KR20200038062A - Sealing member and flat display panel including the same - Google Patents

Sealing member and flat display panel including the same Download PDF

Info

Publication number
KR20200038062A
KR20200038062A KR1020180117701A KR20180117701A KR20200038062A KR 20200038062 A KR20200038062 A KR 20200038062A KR 1020180117701 A KR1020180117701 A KR 1020180117701A KR 20180117701 A KR20180117701 A KR 20180117701A KR 20200038062 A KR20200038062 A KR 20200038062A
Authority
KR
South Korea
Prior art keywords
sealing member
display panel
polarizing plate
weight
lower substrate
Prior art date
Application number
KR1020180117701A
Other languages
Korean (ko)
Other versions
KR102545120B1 (en
Inventor
송켈리수연
진미형
황준하
김재영
Original Assignee
엘지디스플레이 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 엘지디스플레이 주식회사 filed Critical 엘지디스플레이 주식회사
Priority to KR1020180117701A priority Critical patent/KR102545120B1/en
Publication of KR20200038062A publication Critical patent/KR20200038062A/en
Application granted granted Critical
Publication of KR102545120B1 publication Critical patent/KR102545120B1/en

Abstract

The present invention relates to a sealing member and a flat display panel comprising the same. The sealing member according to the present invention comprises a urethane acrylate oligomer and an acrylate monomer, and can exhibit excellent adhesion and elasticity. In addition, the sealing member according to the present invention can integrate an inner sealing material for bonding a lower substrate and an upper substrate with a side sealing material for sealing a side surface of the flat display panel.

Description

실링부재 및 이를 포함하는 평판 디스플레이 패널{SEALING MEMBER AND FLAT DISPLAY PANEL INCLUDING THE SAME}Sealing member and flat panel display panel including the same {SEALING MEMBER AND FLAT DISPLAY PANEL INCLUDING THE SAME}

본 발명은 평판 디스플레이 패널의 측면에 배치되는 실링 부재에 관한 것이다.The present invention relates to a sealing member disposed on the side of a flat panel display panel.

또한, 본 발명은 상기 실링 부재를 포함하는 평판 디스플레이 패널에 관한 것이다.In addition, the present invention relates to a flat panel display panel including the sealing member.

디스플레이 기술이 발달하면서 평판 디스플레이 패널(Flat Display Panel)들이 많이 사용되고 있다. 평판 디스플레이 패널로는 액정 디스플레이(Liquid Crystal Display) 패널, OLED 디스플레이(Organic Light Emitting Diode Display) 패널 등이 있다.2. Description of the Related Art With the development of display technology, flat panel displays are widely used. The flat panel display panel includes a liquid crystal display panel, an organic light emitting diode display (OLED) panel, and the like.

평판 디스플레이 패널은 일반적으로 상부 기판과 하부 기판을 포함한다.A flat panel display panel generally includes an upper substrate and a lower substrate.

한편, 평판 디스플레이 패널의 측면에는 측면 실링재가 배치되어 있다. 측면 실링재는 외부 충격으로부터 디스플레이 패널에 포함되는 각각의 요소들을 보호하는 역할, 디스플레이 패널 내부로 수분이 침투하는 것을 방지하는 역할, 디스플레이 패널 측면으로의 빛 손실 방지 역할 등을 할 수 있어야 한다. On the other hand, a side sealing material is disposed on the side of the flat panel display panel. The side sealing material should be able to play a role of protecting each element included in the display panel from external impact, preventing moisture from entering the display panel, and preventing light loss to the side of the display panel.

또한, 평판 디스플레이 패널의 상부 기판 및 하부 기판은 일반적으로 내부 실링재를 통하여 합착된다. 내부 실링재는 상부 기판 및 하부 기판을 견고히 접착시키고, 상부 기판과 하부 기판 사이의 갭이 요구되는 경우에 이 갭을 유지할 수 있어야 한다. Further, the upper substrate and the lower substrate of the flat panel display panel are generally bonded through an inner sealing material. The inner sealing material should be able to firmly bond the upper substrate and the lower substrate, and be able to maintain this gap when a gap between the upper substrate and the lower substrate is required.

전술한 바와 같이, 측면 실링재와 내부 실링재는 목적하는 기능이 서로 상이하므로, 이들을 구성하는 재료 역시 일반적으로 상이하다. 내부 실링재와 측면 실링재가 서로 다른 재료로 구성되는 경우, 내부 실링재를 배치하는 공정과 실링 부재를 배치하는 공정이 별도로 요구된다. As described above, since the desired functions of the side sealing material and the inner sealing material are different from each other, the materials constituting them are also generally different. When the inner sealing material and the side sealing material are made of different materials, the process of disposing the inner sealing material and the process of disposing the sealing member are separately required.

본 발명의 목적은 내부 실링재 및 측면 실링재 어느 쪽으로도 사용 가능하며, 특히 평판 디스플레이 패널의 상부 기판 및 하부 기판의 접착과 평판 디스플레이 패널의 측면 실링이 동시에 가능한 신규한 실링 부재를 제공하는 것이다. An object of the present invention is to provide a new sealing member that can be used for both the inner sealing material and the side sealing material, and in particular, it is possible to simultaneously bond the upper substrate and the lower substrate of the flat panel display panel and the side sealing of the flat panel display panel.

또한, 본 발명의 목적은 상기 실링 부재를 포함하는 평판 디스플레이 패널, 특히 편광판을 포함하는 평판 디스플레이 패널을 제공하는 것이다.It is also an object of the present invention to provide a flat panel display panel comprising the sealing member, in particular a flat panel display panel including a polarizing plate.

본 발명의 목적들은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 본 발명의 다른 목적 및 장점들은 하기의 설명에 의해서 이해될 수 있고, 본 발명의 실시예에 의해 보다 분명하게 이해될 것이다. 또한, 본 발명의 목적 및 장점들은 특허 청구 범위에 나타낸 수단 및 그 조합에 의해 실현될 수 있음을 쉽게 알 수 있을 것이다.The objects of the present invention are not limited to the objects mentioned above, and other objects and advantages of the present invention not mentioned can be understood by the following description, and will be more clearly understood by the embodiments of the present invention. In addition, it will be readily appreciated that the objects and advantages of the present invention can be realized by means of the appended claims and combinations thereof.

상기 목적을 달성하기 위한 본 발명에 따른 평판 디스플레이 패널용 실링 부재는 우레탄 아크릴레이트 올리고머 60~70중량%, 아크릴레이트 모노머 10~30중량%, 안료 1~5중량%, 광 개시제 1~5중량% 및 가교제 1~5중량%를 포함한다. The sealing member for a flat panel display panel according to the present invention for achieving the above object is urethane acrylate oligomer 60 to 70 wt%, acrylate monomer 10 to 30 wt%, pigment 1 to 5 wt%, photoinitiator 1 to 5 wt% And 1 to 5% by weight of a crosslinking agent.

상기 구성을 갖는 본 발명에 따른 실링 부재는 상부 기판 및 하부 기판을 합착하기 위한 내부 실링재에 요구되는 우수한 접착력을 가지며, 아울러 평판 디스플레이 패널의 측면을 실링하기 위한 측면 실링재에 요구되는 우수한 수분 침투 방지 특성을 나타낼 수 있다. 추가로 본 발명에 따른 실링 부재는 우레탄 아크릴 올리고머를 주 성분으로 포함함에 따라 우수한 탄성을 가질 수 있다. The sealing member according to the present invention having the above configuration has excellent adhesive strength required for the inner sealing material for bonding the upper substrate and the lower substrate, and also excellent moisture penetration prevention properties required for the side sealing material for sealing the side surface of the flat panel display panel. Can represent In addition, the sealing member according to the present invention may have excellent elasticity by including a urethane acrylic oligomer as a main component.

바람직하게는 상기 실링 부재는 PMMA(polymethylmetacrylate) 입자, 폴리우레탄 입자 및 실리콘 입자 등과 같은 강성 보강 입자 1~35중량%를 추가로 포함할 수 있다. 이와 같은 강성 보강 입자가 추가로 포함됨에 따라, 실링 부재가 평판 디스플레이 패널의 편광판과 접촉할 때, 편광판의 수축 제어 효과가 향상될 수 있다. Preferably, the sealing member may further include 1 to 35% by weight of rigid reinforcement particles such as PMMA (polymethylmetacrylate) particles, polyurethane particles and silicon particles. As such rigid reinforcing particles are additionally included, when the sealing member contacts the polarizing plate of the flat panel display panel, the shrinkage control effect of the polarizing plate may be improved.

