wt% to 95 wt% of cosmetic raw material mixing step of mixing; including, the zeolite fine There is provided a method for producing a functional cosmetic composition containing cosmetic salt and a zeolite component, characterized in that the powder or ceramic powder is treated by irradiating gamma rays. In another aspect of the present invention, in the powder preparation step, the zeolite powder is prepared as a powder pulverized to a size of 0.3 μm to 0.6 μm, the zeolite powder or ceramic powder has a pH of 7 to 7.2, and the composition raw material is mixed The moisture content before the step is 5% to 15%, and the step of mixing the raw material is one natural selected from coco-glucoside, decyl glucoside, and potassium cocoate. There is provided a method for producing a functional cosmetic composition containing cosmetic salt and a zeolite component, comprising mixing a surfactant. In another aspect of the present invention, the step of mixing the ingredients includes at least one additional functional extract of seaweed extract, coconut extract, old jujube leaf extract, purslane extract, camellia flower extract, centella asiatica extract, and hydrolyzed collagen And at least one auxiliary functional substance of beta-glucan and at least one of at least one moisture retention functional substance of jojoba seed oil and shea butter is mixed. In another aspect of the present invention, the additional functional extract is mixed in 3 parts by weight to 7 parts by weight based on 100 parts by weight of the functional cosmetic composition, and the auxiliary functional material is 2 parts by weight based on 100 parts by weight of the functional cosmetic composition to 4 parts by weight, and the moisture-retaining functional material is preferably mixed in an amount of 2 to 4 parts by weight based on 100 parts by weight of the functional cosmetic composition.

본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물 및 이의 제조 방법에 의하면, 미용소금과 제올라이트 성분이 갖는 탁월한 기능으로 두피를 촉촉하고 생기 넘치게 가꿀 수 있으며, 두피 수렴에도 도움을 줄 수 있는 효과가 있다. 또한, 본 발명에 의하면, 민감성 두피 진정, 노폐물 제거 및 탁월한 피부 보습이 가능한 효과가 있다. 또한, 본 발명에 의하면, 세공 용적을 높여 흡착 표면적을 높이고, 내부 세공의 미생물을 제거하고 pH를 낮춰 피부자극성이 거의 없으며 수분공급 성능이 뛰어난 효과가 있다. 또한, 본 발명에 의하면, 보조 기능성물질의 성분을 통해 피부진정, 피부회복, 항산화, 피부활력, 모공케어, 피지조절, 생기부여, 피부 결케어, 피부 윤기 및 항염을 도모할 수 있어 두피 건강에 더욱 도움을 줄 수 있는 효과가 있다. 본 발명의 효과는 이상에서 언급된 것들에 한정되지 않으며, 언급되지 아니한 다른 해결과제들은 아래의 기재로부터 당업자에게 명확하게 이해되어 질 수 있을 것이다According to the functional cosmetic composition containing beauty salt and zeolite component according to the present invention and a manufacturing method thereof, it is possible to make the scalp moist and lively with the excellent function of the cosmetic salt and zeolite component, and to help the scalp convergence. It works. In addition, according to the present invention, there are effects that can soothe the sensitive scalp, remove wastes, and provide excellent skin moisturizing. In addition, according to the present invention, there is an effect of increasing the adsorption surface area by increasing the pore volume, removing microorganisms in the internal pores, and lowering the pH to have little skin irritation and excellent moisture supply performance. In addition, according to the present invention, it is possible to promote skin soothing, skin recovery, antioxidant, skin vitality, pore care, sebum control, vitality, skin texture care, skin gloss and anti-inflammatory through the components of auxiliary functional substances, thereby improving scalp health. There are more ways to help. Effects of the present invention are not limited to those mentioned above, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.

도 1은 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 과정을 나타내는 플로차트이다. 도 2는 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 예시에 따른조성을 나타내는 표이다.1 is a flowchart showing a manufacturing process of a functional cosmetic composition containing cosmetic salt and a zeolite component according to the present invention. 2 is a table showing the composition according to an example of the preparation of a functional cosmetic composition containing cosmetic salt and zeolite components according to the present invention.

