KR20220084653A - A biodegradable mask included tea-tree and biodegradable fiber contained PBS and PLA, AND Manufacturing method of the same - Google Patents

A biodegradable mask included tea-tree and biodegradable fiber contained PBS and PLA, AND Manufacturing method of the same Download PDF

Info

Publication number
KR20220084653A
KR20220084653A KR1020200174338A KR20200174338A KR20220084653A KR 20220084653 A KR20220084653 A KR 20220084653A KR 1020200174338 A KR1020200174338 A KR 1020200174338A KR 20200174338 A KR20200174338 A KR 20200174338A KR 20220084653 A KR20220084653 A KR 20220084653A
Authority
KR
South Korea
Prior art keywords
mask
biodegradable
tea tree
resin
fiber
Prior art date
Application number
KR1020200174338A
Other languages
Korean (ko)
Inventor
하창호
Original Assignee
주식회사 신화그룹
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 신화그룹 filed Critical 주식회사 신화그룹
Priority to KR1020200174338A priority Critical patent/KR20220084653A/en
Publication of KR20220084653A publication Critical patent/KR20220084653A/en

Abstract

본 발명은 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법에 관한 것으로, 그 절차는 PBS 수지와 다공성의 파라셀 분말의 무기계 충진제를 혼합한 혼합물을 용융온도 114℃ 이상, 열분해 온도인 255℃ 미만의 온도로 하고 압출기의 온도는 150 ~ 180℃ 범위로 압출하고 티트리 추출물을 혼합하여 배치를 제조하는 제 1 공정; PLA 수지 88 ~ 95 중량%과 배치 5 ~ 12 중량%을 혼합한 혼합물을 PLA 수지의 용융온도 151℃ 이상으로 하고 255℃ 미만의 온도에서 압출하여 생분해성 섬유 재료를 제조한 후 건조하는 제 2 공정; 상기 건조된 생분해성 섬유 재료를 압출 방사하여 미연신 원사를 연신하는 제 3 공정; 상기 압출 방사된 미연신 원사를 연신 단계를 거친 후, 연신된 원사를 90 ~ 100℃의 온도 범위로 유지하여 섬유 결정화하는 제 4 공정; 결정화된 섬유에 필라멘트 권축을 위해 크래핑 절차를 진행하는 제 5 공정; 크래핑 단계를 통해 권축된 필라멘트에 친수성 방사유제 에멀젼이 함유된 액상수지를 표면에 부착시키고 열 고정하는 제 6 공정; 및 열 고정단계에 의해 구비된 섬유를 소정의 길이만큼 절단하여 마스크 형태로 성형하여 내피에 겔 타입의 마스크 필터를 안착하거나, 마스크 표면에 겔 상태의 조성물를 도포하여 마스크를 제작하는 제 7 공정;을 포함하여 구성된다.The present invention relates to a biodegradable mask containing biodegradable fibers containing PBS and PLA resins and tea tree extract, and a method for manufacturing the same, and the procedure is a mixture of PBS resin and inorganic filler of porous Paracell powder. A first step of preparing a batch by extruding at a melting temperature of 114° C. or higher and a thermal decomposition temperature of less than 255° C., extruding the extruder at a temperature in the range of 150 to 180° C., and mixing the tea tree extract; The second process of manufacturing a biodegradable fiber material by extruding a mixture of 88 to 95 wt% of PLA resin and 5 to 12 wt% of a batch at a melting temperature of 151°C or higher of PLA resin and lower than 255°C, followed by drying ; a third step of stretching the undrawn yarn by extrusion spinning the dried biodegradable fiber material; a fourth process of fiber crystallization by maintaining the stretched yarn in a temperature range of 90 to 100° C. after the extrusion spun undrawn yarn undergoes a drawing step; a fifth step of performing a crimping procedure for crimping the crystallized fibers with filaments; a sixth step of attaching a liquid resin containing a hydrophilic spinning emulsion to the crimped filaments through the scraping step to the surface and heat fixing; and a seventh process of cutting the fiber provided by the heat setting step by a predetermined length and molding it into a mask shape to seat a gel-type mask filter on the endothelium, or applying a gel-state composition to the mask surface to produce a mask; is comprised of

Description

PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법{A biodegradable mask included tea-tree and biodegradable fiber contained PBS and PLA, AND Manufacturing method of the same}{A biodegradable mask included tea-tree and biodegradable fiber contained PBS and PLA, AND Manufacturing method of the same}

본 발명은 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법에 관한 것으로, 보다 구체적으로는, PBS 및 PLA 수지가 함유된 생분해성 섬유 또는 직물지와 자연분해 성분인 티트리 추출물로 구성된 일체형 생분해성 마스크 또는 PBS 및 PLA 수지가 함유된 생분해성 섬유에 티트리 분말, 황토, 맥반석 화합물로 겔 타입의 필터를 구비하여 마스크의 내피에 고정 삽입, 안착되는 필터 교체형으로 사용 가능한 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법에 관한 것이다.The present invention relates to a biodegradable mask containing biodegradable fibers containing PBS and PLA resins and tea tree extract, and a method for manufacturing the same, and more specifically, to biodegradable fibers or fabrics containing PBS and PLA resins and natural An integrated biodegradable mask composed of tea tree extract, which is a decomposition component, or a biodegradable fiber containing PBS and PLA resin with a gel-type filter made of tea tree powder, ocher, and elvan stone compound. It relates to a biodegradable mask containing biodegradable fibers and tea tree extract containing PBS and PLA resins that can be used as replacements, and a method for manufacturing the same.

일반적으로 마스크는 얼굴 부위에 착용되어 추위를 막아주는 방한용품으로 많이 사용되어 왔으나, 대기오염이 심각해진 현대에는 공기 중에 포함된 먼지나 오염물질 등의 흡입을 막기 위하여 코와 입을 커버할 수 있도록 하는 위생용품으로 자리매김하고 있다.In general, a mask is worn on the face and has been used a lot as a cold protection product to block the cold. It is positioned as a hygiene product.

종래에는 마스크는 주로 감기환자, 호흡기 질환이 있는 사람이나 찬 공기에 특히 약한 사람들이 착용하여 왔으며 환자의 호흡시 병원균의 확산을 감소시키기 위해서도 필요하며, 최근에는 중국으로부터의 미세 먼지, 중금속 등의 성분이 많은 황사로 인한 문제가 크게 대두됨에 따라 호흡기질환이 있는 환자뿐만 아니라, 어린이나 노인과 같이 호흡기가 약하고 신체가 특히 약한 사람외에 일반인들도 특히 황사가 자주 발생되는 봄철에는 마스크를 휴대해야 하는 경우가 많아졌다.In the past, masks have been mainly worn by cold patients, people with respiratory diseases, or people who are particularly weak to cold air, and they are also needed to reduce the spread of pathogens when breathing in patients. As the problem caused by many yellow dust has risen significantly, not only patients with respiratory diseases, but also people with weak respiratory tract and particularly weak bodies such as children and the elderly, the general public, especially in the springtime when yellow dust occurs frequently, must carry a mask. has become more

일반적인 마스크 구조는 호흡에 불편함이 크지 않도록 통기성이 좋은 직물로 만들어진 마스크 패드와, 그 양측부에 귀에 걸어 착용하도록 귀걸이 줄이 부착되어 구성되는데, 이로인해 마스크는 먼지나 오염물질 등을 걸러낼 수 있지만, 박테리아나 세균까지는 걸러낼 수 없는 문제점이 있다.A general mask structure consists of a mask pad made of a breathable fabric to prevent discomfort in breathing, and an earring string attached to both sides of the earring to be worn over the ear. However, there is a problem in that even bacteria or bacteria cannot be filtered out.

또한, 종래의 마스크를 장시간 동안 착용하는 경우에는 착용자의 날숨에 포함된 수분, 땀과 같은 분비물, 구강 내 세균 등으로 인해 마스크가 오염됨에 따라 새로운 마스크로 자주 교체해야 하는 문제점이 있다.In addition, when the conventional mask is worn for a long time, there is a problem in that the mask must be frequently replaced with a new mask as the mask is contaminated due to moisture contained in the wearer's exhaled breath, secretions such as sweat, and oral bacteria.

그러나 종래의 마스크는 내피나 외피 등에 흡습성 소재가 적용됨과 동시에 광촉매제 또는 무기항균제를 함침 또는 코팅하는 형태로 별도 항균 처리됨에 따라 세탁시 기능저하로 인해 반영구적인 사용이 불가능한 문제점이 있었다.However, as the conventional mask is separately antibacterial in the form of impregnating or coating a photocatalyst or inorganic antibacterial agent at the same time as a hygroscopic material is applied to the inner skin or outer skin, there is a problem that it cannot be used semi-permanently due to deterioration of function during washing.

또한 종래의 항균 마스크의 경우에는 내피, 외피, 필터 등에 예를 들어 부직포와 같은 흡습성 소재가 적용됨에 따라 착용자의 입김에서 비롯되는 수분에 취약할 뿐만아니라 세균이나 박테리아가 서식할 수 있는 환경이 제공될 수 있는 문제점이 있다.In addition, in the case of a conventional antibacterial mask, as a hygroscopic material such as a non-woven fabric is applied to the inner skin, outer skin, filter, etc., it is not only vulnerable to moisture from the wearer's breath, but also provides an environment in which bacteria or bacteria can inhabit. There are possible problems.

또한 종래의 항균 마스크의 경우에는 항균처리를 위한 광촉매제 또는 무기항균제로 인해 상대적으로 좋지 않은 냄새가 나며 오랫동안 착용할 경우 피부에 부작용을 유발하기도 하는 문제점이 있다.In addition, in the case of a conventional antibacterial mask, a photocatalyst or inorganic antibacterial agent for antibacterial treatment has a relatively bad odor, and there is a problem in that it may cause side effects on the skin when worn for a long time.

이에 본 출원인은 교체가 편리하고 생분해 성분으로 환경오염 문제를 해결할 수 있는 마스크 제조방안을 제시하고자 한다.Accordingly, the present applicant intends to propose a mask manufacturing method that is convenient to replace and can solve the environmental pollution problem with biodegradable ingredients.