한편, 상기 안료는 블랙 안료와 같은 광흡수성 안료일 수 있다. 이를 통하여 실링 부재는 디스플레이 패널 측면으로의 빛 손실 방지 역할을 할 수 있다. Meanwhile, the pigment may be a light absorbing pigment such as a black pigment. Through this, the sealing member may serve to prevent light loss to the side of the display panel.

상기 목적을 달성하기 위한 본 발명에 따른 평판 디스플레이 패널은 박막 트랜지스터가 배치된 하부 기판, 하부 기판의 가장자리를 따라 배치된 실링 부재, 및 상기 실링 부재를 통하여 상기 하부 기판과 합착되며, 상부면에 편광판이 배치된 상부 기판;을 포함한다. 이때, 상기 실링 부재는 상기 상부 기판의 측면을 커버하면서 상기 편광판의 측면과 접촉되도록 연장되어 있다. 또한, 상기 실링 부재는 전술한 바와 같이 우레탄 아크릴레이트 올리고머 60~70중량%, 아크릴레이트 모노머 10~30중량%, 안료 1~5중량%, 광 개시제 1~5중량% 및 가교제 1~5중량%를 포함할 수 있으며, 추가로 강성 보강 입자 1~35중량%를 포함할 수 있다. The flat panel display panel according to the present invention for achieving the above object is bonded to the lower substrate through the lower substrate on which the thin film transistor is disposed, the sealing member disposed along the edge of the lower substrate, and the sealing member, and a polarizing plate on the upper surface It includes; the upper substrate is disposed. At this time, the sealing member is extended to cover the side surface of the upper substrate and contact the side surface of the polarizing plate. In addition, the sealing member is 60 to 70% by weight of urethane acrylate oligomer, 10 to 30% by weight of acrylate monomer, 1 to 5% by weight of pigment, 1 to 5% by weight of photoinitiator, and 1 to 5% by weight of crosslinking agent as described above It may include, it may further include a rigid reinforcement particles 1 to 35% by weight.

본 발명에 따른 평판 디스플레이 패널은 실링 부재와 편광판이 접촉되어 있다. 본 발명에 따른 실링 부재가 우수한 탄성을 가짐에 따라 다음과 같은 효과를 발휘할 수 있다. In the flat panel display panel according to the present invention, the sealing member and the polarizing plate are in contact. As the sealing member according to the present invention has excellent elasticity, the following effects can be exhibited.

편광판은 고온 다습한 환경에서 수축하는 특성이 있다. 이때, 편광판이 수축함에 따라 편광판과 실링 부재 간에 파단이 발생하면, 해당 영역에서 빛 누출의 문제점이 발생할 수 있다. 그러나, 편광판이 수축함에 따라 실링 부재도 연신이 일어난다면 편광판과 실링 부재 간의 파단이 발행하지 않는다면 빛 누출의 문제점이 발생하지 않는다. 편광판의 재질이나 구조 변경을 통하여 고온 다습한 환경에서 수축이 발생하지 않도록 하는 것이 고려될 수 있다. 그러나, 편광판의 광학 특성을 유지하면서 고온 다습한 환경에서 수축이 발생하지 않도록 하는 재료나 구조를 달성하기는 매우 어렵다. The polarizing plate has a characteristic of shrinking in a high temperature and high humidity environment. At this time, if a fracture occurs between the polarizing plate and the sealing member as the polarizing plate shrinks, a problem of light leakage may occur in the corresponding region. However, if stretching occurs in the sealing member as the polarizing plate shrinks, there is no problem of light leakage unless breakage between the polarizing plate and the sealing member occurs. It may be considered that shrinkage does not occur in a high temperature and high humidity environment by changing the material or structure of the polarizing plate. However, it is very difficult to achieve a material or structure that prevents shrinkage in a high temperature and high humidity environment while maintaining the optical properties of the polarizing plate.

이에 본 발명에서는 실링 부재가 탄성을 가질 경우 편광판 수축시 실링 부재의 연신이 함께 일어날 수 있다는 전혀 다른 관점에서 접근하여, 상기와 같은 편광판 수축시 실링 부재가 편광판의 수축 방향으로 연신되어 편광판과 실링 부재의 접촉이 계속 유지되도록 함으로써 빛 누출을 억제할 수 있었다. Accordingly, in the present invention, when the sealing member has elasticity, the sealing member may be stretched when the polarizing plate contracts, and the sealing member is stretched in the contracting direction of the polarizing plate when the polarizing plate is contracted. Light leakage could be suppressed by maintaining the contact of.

본 발명에 따른 실링 부재는 우수한 접착력, 우수한 수분 침투 방지 특성을 통하여 상부 기판과 하부 기판의 합착을 위한 내부 실링재 및 평판 디스플레이 패널의 측면 실링을 이한 측면 실링재 역할을 모두 할 수 있으며, 내부 실링재와 측면 실링재를 하나의 재료로 통합할 수 있다. The sealing member according to the present invention can serve as both an inner sealing material for bonding the upper substrate and the lower substrate and a side sealing material with side sealing of the flat panel display panel through excellent adhesion and excellent moisture intrusion prevention properties. The sealing material can be integrated into one material.

나아가, 본 발명에 따른 실링 부재는 우레탄 아크릴레이트 올리고머를 주성분으로 함에 따라 에폭시 등에 비하여 우수한 탄성을 가질 수 있다. 이에 따라 편광판 수축시 연신이 가능하여, 편광판 수축 시에 실링 부재와의 파단에 기인하는 빛 누출을 억제할 수 있다. Furthermore, the sealing member according to the present invention may have excellent elasticity compared to epoxy or the like as the urethane acrylate oligomer is a main component. Accordingly, stretching is possible when the polarizing plate is contracted, and light leakage due to breakage with the sealing member can be suppressed when the polarizing plate is contracted.

상술한 효과와 더불어 본 발명의 구체적인 효과는 이하 발명을 실시하기 위한 구체적인 사항을 설명하면서 함께 기술한다.In addition to the above-described effects, the concrete effects of the present invention will be described together while describing the specific matters for carrying out the invention.

도 1은 본 발명의 실시예에 따른 실링 부재를 포함하는 평판 디스플레이 패널을 개략적으로 나타낸 것이다.
도 2는 도 1의 I-II 단면도를 나타낸 것이다.
도 3은 실링 부재가 탄성을 갖지 않을 경우, 편광판 수축 시에 파단이 발생한 예를 나타낸 것이다.
도 4는 실링 부재가 탄성을 가질 경우, 편광판 수축 시에 파단이 발생하지 않는 예를 나타낸 것이다.
도 5a는 본 발명의 다른 실시예에 따른 실링 부재를 포함하는 평판 디스플레이 패널을 개략적으로 나타낸 것이다.
도 5b는 본 발명의 또 다른 실시예에 따른 실링 부재를 포함하는 평판 디스플레이 패널을 개략적으로 나타낸 것이다.
도 6은 본 발명의 실시예에 따른 실링 부재를 포함하는 액정 디스플레이 패널의 예를 개략적으로 나타내는 단면도이다.
도 7은 본 발명의 다른 실시예에 따른 실링 부재를 포함하는 액정 디스플레이 패널의 예를 개략적으로 나타내는 단면도이다.
도 8은 본 발명의 또 다른 실시예에 따른 실링 부재를 포함하는 액정 디스플레이 패널의 예를 개략적으로 나타내는 단면도이다.
1 schematically shows a flat panel display panel including a sealing member according to an embodiment of the present invention.
FIG. 2 is a sectional view taken along line I-II in FIG. 1.
3 shows an example in which fracture occurs when the polarizing plate contracts when the sealing member does not have elasticity.
4 shows an example in which fracture does not occur when the polarizing plate contracts when the sealing member has elasticity.
5A schematically illustrates a flat panel display panel including a sealing member according to another embodiment of the present invention.
5B schematically illustrates a flat panel display panel including a sealing member according to another embodiment of the present invention.
6 is a cross-sectional view schematically showing an example of a liquid crystal display panel including a sealing member according to an embodiment of the present invention.
7 is a cross-sectional view schematically showing an example of a liquid crystal display panel including a sealing member according to another embodiment of the present invention.
8 is a cross-sectional view schematically showing an example of a liquid crystal display panel including a sealing member according to another embodiment of the present invention.