본 발명의 추가적인 목적들, 특징들 및 장점들은 다음의 상세한 설명 및 첨부도면으로부터 보다 명료하게 이해될 수 있다. 본 발명의 상세한 설명에 앞서, 본 발명은 다양한 변경을 도모할 수 있고, 여러 가지 실시 예를 가질 수 있는 바, 아래에서 설명되고 도면에 도시된 예시들은 본 발명을 특정한 실시 형태에 대해 한정하려는 것이 아니며, 본 발명의 사상 및 기술 범위에 포함되는 모든 변경, 균등물 내지 대체물을 포함하는 것으로 이해되어야 한다. 어떤 구성요소가 다른 구성요소에 "연결되어" 있다거나 "접속되어" 있다고 언급된 때에는, 그 다른 구성요소에 직접적으로 연결되어 있거나 또는 접속되어 있을 수도 있지만, 중간에 다른 구성요소가 존재할 수도 있다고 이 해되어야 할 것이다. 반면에, 어떤 구성요소가 다른 구성요소에 "직접 연결되어" 있다거나 "직접 접속되어" 있다고 언급된 때에는, 중간에 다른 구성요소가 존재하지 않는 것으로 이해되어야 할 것이다. 본 명세서에서 사용한 용어는 단지 특정한 실시 예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도는 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요 소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다. 이하, 본 발명의 바람직한 실시 예에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물 및 이의 제조 방법에 대하여 설명한다. 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물은, 미용소금과 제올라이트 분말 및 및 화장품 원료를 포함한다. 바람직하게, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물은, 미용소금은 약 2중량% 내지 5중량%이고, 제올라이트 분말은 약 3중량% 내지 약 10중량%이며, 화장품 원료를 잔부(약 85 중량% 내지 약 95 중량%)로 하는 조성 비율로 이루어지는 것을 특징으로 한다. 상기 미용소금은 항균활성이 탁월하며 pH안정성이 항균활성을 돕고, 자극으로부터 피부를 보호하는 기능을 갖는다. 특히, 피부 컨디셔닝 역할을 하여 생기 있고 활력 있는 피부로 케어해 주며, 피부 주기의 순환을 촉진하는데 관여하여 피부 상태를 개선하고 건강하게 가꾸는데 도움을 준다. 다음으로, 상기 제올라이트는 0.3㎛ ~ 0.6㎛의 크기로 분쇄된 분말의 것이 사용되며, 0.5㎛인 것이 바람직하다. 여기에서, 상기 제올라이트(제올라이트 분말)는 감마선을 조사하여 처리된 것일 수 있다. 상기 감마선은 특별히 제한되는 것은 아니지만 60 Co 또는 137 Cs에서 방출되는 감마선일 수 있다. 바람직하게, 상기 제올라이트는 60 Co 또는 137 Cs에서 방출되는 감마선을 흡수선량 기준으로 약 1k 내지 약 50k로 조사하여 처리된 것일 수 있다. 상기 제올라이트의 감마선 흡수선량은, 예를 들어, 약 1k 내지 약 50k, 약 1k 내지 약 40k, 약 1k 내지 약 30k, 약 1k 내지 약 20k, 약 1k 내지 약 10k, 약 10k 내지 약 50k, 약 20k 내지 약 50k, 약 30k 내지 약 50k, 약 40k 내지 약 50k, 또는 약 10k 내지 약 30k일 수 있다. 감마선 처리 시간은, 예를 들어, 약 10분 내지 약 120분일 수 있으나, 이에 한정되는 것은 아니다. 또한, 상기 제올라이트는 미생물 함량이 0 CFU/g 내지 약 50 CFU/g인 것일 수 있다. 화장료 조성물에 사용하기 위한 제올라이트 분말은 100 CFU/g 이하로 미생물을 포함하는 것이 적합한데, 상기한 감마선 처리에 의해 제올 라이트 분말의 미생물 저하 효과를 구현할 수 있게 된다. 또한, 상기 제올라이트 분말은 pH가 약 7 내지 약 7.2인 것일 수 있는데, 이러한 제올라이트 분말은 감마선 처 리에 의해서 pH가 저하된 것일 수 있다. 또한, 상기 제올라이트 분말은 화장품 원료와 혼합되기 전의 수분함량이 약 5중량% 내지 약 15중량%인 것이 바 람직하다. 상기 제올라이트 분말은 세공을 가져 물을 흡수하는 성질을 가지는데, 화장품 원료와 혼합되면 물을 흡수하여 세공에 물을 머금은 상태가 될 수 있다. 화장품 원료와 혼합되어 세공에 물을 머금은 상태의 제올라이트 분말은 피부에 적용하여 롤링하게 되면 세공에서 피부로 물을 내놓고, 피부에 존재하는 미세먼지, 피지, 또는 각질을 세공이 흡착하게 된다. 한편, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물은, 상기 제올라이트 분 말 대신에 제올라이트를 포함하는 세라믹 분말로 이루어질 수 있으며, 이때 세라믹 분말은 부피 가중평균직경이 약 0.1 내지 약 10인 세라믹 분말인 것이 바람직하다. 상기 세라믹 분말은 또한 감마선을 조사하여 처리된 것일 수 있는데, 상기 감마선은 특별히 제한되는 것은 아니 지만 60 Co 또는 137 Cs에서 방출되는 감마선일 수 있다. 또한, 상기 세라믹 분말은 60 Co 또는 137 Cs에서 방출되는 감마선을 흡수선량 기준으로 약 1k 내지 약 50k로 조사하여 처리된 것일 수 있다. 상기 세라믹 분말의 감마선 흡수선량은, 예를 들어, 약 1k 내지 약 50k, 약 1k 내지 약 40k, 약 1k 내지 약 30k, 약 1k 내지 약 20k, 약 1k 내지 약 10k, 약 10k 내지 약 50k, 약 20k 내지 약 50k, 약 30k 내지 약 50k, 약 40k 내지 약 50k, 또는 약 10k 내지 약 30k일 수 있다. 감마선 처리 시간은, 예를 들어, 약 10분 내지 약 120분일 수 있으나, 이에 한정되는 것은 아니다. 여기에서, 상기 세라믹 분말은 규소와 게르마늄의 비율인 Si/Ge비가 중량비로 1: 5.0 내지 6.0, 바람직하게는 5.3 내지 5.5인 게르마늄실리케이트 제올라이트, 장석, 및 석영으로 이루어진 것일 수 있다. 여기에서, 상기 게르마늄실리케이트 제올라이트의 Si/Ge 비가 5.0 미만이면 세공의 크기가 너무 작은 미세세공의 비율이 높아져 먼지, 피지, 또는 각질 등이 세공 입구를 통과하지 못할 가능성이 커지고, 6.0 초과이면 중형 세공의 비율이 너무 높아져 전체 표면적이 감소함으로써 흡착 면적이 감소로 인해 화장료 조성물의 주요 성능이 떨어질 수 있다. 또한, 상기 세라믹 분말은 미생물 함량이 약 0 CFU/g 내지 약 50 CFU/g인 것일 수 있다. 화장료 조성물에 사용하기 위한 세라믹 분말은 100 CFU/g 이하로 미생물을 포함하는 것이 적합하다. 세라믹 분말에 포함된 장석, 석 영 등은 미생물 함량이 높아 화장료 조성물의 재료로 부적합할 수 있으며, 이러한 미생물로 인해 게르마늄실리 케이트 제올라이트의 세공이 막혀 흡착력과 직결되는 게르마늄실리케이트 제올라이트의 표면적이 감소할 수 있다. 본 발명에서 세라믹 분말은 감마선 처리하여 미생물 함량을 저하시킨 것을 사용하는 것이 바람직하며, 상기한 감마선 처리에 의해 세라믹 분말의 미생물 저하 효과를 구현할 수 있게 된다. 또한, 상기 세라믹 분말은 pH가 약 7 내지 약 7.2인 것일 수 있다. 상기 세라믹 분말은 감마선 처리에 의해서 pH가 저하된 것일 수 있다. 상기 세라믹 분말은 총 중량 기준으로, 게르마늄실리케이트 제올라이트 약 40중량% 내지 약 75중량%, 장석 약 10중량% 내지 약 30중량%, 및 석영 약 15중량% 내지 약 30중량%로 이루어진 것일 수 있다. 상기 세라믹 분말은, 상기 장석 외에 장석이 변질되어 생성된 점토 광물인 스멕타이트(smectite)를 포함할 수도 있으며, 상기 석영 외에 오팔을 포함할 수도 있다. 또한, 상기 세라믹 분말은 화장품 원료와 혼합되기 전의 수분함량이 약 5중량% 내지 약 15중량%인 것이 바람직 하며, 이러한 세라믹 분말은 세공을 가져 물을 흡수하는 성질을 가지는데, 화장품 원료와 혼합되면 물을 흡수하 여 세공에 물을 머금은 상태가 될 수 있다. 화장품 원료와 혼합되어 세공에 물을 머금은 상태의 세라믹 분말은 피부에 적용하여 롤링하게 되면 세공에서 피부로 물을 내놓고, 피부에 존재하는 미세먼지, 피지, 또는 각질을 세공이 흡착하게 된다. 계속해서, 상기 화장품 원료는 정제수, 유지성분, 보습제, 에몰리엔트제, 계면활성제, 킬레이팅제, 안료, 자외 선흡수제, 방부제, 살균제, 산화방지제, pH조절제, 알코올, 및 향료로 이루어진 군으로부터 선택된 하나 이상을 포함할 수 있으나, 이에 제한되지 않을 수 있다. 여기에서, 본 발명은 계면활성제에 있어서 코코-글루코사이드(Coco-glucoside), 데실글루코사이드(Decyl Glucoside), 포타슘코코에이트(Potassium Cocoate)에서 선택되는 하나의 천연 계면활성제가 적용된다. 한편, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물은, 미역 추출물, 코코넛 추출물, 구주소나무잎 추출물, 쇠비름 추출물, 동백나무꽃 추출물, 병풀 추출물 중 적어도 하나의 부가기능 추출물을 더 포함할 수 있다. 이러한 부가기능 추출물은 상기한 기능성 화장료 조성물의 100중량부에 대하여 약 3중량부 내지 7중량부, 바람직하게는 5중량부로 혼합되는 것이 바람직하다. 여기에서, 본 발명은 상기 부가기능 추출물을 마련함에 있어 해당 구성요소에 따라 최적의 추출방법, 예를 들면 초음파 추출 방법, 초임계 추출 방법 등을 통해 추출할 수 있다. 여기에서, 초음파 추출물이라 함은 건조 분쇄한 추출 대상물을 초음파 추출 방법을 이용하여 추출하여 제조된 추출물을 의미한다. 또한, 초임계 추출이라 함은 건조하여 파쇄한 추출 대상물과 보조용매로 에탄올(99.5%) 500~700mL를 초임계 유체 추출 반응기(Natex, Autstria)에 넣고 반응기 내의 온도가 65℃압력이 450 bar, S/F 비(supercritical fluid ㎏/Feed ㎏) 35가 되는 조건하에서 추출하는 방법을 의미한다. 한편, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물은, 하이드롤라이즈드 콜라겐 및 베타글루칸 중 적어도 하나 이상의 보조 기능성 물질을 더 포함할 수 있다. 여기에서, 상기 보조 기능성 물질은 상기한 부가기능 추출물을 포함하는 기능성 화장료 조성물이나 부가기능 추출물을 포함하지 않는 기능성 화장료 조성물에 포함될 수 있다. 상기 보조 기능성 물질에서 하이드롤라이즈드 콜라겐은 인간피부에서 발견되는 콜라겐과 동일한 성질을 지니고 있어 인체 흡수율이 탁월하고, 피부 탄력 개선과 주름 개선의 효과가 있으며, 상기 베타글루칸은 풍부한 영양 성분을 피부에 전달해주고 수분을 보유하여 촉촉하고 탄력있는 피부 관리에 도움을 주며 예민해진 피부를 편안 하게 진정시키고, 피부 컨디셔닝 및 면역력 향상에 관여하여 건강한 피부 관리에 도움을 준다. 상기 보조 기능성 물질(제1 기능성 물질)은 상기한 기능성 화장료 조성물(부가기능 추출물을 포함하는 기능성 화장료 조성물이나 부가기능 추출물을 포함하지 않는 기능성 화장료 조성물)의 100중량부에 대하여 약 2중량부 내지 4중량부, 바람직하게는 3중량부로 혼합되는 것이 바람직하다. 한편, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물은, 마카다미아씨 오일 및 비즈왁스 중 적어도 하나의 수분유지 기능성 물질을 더 포함할 수 있다. 상기 마카다미아씨 오일은 피부의 수분 증발을 차단하는 장벽 기능을 하고, 비즈왁스는 피부에 보호막을 형성하 여 수분이 날아가지 않도록 한다. 상기 수분유지 기능성물질은 상기한 기능성 화장료 조성물(부가기능 추출물을 포함하는 기능성 화장료 조성물이 나 부가기능 추출물을 포함하지 않는 기능성 화장료 조성물)의 100중량부에 대하여 약 2중량부 내지 4중량부, 바람직하게는 3중량부로 혼합되는 것이 바람직하다. 다음으로, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 방법에 대 하여 도 1을 참조하여 상세히 설명한다. 도 1은 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 과정을 나타내는 플로차트이다. 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 방법은, 도 1에 낸 바와 같이, 제올라이트 미세분말을 마련하는 제올라이트 분말 마련 단계(S100); 미용소금을 마련하는 미용소금 마련 단계(S200); 및 상기 마련된 제올라이트 분말 약 3중량부 내지 약 10중량부와, 미용소금 약 2 중량부 내지 5중량부 및 화장품 원료를 잔부로 하여 혼합하는 조성원료 혼합 단계(S300);를 포함한다. 상기 제올라이트 분말 마련 단계(S100)는 0.3㎛ ~ 0.6㎛의 크기로 분쇄된 분말로 마련되며, 0.5㎛인 분말로 마련되는 것이 바람직하다. 본 발명에서 제올라이트 분말은 제올라이트 파쇄물을 분쇄하여 마련되는데, 이때 제올라이트 파쇄물 또는 제올라이트 분말(이하, "제올라이트"로 통칭함)에 감사선을 조사한 후 분쇄하여 마련되는 제올라이트 감마선 처리단 계(S110)를 더 포함할 수 있다. 상기 제올라이트 감마선 처리 단계(S110)에서 감마선은 특별히 제한되는 것은 아니지만 60 Co 또는 137 Cs에서 방출되는 감마선일 수 있다. 바람직하게, 상기 제올라이트 감마선 처리 단계(S110)에서 제올라이트는 60 Co 또는 137 Cs에서 방출되는 감마 선을 흡수선량 기준으로 약 1k 내지 약 50k로 조사하여 처리된 것일 수 있다. 상기 제올라이트의 감마선 흡수선 량은, 예를 들어, 약 1k 내지 약 50k, 약 1k 내지 약 40k, 약 1k 내지 약 30k, 약 1k 내지 약 20k, 약 1k 내지 약 10k, 약 10k 내지 약 50k, 약 20k 내지 약 50k, 약 30k 내지 약 50k, 약 40k 내지 약 50k, 또는 약 10k 내 지 약 30k일 수 있다. 감마선 처리 시간은, 예를 들어, 약 10분 내지 약 120분일 수 있으나, 이에 한정되는 것은 아니다. 또한, 상기 제올라이트 분말 마련 단계(S100)에서 제올라이트는 미생물 함량이 0 CFU/g 내지 약 50 CFU/g인 것 일 수 있다. 화장료 조성물에 사용하기 위한 제올라이트 분말은 100 CFU/g 이하로 미생물을 포함하는 것이 적합 한데, 상기한 감마선 처리에 의해 제올라이트 분말의 미생물 저하 효과를 구현할 수 있게 된다. 또한, 상기 제올라이트 분말 마련 단계(S110)에서 제올라이트는 pH가 약 7 내지 약 7.2인 것으로 마련될 수 있는데, 이러한 제올라이트는 상기한 감마선 처리에 의해서 pH가 저하된 것일 수 있다. 또한, 상기 제올라이트 분말은 조성원료 혼합단계(S300) 이전에서의 수분함량이 약 5중량% 내지 약 15중량%인 것이 바람직하다. 상기 제올라이트는 세공을 가져 물을 흡수하는 성질을 가지는데, 화장품 원료와 혼합되면 물을 흡수하여 세공에 물을 머금은 상태가 될 수 있다. 화장품 원료와 혼합되어 세공에 물을 머금은 상태의 제올라이트 분말은 피부에 적용하여 롤링하게 되면 세공에서 피부로 물을 내놓고, 피부에 존재하는 미세먼지, 피지, 또는 각질을 세공이 흡착하게 된다. 한편, 본 발명의 기능성 화장료 조성물의 제조 방법에서, 상기 제올라이트 대신에, 세라믹 분말로 마련될 수 있다. 여기에서, 세라믹 분말로 마련되는 경우, 세라믹 분말이 규소와 게르마늄의 비율인 Si/Ge 비가 중량비로 5.0 내 지 6.0, 바람직하게는 5.3 내지 5.5인 게르마늄실리케이트 제올라이트, 장석, 및 석영으로 이루어진 것이 되도록 마련된다. 이때, 상기 게르마늄실리케이트 제올라이트의 Si/Ge 비가 5.0 미만이면 세공의 크기가 너무 작은 미세세공의 비 율이 높아져 먼지, 피지, 또는 각질 등이 세공 입구를 통과하지 못할 가능성이 커지고, 6.0 초과이면 중형세공의 비율이 너무 높아져 전체 표면적이 감소함으로써 흡착 면적이 감소로 인해 화장료 조성물의 주요 성능이 떨 어질 수 있다. 상기 세라믹 분말은 총 중량 기준으로, 게르마늄실리케이트 제올라이트 약 40중량% 내지 약 75중량%, 장석 약 10중량% 내지 약 30중량%, 및 석영 약 15중량% 내지 약 30중량%로 이루어진 것일 수 있다. 상기 세라믹 분말은 장석 외에 장석이 변질되어 생성된 점토 광물인 스멕타이트(smectite)를 포함할 수도 있으며, 상기 석영 외에 오팔을 포함할 수도 있다. 다음으로, 상기 미용소금 마련 단계(S200)에서 마련되는 미용소금은 화장품 원료로 효능이 입증된 씨솔트 혹은 히말라야솔트로 마련된다. 계속해서, 상기 조성원료 혼합 단계(S400)에서 혼합되는 화장품 원료는 정제수, 유지성분, 보습제, 에몰리엔트제, 계면활성제, 킬레이팅제, 안료, 자외선흡수제, 방부제, 살균제, 산화방지제, pH조절제, 알코올, 및 향료로 이루어진 군으로부터 선택된 하나 이상을 포함할 수 있으나, 이에 제한되지 않을 수 있다. 한편, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 방법은, 상기 조성원료 혼합 단계(S400)에서 미역 추출물, 코코넛 추출물, 구주소나무잎 추출물, 쇠비름 추출물, 동백나무꽃 추출물, 병풀 추출물을 더 혼합 하는 것을 포함할 수 있다. 상기 부가기능 추출물은 상기한 혼합물의 100중량부에 대하여 약 3중량부 내지 7중량부, 바람직하게는 5중량부 로 혼합되는 것이 바람직하다. 