KR20220006377A - Towel printing method using a printing device including a surface treatment function - Google Patents

Towel printing method using a printing device including a surface treatment function Download PDF

Info

Publication number
KR20220006377A
KR20220006377A KR1020200084263A KR20200084263A KR20220006377A KR 20220006377 A KR20220006377 A KR 20220006377A KR 1020200084263 A KR1020200084263 A KR 1020200084263A KR 20200084263 A KR20200084263 A KR 20200084263A KR 20220006377 A KR20220006377 A KR 20220006377A
Authority
KR
South Korea
Prior art keywords
towel
unit
printing
measuring
surface treatment
Prior art date
Application number
KR1020200084263A
Other languages
Korean (ko)
Other versions
KR102460722B1 (en
Inventor
최인숙
김석호
주미경
정인주
Original Assignee
최인숙
삼육대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 최인숙, 삼육대학교산학협력단 filed Critical 최인숙
Priority to KR1020200084263A priority Critical patent/KR102460722B1/en
Publication of KR20220006377A publication Critical patent/KR20220006377A/en
Application granted granted Critical
Publication of KR102460722B1 publication Critical patent/KR102460722B1/en

Abstract

The present invention relates to a printing apparatus, comprising: a surface treatment unit for treating the surface of a towel which cannot be directly printed; a measuring unit for measuring surface characteristics of the towel treated in the surface treatment unit; and a printing unit for printing directly on the towel. An objective of the present invention is to provide the printing apparatus including a surface treatment function capable of high-resolution printing on the towel which cannot be directly printed.

Description

표면 처리 기능을 포함하는 프린팅 장치를 이용한 타월 인쇄 방법 {Towel printing method using a printing device including a surface treatment function}Towel printing method using a printing device including a surface treatment function

본 발명은 표면 처리 기능을 포함하는 프린팅 장치를 이용한 타월 인쇄 방법에 관한 것이다.The present invention relates to a towel printing method using a printing device including a surface treatment function.

본 명세서의 전반에서는 표면에 잉크가 흡수되지 않는 타월들이 많이 존재하지만, 설명의 편의를 위하여 이러한 타월 중에서 통상의 기술자에게 비교적 친숙한 타월 타월를 예를 들어 설명하도록 한다.In the first half of the present specification, there are many towels that do not absorb ink on the surface, but for convenience of explanation, a towel towel relatively familiar to those skilled in the art among these towels will be described as an example.

현재 타월 타월 상에 인쇄를 하는 방식으로 실크 스크린 인쇄 방식이 널리 사용되고 있다.Currently, a silk screen printing method is widely used as a method of printing on a towel.

이때, 사용되는 잉크는 타월용 고점도 옵셋 잉크로서, 200℃ 이상의 고온에서 타월 타월 상에 잉크를 부착하는 방식으로 인쇄가 이루어진다.In this case, the ink used is a high-viscosity offset ink for towels, and printing is performed by attaching the ink to the towel at a high temperature of 200° C. or higher.

즉, 종래의 타월 타월 인쇄는 일반적으로 종이에 인쇄하는 방식처럼 잉크가 종이에 흡수되며 인쇄되는 것이 아니라, 잉크가 타월 타월로 흡수되지 않고, 단지 타월 타월 상에 일정 두께로 부착되도록 하는 것에 불과하기 때문에, 부착된 잉크가 타월 타월로부터 박리되기 쉽고, 타월 타월의 특성상 신장과 축소가 반복적으로 이루어지는 경우, 잉크와 타월 타월의 박리가 더욱 심각해질 수 밖에 없는 문제점이 있다.That is, conventional towel towel printing is not printed with ink absorbed into the paper as in the method of printing on paper in general, the ink is not absorbed into the towel towel, just to be attached to a certain thickness on the towel towel. Therefore, there is a problem in that the attached ink is easy to peel from the towel, and when the towel is stretched and contracted repeatedly due to the nature of the towel, the peeling of the ink and the towel becomes more serious.

또한, 종래의 타월 타월 인쇄는 상술한 바와 같이 옵셋 잉크를 이용한 실크 스크린 인쇄를 통해, 색상별로 1도씩 인쇄되는 방식이기 때문에 그라데이션 등과 같이 도수가 복잡한 인쇄뿐만 아니라, 다양한 색상의 잉크를 이용한 고해상도의 표현이 불가능하다.In addition, as described above, conventional towel towel printing is a method of printing 1 degree per color through silk screen printing using offset ink as described above. This is impossible.

아울러, 종래에는 타월 타월 상에 부착성을 높이기 위해 고점도의 잉크를 사용하기 때문에, 타월 인쇄를 통해서는 고점도 잉크로 인한 유광(광택) 표면만이 가능한 단점이 있다.In addition, there is a disadvantage in that only a glossy (glossy) surface is possible due to the high viscosity ink through towel printing, since high viscosity ink is used to increase adhesion on the towel in the prior art.

나아가, 종래의 타월 타월 상에 실크 스크린 인쇄 방식을 이용하는 경우, 잉크를 타월 표면에 부착하기 위하여 인체에 유해한 프라이머 (접착제) 성분을 포함하는 것이 필수적이었기 때문에, 인쇄를 수행한 타월 타월 상에 인체에 유해한 프라이머 성분이 잔존하는 문제가 있었다.Furthermore, in the case of using the silk screen printing method on the conventional towel towel, it was essential to include a primer (adhesive) component harmful to the human body in order to attach the ink to the towel surface. There was a problem that harmful primer components remained.

본 발명은 직접 인쇄가 불가능한 타월에 고해상도 인쇄가 가능한 표면 처리 기능을 포함하는 프린팅 장치를 제공하는 것을 해결하고자 하는 과제로 한다.An object of the present invention is to provide a printing apparatus including a surface treatment function capable of high-resolution printing on a towel that cannot be directly printed.

또한, 본 발명은 종래의 타월 타월 상에 실크 스크린 인쇄 방식을 이용하는 경우, 잉크를 타월 표면에 부착하기 위하여 인체에 유해한 프라이머 (접착제) 성분을 포함하는 것이 필수적이었기 때문에, 인쇄를 수행한 타월 타월 상에 인체에 유해한 프라이머 성분이 잔존하는 문제를 방지하는 고해상도 인쇄가 가능한 표면 처리 기능을 포함하는 프린팅 장치를 제공하는 것을 해결하고자 하는 과제로 한다.In addition, in the present invention, when using a silk screen printing method on a conventional towel towel, it was essential to include a primer (adhesive) component harmful to the human body in order to attach the ink to the towel surface. An object of the present invention is to provide a printing device including a surface treatment function capable of high-resolution printing that prevents the residual primer component harmful to the human body.