전술한 목적, 특징 및 장점은 첨부된 도면을 참조하여 상세하게 후술되며, 이에 따라 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 본 발명의 기술적 사상을 용이하게 실시할 수 있을 것이다. 본 발명을 설명함에 있어서 본 발명과 관련된 공지 기술에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 상세한 설명을 생략한다. 이하, 첨부된 도면을 참조하여 본 발명에 따른 바람직한 실시예를 상세히 설명하기로 한다. 도면에서 동일한 참조부호는 동일 또는 유사한 구성요소를 가리키는 것으로 사용된다.The above-described objects, features, and advantages will be described in detail below with reference to the accompanying drawings, and accordingly, a person skilled in the art to which the present invention pertains can easily implement the technical spirit of the present invention. In describing the present invention, when it is determined that the detailed description of the known technology related to the present invention may unnecessarily obscure the subject matter of the present invention, the detailed description will be omitted. Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the drawings, the same reference numerals are used to indicate the same or similar components.

이하에서 구성요소의 "상부 (또는 하부)" 또는 구성요소의 "상 (또는 하)"에 임의의 구성이 배치된다는 것은, 임의의 구성이 상기 구성요소의 상면 (또는 하면)에 접하여 배치되는 것뿐만 아니라, 상기 구성요소와 상기 구성요소 상에 (또는 하에) 배치된 임의의 구성 사이에 다른 구성이 개재될 수 있음을 의미할 수 있다. In the following, the arrangement of any component in the "upper (or lower)" or "upper (or lower)" of the component means that any component is disposed in contact with the upper surface (or lower surface) of the component. In addition, it may mean that other components may be interposed between the component and any component disposed on (or under) the component.

또한 어떤 구성요소가 다른 구성요소에 "연결", "결합" 또는 "접속"된다고 기재된 경우, 상기 구성요소들은 서로 직접적으로 연결되거나 또는 접속될 수 있지만, 각 구성요소 사이에 다른 구성요소가 "개재"되거나, 각 구성요소가 다른 구성요소를 통해 "연결", "결합" 또는 "접속"될 수도 있는 것으로 이해되어야 할 것이다. Also, when a component is described as being "connected", "coupled" or "connected" to another component, the components may be directly connected to or connected to each other, but other components may be "interposed" between each component. It should be understood that "or, each component may be" connected "," coupled "or" connected "through other components.

이하에서는, 본 발명의 몇몇 실시예에 따른 실링 부재 및 이를 포함하는 평판 디스플레이 패널을 설명하도록 한다.Hereinafter, a sealing member and a flat panel display panel including the same according to some embodiments of the present invention will be described.

도 1은 본 발명의 실시예에 따른 실링 부재를 포함하는 평판 디스플레이 패널을 개략적으로 나타낸 것이다. 설명을 위해 도 1에서는 평판 디스플레이 패널의 좌측 및 우측에 실링 부재가 배치된 것을 나타내었으나, 전면 및 후면에도 실링 부재가 배치될 수 있다. 또한, 도 2는 도 1의 I-II 단면도를 나타낸 것이다.1 schematically shows a flat panel display panel including a sealing member according to an embodiment of the present invention. For illustration, although the sealing members are disposed on the left and right sides of the flat panel display panel, the sealing members may be disposed on the front and rear surfaces. 2 is a sectional view taken along line I-II in FIG. 1.

도 1 및 도 2를 참조하면, 본 발명에 따른 평판 디스플레이 패널은 하부 기판(110), 상부 기판(120) 및 실링 부재(140)를 포함한다. 1 and 2, the flat panel display panel according to the present invention includes a lower substrate 110, an upper substrate 120 and a sealing member 140.

하부 기판(110)의 상부면에는 박막 트랜지스터가 배치되어 있다. 하부 기판(110)의 하부면에는 편광판(115)이 배치될 수 있다. 상부 기판(120)의 상부면에는 편광판(125)이 배치되어 있다. A thin film transistor is disposed on the upper surface of the lower substrate 110. A polarizing plate 115 may be disposed on a lower surface of the lower substrate 110. The polarizing plate 125 is disposed on the upper surface of the upper substrate 120.

액정 디스플레이 패널의 예를 들면, 하부 기판(110)은 박막 트랜지스터 기판이고, 상부 기판(120)은 컬러필터 기판이다. 평판 디스플레이 패널이 액정 디스플레이 패널일 때, 실링 부재(140), 하부 기판(110) 및 상부 기판(120)에 의해 정의되는 공간은 액정층(130)이 되고, 이 액정층(130)에는 액정(135)이 배치된다. 하부 기판(110)의 하부면에 배치된 편광판(115)은 백라이트 유닛(미도시)을 통하여 공급되는 광을 편광시키고, 상부 기판(120)의 상부면에 배치된 편광판(125)은 하부 기판(110), 액정층(130) 및 상부 기판(120)을 통과하는 광을 편광시키는 기능을 한다. For example, a liquid crystal display panel, the lower substrate 110 is a thin film transistor substrate, and the upper substrate 120 is a color filter substrate. When the flat panel display panel is a liquid crystal display panel, the space defined by the sealing member 140, the lower substrate 110, and the upper substrate 120 becomes the liquid crystal layer 130, and the liquid crystal layer 130 includes liquid crystal ( 135). The polarizing plate 115 disposed on the lower surface of the lower substrate 110 polarizes light supplied through a backlight unit (not shown), and the polarizing plate 125 disposed on the upper surface of the upper substrate 120 has a lower substrate ( 110), and functions to polarize light passing through the liquid crystal layer 130 and the upper substrate 120.

실링 부재(140)는 내측부(140a) 및 외측부(140b)를 포함한다. 내측부(140a)는 하부 기판(110)의 상부면의 가장자리를 따라 배치되며, 하부 기판(110)과 상부 기판(120)을 합착하는 역할 및 하부 기판(110)과 상부 기판(120) 간의 갭을 유지하는 역할을 한다. 외측부(140b)는 내측부(140a)로부터 연장된 부분이다. 외측부(140b)는 상부 기판(120)의 측면을 커버하면서 편광판(125)의 측면과 접촉되도록 내측부(140a)로부터 연장되어 있다. 또한, 외측부(140b)는 하부 기판(110)의 측면을 커버하면서 편광판(115)의 측면과 접촉되도록 내측부(140a)로부터 추가 연장되어 있을 수 있다. The sealing member 140 includes an inner portion 140a and an outer portion 140b. The inner portion 140a is disposed along the edge of the upper surface of the lower substrate 110, serves to bond the lower substrate 110 and the upper substrate 120, and fills the gap between the lower substrate 110 and the upper substrate 120. It serves to maintain. The outer portion 140b is a portion extending from the inner portion 140a. The outer portion 140b extends from the inner portion 140a to cover the side surface of the upper substrate 120 and contact the side surface of the polarizing plate 125. In addition, the outer portion 140b may further extend from the inner portion 140a so as to cover the side surface of the lower substrate 110 and contact the side surface of the polarizing plate 115.

이때, 본 발명에 따른 실링 부재는 우레탄 아크릴레이트 올리고머 60~70중량%(wt%), 아크릴레이트 모노머 10~30중량%, 안료 1~5중량%, 광 개시제 1~5중량% 및 가교제 1~5중량%를 포함한다. 본 발명에 따른 실링 부재는 강성 보강 입자 1~35중량%를 추가로 포함하는 것이 보다 바람직하다. At this time, the sealing member according to the present invention is urethane acrylate oligomer 60 ~ 70% by weight (wt%), acrylate monomer 10 ~ 30% by weight, pigment 1 ~ 5% by weight, photoinitiator 1 ~ 5% by weight and crosslinking agent 1 ~ 5% by weight. It is more preferable that the sealing member according to the present invention further comprises 1 to 35% by weight of the rigid reinforcing particles.

이하, 본 발에 따른 실링 부재에 포함되는 각 성분 및 그 함량에 대하여 설명하기로 한다. Hereinafter, each component included in the sealing member according to the present invention and its content will be described.