상기 부가기능 추출물을 마련함에 있어 해당 구성요소에 따라 최적의 추출방법, 예를 들면 초음파 추출 방법, 초임계 추출 방법 등을 통해 추출할 수 있다. Additional objects, features and advantages of the present invention may be more clearly understood from the following detailed description and accompanying drawings. Prior to the detailed description of the present invention, the present invention can make various changes and can have various embodiments, and the examples described below and shown in the drawings are not intended to limit the present invention to specific embodiments. No, it should be understood to include all modifications, equivalents, and substitutes included in the spirit and scope of the present invention. When a component is referred to as being “connected” or “connected” to another component, it may be directly connected or connected to the other component, but other components may exist in between. it will have to be done On the other hand, when it is said that a certain element is "directly connected" or "directly connected" to another element, it should be understood that the other element does not exist in the middle. The terms used herein are used only to describe specific embodiments, and are not intended to limit the present invention. The singular expression includes the plural expression unless the context clearly dictates otherwise. In the present specification, terms such as “comprise” or “have” are intended to designate that a feature, number, step, operation, component, part, or combination thereof described in the specification exists, but one or more other features It is to be understood that this does not preclude the possibility of addition or existence of numbers, steps, operations, components, parts, or combinations thereof. Hereinafter, a functional cosmetic composition containing cosmetic salt and a zeolite component according to a preferred embodiment of the present invention and a manufacturing method thereof will be described. The functional cosmetic composition containing cosmetic salt and zeolite ingredients according to the present invention includes cosmetic salt, zeolite powder, and cosmetic raw materials. Preferably, in the functional cosmetic composition containing cosmetic salt and zeolite component according to the present invention, the cosmetic salt is about 2% to 5% by weight, the zeolite powder is about 3% to about 10% by weight, and the cosmetic raw material is It is characterized in that it consists of a composition ratio of the balance (about 85% by weight to about 95% by weight). The cosmetic salt has excellent antibacterial activity, pH stability helps antibacterial activity, and has a function of protecting the skin from irritation. In particular, it plays a role in conditioning the skin to care for the skin with vitality and vitality, and by participating in promoting the circulation of the skin cycle, it helps to improve the skin condition and make it healthy. Next, as the zeolite, a powder pulverized to a size of 0.3 µm to 0.6 µm is used, and preferably 0.5 µm. Here, the zeolite (zeolite powder) may be treated by irradiating gamma rays. The gamma rays are not particularly limited, but may be gamma rays emitted at 60 Co or 137 Cs. Preferably, the zeolite may be treated by irradiating gamma rays emitted at 60 Co or 137 Cs at about 1k to about 50k based on the absorbed dose. The absorbed dose of gamma rays of the zeolite is, for example, about 1k to about 50k, about 1k to about 40k, about 1k to about 30k, about 1k to about 20k, about 1k to about 10k, about 10k to about 50k, about 20k to about 50k, about 30k to about 50k, about 40k to about 50k, or about 10k to about 30k. The gamma-ray treatment time may be, for example, about 10 minutes to about 120 minutes, but is not limited thereto. In addition, the zeolite may have a microbial content of 0 CFU/g to about 50 CFU/g. It is suitable that the zeolite powder for use in the cosmetic composition contains microorganisms at an amount of 100 CFU/g or less. In addition, the zeolite powder may have a pH of about 7 to about 7.2, and the zeolite powder may have a pH lowered by gamma-ray treatment. In addition, the zeolite powder preferably has a moisture content of about 5% to about 15% by weight before mixing with the cosmetic raw material. The zeolite powder has pores and has a property of absorbing water, and when mixed with cosmetic raw materials, it can absorb water and become a state in which water is contained in the pores. When the zeolite powder mixed with cosmetic raw materials is applied to the skin and rolled, water is released from the pores to the skin and the pores adsorb fine dust, sebum, or dead skin cells present on the skin. On the other hand, the functional cosmetic composition containing the cosmetic salt and the zeolite component according to the present invention may be made of a ceramic powder containing a zeolite instead of the zeolite powder, wherein the ceramic powder has a volume-weighted average diameter of about 0.1 to about 10 It is preferable that it is phosphorus ceramic powder. The ceramic powder may also be treated by irradiating gamma rays, and the gamma rays are not particularly limited, but may be gamma rays emitted from 60 Co or 137 Cs. In addition, the ceramic powder may be treated by irradiating gamma rays emitted at 60 Co or 137 Cs at about 1k to about 50k based on the absorbed dose. The absorbed dose of gamma rays of the ceramic powder is, for example, about 1k to about 50k, about 1k to about 40k, about 1k to about 30k, about 1k to about 20k, about 1k to about 10k, about 10k to about 50k, about 20k to about 50k, about 30k to about 50k, about 40k to about 50k, or about 10k to about 30k. The gamma-ray treatment time may be, for example, about 10 minutes to about 120 minutes, but is not limited thereto. Here, the ceramic powder may be made of germanium silicate zeolite, feldspar, and quartz having a Si/Ge ratio of silicon and germanium in a weight ratio of 1: 5.0 to 6.0, preferably 5.3 to 5.5. Here, if the Si/Ge ratio of the germanium silicate zeolite is less than 5.0, the proportion of micropores with too small pore size increases, so that dust, sebum, or dead skin cells cannot pass through the pore entrance. If it exceeds 6.0, medium pores The ratio of is too high and the total surface area is reduced, so that the main performance of the cosmetic composition may be deteriorated due to a decrease in the adsorption area. In addition, the ceramic powder may have a microbial content of about 0 CFU/g to about 50 CFU/g. It is suitable that the ceramic powder for use in the cosmetic composition contains microorganisms in an amount of 100 CFU/g or less. Feldspar, quartz, etc. contained in the ceramic powder may be unsuitable as a material for cosmetic compositions due to their high microbial content, and these microorganisms block the pores of the germanium silicate zeolite and reduce the surface area of the germanium silicate zeolite, which is directly related to the adsorption capacity. have. In the present invention, it is preferable to use a ceramic powder in which the content of microorganisms is reduced by gamma-ray treatment, and it is possible to realize the effect of reducing microorganisms of the ceramic powder by the gamma-ray treatment. In addition, the ceramic powder may have a pH of about 7 to about 7.2. The ceramic powder may have a pH lowered by gamma-ray treatment. The ceramic powder may be composed of about 40 wt% to about 75 wt% of germanium silicate zeolite, about 10 wt% to about 30 wt% of feldspar, and about 15 wt% to about 30 wt% of quartz based on the total weight. In addition to the feldspar, the ceramic powder may include smectite, which is a clay mineral produced by degeneration of feldspar, and may include opal in addition to the quartz. In addition, the ceramic powder preferably has a moisture content of about 5% to about 15% by weight before mixing with the cosmetic raw material, and this ceramic powder has pores and has a property of absorbing water. It can absorb water and leave the pores with water. When the ceramic powder in the state of being mixed with cosmetic raw materials is applied to the skin and rolled, water is released from the pores to the skin, and the pores adsorb fine dust, sebum, or dead skin cells present on the skin. Subsequently, the cosmetic raw material is purified water, oil components, moisturizers, emollients, surfactants, chelating agents, pigments, UV absorbers, preservatives, disinfectants, antioxidants, pH adjusters, alcohols, and fragrances from the group consisting of It may include one or more selected, but may not be limited thereto. Here, in the present invention, in the surfactant, one natural surfactant selected from coco-glucoside, decyl glucoside, and potassium cocoate is applied. On the other hand, the functional cosmetic composition containing the beauty salt and zeolite component according to the present invention, seaweed extract, coconut extract, oleander leaf extract, purslane extract, camellia flower extract, centella asiatica extract, at least one additional functional extract further comprising can do. This additional functional extract is preferably mixed