KR20190115698A - Inorganic paint composition for coating image film and construction method of scenery type finish layer using the same - Google Patents
Inorganic paint composition for coating image film and construction method of scenery type finish layer using the sameInfo
- Publication number
- KR20190115698A KR20190115698A KR1020180038705A KR20180038705A KR20190115698A KR 20190115698 A KR20190115698 A KR 20190115698A KR 1020180038705 A KR1020180038705 A KR 1020180038705A KR 20180038705 A KR20180038705 A KR 20180038705A KR 20190115698 A KR20190115698 A KR 20190115698A
- Authority
- KR
- South Korea
- Prior art keywords
- coating composition
- coating
- film
- inorganic coating
- layer
- Prior art date
Abstract
Description
본 발명은 도료 조성물에 관한 것으로서, 보다 상세하게는 뛰어난 코팅 성능을 갖고 있으면서 투명하게 시공 가능하며, 빛이 코팅층에 의해 반사되는 문제를 제거할 수 있는 실사필름 코팅용 무기질 도료 조성물 및 이를 이용한 경관형 마감층 시공 방법에 관한 것이다.The present invention relates to a coating composition, and more particularly, having an excellent coating performance, and can be transparently installed, and an inorganic coating composition for live action film coating capable of eliminating a problem in which light is reflected by the coating layer and a landscape type using the same. It is about a method of constructing a finishing layer.
인도, 자전거 도로, 건축물 바닥면, 벽면 등은 블록시공을 하거나 또는 도료 등을 사용하여 그 외장을 마감하고 있다. 이와 같은 마감층용 도료는 통상적으로 내구성, 내수성, 난연성, 내오염성 등 여러 가지 성능이 필요하다.Sidewalks, bicycle paths, building floors, walls, etc. are covered with blocks or with paint to finish the exterior. Paint for such a finishing layer typically requires a variety of performance, such as durability, water resistance, flame retardancy, pollution resistance.
종래에는 이러한 도료 조성물로 에폭시계 수지, 우레탄계 수지, 아크릴계 수지 등과 같은 유기 수지를 주성분으로 하는 유기 도료를 주로 사용하여 왔다. 이러한 유기 도료들은 가공성, 접착성, 유연성 등이 우수하다는 장점이 있으나, 도막을 형성하는 유기물이 자외선에 의해 변질되기 쉽고, 수분 흡수에 의한 열화가 일어나는 등 내구성이 떨어지며, 내열성이 낮고, 기름과 같은 유기 물질이 혼입되어 오염되기 쉽다는 문제점이 있었다.Conventionally, as such a coating composition, the organic coating which mainly consists of organic resins, such as an epoxy resin, urethane resin, acrylic resin, etc., has been mainly used. These organic paints have the advantages of excellent processability, adhesion, flexibility, etc., but organic materials forming the coating film are easily deteriorated by ultraviolet rays, deteriorated due to moisture absorption, and have low durability, low heat resistance, oil-like properties, and the like. There was a problem that organic substances are easily mixed and contaminated.
또한, 유기 도료의 경우, 도료 제조시 또는 도막 형성시에 유해한 유기 휘발분이 발생하여 대기 오염의 원인이 될 뿐 아니라, 일단 도막이 형성되면 자연적으로 분해되지 않아 산업 폐기물을 발생시키기 때문에 환경적으로 바람직하지 않다.In addition, in the case of organic paints, harmful organic volatiles are generated during paint production or coating film formation, causing air pollution, and once the coating film is formed, it is not environmentally preferable because it does not decompose naturally and generates industrial waste. not.
