KR20220109138A - Materials for endothelial of fireproof clothing containing meta-aramid and cold sensitive material - Google Patents

Abstract

The present invention relates to an endothelial material for fireproof clothing and, specifically, to an endothelial material for fireproof clothing containing meta-aramid and a cold-sensitive material so that burns due to heat at a fire site can be prevented and moisture accumulated inside the fire protection clothing can quickly evaporate. The endothelial material for fireproof clothing according to the present invention contains the meta-aramid having high flame retardancy and the cold-sensitive material giving a cool feeling if clothing fabric touches the skin when the clothing is worn, so that burns due to heat at a fire site may be prevented and internally accumulated moisture may quickly evaporate by adding fiber for absorption and quick-drying, thereby reducing the possibility of burns, increasing work efficiency, and providing comfort to the inside of the fireproof clothing.

Description

메타아라미드 및 냉감소재를 포함하는 방화복 내피용 소재{MATERIALS FOR ENDOTHELIAL OF FIREPROOF CLOTHING CONTAINING META-ARAMID AND COLD SENSITIVE MATERIAL}Material for inner shell of fire protection clothing including meta-aramid and cold-sensitive material

본 발명은 방화복 내피용 소재로서, 구체적으로는 화재 현장에서 열기로 인한 화상을 막고 방화복 내부에 누적되는 수분이 빠르게 증발되도록 하는 메타아라미드 및 냉감소재를 포함하는 방화복 내피용 소재이다.The present invention is a material for the inner covering of fire suits, and specifically, it is a material for inner coverings of fire suits containing meta-aramid and a cooling material that prevents burns due to heat at the scene of a fire and allows moisture accumulated inside the fire suits to quickly evaporate.

우리나라의 연간 화재 발생 건수 현황을 살펴보면, 평균 4만 건 이상의 화재가 발생하고 있다. 이에 따라 소방관의 공상(공무로 인하여 입은 상처) 현황은 2010년부터 현재까지 계속해서 증가하는 추세이며, 그 중 화재로 인한 공상이 많은 부분을 차지하고 있다.Looking at the current status of the annual number of fires in Korea, an average of more than 40,000 fires occur. Accordingly, the status of firefighters' daydreaming (injuries caused by official duties) has been continuously increasing from 2010 to the present, and among them, daydreaming due to fire occupies a large portion.

화재 현장에서 소방관들이 착용하는 방화복은 화재진압 및 인명구조 활동을 위하여 착용하는 옷으로서, 불 또는 열기로부터의 보호 성능을 지닌 의류이다. 방화복은 외피(outer shell), 방수 투습천(moisture barrier)과 단열 내피(thermal barrier)로 구성되며 각 층은 고유의 역할을 가지고 있다. 외피는 불꽃에 직접 닿는 부분으로서 불길에 대한 보호 역할을 하며, 찢김, 뚫림 등에 대한 방어를 맡고 있다. 방수 투습천은 방수와 투습의 역할을 하며, 물기가 들어오는 것은 막아주고 땀은 밖으로 내보내는 기능을 가지고 있다. 단열 내피는 피부에 닿는 부분으로 뜨거운 열을 막아주는 역할을 하며, 보통은 부직포(펠트, felt)를 단열층으로 하여 열의 침투 속도를 늦추게 된다.Fire fighting clothing worn by firefighters at the scene of a fire is clothing that is worn for fire suppression and lifesaving activities, and has protection from fire or heat. Fire protection clothing consists of an outer shell, a waterproof moisture barrier and a thermal barrier, and each layer has a unique role. The outer shell is the part that comes in direct contact with the flame and acts as a protection against flames and is responsible for protection against rips and punctures. The waterproof breathable cloth plays the role of waterproofing and moisture permeability, and has the function of preventing water from entering and letting sweat out. The insulating endothelium is the part that comes into contact with the skin and serves to block hot heat, and usually a nonwoven fabric (felt) is used as an insulating layer to slow the rate of heat penetration.

