KR20210033840A - Dental compostion and mehod for preparing oral device comprising same - Google Patents

Dental compostion and mehod for preparing oral device comprising same Download PDF

Info

Publication number
KR20210033840A
KR20210033840A KR1020190115643A KR20190115643A KR20210033840A KR 20210033840 A KR20210033840 A KR 20210033840A KR 1020190115643 A KR1020190115643 A KR 1020190115643A KR 20190115643 A KR20190115643 A KR 20190115643A KR 20210033840 A KR20210033840 A KR 20210033840A
Authority
KR
South Korea
Prior art keywords
cbma
dental composition
thermoplastic resin
composition
dental
Prior art date
Application number
KR1020190115643A
Other languages
Korean (ko)
Other versions
KR102238313B1 (en
Inventor
최성환
권재성
김걸
이명진
김지영
서지영
유재훈
Original Assignee
연세대학교 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 연세대학교 산학협력단 filed Critical 연세대학교 산학협력단
Priority to KR1020190115643A priority Critical patent/KR102238313B1/en
Publication of KR20210033840A publication Critical patent/KR20210033840A/en
Application granted granted Critical
Publication of KR102238313B1 publication Critical patent/KR102238313B1/en

Abstract

Provided in the present specification is a dental composition comprising CBMA and a thermoplastic resin. The dental composition can overcome the limitations, in the formation of a biofilm, of a conventional dental composition composed of only a thermoplastic resin.

Description

치과용 조성물 및 이를 포함하는 구강 내 장치 제조 방법{DENTAL COMPOSTION AND MEHOD FOR PREPARING ORAL DEVICE COMPRISING SAME}Dental composition and method for manufacturing an intraoral device including the same TECHNICAL FIELD [DENTAL COMPOSTION AND MEHOD FOR PREPARING ORAL DEVICE COMPRISING SAME}

본 발명은 치과용 조성물에 관한 것으로, 보다 구체적으로는 교정 치료에 이용되는 구강 내 장치에 적용되어 방오 효과를 제공할 수 있는 치과용 조성물 및 이를 포함하는 구강 내 장치 제조 방법에 관한 것이다. The present invention relates to a dental composition, and more particularly, to a dental composition that can provide an antifouling effect by being applied to an intraoral device used for orthodontic treatment, and a method of manufacturing an intraoral device including the same.

최근 안모 개선에 대한 관심이 증가하면서 교정 치료에 대한 요구가 증가하고 있다. 이에 따라, 상악 또는 하악 악궁에 탈착이 가능하게 장착되어 치아의 이동 및 치아의 위치 유지 등의 기능을 하는 구강 내 장치인, 가철성 교정장치 및 리테이너 (retainer), 턱관절 장애의 치료를 위한 교합안정장치 (occlusal splint) 를 착용하는 환자의 빈도 또한 증가하고 있다. Recently, as interest in facial improvement has increased, the demand for orthodontic treatment is increasing. Accordingly, a removable orthodontic device and a retainer, a removable orthodontic device and a retainer, which are detachably mounted on the maxillary or mandibular arch to function such as moving teeth and maintaining the position of teeth, and stabilizing occlusion for the treatment of jaw joint disorders. The frequency of patients wearing occlusal splints is also increasing.

이러한, 구강 내 장치의 소재는 찬 음식 및 더운 음식 등에 의한 온도 변화, 산성 및 알칼리성 음식 등에 의한 산도 변화 및 저작하는 힘에 의한 압력 변화가 심하고, 항상 타액에 젖어있는 사람 구강의 특성에 견딜 수 있어야 한다. The material of these intraoral devices must be able to withstand the characteristics of the oral cavity of a person who is always wet with saliva, temperature changes due to cold and hot foods, acidity changes due to acidic and alkaline foods, and pressure changes due to masticating force. do.

나아가, 구강 내 장치는 대부분 최소 1년 이상 착용되어, 브러쉬질과 같은 기계적 세척이 무시되면 세균성 플라그 (bacterial plaque) 및 치석이 부착될 수 있다. 또한, 습한 구강 내 환경으로 인해 바이오필름 (biofilm) 이 쉽게 형성될 수 있으며, 형성된 바이오필름은 박테리아 및 곰팡이의 응집 형성을 더 야기시킬 수 있다.Furthermore, most intraoral devices are worn for at least one year, and if mechanical cleaning such as brushing is neglected, bacterial plaque and tartar may adhere. In addition, due to the humid oral environment, a biofilm may be easily formed, and the formed biofilm may further cause the formation of agglomeration of bacteria and fungi.

이에, 구강 내의 온도, 산도, 압력 및 습도 변화 등에 견딜수 있는 적절한 단단함을 구비하고, 박테리아 및 곰팡이의 번식이 어려우며, 인체에 대한 알레르기 및 내분비 교란과 같은 악영향을 끼치는 물질에 대한 용출이 없는 안정성 높은 소재가 요구되고 있다.Therefore, it is a highly stable material that has adequate hardness to withstand changes in temperature, acidity, pressure and humidity in the oral cavity, it is difficult to propagate bacteria and fungi, and does not dissolve substances that have adverse effects such as allergies to the human body and endocrine disturbance. Is required.

발명의 배경이 되는 기술은 본 발명에 대한 이해를 보다 용이하게 하기 위해 작성되었다. 발명의 배경이 되는 기술에 기재된 사항들이 선행기술로 존재한다고 인정하는 것으로 이해되어서는 안 된다. The technology that is the background of the invention has been prepared to facilitate understanding of the present invention. It should not be understood as an admission that the matters described in the technology underlying the invention exist as prior art.

구강 내 장치에는 취급 용이성, 기계적 특성 및 저렴한 비용으로 인해 폴리메틸메타크릴레이트 (poly methyl methacrylate, PMMA) 같은 아크릴계 고분자, 폴리카보네이트 (poly carbonate, PC), 폴리에틸렌테레프탈레이트 (polyethylene terephthalate, PET) 등과 같은 열가소성 수지가 사용되고 있다. 특히, 이중 PMMA가 가장 널리 쓰이고 있다. Due to its ease of handling, mechanical properties, and low cost, oral devices include acrylic polymers such as polymethyl methacrylate (PMMA), polycarbonate (PC), and polyethylene terephthalate (PET). Thermoplastic resins are being used. In particular, PMMA is the most widely used.

PMMA는 내마모성, 내화학성, 내열성과 같은 기계적 특성이 우수할 뿐만 아니라 유해성분의 용출이 거의 없기 때문에 생체 친화성이 우수하여 치과용을 비롯한 의료용 재료로 널리 이용되고 있다. 그러나, PMMA는 중합 시 발생한 기포 등으로 인해 표편이 거칠어 질 수 있다. 이러한, PMMA의 표면 거침성은 치은 조직면과의 상시적이며 긴밀한 접촉관계를 가지는 구강 내 장치 내면 상에 세균부착 및 바이오필름 형성이 쉽게 유발될 수 있으며, 이로 인해 만성 염증상태인 의치 구내염을 야기할 수 있으므로, 항균성이 낮다는 문제점이 있다.PMMA has excellent mechanical properties such as abrasion resistance, chemical resistance, and heat resistance, and has excellent biocompatibility because it hardly dissolves harmful components, so it is widely used as a medical material including dentistry. However, PMMA may have a rough surface due to air bubbles generated during polymerization. The surface roughness of PMMA can easily cause bacterial adhesion and biofilm formation on the inner surface of the device in the oral cavity that has a constant and close contact relationship with the gingival tissue surface, and this can lead to denture stomatitis, which is a chronic inflammatory state. Therefore, there is a problem that antibacterial properties are low.

이에, PMMA의 표면 거침성을 해소하기 위하여 PMMA로 이루어진 구강 내 장치는 연삭, 연마, 폴리싱 등의 표면 가공을 필수적으로 수행하게 된다. 그러나, 표면 가공시에 스크래치, 보풀 등이 발생하여 최종 완제품을 만드는데 가공시간이 오래 걸리고, 이는 제조비용의 증가를 유발하게 된다. 이러한 점에서, 종래의 열가소성 수지를 이용한 구강 내 장치는 한계를 갖고 있다.Accordingly, in order to eliminate the surface roughness of PMMA, an intraoral device made of PMMA essentially performs surface processing such as grinding, polishing, and polishing. However, scratches and fluffs are generated during surface processing, so it takes a long time to produce the final finished product, which causes an increase in manufacturing cost. In this respect, conventional intraoral devices using thermoplastic resins have limitations.

이상의 문제점을 해결하기 위해, 내구성 및 항균성이 증진되어 보다 나은 교정 치료 예후를 제공할 수 있는 치과용 조성물의 개발이 지속적으로 요구되고 있다.In order to solve the above problems, there is a continuous demand for the development of a dental composition capable of providing a better orthodontic treatment prognosis by improving durability and antibacterial properties.

종래의 열 가소성 수지인 PMMA를 포함하는 치과용 조성물이 갖는 문제점을 해결하기 위한 방안으로, PMMA와 함께 아크릴로니트릴 부타디엔 스티렌 (Acrylonitrile Butadiene Styrene, ABS) 과 같은 물질이 조합된 복합 수지로 이루어진 치과용 조성물의 이용이 제안되었다. As a solution to the problem of dental compositions containing PMMA, which is a conventional thermoplastic resin, dental use made of a composite resin in which a material such as acrylonitrile butadiene styrene (ABS) is combined with PMMA. The use of the composition has been proposed.

그러나, 종래의 복합 수지로는 여전히 구강 내 장치의 충분한 교정력, 결속력 및 항균성을 가지기에는 부족하여, 보다 높은 교정력, 결속력 및 항균성을 가지고, 장시간 사용 가능한 치과용 조성물을 포함하는 구강 내 장치가 요구되고 있다.However, the conventional composite resin is still insufficient to have sufficient orthodontic power, binding power, and antibacterial properties of the oral device, and thus an intraoral device including a dental composition that can be used for a long time with higher orthodontic power, binding power and antibacterial property is required have.

한편, 본 발명의 발명자들은, 상기와 같은 치과용 조성물로서의 열가소성 수지가 갖는 한계를 극복하기 위해, 병원성 박테리아의 감염을 방지하는 항균 활성의 증진의 필요성에 대하여 인지할 수 있었다. On the other hand, the inventors of the present invention were able to recognize the necessity of enhancing antibacterial activity to prevent infection of pathogenic bacteria in order to overcome the limitations of the thermoplastic resin as a dental composition as described above.

이에, 본 발명의 발명자들은 열가소성 수지와 같은 치과용 조성물과 함께 구강 내 장치에 적용되어 박테리아에 의한 감염을 효과적으로 방지할 수 있는 새로운 치과용 조성물에 대하여 연구 개발하였다. Accordingly, the inventors of the present invention have researched and developed a new dental composition that can effectively prevent infection by bacteria by being applied to an intraoral device together with a dental composition such as a thermoplastic resin.

그 결과, 본 발명의 발명자들은, 쌍성 이온성 물질을 열가소성 수지와 함께 이용할 경우, 열가소성 수지를 단독으로 이용했을 때 보다 표면 단백질 및 박테리아 흡착의 차단 효과가 증가한 것을 발견하기에 이르렀다. As a result, the inventors of the present invention have come to find that when the zwitterionic material is used together with a thermoplastic resin, the blocking effect of the adsorption of surface proteins and bacteria is increased compared to when the thermoplastic resin is used alone.

보다 구체적으로, 본 발명의 발명자들은 쌍성 이온성 물질 중, CBMA (carboxybetaine methacrylate) 가 첨가된 치과용 조성물에 대하여, 단백질과 박테리아의 흡착을 차단하는 방오 (anti-fouling) 효과에 기여하는 자기 결합을 감소시킬 수 있음을 확인할 수 있었다. 이에, 본 발명의 발명자들은, CBMA와 같은 쌍성 이온성 물질이 첨가된 치과용 조성물에 대하여 생물 방오 효과 및 항균성 향상을 기대할 수 있었다.More specifically, the inventors of the present invention have made magnetic bonding that contributes to the anti-fouling effect of blocking the adsorption of proteins and bacteria with respect to the dental composition to which CBMA (carboxybetaine methacrylate) is added among the zwitterionic materials. It was confirmed that it can be reduced. Accordingly, the inventors of the present invention could expect to improve the biofouling effect and antimicrobial properties of a dental composition to which a binary ionic substance such as CBMA is added.

이에, 본 발명이 해결하고자 하는 과제는, CBMA 및 열가소성 수지를 포함하는, 치과용 조성물을 제공하는 것이다.Thus, the problem to be solved by the present invention is to provide a dental composition comprising CBMA and a thermoplastic resin.

본 발명이 해결하고자 하는 다른 과제는, 치과용 조성물을 포함하는 구강 내 장치를 제공하는 것이다. Another problem to be solved by the present invention is to provide an intraoral device comprising a dental composition.

본 발명이 해결하고자 하는 또 다른 과제는, 치과용 조성물을 포함하는 구강 내 장치의 제조 방법을 제공하는 것이다. Another problem to be solved by the present invention is to provide a method of manufacturing an intraoral device comprising a dental composition.

본 발명의 과제들은 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다. The problems of the present invention are not limited to the problems mentioned above, and other problems that are not mentioned will be clearly understood by those skilled in the art from the following description.

본 발명의 일 실시예에 따르면, CBMA 및 열가소성 수지를 포함하는, 치과용 조성물이 제공된다.According to an embodiment of the present invention, a dental composition comprising CBMA and a thermoplastic resin is provided.

본 명세서에서 사용되는 용어, "CBMA (carboxybetaine methacrylate)"는 쌍성 이온성 물질로서, 강한 정전기 상호작용을 통하여 수화 쉘 (hydration shell) 을 형성할 수 있는 물질을 의미할 수 있다. 또한, CBMA는 쌍성 이온성 물질 중에서 친수성이 높고 자기 결합 (self-association) 이 적은 것으로 알려져 있다. 이때, 자기 결합이 높은 쌍성 이온성 물질은 항 고분자 전해질 효과 (anti- polyelectrolyte effect) 및 소수성을 유발하여, 쌍성 이온성 물질의 생물 부착 방지 효과 (anti-biofouling effect) 를 상실할 수 있다.The term "carboxybetaine methacrylate (CBMA)" as used herein is a binary ionic material, and may mean a material capable of forming a hydration shell through strong electrostatic interaction. In addition, CBMA is known to have high hydrophilicity and low self-association among zwitterionic materials. In this case, the zwitterionic material having high magnetic bonding may cause an anti-polyelectrolyte effect and hydrophobicity, and thus the anti-biofouling effect of the zwitterionic material may be lost.

이러한 CBMA는 비특이적 단백질 접착을 방지할 수 있으며, 박테리아 흡착을 차단하는 방오 효과 (anti-fouling) 를 제공할 수 있다. 이에, CBMA는 치과용 조성물 (composite materials), 교정용 시멘트 (orthodontic cement), 및 치아 접착제 (dentin bonding agents) 의 용도로 이용될 수 있다.Such CBMA can prevent non-specific protein adhesion and can provide an anti-fouling effect of blocking bacterial adsorption. Accordingly, CBMA can be used for dental compositions (composite materials), orthodontic cements, and dental adhesives (dentin bonding agents).

본 명세서에서 사용되는 용어, "쌍성 이온성 물질"은 분자 내에 산성 및 염기성 원자단을 가지고 있고, 양쪽의 기가 동시에 이온화 상태이며 음, 양의 두 전하를 갖고 있는 이온성 물질을 의미할 수 있다. As used herein, the term "zinctive ionic substance" may mean an ionic substance having acidic and basic atomic groups in a molecule, both groups in an ionized state at the same time, and having both negative and positive charges.

한편, CBMA와 같은 쌍성 이온성 물질은, 열가소성 수지와 함께 이용될 경우, 열가소성 수지를 단독으로 이용했을 때 보다 단백질 및 박테리아의 흡착을 높은 수준으로 차단할 수 있다. 예를 들어, 쌍성 이온성 물질은, CBMA 같은 열가소성 수지와 함께 치과용 조성물에 이용될 경우, 박테리아성 바이오필름의 흡착을 차단하는 방오 효과를 향상시킬 수 있다. 이에, 쌍성 이온성 물질은 열가소성 수지와 함께 치과용 조성물로서 이용될 수 있다. On the other hand, when a zwitterionic material such as CBMA is used together with a thermoplastic resin, it is possible to block adsorption of proteins and bacteria to a higher level than when the thermoplastic resin is used alone. For example, when the zwitterionic material is used in a dental composition together with a thermoplastic resin such as CBMA, the antifouling effect of blocking the adsorption of the bacterial biofilm can be improved. Thus, the zwitterionic material may be used as a dental composition together with a thermoplastic resin.

본 발명의 특징에 따르면, 치과용 조성물은 MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), 트리고넬린 (trigonelline), 엑토인 (ectoine), 베타인 (betaine), 설포베타인 메타크릴레이트 (sulfobetaine methacrylate), SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-(3-methacryloylimino)propyl-N,N-dimethylammonio propanesulfonate) 및 SPV (3-(2'-vinyl-pyridinio)propanesulfonate) 으로 이루어진 그룹 중 적어도 하나인 쌍성 이온성 물질을 더 포함할 수 있다.According to a feature of the present invention, the dental composition is MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), trigonelline, ecto Phosphorus (ectoine), betaine (betaine), sulfobetaine methacrylate, SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-(3-methacryloylimino) It may further include a binary ionic material that is at least one of the group consisting of propyl-N,N-dimethylammonio propanesulfonate) and SPV (3-(2'-vinyl-pyridinio)propanesulfonate).

