KR20210070953A - A Environmental-friendly Plastering Additives Containing Vegetable Additives and Environmental-frie ndly Plastering Cement Using the Same and Mortar Containing the Same - Google Patents

A Environmental-friendly Plastering Additives Containing Vegetable Additives and Environmental-frie ndly Plastering Cement Using the Same and Mortar Containing the Same Download PDF

Info

Publication number
KR20210070953A
KR20210070953A KR1020210065739A KR20210065739A KR20210070953A KR 20210070953 A KR20210070953 A KR 20210070953A KR 1020210065739 A KR1020210065739 A KR 1020210065739A KR 20210065739 A KR20210065739 A KR 20210065739A KR 20210070953 A KR20210070953 A KR 20210070953A
Authority
KR
South Korea
Prior art keywords
weight
parts
powder
additive
activated carbon
Prior art date
Application number
KR1020210065739A
Other languages
Korean (ko)
Inventor
왕미정
Original Assignee
왕미정
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 왕미정 filed Critical 왕미정
Priority to KR1020210065739A priority Critical patent/KR20210070953A/en
Publication of KR20210070953A publication Critical patent/KR20210070953A/en

Abstract

The present invention relates to an eco-friendly plastering additives containing plant additives, and cement and mortar using the same. The eco-friendly plastering additive containing the vegetable additive according to the present invention comprises: gypsum, activated carbon, a vegetable additive and an adsorption deodorant, wherein the gypsum is dihydrate gypsum or anhydrite. The activated carbon is prepared by the steps of: cutting bamboo, oak, and pine trees to a length of 500 to 1000 mm, individually; preparing activated carbon for carbonizing the cut-processed bamboo, oak and pine at a temperature of 1000 to 1500°C, individually; selecting and separating the carbonized activated carbon, individually; and grinding the separated activated carbon, individually, and selecting a particle size in the range of 50 to 250 mesh. The vegetable additive is prepared by mixing ginkgo leaf powder and mugwort powder, wherein the ginkgo leaf powder and mugwort powder are mixed in a weight ratio of 60:40 to 40:60, and the adsorption deodorant is prepared by mixing diatomaceous earth, zeolite, adsorbent and gelite. According to the present invention, the condensing speed is reduced by rapidly evaporating moisture by the gypsum during initial curing of curing, and when drying after condensing, the drying time is delayed by continuous moisture supply of activated carbon or adsorption deodorant to prevent cracks in the floor or wall of the building due to rapid drying. By preparing plastering additives using plant additives beneficial to human health, it is harmless to the human body, and also it can be widely used as an eco-friendly building material to form an eco-friendly residential space.

Description

식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 시멘트 및 몰탈{A Environmental-friendly Plastering Additives Containing Vegetable Additives and Environmental-frie ndly Plastering Cement Using the Same and Mortar Containing the Same}Eco-friendly plastering additives containing vegetable additives, cement and mortar using the same {A Environmental-friendly Plastering Additives Containing Vegetable Additives and Environmental-frie ndly Plastering Cement Using the Same and Mortar Containing the Same}

본 발명은 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈에 관한것으로, 더욱 상세하게는 석고, 활성탄, 식물성 첨가제 및 흡착탈취제를 혼합하여 수축 절감 성능을 가지는 미장용 첨가제를 제조함으로써, 양생 초기 응결시 상기 석고에 의해 수분이 급격하게 증발되어 응결속도를 단축할수 있고, 응결 후 건조시에는 활성탄 또는 흡착탈취제의 지속적인 수분 공급에 의해 건조시간을 지연시켜 급격한 건조에 의한 건축물의 바닥이나 벽면의 균열을 방지하며, 시멘트에서 발생하는 다양한 유해가스를 흡착 제거함으로써, 시공자와 사용자의 건강을 도모할 수 있는 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈에 관한 것이다. The present invention relates to an eco-friendly cosmetic additive containing a vegetable additive, and cosmetic cement and mortar using the same, and more particularly, to a cosmetic additive having shrinkage reduction performance by mixing gypsum, activated carbon, vegetable additive and adsorption deodorant By doing so, moisture is rapidly evaporated by the gypsum during the initial setting of curing, and the setting speed can be shortened, and when drying after setting, the drying time is delayed by continuous moisture supply of activated carbon or adsorption deodorant, so that the floor of the building by rapid drying It relates to an eco-friendly cosmetic additive containing plant additives that can prevent cracks or wall cracks and promote the health of builders and users by adsorbing and removing various harmful gases generated from cement, and plastering cement and mortar using the same. .

일반적으로, 주택은 목재, 석재 및 황토와 같은 천연재료를 이용하여 건축이 이루어졌으나, 산업화와 도시화로 인하여 좁은 장소에 주거공간이 밀집됨에 따라 건축재료가 시멘트와 콘크리트로 변화되면서 신속하고 견고한 건축이 가능하게 되었다. In general, houses were built using natural materials such as wood, stone, and loess, but as residential spaces are concentrated in narrow places due to industrialization and urbanization, the building materials are changed to cement and concrete, resulting in rapid and robust construction. It became possible.

이러한 시멘트 및 콘크리트를 이용한 건축은, 사람이 거주하는 시멘트로 된 주거공간은 전자제품들에 의해 통풍과 습도 및 온도 등을 인위적으로 조절하게 됨으로써 전자파에 거의 노출된 상태이며, 시멘트에서 발생 되는 유해한 화학물질은 아토피와 같은 현대병을 유발하는 요인으로 작용하고 있다. In the construction using cement and concrete, the cement residential space where people live is almost exposed to electromagnetic waves by artificially controlling ventilation, humidity, and temperature by electronic products, and harmful chemicals generated from cement. Substances are acting as factors inducing modern diseases such as atopy.

즉, 변화된 건축자재에 의해 인체에 유익한 물질을 배출시키는 천연재료는 사용량이 줄어들면서 인체에 유해한 물질을 배출시키는 시멘트의 사용량은 증가 됨에 따라 거주자에게 장시간 영향을 주어 건강을 해치는 결과를 초래하고 있다. In other words, as the amount of natural materials that discharge beneficial substances to the human body by the changed building materials decreases and the amount of cement that discharges substances harmful to the human body increases, it affects residents for a long time, resulting in harming their health.

좀더 상세하게 설명하면, 건축물의 벽이나 바닥을 형성하는 콘크리트와 이의 마감을 위해 사용되는 미장재료에는 시멘트가 포함되는바, 이러한 시멘트는 우수한 강도를 제공하고 있으나, 물질 내에 독성가스 물질이 함유되는 문제점이 있다. More specifically, the concrete forming the wall or floor of a building and the plastering material used for its finishing include cement. Such cement provides excellent strength, but the problem that toxic gas substances are contained in the material There is this.

근자에는, 폐기물 중 일부를 시멘트에 혼합하여 사용함으로써 중금속에 대한 각종 폐해가 발생하는 문제점도 있다. Recently, there is also a problem that various harmful effects on heavy metals occur by mixing some of the wastes with cement and using them.

또한, 마감을 위해 시멘트와 모래와 물을 혼합하는 단순 몰탈의 경우에는 불균일한 건조 또는 급격한 건조에 의해 균열(crack)발생률이 높게 나타나고, 이러한 크랙은 구조강도를 낮추는 것은 물론 외부로부터 방사성 물질인라돈을 유입시키게 되므로 이를 해소하기 위해서 첨가제를 혼합사용하여 균열발생을 억제하고 있다. In addition, in the case of a simple mortar that mixes cement, sand and water for finishing, the crack occurrence rate is high due to non-uniform drying or rapid drying, and these cracks not only lower the structural strength, but also reduce the structural strength of radon, a radioactive material from the outside. In order to solve this problem, additives are mixed and used to suppress the occurrence of cracks.

상기에서, 대표적인 첨가제로는 혼합되는 물질로는 고로슬래그 미분말이나, 수축저감제(균열방지제)가 있다. In the above, representative additives include fine blast furnace slag powder or a shrinkage reducing agent (crack inhibitor) as a mixed material.

상기 고로슬래그는 제철소의 용광로에서 생산되는 부산물로서 보통 포틀랜드 시멘트에 일정량 혼합사용하여 시멘트의 장기강도를 향상시킬 수 있고, 수화열이 낮아 상대적으로 포틀랜드 시멘트보다 균열을 예방할 수 있다. The blast furnace slag is a by-product produced in a blast furnace of an ironworks, and it is possible to improve the long-term strength of cement by mixing it with portland cement in a certain amount, and to prevent cracking compared to portland cement because of its low heat of hydration.

또한, 수축방지제로는 주로 탈황석고를 사용하는 것으로, 상기 탈황석고는 정유공장 또는 화력발전소에서 연소정제작업 후 배출되는 일종의 폐기물로서 그 주성분인 CaO 중에는 석유나 코크스 연소시 발생 되는 아황산가스가 결합 된 황화합물이 다량 함유되어 있다. In addition, as a shrinkage inhibitor, desulfurized gypsum is mainly used, and the desulfurized gypsum is a kind of waste discharged after combustion refining work in an oil refinery or thermal power plant. It contains a large amount of sulfur compounds.

그러나, 탈황석고는 자체 발열로 동절 기는 약 15℃ 내외, 하 절기 약 39℃ 내외, 춘추 절기 약 25℃ 내외로 형성되는 몰탈 온도로 인하여 미장마감시간이 동 절기 약 5~6시간, 하 절기 약 2~3시간, 춘추 절기 약 4시간 정도 소요되는 등 기존 타설후 7~12시간씩 소요되는 미장 마감시간을 획기적으로 단축할 수 있으며, CaSO4로 인한 팽창작용으로 건조 수축에 따른 용적 감소를 보상하여 건조수축에 의한 균열을 저감할 수 있다. However, due to the self-heating of desulfurized gypsum, due to the mortar temperature formed around 15℃ in winter, about 39℃ in summer, and about 25℃ in spring and autumn, the finishing time for plastering is about 5 to 6 hours in winter and about 5 to 6 hours in summer. It can dramatically shorten the plastering finishing time, which takes 7 to 12 hours after pouring, such as 2 to 3 hours and about 4 hours in the spring and autumn seasons, and compensates for the volume decrease due to drying and shrinkage due to the expansion action of CaSO4. Cracking due to drying shrinkage can be reduced.

따라서, 방통 몰탈에 사용되는 수축저감제로는 가격이 저렴하면서 특성상 높은 물/시멘트 비에 따른 부작용(균열, 마감 미장에 장시간 소요) 해소에 탁월한 기능을 발휘하는 탈황석고를 주로 사용하고 있다. Therefore, as a shrinkage reducing agent used for ventilation mortar, desulfurized gypsum, which is inexpensive and exhibits excellent functions in resolving side effects (cracking, long time required for finishing plastering) due to the high water/cement ratio, is mainly used.

상기 탈황석고를 사용하지 않는 몰탈은 심한 균열 발생으로 균열을 통해 라돈가스, 암모니아, 중금속이 마감된 장판이나 마루 사이로 방출되어 아토피질환 등의 기타 질병을 유발시킨다. The mortar that does not use the desulfurized gypsum is severely cracked, and radon gas, ammonia, and heavy metals are released through the cracks between the finished flooring boards or floors, causing other diseases such as atopic diseases.

또한, 시중에 사용하고 있는 균열방지제는 시멘트 독성 유해물질 라돈이나 암모니아, 중금속, 아황산가스 등을 흡착, 탈취할 수 없는 제품이다. In addition, crack inhibitors used in the market are products that cannot adsorb and deodorize radon, ammonia, heavy metals, sulfurous acid gas, etc., which are harmful substances toxic to cement.

이와 같이 미장용 또는 타설용 시멘트조성물에는 수축저감제(균열방지재)로서 탈황석고를 첨가하여 균열발생을 억제해 구조강도의 저하를 방지하고 있으나, 탈황석고에서 발생하는 아황산가스나 시멘트에서 배출 또는 균열에 의해 유입되는 라돈, 암모니아, 중금속에 대해서는 아직 확실한 대안이 제시되지 못하였다. As described above, desulfurized gypsum is added as a shrinkage reducing agent (crack prevention material) to the cement composition for plastering or pouring to prevent cracks from occurring to prevent deterioration of structural strength. For radon, ammonia, and heavy metals introduced by cracks, no clear alternative has yet been proposed.

한편, 대한민국 특허공개 10-2000-0024422(20000506공개)의 시멘트 몰탈용 수축저감제에는 정유공장에서 배출되는 황화물이 결합된 연소재(탈황석고)를 아무 가공 또는 정제 과정 없이 방통몰탈 제조에 사용하였다. On the other hand, in the shrinkage reducing agent for cement mortar of the Republic of Korea Patent Publication No. 10-2000-0024422 (published 20000506), a combustion material (desulfurized gypsum) combined with sulfide emitted from an oil refinery was used for manufacturing mortar without any processing or refining process. .

그리고, 대한민국 특허공개 10-2011-0004807호(20110114 공개)에는 무기질 섬유상재료(해포석) 45~70중량％,칼슘 설포 알루미네이트 3~8중량％, 탈황석고 3~8중량％, 실리케이트계 미네랄 5~20중량％, 점토질 보강재 5~20 중량％, 수산화물 첨가제 05~5중량％로 혼합하여 무기질 섬유계 콘크리트 균열저감재 조성물을 제시하였다. And, in Korean Patent Publication No. 10-2011-0004807 (published 20110114), 45-70 wt% of inorganic fibrous material (Haepo-seok), 3-8 wt% of calcium sulfoaluminate, 3-8 wt% of desulfurized gypsum, and 5 silicate-based minerals An inorganic fiber-based concrete crack reducing material composition was presented by mixing ~20% by weight, 5 to 20% by weight of a clay reinforcing material, and 05 to 5% by weight of a hydroxide additive.

그러나, 상기 종래의 조성물들은 균열방지 효과만을 구현할 뿐, 배출되는 각종 유해성분에 대한 대처방안에 대해서는 제안하지 못하는 문제점이 있었다. However, the conventional compositions have a problem that only implements a crack prevention effect, and cannot propose a countermeasure for various harmful components discharged.

즉, 기존 균열저감재를 마감재 또는 시멘트에 혼합사용해 균열발생을 억제함으로써 건물구조강도의 저하를 방지하는 효과를 제공하나, 각종 유해성분을 차단하는 기능은 구현하지 못하는 문제점이 있었다. That is, the existing crack reducing materials are mixed with finishing materials or cement to suppress cracks from occurring, thereby providing an effect of preventing the deterioration of building structural strength, but there was a problem in that the function of blocking various harmful components could not be realized.

본 발명은 석고, 활성탄, 식물성 첨가제 및 흡착탈취제를 혼합하여 수축 절감 성능을 가지는 미장용 첨가제를 제조함으로써, 양생 초기 응결시 상기 석고에 의해 수분이 급격하게 증발되어 응결속도를 단축할 수 있고, 응결후 건조시에는 활성탄 또는 흡착탈취제의 지속적인 수분 공급에 의해 건조시간을 지연시켜 급격한 건조에 의한 건축물의 바닥이나 벽면의 균열을 방지할 수 있는 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈을 제공하는데 있다. In the present invention, by mixing gypsum, activated carbon, vegetable additive and adsorption deodorant to produce a cosmetic additive having shrinkage reduction performance, moisture is rapidly evaporated by the gypsum during initial curing during curing to shorten the setting speed, and During post-drying, an eco-friendly cosmetic additive containing plant additives that can prevent cracks in the floor or wall of a building due to rapid drying by delaying the drying time by continuous moisture supply of activated carbon or adsorption deodorant, and plastering cement using the same and to provide a mortar.