상술한 과제를 해결하기 위하여, 본 발명은 직접 인쇄가 불가능한 타월의 표면을 플라즈마 처리하는 타월표면처리부, 상기 타월표면처리부에서 처리된 타월의 표면 특성을 측정하는 측정부, 상기 타월에 직접 인쇄를 하는 프린팅부 및 상기 인쇄된 타월에 열을 가하여 경화시키는 열경화부를 포함하는 것을 특징으로 하는 타월 프린팅 장치를 제공하는 것을 과제의 해결 수단으로 한다.In order to solve the above problems, the present invention is a towel surface treatment unit for plasma-treating the surface of a towel that cannot be directly printed, a measuring unit for measuring the surface characteristics of the towel treated in the towel surface treatment unit, and direct printing on the towel To provide a towel printing device comprising a printing unit and a thermosetting unit for curing by applying heat to the printed towel as a means of solving the problem.

또한, 상기 표면처리부는 상기 적어도 하나 이상의 전극을 포함하며, 상기 적어도 하나 이상의 전극은 상기 타월의 상부와 하부에 배치되는 다 전극 양면 플라즈마 장치인 것을 특징으로 하는 타월 프린팅 장치를 제공하는 것을 과제의 해결 수단으로 한다.In addition, the surface treatment unit comprises the at least one electrode, the at least one electrode is to provide a towel printing device, characterized in that the multi-electrode double-sided plasma device disposed on the top and bottom of the towel to solve the problem do it by means

또한, 상기 표면처리부에서 표면 처리된 타월의 컨택 앵글은 0°내지 50°인 것을 특징으로 하는 타월 프린팅 장치를 제공하는 것을 과제의 해결 수단으로 한다.In addition, the contact angle of the towel surface-treated in the surface treatment unit is to provide a towel printing device, characterized in that 0 ° to 50 ° as a means of solving the problem.

또한, 상기 표면처리부에서 표면 처리된 타월의 표면조도는 0.3a 내지 0.9a 인 것을 특징으로 하는 타월 프린팅 장치를 제공하는 것을 과제의 해결 수단으로 한다.In addition, the surface roughness of the towel surface-treated in the surface treatment unit is to provide a towel printing device, characterized in that 0.3a to 0.9a as a means of solving the problem.

또한, 상기 표면처리부에서 표면 처리된 타월에 다인 펜슬을 도포한 경우에 42dyne/cm 인 것을 특징으로 하는 타월 프린팅 장치를 제공하는 것을 과제의 해결 수단으로 한다.In addition, it is to provide a towel printing device, characterized in that the 42 dyne / cm in the case of applying a dyne pencil to the towel surface-treated in the surface treatment unit as a means of solving the problem.

또한, 상기 프린팅부에 인쇄하기 전에 타월를 예열하는 예열부 및In addition, a preheating unit for preheating the towel before printing on the printing unit and

상기 프린팅부에 의해 인쇄된 이후 타월를 건조하는 건조부를 포함하는 것을 특징으로 하는 타월 프린팅 장치를 제공하는 것을 과제의 해결 수단으로 한다.It is to provide a towel printing device comprising a drying unit for drying the towel after being printed by the printing unit as a means of solving the problem.

또한, 상기 타월의 표면의 컨택앵글을 측정하는 컨택앵글 측정부, 상기 타월의 조도를 측정하는 조도 측정부 및 상기 타월의 표면장력을 측정하는 표면장력 측정부를 포함하는 것을 특징으로 하는 타월 프린팅 장치를 제공하는 것을 과제의 해결 수단으로 한다.In addition, a towel printing device comprising a contact angle measuring unit for measuring the contact angle of the surface of the towel, a roughness measuring unit for measuring the roughness of the towel, and a surface tension measuring unit for measuring the surface tension of the towel Provide as a means of solving the problem.

또한, 직접 인쇄가 불가능한 타월의 표면을 플라즈마 처리하는 단계, 상기 타월표면처리부에서 처리된 타월의 표면 특성을 측정하는 단계, 상기 타월에 직접 인쇄를 하는 프린팅하는 단계, 상기 인쇄된 타월에 열을 가하여 경화시키는 단계; 를 포함하고, 상기 타월의 표면 특성을 측정하는 단계는, 상기 타월의 표면의 컨택앵글을 측정하는 단계, 상기 타월의 조도를 측정하는 단계 및 상기 타월의 표면장력을 측정하는 단계를 포함하고, 상기 타월의 컨택앵글, 조도 및 표면장력 중 어느 하나의 특성이 기 설정된 기준을 만족시키지 못하는 경우에는 다시 상기 타월의 표면을 플라즈마 처리하는 것을 특징으로 하는 타월 프린팅 방법을 제공하는 것을 과제의 해결 수단으로 한다.In addition, plasma treatment of the surface of the towel that cannot be directly printed, the step of measuring the surface properties of the towel treated in the towel surface treatment unit, the step of printing to print directly on the towel, applying heat to the printed towel curing; Including, the step of measuring the surface properties of the towel, measuring the contact angle of the surface of the towel, measuring the roughness of the towel and measuring the surface tension of the towel, the If any one of the characteristics of the towel's contact angle, roughness, and surface tension does not satisfy the preset criteria, it is to provide a towel printing method, characterized in that the surface of the towel is plasma-treated again as a means of solving the problem. .

본 발명은 직접 인쇄가 불가능한 타월에 고해상도 인쇄가 가능한 표면 처리 기능을 포함하는 프린팅 장치를 제공할 수 있다.The present invention may provide a printing apparatus including a surface treatment function capable of high-resolution printing on a towel that cannot be directly printed.

또한, 본 발명은 종래의 타월 타월 상에 실크 스크린 인쇄 방식을 이용하는 경우, 잉크를 타월 표면에 부착하기 위하여 인체에 유해한 프라이머 (접착제) 성분을 포함하는 것이 필수적이었기 때문에, 인쇄를 수행한 타월 타월 상에 인체에 유해한 프라이머 성분이 잔존하는 문제를 방지하는 고해상도 인쇄가 가능한 표면 처리 기능을 포함하는 프린팅 장치를 제공할 수 있다.In addition, in the present invention, when using a silk screen printing method on a conventional towel towel, it was essential to include a primer (adhesive) component harmful to the human body in order to attach the ink to the towel surface. It is possible to provide a printing device including a surface treatment function capable of high-resolution printing that prevents the residual primer component harmful to the human body.

