KR20200007105A - 말레산무수물 그래프트 poe 케이블 재료 및 그 제조 방법 - Google Patents

말레산무수물 그래프트 poe 케이블 재료 및 그 제조 방법 Download PDF

Info

Publication number
KR20200007105A
KR20200007105A KR1020177027144A KR20177027144A KR20200007105A KR 20200007105 A KR20200007105 A KR 20200007105A KR 1020177027144 A KR1020177027144 A KR 1020177027144A KR 20177027144 A KR20177027144 A KR 20177027144A KR 20200007105 A KR20200007105 A KR 20200007105A
Authority
KR
South Korea
Prior art keywords
weight
parts
maleic anhydride
cable material
silicon dioxide
Prior art date
Application number
KR1020177027144A
Other languages
English (en)
Inventor
썬 위엔
리우슈 위엔
항 우
멍 흐어
아이화 바이
지아예 탕
Original Assignee
옌청 썬위엔 플라스틱 컴퍼니 리미티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 옌청 썬위엔 플라스틱 컴퍼니 리미티드 filed Critical 옌청 썬위엔 플라스틱 컴퍼니 리미티드
Publication of KR20200007105A publication Critical patent/KR20200007105A/ko

Abstract

말레산무수물 그래프트 POE 케이블 재료는 POE 60 내지 86중량부, 말레산무수물 55 내지 65중량부, 가교보조제 1 내지 3중량부, 강화제 5 내지 9중량부, 무정형 이산화규소 섬유 3 내지 7중량부, 커플링제 1 내지 3중량부, 삼산화안티몬 10 내지 14중량부, 멜라민 12 내지 20중량부, 항산화제 3 내지 9부를 포함하고, 상기 가교보조제는 트리알릴 이소시아누레이트(triallyl isocyanurate), 트리메타크릴레이트 트리메틸올프로판(trimethacrylate trimethylolpropane) 또는 트리메틸올프로판 트리메타크릴레이트(trimethylolpropane trimethacrylate)로 이루어진 군에서 선택된 하나 이상이다. 본 발명은 무정형 이산화규소 섬유를 첨가해 케이블 재료의 인성을 향상시키고 내후성을 강화시키는 데 유리하고; 본 발명의 케이블은 저온(-40℃) 충격 시 크랙이 생기지 않으며, 저온(-40℃) 굽힘 시에도 크랙이 생기지 않는다. 본 발명은 동방향 이축압출기를 이용해 압출한 후 조립하며, 제조한 케이블 재료에는 할로겐이 함유되어 있지 않기 때문에 물리적 성능과 가공 성능이 비교적 우수하고 사용수명이 길다.