또한, 본 발명은 시멘트에서 발생하는 다양한 유해가스를 흡착 제거할 수 있는 미장용 참가제를 제조함으로써, 경화시간을 조절하여 원하는 압축강도를 얻을 수 있고, 내마모성, 내화학성 및 표면 강도를 증진시킬 수 있으며, 시공자와 사용자의 건강을 도모하고 쾌적한 환경을 조성할 수 있는 식물성 첨가제를 포함하는 친환경미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈을 제공하는데 있다. In addition, the present invention can obtain a desired compressive strength by controlling the curing time by manufacturing a plastering agent capable of adsorbing and removing various harmful gases generated from cement, and can improve abrasion resistance, chemical resistance and surface strength. It is to provide an eco-friendly cosmetic additive including a plant additive that can promote the health of constructors and users and create a pleasant environment, and cement and mortar for plastering using the same.

또한, 본 발명은 인체 건강에 유익한 식물성 첨가제를 이용하여 미장용 첨가제를 제조함으로써, 인체에 무해할뿐만 아니라 친환경 건축 재료로서 널리 사용될 수 있고 친환경적인 주거공간을 형성할 수 있는 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈을 제공하는데 있다. In addition, the present invention is an eco-friendly containing plant additive that can be widely used as an eco-friendly building material as well as harmless to the human body by manufacturing a cosmetic additive using a plant additive beneficial to human health and can form an eco-friendly residential space. To provide a cosmetic additive, a plastering cement and mortar using the same.

또한, 본 발명은 방동제를 포함하여 제조된 미장용 몰탈을 타설함으로써, 0℃ 이하의 가혹한 조건에서도 동결안정성을 가지면서 우수한 조강성 및 시공성을 유지할 수 있는 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈을 제공하는데 있다. In addition, the present invention is an eco-friendly cosmetic additive containing a vegetable additive that can maintain excellent roughness and workability while having freeze stability even under severe conditions of 0 ° C. or less by pouring a cosmetic mortar prepared including an antifreeze agent, An object of the present invention is to provide cement and mortar for plastering using the same.

본 발명이 해결하고자 하는 다양한 과제들은 이상에서 언급한 과제들에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다. Various problems to be solved by the present invention are not limited to the above-mentioned problems, and other problems not mentioned will be clearly understood by those skilled in the art from the following description.

본 발명에 따른 식물성 첨가제를 포함하는 친환경 미장용 첨가제는 석고, 활성탄, 식물성 첨가제 및 흡착탈취제를 포함하되, 상기 석고는 이수석고 또는 무수석고가 사용되고, 상기 활성탄은 대나무, 참나무 및 소나무를 각각 500 내지 1000mm의 길이로 절단 가공하는 단계, 상기 절단 가공된 대나무, 참나무 및 소나무를 각각 1000 내지 1500℃의 온도로 탄화시키는 활성탄을 제조하는 단계, 상기 탄화된 활성탄을 각각 선별, 분리하는 단계, 및 상기 분리한 활성탄을 각각 분쇄하여 50 내지 250메쉬(mesh) 범위의 입경으로 선별하는 단계를 포함하여 제조되며, 상기 식물성 첨가제는 은행잎 분말 및 쑥 분말이 혼합되어 제조되며, 상기 은행잎 분말 및 쑥 분말은 60:40내지 40:60의 중량비로 혼합되고, 상기 흡착탈취제는 규조토, 제올라이트, 흡착제 및 겔 라이트를 혼합하여 제조된다. The eco-friendly cosmetic additive containing the vegetable additive according to the present invention includes gypsum, activated carbon, a vegetable additive and an adsorption deodorant, wherein the gypsum dihydrate gypsum or anhydrite is used, and the activated carbon is bamboo, oak and pine from 500 to 500, respectively. Cutting to a length of 1000 mm, preparing activated carbon for carbonizing the cut-processed bamboo, oak, and pine at a temperature of 1000 to 1500 ° C., selecting and separating the carbonized activated carbon, respectively, and the separation It is prepared by pulverizing each activated carbon and selecting a particle size in the range of 50 to 250 mesh, wherein the vegetable additive is prepared by mixing ginkgo leaf powder and mugwort powder, wherein the ginkgo leaf powder and mugwort powder are 60: 40 to 40: mixed in a weight ratio of 60, the adsorption deodorant is prepared by mixing diatomaceous earth, zeolite, adsorbent and gelite.

상기 석고는 40 내지 80 중량부가 사용되고, 상기 활성탄은 5 내지 35 중량부가 사용되고, 입경이 50 내지 250메쉬(mesh) 범위를 가지는 분말로 구성되며, 상기 식물성 첨가제는 2 내지 10 중량부가 사용되고, 상기 흡착탈취제는 2 내지 35 중량부가 사용될 수 있다. The gypsum is used in 40 to 80 parts by weight, the activated carbon is used in 5 to 35 parts by weight, and is composed of a powder having a particle size in the range of 50 to 250 mesh, and 2 to 10 parts by weight of the vegetable additive is used, and the adsorption 2 to 35 parts by weight of the deodorant may be used.

상기 활성탄은 경도 90 질량분율% 이상, 충전밀도 045 내지 052g/ml, 비표면적 1,000 내지 1,100m 2/g, 세공분포는 세공직경이 3Å 내지 12Å, 요오드 흡착력 1,000mg/g 이상, 세공용적 0501ml/g, pH 10~11, 페놀 흡착력 18ml/g, M·B탈색력 150ml/g 이상인 것이 사용되고, 상기 식물성 첨가제는 편백나무 분말, 목초액, 흑운모 분말 및 소금의 혼합물로 구성되는 추가 첨가제를 더 포함하되, 상기 추가 첨가제는 상기 은행잎 분말 및 쑥 분말 전체 100 중량부를 기준으로 하여 20 내지 50 중량부의 중량비율로 포함되며, 상기 흡착탈취제는 상기 규조토, 제올라이트, 흡착제 및 겔 라이트가 각각 규조토 10 내지 30 중량부, 제올라이트 25 내지 45 중량부, 흡착제 25내지 45 중량부, 겔 라이트 10 내지 25 중량부의 중량비율로 혼합되어 제조될 수 있다.The activated carbon has a hardness of 90% by mass or more, a packing density of 045 to 052 g/ml, a specific surface area of 1,000 to 1,100 m 2/g, and the pore distribution has a pore diameter of 3 Å to 12 Å, an iodine adsorption power of 1,000 mg/g or more, a pore volume of 0501 ml/ g, pH 10-11, phenol adsorption power 18ml/g, M B discoloration power 150ml/g or more is used, and the vegetable additive further comprises an additional additive consisting of a mixture of cypress powder, wood vinegar, biotite powder and salt , The additional additive is included in a weight ratio of 20 to 50 parts by weight based on 100 parts by weight of the total ginkgo leaf powder and mugwort powder, and the adsorption deodorant contains 10 to 30 parts by weight of the diatomaceous earth, zeolite, adsorbent and gelite, respectively. , 25 to 45 parts by weight of zeolite, 25 to 45 parts by weight of adsorbent, and 10 to 25 parts by weight of gelite can be prepared by mixing.

상기 추가 첨가제를 구성하는 편백나무 분말, 목초액, 흑운모 분말 및 소금은 각각 편백나무 분말 10 내지 20 중량부, 목초액 5 내지 15 중량부, 흑운모 분말 5 내지 10 중량부, 소금 10 내지 15 중량부의 중량비율로 혼합되어 사용되고, 상기 흑운모는 분말화되기 전에 1300 내지 1500℃의 범위 내에서 열처리를 진행한 후 사용되며, 상기 소금은 1000℃ 내지 1200℃에서 8 내지 10시간 동안 가열하여 구운 천일염이 사용될 수 있다. Cypress powder, wood vinegar, biotite powder and salt constituting the additional additive are each 10 to 20 parts by weight of cypress powder, 5 to 15 parts by weight of wood vinegar, 5 to 10 parts by weight of biotite powder, and 10 to 15 parts by weight of salt. The biotite is used after heat treatment in the range of 1300 to 1500 ° C before being powdered, and the salt is heated and baked at 1000 ° C to 1200 ° C for 8 to 10 hours. .

또한, 본 발명에 따른 미장용 첨가제를 이용한 미장용 시멘트는 미장용 첨가제 및 시멘트가 혼합되어 제조되되, 상기 미장용 첨가제는, 석고, 활성탄, 식물성 첨가제 및 흡착탈취제를 포함하되, 상기 석고는 이수석고 또는 무수석고가 사용되고, 상기 활성탄은 대나무, 참나무 및 소나무를 각각 500 내지 1000mm의 길이로 절단 가공하는 단계, 상기 절단 가공된 대나무, 참나무 및 소나무를 각각 1000 내지 1500℃의 온도로 탄화시키는 활성탄을 제조하는 단계, 상기 탄화된 활성탄을 각각 선별, 분리하는 단계, 및 상기 분리한 활성탄을 각각 분쇄하여 50 내지 250메쉬(mesh) 범위의 입경으로 선별하는 단계를 포함하여 제조되며, 상기 식물성 첨가제는 은행잎 분말 및 쑥 분말이 혼합되어 제조되며, 상기 은행잎 분말 및 쑥 분말은 60:40 내지 40:60의 중량비로 혼합되고, 상기 흡착탈취제는 규조토, 제올라이트, 흡착제 및 겔 라이트를 혼합하여 제조되며, 상기 시멘트는 고로슬래그 시멘트 In addition, the plastering cement using the plastering additive according to the present invention is prepared by mixing a plastering additive and cement, wherein the plastering additive includes gypsum, activated carbon, a vegetable additive and an adsorption deodorant, wherein the gypsum is dihydrate gypsum Or anhydrite is used, and the activated carbon is prepared by cutting and processing bamboo, oak, and pine to a length of 500 to 1000 mm, respectively, carbonizing the cut-processed bamboo, oak and pine at a temperature of 1000 to 1500 ° C. It is prepared including the steps of selecting and separating the carbonized activated carbon, respectively, and grinding the separated activated carbon, respectively, and selecting a particle size in the range of 50 to 250 mesh, wherein the vegetable additive is Ginkgo biloba powder and mugwort powder is mixed, the ginkgo leaf powder and mugwort powder are mixed in a weight ratio of 60:40 to 40:60, and the adsorption deodorant is prepared by mixing diatomaceous earth, zeolite, adsorbent and gelite, and the cement is Blast Furnace Slag Cement

가 사용되고, 상기 미장용 첨가제는 고로슬래그 시멘트 전체 100 중량부를 기준으로 하여 40 내지 60 중량부가 포함된다.is used, and the cosmetic additive is included in an amount of 40 to 60 parts by weight based on 100 parts by weight of the total blast furnace slag cement.

상기 석고는 40 내지 80 중량부가 사용되고, 상기 활성탄은 5 내지 35 중량부가 사용되고, 입경이 50 내지 250메쉬(mesh) 범위를 가지는 분말로 구성되며, 상기 식물성 첨가제는 2 내지 10 중량부가 사용되고, 상기 흡착탈취제는 2 내지 35 중량부가 사용되며, 상기 활성탄은 경도 90 질량분율% 이상, 충전밀도 045 내지 052g/ml, 비표면적 1,000 내지 1,100m 2/g, 세공분포는 세공직경이 3Å 내지 12Å, 요오드 흡착력 1,000mg/g 이상, 세공용적 0501ml/g, pH 10~11, 페놀 흡착력 18ml/g, M·B탈색력 150ml/g 이상인 것이 사용되고, 상기 식물성 첨가제는 편백나무 분말, 목초액, 흑운모 분말 및 소금의 혼합물로 구성되는 추가 첨가제를 더 포함하되, 상기 추가 첨가제는 상기 은행잎 분말 및 쑥 분말 전체 100 중량부를 기준으로 하여 20 내지 50 중량부의 중량비율로 포함되며, 상기 흡착탈취제는 상기 규조토, 제올라이트, 흡착제 및 겔 라이트가 각각 규조토 10 내지 30 중량부, 제 The gypsum is used in 40 to 80 parts by weight, the activated carbon is used in 5 to 35 parts by weight, and is composed of a powder having a particle size in the range of 50 to 250 mesh, and 2 to 10 parts by weight of the vegetable additive is used, and the adsorption 2 to 35 parts by weight of the deodorant is used, the activated carbon has a hardness of 90 mass fraction% or more, a packing density of 045 to 052 g/ml, a specific surface area of 1,000 to 1,100 m 2/g, and the pore distribution has a pore diameter of 3 Å to 12 Å, iodine adsorption power 1,000mg/g or more, pore volume 0501ml/g, pH 10~11, phenol adsorption power 18ml/g, M B discoloration power 150ml/g or more are used, and the vegetable additive is cypress powder, wood vinegar, biotite powder and salt. Further comprising an additional additive composed of a mixture, wherein the additional additive is included in a weight ratio of 20 to 50 parts by weight based on 100 parts by weight of the total ginkgo leaf powder and mugwort powder, and the adsorption deodorant is the diatomaceous earth, zeolite, adsorbent and Gelite is each 10 to 30 parts by weight of diatomaceous earth,

올라이트 25 내지 45 중량부, 흡착제 25 내지 45 중량부, 겔 라이트 10 내지 25 중량부의 중량비율로 혼합되어 제조된다.It is prepared by mixing 25 to 45 parts by weight of olite, 25 to 45 parts by weight of adsorbent, and 10 to 25 parts by weight of gelite.

상기 추가 첨가제를 구성하는 편백나무 분말, 목초액, 흑운모 분말 및 소금은 각각 편백나무 분말 10 내지 20중량부, 목초액 5 내지 15 중량부, 흑운모 분말 5 내지 10 중량부, 소금 10 내지 15 중량부의 중량비율로 혼합되어 사용되고, 상기 흑운모는 분말화되기 전에 1300 내지 1500℃의 범위 내에서 열처리를 진행한 후 사용되며, 상기 소금은 1000℃ 내지 1200℃에서 8 내지 10시간 동안 가열하여 구운 천일염이 사용될 수 있다. Cypress powder, wood vinegar, biotite powder and salt constituting the additional additive are each 10 to 20 parts by weight of cypress powder, 5 to 15 parts by weight of wood vinegar, 5 to 10 parts by weight of biotite powder, and 10 to 15 parts by weight of salt. The biotite is used after heat treatment in the range of 1300 to 1500 ° C before being powdered, and the salt is heated and baked at 1000 ° C to 1200 ° C for 8 to 10 hours. .