본 발명의 다른 특징에 따르면, CBMA의 함량은 치과용 조성물의 전체 질량에 대하여 1.5 내지 5 wt %일 수 있다. According to another feature of the present invention, the content of CBMA may be 1.5 to 5 wt% based on the total mass of the dental composition.

나아가, CBMA의 함량이 치과용 조성물의 전체 질량에 대하여 1.5 내지 5 wt % 로 함유된 경우보다 바람직하게, 치과용 조성물의 전체 질량에 대하여 1.5 내지 3 wt %로 함유된 치과용 조성물의 기계적 특성은 치과용 조성물에 대한 ISO 표준에 충족되는 굴곡 강도 (flexural strength), 탄성 계수 (elastic modulus) 및 경도 (vickers hardness) 를 가질 수 있다. 한편, 치과용 조성물의 전체 질량에 대하여 CBMA가 5 wt % 초과로 함유될 경우, CBMA 분말의 혼합 및 분포가 어려워져 PMMA에 대한 미세 결합의 응력 (stress) 으로 집중될 수 있다. 결과적으로, 치과용 조성물의 전체 질량에 대하여 CBMA가 5 wt % 초과로 함유될 경우, 치과용 조성물의 굴곡 강도 (flexural strength), 탄성 계수 (elastic modulus) 및 경도 (vickers hardness) 가 치과용 조성물의 전체 질량에 대하여 1.5 내지 5 wt % 로 함유된, 바람직하게 치과용 조성물의 전체 질량에 대하여 1.5 내지 3 wt % 로 함유된 치과용 조성물 기준 보다 낮아질 수 있다.Furthermore, the mechanical properties of the dental composition contained in an amount of 1.5 to 3 wt% with respect to the total mass of the dental composition are more preferable than when the content of CBMA is contained in an amount of 1.5 to 5 wt% with respect to the total mass of the dental composition. It can have flexural strength, elastic modulus, and vickers hardness that meet ISO standards for dental compositions. On the other hand, when CBMA is contained in an amount of more than 5 wt% with respect to the total mass of the dental composition, mixing and distribution of the CBMA powder may be difficult, and thus the stress of micro-bonding to PMMA may be concentrated. As a result, when CBMA is contained in an amount of more than 5 wt% with respect to the total mass of the dental composition, the flexural strength, elastic modulus, and vickers hardness of the dental composition are It may be lower than the standard of the dental composition contained in 1.5 to 5 wt% with respect to the total mass, preferably 1.5 to 3 wt% with respect to the total mass of the dental composition.

나아가, 본 발명의 치과용 조성물은, 치과용 조성물의 전체 질량에 대하여 1.5 내지 5 wt %, 보다 바람직하게, 치과용 조성물의 전체 질량에 대하여 1.5 내지 3 wt % 의 CBMA의 함량에서 박테리아 및 단백질에 대한 방오 효과가 다른 함량에서보다 우수할 수 있다. Furthermore, the dental composition of the present invention is applied to bacteria and proteins in a content of CBMA of 1.5 to 5 wt %, more preferably, 1.5 to 3 wt% of the total mass of the dental composition. The antifouling effect against it may be better than at other contents.

본 명세서에서 사용되는 용어, "열가소성 수지"는 열이나 압력으로 소성 변형을 시켜 성형할 수 있으며, 치과용으로 사용 가능한 고분자 화합 물질을 의미할 수 있다. As used herein, the term "thermoplastic resin" may refer to a polymeric compound that can be molded by plastic deformation by heat or pressure, and can be used for dentistry.

본 발명의 또 다른 특징에 따르면, 열가소성 수지는 PMMA (ploy methyl methacrylate), 폴리에틸렌 (polyethylene), 폴리프로필렌 (polypropylene), 폴리카보네이트 (polycarbonate), 폴리에틸렌 테레프탈레이트 (polyethylene terephthalate), 나일론 (nylon), 실리콘 및 ABS (acrylonitrile-butadien-styrene) 중 적어도 하나일 수 있다. 바람직하게, 열가소성 수지는, PMMA일 수 있으나, 이에 제한되는 것은 아니다.According to another feature of the present invention, the thermoplastic resin is PMMA (ploy methyl methacrylate), polyethylene, polypropylene, polycarbonate, polyethylene terephthalate, nylon, silicone And it may be at least one of ABS (acrylonitrile-butadien-styrene). Preferably, the thermoplastic resin may be PMMA, but is not limited thereto.

이때, PMMA는 높은 심미성, 화학 및 물리적 안정성, 상대적으로 낮은 독성 및 저렴한 가격 등으로 인하여 치과용 조성물로서 우수한 장점을 가지고 있는 유기 분자이다. 그러나, 이러한, PMMA의 자체 물성만으로는 저작압 등에 견딜 수 있는 정도의 충분한 경도, 강도, 내마모성 및 항균성을 갖지 못한다. 보다 구체적으로, PMMA는 중량체 (polymer) 와 단량체 (monomer) 가 합쳐져서 중합되는 형태로, 중합과정 중에 기포가 많이 발생하며, 이러한 기포는 박테리아의 서식지가 될 수 있으므로 구강 내 장치의 상태가 불량하게 될 수 있다. 이에, PMMA에 생물 부착 방지 효과를 제공할 수 있는 쌍성 이온성 물질인 CBMA가 첨가하여 항균성을 향상시킬 수 있다. 보다 구체적으로, CBMA는 높은 친수성으로 인하여 안정적인 수화 쉘이 형성되고, 이로 인하여 비특이적 단백질 접착 및 박테리아 흡착을 차단하는 우수한 생물 부착 방지 효과 즉, 방오 효과를 제공할 수 있다. 본 발명의 또 다른 특징에 따르면, 열가소성 수지의 함량은 치과용 조성물의 전체 질량에 대하여 95.0 내지 98.5 wt %일 수 있다. At this time, PMMA is an organic molecule that has excellent advantages as a dental composition due to high aesthetics, chemical and physical stability, relatively low toxicity, and low price. However, the PMMA does not have sufficient hardness, strength, abrasion resistance, and antibacterial properties that can withstand mastication pressure, etc. only with its own physical properties. More specifically, PMMA is a form in which a polymer and a monomer are combined and polymerized, and a lot of bubbles are generated during the polymerization process, and these bubbles can become a habitat for bacteria, so the condition of the device in the oral cavity is poor. Can be. Accordingly, CBMA, which is a binary ionic material capable of providing an effect of preventing biological adhesion, may be added to PMMA to improve antibacterial properties. More specifically, CBMA has a stable hydration shell due to its high hydrophilicity, and thus can provide an excellent anti-biofouling effect, that is, an antifouling effect, which blocks non-specific protein adhesion and bacterial adsorption. According to another feature of the present invention, the content of the thermoplastic resin may be 95.0 to 98.5 wt% based on the total mass of the dental composition.

그러나, CBMA 및 열가소성 수지의 함량은, 이에 제한되는 것은 아니며, 치과용 조성물의 함유로 달성하고자 하는 반응의 종류와 정도, 함유 대상이 되는 물질의 종류, 개체의 교정 여부, 치아 상태, 연령, 체중, 일반적인 건강 상태, 질병의 증세나 정도, 성별, 식이, 배설 및 해당 개체에 동시 또는 다른 시기에 함께 사용되는 약물 기타 조성물의 성분 등을 비롯한 여러 인자 및 의약 분야에서 잘 알려진 유사 인자에 따라 다양해질 수 있다. 나아가, 당해 기술 분야에서 통상의 지식을 가진 자는 목적하는 치과용 조성물 형성에 효과적인, CBMA 및 열가소성 수지의 함량을 용이하게 결정하고 함유할 수 있다.However, the content of CBMA and thermoplastic resin is not limited thereto, and the type and degree of reaction to be achieved by the inclusion of the dental composition, the type of material to be contained, whether or not the individual is corrected, tooth condition, age, weight , General health conditions, symptoms or severity of the disease, sex, diet, excretion, and components of drugs and other compositions used concurrently or at different times in the subject, as well as a number of factors and similar factors well known in the field of medicine. I can. Furthermore, those of ordinary skill in the art can easily determine and contain the content of CBMA and thermoplastic resin, which is effective in forming a desired dental composition.

한편, 열가소성 수지는 전술한 바와 같이 단독으로 이용되는 경우, 박테리아의 감염을 완벽하게 막을 수 없다는 한계점이 있을 수 있다. 이에, 쌍성 이온성 물질인 CBMA가 첨가된 치과용 조성물은, 박테리아성 바이오필름의 흡착을 차단하는 방오 효과를 제공할 수 있다.Meanwhile, when the thermoplastic resin is used alone as described above, there may be a limitation in that it cannot completely prevent infection of bacteria. Accordingly, the dental composition to which CBMA, which is a zwitterionic material, is added may provide an antifouling effect of blocking the adsorption of the bacterial biofilm.

보다 구체적으로, 본 발명의 또 다른 특징에 따르면, CBMA 및 열가소성 수지를 포함하는 치과용 조성물은, 칸디다균 (Candida albicans), 액티노마이세스 나이슬런디 (Actinomyces naeslundii), 베일로넬라 파르불라 (Veillonella parvula), 스트랩토코커스 소브리누스 (Streptococcus sobrinus), 스트랩토코커스 상기스 (Streptococcus sanguis), 스트랩토코커스 미티스 (Streptococcus mitior), 락토바실러스 카제이 (Lactbacillus casei), 락토바실러스 아시도필루스 (Lactbacillus acidophilus), 액티노마이세스 비스코서스 (Actinomyces viscosus) 및 액티노마이세스 네슬룬디 (Actinomyces naeslundii) 같은 구강 내에서 감염을 유도하는 박테리아에 대한 생물 부착을 방지하는 방오 효과를 제공할 수 있다.More specifically, according to another feature of the present invention, the dental composition comprising CBMA and a thermoplastic resin, Candida albicans, Actinomyces naeslundii, Baylonella parbula ( Veillonella parvula), Streptococcus sobrinus, Streptococcus sanguis, Streptococcus mitior, Lactbacillus casei, Lactbacillus casei, Lactobacillus acidophilus (Lactbacillus acidophilus), Actinomyces viscosus (Actinomyces viscosus) and Actinomyces naeslundii (Actinomyces naeslundii) can provide an antifouling effect to prevent biological adhesion to bacteria that induce infection in the oral cavity.

예를 들어, 본 발명의 또 다른 특징에 따르면, 상기 박테리아 노출 24시간 이후, 치과용 조성물에서의 박테리아의 밀도는 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 50 배 내지 300 배 낮은 수준일 수 있다.For example, according to another feature of the present invention, after 24 hours of exposure to the bacteria, the density of bacteria in the dental composition may be 50 to 300 times lower than that of a composition composed of only a thermoplastic resin without CBMA. have.

이때, 쌍성 이온성 물질인 CBMA는 항균 성질이 아닌 비특이적 단백질 반발성 의존적으로 생물 부착 방지성을 가질 수 있어, 치과용 조성물에 적용될 경우 전술한 박테리아의 흡착이 저해될 수 있다. At this time, CBMA, which is a binary ionic material, may have an antimicrobial property, but a non-specific protein repellency dependent, to prevent biological adhesion, and thus, when applied to a dental composition, adsorption of the aforementioned bacteria may be inhibited.

또한, 본 발명의 또 다른 특징에 따르면, 상기 박테리아 노출 48시간 이후, 치과용 조성물에서의 박테리아에 의한 바이오필름의 두께는 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 1.5 배 내지 2 배 낮은 수준일 수 있다. In addition, according to another feature of the present invention, after 48 hours of exposure to the bacteria, the thickness of the biofilm by the bacteria in the dental composition is 1.5 to 2 times lower than that of the composition consisting of only thermoplastic resin without CBMA. Can be

본 명세서에서 사용되는 용어, "바이오필름 (biofilm) "은 치아 및 치과용 구강 내 장치의 표면에 형성된 단백질, 곰팡이 및 박테리아 등으로 이루어진 군집을 의미할 수 있다. 이러한 바이오필름은 구강 내의 일정한 온도 및 습도와 박테리아의 영양이 되는 음식물 찌꺼기로 인해 계속 성장하여 두꺼워질 수 있다. 두꺼워진 바이오필름은 독성 물질이 생겨 충치 및 잇몸 염증을 일으키고, 결국 치은염과 치주염을 야기시킨다. 나아가, 바이오필름이 형성되면 그 위로 음식물 찌꺼기 등에 의한 단백질 등이 쌓여 플라그 (plaque) 가 형성되고, 플라그가 두꺼워지면서 딱딱해져 치석이 형성될 수 있다. 이에, 플라그 및 치석의 형성을 차단하기 위해서는 플라그 및 치석의 원인이 되는 바이오필름의 형성부터 저해시켜야 한다.As used herein, the term "biofilm" may refer to a group consisting of proteins, molds, bacteria, etc. formed on the surfaces of teeth and dental oral devices. These biofilms may continue to grow and thicken due to constant temperature and humidity in the oral cavity and food waste that is nutrient for bacteria. The thickened biofilm produces toxic substances, causing tooth decay and inflammation of the gums, eventually causing gingivitis and periodontitis. Furthermore, when the biofilm is formed, proteins, etc., are accumulated on the top of the biofilm, and plaque is formed, and the plaque becomes thick and hard, thereby forming tartar. Therefore, in order to block the formation of plaque and calculus, it is necessary to inhibit the formation of a biofilm that causes plaque and calculus.

나아가, 본 발명의 또 다른 특징에 따르면, 바이오필름의 바이오매스 밀도는 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 4 배 내지 6 배 낮은 수준일 수 있다.Further, according to another feature of the present invention, the biomass density of the biofilm may be 4 to 6 times lower than that of a composition comprising only a thermoplastic resin without CBMA.

본 명세서에서 사용되는 용어, "바이오매스 (biomass) "는 바이오필름에 형성되어 있는 군집의 전체 박테리아 생물량을 의미할 수 있다. As used herein, the term "biomass" may mean the total biomass of bacteria in a community formed on a biofilm.

한편, 본 발명의 또 다른 특징에 따르면, BSA 노출 4시간 이후, 상기 치과용 조성물에서의 단백질 흡착 수준은 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 1.5 배 내지 2 배 낮은 수준일 수 있다. On the other hand, according to another feature of the present invention, after 4 hours of exposure to BSA, the protein adsorption level in the dental composition may be 1.5 to 2 times lower than that of a composition comprising only a thermoplastic resin without CBMA.

또한, 본 발명의 또 다른 특징에 따르면, 효모 및 곰팡이 브로스를 포함하는 YM 배지 노출 4시간 이후, 상기 치과용 조성물에서의 단백질 흡착 수준은 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 1.5 배 내지 3 배 낮은 수준일 수 있다. In addition, according to another feature of the present invention, after 4 hours of exposure to the YM medium containing yeast and mold broth, the level of protein adsorption in the dental composition is 1.5 times to that of the composition consisting only of a thermoplastic resin without CBMA. It can be three times lower.

본 발명의 또 다른 특징에 따르면, 치과용 조성물은 안정화제, 난연제, 대전방지제, 연화제, 강화재, 충전재, 형광 중백제, 윤활제, 함입 감소제, 중축제 촉매, 소포제, 유화제, 증점제, 및 향료로 이루어진 그룹 중 적어도 하나를 더 포함할 수 있다. According to another feature of the present invention, the dental composition is a stabilizer, a flame retardant, an antistatic agent, a softener, a reinforcing material, a filler, a fluorescent whitening agent, a lubricant, an inclusion reducing agent, a polycondensing agent catalyst, an antifoaming agent, an emulsifying agent, a thickening agent, and a fragrance. It may further include at least one of the group consisting of.

본 발명의 또 다른 특징에 따르면, 치과용 조성물은 하이드록시프로필 메틸셀룰로스 (Hydroxypropyl Methylcellulose), 하이드록시에틸 셀룰로스 (Hydroxyethyl Cellulose), 하이드록시프로필 셀룰로스 (Hydroxypropyl Cellulose), 폴리비닐 알코올 (Polyvinyl Alcohol), 폴리비닐 피롤리돈 (Polyvinyl Pyrrolidone), 카보머 (Carbomer), 및 초산 비닐 수지 (Polyvinyl Acetate) 로 이루어진 그룹 중 적어도 하나의 접착성 물질을 더 포함할 수 있다.According to another feature of the present invention, the dental composition is hydroxypropyl methylcellulose (Hydroxypropyl Methylcellulose), hydroxyethyl cellulose (Hydroxyethyl Cellulose), hydroxypropyl cellulose (Hydroxypropyl Cellulose), polyvinyl alcohol (Polyvinyl Alcohol), poly It may further include at least one adhesive material from the group consisting of vinyl pyrrolidone (Polyvinyl Pyrrolidone), carbomer (Carbomer), and vinyl acetate resin (Polyvinyl Acetate).

그러나, 전술한 것에 제한되지 않고 본 발명의 치과용 조성물은 보다 다양한 첨가물을 더 포함할 수 있다. However, it is not limited to the above, and the dental composition of the present invention may further include a variety of additives.

본 발명의 일 실시예에 따르면, 전술한 특징의 치과용 조성물을 포함하는 구강 내 장치가 제공된다.According to an embodiment of the present invention, an intraoral device including the dental composition of the above-described characteristics is provided.