Description

말레산무수물 그래프트 POE 케이블 재료 및 그 제조 방법
본 발명은 케이블 재료 분야에 관한 것으로서, 더욱 상세하게는 말레산무수물 그래프트 POE 케이블 재료 및 그 제조 방법에 관한 것이다.
전선 케이블 절연 및 보호용 플라스틱을 통상적으로 케이블 재료라고 부르며, 여기에는 고무, 플라스틱, 나일론 등 다양한 품종이 포함된다. 전선 케이블은 전기 에너지를 전송하는 과정에서 노화로 인한 자체 발열이나 외부 화재 때문에 연소될 수 있다. 다양한 분야에서 케이블의 품질과 성능에 대한 요구가 갈수록 높아지면서 전선 케이블의 난연성에 대한 요구 수준이 높아져 할로겐 함유 난연제를 첨가하고 있는데, 할로겐 함유 전선 케이블은 연소 과정에서 대량의 연무와 할로겐화 수소 기체가 방출돼 화재 시 질식사가 일어나기 쉽고 기계 설비도 비교적 크게 부식시킨다. 현재 국내외 케이블 및 그 제조 영역에서는 저연, 저할로겐 및 비할로겐 난연 재료의 방향으로 연구과 제조가 이루어지고 있다.
출원번호 201510197415.7 발명특허 “고난연성의 저연 비할로겐 케이블 재료 및 그 제조 방법”은 고난연성의 저연 비할로겐 케이블 재료 및 그 제조 방법에 관한 것으로서, 여기에서 고난연성의 저연 비할로겐 케이블 재료는 질량백분율로 계산할 경우 구성성분과 각각의 함량이 에틸렌 비닐아세테이트 공중합체 12 내지 22%, 폴리에틸렌 5 내지 10%, 말레산무수물 그래프트 폴리에틸렌 5 내지 10%, 무기충전재 40 내지 50%, 자체 제작 복합 난연제 15 내지 20%, 항산화 보조제 1 내지 3%이고, 각 성분의 질량백분율의 합은 100%이다. 장점은 자체 제작 복합 난연제가 케이블의 탄화 성능과 자기소화 성능을 향상시킬 수 있으며, 제조한 케이블 재료로 제작한 1.5mm2 단심 케이블은 UL의 VW-1 연소 테스트를 통과해 케이블 재료의 전기 절연 성능이 보장되고, 케이블 재료의 백색 외관은 고객의 수요에 맞는 각종 색상을 제조하는 데 적합하다는 것이다. 그러나 그 강도가 높지 않고 사용수명이 짧다는 단점이 있다.
현재 비할로겐계 저연 난연성 케이블 재료의 생산은 대부분이 폴리올레핀 기재에 대량의 수산화마그네슘 또는 수산화알루미늄을 첨가해 난연의 목적을 달성한다. 그러나 대량의 무기 재료를 첨가하면 케이블 재료의 물리 전기적 성능과 가공 공정 성능이 떨어지게 되며, 내후성, 내유성 및 내냉성이 모두 나빠지게 된다.
본 발명의 목적은, 말레산무수물 그래프트 POE 케이블 재료 및 그 제조 방법을 제안함으로써 상기 문제를 해결하는 데에 있다.
상기 목적을 달성하기 위해 본 발명에서는 이하의 기술방안을 채택하였다.
말레산무수물 그래프트 POE 케이블 재료는 POE 60 내지 86중량부, 말레산무수물 55 내지 65중량부, 가교보조제 1 내지 3중량부, 강화제 5 내지 9중량부, 무정형 이산화규소 섬유 3 내지 7중량부, 커플링제 1 내지 3중량부, 삼산화안티몬 10 내지 14중량부, 멜라민 12 내지 20중량부, 항산화제 3 내지 9부를 포함하고, 상기 가교보조제는 트리알릴 이소시아누레이트(triallyl isocyanurate), 트리메타크릴레이트 트리메틸올프로판(trimethacrylate trimethylolpropane) 또는 트리메틸올프로판 트리메타크릴레이트(trimethylolpropane trimethacrylate)로 이루어진 군에서 선택된 하나 이상이다.
바람직하게는, 상기 강화제는 시스-폴라부타디엔 수지 10 내지 16중량부, 산화마그네슘 6 내지 12중량부, 이산화규소 7 내지 11중량부, 그래핀 2 내지 4중량부를 포함한다.
바람직하게는, 상기 무정형 이산화규소 섬유의 평균 입경은 20nm이고, 비표면적은 180m2/g이다.
바람직하게는, 상기 커플링제는 트리메톡시프로필실란 (trimethoxypropylsilane), 페닐트리메톡시실란(phenyltrimethoxysilane), 티타늄 이소부톡사이드(titanium isobutoxide) 또는 스테아르산으로 이루어진 군에서 선택된 하나 이상이다.