또한, 본 발명에 따른 미장용 첨가제를 이용한 미장용 몰탈은 미장용 첨가제를 포함하는 시멘트, 규사, 셀룰로스 파이버, EVA 폴리머, 무기결합재, 섬유보강재, 방동제, 감수제, 증점제, 방수제 및 배합수를 포함하여 제조 In addition, the cosmetic mortar using the cosmetic additive according to the present invention includes cement, silica sand, cellulose fiber, EVA polymer, inorganic binder, fiber reinforcement, antifreeze, water reducing agent, thickener, waterproofing agent, and water containing the cosmetic additive. manufactured by

되되, 상기 미장용 첨가제를 포함하는 시멘트는 60 내지 80 중량부가 포함되고, 상기 규사는 입도분포가 50 내지 150메쉬(mesh)를 가지고, 40 내지 70 중량부 포함되며, 상기 셀룰로스 파이버는 천연 목재에서 추출된 파이버로 3 내지 8 중량부가 포함되고, 상기 EVA 폴리머는 5 내지 10 중량부 포함되며, 상기 무기결합재는 10 내지 15 중량부 포함되고, 상기 섬유보강재는 자연마섬유가 사용되고, 상기 자연마섬유는 05 내지 3 중량부 포함되며, 상기 방동제는 3 내지 7 중량부가 포함되고, 상기 감수제는 1 내지 3 중량부가 포함되되, 상기 감수제로는 나프탈렌설폰산염계, 멜라민설폰산염계 및 폴리카르본산염계 중에서 선택된 1종 이상의 물질이 사용되며, 상기 증점제는 03 내지 1 중량부가 포함되고, 상기 방수제는 분말형 방수제로 2 내지 5 중량부가 포함되며, 상기 배합수는 60 내지 80 중량부가 포함되고, 상기 시멘트는 고로슬래그 시멘트가 사용되되, 상기 미장용 첨가제는 고However, 60 to 80 parts by weight of the cement including the cosmetic additive is included, the silica sand has a particle size distribution of 50 to 150 mesh, and 40 to 70 parts by weight is included, and the cellulose fiber is from natural wood. 3 to 8 parts by weight of the extracted fiber is included, 5 to 10 parts by weight of the EVA polymer is included, 10 to 15 parts by weight of the inorganic binder is included, and natural hemp fiber is used as the fiber reinforcement material, and the natural hemp fiber is included. is included in 05 to 3 parts by weight, the antifreeze agent is included in 3 to 7 parts by weight, the water reducing agent is included in 1 to 3 parts by weight, and the water reducing agent is naphthalenesulfonate-based, melaminesulfonate-based and polycarboxylate. At least one material selected from the group consisting of 03 to 1 parts by weight of the thickener is used, the waterproofing agent is included in 2 to 5 parts by weight as a powder-type waterproofing agent, the mixing water is included in 60 to 80 parts by weight, and For cement, blast furnace slag cement is used, and the cosmetic additive is

로슬래그 시멘트 전체 100 중량부를 기준으로 하여 40 내지 60 중량부의 중량비율로 혼합되어 사용되고, 상기 EVA 폴리머는 Tg = 0℃ 내지 -10℃, 고형분 15~40질량%의 시멘트 혼화형 EVA 폴리머가 사용되며, 상기 무기결합재는 고로 슬래그와 플라이 애시 및 실리카흄의 혼합물이 사용되되, 상기 무기결합재는 고로 슬래그 50 내지 70 중량부, 플라이 애시 30 내지 50 중량부, 실리카흄 20 내지 30 중량부의 중량 비율로 혼합되어 제조되고, 상기 실리카흄의 밀도는 20 내지 22g/cm 3이고, 비표면적 150,000 내지 200,000cm 2/g의 분말도를 가지며, 평균 입경은 02 내지 05㎛이며, 상기 방동제는 정제수, 질산칼슘 및 포타슘포메이트(PF)를 혼합하여 제조되되, 상기 방동제는 정제수가 55 내지 65 중량부, 질산칼슘이 20 내지 30 중량부, 포타슘포메이트(PF)가 3 내지 8 중량부의 중량비율로 혼합되어 제조된다.Based on 100 parts by weight of the total roast slag cement, it is mixed and used in a weight ratio of 40 to 60 parts by weight, and the EVA polymer is Tg = 0°C to -10°C, and a cement-mixable EVA polymer having a solid content of 15 to 40% by weight is used. , The inorganic binder is a mixture of blast furnace slag, fly ash and silica fume is used, and the inorganic binder is prepared by mixing 50 to 70 parts by weight of blast furnace slag, 30 to 50 parts by weight of fly ash, and 20 to 30 parts by weight of silica fume. and the silica fume has a density of 20 to 22 g/cm 3 , a specific surface area of 150,000 to 200,000 cm 2 / g, and an average particle diameter of 02 to 05 μm, and the antifreeze agent is purified water, calcium nitrate and potassium po It is prepared by mixing mate (PF), and the antifreeze agent is prepared by mixing 55 to 65 parts by weight of purified water, 20 to 30 parts by weight of calcium nitrate, and 3 to 8 parts by weight of potassium formate (PF) .

상기 미장용 첨가제는, 석고, 활성탄, 식물성 첨가제 및 흡착탈취제를 포함하되, 상기 석고는 이수석고 또는 무수석고가 사용되고, 상기 활성탄은 대나무, 참나무 및 소나무를 각각 500 내지 1000mm의 길이로 절단 가공하는 단계, 상기 절단 가공된 대나무, 참나무 및 소나무를 각각 1000 내지 1500℃의 온도로 탄화시키는 활성탄을 제조하는 단계, 상기 탄화된 활성탄을 각각 선별, 분리하는 단계, 및 상기 분리한 활성탄을 각각 분쇄하여 50 내지 250메쉬(mesh) 범위의 입경으로 선별하는 단계를 포함하여 제조되며, 상기 식물성 첨가제는 은행잎 분말 및 쑥 분말이 혼합되어 제조되며, 상기 은행잎 분말 및 쑥 분말은 60:40 내지 40:60의 중량비로 혼합되고, 상기 흡착탈취제는 규조토, 제올라이트, 흡착제 및 겔 라이트를 혼합하여 제조되며, 상기 시멘트는 고로슬래그 시멘트가 사용되고, 상기 미장용 첨가제는 고로슬래그 시멘트 전체 100 중량부를 기준으로 하여 40 내지 60 중량부가 포함되며, 상기 석고는 40 내지 80 중량부가 사용되고, 상기 활성탄은 5 내지 35 중량부가 사용되고, 입경이 50내지 250메쉬(mesh) 범위를 가지는 분말로 구성되며, 상기 식물성 첨가제는 2 내지 10 중량부가 사용되고, 상기 흡착탈취제는 2 내지 35 중량부가 사용되며, 상기 활성탄은 경도 90 질량분율% 이상, 충전밀도 045 내지 052g/ml, 비표면적 1,000 내지 1,100m 2/g, 세공분포는 세공직경이 3Å 내지 12Å, 요오드 흡착력 1,000mg/g 이상, 세공용적 0501ml/g, pH 10~11, 페놀 흡착력 18ml/g, M·B탈색력 150ml/g 이상인 것이 사용되고, 상기 식물성 첨가제는 편백나무 분말, 목초액, 흑운모 분말 및 소금의 혼합물로 구성되는 추가 첨가제를 더 포함하되, The cosmetic additive includes gypsum, activated carbon, a vegetable additive and an adsorption deodorant, wherein the gypsum is used gypsum dihydrate or anhydrite, and the activated carbon is bamboo, oak, and pine cutting and processing to a length of 500 to 1000 mm, respectively. , preparing activated carbon for carbonizing the cut-processed bamboo, oak, and pine at a temperature of 1000 to 1500 ° C, respectively, selecting and separating the carbonized activated carbon, and pulverizing the separated activated carbon, respectively, to 50 to It is prepared including the step of screening to a particle size in the range of 250 mesh, and the vegetable additive is prepared by mixing ginkgo leaf powder and mugwort powder, and the ginkgo leaf powder and mugwort powder are 60:40 to 40:60 in a weight ratio of 60:40 to 40:60. is mixed, and the adsorption deodorant is prepared by mixing diatomaceous earth, zeolite, adsorbent and gelite, the cement is blast furnace slag cement, and the plaster additive is 40 to 60 parts by weight based on 100 parts by weight of the total blast furnace slag cement Included, the gypsum is used in 40 to 80 parts by weight, the activated carbon is used in 5 to 35 parts by weight, and is composed of a powder having a particle size in the range of 50 to 250 mesh, and the vegetable additive is used in 2 to 10 parts by weight , The adsorption deodorant is used in 2 to 35 parts by weight, the activated carbon has a hardness of 90 mass fraction% or more, a packing density of 045 to 052 g/ml, a specific surface area of 1,000 to 1,100 m 2/g, and the pore distribution has a pore diameter of 3 Å to 12 Å , iodine adsorption power of 1,000 mg/g or more, pore volume 0501 ml/g, pH 10-11, phenol adsorption power of 18 ml/g, M B discoloration power of 150 ml/g or more, and the vegetable additives are cypress powder, wood vinegar, biotite powder And further comprising an additional additive consisting of a mixture of salt,

상기 추가 첨가제는 상기 은행잎 분말 및 쑥 분말 전체 100 중량부를 기준으로 하여 20 내지 50 중량부의 중량비율로 포함되며, 상기 흡착탈취제는 상기 규조토, 제올라이트, 흡착제 및 겔 라이트가 각각 규조토 10 내지 30 중량부, 제올라이트 25 내지 45 중량부, 흡착제 25 내지 45 중량부, 겔 라이트 10 내지 25 중량부의 중량비율로 혼합되어 제조되고, 상기 추가 첨가제를 구성하는 편백나무 분말, 목초액, 흑운모 분말 및 소금은 각각 편백나무 분말 10 내지 20 중량부, 목초액 5 내지 15 중량부, 흑운모 분말 5 내지 10 중량부, 소금 10 내지 15 중량부의 중량비율로 혼합되어 사용되고, 상기 흑운모는 분말화되기 전에 1300 내지 1500℃의 범위 내에서 열처리를 진행한 후 사용되며, 상기 소금은 1000℃ 내지 1200℃에서 8 내지 10시간 동안 가열하여 구운 천일염이 사용될 수 있다.The additional additive is included in a weight ratio of 20 to 50 parts by weight based on 100 parts by weight of the total ginkgo leaf powder and mugwort powder, and the adsorption and deodorizing agent contains 10 to 30 parts by weight of each of the diatomaceous earth, zeolite, adsorbent and gelite, It is prepared by mixing 25 to 45 parts by weight of zeolite, 25 to 45 parts by weight of adsorbent, and 10 to 25 parts by weight of gelite, and each of cypress powder, wood vinegar, biotite powder and salt constituting the additional additive is cypress powder. 10 to 20 parts by weight, 5 to 15 parts by weight of wood vinegar, 5 to 10 parts by weight of biotite powder, and 10 to 15 parts by weight of salt are mixed and used in a weight ratio, and the biotite is heat-treated within the range of 1300 to 1500° C. before being powdered. It is used after the process, and the salt may be heated and baked at 1000°C to 1200°C for 8 to 10 hours.

기타 실시 예들의 구체적인 사항들은 상세한 설명에 포함되어 있다. Specific details of other embodiments are included in the detailed description.

본 발명에 따른 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈은 석고, 활성탄, 천연광석 분말 및 흡착탈취제를 혼합하여 수축 절감 성능을 가지는 미장용 첨가제를 제조함으로써, 양생 초기 응결시 상기 석고에 의해 수분이 급격하게 증발되어 응결속도를 단축할 수 있고, 응결 후 건조시에는 활성탄 또는 흡착탈취제의 지속적인 수분 공급에 의해 건조시간을 지연시켜 급격한 건조에 의한 건축물의 바닥이나 벽면의 균열을 방지할 수 있다. An eco-friendly cosmetic additive comprising a vegetable additive according to the present invention, plastering cement and mortar using the same is mixed with gypsum, activated carbon, natural ore powder and adsorption deodorant to produce a cosmetic additive having shrinkage reduction performance, thereby initial curing When the moisture is rapidly evaporated by the gypsum, the setting speed can be shortened, and when drying after setting, the drying time is delayed by continuous moisture supply of activated carbon or adsorption deodorant, so that the floor or wall surface of the building is cracked due to rapid drying. can prevent

또한, 본 발명에 따른 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈은 시멘트에서 발생하는 다양한 유해가스를 흡착 제거할 수 있는 미장용 참가제를 제조함으로써, 경화시간을 조절하여 원하는 압축강도를 얻을 수 있고, 내마모성, 내화학성 및 표면 강도를 증진시킬 수 있으며, 시공자와 사용자의 건강을 도모하고 쾌적한 환경을 조성할 수 있다. In addition, the eco-friendly plastering additive containing the vegetable additive according to the present invention, the plastering cement and mortar using the same are prepared by preparing a plastering agent capable of adsorbing and removing various harmful gases generated from the cement, thereby controlling the curing time. Desired compressive strength can be obtained, abrasion resistance, chemical resistance and surface strength can be improved, and the health of the installer and user can be promoted and a pleasant environment can be created.

또한, 본 발명에 따른 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈은 인체 건강에 유익한 식물성 첨가제를 이용하여 미장용 첨가제를 제조함으로써, 인체에 무해할 뿐만 아니라 친환경 건축 재료로서 널리 사용될 수 있고 친환경적인 주거공간을 형성할 수 있다. In addition, the eco-friendly cosmetic additive containing the vegetable additive according to the present invention, and the cosmetic cement and mortar using the same are harmless to the human body as well as an eco-friendly building material by manufacturing the cosmetic additive using a vegetable additive beneficial to human health. It can be widely used and can form an eco-friendly residential space.

또한, 본 발명에 따른 식물성 첨가제를 포함하는 친환경 미장용 첨가제, 이를 이용한 미장용 시멘트 및 몰탈은 방동제를 포함하여 제조된 미장용 몰탈을 타설함으로써, 0℃ 이하의 가혹한 조건에서도 동결안정성을 가지면서 우수한 조강성 및 시공성을 유지할 수 있다. In addition, the eco-friendly cosmetic additive containing the vegetable additive according to the present invention, the plastering cement and mortar using the same is poured by pouring the cosmetic mortar prepared including the antifreeze agent, so that it has freeze stability even in harsh conditions of 0 ° C. or less. Excellent roughness and workability can be maintained.

본 발명의 기술적 사상의 실시예는, 구체적으로 언급되지 않은 다양한 효과를 제공할 수 있다는 것이 충분히 이해될 수 있을 것이다. It will be fully understood that embodiments of the technical idea of the present invention may provide various effects not specifically mentioned.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 상세하게 후술되어 있는 실시예를 참조하면 명확해질 것이다. 그러나 본 발명은 여기서 설명되는 실시예들에 한정되지 않고 다른 형태로 구체화될 수도 있다. 오히려, 여기서 소개되는 실시예들은 개시된 내용이 철저하고 완전해질 수 있도록 그리고 당업자에게 본 발명의 사상이 충분히 전달될 수 있도록 하기 위해 제공되는 것이다. Advantages and features of the present invention, and a method of achieving them, will become apparent with reference to the embodiments described below in detail. However, the present invention is not limited to the embodiments described herein and may be embodied in other forms. Rather, the embodiments introduced herein are provided so that the disclosed subject matter may be thorough and complete, and that the spirit of the present invention may be sufficiently conveyed to those skilled in the art.

본 출원에서 사용한 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. The terms used in the present application are only used to describe specific embodiments, and are not intended to limit the present invention. The singular expression includes the plural expression unless the context clearly dictates otherwise.

다르게 정의되지 않는 한, 기술적이거나 과학적인 용어를 포함해서 여기서 사용되는 모든 용어들은 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 일반적으로 이해되는 것과 동일한 의미가 있다. 일반적으로 사용되는 사전에 정의되어 있는 것과 같은 용어들은 관련 기술의 문맥상 가지는 의미와 일치하는 의미가 있는 것으로 해석되어야 하며, 본 출원에서 명백하게 정의하지 않는 한, 이상적이거나 과도하게 형식적인 의미로 해석되지 않는다. Unless defined otherwise, all terms used herein, including technical or scientific terms, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Terms such as those defined in a commonly used dictionary should be interpreted as having a meaning consistent with the meaning in the context of the related art, and should not be interpreted in an ideal or excessively formal meaning unless explicitly defined in the present application. does not

이하, 본 발명에 따른 식물성 첨가제를 포함하는 친환경 미장용 첨가제에 대하여 상세하게 설명하기로 한다. Hereinafter, the eco-friendly cosmetic additive including the vegetable additive according to the present invention will be described in detail.

본 발명에 따른 식물성 첨가제를 포함하는 친환경 미장용 첨가제는 석고, 활성탄, 식물성 첨가제 및 흡착탈취제를 포함한다. The eco-friendly cosmetic additive containing the vegetable additive according to the present invention includes gypsum, activated carbon, vegetable additive and adsorption deodorant.