1. 마스크(A MASK)(특허출원번호 제10-2007-0045128호)1. Mask (A MASK) (Patent Application No. 10-2007-0045128) 2. 1회용 기능성 마스크(FUNCTIONAL MASK)(실용신안출원번호 제20-2012-0001074호)2. Disposable Functional Mask (FUNCTIONAL MASK) (Utility Model Application No. 20-2012-0001074) 3. 어성초 추출물을 포함하는 바이러스 감염예방 마스크 및 필터(Face mask or filter material comprising Houttuynia cordata extract)(특허출원번호 제10-2010-0096510호)3. Face mask or filter material comprising Houttuynia cordata extract (Patent Application No. 10-2010-0096510)

상기한 문제점을 개선하기 위해 안출된 본 발명의 기술적 과제는 PBS 및 PLA 수지가 함유된 생분해성 섬유 또는 직물지와 자연분해 성분인 티트리 추출물이 일체로 구성된 생분해성 마스크 또는 PBS 및 PLA 수지가 함유된 생분해성 섬유에 티트리 분말, 황토, 맥반석 화합물을 겔 타입으로 구비된 필터를 마스크의 내피에 고정 삽입, 안착되는 필터 교체형으로 사용 가능한 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법을 제공하는데 있다.The technical problem of the present invention devised to improve the above problems is a biodegradable mask comprising a biodegradable fiber or fabric containing PBS and PLA resin and a tea tree extract, a biodegradable component, or a biodegradable mask containing PBS and PLA resin. A filter equipped with tea tree powder, ocher, and elvan stone compound in the biodegradable fiber is fixedly inserted into the endothelium of the mask, and biodegradable fiber containing PBS and PLA resin and tea tree extract that can be used as a filter replacement type to be seated To provide a biodegradable mask and a method for manufacturing the same.

또한, 본 발명은 티트리의 약리작용, 황토의 유해한 미생물을 사멸, 항균성을 발현 및 맥반석의 탈취, 유해물질 분해 작용을 통해 티트리, 황토 및 맥반석의 조성물로 마스크 필터를 형성하여 마스크 내부층 공간부에 일체로 형성하거나, 내면에 삽입 안착되도록 형성하여 외부에서 유입되는 유해물질을 차단할 수 있는 항균, 방취 기능이 있는 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법을 제공하는데 있다.In addition, the present invention forms a mask filter with a composition of tea tree, loess and elvan through the pharmacological action of tea tree, killing harmful microorganisms of loess, expressing antibacterial properties, deodorizing elvan stone, and decomposing harmful substances to form a mask inner layer space A biodegradable mask containing tea tree extract and biodegradable fibers containing PBS and PLA resins with antibacterial and deodorizing functions that can be formed integrally with the body or inserted and seated on the inner surface to block harmful substances from the outside and to provide a method for manufacturing the same.

그러나 본 발명의 목적들은 상기에 언급된 목적으로 제한되지 않으며, 언급되지 않은 또 다른 목적들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.However, the objects of the present invention are not limited to the above-mentioned objects, and other objects not mentioned will be clearly understood by those skilled in the art from the following description.

상기의 목적을 달성하기 위한 본 발명의 실시예에 따른 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크는 PBS 수지와 다공성의 파라셀 분말의 무기계 충진제를 혼합한 혼합물을 용융온도 114℃ 이상, 열분해 온도인 255℃ 미만의 온도로 하고 압출기의 온도는 150 ~ 180℃ 범위로 압출한 후 티트리 추출물을 혼합하여 구비된 배치 5 ~ 12 중량%과 PLA 수지 88 ~ 95 중량% 혼합한 혼합물을 압출하여 생분해성 섬유 재료를 제조하고 건조한 후, 건조된 생분해성 섬유 재료를 압출 방사하여 미연신 원사를 연신단계를 통해 연신된 원사를 하여 90 ~ 100℃의 온도를 유지하여 섬유 결정화가 이루어지도록 하고, 결정화된 섬유에 필라멘트 권축을 위해 크래핑하여 권축된 필라멘트에 친수성 방사유제 에멀젼이 함유된 액상수지를 표면에 부착하고 열고정하여 구비된 생분해성 섬유를 소정의 길이로 절단하여 마스크 형태로 성형하여 마스크 외부 및 내부 사이에 티트리, 황토, 맥반석 및 물을 혼합하여 숙성, 건조된 혼합물에 미강, 찹쌀 및 물을 혼합하여 95℃로 2 ~ 4시간 가열하여 냉각시켜 구비된 액체 접착물질과 혼합하여 구비된 마스크 필터(F)를 적층하여 일체로 성형하여 마스크 외부와 내부 사이의 내피층에 마스크 필터(F)가 안착되어 일체로 형성되는 것을 특징으로 한다.In order to achieve the above object, the biodegradable mask containing the biodegradable fiber containing the PBS and PLA resin and the tea tree extract according to the embodiment of the present invention for achieving the above object is a mixture of PBS resin and inorganic filler of porous Paracell powder 5 to 12 wt% of a batch prepared by mixing tea tree extract after extruding at a melting temperature of 114°C or higher and a thermal decomposition temperature of less than 255°C and the temperature of the extruder in the range of 150-180°C and PLA resin 88-95 After extruding the mixture mixed by weight% to produce a biodegradable fiber material and drying it, the dried biodegradable fiber material is extruded and spun to the undrawn yarn through the drawing step, and the temperature of 90 ~ 100 ℃ is maintained. Fiber crystallization is made, and the biodegradable fiber is cut to a predetermined length by attaching a liquid resin containing a hydrophilic spinning emulsion to the crimped filament to the surface and heat-setting it. A liquid provided by molding into a mask shape, mixing tea tree, ocher, elvan stone, and water between the outside and inside of the mask, mixing rice bran, glutinous rice and water in the dried mixture, heating it at 95°C for 2 to 4 hours and cooling it It is characterized in that the mask filter (F) provided by mixing with an adhesive material is laminated and integrally formed so that the mask filter (F) is seated on the inner skin layer between the outside and the inside of the mask to be integrally formed.

또한, 본 발명에 따른 일 실시예로서 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 마스크 제조방법은 PBS 수지와 다공성의 파라셀 분말의 무기계 충진제를 혼합한 혼합물을 용융온도 114℃ 이상, 열분해 온도인 255℃ 미만의 온도로 하고 압출기의 온도는 150 ~ 180℃ 범위로 압출하고 티트리 추출물을 혼합하여 배치를 제조하는 제 1 공정; PLA 수지 88 ~ 95 중량%과 배치 5 ~ 12 중량%을 혼합한 혼합물을 PLA 수지의 용융온도 151℃ 이상으로 하고 255℃ 미만의 온도에서 압출하여 생분해성 섬유 재료를 제조한 후 건조하는 제 2 공정; 상기 건조된 생분해성 섬유 재료를 압출 방사하여 미연신 원사를 연신하는 제 3 공정; 상기 압출 방사된 미연신 원사를 연신 단계를 거친 후, 연신된 원사를 90 ~ 100℃의 온도 범위로 유지하여 섬유 결정화하는 제 4 공정; 결정화된 섬유에 필라멘트 권축을 위해 크래핑 절차를 진행하는 제 5 공정; 크래핑 단계를 통해 권축된 필라멘트에 친수성 방사유제 에멀젼이 함유된 액상수지를 표면에 부착시키고 열 고정하는 제 6 공정; 및 열 고정단계에 의해 구비된 섬유를 소정의 길이만큼 절단하여 마스크 형태로 성형하여 내피에 겔 타입의 마스크 필터를 안착하거나, 마스크 표면에 겔 상태의 조성물를 도포하여 마스크를 제작하는 제 7 공정;을 포함하여 구성되는 것을 특징으로 한다.In addition, in the method for manufacturing a mask containing biodegradable fiber containing PBS and PLA resin and tea tree extract as an embodiment according to the present invention, a mixture of PBS resin and inorganic filler of porous Paracel powder is mixed with a melting temperature of 114 A first step of producing a batch by extruding at a temperature of ℃ or more and less than 255 ℃, which is a thermal decomposition temperature, and the temperature of the extruder is in the range of 150 to 180 ℃, and mixing the tea tree extract; The second process of manufacturing a biodegradable fiber material by extruding a mixture of 88 to 95 wt% of PLA resin and 5 to 12 wt% of a batch at a melting temperature of 151°C or higher of PLA resin and lower than 255°C, followed by drying ; a third step of stretching the undrawn yarn by extrusion spinning the dried biodegradable fiber material; a fourth process of fiber crystallization by maintaining the stretched yarn in a temperature range of 90 to 100° C. after the extrusion spun undrawn yarn undergoes a drawing step; a fifth step of performing a crimping procedure for crimping the crystallized fibers with filaments; a sixth step of attaching a liquid resin containing a hydrophilic spinning emulsion to the crimped filaments through the scraping step to the surface and heat fixing; and a seventh process of cutting the fiber provided by the heat setting step by a predetermined length and molding it into a mask shape to seat the gel-type mask filter on the endothelium, or applying a gel-like composition to the mask surface to produce a mask; It is characterized in that it is configured to include.

본 발명에 따른 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법은 PBS 및 PLA 수지가 함유된 생분해성 섬유 또는 직물지와 자연분해 성분인 티트리 추출물이 일체로 구성된 생분해성 마스크 또는 PBS 및 PLA 수지가 함유된 생분해성 섬유에 티트리 분말, 황토, 맥반석 화합물로 겔 타입으로 구비된 필터를 마스크의 내피에 고정 삽입, 안착되는 필터 교체형으로 사용 가능하여 생분해에 따른 환경오염을 개선할 수 있는 마스크를 제공할 수 있다.A biodegradable mask containing biodegradable fibers containing PBS and PLA resins and tea tree extract according to the present invention and a manufacturing method thereof include biodegradable fibers or textile paper containing PBS and PLA resins and tea tree extract, which is a naturally degradable component, according to the present invention. It can be used as a filter replacement type that is fixedly inserted and seated on the endothelium of the mask with a filter provided in a gel type with tea tree powder, ocher, and elvan compound on a biodegradable mask or biodegradable fiber containing PBS and PLA resin. It is possible to provide a mask capable of improving environmental pollution caused by biodegradation.

또한, 본 발명의 실시예에 따른 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법은 티트리의 약리작용, 황토의 유해한 미생물을 사멸, 항균성을 발현 및 맥반석의 탈취, 유해물질 분해 작용을 통해 티트리, 황토 및 맥반석의 조성물을 마스크 필터를 형성하여 마스크 내부층 공간부에 일체로 형성하거나, 내면에 삽입 안착되도록 형성하여 외부에서 유입되는 유해물질을 차단할 수 있는 항균, 방취 기능이 있는 마스크를 제공할 수 있다.In addition, the biodegradable mask containing the biodegradable fiber containing the PBS and PLA resin and the tea tree extract according to the embodiment of the present invention and the manufacturing method therefor, the pharmacological action of tea tree, killing harmful microorganisms of ocher, and expressing antibacterial properties And through the deodorization of elvan stone and decomposition of harmful substances, the composition of tea tree, loess, and elvan stone is formed as a mask filter to form a mask in the inner space of the mask, or is formed to be inserted and seated on the inner surface of the mask to remove harmful substances flowing in from the outside It is possible to provide a mask with antibacterial and deodorizing functions that can block it.