방화복 제조에 있어서, 전체적으로 난연성(難燃性) 섬유인 아라미드(aramid) 계열 섬유로 만들며, 겉감에는 폴리벤지미다졸(Polybenzimidazole, PBI) 섬유가 사용되는 경우도 많다. 난연성은 불에 잘 타지 않는 성질로서, 불꽃에 접촉하고 있을 때는 타지만 불꽃을 제거하면 스스로 불꽃을 내면서 연소하는 것을 방지 또는 억제하는 특징이 있다. 불꽃을 접촉하여도 연소가 전혀 일어나지 않는 불연성, 자체적으로 연소가 활성화되는 가연성에 대비하여, 난연성 재료는 연소의 속도가 불연성과 가연성 재료의 중간에 놓인다.In the manufacture of fire protection clothing, it is made of aramid-based fibers, which are flame-retardant fibers as a whole, and polybenzimidazole (PBI) fibers are often used for the outer material. Flame retardancy is a property that does not burn easily. It burns when in contact with a flame, but when the flame is removed, it prevents or suppresses combustion by emitting a flame by itself. In contrast to non-combustible materials in which combustion does not occur even when in contact with flames, and combustible materials in which combustion is activated by itself, flame-retardant materials have a combustion rate intermediate between non-combustible and combustible materials.

아라미드는 5㎜ 정도 굵기의 가는 실이지만 같은 중량의 철보다 5배 강하고 500℃가 넘는 고온에도 견딜 수 있는 특수 소재다. 아라미드 섬유는 크게 메타아라미드(meta-Aramid)와 파라아라미드(para-Aramid)로 나뉜다. 메타아라미드는 섭씨 500도까지 견딜 수 있는 내열성이 특징이다. 이에 비해 파라아라미드는 고강도 특성이 있어 강도가 같은 무게 강철보다 5배나 높다. 이에 따라 메타아라미드는 주로 소방복, 파라아라미드는 방탄복, 방탄 헬멧, 방탄 차량 등에 쓰인다.Aramid is a thin thread with a thickness of about 5 mm, but it is five times stronger than iron of the same weight and is a special material that can withstand high temperatures exceeding 500 °C. Aramid fibers are largely divided into meta-aramid and para-aramid. Meta-aramid is characterized by heat resistance that can withstand temperatures up to 500 degrees Celsius. In comparison, para-aramid has high strength properties, which is five times higher than steel of the same weight. Accordingly, meta-aramid is mainly used for firefighting suits, and para-aramid is used for body armor, bullet-proof helmets, and bullet-proof vehicles.

일반적으로 방화복은 메타아라미드 소재를 사용하여 높은 방염성, 내구성, 전기 절연성, 고강도, 높은 난연성의 특징이 있다. 높은 내열성으로 400℃의 고온 및 200~210℃에서 연속 사용 가능하다는 장점이 있다. 또한, 자체 불연성으로 타 소재와 비교했을 때 탄화 시에 유독가스나 유해 물질을 배출하지 않아 친환경 섬유로도 우수한 성질을 가지고 있다. 그러나 단점으로는 아라미드 섬유는 신축성이 극히 낮고 열안정이 매우 높기 때문에 스트래치성이 매우 낮아 소방관들이 착용 시 쾌적성이 낮을 뿐 아니라 소방방재 활동 시 기동성 떨어지는 단점을 갖고 있다.In general, fire protective clothing uses meta-aramid material and has high flame retardancy, durability, electrical insulation, high strength, and high flame retardancy. It has the advantage that it can be used continuously at high temperature of 400℃ and 200~210℃ due to its high heat resistance. In addition, it has excellent properties as an eco-friendly fiber because it does not emit toxic gas or harmful substances during carbonization compared to other materials due to its incombustibility. However, as a disadvantage, aramid fiber has very low elasticity and very high thermal stability, so its stretchability is very low, so it not only has low comfort when worn by firefighters, but also has the disadvantage of poor mobility during firefighting and disaster prevention activities.