이때, 본 발명의 또 다른 특징에 따르면, 구강 내 장치는 가철성 교정장치, 의치, 국소의치, 마우스피스, 교합안정장치 및 나이트 가드로 이루어진 그룹 중 적어도 하나를 포함할 수 있다. 바람직하게, 구강 내 장치는, 교합안정장치일 수 있으나, 이에 제한되는 것은 아니다.In this case, according to another feature of the present invention, the intraoral device may include at least one of a group consisting of a removable orthodontic device, a denture, a local denture, a mouthpiece, an occlusal stabilizing device, and a night guard. Preferably, the intraoral device may be an occlusal stabilizing device, but is not limited thereto.

본 발명의 일 실시예에 따르면, 치과용 조성물 전체 질량에 대하여 1.5 내지 5 wt %의 CBMA 분말을 38 내지 39.4 wt %의 열가소성 수지 액체에 혼합시키는 단계, CBMA 분말이 혼합된 열가소성 수지 액체에 57 내지 59.1 wt %의 열가소성 수지 분말을 혼합시키는 단계, CBMA 분말, 열가소성 수지 분말 및 열가소성 수지 액체가 저온 중합되어 혼합 수지를 형성하는 단계 및 혼합 수지를 탄화 규소 원형 사포로 연마하는 단계를 포함하는 구강 내 장치 제조 방법이 제공된다.According to an embodiment of the present invention, mixing 1.5 to 5 wt% of CBMA powder with 38 to 39.4 wt% of a thermoplastic resin liquid based on the total mass of the dental composition, 57 to 57 to the thermoplastic resin liquid mixed with the CBMA powder Intraoral device comprising the step of mixing 59.1 wt% of thermoplastic resin powder, forming a mixed resin by low-temperature polymerization of CBMA powder, thermoplastic resin powder and thermoplastic resin liquid, and grinding the mixed resin with silicon carbide circular sandpaper A manufacturing method is provided.

나아가, 혼합시키는 단계에서, 안정화제, 난연제, 대전방지제, 연화제, 강화재, 충전재, 형광 중백제, 윤활제, 함입 감소제, 중축제 촉매, 소포제, 유화제, 증점제, 및 향료로 이루어진 그룹 중 적어도 하나가 더 혼합될 수 있다.Furthermore, in the mixing step, at least one of the group consisting of a stabilizer, a flame retardant, an antistatic agent, a softener, a reinforcing material, a filler, a fluorescent whitening agent, a lubricant, a content reducing agent, a polycondensing agent catalyst, an antifoaming agent, an emulsifier, a thickener, and a fragrance Can be further mixed.

또한, 혼합시키는 단계에서, 하이드록시프로필 메틸셀룰로스 (Hydroxypropyl Methylcellulose), 하이드록시에틸 셀룰로스 (Hydroxyethyl Cellulose), 하이드록시프로필 셀룰로스 (Hydroxypropyl Cellulose), 폴리비닐 알코올 (Polyvinyl Alcohol), 폴리비닐 피롤리돈 (Polyvinyl Pyrrolidone), 카보머 (Carbomer), 및 초산 비닐 수지 (Polyvinyl Acetate) 로 이루어진 그룹 중 적어도 하나의 접착성 물질이 더 혼합될 수 있다.In addition, in the mixing step, hydroxypropyl methylcellulose (Hydroxypropyl Methylcellulose), hydroxyethyl cellulose (Hydroxyethyl Cellulose), hydroxypropyl cellulose (Hydroxypropyl Cellulose), polyvinyl alcohol (Polyvinyl Alcohol), polyvinyl pyrrolidone (Polyvinyl At least one adhesive material from the group consisting of Pyrrolidone), Carbomer, and Polyvinyl Acetate may be further mixed.

이하, 실시예를 통하여 본 발명을 보다 상세히 설명한다. 다만, 이들 실시예는 본 발명을 예시적으로 설명하기 위한 것에 불과하므로 본 발명의 범위가 이들 실시예에 의해 한정되는 것으로 해석되어서는 아니된다. Hereinafter, the present invention will be described in more detail through examples. However, these examples are for illustrative purposes only, and the scope of the present invention should not be construed as being limited by these examples.

본 발명은, CBMA 및 열가소성 수지를 포함하는 치과용 조성물을 제공함으로써, 종래의 열가소성 수지 단독으로 구성된 치과용 조성물이 갖는 바이오 필름 형성과 연관된 한계점을 극복할 수 있다.The present invention, by providing a dental composition comprising CBMA and a thermoplastic resin, it is possible to overcome the limitations associated with the biofilm formation of the conventional dental composition composed of only a thermoplastic resin.

보다 구체적으로, 본 발명은, 열가소성 수지와 CBMA를 함께 이용함에 따라, 열가소성 수지를 단독으로 이용했을 때 보다 향상된 방오 효과를 제공할 수 있다. More specifically, according to the present invention, as the thermoplastic resin and CBMA are used together, an improved antifouling effect can be provided when the thermoplastic resin is used alone.

즉, 본 발명은, 구강내 장치에 적용되어 방오 작용과 함께 이에 따른 항균 활성을 제공하는 치과용 조성물을 제공함으로써, 박테리아에 의해 야기되는 감염에 의한 염증 반응을 예방하고, 우수한 항균력을 갖는 구강 내 장치를 제공할 수 있는 효과가 있다. That is, the present invention is applied to an intraoral device to provide a dental composition that provides antifouling action and antibacterial activity accordingly, thereby preventing an inflammatory reaction caused by infection caused by bacteria, and having excellent antibacterial activity in the oral cavity. There is an effect that the device can provide.

특히, 본 발명은, 구강 내 조직에 대하여 감염을 일으키는 칸디다균 (Candida albicans), 액티노마이세스 나이슬런디 (Actinomyces naeslundii), 베일로넬라 파르불라 (Veillonella parvula), 스트랩토코커스 소브리누스 (Streptococcus sobrinus), 스트랩토코커스 상기스 (Streptococcus sanguis), 스트랩토코커스 미티스 (Streptococcus mitior), 락토바실러스 카제이 (Lactbacillus casei), 락토바실러스 아시도필루스 (Lactbacillus acidophilus), 액티노마이세스 비스코서스 (Actinomyces viscosus) 및 액티노마이세스 네슬룬디 (Actinomyces naeslundii) 와 같은 병원성 박테리아의 생물 부착 방지 효과가 우수할 수 있다. In particular, the present invention relates to Candida albicans, Actinomyces naeslundii, Veillonella parvula, and Stratococcus sobrinus ( Streptococcus sobrinus), Streptococcus sanguis, Streptococcus mitior, Lactbacillus casei, Lactbacillus acidophilus, Actinomyces biscoccus (Actinomyces viscosus) and Actinomyces naeslundii (Actinomyces naeslundii) can be excellent in the prevention of biological adhesion of pathogenic bacteria.

본 발명에 따른 효과는 이상에서 예시된 내용에 의해 제한되지 않으며, 더욱 다양한 효과들이 본 명세서 내에 포함되어 있다. The effects according to the present invention are not limited by the contents exemplified above, and more various effects are included in the present specification.

도 1은 본 발명의 일 실시예에 따른 치과용 조성물을 포함하는 구강 내 장치의 제조 방법을 예시적으로 도시한 것이다.
도 2는 본 발명의 일 실시예에 따른 치과용 조성물의 조성 및 함량을 도시한 것이다.
도 3a은 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 습윤성을 나타내는 결과이다.
도 3b는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 기계적 특성을 나타내는 결과이다.
도 4는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 구강 내 장치에서의 단백질 흡착 수준을 나타내는 결과이다.
도 5a 내지 5c는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 박테리아 저해 수준을 나타내는 결과이다.
도 6a 내지 6b는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 구강 내 장치에서의 바이오필름을 나타내는 결과이다.
도 7a 및 7b는 본 발명의 일 실시예에 따른 치과용 조성물을 포함하는 구강 내 장치의 형성 평가를 나타내는 결과이다. 1 is an exemplary view showing a method of manufacturing an intraoral device including a dental composition according to an embodiment of the present invention.
Figure 2 shows the composition and content of the dental composition according to an embodiment of the present invention.
Figure 3a is a result showing the wettability according to the CBMA content in the dental composition according to an embodiment of the present invention.
Figure 3b is a result showing the mechanical properties according to the CBMA content in the dental composition according to an embodiment of the present invention.
Figure 4 is a result showing the protein adsorption level in the oral device according to the CBMA content in the dental composition according to an embodiment of the present invention.
5A to 5C are results showing the level of inhibition of bacteria according to the CBMA content in the dental composition according to an embodiment of the present invention.
6A to 6B are results showing a biofilm in an intraoral device according to the CBMA content in a dental composition according to an embodiment of the present invention.
7A and 7B are results showing evaluation of formation of an intraoral device including a dental composition according to an embodiment of the present invention.

본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나, 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. Advantages and features of the present invention, and a method of achieving them will become apparent with reference to the embodiments described below in detail together with the accompanying drawings. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in a variety of different forms, only the present embodiments are intended to complete the disclosure of the present invention, and common knowledge in the technical field to which the present invention pertains. It is provided to completely inform the scope of the invention to those who have, and the invention is only defined by the scope of the claims.

이하에서는 도 1을 참조하여, 본 발명의 다양한 실시예에 이용되는 치과용 조성물을 포함하는 구강 내 장치의 제조 방법을 설명한다.Hereinafter, a method of manufacturing an intraoral device including a dental composition used in various embodiments of the present invention will be described with reference to FIG. 1.

도 1은 본 발명의 일 실시예에 따른 치과용 조성물을 포함하는 구강 내 장치의 제조 방법을 예시적으로 도시한 것이다. 1 is an exemplary view showing a method of manufacturing an intraoral device including a dental composition according to an embodiment of the present invention.

도 1을 참조하면, 본 발명의 치과용 조성물을 포함하는 구강 내 장치의 제조 방법은, 먼저 CBMA 및 열가소성 수지를 혼합한다 (S110). 보다 구체적으로, 치과용 조성물 전체 질량에 대하여 38 내지 39.4 wt %의 열가소성 수지 액체에 치과용 조성물의 전체 질량에 대하여 1.5 내지 5 wt %의 CBMA 분말을 투입하고, 초음파 처리하에 분산시킨다. 그 다음, CBMA 분말이 혼합된 열가소성 수지 액체에 치과용 조성물 전체 질량에 대하여 57 내지 59.1 wt %의 열가소성 수지 분말을 투입하여 초음파 처리하에 1시간 동안 분산시키고, CBMA 및 열가소성 수지 분말이 혼합된 열가소성 수지 액체를 4시간 동안 자동 교반시켜준다. Referring to Figure 1, the method of manufacturing an intraoral device including the dental composition of the present invention, first, CBMA and a thermoplastic resin are mixed (S110). More specifically, in a thermoplastic resin liquid of 38 to 39.4 wt% with respect to the total mass of the dental composition, 1.5 to 5 wt% of CBMA powder with respect to the total mass of the dental composition is added and dispersed under ultrasonic treatment. Then, a thermoplastic resin powder of 57 to 59.1 wt% based on the total mass of the dental composition was added to the thermoplastic resin liquid mixed with CBMA powder, dispersed for 1 hour under ultrasonic treatment, and a thermoplastic resin mixed with CBMA and thermoplastic resin powder The liquid is automatically stirred for 4 hours.

이때, 구강 내 장치는 가철성 교정장치, 의치, 국소의치, 마우스피스, 교합안정장치 및 나이트 가드로 이루어진 그룹 중 적어도 하나를 포함할 수 있으나, 예를 들어 구강 내 장치는 교합안정장치일 수 있다.At this time, the intraoral device may include at least one of a group consisting of a removable orthodontic device, a denture, a local denture, a mouthpiece, an occlusal stabilizing device, and a night guard, but, for example, the intraoral device may be an occlusal stabilizing device.

또한, CMMA 및 열가소성 수지를 혼합시키는 단계 (S110) 에서, MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), 트리고넬린 (trigonelline), 엑토인 (ectoine), 베타인 (betaine), 설포베타인 메타크릴레이트 (sulfobetaine methacrylate), SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-(3-methacryloylimino)propyl-N,N-dimethylammonio propanesulfonate) 및 SPV (3-(2'-vinyl-pyridinio)propanesulfonate) 으로 이루어진 그룹 중 적어도 하나인 쌍성 이온성 물질 (Zwitterionic material) 이 더 포함될 수 있다.In addition, in the step of mixing CMMA and a thermoplastic resin (S110), MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), trigonelline ( trigonelline), ectoine, betaine, sulfobetaine methacrylate, SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-( At least one of the group consisting of 3-methacryloylimino)propyl-N,N-dimethylammonio propanesulfonate) and SPV (3-(2'-vinyl-pyridinio)propanesulfonate), a Zwitterionic material, may be further included.

또한, CMMA 및 열가소성 수지를 혼합시키는 단계 (S110) 에서, 열가소성 수지 물질로서 PMMA (ploy methyl methacrylate), 폴리에틸렌 (polyethylene), 폴리프로필렌 (polypropylene), 폴리카보네이트 (polycarbonate), 폴리에틸렌 테레프탈레이트 (polyethylene terephthalate), 나일론 (nylon), 실리콘 및 ABS (acrylonitrile-butadien-styrene) 으로 이루어진 그룹 중 적어도 하나가 이용될 수 있다. 그러나, 바람직하게, 열가소성 수지는, PMMA일 수 있으나, 이에 제한되는 것은 아니다.In addition, in the step of mixing CMMA and thermoplastic resin (S110), as a thermoplastic resin material, PMMA (ploy methyl methacrylate), polyethylene, polypropylene, polycarbonate, polyethylene terephthalate (polyethylene terephthalate) , Nylon (nylon), silicon, and at least one of the group consisting of ABS (acrylonitrile-butadien-styrene) may be used. However, preferably, the thermoplastic resin may be PMMA, but is not limited thereto.

또한, CMMA 및 열가소성 수지를 혼합시키는 단계 (S110) 에서, 안정화제, 난연제, 대전방지제, 연화제, 강화재, 충전재, 형광 중백제, 윤활제, 함입 감소제, 중축제 촉매, 소포제, 유화제, 증점제, 및 향료로 이루어진 그룹 중 적어도 하나가 더 포함될 수 있다. In addition, in the step of mixing CMMA and thermoplastic resin (S110), a stabilizer, a flame retardant, an antistatic agent, a softener, a reinforcing material, a filler, a fluorescent neutralizing agent, a lubricant, an inclusion reducing agent, a polycondensing agent catalyst, an antifoaming agent, an emulsifying agent, a thickening agent, and At least one of the group consisting of fragrance may be further included.

또한, CMMA 및 열가소성 수지를 혼합시키는 단계 (S110) 에서, 하이드록시프로필 메틸셀룰로스 (Hydroxypropyl Methylcellulose), 하이드록시에틸 셀룰로스 (Hydroxyethyl Cellulose), 하이드록시프로필 셀룰로스 (Hydroxypropyl Cellulose), 폴리비닐 알코올 (Polyvinyl Alcohol), 폴리비닐 피롤리돈 (Polyvinyl Pyrrolidone), 카보머 (Carbomer), 및 초산 비닐 수지 (Polyvinyl Acetate) 로 이루어진 그룹 중 적어도 하나의 접착성 물질이 더 포함될 수 있다.In addition, in the step of mixing CMMA and thermoplastic resin (S110), hydroxypropyl methylcellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, polyvinyl alcohol , Polyvinyl Pyrrolidone (Polyvinyl Pyrrolidone), Carbomer (Carbomer), and at least one adhesive material from the group consisting of a vinyl acetate resin (Polyvinyl Acetate) may be further included.

한편, 본 발명의 치과용 조성물은 전술한 것에 제한되지 않고 보다 다양한 첨가물을 더 함유할 수 있다. On the other hand, the dental composition of the present invention is not limited to the above, and may further contain more various additives.

그 다음, 혼합된 CBMA 및 열가소성 수지가 저온 중합되어 혼합 수지가 형성된다 (S120). 이때, 저온 중합은 60 ℃ 및 4.0 bar의 환경 조건에서 15분 동안 이루어지는 중합 반응을 의미할 수 있다. Then, the mixed CBMA and the thermoplastic resin are polymerized at a low temperature to form a mixed resin (S120). In this case, the low-temperature polymerization may mean a polymerization reaction performed for 15 minutes under environmental conditions of 60° C. and 4.0 bar.

마지막으로, 저온 중합이 끝난 혼합 수지를 탄화 규소 원형 사포로 연마시킨다. 이때, 탄화 규소 원형 사포는 최대 2000 grit의 입도를 가질 수 있다. Finally, the mixed resin after low-temperature polymerization is polished with a silicon carbide circular sandpaper. At this time, the silicon carbide circular sandpaper may have a particle size of up to 2000 grit.

치과용 조성물을 포함하는 구강 내 장치의 제조 방법의 결과로, 치과용 조성물을 포함하는 구강 내 장치는, 단백질, 나아가 박테리아의 흡착을 차단하는 방오 활성을 가질 수 있다.As a result of a method of manufacturing an intraoral device comprising a dental composition, an intraoral device comprising a dental composition may have antifouling activity to block adsorption of proteins and even bacteria.

이에, 본 발명의 치과용 조성물은, 구강 내 장치에 적용되어 생물 부착 방지에 따른 병원성 박테리아의 감염을 방지하는 항균 활성을 제공할 수 있다. Accordingly, the dental composition of the present invention may be applied to an intraoral device to provide antibacterial activity to prevent infection of pathogenic bacteria due to the prevention of attachment of organisms.