in an amount of about 3 parts by weight to 7 parts by weight, preferably 5 parts by weight, based on 100 parts by weight of the functional cosmetic composition. Here, the present invention can be extracted through an optimal extraction method, for example, an ultrasonic extraction method, a supercritical extraction method, etc. according to the corresponding components in preparing the additional functional extract. Here, the ultrasonic extract refers to an extract prepared by extracting a dry-pulverized extraction target using an ultrasonic extraction method. In addition, supercritical extraction refers to the drying and crushing of the extraction target and ethanol (99.5%) 500~700mL as an auxiliary solvent into a supercritical fluid extraction reactor (Natex, Autstria), the temperature in the reactor is 65 ℃, the pressure is 450 bar, S/F ratio (supercritical fluid kg/Feed kg) refers to a method of extraction under conditions of 35. Meanwhile, the functional cosmetic composition containing the cosmetic salt and zeolite component according to the present invention may further include at least one auxiliary functional material selected from hydrolyzed collagen and beta-glucan. Here, the auxiliary functional material may be included in the functional cosmetic composition containing the additional functional extract or functional cosmetic composition that does not include the additional functional extract. In the auxiliary functional material, hydrolyzed collagen has the same properties as collagen found in human skin, so it has excellent absorption into the human body, has the effect of improving skin elasticity and improving wrinkles, and the beta-glucan is rich in nutrients to the skin. It delivers moisture and helps to maintain moist and elastic skin, soothes sensitive skin comfortably, and helps to maintain healthy skin by participating in skin conditioning and immunity enhancement. The auxiliary functional material (first functional material) is about 2 parts by weight to 4 parts by weight based on 100 parts by weight of the functional cosmetic composition (functional cosmetic composition containing an additional functional extract or a functional cosmetic composition not containing an additional functional extract) It is preferably mixed in an amount of 3 parts by weight, preferably 3 parts by weight. On the other hand, the functional cosmetic composition containing cosmetic salt and zeolite components according to the present invention may further include at least one moisture-retaining functional material of macadamia seed oil and beeswax. The macadamia seed oil acts as a barrier to block moisture evaporation from the skin, and beeswax forms a protective film on the skin to prevent moisture from escaping. The moisture-retaining functional material is about 2 parts by weight to 4 parts by weight, preferably based on 100 parts by weight of the functional cosmetic composition (a functional cosmetic composition containing an additional functional extract or a functional cosmetic composition not containing an additional functional extract) It is preferably mixed in 3 parts by weight. Next, a method for preparing a functional cosmetic composition containing cosmetic salt and a zeolite component according to the present invention will be described in detail with reference to FIG. 1 . 1 is a flowchart showing a manufacturing process of a functional cosmetic composition containing cosmetic salt and a zeolite component according to the present invention. A method for producing a functional cosmetic composition containing cosmetic salt and a zeolite component according to the present invention, as shown in FIG. 1, includes a zeolite powder preparation step (S100) of preparing a zeolite fine powder; A beauty salt preparation step of preparing beauty salt (S200); and a raw material mixing step (S300) of mixing the prepared zeolite powder with about 3 parts by weight to about 10 parts by weight, about 2 parts by weight to 5 parts by weight of cosmetic salt, and cosmetic raw materials as the balance. The zeolite powder preparation step (S100) is provided as a powder pulverized to a size of 0.3 µm to 0.6 µm, and is preferably prepared as a powder having a size of 0.5 µm. In the present invention, the zeolite powder is prepared by pulverizing the crushed zeolite. At this time, the crushed zeolite or zeolite powder (hereinafter, collectively referred to as "zeolite") is irradiated with inspection radiation and then pulverized. A zeolite gamma-ray treatment step (S110) is further added. may include In the zeolite gamma ray treatment step S110, gamma rays are not particularly limited, but may be gamma rays emitted at 60 Co or 137 Cs. Preferably, in the zeolite gamma-ray treatment step (S110), the zeolite may be treated by irradiating gamma rays emitted at 60 Co or 137 Cs at about 1k to about 50k based on the absorbed dose. The amount of absorbed gamma rays of the zeolite is, for example, about 1k to about 50k, about 1k to about 40k, about 1k to about 30k, about 1k to about 20k, about 1k to about 10k, about 10k to about 50k, about 20k to about 50k, about 30k to about 50k, about 40k to about 50k, or about 10k to about 30k. The gamma-ray treatment time may be, for example, about 10 minutes to about 120 minutes, but is not limited thereto. In addition, the zeolite in the zeolite powder preparation step (S100) may have a microbial content of 0 CFU/g to about 50 CFU/g. It is suitable that the zeolite powder for use in the cosmetic composition contains microorganisms at an amount of 100 CFU/g or less, and it is possible to realize the effect of reducing microorganisms of the zeolite powder by the above-described gamma-ray treatment. In addition, in the zeolite powder preparation step (S110), the zeolite may have a pH of about 7 to about 7.2, and the zeolite may have a pH lowered by the gamma ray treatment. In addition, the zeolite powder preferably has a moisture content of about 5 wt% to about 15 wt% before the raw material mixing step (S300). The zeolite has pores and has a property of absorbing water, and when mixed with cosmetic raw materials, it can absorb water and become a state in which water is contained in the pores. When the zeolite powder mixed with cosmetic raw materials is applied to the skin and rolled, water is released from the pores to the skin and the pores adsorb fine dust, sebum, or dead skin cells present on the skin. On the other hand, in the manufacturing method of the functional cosmetic composition of the present invention, instead of the zeolite, it may be provided as a ceramic powder. Here, when prepared as a ceramic powder, the ceramic powder is prepared to be made of germanium silicate zeolite, feldspar, and quartz having a Si/Ge ratio of silicon and germanium in a weight ratio of 5.0 to 6.0, preferably 5.3 to 5.5 do. At this time, if the Si/Ge ratio of the germanium silicate zeolite is less than 5.0, the ratio of micropores with too small pore size increases, so that dust, sebum, or dead skin cells cannot pass through the pore entrance. If the ratio of α is too high, the total surface area decreases, and thus the main performance of the cosmetic composition may deteriorate due to the decrease in the adsorption area. The ceramic powder may be composed of about 40 wt% to about 75 wt% of germanium silicate zeolite, about 10 wt% to about 30 wt% of feldspar, and about 15 wt% to about 30 wt% of quartz based on the total weight. In addition to feldspar, the ceramic powder may include smectite, which is a clay mineral produced by degeneration of feldspar, and may include opal in addition to quartz. Next, the beauty salt prepared in the cosmetic salt preparation step (S200) is prepared as a sea salt or Himalayan salt whose efficacy has been proven as a cosmetic raw material. Subsequently, the cosmetic raw materials to be mixed in the raw material mixing step (S400) are purified water, oil and fat ingredients, moisturizers, emollients, surfactants, chelating agents, pigments, UV absorbers, preservatives, sterilizers, antioxidants, pH adjusters , alcohol, and may include one or more selected from the group consisting of fragrances, but may not be limited thereto. On the other hand, the method for producing a functional cosmetic composition containing beauty salt and zeolite components according to the present invention, in the raw material mixing step (S400), seaweed extract, coconut extract, oleander leaf extract, purslane extract, camellia flower extract, It may include further mixing the Centella asiatica extract. The additive-functional extract is preferably mixed in an amount of about 3 to 7 parts by weight, preferably 5 parts by weight, based on 100 parts by weight of the mixture. can be extracted through an extraction method, for example, an ultrasonic extraction method, a supercritical extraction method, and the like.