최근에는 이러한 유기 도료의 단점을 극복하기 위해, 세라믹, 변성 실리콘, 물유리와 같은 무기 성분을 이용한 도료 개발이 적극적으로 시도되고 있다. 이러한 무기 성분을 이용한 도료들은 유기 도료에 비해 자외선이나 수분 흡수에 대한 저항성이 우수하며, 내구성이 강하고, 유기 물질과의 상용성이 나쁘기 때문에 오염에 강하며, 유독성 유기 물질을 거의 사용하지 않기 때문에 친환경적이라는 장점이 있다.Recently, in order to overcome the disadvantages of such organic paints, development of paints using inorganic components such as ceramics, modified silicon, and water glass has been actively attempted. Paints using these inorganic components are more resistant to UV and moisture absorption than organic paints, are more durable, are more resistant to contamination due to poor compatibility with organic materials, and are environmentally friendly because they use little toxic organic materials. There is an advantage.
여러 가지 무기 성분들 중에서도 특히 물유리는 저가이고, 접착성 및 난연성이 우수하여, 무기 도료의 주성분으로 폭넓게 이용되고 있다. 그러나, 물유리는 친수성이기 때문에 장시간 물에 노출될 경우, 도막이 쉽게 손상된다는 문제점이 있으며, 그 결과 내수성이 요구되는 분야에는 사용이 제한되어 왔다. 또한, 경화를 위해 고온이 요구되는 등 도막 형성이 쉽지 않아 상용화에 제약이 되고 있다.Among various inorganic components, especially water glass is inexpensive, has excellent adhesiveness and flame retardancy, and is widely used as a main component of inorganic paints. However, since water glass is hydrophilic, there is a problem in that the coating film is easily damaged when exposed to water for a long time, and as a result, its use has been limited in fields requiring water resistance. In addition, it is difficult to form a coating film such as high temperature is required for curing, which is a limitation in commercialization.
한편, 소정의 그림, 문양 등이 인쇄되어 있는 실사필름으로 마감층을 형성할 경우, 이 실사필름의 보호를 위해 코팅층이 형성되어야 한다. 그런데, 실사필름에 형성되는 코팅층은 투명하게 시공 가능해야 이 실사필름에 인쇄되는 그림 내지 색채 등을 시각적으로 연출할 수 있게 된다.On the other hand, in the case of forming a finish layer with a realistic film on which a predetermined picture, pattern, etc. are printed, a coating layer should be formed to protect the optical film. By the way, the coating layer formed on the live-action film should be able to be transparently constructed to visually produce a picture or color printed on the live-action film.
결국, 실사필름을 이용한 마감층(이하, '경관형 마감층'이라 함)은 외부환경으로부터 실사필름을 보호할 수 있는 코팅성능은 물론 투명성도 함께 확보할 수 있어야 한다.As a result, the finishing layer using the optical film (hereinafter, referred to as the 'ceiling type finishing layer') should be able to secure transparency as well as coating performance to protect the actual film from the external environment.
또한, 실사필름에 도료 조성물을 코팅하면, 코팅층 표면이 매우 고르기 때문에 빛이 이 코팅층 표면에 반사되고, 이에 의해 실사필름에 인쇄된 그림의 외부연출 및 감상이 제대로 이루어지지 못하는 문제가 발생할 수 있다.In addition, when the coating composition is coated on the optical film, light may be reflected on the surface of the coating layer because the surface of the coating layer is very even, and thus, external drawing and viewing of the picture printed on the optical film may not be performed properly.
본 발명의 목적은 실사필름 위에 코팅층을 투명하게 시공 가능하여 다양한 그림 및 색채를 연출할 수 있으면서, 동시에 친환경성, 내화학성, 내마모성, 내오염성, 발수성, 내후성 등의 우수한 코팅성능을 구현할 수 있는 실사필름 코팅용 무기질 도료 조성물 및 이를 이용한 경관형 마감층 시공 방법을 제공하는 것이다.An object of the present invention is to produce a coating layer on the optical film transparently to produce a variety of pictures and colors, while at the same time an environmentally friendly film, chemical resistance, abrasion resistance, fouling resistance, water repellency, weather resistance that can realize excellent coating performance, such as weather resistance It is to provide an inorganic coating composition for coating and landscape finishing layer construction method using the same.