바람직하게는, 상기 항산화제는 L-아스코르빌 팔미테이트(L-ascorbyl palmitate)와 1,2-아미노아조페닐렌(1,2-aminoazophenylene)이고, 상기 L-아스코르빌 팔미테이트와 1,2-아미노아조페닐렌의 중량비는 2:1이다.
말레산무수물 그래프트 POE 케이블 재료 및 그 제조 방법은 이하 단계를 포함한다.
단계 S1: POE와 말레산무수물은 혼합기로 1 내지 3시간 혼합하고, 가교보조제를 첨가해 3 내지 6시간 혼합하고;
단계 S2: 무정형 이산화규소 섬유를 파쇄기에 넣고 30 내지 60분간 연마하고, 커플링제를 첨가해 계속해서 1 내지 2시간 파쇄하고;
단계 S3: 단계 S1과 S2에서 수득한 물질을 혼합하고, 동방향 이축압출기에 넣은 후 다시 강화제, 삼산화안티몬, 멜라민과 항산화제를 첨가하고, 200 내지 260℃ 가공 온도에서 압출하고;
단계 S4: 단계 S3에서 수득한 물질을 조립한 후 패키징한다.
바람직하게는, 상기 단계 S1의 혼합기는 이축혼합기이고, 상기 혼합기의 혼합축 온도는 45℃이다.
바람직하게는, 상기 동방향 이축압출기의 축은 원추형이고, 상기 축의 장경(long diameter)은 22보다 크거나 같다.
본 발명의 유익한 효과는 이하와 같다. 즉, 본 발명은 무정형 이산화규소 섬유를 첨가해 케이블 재료의 인성을 향상시키고 내후성을 강화시키는 데 유리하다. 본 발명의 케이블은 저온(-40℃) 충격 시 크랙이 생기지 않으며, 저온(-40℃) 굽힘 시에도 크랙이 생기지 않는다. 본 발명은 동방향 이축압출기를 이용해 압출한 후 조립하며, 제조한 케이블 재료에는 할로겐이 함유되어 있지 않기 때문에 물리적 성능과 가공 성능이 비교적 우수하고 사용수명이 길다.
이하에서는, 예시적인 실시형태들을 통해 본 발명을 보다 상세히 설명한다. 이하의 구체적인 실시방식은 본 발명을 설명하기 위한 것으로서 본 발명의 범위를 제한하지 않는다.
본 발명 실시예에서 사용한 무정형 이산화규소 섬유의 평균 임경은 20nm이고, 비표면적은 180m2/g이다.
실시예 1
말레산무수물 그래프트 POE 케이블 재료의 제조 방법은 이하 단계를 포함한다.
단계 S1: 60중량부의 POE와 55중량부의 말레산무수물은 이축혼합기로 1시간 혼합하며 혼합축 온도는 45℃이고, 1중량부의 가교보조제 트리알릴 이소시아누레이트를 첨가해 3시간 혼합하고;
단계 S2: 3중량부의 무정형 이산화규소 섬유를 파쇄기에 넣고 30분간 연마하고, 1중량부의 트리메톡시프로필실란을 첨가해 계속해서 1시간 파쇄하고;
단계 S3: 단계 S1과 S2에서 수득한 물질을 혼합하고, 축이 원추형이고 장경이 22보다 크거나 같은 동방향 이축압출기에 넣은 후 다시 5중량부의 강화제, 10 내지 14중량부의 삼산화안티몬, 12 내지 20중량부의 멜라민과 3 내지 9중량부의 항산화제를 첨가하고, 항산화제의 중량비가 2:1인 L-아스코르빌 팔미테이트와 1,2-아미노아조페닐렌이고, 강화제는 시스-폴라부타디엔 수지 10중량부, 산화마그네슘 6중량부, 이산화규소 7중량부, 그래핀 2중량부를 포함하고, 200℃ 가공 온도에서 압출하고;
단계 S4: 단계 S3에서 수득한 물질을 조립한 후 패키징한다.
실시예 2
말레산무수물 그래프트 POE 케이블 재료의 제조 방법은 이하 단계를 포함한다.
단계 S1: 86중량부의 POE와 65중량부의 말레산무수물은 이축혼합기로 3시간 혼합하며 혼합축 온도는 45℃이고, 1중량부의 가교보조제 트리알릴 이소시아누레이트를 첨가해 6시간 혼합하고;
단계 S2: 7중량부의 무정형 이산화규소 섬유를 파쇄기에 넣고 60분간 연마하고, 3중량부의 트리메톡시프로필실란을 첨가해 계속해서 2시간 파쇄하고;
단계 S3: 단계 S1과 S2에서 수득한 물질을 혼합하고, 축이 원추형이고 장경이 22보다 크거나 같은 동방향 이축압출기에 넣은 후 다시 9중량부의 강화제, 14중량부의 삼산화안티몬, 20중량부의 멜라민과 9중량부의 항산화제를 첨가하고, 항산화제의 중량비가 2:1인 L-아스코르빌 팔미테이트와 1,2-아미노아조페닐렌이고, 강화제는 시스-폴라부타디엔 수지 16중량부, 산화마그네슘 12중량부, 이산화규소 11중량부, 그래핀 4중량부를 포함하고, 260℃ 가공 온도에서 압출하고;
단계 S4: 단계 S3에서 수득한 물질을 조립한 후 패키징한다.