상기 석고는 단사정계(單斜晶系)의 광물로, 화학성분은 CaSO4·2H2O이며, 능판상(菱板狀) 또는 주상 결정을 이루는 것으로, 본 발명에서 상기 석고는 무수석고, 이수석고, 반수석고 등 어떠한 것도 사용 가능한데, 이수석고가 The gypsum is a monoclinic mineral, the chemical component is CaSO4·2H2O, and forms ridge plate or columnar crystals, and in the present invention, the gypsum is anhydrite, dihydrate gypsum, and hemihydrate. Anything such as gypsum can be used, but dihydrate gypsum

무수석고에 비해 초기 응결시간이 길어 하절기에 유리하기 때문에 동절기에는 무수석고를 사용하고 하절기에는 이수석고를 사용하는 것이 바람직하다.Since the initial setting time is longer than that of anhydrite, which is advantageous in summer, it is preferable to use anhydrite in winter and dihydrate in summer.

상기 석고는 수화반응에 의해 발열이 이루어짐과 아울러, 팽창되면서 강도를 강화시키는 것으로, 본 발명에서 상기 석고는 40 내지 80 중량부가 사용될 수 있다. 상기 석고가 40 중량부 미만으로 포함되는 경우에는 팽창 정도가 낮고 수분증발시간이 오래 걸리며, 응결 후 건조가 급속하게 진행되어 균열이 발생할 수 있으며, 80 중량부를 초과하여 포함되는 경우에는 균열이 발생하여 강도가 저하될 수 있다. The gypsum generates heat by the hydration reaction and strengthens the strength while expanding, and in the present invention, 40 to 80 parts by weight of the gypsum may be used. When the gypsum is included in less than 40 parts by weight, the degree of expansion is low and the moisture evaporation time is long, and after setting, drying rapidly proceeds and cracks may occur, and when it contains more than 80 parts by weight, cracks occur. strength may be reduced.

상기 활성탄은 미세세공이 발달된 탄소집합체로서, 활성화과정에 의해 내부 표면적을 변화시킬 수 있으며, 내부의 탄소 원자 관능 기에 의해 주위 액체 또는 기체와 흡착이 이루어지는 흡수성과 흡착성이 우수한 성질을 갖는다. The activated carbon is a carbon aggregate with micropores developed, and the internal surface area can be changed by the activation process, and has excellent absorbency and adsorption properties through which it is adsorbed with a surrounding liquid or gas by an internal carbon atom functional group.

본 발명에서 상기 활성탄은 시멘트나 석고에서 배출되는 유해물질의 흡착제거 효과도 구현하며, 몰탈 제조시 흡습이 이루어지고 미장작업이 이루어진 몰탈의 응결 후 건조과정에서는 흡수한 수분을 서서히 배출해 건조시간을 증대시켜 급격한 건조에 의한 균열발생을 억제할 수 있다. In the present invention, the activated carbon also implements the effect of adsorption and removal of harmful substances discharged from cement or gypsum, and increases the drying time by gradually discharging the absorbed moisture during the drying process after the mortar is absorbed and plastered during the production of mortar. It can suppress the occurrence of cracks due to rapid drying.

상기 활성탄은 5 내지 35 중량부가 사용되고, 상기 활성탄 분말은 입경이 50 내지 250메쉬(mesh) 범위를 가질 수 있다. 본 발명에서 상기 활성탄이 상기한 하한 미만으로 포함되는 경우에는 양생시 수분배출에 의한 건조지연 효과와 유해물질 제거효과가 낮아지고, 상기한 상한을 초과하여 포함되는 경우에는 건조지연 효과의 증진 정도가 미미할 수 있다. 5 to 35 parts by weight of the activated carbon is used, and the activated carbon powder may have a particle size in the range of 50 to 250 mesh. In the present invention, when the activated carbon is included below the lower limit, the drying delay effect and the harmful substance removal effect due to water discharge during curing are lowered, and when the activated carbon is included in excess of the upper limit, the degree of enhancement of the drying delay effect is can be insignificant.

또한, 본 발명에서 상기 활성탄은 분말 형태로 사용될 수 있는데, 이러한 분말 형태의 활성탄은 다공성인 활성탄 자체의 흡착력을 보다 증진시킬 뿐만 아니라, 활성탄이 미세한 분말일수록 입자와 입자 사이가 치밀하여 부착력이 증대되고 산화방지 및 소수성의 기능을 부여할 수 있다. In addition, in the present invention, the activated carbon may be used in the form of a powder, and the activated carbon in powder form not only further enhances the adsorption power of the porous activated carbon itself, but the finer the activated carbon is, the denser the particles are between the particles, so that the adhesion is increased. Anti-oxidation and hydrophobic functions can be imparted.

본 발명에서 상기 활성탄 분말은 몸 안의 독소를 몰아내는 힘이 강하므로 체내의 독성이 누적되어 발생하는 각종 성인병이나 피부염 알레르기 증상에 탁월한 효능이 있는데, 상기 활성탄 분말은 대나무, 참나무 및 소나무를 각각 500 내지 1000mm의 길이로 절단 가공하는 단계, 상기 절단 가공된 대나무, 참나무 및 소나무를 각각 1000내지 1500℃의 온도로 탄화시키는 활성탄을 제조하는 단계, 상기 탄화된 활성탄을 각각 선별, 분리하는 단계, 상기 분리한 활성탄을 각각 분쇄하여 50 내지 250메쉬(mesh) 범위의 입경으로 선별하는 단계로 제조될 수 있다. In the present invention, the activated carbon powder has an excellent effect on various adult diseases or dermatitis allergy symptoms caused by the accumulation of toxins in the body because the activated carbon powder has a strong power to drive out toxins in the body. Cutting to a length of 1000 mm, preparing activated carbon for carbonizing the cut-processed bamboo, oak and pine at a temperature of 1000 to 1500 ° C, respectively, selecting and separating the carbonized activated carbon, respectively, the separated It may be prepared by pulverizing the activated carbon, respectively, and selecting the particle size in the range of 50 to 250 mesh (mesh).

또한, 본 발명에서 상기 활성탄은 경도 90 질량분율% 이상, 충전밀도 045 내지 052g/[0064] ml, 비표면적 1,000 내지1,100m 2/g, 세공분포는 세공직경이 3Å 내지 12Å, 요오드 흡착력 1,000mg/g 이상, 세공용적 0501ml/g, pH10~11, 페놀 흡착력 18ml/g, M·B탈색력 150ml/g 이상인 것이 사용될 수 있다. In addition, in the present invention, the activated carbon has a hardness of 90 mass fraction% or more, a packing density of 045 to 052 g/ml, a specific surface area of 1,000 to 1,100 m 2/g, and the pore distribution has a pore diameter of 3 Å to 12 Å, iodine adsorption power of 1,000 mg /g or more, pore volume 0501ml/g, pH10-11, phenol adsorption power 18ml/g, M B discoloration power 150ml/g or more can be used.

상기 식물성 첨가제는 인체 건강에 유익한 효과를 제공하고 천연 항균제 기능을 수행할 수 있는 물질로, 본 발명에서 상기 식물성 첨가제는 2 내지 10 중량부가 포함되고 은행잎 분말 및 쑥 분말을 혼합하여 제조될 수 있는데, 상기 은행잎 분말 및 쑥 분말은 60:40 내지 40:60의 중량비로 혼합될 수 있다. The plant additive is a material that provides a beneficial effect on human health and can perform a natural antibacterial function. In the present invention, the plant additive contains 2 to 10 parts by weight and can be prepared by mixing ginkgo leaf powder and mugwort powder, The ginkgo leaf powder and mugwort powder may be mixed in a weight ratio of 60:40 to 40:60.

상기 은행잎 분말은 항균 성분인 플라보노이드 성분을 포함하고 있는데, 상기 플라보노이드 성분은 항균성이 있어 곰팡이 예방과 해충 접근방지의 효과를 가질 수 있다. 또한, 상기 은행잎 분말에는 징코라이드와 테포닌, 비라미드 등의 성분이 포함되어 있어 혈전용해 작용과 혈소판 질환, 고혈압, 당뇨 예방 및 치료에 특효가 있다. The ginkgo leaf powder contains a flavonoid component that is an antibacterial component, and the flavonoid component has antibacterial properties, so it can have the effect of preventing mold and pest access. In addition, the ginkgo leaf powder contains ingredients such as ginger, teponin, and viramide, and thus has a specific effect in preventing and treating thrombolytic action, platelet disease, hypertension, and diabetes.

상기 쑥 분말은 상기 은행잎 분말과 혼합되고, 향기로운 향을 발산하여 거주자에게 심신의 안정감을 취할 수 있도록 하는데, 본 발명은 상기 쑥 분말을 포함하여 미장용 첨가제를 제조함으로써, 치네롤이 포함된 쑥향을 맡을 수 있게 되어 소화를 돕고 숙면을 취하는데 도움을 주며 머리를 맑게 해주는 효과가 있다. The mugwort powder is mixed with the ginkgo leaf powder and emits a fragrant scent so that residents can take a sense of stability in mind and body. It helps digestion, helps you get a good night's sleep, and clears your head.

본 발명에서 상기 식물성 첨가제는 상기한 은행잎 분말 및 쑥 분말 이외에도 다양한 친환경적인 추가 첨가제가 더 포함될 수 있는데, 상기 추가 첨가제는 편백나무 분말, 목초액, 흑운모 분말 및 소금으로 구성될 수 있고, 상기 추가 첨가제는 상기 은행잎 분말 및 쑥 분말 전체 100 중량부를 기준으로 하여 20 내지 50 중량부의 비율로 포함될 수 있다. In the present invention, the vegetable additive may further include various eco-friendly additional additives in addition to the ginkgo leaf powder and mugwort powder described above. The additional additives may be composed of cypress powder, wood vinegar, biotite powder and salt, and the additional additives include It may be included in a ratio of 20 to 50 parts by weight based on 100 parts by weight of the total ginkgo leaf powder and mugwort powder.

또한, 본 발명에서 상기 추가 첨가제를 구성하는 편백나무 분말, 목초액, 흑운모 분말 및 소금은 각각 편백나무분말 10 내지 20 중량부, 목초액 5 내지 15 중량부, 흑운모 분말 5 내지 10 중량부, 소금 10 내지 15 중량부의 중량비율로 혼합되어 사용될 수 있다. In addition, each of the cypress powder, wood vinegar, biotite powder and salt constituting the additional additive in the present invention is 10 to 20 parts by weight of cypress powder, 5 to 15 parts by weight of wood vinegar, 5 to 10 parts by weight of biotite powder, 10 to 10 parts by weight of salt. It can be used by mixing in a weight ratio of 15 parts by weight.

상기 편백나무 분말은 침엽수 분말로 많은 양의 피톤치드를 발산하여 인체에 무리없이 흡수될 수 있고 인체에 해로운 균들을 선택적으로 살균할 수 있다. 또한, 상기 편백나무 분말에 포함되어 있는 피톤치드 성분은 항균작용, 소취작용, 진정작용 및 스트레스 해조작용 등 수많은 기능을 수행할 수 있다. The cypress powder is a coniferous powder that emits a large amount of phytoncide and can be safely absorbed into the human body and selectively sterilizes harmful bacteria. In addition, the phytoncide component contained in the cypress tree powder can perform numerous functions, such as antibacterial action, deodorizing action, sedative action, and stress detoxifying action.

상기 목초액은 나무로 숯을 만드는 과정에서 나오는 연기를 액화시켜 채취한 뒤, 6개월 이상 숙성시켜 독성과 유해물질을 제거한 것을 말하며, 옅은 붉은색이 나고 냄새가 강하다. 상기 목초액의 채취방법은 목재를 태우다가 황백색 연기가 나면 작은 통기구만 남기고 가마 입구를 폐쇄한 후, 연기가 외부 공기와 접촉하여 자연 냉각되어 떨어지는 액체를 수집하여 채취할 수 있다. The wood vinegar refers to a product obtained by liquefying smoke from the process of making charcoal from wood and then aged for at least 6 months to remove toxic and harmful substances, and has a light red color and strong odor. In the method of collecting wood vinegar, if yellowish white smoke is emitted while burning wood, after closing the kiln entrance leaving only a small vent, the smoke can be collected by collecting the liquid that is naturally cooled by contact with the outside air.

상기 흑운모 분말은 철분(Fe), 마그네슘(Mg), 아연(Zn), 망간(Mn), 구리(Cu), 몰리브덴(Mo), 셀레늄(Se), 게르마늄(Ge), 규소(Si), 바나듐(V) 및 스트론튬(Sr) 등의 다양한 인체 필수 미네랄을 내포하는 점토성 광물로, 강한 환원력을 지닌 활성산소의 분해용도로 사용되는 생리활성 물질로 살균작용을 할 수 있다. 본 발명에서 상기 흑운모는 발포하여 분말화하여 사용하므로 분체 내부에 공기층이 형성되어 습도 조절이 가능함은 물론 탈취 효과나 곰팡이의 발생 방지 및 음이온과 원적외선 효과가 있다. The biotite powder is iron (Fe), magnesium (Mg), zinc (Zn), manganese (Mn), copper (Cu), molybdenum (Mo), selenium (Se), germanium (Ge), silicon (Si), vanadium It is a clay mineral containing various essential minerals such as (V) and strontium (Sr). It is a physiologically active substance used for decomposition of active oxygen with strong reducing power and can sterilize. In the present invention, since the biotite is foamed and powdered, an air layer is formed inside the powder to control humidity, as well as to have a deodorizing effect or prevention of mold generation, and an anion and far-infrared effect.

또한, 상기 흑운모는 분말화되기 전에 강도의 증가를 위해 1300 내지 1500℃의 범위 내에서 열처리를 진행할 수 있다. 이때, 열처리의 가열온도가 1300℃ 미만인 경우에는 흑운모가 적정 강도를 얻을 수 없고, 가열온도가 1500℃ 이상인 경우에는 견운모가 소실될 우려가 있다. In addition, the biotite may be subjected to heat treatment within the range of 1300 to 1500° C. in order to increase strength before being powdered. At this time, when the heating temperature of the heat treatment is less than 1300 ℃, biotite cannot obtain an appropriate strength, and when the heating temperature is 1500 ℃ or more, there is a fear that the sericite is lost.

상기 소금은 몰탈 조성물을 배합수와 혼합하여 경화시켰을 때 냄새를 제거하고 벌레와 같은 해충이 발생되는 것을 방지하기 위하여 사용될 수 있다. 본 발명에서 상기 소금은 1000℃ 내지 1200℃에서 8 내지 10시간 동안 가열하여 구운 천일염을 사용하는 것이 바람직하다. The salt may be used to remove odors and prevent pests such as insects from being generated when the mortar composition is mixed with mixing water and hardened. In the present invention, it is preferable to use sea salt baked by heating at 1000°C to 1200°C for 8 to 10 hours.

상기 흡착탈취제는 시멘트에서 발생하는 다양한 유해가스를 흡착 제거하여 시공자와 사용자의 건강을 도모할 수 있도록 하기 위하여 첨가되고, 본 발명에서 상기 흡착탈취제는 2 내지 35 중량부가 사용될 수 있다. The adsorption deodorant is added to adsorb and remove various harmful gases generated from cement to promote the health of the installer and the user, and in the present invention, 2 to 35 parts by weight of the adsorption deodorant may be used.

본 발명에서 상기 흡착탈취제는 규조토, 제올라이트, 흡착제 및 겔 라이트를 혼합하여 제조될 수 있는데, 상기 흡착탈취제는 규조토 10 내지 30 중량부, 제올라이트 25 내지 45 중량부, 흡착제 25 내지 45 중량부, 겔 라이트 10 내지 25 중량부의 중량비율로 혼합되어 제조될 수 있다. In the present invention, the adsorption deodorant may be prepared by mixing diatomaceous earth, zeolite, adsorbent and gelite, and the adsorption deodorant is 10 to 30 parts by weight of diatomaceous earth, 25 to 45 parts by weight of zeolite, 25 to 45 parts by weight of adsorbent, gelite. It may be prepared by mixing in a weight ratio of 10 to 25 parts by weight.