한편, 밖에서 안으로 들어오는 열을 지연시키는 능력(열 방호성)은 안에서 밖으로 나가려는 열(열 배출성)에 대해서도 적용된다는 문제가 발생하는데, 열 방호성이 높은 방화복은 대채로 열 배출성이 떨어진다. 방화복 내부에 수분이 누적되면 열전도가 빨라지기 때문에 화상의 가능성이 증가하게 되는데, 화재 현장의 열기와 밖으로 방출되지 못한 열기로 인하여 열화상, 열사병 등이 발생할 수 있다. 또한, 누적된 수분으로 인해 심한 불쾌감을 느낄 수도 있다.On the other hand, there is a problem that the ability to delay the heat coming in from the outside (thermal protection property) is also applied to the heat going out from the inside (heat dissipation property). If moisture accumulates inside the fire protection clothing, heat conduction is accelerated, so the possibility of burns increases. Also, you may feel severe discomfort due to the accumulated moisture.

따라서, 화재 현장의 열기로 인한 화상을 막고 내부에 누적되는 수분을 빠르게 증발시키는 소재의 개발이 필요하다.Therefore, it is necessary to develop a material that prevents burns due to the heat of the fire site and rapidly evaporates moisture accumulated therein.

본 발명에서 해결하고자 하는 과제는 기존 방화복 내피 제조에 사용되는 메타아라미드에 냉감소재를 추가함으로써, 기존의 내피 기능을 유지함과 동시에 화재 현장에서 발생하는 열기로 인한 화상을 막고 방화복 내부에 누적되는 수분이 빠르게 증발되도록 하여 화재 공상의 위험을 줄일 수 있는 방화복 내피용 소재를 제공하는 것이다.The problem to be solved in the present invention is by adding a cooling material to meta-aramid used for the production of the existing fire-fighting inner skin, thereby maintaining the existing endothelial function and at the same time preventing burns caused by heat generated at the fire site and reducing the moisture accumulated inside the fire-fighting clothing. The purpose of this invention is to provide a material for the inner skin of fire suits that can be rapidly evaporated to reduce the risk of fire fancy.

본 발명에 따른 과제의 해결 수단으로 기존의 방화복에 사용되는 메타아라미드에 열을 빠르게 흡수하고 방출하는 성질이 우수하여 피부의 표면 온도를 낮춰주고 시원한 느낌을 제공하는 냉감소재를 추가로 포함하도록 한다. 상기 냉감소재는 레이온 또는 큐프라를 포함하는 접촉냉감 소재인 것을 특징으로 한다.As a means of solving the problem according to the present invention, meta-aramid used in conventional fire-fighting clothing has excellent properties of rapidly absorbing and emitting heat, thereby lowering the surface temperature of the skin and providing a cool feeling to additionally include a cooling material. The cooling material is characterized in that the contact cooling material including rayon or cupra.

또한, 수분을 효과적으로 흡수하고 흡수한 수분을 방화복 밖으로 배출되도록 흡수속건 섬유를 추가로 포함할 수 있다. 메타아라미드와 냉감소재로 섬유 다발을 제조하고 섬유 다발 사이에 흡수속건 소재를 추가하도록 한다.In addition, it may further include an absorbent quick-drying fiber to effectively absorb moisture and discharge the absorbed moisture out of the fire protection suit. Prepare a fiber bundle with meta-aramid and a cooling material, and add an absorbent quick-drying material between the fiber bundles.

본 발명의 냉감소재를 이용한 방화복 내피는 높은 난연성의 메타아라미드 및 옷을 착용할 때 옷감이 피부에 닿으면 시원한 느낌을 주는 냉감소재를 포함하여 화재 현장에서 열기로 인한 화상을 막으며, 땀을 빠르게 흡수하고 건조시키는 흡수속건 섬유를 추가하여 내부에 누적되는 수분이 빠르게 증발되도록 하여 화상의 가능성 감소 및 일의 효율 증대, 방화복 내부에 쾌적함을 제공한다.The fire-resisting clothing lining using the cooling material of the present invention contains meta-aramid of high flame retardancy and a cooling material that gives a cool feeling when the cloth touches the skin when wearing clothes, prevents burns caused by heat at the scene of a fire, and quickly wicks away sweat. By adding absorbent quick-drying fiber that absorbs and dries, the moisture accumulated inside is quickly evaporated, reducing the possibility of burns, increasing work efficiency, and providing comfort to the inside of fireproof clothing.