도 1 은 본 발명의 표면 처리를 하는 플라즈마 장치를 나타낸 사시도이다.
도 2 는 처리부와 이송장치와 플라즈마 전극장치를 나타낸 사시도이다.
도 3 은 도 1 에 도시된 이송장치의 롤러를 나타낸 사시도이다.
도 4 는 도 1 의 A-A 선을 따라 도시한 것이다.
도 5 는 도 1 에 도시된 프레임을 나타낸 사시도이다.
도 6 은 도 1 에 도시된 프레임의 작동을 도시한 것이다.
도 7 은 도 1 에 도시된 플라즈마 전극의 여러가지 실시예를 도시한 것이다.
도 8 은 도 1 에 도시된 진입부의 내부 작동상태를 도시한 것이다.
도 9 는 본 발명의 일 실시예에 따른 표면 처리 기능을 포함하는 프린팅 장치의 블록도를 도시한 것이다.
도 10 은 본 발명의 일 실시예에 따른 표면 처리 기능을 포함하는 프린팅 장치를 이용하여, 직접 인쇄가 불가능한 타월에 프린팅을 하는 공정을 도시한 것이다.1 is a perspective view showing a plasma apparatus for surface treatment of the present invention.
2 is a perspective view showing a processing unit, a transfer device, and a plasma electrode device.
3 is a perspective view showing a roller of the conveying device shown in FIG.
FIG. 4 is a view taken along line AA of FIG. 1 .
FIG. 5 is a perspective view illustrating the frame shown in FIG. 1 .
FIG. 6 shows the operation of the frame shown in FIG. 1 .
FIG. 7 shows various embodiments of the plasma electrode shown in FIG. 1 .
FIG. 8 shows the internal operating state of the entry unit shown in FIG. 1 .
9 is a block diagram of a printing apparatus including a surface treatment function according to an embodiment of the present invention.
Figure 10 shows a process of printing on a towel that cannot be directly printed using a printing apparatus including a surface treatment function according to an embodiment of the present invention.

이하, 첨부한 도면을 참조하여 본 발명의 바람직한 실시 예를 보다 상세하게 설명한다. 도면상의 동일한 구성요소에 대해서는 동일한 참조부호를 사용하고 동일한 구성요소에 대해서 중복된 설명은 생략한다. 그리고, 본 발명은 다수의 상이한 형태로 구현될 수 있고, 기술된 실시 예에 한정되지 않음을 이해하여야 한다.Hereinafter, preferred embodiments of the present invention will be described in more detail with reference to the accompanying drawings. The same reference numerals are used for the same components in the drawings, and repeated descriptions of the same components are omitted. And, it should be understood that the present invention may be implemented in many different forms and is not limited to the described embodiments.

도 1 은 본 발명의 표면처리를 수행하기 위한 플라즈마 장치를 나타낸 사시도이다.1 is a perspective view showing a plasma apparatus for performing surface treatment of the present invention.

도 1 을 참조하면, 본 발명의 표면처리를 수행하기 위한 플라즈마 장치 (100) 는 플라즈마 처리부 (110), 송풍부 (150), 배기부 (160), 진입부 (170), 배출부 (180) 를 포함할 수 있다.Referring to FIG. 1 , the plasma apparatus 100 for performing the surface treatment of the present invention includes a plasma processing unit 110 , a blower 150 , an exhaust unit 160 , an entry unit 170 , and an exhaust unit 180 . may include

먼저, 플라즈마 처리부 (110) 는 타월 (a) 를 이동시키면서 플라즈마에 의해 처리되는 곳이다.First, the plasma processing unit 110 is a place that is processed by plasma while moving the towel (a).

이러한 플라즈마 처리부 (110) 는 밀폐된 공간으로 형성되고, 이 밀폐된 공간의 일측으로 타월 (a) 가 투입되며, 타측으로 플라즈마 표면 처리된 타월가 배출된다.This plasma processing unit 110 is formed in a closed space, the towel (a) is put into one side of the closed space, the plasma surface-treated towel is discharged to the other side.

그리고, 플라즈마 처리부 (110) 의 일측과 타측사이에는 타월를 이동시키기 위한 이송장치 (120) 및 플라즈마 전극장치 (130) 가 구비된다.In addition, a transfer device 120 and a plasma electrode device 130 for moving the towel are provided between one side and the other side of the plasma processing unit 110 .

바람직하게는 플라즈마 처리부 (110) 의 바닥면은 송풍부 (150) 와 구획되는 베이스판 (112) 이 구비되며, 플라즈마 처리부 (110) 의 양측 및 상부에는 플라즈마 처리부 (110) 를 밀폐시키기 위한 측면판 및 천정판으로 구성된 덮개 (111) 가 설치될 수 있다.Preferably, the bottom surface of the plasma processing unit 110 is provided with a base plate 112 partitioned from the blower 150 , and side plates for sealing the plasma processing unit 110 are provided on both sides and upper portions of the plasma processing unit 110 . and a cover 111 composed of a ceiling plate may be installed.

더욱 바람직하게는 덮게 (111) 는 내부가 투영되도록 투명 아크릴판으로 제작될 수 있다.More preferably, the cover 111 may be made of a transparent acrylic plate so that the inside is projected.

도 2 는 처리부와 이송장치와 플라즈마 전극장치를 나타낸 사시도이고, 도 3 은 도 1 에 도시된 이송장치의 롤러를 나타낸 사시도이며, 도 4 는 도 1 의 A-A 선을 따라 도시한 것이다.FIG. 2 is a perspective view showing a processing unit, a transport device, and a plasma electrode device, FIG. 3 is a perspective view showing a roller of the transport device shown in FIG. 1 , and FIG. 4 is a view taken along line A-A of FIG. 1 .

도 2 내지 도 4 를 참조하면, 이송장치 (120) 는 도 2 에 도시된 바와 같이 상하에서 서로 맞물려 회전하는 다수의 롤러 (121) 가 구비될 수 있다.Referring to FIGS. 2 to 4 , the conveying device 120 may include a plurality of rollers 121 that rotate in engagement with each other up and down as shown in FIG. 2 .

상기 롤러 (121) 들은 플라즈마 처리부 (110) 의 입구측에서부터 출구측까지 연속해서 구비되며, 덮개 (111) 의 측면판에 고정되어 통상의 동력전달수단으로 구동될 수 있다.The rollers 121 are continuously provided from the inlet side to the outlet side of the plasma processing unit 110 , and are fixed to the side plate of the cover 111 and may be driven by a conventional power transmission means.

통상의 동력전달수단이라 함은 각 롤러 (121) 들의 일단이나 타단에 체인이나 벨트 또는 기어 등으로 연결되어 이 체인이나 벨트 또는 기어가 모터에 의해 회전되는 수단을 말한다.The normal power transmission means is connected to one end or the other end of each roller 121 with a chain, belt, or gear, and the chain, belt, or gear is rotated by a motor.

상기 롤러 (121) 들은 도 3 에 도시된 바와 같이 타월 재질의 비교적 마찰력이 큰 외피가 사용되고, 외피의 표면에는 엠보싱 (122) 처리가 된다.As shown in FIG. 3 , the rollers 121 are made of a towel material with a relatively high frictional force, and the surface of the outer shell is embossed (122).

엠보싱 (122) 은 돌기형태로 형성될 수도 있고, 일자형으로 형성될 수도 있다.The embossing 122 may be formed in a protrusion shape or may be formed in a straight shape.