상기 규조토는 평균 입자의 크기가 50 내지 100 마이크로미터의 규조류(diatome)[0081] 라고 불리는 부유성조류(藻類;algae) 껍데기로 이루어진 퇴적물의 집합체로써 대부분이 비정질 실리카로 구성될 수 있다. 상기 규조토는 The diatomaceous earth is an aggregate of sediments composed of the shells of suspended algae called diatoms having an average particle size of 50 to 100 micrometers, and may be mostly composed of amorphous silica. The diatomaceous earth is

활성탄의 5천 배에 이르는 미세기공이 형성되어 있어 미세기공을 통해 오염된 입자까지 여과시키는 초다공질체이며, 미세기공을 통해 습도를 유지시켜주거나 냄새를 제거하는 흡착 및 탈취기능을 제공한다. 또한 규조토는 원적외선과 음이온을 방출하고 단열방음 효과가 있으며, 포름알데히드나 VOC(휘발성유기화합물)을 흡착 분해할 수 있다.It has micropores 5,000 times that of activated carbon, so it is an ultra-porous material that filters even polluted particles through micropores, and provides adsorption and deodorization functions that maintain humidity or remove odors through micropores. In addition, diatomaceous earth emits far-infrared rays and negative ions, has an adiabatic sound insulation effect, and can adsorb and decompose formaldehyde and VOC (volatile organic compounds).

따라서, 활성탄에서 제거되지 않은 미세입자까지 흡착제거하고, 새집증후군 발생요인인 포름알데히드나 VOC를 흡착분해하는 등 유해성분 제거효율을 지속적으로 증대시킬 수 있다. Therefore, it is possible to continuously increase the removal efficiency of harmful components by adsorbing and removing even fine particles that are not removed from the activated carbon and adsorbing and decomposing formaldehyde or VOC, which are factors that cause sick house syndrome.

본 발명에서 상기 규조토가 상기한 하한 범위 미만으로 포함되는 경우에는 유해성분 제거효율이 낮아지며, 상기한 상한 범위를 초과하여 포함되는 경우에는 함유량 증가에 따른 유해성분의 제거효율 증대가 미미하므로, 상기 규조토는 상기한 비율 범위로 혼합사용하는 것이 바람직하다. In the present invention, when the diatomaceous earth is included below the lower limit range, the removal efficiency of harmful components is lowered, and when the diatomaceous earth is included in excess of the upper limit range, the increase in the removal efficiency of harmful components according to the content increase is insignificant, so the diatomaceous earth It is preferable to mix and use in the above ratio range.

상기 제올라이트(Zeolite)는 규산염 광물로서 결정의 구조적으로 각 원자의 결합이 느슨하여 그 사이를 채우고있는 수분을 고열로 방출시켜도 골격은 그대로 유지하고 있어 내부 공간으로 다른 미립물질을 흡착시킬 수 있다. 특히, 상기 제올라이트는 탈취효과와 흡착효과가 우수하여 탈황석고에서 배출되는 아황산가스나 시멘트에서 배출되는 유해성분을 흡착 제거할 수 있다. The zeolite (Zeolite) is a silicate mineral, structurally the bond between each atom is loose in the crystal structure, so even if the moisture filling the gap is released with high heat, the skeleton is maintained as it is, so that other particulate matter can be adsorbed into the internal space. In particular, the zeolite has excellent deodorizing effect and adsorption effect, so it can adsorb and remove harmful components discharged from sulfur dioxide gas or cement discharged from desulfurized gypsum.

또한, 상기 제올라이트가 갖는 흡수성에 의해 사용시 몰탈이 응결 후 건조과정에서 강도 저감없이 제올라이트 내부의 수분을 지속적으로 방출시켜 건조시간을 지연시킴으로써 급속한 건조에 의한 균열발생을 억제할 수 있다. In addition, due to the absorbency of the zeolite, it is possible to suppress cracking due to rapid drying by delaying the drying time by continuously releasing moisture inside the zeolite without reducing the strength in the drying process after the mortar solidifies when used.

본 발명에서 상기 제올라이트가 상기한 하한 범위 미만으로 포함되는 경우에는 유해성분 제거효율과 건조지연에 대한 효과가 낮아지며, 상기한 상한 범위를 초과하여 포함되는 경우에는 함유량 증가에 따른 유해성분의 제거효율과 건조지연 효과가 미미함으로, 상기 제올라이트는 상기한 비율 범위로 혼합사용하는 것이 바람직하다. In the present invention, when the zeolite is included below the lower limit, the effect on the removal efficiency of harmful components and drying delay is lowered, and when the zeolite is included in excess of the upper limit, the removal efficiency of harmful components according to the content increase and Since the drying delay effect is insignificant, the zeolite is preferably mixed and used in the above ratio range.

상기 흡착제는 주식회사 비케이의 X-deo라는 상품명으로 시판되고 있는 것을 사용하는데, 상기 흡착제는 특허등록 제10-1059387호에 의해 제조되는 것으로, 건조파쇄된 상수오니 100 중량부에 60 내지 90% 농도의 인산공급원 5 중량부를 혼합 교반하여 10 내지 30시간 교반숙성하고 200 내지 300℃에서 5 내지 15시간 가열하여 숙성된 100 내지 200 메쉬의 복층다공형원통 구조를 갖는 분말인산물질과, 건조파쇄된 상수오니 100 중량부에 60 내지 90% 농도의 황산공급원 5 중량부를 혼합교반하여 10 내지 30시간 교반숙성하고 200 내지 300℃에서 5 내지 15시간 가열하여 숙성된 100 내지 200메쉬의 복층다공형원통 구조를 갖는 분말황산물질이다. 상기 분말인산물질과 분말황산물질은 경도가 92% 이상이고 분말인산물질과 분말황산물질이 55:45의 중량% 비율로 혼합된 흡착제이다. The adsorbent is commercially available under the trade name of X-deo of BK Co., Ltd. The adsorbent is manufactured by Patent Registration No. 10-1059387, and contains 60 to 90% concentration in 100 parts by weight of dry crushed tap water sludge. Powdered phosphoric acid material having a multi-layer porous cylindrical structure of 100 to 200 mesh, aged by stirring for 10 to 30 hours by mixing and stirring 5 parts by weight of a phosphoric acid source, and heating at 200 to 300 ° C. for 5 to 15 hours, and dry crushed tap water sludge It has a multilayer porous cylindrical structure of 100 to 200 mesh that is aged by mixing and stirring 5 parts by weight of a sulfuric acid source with a concentration of 60 to 90% to 100 parts by weight, stirring and aging for 10 to 30 hours, and heating for 5 to 15 hours at 200 to 300 ° C. It is powdered sulfuric acid. The powdered phosphoric acid material and the powdered sulfuric acid material have a hardness of 92% or more and are adsorbents in which the powdered phosphoric acid material and the powdered sulfuric acid material are mixed in a weight % ratio of 55:45.

상기 흡착제는 활성탄보다 비표면적이 2 내지 4배 높으며, 암모니아, 황화수소, 아민, 알데히드(aldehyde) 등 다양한 형태의 악취제거 가스에 효율적으로 작용하여 본 발명의 수축저감제의 탈황석고나 시멘트에서 배출되는 유해성분에 대한 흡착제거효율을 증대시키는 것이다. The adsorbent has a specific surface area 2 to 4 times higher than that of activated carbon, and it effectively acts on various types of odor removal gas such as ammonia, hydrogen sulfide, amine, and aldehyde, so that the shrinkage reducing agent of the present invention is discharged from desulfurized gypsum or cement. It is to increase the adsorption and removal efficiency of harmful components.

본 발명에서 상기 흡착제가 상기한 하한 범위 미만으로 포함되는 경우에는 유해성분 제거효율이 낮아지며, 상기한 상한 범위를 초과하여 포함되는 경우에는 함유량 증가에 따른 유해성분의 제거효율 증대가 미미함으로, 상기흡착제는 상기한 비율 범위로 혼합사용하는 것이 바람직하다. In the present invention, when the adsorbent is included below the lower limit, the removal efficiency of harmful components is lowered, and when it is included in excess of the upper limit, the increase in the removal efficiency of harmful components according to the content increase is insignificant, so the adsorbent It is preferable to mix and use in the above ratio range.

상기 겔 라이트(Ge-lite)는 포졸란이라고 불리우며, 게르마늄이 약 20ppm 함유되어 있고 다량의 원적외선과 음이온을 함유하고 있는 것으로 대표적으로는 화산재, 규산백토, 규산토 등이 있다. 즉, 상기 겔 라이트는 황토의 약 180배에 해당하는 원적외선을 방출하여 식물의 성장을 촉진하고 습도조절기능이 있으며, 음이온과 인체활성에너지를 방출하고 유해전자파차단기능이 있고, 탈취 및 살균효과와 중금속 중화 효과도 제공한다. The Ge-lite is called pozzolan, and contains about 20 ppm of germanium and contains a large amount of far-infrared rays and anions. Representative examples include volcanic ash, silicate clay, and silicate soil. That is, the gel light emits far-infrared rays equivalent to about 180 times that of loess, promotes plant growth, has a humidity control function, emits negative ions and human active energy, has a harmful electromagnetic wave blocking function, and has a deodorizing and sterilizing effect and It also provides a neutralizing effect of heavy metals.

상기 겔 라이트는 상술한 조성물들과 같이 흡착제로 작용하여 탈황석고와 시멘트에서 배출되는 유해성분을 흡착제거하며, 라돈과 같은 방사능 물질과 전자파를 차단하며, 암모니아와 같은 악취성분을 제거할 수 있다. The gel light acts as an adsorbent like the above-mentioned compositions to adsorb and remove harmful components emitted from desulfurized gypsum and cement, block radioactive substances such as radon and electromagnetic waves, and remove odor components such as ammonia.

또한, 상기 겔 라이트는 활성탄이나 제올라이트보다는 효과가 낮지만 습도조절 기능을 가지고 있으므로, 몰탈의 양생과정에서 함습한 수분을 지속적으로 배출시켜 건조시간을 증대시킴으로써 급격한 건조에 의한 균열발생을 억제할 수 있다. In addition, since the gel light has a lower effect than activated carbon or zeolite, but has a humidity control function, it continuously discharges moisture contained in the curing process of mortar to increase the drying time, thereby suppressing the occurrence of cracks due to rapid drying. .

본 발명에서 상기 겔 라이트가 상기한 하한 범위 미만으로 포함되는 경우에는 유해성분 제거나 원적외선 방출 및 유해전파 차단효율이 낮아지며, 상기한 상한 범위를 초과하여 포함되는 경우에는 함유량 증가에 따른 유해성분의 제거효율과 유해전파차단효율 증대가 미미함으로, 상기 겔 라이트는 상기한 비율 범위로 혼합사용하는 것이 바람직하다. In the present invention, when the gel light is included below the lower limit, the removal of harmful components or far-infrared emission and harmful radio wave blocking efficiency are lowered, and when the gel light is included in excess of the upper limit, the removal of harmful ingredients according to the content increase Since the increase in efficiency and harmful radio wave blocking efficiency is insignificant, it is preferable to mix and use the gel light in the above-mentioned ratio range.

상술한 바와 같이, 본 발명은 미장용 첨가제를 구성하는 조성물로 석고 이외에 다수의 흡착성을 갖는 성분을 포함함으로써, 몰탈의 양생과정에서 흡습한 수분을 지속적으로 배출하여 건조시간을 지연시켜 균열발생을 억제하는 효과와 함께 다양한 유해성분에 대한 흡착제거기능을 구현할 수 있다. As described above, the present invention suppresses cracking by delaying the drying time by continuously discharging moisture absorbed during the curing process of mortar by including a plurality of components having adsorption properties in addition to gypsum as a composition constituting the cosmetic additive. It is possible to implement the function of adsorption and removal of various harmful components along with the effect of

즉, 본 발명에 따라 제조된 미장용 첨가제는 입자크기가 작은 유해성분에서 큰 성분까지 다양한 성분에 대해 대응이 가능하도록 함으로써, 거주자에게 쾌적한 주거환경을 구현할 수 있다. That is, the cosmetic additive manufactured according to the present invention can respond to various components ranging from harmful components with small particle sizes to large components, thereby realizing a comfortable residential environment for residents.

이하, 본 발명에 따른 미장용 첨가제를 이용한 미장용 시멘트에 대하여 상세하게 설명하기로 한다. Hereinafter, the plastering cement using the plastering additive according to the present invention will be described in detail.

본 발명에 따른 미장용 시멘트는 상기한 바와 같은 조성물들로 제조된 미장용 첨가제와 시멘트를 혼합함으로써 제조될 수 있다. The plastering cement according to the present invention can be prepared by mixing cement with the plastering additive prepared from the compositions as described above.

본 발명에서 상기 시멘트는 고로슬래그 시멘트가 사용될 수 있는데, 상기 고로슬래그 시멘트는 포틀랜드 시멘트클링커(Portland Cement Clinker)와 제철소에서 선철을 제조할 때 부산되는 고로슬래그에 적량의 석고를 가해 혼합 분쇄하거나 조합시켜 분쇄한 것을 균일하게 혼합한 것으로, 한국산업규격 KS L 5210에서는 고로슬래그 혼합량을 중량기준 24%~65%로 규정하고 있다. In the present invention, blast furnace slag cement may be used as the cement. The blast furnace slag cement is mixed and pulverized by adding an appropriate amount of gypsum to Portland Cement Clinker and blast furnace slag that is produced when pig iron is produced at an ironworks. The pulverized product is uniformly mixed, and the Korean industrial standard KS L 5210 stipulates that the mixing amount of the blast furnace slag is 24% to 65% by weight.

또한, 고로슬래그 시멘트의 등급은 특급과 1급으로 구분하고 있으며, 이에 대한 차이는 압축강도로 차등화하고있다. 상기 고로슬래그 시멘트의 화학성분(KS L 5210)은 아래의 [표 1]에 나타낸 바와 같고, 물리적 성능(KS L5210)은 아래의 [표 2]에 나타낸 바와 같다. In addition, the grade of blast furnace slag cement is divided into special grade and grade 1, and the difference is differentiated by compressive strength. The chemical composition (KS L 5210) of the blast furnace slag cement is as shown in [Table 1] below, and the physical performance (KS L5210) is as shown in [Table 2] below.

표 1 Table 1

고로슬래그 시멘트의 화학성분(KS L 5210) Chemical composition of blast furnace slag cement (KS L 5210)

Figure pat00001
Figure pat00001

표 2 Table 2

고로슬래그 시멘트의 물리적 성능(KS L 5210) Physical performance of blast furnace slag cement (KS L 5210)

Figure pat00002
Figure pat00002

상기 고로슬래그 시멘트는 시멘트를 제철공정에서 발생하는 산업폐기물인 고로슬래그로 일부 치환하여 대체한 시멘트를 의미하는 것으로, 상기 고로슬래그 시멘트는 수화열이 적고, 몰탈의 수밀성 및 화학적 내구성이 좋은장점을 가지고 있으나, 수화열이 낮기 때문에 몰탈의 응결지연 즉, 초기강도가 저하되는 단점이 있다. 본 발명에 따른 미장용 첨가제를 이용한 미장용 시멘트에서 상기 고로슬래그 시멘트와 미장용 첨가제는 일정한 중량비로 혼합되어 사용될 수 있는데, 상기 미장용 첨가제는 고로슬래그 시멘트 전체 100 중량부를 기준으로 하여 40 내지 60 중량부가 포함될 수 있다. The blast furnace slag cement refers to cement in which cement is partially substituted with blast furnace slag, an industrial waste generated in the iron making process, and the blast furnace slag cement has the advantages of low heat of hydration and good water tightness and chemical durability of mortar. , because the heat of hydration is low, the setting delay of the mortar, that is, the initial strength is lowered. In the plastering cement using the plastering additive according to the present invention, the blast furnace slag cement and the plastering additive may be mixed in a constant weight ratio and used, and the plastering additive is 40 to 60 parts by weight based on 100 parts by weight of the total blast furnace slag cement. Additions may be included.