도 1은 본 발명의 실시예에 따른 메타아라미드 및 냉감소재를 포함하는 방화복 내피용 소재의 모습을 나타낸 사시도이다.1 is a perspective view showing the appearance of a fire protection inner skin material including meta-aramid and a cooling material according to an embodiment of the present invention.

이하에서는 본 발명의 목적이 구체적으로 실현될 수 있는 본 발명의 바람직한 실시예를 첨부한 도면을 이용하여 설명한다.Hereinafter, preferred embodiments of the present invention in which the object of the present invention can be specifically realized will be described with reference to the accompanying drawings.

도 1은 본 발명의 실시예에 따른 메타아라미드 및 냉감소재를 포함하는 방화복 내피용 소재의 모습을 나타낸 사시도이다.1 is a perspective view showing the appearance of a fire protection inner skin material including meta-aramid and a cooling material according to an embodiment of the present invention.

본 발명은 방화복 내피용 소재로서, 화재 현장에서 열기로 인한 화상을 막고 방화복 내부에 누적되는 수분이 빠르게 증발되도록 하는 메타아라미드 및 냉감소재를 포함하는 방화복 내피용 소재이다.The present invention is a fire protection inner covering material, comprising meta-aramid and a cooling material that prevents burns due to heat at the scene of a fire and allows moisture accumulated inside the fire clothing to evaporate quickly.

방화복은 화재진압 및 인명구조 활동을 위하여 화재 현장에서 소방관들이 착용하며, 불 또는 열기로부터의 보호 성능을 지닌 의류이다. 일반적으로 난연성(難燃性) 섬유인 아라미드(aramid) 계열 섬유로 만든다. 아라미드는 5㎜ 정도 굵기의 가는 실이지만 같은 중량의 철보다 5배 강하고 500℃가 넘는 고온에도 견딜 수 있는 특수 소재다.Fire protection clothing is worn by firefighters at fire sites for fire suppression and life-saving activities, and has protective performance against fire or heat. In general, it is made of aramid-based fibers, which are flame-retardant fibers. Aramid is a thin thread with a thickness of about 5 mm, but it is five times stronger than iron of the same weight and is a special material that can withstand high temperatures exceeding 500 °C.

아라미드는 방향족 폴리아미드로 크게 메타아라미드(meta-Aramid)와 파라아라미드(para-Aramid)로 나뉜다. 메타아라미드는 듀폰사에서 개발된 노멕스(Nomex), 데이진사에서 개발된 코넥스(Conex)가 대표적이며, 파라아라미드는 듀폰사에서 개발된 케블라(Kevlar)가 대표적이다.Aramid is an aromatic polyamide and is largely divided into meta-aramid and para-aramid. Meta-aramid is representative of Nomex developed by DuPont and Conex developed by Teijin, and Kevlar developed by DuPont is representative of para-aramid.

메타아라미드는 벤젠고리가 메타 위치에서 아미드기와 결합된 것으로, 강도와 신도는 보통의 나일론과 비슷하나 열에 대한 안정성이 대단히 좋으며, 다른 내열용 소재에 비하여 가벼워 주로 방화복 등에 사용되고 있다. 파라아라미드는 벤젠 고리가 파라 위치에서 아미드기와 결합된 것으로, 강도가 매우 높고 탄성률이 특히 높아 충격을 흡수하는 성능이 매우 우수하여 탄복, 방탄 헬멧, 방탄 차량 등에 사용되고 있다.Meta-aramid is a benzene ring bonded to an amide group at the meta position. Its strength and elongation are similar to those of normal nylon, but it has very good thermal stability, and is light compared to other heat-resistant materials, and is mainly used for fire-fighting clothing. Para-aramid is a benzene ring bonded to an amide group at the para position, and has very high strength and particularly high modulus of elasticity, so it has excellent shock absorbing performance and is used in bullet-proof vests, bullet-proof helmets, and bullet-proof vehicles.

