KR20200068931A - Low reflection coating glass - Google Patents

Low reflection coating glass Download PDF

Info

Publication number
KR20200068931A
KR20200068931A KR1020180155889A KR20180155889A KR20200068931A KR 20200068931 A KR20200068931 A KR 20200068931A KR 1020180155889 A KR1020180155889 A KR 1020180155889A KR 20180155889 A KR20180155889 A KR 20180155889A KR 20200068931 A KR20200068931 A KR 20200068931A
Authority
KR
South Korea
Prior art keywords
low
index layer
refractive index
refractive
layer
Prior art date
Application number
KR1020180155889A
Other languages
Korean (ko)
Other versions
KR102177964B1 (en
Inventor
이현주
강현민
윤성군
오영훈
김진용
Original Assignee
주식회사 케이씨씨
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 케이씨씨 filed Critical 주식회사 케이씨씨
Priority to KR1020180155889A priority Critical patent/KR102177964B1/en
Priority to PCT/KR2019/012412 priority patent/WO2020116757A1/en
Publication of KR20200068931A publication Critical patent/KR20200068931A/en
Application granted granted Critical
Publication of KR102177964B1 publication Critical patent/KR102177964B1/en

Abstract

The present invention relates to a low-reflection coating glass. In particular, the low-reflection coating glass according to the present invention comprises: a glass substrate; and a low-reflection coating layer which includes a structure in which a first high-refractive index layer, a first low-refractive index layer, a second high-refractive index layer, and a second low-refractive index layer are sequentially stacked. In particular, the first high-refractive index layer and the second high-refractive index layer each have a refractive index of 2.0-2.5 and contain titanium oxide, the first low-refractive index layer and the second low-refractive index each have a refractive index of 1.3-1.6 and contain silicon oxide, and the low-reflection coating layer has a total thickness of 300-600 nm.

Description

저반사 코팅 유리{LOW REFLECTION COATING GLASS}Low-reflection coated glass{LOW REFLECTION COATING GLASS}

본 발명은 저반사 코팅 유리에 관한 것이다.The present invention relates to low-reflection coated glass.

저반사 코팅 유리는 가시광 반사율이 낮아 눈부심이 감소되고 시인성이 향상된 기능성 유리로서, 렌즈, 창유리, 장식 유리, 디스플레이 등의 영역에서 광범위하게 사용되고 있다. 이러한 저반사 코팅 유리는 통상적으로 고굴절률을 갖는 유전체층과 저굴절률을 갖는 유전체층을 3 내지 6층 교대로 적층하여 제조한다.Low-reflection coated glass is a functional glass with reduced visible light reflectance and reduced glare and improved visibility, and is widely used in areas such as lenses, window panes, decorative glass, and displays. Such low-reflection coated glass is usually manufactured by alternately stacking 3 to 6 layers of dielectric layers having a high refractive index and dielectric layers having a low refractive index.

구체적으로, 한국 등록특허공보 제1,015,155호(특허문헌 1)에는 고굴절률층 및 저굴절률층을 각각 특정 두께 범위로 교대로 적층하여 제조된 다층 투명 기판을 개시하고 있다. 그러나, 특허문헌 1의 다층 투명 기판은 측면 반사색상이 붉은 빛을 내는 단점이 있다.Specifically, Korean Patent Publication No. 1,015,155 (Patent Document 1) discloses a multi-layer transparent substrate prepared by alternately laminating a high-refractive-index layer and a low-refractive-index layer in a specific thickness range, respectively. However, the multilayer transparent substrate of Patent Document 1 has a disadvantage in that the side reflection color emits red light.

따라서, 가시광선 반사율이 낮고 적외선 차단율이 높은 측면 관찰시 중성색상을 갖는 저반사 코팅층에 대한 연구개발이 필요한 실정이다.Accordingly, research and development of a low-reflection coating layer having a neutral color is necessary when observing a side having a low visible light reflectance and a high infrared blocking rate.

한국 등록특허공보 제1,015,155호 (공개일: 2005. 03. 10.)Korean Registered Patent Publication No. 1,015,155 (Publication date: 2005. 03. 10.)

이에, 본 발명은 측면 관찰시 중성 색상을 갖고, 가시광선 반사율이 낮고, 적외선 차단율이 높은 저반사 코팅층을 포함하는 저반사 코팅 유리를 제공하고자 한다.Accordingly, the present invention is to provide a low-reflection coating glass comprising a low-reflection coating layer having a neutral color when viewed from the side, a low visible light reflectance, and a high infrared blocking rate.