이하, 본 발명에 따른 미장용 시멘트를 이용한 몰탈에 대하여 상세하게 설명하기로 한다. Hereinafter, the mortar using the plastering cement according to the present invention will be described in detail.

본 발명에 따른 몰탈은 미장용 첨가제를 포함하는 시멘트, 규사, 셀룰로스 파이버, EVA 폴리머, 무기결합재, 섬유보강재, 방동제, 감수제, 증점제, 방수제 및 배합수를 포함하여 제조된다. The mortar according to the present invention is prepared by including cement, silica sand, cellulose fiber, EVA polymer, inorganic binder, fiber reinforcement, antifreeze, water reducing agent, thickener, waterproofing agent, and water containing additives for decoration.

상기 미장용 첨가제를 포함하는 시멘트는 상술한 방법에 의해 배합되어 제조된 시멘트가 사용될 수 있고, 60 내지 80 중량부가 포함될 수 있다. The cement including the cosmetic additive may be a cement prepared by mixing by the above-described method, and may contain 60 to 80 parts by weight.

상기 시멘트는 미장용 첨가제가 포함된 고로슬래그 시멘트가 사용되고, 상기 미장용 첨가제는 고로슬래그 시멘트 전체 100 중량부를 기준으로 하여 40 내지 60 중량부의 비율로 포함될 수 있다. As the cement, blast furnace slag cement including a plastering additive may be used, and the plastering additive may be included in an amount of 40 to 60 parts by weight based on 100 parts by weight of the total blast furnace slag cement.

본 발명에서 상기 미장용 첨가제가 포함된 고로슬래그 시멘트가 상기한 하한 미만으로 포함되는 경우에는 몰탈의 강도가 약해져서 미장용 몰탈로서의 역할을 담당하기 어려우며, 상기한 상한을 초과하여 포함되는 경우에는 몰탈의 품질저하가 발생할 수 있고 시공상 어려움이 따르며, 또한 알칼리도를 상승시킬 수 있다. In the present invention, when the blast furnace slag cement containing the plastering additive is included below the lower limit, the strength of the mortar is weakened, making it difficult to serve as a plastering mortar. It may cause deterioration of quality, difficulty in construction, and may increase alkalinity.

상기 규사는 천연규사 또는 암석을 파쇄하여 체가름한 인조규사를 사용할 수 있는데, 바람직하게는 인조규사를 사용할 수 있다. 상기 인조규사를 구성하는 암석으로는 석회석, 돌로마이트 등을 파쇄하여 된 것일 수 있다. The silica sand may be natural silica sand or artificial silica sand sifted by crushing rocks, preferably artificial silica sand. The rocks constituting the artificial silica sand may be formed by crushing limestone, dolomite, and the like.

본 발명에서 상기 규사는 흡수율이 3% 이하이고, 입도분포가 50 내지 150메쉬(mesh)가 되도록 조합한 것을 사용할 수 있는데, 상기 규사의 입도가 50메쉬 보다 크게 되면 규사가 너무 거칠어 부드러운 작업성을 확보하기 어렵고, 150메쉬 이하의 규사가 포함되면 혼련수의 비율이 높아져 강도의 저하와 접착 기능시간의 저하를 유발하게 될 수 있다. In the present invention, the silica sand has a water absorption rate of 3% or less and a particle size distribution of 50 to 150 mesh can be used in combination. If the particle size of the silica sand is larger than 50 mesh, the silica sand is too rough and soft workability is achieved. It is difficult to secure, and if silica sand of 150 mesh or less is included, the ratio of the kneaded water increases, which may cause a decrease in strength and a decrease in the adhesion function time.

또한, 본 발명에서 상기 규사는 40 내지 70 중량부 포함될 수 있는데, 상기 규사의 함량이 40 중량부 미만일 경우에는 시멘트 함량이 상대적으로 높아져 몰탈의 유연성 저하와 원재료 가격이 상승하는 문제점이 있고, 70 중량부를 초과하는 경우에는 시멘트의 함량이 상대적으로 적어져 충분한 강도를 확보하기 어려운 문제가 있다. In addition, in the present invention, the silica sand may be included in 40 to 70 parts by weight. When the content of the silica sand is less than 40 parts by weight, the cement content is relatively high, so there is a problem in that the flexibility of the mortar and the raw material price increase, and the 70 weight part In the case of exceeding the part, there is a problem in that the content of cement is relatively small, so that it is difficult to secure sufficient strength.

상기 셀룰로스 파이버는 파이버 표면을 특수 코팅처리하여 배합수량을 늘리지 않는 것을 사용하여 급격한 흐름성 저하를 막고 유체의 이동이 뛰어난 친환경 파이버로서, 표면에서 겉마름 현상이 일어날 때 몰탈 내부의 수분을 표면으로 이동시켜 겉표면과 내부의 경화속도를 일정하게 해주는 역할을 한다. The cellulose fiber is an eco-friendly fiber with excellent fluid movement and preventing rapid flow deterioration by using a special coating treatment on the surface of the fiber that does not increase the amount of water blended, and moves the moisture inside the mortar to the surface when dryness occurs on the surface. It plays a role in making the curing rate of the outer surface and the inner surface constant.

또한, 상기 셀룰로스 파이버는 본 발명에 따른 몰탈을 시공 시 재료가 처지거나 떨어지는 것을 방지해주는 시공안정성을 부여하고, 시멘트와 일체화되어 균열 저항성을 증가시켜 몰탈의 치수안정성을 부여할 수 있다. In addition, the cellulose fiber provides construction stability that prevents the material from sagging or falling when constructing the mortar according to the present invention, and is integrated with cement to increase crack resistance, thereby providing dimensional stability of the mortar.

본 발명에서 상기 셀룰로스 파이버는 합성 수지계 파이버 또는 천연 목재에서 추출된 파이버를 사용할 수 있는데, 바람직하게는 천연 목재에서 추출된 파이버를 사용할 수 있다. 상기 천연 목재에서 추출된 파이버는 환경친화적이고, 섬유 표면이 친수성이므로 물리적인 수분의 흡착이 용이하여 젖음성이 양호할 수 있다. In the present invention, the cellulose fiber may be a synthetic resin-based fiber or a fiber extracted from natural wood, preferably a fiber extracted from natural wood. The fibers extracted from the natural wood are environmentally friendly, and since the surface of the fibers is hydrophilic, physical moisture is easily adsorbed, so that the wettability may be good.

본 발명에서 상기 셀룰로스 파이버는 3 내지 8 중량부가 포함될 수 있는데, 상기 셀루로스 파이버가 3 중량부미만으로 포함되는 경우에는 몰탈 내부와 표면의 경화속도가 일정하지 않고 표면에서의 겉마름 현상이 일어나며, 8 중량부를 초과하여 포함되는 경우에는 강도 저하에 의한 몰탈의 내부 균열이 발생할 수 있다. In the present invention, 3 to 8 parts by weight of the cellulose fiber may be included, and when the cellulose fiber is included in less than 3 parts by weight, the curing rate of the inside and the surface of the mortar is not constant, and the surface of the surface becomes dry. When included in excess of 8 parts by weight, internal cracking of the mortar may occur due to a decrease in strength.

상기 EVA 폴리머는 바닥이나 벽면의 표면과 몰탈의 부착성을 높이고 몰탈의 표면강도를 높이기 위하여 사용되는 것으로, 유/무기 복합몰탈의 배합용액으로 사용될 수 있다. The EVA polymer is used to increase the adhesion of the mortar to the surface of the floor or wall surface and to increase the surface strength of the mortar, and can be used as a compounding solution of organic/inorganic composite mortar.

본 발명에서 상기 EVA 폴리머는 Tg = 0℃ 내지 -10℃, 고형분 15~40질량%의 시멘트 혼화형 EVA 폴리머를 사용할수 있고, 상기 Tg 값이 0℃ 초과할 경우 몰탈이 경질화되어 크랙 발생의 우려가 있고 내충격성이 약해지며, Tg값이 -10℃ 미만일 경우 몰탈이 연질화되어 폴리싱 작업 시 균일한 표면강도를 내기 어렵고 몰탈 배합시에도 너무 끈적거리는 현상이 발생해 작업성이 떨어질 수 있다. In the present invention, the EVA polymer may be a cement-miscible EVA polymer having a Tg = 0° C. to -10° C. and a solid content of 15 to 40 mass%, and when the Tg value exceeds 0° C., the mortar is hardened and cracks occur. If the Tg value is less than -10°C, the mortar becomes soft and it is difficult to obtain a uniform surface strength during polishing, and the workability may be deteriorated due to the phenomenon of being too sticky even when mixing the mortar.

또한, 본 발명에 따른 몰탈은 Tg = 0℃ 내지 -10℃의 고분산성 EVA 폴리머와 셀룰로스 파이버를 사용할 수 있는데, 상기 EVA 폴리머와 셀룰로스 파이버는 표면 건조 저항성을 높이고 부착강도를 증진시키며, 또한 경질화로인해 내충격성이 약해지는 것을 방지하여, 기존의 바닥용 셀프레벨링 몰탈이 구비한 문제점 즉, 표면건조에 대한 저항성 부족, 부착성 부족, 경질화로 인해 크랙 및 탈락 등의 문제점을 해소할 수 있다. In addition, the mortar according to the present invention can use a high dispersibility EVA polymer and cellulose fiber having Tg = 0°C to -10°C, wherein the EVA polymer and the cellulose fiber increase the surface drying resistance and improve adhesion strength, and By preventing the impact resistance from being weakened due to this, it is possible to solve the problems of the existing self-leveling mortar for flooring, that is, the lack of resistance to surface drying, lack of adhesion, and problems such as cracking and dropping due to hardening.

본 발명에서 상기 EVA 폴리머는 5 내지 10 중량부 포함될 수 있는데, 상기 EVA 폴리머가 5 중량부 미만으로 포함되는 경우에는 표면건조에 대한 저항성이나 부착성이 부족할 수 있고, 10 중량부를 초과하는 경우에는 몰탈이 연질화되어 폴리싱 작업 시 균일한 표면강도를 내기 어렵고 몰탈 배합시에도 너무 끈적거리는 현상이 발생해 작업성이 떨어지는 문제점이 발생할 수 있다. In the present invention, the EVA polymer may be included in 5 to 10 parts by weight. When the EVA polymer is included in an amount of less than 5 parts by weight, resistance to surface drying or adhesion may be insufficient, and when it exceeds 10 parts by weight, mortar This softening makes it difficult to obtain a uniform surface strength during polishing, and may cause a problem of poor workability due to excessive stickiness even when mixing mortar.

상기 무기결합재는 고로 슬래그와 플라이 애시 및 실리카흄의 혼합물이 사용되고, 10 내지 15 중량부가 포함될 수 있다. 본 발명에서 상기 무기결합재는 고로 슬래그 50 내지 70 중량부, 플라이 애시 30 내지 50 중량부, 실리카흄 20 내지 30 중량부의 중량 비율로 혼합되어 첨가될 수 있다. A mixture of blast furnace slag, fly ash, and silica fume is used as the inorganic binder, and 10 to 15 parts by weight may be included. In the present invention, the inorganic binder may be mixed and added in a weight ratio of 50 to 70 parts by weight of blast furnace slag, 30 to 50 parts by weight of fly ash, and 20 to 30 parts by weight of silica fume.

상기 실리카흄(silica fume)은 알칼리 이온과의 높은 결합력을 발휘하고, 몰탈의 타설시 구성성분들 간의 혼합성을 향상시킬 수 있다. 상기 실리카흄은 용광로에서 배출되는 가스로부터 농축된 물질로 비결정질 실리콘 제2산화물을 다량으로 함유하고 있으며, 매우 미세한 구형의 입자일 수 있다. 또한, 실리카흄의 밀도는 20 내지 22g/cm 3이고, 비표면적 150,000 내지 200,000cm 2/g의 분말도를 갖는 초미립자일 수 있다. 상기 실리카흄의 평균 입경은 02 내지 05㎛일 수 있으며, 바람직하게는 반응성이 높은 몰탈 재료로 작용이 유리한 평균 입경 02㎛의 초미립자일 수 있다. 상기 실리카흄 종류는 포집된 원래의 상태인 분말형(as-produced), 물에 현탁한 슬러지형(slurried), 덩어리형(pelletized), 응축시킨 과립형(densified or compacted) 등일 수 있으며, 바람직하게는 다른 분체와의 혼합성과 작업성을 고려하여 과립형일 수 있다. The silica fume may exhibit a high bonding strength with alkali ions and improve the mixing property between the constituents when the mortar is poured. The silica fume is a substance concentrated from the gas discharged from the furnace, and contains a large amount of amorphous silicon secondary oxide, and may be very fine spherical particles. In addition, the density of silica fume may be 20 to 22 g/cm 3 , and may be ultra-fine particles having a specific surface area of 150,000 to 200,000 cm 2/g. The silica fume may have an average particle diameter of 02 to 05 μm, and preferably may be ultra-fine particles having an average particle diameter of 02 μm, which is advantageous as a highly reactive mortar material. The silica fume type may be in the form of collected original powder (as-produced), sludge suspended in water, pelletized, condensed granulated (densified or compacted), etc. It may be granular in consideration of mixing with other powders and workability.

상기 섬유보강재는 미장용 몰탈의 취성적 파괴를 방지하기 위하여 사용될 수 있고, 상기 섬유보강재는 미장용 몰탈 내에 짧고 임의적으로 분산되어 상기 미장용 몰탈내에서 발생하는 균열의 성장을 조절하여 파괴를 방지할수 있다. 예를 들어, 상기 섬유보강재는 고로슬래그 시멘트 모체 내부의 균열성장을 멈추게 하거나 지연시킬 수 있으며, 이로 인한 몰탈의 인발 특성과 균열 저항성을 향상시킬 수 있다. The fiber reinforcing material can be used to prevent brittle fracture of the plastering mortar, and the fiber reinforcing material is briefly and randomly dispersed in the plastering mortar to control the growth of cracks occurring in the plastering mortar to prevent destruction. have. For example, the fiber reinforcement can stop or delay crack growth inside the blast furnace slag cement matrix, thereby improving the pulling properties and crack resistance of the mortar.

본 발명에서 상기 섬유보강재로는 자연마섬유가 사용될 수 있는데, 상기 자연마섬유의 특성은 [표 3]에 나타낸바와 같다. In the present invention, natural hemp fibers may be used as the fiber reinforcement material, and the characteristics of the natural hemp fibers are as shown in [Table 3].

표 3 Table 3

자연마섬유의 특성 Characteristics of natural hemp fibers

Figure pat00003
Figure pat00003

본 발명에서 상기 자연마섬유는 혼화재료로 사용되는 것으로, 05 내지 3 중량부가 포함될 수 있는데, 상기 자연마섬유가 05 중량부 미만으로 포함되는 경우에는 미장용 몰탈에 균열이 발생하였을 때 섬유의 가교작용, 즉 충분한 인발 특성과 균열 저항성을 보일 수 없으며, 3 중량부를 초과하여 포함되는 경우에는 미장용 몰탈에서 요구되는 충분한 강성을 얻을 수 없어 강도 저하 문제를 발생할 수 있다. In the present invention, the natural hemp fiber is used as an admixture material, and 05 to 3 parts by weight may be included. When the natural hemp fiber is included in an amount of less than 05 parts by weight, when a crack occurs in the mortar for plastering, the fiber is crosslinked Action, that is, it cannot show sufficient drawing properties and crack resistance, and when it contains more than 3 parts by weight, sufficient rigidity required for a mortar for decoration cannot be obtained, and thus a problem of strength reduction may occur.