또한, 본 발명의 실시예에 따른 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법은 티트리 추출물을 PBS 및 PLA 수지가 함유된 생분해성 섬유에 도포후 건조하여 마스크 형태의 일정크기로 제단하여 마스크를 제조할 수 있고, PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물을 혼합하여 생분해성 재질의 섬유를 직조하여 마스크 형태로 제조할 있는데, 이를 통해 티트리의 자연분해 성분과 생분해성 섬유의 생분해 성분을 통해 구비된 마스크를 사용후 폐기시 분해되어 자연소거를 유도할 수 있다.In addition, in the biodegradable mask containing the biodegradable fiber containing PBS and PLA resin and the tea tree extract according to an embodiment of the present invention, and the manufacturing method thereof, the tea tree extract is applied to the biodegradable fiber containing the PBS and PLA resin After drying, the mask can be manufactured by cutting it to a certain size in the form of a mask, and by mixing biodegradable fibers containing PBS and PLA resin and tea tree extract, weaving fibers of a biodegradable material to make a mask. Through this, the mask provided through the biodegradable component of the tea tree and the biodegradable component of the biodegradable fiber is decomposed upon disposal after use to induce natural erasure.

또한, 또한, 본 발명의 실시예에 따른 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 및 그 제조방법은 황토 성분이 함유된 기능성 물질을 마스크 필터로 이용함으로써 우수한 항균성, 방취성 및 원적외선 효과와 생분해성 부직포 직물을 마스크의 원단으로 사용하여 신축성 및 질감이 있어 장시간 유지되고, 촉감이 부드러운 마스크를 제공할 수 있다.In addition, the biodegradable mask containing the biodegradable fiber containing the PBS and PLA resin and the tea tree extract according to the embodiment of the present invention and the manufacturing method thereof are excellent by using the functional material containing the ocher component as a mask filter. It is possible to provide a mask with antibacterial, deodorizing and far-infrared effects and biodegradable non-woven fabric as the fabric for the mask, which has elasticity and texture, which is maintained for a long time and is soft to the touch.

도 1은 본 발명의 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 제조절차를 도시한 흐름도
도 2는 도 1에 의해 구비된 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크의 사시도
도 3은 도 2에 따른 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크의 배면도
도 4는 본 발명의 일 실시예에 따른 티트리, 황토 및 맥반석이 함유된 마스크 필터 조성물의 제조방법을 도시한 흐름도
도 5는 도 4에 의해 제조된 티트리, 황토 및 맥반석이 함유된 마스크 필터의 단면도
도 6은 본 발명에 따른 티트리, 황토 및 맥반석 함유된 조성물이 마스크 내부에 안착되어 일체로 형성된 상태를 도시한 사시도
도 7은 도 6에 따른 티트리, 황토 및 맥반석이 함유된 조성물이 마스크 내부에 안착되어 구성된 생분해성 마스크의 단면도
도 8은 본 발명의 다른 실시예에 따른 티트리, 황토 및 맥반석 함유된 조성물이 마스크 필터로 구비되어 형성된 생분해성 마스크의 상태를 도시한 사시도
도 9는 도 8에 의해 티트리, 황토 및 맥반석 함유된 마스크 필터로 구비되어 형성된 생분해성 마스크의 전면을 도시한 사시도
도 10은 본 발명에 따른 티트리, 황토 및 맥반석 함유된 마스크 필터로 구비되어 형성된 생분해성 마스크의 내면을 도시한 사시도
도 11은 본 발명에 따른 티트리, 황토 및 맥반석 함유된 조성물이 마스크 필터로 마스크 내부에 삽입되어 안착된 상태를 보인 사시도
도 12는 도 11에 따른 티트리, 황토 및 맥반석이 함유된 조성물이 마스크 필터로 내부에 안착되어 구성된 마스크의 단면도1 is a flow chart showing a biodegradable mask manufacturing procedure containing biodegradable fiber and tea tree extract containing PBS and PLA resin of the present invention
Figure 2 is a perspective view of a biodegradable mask containing biodegradable fibers and tea tree extract containing PBS and PLA resin provided by Figure 1;
3 is a rear view of a biodegradable mask containing biodegradable fibers and tea tree extract containing PBS and PLA resin according to FIG.
4 is a flowchart illustrating a method of manufacturing a mask filter composition containing tea tree, loess and elvan according to an embodiment of the present invention;
5 is a cross-sectional view of the mask filter containing tea tree, loess and elvan manufactured by FIG.
6 is a perspective view showing a state in which the composition containing tea tree, loess, and elvan according to the present invention is seated inside the mask and formed integrally;
7 is a cross-sectional view of a biodegradable mask in which the composition containing tea tree, loess, and elvan according to FIG. 6 is seated inside the mask;
8 is a perspective view showing the state of a biodegradable mask formed by providing a composition containing tea tree, loess and elvan stone as a mask filter according to another embodiment of the present invention;
9 is a perspective view showing the front of the biodegradable mask formed by being provided with a mask filter containing tea tree, loess, and elvan by FIG. 8;
10 is a perspective view showing the inner surface of a biodegradable mask provided with a mask filter containing tea tree, loess and elvan according to the present invention;
11 is a perspective view showing a state in which the composition containing tea tree, loess, and elvan according to the present invention is inserted and seated inside the mask as a mask filter;
12 is a cross-sectional view of a mask in which the composition containing tea tree, loess, and elvan according to FIG. 11 is seated inside as a mask filter;

이하, 본 발명의 바람직한 실시 예의 상세한 설명은 첨부된 도면들을 참조하여 설명할 것이다. 하기에서 본 발명을 설명함에 있어서, 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다.Hereinafter, a detailed description of a preferred embodiment of the present invention will be described with reference to the accompanying drawings. In the following description of the present invention, if it is determined that a detailed description of a related well-known function or configuration may unnecessarily obscure the gist of the present invention, the detailed description thereof will be omitted.

본 발명은 PBS 및 PLA 수지가 함유된 생분해성 섬유 또는 직물지와 자연분해 성분인 티트리 추출물이 일체로 구성된 생분해성 마스크 또는 PBS 및 PLA 수지가 함유된 생분해성 섬유에 티트리 분말, 황토, 맥반석 화합물로 겔 타입의 마스크 필터를 구비하여 이를 마스크의 내피에 고정 삽입, 안착되는 필터 교체형으로 사용이 가능한 마스크를 제공하기 위한 것이다.The present invention relates to a biodegradable mask composed of a biodegradable fiber or textile paper containing PBS and PLA resin and a tea tree extract, which is a biodegradable component, or a tea tree powder, ocher, and elvan stone compound on a biodegradable fiber containing PBS and PLA resin. It is to provide a mask that can be used as a filter replacement type that is provided with a rogel-type mask filter and fixedly inserted into and seated on the endothelium of the mask.

본 발명에 따른 생분해성이란 분해의 한 과정에 광(자외선)이나 자연계에서 존재하는 미생물이 분비하는 효소에 의해 저 분자량 화합물로 변환하는 것을 말한다. 고분자 재료의 분해는, 우선 미생물이 균체 외로 분비하는 분해효소가 고분자 재료 표면에 흡착하여, 고분자의 에스테르 결합, 글리코시드 결합, 펩티드 결합 등의 화학결합을 가수분해 반응으로 절단된다. 고분자 물질의 저 분자량화에 따라 재료는 붕괴하고, 생성물은 효소분해에 의해 단량체 단위, 즉 단량체나 이량체의 저분자량 분해 생성물로 된다.Biodegradability according to the present invention refers to conversion into low molecular weight compounds by light (ultraviolet rays) or enzymes secreted by microorganisms existing in nature in one process of decomposition. In the decomposition of polymer materials, first, degradative enzymes secreted by microorganisms outside the cells adsorb to the surface of the polymer material, and chemical bonds such as ester bonds, glycosidic bonds, and peptide bonds of the polymer are cleaved by a hydrolysis reaction. As the molecular weight of the high molecular substance is reduced, the material is disintegrated, and the product is a low molecular weight decomposition product of a monomer unit, that is, a monomer or a dimer by enzymatic decomposition.

즉, 생분해는, 생명체(living things)인 세균, 곰팡이 또는 임의의 다른 미세한 유기체의 미생물에 의하여 분비 생성된 효소의 작용에 의해 물질의 무해한(innocuous) 생성물, 특히 물, 이산화탄소, 메탄 및 바이오매스로의, 분해, 붕해(disintegration), 부패(decay), 브레이크다운(breakdown) 또는 변형(transformation)이다. In other words, biodegradation is the innocuous product of substances, especially water, carbon dioxide, methane and biomass, by the action of enzymes secreted and produced by microorganisms of living things, bacteria, fungi or any other microscopic organism. of, disintegration, disintegration, decay, breakdown or transformation.

생분해는 호기성으로(산소 존재함) 또는 혐기성으로(산소 존재하지 않음) 발생할 수 있다. 따라서, 생분해 가능한 물질의 분해(Decomposition)는 생물학적인(biological) 단계와 비생물학적인(abiotic) 단계를 모두 포함할 수 있다.Biodegradation can occur aerobically (with oxygen) or anaerobically (without oxygen). Accordingly, the decomposition of the biodegradable material may include both a biological (biological) step and an abiotic (abiotic) step.

이하, 본 발명에 사용되는 재료의 특징을 살펴보면, 먼저 PLA 수지는 PLA(Polylactic acid 또는 Polylactide) 수지는 지방족 폴리에스테르의 일종으로서 옥수수나 감자 전분, 타이오카 뿌리, 목재 조각 또는 사탕수수 등의 바이오매스(Bio Mass)로부터 추출하는 젖산(Lactide) 단량체를 이용하여 합성한 열가소성 고분자 중합체 소재로서, 락트산(Lactic acid)을 단량체로 구성한 폴리머 전체를 지칭하며, PLA 수지는 이성질체 D-Lactide, L-Lactide 함량 및 배열(랜덤공중합, 블럭공중합)에 따라 열특성 및 물리적 특성 등이 달라질 수 있다. Hereinafter, looking at the characteristics of the material used in the present invention, PLA resin is polylactic acid or polylactide (PLA) resin as a kind of aliphatic polyester, and biomass such as corn or potato starch, taioka root, wood chips or sugar cane It is a thermoplastic polymer polymer material synthesized using lactic acid (Lactide) monomer extracted from (Bio Mass). It refers to the entire polymer composed of lactic acid as a monomer, and PLA resin is isomer D-Lactide, L-Lactide content And thermal properties and physical properties may vary depending on the arrangement (random copolymerization, block copolymerization).