한편, 롤러 (121) 들의 가장자리에는 타이밍벨트풀리 (123) 가 형성되며, 상기 타이밍벨트풀리 (123) 에는 타이밍벨트가 체결되도록 구비될 수 있다.On the other hand, a timing belt pulley 123 is formed at the edges of the rollers 121 , and the timing belt pulley 123 may be provided to fasten the timing belt.

이 때, 타이밍벨트에는 도 4 에 도시된 바와 같이 자석 (M) 이 내장되어 상하측의 타이밍벨트 (124) 가 맞닿는 부근에서는 자력에 의해 서로 붙게 된다.At this time, as shown in FIG. 4 , a magnet M is embedded in the timing belt, and in the vicinity where the upper and lower timing belts 124 abut, they are attached to each other by magnetic force.

즉, 롤러 (121) 들의 사이를 지나가면서 플라즈마 처리되는 타월 (a) 가 타이밍벨트 (124) 들의 사이를 통과하면서 타이밍벨트 (124) 간의 자력에 의해 강력하게 밀착되어 얇은 타월라도 헛돌지 않도록 타이밍벨트 (124) 가 움켜잡고 이송시켜주게 된다.That is, the towel (a) plasma-treated while passing between the rollers 121 is strongly adhered by the magnetic force between the timing belts 124 while passing between the timing belts 124 so that even a thin towel does not spin in vain. (124) grabs it and transfers it.

도 1 및 도 2 를 참조하면, 플라즈마 전극장치 (130) 는 횡방향으로 배열된 롤러 (121) 들의 사이에 전극 (131) 이 구비된다. 이러한 전극 (131) 은 롤러 (121) 와 마찬가지로 상하로 이격되게 구비될 수 있다.1 and 2, in the plasma electrode device 130, the electrode 131 is provided between the rollers 121 arranged in the transverse direction. The electrode 131 may be provided to be vertically spaced apart from the roller 121 .

즉, 롤러 (121) 들의 사이를 타월가 지나갈 때 상하의 전극 (131) 들이 타월의 상하부측에서 반응하여 타월의 상하부 표면에 플라즈마 처리를 하게 된다.That is, when the towel passes between the rollers 121 , the upper and lower electrodes 131 react at the upper and lower sides of the towel, and plasma treatment is performed on the upper and lower surfaces of the towel.

이와 같은 전극 (131) 들이 롤러 (121) 들의 사이에 배치되기 위해 처리부 (110) 의 가장자리를 따라 상하로 소정 간격 이격된 프레임 (140) 이 구비된다.In order for the electrodes 131 to be disposed between the rollers 121 , a frame 140 spaced up and down by a predetermined distance is provided along the edge of the processing unit 110 .

프레임 (140) 은 전극 (131) 들을 안치시키기 위한 것으로, 프레임 (140) 을 지지하기 위한 다수의 가이드봉 (141) 과 프레임 (140) 의 상하 간격을 조절하기 위한 간격조절수단 (142) 이 더 구비될 수 있다.The frame 140 is for placing the electrodes 131 in place, and a plurality of guide rods 141 for supporting the frame 140 and a gap adjusting means 142 for adjusting the vertical spacing of the frame 140 are further included. can be provided.

이 때, 가이드봉 (141) 에는 프레임 (140) 의 간격을 확인할 수 있도록 눈금이 형성될 수 있다.At this time, a scale may be formed on the guide rod 141 to check the interval between the frames 140 .

그리고, 간격조절수단 (142) 은 도 6 에 도시된 바와 같이 프레임 (140) 에 나사결합되면서 관통하여 베이스판 (112) 에 고정되는 것으로, 간격조절수단 (142) 의 하단부가 베이스판 (112) 에 고정만 되면서 제자리에서 회전될 수 있는 구조를 갖도록 구비될 수 있다.And, the gap adjusting means 142 is fixed to the base plate 112 while being screwed to the frame 140 as shown in FIG. 6 , and the lower end of the gap adjusting means 142 is the base plate 112 . It may be provided to have a structure that can be rotated in place while being fixed to the .

이 때, 간격조절수단 (142) 의 상측 및 하측에는 서로 반대되는 수나사 (143) 가 형성되어 간격조절수단 (142) 을 정회전 및 역회전시키면 상하부 프레임 (140) 이 서로 오므라들었다 벌어졌다 하게 된다.At this time, opposite male screws 143 are formed on the upper and lower sides of the gap adjusting means 142, and when the gap adjusting means 142 is rotated forward and reversed, the upper and lower frames 140 are retracted and opened from each other. .

이와 같이 형성된 프레임 (140) 에는 다수의 전극 (131) 이 장착되도록 구비될 수 있다.A plurality of electrodes 131 may be mounted on the frame 140 formed in this way.

바람직하게는 프레임 (140) 에는 도 5 에 도시된 바와 같이 전극 (131) 이 꽂혀지도록 홈이 패인 소켓 (145) 이 형성되고, 그 소켓 (145) 의 내부에는 단자가 형성되도록 구비될 수 있다.Preferably, as shown in FIG. 5 , the frame 140 has a socket 145 with a groove in which the electrode 131 is inserted, and a terminal may be formed inside the socket 145 .

그리고 각 단자들은 병렬로 연결되면서 발진기와 연결되도록 구비될 수 있다.In addition, each terminal may be provided to be connected to the oscillator while being connected in parallel.

이 때, 전극 (131) 은 도 7 에 도시된 바와 같이 직립되는 판 형상을 가지면서 석영관 (132) 으로 싸여지고, 양 단부에는 소켓 (145) 에 끼워져 단자와 접속되는 접촉부 (133) 가 돌출 형성되도록 구비될 수 있다.At this time, as shown in FIG. 7 , the electrode 131 has an upright plate shape and is covered with a quartz tube 132 , and a contact portion 133 inserted into the socket 145 and connected to the terminal protrudes from both ends of the electrode 131 . It may be provided to be formed.

상기 전극 (131) 은 상부측 프레임 및 하부측 프레임에 서로 마주보도록 대칭되게 장착될 수 있는데, 서로 마주보는 하단부 및 상단부에는 전류의 퍼짐을 방지하기 위해 칼날 (134) 형상이나 둥그런 반원 형상 (135) 또는 납작한 사각형상 (136) 으로 구비될 수 있다.The electrode 131 may be symmetrically mounted on the upper frame and the lower frame to face each other, and the lower and upper ends facing each other have a blade 134 shape or a round semicircle shape 135 to prevent the spread of current. ) or may be provided in a flat rectangular shape (136).

한편, 전극 (131) 의 배치에 의해 형성된 프레임 (140) 과 롤러 (121) 들의 간섭을 피하기 위해 프레임 (140) 에는 도 5 에 도시된 바와 같이 롤러 (121) 가 관통되도록 관통홈 (146) 이 형성되고, 상기 관통홈 (146) 은 프레임 (140) 의 상하운동으로도 롤러 (121) 와 간섭을 피하기 위해 상하로 길쭉한 장공형태로 형성될 수 있다.On the other hand, in order to avoid interference between the frame 140 and the rollers 121 formed by the arrangement of the electrodes 131, the frame 140 has a through groove 146 through which the roller 121 passes as shown in FIG. is formed, and the through-groove 146 may be formed in the form of a long hole elongated vertically in order to avoid interference with the roller 121 even with the vertical movement of the frame 140 .