상기 방동제는 0℃ 이하의 가혹한 조건에서도 동결안정성을 가지면서 우수한 조강성 및 시공성을 유지시키기 위하여 사용되는 것으로, 3 내지 7 중량부가 포함될 수 있는데, 본 발명에서 상기 방동제는 정제수, 질산칼슘 및 포타슘포메이트(PF)를 혼합하여 제조될 수 있다. The antifreeze agent is used to maintain excellent roughness and workability while having freeze stability even under severe conditions of 0° C. or less, and may include 3 to 7 parts by weight. In the present invention, the antifreeze agent includes purified water, calcium nitrate and It may be prepared by mixing potassium formate (PF).

상기 정제수는 질산칼슘 및 포타슘포메이트(PF)를 혼합하기 위하여 사용되는 것으로, 종류에 한정되지 않으나 불순물이 없고 깨끗하게 정제된 증류수를 사용하는 것이 바람직하다. The purified water is used to mix calcium nitrate and potassium formate (PF), but it is not limited to the type, but it is preferable to use distilled water that is purified without impurities.

상기 질산칼슘은 화학식이 Ca(NO3)2으로, 콘크리트 타설 시 조기 강도를 증진시키기 위해 혼합되는 원료로서, 단시간 내에 몰탈의 양생속도를 빠르게 하기 위하여 첨가될 수 있다. The calcium nitrate has a chemical formula of Ca(NO3)2, is a raw material mixed to enhance early strength during concrete pouring, and may be added to speed up the curing rate of mortar within a short time.

상기 포타슘포메이트(PF)는 어느점이 매우 낮아 저온에서의 응결촉진 기능을 수행할 수 있는 것으로, 본 발명에 따른 미장용 몰탈에 혼합되어 사용되는 경우 어느점 내림의 효과를 부여함과 동시에 강도 증진의 역할도 수행할 수 있다. The potassium formate (PF) has a very low certain point, so it can perform a setting promoting function at a low temperature. can also perform the role of

본 발명에서 상기 방동제는 정제수, 질산칼슘 및 포타슘포메이트(PF)를 혼합하여 제조되는데, 상기 방동제를 구성하는 정제수, 질산칼슘 및 포타슘포메이트(PF)는 각각 정제수 55 내지 65 중량부, 질산칼슘 20 내지 30 중량 In the present invention, the antifreeze agent is prepared by mixing purified water, calcium nitrate and potassium formate (PF), and the purified water, calcium nitrate and potassium formate (PF) constituting the antifreeze agent contain 55 to 65 parts by weight of purified water, respectively, 20 to 30 weight of calcium nitrate

부, 포타슘포메이트(PF) 3 내지 8 중량부의 중량비율로 혼합되어 본 발명에 따른 방동제를 제조할 수 있다.Parts, potassium formate (PF) may be mixed in a weight ratio of 3 to 8 parts by weight to prepare the antifreeze agent according to the present invention.

상기 감수제(減水劑, water-reducing agent)는 몰탈의 워커빌리티(workability)의 개선을 주목적으로 하여 첨가되는 혼합제로서, 상기 감수제를 사용하면 몰탈의 양을 줄일 수 있고, 내구성 및 강도가 개선될 수 있다. The water-reducing agent (減水劑, water-reducing agent) is a mixture added for the main purpose of improving the workability of the mortar. When the water-reducing agent is used, the amount of mortar can be reduced, and durability and strength can be improved. .

본 발명에서 상기 감수제는 1 내지 3 중량부가 포함될 수 있는데, 상기 감수제로는 나프탈렌설폰산염계, 멜라민설폰산염계 및 폴리카르본산염계 중에서 선택된 1종 이상의 물질이 사용될 수 있다. In the present invention, 1 to 3 parts by weight of the water reducing agent may be included, and as the water reducing agent, one or more materials selected from naphthalenesulfonate-based, melaminesulfonate-based and polycarboxylate-based materials may be used.

상기 증점제는 몰탈 조성물들을 뭉쳐주는 역할을 하는 것으로, 본 발명에 따른 몰탈을 이용하여 바닥이나 벽면을 시공하는 경우 시공이 용이하도록 일정한 점성을 유지하도록 하며 결합력을 부여하여 강도 또한 향상시키는 역할을 할 수 있다. The thickener serves to aggregate the mortar compositions, and when the mortar according to the present invention is used to construct a floor or wall, it maintains a certain viscosity for easy construction, and it can also serve to improve strength by imparting binding force. have.

본 발명에서 상기 증점제는 폴리아크릴계, 셀룰로오스계, 폴리사카라이드계, 폴리알킬렌옥사이드, 폴리알킬렌글리콜알킬에테르 등을 사용할 수 있으며, 상기 증점제들을 2종 이상 혼합하여 사용할 수도 있으나, 상기 증점제가 이에 제한되는 것은 아니다. In the present invention, the thickener may be polyacrylic, cellulose, polysaccharide, polyalkylene oxide, polyalkylene glycol alkyl ether, etc., and may be used by mixing two or more of the thickeners, but the thickener It is not limited.

상기 폴리아크릴계로는 폴리아크릴산, 폴리아크릴산에스테르, 폴리아크릴산염 등을 사용할 수 있다. 상기 셀룰로오스계는 카르복시메틸셀룰로오스, 메틸셀룰로오스, 하이드록시에틸셀룰로즈, 히드록시프로필셀룰로오스, 메틸에틸셀룰로오스, 에틸셀룰로오스 등을 사용할 수 있으며, 상기 폴리사카라이드계는 웰란검, 커들란, 아밀로오스, 한천, 알긴산, 알긴산나트륨, 풀루란, 구아검 등을 사용할 수 있고, 상기 폴리알킬렌옥사이드로는 폴리에틸렌옥사이드, 폴리프로필렌옥사이드, 폴리부틸렌옥사이드 등을 사용할 수 있다. 상기 폴리알킬렌글리콜알킬에테르로는 폴리에틸렌글리콜메틸에테르 등을 사용할 수 있다. 또한, 비닐알코올, 에틸렌옥사이드, 아크릴산, 아크릴산에스테르, 아크릴산염, 아세트산비닐 등을 포함하는 공중합체 등을 사용할 수 있다. As the polyacrylic acid, polyacrylic acid, polyacrylic acid ester, polyacrylic acid salt, etc. may be used. The cellulose-based carboxymethyl cellulose, methyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, methyl ethyl cellulose, ethyl cellulose, etc. can be used, and the polysaccharide-based is welan gum, curdlan, amylose, agar, alginic acid. , sodium alginate, pullulan, guar gum, etc. may be used, and the polyalkylene oxide may include polyethylene oxide, polypropylene oxide, polybutylene oxide, and the like. As the polyalkylene glycol alkyl ether, polyethylene glycol methyl ether or the like can be used. In addition, a copolymer containing vinyl alcohol, ethylene oxide, acrylic acid, acrylic acid ester, acrylate, vinyl acetate, or the like can be used.

또한, 본 발명에서 상기 증점제는 03 내지 1 중량부가 포함될 수 있는데, 상기 증점제가 03 중량부 미만으로 포함되는 경우에는 분진이 발생하고, 강도와 광택이 저하되는 문제가 발생할 수 있고, 1 중량부를 초과하는 경우에는 양생시간이 길게 소요되고, 양생하는 동안 균열이 발생할 수 있으며, 오랜 양생시간 때문에 색이 변하는 문제점과 작업성이 저하되는 문제가 발생할 수 있다. In addition, in the present invention, 03 to 1 parts by weight of the thickener may be included, but when the thickener is included in an amount of less than 03 parts by weight, dust may occur, and a problem of lowering strength and gloss may occur, and exceeding 1 part by weight In this case, a long curing time is required, cracks may occur during curing, and a problem of color change and workability may occur due to a long curing time.

상기 방수제는 몰탈로 제조된 바닥이나 벽면에 습기가 침투하는 것을 방지하기 위하여 첨가되는 것으로, 상기 방수제로는 무기질 도포형 시멘트 방수제, 침투형 방수제, 규질산계 방수제, 분말형 방수제 등이 있는데, 본 발명에서는 분말형 방수제가 2 내지 5 중량부 포함될 수 있다. The waterproofing agent is added to prevent moisture from penetrating into the floor or wall surface made of mortar, and the waterproofing agent includes an inorganic coating type cement waterproofing agent, a penetration type waterproofing agent, a siliceous acid-based waterproofing agent, a powder type waterproofing agent, etc., In the present invention, 2 to 5 parts by weight of the powder-type waterproofing agent may be included.

본 발명에서 상기 분말형 방수제는 포틀랜드 시멘트 37 내지 43 중량부, 인조규사 30 내지 34 중량부, 실리카흄3 내지 10 중량부, 에틸렌/비닐라우레이트/비닐클로라이드 삼원 공중합체 3 내지 22 중량부 및 아크릴레이트 공중합체 3 내지 22 중량부를 배합하여 제조될 수 있다. In the present invention, the powder-type waterproofing agent is 37 to 43 parts by weight of Portland cement, 30 to 34 parts by weight of artificial silica sand, 3 to 10 parts by weight of silica fume, 3 to 22 parts by weight of ethylene/vinyllaurate/vinylchloride terpolymer and acrylate It can be prepared by blending 3 to 22 parts by weight of the copolymer.

상기 배합수는 상기한 조성물들을 혼합하기 위하여 사용되는 것으로, 종류에 한정되지 않으나 불순물이 없고 깨끗하게 정제된 증류수를 사용하는 것이 바람직하다. The compounding water is used to mix the above-mentioned compositions, but it is not limited to a type, but it is preferable to use distilled water that is purified without impurities.

본 발명에서 상기 배합수는 60 내지 80 중량부가 사용될 수 있는데, 상기 배합수가 60 중량부 미만으로 포함되는 경우에는 배합수의 사용량이 너무 적어 혼합이 용이하지 않고 몰탈 조성물들이 균일하게 혼합되지 않을 수 있으며, 80 중량부를 초과하는 경우에는 배합수의 사용량이 지나치게 많아지게 되므로, 제조되는 몰탈의 물성이 저하되는 문제점이 발생할 수 있다. In the present invention, 60 to 80 parts by weight of the compounding water may be used, and when the compounding water is included in less than 60 parts by weight, the amount of the compounding water is too small, so mixing is not easy, and the mortar compositions may not be uniformly mixed. , when it exceeds 80 parts by weight, the amount of the blended water is excessively increased, and thus there may be a problem in that the physical properties of the mortar to be manufactured are reduced.

이하, 본 발명에 따른 미장용 몰탈에 대한 바람직한 실시예를 더욱 상세하게 설명하기로 한다. Hereinafter, a preferred embodiment of the mortar for plastering according to the present invention will be described in more detail.

< 실시예 > <Example>

먼저, 석고 60 중량부, 활성탄 20 중량부, 식물성 첨가제 7 중량부 및 흡착탈취제 20 중량부를 배합하여 미장용첨가제를 제조하였다. 이때, 상기 식물성 첨가제와 흡착탈취제는 상술한 바와 같은 조성비율로 제조되었다. First, a cosmetic additive was prepared by mixing 60 parts by weight of gypsum, 20 parts by weight of activated carbon, 7 parts by weight of a vegetable additive and 20 parts by weight of an adsorption deodorant. In this case, the vegetable additive and the adsorption deodorant were prepared in the same composition ratio as described above.

다음으로, 미장용 첨가제를 포함하는 고로슬래그 시멘트 70 중량부, 규사 50 중량부, 셀룰로스 파이버 5중량부, EVA 폴리머 7 중량부, 무기결합재 12 중량부, 섬유보강재 2 중량부, 방동제 5 중량부, 감수제 2중량부, 증점제 05 중량부, 방수제 3 중량부 및 배합수 70 중량부를 혼합하여 몰탈을 제조하였다. Next, 70 parts by weight of blast furnace slag cement containing additives for plastering, 50 parts by weight of silica sand, 5 parts by weight of cellulose fiber, 7 parts by weight of EVA polymer, 12 parts by weight of inorganic binder, 2 parts by weight of fiber reinforcement, 5 parts by weight of antifreeze agent , 2 parts by weight of a water reducing agent, 05 parts by weight of a thickener, 3 parts by weight of a waterproofing agent, and 70 parts by weight of a compounding water were mixed to prepare a mortar.

이때, 상기 고로슬래그 시멘트에는 상기 고로슬래그 시멘트 전체 100 중량부를 기준으로 하여 미장용 첨가제가 50 중량부의 비율로 첨가되도록 구성하였다. At this time, the blast furnace slag cement was configured to contain 50 parts by weight of the cosmetic additive based on 100 parts by weight of the total blast furnace slag cement.

< 비교예 1 > < Comparative Example 1 >

실시예에서 식물성 첨가제 및 흡착탈취제를 첨가하지 않은 것을 제외하고 동일한 방법으로 몰탈을 제조하였다. A mortar was prepared in the same manner as in Example, except that the vegetable additive and adsorption deodorant were not added.

< 비교예 2 > < Comparative Example 2 >

실시예에서 미장용 첨가제를 첨가하지 않은 것을 제외하고 동일한 방법으로 몰탈을 제조하였다. A mortar was prepared in the same manner as in Examples except that no cosmetic additive was added.

상기와 같이 실시예, 비교예 1 및 비교예 2에 제시된 방법으로 제조된 몰탈의 시편을 준비한 후, 상기 시편의 물성을 측정하였다. After preparing the specimens of mortar prepared by the methods presented in Examples, Comparative Examples 1 and 2 as described above, the physical properties of the specimens were measured.

1 강도 시험 결과 1 Strength test results

본 발명의 실시예에 따른 미장용 첨가제를 이용한 미장용 몰탈과 비교예 1 및 비교예 2에 의해 몰탈의 물리적인 특성을 비교하기 위하여, 상기에서 설명한 실시예의 미장용 몰탈과 비교예 1 및 비교예 2에 의해 제조된 몰탈을 KS F 2405(몰탈의 압축강도 시험방법)에 의한 압축강도 시험을 수행하였고, 그 결과를 하기 [표 4]에 나타내었다. In order to compare the physical properties of the cosmetic mortar using the cosmetic additive according to the embodiment of the present invention and the mortar according to Comparative Examples 1 and 2, the cosmetic mortar of the above-described Examples and Comparative Examples 1 and 2 The mortar prepared by 2 was subjected to a compressive strength test according to KS F 2405 (Test method for compressive strength of mortar), and the results are shown in [Table 4] below.

또한, KS F 2408(몰탈의 휨강도 시험방법)에 의하여 휨강도 시험을 수행하였고, JIS A 6916 (마무리 도장재용 바탕 조정재)에 의하여 시편의 접착강도를 측정하여 각각의 결과를 하기 [표 4]에 나타내었다. In addition, the flexural strength test was performed according to KS F 2408 (Bending strength test method of mortar), and the adhesive strength of the specimen was measured according to JIS A 6916 (ground adjusting material for finishing coating material), and the results are shown in [Table 4] below. It was.

표 4 Table 4

Figure pat00004
Figure pat00004

상기 [표 4]에 나타난 바와 같이, 본 발명에 따라 제조된 미장용 첨가제를 이용한 미장용 몰탈(실시예)의 휨,압축 및 접착강도는 비교예 1과 비교예 2에 의해 제조된 몰탈보다 월등히 높았다. As shown in [Table 4], the bending, compression and adhesive strength of the cosmetic mortar (Example) using the cosmetic additive prepared according to the present invention was significantly higher than that of the mortar prepared by Comparative Examples 1 and 2 was high.