이하에서는 본 발명의 다양한 실시예에 따른 치과용 조성물의 효과에 대하여 설명한다. 이때, 쌍성 이온성 물질로 CBMA가 이용되고, 열가소성 수지로 PMMA가 이용되었으나 본 발명의 효과는 이에 제한되는 것은 아니다. 예를 들어, 쌍성 이온성 물질은, CBMA 외에 MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), 트리고넬린 (trigonelline), 엑토인 (ectoine), 베타인 (betaine), 설포베타인 메타크릴레이트 (sulfobetaine methacrylate), SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-(3-methacryloylimino)propyl-N,N-dimethylammonio propanesulfonate) 및 SPV (3-(2'-vinyl-pyridinio)propanesulfonate) 으로 이루어진 그룹 중 적어도 하나를 더 포함할 수 있으며, CBMA를 치과용 조성물로 사용한 것과 유사한 효과를 가질 수 있다.Hereinafter, the effect of the dental composition according to various embodiments of the present invention will be described. At this time, CBMA was used as a zwitterionic material and PMMA was used as a thermoplastic resin, but the effect of the present invention is not limited thereto. For example, binary ionic substances, in addition to CBMA, are MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), trigonelline, Ectoine, betaine, sulfobetaine methacrylate, SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-(3-methacryloylimino) ) may further include at least one of the group consisting of propyl-N,N-dimethylammonio propanesulfonate) and SPV (3-(2'-vinyl-pyridinio)propanesulfonate), and have an effect similar to that of using CBMA as a dental composition. I can.

도 2는 본 발명의 일 실시예에 따른 치과용 조성물의 조성 및 함량을 도시한 것이다.Figure 2 shows the composition and content of the dental composition according to an embodiment of the present invention.

도 2를 참조하면, 이하의 다양한 실시예에서 이용되는 치과용 조성물의 조성 및 함량이 도시된다. 보다 구체적으로, 이하에서는, 전체 치과용 조성물에 대하여 100 wt %의 PMMA를 함유하는 조성물 (control), 전체 치과용 조성물에 대하여 0.75 wt %의 CBMA 및 99.25 wt %의 PMMA 함량을 갖는 치과용 조성물 (0.75 % CBMA), 전체 치과용 조성물에 대하여 7.5 wt %의 CBMA 및 92.5 wt %의 PMMA 함량을 갖는 치과용 조성물 (7.5 % CBMA) 및 전체 치과용 조성물에 대하여 3 wt %의 MPC 및 97 wt %의 PMMA 함량을 갖는 치과용 조성물 (3 % MPC) 을 비교예로 설정하였다. Referring to Figure 2, the composition and content of the dental composition used in the following various examples are shown. More specifically, hereinafter, a composition containing 100 wt% of PMMA with respect to the total dental composition (control), a dental composition having a content of 0.75 wt% of CBMA and 99.25 wt% of PMMA with respect to the total dental composition ( 0.75% CBMA), a dental composition having a content of 7.5 wt% CBMA and 92.5 wt% PMMA based on the total dental composition (7.5% CBMA) and 3 wt% MPC and 97 wt% based on the total dental composition A dental composition having a PMMA content (3% MPC) was set as a comparative example.

나아가, 전체 치과용 조성물에 대하여 1.5 wt %의 CBMA 및 98.5 wt %의 PMMA 함량을 갖는 치과용 조성물 (1.5 % CBMA), 전체 치과용 조성물에 대하여 3 wt %의 CBMA 및 97 wt %의 PMMA 함량을 갖는 치과용 조성물 (3 % CBMA) 및 전체 치과용 조성물에 대하여 5 wt %의 CBMA 및 95 wt %의 PMMA 함량을 갖는 치과용 조성물 (5 % CBMA)을 실시예로 설정하였다.Furthermore, a dental composition having a content of 1.5 wt% CBMA and 98.5 wt% PMMA with respect to the total dental composition (1.5% CBMA), 3 wt% CBMA and 97 wt% PMMA content with respect to the total dental composition. A dental composition having a dental composition (3% CBMA) and a dental composition having a content of 5 wt% CBMA and 95 wt% PMMA with respect to the total dental composition (5% CBMA) were set as examples.

이때, 각각의 실시예 및 비교예들은 전술된 제조 방법에서 미리 설정된 함량에 따라, 분말 형태의 CBMA 및 MPC와 액체 및 분말 형태의 PMMA를 혼합함으로써 준비되었다.At this time, each of the Examples and Comparative Examples was prepared by mixing CBMA and MPC in powder form and PMMA in liquid and powder form according to a preset content in the above-described manufacturing method.

이때, MPC (2-methacryloyloxyethyl phosphorylcholine) 는 본 발명의 실시예에 따른 치과용 조성물에 포함되는 CBMA와 같은 쌍성 이온성 물질로서, 생체 이중막 인중막 인지질 구성성분인 포스파티딜콜린 (Phosphatidylcholine) 의 친수성 작용기를 모사해 생체친화적이고, 친환경적인 소재로 각광받고 있다. 나아가, MPC는 높은 친수성으로 인하여 안정적인 수화 쉘을 형성할 수 있어 우수한 방오 기능을 갖는 것으로 알려져 있다. 이에, CBMA의 방오 효과를 비교하기 위하여 대조군과 함께 종래의 치과용 혼합 수지 조성물인 MPC를 추가적으로 설정하였다.At this time, MPC (2-methacryloyloxyethyl phosphorylcholine) is a binary ionic material such as CBMA included in the dental composition according to an embodiment of the present invention, and mimics the hydrophilic functional group of phosphatidylcholine, which is a component of a double membrane phosphorus membrane in a living body. It is in the spotlight as a bio-friendly and eco-friendly material. Furthermore, MPC is known to have an excellent antifouling function because it can form a stable hydrated shell due to its high hydrophilicity. Accordingly, in order to compare the antifouling effect of CBMA, MPC, which is a conventional dental mixed resin composition, was additionally set together with the control group.

치과용 조성물 내의 CBMA 함량에 따른 습윤성 및 기계적 특성Wetability and mechanical properties according to CBMA content in dental compositions

이하에서는, 치과용 조성물 내의 대조군, 0.75 % CBMA, 7.5 % CBMA 및 3 % MPC로 이루어진 비교예 그룹과 1.5 % CBMA, 3 % CBMA 및 5 % CBMA로 이루어진 실시예 그룹 각각에 대한 습윤성 및 기계적 특성을 평가하기 위해, 습윤성 (wettability), 굴곡 강도 (flexural strength), 탄성 계수 (elastic modulus) 및 경도 (vickers hardness) 를 측정하였다. Hereinafter, the wettability and mechanical properties of the control group in the dental composition, the comparative example group consisting of 0.75% CBMA, 7.5% CBMA, and 3% MPC, and the example group consisting of 1.5% CBMA, 3% CBMA, and 5% CBMA, respectively. To evaluate, the wettability, flexural strength, elastic modulus and hardness were measured.

도 3a는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 습윤성을 나타내는 결과이다. 이때, 습윤성 평가는 액체(물)를 고체 표면 위에 떨어트렸을 때, 액체가 고체 표면에서 액체 방울을 형성하게 되는데, 이때의 액체와 고체 표면이 이루는 접촉각 (contact angle) 을 측정함으로써 수행되었다.Figure 3a is a result showing the wettability according to the CBMA content in the dental composition according to an embodiment of the present invention. At this time, the wettability evaluation was performed by measuring the contact angle between the liquid and the solid surface when the liquid (water) was dropped on the solid surface, and the liquid formed liquid droplets on the solid surface.

도 3a를 참조하면, 실시예 및 비교예에 대한 습윤성 평가가 도시된다. 0.75 % CBMA, 7.5 % CBMA 및 3 % MPC의 비교예와 1.5 % CBMA, 3 % CBMA 및 5 % CBMA 실시예는 대조군에 비해 유의하게 낮은 접촉각을 갖는 것으로 나타난다 (p<0.001). 보다 구체적으로, 0.75 % CBMA 비교예 및 1.5 % 실시예에 비해 3 % CBMA 실시예가 유의하게 낮은 접촉각을 갖으며, 3 % CBMA 실시예에 비해 5 % CBMA 실시예 및 7.5 % CBMA 비교예가 유의하게 낮은 접촉각을 갖는 것으로 나타난다 (p<0.001). 이때, 1.5 % CBMA 및 3 % CBMA 실시예는 3 % MPC 비교예와는 통계적 차이 없이 유사한 수준의 접촉각을 갖는 것으로 나타난다. 즉, CBMA의 함량이 증가함에 따라 PMMA의 친수성이 증가하여 접촉각이 감소할 수 있다. 또한, 쌍성 이온성 물질인 MPC의 첨가에 의해서도 PMMA의 친수성이 증가하여 접촉각이 감소할 수 있다. 이러한, 친수성의 증가는 물과의 강한 정전기적 상호작용을 의미할 수 있다. 이에, 본 발명의 다양한 실시예에 이용되는 치과용 조성물을 포함하는 구강 내 장치에 얇은 피막과 같은 수화 쉘을 형성하여 박테리아의 접근 및 각종 오염 물질이 달라붙지 못하게 하는 방오 효과를 제공할 수 있다.3A, evaluation of wettability for Examples and Comparative Examples is shown. The comparative examples of 0.75% CBMA, 7.5% CBMA and 3% MPC and the examples of 1.5% CBMA, 3% CBMA and 5% CBMA appeared to have significantly lower contact angles compared to the control group (p<0.001). More specifically, compared to the 0.75% CBMA Comparative Example and the 1.5% Example, the 3% CBMA Example had a significantly lower contact angle, and the 5% CBMA Example and the 7.5% CBMA Comparative Example were significantly lower than the 3% CBMA Example. It appears to have a contact angle (p<0.001). At this time, the 1.5% CBMA and 3% CBMA examples were found to have similar contact angles with no statistical difference from the 3% MPC comparative example. That is, as the content of CBMA increases, the hydrophilicity of PMMA increases and the contact angle may decrease. In addition, the hydrophilicity of PMMA may increase even by the addition of MPC, which is a zwitterionic material, and thus the contact angle may decrease. Such an increase in hydrophilicity may mean a strong electrostatic interaction with water. Accordingly, by forming a hydration shell such as a thin film on an intraoral device including a dental composition used in various embodiments of the present invention, it is possible to provide an antifouling effect that prevents the access of bacteria and various contaminants from sticking to each other.

도 3b는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 기계적 특성을 나타내는 결과이다. 이때, 기계적 특성에 사용되는 시편은 ISO 20795-2의 교정용 베이스 폴리머에 대한 국제 규격에 의거하여 3.3 mm x 10 mm x 25 mm 크기로 각 실험군당 10개씩 제작하였다. 기계적 특성을 측정하는 굴곡 강도 (flexural strength) 및 탄성 계수 (elastic modulus) 시험은 지지대 간격이 50 mm인 컴퓨터 제어 범용를 이용하여 지지대의 중앙에 올려 놓고, 하중 속도 5 mm/min로 수직하중을 가해서 시편이 파절 될 때까지의 최대하중을 측정하였다. Figure 3b is a result showing the mechanical properties according to the CBMA content in the dental composition according to an embodiment of the present invention. At this time, the specimens used for the mechanical properties were 3.3 mm x 10 mm x 25 mm in size according to the international standard for calibration base polymer of ISO 20795-2, and 10 specimens were prepared for each experimental group. The flexural strength and elastic modulus tests, which measure mechanical properties, are carried out using a computer-controlled general purpose with a 50 mm spacing of the supports, placed in the center of the support, and applied a vertical load at a load speed of 5 mm/min. The maximum load until fracture was measured.

굴곡 강도(σ)는 아래의 수학식 1에 의해 측정하였다. The flexural strength (σ) was measured by Equation 1 below.

[수학식 1][Equation 1]

σ = 3Fl / (2bh2)σ = 3Fl / (2bh2)

이때, F는 시편에 가해진 최대 힘(N), l는 지지대간의 거리 (mm), b는 시편의 두께 (mm), h는 시편의 높이 (mm) 를 의미한다.Here, F is the maximum force applied to the specimen (N), l is the distance between the supports (mm), b is the thickness of the specimen (mm), and h is the height of the specimen (mm).

탄성 계수(E)는 아래의 수학식 2에 의해 측정하였다.The elastic modulus (E) was measured by Equation 2 below.

[수학식 2][Equation 2]

E= F1l3 / (4bh3d)E= F1l3 / (4bh3d)

이때, F1은 수직하중, l는 지지대간의 거리 (mm), b는 시편의 두께 (mm), h는 시편의 높이 (mm), d는 F1에 의한 변형률을 의미한다.Here, F1 is the vertical load, l is the distance between the supports (mm), b is the thickness of the specimen (mm), h is the height of the specimen (mm), and d is the strain due to F1.

나아가, 기계적 특성을 측정하는 경도 시험은 비커스 경도기를 이용하여 30초 동안 300gf (2.94N) 하중을 가해서 측정하였다. Further, the hardness test for measuring mechanical properties was measured by applying a load of 300gf (2.94N) for 30 seconds using a Vickers hardness tester.

먼저, 도 3b의 (a)를 참조하면, 실시예 및 비교예에 대한 굴곡 강도 시험 결과가 도시된다. 보다 구체적으로, 3 % CBMA 실시예는 대조군에 비해 유의하게 낮은 수준의 굴곡 강도를 갖는 것으로 나타난다 (p<0.001). 그러나, 1.5 % CBMA 실시예는 대조군 및 0.75 % CBMA 비교예와 통계적 차이 없이 유사한 수준의 굴곡 강도를 갖는 것으로 나타나며, 3 % CBMA 실시예는 0.75 % CBMA 비교예 및 3 % CBMA 실시예와 통계적인 차이 없이 유사한 수준의 굴곡 강도를 갖는 것으로 나타난다. 또한, 1.5 % CBMA 및 3 % CBMA 실시예는 3 % MPC 비교예와도 통계적인 차이 없이 유사한 수준의 굴곡 강도를 갖는 것으로 나타난다. 이에, 1.5 % CBMA 및 3 % CBMA 실시예는 종래의 치과용 조성물로서 이용되는 대조군 및 3 % MPC 비교예와 같은 굴곡 강도를 갖는 것을 의미할 수 있다.First, referring to (a) of FIG. 3B, the results of the flexural strength test for Examples and Comparative Examples are shown. More specifically, the 3% CBMA example appears to have a significantly lower level of flexural strength compared to the control (p<0.001). However, the 1.5% CBMA example was shown to have a similar level of flexural strength without statistical difference from the control and 0.75% CBMA comparative example, and the 3% CBMA example was statistically different from the 0.75% CBMA comparative example and the 3% CBMA example. Appears to have a similar level of flexural strength without. In addition, the 1.5% CBMA and 3% CBMA examples were shown to have similar levels of flexural strength without statistical difference even with the 3% MPC comparative example. Thus, the examples of 1.5% CBMA and 3% CBMA may mean having the same flexural strength as the control and 3% MPC comparative examples used as conventional dental compositions.

한편, 5 % CBMA 실시예 및 7.5 % CBMA 비교예는 1.5 % CBMA 및 3 % CBMA 실시예에 비해 유의하게 낮은 굴곡 강도를 갖는 것으로 나타난다 (p<0.001). 보다 구체적으로, 1.5 % CBMA 실시예보다 3 % CBMA 실시예가 유의하게 낮은 굴곡 강도를 갖는 것으로 나타나며, 3 % CBMA 실시예보다 5 % CBMA 실시예가 유의하게 낮은 굴곡 강도를 갖는 것으로 나타나며, 5 % CBMA 실시예보다 7.5 % CBMA 비교예가 유의하게 낮은 굴곡 강도를 갖는 것으로 나타난다. 즉, CBMA 함량이 증가함에 따라 굴곡 강도의 수준이 감소할 수 있다. 이때, 5 % CBMA 실시예 및 7 % CBMA 비교예는 대조군 및 ISO 표준보다 낮은 굴곡 강도를 갖는 것으로 나타난다. 이에, CBMA가 5 % 이상 치과용 조성물에 첨가되었을 경우, 종래의 치과용 조성물로서 기준이 되는 ISO 표준보다 굴곡 강도가 낮을 수 있으므로, 바람직하게, CBMA 함량은 5% 미만일 수 있다.On the other hand, 5% CBMA Example and 7.5% CBMA Comparative Example appeared to have significantly lower flexural strength compared to the 1.5% CBMA and 3% CBMA Example (p<0.001). More specifically, the 3% CBMA example was shown to have a significantly lower flexural strength than the 1.5% CBMA example, the 5% CBMA example was shown to have a significantly lower flexural strength than the 3% CBMA example, and the 5% CBMA example It appears that the 7.5% CBMA comparative example has significantly lower flexural strength than the example. That is, as the CBMA content increases, the level of flexural strength may decrease. At this time, 5% CBMA Example and 7% CBMA Comparative Example appeared to have a lower flexural strength than the control and ISO standards. Accordingly, when CBMA is added to the dental composition by 5% or more, the flexural strength may be lower than the ISO standard, which is a standard as a conventional dental composition, so preferably, the CBMA content may be less than 5%.