우레탄 아크릴레이트 올리고머는 실링 부재의 주성분으로서, 접착력과 함께 탄성을 제공하는 역할을 한다. 우레탄 아크릴레이트 올리고머는 공지된 다양한 구조의 것들을 제한없이 이용할 수 있다. 상기 우레탄 아크릴레이트 올리고머는 실링 부재 전체 중량의 60~70중량%로 포함되는 것이 바람직하다. 우레탄 아크릴레이트 올리고머의 함량이 60중량% 이상일 때, 실링 부재에 충분한 탄성을 부여될 수 있다. 다만, 본 발명에 따른 실링 부재가 조성물 도포, 건조 및 UV 경화에 의해 형성되는 것을 고려하면, 우레탄 아크릴레이트 올리고머의 함량이 70중량%를 초과하면 조성물의 점도가 지나치게 높아져 도포 자체가 어려워질 수 있다. The urethane acrylate oligomer is a main component of the sealing member, and serves to provide elasticity together with adhesion. The urethane acrylate oligomer can use various known structures without limitation. The urethane acrylate oligomer is preferably included in 60 to 70% by weight of the total weight of the sealing member. When the content of the urethane acrylate oligomer is 60% by weight or more, sufficient elasticity can be imparted to the sealing member. However, considering that the sealing member according to the present invention is formed by coating, drying, and UV curing the composition, when the content of the urethane acrylate oligomer exceeds 70% by weight, the viscosity of the composition may be excessively high and coating itself may be difficult. .

아크릴레이트 모노머는 우레탄 아크릴레이트 올리고머와 반응하여 실링 부재를 형성한다. 아크릴레이트 모노머로는 2-에틸헥실 아크릴레이트(2-EHA), 옥타데실 아크릴레이트, 이소데실 아크릴레이트, 스테아릴 아크릴레이트, 트리데실 메타크릴레이트, 이소보닐 아크릴레이트, 에틸렌글리콜 디메타크릴레이트 등 공지된 것들이 이용될 수 있다. 상기 아크릴레이트 모노머의 함량은 실링 부재 전체 중량의 10~30중량%로 포함되는 것이 바람직하다. 아크릴레이트 모노머의 함량이 10중량% 이상일 때 안정적으로 실링 부재가 형성될 수 있다. 다만, 아크릴레이트 모노머의 함량이 30중량%를 초과하는 경우, 본 발명에서 목표하는 실링 부재의 탄성 확보가 어려워질 수 있다. The acrylate monomer reacts with the urethane acrylate oligomer to form a sealing member. As the acrylate monomer, 2-ethylhexyl acrylate (2-EHA), octadecyl acrylate, isodecyl acrylate, stearyl acrylate, tridecyl methacrylate, isobornyl acrylate, ethylene glycol dimethacrylate, etc. Known ones can be used. The content of the acrylate monomer is preferably included in 10 to 30% by weight of the total weight of the sealing member. When the content of the acrylate monomer is 10% by weight or more, a sealing member can be stably formed. However, when the content of the acrylate monomer exceeds 30% by weight, it may be difficult to secure elasticity of the sealing member targeted in the present invention.

안료는 실링 부재의 색상을 결정하는 역할을 한다. 본 발명에서 실링 부재는 빛 누출을 방지하는 역할을 하는 점에서 블랙 안료와 같은 광 흡수성 안료를 사용하는 것이 바람직하다. 광 흡수성 안료의 예로는 산화철, 카본블랙, 티탄 블랙 등을 제시할 수 있다. 안료의 함량은 실링 부재 전체 중량의 1~5중량%인 것이 바람직하다. 안료 함량이 1중량% 미만일 경우 원하는 색상의 실링 부재의 달성이 어려울 수 있고, 안료의 함량이 5중량%를 초과하더라도 안료 첨가 효과가 더 이상 증대되지 않을 수 있다. The pigment serves to determine the color of the sealing member. In the present invention, since the sealing member serves to prevent light leakage, it is preferable to use a light absorbing pigment such as a black pigment. Examples of the light absorbing pigment may include iron oxide, carbon black, and titanium black. The content of the pigment is preferably 1 to 5% by weight of the total weight of the sealing member. When the pigment content is less than 1% by weight, it may be difficult to achieve a sealing member of a desired color, and even if the pigment content exceeds 5% by weight, the effect of adding the pigment may not be increased any more.

광 개시제는 자외선에 의해 활성을 나타내어 광 중합 반응이 개시되도록 한다. 광 개시제로는 벤조페논, 아세토페논, 안트라퀴논 등 공지된 광 개시제가 이용될 수 있다. 광 개시제는 실링 부재 전체 중량의 1~5중량%로 첨가될 수 있다. 광 개시제의 함량이 1중량% 이상일 때 단시간에 UV 중합 반응이 이루어질 수 있다. 다만, 광 개시제의 함량이 5중량%를 초과하여 지나치게 높을 경우 최종 실링 부재에 다량의 미반응 광 개시제가 불순물로 존재할 수 있다. The photoinitiator exhibits activity by ultraviolet light so that a photopolymerization reaction is initiated. As the photoinitiator, known photoinitiators such as benzophenone, acetophenone, and anthraquinone can be used. The photoinitiator may be added at 1 to 5% by weight of the total weight of the sealing member. When the content of the photoinitiator is 1% by weight or more, a UV polymerization reaction can be achieved in a short time. However, when the content of the photoinitiator exceeds 5 wt% and is too high, a large amount of unreacted photoinitiator may be present as impurities in the final sealing member.

가교제는 우레탄 아크릴레이트 올리고머와 아크릴레이트 모노머 간의 가교 반응이 이루어질 수 있도록 한다. 가교제는 공지된 멜라민, 퍼옥사이드, 이소시아네이트 등이 제한없이 이용될 수 있다. 상기 가교제는 실링 부재 전체 중량에 대하여 1~5중량%로 첨가될 수 있다. 가교제의 함량이 1중량% 미만에서는 우레탄 아크릴레이트 올리고머와 아크릴레이트 모노머 간의 가교 반응이 불충분할 수 있다. 반면, 가교제 함량이 5중량%를 초과하여 지나치게 높을 경우 다량의 미반응 가교제가 불순물로 존재할 수 있다. The crosslinking agent enables a crosslinking reaction between the urethane acrylate oligomer and the acrylate monomer. Known melamine, peroxide, isocyanate and the like can be used without limitation. The crosslinking agent may be added in 1 to 5% by weight relative to the total weight of the sealing member. When the content of the crosslinking agent is less than 1% by weight, the crosslinking reaction between the urethane acrylate oligomer and the acrylate monomer may be insufficient. On the other hand, when the content of the crosslinking agent exceeds 5 wt% and is too high, a large amount of unreacted crosslinking agent may exist as impurities.

또한, 필요에 따라서는 레벨링제, 소포제 등이 각각 약 0.1~3중량% 정도로 소량 포함될 수 있다. In addition, if necessary, a leveling agent, an antifoaming agent, etc. may be included in a small amount of about 0.1 to 3% by weight, respectively.

한편, 본 발명에 따른 실링 부재에는 강성 보강 입자가 추가로 포함될 수 있다. 이 강성 보강 입자는 실링 부재의 강성을 보강함으로써 실링 부재와 접촉된 편광판의 수축을 억제하는 역할을 한다. 이에 의하면, 편광판 수축 시에 실링 부재가 편광판 수축 방향으로 연신이 되면서도 보강된 강성을 통하여 편광판 수축에 대한 저항성을 높임으로써 편광판의 수축을 억제한다. 이러한 강성 보강 입자는 PMMA(polymethylmetacrylate) 입자, 폴리우레탄 입자 및 실리콘 입자 등이 1종 이상 포함될 수 있다. 강성 보강 입자는 분말의 형태가 될 수 있다. 다른 예로, 강성 보강 입자는 이들 PMMA 입자들이 고분자에 수용된 캡슐 형태가 될 수 있다. 상기 강성 보강 입자는 실링 부재 전체 중량의 1~35중량%로 포함되는 것이 바람직하다. 강성 보강 입자의 함량이 1 중량% 미만일 경우 강성 보강 효과가 크지 않다. 반면, 강성 보강 입자의 함량이 35중량%를 초과하는 경우, 상대적으로 우레탄 아크릴레이트 올리고머나 아크릴레이트 모노머의 함량이 감소하므로 접착력이 저하될 수 있다. On the other hand, the sealing member according to the present invention may further include rigid reinforcement particles. The stiffness-reinforcing particles serve to suppress the shrinkage of the polarizing plate in contact with the sealing member by reinforcing the rigidity of the sealing member. According to this, the shrinking of the polarizing plate is suppressed by increasing the resistance to the shrinking of the polarizing plate through the reinforced rigidity while the sealing member is stretched in the shrinking direction of the polarizing plate during the shrinking of the polarizing plate. The stiffness-reinforcing particles may include one or more of PMMA (polymethylmetacrylate) particles, polyurethane particles and silicon particles. The rigid reinforcing particles can be in the form of powder. As another example, the rigid reinforcing particles may be in the form of capsules in which these PMMA particles are accommodated in a polymer. The rigid reinforcement particles are preferably included in 1 to 35% by weight of the total weight of the sealing member. When the content of the stiffening reinforcing particles is less than 1% by weight, the stiffening reinforcing effect is not large. On the other hand, when the content of the stiffening reinforcing particles exceeds 35% by weight, the content of the urethane acrylate oligomer or acrylate monomer is relatively reduced, so the adhesion may be lowered.

