KR20190124008A - Heating textile and method for manufacturing the same - Google Patents
Heating textile and method for manufacturing the same Download PDFInfo
- Publication number
- KR20190124008A KR20190124008A KR1020180048029A KR20180048029A KR20190124008A KR 20190124008 A KR20190124008 A KR 20190124008A KR 1020180048029 A KR1020180048029 A KR 1020180048029A KR 20180048029 A KR20180048029 A KR 20180048029A KR 20190124008 A KR20190124008 A KR 20190124008A
- Authority
- KR
- South Korea
- Prior art keywords
- fiber
- pattern
- heating layer
- carbon nanotubes
- forming
- Prior art date
Abstract
Description
본 발명은 발열 섬유 및 발열 섬유 제조방법에 관한 것으로, 보다 상세하게는 신축 가능하면서도 내구성이 뛰어난 발열 섬유 및 발열 섬유 제조방법에 관한 것이다.The present invention relates to a heat generating fiber and a method for producing a heat generating fiber, and more particularly, to a heat generating fiber and a method for producing a heat generating fiber excellent in durability.
의류용 섬유, 직물의 내부 소재가 발열 효과를 갖는다면 보온 효과 및 난방비 절약 효과를 가져올 것이다. 최근 이러한 목적으로 발열 기능을 갖는 섬유나 직물 또는 의류를 개발하고자 하는 노력이 지속되고 있다.If the inner material of the clothing fibers and fabrics have a heating effect, it will bring about the effect of keeping warm and saving heating costs. Recently, efforts have been made to develop fibers, fabrics, or clothes having a heating function for this purpose.
일반적으로 발열 섬유(또는 발열 직물)는 금속사 등의 전도성사를 이용하여 직접 섬유를 직조하여 제조하고 있으나, 금속사 등의 전도성사의 경우에는 단가가 매우 높고, 제조하기 매우 힘들며 고가의 장비를 필요로 한다. 또한, 이러한 방식으로 제조된 발열 섬유는 탄성력을 가지지 못하는 단점이 있고, 이에 따라 의류 및 탄성이 필요한 웨어러블 제품 등에는 사용하지 못하였다.In general, heat generating fibers (or heat generating fabrics) are manufactured by directly weaving fibers using conductive yarns such as metal yarns, but in the case of conductive yarns such as metal yarns, the unit cost is very high, very difficult to manufacture, and expensive equipment is required. Shall be. In addition, the heating fiber produced in this manner has a disadvantage that does not have an elastic force, and thus could not be used in clothing and wearable products that require elasticity.
본 발명은 패턴 발열층의 손상없이 신축 가능하면서도 내구성이 뛰어난 발열 섬유 및 발열 섬유 제조방법을 제공한다.The present invention provides a heat-generating fiber and a heat-generating fiber manufacturing method excellent in durability without damage to the pattern heat generating layer.
본 발명의 일실시예에 따른 발열 섬유는 섬유; 오픈부를 형성하는 연속적인 망 구조로 상기 섬유의 일면 상에 제공되며, 카본나노튜브로 이루어진 패턴 발열층; 및 상기 패턴 발열층에 전기적으로 연결되는 전극;을 포함할 수 있다.Heating fiber according to an embodiment of the present invention is a fiber; A patterned heating layer provided on one surface of the fiber in a continuous network structure forming an open portion and made of carbon nanotubes; And an electrode electrically connected to the pattern heating layer.
상기 섬유는 결(grain)을 갖고, 상기 패턴 발열층은, 상기 섬유의 결을 따라 제공되는 제1 라인부; 및 상기 섬유의 결과 교차하는 방향으로 연장되는 제2 라인부를 포함할 수 있다.The fiber has a grain, and the pattern heating layer comprises: a first line portion provided along the grain of the fiber; And a second line portion extending in the resulting intersecting direction of the fiber.
상기 제2 라인부는 각각 다른 방향으로 연장되어 서로 교차하는 복수의 단위 라인으로 이루어질 수 있다.The second line part may be formed of a plurality of unit lines extending in different directions to cross each other.
상기 제1 라인부와 상기 제2 라인부는 단위 패턴을 이루며, 상기 단위 패턴의 상기 결에 수직한 방향의 길이는 상기 단위 패턴의 상기 결에 평행한 방향의 길이보다 짧을 수 있다.The first line portion and the second line portion form a unit pattern, and a length in a direction perpendicular to the grains of the unit pattern may be shorter than a length in a direction parallel to the grains of the unit pattern.
상기 제1 라인부의 폭은 상기 결 사이의 간격보다 클 수 있다.The width of the first line portion may be greater than the gap between the grains.
상기 섬유의 표면에 제공되며, 작용기를 포함하는 표면개질물질로 이루어진 자가조립단층;을 더 포함하고, 상기 자가조립단층은, 상기 섬유의 표면과 결합되는 헤드 그룹; 및 상기 자가조립단층의 말단에 제공되는 상기 작용기를 포함하며, 상기 헤드 그룹과 연결되는 엔드 그룹을 포함하며, 상기 카본나노튜브의 표면에는 상기 작용기와 이온 결합되는 기능기가 형성될 수 있다.A self-assembled monolayer formed on the surface of the fiber and comprising a surface modifying material including a functional group, wherein the self-assembled monolayer comprises: a head group coupled to the surface of the fiber; And a functional group provided at an end of the self-assembled monolayer, including an end group connected to the head group, and a functional group ion-bonded with the functional group on the surface of the carbon nanotube.
상기 패턴 발열층 상에 제공되며, 전기절연성을 갖는 보호막;을 더 포함할 수 있다.A protective film provided on the pattern heat generating layer and having electrical insulation may be further included.
전기적 신호가 공급되는 단자;를 더 포함하고, 상기 전극은 상기 섬유와 상기 패턴 발열층을 재봉하는 전도성사로 제공될 수 있다.It further comprises a terminal to which an electrical signal is supplied, wherein the electrode may be provided as a conductive yarn for sewing the fiber and the pattern heating layer.
상기 단자는 한 쌍으로 이루어지고, 상기 전극은 상기 단자 각각으로부터 서로 나란하게 연장되어 상기 단자와 상기 패턴 발열층을 전기적으로 연결할 수 있다.The terminals may be formed in a pair, and the electrodes may extend in parallel from each other of the terminals to electrically connect the terminal and the pattern heating layer.
본 발명의 다른 실시예에 따른 발열 섬유 제조방법은 카본나노튜브를 분산매에 분산시키는 과정; 섬유의 일면 상에 상기 카본나노튜브가 상기 분산매에 분산된 분산 용액을 제공하여 오픈부를 형성하는 연속적인 망 구조로 패턴 발열층을 형성하는 과정; 및 상기 패턴 발열층에 전기적으로 연결되는 전극을 형성하는 과정;을 포함할 수 있다.Exothermic fiber manufacturing method according to another embodiment of the present invention comprises the steps of dispersing carbon nanotubes in a dispersion medium; Forming a patterned heating layer in a continuous network structure in which the carbon nanotubes are dispersed in the dispersion medium on one surface of the fiber to form an open portion; And forming an electrode electrically connected to the pattern heating layer.
상기 섬유는 결(grain)을 갖고, 상기 패턴 발열층을 형성하는 과정은, 상기 섬유의 결을 따라 제1 라인부를 형성하는 과정; 및 상기 제1 라인부와 단위 패턴을 이루도록 상기 섬유의 결과 교차하는 방향으로 연장되는 제2 라인부를 형성하는 과정을 포함할 수 있다. The fiber has a grain, and the forming of the pattern heating layer comprises: forming a first line portion along the grain of the fiber; And forming a second line part extending in a direction crossing the result of the fiber to form a unit pattern with the first line part.
상기 패턴 발열층을 형성하는 과정에서는 상기 단위 패턴의 상기 결에 수직한 방향의 길이가 상기 단위 패턴의 상기 결에 평행한 방향의 길이보다 짧게 상기 패턴 발열층을 형성할 수 있다.In the process of forming the pattern heating layer, the pattern heating layer may be formed such that the length of the unit pattern in the direction perpendicular to the grain is shorter than the length of the unit pattern in the direction parallel to the grain of the unit pattern.
상기 제1 라인부를 형성하는 과정에서는 상기 제1 라인부의 폭을 상기 결 사이의 간격보다 크게 형성할 수 있다.In the process of forming the first line portion, the width of the first line portion may be greater than the gap between the grains.
상기 카본나노튜브를 산처리하여 상기 카본나노튜브의 표면에서 적어도 일부의 카본 본딩을 제거하는 과정; 카본 본딩이 제거된 상기 카본나노튜브의 표면에 상기 작용기와 이온 결합되는 기능기를 형성하는 과정; 및 상기 섬유의 표면에 작용기를 포함하는 표면개질물질로 형성되는 자가조립단층을 형성하는 과정;을 더 포함할 수 있다.Acid treatment of the carbon nanotubes to remove at least a portion of the carbon bonding from the surface of the carbon nanotubes; Forming a functional group ionically bonded to the functional group on the surface of the carbon nanotubes from which carbon bonding is removed; And forming a self-assembled monolayer formed of a surface modification material including a functional group on the surface of the fiber.
전기적 신호가 공급되는 단자를 형성하는 과정;을 더 포함하고, 상기 전극을 형성하는 과정은 상기 섬유와 상기 패턴 발열층을 전도성사로 재봉하여 상기 단자와 상기 패턴 발열층을 전기적으로 연결하는 과정을 포함할 수 있다.The method may further include forming a terminal to which an electrical signal is supplied. The forming of the electrode may include stitching the fiber and the pattern heating layer with a conductive yarn to electrically connect the terminal and the pattern heating layer. can do.
상기 패턴 발열층 상에 전기절연성을 갖는 보호막을 형성하는 과정;을 더 포함할 수 있다.The method may further include forming a protective film having electrical insulation on the pattern heating layer.
본 발명의 실시 형태에 따른 발열 섬유는 섬유 상에 카본나노튜브(Carbon NanoTube; CNT)로 패턴 발열층을 형성하여 패턴 발열층이 탄성력을 가질 수 있고, 섬유의 변형 시에도 패턴 발열층의 발열 효율과 복원력을 유지할 수 있다. 또한, 오픈부를 형성하는 연속적인 망 구조로 패턴 발열층을 형성하여 섬유의 결(grain)과 평행 또는 수직 방향으로 변형하는 섬유의 변형(또는 신축)에 따라 패턴 발열층의 각 단위 패턴이 방향성을 갖고 잘 변형될 수 있다. 이에 따라 패턴 발열층의 손상(또는 단선)없이 발열 섬유의 내구성을 향상시킬 수 있다.The heat generating fiber according to the embodiment of the present invention forms a pattern heat generating layer with carbon nanotubes (Carbon NanoTube; CNT) on the fiber so that the pattern heat generating layer may have elastic force, and the heat generating efficiency of the pattern heat generating layer even when the fiber is deformed. And maintain resilience. In addition, each unit pattern of the pattern heating layer is oriented according to the deformation (or stretching) of the fiber deforming in a parallel or vertical direction with the grain of the fiber by forming a pattern heating layer in a continuous network structure forming an open portion. And well deformed. Accordingly, durability of the heat generating fiber can be improved without damaging (or breaking) the pattern heat generating layer.
또한, 섬유의 결을 따라 제1 라인부를 형성하여 섬유의 변형에 따라 변형되면서도 전기전도도를 유지할 수 있는 부분(또는 면적)을 확보할 수 있고, 각 단위 패턴의 결에 수직한 방향의 길이를 각 단위 패턴의 결에 평행한 방향의 길이보다 짧게 하여 결에 수직한 방향으로 신축함으로 인해 저항 변화가 큰 성분을 줄일 수 있다.In addition, the first line portion is formed along the grains of the fiber to secure a portion (or area) capable of maintaining electrical conductivity while being deformed as the fiber is deformed, and each unit has a length perpendicular to the grain of each unit pattern. By shortening the length in the direction parallel to the grain of the pattern and stretching in the direction perpendicular to the grain, a component having a large resistance change can be reduced.
그리고 섬유의 표면에 자가조립단층을 형성하여 표면개질한 후에 패턴 발열층을 형성함으로써, 섬유와 패턴 발열층의 결합력이 향상될 수 있고, 발열 섬유의 내구성이 보다 향상될 수 있다. 또한, 패턴 발열층 상에 보호막을 코팅하여 발열 섬유의 표면을 전기절연시킬 뿐만 아니라 패턴 발열층의 박리를 방지할 수도 있다.And by forming a self-assembled monolayer on the surface of the fiber to form a pattern heating layer after surface modification, the bonding force of the fiber and the pattern heating layer can be improved, the durability of the heating fiber can be further improved. In addition, a protective film may be coated on the pattern heating layer to not only electrically insulate the surface of the heating fiber, but also to prevent peeling of the pattern heating layer.
도 1은 본 발명의 일실시예에 따른 발열 섬유를 나타낸 개략도.
도 2는 본 발명의 일실시예에 따른 섬유의 결 및 단위 패턴을 설명하기 위한 개념도.
도 3은 본 발명의 일실시예에 따른 단위 패턴을 나타내는 개략도.
도 4는 본 발명의 일실시예에 따른 결에 수직한 방향으로 늘어난 섬유와 패턴 발열층을 설명하기 위한 개념도.
도 5는 본 발명의 일실시예에 따른 자가조립단층과 카본나노튜브의 결합을 설명하기 위한 개념도.
도 6은 본 발명의 다른 실시예에 따른 발열 섬유 제조방법을 나타낸 순서도.1 is a schematic view showing a heating fiber according to an embodiment of the present invention.
Figure 2 is a conceptual diagram for explaining the grain and unit pattern of the fiber according to an embodiment of the present invention.
Figure 3 is a schematic diagram showing a unit pattern according to an embodiment of the present invention.
4 is a conceptual view illustrating a fiber and a pattern heating layer elongated in a direction perpendicular to a grain according to an embodiment of the present invention.
5 is a conceptual diagram for explaining the combination of a self-assembled monolayer and carbon nanotubes according to an embodiment of the present invention.
Figure 6 is a flow chart showing a heating fiber manufacturing method according to another embodiment of the present invention.
이하에서는 첨부된 도면을 참조하여 본 발명의 실시예를 더욱 상세히 설명하기로 한다. 그러나 본 발명은 이하에서 개시되는 실시예에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이다. 설명 중, 동일 구성에 대해서는 동일한 참조부호를 부여하도록 하고, 도면은 본 발명의 실시예를 정확히 설명하기 위하여 크기가 부분적으로 과장될 수 있으며, 도면상에서 동일 부호는 동일한 요소를 지칭한다.Hereinafter, with reference to the accompanying drawings will be described an embodiment of the present invention in more detail. However, the present invention is not limited to the embodiments disclosed below, but will be implemented in various forms, and only the embodiments are intended to complete the disclosure of the present invention, and to those skilled in the art to fully understand the scope of the invention. It is provided to inform you. In the description, like reference numerals refer to like elements, and the drawings may be partially exaggerated in size in order to accurately describe embodiments of the present invention, and like reference numerals refer to like elements in the drawings.