도 3b의 (b)를 참조하면, 실시예 및 비교예에 대한 탄성 계수 시험 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예는 대조군, 0.75 % CBMA 및 3 % MPC 비교예와 통계적인 차이 없이 유사한 수준의 탄성 계수를 갖는 것으로 나타난다. 이는, 1.5 % CBMA 및 3 % CBMA 실시예가 종래의 치과용 조성물로서 이용되는 대조군 및 3 % MPC 비교예와 같은 탄성 계수를 갖는 것을 의미할 수 있다.Referring to (b) of FIG. 3B, elastic modulus test results for Examples and Comparative Examples are shown. More specifically, the 1.5% CBMA and 3% CBMA examples were shown to have similar levels of elastic modulus with no statistical difference to the control, 0.75% CBMA and 3% MPC comparative examples. This may mean that the 1.5% CBMA and 3% CBMA examples have the same elastic modulus as the control and 3% MPC comparative examples used as conventional dental compositions.

한편, 5 % CBMA 실시예 및 7.5 % CBMA 비교예는 1.5 % CBMA 및 3 % CBMA 실시예에 비해 유의하게 탄성 계수를 갖는 것으로 나타난다 (p<0.001). 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예보다 5 % CBMA 실시예가 유의하게 낮은 탄성 계수를 갖는 것으로 나타나며, 5 % CBMA 실시예보다 7.5 % CBMA 비교예가 유의하게 탄성 계수를 갖는 것으로 나타난다. 즉, CBMA 함량이 증가함에 따라 탄성 계수의 수준이 감소할 수 있다. 이때, 5 % CBMA 실시예 및 7 % CBMA 비교예는 대조군 및 ISO 표준보다 낮은 탄성 계수를 갖는 것으로 나타난다. 이에, CBMA가 5 % 이상 치과용 조성물에 첨가되었을 경우, 종래의 치과용 조성물로서 기준이 되는 ISO 표준보다 탄성 계수가 낮을 수 있으므로, 바람직하게 CBMA 함량은 5% 미만일 수 있다.On the other hand, 5% CBMA Example and 7.5% CBMA Comparative Example appeared to have a significantly more elastic modulus compared to the 1.5% CBMA and 3% CBMA Example (p<0.001). More specifically, the 5% CBMA example was shown to have significantly lower elastic modulus than the 1.5% CBMA and 3% CBMA example, and the 7.5% CBMA comparative example was shown to have significantly less elastic modulus than the 5% CBMA example. That is, as the CBMA content increases, the level of the elastic modulus may decrease. At this time, 5% CBMA Example and 7% CBMA Comparative Example appeared to have a lower modulus of elasticity than the control and ISO standards. Accordingly, when CBMA is added to the dental composition by 5% or more, the modulus of elasticity may be lower than that of the ISO standard as a conventional dental composition, and the CBMA content may preferably be less than 5%.

도 3b의 (c)를 참조하면, 실시예 및 비교예에 대한 경도 시험 결과가 도시된다. 보다 구체적으로, 0.75 % CBMA 비교예는 대조군과 통계적 차이 없이 유사한 수준의 경도를 갖는 것으로 나타난다. 한편, 1.5 % CBMA, 3 % CBMA 및 5 % CBMA 실시예는 통계적인 차이 없이 유사한 수준의 경도를 갖는 것으로 나타나며, 대조군에 비해 유의하게 낮은 경도를 갖는 것으로 나타난다 (p<0.001). 그러나, 1.5 % CBMA, 3 % CBMA 및 5% CBMA 실시예는 대조군과 통계적 차이가 없는 0.75 % CBMA 및 3 % MPC 비교예와 통계적 차이 없이 유사한 수준의 경도를 갖는 것으로 나타난다. 이에, 1.5 % CBMA, 3 % CBMA 및 5 % CBMA 실시예는 종래의 치과용 조성물로서 이용되는 대조군 및 3 % MPC 비교예와 비슷한 수준의 경도를 갖는 것을 의미할 수 있다. 한편, 7.5 % CBMA 비교예는 1.5 % CBMA, 3 % CBMA 및 5% CBMA 실시예에 비해 유의하게 낮은 경도를 갖는 것으로 나타난다. 이에, CBMA가 7.5 % 이상 치과용 조성물에 첨가되었을 경우, 경도가 감소할 수 있으므로, 바람직하게, CBMA 함량은 7.5 % 미만일 수 있다.Referring to (c) of FIG. 3B, hardness test results for Examples and Comparative Examples are shown. More specifically, the 0.75% CBMA comparative example appeared to have a similar level of hardness with no statistical difference from the control group. On the other hand, 1.5% CBMA, 3% CBMA and 5% CBMA examples were shown to have similar levels of hardness without statistical difference, and were shown to have significantly lower hardness compared to the control group (p<0.001). However, the 1.5% CBMA, 3% CBMA and 5% CBMA examples were shown to have similar levels of hardness with no statistical difference to the 0.75% CBMA and 3% MPC comparative examples, which were not statistically different from the control. Accordingly, the examples of 1.5% CBMA, 3% CBMA and 5% CBMA may mean having a hardness similar to that of the control and 3% MPC comparative examples used as conventional dental compositions. On the other hand, the 7.5% CBMA comparative example appears to have significantly lower hardness compared to the 1.5% CBMA, 3% CBMA and 5% CBMA examples. Accordingly, when CBMA is added to the dental composition by 7.5% or more, the hardness may decrease, and thus, preferably, the CBMA content may be less than 7.5%.

이상의 결과로, 본 발명의 다양한 실시예에서 이용되는 치과용 조성물은, 0.75 내지 5 wt %의 CBMA 함량에서 100 %의 PMMA 및 3 %의 MPC를 함유한 종래의 치과용 조성물과 유사한 수준의 습윤성 및 기계적 특성을 가지는 것으로 나타났다. As a result of the above, the dental composition used in various embodiments of the present invention has a wettability similar to that of a conventional dental composition containing 100% PMMA and 3% MPC at a CBMA content of 0.75 to 5 wt%, and It has been shown to have mechanical properties.

보다 구체적으로, 전체 치과용 조성물의 총 중량에 대하여 0.75 내지 3 wt %의 CBMA 함량에서 100 wt %의 PMMA 및 3 wt %의 MPC를 함유한 종래의 치과용 조성물과 유사한 수준의 습윤성, 굴곡 강도 및 탄성 계수를 가지는 것으로 나타나며, 전체 치과용 조성물의 총 중량에 대하여 0.75 내지 5 wt %의 CBMA 함량에서 100 wt %의 PMMA 및 3 wt %의 MPC를 함유한 종래의 치과용 조성물과 유사한 수준의 경도를 가지는 것으로 나타난다.More specifically, the wettability, flexural strength, and similar levels of conventional dental compositions containing 100 wt% PMMA and 3 wt% MPC at a CBMA content of 0.75 to 3 wt% based on the total weight of the total dental composition It appears to have a modulus of elasticity, and has a hardness similar to that of a conventional dental composition containing 100 wt% of PMMA and 3 wt% of MPC at a CBMA content of 0.75 to 5 wt% with respect to the total weight of the total dental composition. Appears to have.

나아가, 전체 치과용 조성물의 총 중량에 대하여 5 wt % 및 7.5 wt %의 CBMA 함량에서 치과용 조성물의 기계적 특성이 감소될 수 있다. 보다 구체적으로, 전체 치과용 조성물의 총 중량에 대하여 5 wt % 및 7.5 wt %의 CBMA 함량에서 굴곡 강도, 탄성 계수 및 경도가 치과용 조성물에 대한 ISO 표준보다 낮을 수 있다.Furthermore, the mechanical properties of the dental composition may be reduced at 5 wt% and 7.5 wt% CBMA content based on the total weight of the dental composition. More specifically, flexural strength, modulus of elasticity, and hardness at 5 wt% and 7.5 wt% of CBMA content relative to the total weight of the total dental composition may be lower than ISO standards for dental compositions.

이에, 치과용 조성물 및 치과용 조성물을 포함하는 구강 내 장치의 CBMA의 함량은, 전체 치과용 조성물의 총 중량에 대하여 0.75 내지 5 wt % 일 수 있다. 바람직하게, 습윤성 및 기계적 특성의 효과가 극대화될 수 있는, CBMA의 함량은 치과용 조성물의 함량은 전체 치과용 조성물의 총 중량에 대하여 1.5 내지 3 wt % 일 수 있다.Accordingly, the content of CBMA in the oral device including the dental composition and the dental composition may be 0.75 to 5 wt% based on the total weight of the total dental composition. Preferably, the content of CBMA, which can maximize the effect of wettability and mechanical properties, may be 1.5 to 3 wt% based on the total weight of the total dental composition.

치과용 조성물의 단백질 흡착 차단 효과Protein adsorption blocking effect of dental composition

이하에서는, 치과용 조성물 내의 대조군, 0.75 % CBMA 및 3 % MPC로 이루어진 비교예 그룹과 1.5 % CBMA 및 3 % CBMA로 이루어진 실시예 그룹 각각에 대한 단백질 흡착 시험을 수행하였다. 이때, 실시예 및 비교예는 직경 15 mm 및 두께 2 mm의 금형에 의해 디스크 모양의 시편 형태로 준비되었다. Hereinafter, a protein adsorption test was performed for each of the control group in the dental composition, the comparative example group consisting of 0.75% CBMA and 3% MPC, and the example group consisting of 1.5% CBMA and 3% CBMA. At this time, Examples and Comparative Examples were prepared in the form of a disk-shaped specimen by a mold having a diameter of 15 mm and a thickness of 2 mm.

보다 구체적으로, 단백질 흡착 시험을 위해, 디스크 형태의 실시예 및 비교예는, 실온에서 1 시간 동안 PBS (인산염 완충 식염수)에 담궈졌다. 그 다음, 실시예 및 비교예는 BSA (bovine serum albumin) 또는 효모 (yeast) 및 곰팡이 브로스 (mould broth) 를 포함하는 YM 배지 (medium) 의 단백질 용액에 담궈졌다. 이때, 단백질 농도는 2 mg/ml이고, 부피는 100 μl였다. 그 다음, 멸균 습한 조건에서 37 ℃, 5 %의 CO2에서 4 시간 동안 배양한 후, 미 흡착성 단백질을 PBS로 두 번 세척하여 제거하였다. 그 다음, 남아있는 단백질을 200 μl의 Micro BCA (micro bicinchoninic acid) 와 반응시킨 후 37 ℃에서 30 분 동안 배양하였다. 마지막으로, microplate reader를 사용하여 562 nm에서의 흡광도를 측정하였고, Micro BCATM Protein Assay Kit를 사용하여 디스크 형태의 실시예 및 비교예 표면의 흡착 단백질을 정량 분석하였다.More specifically, for the protein adsorption test, Examples and Comparative Examples in the form of disks were immersed in PBS (phosphate buffered saline) for 1 hour at room temperature. Then, Examples and Comparative Examples were immersed in a protein solution of BSA (bovine serum albumin) or YM medium containing yeast and mold broth. At this time, the protein concentration was 2 mg/ml, and the volume was 100 μl. Then, after incubation for 4 hours at 37° C. and 5% CO 2 in sterile humid conditions, the unadsorbed protein was washed twice with PBS to remove it. Then, the remaining protein was reacted with 200 μl of Micro BCA (micro bicinchoninic acid) and incubated at 37° C. for 30 minutes. Finally, absorbance at 562 nm was measured using a microplate reader, and adsorbed proteins on the surfaces of Examples and Comparative Examples in disk form were quantitatively analyzed using Micro BCA™ Protein Assay Kit.

도 4는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 단백질 흡착 수준을 나타내는 결과이다.4 is a result showing the protein adsorption level according to the CBMA content in the dental composition according to an embodiment of the present invention.

도 4의 (a)를 참조하면, 1.5 % CBMA 및 3 % CBMA 실시예에 대한 BSA의 흡착 수준은 대조군 및 0.75 % CBMA 비교예에 비해 유의하게 감소한 것으로 나타난다 (p<0.001). 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예에 대한 BSA의 흡착 수준은 대조군에 비해 약 1.5 배 내지 2 배 감소된 것으로 나타나며, 3 % MPC 비교예와는 통계적인 차이 없이 유사한 수준의 BSA 흡착 수준을 갖는 것으로 나타난다. 특히, 1.5 % CBMA 및 3 % CBMA 실시예는 0.75 % CBMA 비교예보다 BSA 흡착 수준의 감소 폭이 유의하게 큰 것으로 나타난다 (p<0.001). 이러한 결과는 CBMA가 단백질의 흡착 수준을 감소시키는 것에 기여할 수 있으며, 종래의 치과용 조성물인 PMMA의 단점인 낮은 방오 효과를 CBMA의 첨가로 인하여 보안할 수 있다는 것을 의미할 수 있다. 나아가, CBMA의 함유량이 전체 질량에 대하여 1.5 % 이상인 경우, 종래의 우수한 방오 효과를 제공하는 치과용 조성물인 MPC만큼의 방오 효과를 제공할 수 있다.Referring to FIG. 4A, the adsorption level of BSA for the 1.5% CBMA and 3% CBMA examples was significantly decreased compared to the control and 0.75% CBMA comparative examples (p<0.001). More specifically, the adsorption level of BSA for the 1.5% CBMA and 3% CBMA examples was found to be reduced by about 1.5 to 2 times compared to the control, and similar levels of BSA adsorption without statistical difference from the 3% MPC comparative example It appears to have a level. In particular, the 1.5% CBMA and 3% CBMA examples showed a significantly greater reduction in the BSA adsorption level than the 0.75% CBMA comparative example (p<0.001). These results may contribute to the reduction of the adsorption level of CBMA proteins, and may mean that the low antifouling effect, which is a disadvantage of PMMA, which is a conventional dental composition, can be secured by the addition of CBMA. Furthermore, when the content of CBMA is 1.5% or more with respect to the total mass, it is possible to provide an antifouling effect as much as MPC, which is a conventional dental composition providing excellent antifouling effect.

이에, CBMA의 함량은, 전체 치과용 조성물의 총 중량에 대하여 1.5 내지 3 wt %일 수 있으나, 이에 제한되는 것은 아니다.Accordingly, the content of CBMA may be 1.5 to 3 wt% based on the total weight of the total dental composition, but is not limited thereto.

도 4의 (b)를 참조하면, 1.5 % CBMA 및 3 % CBMA 실시예에 대한 YM 배지로부터의 단백질 흡착 수준은 대조군 및 0.75 % CBMA 비교예에 비해 유의하게 감소한 것으로 나타난다 (p<0.001). 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예에 대한 YM 배지로부터의 단백질 흡착 수준은 대조군에 비해 약 1.5 배 내지 3 배 감소된 것으로 나타나며, 3 % MPC 비교예와는 통계적인 차이 없이 유사한 수준의 YM 배지로부터의 단백질 흡착 수준을 갖는 것으로 나타난다. 특히, 1.5 % CBMA 및 3 % CBMA 실시예는 0.75 % CBMA 비교예보다 YM 배지로부터의 단백질 흡착 수준의 감소 폭이 유의하게 큰 것으로 나타난다 (p<0.001). 이러한 결과는 CBMA가 단백질 흡착 수준을 감소시키는 것에 기여할 수 있으며, 종래의 치과용 조성물인 PMMA의 단점인 낮은 방오 효과를 CBMA의 첨가로 인하여 보안할 수 있다는 것을 의미할 수 있다. 나아가, CBMA의 함유량이 전체 질량에 대하여 1.5 % 이상인 경우, 종래의 우수한 방오 효과를 제공하는 치과용 조성물인 MPC만큼의 방오 효과를 제공할 수 있다. 이에, CBMA의 함량은, 전체 치과용 조성물의 총 중량에 대하여 1.5 내지 3 wt %일 수 있으나, 이에 제한되는 것은 아니다.Referring to (b) of FIG. 4, the protein adsorption level from YM medium for the 1.5% CBMA and 3% CBMA examples was significantly decreased compared to the control and 0.75% CBMA comparative examples (p<0.001). More specifically, the level of protein adsorption from the YM medium for the 1.5% CBMA and 3% CBMA examples was found to be reduced by about 1.5 to 3 times compared to the control, and a similar level with no statistical difference from the 3% MPC comparative example. Appears to have a level of protein adsorption from YM medium. In particular, the 1.5% CBMA and 3% CBMA examples showed a significantly greater reduction in protein adsorption level from the YM medium than the 0.75% CBMA comparative example (p<0.001). These results may contribute to the reduction of the protein adsorption level of CBMA, and may mean that the low antifouling effect, which is a disadvantage of PMMA, which is a conventional dental composition, can be secured by the addition of CBMA. Furthermore, when the content of CBMA is 1.5% or more with respect to the total mass, it is possible to provide an antifouling effect as much as MPC, which is a conventional dental composition that provides an excellent antifouling effect. Accordingly, the content of CBMA may be 1.5 to 3 wt% based on the total weight of the total dental composition, but is not limited thereto.

이상의 결과로, CBMA가 치아의 단백질 흡착을 높은 수준으로 차단하는 것에 기여한다는 것을 확인하였다. 특히, 본 발명의 다양한 실시예에 따른 치과용 조성물은, PMMA 단독으로 이용했을 경우보다 CBMA를 포함하는 PMMA를 이용했을 경우에 단백질 흡착의 차단 효과가 향상된 것으로 나타났다. 나아가, CBMA가 전체 질량에 대하여 1.5 % 이상으로 함유되었을 경우, 우수한 방오 효과를 제공하는 종래의 치과용 조성물인 MPC 만큼의 단백질에 대한 흡착을 차단하는 효과를 갖는 것으로 나타난다. As a result of the above, it was confirmed that CBMA contributes to blocking the protein adsorption of teeth to a high level. In particular, the dental composition according to various embodiments of the present invention was found to have improved protein adsorption blocking effect when using PMMA containing CBMA than when using PMMA alone. Furthermore, when CBMA is contained in an amount of 1.5% or more with respect to the total mass, it appears to have an effect of blocking adsorption to proteins as much as MPC, a conventional dental composition that provides excellent antifouling effect.