본 발명의 또 다른 목적은 빛이 코팅층에 의해 반사되는 문제를 제거할 수 있어, 빛 반사에 의해 실사필름의 그림의 외부연출 및 시인성이 저해되는 문제를 해결할 수 있는 실사필름 코팅용 무기질 도료 조성물 및 이를 이용한 경관형 마감층 시공 방법을 제공하는 것이다.Another object of the present invention can eliminate the problem that the light is reflected by the coating layer, the inorganic coating composition for the actual film coating for solving the problem that the external rendering and visibility of the picture of the optical film due to light reflection and It is to provide a landscape finishing layer construction method using the same.
본 발명에 따른 실사필름 코팅용 무기질 도료 조성물은 메틸트리메톡시실란 10 ~ 20 중량%와; γ-글리시독시프로필트리메톡시실란 10 ~ 20 중량%와; 이산화티타늄 20 ~ 30 중량%와; 실리카 10 ~ 15 중량%; 및 폴리옥시프로필렌디아민 20 ~ 30 중량%를 포함한다.The inorganic coating composition for the actual optical film coating according to the present invention comprises 10 to 20 wt% of methyltrimethoxysilane; 10 to 20% by weight of γ-glycidoxypropyltrimethoxysilane; 20 to 30% by weight of titanium dioxide; 10-15 weight percent silica; And 20-30 wt% of polyoxypropylenediamine.
바람직하게는, 메틸트리메톡시실란과 γ-글리시독시프로필트리메톡시실란은 중량비 기준으로 1:1 비율로 혼합될 수 있다.Preferably, methyltrimethoxysilane and γ-glycidoxypropyltrimethoxysilane may be mixed in a 1: 1 ratio by weight.
바람직하게는, 이산화티타늄과 실리카는 중량비 기준으로 2:1 비율로 혼합될 수 있다.Preferably, titanium dioxide and silica may be mixed in a 2: 1 ratio by weight.
본 발명에 따른 경관형 마감층 시공 방법은 인도, 도로, 건축물의 바닥면 또는 건축물 벽면에 하도층을 형성하는 단계와; 상기 하도층 위에 실사필름을 부착하는 단계와; 상기 실사필름 위에 본 발명의 무기질 도료 조성물을 도포하여 코팅층을 형성하는 단계; 및 상기 코팅층을 건조 및 경화시키는 단계를 포함한다.Landscape type finishing layer construction method according to the present invention comprises the steps of forming a sub-floor layer on the floor surface of the sidewalk or building, road, building; Attaching a live-action film on the undercoat; Forming a coating layer by coating the inorganic coating composition of the present invention on the optical film; And drying and curing the coating layer.
본 발명에 따른 실사필름 코팅용 무기질 도료 조성물 및 이를 이용한 경관형 마감층 시공 방법에 의하면, 종래 유기 도료에서 발생되는 중금속, TVOC 및 HCHO 등의 독성 없이 내화학성, 내마모성, 내오염성, 발수성, 내후성 등이 뛰어난 코팅층을 구현할 수 있으면서 또한 도료를 투명하게 제조할 수 있게 되었다.According to the inorganic coating composition for the actual film coating according to the present invention and the method for constructing a landscape finish layer using the same, chemical resistance, abrasion resistance, fouling resistance, water repellency, weather resistance, etc. This excellent coating layer can be realized and the paint can be made transparent.
이에 따라, 본 발명의 도료 조성물은 바닥, 벽면 등의 마감층의 상도층으로 사용할 수 있고, 특히 도료의 투명성으로 인해 다양한 그림 및 칼라 등의 시각적 디자인을 연출할 수 있으며, 더 나아가 빛 반사에 의해 실사필름의 그림/칼라 등의 외부연출 및 시인성이 저해되는 문제를 해결할 수 있어 마감층의 경관 효과를 극대화할 수 있는 효과가 있다.Accordingly, the coating composition of the present invention can be used as a top coat layer of the finishing layer, such as floor, wall surface, and in particular, due to the transparency of the paint can produce a visual design, such as a variety of pictures and colors, and further due to light reflection It can solve the problem that the external rendering and visibility of film, color, etc. are impaired, thereby maximizing the landscape effect of the finishing layer.