도 3은 실링 부재가 탄성을 갖지 않을 경우, 편광판 수축 시에 파단이 발생한 예를 나타낸 것이다. 도 4는 실링 부재가 탄성을 가질 경우, 편광판 수축 시에 파단이 발생하지 않는 예를 나타낸 것이다. 3 shows an example in which fracture occurs when the polarizing plate contracts when the sealing member does not have elasticity. 4 shows an example in which fracture does not occur when the polarizing plate contracts when the sealing member has elasticity.

실링 부재가 예를 들어 에폭시 올리고머를 주성분으로 하는 조성으로 되어 있는 경우, 실링 부재는 탄성이 작은 단단한 특성을 갖는다. 이 경우, 고온 다습한 환경에서 편광판(125)이 수축할 때 실링 부재(140)가 연신되지 못하여 도 3에 도시된 바와 같이 편광판(125)과 실링 부재(140) 간의 파단이 발생한다. 파단에 의해 갭 부분(A)이 발생되었을 때, 이 갭 부분(A)으로 입사되는 빛은 편광판을 통과하지 않고 그대로 외부로 방출되어, 빛 누출 문제가 발생될 수 있다. When the sealing member has, for example, a composition containing an epoxy oligomer as a main component, the sealing member has rigidity with low elasticity. In this case, when the polarizing plate 125 contracts in a high-temperature and high-humidity environment, the sealing member 140 cannot be stretched, and thus a fracture between the polarizing plate 125 and the sealing member 140 occurs. When the gap portion A is generated by the rupture, light incident to the gap portion A is emitted to the outside without passing through the polarizing plate, and a light leakage problem may occur.

그러나, 실링 부재가 예를 들어 우레탄 아크릴레이트 올리고머를 주성분으로 하는 것과 같이 탄성이 우수한 특성을 갖는 경우, 도 4에 도시된 바와 같이 편광판(125)이 수축할 때 실링 부재(140) 역시 편광판 수축 방향으로 연신하게 되고, 이에 따라 편광판(125)과 실링 부재(140) 간의 접촉이 계속 유지될 수 있다. 이 경우, 입사되는 빛이 실링 부재의 연신된 부분(B)에 의해 흡수될 수 있으므로, 빛 누출 문제가 발생하지 않는다. However, when the sealing member has excellent elasticity, for example, as a main component of a urethane acrylate oligomer, when the polarizing plate 125 contracts, as shown in FIG. 4, the sealing member 140 also contracts the polarizing plate direction As a result, the contact between the polarizing plate 125 and the sealing member 140 may be maintained. In this case, since the incident light can be absorbed by the elongated portion B of the sealing member, no light leakage problem occurs.

도 5a는 본 발명의 다른 실시예에 따른 실링 부재를 포함하는 평판 디스플레이 패널을 개략적으로 나타낸 것이다. 5A schematically illustrates a flat panel display panel including a sealing member according to another embodiment of the present invention.

도 5a를 참조하면, 실링 부재의 외측부(140b)는 편광판(125)의 측면 뿐만 아니라 편광판(125)의 상부면과도 접촉할 수 있다. 이 경우 편광판과 실링 부재 간의 접촉 면적이 더 증가하므로 편광판과 실링 부재 간의 파단 현상을 보다 효과적으로 억제할 수 있다. 물론, 도 5a에 도시된 예와 같이, 실링 부재의 외측부(140b)는 편광판(115)의 측면뿐만 아니라 편광판(115)의 하부면과도 접촉할 수 있다.Referring to FIG. 5A, the outer portion 140b of the sealing member may contact not only the side surface of the polarizing plate 125 but also the upper surface of the polarizing plate 125. In this case, since the contact area between the polarizing plate and the sealing member is further increased, the rupture phenomenon between the polarizing plate and the sealing member can be more effectively suppressed. Of course, as shown in the example shown in FIG. 5A, the outer portion 140b of the sealing member may contact not only the side surface of the polarizing plate 115 but also the lower surface of the polarizing plate 115.

도 5b는 본 발명의 또 다른 실시예에 따른 실링 부재를 포함하는 평판 디스플레이 패널을 개략적으로 나타낸 것이다.5B schematically illustrates a flat panel display panel including a sealing member according to another embodiment of the present invention.

도 2 및 도 4에 도시된 예들의 경우, 실링 부재의 외측부(140b)가 하부 기판(110)의 측면을 덮는 형태이나, 도 5b에 도시된 예는, 실링 부재의 외측부(140b)가 상부 기판(120)의 측면만 덮는 형태이다. 도 2 및 도 4에 도시된 예들의 경우, 평면에서 볼 때 하부 기판(110) 및 상부 기판(120)의 가장자리가 서로 중첩되는 경우에 주로 적용될 수 있다. 도 5b에 도시된 예의 경우, 평면에서 볼 때 하부 기판(110)의 가장자리가 상부 기판(120)의 가장자리보다 외측으로 더 돌출되어 있는 경우에 주로 적용될 수 있다. 2 and 4, the outer portion 140b of the sealing member covers the side surface of the lower substrate 110. In the example illustrated in FIG. 5B, the outer portion 140b of the sealing member is the upper substrate. It is a form that covers only the side of (120). 2 and 4, the edges of the lower substrate 110 and the upper substrate 120 when viewed in a plan view may be mainly applied. In the case of the example shown in FIG. 5B, it can be mainly applied when the edge of the lower substrate 110 is more protruding outward than the edge of the upper substrate 120 when viewed in plan.

한편, 도 5b에는 평판 디스플레이 패널을 외부와 전기적으로 연결하기 위한 회로 기판(160)이 하부 기판의 일 가장자리에 배치되어 있고, 실링 부재(140)의 외측부(140b)가 회로 기판(160)의 일부분을 덮는 형태가 제시되어 있다. 실링 부재(140)는 상부 기판(120)의 측면과, 액정층(130)의 측면을 커버하면서 또한 하부 기판(110)과 중첩되는 회로 기판(160)의 일부분도 함께 커버한다. 하부 기판(110)과 중첩되는 회로 기판(160)의 일부분은 하부 기판(120)에 접착제 등에 의해 접착되어 회로 기판(160)이 하부 기판(120)에 고정될 수 있다 .추가로 실링 부재(130)가 회로 기판(160)의 일부분 및 하부 기판(120)의 가장자리를 모두 커버하면서 회로 기판(160)의 일부분이 실링 부재(140)에 추가로 고정될 수 있다.Meanwhile, in FIG. 5B, a circuit board 160 for electrically connecting a flat panel display panel to the outside is disposed at one edge of the lower substrate, and the outer portion 140b of the sealing member 140 is a part of the circuit board 160 The form of covering is presented. The sealing member 140 covers the side surface of the upper substrate 120 and the side surface of the liquid crystal layer 130 and also covers a part of the circuit board 160 overlapping the lower substrate 110. A portion of the circuit board 160 overlapping the lower substrate 110 may be adhered to the lower substrate 120 by an adhesive or the like, so that the circuit board 160 may be fixed to the lower substrate 120. In addition, the sealing member 130 ) Covers a portion of the circuit board 160 and an edge of the lower substrate 120, and a portion of the circuit board 160 may be further fixed to the sealing member 140.

도 6 내지 도 8은 본 발명의 실시예에 따른 실링 부재를 포함하는 액정 디스플레이 패널의 예들을 개략적으로 나타내는 단면도들이다. 도 6에 도시된 예는 실링 부재의 외측부가 상부 패널 및 하부 패널의 측면을 커버하는 구조이다. 도 7에 도시된 예는 실링 부재의 외측부가 상부 패널의 측면을 커버하는 구조이다. 도 8에 도시된 예는 실링 부재의 구조는 도 7에 도시된 예와 유사하되, 하부 기판의 일 가장자리에 회로 기판(160)이 배치되어 있다. 6 to 8 are cross-sectional views schematically showing examples of a liquid crystal display panel including a sealing member according to an embodiment of the present invention. The example shown in FIG. 6 is a structure in which the outer portion of the sealing member covers the side surfaces of the upper panel and the lower panel. The example shown in FIG. 7 is a structure in which the outer portion of the sealing member covers the side surface of the upper panel. In the example shown in FIG. 8, the structure of the sealing member is similar to the example shown in FIG. 7, but the circuit board 160 is disposed on one edge of the lower substrate.