또한, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 방법은, 상기 조성원료 혼합 단계(S400)에서 하이드롤라이즈드 콜라겐 및 베타글루칸 중 적어도 하나 이상의 보조 기능성 물 질을 더 혼합하는 것을 포함할 수 있다. 여기에서, 상기 보조 기능성 물질은 상기한 부가기능 추출물이 혼합되는 혼합물이나 부가기능 추출물을 포함하지 않는 혼합물에 포함될 수 있다. 상기 보조 기능성 물질은 상기한 기능성 화장료 조성물(부가기능 추출물을 포함하는 혼합물이나 부가기능 추출 물을 포함하지 않은 혼합물)의 100중량부에 대하여 약 2중량부 내지 4중량부, 바람직하게는 3중량부로 혼합되는 것이 바람직하다. 한편, 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 방법은, 마카다 미아씨 오일 및 비즈왁스 중 적어도 하나의 수분유지 기능성 물질을 더 혼합하는 것을 포함할 수 있다. 상기 수분유지 기능성물질은 상기한 기능성 화장료 조성물(부가기능 추출물을 포함하는 기능성 화장료 조성물이 나 부가기능 추출물을 포함하지 않는 기능성 화장료 조성물)의 100중량부에 대하여 약 2중량부 내지 4중량부, 바람직하게는 3중량부로 혼합되는 것이 바람직하다.In addition, in the method for producing a functional cosmetic composition containing cosmetic salt and zeolite components according to the present invention, at least one auxiliary functional material of hydrolyzed collagen and beta-glucan is further mixed in the raw material mixing step (S400). may include doing Here, the auxiliary functional substance may be included in a mixture in which the additional functional extract is mixed or in a mixture that does not include the additional functional extract. The auxiliary functional substance is used in an amount of about 2 to 4 parts by weight, preferably 3 parts by weight, based on 100 parts by weight of the functional cosmetic composition (a mixture containing an additional functional extract or a mixture not containing an additional functional extract). Mixing is preferred. Meanwhile, the method for producing a functional cosmetic composition containing cosmetic salt and zeolite according to the present invention may further include mixing at least one moisture-retaining functional material of macadamia seed oil and beeswax. The moisture-retaining functional material is about 2 parts by weight to 4 parts by weight, preferably based on 100 parts by weight of the functional cosmetic composition (a functional cosmetic composition containing an additional functional extract or a functional cosmetic composition not containing an additional functional extract) It is preferably mixed in 3 parts by weight.