본 발명은 유리 기재; 및 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층이 순차적으로 적층된 형태를 포함하는 저반사 코팅층;을 포함하고, 상기 제1 고굴절률층 및 상기 제2 고굴절률층 각각은 굴절률이 2.0 내지 2.5이고, 티타늄 산화물을 포함하며, 상기 제1 저굴절률층 및 상기 제2 저굴절률층 각각은 굴절률이 1.3 내지 1.6이고, 규소 산화물을 포함하고, 상기 저반사 코팅층은 총 두께가 300nm 내지 600nm인, 저반사 코팅 유리를 제공한다.The present invention is a glass substrate; And a first low-refractive-index layer, a first low-refractive-index layer, a second high-refractive-index layer, and a second low-refractive-index layer, the low-reflection coating layer including a stacked form; 2 Each of the high refractive index layer has a refractive index of 2.0 to 2.5, includes titanium oxide, and each of the first low refractive index layer and the second low refractive index layer has a refractive index of 1.3 to 1.6, contains silicon oxide, and the low reflection The coating layer provides a low-reflection coated glass having a total thickness of 300 nm to 600 nm.

본 발명에 따른 저반사 코팅 유리는 가시광선 반사율이 낮고, 적외선 차단율이 높아 외부의 높은 온도에 노출된 디스플레이를 효과적으로 보호 가능하고, 측면 관찰시 중성 색상을 가져 디스플레이의 시인성을 향상시키는 장점이 있다.The low-reflection coated glass according to the present invention has an advantage of improving visibility of a display by having a low visible light reflectance, a high infrared blocking rate, and effectively protecting a display exposed to a high temperature outside, and having a neutral color during side observation.

이하 본 발명을 상세히 설명한다.Hereinafter, the present invention will be described in detail.

저반사 코팅 유리Low reflective coating glass

본 발명에 따른 저반사 코팅 유리는 유리 기재; 및 저반사 코팅층;을 포함한다.The low-reflection coated glass according to the present invention includes a glass substrate; And a low reflection coating layer.

본 명세서의 "굴절률"은 분광 엘립소미터를 이용하여 파장 550㎚에 대해 측정한 굴절률값이다.“Refractive index” in this specification is a refractive index value measured for a wavelength of 550 nm using a spectroscopic ellipsometer.

유리 기재Glass substrate

상기 유리 기재는 예를 들어, 소다라임 유리, 소다-석회-규산염 유리, 용융 실리카 유리와 같은 통상의 유리; 저철분 무늬 유리(low-iron patterned glass), 저철분 판유리(low-iron float glass), 투명전도막(transparent conductive oxide, TCO) 유리 등을 들 수 있다. 또한, 상기 유리 기재로는 필요에 따라 표면 결처리(surface texture treatment)되거나 강화 또는 부분 강화된 유리를 사용할 수 있다.The glass substrate may be, for example, ordinary glass such as soda lime glass, soda-lime-silicate glass, fused silica glass; And low-iron patterned glass, low-iron float glass, and transparent conductive oxide (TCO) glass. Further, as the glass substrate, surface texture treatment or tempered or partially strengthened glass may be used as necessary.

저반사 코팅층Low reflection coating layer

상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층이 순차적으로 적층된 형태를 포함한다. 구체적으로, 상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층이 순차적으로 적층된 4층 구조일 수 있다.The low reflection coating layer includes a form in which a first high refractive index layer, a first low refractive index layer, a second high refractive index layer, and a second low refractive index layer are sequentially stacked. Specifically, the low-reflection coating layer may be a four-layer structure in which a first high-refractive-index layer, a first low-refractive-index layer, a second high-refractive-index layer, and a second low-refractive-index layer are sequentially stacked.

<제1 고굴절률층><1st high refractive index layer>

상기 제1 고굴절률층은 굴절률이 2.0 내지 2.5이고, 티타늄 산화물을 포함한다. 구체적으로, 상기 제1 고굴절률층은 굴절률이 2.1 내지 2.5, 2.1 내지 2.4, 또는 2.2 내지 2.4이고, 티타늄 산화물을 포함할 수 있다. 제1 고굴절률층의 굴절률이 상기 범위를 벗어날 경우, 저반사 코팅 유리의 가시광 반사율 이 충분하지 못할 수 있다.The first high refractive index layer has a refractive index of 2.0 to 2.5, and includes titanium oxide. Specifically, the first high refractive index layer has a refractive index of 2.1 to 2.5, 2.1 to 2.4, or 2.2 to 2.4, and may include titanium oxide. When the refractive index of the first high-refractive-index layer is outside the above range, the visible light reflectivity of the low-reflection coated glass may not be sufficient.