실시예 3
말레산무수물 그래프트 POE 케이블 재료의 제조 방법은 이하 단계를 포함한다.
단계 S1: 73중량부의 POE와 60중량부의 말레산무수물은 이축혼합기로 2시간 혼합하며 혼합축 온도는 45℃이고, 2중량부의 가교보조제 트리알릴 이소시아누레이트를 첨가해 4.5시간 혼합하고;
단계 S2: 5중량부의 무정형 이산화규소 섬유를 파쇄기에 넣고 45분간 연마하고, 2중량부의 트리메톡시프로필실란을 첨가해 계속해서 1.5시간 파쇄하고;
단계 S3: 단계 S1과 S2에서 수득한 물질을 혼합하고, 축이 원추형이고 장경이 22보다 크거나 같은 동방향 이축압출기에 넣은 후 다시 7중량부의 강화제, 12중량부의 삼산화안티몬, 16중량부의 멜라민과 6중량부의 항산화제를 첨가하고, 항산화제의 중량비가 2:1인 L-아스코르빌 팔미테이트와 1,2-아미노아조페닐렌이고, 강화제는 시스-폴라부타디엔 수지 13중량부, 산화마그네슘 9중량부, 이산화규소 9중량부, 그래핀 3중량부를 포함하고, 230℃ 가공 온도에서 압출하고;
단계 S4: 단계 S3에서 수득한 물질을 조립한 후 패키징한다.
실시예 4
말레산무수물 그래프트 POE 케이블 재료의 제조 방법은 이하 단계를 포함한다.
단계 S1: 63중량부의 POE와 57중량부의 말레산무수물은 이축혼합기로 1시간 혼합하며 혼합축 온도는 45℃이고, 2중량부의 가교보조제 트리알릴 이소시아누레이트를 첨가해 4시간 혼합하고;
단계 S2: 4중량부의 무정형 이산화규소 섬유를 파쇄기에 넣고 350분간 연마하고, 2중량부의 트리메톡시프로필실란을 첨가해 계속해서 1시간 파쇄하고;
단계 S3: 단계 S1과 S2에서 수득한 물질을 혼합하고, 축이 원추형이고 장경이 22보다 크거나 같은 동방향 이축압출기에 넣은 후 다시 6중량부의 강화제, 11중량부의 삼산화안티몬, 13중량부의 멜라민과 4중량부의 항산화제를 첨가하고, 항산화제의 중량비가 2:1인 L-아스코르빌 팔미테이트와 1,2-아미노아조페닐렌이고, 강화제는 시스-폴라부타디엔 수지 11중량부, 산화마그네슘 7중량부, 이산화규소 8중량부, 그래핀 3중량부를 포함하고, 210℃ 가공 온도에서 압출하고;
단계 S4: 단계 S3에서 수득한 물질을 조립한 후 패키징한다.
실시예 5
말레산무수물 그래프트 POE 케이블 재료의 제조 방법은 이하 단계를 포함한다.
단계 S1: 84중량부의 POE와 63중량부의 말레산무수물은 이축혼합기로 2시간 혼합하며 혼합축 온도는 45℃이고, 3중량부의 가교보조제 트리알릴 이소시아누레이트를 첨가해 5시간 혼합하고;
단계 S2: 6중량부의 무정형 이산화규소 섬유를 파쇄기에 넣고 50분간 연마하고, 2중량부의 트리메톡시프로필실란을 첨가해 계속해서 2시간 파쇄하고;
단계 S3: 단계 S1과 S2에서 수득한 물질을 혼합하고, 축이 원추형이고 장경이 22보다 크거나 같은 동방향 이축압출기에 넣은 후 다시 8중량부의 강화제, 13중량부의 삼산화안티몬, 18중량부의 멜라민과 8중량부의 항산화제를 첨가하고, 항산화제의 중량비가 2:1인 L-아스코르빌 팔미테이트와 1,2-아미노아조페닐렌이고, 강화제는 시스-폴라부타디엔 수지 15중량부, 산화마그네슘 10중량부, 이산화규소 10중량부, 그래핀 4중량부를 포함하고, 250℃ 가공 온도에서 압출하고;
단계 S4: 단계 S3에서 수득한 물질을 조립한 후 패키징한다.
시험 1
본 실시예 1 내지 5의 샘플을 산업표준에 따라 역학성능 시험을 진행했으며, 상세한 실험데이터는 표 1과 같다.
Figure pct00001
표 1에서 알 수 있듯이, 본 발명의 말레산무수물 그래프트 POE 케이블 재료는 비교적 우수한 굽힘 강도와 파단신율을 가지고 있다. 굽힘 강도는 최고 18.5MPa, 파단신율은 최고 200%이고, 저온(-40℃) 충격 시 크랙이 생기지 않으며, 저온(-40℃) 굽힘 시에도 크랙이 생기지 않아 유연성이 우수하였다.
본 발명에서 공개한 기술수단은 상기 실시방식에서 공개한 기술수단에 제한되지 않으며, 상기 기술특징을 임의로 조합한 기술방안도 포함한다. 본 발명이 속한 기술분야의 당업자는 본 발명의 원리를 기반으로 약간의 개선과 변경을 진행할 수 있으며, 이러한 개선과 변경은 모두 본 발명의 보호범위에 속한다.