이러한 PLA 수지는 자연 상태에서 미생물 등에 의해 환경에 유해한 요소를 남기지 않은 채 분해될 수 있는 생분해성을 갖추었을 뿐만 아니라, 다른 합성수지 원료와는 달리 원유가 아닌 바이오매스로부터 얻을 수 있는 것이라는 점에서 최근 그 용도가 널리 확대되고 있다.This PLA resin has biodegradability that can be decomposed without leaving harmful elements to the environment by microorganisms in its natural state, and unlike other synthetic resin raw materials, its use in recent years is that it can be obtained from biomass rather than crude oil. is being widely expanded.

티트리는 Leptospermum, Melaleuca, Kunzea 속에 해당하며, 세계적으로 Leptospermum 속(genus)에 약 86종, Melaleuca 속에 약 230 여종의 식물이 알려져 있는데, 원산지는 오스트레일리아로 뉴사우스웨일스주에서 자생한다. 높이 약 6m까지 늪지대에서 자라며 생명력이 강해서 줄기를 잘라내도 잘 자란다. 공기를 상쾌하게 정화하는 역할을 하는 허브의 한 종류이다.Tea tree belongs to the genus Leptospermum, Melaleuca, and Kunzea, and about 86 species of plants in the genus Leptospermum and about 230 species of plants in the genus Melaleuca are known worldwide. It grows up to about 6m in height in a swampy area and has strong vitality, so it grows well even if the stem is cut. It is a type of herb that plays a role in refreshing and purifying the air.

티트리는 자극성이 강하기 때문에 원액을 아몬드, 아프리코트, 헤즐넛과 같은 캐리어 오일에 2%를 희석하여 사용하며, 항 박테리아, 항바이러스 항진균 효과와 더불어 가장 강력한 면역 자극제, 백혈구를 활성화시켜 체내에 침입한 유기체에 대한 방어선을 구축하고 병에 걸려있는 기간을 단축하고, 호흡계 및 비뇨기계에 항박테리아 작용으로 호흡기계 및 비뇨기계 감염에 사용되는 물질이다.Because tea tree has strong stimulatory properties, the undiluted solution is diluted 2% in carrier oils such as almonds, apricots, and hazelnuts. It is a substance used for respiratory and urinary system infections by building defense lines against the disease, shortening the period of illness, and antibacterial action on the respiratory and urinary systems.

티트리 오일이 햇빛에 노출되면, 미량의 성분인 파라시멘이 3%에서 305d로 급격히 늘어나며, 항 미생물효과가 있는 terpinene-4-ol이 산화되어 트리하이드톡시멘테인으로 변화된다. When tea tree oil is exposed to sunlight, paracymene, a trace component, increases rapidly from 3% to 305d, and terpinene-4-ol, which has an antimicrobial effect, is oxidized and changed to trihydrotoxymentane.

황토는 한반도를 비롯한 중국의 화북지방 황하 연안 등 주로 동북아에 집중적으로 분포되어 있으며, 주로 석영을 함유하면서 그 밖에 휘석 각섬석 등을 함유하는 황갈색 석회질로서, 실리카(SiO2) 60 내지 65 중량%, 철분 5 내지 6 중량%, 알루미나(Al2O3) 10 내지 13 중량%, 마그네슘(Mg)과 나트륨(Na) 각 2 중량% 내외, 칼리 1.5 중량%, 석회 8 중량% 내외의 화학적 조성을 가지며, 분해력, 자정력, 흡수력 등이 뛰어나며 인체에 유익한 약성을 갖는 것으로 알려져 왔다.Loess is mainly distributed in Northeast Asia such as the Yellow River coast of North China, including the Korean Peninsula, and is a yellowish-brown limestone containing mainly quartz and other pyroxene amphibole, silica (SiO 2 ) 60 to 65 wt%, iron 5 to 6 wt%, alumina (Al 2 O 3 ) 10 to 13 wt%, magnesium (Mg) and sodium (Na) each about 2 wt%, potassium 1.5 wt%, lime 8 wt% , self-cleaning power, absorption power, etc. are excellent, and has been known to have beneficial medicinal properties to the human body.

또한, 황토는 물질을 활성화시키는데 가장 효력 있는 생명광선이라고 불리는 인체친화성 원적외선을 대량흡수하고 방사하는데, 황토의 가장 근본적인 효능은 이 원적외선이라고 할 수 있다. 황토는 표면이 넓은 벌집 구조로 수많은 공간이 복층 구조를 이루고 있다. 이 스폰지 같은 구멍 안에 태양광선 중 원적외선이 다량으로 흡수, 저장, 방사되어 다른 물체의 분자활동을 자극한다. 따라서 유기물과도 반응하며, 황토가 피부의 지방 등의 유기물을 포함한 노폐물을 흡수해 황토-유기물 복합체를 만들어 배출함으로서 혈액 순환을 촉진하여 건강을 증진시킨다. 그리고 황토는 음이온을 방출하는데, 이 음이온은 각종 오염으로부터 생활주변에 방출된 양이온을 흡착, 중화하여 생활환경을 쾌적하게 하며, 항균, 탈취, 방습 작용 등을 하여 인체에 매우 유익한 영향을 준다. 황토는 일반적으로 물을 함유하고 있지만 습도의 변화에 따라 황토가 가지고 있는 물 분자를 방출 또는 흡수하기도 한다.In addition, loess absorbs and radiates a large amount of human-friendly far-infrared rays, which are called life rays, which are the most effective in activating substances, and the most fundamental effect of loess is this far-infrared rays. Loess is a honeycomb structure with a wide surface, and numerous spaces form a double-layered structure. In this sponge-like hole, a large amount of far-infrared rays among the sun's rays are absorbed, stored, and radiated to stimulate the molecular activity of other objects. Therefore, it also reacts with organic matter, and ocher absorbs wastes including organic matter such as fat from the skin and creates and discharges ocher-organic complex, which promotes blood circulation and improves health. And loess emits negative ions, which adsorb and neutralize cations emitted from various types of pollution to make the living environment comfortable, and have a very beneficial effect on the human body by antibacterial, deodorizing, and moisture-proofing actions. Although loess generally contains water, it may release or absorb water molecules contained in loess according to changes in humidity.

상기 황토 성분에 포함되는 포르말린은 황토속에 있는 유해한 미생물을 사멸시켜 살균, 항균성을 발현시키며 황토의 유익한 성질이 탁월하게 발휘되도록 한다.Formalin included in the loess component kills harmful microorganisms in loess to express sterilization and antibacterial properties, and enables the beneficial properties of loess to be excellently exhibited.

또한, 맥반석은 화성암류 중 화강섬록반암에 속하며, 석영과 장성이 촘촘하게 썩여 있는데, 그 성질이 달고, 따뜻하며, 독이 없어서, 예전에는 환약을 정제하는 여과제, 등에 부스럼 또는 종기 등 피부질병을 치료하는 소염제로 사용되었고, 열을 가하면 원적외선을 방출하는 것으로 알려져있다.In addition, elvan stone belongs to granite diorite porphyry among igneous rocks, and it is densely rotted with quartz and intestinal wall, and its properties are sweet, warm, and non-toxic. It has been used as an anti-inflammatory agent and is known to emit far-infrared rays when heated.

맥반석은 무수규산(SiO2) 73,6%, 산화알미늄(AL2O3) 15,3%, 산화나트륨(NA2O) 3.44%, 산화마그네슘(MgO) 0.31%, 산화티타늄(TiO2) 0.17%, 산화제2철(Fe2O3) 1.71%, 산화칼륨(K2O) 4.43%, 산화몰리브텐(MnO) 0.05%의 성분을 이루어져, 1㎤당 3만 ~ 15만개의 다층 다공질로 구성되고, 비 표면적이 넓어 오염물질, 중금속 등을 흡착, 분해하는 작용을 하며, 인체에 활력을 주는 40여종 이상의 미네랄이 용출되어 신진대사와 피부건강관리에 효과가 있으며, 산성이나 강한 알칼리성 물을 약알칼리성(pH7.2 ~ 7.4)으로 조절하며, 수질을 활성화시켜 정수작용을 하고, 원적외선 방사에 의한 공명, 공진, 흡수작용 등으로 식품의 선도유지, 맛의 증가, 혈액순환 및 신진대사 촉진 등에 효과가 있다.Elvan is anhydrous silicic acid (SiO 2 ) 73,6%, aluminum oxide (AL 2 O 3 ) 15,3%, sodium oxide (NA 2 O) 3.44%, magnesium oxide (MgO) 0.31%, titanium oxide (TiO 2 ) 0.17%, ferric oxide (Fe 2 O 3 ) 1.71%, potassium oxide (K 2 O) 4.43%, and molybdenum oxide (MnO) 0.05% It has a wide specific surface area, so it absorbs and decomposes pollutants and heavy metals, and more than 40 minerals that give vitality to the human body are eluted, which is effective for metabolism and skin health management. Acidic or strong alkaline water is slightly alkaline (pH7.2 ~ 7.4), purifying water by activating water quality, maintaining freshness of food, increasing taste, promoting blood circulation and metabolism by resonance, resonance, and absorption by far-infrared radiation etc. is effective.

또한, 맥반석은 중금속 이온과 강력한 이온 교환능력이 있어서 유해금속 제제로 사용되어서 폐수처리공장 등에 사용되어 강한 탈취효과를 가지고 있으며 이를 응용하여 화장품 원료, 피부질환 등에 사용되며, 수질에서 지속적으로 산소를 공급하는 기능을 통해 양어장, 어항 등에 사용되고 있으며 대장균 등의 세균을 제거하여 산소량을 증가시킨다.In addition, elvan stone has a strong ion exchange ability with heavy metal ions, so it is used as a hazardous metal preparation and used in wastewater treatment plants, and has a strong deodorizing effect. It is used in fish farms and fish tanks through its function to increase oxygen content by removing bacteria such as E. coli.