상기 제1 고굴절률층은 5nm 내지 15nm의 두께를 가질 수 있다. 구체적으로, 상기 제1 고굴절률층은 7nm 내지 15nm, 7nm 내지 13nm, 또는 8nm 내지 12nm의 두께를 가질 수 있다.The first high refractive index layer may have a thickness of 5nm to 15nm. Specifically, the first high refractive index layer may have a thickness of 7nm to 15nm, 7nm to 13nm, or 8nm to 12nm.

또한, 상기 제 1 고굴절률층은 100nm 내지 130nm의 두께를 가질 수 있다. 구체적으로, 상기 제 1 고굴절률층은 110nm 내지 120nm, 또는 112nm 내지 118nm의 두께를 가질 수 있다.In addition, the first high refractive index layer may have a thickness of 100nm to 130nm. Specifically, the first high refractive index layer may have a thickness of 110nm to 120nm, or 112nm to 118nm.

<제2 고굴절률층><2nd high refractive index layer>

상기 제2 고굴절률층은 굴절률이 2.0 내지 2.5이고, 티타늄 산화물을 포함한다. 보다 구체적으로, 상기 제2 고굴절률층은 굴절률이 2.1 내지 2.5, 2.1 내지 2.4, 또는 2.2 내지 2.4이고, 티타늄 산화물을 포함할 수 있다. 제2 고굴절률층의 굴절률이 상기 범위를 벗어날 경우, 저반사 코팅 유리의 가시광 반사율이 충분하지 못할 수 있다.The second high refractive index layer has a refractive index of 2.0 to 2.5, and includes titanium oxide. More specifically, the second high refractive index layer has a refractive index of 2.1 to 2.5, 2.1 to 2.4, or 2.2 to 2.4, and may include titanium oxide. When the refractive index of the second high-refractive-index layer is outside the above range, the visible light reflectivity of the low-reflection coated glass may not be sufficient.

상기 제2 고굴절률층은 100nm 내지 135nm의 두께를 가질 수 있다. 구체적으로, 상기 제2 고굴절률층은 100nm 내지 120nm, 또는 100nm 내지 110nm의 두께를 가질 수 있다.The second high refractive index layer may have a thickness of 100nm to 135nm. Specifically, the second high refractive index layer may have a thickness of 100nm to 120nm, or 100nm to 110nm.

<제1 저굴절률층><1st low refractive index layer>

상기 제1 저굴절률층은 굴절률이 1.3 내지 1.6이고, 규소 산화물을 포함한다. 구체적으로, 상기 제1 저굴절률층은 굴절률이 1.3 내지 1.5, 또는 1.4 내지 1.5이고, 규소 산화물을 포함할 수 있다. 제1 저굴절률층의 굴절률이 상기 범위를 벗어날 경우, 코팅면 측면 반사색상이 중성 색상을 가지지 못하고 매우 붉은 색상을 가지는 단점이 있다.The first low refractive index layer has a refractive index of 1.3 to 1.6, and includes silicon oxide. Specifically, the first low refractive index layer has a refractive index of 1.3 to 1.5, or 1.4 to 1.5, and may include silicon oxide. When the refractive index of the first low-refractive-index layer is outside the above range, there is a disadvantage in that the reflective color on the side of the coating surface does not have a neutral color and has a very red color.

상기 제1 저굴절률층은 180nm 내지 230nm의 두께를 가질 수 있다. 구체적으로, 상기 제 1 저굴절률층은 182nm 내지 225nm의 두께를 가질 수 있다.The first low refractive index layer may have a thickness of 180nm to 230nm. Specifically, the first low refractive index layer may have a thickness of 182nm to 225nm.

<제2 저굴절률층><2nd low refractive index layer>

상기 제2 저굴절률층은 굴절률이 1.3 내지 1.6이고, 규소 산화물을 포함한다. 구체적으로, 상기 제2 저굴절률층은 굴절률이 1.3 내지 1.5, 또는 1.4 내지 1.5이고, 규소 산화물을 포함할 수 있다. 제2 저굴절률층의 굴절률이 상기 범위를 벗어날 경우, 저반사 코팅 유리의 가시광 반사율이 충분하지 못하고, 유리를 측면 관찰시 중성 색상이 아닌 적색을 띄는 단점이 발생할 수 있다.The second low refractive index layer has a refractive index of 1.3 to 1.6, and includes silicon oxide. Specifically, the second low refractive index layer has a refractive index of 1.3 to 1.5, or 1.4 to 1.5, and may include silicon oxide. When the refractive index of the second low-refractive-index layer is out of the above range, the visible light reflectance of the low-reflection coated glass is insufficient, and when the glass is viewed from the side, there may be a disadvantage of red instead of neutral color.