<실시 예 및 비교 예의 제조><Preparation of Examples and Comparative Examples>

실시 예 및 비교 예: 기능성 화장료 조성물 제조Examples and Comparative Examples: Preparation of functional cosmetic compositions

입경을 달리하는(각각 실시 예: 0.5㎛, 비교 예1: 4㎛, 비교 예2: 7㎛) 제올라이트 파쇄물에 60 Co를 이용하여 시간당 30 k의 감마선을 30분 동안 조사하여 감마선 처리된 제올라이트 파쇄물을 제조하였다. 감마선 처리된 제올라이트 파쇄물을 해머밀로 분쇄하여 각각 입경을 달리하는 제올라이트 분말을 포함하는 기능 성 화장료 조성물을 제조하였다. 도 2는 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물의 제조 예시에 따른 조성을 나타내는 표이다.The crushed zeolite was irradiated with gamma rays of 30 k per hour for 30 minutes using 60 Co to the crushed zeolite having different particle sizes (Example: 0.5 μm, Comparative Example 1: 4 μm, Comparative Example 2: 7 μm) was prepared. A functional cosmetic composition comprising zeolite powders having different particle diameters was prepared by pulverizing the gamma-ray-treated zeolite crushed material with a hammer mill. 2 is a table showing a composition according to an example of the preparation of a functional cosmetic composition containing cosmetic salt and a zeolite component according to the present invention.

<배합과정><Formulation process>

온도조절, 교반, 호모 공정이 가능한 진공 유화 교반조에 정제수를 투입하여 70 내지 90℃로 가온한 후, 여기에 글리세린, 미리스틱에씨드 및 팔미틱에 씨드를 첨가하고 제올라이트 분말을 투입하여 균일화하여 제올라이트 분 말상을 제조하였다. 별도로 글리세릴 스테아레이트와 피이지-100 스테아레이트를 혼합하여 혼합물을 제조하였다. 상기 제올라이트 분말상을 10rpm 내지 40rpm의 패들 믹서 및 호모 믹서를 이용하여 2,500rpm 내지 3,500rpm의 회전속도로 교반을 유지한 상태에서, 여기에 별도로 준비된 글리세릴 스테아레이트와 피이지-100 스테아레이트의 혼합물을 투입하였으며, 상기 온도와 교반 속도를 유지한 상태에서, 별도로 정제수에 용해시켜 둔 pH조절제 (포타슘하이드록사 이드)를 투입하여 pH가 9 내지 10이 되게 반응시켰다. pH가 안정화되면 35까지 냉각시키고, 비즈왁스, 스테아릭에씨드, 컨디셔닝제, 폴리소르베이트20, 킬레이팅제, 피이지-14M 및 방부제를 순차적으로 각각 투입하여 균일화하였다. 여기에, 향료를 투입하여 기능성 화장료 조성 물을 제조하였다. After adding purified water to a vacuum emulsification stirring tank capable of temperature control, stirring, and homo processing and heating to 70 to 90° C., seeds are added to glycerin, myristic acid and palmitic, and zeolite powder is added to homogenize the zeolite. A powder phase was prepared. Separately, a mixture was prepared by mixing glyceryl stearate and PEG-100 stearate. A mixture of glyceryl stearate and PEG-100 stearate separately prepared here while maintaining the stirring of the zeolite powder phase at a rotation speed of 2,500 rpm to 3,500 rpm using a paddle mixer and a homo mixer of 10 rpm to 40 rpm. was added, and while maintaining the temperature and stirring speed, a pH adjusting agent (potassium hydroxide) dissolved in purified water was added and reacted so that the pH became 9 to 10. When the pH was stabilized, it was cooled to 35, and beeswax, stearic acid, conditioning agent, polysorbate 20, chelating agent, PEG-14M and preservative were sequentially added to make it uniform. Here, a fragrance was added to prepare a functional cosmetic composition.

실험 예 1: pH 측정Experimental Example 1: pH Measurement

실시 예 1에 사용된 제올라이트 분말의 pH를, KS I ISO 10390:2005에 의거하여 측정하였으며, 그 결과는 하기 표 1에 나타내었다. pH는 감마선 처리 전후의 세라믹 분말에 대해 각각 측정되었다.The pH of the zeolite powder used in Example 1 was measured in accordance with KS I ISO 10390:2005, and the results are shown in Table 1 below. The pH was measured for the ceramic powder before and after gamma-irradiation, respectively.