도 1은 본 발명에 따른 실사필름 코팅용 무기질 도료 조성물의 TVOC 및 폼알데히드 방출량 시험 성적서.
도 2는 본 발명에 따른 실사필름 코팅용 무기질 도료 조성물의 중금속 검출 여부 시험 성적서.
도 3은 본 발명에 따른 실사필름 코팅용 무기질 도료 조성물의 내오염성 시험 성적서.
도 4는 본 발명에 따른 실사필름 코팅용 무기질 도료 조성물의 발수기능을 보여주는 사진.
도 5는 본 발명에 따른 이산화티타늄-실리카 미소캡슐의 개략적 단면도.
도 6은 나노 배합액과 매크로 배합액의 비교 실험예.
도 7은 본 발명에 따른 실사필름 코팅용 무기질 도료 조성물을 이용하여 건물 바닥면에 경관형 마감층을 시공한 모습을 보여주는 사진.1 is a TVOC and formaldehyde emission test report of the inorganic coating composition for live-action film coating according to the present invention.
Figure 2 is a heavy metal detection test report of the inorganic coating composition for live-action film coating according to the present invention.
Figure 3 is a stain resistance test report of the inorganic coating composition for the live-action film coating according to the present invention.
Figure 4 is a photograph showing the water-repellent function of the inorganic coating composition for the live-action film coating according to the present invention.
5 is a schematic cross-sectional view of a titanium dioxide-silica microcapsules according to the present invention.
6 is a comparative experimental example of a nano compounding solution and a macro compounding solution.
Figure 7 is a photograph showing the construction of a landscape finish layer on the building floor using the inorganic coating composition for live-action film coating according to the present invention.
본 명세서에서 사용하는 용어는 단지 특정한 실시예를 설명하기 위해 사용된 것으로, 본 발명을 한정하려는 의도가 아니다. 단수의 표현은 문맥상 명백하게 다르게 뜻하지 않는 한, 복수의 표현을 포함한다. 본 명세서에서, "포함하다" 또는 "가지다" 등의 용어는 명세서상에 기재된 특징, 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것이 존재함을 지정하려는 것이지, 하나 또는 그 이상의 다른 특징들이나 숫자, 단계, 동작, 구성요소, 부품 또는 이들을 조합한 것들의 존재 또는 부가 가능성을 미리 배제하지 않는 것으로 이해되어야 한다.The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. Singular expressions include plural expressions unless the context clearly indicates otherwise. As used herein, the terms "comprise" or "have" are intended to indicate that there is a feature, number, step, action, component, part, or combination thereof described on the specification, and one or more other features. It is to be understood that the present invention does not exclude the possibility of the presence or the addition of numbers, steps, operations, components, components, or a combination thereof.
또한, 본 명세서에서, "~ 상에 또는 ~ 상부에" 라 함은 대상 부분의 위 또는 아래에 위치함을 의미하는 것이며, 반드시 중력 방향을 기준으로 상 측에 위치하는 것을 의미하는 것은 아니다. 또한, 영역, 판 등의 부분이 다른 부분 "상에 또는 상부에" 있다고 할 때, 이는 다른 부분 "바로 상에 또는 상부에" 접촉하여 있거나 간격을 두고 있는 경우뿐 아니라 그 중간에 또 다른 부분이 있는 경우도 포함한다.In addition, in the present specification, "on or above" means to be located above or below the target portion, and does not necessarily mean to be located above the gravity direction. In addition, when a portion such as an area, a plate, etc. is said "on or on top of" another part, it is not only in contact with or spaced apart from another part, but also in the middle of another part. This includes any case.