따라서, 본 발명에 사용되는 맥반석을 1000 ~ 1400℃로 12시간 이상 소결하여 300 mesh 이상으로 분쇄한 맥반석 분말을 마스크 필터 제조에 사용하고, 이를 위해 맥반석 분말 1∼10% 가량 혼합기에서 혼합하여 사용한다.Therefore, the elvan stone used in the present invention is sintered at 1000 to 1400° C. for 12 hours or more and pulverized to 300 mesh or more is used for manufacturing a mask filter, and for this purpose, 1 to 10% of the elvan stone powder is mixed in a mixer and used. .

본 발명에 따른 생분해성 마스크는 티트리 추출물과 PBS 및 PLA 수지가 함유된 생분해성 섬유와 혼합하여 일체의 생분해성 마스크 면으로 형성할 수 있고, 티트리 미세분말 상의 조성물을 마스크 패드 또는 필터로 구성으로 이루어질 수 있는데, 이는 마스크 내피에 삽입되어 사용되는 마스크 패드 또는 필터를 구성하기 위해 티트리 분말, 황토 분말 및 맥반석을 혼합 가공하여 물과 배합하여 겔 타입으로 성형하여 마스크 내부의 필터용으로 적용할 수 있다.The biodegradable mask according to the present invention can be formed into a single biodegradable mask surface by mixing the tea tree extract and biodegradable fibers containing PBS and PLA resin, and the composition on the tea tree fine powder is composed of a mask pad or filter It can be made of, which is mixed and processed with tea tree powder, ocher powder and elvan stone to form a mask pad or filter that is inserted into the endothelium of the mask and mixed with water to form a gel type to be applied as a filter inside the mask. can

따라서, 티트리 분말, 황토 분말 및 맥반석을 혼합 가공하여 물과 배합하여 마스크 패드 또는 필터의 형태로 구비될 때 티트리, 황토 및 맥반석 분말을 물과 혼합물을 미강, 찹쌀 등의 곡물가루에 물을 혼합하여 천연 접착성 액체를 형성, 혼합하여 패드 또는 필터 구성을 위해 함침되도록 티트리, 황토 및 맥반석 조성물을 가열 중탕시킨 후 생성된 고상의 조성물을 감압 농축을 통해 겔 상태로 조성하여 겔 상태의 조성물을 마스크에 도포를 통해 건조 고착시키거나, 마스크 필터로 생성하여 마스크 내부에 삽입하여 착탈이 가능하도록 이루어질 수도 있다. Therefore, when tea tree powder, loess powder and elvan stone are mixed and processed with water and provided in the form of a mask pad or filter, a mixture of tea tree, ocher and elvan stone powder with water is added to grain flour such as rice bran and glutinous rice. After mixing the tea tree, loess and elvan compositions to form and mixing a natural adhesive liquid to be impregnated for pad or filter composition, the resulting solid composition is concentrated under reduced pressure to form a gel composition in a gel state It may be made to be fixed by drying through application to the mask, or may be created as a mask filter and inserted into the mask so that it can be detached.

한편, 필터 제조시 사용되는 천연 접착성 액체 조성물은 미강, 찹쌀 및 물을 혼합하여 95℃로 일정시간 가열하여 냉각시켜 천연 접착제를 준비하는데, 이때 전체 중량비를 고려하여 미강 20 ~ 40 중량%, 찹쌀 20 ~ 40 중량% 및 물 30 ~ 50 중량%을 혼합하여 95℃로 2 ~ 4시간 가열하여 냉각시키면 미강과 찹쌀 성분을 통해 천연의 접착제가 형성된다.On the other hand, the natural adhesive liquid composition used in the manufacture of the filter is prepared by mixing rice bran, glutinous rice and water, heating it to 95° C. for a certain period of time and cooling it to prepare a natural adhesive. When 20 to 40% by weight and 30 to 50% by weight of water are mixed and heated at 95°C for 2 to 4 hours to cool, a natural adhesive is formed through the rice bran and glutinous rice ingredients.

이후, 티트리 분말, 황토 및 맥반석과 혼합하여 교반한 혼합물에 미강, 찹쌀 및 물이 혼합된 접착제를 혼합하여 겔 타입의 필터를 제조하는데, 이때 분말 형태의 티트리, 황토, 맥반석의 혼합물은 미강, 찹쌀 및 물이 혼합된 접착제와 교반하면, 분말과 일정 크기를 갖는 알갱이가 접착성분으로 활성화된다.Thereafter, a gel-type filter is prepared by mixing an adhesive mixed with rice bran, glutinous rice and water in a mixture stirred by mixing with tea tree powder, loess, and elvan stone, in which case the mixture of tea tree, loess, and elvan in powder form is rice bran , Glutinous rice and water are mixed with the adhesive and stirred, the powder and grains having a certain size are activated as an adhesive component.

또한, 본 발명의 일 실시예로서 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물을 성형하여 구비된 생분해성 섬유를 일체로 생분해성 마스크를 제작할 수 있는데, PBS 및 PLA 수지가 함유된 생분해성 섬유와 혼합된 티트리 추출물은 티트리 잎을 세척 및 건조한 후 증류수로 80℃에서 3시간 추출하고 여과하여 여과액을 모으고, 남은 잔사는 다시 증류수를 첨가하여 80℃에서 3시간 더 추출하고 여과한다. 상기 여과액을 합치고, 감압 농축한 뒤 동결건조하여 티트리 추출물을 얻는다.In addition, as an embodiment of the present invention, it is possible to manufacture a biodegradable mask integrally with the biodegradable fibers provided by molding the biodegradable fibers containing PBS and PLA resins and the tea tree extract, and biodegradation containing PBS and PLA resins After washing and drying the tea tree leaves, the tea tree extract mixed with sex fiber is extracted with distilled water at 80°C for 3 hours, filtered to collect the filtrate, and the remaining residue is extracted again at 80°C for 3 hours by adding distilled water and filtered. do. The filtrates are combined, concentrated under reduced pressure, and freeze-dried to obtain a tea tree extract.

보다 세부적으로 티트리 추출물은 티트리 잎을 세척 및 건조하여 물, C1 내지 C4의 저급 알코올 또는 이들의 혼합용매로 추출하여 얻을 수 있으며, 상기 C1 내지 C4의 저급 알코올로는 메탄올, 에탄올, 프로판올, 이소프로판올, 부탄올 등을 이용할 수 있다. 또한, 상기 티트리 추출물은 유기 용매로 재분획한 분획물일 수 있으며, 상기 유기 용매로는 아세톤, n-헥산, 클로로포름 및 에틸아세테이트를 이용할 수 있다. In more detail, the tea tree extract can be obtained by washing and drying tea tree leaves and extracting with water, C1 to C4 lower alcohol or a mixed solvent thereof, and the C1 to C4 lower alcohol includes methanol, ethanol, propanol, Isopropanol, butanol, etc. can be used. In addition, the tea tree extract may be a fraction re-fractionated with an organic solvent, and acetone, n-hexane, chloroform and ethyl acetate may be used as the organic solvent.

상기에 의해 추출된 티트리 추출물을 PBS 및 PLA 수지가 함유된 생분해성 섬유에 도포후 건조하여 마스크 형태의 일정크기로 재단하여 일체형 마스크를 제조할 수 있고, PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물을 혼합하여 생분해성 재질의 생분해성 섬유를 직조하여 마스크 형태로 제조할 수 있는데, 이를 통해 티트리의 자연분해 성분과 PBS 및 PLA 수지가 함유된 생분해성 섬유의 생분해 성분을 통해 구비된 마스크를 사용 후 폐기시 분해되어 자연소거되는 것이다.The tea tree extract extracted by the above is applied to biodegradable fibers containing PBS and PLA resins, dried and cut to a certain size in the shape of a mask to manufacture an integrated mask, and biodegradable fibers containing PBS and PLA resins It can be manufactured in the form of a mask by weaving biodegradable fibers of biodegradable material by mixing tea tree extract and tea tree extract. When discarded after use, the mask is decomposed and removed naturally.

첨부된 도 1은 본 발명의 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 제조절차를 도시한 흐름도로서, 보다 세부적으로 생분해성 섬유는 PBS 수지 배치제조 단계, 압출 단계, 연신 단계, 섬유 결정화 단계, 크림핑 단계, 열고정 단계, 섬유 형성단계 및 일체형 마스크 제작단계로 진행될 수 있다.1 is a flowchart showing the biodegradable mask manufacturing procedure containing the biodegradable fiber and tea tree extract containing the PBS and PLA resin of the present invention, in more detail, the biodegradable fiber is the PBS resin batch manufacturing step, extrusion Step, stretching step, fiber crystallization step, crimping step, heat setting step, fiber formation step, and may proceed to the integral mask manufacturing step.

먼저, PBS계 수지와 다공성의 파라셀 분말의 무기계 충진제를 혼합한 혼합물을 용융온도 114℃ 이상, 열분해 온도인 255℃ 미만의 온도로 하고 압출기의 온도는 150 ~ 180℃ 범위로 압출하고 티트리 추출물을 혼합하여 배치를 제조한다.(S100 단계)First, a mixture of PBS-based resin and inorganic filler of porous Paracel powder is extruded at a melting temperature of 114°C or higher and a thermal decomposition temperature of less than 255°C, and the temperature of the extruder is in the range of 150 to 180°C, and tea tree extract to prepare a batch by mixing. (Step S100)

PLA 수지 88 ~ 95 중량%과 배치 5 ~ 12 중량%을 혼합한 혼합물을 상기 PLA 수지의 용융온도 151℃ 이상으로 하고 255℃ 미만의 온도에서 압출하여 생분해성 섬유 재료를 제조후 건조한다.(S200 단계)A mixture of 88 to 95% by weight of PLA resin and 5 to 12% by weight of a batch is extruded at a melting temperature of 151°C or higher of the PLA resin and lower than 255°C to produce a biodegradable fiber material and then dried. (S200 step)

상기 건조된 생분해성 섬유 재료를 압출 방사하여 미연신 원사를 연신한다.(S300 단계)The undrawn yarn is drawn by extrusion spinning the dried biodegradable fiber material. (Step S300)

상기 압출 방사된 미연신 원사를 연신 단계를 거친 후, 연신된 원사를 90 ~ 100℃의 온도 범위로 유지하여 섬유 결정화가 이루어지도록 한다.(S400 단계)After the extrusion spun undrawn yarn is subjected to a drawing step, the drawn yarn is maintained at a temperature range of 90 to 100° C. to achieve fiber crystallization. (Step S400)

결정화된 섬유에 필라멘트 권축을 위해 크래핑 절차를 진행하고(S500 단계) 크래핑 단계를 통해 권축된 필라멘트에 친수성 방사유제 에멀젼이 함유된 액상수지를 표면에 부착시키고 열 고정한다.(S600 단계)The crystallized fiber is subjected to a crimping procedure to crimp the filament (step S500), and a liquid resin containing a hydrophilic spinning emulsion is attached to the surface of the crimped filament through the crimping step and heat fixed. (step S600)

이후, 열 고정단계에 의해 구비된 섬유를 소정의 길이만큼 절단하여 마스크를 제작한다.(S700 단계)Thereafter, the fiber provided by the heat setting step is cut to a predetermined length to manufacture a mask. (Step S700)

한편, 상기 PBS계 수지는 PBS(Polybutylene Succinate), PBSA(Polybutylene Succinate-co-adipate) 또는 PBSF(Polybutylene succinate fumaric)를 포함하는 그룹에서 선택된 적어도 하나이거나 이들의 혼합물로 구성되고, 상기 생분해성 수지는 폴리락트산(PLA, 이하 PLA라 칭함)수지 45 내지 90 중량%와 PBS계 수지 10 내지 55 중량%의 함량으로 포함되는 것이 바람직하다.On the other hand, the PBS-based resin is at least one selected from the group comprising PBS (Polybutylene Succinate), PBSA (Polybutylene Succinate-co-adipate), or PBSF (Polybutylene succinate fumaric) or a mixture thereof, and the biodegradable resin is It is preferable to contain 45 to 90% by weight of polylactic acid (PLA, hereinafter referred to as PLA) resin and 10 to 55% by weight of PBS-based resin.