도 6 내지 도 8의 액정 디스플레이 패널에 대하여 설명하면 다음과 같다. The liquid crystal display panel of FIGS. 6 to 8 will be described below.

본 발명에 따른 액정 디스플레이 패널은 하부 기판(110), 상부 기판(120), 액정층(130) 및 실링 부재(140)를 포함한다. 하부 기판(110)은 박막 트랜지스터 기판으로도 지칭되고, 상부 기판(120)은 컬러필터 기판으로도 지칭된다.The liquid crystal display panel according to the present invention includes a lower substrate 110, an upper substrate 120, a liquid crystal layer 130 and a sealing member 140. The lower substrate 110 is also referred to as a thin film transistor substrate, and the upper substrate 120 is also referred to as a color filter substrate.

하부 기판(110) 상에는 서로 교차하는 방향으로 배치되는 게이트 배선 및 데이터 배선에 의해 단위 화소(R, G, B)가 정의된다. 또한, 게이트 배선 및 데이터 배선의 교차 지점에는 스위칭 소자인 박막 트랜지스터(T)가 형성된다. 또한, 박막 트랜지스터의 드레인 전극(630)은 화소 전극(634)과 연결된다. 박막 트랜지스터의 게이트 전극(622)은 게이트 배선의 일부분이 될 수 있고, 소스 전극(628)은 데이터 배선의 일부분이 될 수 있다. 게이트 전극(622)이 배치된 기판 상에는 게이트 절연막(624)이 배치된다. 게이트 절연막(624) 상에는, 게이트 전극(622)과 중첩되며, 일단이 소스 전극(628)과 접속되며, 타단이 드레인 전극(630)과 접속되는 액티브층(626)이 배치된다. 도면에 도시하지 않았지만, 화소 전극(634)은 공통 전극(미도시)와 서로 엇갈리게 교차되어 횡전계를 발생시킬 수 있다. 도 6 내지 도 8에서 도면부호 632는 층간 절연층(포토아크릴층, 패시베이션층이라고도 한다)이다. The unit pixels R, G, and B are defined on the lower substrate 110 by gate wiring and data wiring arranged in directions intersecting each other. Further, a thin film transistor T, which is a switching element, is formed at the intersection of the gate wiring and the data wiring. Further, the drain electrode 630 of the thin film transistor is connected to the pixel electrode 634. The gate electrode 622 of the thin film transistor may be part of the gate wiring, and the source electrode 628 may be part of the data wiring. The gate insulating layer 624 is disposed on the substrate on which the gate electrode 622 is disposed. On the gate insulating layer 624, an active layer 626 overlapping the gate electrode 622, one end connected to the source electrode 628, and the other end connected to the drain electrode 630 is disposed. Although not shown in the drawing, the pixel electrode 634 may cross each other with a common electrode (not shown) to generate a transverse electric field. 6 to 8, reference numeral 632 denotes an interlayer insulating layer (also called a photoacrylic layer or a passivation layer).

하부 기판(110) 상에는 액정층(130)이 배치된다. 액정층(130) 상에는 상부 기판(120)이 배치된다. 하부 기판(110)과 상부 기판(120) 간의 갭을 유지하기 위해 컬럼 스페이서(650)가 배치되어 있다. 액정층(130)상에는 상부 기판, 즉 컬러필터 기판의 오버 코트층(646)이 보호층이 배치될 수 있다. The liquid crystal layer 130 is disposed on the lower substrate 110. The upper substrate 120 is disposed on the liquid crystal layer 130. Column spacers 650 are disposed to maintain a gap between the lower substrate 110 and the upper substrate 120. On the liquid crystal layer 130, an overcoat layer 646 of an upper substrate, that is, a color filter substrate, may be provided with a protective layer.

한편, 박막트랜지스터 기판에서 화소 영역은 투과 영역에 해당하며, 게이트 배선, 데이터 배선, 박막 트랜지스터 등은 비투과 영역에 해당하며, 컬러필터 기판의 블랙매트릭스(613)는 비투과 영역에 대응하도록 형성된다. 블랙매트릭스(613)가 배치된 상부 기판(120)의 하부면에는 RGB 컬러필터층(612)이 배치되어 있다. Meanwhile, in the thin film transistor substrate, the pixel region corresponds to the transmissive region, the gate wiring, the data wiring, the thin film transistor and the like correspond to the non-transmissive region, and the black matrix 613 of the color filter substrate is formed to correspond to the non-transmissive region. An RGB color filter layer 612 is disposed on a lower surface of the upper substrate 120 on which the black matrix 613 is disposed.

액정 디스플레이 패널에 있어서, 박막트랜지스터 기판 및 컬러필터 기판의 구조 및 각 층의 소재는 이미 다양한 형태로 공지되어 있는 바, 본 발명에서는 이들에 대한 상세한 설명을 생략한다. In the liquid crystal display panel, the structure of the thin film transistor substrate and the color filter substrate and the material of each layer are already known in various forms, and thus detailed description thereof will be omitted in the present invention.

한편, 도 6에 도시된 예에서, 실링 부재(140)는 하부 기판(110) 및 상부 기판(120)의 측면과, 하부 기판(110) 및 상부 기판(120) 사이에 배치된 액정층(130)의 측면을 커버하도록 연장되어 있다. 보다 구체적으로, 실링 부재(140)는 상부 기판(120)의 측면을 커버함에 있어, 편광판(125), 상부 기판(120), 컬러필터층(612) 및 오버코트층(646)의 측면과 접촉할 수 있다. 또한, 실링 부재(140)는 하부 기판(110)의 측면을 커버함에 있어, 편광판(115), 하부 기판(120), 게이트 절연막(624) 및 층간 절연층(632)의 측면과 접촉할 수 있다. 또한, 실링 부재(140)는 하부 기판(110) 및 상부 기판(120)의 합착이 가능하도록, 하부 기판(110) 및 상부 기판(120)의 가장자리 내측으로 돌출되어 있는 형태를 갖는다.On the other hand, in the example shown in Figure 6, the sealing member 140 is a liquid crystal layer 130 disposed between the lower substrate 110 and the side of the upper substrate 120 and the lower substrate 110 and the upper substrate 120 ). More specifically, when the sealing member 140 covers the side surface of the upper substrate 120, it may contact the side surfaces of the polarizing plate 125, the upper substrate 120, the color filter layer 612 and the overcoat layer 646. have. In addition, the sealing member 140 may contact the side surfaces of the polarizing plate 115, the lower substrate 120, the gate insulating layer 624, and the interlayer insulating layer 632 when covering the side surfaces of the lower substrate 110. . In addition, the sealing member 140 has a shape protruding inside the edges of the lower substrate 110 and the upper substrate 120 so that the lower substrate 110 and the upper substrate 120 can be bonded.

도 7에 도시된 예에서, 실링 부재(140)는 상부 기판(120)의 측면과, 하부 기판(110) 및 상부 기판(120) 사이에 배치된 액정층(130)의 측면을 커버하도록 연장되어 있다. 보다 구체적으로, 실링 부재(140)는 상부 기판(120)의 측면을 커버함에 있어, 편광판(125), 상부 기판(120), 컬러필터층(612) 및 오버코트층(646)의 측면과 접촉할 수 있다. 또한, 실링 부재(140)는 하부 기판(110)의 상부에 배치된 게이트 절연막(624) 및 층간 절연층(632)의 측면과 접촉할 수 있다. 또한, 실링 부재(140)는 하부 기판(110) 및 상부 기판(120)의 합착이 가능하도록, 하부 기판(110) 및 상부 기판(120)의 가장자리 내측으로 돌출되어 있는 형태를 갖는다.In the example shown in FIG. 7, the sealing member 140 is extended to cover the side surface of the upper substrate 120 and the side surface of the liquid crystal layer 130 disposed between the lower substrate 110 and the upper substrate 120. have. More specifically, when the sealing member 140 covers the side surface of the upper substrate 120, it may contact the side surfaces of the polarizing plate 125, the upper substrate 120, the color filter layer 612, and the overcoat layer 646. have. In addition, the sealing member 140 may contact the side surfaces of the gate insulating layer 624 and the interlayer insulating layer 632 disposed on the lower substrate 110. In addition, the sealing member 140 has a shape protruding inside the edges of the lower substrate 110 and the upper substrate 120 so that the lower substrate 110 and the upper substrate 120 can be bonded.