상기 제2 저굴절률층은 65nm 내지 95nm의 두께를 가질 수 있다. 구체적으로, 상기 제2 저굴절률층은 70nm 내지 90nm, 또는 75nm 내지 85nm의 두께를 가질 수 있다.The second low refractive index layer may have a thickness of 65 nm to 95 nm. Specifically, the second low refractive index layer may have a thickness of 70nm to 90nm, or 75nm to 85nm.

상기 저반사 코팅층은 총 두께가 300nm 내지 600nm이다. 구체적으로, 상기 저반사 코팅층은 총 두께가 350nm 내지 570nm, 400nm 내지 500nm, 또는 410nm 내지 490nm일 수 있다. The low-reflection coating layer has a total thickness of 300nm to 600nm. Specifically, the low-reflection coating layer may have a total thickness of 350nm to 570nm, 400nm to 500nm, or 410nm to 490nm.

상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층을 1: 15~36 : 8~21 : 5~17의 두께비로 포함할 수 있다. 구체적으로, 상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층을 1: 21~23 : 10~11 : 7.5~9의 두께비로 포함할 수 있다. The low reflection coating layer may include a first high refractive index layer, a first low refractive index layer, a second high refractive index layer, and a second low refractive index layer in a thickness ratio of 1: 15 to 36: 8 to 21: 5 to 17. Specifically, the low-reflection coating layer may include a first high refractive index layer, a first low refractive index layer, a second high refractive index layer, and a second low refractive index layer at a thickness ratio of 1: 21 to 23: 10 to 11: 7.5 to 9. Can be.

상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층을 1: 1.3~2.3 : 0.7~1.4 : 0.5~0.9의 두께비로 포함할 수 있다. 구체적으로, 상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층을 1: 1.4~2.0 : 0.8~1.1 : 0.6~0.8의 두께비로 포함할 수 있다.The low reflection coating layer may include a first high refractive index layer, a first low refractive index layer, a second high refractive index layer, and a second low refractive index layer at a thickness ratio of 1: 1.3 to 2.3: 0.7 to 1.4: 0.5 to 0.9. Specifically, the low reflection coating layer may include a first high refractive index layer, a first low refractive index layer, a second high refractive index layer, and a second low refractive index layer in a thickness ratio of 1: 1.4 to 2.0: 0.8 to 1.1: 0.6 to 0.8. Can be.

각 층의 두께비가 상기 범위를 벗어날 경우, 저반사 코팅 유리의 가시광 반사율 및 투과율, 및 적외선 반사율 및 차단율이 충분하지 못하고, 유리의 측면 관찰시 중성색이 아닌 적색으로 보이는 문제가 발생할 수 있다.When the thickness ratio of each layer is outside the above range, the visible light reflectance and transmittance of the low-reflection coated glass, and the infrared reflectance and the cutoff rate are insufficient, and a problem that the red color is observed instead of the neutral color may occur when observing the side of the glass.

상기 저반사 코팅 유리는 가시광선 반사율이 5% 이하이고, 가시광선 투과율이 90% 이상이며, 적외선 차단율이 45% 이상이고, 50°의 측면 관측시 │a*│≤10 및 │b*│≤10인 중성 색상을 가질 수 있다. 구체적으로, 상기 저반사 코팅 유리는 가시광선 반사율이 4.9% 이하이고, 가시광선 투과율이 90.1% 이상이며, 적외선 차단율이 47% 이상이고, 50°의 측면 관측시 │a*│≤8 또는 3, 및 │b*│≤7, 또는 6인 중성 색상을 가질 수 있다.The low-reflection coated glass has a visible light reflectance of 5% or less, a visible light transmittance of 90% or more, an infrared cutoff rate of 45% or more, and │a*│≤10 and │b*│≤ when observing the side at 50° It can have a neutral color of 10 people. Specifically, the low-reflection coated glass has a visible light reflectance of 4.9% or less, a visible light transmittance of 90.1% or more, an infrared cutoff rate of 47% or more, and 50° side observations when │a*│≤8 or 3, And │b*│≤7, or 6.

상술한 바와 같은 저반사 코팅 유리는 측면 색상이 중간색을 나타냄으로써, 측면 색상이 붉은색을 띠는 기존의 저반사 코팅 유리에 비해 LFD(large format display)와 같은 디스플레이의 보호용으로 매우 적합하다. 또한, 상기 저반사 코팅 유리는 가시광선 투과율이 낮고, 적외선 차단율이 높아 외부의 높은 온도에 노출된 디스플레이를 효과적으로 보호할 수 있다.The low-reflection coated glass as described above is suitable for protecting a display, such as a large format display (LFD), compared to a conventional low-reflection coated glass in which the side color has a red color because the side color represents an intermediate color. In addition, the low-reflection coating glass has a low visible light transmittance and a high infrared blocking rate, and thus can effectively protect a display exposed to a high external temperature.