이에, CBMA 및 PMMA를 포함하는 치과용 조성물은 우수한 수준으로 박테리아성 미생물막의 흡착 및 박테리아의 감염을 차단할 수 있다. 한편, CBMA의 함량은, 전체 치과용 조성물의 총 중량에 대하여 1.5 wt % 내지 5 wt % 일 수 있다. 바람직하게, 단백질에 대한 흡착에 있어 차단 효과가 극대화될 수 있는, CBMA의 함량은 전체 치과용 조성물의 총 중량에 대하여 1.5 내지 3 wt % 일 수 있다.Accordingly, the dental composition including CBMA and PMMA can block the adsorption of the bacterial microbial membrane and infection of the bacteria at an excellent level. Meanwhile, the content of CBMA may be 1.5 wt% to 5 wt% based on the total weight of the total dental composition. Preferably, the content of CBMA, which can maximize the blocking effect in adsorption to proteins, may be 1.5 to 3 wt% based on the total weight of the total dental composition.

치과용 조성물의 박테리아 흡착 차단 효과 (배지)Bacterial adsorption blocking effect of dental composition (medium)

이하에서는, 치과용 조성물 내의 대조군 및 3 % MPC로 이루어진 비교예 그룹과 1.5 % CBMA 및 3 % CBMA로 이루어진 실시예 그룹 각각에 대한 박테리아 흡착 차단 평가를 수행하였다. 이때, 실시예 및 비교예는 직경 10 mm 및 두께 2 mm의 금형에 의해 디스크 모양의 시편 형태로 준비되었다. Hereinafter, the evaluation of blocking bacterial adsorption was performed for each of the control group in the dental composition and the comparative example group consisting of 3% MPC and the example group consisting of 1.5% CBMA and 3% CBMA. At this time, Examples and Comparative Examples were prepared in the form of a disk-shaped specimen by a mold having a diameter of 10 mm and a thickness of 2 mm.

보다 구체적으로, 박테라이 흡착 평가를 위해, 구강 내 장치에 있어서 감염을 유발하는 균인 칸디다균 (Candida albicans), 액티노마이세스 나이슬런디 (Actinomyces naeslundii) 및 베일로넬라 파르불라 (Veillonella parvula) 를 준비하였다. 칸디다균은 YM 배지에서 배양하였고, 액티노마이세스 나이슬런디 및 베일로넬라 파르불라는 0.5 % 효모 추출물, 4 μg/ml 레조아주린 (resazurin), 5 μg/ml 헤민 (hemin), 0.05 % L-cysteine HCl•H2O 및 2 μg/ml 비타민 K가 함유된 3.8 %의 BHI (Brain Heart Infusion) 브로스에서 배양하였다. 이때, 배지들의 환경 조건은 혐기성 상태였다. 그 다음, 준비된 디스크 형태의 실시예 및 비교예 각각을 1 ml의 곰팡이 또는 박테리아 현탁액 (1×108 cells/ml) 에 넣어 37 ℃에서 24 시간 동안 배양하였다. 그 다음, 미 흡착 성 박테리아를 PBS로 두 번 세척하여 제거하였다. More specifically, for the evaluation of Bacterii adsorption, Candida albicans, Actinomyces naeslundii, and Veillonella parvula, which are bacteria that cause infection in oral devices, were used. Ready. Candida bacteria were cultured in YM medium, Actinomyces nislundi and Baylonella parbula were 0.5% yeast extract, 4 μg/ml resazurin, 5 μg/ml hemin, 0.05% It was cultured in 3.8% BHI (Brain Heart Infusion) broth containing L-cysteine HCl•H2O and 2 μg/ml vitamin K. At this time, the environmental conditions of the media were anaerobic. Then, each of the prepared disk-shaped Examples and Comparative Examples was put into 1 ml of a fungal or bacterial suspension (1×10 8 cells/ml) and cultured at 37° C. for 24 hours. Then, unadsorbed bacteria were removed by washing twice with PBS.

디스크의 실시예 및 비교예 각각에 존재하는 박테리아의 CFU (colony forming unit) 를 확인하기 위해, 5 분 동안 초음파 처리를 하여, 1 ml의 BHI로 박테리아 현탁액을 획득하였다. 그 다음, 박테리아 현탁액의 100 μl를 BHI 배지에 도말한 후, 37 ℃에서 24 시간동안 배양하였다. 마지막으로, 총 콜로니 수를 계수하였다.In order to confirm the colony forming unit (CFU) of bacteria present in each of the Examples and Comparative Examples of the disk, ultrasonic treatment was performed for 5 minutes to obtain a bacterial suspension with 1 ml of BHI. Then, 100 μl of the bacterial suspension was plated on BHI medium, followed by incubation at 37° C. for 24 hours. Finally, the total number of colonies was counted.

디스크의 실시예 및 비교예 각각에 존재하는 박테리아의 생존력 (viability) 을 확인하기 위해, 생사 여부에 따라 박테리아가 염색되는 키트를 이용하였다. 보다 구체적으로, 동일 부피의 Syto 9 염료 및 프로피디움 요오드화물 (propidium iodide)이 혼합된 혼합물 3 μl를 1 ml의 박테리아 현탁액에 주입한 후, 실온 (room temperature) 의 암실에서 15분 동안 배양하였다. 마지막으로, 공초점 레이져 현미경 (confocal laser microscopy) 을 이용하여 박테리아의 생사 여부를 관찰하였다. 이때, 살아있는 박테리아는 녹색으로 보였고, 죽은 박테리아는 적색으로 보였다.In order to check the viability of bacteria present in each of the Examples and Comparative Examples of the disk, a kit in which bacteria are stained according to whether they live or die was used. More specifically, 3 μl of a mixture of the same volume of Syto 9 dye and propidium iodide was injected into 1 ml of a bacterial suspension, followed by incubation for 15 minutes in a dark room at room temperature. Finally, the survival or death of bacteria was observed using a confocal laser microscopy. At this time, live bacteria appeared green and dead bacteria appeared red.

도 5a 내지 5c는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 박테리아 저해 수준을 나타내는 결과이다.5A to 5C are results showing the level of inhibition of bacteria according to the CBMA content in the dental composition according to an embodiment of the present invention.

먼저, 도 5a의 (a)를 참조하면, 공초점 레이져 현미경으로 측정된 칸디다균에 대한 생사 여부의 염색 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예는 3 % MPC 비교예와 비슷한 수준의 살아있는 칸다디균에 대한 형광발현을 갖는 것으로 나타나며, 대조군에 비해 살아있는 칸디다균에 대한 형광발현이 현저하게 감소한 것으로 나타난다. 이는, 1.5 % CBMA 및 3 % CBMA 실시예가 칸디다균에 대하여 대조군에 비해 높은 방오 효과를 가지고 있으며, 우수한 방오 효과를 제공하는 종래의 치과용 조성물인 MPC 만큼의 방오 효과를 갖는 것을 의미할 수 있다. First, referring to (a) of FIG. 5A, the staining results of whether Candida bacteria live or die measured by a confocal laser microscope are shown. More specifically, the 1.5% CBMA and 3% CBMA examples were shown to have a similar level of fluorescence expression for live Candadi bacteria as in the 3% MPC comparative example, and the fluorescence expression for live Candida was significantly reduced compared to the control group. appear. This may mean that the 1.5% CBMA and 3% CBMA examples have a higher antifouling effect on Candida compared to the control, and have an antifouling effect as much as MPC, a conventional dental composition that provides excellent antifouling effect.

나아가, 도 5a의 (b)를 참조하면, 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 및 MPC 함량에 따른 배지 상에서의 칸디다균 흡착 수준을 나타내는 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예에 부착된 칸디다균의 CFU 수준은 대조군에 비해 유의하게 낮은 것으로 나타난다 (p<0.001). 나아가, 1.5 % CBMA 실시예에 부착된 칸다디균의 CFU 수준은 3 % MPC 비교에에 비해 유의하게 높은 것으로 나타나지만, 3 % CBMA 실시예에 부착된 칸다디균의 CFU 수준은 3 % MPC 비교에에 비해 유의하게 낮은 것으로 나타난다 (p<0.001). 특히, 3 % CBMA 실시예로부터 획득된 현탁액을 도말한 배지에서의 칸디다균에 대한 CFU는 유의하게 가장 낮은 것으로 나타난다 (p<0.001). 이때, 3 % CBMA 실시예로부터 획득된 현탁액을 도말한 배지에서의 칸디다균에 대한 CFU는 대조군에 비하여 250 배 내지 300 배 낮은 것으로 나타난다. Further, referring to (b) of FIG. 5A, a result showing the adsorption level of Candida bacteria on the medium according to the CBMA and MPC contents in the dental composition according to an embodiment of the present invention is shown. More specifically, the CFU levels of Candida bacteria attached to the 1.5% CBMA and 3% CBMA examples appear to be significantly lower than the control group (p<0.001). Furthermore, the CFU level of Candadi bacteria attached to the 1.5% CBMA example appeared to be significantly higher than that of the 3% MPC comparison, but the CFU level of the Candadi bacteria attached to the 3% CBMA example was compared to the 3% MPC comparison. It appears to be significantly low (p<0.001). In particular, the CFU for Candida in the medium plated with the suspension obtained from the 3% CBMA example appeared to be significantly lowest (p<0.001). At this time, the CFU for Candida in the medium plated with the suspension obtained from the 3% CBMA example appeared to be 250 to 300 times lower than that of the control.

이러한 결과는, CBMA가 칸디다균의 흡착을 차단함에 따라 획득된 현탁액에 대한 콜로니의 수가 감소했음을 의미할 수 있다. 이때, 칸다디균의 흡착을 차단할 수 있는 CBMA의 함량은, 전체 치과용 조성물의 총 중량에 대하여 1.5 wt % 내지 3 wt %일 수 있으며, 바람직하게는, 3 wt %일 수 있으나, 이에 제한되는 것은 아니다.These results may mean that the number of colonies in the obtained suspension decreased as CBMA blocked the adsorption of Candida bacteria. At this time, the content of CBMA capable of blocking the adsorption of Candadi bacteria may be 1.5 wt% to 3 wt %, preferably, 3 wt %, but is limited thereto. no.

먼저, 도 5b의 (a)를 참조하면, 공초점 레이져 현미경으로 측정된 액티노마이세스 나이슬런디에 대한 생사 여부의 염색 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예는 3 % MPC 비교예와 비슷한 수준의 살아있는 액티노마이세스 나이슬런디에 대한 형광발현을 갖는 것으로 나타나며, 대조군에 비해 살아있는 액티노마이세스 나이슬런디에 대한 형광발현이 현저하게 감소한 것으로 나타난다. 이는, 1.5 % CBMA 및 3 % CBMA 실시예가 액티노마이세스 나이슬런디에 대하여 대조군에 비해 높은 방오 효과를 가지고 있으며, 우수한 방오 효과를 제공하는 종래의 치과용 조성물인 MPC 만큼의 방오 효과를 갖는 것을 의미할 수 있다.First, referring to (a) of FIG. 5B, the staining result of the live or death of Actinomyces nislundi measured with a confocal laser microscope is shown. More specifically, the 1.5% CBMA and 3% CBMA examples were shown to have fluorescence expression for live Actinomyces nislundi at a level similar to that of the 3% MPC comparative example, and compared to the control group, live Actinomyces nisle. It appears that the fluorescence expression for lundy was significantly reduced. This is that the 1.5% CBMA and 3% CBMA examples have a higher antifouling effect than the control for Actinomyces nislundi, and have an antifouling effect as much as MPC, a conventional dental composition that provides an excellent antifouling effect. It can mean.

나아가, 도 5b의 (b)를 참조하면, 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 및 MPC 함량에 따른 배지 상에서의 액티노마이세스 나이슬런디 흡착 수준을 나타내는 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예에 부착된 액티노마이세스 나이슬런디의 CFU 수준은 대조군에 비해 유의하게 낮은 것으로 나타난다 (p<0.001). 나아가, 1.5 % CBMA 실시예에 부착된 액티노마이세스 나이슬런디의 CFU 수준은 3 % MPC 비교에에 비해 유의하게 높은 것으로 나타나지만, 3 % CBMA 실시예에 부착된 액티노마이세스 나이슬런디의 CFU 수준은 3 % MPC 비교에에 비해 유의하게 낮은 것으로 나타난다 (p<0.001). 특히, 3 % CBMA 실시예로부터 획득된 현탁액을 도말한 배지에서의 액티노마이세스 나이슬런디에 대한 CFU는 유의하게 가장 낮은 것으로 나타난다 (p<0.001). 이때, 3 % CBMA 실시예로부터 획득된 현탁액을 도말한 배지에서의 액티노마이세스 나이슬런디에 대한 CFU는 대조군에 비하여 50 배 내지 70 배 낮은 것으로 나타난다.Further, referring to (b) of FIG. 5B, a result showing the adsorption level of Actinomyces nislundi on the medium according to the CBMA and MPC contents in the dental composition according to an embodiment of the present invention is shown. More specifically, the CFU level of Actinomyces nislundi attached to the 1.5% CBMA and 3% CBMA examples appeared to be significantly lower than that of the control group (p<0.001). Furthermore, the CFU level of Actinomyces nislundi attached to the 1.5% CBMA example appeared to be significantly higher than that of the 3% MPC comparison, but the CFU level of Actinomyces nislundi attached to the 3% CBMA example The CFU level appears to be significantly lower compared to the 3% MPC comparison (p<0.001). In particular, the CFU for Actinomyces nislundi in the medium plated with the suspension obtained from the 3% CBMA example appeared to be significantly lowest (p<0.001). At this time, the CFU for Actinomyces nislundi in the medium plated with the suspension obtained from the 3% CBMA example appeared to be 50 to 70 times lower than that of the control group.

이러한 결과는, CBMA가 액티노마이세스 나이슬런디의 흡착을 차단함에 따라 획득된 현탁액에 대한 콜로니의 수가 감소했음을 의미할 수 있다. 이때, 액티노마이세스 나이슬런디의 흡착을 차단할 수 있는 CBMA의 함량은, 전체 치과용 조성물의 총 중량에 대하여 1.5 wt % 내지 3 wt %일 수 있으며, 바람직하게는, 3 wt %일 수 있으나, 이에 제한되는 것은 아니다.These results may mean that the number of colonies for the obtained suspension decreased as CBMA blocked the adsorption of Actinomyces nislundi. At this time, the content of CBMA capable of blocking the adsorption of Actinomyces nislundi may be 1.5 wt% to 3 wt %, preferably 3 wt %, based on the total weight of the dental composition. , But is not limited thereto.

도 5c의 (a)를 참조하면, 공초점 레이져 현미경으로 측정된 베일로넬라 파르불라에 대한 생사 여부의 염색 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예는 3 % MPC 비교예와 비슷한 수준의 살아있는 베일로넬라 파르불라에 대한 형광발현을 갖는 것으로 나타나며, 대조군에 비해 살아있는 베일로넬라 파르불라에 대한 형광발현이 현저하게 감소한 것으로 나타난다. 이는, 1.5 % CBMA 및 3 % CBMA 실시예가 베일로넬라 파르불라에 대하여 대조군에 비해 높은 방오 효과를 가지고 있으며, 우수한 방오 효과를 제공하는 종래의 치과용 조성물인 MPC 만큼의 방오 효과를 갖는 것을 의미할 수 있다.Referring to (a) of FIG. 5C, the staining result of live or death of Baylonella parvula measured by a confocal laser microscope is shown. More specifically, the 1.5% CBMA and 3% CBMA examples were shown to have a similar level of fluorescence expression for live Baylonella parbula as compared to the 3% MPC comparative example, and fluorescence for live Baylonella parbula compared to the control group. The expression appears to be markedly reduced. This means that the 1.5% CBMA and 3% CBMA examples have a higher antifouling effect compared to the control group with respect to Baylonella parvula, and have an antifouling effect as much as MPC, a conventional dental composition that provides excellent antifouling effect. I can.

나아가, 도 5c의 (b)를 참조하면, 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 및 MPC 함량에 따른 배지 상에서의 베일로넬라 파르불라 흡착 수준을 나타내는 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예에 부착된 베일로넬라 파르불라의 CFU 수준은 대조군에 비해 유의하게 낮은 것으로 나타난다 (p<0.001). 나아가, 1.5 % CBMA 및 3 % CBMA 실시예에 부착된 베일로넬라 파르불라의 CFU 수준은 3 % MPC 비교에 비해 유의하게 낮은 것으로 나타난다 (p<0.001). 특히, 3 % CBMA 실시예로부터 획득된 현탁액을 도말한 배지에서의 베일로넬라 파르불라에 대한 CFU는 유의하게 가장 낮은 것으로 나타난다 (p<0.001). 이때, 3 % CBMA 실시예로부터 획득된 현탁액을 도말한 배지에서의 베일로넬라 파르불라에 대한 CFU는 대조군에 비하여 150 배 내지 170 배 낮은 것으로 나타난다.Further, referring to (b) of FIG. 5C, results showing the adsorption level of Baylonella parvula on the medium according to the CBMA and MPC contents in the dental composition according to an embodiment of the present invention are shown. More specifically, the CFU levels of Baylonella parvula attached to the 1.5% CBMA and 3% CBMA examples appear to be significantly lower than that of the control group (p<0.001). Furthermore, the CFU level of the Baylonella parvula attached to the 1.5% CBMA and 3% CBMA examples appeared to be significantly lower compared to the 3% MPC comparison (p<0.001). In particular, the CFU for Baylonella parvula in the medium plated with the suspension obtained from the 3% CBMA example appeared to be significantly lowest (p<0.001). At this time, the CFU for Baylonella parvula in the medium plated with the suspension obtained from the 3% CBMA example appeared to be 150 to 170 times lower than that of the control.