PLA 수지는 바이오매스를 발효하여 얻는 젖산(Lactide) 단량체를 중합하여 형성하는데, 이 중합체 수지 소재는 매우 취성이 강하여 PLA 수지만을 재료로 하여 섬유를 만드는 경우, 그러한 섬유는 쉽게 끊어질 수 있다. PLA resin is formed by polymerizing lactic acid (Lactide) monomer obtained by fermenting biomass, and this polymer resin material is very brittle.

본 발명에서는 이러한 문제점을 해결하기 위하여 PBS 수지, PBAT 수지, PCL 수지 중에서 선택된 하나 이상의 수지 재료와 PLA 수지를 혼합한 재료를 사용하는데, PBA(PolyButylene Succinate), PBAT(Polybutyrate)와 PCL(PolyCaproLactione)는 모두 폴리에스터계의 열가소성 중합체로서 생분해성을 가지며, PLA와 마찬가지로 토양 중의 미생물 등에 의해 이산화탄소와 물로 분해되는 생분해성을 갖는 것이다.In the present invention, in order to solve this problem, one or more resin materials selected from PBS resin, PBAT resin, and PCL resin and a material mixed with PLA resin are used. PBA (PolyButylene Succinate), PBAT (Polybutyrate) and PCL (PolyCaproLactione) are All of them are polyester-based thermoplastic polymers and have biodegradability, and like PLA, they are biodegradable by being decomposed into carbon dioxide and water by microorganisms in the soil.

본 발명은 PLA를 주성분으로 섬유를 제조하는데 PLA 수지가 갖는 고유의 광택성을 없애기 위해 광흡수 성질을 갖는 첨가제로서 다공성을 갖는 무기계 충진제를 사용한다. 그러한 다공성의 무기계 충진제를 사용하면, 섬유에 조사된 광이 섬유에 분산되어 배치되는 무기계 충진제의 입자에 형성되어 있는 구멍에 의해 분산 및 흡수됨으로써 섬유의 광반사율이 감소하여 PLA를 주원료로 하는 섬유로부터 광택성을 제거할 수 있다.The present invention uses an inorganic filler having porosity as an additive having light absorption properties in order to remove the inherent glossiness of PLA resin in manufacturing a fiber with PLA as a main component. When such a porous inorganic filler is used, the light irradiated to the fiber is dispersed and absorbed by the holes formed in the particles of the inorganic filler that are dispersed and disposed in the fiber, so that the light reflectance of the fiber is reduced, and thus the light reflectance of the fiber is reduced. The gloss can be removed.

더욱이, 이러한 무기계 충진제는 이후의 제조 단계에서 PLA 수지의 결정화를 촉진하는 결정화핵으로서의 역할을 한다. PLA 수지의 결정화는 수지의 인장 강도를 향상시켜주며 방적 과정에서 섬유가 단사되지 않도록 해준다.Moreover, these inorganic fillers serve as crystallization nuclei that promote the crystallization of PLA resin in the subsequent manufacturing step. The crystallization of PLA resin improves the tensile strength of the resin and prevents the fibers from being singled out during the spinning process.

특히 PLA 수지는 투명 또는 반투명한 고유의 색상을 가지지만, 이러한 결정화한 PLA 수지를 주원료로 한 섬유는 별도의 염색 과정 없이도 백색 또는 미백색을 띠게 된다.In particular, the PLA resin has a transparent or translucent color, but the fibers using the crystallized PLA resin as a main raw material are white or off-white without a separate dyeing process.

그러한 다공성의 무기계 충진제로서 파라셀을 사용하며, 파라셀은 산성 또는 중성을 띄는데, 본 발명에 따른 섬유의 주원료인 PLA 수지는 Ph 6 정도의 약산성을 띄는데 충전제로서 알카리성을 가진 재료를 사용하는 것은 단사의 원인이 되므로, 산성 또는 중성을 띄는 파라셀 분말을 충진제로서 첨가하게 된다.Paracel is used as such a porous inorganic filler, and Paracel is acidic or neutral. Since it causes single yarn, acidic or neutral Paracel powder is added as a filler.

상기 PBS계 수지는 PBS (Polybutylene Succinate), PBSA (Polybutylene Succinate-co-adipate) 또는 PBSF(Polybutylene succinate fumaric)을 단독 또는 2이상 혼합 용융하는 것이 바람직하다.The PBS-based resin is preferably PBS (Polybutylene Succinate), PBSA (Polybutylene Succinate-co-adipate), or PBSF (Polybutylene succinate fumaric) alone or by mixing two or more.

상기 폴리머를 연신한 뒤 연신된 필라멘트에 권축을 부여하는 크림핑 단계를 거친 후, 방사유제를 섬유 표면에 부착하는데 권축이 부여된 필라멘트에 기능성 방사유제가 함유된 액상수지를 분사하여 부착시킨다.After stretching the polymer, a crimping step of applying crimping to the stretched filament is performed, and then, a liquid resin containing a functional spinning emulsion is sprayed to attach the spinning emulsion to the fiber surface.

이때, 사용되는 상기 방사유제의 양은 전체 섬유 100 중량%에 대하여 0.3 내지 0.5 중량%가 포함되도록 방사유제를 섬유표면에 부착시키는 것이 바람직하다.In this case, it is preferable to attach the spinning emulsion to the fiber surface so that the amount of the spinning emulsion used is 0.3 to 0.5 wt% based on 100 wt% of the total fiber.

상기 방사유제 에멀젼이 함유된 액상수지는 생분해성 수지가 고화될 때 마찰열을 완화시키는 대전방지 역할을 하며, 상기에서 제조된 생분해 섬유 100을 기준으로 0.3 내지 1 중량%가 포함될 수 있다.The liquid resin containing the spinning emulsion emulsion serves as an antistatic role to relieve frictional heat when the biodegradable resin is solidified, and may be included in an amount of 0.3 to 1% by weight based on the biodegradable fiber 100 prepared above.

상기 절차에 의해 구비된 마스크는 첨부된 도 2 내지 도 3에 도시된 바와 같이 생분해 성분의 티트리 추출물과 PBS 및 PLA 수지가 함유된 생분해성 섬유의 생분해성인 특징을 갖는 마스크가 제작되고, 이를 통해 환경오염 방지 및 인체에 무해한 성분으로 구성된 장점이 있다.The mask provided by the above procedure is a mask with biodegradable characteristics of biodegradable fibers containing tea tree extract and PBS and PLA resins of biodegradable components, as shown in the accompanying FIGS. 2 to 3, through which It has the advantage of preventing environmental pollution and being composed of ingredients that are harmless to the human body.

도 4는 본 발명의 실시예에 따른 티트리, 황토 및 맥반석이 함유된 마스크 필터의 제조절차를 도시한 흐름도로서, 첨부된 도 4를 참조하여 본 발명에 따른 티트리, 황토 및 맥반석을 이용하여 마스크에 적용되는 필터의 생성 절차를 살펴보면 다음과 같다.4 is a flowchart illustrating a manufacturing procedure of a mask filter containing tea tree, loess and elvan according to an embodiment of the present invention. Referring to FIG. 4, using tea tree, loess and elvan stone according to the present invention The procedure for creating a filter applied to a mask is as follows.

먼저, 티트리를 세척 후 건조하여 300 mesh 이상으로 잘게 썰어서 분쇄하고(S10 단계참조), 맥반석을 1000 ~ 1400℃로 12시간 이상 소결하여 300 mesh 이상으로 분쇄한 맥반석 분말을 생성하고(S20 단계참조) 60 ~ 70℃ 가열된 더운물에 티트리 분말, 황토 분말, 맥반석 분말를 넣고 반죽절차를 진행한다.(S30 단계참조) First, wash the tea tree, dry it, cut it into pieces of 300 mesh or more and pulverize it (see step S10), and sinter the elvan stone at 1000 ~ 1400 ° C for more than 12 hours to produce an elvan stone powder pulverized to 300 mesh or more (see step S20) ) Add tea tree powder, loess powder, and elvan stone powder to hot water heated to 60 ~ 70℃ and proceed with the kneading procedure. (Refer to step S30)

상기 S30 단계의 반죽 절차시 티트리, 황토, 맥반석 및 물의 비율은 티트리 12 ~ 20 중량%, 황토 13 ~ 21 중량%, 맥반석 3 ~ 10 중량% 및 물 64 ~ 70 중량%로 구성되며, 보다 세부적으로는 티트리 15.21 중량%, 황토 12.58 중량%, 맥반석 4.72 중량% 및 물 67.49 중량%으로 이루어지는 것이 바람직하다.The ratio of tea tree, loess, elvan stone and water during the kneading procedure of step S30 is 12 to 20% by weight of tea tree, 13 to 21% by weight of loess, 3 to 10% by weight of elvan and 64 to 70% by weight of water, and more Specifically, it is preferable to consist of 15.21 wt% of tea tree, 12.58 wt% of loess, 4.72 wt% of elvan and 67.49 wt% of water.