도 1 을 참조하면, 송풍부 (150) 는 플라즈마 처리부 (110) 의 하부에 형성되며, 내부에 통상의 송풍기가 설치되고, 이 송풍기가 플라즈마 처리부 (110) 의 내부로 찬바람을 불어주어 플라즈마 처리부 (110) 의 내부를 냉각시킨다.1, the blower 150 is formed under the plasma processing unit 110, a conventional blower is installed therein, and the blower blows cold wind into the plasma processing unit 110 to the plasma processing unit ( 110) to cool the inside.

이 때, 송풍부 (150) 와 플라즈마 처리부 (110) 의 사이에 구비된 베이스판 (112) 에는 송풍부 (150) 의 바람이 플라즈마 처리부 (110) 쪽으로 통과되도록 다수의 통공 (113) 이 구비될 수 있다.At this time, the base plate 112 provided between the blower 150 and the plasma processing unit 110 is provided with a plurality of through holes 113 so that the wind of the blower 150 passes toward the plasma processing unit 110 . can

여기에서, 상기 통공 (113) 은 슬릿 (slit) 형태로 형성될 수 있다.Here, the through hole 113 may be formed in a slit shape.

배기부 (160) 는 플라즈마 처리부 (110) 의 덮개 (111) 위쪽에 형성된다. 상기 배기부 (160) 는 플라즈마 처리부 (110) 의 일측에서부터 타측까지 다수의 덕트 (161) 가 장착되어 덕트 (161) 에서 흡입한 배출가스를 별도의 포집장치로 배기시킨다.The exhaust unit 160 is formed above the cover 111 of the plasma processing unit 110 . The exhaust unit 160 is equipped with a plurality of ducts 161 from one side to the other side of the plasma processing unit 110 to exhaust the exhaust gas sucked in the duct 161 to a separate collection device.

진입부 (170) 는 플라즈마 처리부 (110) 의 입구 앞에 형성되는 것으로, 플라즈마 처리부 (110) 로 들어갈 타월를 전처리하는 공정을 수행한다.The entry unit 170 is formed in front of the entrance of the plasma processing unit 110 , and performs a process of pre-treating the towel to be entered into the plasma processing unit 110 .

즉, 타월에 최적의 플라즈마 처리를 하기 위해서는 적절한 온도를 맞추어 주어야 하고, 표면의 먼지나 이물질이 제거되어야 하기 때문에 이러한 전처리를 하도록 구비될 수 있다.That is, in order to perform an optimal plasma treatment on the towel, an appropriate temperature must be adjusted, and since dust or foreign substances on the surface must be removed, it may be provided to perform such a pretreatment.

도 8 은 도 1 에 도시된 진입부의 내부 작동상태를 도시한 것이다.FIG. 8 shows the internal operating state of the entry unit shown in FIG. 1 .

진입부 (170) 에는 도 1 및 도 8 에 도시된 바와 같이 플라즈마 처리부 (110) 의 입구로 타월 (a) 를 밀어넣는 통상의 롤러 (171) 가 구비되고, 상기 롤러 (171) 들의 사이사이에 타월측으로 바람을 불어 넣는 진입부 분사노즐 (172) 이 구비된다.The entry part 170 is provided with a normal roller 171 for pushing the towel (a) into the inlet of the plasma processing unit 110 as shown in FIGS. 1 and 8 , and between the rollers 171 . An inlet injection nozzle 172 for blowing wind to the towel side is provided.

진입부 분사노즐 (172) 은 타월의 상측 및 하측에 다수가 연속으로 형성되는 것으로, 송풍부 (150) 에서 연결된 진입부 에어 공급관 (175) 과 연결되며, 각각의 진입부 분사노즐 (172) 에는 타월측으로 고압의 에어를 불어 넣도록 좁은 분사통로 (173) 가 형성된다.The entry jet nozzle 172 is a plurality of continuously formed on the upper and lower sides of the towel, and is connected to the entry air supply pipe 175 connected from the blower 150, and each entry jet nozzle 172 has A narrow injection passage 173 is formed to blow high-pressure air toward the towel side.

또한, 진입부 (170) 에는 진입부 (170) 의 실내온도를 체크하는 온도센서가 구비되며, 상기 온도센서에 의해 진입부 (170) 온도를 체크하여 타월측으로 적절한 온도의 에어를 분사시켜준다.In addition, the entry part 170 is provided with a temperature sensor for checking the indoor temperature of the entry part 170, and checks the temperature of the entry part 170 by the temperature sensor, and sprays air of an appropriate temperature to the towel side.

이와 같은 자동온도조절은 별도의 컨트롤러가 구비되며 송풍부 (150) 에서 예열되어 분사되도록 할 수 있다.Such automatic temperature control is provided with a separate controller and can be preheated and sprayed by the blower 150 .

또한, 진입부 분사노즐 (172) 에서 분사된 에어는 배기부 (160) 의 덕트 (161) 를 추가 구성하여 배출시킨다.In addition, the air injected from the entry part injection nozzle 172 is discharged by additionally configuring the duct 161 of the exhaust part 160 .

배출부 (180) 는 플라즈마 처리부 (110) 의 출구측에 형성되는 것으로, 플라즈마 처리된 타월의 표면온도를 냉각시켜주는 역할을 수행한다.The discharge unit 180 is formed on the outlet side of the plasma processing unit 110, and serves to cool the surface temperature of the plasma-treated towel.

이러한 배출부 (180) 는 진입부 (170) 와 마찬가지로 상하로 이격되게 다수가 배치되는 배출부 분사노즐과 배출부 분사노즐로 냉풍을 공급하는 송풍부 (150) 와 연결되는 배출부 에어 공급관 (185) 과 배출부 (180) 내의 공기를 외부로 배출시키는 배기부 (160) 덕트 (161) 를 추가 구성한다.The discharge unit 180 has a discharge unit air supply pipe 185 that is connected to the discharge unit injection nozzle and the blower unit 150 that supplies cold air to the discharge unit injection nozzle, which are arranged to be vertically spaced apart from each other, similar to the entry unit 170 . ) and the exhaust part 160 for discharging the air in the exhaust part 180 to the outside, the duct 161 is additionally configured.

도 9 는 본 발명의 일 실시예에 따른 표면 처리 기능을 포함하는 프린팅 장치의 블록도를 도시한 것이다.9 is a block diagram of a printing apparatus including a surface treatment function according to an embodiment of the present invention.