이하, 실시예를 통하여 본 발명을 보다 구체적으로 설명한다.Hereinafter, the present invention will be described in more detail through examples.

그러나 이들 실시예는 본 발명의 이해를 돕기 위한 것일 뿐 어떠한 의미로든 본 발명의 범위가 이들 실시예로 한정되는 것은 아니다.However, these examples are only for understanding the present invention, and the scope of the present invention is not limited to these examples in any sense.

[실시예][Example]

실시예 1.Example 1.

6mm 유리 기판에 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층을 순차적으로 성막하여 저반사 코팅 유리를 제조하였으며, 각각의 굴절률층의 두께는 하기 표 1에 나타냈다. The first high refractive index layer, the first low refractive index layer, the second high refractive index layer and the second low refractive index layer were sequentially deposited on a 6mm glass substrate to prepare a low-reflection coating glass, and the thickness of each refractive index layer is shown in Table 1 below. Showed on.

구체적으로, 각 굴절률층의 성막은 마그네트론 스퍼터링 설비를 사용하여 수행하였으며, TiO2 타겟과 SiAl 타겟을 사용하였다. 이로 인해, 제1 고굴절률층 및 제2 고굴절률층은 2.32의 굴절률을 갖는 티타늄 산화물로 구성되고, 제1 저굴절률층 및 제2 저굴절률층은 1.45의 굴절률을 갖는 규소 산화물로 구성되었다.Specifically, the film formation of each refractive index layer was performed using a magnetron sputtering facility, and a TiO 2 target and a SiAl target were used. For this reason, the first high refractive index layer and the second high refractive index layer were made of titanium oxide having a refractive index of 2.32, and the first low refractive index layer and the second low refractive index layer were composed of silicon oxide having a refractive index of 1.45.

실시예 2 내지 8 및 비교예 1 내지 10. Examples 2 to 8 and Comparative Examples 1 to 10.

각 굴절률층의 두께를 하기 표 1 및 2의 기재와 같이 조절한 것을 제외하고는, 실시예 1과 동일한 방법으로 저반사 코팅 유리를 제조하였다.A low-reflection coated glass was prepared in the same manner as in Example 1, except that the thickness of each refractive index layer was adjusted as described in Tables 1 and 2 below.

시험예: 저반사 코팅 유리의 물성 측정Test Example: Measurement of physical properties of low-reflection coated glass

실시예 1 내지 8 및 비교예 1 내지 10의 저반사 코팅 유리를 대상으로 하기와 같은 방법으로 물성을 측정하였으며, 그 결과를 표 1 내지 3에 나타냈다.The properties of the low-reflection coated glass of Examples 1 to 8 and Comparative Examples 1 to 10 were measured in the following manner, and the results are shown in Tables 1 to 3.

(1) 적외선 및 가시광선 투과율 및 반사율(1) Infrared and visible light transmittance and reflectance

300nm 내지 1500nm의 영역에서 KS L 2514규격에 따라 투과율 및 반사율을 분광광도계 Lambda950(PerkinElmer 사, KS L 2514 규격)을 이용하여 측정하고 그 결과를 표 1 및 2에 나타냈다. 이때, 적외선 차단율은 (100-적외선 투과율)%로 정의한다. 또한, 표 1 및 2의 가시광 투과율 및 반사율은 380nm 내지 780nm의 값이고, 적외선 차단율 및 반사율은 780nm 내지 2,500nm의 값이다.Transmittance and reflectance according to the KS L 2514 standard in the region of 300 nm to 1500 nm were measured using a spectrophotometer Lambda950 (PerkinElmer, KS L 2514 standard) and the results are shown in Tables 1 and 2. In this case, the infrared blocking rate is defined as (100-infrared transmittance)%. In addition, the visible light transmittance and reflectance of Tables 1 and 2 are values of 380 nm to 780 nm, and the infrared cutoff rate and reflectance are values of 780 nm to 2,500 nm.

(2) 반사색상 및 각도별 색상 변화치(2) Color change value by reflection color and angle

저반사 코팅 유리의 반사색상 및 각도별 색상 변화치 값을 C.I.E 시스템에 따라 측정하였다. 구체적으로, 색차는 분광광도계 Lambda950(PerkinElmer 사)을 사용하여 측정하였고, 각도별 색상을 찍는 액세서리를 이용하여 확인하였으며, 그 결과를 표 1 내지 3에 나타냈다.The color change value of each reflection color and angle of the low-reflection coated glass was measured according to the C.I.E system. Specifically, the color difference was measured using a spectrophotometer Lambda950 (PerkinElmer), and was confirmed using an accessory that takes color by angle, and the results are shown in Tables 1 to 3.