이러한 결과는, CBMA가 베일로넬라 파르불라의 흡착을 차단함에 따라 획득된 현탁액에 대한 콜로니의 수가 감소했음을 의미할 수 있다. 이때, 베일로넬라 파르불라의 흡착을 차단할 수 있는 CBMA의 함량은, 전체 치과용 조성물의 총 중량에 대하여 1.5 wt % 내지 3 wt %일 수 있으며, 바람직하게는 3 wt % 있으나, 이에 제한되는 것은 아니다.These results may mean that the number of colonies for the obtained suspension was reduced as CBMA blocked the adsorption of Baylonella parvula. At this time, the content of CBMA capable of blocking the adsorption of Baylonella parvula may be 1.5 wt% to 3 wt% based on the total weight of the total dental composition, preferably 3 wt %, but is limited thereto. no.

이상의 결과로, 본 발명의 다양한 실시예에서 이용되는 CBMA가 박테리아의 흡착, 보다 구체적으로 칸디다균, 액티노마이세스 나이슬런디 및 베일로넬라 파르불라의 흡착을 높은 수준으로 차단하는 것에 기여한다는 것을 확인하였다. 특히, 전체 조성물의 함량에 대하여 3 wt %의 CBMA를 포함하는 치과용 조성물을 이용했을 경우, PMMA 단독으로 이용했을 경우 보다 박테리아 흡착의 차단 효과가 향상된 것으로 나타난다. 나아가, 전체 조성물의 함량에 대하여 3 wt %의 CBMA를 포함하는 치과용 조성물을 이용했을 때, PMMA 단독으로 이용했을 경우 보다 50 배 내지 300 배 낮은 수준의 박테리아 밀도를 갖는 것으로 나타난다. 이에, CBMA의 함량은 전체 치과용 조성물의 총 중량에 대하여 1.5 내지 5 wt %일 수 있다. 바람직하게, 박테리아 흡착의 차단 효과가 극대화될 수 있는, CBMA의 함량은 전체 치과용 조성물의 총 중량에 대하여 1.5 내지 3 wt % 일 수 있다.As a result of the above, it was found that CBMA used in various embodiments of the present invention contributes to blocking the adsorption of bacteria, more specifically, Candida, Actinomyces nislundi, and Baylonella parvula to a high level. Confirmed. Particularly, when a dental composition containing 3 wt% of CBMA based on the total composition content is used, it appears that the blocking effect of bacterial adsorption is improved compared to when PMMA alone is used. Furthermore, when using a dental composition containing 3 wt% of CBMA based on the content of the total composition, it appears to have a bacterial density of 50 to 300 times lower than that of using PMMA alone. Accordingly, the content of CBMA may be 1.5 to 5 wt% based on the total weight of the total dental composition. Preferably, the content of CBMA, in which the blocking effect of bacterial adsorption can be maximized, may be 1.5 to 3 wt% based on the total weight of the total dental composition.

치과용 조성물의 항균 활성 평가Evaluation of antibacterial activity of dental compositions

이하에서는, 치과용 조성물 내의 대조군 및 3 % MPC로 이루어진 비교예 그룹과 1.5 % CBMA 및 3 % CBMA로 이루어진 실시예 그룹 각각에 대한 항균 활성 평가를 수행하였다. 이때, 대조군 및 각각의 실험군은 직경 10 mm 및 두께 2 mm의 금형에 의해 디스크 모양의 시편 형태로 준비되었다.In the following, antimicrobial activity evaluation was performed for each of the control group and the comparative example group consisting of 3% MPC and the example group consisting of 1.5% CBMA and 3% CBMA in the dental composition. At this time, the control group and each experimental group were prepared in the form of a disk-shaped specimen by a mold having a diameter of 10 mm and a thickness of 2 mm.

보다 구체적으로, 자연 타액과 유사한 환경을 제공하여 바이오필름을 성장시킬 수 있는 McBain 배지를 포함하는 박테리아 용액 1.5 ml을 대조군 (control), 1.5 % CBMA, 3 % CBMA 및 3 % MPC 각각의 시편 위에 배치하여 배양하였다. 그 다음, 8, 16 및 24 시간 후에 박테리아 용액을 1.5 ml씩 더 추가로 시편 위에 배치하여 총 48시간 동안 바이오필름을 성장시켰다.More specifically, 1.5 ml of a bacterial solution containing McBain medium that can grow a biofilm by providing an environment similar to natural saliva is placed on the specimens of each of the control, 1.5% CBMA, 3% CBMA, and 3% MPC. And cultured. Then, after 8, 16 and 24 hours, the bacterial solution was further placed on the specimen by 1.5 ml to grow the biofilm for a total of 48 hours.

이때, 박테리아 용액은 뮤신 2.5 g/l, 세균 펩톤 (bacteriological peptone) 2.0 g/l, 트립톤 (tryptone) 2.0 g/l, 효모 추출물 1.0 g/l, NaCl 0.35 g/l, KCl 0.2 g/l, CaCl2 g/l, 시스테인 하이드로 클로라이드(cysteine hydrochloride) 0.1 g/l, 헤민 (heamin) 0.001 g/l 및 비타민 K1 0.0002 g/l을 포함하는 McBain 배지에 바이오필름 모델이 혼합되어, 37 ℃에서 24시간 동안 배양되었다. At this time, the bacterial solution is mucin 2.5 g/l, bacterial peptone 2.0 g/l, tryptone 2.0 g/l, yeast extract 1.0 g/l, NaCl 0.35 g/l, KCl 0.2 g/l , CaCl2 g/l, cysteine hydrochloride 0.1 g/l, hemin 0.001 g/l, and vitamin K1 0.0002 g/l. Incubated for hours.

나아가, 바이오필름 모델은 충치 또는 치주 질환이 없고, 6개월 동안 항생제를 섭취하지 않았으며, 수집 전 24시간 동안은 양치질을 하지 않았고 수집전 2시간 동안은 취식을 하지 않은 6명의 공여자로부터 타액을 수집하여, 동일한 비율로 혼합하였다. 그 다음, 혼합된 타액은 멸균 글리세롤에 30 %의 농도로 희석하고, -80 ℃에서 저장하여 바이오필름 모델로 사용하였다.Furthermore, the biofilm model collected saliva from 6 donors who did not have caries or periodontal disease, did not take antibiotics for 6 months, did not brush their teeth for 24 hours before collection, and did not eat for 2 hours before collection. Then, they were mixed in the same ratio. Then, the mixed saliva was diluted to a concentration of 30% in sterile glycerol, and stored at -80 °C to be used as a biofilm model.

바이오필름 염색은 전술한 생존력 검사에서 사용된 생사 여부에 따라 박테리아가 염색되는 키트를 이용하여 염색하였다. 그 다음, 공초점 레이져 현미경 (confocal laser microscopy) 을 이용하여 무작위로 선택된 5곳의 위치에서 바이오필름을 시각화하였다. 그 다음, 축 방향으로 적층된 바이오필름의 이미지를 획득하고, 소프트웨어 (Zen, Carl Zeiss, Thornwood, NY, USA) 를 사용하여 각 바이오 필름의 두께를 측정하였다. The biofilm staining was performed using a kit in which bacteria were stained according to whether or not the biofilm was used in the above-described viability test. Then, the biofilm was visualized at five randomly selected locations using a confocal laser microscopy. Then, an image of the biofilm laminated in the axial direction was acquired, and the thickness of each biofilm was measured using software (Zen, Carl Zeiss, Thornwood, NY, USA).

도 6a 내지 6b는 본 발명의 일 실시예에 따른 치과용 조성물 내의 CBMA 함량에 따른 구강 내 장치에서의 바이오필름을 나타내는 결과이다.6A to 6B are results showing a biofilm in an oral device according to the CBMA content in a dental composition according to an embodiment of the present invention.

도 6a를 참조하면, 공초점 레이져 현미경으로 측정된 형성된 바이오필름에 대한 생사 여부의 염색 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예는 대조군에 비해 바이오필름의 형광 발현이 현저하게 감소한 것으로 나타나며, 3 % CBMA 실시예는 3 % MPC 비교예와 비슷한 바이오필름의 형광발현을 갖는 것으로 나타난다. 또한, 축 방향으로 적층된 바이오필름의 이미지에서도 1.5 % CBMA 및 3 % CBMA 실시예에 대한 적층된 바이오필름의 두께가 대조군에 비하여 현저하게 낮은 수준인 것으로 나타나며, 3 % CBMA 실시예는 3 % MPC 비교예와 비슷한 바이오필름의 두께를 갖는 것으로 나타난다.Referring to FIG. 6A, a result of dyeing the biofilm formed as measured by a confocal laser microscope is shown. More specifically, the 1.5% CBMA and 3% CBMA examples showed that the fluorescence expression of the biofilm was significantly reduced compared to the control, and the 3% CBMA example had the fluorescence expression of the biofilm similar to that of the 3% MPC comparative example. appear. In addition, in the image of the biofilm laminated in the axial direction, the thickness of the laminated biofilm for the 1.5% CBMA and 3% CBMA examples was found to be significantly lower than that of the control, and the 3% CBMA example was 3% MPC. It appears to have a thickness of a biofilm similar to that of the comparative example.

나아가, 도 6b의 (a)를 참조하면, 공초점 레이져 현미경으로 획득된 바이오필름의 이미지에서 측정된 바이오필름의 두께 비교 결과가 도시된다. 보다 구체적으로, 대조군 및 1.5 % CBMA 실시예에 증식된 바이오필름의 두께는 3 % CBMA 실시예에 증식된 바이오필름의 두께는 통계적인 차이 없이 유사한 수준을 갖는 것으로 나타난다. 그러나, 3 % CBMA 실시예에 증식된 바이오 필름의 두께는 대조군에 비해 유의하게 낮은 수준인 것으로 나타나며 (p<0.001), 3 % MPC 비교예와는 통계적인 차이 없이 유사한 수준을 갖는 것으로 나타난다. 이때, 3 % CBMA 실시예에 증시된 바이오필름의 두께는 대조군에 비해 1.5 내지 2 배 낮은 수준인 것으로 나타난다.Further, referring to (a) of FIG. 6B, a result of comparing the thickness of the biofilm measured from the image of the biofilm obtained with a confocal laser microscope is shown. More specifically, the thickness of the biofilm grown in the control and 1.5% CBMA examples was found to have a similar level without statistical difference in the thickness of the biofilm grown in the 3% CBMA example. However, the thickness of the biofilm grown in the 3% CBMA example appeared to be at a significantly lower level than the control (p<0.001), and it appeared to have a similar level with no statistical difference from the 3% MPC comparative example. At this time, the thickness of the biofilm stocked in the 3% CBMA example appears to be 1.5 to 2 times lower than that of the control group.

더 나아가, 도 6b의 (b)를 참조하면, 공초점 레이져 현미경으로 획득된 바이오필름의 이미지에서 측정된 바이오필름의 바이오매스 비교 결과가 도시된다. 보다 구체적으로, 1.5 % CBMA 및 3 % CBMA 실시예에 증식된 바이오필름의 바이오매스는 대조군에 비해 유의하게 낮은 수준인 것으로 나타난다 (p<0.001). 나아가, 1.5 % CBMA 실시예에 증식된 바이오필름의 바이오매스는 3 % MPC 비교에에 비해 유의하게 높은 것으로 나타나지만, 3 % CBMA 실시예에 증식된 바이오필름의 바이오매스는 3 % MPC 비교에에 비해 유의하게 낮은 것으로 나타난다 (p<0.001). 특히, 3 % CBMA 실시예에 증식된 바이오필름의 바이오매스가 유의하게 가장 낮은 것으로 나타난다 (p<0.001). 이때, 3 % CBMA 실시예에 증식된 바이오필름의 두께는 대조군에 비하여 4 내지 6 배 낮은 수준인 것으로 나타난다.Further, referring to (b) of FIG. 6B, a comparison result of the biomass of the biofilm measured from the image of the biofilm obtained with a confocal laser microscope is shown. More specifically, the biomass of the biofilm grown in the 1.5% CBMA and 3% CBMA examples appeared to be at a significantly lower level compared to the control group (p<0.001). Furthermore, the biomass of the biofilm grown in the 1.5% CBMA example appeared to be significantly higher than that of the 3% MPC comparison, but the biomass of the biofilm grown in the 3% CBMA example was compared to the 3% MPC comparison. It appears to be significantly low (p<0.001). In particular, it appears that the biomass of the biofilm grown in the 3% CBMA example was significantly lowest (p<0.001). At this time, the thickness of the biofilm grown in the 3% CBMA example appeared to be 4 to 6 times lower than that of the control group.

이상의 결과로, CBMA의 방오 활성이 박테리아에 대하여 직접적인 항균 활성에 의한 것이 아니라, 단백질 반발성과 같은 생물 활성에 의해 유도되는 것임을 의미할 수 있다. 또한, 본 발명의 다양한 실시예에서 이용되는 치과용 조성물은 3 %의 CBMA 함량에서 바이오필름 및 바이오매스 수준을 가장 낮은 것으로 나타난다. 이에, 치과용 조성물 및 치과용 조성물을 포함하는 구강 내 장치의 CBMA 함량은 전체 치과용 조성물의 총 중량에 대하여 3 wt %가 가장 효과적인 단백질 반발성을 유도할 수 있다. As a result of the above, it may mean that the antifouling activity of CBMA is not caused by direct antibacterial activity against bacteria, but is induced by biological activities such as protein repellency. In addition, the dental composition used in various embodiments of the present invention appears to have the lowest level of biofilm and biomass at a CBMA content of 3%. Accordingly, the CBMA content of the dental composition and the oral device including the dental composition may induce the most effective protein repellency of 3 wt% based on the total weight of the total dental composition.

치과용 조성물의 구강 내 장치 형성 평가Evaluation of oral device formation of dental composition

이하에서는, 치과용 조성물 내의 대조군 및 3 % MPC로 이루어진 비교예 그룹과 3 % CBMA로 이루어진 실시예에서의 구강 내 장치 형성에 대한 평가를 수행하였다. 구강 내 장치는 교정 치료 이후의 실제 환자 석고 모델을 복제하여 3개의 동일한 모델로 제조되었다. 이때, 구강 내 장치는 교합안정장치 형태로 제작되었으나 이에 제한되는 것은 아니며, 가철성 교정장치, 의치, 국소의치, 마우스피스 및 나이트 가드 등으로 다양하게 제작될 수 있다. 먼저, 왁스로 윤곽선을 설정하였다. 그 다음, 윤곽선 영역에 대조군, 3 % CBMA 및 3 % MPC의 치과용 조성물을 첨가하여 저온 중합 (60 ℃4.0 bar, 15 분) 조건으로 각각 치과용 조성물에 대한 교합안정장치를 제작하였다. 그 다음, 교합안정장치 표면은 종래의 방법으로 스무딩 및 폴리싱 처리되었다. Hereinafter, evaluation of the oral device formation in the comparative example group consisting of the control group and 3% MPC in the dental composition and the example consisting of 3% CBMA was performed. The intraoral device was made with three identical models by replicating the actual patient gypsum model after orthodontic treatment. At this time, the intraoral device is manufactured in the form of an occlusal stabilizing device, but is not limited thereto, and may be variously manufactured as a removable orthodontic device, dentures, local dentures, mouthpieces, and night guards. First, the outline was set with wax. Then, a control group, 3% CBMA, and 3% MPC of the dental composition were added to the contour area to prepare an occlusal stabilizer for each dental composition under low temperature polymerization (60° C. 4.0 bar, 15 minutes). Then, the occlusal stabilizer surface was smoothed and polished by a conventional method.

나아가, 표면 광택, 투명도 및 색상을 측정하기 위하여, 대조군 및 실험군 (3 % CBMA, 3 % MPC) 은 직경 15 mm 및 두께 2mm의 금형에 의해 디스크 모양의 시편 형태로 준비되었다. Further, in order to measure the surface gloss, transparency and color, the control group and the experimental group (3% CBMA, 3% MPC) were prepared in the form of a disk-shaped specimen by a mold having a diameter of 15 mm and a thickness of 2 mm.

표면 광택은 적외선 광택계를 이용하여 입사각 60 °에서 측정하였다. Surface gloss was measured at an incidence angle of 60° using an infrared gloss meter.

투명도는 자외선 분광 광도계를 이용하여 400-780 nm 파장 범위에서 5 nm의 간격으로 측정하였다. Transparency was measured at intervals of 5 nm in the wavelength range of 400-780 nm using an ultraviolet spectrophotometer.

시편의 색상은 분광 광도계를 사용하여 국제 조명 위원회 (Commission Internationale d' Eclairge, CIE)의 L*a*b* 표색계 값을 측정하였다. 이때, L은 밝기를 나타내는 값으로, 0에 가까울수록 어두운색(검정)을 의미하며, 100에 가까울수록 밝은색(흰색)을 의미한다. 나아가, a는 -60에 가까울수록 초록색을 의미하며, 60에 가까울수록 빨간색을 의미한다. 더 나아가, b는 -60에 가까울수록 파란색을 의미하며, 60에 가까울수록 노란색을 의미한다.The color of the specimen was measured using a spectrophotometer to measure the L*a*b* colorimetric value of the Commission Internationale d'Eclairge (CIE). In this case, L is a value representing brightness, and the closer to 0 means dark (black), and the closer to 100 means bright (white). Furthermore, the closer to -60 means green, and closer to 60 means red. Furthermore, b means blue as it approaches -60, and yellow as it approaches 60.