도 1은 본 발명의 일실시예에 따른 발열 섬유를 나타낸 개략도로, 도 1(a)는 발열 섬유의 평면도이고, 도 1(b)는 발열 섬유의 단면도이다.1 is a schematic view showing a heating fiber according to an embodiment of the present invention, Figure 1 (a) is a plan view of the heating fiber, Figure 1 (b) is a cross-sectional view of the heating fiber.
도 1을 참조하면, 본 발명의 일실시예에 따른 발열 섬유(100)는 섬유(110); 오픈부(120a)를 형성하는 연속적인 망 구조로 상기 섬유(110)의 일면 상에 제공되며, 카본나노튜브(125)로 이루어진 패턴 발열층(120); 및 상기 패턴 발열층(120)에 전기적으로 연결되는 전극(130);을 포함할 수 있다.1, the
섬유(110)는 사람의 신체에 착용할 수 있는 장갑, 옷 등의 의복 소재일 수 있으며, 천연섬유, 합성섬유 등일 수 있다. 그리고 섬유(110)는 패턴 발열층(120)을 지지할 수 있고, 의류 및 웨어러블 제품에 활용할 수 있다. 또한, 섬유(110)는 사이사이가 뚫려 있으므로, 카본나노튜브(125)는 섬유(110)의 표면에 남아있을 수 있고, 분산매만 섬유(110)를 통과하여 빠져나갈 수 있다. 이에 섬유(110)를 사용하게 되면, 패턴 발열층(120)을 형성하는 데에 진공흡착법을 사용할 수 있으며, 진공흡착법에 대한 자세한 설명은 후술하도록 한다.The
한편, 섬유(110)는 신축성 소재로 이루어질 수 있으며, 답답함과 불편함 없이 착용감이 우수한 발열 섬유(100)를 제공할 수 있다. 또한, 자가조립단층(140)의 헤드 그룹(141)이 섬유(110)의 표면에 잘 결합되도록 섬유(110)는 천연섬유 표면의 수산화기(-OH)를 활용한 천연섬유 복합재료일 수도 있고, 섬유(110)의 표면을 활성화시켜 섬유(110)의 표면에 수산화기를 형성할 수도 있다.On the other hand, the
패턴 발열층(120)은 카본나노튜브(125)로 이루어질 수 있으며, 오픈부(120a)를 형성하는 연속적인 망 구조로 섬유(110)의 일면 상에 제공될 수 있다. 여기서, 카본나노튜브(Carbon NanoTube; CNT, 125)는 탄소원자(C) 6개가 육각형의 모양으로 결합된 판상의 흑연시트가 직경이 수 나노미터에서 수백 나노미터 정도로 이루어진 튜브 형태의 나노소재이다. 또한, 카본나노튜브(125)는 탄성력을 가질 수 있으며, 입자들이 붙어있지 않고 어느 정도 이격 거리가 발생하여도 섬유상 구조와 유사하여 전기가 통하는 전기적 네트 워크 현상을 유지함으로써, 일반 카본의 함량에 비해 매우 적은 함량으로도 동등 이상의 성능을 구현하고 전기적 안정성도 보유할 수 있다. 그리고 패턴 발열층(120)은 탄성력을 갖는 카본나노튜브(125)에 의해 탄성력을 가질 수 있으며, 섬유(110)의 변형(또는 신축)에 따라 변형될 수 있고, 섬유(110)의 변형 시에도 발열 효율과 복원력을 유지할 수 있다. 이때, 패턴 발열층(120)은 표면적의 변화 또는 카본나노튜브(125)의 접촉점 개수의 변화에 의해 적어도 부분적으로 저항이 변화될 수 있다.The
그리고 패턴 발열층(120)은 오픈부(120a)를 형성하는 연속적인 망 구조로 형성될 수 있으며, 이러한 경우에 섬유(110)의 변형에 따라 패턴 발열층(120)의 각 단위 패턴(120b)이 방향성을 갖고 잘 변형될 수 있다. 즉, 오픈부(120a)가 패턴 발열층(120)이 변형될 공간(예를 들어, 상기 패턴 발열층의 라인들이 이동할 공간)을 제공하여 섬유(110)의 변형에 의한 패턴 발열층(120)의 변형에 대해 완충 역할을 할 수 있고, 패턴 발열층(120)의 변형에 따라 각각의 오픈부(120a)의 형상이 변화되면서 패턴 발열층(120)이 전체적으로 안정적이게 변형될 수 있으며, 각각의 오픈부(120a)를 통해 섬유(110)의 변형에 맞추어 각 단위 패턴(120b)마다 부분적으로 변형될 수도 있다. 여기서, 상기 망 구조는 잡아 당기면 늘어나고 놓으면 오므라드는 원리로서, 섬유(110)의 변형에 따라 오픈부(120a)의 크기가 자유롭게 신축할 수 있고, 섬유(110) 상에 패턴 발열층(120)이 형성되는 면적이 줄어들어 패턴 발열층(120)을 형성하는 재료(예를 들어, 상기 카본나노튜브 등)를 절감할 수도 있다. 그리고 오픈부(120a)는 마름모꼴이나 타원형 등으로 이루어질 수 있으며, 이에 한정되지 않고, 수축이 가능한 원리의 모양이면 족하다. 예를 들어, 육각형의 벌집무늬로 패턴 발열층(120)을 형성할 수 있고, 이러한 경우에 늘어나는 방향과 각도가 30 내지 60°로 변화할 수 있어 변형 특성을 최소화할 수 있다. 이에 패턴 발열층(120)의 손상(또는 단선)없이 발열 섬유(100)의 내구성을 향상시킬 수 있으며, 벌집무늬의 경우에 발열 섬유(100)의 내구성 및 발열 균일성을 최대화할 수 있다.In addition, the
한편, 신축성 소재로 이루어진 섬유(110)와 탄성력을 갖는 패턴 발열층(120)을 통해 답답함과 불편함 없이 착용감이 우수한 발열 섬유(100)를 제공할 수도 있다. 그리고 패턴 발열층(120)의 두께는 5 내지 300 ㎛일 수 있으며, 300 ㎛보다 두꺼운 경우에는 패턴 발열층(120) 및/또는 섬유(110)가 잘 신축되지 않거나 구부러지지 않아 패턴 발열층(120)에 크랙(crack)이 발생하여 절단되거나 파손될 수 있고, 5 ㎛보다 얇은 경우에는 패턴 발열층(120)이 너무 얇아 충분한 열량이 발생되지 않을 뿐만 아니라 충분한 인장력을 가질 수 없어 패턴 발열층(120)이 신축하면서 절단되거나 파손될 수 있다.On the other hand, through the
전극(130)은 패턴 발열층(120)에 전기적으로 연결될 수 있으며, 패턴 발열층(120)의 양쪽 끝단에 형성될 수 있다. 전극(130)을 통해 패턴 발열층(120)에 전류를 흘려주어 패턴 발열층(120)을 전기 발열(또는 저항 발열)시킬 수 있다.The
도 2는 본 발명의 일실시예에 따른 섬유의 결 및 단위 패턴을 설명하기 위한 개념도로, 도 2(a)는 섬유의 결을 나타내고, 도 2(b)는 단위 패턴을 나타낸다.FIG. 2 is a conceptual view illustrating a fiber grain and a unit pattern according to an embodiment of the present invention. FIG. 2 (a) shows a grain of fiber and FIG. 2 (b) shows a unit pattern.
도 2를 참조하면, 섬유(110)는 결(grain, 111)을 가질 수 있으며, 섬유(110)마다 다른 특성의 결(111)을 가질 수 있고, 그 결(111)에 따라 늘어나는 길이 대비 저항의 변화량이 달라 패턴 발열층(120)의 저항 변화 시 방향성을 부가해줄 수 있다. 여기서, 섬유(110)는 섬유(110)의 결(111)에 평행한 방향(11) 또는 수직한 방향(12)으로 신축(또는 변형)될 수 있다. 또한, 섬유(110)의 결(111)은 카본나노튜브(125)가 흡착되는 흡착면을 제공할 수 있으며, 패턴 발열층(120)을 이루는 대부분의 카본나노튜브(125)가 결(111)에 흡착될 수 있다.Referring to FIG. 2, the
그리고 패턴 발열층(120)은 섬유(110)의 결(111)을 따라 제공되는 제1 라인부(121); 및 섬유(110)의 결(111)과 교차하는 방향으로 연장되는 제2 라인부(122)를 포함할 수 있다. 제1 라인부(121)는 섬유(110)의 결(111)을 따라 제공될 수 있으며, 섬유(110)의 결(111)을 따라 신축할 수 있어 신축에 따른 저항 변화가 작을 수 있다. 카본나노튜브(125)는 머리카락 구조로 되어 서로 엉켜 있는 구조이며, 분자 구조상 부분 단락이 발생하여도 연결되어 있는 접촉점이 많아 쇼트나 화재의 위험성이 없고, 장기간 사용에 따른 내구성이 뛰어나다. 이러한 카본나노튜브(125)는 제1 라인부(121)가 늘어남에 따라 서로 엉켜 있던 입자들이 풀리거나 서로 떨어질 수 있으며, 이에 따라 카본나노튜브(125)의 접촉점의 개수가 변할 수 있고, 카본나노튜브(125)의 접촉점 개수의 변화에 의해 제1 라인부(121)의 저항이 변화할 수 있다. 제1 라인부(121)는 대부분의 카본나노튜브(125)가 흡착 고정된 섬유(110)의 결(111)을 따라 신축됨으로써, 제1 라인부(121)가 늘어나더라도 섬유(110)의 결(111)을 따라 촘촘히 제공된 카본나노튜브(125)에 의해 입자들 간의 연결이 대부분 유지될 수 있고, 이에 따라 카본나노튜브(125)의 접촉점 개수의 변화가 적어 신축에 따른 저항 변화가 작을 수 있다.The
제2 라인부(122)는 섬유(110)의 결(111)과 교차하는 방향으로 연장될 수 있으며, 제1 라인부(121) 간을 연결할 수 있고, 제1 라인부(121)와 단위 패턴(120b)을 이룰 수 있다. 그리고 제2 라인부(122)는 섬유(110)의 결(111)과 교차하는 방향으로 신축하게 되어 신축에 따른 저항 변화가 클 수 있다. 제2 라인부(122)를 이루는 카본나노튜브(125)는 제2 라인부(122)가 늘어남에 따라 서로 엉켜 있던 입자들이 떨어져 어느 정도 이격 거리가 발생할 수 있으며, 이에 따라 카본나노튜브(125)의 접촉점의 개수가 변할 수 있고, 카본나노튜브(125)의 접촉점 개수의 변화에 의해 제2 라인부(122)의 저항이 변화할 수 있다. 제2 라인부(122)는 섬유(110)의 결(111)과 교차하는 방향으로 신축됨으로써, 제2 라인부(122)가 늘어남에 따라 대부분의 카본나노튜브(125)가 흡착 고정된 섬유(110)의 결(111)들이 분리되고, 결(111)들 간에 서로 엉켜 있던 입자들이 떨어져 입자들 간의 연결이 대부분 끊어질 수 있으며, 이에 따라 카본나노튜브(125)의 접촉점 개수의 변화가 많게 되어 신축에 따른 저항 변화가 클 수 있다.The
도 3은 본 발명의 일실시예에 따른 단위 패턴을 나타내는 개략도로, 도 3(a)는 벌집 구조의 단위 패턴을 나타내고, 도 3(b)는 격자 구조의 단위 패턴을 나타낸다.3 is a schematic diagram illustrating a unit pattern according to an embodiment of the present invention. FIG. 3 (a) shows a unit pattern of a honeycomb structure, and FIG. 3 (b) shows a unit pattern of a lattice structure.
도 3을 참조하면, 제2 라인부(122)는 각각 다른 방향으로 연장되어 서로 교차하는 복수의 단위 라인(122a,122b)으로 이루어질 수 있으며, 각각 다른 방향으로 연장되는 복수의 단위 라인(122a,122b)이 서로 교차하여(또는 연결되어) 제1 라인부(121) 간을 연결할 수 있다. 여기서, 각각 다른 방향은 모두 섬유(110)의 결(111)과 교차하는 방향일 수 있고, 상기 교차하는 방향은 수직으로 교차하는 것뿐만 아니라 평행하지 않고 비스듬한(또는 엇갈리는) 방향을 모두 포함할 수 있다. 이를 통해 제1 라인부(121)와 수직으로 교차하여 형성되는 사각형의 격자 구조뿐만 아니라 육각형의 벌집 구조 등의 다양한 단위 패턴(120b)을 형성할 수 있다.Referring to FIG. 3, the
그리고 제1 라인부(121)와 제2 라인부(122)는 단위 패턴을 이룰 수 있다. 제1 라인부(121)와 제2 라인부(122)는 서로 연결되어 단위 패턴(120b)을 이룰 수 있고, 단위 패턴(120b)이 서로 연결되어 연속적인 망 구조를 형성할 수 있다.The
도 4는 본 발명의 일실시예에 따른 결에 수직한 방향으로 늘어난 섬유와 패턴 발열층을 설명하기 위한 개념도로, 도 4(a)는 늘어나기 전을 나타내고, 도 4(b)는 늘어난 후를 나타낸다.4 is a conceptual diagram illustrating a fiber and a pattern heating layer extending in a direction perpendicular to a grain according to an embodiment of the present invention. FIG. 4 (a) shows before stretching, and FIG. 4 (b) shows stretching. Indicates.