상기 S30 단계에서 반죽된 티트리, 황토 및 맥반석의 혼합물을 세라믹 용기에 옮겨 25 ~ 30℃ 온도에서 40 ~ 50일 동안 숙성시켜 숙성된 조성물을 건조장으로 이동하여 40 ~ 50℃의 온도를 유지하여 빠른 건조 후 진공 포장한다.(S40 단계참조) The mixture of tea tree, loess, and elvan kneaded in step S30 is transferred to a ceramic container and aged for 40 to 50 days at a temperature of 25 to 30 ° C. After drying, vacuum packaging. (Refer to step S40)

진공 포장된 조성물의 원료를 미강, 찹쌀가루 등의 곡물가루를 이용하여 형성된 무독성 액체 접착물질과 혼합한다.(S50 단계참조)The raw material of the vacuum-packed composition is mixed with a non-toxic liquid adhesive material formed using grain flour such as rice bran and glutinous rice flour. (See step S50)

상기 숙성 및 진공 포장된 티트리, 황토 및 맥반석의 혼합물과 미강, 찹쌀가루의 천연 접착물과 혼합하여 구비되는 마스크 필터는 마스크 외부와 내부 사이에 일체로 적층되거나, 필터 자체를 탈부착이 가능하도록 마스크 후면의 삽입부를 통해 삽입되어 안착될 수 있다.The mask filter provided by mixing the aged and vacuum-packed mixture of tea tree, loess, and elvan stone with natural adhesive of rice bran and glutinous rice flour is integrally laminated between the outside and the inside of the mask, or the filter itself is detachable. It can be inserted and seated through the insertion part on the rear side.

S50 단계 후, 진공 포장된 조성물과 무독성 액체의 혼합물을 두루마리 형태로 생산하여 마스크 크기에 따라 절개하여 마스크 내피에 부착시켜 티트리, 황토 및 맥반석 조성물이 함유된 마스크 필터를 생산한다.(S60 단계참조)After step S50, a mixture of vacuum-packaged composition and non-toxic liquid is produced in the form of a roll, cut according to the size of the mask, and attached to the endothelium of the mask to produce a mask filter containing tea tree, ocher and elvan composition (see step S60). )

한편, 상기 S60 단계에서 진공 포장된 티트리, 황토 및 맥반석이 함유된 조성물을 하기에 기술될 마스크 전면 및 내면 사이에 안착시켜 티트리, 황토, 맥반석이 함유된 조성물이 함유된 마스크를 일체로 생산할 수도 있다.On the other hand, the composition containing tea tree, loess, and elvan, vacuum-packed in step S60, is seated between the front and inner surfaces of the mask to be described below to produce a mask containing the composition containing tea tree, loess, and elvan in one piece. may be

상기의 공정에 의해 첨부된 도 5는 티트리, 황토 및 맥반석이 함유된 마스크 필터의 단면도를 나타내고, 도 6은 본 발명에 따른 티트리, 황토 및 맥반석 함유된 마스크 필터가 마스크 내부에 안착되어 일체로 형성된 상태를 도시한 사시도이며, 도 7은 도 6에 따른 티트리, 황토 및 맥반석이 함유된 마스크 필터가 마스크 내부에 안착된 마스크의 내부의 단면도를 도시한 것으로서, 도 5에 도시된 바와 같이 티트리, 황토 및 및 맥반석이 함유된 마스크 필터를 마스크와 일체로 마스크 전면 및 후면 사이에 삽입하여 마스크를 형성될 수 있다.FIG. 5 attached by the above process shows a cross-sectional view of a mask filter containing tea tree, loess, and elvan stone, and FIG. 6 is a mask filter containing tea tree, ocher and elvan stone according to the present invention. As shown in FIG. 5, it is a perspective view showing a state formed as A mask may be formed by inserting a mask filter containing tea tree, loess, and elvan stone between the front and rear surfaces of the mask integrally with the mask.

즉, PBS 및 PLA 수지가 함유된 섬유와 티트리 추출물이 함유된 생분해성 수지는 마스크 외부(200)와 착용자의 얼굴이 맞닿는 마스크 내부(300)로 마스크 형태로 구비하고, 마스크 외부(200) 및 내부(300) 사이에 티트리, 황토 및 맥반석이 접착성 성분과 함유되어 구비된 마스크 필터(F)를 적층하여 일체로 성형하여 티트리, 황토 및 맥반석 함유된 생분해성 마스크가 구비되는데, 마스크 외부(200)와 내부(300) 사이의 내피층(500)에 마스크 필터(F)가 일체로 형성되어 마스크로 구성된다.That is, the biodegradable resin containing the fibers and tea tree extract containing PBS and PLA resin is provided in the form of a mask as the outside of the mask 200 and the inside of the mask 300 where the wearer's face is in contact, and the outside of the mask 200 and A biodegradable mask containing tea tree, loess and elvan is provided by stacking and integrally molding a mask filter (F) provided with tea tree, loess, and elvan between the inside 300, and the outside of the mask The mask filter F is integrally formed on the inner skin layer 500 between the 200 and the inner 300 to constitute a mask.

또한, 끈 부(400)는 마스크 내부(300)의 일측에서 연결되어 착용자의 귀를 감싸는 고리형으로 형성되며 끈 부(400) 일측에는 길이를 조절할 수 있는 길이 조절부(420)가 구비된다.In addition, the string part 400 is connected from one side of the mask inner 300 to form a ring shape surrounding the wearer's ear, and a length adjustment part 420 capable of adjusting the length is provided on one side of the string part 400 .

또한, 본 발명의 다른 실시예로서 티트리, 황토 및 맥반석이 함유된 마스크 필터를 생분해성 폴리에스테르 수지의 마스크 전면 및 후면 사이 사이에 삽입하여 안착되는 필터 교체형으로 선택적으로 구비될 수 있는데, 첨부된 도 8은 본 발명의 다른 실시예에 따른 티트리, 황토 및 맥반석 함유된 조성물이 마스크 필터로 구비되어 형성된 생분해성 마스크의 상태를 도시한 사시도이고, 도 9는 도 8에 의해 티트리, 황토 및 맥반석 함유된 마스크 필터로 구비되어 형성된 생분해성 마스크의 전면을 도시한 사시도를 나타내고, 도 10은 본 발명에 따른 티트리, 황토 및 맥반석 함유된 마스크 필터로 구비되어 형성된 생분해성 마스크의 내면을 도시한 사시도이며, 도 11은 본 발명에 따른 티트리, 황토 및 맥반석 함유된 조성물이 마스크 필터로 마스크 내부에 삽입되어 안착된 상태를 보인 사시도이고, 도 12은 도 11에 따른 티트리, 황토 및 맥반석이 함유된 조성물이 마스크 필터로 내부에 안착되어 구성된 마스크의 단면도를 나타내는데, 티트리, 황토 및 맥반석이 함유된 마스크 필터(F)를 구비한 생분해성 마스크(100)는 크게 마스크 외부(200), 마스크 내부(300), 삽입부(330), 끈 부(400), 내피층(500)으로 구성되는데, 상기 마스크 외부(200)는 BS 및 PLA 수지가 함유된 생분해성 섬유 및 티트리 추출물로 구비된 생분해성 수지로 구성되어 햇빛에 강하고, 먼지 등의 유입이 차단될 수 있도록 정적한 밀도를 가지며, 신축성 소재로 구성되고, 용도에 따라 자외선의 흡수력을 차단할 수 있는 소재를 사용할 수도 있다.In addition, as another embodiment of the present invention, a mask filter containing tea tree, loess, and elvan stone may be optionally provided as a filter replacement type that is seated by inserting a mask filter between the front and rear surfaces of the biodegradable polyester resin mask. 8 is a perspective view showing the state of a biodegradable mask formed by providing a composition containing tea tree, ocher and elvan stone as a mask filter according to another embodiment of the present invention, and FIG. and a perspective view showing the front side of a biodegradable mask formed with a mask filter containing elvan stone, and FIG. 10 shows the inner surface of a biodegradable mask formed with a mask filter containing tea tree, loess and elvan stone according to the present invention 11 is a perspective view showing a state in which the composition containing tea tree, loess and elvan according to the present invention is inserted and seated inside the mask as a mask filter, and FIG. 12 is tea tree, loess and elvan stone according to FIG. A cross-sectional view of a mask in which the composition containing this composition is seated inside as a mask filter is shown. It is composed of an inner mask 300, an insertion portion 330, a string portion 400, and an inner skin layer 500, and the outer mask 200 is provided with biodegradable fibers and tea tree extract containing BS and PLA resins. It is made of a biodegradable resin that is strong in sunlight, has a static density to block the inflow of dust, and is composed of a stretchable material.

상기 마스크 내부(300)는 착용자의 얼굴이 맞닿는 곳으로 먼지 차단효과를 갖지고 생분해성 수지로 구성되고, 마스크 내부(300)의 중심에는 상기 마스크 필터(F)가 내피층(500)에 삽입하여 안착될 수 있도록 삽입부(330)가 구비되고, 상기 마스크 내부(300)의 좌우측에 상기 삽입부(330)를 통해 삽입된 마스크 필터(F)가 내피층(500) 좌우로 안착시 마스크 필터(F)를 길이, 위치를 조절할 수 있는 절개홈(350)이 구비된다. 즉, 상기 절개홈(350)은 삽입부(330)를 통해 삽입된 마스크 필터(F)가 마스크 내피층(500)으로 고르게 펴져 자리를 잡을 수 있도록 상기 절개홈(350)을 통해 마스크 필터(F)의 위치를 조절하도록 마스크 내부(300)의 삽입부(330)를 기준으로 좌우로 각각 1개씩 구성된다.The inside of the mask 300 is a place where the wearer's face abuts, has a dust blocking effect and is made of biodegradable resin, and the mask filter F is inserted into the inner skin layer 500 at the center of the inside of the mask 300. The insertion part 330 is provided so that it can be seated, and when the mask filter F inserted through the insertion part 330 on the left and right sides of the inside of the mask 300 is seated on the left and right sides of the inner skin layer 500, the mask filter ( F) is provided with an incision groove 350 that can adjust the length and position. That is, the incision groove 350 is formed through the incision groove 350 so that the mask filter F inserted through the insertion part 330 can be spread evenly into the mask endothelial layer 500 to be seated. ), one each on the left and right with respect to the insertion part 330 of the inside of the mask 300 to adjust the position.

따라서, 상기의 구성에 따라 티트리, 황토 및 백반석이 함유된 마스크 필터(F)가 구비된 생분해성 마스크는 황토, 티트리가 합성이 되면 향긋한 냄새와 더불어서 탈취, 항균 기능을 제공하며 외부 공기 및 먼지를 차단할 수 있다.Therefore, according to the above configuration, a biodegradable mask equipped with a mask filter (F) containing tea tree, loess and alum provides deodorizing and antibacterial functions along with a fragrant smell when ocher and tea tree are synthesized, and It can block out dust.