도 9 를 참조하면, 본 발명의 일 실시예에 따른 표면 처리 기능을 포함하는 프린팅 장치는 직업 인쇄가 불가능한 타월의 표면을 직접 인쇄가 가능하게 표면을 처리하는 표면 처리부 (100), 상기 표면 처리부 (100) 에서 표면 처리된 타월의 표면의 컨택앵글을 측정하는 컨택앵글 측정부 (210), 상기 표면 처리부 (100) 에서 표면 처리된 타월의 표면의 조도를 측정하는 조도 측정부 (230), 상기 표면 처리부 (100) 에서 표면 처리된 타월의 표면의 표면장력을 측정하는 표면장력 측정부 (250), 상기 측정된 타월를 예열하는 예열부 (300), 예열된 타월에 인쇄를 하는 프린팅부 (400) 및 프린팅이 완료된 타월를 건조시키는 건조부 (500) 를 포함하도록 구비될 수 있다.Referring to Figure 9, the printing apparatus including a surface treatment function according to an embodiment of the present invention is a surface treatment unit 100, the surface treatment unit ( 100), a contact angle measuring unit 210 for measuring the contact angle of the surface of the surface-treated towel, the roughness measuring unit 230 for measuring the roughness of the surface of the towel surface-treated in the surface treatment unit 100 , the surface A surface tension measuring unit 250 for measuring the surface tension of the towel surface treated in the treatment unit 100, a preheating unit 300 for preheating the measured towel, a printing unit 400 for printing on the preheated towel, and It may be provided to include a drying unit 500 for drying the towel on which printing is completed.

상기 표면 처리부 (100) 는 앞선 도 1 내지 도 8 에서 설명한 바와 같이, 플라즈마 처리 방식을 이용하여, 직접 인쇄가 불가능한 타월의 표면을 직접 인쇄가 가능하도록 표면처리하는 기능을 한다.As described above with reference to FIGS. 1 to 8 , the surface treatment unit 100 functions to surface-treat the surface of a towel that cannot be directly printed using a plasma treatment method so that direct printing is possible.

표면 처리된 타월가 직접 인쇄가 가능할 정도로 표면 처리된 타월의 특성을 측정하는 컨택앵글 측정부 (210), 조도 측정부 (230) 및 표면장력 측정부 (250) 를 포함할 수 있다.The surface-treated towel may include a contact angle measuring unit 210 , a roughness measuring unit 230 , and a surface tension measuring unit 250 for measuring the characteristics of the surface-treated towel to the extent that direct printing is possible.

보다 구체적으로는 컨택앵글은 고체 표면의 젖음성 (wettability) 를 나타내는 척도로서 대부분 고착된 물방울에 의해 측정된다.More specifically, the contact angle is a measure of the wettability of a solid surface and is mostly measured by fixed water droplets.

낮은 접촉각은 높은 젖음성 (친수성, hydrophilic) 과 높은 표면 에너지를 나타내고, 높은 접촉각은 낮은 젖음성 (소수성, hydrophobic) 과 낮은 표면 에너지를 나타낸다. A low contact angle indicates high wettability (hydrophilic) and high surface energy, and a high contact angle indicates low wettability (hydrophobic) and low surface energy.

편평한 고체표면에 접촉한 액체의 접촉각은 액체, 고체, 기체의 접합점에서 물방울 곡선의 끝점과 고체 표면의 접촉점에서 측정된다,The contact angle of a liquid in contact with a flat solid surface is measured at the point of contact between the solid surface and the endpoint of the droplet curve at the junction of liquid, solid, and gas.

즉, 본 발명의 프린팅 장치는 직접 인쇄가 불가능한 타월에 직접 인쇄가 가능하도록 타월의 표면을 친수성으로 성질을 변화시키는 것을 주된 과제 해결 방법으로 하기 때문에, 타월 표면의 컨택앵글은 인쇄가능성에 있어서 중요한 파라미터가 된다.That is, since the printing apparatus of the present invention is to change the property of the towel surface to hydrophilicity so that direct printing is possible on the towel that cannot be directly printed as a main problem solving method, the contact angle of the towel surface is an important parameter in printability becomes

따라서, 상기 컨택앵글 측정부 (210) 는 표면처리가 완료된 타월의 표면의 컨택앵글을 측정하여, 상기 측정된 컨택앵글이 0°내지 50°이하 이하가 되는지 판단 하고, 상기 범위를 만족하는 경우에는 True 신호를 제어부에 송출하게 된다.Therefore, the contact angle measuring unit 210 measures the contact angle of the surface of the towel on which the surface treatment is completed, and determines whether the measured contact angle is 0° to 50° or less, and if the range is satisfied, A true signal is transmitted to the control unit.

한편, 표면 조도 (Surface Roughness) 는 표면 거칠기의 대표적인 종류로 중심선 평균 산출법 (Ra), 최대 높이 산출법 (Rs), 십점 평균 산출법 (Rz) 이 있고, 설명의 편의상 본 발명의 경우에는 산술 평균 조도 (Ra) 를 측정하는 것으로 설명하도록 한다.On the other hand, the surface roughness (Surface Roughness) is a representative type of surface roughness, and there are a centerline average calculation method (Ra), a maximum height calculation method (Rs), and a ten-point average calculation method (Rz). It will be explained by measuring Ra).

본 발명자가 상기 타월의 표면에 직접 인쇄가 가능하기 위해서 연구를 거듭한 결과, 타월의 산술 평균 조도 (Ra) 는 0.3a 이상 0.9a 이하가 되어야 타월에 직접 인쇄를 할 수 있는 것을 발견하였다.As a result of repeated research by the present inventors to enable direct printing on the surface of the towel, the arithmetic mean roughness (Ra) of the towel was found to be 0.3a or more and 0.9a or less to directly print on the towel.

따라서, 본 발명의 일 실시예에 따른 조도 측정부 (230) 는 타월의 표면 조도를 측정하고, 측정된 타월의 산술 평균 조도 (Ra) 가 0.3a 이상 0.9a 이하가 되는지 판단 하고, 상기 범위를 만족하는 경우에는 True 신호를 제어부에 송출하게 된다.Therefore, the roughness measurement unit 230 according to an embodiment of the present invention measures the surface roughness of the towel, and determines whether the measured arithmetic mean roughness (Ra) of the towel is 0.3a or more and 0.9a or less, and the range is If it is satisfied, a True signal is transmitted to the control unit.

한편, 표면장력이라 함은 액체의 자유 표면에서 표면을 작게 하려고 작용하는 힘인데, 표면장력이 커지면 타월 표면의 물방울이 보다 더 잘 뭉치고, 퍼짐성이 낮아지게 된다.On the other hand, the surface tension is a force acting to make the surface smaller on the free surface of the liquid.

고체의 표면장력 값은 표면에너지라고 정의될 수 있는데, 보다 구체적으로는 고체에 있어서 표면에너지는 고체와 기체 사이의 값으로 정의되고, 접착의 중요한 지표가 된다.The surface tension value of a solid can be defined as surface energy. More specifically, in a solid, the surface energy is defined as a value between a solid and a gas, and is an important indicator of adhesion.