도 2 내지 도 4를 참조하면, 단위 패턴(120b)의 결(111)에 수직한 방향(12)의 길이(V)는 단위 패턴(120b)의 결(111)에 평행한 방향(11)의 길이(P)보다 짧을 수 있다. 패턴 발열층(120)이 결(111)에 평행한 방향(11)으로 신축하는 경우에는 섬유(110)의 결(111)을 따라 신축할 수 있어 신축에 따른 저항 변화가 작을 수 있다. 패턴 발열층(120)이 결(111)에 평행한 방향(11)으로 늘어나는 경우, 패턴 발열층(120)이 늘어나더라도 섬유(110)의 결(111)을 따라 촘촘히 제공된 카본나노튜브(125)에 의해 입자들 간의 연결이 대부분 유지될 수 있고, 이에 따라 카본나노튜브(125)의 접촉점 개수의 변화가 적어 신축에 따른 저항 변화가 작을 수 있다.2 to 4, the length V of the
반면에, 패턴 발열층(120)이 결(111)에 수직한 방향(12)으로 신축하는 경우에는 섬유(110)의 결(111)들 사이가 붙었다 떨어졌다 하게 되므로, 신축에 따른 저항 변화가 클 수 있다. 즉, 섬유(110)의 결(111)들이 붙어 있을 때와 섬유(110)의 결(111)들 사이가 떨어져 있을 때에 카본나노튜브(125)의 접촉점 개수의 차이가 많이 나게 되며, 이로 인해 신축에 따른 저항 변화가 크게 된다. 패턴 발열층(120)이 결(111)에 수직한 방향(12)으로 늘어나는 경우, 대부분의 카본나노튜브(125)가 흡착 고정된 섬유(110)의 결(111)들 사이가 벌어지게 되고 패턴 발열층(120)이 섬유(110)의 결(111)들 사이의 공간에서 신축하면서 결(111)들 간에 서로 엉켜 있던 입자들이 떨어져 입자들 간의 연결이 대부분 끊어질 수 있으며, 이에 따라 카본나노튜브(125)의 접촉점 개수의 변화가 많게 되어 신축에 따른 저항 변화가 클 수 있다.On the other hand, when the
이에 단위 패턴(120b)의 결(111)에 수직한 방향(12)의 길이(V)를 단위 패턴(120b)의 결(111)에 평행한 방향(11)의 길이(P)보다 짧게 함으로써, 패턴 발열층(120)에서 결(111)에 수직한 방향(12)으로 신축하여(또는 신축함으로 인해) 저항 변화가 큰 성분(또는 부분)을 결(111)에 평행한 방향(11)으로 신축하여 저항 변화가 작은 성분보다 줄일 수 있다. 이를 통해 패턴 발열층(120)이 신축하더라도 패턴 발열층(120)의 저항 변화를 줄일 수 있고, 패턴 발열층(120)의 영역별 저항 변화에 따라 영역별로 발생하는 열효율 차이도 억제 또는 방지할 수 있다.Accordingly, by making the length V of the
그리고 제1 라인부(121)의 폭은 결(111) 사이의 간격보다 클 수 있다. 제1 라인부(121)의 폭이 섬유(110)의 결(111) 사이의 간격(또는 상기 결 간의 거리)보다 작게 되면, 패턴 발열층(120)이 섬유(110)의 결(111) 사이에만 형성되고, 섬유(110)의 결(111)에는 형성되지 않을 수 있다. 이러한 경우, 패턴 발열층(120)의 저항 변화 시 방향성을 부가해줄 수 없고, 안정적인 카본나노튜브(125)의 흡착면을 제공하는 결(111)에 카본나노튜브(125)가 흡착되지 않아 패턴 발열층(120)이 섬유(110) 상에 안정적으로 고정될 수 없으며, 패턴 발열층(120)의 신축에 의한 저항 변화를 예측 및/또는 제어할 수 없다.The width of the
하지만, 제1 라인부(121)의 폭이 결(111) 사이의 간격보다 큰 경우에는 적어도 부분적으로 섬유(110)의 결(111)에 흡착되는 카본나노튜브(125)가 생기게 되고, 패턴 발열층(120)이 섬유(110) 상에 안정적으로 고정될 수 있다. 또한, 패턴 발열층(120)의 저항 변화 시 방향성을 부가해줄 수 있어 패턴 발열층(120)의 신축에 의한 저항 변화를 예측 및/또는 제어할 수 있다.However, when the width of the
한편, 제1 라인부(121)는 적어도 하나 이상의 결(111)에 걸쳐서 형성될 수 있으며, 제1 라인부(121)의 중앙 라인(또는 중앙부)을 중심으로 결(111)이 대칭되어 배치될 수 있고, 제1 라인부(121)의 중앙 라인에 결(111)이 위치할 수 있다. 이를 통해 제1 라인부(121)가 섬유(110) 상에 안정적으로 고정될 수 있으면서 섬유(110)의 변형에 따라 방향성을 갖고 잘 변형되도록 할 수 있다. 그리고 제2 라인부(122)의 폭도 결(111) 사이의 간격보다 클 수 있다. 제1 라인부(121)와 제2 라인부(122)의 균일한 발열을 위해 제2 라인부(122)의 폭은 제1 라인부(121)의 폭과 동일할 수 있고, 결(111) 사이의 간격보다 클 수 있다. 또한, 결(111)에 흡착되는 카본나노튜브(125)의 수(또는 면적)가 많아져(또는 넓어져) 제2 라인부(122)가 안정적으로 고정될 수 있고, 패턴 발열층(120)이 섬유(110) 상에 보다 안정적으로 고정될 수 있다.Meanwhile, the
도 5는 본 발명의 일실시예에 따른 자가조립단층과 카본나노튜브의 결합을 설명하기 위한 개념도로, 도 5(a)는 섬유 상에 형성된 자가조립단층의 개념도이며, 도 5(b)는 카본나노튜브의 표면에 수산화기가 형성되는 개념도이고, 도 5(c)는 자가조립단층과 카본나노튜브의 결합 개념도이다.FIG. 5 is a conceptual view illustrating the bonding of a self-assembled monolayer and carbon nanotubes according to an embodiment of the present invention. FIG. 5 (a) is a conceptual view of a self-assembled monolayer formed on a fiber. A conceptual diagram of forming a hydroxyl group on the surface of the carbon nanotubes, Figure 5 (c) is a conceptual diagram of the coupling between the self-assembled monolayer and the carbon nanotubes.
도 5를 참조하면, 본 발명에 따른 발열 섬유(100)는 섬유(110)의 표면에 제공되며, 작용기를 포함하는 표면개질물질로 이루어진 자가조립단층(140);을 더 포함할 수 있다. 자가조립단층(Self-Assembled Monolayer; SAM, 140)은 작용기를 포함하는 표면개질물질로 형성될 수 있고, 섬유(110)의 표면에 제공될 수 있다. 섬유(110)의 표면에 자가조립단층(140)을 형성하여 섬유(110)를 표면처리하면, 섬유(110)와 패턴 발열층(120)의 사이에 개재되는 자가조립단층(140)에 의해 섬유(110)와 패턴 발열층(120)의 결합력이 향상되어 섬유(110) 상에 패턴 발열층(120)이 잘 형성될 수 있다.Referring to FIG. 5, the
그리고 자가조립단층(140)은 섬유(110)의 표면과 결합되는 헤드 그룹(141); 및 자가조립단층(140)의 말단에 제공되는 상기 작용기를 포함하며, 헤드 그룹(141)과 연결되는 엔드 그룹(142)을 포함할 수 있다. 헤드 그룹(141)은 섬유(110)의 표면과 결합할 수 있고, 섬유(110)의 종류에 따라 선택할 수 있으며, 일반적으로 실리콘 원자(Si)를 포함하는 물질(예를 들어, 실란계)이 선택될 수 있다.And the self-assembled
엔드 그룹(142)은 자가조립단층(140)의 말단에 기능성을 부여할 수 있는 상기 작용기를 포함할 수 있고, 헤드 그룹(141)과 연결될 수 있으며, 상기 작용기는 이후 반응이 될 부분(즉, 어떤 물질을 붙일 것이냐)에 따라 다양한 작용기 중에서 선택될 수 있다.The
또한, 자가조립단층(140)은 헤드 그룹(141)과 엔드 그룹(142)을 연결하는 백본(backbone, 143)을 더 포함할 수 있다. 백본(143)은 주로 알킬 사슬로 구성될 수 있고, 하이드로 카본 체인이나 플로 카본 체인들일 수 있다.In addition, the self-assembled
상기 작용기는 아민기(-NH), 아미노기(-NH2), 티올기(-SH), 카르복실기(-COOH), 포르밀기(-CHO), 시아나토기(-OCN), 실라놀기(Si-OH), 포스핀기(-PO2H2), 포스폰기(-PO3H2), 술폰기(-SO3H), 에폭시기 중에서 선택된 적어도 어느 하나일 수 있다. 상기 작용기를 통해 섬유(110)의 표면을 (+)로 대전시켜 섬유(110)의 표면에 정전기력을 부과할 수 있고, 카본나노튜브(125)의 표면에 수산화기(-OH)를 형성하는 경우에는 상기 작용기와 수산화기가 이온 결합할 수 있다. 이에 따라 섬유(110)와 패턴 발열층(120)의 결합력(즉, 상기 자가조립단층과 상기 패턴 발열층의 결합력)을 향상시킬 수 있다.The functional group is an amine group (-NH), amino group (-NH 2 ), thiol group (-SH), carboxyl group (-COOH), formyl group (-CHO), cyanato group (-OCN), silanol group (Si- OH), a phosphine group (-PO 2 H 2 ), a phosphone group (-PO 3 H 2 ), a sulfone group (-SO 3 H), may be at least one selected from an epoxy group. In the case of forming a hydroxyl group (-OH) on the surface of the
섬유(110)에 자가조립단층(140)을 형성하는 경우에는 섬유(110)의 표면에 결합되는 헤드 그룹(141)으로 실란계가 선택될 수 있으며, 자가조립단층(140)을 형성하는 표면개질물질은 아민기(-NH), 아미노기(-NH2), 티올기(-SH), 카르복실기(-COOH), 포르밀기(-CHO), 시아나토기(-OCN), 실라놀기(Si-OH), 포스핀기(-PO2H2), 포스폰기(-PO3H2), 술폰기(-SO3H), 에폭시기 중 선택된 적어도 어느 하나의 작용기를 포함하는 실란계 물질일 수 있고, 아미노실란(Aminosilane), 3-아미노프로필트리에톡시실란(3-aminopropyltriethoxysilane; APTES) 등일 수 있다. 상기 실란계 물질은 고분자 및 무기물을 연결할 수 있는 기를 동시에 갖고 있으므로, 섬유(110)와 잘 결합할 수 있으며, 유리섬유와 유사하게 천연섬유 표면의 수산화기(-OH)를 활용하는 경우에는 실란계 물질에 포함된 실리콘(Si)이 섬유(110) 표면의 수산화기와 이온 결합하여 헤드 그룹(141)이 섬유(110)의 표면에 잘 결합될 수 있다. 따라서, 표면개질물질로 실란계 물질을 사용하는 경우에는 헤드 그룹(141)이 섬유(110)의 표면에 잘 결합될 수 있어 섬유(110)의 표면에 자가조립단층(140)이 잘 형성될 수 있다. 또한, 실란계 물질을 사용하면, 표면개질물질의 이온들을 일정한 방향으로 섬유(110)의 표면에 유도시킬 수 있고, 섬유(110)의 표면을 대전시켜 섬유(110)의 표면에 정전기력을 부과할 수 있다.When the self-assembled
카본나노튜브(125)의 표면에는 상기 작용기와 이온 결합되는 기능기가 형성될 수 있다. 카본나노튜브(125)를 산처리하면, 카본나노튜브(125)의 표면에서 적어도 일부의 카본 본딩이 끊어질 수 있고, 카본 본딩이 끊어진 자리(예를 들어, 상기 카본나노튜브의 말단)에 상기 기능기가 형성될 수 있다. 예를 들어, 카본나노튜브(125)의 표면에는 수산화기(-OH)가 형성될 수 있으며, 카본나노튜브(125)의 표면에서 적어도 일부의 카본 본딩이 끊어지고, 카본 본딩이 끊어진 자리에 수산화기가 형성될 수 있다. 카본나노튜브(125)의 표면에 수산화기가 형성되면, 카본나노튜브(125)의 수산화기와 자가조립단층(140)의 작용기가 이온 결합함으로써, 패턴 발열층(120)이 섬유(110) 상에 잘 흡착될 수 있다.On the surface of the
여기서, 카본나노튜브(125)의 수산화기(-OH)와 자가조립단층(140)의 작용기는 서로 이온 결합할 수 있으며, 카본나노튜브(125)의 수산화기가 엔드 그룹(142)의 작용기와 이온 결합하여 패턴 발열층(120)이 형성될 수 있다. 예를 들어, 카본나노튜브(125)의 표면에 형성된 수산화(OH-)기와 엔드 그룹(142)의 아민(NH+)기가 이온 결합할 수 있다. 이에 따라 섬유(110)와 패턴 발열층(120)이 더욱 강한 에너지로 결합하게 되어 섬유(110)와 패턴 발열층(120)의 결합력이 향상될 수 있으며, 신축에 따른 패턴 발열층(120)의 박리가 억제 또는 방지될 수 있고, 발열 섬유(100)의 내구성이 향상될 수 있다.Here, the hydroxyl group (-OH) of the
한편, 카본나노튜브(125)를 산처리하여 표면처리함으로써, 카본나노튜브(125)의 표면에 수산화기(-OH)를 형성할 수 있다. 산처리에 의해 카본나노튜브(125)의 표면에 불포화 결합(dangling bond)을 형성시켜 수산화기(-OH)가 카본나노튜브(125)의 표면에 형성되도록 할 수 있다.On the other hand, by acid treatment of the
그리고 패턴 발열층(120)은 진공흡착법으로 섬유(110) 상에 형성될 수 있다. 섬유(110)의 타면에 진공압을 형성하여 카본나노튜브(125)를 섬유(110)의 일면에서 타면 방향으로 흡착시키는 진공흡착법에 의해 패턴 발열층(120)을 섬유(110)의 일면 상에 형성할 경우, 강한 진공압에 의한 흡착 에너지에 의해 섬유(110) 내부까지 카본나노튜브(125)가 침투할 수 있고, 패턴 발열층(120)이 섬유(110) 상에 효과적으로 흡착될 수 있다.The
본 발명에 따른 발열 섬유(100)는 패턴 발열층(120) 상에 제공되며, 전기절연성을 갖는 보호막(미도시);을 더 포함할 수 있다. 보호막(미도시)은 패턴 발열층(120) 상에 제공될 수 있으며, 패턴 발열층(120)을 보호할 수 있고, 전기절연성을 가져 전류(또는 전기)가 흐르는 패턴 발열층(120)을 전기절연시킬 수 있다. 또한, 상기 보호막(미도시)은 패턴 발열층(120)에서 발생되는 열이 원활히 외부로 전달되도록 하기 위해 열전도성을 가질 수 있으며, 열전도성이 우수한 재질로 이루어질 수 있다. 여기서, 상기 보호막(미도시)은 효과적인 열전도를 위해 그래파이트, 카본나노튜브(CNT) 등으로 구성된 군으로부터 선택되는 어느 하나 이상을 포함할 수도 있다.The
예를 들어, 상기 보호막(미도시)은 연성의 재질로 이루어질 수 있고, 패턴 발열층(120) 상에 코팅될 수 있다. 섬유(110)의 과도한 변형(예를 들어, 잦은 변형, 상기 패턴 발열층의 탄성한계 이상의 변형 등) 또는 급격한 변형으로 인해 패턴 발열층(120)이 박리될 수 있는데, 섬유(110)의 변형에 따라 신축 가능한 연성의 보호막(미도시)을 통해 패턴 발열층(120)의 박리를 방지할 수 있고, 섬유(110)의 변형에 따른 표면적 변화로 인한 패턴 발열층(120)의 응력(stress)을 완화시켜 줄 수 있다. 상기 보호막(미도시)은 수지(resin)로 이루어질 수 있으며, 이에 특별히 한정되지 않고, 섬유(110)의 변형에 따라 신축이 될 수 있도록 탄성력이 우수한 연성의 소재이면 족하다. 예를 들어, 상기 보호막(미도시)은 폴리에틸렌(PolyEthylene; PE), 폴리염화비닐(PolyVinyl Chloride; PVC), 폴리우레탄(PolyUrethane; PU), 열가소성폴리우레탄(Thermoplastic Poly Urethane; TPU), 폴리에틸렌테레프탈레이트(PolyEthylene Terephthalate; PET), 실리콘(silicone) 및 폴리테트라플루오로에틸렌(PolyTetraFluoroEthylene; PTFE) 중 어느 하나 이상으로 코팅(또는 접착)되어 형성될 수 있다.For example, the passivation layer (not shown) may be made of a flexible material, and may be coated on the
한편, 본 발명의 발열 섬유(100)는 섬유(110)의 일면과 대향하는 타면 상에 제공되는 단열층(미도시);을 더 포함할 수 있다. 단열층(미도시)은 섬유(110)의 타면 상에 형성될 수 있으며, 패턴 발열층(120)에서 발생되는 열이 섬유(110)를 통해 외부로 손실되지 않도록 단열시킬 수 있고, 패턴 발열층(120)에서 발생되는 열이 섬유(110)와 반대 방향(예를 들어, 상기 보호막 방향)으로만 전달되도록 할 수 있다. 이를 통해 발열 섬유(100)의 착용자에게 패턴 발열층(120)에서 발생되는 열이 효과적으로 전달될 수 있다. 이때, 상기 단열층(미도시)은 에어로겔(aerogel), 유리솜, 석영솜, 글라스울, 코르크 및 발포 플라스틱으로 구성된 군으로부터 선택되는 어느 하나 이상을 포함할 수 있다.On the other hand, the
그리고 본 발명에 따른 발열 섬유(100)는 전기적 신호가 공급되는 단자(150);를 포함할 수 있고, 전극(130)은 섬유(110)와 패턴 발열층(120)을 재봉하는 전도성사로 제공될 수 있다. 단자(150)는 배터리 등의 외부 전원이 연결되어 전기적 신호가 공급될 수 있고, 공급되는 전기적 신호를 전극(130)으로 전달할 수 있다.The
전극(130)은 은(Ag)사(絲), 금(Au)사 등의 전도성사로 섬유(110)에 재봉(또는 바느질)하여 형성될 수 있으며, 단자(150)와 패턴 발열층(120)을 전기적으로 연결할 수 있고, 단자(150)로부터 전달되는 전기적 신호를 패턴 발열층(120)에 전달할 수 있다. 이러한 경우, 단락되는 부분없이 패턴 발열층(120) 전체에 전기적 신호(예를 들어, 전류)가 제공될 수 있을 뿐만 아니라 패턴 발열층(120) 전체에 균일하게 전기적 신호를 제공할 수 있고, 간단하게 전극(130)을 형성할 수 있다. 또한, 상기 보호막(미도시)을 형성한 후에도 별도의 식각(etching) 공정없이 전극(130)을 형성할 수도 있다. 그리고 전도성사로 섬유(110)와 패턴 발열층(120)을 함께 재봉하면, 간단하게 전극(130)을 형성할 수 있을 뿐만 아니라 섬유(110)와 패턴 발열층(120)을 단단히 결합(또는 고정)시킬 수 있다.The