또한, 표면적 특성을 촬영하기 위하여, 3.3 mm x 10 mm x 25 mm 크기의 대조군, 3 % CBMA 및 3 % MPC 시편을 컴퓨터 제어 범용 시험기를 이용하여 파쇄하였다. 그 다음, 파쇄된 시편을 이온 코터를 사용하여 Pt (5 nm) 로 코팅하고 주사 전자 현미경을 사용하여 2 kV에서 촬영하였다. In addition, in order to photograph the surface area characteristics, the control, 3% CBMA and 3% MPC specimens with a size of 3.3 mm x 10 mm x 25 mm were crushed using a computer-controlled universal tester. Then, the crushed specimen was coated with Pt (5 nm) using an ion coater and photographed at 2 kV using a scanning electron microscope.

도 7a 및 7b는 본 발명의 일 실시예에 따른 치과용 조성물을 포함하는 구강 내 장치의 형성 평가를 나타내는 결과이다. 7A and 7B are results showing evaluation of formation of an intraoral device including a dental composition according to an embodiment of the present invention.

도 7a를 참조하면, 실시예 및 대조군에 따른 구강 내 장치의 표면 광택 및, 투명도 및 색상의 결과가 도시된다. 3 % CBMA 실시예의 광택도는 78.6 %로 대조군 93.6 % 및 3 % MPC 비교예 87.83 %에 비해 가장 낮은 광택도를 갖는 것으로 나타난다. 또한, 3 % CBMA 실시예의 투명도는 1.74 %로 대조군 21.17 % 및 3 % MPC 비교예 14.11 %에 비해 가장 낮은 투명도를 갖는 것으로 나타난다. 이는, CBMA를 포함하는 치과용 조성물이 PMMA로만 이루어진 치과용 조성물에 비하여 혼탁한 탁도를 갖는 것 의미할 수 있다. 나아가, 3 % CBMA 실시예의 색상은 35.4*11.91*1.6*으로 대조군 27.8*5.94*0.4 및 3 % MPC 비교예 28.25*6.13*0.42*에 비해 밝은 색상을 갖는 것으로 나타난다.Referring to Figure 7a, the results of the surface gloss, transparency and color of the intraoral device according to the embodiment and the control are shown. The glossiness of the 3% CBMA example was 78.6%, which was the lowest gloss compared to the control 93.6% and the 3% MPC comparative example 87.83%. In addition, the transparency of the 3% CBMA example was 1.74%, which was found to have the lowest transparency compared to the control 21.17% and the 3% MPC comparative example 14.11%. This may mean that the dental composition containing CBMA has turbidity compared to the dental composition made of only PMMA. Furthermore, the color of the 3% CBMA example is 35.4*11.91*1.6*, which appears to have a brighter color compared to the control 27.8*5.94*0.4 and the 3% MPC comparative example 28.25*6.13*0.42*.

도 7b를 참조하면, 전자 현미경으로 촬영된 실시예 및 비교예에 따른 구강 내 장치의 파쇄된 표면 이미지가 도시된다. 보다 구체적으로, 3 % MPC 비교예에서는 큰 입자들이 모여있으나, 3 % CBMA 실시예에서는 매우 균일한 입자 분포를 보이는 것으로 나타난다. 이는, CBMA가 MPC에 비하여 덜 응집되고, PMMA에서의 분산력이 더 좋은 것으로 나타난다. 즉, CBMA가 자기 결합을 거의 갖지 않음을 의미할 수 있다. 이에, 3 % CBMA 실시예가 3 % MPC 실험군 보다 균일하고 작은 입자로 형성됨으로서 보다 높은 탁도를 가질수 있다.Referring to FIG. 7B, images of a crushed surface of an intraoral device according to Examples and Comparative Examples taken with an electron microscope are shown. More specifically, in the 3% MPC comparative example, large particles were gathered, but in the 3% CBMA example, it was found to exhibit a very uniform particle distribution. This shows that CBMA is less agglomerated compared to MPC and has better dispersibility in PMMA. In other words, it may mean that CBMA has little magnetic coupling. Accordingly, the 3% CBMA example may have a higher turbidity as it is formed of uniform and smaller particles than the 3% MPC test group.

이상의 결과로, CBMA 및 PMMA로 구성된 치과용 조성물은, 구강 내 장치에 적용될 경우, 종래의 쌍성 이온성 물질인 MPC 및 PMMA를 함유한 치과용 조성물보다 낮은 자기 결합을 가질 수 있는 것으로 나타난다.As a result of the above, it is shown that the dental composition composed of CBMA and PMMA, when applied to an oral device, may have a lower magnetic bond than a dental composition containing MPC and PMMA, which are conventional binary ionic materials.

이에, CBMA 및 PMMA를 함유하는 본 발명의 치과용 조성물은, 구강 내 장치에 적용되었을 때 생물 부착 방지에 대하여 우수한 효과를 제공할 수 있다. Accordingly, the dental composition of the present invention containing CBMA and PMMA can provide an excellent effect on preventing biological adhesion when applied to an intraoral device.

이에, 본 발명은, CBMA 및 열가소성 수지를 포함하는 치과용 조성물을 제공함으로써, 열가소성 수지를 단독으로 이용했을 때 나타나는 치과용 조성물로서의 한계를 극복할 수 있다.Thus, the present invention, by providing a dental composition comprising CBMA and a thermoplastic resin, it is possible to overcome the limitation as a dental composition that appears when the thermoplastic resin is used alone.

예를 들어, 본 발명의 치과용 조성물은, 단백질의 침착 및 박테리아의 침착을 방지하는 방오 효과 및 이에 따른 박테리아에 대한 항균 활성을 제공하여 박테리아 감염에 취약한 치과용 조성물에 대한 한계점을 극복할 수 있다. For example, the dental composition of the present invention can overcome the limitations of a dental composition susceptible to bacterial infection by providing an antifouling effect to prevent deposition of proteins and bacteria, and thus antibacterial activity against bacteria. .

이상 첨부된 도면을 참조하여 본 발명의 실시 예들을 더욱 상세하게 설명하였으나, 본 발명은 반드시 이러한 실시 예로 국한되는 것은 아니고, 본 발명의 기술사상을 벗어나지 않는 범위 내에서 다양하게 변형 실시될 수 있다. 따라서, 본 발명에 개시된 실시 예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시 예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 그러므로, 이상에서 기술한 실시 예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.Although the embodiments of the present invention have been described in more detail with reference to the accompanying drawings, the present invention is not necessarily limited to these embodiments, and various modifications may be made without departing from the spirit of the present invention. Accordingly, the embodiments disclosed in the present invention are not intended to limit the technical idea of the present invention, but to explain the technical idea, and the scope of the technical idea of the present invention is not limited by these embodiments. Therefore, it should be understood that the embodiments described above are illustrative and non-limiting in all respects. The scope of protection of the present invention should be interpreted by the following claims, and all technical ideas within the scope equivalent thereto should be construed as being included in the scope of the present invention.

Claims (18)

CBMA (carboxybetaine methacrylate) 및 열가소성 수지를 포함하는, 치과용 조성물Dental composition containing CBMA (carboxybetaine methacrylate) and a thermoplastic resin 제 1항에 있어서,
MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), 트리고넬린 (trigonelline), 엑토인 (ectoine), 베타인 (betaine), 설포베타인 메타크릴레이트 (sulfobetaine methacrylate), SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-(3-methacryloylimino)propyl-N,N-dimethylammonio propanesulfonate) 및 SPV (3-(2'-vinyl-pyridinio)propanesulfonate) 으로 이루어진 그룹 중 적어도 하나인 쌍성 이온성 물질 (Zwitterionic material)을 더 포함하는, 치과용 조성물.The method of claim 1,
MPC (2-methacryloyloxyethyl phosphorylcholine), DMPC (1,2-dimyristoyl-sn-glycero-3-phosphatidylcholine), DMSP (3-dimethylsulfoniopropanoate), trigonelline, ectoine, betaine, Sulfobetaine methacrylate, SPE (N-(2-methacryloyloxy)ethyl-N,N-dimethylammonio propanesulfonate), SPP (N-(3-methacryloylimino)propyl-N,N-dimethylammonio propanesulfonate) and SPV (3-(2'-vinyl-pyridinio)propanesulfonate) Further comprising a zwitterionic material (Zwitterionic material) of at least one of the group consisting of, a dental composition. 제 1항에 있어서,
상기 CBMA의 함량은, 상기 치과용 조성물 전체 질량에 대하여 1.5 내지 5 wt %를 갖는, 치과용 조성물.The method of claim 1,
The content of the CBMA, having 1.5 to 5 wt% of the total mass of the dental composition, dental composition. 제 1항에 있어서,
상기 열가소성 수지는,
PMMA(ploy methyl methacrylate), 폴리에틸렌(polyethylene), 폴리프로필렌 (polypropylene), 폴리카보네이트 (polycarbonate), 폴리에틸렌 테레프탈레이트(polyethylene terephthalate), 나일론(nylon), 실리콘 및 ABS(acrylonitrile-butadien-styrene) 으로 이루어진 그룹 중 적어도 하나인, 치과용 조성물.The method of claim 1,
The thermoplastic resin,
The group consisting of ploy methyl methacrylate (PMMA), polyethylene, polypropylene, polycarbonate, polyethylene terephthalate, nylon, silicone, and acrylonitrile-butadien-styrene (ABS) At least one of, a dental composition. 제 4항에 있어서,
상기 열가소성 수지는,
PMMA인, 치과용 조성물.The method of claim 4,
The thermoplastic resin,
PMMA, a dental composition. 제 1항에 있어서,
상기 열가소성 수지의 함량은,
상기 치과용 조성물의 전체 질량에 대하여 95.0 내지 98.5 wt %인, 치과용 조성물.The method of claim 1,
The content of the thermoplastic resin,
95.0 to 98.5 wt% with respect to the total mass of the dental composition, a dental composition. 제 1항에 있어서,
상기 치과용 조성물은, 칸디다균(Candida albicans), 액티노마이세스 나이슬런디(Actinomyces naeslundii), 베일로넬라 파르불라(Veillonella parvula), 스트랩토코커스 소브리누스 (Streptococcus sobrinus), 스트랩토코커스 상기스 (Streptococcus sanguis), 스트랩토코커스 미티스 (Streptococcus mitior), 락토바실러스 카제이 (Lactbacillus casei), 락토바실러스 아시도필루스 (Lactbacillus acidophilus), 액티노마이세스 비스코서스 (Actinomyces viscosus) 및 액티노마이세스 네슬룬디 (Actinomyces naeslundii) 로 이루어진 그룹 중 적어도 하나의 박테리아에 대한 항균 활성을 갖는, 치과용 조성물.The method of claim 1,
The dental composition is Candida albicans, Actinomyces naeslundii, Veillonella parvula, Stratococcus sobrinus, Stratococcus, the above Streptococcus sanguis, Streptococcus mitior, Lactbacillus casei, Lactbacillus acidophilus, Actinomyces viscosus and Actinomyces viscosus A dental composition having an antimicrobial activity against at least one bacterium from the group consisting of Seth Nestlundii (Actinomyces naeslundii). 제 7항에 있어서,
상기 박테리아 노출 24시간 이후, 상기 치과용 조성물에서의 박테리아의 밀도는,
상기 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 50 배 내지 300 배 낮은 수준인, 치과용 조성물.The method of claim 7,
After 24 hours of exposure to the bacteria, the density of bacteria in the dental composition is,
The level of 50 to 300 times lower than that of the composition consisting of only a thermoplastic resin without containing the CBMA, a dental composition. 제 7항에 있어서,
상기 박테리아 노출 48시간 이후, 상기 치과용 조성물에서의 박테리아에 의한 바이오필름의 두께는,
상기 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 1.5 배 내지 2 배 낮은 수준인, 치과용 조성물.The method of claim 7,
After 48 hours of exposure to the bacteria, the thickness of the biofilm by bacteria in the dental composition is,
A level of 1.5 to 2 times lower than that of the composition consisting only of a thermoplastic resin without containing the CBMA, a dental composition. 제 9항에 있어서,
상기 바이오필름의 바이오매스 밀도는,
상기 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 4 배 내지 6 배 낮은 수준인, 치과용 조성물.The method of claim 9,
The biomass density of the biofilm is,
The level of 4 to 6 times lower than that of the composition consisting only of a thermoplastic resin without containing the CBMA, a dental composition. 제 1항에 있어서,
BSA 노출 4시간 이후, 상기 치과용 조성물에서의 단백질 흡착 수준은,
상기 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 1.5 배 내지 2 배 낮은 수준인, 치과용 조성물.The method of claim 1,
After 4 hours of BSA exposure, the level of protein adsorption in the dental composition is,
A level of 1.5 to 2 times lower than that of the composition consisting only of a thermoplastic resin without containing the CBMA, a dental composition. 제 1항에 있어서,
효모 및 곰팡이 브로스를 포함하는 YM 배지 노출 4시간 이후, 상기 치과용 조성물에서의 단백질 흡착 수준은,
상기 CBMA를 포함하지 않고 열가소성 수지로만 이루어진 조성물에 대하여 1.5 배 내지 3 배 낮은 수준인, 치과용 조성물.The method of claim 1,
After 4 hours of exposure to YM medium containing yeast and mold broth, the level of protein adsorption in the dental composition is,
A level of 1.5 to 3 times lower than that of the composition consisting only of a thermoplastic resin without containing the CBMA, a dental composition. 제 1항에 있어서,
안정화제, 난연제, 대전방지제, 연화제, 강화재, 충전재, 형광 중백제, 윤활제, 함입 감소제, 중축제 촉매, 소포제, 유화제, 증점제, 및 향료로 이루어진 그룹 중 적어도 하나를 더 포함하는, 치과용 조성물.The method of claim 1,
A dental composition further comprising at least one of the group consisting of stabilizers, flame retardants, antistatic agents, softeners, reinforcing agents, fillers, fluorescent whitening agents, lubricants, inclusion reducing agents, polycondensing agent catalysts, defoamers, emulsifiers, thickeners, and fragrances . 제 1항에 있어서,
하이드록시프로필 메틸셀룰로스 (Hydroxypropyl Methylcellulose), 하이드록시에틸 셀룰로스 (Hydroxyethyl Cellulose), 하이드록시프로필 셀룰로스 (Hydroxypropyl Cellulose), 폴리비닐 알코올 (Polyvinyl Alcohol), 폴리비닐 피롤리돈 (Polyvinyl Pyrrolidone), 카보머 (Carbomer), 및 초산 비닐 수지 (Polyvinyl Acetate) 로 이루어진 그룹 중 적어도 하나의 접착성 물질을 더 포함하는, 치과용 조성물. The method of claim 1,
Hydroxypropyl Methylcellulose, Hydroxyethyl Cellulose, Hydroxypropyl Cellulose, Polyvinyl Alcohol, Polyvinyl Pyrrolidone, Carbomer ), and at least one adhesive material from the group consisting of vinyl acetate resin (Polyvinyl Acetate). 제 1 내지 13항 중 어느 한 항에 기재된 치과용 조성물을 포함하는, 구강 내 장치.An intraoral device comprising the dental composition according to any one of claims 1 to 13. 제 15항에 있어서,
상기 구강 내 장치는,
가철성 교정장치, 의치, 국소의치, 마우스피스, 교합안정장치 및 나이트 가드로 이루어진 그룹 중 적어도 하나인, 구강 내 장치.The method of claim 15,
The intraoral device,
At least one of the group consisting of a removable orthodontic device, dentures, local dentures, mouthpieces, occlusal stabilizers, and night guards, intraoral device. 제 16항에 있어서,
상기 구강 내 장치는,
상기 교합안정장치인, 구강 내 장치.The method of claim 16,
The intraoral device,
The occlusal stabilizing device, an intraoral device. 치과용 조성물 전체 질량에 대하여 1.5 내지 5 wt %의 CBMA 분말을 38 내지 39.4 wt %의 열가소성 수지 액체에 혼합시키는 단계;
상기 CBMA 분말이 혼합된 열가소성 수지 액체에 57 내지 59.1 wt %의 PMMA 분말을 혼합시키는 단계;
상기 CBMA 분말, 열가소성 수지 분말 및 열가소성 수지 액체가 저온 중합되어 혼합 수지를 형성하는 단계, 및
상기 혼합 수지를 탄화 규소 원형 사포로 연마하는 단계를 포함하는, 구강 내 장치 제조 방법.Mixing 1.5 to 5 wt% of CBMA powder with 38 to 39.4 wt% of a thermoplastic resin liquid based on the total mass of the dental composition;
Mixing 57 to 59.1 wt% of PMMA powder in the thermoplastic resin liquid in which the CBMA powder is mixed;
The CBMA powder, the thermoplastic resin powder and the thermoplastic resin liquid are polymerized at a low temperature to form a mixed resin, and
Intraoral device manufacturing method comprising the step of polishing the mixed resin with a silicon carbide circular sandpaper.
KR1020190115643A 2019-09-19 2019-09-19 Dental compostion and mehod for preparing oral device comprising same KR102238313B1 (en)