Claims (8)

  1. POE 60 내지 86중량부, 말레산무수물 55 내지 65중량부, 가교보조제 1 내지 3중량부, 강화제 5 내지 9중량부, 무정형 이산화규소 섬유 3 내지 7중량부, 커플링제 1 내지 3중량부, 삼산화안티몬 10 내지 14중량부, 멜라민 12 내지 20중량부, 항산화제 3 내지 9부인 물질을 포함하고, 상기 가교보조제는 트리알릴 이소시아누레이트(triallyl isocyanurate), 트리메타크릴레이트 트리메틸올프로판(trimethacrylate trimethylolpropane) 또는 트리메틸올프로판 트리메타크릴레이트(trimethylolpropane trimethacrylate)로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료.
  2. 제 1항에 있어서,
    상기 강화제는 시스-폴라부타디엔 수지 10 내지 16중량부, 산화마그네슘 6 내지 12중량부, 이산화규소 7 내지 11중량부, 그래핀 2 내지 4중량부를 포함하는 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료.
  3. 제 1항에 있어서,
    상기 무정형 이산화규소 섬유의 평균 입경은 20nm이고, 비표면적은 180m2/g인 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료.
  4. 제 1항에 있어서,
    상기 커플링제는 트리메톡시프로필실란 (trimethoxypropylsilane), 페닐트리메톡시실란(phenyltrimethoxysilane), 티타늄 이소부톡사이드(titanium isobutoxide) 또는 스테아르산으로 이루어진 군에서 선택된 하나 이상인 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료.
  5. 제 1항에 있어서,
    상기 항산화제는 L-아스코르빌 팔미테이트(L-ascorbyl palmitate)와 1,2-아미노아조페닐렌(1,2-aminoazophenylene)이고, 상기 L-아스코르빌 팔미테이트와 1,2-아미노아조페닐렌의 중량비는 2:1인 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료.
  6. 제 5항에 있어서,
    POE와 말레산무수물은 혼합기로 1 내지 3시간 혼합하고, 가교보조제를 첨가해 3 내지 6시간 혼합하는 단계 S1;
    무정형 이산화규소 섬유를 파쇄기에 넣고 30 내지 60분간 연마하고, 커플링제를 첨가해 계속해서 1 내지 2시간 파쇄하는 단계 S2;
    상기 단계 S1과 S2에서 수득한 물질을 혼합하고, 동방향 이축압출기에 넣은 후 다시 강화제, 삼산화안티몬, 멜라민과 항산화제를 첨가하고, 200 내지 260℃ 가공 온도에서 압출하는 단계 S3;
    상기 단계 S3에서 수득한 물질을 조립한 후 패키징하는 단계 S4를 포함하는 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료의 제조 방법.
  7. 제 6항에 있어서,
    상기 단계 S1의 혼합기는 이축혼합기이고, 상기 혼합기의 혼합축 온도는 45℃인 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료의 제조 방법.
  8. 제 6항에 있어서,
    상기 동방향 이축압출기의 축은 원추형이고, 상기 축의 장경(long diameter)은 22보다 크거나 같은 것을 특징으로 하는 말레산무수물 그래프트 POE 케이블 재료의 제조 방법.
KR1020177027144A 2017-05-16 2017-08-09 말레산무수물 그래프트 poe 케이블 재료 및 그 제조 방법 KR20200007105A (ko)