또한, 본 명세서에서, 일 구성요소가 다른 구성요소와 "연결된다" 거나 "접속된다" 등으로 언급된 때에는, 상기 일 구성요소가 상기 다른 구성요소와 직접 연결되거나 또는 직접 접속될 수도 있지만, 특별히 반대되는 기재가 존재하지 않는 이상, 중간에 또 다른 구성요소를 매개하여 연결되거나 또는 접속될 수도 있다고 이해되어야 할 것이다.In addition, in the present specification, when one component is referred to as "connected" or "connected" with another component, the one component may be directly connected or directly connected to the other component, but in particular It is to be understood that, unless there is an opposite substrate, it may be connected or connected via another component in the middle.
또한, 본 명세서에서, 제1, 제2 등의 용어는 다양한 구성요소들을 설명하는데 사용될 수 있지만, 상기 구성요소들은 상기 용어들에 의해 한정되어서는 안 된다. 상기 용어들은 하나의 구성요소를 다른 구성요소로부터 구별하는 목적으로만 사용된다.Also, in this specification, terms such as first and second may be used to describe various components, but the components should not be limited by the terms. The terms are used only for the purpose of distinguishing one component from another.
본 발명은 무독성의 실사필름 위에 코팅층을 투명하게 시공 가능하여 다양한 그림 및 색채를 연출할 수 있으면서, 동시에 친환경성, 내화학성, 내마모성, 내오염성, 발수성, 내후성 등의 우수한 코팅성능을 구현할 수 있고, 더 나아가 빛이 투명 코팅층에 의해 반사되는 현상을 크게 감소시킬 수 있어, 빛 반사에 의해 실사필름의 그림의 시인성이 저해되는 문제를 제거할 수 있는 실사필름 코팅용 무기질 도료 조성물을 제시한다.The present invention can produce a variety of paintings and colors by transparently coating the coating layer on the non-toxic realistic film, and at the same time can realize excellent coating performance, such as environmentally friendly, chemical resistance, wear resistance, pollution resistance, water repellency, weather resistance, and more Furthermore, the phenomenon in which the light is reflected by the transparent coating layer can be greatly reduced, and the present invention provides an inorganic coating composition for the actual film coating, which can eliminate the problem that visibility of the picture of the actual film is impaired by the light reflection.
상기와 같은 목적을 달성하기 위한 본 발명의 실사필름 코팅용 무기질 도료 조성물은 γ-글리시독시프로필트리메톡시실란 10 ~ 20 중량, 메틸트리메톡시실란 10 ~ 20 중량%, 이산화티타늄 20 ~ 30 중량%, 실리카 10 ~ 15 중량%, 및 폴리옥시프로필렌디아민 20 ~ 30 중량%를 포함하는 것을 특징으로 한다.Inorganic coating composition for the actual optical film coating of the present invention for achieving the above object is γ-glycidoxy propyltrimethoxysilane 10 to 20% by weight, methyltrimethoxysilane 10 to 20% by weight, titanium dioxide 20 to 30 It comprises a weight percent, 10 to 15 weight percent silica, and 20 to 30 weight percent polyoxypropylenediamine.
더 나아가, 본 발명의 도료 조성물은 그 투명도를 더욱 높이고자할 경우, 이산화티타늄과 실리카를 미소캡슐 형태로 형성할 수 있으며, 상기 경우 이산화티타늄과 실리카로 이루어진 미소캡슐은 나노 사이즈로 제조되어 도료 조성물 내에 분산된 구조로 혼합 배치된다.Furthermore, the coating composition of the present invention may form titanium dioxide and silica in the form of microcapsules in order to further increase the transparency thereof, and in this case, the microcapsules made of titanium dioxide and silica may be manufactured in a nano-size coating composition. It is mixed and arranged in a structure dispersed within.
이하에서, 첨부된 도면을 참조하여 본 발명의 바람직한 실시예, 장점 및 특징에 대하여 상세히 설명하도록 한다.Hereinafter, with reference to the accompanying drawings will be described in detail a preferred embodiment, advantages and features of the present invention.