표1Table 1

표 1을 참조하면, 감마선 처리 후 제올라이트 분말의 pH가 약 10% 정도 감소하였음을 알 수 있다. 감마선 처리에 의해 제올라이트 분말의 pH가 감소함에 따라, 물의 pH에 가까운 중성상태를 갖게 된 것으로 확인이 되며, 이 에 따라, 피부 자극성이 저감되어, 3중량%(즉, 3만ppm) 이상 많은 양의 제올라이트 분말을 사용하여도 피부자극 이 거의 없다.Referring to Table 1, it can be seen that the pH of the zeolite powder decreased by about 10% after gamma-ray treatment. As the pH of the zeolite powder is decreased by the gamma-ray treatment, it is confirmed that it has a neutral state close to the pH of water, and accordingly, the skin irritation is reduced, and a large amount of 3% by weight (ie, 30,000 ppm) or more There is almost no skin irritation even when using zeolite powder of

실험 예 2: 미생물 함량 측정Experimental Example 2: Determination of Microbial Content

실시 예 1에 사용된 제올라이트 분말의 세공 내부에 존재하는 미생물의 함량을 측정하기 위하여 미생물 집락수 측정 시험을 실시였으며, 그 결과는 하기 표 2에 나타내었다. 미생물 집락수 측정 시험에 앞서 감마선 처리 전 후의 제올라이트 분말 10g을 25℃에서 채취하여 검체로 사용하였다. 각각의 검체 10g을 증류수 100ml로 희석하 여 검체 희석액을 제조한 후, 제조된 검체 희석액 0.1ml를 TSA(trypticase soy agar) 고체 배지를 포함하는 패 트리디쉬에 접종하고 32.52.5의 배양온도에서 5일 동안 배양하였다(도말 평판법). 표 2에서 TNTC 는 too numerous to count의 약자로 집락이 너무 많아 셀 수 없는 정도를 의미한다. 화장료 조성물에 적용하기 위한 적 합/부적합 판정의 기준은 100CFU/g으로, g당 집락형성단위가 100CFU/g 이하일 경우를 적합으로 판정하고, g당 집락형성단위가 100CFU/g을 초과할 경우를 부적합으로 판정하였다.In order to measure the content of microorganisms present in the pores of the zeolite powder used in Example 1, a microbial colony measurement test was performed, and the results are shown in Table 2 below. Prior to the test for measuring the number of microbial colonies, 10 g of zeolite powder before and after gamma-ray treatment was collected at 25° C. and used as a sample. After preparing a sample dilution solution by diluting 10 g of each sample with 100 ml of distilled water, 0.1 ml of the prepared sample dilution solution was inoculated into a paddy dish containing a TSA (trypticase soy agar) solid medium and 5 at a culture temperature of 32.52.5. Incubated for one day (smear plate method). In Table 2, TNTC is an abbreviation of too numerous to count, which means that there are too many colonies to count. The criterion of suitability/unsuitability for application to cosmetic compositions is 100 CFU/g, when the colony-forming unit per g is 100 CFU/g or less, and when the colony-forming unit per g exceeds 100 CFU/g It was judged as non-conforming.

표2Table 2

표 2를 참조하면, 실시 예에 사용된 제올라이트 분말의 세공 내부에 존재하는 미생물의 함량은 감마선 처리 전 후에 큰 차이를 보였다. 감마선 처리 후 제올라이트 분말의 g당 집락형성단위는 현저히 감소하였으며, 감마선 처리에 의해 대략적으로 g당 집락형성단위가 50CFU/g 이하로 확인되었고, 감마선 처리에 의해 제올라이트 분말의 세공 내부가 깨끗이 정리되었음을 알 수 있다.Referring to Table 2, the content of microorganisms present inside the pores of the zeolite powder used in Examples showed a large difference before and after gamma-ray treatment. After gamma-irradiation treatment, the colony-forming unit per g of the zeolite powder was significantly reduced, and it was confirmed that the colony-forming unit per g was approximately 50 CFU/g or less by the gamma-irradiation treatment, and the inside of the pores of the zeolite powder was cleaned by gamma-ray treatment. can

표3Table 3

실험 예 3: 은나노분말 흡착 성능 측정Experimental Example 3: Measurement of Adsorption Performance of Silver Nanopowder

실시 예 1, 비교 예 1 및 비교 예 2에 사용된 제올라이트 분말의 피부각질, 먼지 등의 흡착 성능을 측정하기 위 하여, 은나노 분말을 5g을 정제수에 분산시키고 원자흡수분광법에 의해 농도(A)를 측정한 후에, 여기에 정제수 중량대비 10%의 제올라이트 분말을 첨가하고 20분간 교반한 후에 다시 농도(B)를 측정하여, 그 결과를 하기 표 3에 나타내었다.In order to measure the adsorption performance of the zeolite powder used in Example 1, Comparative Example 1, and Comparative Example 2, 5 g of silver nano-powder was dispersed in purified water and the concentration (A) was determined by atomic absorption spectroscopy. After the measurement, 10% of zeolite powder based on the weight of purified water was added thereto, and the concentration (B) was measured again after stirring for 20 minutes, and the results are shown in Table 3 below.

표 3을 참조하면, 실시 예 1에 사용된 제올라이트 분말의 경우, 흡착도가 0.48로서 제올라이트 분말에 의한 흡 착 전후에 농도가 큰 차이를 보이고 있는데 비하여, 비교 예 1 및 비교 예 2의 경우 각각 0.82, 0.73으로서 실시 예 1에 비하여 흡착 전후의 농도 변화가 현저히 작은 것을 알 수 있다.Referring to Table 3, in the case of the zeolite powder used in Example 1, the adsorption degree was 0.48, showing a large difference in concentration before and after adsorption by the zeolite powder, whereas in Comparative Examples 1 and 2, respectively, 0.82 , 0.73, it can be seen that the concentration change before and after adsorption is significantly smaller than in Example 1.

이상에서 설명한 바와 같은 본 발명에 따른 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물 및 이의 제조 방법에 의하면, 미용소금과 제올라이트 성분이 갖는 탁월한 기능으로 피부를 촉촉하고 생기 넘 치게 가꿀 수 있으며, 피부 수렴에도 도움을 줄 수 있고, 민감한 피부 진정, 노폐물 제거 및 탁월한 피부 보습 이 가능한 이점이 있다.According to the functional cosmetic composition containing the cosmetic salt and zeolite component according to the present invention as described above and the manufacturing method thereof, it is possible to moisturize and vitalize the skin with the excellent function of the cosmetic salt and the zeolite component, and to converge the skin It also has the advantage of soothing sensitive skin, removing waste products, and providing excellent skin hydration.

또한, 본 발명에 의하면, 세공 용적을 높여 흡착 표면적을 높이고, 내부 세공의 미생물을 제거하고 pH를 낮춰 피부자극성이 거의 없으며 수분공급 성능이 뛰어나며, 보조 기능성물질의 성분을 통해 피부진정, 피부회복, 항 산화, 피부활력, 모공케어, 피지조절, 생기부여, 피부 결케어, 피부 윤기 및 항염을 도모할 수 있어 피부 건강에 더욱 도움을 줄 수 있는 이점이 있다.In addition, according to the present invention, the pore volume is increased to increase the adsorption surface area, and the microorganisms in the internal pores are removed and the pH is lowered to have little skin irritation and excellent moisture supply performance. Antioxidant, skin vitality, pore care, sebum control, vitality, skin texture care, skin gloss and anti-inflammation can be promoted, so it has the advantage of being more helpful for skin health.

본 명세서에서 설명되는 실시 예와 첨부된 도면은 본 발명에 포함되는 기술적 사상의 일부를 예시적으로 설명하는 것에 불과하다. 따라서, 본 명세서에 개시된 실시 예는 본 발명의 기술적 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이므로, 이러한 실시 예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아님은 자명하 다. 본 발명의 명세서 및 도면에 포함된 기술적 사상의 범위 내에서 당업자가 용이하게 유추할 수 있는 변형 예 와 구체적인 실시 예는 모두 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The embodiments described in this specification and the accompanying drawings are merely illustrative of some of the technical ideas included in the present invention. Therefore, since the embodiments disclosed in the present specification are for explanation rather than limitation of the technical spirit of the present invention, it is obvious that the scope of the technical spirit of the present invention is not limited by these embodiments. Modifications and specific embodiments that can be easily inferred by those skilled in the art within the scope of the technical idea included in the specification and drawings of the present invention should be interpreted as being included in the scope of the present invention.