상기 본 발명의 내용은 도면에 도시된 일 실시 예를 참고로 설명되었으나 이는 예시적인 것에 불과하며, 본 기술 분야의 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시 예가 가능하다는 점을 이해할 것이다. 따라서 본 발명의 진정한 기술적 보호 범위는 첨부된 특허청구범위의 기술적 사상에 의해 정해져야 할 것이다.The content of the present invention has been described with reference to an embodiment shown in the drawings, but this is merely exemplary, and those of ordinary skill in the art will recognize that various modifications and equivalent other embodiments are possible therefrom. will understand Therefore, the true technical protection scope of the present invention should be determined by the technical spirit of the appended claims.

100 : 마스크
110 : 마스크 필터 200 : 마스크 외부
300 : 마스크 내부 330 : 삽입부
350 : 절개홈 370 : 고정부
400 : 끈 부 420 : 길이조절부
500 : 내피층 600 : 고정지지부100: mask
110: mask filter 200: outside the mask
300: inside the mask 330: insertion part
350: incision groove 370: fixing part
400: string part 420: length adjustment part
500: inner cortical layer 600: fixed support part

Claims (3)

PBS 수지와 다공성의 파라셀 분말의 무기계 충진제를 혼합한 혼합물을 용융온도 114℃ 이상, 열분해 온도인 255℃ 미만의 온도로 하고 압출기의 온도는 150 ~ 180℃ 범위로 압출한 후 티트리 추출물을 혼합하여 구비된 배치 5 ~ 12 중량%과 PLA 수지 88 ~ 95 중량% 혼합한 혼합물을 압출하여 생분해성 섬유 재료를 제조하고 건조한 후, 건조된 생분해성 섬유 재료를 압출 방사하여 미연신 원사를 연신단계를 통해 연신된 원사를 하여 90 ~ 100℃의 온도를 유지하여 섬유 결정화가 이루어지도록 하고, 결정화된 섬유에 필라멘트 권축을 위해 크래핑하여 권축된 필라멘트에 친수성 방사유제 에멀젼이 함유된 액상수지를 표면에 부착하고 열고정하여 구비된 생분해성 섬유를 소정의 길이로 절단하여 마스크 형태로 성형하여 마스크 외부(200) 및 내부(300) 사이에 티트리, 황토, 맥반석 및 물을 혼합하여 숙성, 건조된 혼합물에 미강, 찹쌀 및 물을 혼합하여 95℃로 2 ~ 4시간 가열하여 냉각시켜 구비된 액체 접착물질과 혼합하여 구비된 마스크 필터(F)를 적층하여 일체로 성형하여 마스크 외부(200)와 내부(300) 사이의 내피층(500)에 마스크 필터(F)가 안착되어 일체로 형성되는 것을 특징으로 하는 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크.
A mixture of PBS resin and inorganic filler of porous Paracel powder is extruded at a melting temperature of 114°C or higher and a thermal decomposition temperature of less than 255°C, and the temperature of the extruder is in the range of 150 to 180°C, and then the tea tree extract is mixed. A biodegradable fiber material is prepared by extruding a mixture of 5 to 12 wt% of the prepared batch and 88 to 95 wt% of PLA resin, dried, and then extruded and spun the dried biodegradable fiber material to draw an undrawn yarn The fiber is crystallized by maintaining the temperature of 90 ~ 100℃ with the yarn drawn through it, and the liquid resin containing the hydrophilic spinning emulsion is attached to the crimped filament by scraping the crystallized fiber to crimp the filament on the surface. After heat-setting, the provided biodegradable fiber is cut to a predetermined length and molded into a mask shape, and tea tree, loess, elvan and water are mixed between the outside 200 and inside 300 of the mask to ripen and dry the rice bran in the mixture. , mixed with glutinous rice and water, heated to 95° C. for 2 to 4 hours, cooled, mixed with the provided liquid adhesive material, stacked with the provided mask filter (F), and molded integrally to form the mask outside (200) and inside (300) A biodegradable mask containing biodegradable fibers and tea tree extract containing PBS and PLA resin, characterized in that the mask filter (F) is seated on the inner skin layer 500 between them and is integrally formed.
 PBS 수지와 다공성의 파라셀 분말의 무기계 충진제를 혼합한 혼합물을 용융온도 114℃ 이상, 열분해 온도인 255℃ 미만의 온도로 하고 압출기의 온도는 150 ~ 180℃ 범위로 압출한 후 티트리 추출물을 혼합하여 구비된 배치 5 ~ 12 중량%과 PLA 수지 88 ~ 95 중량% 혼합한 혼합물을 압출하여 생분해성 섬유 재료를 제조하고 건조한 후, 건조된 생분해성 섬유 재료를 압출방사하여 미연신 원사를 연신단계를 통해 연신된 원사를 하여 90 ~ 100℃의 온도를 유지하여 섬유 결정화가 이루어지도록 하고, 결정화된 섬유에 필라멘트 권축을 위해 크래핑하여 권축된 필라멘트에 친수성 방사유제 에멀젼이 함유된 액상수지를 표면에 부착하고 열고정하여 구비된 생분해성 섬유를 소정의 길이로 절단하여 마스크 형태로 성형하여 티트리, 황토, 맥반석 및 물을 혼합하여 숙성, 건조된 혼합물에 미강, 찹쌀 및 물을 혼합하여 95℃로 2 ~ 4시간 가열하여 냉각시켜 구비된 액체 접착물질과 혼합하여 구비된 마스크 필터(F)가 마스크 내부(300)의 중심에 절개홈(350)을 통해 좌우 절개되어 위치한 삽입부(330)을 통해 마스크 외부(200)와 마스크 내부(300) 사이의 내피층(500)을 통해 좌우로 삽입 안착되도록 구성된 것을 특징으로 하는 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크.
A mixture of PBS resin and inorganic filler of porous Paracel powder is extruded at a melting temperature of 114°C or higher and a thermal decomposition temperature of less than 255°C, and the temperature of the extruder is in the range of 150 to 180°C, and then the tea tree extract is mixed. A biodegradable fiber material is prepared by extruding a mixture of 5 to 12% by weight of the prepared batch and 88 to 95% by weight of PLA resin and dried, and then the dried biodegradable fiber material is extruded and spun to draw an undrawn yarn. The fiber is crystallized by maintaining the temperature of 90 ~ 100℃ with the yarn drawn through it, and the liquid resin containing the hydrophilic spinning emulsion is attached to the crimped filament by scraping the crystallized fiber to crimp the filament on the surface. After heat-setting, the provided biodegradable fiber is cut to a predetermined length and molded into a mask shape, aged by mixing tea tree, loess, elvan and water, and rice bran, glutinous rice and water are mixed in the dried mixture at 95 ° C. The mask filter (F) provided by mixing with the liquid adhesive material provided by heating and cooling for 4 hours is cut left and right through the incision groove 350 in the center of the mask inside 300 through the insertion part 330 located outside the mask A biodegradable mask containing biodegradable fibers and tea tree extract containing PBS and PLA resin, characterized in that it is configured to be inserted and seated left and right through the endothelial layer 500 between the 200 and the inside of the mask 300.
 PBS 수지와 다공성의 파라셀 분말의 무기계 충진제를 혼합한 혼합물을 용융온도 114℃ 이상, 열분해 온도인 255℃ 미만의 온도로 하고 압출기의 온도는 150 ~ 180℃ 범위로 압출하고 티트리 추출물을 혼합하여 배치를 제조하는 제 1 공정;
PLA 수지 88 ~ 95 중량%과 배치 5 ~ 12 중량%을 혼합한 혼합물을 PLA 수지의 용융온도 151℃ 이상으로 하고 255℃ 미만의 온도에서 압출하여 생분해성 섬유 재료를 제조한 후 건조하는 제 2 공정;
상기 건조된 생분해성 섬유 재료를 압출 방사하여 미연신 원사를 연신하는 제 3 공정;
상기 압출 방사된 미연신 원사를 연신 단계를 거친 후, 연신된 원사를 90 ~ 100℃의 온도 범위로 유지하여 섬유 결정화하는 제 4 공정;
결정화된 섬유에 필라멘트 권축을 위해 크래핑 절차를 진행하는 제 5 공정;
크래핑 단계를 통해 권축된 필라멘트에 친수성 방사유제 에멀젼이 함유된 액상수지를 표면에 부착시키고 열 고정하는 제 6 공정; 및
열 고정단계에 의해 구비된 섬유를 소정의 길이만큼 절단하여 마스크 형태로 성형하여 내피에 겔 타입의 마스크 필터를 안착하거나, 마스크 표면에 겔 상태의 조성물를 도포하여 마스크를 제작하는 제 7 공정;을 포함하여 구성되는 것을 특징으로 하는 PBS 및 PLA 수지가 함유된 생분해성 섬유와 티트리 추출물이 함유된 생분해성 마스크 제조방법.
A mixture of PBS resin and inorganic filler of porous Paracel powder is extruded at a melting temperature of 114°C or higher and a thermal decomposition temperature of less than 255°C, the temperature of the extruder is in the range of 150 to 180°C, and the tea tree extract is mixed. a first process of making a batch;
The second process of manufacturing a biodegradable fiber material by extruding a mixture of 88 to 95 wt% of PLA resin and 5 to 12 wt% of a batch at a melting temperature of 151°C or higher of PLA resin and lower than 255°C, followed by drying ;
a third step of stretching the undrawn yarn by extrusion spinning the dried biodegradable fiber material;
a fourth process of fiber crystallization by maintaining the stretched yarn in a temperature range of 90 to 100° C. after the extrusion spun undrawn yarn undergoes a drawing step;
a fifth step of performing a crimping procedure to crimp the crystallized fibers;
a sixth step of attaching a liquid resin containing a hydrophilic spinning emulsion to the crimped filaments through the scraping step to the surface and heat fixing; and
A seventh process of cutting the fiber provided by the heat setting step by a predetermined length and molding it into a mask shape to seat a gel-type mask filter on the endothelium, or applying a gel-like composition to the mask surface to make a mask; includes; A method for manufacturing a biodegradable mask containing biodegradable fibers and tea tree extract containing PBS and PLA resin, characterized in that it is composed of
KR1020200174338A 2020-12-14 2020-12-14 A biodegradable mask included tea-tree and biodegradable fiber contained PBS and PLA, AND Manufacturing method of the same KR20220084653A (en)