냉감소재는 옷을 착용할 때 옷감이 피부에 닿으면 시원한 느낌을 주는 소재로서, 땀 흡수가 잘되고 통기성이 우수하며, 건조 속도가 빠르다는 장점이 있다. 이러한 특징 때문에 냉감소재는 의류뿐 아니라 다양한 제품군에 사용되고 있으며 시장 규모도 매년 커지고 있다.Cooling material is a material that gives a feeling of coolness when the cloth touches the skin when wearing it. Because of these characteristics, cooling materials are used not only in clothing but also in various product groups, and the market size is growing every year.

냉감소재가 냉감(시원한 느낌)을 주는 방법으로는 피부의 열이 옷감으로 순식간에 이동하여 느끼게 되는 접촉냉감, 이형 단면을 활용한 모세관 현상으로 수분을 빨리 빨아들여 기화함으로써 열을 내려가게 하는 흡한·흡습냉감, 신경작용으로 차가움을 느끼게 하는 신경냉감의 3 종류가 있다. 본 발명에서는 접촉냉감 소재를 사용한다.As a method of giving a feeling of coolness (cool feeling), a feeling of contact cooling, which is felt by the instantaneous movement of skin heat to the fabric, and a sweat absorption/ There are three types: moisture absorption sensation and nerve cooling sensation, which makes you feel cold through nerve action. In the present invention, a contact cooling material is used.

접촉냉감은 피부에 닿았을 때 피부 표면온도를 낮춰, 피부에서 옷감으로 순식간에 열이 이동해 차가움을 느끼는 것을 말한다. 이는 열 전도현상에 의한 것으로, 뜨거운 온돌방에 앉아 있으면 엉덩이가 뜨거워지는 것처럼 물질의 직접적인 이동을 수반하지 않고 접촉하고 있는 두 물체의 온도차에 의해서 열(에너지)이 흐르는 방식이 열전도(heat conduction)이다. 피부가 소재에 닿았을 때, 열 전도현상이 발생하여 차가움을 느끼게 된다.Contact coolness refers to the sensation of coldness by lowering the surface temperature of the skin when it comes into contact with the skin and instantaneous heat transfer from the skin to the fabric. This is due to the heat conduction phenomenon, and heat conduction is the way heat (energy) flows by the temperature difference between two objects in contact without direct movement of substances, just as the hips become hot when sitting in a hot ondol room. When the skin comes into contact with the material, heat conduction occurs and the person feels cold.

접촉냉감은 실제 만졌을 때 차가운 것이 아닌, 사람의 열이 얼마나 빠르게 많은 양이 움직이느냐에 따라 차갑게 또는 차갑지 않게 느끼게 된다. 우리의 몸은 평소 온도를 느끼는 것이 아니라, 몸에서 에너지가 빠져나갈 때 시원하게 느끼게 되는데, 여기에서 착안해 만든 것이 바로 접촉냉감 소재이다. 열을 빠르게 흡수하고 방출하는 성질이 우수하여 피부의 표면 온도를 낮춰주고 시원한 느낌을 제공하여 여름철에 사용하기 좋다. 접촉냉감소재는 섬유에 열 전도성이 좋은 물질을 첨가하거나 가공해 만든다. 대표적인 접촉냉감 소재로는 화학섬유에서는 레이온(rayon)이나 큐프라(cupra)가 접촉냉감이 뛰어난 성질을 가지고 있다.Contact cold sensation is not cold when touched, but feels cold or not cold depending on how quickly a person's heat moves a lot. Our body does not normally feel the temperature, but when energy is released from the body, it feels cool. It has excellent properties of absorbing and discharging heat quickly, lowering the surface temperature of the skin and providing a cool feeling, so it is good to use in summer. Contact cooling materials are made by adding or processing materials with good thermal conductivity to fibers. As a representative contact cooling material, in chemical fibers, rayon or cupra has excellent contact cooling sensation.