고체의 표면에너지가 높다는 뜻은 단위 면적당 더 높은 에너지가 집중되어 있어 보다 강한 결합을 할 수 있기 때문에, 타월의 표면에 직접 인쇄를 하기 위해서는 고체의 타월의 표면에너지가 일정 수준보다 높아야 한다.The high surface energy of the solid means that higher energy is concentrated per unit area and stronger bonding is possible. Therefore, in order to print directly on the surface of the towel, the surface energy of the solid towel must be higher than a certain level.

따라서, 본 발명의 일 실시예에 따른 표면장력 측정부 (250) 는 표면 처리된 타월가 직접 인쇄가 가능한지 판단하기 위해 타월의 표면장력을 측정할 수 있는데, 그 방법중에 하나로 다인 펜슬 또는 다인 잉크를 이용하여 타월의 표면장력을 측정할 수 있다.Therefore, the surface tension measuring unit 250 according to an embodiment of the present invention can measure the surface tension of the towel to determine whether the surface-treated towel can be directly printed. One of the methods is using a dyne pencil or dyne ink. Thus, the surface tension of the towel can be measured.

보다 구체적으로는, 상기 표면장력 측정부 (250) 는 42dyne/cm 이 되는지 판단하고, 상기 범위를 만족하는 경우에는 True 신호를 제어부에 송출하게 된다.More specifically, the surface tension measuring unit 250 determines whether it is 42 dyne/cm and transmits a True signal to the control unit when the range is satisfied.

상술한 바와 같이, 본 발명의 측정부 (200) 는 표면 처리된 타월의 특성을 여러 방법으로 측정할 수 있는데, 사용자는 타월의 표면 특성을 측정하기 위해 상기 세 개의 측정부 (200) 모두 이용할 수 있고, 이들 중에 일부를 선택적으로 이용할 수도 있으며, 이는 본 발명의 권리범위를 한정하지 아니한다.As described above, the measuring unit 200 of the present invention can measure the characteristics of the surface-treated towel in various ways, and the user can use all three measuring units 200 to measure the surface characteristics of the towel. and some of them may be selectively used, which does not limit the scope of the present invention.

한편, 상기 예열부 (300) 는 타월가 프린팅부 (400) 에 진입하기 전에 타월의 온도를 상승시키기 위하여, 타월를 예열하는 기능을 수행한다.On the other hand, the preheating unit 300 performs a function of preheating the towel in order to increase the temperature of the towel before the towel enters the printing unit (400).

이는, 프린팅 잉크가 수성잉크를 사용하는 경우에는 건조를 위하여, 타월 자체의 온도를 높이게 되는데, 이 때, 상기 예열부 (300) 는 타월 표면의 온도가 50°C 이하가 되도록 제어될 수 있다.This is to increase the temperature of the towel itself for drying when the printing ink uses water-based ink, at this time, the preheating unit 300 may be controlled so that the temperature of the towel surface is 50 ° C or less.

또한, 상기 프린팅부 (400) 에서 타월의 표면에 프린팅을 완료한 이후에, 상기 타월는 건조부 (500) 에 전달될 수 있고, 전달된 타월는 상기 건조부 (500) 를 지나면서 완전 건조될 수 있다.In addition, after the printing unit 400 completes printing on the surface of the towel, the towel may be delivered to the drying unit 500, and the delivered towel may be completely dried while passing through the drying unit 500. .

도 10 은 본 발명의 일 실시예에 따른 표면 처리 기능을 포함하는 프린팅 장치를 이용하여, 직접 인쇄가 불가능한 타월에 프린팅을 하는 공정을 도시한 것이다.Figure 10 shows a process of printing on a towel that cannot be directly printed using a printing apparatus including a surface treatment function according to an embodiment of the present invention.

도 10 을 참조하면, 본 발명의 일 실시예에 따른 표면 처리 기능을 포함하는 프린팅 장치를 이용하여, 직접 인쇄가 불가능한 타월에 프린팅을 하기 위하여, 타월의 표면을 처리하는 표면처리단계 (S100), 상기 표면처리단계 (S100) 이후, 표면처리단계 (S100) 에서의 표면 처리가 적합한지 여부를 측정하는 측정단계 (S200), 상기 측정단계 (S200) 이후, 상기 타월가 프린팅되기 전에 타월 표면의 온도가 50°C 이하가 되도록 예열하는 예열 단계 (S300), 상기 예열 단계 (S300) 에서 예열된 타월에 직접 인쇄를 하는 프린팅 단계 (S400) 및 상기 프린팅 단계 (S400) 에서 프린팅이 완료된 타월를 건조시키는 건조 단계 (S500) 을 포함할 수 있다.Referring to Figure 10, using the printing apparatus including a surface treatment function according to an embodiment of the present invention, in order to print on a towel that cannot be directly printed, a surface treatment step of treating the surface of the towel (S100), After the surface treatment step (S100), the measuring step (S200) of measuring whether the surface treatment in the surface treatment step (S100) is suitable, after the measuring step (S200), the temperature of the towel surface before the towel is printed Preheating step (S300) of preheating to be below 50 °C, printing step (S400) of printing directly on the towel preheated in the preheating step (S300), and drying step of drying the towel after printing in the printing step (S400) (S500) may be included.

한편, 상기 측정단계 (S200) 은 타월의 컨택 앵글을 측정하는 컨택앵글측정단계 (S211), 상기 타월의 조도를 측정하는 조도 측정 단계 (S213) 및 상기 타월의 표면장력을 측정하는 표면장력 측정단계 (S215) 를 포함하도록 구비될 수 있다.On the other hand, the measuring step (S200) is a contact angle measuring step (S211) of measuring the contact angle of the towel, the roughness measuring step (S213) of measuring the roughness of the towel, and the surface tension measuring step of measuring the surface tension of the towel (S215) may be provided to include.