본 발명의 γ-글리시독시프로필트리메톡시실란(γ-glycidoxypropyl trimethoxy silane)은 글리시독시 반응성유기기 및 트리메톡시시릴 무기기가 함유된 이작용기성 실란으로서, 본 발명의 무기질 도료 조성물에 따른 코팅층의 접착력, 내구성 및 강도를 향상시키고 점도를 낮추는 기능을 한다.Γ-glycidoxypropyl trimethoxy silane of the present invention is a difunctional silane containing a glycidoxy reactive organic group and a trimethoxysilyl inorganic group, and according to the inorganic coating composition of the present invention. It improves the adhesion, durability and strength of the coating layer and serves to lower the viscosity.
감마-글리사이독시프로필트리메톡시실란(gamma-glycidoxypropyltrimethoxy silane)의 조성비는 10 ~ 20 중량%로 구성되고, 바람직하게는 13 ~ 17중량%로 구성될 수 있다.The composition ratio of gamma-glycidoxypropyltrimethoxy silane is composed of 10 to 20% by weight, preferably 13 to 17% by weight.
γ-글리시독시프로필트리메톡시실란의 함량이 20 중량%를 초과하면, 그 초과량 대비 본 발명의 무기질 도료 조성물(즉, 코팅층)의 접착력 향상 효과가 미미하고, 오히려 내수성 및 내식성 등이 저하될 수 있다. γ-글리시독시프로필트리메톡시실란의 함량이 10 중량% 미만이면, 실사필름에 대한 코팅층의 견고한 부착 상태를 보장하기 위한 최소한의 접착력을 만족할 수 없게 되고, 무기질 도료 조성물의 점도가 너무 높아져 코팅층 시공성이 저하된다. 참고로, 본 발명의 무기질 도료 조성물의 점도는 50 ~ 150 cps로 형성되는 것이 바람직하다.When the content of γ-glycidoxypropyltrimethoxysilane exceeds 20% by weight, the effect of improving the adhesion of the inorganic coating composition (i.e., coating layer) of the present invention is insignificant compared to that amount, and rather water resistance and corrosion resistance are reduced. Can be. If the content of γ-glycidoxypropyltrimethoxysilane is less than 10% by weight, the minimum adhesion to ensure a firm adhesion state of the coating layer to the live-action film cannot be satisfied, and the viscosity of the inorganic coating composition becomes so high that the coating layer Workability falls. For reference, the viscosity of the inorganic coating composition of the present invention is preferably formed in 50 ~ 150 cps.
본 발명의 메틸트리메톡시실란(methyltrimethoxy silane)은 본 발명의 무기질 도료 조성물에 따른 코팅층의 내화학성, 내마모성 및 발수성을 향상시키기 위한 성분으로서, 그 조성비는 10 ~ 20 중량%로 구성되고, 바람직하게는 13 ~ 17중량%로 구성될 수 있다.Methyltrimethoxy silane of the present invention is a component for improving the chemical resistance, abrasion resistance and water repellency of the coating layer according to the inorganic coating composition of the present invention, the composition ratio is composed of 10 to 20% by weight, preferably May be composed of 13 to 17% by weight.
메틸트리메톡시실란의 함량이 20 중량%를 초과하면 반응 후 내수성이 떨어질 수 있고, 10 중량% 미만이면 코팅층의 내마모성 및 내화학성이 크게 저하되어 실사필름용 코팅층으로써 부적합하게 된다.If the content of the methyltrimethoxysilane exceeds 20% by weight may lower the water resistance after the reaction, if less than 10% by weight of the coating layer greatly reduces the wear resistance and chemical resistance of the coating film for the live action film is not suitable.
바람직한 실시예에 따르면, 메틸트리메톡시실란은 중량비 기준으로 γ-글리시독시프로필트리메톡시실란과 1:1 비율로 혼합되는 것을 가장 좋다.According to a preferred embodiment, methyltrimethoxysilane is best mixed with γ-glycidoxypropyltrimethoxysilane in a 1: 1 ratio by weight.