실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 실시예 4Example 4 실시예 5Example 5 실시예 6Example 6 실시예 7Example 7 실시예 8Example 8 제2 저굴절률층2nd low refractive index layer 80 nm80 nm 80 nm80 nm 80 nm80 nm 80 nm80 nm 80 nm80 nm 80 nm80 nm 80 nm80 nm 80 nm80 nm 제2 고굴절률층2nd high refractive index layer 102 nm102 nm 102 nm102 nm 120 nm120 nm 120 nm120 nm 105 nm105 nm 105 nm105 nm 105 nm105 nm 135 nm135 nm 제1 저굴절률층1st low refractive index layer 180 nm180 nm 220 nm220 nm 230 nm230 nm 230 nm230 nm 183 nm183 nm 190 nm190 nm 183 nm183 nm 220 nm220 nm 제1 고굴절률층1st high refractive index layer 5 nm5 nm 10 nm10 nm 12 nm12 nm 15 nm15 nm 100 nm100 nm 110 nm110 nm 115 nm115 nm 130 nm130 nm 가시광선 투과율Visible light transmittance 91.20%91.20% 91.30%91.30% 90.84%90.84% 90.44%90.44% 90.02%90.02% 90.03%90.03% 90.20%90.20% 90.51%90.51% 가시광선 반사율Visible light reflectance 4.97%4.97% 4.40%4.40% 4.91%4.91% 4.95%4.95% 4.96%4.96% 4.89%4.89% 4.90%4.90% 4.83%4.83% 적외선 반사율Infrared reflectance 23.40%23.40% 24.70%24.70% 25.10%25.10% 27.70%27.70% 32.00%32.00% 36.20%36.20% 36.00%36.00% 36.90%36.90% 적외선 차단율Infrared blocking rate 46.10%46.10% 47.60%47.60% 48.90%48.90% 49.10%49.10% 52.90%52.90% 53.10%53.10% 55.30%55.30% 57.10%57.10% △a*b*△a*b* 9.99.9 20.320.3 15.515.5 15.515.5 15.815.8 12.912.9 10.610.6 14.414.4 코팅면 반사색상Coated surface reflection color 50°a*50°a* 4.84.8 2.52.5 -3.1-3.1 -2.6-2.6 -3.2-3.2 -0.3-0.3 1.21.2 -2.7-2.7 50°b*50°b* -1.9-1.9 -0.5-0.5 -4.4-4.4 -5.1-5.1 -5.5-5.5 2.82.8 -6.2-6.2 4.84.8

비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 비교예 6Comparative Example 6 비교예 7Comparative Example 7 비교예 8Comparative Example 8 비교예 9Comparative Example 9 비교예 10Comparative Example 10 제2 저굴절률층2nd low refractive index layer 9595 6565 6565 120120 180180 8080 8080 8080 4040 8080 제2 고굴절률층2nd high refractive index layer 135135 100100 100100 8080 110110 102102 102102 4040 102102 100100 제1 저굴절률층1st low refractive index layer 230230 180180 180180 2020 200200 220220 55 220220 220220 3535 제1 고굴절률층1st high refractive index layer 44 1616 140140 4040 1010 5050 1010 1010 1010 1010 가시광선 투과율Visible light transmittance 89.18%89.18% 88.80%88.80% 87.13%87.13% 87.40%87.40% 84.70%84.70% 78.10%78.10% 89.60%89.60% 85.50%85.50% 86.40%86.40% 90.10%90.10% 가시광선 반사율Visible light reflectance 7.38%7.38% 7.61%7.61% 8.96%8.96% 8.80%8.80% 11%11% 17%17% 5.20%5.20% 9.80%9.80% 8.20%8.20% 5.20%5.20% 적외선 반사율Infrared reflectance 33.00%33.00% 23.70%23.70% 22.70%22.70% 21.20%21.20% 38.40%38.40% 30.40%30.40% 19.10%19.10% 21.90%21.90% 30.50%30.50% 21.20%21.20% 적외선 차단율Infrared blocking rate 52.70%52.70% 42.10%42.10% 45.90%45.90% 42.70%42.70% 57.10%57.10% 50.00%50.00% 31.90%31.90% 42.60%42.60% 48.10%48.10% 41.50%41.50% △a*b*△a*b* 11.611.6 16.616.6 7.97.9 21.121.1 14.314.3 9.39.3 19.919.9 20.520.5 18.918.9 31.331.3 코팅면 반사색상Coated surface reflection color 50°a*50°a* 17.0717.07 -5.8-5.8 3.563.56 17.617.6 22.322.3 16.316.3 20.420.4 11.511.5 23.123.1 19.819.8 50°b*50°b* -5.7-5.7 -13.9-13.9 -20.79-20.79 -35.4-35.4 -7.2-7.2 -6.2-6.2 -10.7-10.7 -15.9-15.9 -1.8-1.8 -8.4-8.4

표 1에서 보는 바와 같이, 실시예 1 내지 8의 저반사 코팅 유리는 가시광선 투과율 및 적외선 차단율이 높고, 가시광선 반사율이 낮으며, 측면 색상이 중성색이였다. As shown in Table 1, the low-reflection coated glass of Examples 1 to 8 had a high visible light transmittance and an infrared cutoff rate, a low visible light reflectance, and a side color having a neutral color.