메타아라미드와 냉감소재를 포함하는 소재는 피부에 닿았을 때 열의 이동이 빠르게 이루어져 효과적인 냉감 효과가 있으며, 방화복 내부의 땀 등의 수분이 섬유 다발의 내부까지 침투하여 수분을 제거한다. 또한, 수분을 더욱 효과적으로 흡수하고 흡수한 수분을 방화복 밖으로 배출되도록 흡수속건 소재를 추가로 포함할 수 있다.Materials containing meta-aramid and cooling materials have an effective cooling effect because heat transfers quickly when they come into contact with the skin, and moisture such as sweat from the inside of the fire-proof suit penetrates to the inside of the fiber bundle to remove moisture. In addition, an absorbent quick-drying material may be additionally included to more effectively absorb moisture and to discharge the absorbed moisture out of the fire protection suit.

흡수속건은 흡한속건이라고도 하며, 땀을 빠르게 흡수하고 건조시킨다는 의미이다. 흡수속건의 원리는 모세관 현상이다. 모세관 현상(Capillarity, Capillary Action)은 중력 등의 외부힘에 상관없이 유체가 가느다란 관이나 다공성 물질 등의 좁은 공간을 타고 올라가는 성질을 말한다. 액체 속에 가는 관(모세관)을 세웠을 때, 관 안 액체의 면이 관 바깥 액체의 면보다 높거나 낮게 나타나는 현상이다. 중공사(단면 가운데 구멍이 있는 것)의 섬유 겉에 미세한 구멍을 무수히 뚫어, 모세관 현상을 이용하여 수분(땀)을 빨리 빨아들이고, 빨아들인 수분을 중공사의 중공 부분을 이용하여 발산한다. 이를 위해 단면 구조가 독특한 섬유로 의류를 만들어, 수분이 좁은 섬유의 사이로 모세관 현상으로 흡수하여 바깥쪽으로 이동하여 발산되도록 한다. 섬유의 단면이 원형보다는 구불구불한 표면적이 넓은 원사로 옷을 이루어 수분을 증발시킬 면적이 넓어 빠른 시간에 수분의 증발이 가능하다.Absorption quick-drying is also called sweat-absorbing quick-drying, meaning that it absorbs sweat quickly and dries it. The principle of quick-drying absorption is capillary action. Capillary action (capillary action) refers to the property of a fluid going up in a narrow space such as a thin tube or porous material regardless of an external force such as gravity. When a thin tube (capillary tube) is erected in the liquid, the surface of the liquid inside the tube appears higher or lower than the surface of the liquid outside the tube. Countless fine holes are drilled on the fiber surface of the hollow fiber (the one with a hole in the middle of the cross section), and moisture (sweat) is quickly absorbed using the capillary phenomenon, and the absorbed moisture is dissipated using the hollow part of the hollow fiber. For this purpose, the clothing is made of fibers with a unique cross-sectional structure, and moisture is absorbed through the narrow fibers through capillary action and moves outward to be released. The cross section of the fiber is made of yarn with a wide surface area rather than a circular one, and the area to evaporate moisture is large, so moisture can be evaporated quickly.