단자(150)는 한 쌍으로 이루어질 수 있으며, 전극(130)은 단자(150)에 대응되어 한 쌍으로 이루어질 수 있고, 단자(150) 각각으로부터 서로 나란하게 연장되어 단자(150)와 패턴 발열층(120)을 전기적으로 연결할 수 있다. 이때, 전극(130)은 패턴 발열층(120)의 양단에 제공될 수 있고, 단자(150)에 공급되는 전기적 신호가 패턴 발열층(120) 전체에 효과적으로 분산(또는 전달)될 수 있다.The
또한, 전극(130)은 버스 전극(bus electrode)으로 형성될 수 있으며, 단자(150)로 공급되는 전기적 신호가 단자(150)에 연결되는 전극(130)의 일단부터 반대쪽의 타단까지 빠르게 전달될 수 있고, 패턴 발열층(120)의 양단에서 패턴 발열층(120)의 전체에 빠르게 퍼질(또는 분산될) 수 있다. 이를 통해 패턴 발열층(120)이 전체적으로 균일한 발열을 할 수 있다. 여기서, 상기 버스 전극은 전극의 전체 저항을 줄이기 위해 일정 방향(예를 들어, 수직 방향)을 따라서 직접 연결된 높은 전도율을 가진 전극을 의미한다.In addition, the
한편, 전극(130)은 섬유(110)의 결(111)에 수직한 방향(12)으로 나란하게 연장되어 형성될 수 있다. 이러한 경우, 단자(150)로 공급된 전기적 신호가 결(111)에 수직한 방향(12)으로 전극(130)을 통해 빠르게 전달되고, 패턴 발열층(120)의 양단에서 섬유(110)의 결(111)을 따라 결(111)에 평행한 방향(11)으로 패턴 발열층(120)의 전체에 빠르게 퍼질 수 있다. 또한, 전극(130)은 은(Ag) 등의 금속 페이스트(metal paste)를 섬유(110) 상에 코팅하여 높은 전기전도율을 갖도록 형성할 수도 있다.On the other hand, the
발열 섬유(100)의 발열 테스트로 인장 전의 발열, 인장된 후의 발열 및 5,200 회 인장 후의 발열 효율을 측정하였는데, 발열 섬유(100)가 인장되어 신축 후에도 큰 온도 변화 및 발열효율의 변화없이 안정적으로 발열하는 것을 확인할 수 있었다. 약 15 % 인장 및 5,200 회 신축 테스트 결과, 발열 섬유(100)는 초기 신축 후에 약 20 ℃의 변화가 있었으나, 추가 신축 후에는 10 ℃ 내외의 변화만 있었으며, 신축 후에도 70 ℃ 이상의 온도를 유지하였다. 19개 지점의 평균 온도에 대한 발열효율을 계산하면, 초기에는 10.3 ℃/W의 발열효율을 나타냈으며, 5,200 회 신축 후에는 9.5 ℃/W의 발열효율을 나타내어 7.7 %의 변화율(또는 감소율)을 보였다. 한편, 섬유의 면 전체에 발열층을 형성하는 경우에는 초기의 발열효율도 낮을 뿐만 아니라 신축 후에는 더 큰 감소율을 보였다. 따라서, 본 발명의 발열 섬유(100)는 인장되어 신축 후에도 큰 온도 변화 및 발열효율의 변화없이 안정적으로 발열할 수 있으며, 내구성이 향상되었다.The exothermic test of the
도 6은 본 발명의 다른 실시예에 따른 발열 섬유 제조방법을 나타낸 순서도이다.6 is a flow chart showing a heating fiber manufacturing method according to another embodiment of the present invention.
도 6을 참조하여 본 발명의 다른 실시예에 따른 발열 섬유 제조방법을 보다 상세히 살펴보는데, 본 발명의 일실시예에 따른 발열 섬유와 관련하여 앞서 설명된 부분과 중복되는 사항들은 생략하도록 한다.With reference to Figure 6 looks at in more detail the method for producing a heating fiber according to another embodiment of the present invention, the matters overlapping with the above-described portion with respect to the heating fiber according to an embodiment of the present invention will be omitted.
본 발명의 다른 실시예에 따른 발열 섬유 제조방법은 카본나노튜브를 분산매에 분산시키는 과정(S100); 섬유의 일면 상에 상기 카본나노튜브가 상기 분산매에 분산된 분산 용액을 제공하여 오픈부를 형성하는 연속적인 망 구조로 패턴 발열층을 형성하는 과정(S200); 및 상기 패턴 발열층에 전기적으로 연결되는 전극을 형성하는 과정(S300);을 포함할 수 있다.Heat generating fiber manufacturing method according to another embodiment of the present invention is a step of dispersing carbon nanotubes in a dispersion medium (S100); Forming a pattern heating layer in a continuous network structure in which the carbon nanotubes are dispersed in the dispersion medium on one surface of the fiber to form an open part (S200); And forming an electrode electrically connected to the pattern heating layer (S300).
먼저, 카본나노튜브를 분산매에 분산시킨다(S100). 카본나노튜브를 분산매에 균일하게 분산시킬 수 있으며, 상기 카본나노튜브를 상기 분산매에 넣고 초음파에 의한 분산법 또는 교반(Stirring)법을 이용하여 균일하게 분산시킬 수 있다. 여기서, 표면에 수산화기가 형성된 카본나노튜브를 분산시킬 수도 있고, 표면에서 적어도 일부의 카본 본딩이 제거된 카본나노튜브를 상기 분산매로 사용하는 초순수에 넣고 상기 카본 본딩이 제거된 카본나노튜브의 표면에 수산화기를 형성할 수도 있다. 표면에서 적어도 일부의 카본 본딩이 제거된 카본나노튜브를 초순수에 넣는 경우에는 상기 카본 본딩이 제거된 카본나노튜브 표면의 불포화 결합으로 인해 물 분자와의 인력이 증가하고 카본 본딩이 제거된 자리에 수산화기가 형성되어 상기 카본 본딩이 제거된 카본나노튜브의 표면이 (-)로 대전되면서 상기 카본 본딩이 제거된 카본나노튜브의 표면에 정전기력을 부과할 수 있다. 그리고 상기 분산매는 초순수(DI water) 등일 수 있으나, 이에 특별히 한정되지 않으며, 상기 카본나노튜브가 용해되지 않고 상기 카본나노튜브에 영향을 주지 않는 액체이면 족하다.First, the carbon nanotubes are dispersed in a dispersion medium (S100). The carbon nanotubes may be uniformly dispersed in the dispersion medium, and the carbon nanotubes may be uniformly dispersed using the ultrasonic dispersion method or the stirring method. Here, the carbon nanotubes having a hydroxyl group formed on the surface may be dispersed, and the carbon nanotubes having at least a portion of the carbon bonding removed from the surface may be placed in ultrapure water used as the dispersion medium, on the surface of the carbon nanotubes from which the carbon bonding is removed. A hydroxyl group can also be formed. When carbon nanotubes from which at least a portion of carbon bonding has been removed from the surface are put into ultrapure water, an unsaturation bond on the surface of the carbon nanotubes from which the carbon bonding has been removed increases the attraction to water molecules and the hydroxyl group in the position where the carbon bonding is removed. When the surface of the carbon nanotubes from which the carbon bonding is removed is charged with (−), electrostatic force may be applied to the surface of the carbon nanotubes from which the carbon bonding is removed. The dispersion medium may be ultrapure water (DI water) or the like, but is not particularly limited thereto. The dispersion medium may be a liquid in which the carbon nanotubes are not dissolved and do not affect the carbon nanotubes.
예를 들어, 초순수(예를 들어, 1 ℓ)에 상기 카본나노튜브(예를 들어, 30 ㎎)를 넣고, 18 내지 30 시간 교반시키면서 분산 공정을 수행할 수 있다.For example, the carbon nanotube (for example, 30 mg) is added to ultrapure water (for example, 1 L), and the dispersion process may be performed while stirring for 18 to 30 hours.
상기 카본나노튜브의 표면이 수산화기에 의해 (-)로 대전되면, 상기 카본나노튜브의 표면에 정전기력이 부과되는데, 이로 인해 상기 카본나노튜브의 침전 현상이나 상기 카본나노튜브가 서로 뭉치는 현상이 발생하지 않고 상기 카본나노튜브가 상기 분산매에 균일하게 분산되어 안정된 분산 용액을 얻을 수 있다. 이에 섬유 상의 패턴 발열층의 균일성과 신뢰성이 향상된 본 발명의 발열 섬유를 제조할 수 있다.When the surface of the carbon nanotubes is charged with (-) by a hydroxyl group, an electrostatic force is applied to the surface of the carbon nanotubes, which causes precipitation of the carbon nanotubes or a phenomenon in which the carbon nanotubes agglomerate with each other. The carbon nanotubes are uniformly dispersed in the dispersion medium, thereby obtaining a stable dispersion solution. Accordingly, it is possible to manufacture the exothermic fiber of the present invention with improved uniformity and reliability of the pattern exothermic layer on the fiber.
다음으로, 섬유의 일면 상에 상기 카본나노튜브가 상기 분산매에 분산된 분산 용액을 제공하여 오픈부를 형성하는 연속적인 망 구조로 패턴 발열층을 형성한다(S200). 패턴 발열층은 진공흡착법 또는 스크린 프린팅(screen printing)법 등을 이용하여 섬유의 일면 상에 후막 코팅하여 형성될 수 있으며, 실크 스크린(또는 마스크) 등을 통해 연속적인 망 구조로 패턴을 형성할 수 있다. 예를 들어, 상기 카본나노튜브의 분산 용액(또는 상기 카본나노튜브 페이스트)을 섬유의 일면에서 타면으로 흘려보내면서 상기 섬유의 일면 상에 제공하면, 상기 분산매는 상기 섬유를 통과하여 밑으로 빠져나오고, 상기 카본나노튜브만 상기 섬유 상에 남게(또는 걸러지게) 된다. 여기서, 상기 카본나노튜브의 분산 용액은 분산 용액 제공용기를 통해 제공될 수 있다. 이렇게 상기 섬유 상에 남은 상기 카본나노튜브를 건조시켜 상기 패턴 발열층을 형성할 수 있다. 또한, 카본나노튜브(CNT) 페이스트를 스크린 프린팅법으로 상기 섬유 상에 인쇄(또는 프린팅)하여 건조시킴으로써, 상기 패턴 발열층을 형성할 수 있다. 이때, 카본나노튜브(CNT) 페이스트에는 바인더(binder)가 혼합될 수 있으며, 50 메쉬(mesh) 이상의 카본나노튜브(CNT)를 10 내지 150 메쉬(예를 들어, 약 110 메쉬)의 실크 스크린을 사용하여 인쇄할 수 있고, 상온(약 25 ℃) 내지 180 ℃(예를 들어, 약 150 ℃)에서 5 내지 10 분간 건조시킬 수 있다. 건조 온도가 상온보다 낮은 경우에는 분산매 등이 완전히 건조되지(또는 다 날아가지) 않아 전기전도도에 영향을 줄 수 있고, 180 ℃보다 높은 경우에는 상기 패턴 발열층에 크랙이 발생하는 등 상기 패턴 발열층 또는 상기 섬유가 손상될 수 있다. 건조 시간은 건조 온도에 따라 분산매 등이 완전히 건조될 수 있는 시간으로 알맞게 정해질 수 있다.Next, the carbon nanotubes on one surface of the fiber to provide a dispersion solution dispersed in the dispersion medium to form a pattern heating layer in a continuous network structure to form an open portion (S200). The pattern heating layer may be formed by thick-film coating on one surface of the fiber using vacuum adsorption or screen printing, and may form a pattern in a continuous network structure through a silk screen (or mask). have. For example, when the dispersion solution of the carbon nanotubes (or the carbon nanotube paste) is provided on one side of the fiber while flowing from one side of the fiber to the other side, the dispersion medium passes through the fiber and exits downward. Only the carbon nanotubes remain (or are filtered out) on the fibers. Here, the dispersion solution of the carbon nanotubes may be provided through a dispersion solution providing container. Thus, the carbon nanotubes remaining on the fibers may be dried to form the pattern heating layer. In addition, the pattern heat generating layer may be formed by printing (or printing) carbon nanotube (CNT) paste on the fiber by screen printing. In this case, a binder may be mixed in the carbon nanotube (CNT) paste, and a silk screen of 10 to 150 mesh (for example, about 110 mesh) may be formed of carbon nanotubes (CNT) of 50 mesh or more. Can be printed and dried at room temperature (about 25 ° C.) to 180 ° C. (eg, about 150 ° C.) for 5 to 10 minutes. If the drying temperature is lower than room temperature, the dispersion medium may not be completely dried (or not blown away) and thus may affect the electrical conductivity. If the drying temperature is higher than 180 ° C, the pattern heating layer may have cracks in the pattern heating layer. Or the fibers may be damaged. The drying time may be appropriately determined as a time at which the dispersion medium and the like can be completely dried according to the drying temperature.