반면, 표 2에서 보는 바와 같이, 비교예 1 내지 10의 유리는 가시광선 반사율이 5% 이상으로 높고, 가시광선 투과율이 낮아 외부의 높은 온도에 노출된 디스플레이의 보호용으로 적합하지 않음을 알 수 있었다.On the other hand, as shown in Table 2, it was found that the glass of Comparative Examples 1 to 10 has a high visible light reflectance of 5% or more and a low visible light transmittance, and thus is not suitable for protecting a display exposed to high temperatures outside. .

코팅면 반사색상Coated surface reflection color △a*b*△a*b* 정면face 30°30° 50°50° 실시예 1Example 1 a*a* 9.69.6 5.65.6 4.84.8 9.99.9 b*b* -7.9-7.9 -2.7-2.7 -1.9-1.9 실시예 2Example 2 a*a* 8.18.1 6.56.5 2.52.5 20.320.3 b*b* -19.9-19.9 -11.7-11.7 -0.5-0.5 실시예 3Example 3 a*a* 2.82.8 -6.8-6.8 -3.1-3.1 15.515.5 b*b* -9.9-9.9 -3.3-3.3 -4.4-4.4 실시예 4Example 4 a*a* 8.18.1 0.10.1 -2.6-2.6 15.515.5 b*b* -19.9-19.9 -11.2-11.2 -5.1-5.1 실시예 5Example 5 a*a* 6.36.3 -1.5-1.5 -3.2-3.2 15.815.8 b*b* -11.2-11.2 -2.1-2.1 -5.5-5.5 실시예 6Example 6 a*a* 4.34.3 33 -0.3-0.3 12.912.9 b*b* -8.8-8.8 -1.3-1.3 2.82.8 실시예 7Example 7 a*a* 6.66.6 2.52.5 1.21.2 10.610.6 b*b* -12.1-12.1 -12.6-12.6 -6.2-6.2 실시예 8Example 8 a*a* 5.25.2 -1.2-1.2 -2.7-2.7 14.414.4 b*b* -7.1-7.1 3.63.6 4.84.8 비교예 1Comparative Example 1 a*a* 99 10.910.9 11.211.2 11.611.6 b*b* -8.2-8.2 -1.3-1.3 -5.7-5.7 비교예 2Comparative Example 2 a*a* 10.310.3 -3.8-3.8 -5.8-5.8 16.616.6 b*b* -16.4-16.4 -13.2-13.2 -13.9-13.9 비교예 3Comparative Example 3 a*a* 8.88.8 2.72.7 3.563.56 7.97.9 b*b* -12.6-12.6 -12.1-12.1 -13.7-13.7 비교예 4Comparative Example 4 a*a* 1212 19.719.7 17.617.6 21.121.1 b*b* -48.7-48.7 -48.6-48.6 -35.4-35.4 비교예 5Comparative Example 5 a*a* 8.28.2 15.815.8 22.322.3 14.314.3 b*b* -8.4-8.4 -8.5-8.5 -7.2-7.2 비교예 6Comparative Example 6 a*a* 7.97.9 11.911.9 16.316.3 9.39.3 b*b* -10.2-10.2 -8.1-8.1 -6.2-6.2 비교예 7Comparative Example 7 a*a* 16.816.8 19.419.4 20.420.4 19.919.9 b*b* 8.98.9 -4.4-4.4 -10.7-10.7 비교예 8Comparative Example 8 a*a* 29.829.8 18.918.9 11.511.5 20.520.5 b*b* -15.9-15.9 -11.3-11.3 -15.9-15.9 비교예 9Comparative Example 9 a*a* 20.120.1 22.822.8 23.123.1 18.918.9 b*b* -20.3-20.3 -10.6-10.6 -1.8-1.8 비교예 10 Comparative Example 10 a*a* 6.66.6 17.817.8 19.819.8 31.331.3 b*b* 19.819.8 -1.3-1.3 -8.4-8.4

표 3 에서 보는 바와 같이, 실시예 1 내지 8의 유리는 정면 및 측면 모두에서 중성색을 나타냈다. 반면, 비교예 1 내지 10의 유리는 정면 및 측면 모두에서 보라색을 띠었다.As shown in Table 3, the glasses of Examples 1 to 8 exhibited neutral colors on both the front and side surfaces. On the other hand, the glasses of Comparative Examples 1 to 10 were purple on both the front and side surfaces.