도 8에 도시된 예에서, 실링 부재(140)는 도 7에 도시된 상부 기판(120)의 측면과, 하부 기판(110) 및 상부 기판(120) 사이에 배치된 액정층(130)의 측면을 커버하면서 또한 회로 기판(160)의 일부분도 함께 커버하도록 배치되어 있다. 회로 기판(160)의 일부분이 하부 기판(120)에 접착제 등에 의해 접착되어 회로 기판(160)이 하부 기판(120)에 1차 고정될 수 있고, 추가로 실링 부재(130)가 회로 기판(160)의 일부분 및 하부 기판(120)의 가장자리를 함께 커버하면서 실링 부재(140)에 2차 고정될 수 있다. In the example shown in FIG. 8, the sealing member 140 has a side surface of the upper substrate 120 shown in FIG. 7 and a side surface of the liquid crystal layer 130 disposed between the lower substrate 110 and the upper substrate 120. It is also arranged to cover a portion of the circuit board 160 while covering the same. A portion of the circuit board 160 may be adhered to the lower substrate 120 by an adhesive or the like, such that the circuit board 160 may be primarily fixed to the lower substrate 120, and the sealing member 130 may further be a circuit board 160. ) May be secondarily fixed to the sealing member 140 while covering a portion of the lower substrate 120 and an edge of the lower substrate 120 together.

이상 본 발명이 액정 디스플레이 패널에 적용되는 예에 대하여 설명하였으나, 본 발명은 이에 한정되지 않는다. 예를 들어, 본 발명은 OLED 디스플레이 패널이나 마이크로 LED 디스플레이 패널 등 다른 형태의 디스플레이 패널에도 적용 가능하다.The example in which the present invention is applied to a liquid crystal display panel has been described above, but the present invention is not limited thereto. For example, the present invention is applicable to other types of display panels, such as OLED display panels and micro LED display panels.

실시예Example

이하, 본 발명의 바람직한 실시예를 통해 본 발명의 구성 및 작용을 더욱 상세히 설명하기로 한다. 다만, 이는 본 발명의 바람직한 예시로 제시된 것이며 어떠한 의미로도 이에 의해 본 발명이 제한되는 것으로 해석될 수는 없다. 여기에 기재되지 않은 내용은 이 기술 분야에서 숙련된 자이면 충분히 기술적으로 유추할 수 있는 것이므로 그 설명을 생략하기로 한다.Hereinafter, the configuration and operation of the present invention through a preferred embodiment of the present invention will be described in more detail. However, this is provided as a preferred example of the present invention and cannot be interpreted as limiting the present invention by any means. The contents not described here will be sufficiently technically inferred by those skilled in the art, and thus the description thereof will be omitted.

1. 실링 부재 및 시편1. Sealing member and specimen

실시예 1, 실시예 2 및 비교예에 따른 실링 부재의 조성을 표 1에 나타내었다. Table 1 shows the composition of the sealing members according to Example 1, Example 2, and Comparative Example.

[표 1] (단위 : 중량%)[Table 1] (unit: weight%)

Figure pat00001
Figure pat00001

하부 글래스 기판과 상부면에 편광판이 배치된 상부 글래스 기판을 마련하고, 하부 글래스 기판과 상부 글래스 기판 사이, 및 하부 글래스 기판의 측면과 상부 글래스 기판 및 편광판의 측면 실시예 1, 실시예 2 및 비교예 조성을 갖는 실링 부재가 접촉된 구조의 시편을 제조하였다.A lower glass substrate and an upper glass substrate on which a polarizing plate is disposed on an upper surface are provided, and between the lower glass substrate and the upper glass substrate, and the side surfaces of the lower glass substrate and the upper glass substrate and the polarizing plate. Examples 1, 2, and comparison Example A specimen having a structure in which a sealing member having a composition was in contact was prepared.

2. 특성 평가2. Characteristic evaluation

각 시편들에 대하여, 접착성 및 수분 차폐성을 평가하여 표 2에 나타내었다. 접착성은 크로스컷 에릭슨 테스트법으로 수행하여, 박리가 발생하였는지 여부로 판단하여 박리 발생(X), 미세 박리(O), 박리 없음(⊙)으로 평가하였다. 수분 차폐성은 실시예 1, 실시예 2 및 비교예에 따른 실링 부재가 적용된 시편들을 80℃ 상대 습도 및 25℃ 온도 조건에서 하루동안 실링 부재 내부로 침투된 수분량을 측정하여, 수분 침투량이 0.5ppm 이하(⊙), 1.0ppm 이하(O), 1.0ppm 초과(X)로 평가하였다. For each specimen, adhesion and moisture shielding properties were evaluated and are shown in Table 2. Adhesion was performed by the cross-cut Ericsson test method, and judged whether peeling occurred or not, and evaluated as peeling occurrence (X), fine peeling (O), and no peeling (⊙). Moisture shielding was measured by measuring the amount of moisture that penetrated into the sealing member for one day at 80 ° C relative humidity and 25 ° C temperature conditions for the specimens to which the sealing member according to Examples 1, 2, and Comparative Examples were applied, and the moisture penetration amount was 0.5 ppm or less. (⊙), 1.0ppm or less (O), was evaluated as more than 1.0ppm (X).

또한, 각 시편들에 대하여 편광판 수축 정도, 실링 부재 연신 정도를 평가하여 표 2에 나타내었다. 편광판 수축 정도, 실링 부재 연신 정도를 평가하기 위해 각 시편을 60℃, 상대습도 90% 조건에서 1일동안 방치하였다. 비교예에서 얻어진 수치를 기준으로 실시예 1 및 실시예 2에서 얻어진 수치를 상대적인 값으로 나타내었다. In addition, for each specimen, the degree of shrinkage of the polarizing plate and the degree of stretching of the sealing member were evaluated and are shown in Table 2. In order to evaluate the degree of shrinkage of the polarizing plate and the degree of stretching of the sealing member, each specimen was left for 1 day at 60 ° C and 90% relative humidity. Based on the numerical values obtained in the comparative examples, the numerical values obtained in Example 1 and Example 2 are shown as relative values.

[표 2][Table 2]

Figure pat00002
Figure pat00002

표 2를 참조하면, 에폭시 올리고머가 주성분인 비교예에 따른 실링 부재가 적용된 경우에 비하여 우레탄 아크릴레이트 올리고머가 주성분인 실시예 1 및 실시예 2에 따른 실링 부재가 적용된 경우가 편광판 수축 정도는 더 낮은 반면, 실링 부재 연신 정도는 더 높은 값을 나타내었다. 이는 에폭시 올리고머가 주성분인 비교예에 따른 실링 부재에 비하여 우레탄 아크릴레이트 올리고머가 주성분인 실시예 1 및 실시예 2에 따른 실링 부재의 탄성이 더 우수한 것에 기인한다. Referring to Table 2, when the sealing member according to Examples 1 and 2 in which the urethane acrylate oligomer is the main component is applied, the degree of shrinkage of the polarizer is lower than when the sealing member according to the comparative example in which the epoxy oligomer is the main component is applied. On the other hand, the degree of stretching of the sealing member showed a higher value. This is due to the elasticity of the sealing member according to Examples 1 and 2 in which the urethane acrylate oligomer is the main component, compared to the sealing member according to the comparative example in which the epoxy oligomer is the main component.

한편, 표 2의 실시예 1 및 실시예 2를 살펴보면, 실시예 2의 경우가 편광판 수축 정도가 더 낮고, 실링 부재의 연신 정도는 더 높은 것을 볼 수 있다. 실시예 2의 경우, 실링 부재에 강성 보강 입자로서 PMMA가 10중량% 포함된 경우로서, 이와 같이 강성 보강 입자가 포함되는 경우, 실링 부재의 탄성 및 강성을 높일 수 있어, 편광판 수축 제어에 보다 효율적이다.  On the other hand, looking at Example 1 and Example 2 of Table 2, it can be seen that in the case of Example 2, the degree of shrinkage of the polarizing plate is lower and the degree of stretching of the sealing member is higher. In the case of Example 2, when the sealing member contains 10% by weight of PMMA as the stiffening reinforcing particles, and when the stiffening reinforcing particles are included in this way, the elasticity and rigidity of the sealing member can be increased, thereby more effectively controlling the shrinkage of the polarizing plate. to be.