상기 패턴 발열층은 탄성력을 갖는 상기 카본나노튜브에 의해 탄성력을 가질 수 있으며, 상기 섬유의 변형에 따라 변형될 수 있고, 상기 섬유의 변형 시에도 발열 효율과 복원력을 유지할 수 있다. 이때, 상기 패턴 발열층은 표면적의 변화 또는 상기 카본나노튜브의 접촉점 개수의 변화에 의해 적어도 부분적으로 저항이 변화될 수 있다. 그리고 오픈부를 형성하는 연속적인 망 구조로 상기 패턴 발열층을 형성함으로써, 상기 섬유의 변형에 따라 상기 패턴 발열층의 각 단위 패턴이 방향성을 갖고 잘 변형될 수 있다. 이에 상기 패턴 발열층의 손상(또는 단선)없이 발열 섬유의 내구성을 향상시킬 수 있다.The pattern heating layer may have elastic force by the carbon nanotubes having elastic force, may be deformed according to the deformation of the fiber, and maintain the heat generating efficiency and the restoring force even when the fiber is deformed. In this case, the pattern heating layer may have a resistance at least partially changed by a change in surface area or a change in the number of contact points of the carbon nanotubes. And by forming the pattern heat generating layer in a continuous network structure forming an open portion, each unit pattern of the pattern heat generating layer can be deformed well with a direction according to the deformation of the fiber. Accordingly, the durability of the heat generating fiber can be improved without damaging (or breaking) the pattern heat generating layer.
상기 패턴 발열층을 형성하는 과정(S200)에서는 상기 섬유의 타면에 진공압을 형성하여 상기 분산 용액을 여과하면서 상기 카본나노튜브를 상기 섬유 상에 진공 흡착시킬 수 있다. 상기 패턴 발열층은 진공흡착법으로 상기 섬유 상에 형성될 수 있다. 상기 섬유의 타면에 진공압을 형성할 수 있으며, 진공배기수단을 통해 이와 연결된 진공 용기에 진공을 형성하여 상기 섬유의 타면에 진공압이 형성되도록 할 수 있다. 이를 통해 상기 카본나노튜브를 상기 섬유의 일면 상에 진공 흡착시킬 수 있으며, 상기 카본나노튜브가 분산매에 분산된 분산 용액에서 여과(filtering)되어 상기 섬유 상에 남게 되는 상기 카본나노튜브가 상기 섬유 또는 상기 자가조립단층 상에 진공 흡착되어 상기 섬유의 일면 상에 상기 패턴 발열층을 형성할 수 있다. 여기서, 상기 섬유마다 다른 특성의 결이 있으며, 그 결에 따라 늘어나는 길이 대비 저항의 변화량이 다르기 때문에 저항의 변형 시 방향성을 부가해줄 수 있다.In the forming of the pattern heating layer (S200), the carbon nanotubes may be vacuum adsorbed onto the fibers while forming a vacuum pressure on the other surface of the fibers to filter the dispersion solution. The pattern heating layer may be formed on the fiber by vacuum adsorption. A vacuum pressure may be formed on the other surface of the fiber, and a vacuum may be formed on the other surface of the fiber by forming a vacuum in a vacuum container connected thereto through a vacuum exhaust means. Through this, the carbon nanotubes may be vacuum adsorbed on one surface of the fiber, and the carbon nanotubes are filtered on a dispersion solution dispersed in a dispersion medium and remain on the fibers. The self-assembled monolayer may be vacuum adsorbed to form the pattern heating layer on one surface of the fiber. Here, each fiber has a grain of different characteristics, and according to the grain, the amount of change in the resistance compared to the length of the stretching may be different, thereby adding direction to the deformation of the resistance.
상기 섬유의 타면에 진공압을 형성하여 상기 카본나노튜브를 상기 섬유의 일면에서 타면 방향으로 흡착시키는 진공흡착법에 의해 상기 패턴 발열층을 상기 섬유의 일면 상에 형성할 경우, 강한 진공압에 의한 흡착 에너지에 의해 상기 섬유 내부까지 상기 카본나노튜브가 침투할 수 있고, 상기 패턴 발열층이 상기 섬유 상에 효과적으로 흡착될 수 있다. 그리고 진공압에 의해 상기 분산매가 진공을 형성하지 않는 것보다 상기 섬유를 잘 빠져나올 수 있기 때문에 빠르게 상기 패턴 발열층을 형성할 수 있고, 이에 따라 상기 패턴 발열층을 형성하는 공정 시간을 단축할 수 있으며, 상기 섬유의 표면에 균일하게 진공압이 형성되므로 균일한 상기 패턴 발열층을 형성할 수 있다.When the pattern heat generating layer is formed on one surface of the fiber by a vacuum adsorption method in which a vacuum pressure is formed on the other surface of the fiber to adsorb the carbon nanotubes from one surface of the fiber to the other surface direction, adsorption by strong vacuum pressure is performed. The carbon nanotubes may penetrate into the fiber by energy, and the pattern heating layer may be effectively adsorbed on the fiber. In addition, since the dispersion medium is able to escape the fibers better than the vacuum without forming a vacuum, the pattern heating layer can be formed quickly, and thus the process time for forming the pattern heating layer can be shortened. In addition, since the vacuum pressure is uniformly formed on the surface of the fiber, it is possible to form the uniform pattern heating layer.
즉, 진공흡착법으로 상기 패턴 발열층을 형성하여 강한 진공압에 의한 흡착 에너지에 의해 상기 섬유 내부까지 상기 카본나노튜브가 침투할 수 있을 뿐만 아니라 상기 카본나노튜브 표면의 수산화기(OH-)와 상기 섬유의 표면에 형성된 상기 자가조립단층의 작용기(예를 들어, NH+)가 이온 결합할 수 있어 더욱 강한 에너지로 상기 섬유와 상기 패턴 발열층이 결합할 수 있다. 이에 진공흡착법을 통해 더욱 내구성이 높은 상기 카본나노튜브가 흡착(또는 코팅)된 상기 섬유로 발열 섬유를 제작할 수 있다.That is, the pattern heating layer is formed by vacuum adsorption, and the carbon nanotubes can penetrate into the fiber by the adsorption energy due to the strong vacuum pressure, as well as the hydroxyl group (OH-) and the fiber on the surface of the carbon nanotubes. The functional group (eg, NH + ) of the self-assembled monolayer formed on the surface of the ionic bond can be bonded to the fiber and the pattern heating layer with a stronger energy. Accordingly, a heat generating fiber may be manufactured from the fiber to which the carbon nanotubes having high durability are adsorbed (or coated) through a vacuum adsorption method.
그 다음 상기 패턴 발열층에 전기적으로 연결되는 전극을 형성한다(S300). 전극은 상기 패턴 발열층에 전기적으로 연결될 수 있으며, 상기 패턴 발열층의 양쪽 끝단에 형성될 수 있다. 상기 전극을 통해 상기 패턴 발열층에 전류를 흘려주어 상기 패턴 발열층을 전기 발열시킬 수 있다.Next, to form an electrode electrically connected to the pattern heating layer (S300). An electrode may be electrically connected to the pattern heating layer, and may be formed at both ends of the pattern heating layer. An electric current may be generated in the pattern heating layer by flowing a current through the electrode in the pattern heating layer.
상기 섬유는 결(grain)을 가질 수 있으며, 섬유마다 다른 특성의 결을 가질 수 있고, 그 결에 따라 늘어나는 길이 대비 저항의 변화량이 달라 상기 패턴 발열층의 저항 변화 시 방향성을 부가해줄 수 있다. 또한, 상기 섬유의 결은 상기 카본나노튜브가 흡착되는 흡착면을 제공할 수 있으며, 대부분의 상기 카본나노튜브가 상기 결에 흡착될 수 있다.The fiber may have a grain (grain), and may have a grain of different characteristics for each fiber, and the amount of change in resistance compared to the length that increases according to the grain may vary, thereby adding directionality when the resistance of the pattern heating layer is changed. In addition, the fiber grains may provide an adsorption surface on which the carbon nanotubes are adsorbed, and most of the carbon nanotubes may be adsorbed on the grains.
상기 패턴 발열층을 형성하는 과정(S200)은 상기 섬유의 결을 따라 제1 라인부를 형성하는 과정(S210); 및 상기 제1 라인부와 단위 패턴을 이루도록 상기 섬유의 결과 교차하는 방향으로 연장되는 제2 라인부를 형성하는 과정(S220)을 포함할 수 있다.Forming the pattern heating layer (S200) is a step of forming a first line portion along the texture of the fiber (S210); And forming a second line part extending in a direction crossing the result of the fiber to form a unit pattern with the first line part (S220).
상기 섬유의 결을 따라 제1 라인부를 형성할 수 있다(S210). 제1 라인부는 상기 섬유의 결을 따라 제공될 수 있으며, 상기 섬유의 결을 따라 신축할 수 있어 신축에 따른 저항 변화가 작을 수 있다. 상기 카본나노튜브는 머리카락 구조로 되어 서로 엉켜 있는 구조이며, 분자 구조상 부분 단락이 발생하여도 연결되어 있는 접촉점이 많아 쇼트나 화재의 위험성이 없고, 장기간 사용에 따른 내구성이 뛰어나다. 이러한 상기 카본나노튜브는 상기 제1 라인부가 늘어남에 따라 서로 엉켜 있던 입자들이 풀리거나 서로 떨어질 수 있으며, 이에 따라 상기 카본나노튜브의 접촉점의 개수가 변할 수 있고, 상기 카본나노튜브의 접촉점 개수의 변화에 의해 상기 제1 라인부의 저항이 변화할 수 있다. 상기 제1 라인부는 대부분의 상기 카본나노튜브가 흡착 고정된 상기 섬유의 결을 따라 신축됨으로써, 상기 제1 라인부가 늘어나더라도 상기 섬유의 결을 따라 촘촘히 제공된 상기 카본나노튜브에 의해 입자들 간의 연결이 대부분 유지될 수 있고, 이에 따라 상기 카본나노튜브의 접촉점 개수의 변화가 적어 신축에 따른 저항 변화가 작을 수 있다.A first line part may be formed along the texture of the fiber (S210). The first line part may be provided along the grain of the fiber, and may be stretched along the grain of the fiber, so that a change in resistance according to the stretch may be small. The carbon nanotubes have a hair structure and are entangled with each other, and have a lot of contact points connected even when a partial short occurs in the molecular structure, and thus there is no risk of short or fire, and excellent durability for long-term use. The carbon nanotubes may have particles entangled with each other as the first line portion increases or may be separated from each other. Accordingly, the number of contact points of the carbon nanotubes may change, and the number of contact points of the carbon nanotubes may change. The resistance of the first line portion can be changed by the. The first line part is stretched along the grains of the fiber on which most of the carbon nanotubes are adsorbed and fixed, so that the connection between the particles is made by the carbon nanotubes closely provided along the grains of the fiber even if the first line portion is stretched. In most cases, the change in the number of contact points of the carbon nanotubes is small, and thus the change in resistance due to stretching may be small.
그리고 상기 제1 라인부와 단위 패턴을 이루도록 상기 섬유의 결과 교차하는 방향으로 연장되는 제2 라인부를 형성할 수 있다(S220). 제2 라인부는 상기 섬유의 결과 교차하는 방향으로 연장될 수 있으며, 상기 제1 라인부 간을 연결할 수 있고, 상기 제1 라인부와 단위 패턴을 이룰 수 있다. 굴곡을 가져 두 개 이상의 방향으로 연속되어 연장될 수 있다. 이때, 상기 제2 라인부는 서로 다른 방향으로 연장되는 복수의 단위 라인으로 이루어질 수 있으며, 서로 다른 방향으로 연장되는 상기 복수의 단위 라인이 연결되어 상기 제1 라인부 간을 연결할 수 있다. 여기서, 서로 다른 방향은 모두 상기 섬유의 결과 교차하는 방향일 수 있고, 상기 교차하는 방향은 수직으로 교차하는 것뿐만 아니라 평행하지 않고 비스듬한(또는 엇갈리는) 방향을 모두 포함할 수 있다. 그리고 상기 제2 라인부는 상기 섬유의 결과 교차하는 방향으로 신축하게 되어 신축에 따른 저항 변화가 클 수 있다. 상기 제2 라인부를 이루는 카본나노튜브는 상기 제2 라인부가 늘어남에 따라 서로 엉켜 있던 입자들이 떨어져 어느 정도 이격 거리가 발생할 수 있으며, 이에 따라 상기 카본나노튜브의 접촉점의 개수가 변할 수 있고, 상기 카본나노튜브의 접촉점 개수의 변화에 의해 상기 제2 라인부의 저항이 변화할 수 있다. 상기 제2 라인부는 상기 섬유의 결과 교차하는 방향으로 신축됨으로써, 상기 제2 라인부가 늘어남에 따라 대부분의 상기 카본나노튜브가 흡착 고정된 상기 섬유의 결들이 분리되고, 상기 결들 간에 서로 엉켜 있던 입자들이 떨어져 입자들 간의 연결이 대부분 끊어질 수 있으며, 이에 따라 상기 카본나노튜브의 접촉점 개수의 변화가 많게 되어 신축에 따른 저항 변화가 클 수 있다. In operation S220, a second line part extending in a direction crossing the result of the fiber may be formed to form a unit pattern with the first line part. The second line portion may extend in a direction intersecting as a result of the fiber, may connect between the first line portions, and form a unit pattern with the first line portion. It can be curved to extend continuously in two or more directions. In this case, the second line part may be formed of a plurality of unit lines extending in different directions, and the plurality of unit lines extending in different directions may be connected to connect the first line parts. Here, the different directions may all be directions that intersect as a result of the fibers, and the directions of intersection may include both vertically as well as non-parallel and oblique (or staggered) directions. In addition, the second line part may be stretched in a direction intersecting as a result of the fiber, and thus the resistance change according to the stretching may be large. The carbon nanotubes forming the second line part may be separated from each other by entangled particles as the second line part is stretched to some extent, and thus, the number of contact points of the carbon nanotubes may change, and the carbon The resistance of the second line part may change due to a change in the number of contact points of the nanotubes. The second line portion is stretched in a direction intersecting as a result of the fibers, so that the grains of the fiber on which most of the carbon nanotubes are adsorbed and fixed are separated as the second line portion is stretched, and particles intertwined with each other among the grains are formed. As a result, the connection between the particles may be mostly broken, and accordingly, the number of contact points of the carbon nanotubes increases, and thus the resistance change according to expansion and contraction may be large.