또한, 본 발명의 다른 실시예에 따른 타월 프린팅 방법은 직접 인쇄가 불가능한 타월의 표면을 플라즈마 처리하는 단계, 상기 타월표면처리부에서 처리된 타월의 표면 특성을 측정하는 단계, 상기 타월에 직접 인쇄를 하는 프린팅하는 단계, 상기 인쇄된 타월에 열을 가하여 경화시키는 단계를 포함하고, 상기 타월의 표면 특성을 측정하는 단계는, 상기 타월의 표면의 컨택앵글을 측정하는 단계, 상기 타월의 조도를 측정하는 단계 및 상기 타월의 표면장력을 측정하는 단계를 포함하고, 상기 타월의 컨택앵글, 조도 및 표면장력 중 어느 하나의 특성이 기 설정된 기준을 만족시키지 못하는 경우에는 다시 상기 타월의 표면을 플라즈마 처리하도록 구비될 수 있다.In addition, the towel printing method according to another embodiment of the present invention comprises the steps of plasma-treating the surface of a towel that cannot be directly printed, measuring the surface characteristics of the towel treated in the towel surface treatment unit, and directly printing on the towel. Printing, comprising the step of curing by applying heat to the printed towel, the step of measuring the surface properties of the towel, measuring the contact angle of the surface of the towel, measuring the roughness of the towel and measuring the surface tension of the towel, and when any one of the contact angle, roughness, and surface tension of the towel does not satisfy the preset criteria, it will be provided to plasma-treat the surface of the towel again can

즉, 상기 타월의 표면의 특성 (컨택앵글, 조도 및 표면장력) 을 만족하지 못하는 경우에는 원하는 수준의 프린팅이 되지 않기 때문에, 상기 타월의 표면의 특성을 만족하지 못한 경우에는 다시 플라즈마 처리를 하도록 구비될 수 있다.That is, if the characteristics of the towel's surface (contact angle, roughness, and surface tension) are not satisfied, the desired level of printing is not achieved. can be

이상에서 본 발명의 바람직한 실시 예를 설명하였으나, 본 발명의 권리범위는 이에 한정되지 않으며, 본 발명의 실시 예와 실질적으로 균등한 범위에 있는 것까지 본 발명의 권리 범위가 미치는 것으로 본 발명의 정신을 벗어나지 않는 범위 내에서 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변형 실시가 가능한 것이다.Although preferred embodiments of the present invention have been described above, the scope of the present invention is not limited thereto, and the scope of the present invention extends to those substantially equivalent to the embodiments of the present invention. Various modifications are possible by those of ordinary skill in the art to which the invention pertains without departing from the scope of the invention.

100 : 표면처리부
200 : 측정부
210 : 컨택앵글 측정부
230 : 조도 측정부
250 : 표면장력 측정부100: surface treatment unit
200: measurement unit
210: contact angle measurement unit
230: illuminance measuring unit
250: surface tension measurement unit

Claims (8)

직접 인쇄가 불가능한 타월의 표면을 플라즈마 처리하는 타월표면처리부;
상기 타월표면처리부에서 처리된 타월의 표면 특성을 측정하는 측정부;
상기 타월에 직접 인쇄를 하는 프린팅부; 및
상기 인쇄된 타월에 열을 가하여 경화시키는 열경화부를 포함하는 것을 특징으로 하는 타월 프린팅 장치.Towel surface treatment unit for plasma-treating the surface of the towel cannot be directly printed;
Measuring unit for measuring the surface characteristics of the towel treated in the towel surface treatment unit;
a printing unit for printing directly on the towel; and
Towel printing apparatus comprising a thermosetting unit for curing by applying heat to the printed towel. 제 1 항에 있어서,
상기 표면처리부는 상기 적어도 하나 이상의 전극을 포함하며,
상기 적어도 하나 이상의 전극은 상기 타월의 상부와 하부에 배치되는 다 전극 양면 플라즈마 장치인 것을 특징으로 하는 타월 프린팅 장치.The method of claim 1,
The surface treatment unit includes the at least one electrode,
The at least one electrode is a towel printing device, characterized in that the multi-electrode double-sided plasma device disposed on the top and bottom of the towel. 제 2 항에 있어서,
상기 표면처리부에서 표면 처리된 타월의 컨택 앵글은 0°내지 50°인 것을 특징으로 하는 타월 프린팅 장치.3. The method of claim 2,
The contact angle of the towel surface-treated in the surface treatment unit is a towel printing device, characterized in that 0 ° to 50 °. 제 2 항에 있어서,
상기 표면처리부에서 표면 처리된 타월의 표면조도는 0.3a 내지 0.9a 인 것을 특징으로 하는 타월 프린팅 장치.3. The method of claim 2,
Towel printing apparatus, characterized in that the surface roughness of the towel surface-treated in the surface treatment unit is 0.3a to 0.9a. 제 2 항에 있어서,
상기 표면처리부에서 표면 처리된 타월에 다인 펜슬을 도포한 경우에 42dyne/cm 인 것을 특징으로 하는 타월 프린팅 장치.3. The method of claim 2,
Towel printing device, characterized in that 42 dyne / cm when the dyne pencil is applied to the towel surface-treated in the surface treatment unit. 제 1 항에 있어서,
상기 프린팅부에 인쇄하기 전에 타월를 예열하는 예열부 및
상기 프린팅부에 의해 인쇄된 이후 타월를 건조하는 건조부를 포함하는 것을 특징으로 하는 타월 프린팅 장치.The method of claim 1,
A preheating unit for preheating the towel before printing on the printing unit, and
Towel printing device, characterized in that it comprises a drying unit for drying the towel after being printed by the printing unit. 제 1 항에 있어서,
상기 타월의 표면의 컨택앵글을 측정하는 컨택앵글 측정부;
상기 타월의 조도를 측정하는 조도 측정부; 및
상기 타월의 표면장력을 측정하는 표면장력 측정부를 포함하는 것을 특징으로 하는 타월 프린팅 장치.The method of claim 1,
a contact angle measuring unit for measuring a contact angle of the surface of the towel;
an illuminance measuring unit for measuring the illuminance of the towel; and
Towel printing apparatus comprising a surface tension measuring unit for measuring the surface tension of the towel. 직접 인쇄가 불가능한 타월의 표면을 플라즈마 처리하는 단계;
상기 타월표면처리부에서 처리된 타월의 표면 특성을 측정하는 단계;
상기 타월에 직접 인쇄를 하는 프린팅하는 단계;
상기 인쇄된 타월에 열을 가하여 경화시키는 단계; 를 포함하고,
상기 타월의 표면 특성을 측정하는 단계는,
상기 타월의 표면의 컨택앵글을 측정하는 단계;
상기 타월의 조도를 측정하는 단계; 및
상기 타월의 표면장력을 측정하는 단계를 포함하고,
상기 타월의 컨택앵글, 조도 및 표면장력 중 어느 하나의 특성이 기 설정된 기준을 만족시키지 못하는 경우에는 다시 상기 타월의 표면을 플라즈마 처리하는 것을 특징으로 하는 타월 프린팅 방법.Plasma treatment of the surface of the towel cannot be directly printed;
Measuring the surface characteristics of the towel treated in the towel surface treatment unit;
Printing to print directly on the towel;
curing the printed towel by applying heat; including,
Measuring the surface properties of the towel is,
measuring a contact angle of the surface of the towel;
measuring the roughness of the towel; and
Comprising the step of measuring the surface tension of the towel,
Towel printing method, characterized in that the plasma treatment of the surface of the towel again when any one of the characteristics of the towel contact angle, roughness, and surface tension does not meet the preset criteria.
KR1020200084263A 2020-07-08 2020-07-08 Towel printing method using a printing device including a surface treatment function KR102460722B1 (en)