또한, 실시예 1 및 실시예 2에 대한 광 밀도(optical density)를 측정한 결과, 실시예 1의 경우 1.8을 나타내었고, 실시예 2의 경우 수회 측정한 결과 1.7~1.8 정도를 나타내었는데, 이는 강성 보강 입자가 추가로 포함되더라도 광 밀도에는 거의 영향을 미치지 않는 결과로 볼 수 있다. In addition, as a result of measuring the optical density (optical density) for Example 1 and Example 2, in the case of Example 1 was shown 1.8, in the case of Example 2 was measured several times, it showed about 1.7 to 1.8, which Even if the stiffening reinforcing particles are additionally included, it can be seen that the light density is hardly affected.

이상과 같이 본 발명에 대해서 예시한 도면을 참조로 하여 설명하였으나, 본 명세서에 개시된 실시 예와 도면에 의해 본 발명이 한정되는 것은 아니며, 본 발명의 기술사상의 범위 내에서 통상의 기술자에 의해 다양한 변형이 이루어질 수 있음은 자명하다. 아울러 앞서 본 발명의 실시 예를 설명하면서 본 발명의 구성에 따른 작용 효과를 명시적으로 기재하여 설명하지 않았을 지라도, 해당 구성에 의해 예측 가능한 효과 또한 인정되어야 함은 당연하다.As described above, the present invention has been described with reference to the exemplified drawings, but the present invention is not limited by the examples and drawings disclosed in the present specification, and can be varied by a person skilled in the art within the scope of the technical idea of the present invention. It is obvious that modifications can be made. In addition, although the operation and effect according to the configuration of the present invention has not been explicitly described and described while explaining the embodiment of the present invention, it is natural that the predictable effect by the configuration should also be recognized.

110: 하부 기판 115: 편광판
120 : 상부 기판 125 : 편광판
130 : 액정층 135 : 액정
140 : 실링 부재 140a: 내측부
140b : 외측부 160 : 회로 기판110: lower substrate 115: polarizing plate
120: upper substrate 125: polarizing plate
130: liquid crystal layer 135: liquid crystal
140: sealing member 140a: inner portion
140b: outer part 160: circuit board

Claims (14)

우레탄 아크릴레이트 올리고머 60~70중량%,
아크릴레이트 모노머 10~30중량%,
안료 1~5중량%,
광 개시제 1~5중량%,
가교제 1~5중량%를 포함하는, 평판 디스플레이 패널용 실링 부재.
Urethane acrylate oligomer 60 ~ 70% by weight,
10-30% by weight of acrylate monomer,
Pigment 1-5% by weight,
1-5% by weight of photoinitiator,
A sealing member for a flat panel display panel comprising 1 to 5% by weight of a crosslinking agent.
제1항에 있어서,
강성 보강 입자 1~35중량%를 추가로 포함하는, 평판 디스플레이 패널용 실링 부재.
According to claim 1,
A sealing member for a flat panel display panel further comprising 1 to 35% by weight of rigid reinforcement particles.
제2항에 있어서,
상기 강성 보강 입자는 PMMA(polymethylmetacrylate) 입자, 폴리우레탄 입자 및 실리콘 입자 중 1종 이상을 포함하는, 평판 디스플레이 패널용 실링 부재.
According to claim 2,
The rigid reinforcement particles include one or more of PMMA (polymethylmetacrylate) particles, polyurethane particles and silicon particles, a sealing member for a flat panel display panel.
제1항에 있어서,
상기 안료는 광흡수성 안료인, 평판 디스플레이 패널용 실링 부재.
According to claim 1,
The pigment is a light absorbing pigment, a sealing member for a flat panel display panel.
박막 트랜지스터가 배치된 하부 기판;
상기 하부 기판의 가장자리를 따라 배치된 실링 부재; 및
상기 실링 부재를 통하여 상기 하부 기판과 합착되며, 상부면에 편광판이 배치된 상부 기판;을 포함하고,
상기 실링 부재는 상기 상부 기판의 측면을 커버하면서 상기 편광판의 측면과 접촉되도록 연장되어 있으며,
상기 실링 부재는 우레탄 아크릴레이트 올리고머 60~70중량%, 아크릴레이트 모노머 10~30중량%, 안료 1~5중량%, 광 개시제 1~5중량% 및 가교제 1~5중량%를 포함하는, 평판 디스플레이 패널.
A lower substrate on which the thin film transistor is disposed;
A sealing member disposed along the edge of the lower substrate; And
Includes; the upper substrate is bonded to the lower substrate through the sealing member, the polarizing plate is disposed on the upper surface;
The sealing member is extended so as to cover the side surface of the upper substrate and contact the side surface of the polarizing plate,
The sealing member comprises 60 to 70% by weight of urethane acrylate oligomer, 10 to 30% by weight of acrylate monomer, 1 to 5% by weight of pigment, 1 to 5% by weight of photo initiator, and 1 to 5% by weight of crosslinking agent panel.
제5항에 있어서,
상기 실링 부재는 상기 하부 기판의 측면을 커버하도록 연장되어 있는, 평판 디스플레이 패널.
The method of claim 5,
The sealing member is extended to cover the side surface of the lower substrate, a flat panel display panel.
제5항에 있어서,
상기 실링 부재는 상기 편광판의 상부면과 접촉되도록 연장되어 있는, 평판 디스플레이 패널.
The method of claim 5,
The sealing member is extended to contact the upper surface of the polarizing plate, a flat panel display panel.
제5항에 있어서,
상기 평판 디스플레이 패널은 액정 디스플레이 패널이고,
상기 실링 부재, 하부 기판 및 상부 기판에 의해 정의되는 공간에 액정이 배치되는, 평판 디스플레이 패널.
The method of claim 5,
The flat panel display panel is a liquid crystal display panel,
A flat panel display panel in which liquid crystal is disposed in a space defined by the sealing member, the lower substrate, and the upper substrate.
제5항에 있어서,
상기 실링 부재는 강성 보강 입자 1~35중량%를 추가로 포함하는, 평판 디스플레이 패널.
The method of claim 5,
The sealing member further comprises 1 to 35% by weight of the rigid reinforcement particles, flat panel display panel.
제9항에 있어서,
상기 강성 보강 입자는 PMMA(polymethylmetacrylate) 입자, 폴리우레탄 입자 및 실리콘 입자 중 1종 이상을 포함하는, 평판 디스플레이 패널.
The method of claim 9,
The rigid reinforcement particles include one or more of PMMA (polymethylmetacrylate) particles, polyurethane particles and silicon particles, flat panel display panel.
제5항에 있어서,
상기 안료는 광흡수성 안료인, 평판 디스플레이 패널.
The method of claim 5,
The pigment is a light absorbing pigment, a flat panel display panel.
박막 트랜지스터가 배치된 하부 기판;
상기 하부 기판의 가장자리를 따라 배치된 실링 부재; 및
상기 실링 부재를 통하여 상기 하부 기판과 합착되며, 상부면에 편광판이 배치된 상부 기판;을 포함하고,
상기 실링 부재는 상기 상부 기판의 측면을 커버하면서 상기 편광판의 측면과 접촉되도록 연장되어 있으며,
상기 실링 부재는 상기 편광판 수축시에 상기 편광판의 수축 방향으로 연신되어 상기 편광판과의 접촉을 유지하는, 평판 디스플레이 패널.
A lower substrate on which the thin film transistor is disposed;
A sealing member disposed along the edge of the lower substrate; And
Includes; the upper substrate is bonded to the lower substrate through the sealing member, the polarizing plate is disposed on the upper surface;
The sealing member is extended so as to cover the side surface of the upper substrate and contact the side surface of the polarizing plate,
The sealing member is stretched in the shrinking direction of the polarizing plate when the polarizing plate is contracted to maintain contact with the polarizing plate.
제12항에 있어서,
상기 실링 부재는 상기 하부 기판의 측면을 커버하도록 연장되어 있는, 평판 디스플레이 패널.
The method of claim 12,
The sealing member is extended to cover the side surface of the lower substrate, a flat panel display panel.
제12항에 있어서,
상기 실링 부재는 상기 편광판의 상부면과 접촉되도록 연장되어 있는, 평판 디스플레이 패널.The method of claim 12,
The sealing member is extended to contact the upper surface of the polarizing plate, a flat panel display panel.
KR1020180117701A 2018-10-02 2018-10-02 Sealing member and flat display panel including the same KR102545120B1 (en)