상기 패턴 발열층을 형성하는 과정(S200)에서는 상기 단위 패턴의 상기 결에 수직한 방향의 길이가 상기 단위 패턴의 상기 결에 평행한 방향의 길이보다 짧게 상기 패턴 발열층을 형성할 수 있다. 상기 패턴 발열층이 상기 결에 평행한 방향으로 신축하는 경우에는 상기 섬유의 결을 따라 신축할 수 있어 신축에 따른 저항 변화가 작을 수 있다. 상기 패턴 발열층이 상기 결에 평행한 방향으로 늘어나는 경우, 상기 패턴 발열층이 늘어나더라도 상기 섬유의 결을 따라 촘촘히 제공된 상기 카본나노튜브에 의해 입자들 간의 연결이 대부분 유지될 수 있고, 이에 따라 상기 카본나노튜브의 접촉점 개수의 변화가 적어 신축에 따른 저항 변화가 작을 수 있다.In the process of forming the pattern heating layer (S200), the pattern heating layer may be formed such that the length of the unit pattern in the direction perpendicular to the grain is shorter than the length of the unit pattern in the direction parallel to the grain of the unit pattern. When the pattern heating layer is stretched in a direction parallel to the grain, the pattern heating layer may be stretched along the grain of the fiber, and thus the resistance change according to the stretch may be small. When the pattern heating layer extends in a direction parallel to the grains, even when the pattern heating layer is stretched, most of the connection between the particles may be maintained by the carbon nanotubes provided closely along the grains of the fiber, and thus the carbon As the number of contact points of the nanotubes is small, the resistance change according to the stretching may be small.
반면에, 상기 패턴 발열층이 상기 결에 수직한 방향으로 신축하는 경우에는 상기 섬유의 결들 사이가 붙었다 떨어졌다 하게 되므로, 신축에 따른 저항 변화가 클 수 있다. 즉, 상기 섬유의 결들이 붙어 있을 때와 상기 섬유의 결들 사이가 떨어져 있을 때에 상기 카본나노튜브의 접촉점 개수의 차이가 많이 나게 되며, 이로 인해 신축에 따른 저항 변화가 크게 된다. 상기 패턴 발열층이 상기 결에 수직한 방향으로 늘어나는 경우, 대부분의 상기 카본나노튜브가 흡착 고정된 상기 섬유의 결들 사이가 벌어지게 되고 상기 패턴 발열층이 상기 섬유의 결들 사이의 공간에서 신축하면서 상기 결들 간에 서로 엉켜 있던 입자들이 떨어져 입자들 간의 연결이 대부분 끊어질 수 있으며, 이에 따라 상기 카본나노튜브의 접촉점 개수의 변화가 많게 되어 신축에 따른 저항 변화가 클 수 있다.On the other hand, when the pattern heating layer stretches in the direction perpendicular to the grains, the gaps between the grains of the fibers stick and fall, and thus the resistance change according to the stretching may be large. That is, when the grains of the fibers are attached and when the grains of the fibers are separated, the difference in the number of contact points of the carbon nanotubes is increased, which causes a large change in resistance due to stretching. When the pattern heating layer extends in a direction perpendicular to the grains, most of the carbon nanotubes adsorb and fix the gaps of the fibers, and the pattern heating layer stretches in the space between the grains of the fibers. Particles that are entangled with each other may fall off, and thus the connection between the particles may be mostly broken. Accordingly, the change in the number of contact points of the carbon nanotubes may increase, resulting in a large change in resistance due to stretching.
이에 상기 단위 패턴의 결에 수직한 방향의 길이를 상기 단위 패턴의 결에 평행한 방향의 길이보다 짧게 함으로써, 상기 패턴 발열층에서 상기 결에 수직한 방향으로 신축하여 저항 변화가 큰 성분(또는 부분)을 상기 결에 평행한 방향으로 신축하여 저항 변화가 작은 성분보다 줄일 수 있다. 이를 통해 상기 패턴 발열층이 신축하더라도 상기 패턴 발열층의 저항 변화를 줄일 수 있고, 상기 패턴 발열층의 영역별 저항 변화에 따라 영역별로 발생하는 열효율 차이도 억제 또는 방지할 수 있다.Accordingly, the length of the direction perpendicular to the grain of the unit pattern is shorter than the length of the direction parallel to the grain of the unit pattern, thereby stretching the component in the pattern heating layer in the direction perpendicular to the grain so that the component (or portion) having a large resistance change is increased. By stretching in a direction parallel to the grain, the resistance change can be reduced to less than that of small components. As a result, even when the pattern heating layer is stretched, the resistance change of the pattern heating layer may be reduced, and a difference in thermal efficiency generated for each region may be suppressed or prevented according to the resistance change of each region of the pattern heating layer.
그리고 상기 제1 라인부를 형성하는 과정(S210)에서는 상기 제1 라인부의 폭을 상기 결의 간격보다 크게 형성할 수 있다. 즉, 상기 제1 라인부의 폭은 상기 섬유의 결 간의 거리보다 클 수 있다. 상기 제1 라인부의 폭이 상기 결의 간격보다 작게 되면, 상기 제1 라인부가 상기 섬유의 결 사이에만 형성되고, 상기 섬유의 결에는 형성되지 않을 수 있다. 이러한 경우, 상기 패턴 발열층의 저항 변화 시 방향성을 부가해줄 수 없고, 안정적인 상기 카본나노튜브의 흡착면을 제공하는 상기 결에 상기 카본나노튜브가 흡착되지 않아 상기 패턴 발열층이 상기 섬유 상에 안정적으로 고정될 수 없다.In the process of forming the first line part (S210), the width of the first line part may be greater than the grain spacing. That is, the width of the first line portion may be greater than the distance between the grains of the fiber. When the width of the first line portion is smaller than the spacing of the grains, the first line portion may be formed only between the grains of the fiber and may not be formed in the grains of the fiber. In this case, the pattern heating layer is stably formed on the fiber because the carbon nanotubes are not adsorbed on the grains, which cannot add directionality when the resistance of the pattern heating layer is changed and provides a stable adsorption surface of the carbon nanotubes. It cannot be fixed.
하지만, 상기 제1 라인부의 폭이 상기 결의 간격보다 큰 경우에는 적어도 부분적으로 상기 섬유의 결에 흡착되는 상기 카본나노튜브가 생기게 되고, 상기 제1 라인부를 포함하는 상기 패턴 발열층이 상기 섬유 상에 안정적으로 고정될 수 있다. 또한, 상기 패턴 발열층의 저항 변화 시 방향성을 부가해줄 수 있어 상기 패턴 발열층의 신축에 의한 저항 변화를 예측 및/또는 제어할 수 있다.However, when the width of the first line portion is greater than the grain spacing, the carbon nanotubes are at least partially adsorbed to the grains of the fiber, and the pattern heat generating layer including the first line portion is stable on the fibers. Can be fixed. In addition, directionality may be added when the resistance of the pattern heating layer is changed, and thus, the resistance change due to expansion and contraction of the pattern heating layer may be predicted and / or controlled.
한편, 상기 제2 라인부의 폭도 상기 결의 간격보다 크게 형성할 수 있다. 상기 제1 라인부와 상기 제2 라인부의 균일한 발열을 위해 상기 제2 라인부의 폭은 상기 제1 라인부의 폭과 동일할 수 있고, 상기 결의 간격보다 클 수 있다. 또한, 상기 결에 흡착되는 상기 카본나노튜브의 수(또는 면적)가 많아져(또는 넓어져) 상기 제2 라인부가 안정적으로 고정될 수 있고, 상기 패턴 발열층이 섬유 상에 보다 안정적으로 고정될 수 있다.On the other hand, the width of the second line portion may be formed larger than the gap between the grains. The width of the second line portion may be equal to the width of the first line portion and may be greater than the grain spacing for uniform heating of the first line portion and the second line portion. In addition, the number (or area) of the carbon nanotubes adsorbed to the grain increases (or widens) so that the second line portion can be stably fixed, and the pattern heat generating layer can be more stably fixed on the fiber. have.
본 발명에 따른 발열 섬유 제조방법은 상기 카본나노튜브를 산처리하여 상기 카본나노튜브의 표면에서 적어도 일부의 카본 본딩을 제거하는 과정(S50); 카본 본딩이 제거된 상기 카본나노튜브의 표면에 상기 작용기와 이온 결합되는 기능기를 형성하는 과정(S60); 및 상기 섬유의 표면에 작용기를 포함하는 표면개질물질로 형성되는 자가조립단층을 형성하는 과정(S40);을 더 포함할 수 있다.Exothermic fiber manufacturing method according to the invention is the step of removing the at least a portion of the carbon bonding on the surface of the carbon nanotubes by acid treatment of the carbon nanotubes (S50); Forming a functional group ionically bonded to the functional group on the surface of the carbon nanotubes from which carbon bonding is removed (S60); And forming a self-assembled monolayer formed of a surface modification material including a functional group on the surface of the fiber (S40).
상기 카본나노튜브를 산처리하여 상기 카본나노튜브의 표면에서 적어도 일부의 카본 본딩을 제거할 수 있다(S50). 상기 카본나노튜브를 산처리하여 상기 카본나노튜브를 표면처리할 수 있다. 산처리에 의해 상기 카본나노튜브의 표면에 불포화 결합(dangling bond)을 형성시켜 수산화기(-OH)가 상기 카본나노튜브의 표면에 형성되도록 할 수 있다. 이때, 상기 카본나노튜브를 상기 분산매에 균일하게 분산시키기 위해 상기 카본나노튜브를 산처리하는 과정(S50)을 상기 카본나노튜브를 분산매에 분산시키는 과정(S100) 이전에 수행할 수도 있다.Acid treatment of the carbon nanotubes may remove at least a portion of the carbon bonding from the surface of the carbon nanotubes (S50). The carbon nanotubes may be acid treated to surface-treat the carbon nanotubes. An acid treatment may form a dangling bond on the surface of the carbon nanotubes such that hydroxyl (-OH) is formed on the surface of the carbon nanotubes. In this case, in order to uniformly disperse the carbon nanotubes in the dispersion medium, an acid treatment of the carbon nanotubes (S50) may be performed before the process of dispersing the carbon nanotubes in the dispersion medium (S100).
상기 카본나노튜브는 질산을 이용하여 산처리할 수 있다. 예를 들어, 상기 카본나노튜브(예를 들어, 1 g)를 99 % 질산(예를 들어, 150 ㎖)에 넣고 산처리할 수 있다. 이때, 담금법으로 산처리를 수행할 수 있으며, 효율적인 상기 카본나노튜브의 표면처리를 위해 100 내지 150 ℃의 온도로 3 내지 5 시간 동안 교반시키면서 산처리를 수행할 수 있다. 질산에서 꺼낸 상기 카본나노튜브는 초순수 등을 이용하여 상기 카본나노튜브의 pH가 7(또는 중성)이 될 때까지 세척공정을 진행할 수 있다. 예를 들어, 질산에서 꺼낸 상기 카본나노튜브를 초순수로 5 내지 10 회 헹구어 낼 수 있다.The carbon nanotubes may be acid treated using nitric acid. For example, the carbon nanotubes (for example, 1 g) may be placed in 99% nitric acid (for example, 150 ml) and acid treated. At this time, the acid treatment can be carried out by a immersion method, the acid treatment may be performed while stirring for 3 to 5 hours at a temperature of 100 to 150 ℃ for efficient surface treatment of the carbon nanotubes. The carbon nanotubes taken out of nitric acid may be washed with ultrapure water until the pH of the carbon nanotubes reaches 7 (or neutral). For example, the carbon nanotubes taken out of nitric acid may be rinsed 5 to 10 times with ultrapure water.
한편, 염산으로 산처리하는 경우에는 염소 이온(Cl-)이 카본 본딩이 끊어진 자리의 탄소 이온(C4+)과 반응하여 카본 본딩이 끊어진 자리에 염소기(-Cl)가 형성될 수 있고, 이로 인해 상기 카본나노튜브의 표면에 불포화 결합을 형성시킬 수 없다.In the case of acid treatment with hydrochloric acid, chlorine ions (Cl − ) may react with carbon ions (C 4+ ) at the sites where carbon bonding is broken, thereby forming chlorine groups (—Cl) at the sites where carbon bonding is broken. For this reason, an unsaturated bond cannot be formed on the surface of the carbon nanotubes.
상기 카본나노튜브를 산처리하는 과정(S50)에서는 상기 카본나노튜브의 표면에서 적어도 일부의 카본 본딩이 제거될 수 있다. 상기 카본나노튜브를 산처리하면, 산화 과정을 통해(또는 산에 의한 에너지나 열에 의해) 카본 본딩이 끊어질 수 있고, 상기 카본나노튜브의 표면에 불포화 결합을 형성시킬 수 있다.In the process of acid treating the carbon nanotubes (S50), at least some carbon bonding may be removed from the surface of the carbon nanotubes. When the carbon nanotubes are acid treated, carbon bonding may be broken through oxidation (or by energy or heat by acid), and an unsaturated bond may be formed on the surface of the carbon nanotubes.