흡수속건 기능이 있는 소재를 만들기 위해서 다음과 같은 기능을 소재에 부여한다. 첫째, 원단이 친수성(Hydro-Philic)을 띄어야 한다. 즉 소재가 물을 좋아해서, 수분을 빠르게 흡수해야 한다는 것이다. 둘째, 원단(원사)의 표면적이 극대화 되어야 한다. 표면적을 극대화하기 위해 취하는 방법이 원사단면의 이형화(異形化)와 극세화(極細化)이다. 이렇게 원단의 설계를 하게 되면, 수분이 빠르게 표면적을 따라 확산되어 증발하게 되는 것이다. 이렇게 만들어진 소재는 흡수속건의 기능을 가질 수 있게 된다. 셋째, 원단의 구조를 이중직으로 설계하여, 피부에 닿는 층과 표면층의 밀도를 다르게 하여, 모세관현상을 구조적으로 만들게 되면, 흡수속건의 기능이 더 좋아지게 된다.In order to make a material with a quick-drying function, the following functions are given to the material. First, the fabric must be hydrophilic. In other words, the material likes water, so it needs to absorb moisture quickly. Second, the surface area of the fabric (yarn) should be maximized. The method taken to maximize the surface area is to make the yarn cross-section molded and micro-fine. When the fabric is designed in this way, the moisture quickly diffuses along the surface area and evaporates. The material made in this way can have the function of absorption and quick-drying. Third, if the structure of the fabric is designed as a double weave, and the density of the layer in contact with the skin and the density of the surface layer are different to make the capillary phenomenon structurally, the function of absorption and quick drying will be better.

본 발명은 냉감소재와 메타아라미드 섬유 사이의 접합 홈에 흡수 속건 소재를 추가하여 화재 현장에서 소방관이 흘리는 땀을 효과적으로 흡수하여 방화복 내부의 수분이 더욱 빠른 속도로 증발 및 제거되도록 한다. 또한, 땀이 기체로 상전이 되는 과정에서 흡열반응이 발생해 피부의 온도를 낮추는 부차적인 효과가 있다.The present invention adds an absorbent quick-drying material to the joint groove between the cooling material and the meta-aramid fiber to effectively absorb the sweat of the firefighter at the fire site, so that the moisture inside the fire-proof suit evaporates and is removed at a faster rate. In addition, an endothermic reaction occurs during the phase change of sweat to gas, which has a secondary effect of lowering the skin temperature.

합성수지 섬유는 제조방식에 따라 크게 건식, 습식 및 용융방사로 나누어지고 있으며, 건식 및 습식 방사법은 합성수지를 용제에 녹인 후 방사 중에 용제를 증발 또는 추출하여 제조하는 방식으로 전세계 제조 프로세스 중 95%이상을 점유하고 있다.Synthetic resin fibers are largely divided into dry, wet and melt spinning depending on the manufacturing method. is occupying

이중 건식방사의 경우 물성면에서 우수한 제품생산이 가능하므로 가장 많이 채용하고 있는 프로세스이다. 섬유 고분자를 증발하기 쉬운 용매에 녹인 후, 이 용액을 가느다란 구멍의 노즐을 통하여 뜨거운 공기나 비활성 가스 속으로 압출하여 용매를 증발시켜 섬유를 얻는 방법으로, 열용융하기 어려운 고분자 물질과 열분해하기 쉬운 고분자 물질에 적용된다. 용매로는 끓는점이 낮고 증발열이 작은 것이 좋으며, 아세톤·디메틸포름아미드·이황화탄소 등이 사용된다. 건식방사에 의해 얻는 섬유의 예로는 아세테이트 섬유·비닐론·비니온·비니온N·다이넬·염화비닐 섬유·올론·아크릴·아라미드 등이 있다. 건식방사는 생산 단위 별 품질이 우수하고 전기절연성이 뛰어나며 습식 방사에 비해 방사속도가 몇 배나 빠르다는 장점이 있으나, 생산조건이 까다롭고 복잡한 설비가 필요하다는 단점이 있다.In the case of dry spinning, it is the most used process because it is possible to produce excellent products in terms of physical properties. After dissolving the fiber polymer in a solvent that is easy to evaporate, the solution is extruded into hot air or inert gas through a nozzle with a narrow hole to evaporate the solvent to obtain fibers. Applied to polymeric materials. The solvent has a low boiling point and low heat of evaporation, and acetone, dimethylformamide, carbon disulfide, etc. are used. Examples of the fiber obtained by dry spinning include acetate fiber, vinylon, vinylon, vinylon N, dynel, vinyl chloride fiber, olon, acryl, aramid, and the like. Dry spinning has the advantages of excellent quality for each production unit, excellent electrical insulation, and spinning speed several times faster than wet spinning, but it has disadvantages in that production conditions are difficult and complex equipment is required.