본 발명의 실시예에 따라 제조된 미장용 첨가제를 이용한 미장용 몰탈이 비교예 1과 비교예 2에 의해 제조된 몰탈보다 강도 면에서 월등히 우수함을 확인할 수 있었다. It was confirmed that the cosmetic mortar using the cosmetic additive prepared according to the embodiment of the present invention was significantly superior to the mortar prepared by Comparative Examples 1 and 2 in terms of strength.

2 건조수축 시험 결과 2 Dry shrinkage test result

본 발명의 실시예에 따라 제조된 미장용 첨가제를 이용한 미장용 몰탈과 비교예 1과 비교예 2에 따라 제조된 몰탈을 KS F 2424(콘크리트의 길이변화 시험방법)에 의하여 건조수축율을 측정하였으며, 그 결과를 하기 [표 5]에 나타내었다. The drying shrinkage of the plastering mortar using the cosmetic additive prepared according to the embodiment of the present invention and the mortar prepared according to Comparative Examples 1 and 2 was measured according to KS F 2424 (Test method for length change of concrete), The results are shown in [Table 5] below.

표 5 Table 5

Figure pat00005
Figure pat00005

위의 [표 5]에서와 같이, 실시예에 따라 제조된 미장용 첨가제를 이용한 미장용 몰탈이 비교예 1과 비교예 2에따라 제조된 몰탈보다 건조수축량이 감소되어 수축 저감 효과가 있음을 확인할 수 있었다. As shown in [Table 5] above, it was confirmed that the amount of drying shrinkage was reduced in the mortar for cosmetic use using the cosmetic additive prepared according to the example compared to the mortar prepared according to Comparative Examples 1 and 2, thereby reducing the shrinkage. could

3 흡수율 시험 결과 3 Absorption rate test result

본 발명의 실시예에 따라 제조된 미장용 첨가제를 이용한 미장용 몰탈과 비교예 1과 비교예 2에 따라 제조된 몰탈을 JIS A 1171(폴리머 시멘트 몰탈의 시험방법)에 규정한 방법에 따라 흡수율의 측정 결과를 아래의 [표 6]에 The water absorption rate of the cosmetic mortar using the cosmetic additive prepared according to the embodiment of the present invention and the mortar prepared according to Comparative Examples 1 and 2 according to the method specified in JIS A 1171 (Test method for polymer cement mortar) The measurement results are shown in [Table 6] below.

나타내었다. 흡수율이 높으면 불순물이나 물이 몰탈의 내부로 침투하게 되면 몰탈의 내부에 기공률이 증가하게되어 구조물의 열화를 촉진시키고 파손을 초래하는 문제가 발생한다.indicated. If the water absorption rate is high, when impurities or water penetrate into the interior of the mortar, the porosity increases inside the mortar, thereby promoting deterioration of the structure and causing damage.

표 6 Table 6

Figure pat00006
Figure pat00006

위의 [표 6]에서와 같이, 실시예에 따라 제조된 미장용 첨가제를 이용한 미장용 몰탈이 비교예 1과 비교예 2에따라 제조된 몰탈에 비해 흡수율이 낮았다. As shown in [Table 6] above, the cosmetic mortar using the cosmetic additive prepared according to Example had a lower absorption rate than the mortar prepared according to Comparative Examples 1 and 2.

이상, 본 발명의 바람직한 일 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 일 실시예는 모든 면에서 예시적인 것이며 한정적이 아닌것으로 이해해야만 한다. In the above, a preferred embodiment of the present invention has been described, but those of ordinary skill in the art to which the present invention pertains will understand that the present invention may be embodied in other specific forms without changing the technical spirit or essential features. will be able Therefore, it should be understood that the embodiment described above is illustrative in all respects and not restrictive.

Claims (5)

석고 40 내지 80 중량부, 활성탄 5 내지 35 중량부, 식물성 첨가제 2 내지 10 중량부 및 흡착탈취제 2 내지 35중량부를 포함하되,
상기 석고는 이수석고 또는 무수석고가 사용되고,
상기 활성탄은 대나무, 참나무 및 소나무를 각각 500 내지 1000mm의 길이로 절단 가공하는 단계, 상기 절단 가공된 대나무, 참나무 및 소나무를 각각 1000 내지 1500℃의 온도로 탄화시키는 활성탄을 제조하는 단계, 상기 탄화된 활성탄을 각각 선별, 분리하는 단계, 및 상기 분리한 활성탄을 각각 분쇄하여 50 내지 250메쉬(mesh) 범위의 입경으로 선별하는 단계를 포함하여 제조되며,
상기 식물성 첨가제는 은행잎 분말 및 쑥 분말이 혼합되어 제조되며, 상기 은행잎 분말 및 쑥 분말은 60:40 내지 40:60의 중량비로 혼합되고,
상기 흡착탈취제는 규조토, 제올라이트, 흡착제 및 겔 라이트를 혼합하여 제조되는 것을 특징으로 하는 식물성 첨가제를 포함하는 친환경 미장용 첨가제.40 to 80 parts by weight of gypsum, 5 to 35 parts by weight of activated carbon, 2 to 10 parts by weight of a vegetable additive, and 2 to 35 parts by weight of an adsorption deodorant,
As the gypsum, dihydrate gypsum or anhydrite is used,
The activated carbon is a step of cutting and processing bamboo, oak, and pine to a length of 500 to 1000 mm, respectively, preparing activated carbon for carbonizing the cut-processed bamboo, oak and pine at a temperature of 1000 to 1500 ° C, respectively, the carbonized It is prepared including the steps of selecting and separating the activated carbon, respectively, and pulverizing the separated activated carbon, respectively, and selecting a particle size in the range of 50 to 250 mesh,
The vegetable additive is prepared by mixing ginkgo leaf powder and mugwort powder, wherein the ginkgo leaf powder and mugwort powder are mixed in a weight ratio of 60:40 to 40:60,
The adsorption deodorant is an eco-friendly cosmetic additive comprising a vegetable additive, characterized in that produced by mixing diatomaceous earth, zeolite, adsorbent and gel light. 제 1항에 있어서,
상기 활성탄은 경도 90 질량분율% 이상, 충전밀도 045 내지 052g/ml, 비표면적 1,000 내지 1,100m 2/g, 세공분포는 세공직경이 3Å 내지 12Å, 요오드 흡착력 1,000mg/g 이상, 세공용적 0501ml/g, pH 10~11, 페놀 흡착력 18ml/g, M·B탈색력 150ml/g 이상인 것이 사용되고, 상기 식물성 첨가제는 편백나무 분말, 목초액, 흑운모 분말 및 소금의 혼합물로 구성되는 추가 첨가제를 더 포함하되, 상기 추가 첨가제는 상기 은행잎 분말 및 쑥 분말 전체 100 중량부를 기준으로 하여 20 내지 50 중량부의 중량비율로 포함되며, 상기 흡착탈취제는 상기 규조토, 제올라이트, 흡착제 및 겔 라이트가 각각 규조토 10 내지 30 중량부, 제올라이트 25 내지 45 중량부, 흡착제 25 내지 45 중량부, 겔 라이트 10 내지 25 중량부의 중량비율로 혼합되어 제조되는 것을 특징으로 하는 식물성 첨가제를 포함하는 친환경 미장용 첨가제The method of claim 1,
The activated carbon has a hardness of 90% by mass or more, a packing density of 045 to 052 g/ml, a specific surface area of 1,000 to 1,100 m 2/g, and the pore distribution has a pore diameter of 3 Å to 12 Å, an iodine adsorption power of 1,000 mg/g or more, a pore volume of 0501 ml/ g, pH 10-11, phenol adsorption power 18ml/g, M B discoloration power 150ml/g or more is used, and the vegetable additive further comprises an additional additive consisting of a mixture of cypress powder, wood vinegar, biotite powder and salt , The additional additive is included in a weight ratio of 20 to 50 parts by weight based on 100 parts by weight of the total ginkgo leaf powder and mugwort powder, and the adsorption deodorant contains 10 to 30 parts by weight of the diatomaceous earth, zeolite, adsorbent and gelite, respectively. Eco-friendly cosmetic additive comprising a vegetable additive, characterized in that it is mixed in a weight ratio of 25 to 45 parts by weight of zeolite, 25 to 45 parts by weight of adsorbent, and 10 to 25 parts by weight of gelite 제 2항에 있어서,
상기 추가 첨가제를 구성하는 편백나무 분말, 목초액, 흑운모 분말 및 소금은 각각 편백나무 분말 10 내지 20중량부, 목초액 5 내지 15 중량부, 흑운모 분말 5 내지 10 중량부, 소금 10 내지 15 중량부의 중량비율로 혼합되어 사용되고,
상기 흑운모는 분말화되기 전에 1300 내지 1500℃의 범위 내에서 열처리를 진행한 후 사용되며, 상기 소금은 1000℃ 내지 1200℃에서 8 내지 10시간 동안 가열하여 구운 천일염이 사용되는 것을 특징으로 하는 식물성 첨가제를 포함하는 친환경 미장용 첨가제.3. The method of claim 2,
Cypress powder, wood vinegar, biotite powder and salt constituting the additional additive are each 10 to 20 parts by weight of cypress powder, 5 to 15 parts by weight of wood vinegar, 5 to 10 parts by weight of biotite powder, and 10 to 15 parts by weight of salt. used in combination with
The biotite is used after heat treatment within the range of 1300 to 1500° C. before being powdered, and the salt is a vegetable additive characterized in that the salt is heated and baked at 1000° C. to 1200° C. for 8 to 10 hours. Eco-friendly cosmetic additives containing. 미장용 첨가제 및 시멘트가 혼합되어 제조되되,
상기 미장용 첨가제는,
석고 40 내지 80 중량부, 활성탄 5 내지 35 중량부, 식물성 첨가제 2 내지 10 중량부 및 흡착탈취제 2 내지 35 중량부를 포함하되,
상기 석고는 이수석고 또는 무수석고가 사용되고,
상기 활성탄은 대나무, 참나무 및 소나무를 각각 500 내지 1000mm의 길이로 절단 가공하는 단계, 상기 절단 가공된 대나무, 참나무 및 소나무를 각각 1000 내지 1500℃의 온도로 탄화시키는 활성탄을 제조하는 단계, 상기 탄화된 활성탄을 각각 선별, 분리하는 단계, 및 상기 분리한 활성탄을 각각 분쇄하여 50 내지 250메쉬(mesh) 범위의 입경으로 선별하는 단계를 포함하여 제조되는 것을 특징으로, 경도 90 질량분율% 이상, 충전밀도 045 내지 052g/ml, 비표면적 1,000 내지 1,100m
2/g, 세공분포는 세공직경이 3Å 내지 12Å, 요오드 흡착력 1,000mg/g 이상, 세공용적 0501ml/g, pH 10~11, 페놀 흡착력 18ml/g, M·B탈색력 150ml/g 이상인 것이 사용되고, 상기 식물성 첨가제는 은행잎 분말 및 쑥 분말이 혼합되어 제조되며, 상기 은행잎 분말 및 쑥 분말은 60:40 내지 40:60의 중량비로 혼합되되, 편백나무 분말, 목초액, 흑운모 분말 및 소금의 혼합물로 구성되는 추가 첨가제를 더 포함하며, 상기 추가 첨가제는 상기 은행잎 분말 및 쑥 분말 전체 100 중량부를 기준으로 하여 20 내지 50 중량부의 중량비율로 포함되는 것이 특징이며,
상기 흡착탈취제는 규조토, 제올라이트, 흡착제 및 겔 라이트를 혼합하여 제조되되, 상기 규조토, 제올라이트, 흡착제 및 겔 라이트가 각각 규조토 10 내지 30 중량부, 제올라이트 25 내지 45 중량부, 흡착제 25 내지 45 중량부, 겔 라이트 10 내지 25 중량부의 중량비율로 혼합되어 제조되며,상기 시멘트는 고로슬래그 시멘트가 사용되고, 상기 미장용 첨가제는 고로슬래그 시멘트 전체 100 중량부를 기준으로 하여 40 내지 60 중량부가 포함되는 것을 특징으로 하는 미장용 첨가제를 이용한 미장용 시멘트.It is manufactured by mixing cosmetic additives and cement,
The cosmetic additive,
40 to 80 parts by weight of gypsum, 5 to 35 parts by weight of activated carbon, 2 to 10 parts by weight of a vegetable additive, and 2 to 35 parts by weight of an adsorption deodorant,
As the gypsum, dihydrate gypsum or anhydrite is used,
The activated carbon is a step of cutting and processing bamboo, oak, and pine to a length of 500 to 1000 mm, respectively, preparing activated carbon for carbonizing the cut-processed bamboo, oak and pine at a temperature of 1000 to 1500 ° C, respectively, the carbonized It is characterized in that it is prepared including the steps of selecting and separating the activated carbon, respectively, and pulverizing the separated activated carbon, respectively, and selecting a particle size in the range of 50 to 250 mesh, hardness of 90% by mass or more, packing density 045 to 052 g/ml, specific surface area from 1,000 to 1,100 m
2/g, pore distribution: pore diameter of 3 Å to 12 Å, iodine adsorption power of 1,000 mg/g or more, pore volume of 0501 ml/g, pH 10-11, phenol adsorption power of 18 ml/g, M B discoloration power of 150 ml/g or more are used , The vegetable additive is prepared by mixing ginkgo leaf powder and mugwort powder, wherein the ginkgo leaf powder and mugwort powder are mixed in a weight ratio of 60:40 to 40:60, consisting of a mixture of cypress powder, wood vinegar, biotite powder and salt It is characterized in that the additional additive is included in a weight ratio of 20 to 50 parts by weight based on 100 parts by weight of the total ginkgo leaf powder and mugwort powder,
The adsorption deodorant is prepared by mixing diatomaceous earth, zeolite, adsorbent and gelite, wherein the diatomaceous earth, zeolite, adsorbent and gelite are each 10 to 30 parts by weight of diatomaceous earth, 25 to 45 parts by weight of zeolite, 25 to 45 parts by weight of adsorbent, It is prepared by mixing gelite in a weight ratio of 10 to 25 parts by weight, the cement is blast furnace slag cement, and the cosmetic additive is 40 to 60 parts by weight based on 100 parts by weight of the total blast furnace slag cement. Plastering cement using cosmetic additives. 제 4항에 있어서
상기 추가 첨가제를 구성하는 편백나무 분말, 목초액, 흑운모 분말 및 소금은 각각 편백나무 분말 10 내지 20 중량부, 목초액 5 내지 15 중량부, 흑운모 분말 5 내지 10 중량부, 소금 10 내지 15 중량부의 중량비율로 혼합되어 사용되고,
상기 흑운모는 분말화되기 전에 1300 내지 1500℃의 범위 내에서 열처리를 진행한 후 사용되며, 상기 소금은 1000℃ 내지 1200℃에서 8 내지 10시간 동안 가열하여 구운 천일염이 사용되는 것을 특징으로 하는 미장용 첨가제를 이용한 미장용 시멘트.5. The method of claim 4
Cypress powder, wood vinegar, biotite powder and salt constituting the additional additive are each 10 to 20 parts by weight of cypress powder, 5 to 15 parts by weight of wood vinegar, 5 to 10 parts by weight of biotite powder, and 10 to 15 parts by weight of salt. used in combination with
The biotite is used after heat treatment within the range of 1300 to 1500° C. before being powdered, and the salt is used for plastering, characterized in that the salt is heated and baked at 1000° C. to 1200° C. for 8 to 10 hours. Cement for plastering with additives.
KR1020210065739A 2021-05-21 2021-05-21 A Environmental-friendly Plastering Additives Containing Vegetable Additives and Environmental-frie ndly Plastering Cement Using the Same and Mortar Containing the Same KR20210070953A (en)