그 다음 상기 카본나노튜브를 산처리하는 과정(S50) 이후에 카본 본딩이 제거된 상기 카본나노튜브의 표면에 상기 작용기와 이온 결합되는 기능기를 형성할 수 있다(S60). 상기 카본나노튜브의 표면에서 카본 본딩이 제거된 부분에는 수산화기 등의 기능기가 달라붙어 상기 카본나노튜브의 표면 말단에 상기 기능기가 형성될 수 있다. 이때, 상기 기능기는 수산화기(-OH)를 포함할 수 있다. 여기서, 수산화기는 공기 중의 수분에 의해서도 제공될 수 있고, 산처리된 상기 카본나노튜브의 세척 공정에서 사용되는 물에 의해 제공될 수도 있으며, 상기 분산매로 초순수를 사용하는 경우에는 상기 분산매에 의해서도 제공될 수 있다. 예를 들어, 상기 카본나노튜브의 표면에 수산화기가 형성되면, 상기 카본나노튜브의 수산화기와 자가조립단층의 작용기가 이온 결합함으로써, 상기 패턴 발열층이 상기 섬유 상에 잘 흡착될 수 있다.Next, after the acid treatment of the carbon nanotubes (S50), a functional group may be formed on the surface of the carbon nanotubes from which the carbon bonding is removed (S60). A functional group such as a hydroxyl group may be attached to a portion where the carbon bonding is removed from the surface of the carbon nanotube so that the functional group is formed at the surface end of the carbon nanotube. In this case, the functional group may include a hydroxyl group (-OH). Here, the hydroxyl group may also be provided by water in the air, may be provided by water used in the washing process of the carbon nanotubes acid-treated, and when using ultrapure water as the dispersion medium may also be provided by the dispersion medium. Can be. For example, when a hydroxyl group is formed on the surface of the carbon nanotubes, the hydroxyl group of the carbon nanotubes and the functional group of the self-assembled monolayer are ion-bonded, so that the pattern heat generating layer may be well adsorbed onto the fibers.
그리고 상기 패턴 발열층을 형성하는 과정(S200) 이전에 상기 섬유의 표면에 작용기를 포함하는 표면개질물질로 형성되는 자가조립단층을 형성할 수 있다(S40). 자가조립단층은 상기 섬유의 표면과 결합되는 헤드 그룹; 자가조립단층의 말단에 제공되는 작용기를 포함하며, 상기 헤드 그룹과 연결되는 엔드 그룹; 및 상기 헤드 그룹과 상기 엔드 그룹을 연결하는 백본(backbone)을 포함할 수 있다. 상기 헤드 그룹은 상기 섬유의 표면과 결합할 수 있고, 상기 섬유의 종류에 따라 선택할 수 있으며, 일반적으로 실란계(Si-)가 선택될 수 있다. 그리고 상기 백본은 주로 알킬 사슬로 구성될 수 있고, 하이드로 카본 체인이나 플로 카본 체인들일 수 있다. 마지막으로, 상기 엔드 그룹은 기능성을 부여할 수 있는 상기 작용기를 포함할 수 있고, 상기 헤드 그룹과 연결될 수 있으며, 상기 작용기는 이후 반응이 될 부분(즉, 어떤 물질을 붙일 것이냐)에 따라 다양한 작용기 중에서 선택될 수 있다.In addition, a self-assembled monolayer formed of a surface modification material including a functional group may be formed on the surface of the fiber before the process of forming the pattern heating layer (S200). The self-assembled monolayer comprises a head group bonded to the surface of the fiber; An end group comprising a functional group provided at the end of the self-assembled monolayer, the end group being connected to the head group; And a backbone connecting the head group and the end group. The head group may be bonded to the surface of the fiber, may be selected according to the type of the fiber, and generally a silane system (Si−) may be selected. And the backbone may be mainly composed of alkyl chains, hydrocarbon chains or flo carbon chains. Finally, the end group may include the functional group capable of imparting functionality, and may be connected to the head group, the functional group being various functional groups depending on the part to be reacted later (ie what material to attach). Can be selected from.
상기 섬유의 표면에 상기 자가조립단층을 형성하여 상기 섬유를 표면처리하면, 상기 섬유와 상기 패턴 발열층의 결합력이 향상되어 상기 섬유 상에 상기 패턴 발열층이 잘 형성될 수 있다.When the self-assembled monolayer is formed on the surface of the fiber to surface-treat the fiber, the bonding force between the fiber and the pattern heat generating layer may be improved, and the pattern heat generating layer may be well formed on the fiber.
상기 자가조립단층을 형성하는 단계(S40)에서는 상기 표면개질물질을 포함하는 표면처리 용액에 상기 섬유를 담지하여 상기 섬유의 표면에 상기 자가조립단층을 형성할 수 있다. 여기서, 상기 섬유는 컨베이어 벨트(conveyor belt) 등의 이송부(미도시)를 통해 이송되어 표면처리 용액에 담지될 수도 있으며, 이송부(미도시)는 상기 섬유에 접촉되는 벨트(미도시)와 상기 벨트를 이동시키는 회전롤러(미도시)로 구성될 수도 있다. 상기 표면처리 용액은 상기 섬유의 표면에 결합되는 상기 헤드 그룹으로 실란계 물질을 더 포함할 수 있으며, 아미노실란(Aminosilane), 3-아미노프로필트리에톡시실란(3-aminopropyltriethoxysilane; APTES) 등일 수 있다. 상기 실란계 물질은 고분자 및 무기물을 연결할 수 있는 기를 동시에 갖고 있으므로, 상기 섬유와 잘 결합할 수 있으며, 유리섬유와 유사하게 천연섬유 표면의 수산화기(-OH)를 활용하는 경우에는 실란계 물질에 포함된 실리콘(Si)이 상기 섬유 표면의 수산화기와 이온 결합하여 상기 헤드 그룹이 상기 섬유의 표면에 잘 결합될 수 있다. 따라서, 상기 표면처리 용액에 실란계 물질이 포함되는 경우에는 상기 헤드 그룹이 상기 섬유의 표면에 잘 결합될 수 있어 상기 표면처리 용액에 상기 섬유를 담지하는 것만으로 상기 섬유에 상기 자가조립단층을 형성할 수 있게 된다. 또한, 실란계 물질이 포함된 상기 표면처리 용액을 사용하면, 상기 표면개질물질의 이온들을 일정한 방향으로 상기 섬유의 표면에 유도시킬 수 있고, 상기 섬유의 표면을 대전시켜 상기 섬유의 표면에 정전기력을 부과할 수 있다.In the forming of the self-assembled monolayer (S40), the self-assembled monolayer may be formed on the surface of the fiber by supporting the fiber in a surface treatment solution containing the surface modification material. Here, the fiber may be transported through a transfer unit (not shown) such as a conveyor belt and supported on a surface treatment solution, and the transfer unit (not shown) may be a belt (not shown) contacting the fiber and the belt. It may be composed of a rotating roller (not shown) for moving. The surface treatment solution may further include a silane-based material as the head group bonded to the surface of the fiber, and may be aminosilane, 3-aminopropyltriethoxysilane (APTES), or the like. . Since the silane-based material has a group capable of linking a polymer and an inorganic material at the same time, the silane-based material can be combined with the fiber well and included in the silane-based material when using a hydroxyl group (-OH) on a natural fiber surface similar to glass fiber. Silicon (Si) is ion-bonded with the hydroxyl group on the surface of the fiber so that the head group can be bonded to the surface of the fiber. Therefore, when the silane-based material is included in the surface treatment solution, the head group can be well bonded to the surface of the fiber to form the self-assembled monolayer on the fiber only by supporting the fiber in the surface treatment solution. You can do it. In addition, by using the surface treatment solution containing a silane-based material, it is possible to induce the ions of the surface modification material to the surface of the fiber in a predetermined direction, to charge the surface of the fiber to apply the electrostatic force to the surface of the fiber Can impose.
상기 작용기는 아민기(-NH), 아미노기(-NH2), 티올기(-SH), 카르복실기(-COOH), 포르밀기(-CHO), 시아나토기(-OCN), 실라놀기(Si-OH), 포스핀기(-PO2H2), 포스폰기(-PO3H2), 술폰기(-SO3H), 에폭시기 중에서 선택된 적어도 어느 하나일 수 있다. 상기 작용기를 통해 상기 섬유의 표면을 (+)로 대전시켜 상기 섬유의 표면에 정전기력을 부과할 수 있고, 상기 작용기가 상기 카본나노튜브의 수산화기와 이온 결합할 수 있다. 이에 따라 상기 섬유와 상기 패턴 발열층의 결합력(즉, 상기 자가조립단층과 상기 패턴 발열층의 결합력)을 향상시킬 수 있다.The functional group is an amine group (-NH), amino group (-NH 2 ), thiol group (-SH), carboxyl group (-COOH), formyl group (-CHO), cyanato group (-OCN), silanol group (Si- OH), a phosphine group (-PO 2 H 2 ), a phosphone group (-PO 3 H 2 ), a sulfone group (-SO 3 H), may be at least one selected from an epoxy group. The functional group may charge the surface of the fiber with (+) to impart an electrostatic force to the surface of the fiber, and the functional group may ionically bond with the hydroxyl group of the carbon nanotubes. Accordingly, the bonding force between the fiber and the pattern heating layer (that is, the bonding force between the self-assembled monolayer and the pattern heating layer) may be improved.
그리고 상기 카본나노튜브의 수산화기가 상기 엔드 그룹의 작용기와 이온 결합하여 상기 패턴 발열층이 형성될 수 있으며, 예를 들어 상기 카본나노튜브의 표면에 형성된 수산화(OH-)기와 상기 엔드 그룹의 아민(NH+)기가 이온 결합할 수 있다. 이에 따라 상기 섬유와 상기 패턴 발열층이 더욱 강한 에너지로 결합하게 되어 상기 섬유와 상기 패턴 발열층의 결합력이 향상될 수 있으며, 신축에 따른 상기 패턴 발열층의 박리가 억제 또는 방지될 수 있고, 본 발명의 발열 섬유 제조방법으로 제조된 발열 섬유의 내구성이 향상될 수 있다.And the carbon nanotube hydroxyl group is, and the pattern heat generating layer can be formed by bonding the functional group and the ion of the end group, for example hydroxide formed on the surface of the carbon nanotubes (OH -) group and amines of the end group ( NH + ) groups may be ionically bonded. Accordingly, the fiber and the pattern heating layer may be bonded with more strong energy, thereby improving the bonding force between the fiber and the pattern heating layer, and the peeling of the pattern heating layer due to stretching may be suppressed or prevented. Durability of the exothermic fiber produced by the exothermic fiber manufacturing method of the present invention can be improved.
본 발명에 따른 발열 섬유 제조방법은 전기적 신호가 공급되는 단자를 형성하는 과정(S400);을 더 포함할 수 있고, 상기 전극을 형성하는 과정(S300)은 상기 섬유와 상기 패턴 발열층을 전도성사로 재봉하여 상기 단자와 상기 패턴 발열층을 전기적으로 연결하는 과정(S310)을 포함할 수 있다.The method of manufacturing a heating fiber according to the present invention may further include forming a terminal to which an electrical signal is supplied (S400), and forming the electrode (S300) may include the fiber and the pattern heating layer as conductive yarns. It may include a step (S310) of electrically connecting the terminal and the pattern heating layer by sewing.
또한, 전기적 신호가 공급되는 단자를 형성할 수 있다(S400). 단자는 상기 전극의 일단에 형성될 수 있으며, 배터리 등의 외부 전원이 연결되어 전기적 신호가 공급될 수 있고, 공급되는 전기적 신호를 상기 전극으로 전달할 수 있다.In addition, it is possible to form a terminal to which the electrical signal is supplied (S400). The terminal may be formed at one end of the electrode, an external power source such as a battery may be connected to supply an electrical signal, and may transmit the supplied electrical signal to the electrode.
그리고 상기 섬유와 상기 패턴 발열층을 전도성사로 재봉하여 상기 단자와 상기 패턴 발열층을 전기적으로 연결할 수 있다(S310). 전도성사는 상기 섬유에 재봉할 수 있으며, 상기 단자와 상기 패턴 발열층을 전기적으로 연결할 수 있고, 상기 단자로부터 전달되는 전기적 신호를 상기 패턴 발열층에 전달할 수 있다. 여기서, 상기 전도성사는 은(Ag)사(絲), 금(Au)사 등의 전도성 실을 포함할 수 있고, 상기 섬유에 바느질(또는 재봉)하여 제공될 수 있다. 이러한 경우, 단락되는 부분없이 상기 패턴 발열층 전체에 전기적 신호가 제공될 수 있을 뿐만 아니라 상기 패턴 발열층 전체에 균일하게 전기적 신호를 제공할 수 있고, 간단하게 상기 전극을 형성할 수 있다. 또한, 보호막을 형성한 후에도 별도의 식각(etching) 공정없이 상기 전극을 형성할 수도 있다. 그리고 상기 전도성사로 상기 섬유와 상기 패턴 발열층을 함께 바느질하면, 간단하게 상기 전극을 형성할 수 있을 뿐만 아니라 상기 섬유와 상기 패턴 발열층을 단단히 결합(또는 고정)시킬 수 있다.The fiber and the pattern heating layer may be sewn with a conductive yarn to electrically connect the terminal and the pattern heating layer (S310). The conductive yarn may sew on the fiber, electrically connect the terminal and the pattern heating layer, and transmit an electrical signal transmitted from the terminal to the pattern heating layer. Here, the conductive yarn may include a conductive thread such as silver (Ag) yarn, gold (Au) yarn, and the like, and may be provided by sewing (or sewing) the fiber. In this case, not only the electrical signal may be provided to the entire pattern heating layer without being shorted, but also the electrical signal may be uniformly provided to the entire pattern heating layer, and the electrode may be simply formed. In addition, after forming the protective film, the electrode may be formed without a separate etching process. When the fiber and the pattern heating layer are sewn together with the conductive yarns, not only the electrode can be easily formed but also the fiber and the pattern heating layer can be tightly coupled (or fixed).
본 발명에 따른 발열 섬유 제조방법은 상기 패턴 발열층 상에 전기절연성을 갖는 보호막을 형성하는 과정(S500);을 더 포함할 수 있다.The method of manufacturing a heating fiber according to the present invention may further include forming a protective film having electrical insulation on the pattern heating layer (S500).
상기 패턴 발열층 상에 전기절연성을 갖는 보호막을 형성할 수 있다(S500). 보호막은 상기 패턴 발열층 상에 제공될 수 있으며, 상기 패턴 발열층을 보호할 수 있고, 전기절연성을 가져 전류(또는 전기)가 흐르는 상기 패턴 발열층을 전기절연시킬 수 있다. 또한, 상기 보호막은 상기 패턴 발열층에서 발생되는 열이 원활히 외부로 전달되도록 하기 위해 열전도성을 가질 수 있으며, 열전도성이 우수한 재질로 이루어질 수 있다.An electrically insulating protective film may be formed on the pattern heating layer (S500). The passivation layer may be provided on the pattern heating layer, may protect the pattern heating layer, and may electrically insulate the pattern heating layer through which current (or electricity) flows with electrical insulation. In addition, the protective film may have a thermal conductivity in order to smoothly transfer the heat generated from the pattern heating layer to the outside, and may be made of a material having excellent thermal conductivity.