S100: 제올라이트 분말 마련 단계
S110: 제올라이트 감마선 처리 단계
S200: 미용소금 마련 단계
S300: 조성원료 혼합 단계S100: zeolite powder preparation step
S110: zeolite gamma-ray treatment step
S200: Beauty salt preparation step
S300: mixing step of ingredients

Claims (2)

화장료 조성물로서, 미용소금과, 제올라이트, 및 화장품 원료의 기본 화장료 조성물을 포함하고, 상기 미용소금은 2중량% 내지 5중량%이고, 상기 제올라이트는 3중량% 내지 10중량%이며, 화장품 원료는 85중량% 내지 95중량%로 하는 조성 비율을 포함하고,상기 제올라이트는 0.3㎛ ~ 0.6㎛의 크기로 분쇄된 분말이고,
상기 화장품 원료는 코코-글루코사이드(Coco-glucoside), 데실글루코사이드(Decyl Glucoside), 포타슘코코에이트(Potassium Cocoate)에서 선택되는 하나의 천연 계면활성제를 포함하고, 미역 추출물, 코코넛 추출물, 구주소나무잎 추출물, 쇠비름 추출물, 동백나무꽃 추출물, 병풀 추출물 중 적어도 하나의 부가기능 추출물과, 하이드롤라이즈드 콜라겐 및 베타글루칸의 보조 기능성 물질, 및 호호바씨 오일 및 시어버터의 수분유지 기능성 물질을 더 포함하며,상기 제올라이트는 감마선을 조사하여 처리된 것이고, 미생물 함량이 0 내지 50CFU/g이며, pH가 7 내지7.2이며, 수분함량이 5중량% 내지 15중량%이고,상기 부가기능 추출물은 상기 기본 화장료 조성물의 100중량부에 대하여 3중량부 내지 7중량부로 혼합되며,상기 보조 기능성 물질은 상기 기본 화장료 조성물의 100중량부에 대하여 2중량부 내지 4중량부로 혼합되며,상기 수분유지 기능성물질은 상기 기본 화장료 조성물의 100중량부에 대하여 2중량부 내지 4중량부로 혼합되는것을 특징으로 하는 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물.
A cosmetic composition comprising a cosmetic salt, a zeolite, and a basic cosmetic composition of cosmetic raw materials, wherein the cosmetic salt is 2% to 5% by weight, the zeolite is 3% to 10% by weight, and the cosmetic raw material is 85 Including a composition ratio of weight% to 95% by weight, The zeolite is a powder pulverized to a size of 0.3㎛ ~ 0.6㎛,
The cosmetic raw material is coco-glucoside (Coco-glucoside), decyl glucoside (Decyl Glucoside), potassium cocoate (Potassium Cocoate) containing one natural surfactant selected from, seaweed extract, coconut extract, It further comprises an additional functional extract of at least one of purslane extract, camellia flower extract, and Centella asiatica extract, an auxiliary functional substance of hydrolyzed collagen and beta glucan, and a moisture retention functional substance of jojoba seed oil and shea butter, the The zeolite is treated by irradiating gamma rays, the microbial content is 0 to 50 CFU / g, the pH is 7 to 7.2, the moisture content is 5% to 15% by weight, and the additional functional extract is 100 of the basic cosmetic composition 3 parts by weight to 7 parts by weight are mixed, The auxiliary functional material is mixed in 2 parts by weight to 4 parts by weight based on 100 parts by weight of the basic cosmetic composition, The moisture-retaining functional material is the amount of the basic cosmetic composition Functional cosmetic composition containing cosmetic salt and zeolite component, characterized in that it is mixed in an amount of 2 to 4 parts by weight based on 100 parts by weight.
화장료 조성물로서, 미용소금과, 규소와 게르마늄의 비율인 Si/Ge 비가 중량비로 5.0 내지 6.0인 게르마늄실리케이트 제올라이트와 장석 및 석영을 포함하는 세라믹 분말, 및 화장품 원료의 기본 화장료 조성물을 포함하고, 상기 미용소금은 2중량% 내지 5중량%이고, 상기 세라믹 분말은 3중량% 내지 10중량%이며, 화장품 원료 85중량% 내지 95중량%로 하는 조성 비율을 포함하고,상기 세라믹 분말은 감마선을 조사하여 처리된 것이고, 미생물 함량이 0 내지 50CFU/g이며, pH가 7 내지 7.2이며, 수분함량이 5중량% 내지 15중량%이며,상기 세라믹 분말은 총 중량 기준으로, 게르마늄실리케이트 제올라이트 40중량% 내지 75중량%, 장석 10중량% 내지 30중량%, 및 석영 15중량% 내지 30중량%를 포함하고, 상기 화장품 원료는 코코-글루코사이드(Coco-glucoside), 데실글루코사이드(Decyl Glucoside), 포타슘코코에이트(Potassium Cocoate)에서 선택되는 하나의 천연 계면활성제를 포함하고, 미역 추출물, 코코넛 추출물, 구주소나무잎 추출물, 쇠비름 추출물, 동백나무꽃 추출물, 병풀 추출물 중 적어도 하나의 부가기능 추출물과, 하이드롤라이즈드 콜라겐 및 베타글루칸의 보조 기능성 물질, 및 마카다미아씨 오일 및 비즈왁스의 수분유지 기능성 물질을 더 포함하고,상기 부가기능 추출물은 상기 기본 화장료 조성물의 100중량부에 대하여 3중량부 내지 7중량부로 혼합되고,상기 보조 기능성 물질은 상기 기본 화장료 조성물의 100중량부에 대하여 2중량부 내지 4중량부로 혼합되며,상기 수분유지 기능성물질은 상기 기본 화장료 조성물의 100중량부에 대하여 2중량부 내지 4중량부로 혼합되는것을 특징으로 하는 미용소금과 제올라이트 성분을 함유하는 기능성 화장료 조성물
A cosmetic composition, comprising a cosmetic powder, a ceramic powder comprising a germanium silicate zeolite having a Si/Ge ratio, which is a ratio of silicon and germanium, 5.0 to 6.0 by weight, feldspar, and quartz, and a basic cosmetic composition of cosmetic raw materials, Salt is 2 wt% to 5 wt%, the ceramic powder is 3 wt% to 10 wt%, and a composition ratio of 85 wt% to 95 wt% of cosmetic raw materials is included, The ceramic powder is treated by irradiating gamma rays , the microbial content is 0 to 50 CFU / g, the pH is 7 to 7.2, the moisture content is 5 wt% to 15 wt%, and the ceramic powder is 40 wt% to 75 wt% of germanium silicate zeolite based on the total weight %, 10% to 30% by weight of feldspar, and 15% to 30% by weight of quartz, and the cosmetic raw material is coco-glucoside (Coco-glucoside), decyl glucoside (Decyl Glucoside), potassium cocoate (Potassium Cocoate) ), and at least one additional functional extract selected from seaweed extract, coconut extract, old jujube leaf extract, purslane extract, camellia flower extract, and Centella asiatica extract, hydrolyzed collagen and beta It further comprises an auxiliary functional material of glucan, and a water retention functional material of macadamia seed oil and beeswax, The additional function extract is mixed in an amount of 3 to 7 parts by weight based on 100 parts by weight of the basic cosmetic composition, The auxiliary The functional material is mixed in an amount of 2 to 4 parts by weight based on 100 parts by weight of the basic cosmetic composition, and the moisture-retaining functional material is mixed in an amount of 2 to 4 parts by weight based on 100 parts by weight of the basic cosmetic composition. Functional cosmetic composition containing cosmetic salt and zeolite