Claims (6)

유리 기재; 및
제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층이 순차적으로 적층된 형태를 포함하는 저반사 코팅층;을 포함하고,
상기 제1 고굴절률층 및 상기 제2 고굴절률층 각각은 굴절률이 2.0 내지 2.5이고, 티타늄 산화물을 포함하며,
상기 제1 저굴절률층 및 상기 제2 저굴절률층 각각은 굴절률이 1.3 내지 1.6이고, 규소 산화물을 포함하고,
상기 저반사 코팅층은 총 두께가 300nm 내지 600nm인, 저반사 코팅 유리.Glass substrates; And
The first high-refractive-index layer, the first low-refractive-index layer, the second high-refractive-index layer and the second low-refractive-index layer, the low-reflection coating layer comprising a stacked form; includes,
Each of the first high refractive index layer and the second high refractive index layer has a refractive index of 2.0 to 2.5, and includes titanium oxide,
Each of the first low-refractive-index layer and the second low-refractive-index layer has a refractive index of 1.3 to 1.6, and includes silicon oxide,
The low-reflection coating layer has a total thickness of 300nm to 600nm, low-reflection coating glass. 청구항 1에 있어서,
상기 제1 고굴절률층은 5nm 내지 15nm의 두께를 갖고,
상기 제1 저굴절률층은 180nm 내지 230nm의 두께를 갖고,
상기 제2 고굴절률층은 100nm 내지 135nm의 두께를 갖고,
상기 제2 저굴절률층은 65nm 내지 95nm의 두께를 갖는, 저반사 코팅 유리.The method according to claim 1,
The first high refractive index layer has a thickness of 5nm to 15nm,
The first low refractive index layer has a thickness of 180nm to 230nm,
The second high refractive index layer has a thickness of 100nm to 135nm,
The second low refractive index layer has a thickness of 65nm to 95nm, low-reflection coated glass. 청구항 2에 있어서,
상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층을 1: 15~36 : 8~21 : 5~17의 두께비로 포함하는, 저반사 코팅 유리.The method according to claim 2,
The low-reflection coating layer includes a first high-refractive-index layer, a first low-refractive-index layer, a second high-refractive-index layer, and a second low-refractive-index layer at a thickness ratio of 1: 15 to 36: 8 to 21: 5 to 17, and low reflection Coated glass. 청구항 1에 있어서,
상기 제1 고굴절률층은 100nm 내지 130nm의 두께를 갖고,
상기 제1 저굴절률층은 180nm 내지 230nm의 두께를 갖고,
상기 제2 고굴절률층은 100nm 내지 135nm의 두께를 갖고,
상기 제2 저굴절률층은 65nm 내지 95nm의 두께를 갖는, 저반사 코팅 유리.The method according to claim 1,
The first high refractive index layer has a thickness of 100nm to 130nm,
The first low refractive index layer has a thickness of 180nm to 230nm,
The second high refractive index layer has a thickness of 100nm to 135nm,
The second low refractive index layer has a thickness of 65nm to 95nm, low-reflection coated glass. 청구항 4에 있어서,
상기 저반사 코팅층은 제1 고굴절률층, 제1 저굴절률층, 제2 고굴절률층 및 제2 저굴절률층을 1: 1.3~2.3 : 0.7~1.4 : 0.5~0.9의 두께비로 포함하는, 저반사 코팅 유리.The method according to claim 4,
The low-reflection coating layer includes a first high-refractive-index layer, a first low-refractive-index layer, a second high-refractive-index layer, and a second low-refractive-index layer in a thickness ratio of 1: 1.3 to 2.3: 0.7 to 1.4: 0.5 to 0.9. Coated glass. 청구항 1에 있어서,
가시광선 반사율이 5% 이하이고, 가시광선 투과율이 90% 이상이며, 적외선 차단율이 45% 이상이고, 50°의 측면 관측시 │a*│≤10 및 │b*│≤10인 중성 색상을 갖는, 저반사 코팅 유리.
The method according to claim 1,
Visible light reflectance is 5% or less, visible light transmittance is 90% or more, infrared ray blocking rate is 45% or more, and when observing the side of 50°, it has neutral colors of │a*│≤10 and │b*│≤10 , Low-reflection coated glass.
KR1020180155889A 2018-12-06 2018-12-06 Low reflection coating glass KR102177964B1 (en)