예를 들어, 상기 보호막은 연성의 재질로 이루어질 수 있고, 상기 패턴 발열층 상에 코팅될 수 있다. 상기 섬유의 과도한 변형(예를 들어, 잦은 변형, 상기 패턴 발열층의 탄성한계 이상의 변형 등) 또는 급격한 변형으로 인해 상기 패턴 발열층이 박리될 수 있는데, 상기 섬유의 변형에 따라 신축 가능한 연성의 보호막을 통해 상기 패턴 발열층의 박리를 방지할 수 있고, 상기 섬유의 변형에 따른 표면적 변화로 인한 상기 패턴 발열층의 응력(stress)을 완화시켜 줄 수 있다. 상기 보호막은 수지(resin)로 이루어질 수 있으며, 이에 특별히 한정되지 않고, 상기 섬유의 변형에 따라 신축이 될 수 있도록 탄성력이 우수한 연성의 소재이면 족하다.For example, the passivation layer may be made of a flexible material and may be coated on the pattern heating layer. Excessive deformation of the fiber (for example, frequent deformation, deformation above the elastic limit of the pattern heating layer, etc.) or a sudden deformation may cause the pattern heating layer to peel off, the flexible protective film stretchable according to the deformation of the fiber Through the separation of the pattern heating layer can be prevented, it is possible to relieve the stress (stress) of the pattern heating layer due to the surface area change according to the deformation of the fiber. The protective film may be made of a resin, and is not particularly limited thereto. The protective film may be a flexible material having excellent elastic force so as to be stretched according to the deformation of the fiber.
여기서, 실리콘, 경화제 및 희석제를 혼합하여 상기 보호막을 형성할 수 있으며, 실리콘 69.5 g, 경화제 2 g(2.8 wt%) 및 희석제 20 ml를 혼합하여 스크린 프린팅법으로 인쇄하고 건조시켜 상기 보호막을 형성할 수 있다. 이때, 상온 내지 180 ℃(예를 들어, 약 150 ℃)에서 1 분간 건조시킬 수 있다. 건조 온도가 상온보다 낮은 경우에는 경화제, 희석제 등이 완전히 건조되지 않을 수 있고, 180 ℃보다 높은 경우에는 상기 패턴 발열층에 크랙(crack)이 발생하는 등 상기 패턴 발열층 또는 상기 섬유가 손상되거나 상기 보호막의 연성이 저하될 수 있다. 건조 시간은 건조 온도에 따라 경화제, 희석제 등이 완전히 건조될 수 있는 시간으로 알맞게 정해질 수 있다.Here, the protective film may be formed by mixing silicone, a curing agent, and a diluent, and 69.5 g of silicone, 2 g (2.8 wt%) of a curing agent, and 20 ml of a diluent may be mixed, printed and dried by screen printing to form the protective film. Can be. At this time, it can be dried for 1 minute at room temperature to 180 ℃ (for example, about 150 ℃). If the drying temperature is lower than room temperature, the curing agent, the diluent, etc. may not be completely dried. If the drying temperature is higher than 180 ° C., the pattern heating layer or the fiber may be damaged or the crack may be generated in the pattern heating layer. Ductility of the protective film may be lowered. The drying time may be appropriately determined as a time at which the curing agent, diluent and the like can be completely dried depending on the drying temperature.
이처럼, 본 발명에서는 섬유 상에 카본나노튜브(CNT)로 패턴 발열층을 형성하여 패턴 발열층이 탄성력을 가질 수 있고, 섬유의 변형 시에도 패턴 발열층의 발열 효율과 복원력을 유지할 수 있다. 또한, 오픈부를 형성하는 연속적인 망 구조로 패턴 발열층을 형성하여 섬유의 결과 평행 또는 수직 방향으로 변형하는 섬유의 변형(또는 신축)에 따라 패턴 발열층의 각 단위 패턴이 방향성을 갖고 잘 변형될 수 있다. 이에 따라 패턴 발열층의 손상(또는 단선)없이 발열 섬유의 내구성을 향상시킬 수 있다. 또한, 섬유의 결을 따라 제1 라인부를 형성하여 섬유의 변형에 따라 변형되면서도 전기전도도를 유지할 수 있는 부분(또는 면적)을 확보할 수 있고, 각 단위 패턴의 결에 수직한 방향의 길이를 각 단위 패턴의 결에 평행한 방향의 길이보다 짧게 하여 결에 수직한 방향으로 신축함으로 인해 저항 변화가 큰 성분을 줄일 수 있다. 그리고 섬유의 표면에 자가조립단층을 형성하여 표면개질한 후에 패턴 발열층을 형성함으로써, 섬유와 패턴 발열층의 결합력이 향상될 수 있고, 발열 섬유의 내구성이 보다 향상될 수 있다. 또한, 패턴 발열층 상에 보호막을 코팅하여 발열 섬유의 표면을 전기절연시킬 뿐만 아니라 패턴 발열층의 박리를 방지할 수도 있다.As described above, in the present invention, the pattern heating layer may be formed of carbon nanotubes (CNTs) on the fiber so that the pattern heating layer may have elastic force, and the heat generating efficiency and the restoring force of the pattern heating layer may be maintained even when the fiber is deformed. In addition, each unit pattern of the pattern heating layer is directional and well deformed according to the deformation (or stretching) of the fiber deforming in a parallel or vertical direction by forming a pattern heating layer with a continuous network structure forming an open portion. Can be. Accordingly, durability of the heat generating fiber can be improved without damaging (or breaking) the pattern heat generating layer. In addition, the first line portion is formed along the grains of the fiber to secure a portion (or area) capable of maintaining electrical conductivity while being deformed as the fiber is deformed, and each unit has a length perpendicular to the grain of each unit pattern. By shortening the length in the direction parallel to the grain of the pattern and stretching in the direction perpendicular to the grain, a component having a large resistance change can be reduced. And by forming a self-assembled monolayer on the surface of the fiber to form a pattern heating layer after surface modification, the bonding force of the fiber and the pattern heating layer can be improved, the durability of the heating fiber can be further improved. In addition, a protective film may be coated on the pattern heating layer to not only electrically insulate the surface of the heating fiber, but also to prevent peeling of the pattern heating layer.
이상에서 본 발명의 바람직한 실시예에 대하여 도시하고 설명하였으나, 본 발명은 상기한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이로부터 다양한 변형 및 균등한 타 실시예가 가능하다는 점을 이해할 것이다. 따라서, 본 발명의 기술적 보호범위는 아래의 특허청구범위에 의해서 정하여져야 할 것이다.Although the preferred embodiments of the present invention have been shown and described above, the present invention is not limited to the above-described embodiments, and the general knowledge in the field of the present invention belongs without departing from the gist of the present invention as claimed in the claims. Those skilled in the art will appreciate that various modifications and equivalent other embodiments are possible therefrom. Therefore, the technical protection scope of the present invention will be defined by the claims below.
11 : 결에 평행한 방향 12 : 결에 수직한 방향
100 : 발열 섬유 110 : 섬유
111 : 결 120 : 패턴 발열층
120a: 오픈부 120b: 단위 패턴
121 : 제1 라인부 122 : 제2 라인부
122a,122b: 단위 라인 125 : 카본나노튜브
130 : 전극 140 : 자가조립단층
141 : 헤드 그룹 142 : 엔드 그룹
143 : 백본 150 : 단자11: direction parallel to the grain 12: direction perpendicular to the grain
100: heat generating fiber 110: fiber
111
120a:
121: first line portion 122: second line portion
122a, 122b: unit line 125: carbon nanotubes
130
141: head group 142: end group
143: backbone 150: terminal
Claims (16)
오픈부를 형성하는 연속적인 망 구조로 상기 섬유의 일면 상에 제공되며, 카본나노튜브로 이루어진 패턴 발열층; 및
상기 패턴 발열층에 전기적으로 연결되는 전극;을 포함하는 발열 섬유.fiber;
A patterned heating layer provided on one surface of the fiber in a continuous network structure forming an open portion and made of carbon nanotubes; And
Heating fibers comprising; electrode electrically connected to the pattern heating layer.
상기 섬유는 결(grain)을 갖고,
상기 패턴 발열층은,
상기 섬유의 결을 따라 제공되는 제1 라인부; 및
상기 섬유의 결과 교차하는 방향으로 연장되는 제2 라인부를 포함하는 발열 섬유.The method according to claim 1,
The fibers have a grain,
The pattern heating layer,
A first line portion provided along the grain of the fiber; And
And a second line portion extending in the resulting intersecting direction of the fiber.
상기 제2 라인부는 각각 다른 방향으로 연장되어 서로 교차하는 복수의 단위 라인으로 이루어진 발열 섬유.The method according to claim 2,
The second line part is a heating fiber made up of a plurality of unit lines extending in different directions and crossing each other.
상기 제1 라인부와 상기 제2 라인부는 단위 패턴을 이루며,
상기 단위 패턴의 상기 결에 수직한 방향의 길이는 상기 단위 패턴의 상기 결에 평행한 방향의 길이보다 짧은 발열 섬유.The method according to claim 2,
The first line portion and the second line portion form a unit pattern,
And a length in a direction perpendicular to the grain of the unit pattern is shorter than a length in a direction parallel to the grain of the unit pattern.
상기 제1 라인부의 폭은 상기 결 사이의 간격보다 큰 발열 섬유.The method according to claim 2,
And a width of the first line portion greater than a gap between the grains.
상기 섬유의 표면에 제공되며, 작용기를 포함하는 표면개질물질로 이루어진 자가조립단층;을 더 포함하고,
상기 자가조립단층은,
상기 섬유의 표면과 결합되는 헤드 그룹; 및
상기 자가조립단층의 말단에 제공되는 상기 작용기를 포함하며, 상기 헤드 그룹과 연결되는 엔드 그룹을 포함하며,
상기 카본나노튜브의 표면에는 상기 작용기와 이온 결합되는 기능기가 형성되는 발열 섬유.The method according to claim 1,
The self-assembled monolayer is provided on the surface of the fiber, made of a surface modification material containing a functional group;
The self-assembled monolayer,
A head group coupled with the surface of the fiber; And
Including the functional group provided at the end of the self-assembled monolayer, the end group being connected to the head group,
Heat generating fiber is formed on the surface of the carbon nanotubes is a functional group that is ion-bonded with the functional group.
상기 패턴 발열층 상에 제공되며, 전기절연성을 갖는 보호막;을 더 포함하는 발열 섬유.The method according to claim 1,
A heating fiber provided on the pattern heating layer, further comprising a protective film having an electrical insulation.
전기적 신호가 공급되는 단자;를 더 포함하고,
상기 전극은 상기 섬유와 상기 패턴 발열층을 재봉하는 전도성사로 제공되는 발열 섬유. The method according to claim 1,
It further comprises a terminal for supplying an electrical signal,
The electrode is a heating fiber provided as a conductive yarn for sewing the fiber and the pattern heating layer.
상기 단자는 한 쌍으로 이루어지고,
상기 전극은 상기 단자 각각으로부터 서로 나란하게 연장되어 상기 단자와 상기 패턴 발열층을 전기적으로 연결하는 발열 섬유.The method according to claim 8,
The terminal consists of a pair,
The electrode extends in parallel with each other from each of the terminals, the heating fiber electrically connecting the terminal and the pattern heating layer.
섬유의 일면 상에 상기 카본나노튜브가 상기 분산매에 분산된 분산 용액을 제공하여 오픈부를 형성하는 연속적인 망 구조로 패턴 발열층을 형성하는 과정; 및
상기 패턴 발열층에 전기적으로 연결되는 전극을 형성하는 과정;을 포함하는 발열 섬유 제조방법.Dispersing carbon nanotubes in a dispersion medium;
Forming a patterned heating layer in a continuous network structure in which the carbon nanotubes are dispersed in the dispersion medium on one surface of the fiber to form an open portion; And
Forming an electrode electrically connected to the pattern heating layer; Heating fiber manufacturing method comprising a.
상기 섬유는 결(grain)을 갖고,
상기 패턴 발열층을 형성하는 과정은,
상기 섬유의 결을 따라 제1 라인부를 형성하는 과정; 및
상기 제1 라인부와 단위 패턴을 이루도록 상기 섬유의 결과 교차하는 방향으로 연장되는 제2 라인부를 형성하는 과정을 포함하는 발열 섬유 제조방법.The method according to claim 10,
The fibers have a grain,
Forming the pattern heating layer,
Forming a first line portion along the grain of the fiber; And
And forming a second line portion extending in a direction crossing the result of the fibers to form a unit pattern with the first line portion.
상기 패턴 발열층을 형성하는 과정에서는 상기 단위 패턴의 상기 결에 수직한 방향의 길이가 상기 단위 패턴의 상기 결에 평행한 방향의 길이보다 짧게 상기 패턴 발열층을 형성하는 발열 섬유 제조방법.The method according to claim 11,
In the process of forming the pattern heat generating layer, the heat generating fiber manufacturing method of forming the pattern heat generating layer so that the length of the direction perpendicular to the grain of the unit pattern is shorter than the length of the direction parallel to the grain of the unit pattern.
상기 제1 라인부를 형성하는 과정에서는 상기 제1 라인부의 폭을 상기 결 사이의 간격보다 크게 형성하는 발열 섬유 제조방법.The method according to claim 11,
And forming a width of the first line portion greater than a gap between the grains.
상기 카본나노튜브를 산처리하여 상기 카본나노튜브의 표면에서 적어도 일부의 카본 본딩을 제거하는 과정;
카본 본딩이 제거된 상기 카본나노튜브의 표면에 상기 작용기와 이온 결합되는 기능기를 형성하는 과정; 및
상기 섬유의 표면에 작용기를 포함하는 표면개질물질로 형성되는 자가조립단층을 형성하는 과정;을 더 포함하는 발열 섬유 제조방법.The method according to claim 10,
Acid treatment of the carbon nanotubes to remove at least a portion of the carbon bonding from the surface of the carbon nanotubes;
Forming a functional group ionically bonded to the functional group on the surface of the carbon nanotubes from which carbon bonding is removed; And
And forming a self-assembled monolayer formed of a surface modification material containing a functional group on the surface of the fiber.
전기적 신호가 공급되는 단자를 형성하는 과정;을 더 포함하고,
상기 전극을 형성하는 과정은 상기 섬유와 상기 패턴 발열층을 전도성사로 재봉하여 상기 단자와 상기 패턴 발열층을 전기적으로 연결하는 과정을 포함하는 발열 섬유 제조방법.The method according to claim 10,
Forming a terminal to which an electrical signal is supplied;
Forming the electrode comprises a step of electrically connecting the terminal and the pattern heating layer by sewing the fiber and the pattern heating layer with a conductive yarn.
상기 패턴 발열층 상에 전기절연성을 갖는 보호막을 형성하는 과정;을 더 포함하는 발열 섬유 제조방법.The method according to claim 10,
Forming a protective film having an electrical insulation on the pattern heating layer; Heating fiber manufacturing method further comprising.