본 발명의 방화복 내피용 소재는 생산 단위 별 품질이 우수하고 전기 절연성이 뛰어난 건식 방사 제조 공법으로 제조되며, 메타아라미드와 냉감소재로 섬유 다발을 제조하고 섬유 다발 사이에 흡수 속건 소재를 추가하여 이를 방화복 내피의 소재로 사용한다. The fire protection inner covering material of the present invention is manufactured by a dry spinning manufacturing method with excellent quality for each production unit and excellent electrical insulation. It is used as a material for the inner skin.

전술된 바와 같이, 방화복 내피용 소재는 기존의 메타아라미드 섬유에 냉감소재, 흡수 속건 소재를 포함함으로써 화재 현장의 열기로 인한 화상을 막고 내부에 누적되는 수분을 빠르게 증발시켜 일의 효율이 증가하고 방화복 내부에 쾌적함을 제공할 수 있다.As described above, the inner material for fire suits contains a cooling material and an absorbent quick-drying material in the existing meta-aramid fiber to prevent burns caused by the heat at the fire site and quickly evaporate the moisture accumulated inside, thereby increasing the work efficiency and improving the work efficiency. It can provide comfort inside.

이상, <실시예>를 통하여 본 발명을 상세하게 설명하였으나, 본 발명은 상기 구현예들에 한정되지 않고, 여러 가지 다양한 형태로 변형될 수 있으며, 본 발명의 기술적 사상 내에서 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의하여 여러 가지 많은 변형이 가능함이 명백하다. 또한, 청구범위에 기재된 본 발명의 기술적 사상을 벗어나지 않는 범위 내에서 본 발명이 속하는 기술 분야의 통상의 지식을 가진 자에 의해 다양한 형태의 치환, 변형 및 변경이 가능할 것이며, 이 또한 본 발명의 범위에 속한다고 할 것이다.As described above, the present invention has been described in detail through the <Examples>, but the present invention is not limited to the above embodiments, and may be modified in various forms, within the technical spirit of the present invention. It is clear that many modifications are possible by those skilled in the art. In addition, within the scope that does not depart from the technical spirit of the present invention described in the claims, various types of substitution, modification and change will be possible by those skilled in the art to which the present invention belongs, and this is also the scope of the present invention will be said to belong to

1 : 메타아라미드 2 : 냉감소재 3 : 흡수속건 소재1: meta aramid 2: Cooling material 3: Absorption and quick-drying material

Claims (4)

메타아라미드 및 냉감소재를 포함하는 것을 특징으로 하는 방화복 내피용 소재.Fire-fighting inner skin material, characterized in that it contains meta-aramid and a cooling material. 제 1항에 있어서,상기 방화복 내피용 소재에 흡수속건 소재를 추가로 포함하는 것을 특징으로 하는 방화복 내피.According to claim 1, Fire protection clothing endothelium, characterized in that it further comprises an absorbent quick-drying material to the fire protection clothing endothelial material. 제 1항에 있어서,상기 냉감소재는 레이온 또는 큐프라를 포함하는 접촉냉감 소재인 것을 특징으로 하는 방화복 내피용 소재.According to claim 1, The cooling material is a fire protective clothing endothelial material, characterized in that the contact cooling material containing rayon or cupra. 제 2항에 있어서,상기 흡수속건 소재는 상기 냉감소재와 메타아라미드 섬유 다발 사이에 추가되는 것을 특징으로 하는 방화복 내피용 소재.According to claim 2, The absorbent quick-drying material is fire protective clothing endothelial material, characterized in that added between the cooling material and the meta-aramid fiber bundle.