본 발명의 이산화티타늄(TiO2)은 본 발명의 무기질 도료 조성물의 내변색성을 향상시키고, 특히 실리카와 함께 작용하여 빛이 투명 코팅층에 의해 반사되는 현상(이하, "빛 반사 현상"이라 칭함)을 제거하는 기능을 한다.Titanium dioxide (TiO 2 ) of the present invention improves the discoloration resistance of the inorganic coating composition of the present invention, and in particular, works with silica to reflect light by the transparent coating layer (hereinafter referred to as "light reflection phenomenon") To function.
이산화티타늄(TiO2)의 조성비는 20 ~ 30 중량%로 구성되고, 바람직하게는 24 ~ 26 중량%로 구성될 수 있다. 이산화티타늄의 함량이 30 중량%를 초과하면, 본발명의 도료 조성물의 투명성이 급감하여 그 함량이 점차 증가할수록 불투명의 흰색을 띠게 되고, 이로 인해 실사필름용 코팅재로 사용할 수 없게 된다. 한편, 이산화티타늄의 함량이 20 중량% 미만이면 빛 반사 현상 제거 효과가 미미하게 된다.The composition ratio of titanium dioxide (TiO 2 ) is 20 to 30% by weight, preferably 24 to 26% by weight. When the content of titanium dioxide exceeds 30% by weight, the transparency of the coating composition of the present invention is sharply reduced and the content thereof gradually increases to have an opaque white color, and thus cannot be used as a coating material for a live action film. On the other hand, when the content of titanium dioxide is less than 20% by weight, the light reflection phenomenon removing effect is insignificant.
본 발명의 실리카(SiO2)는 본 발명의 무기질 도료 조성물의 마모 및 얼룩에 대한 내성을 향상시키고, 특히 이산화티타늄(TiO2)과 함께 작용하여 빛 반사 현상을 제거하는 기능을 한다.The silica (SiO 2 ) of the present invention improves resistance to abrasion and staining of the inorganic coating composition of the present invention, and in particular, works with titanium dioxide (TiO 2 ) to remove light reflection phenomenon.
실리카(SiO2)의 조성비는 10 ~ 15 중량%로 구성되고, 바람직하게는 12 ~ 13 중량%로 구성될 수 있다. 이는, 실리카는 중량비 기준으로 이산화티타늄과 1:2 (실리카:이산화티타늄) 비율로 혼합될 때, 본 발명의 도료 조성물의 투명성을 보장하면서 동시에 전술한 빛 반사 현상을 유의미한 수준으로 감소시킬 수 있기 때문이다. 여기서, 상기 "유의미한 수준"이란, 실사필름에 인쇄된 그림을 안견시, 코팅층에 의해 빛이 반사되는 현상을 시각적으로 거의 느끼지 못하는 수준을 의미한다.The composition ratio of silica (SiO 2 ) is 10 to 15% by weight, preferably 12 to 13% by weight. This is because, when silica is mixed with titanium dioxide in a ratio of 1: 2 (silica: titanium dioxide) by weight ratio, it is possible to ensure the transparency of the coating composition of the present invention while reducing the aforementioned light reflection phenomenon to a significant level. to be. Here, the "significant level" refers to a level that visually hardly feels a phenomenon in which light is reflected by the coating layer when looking at a picture printed on a live-action film.
본 발명의 이산화티타늄과 실리카에 의한 빛 반사 현상 제거 작용에 대하여 설명하면 다음과 같다.Referring to the light reflection phenomenon removal effect by the titanium dioxide and silica of the present invention will be described.
대기의 굴절률은 1.0이고, 이산화티타늄(TiO2)은 2.55~2.76의 고굴절률을 갖으며, 실리카(SiO2)는 1.46의 저굴절률을 갖는다. 따라서, 실사필름 코팅층(즉, 본 발명의 무기질 도료 조성물)으로 빛이 입사되면, 이에 분산 혼합되어 있는 이산화티타늄 입자) 의해 일부 빛은 굴절률이 증가된 후 실리카 입자에 의해 굴절률이 낮아지는 과정을 반복하게 된다. 그리고, 상기 과정이 다수 회 반복되면 종국에는 굴절률이 1.0에 가까워져 코팅층의 빛 반사 현상을 대폭 감소시킬 수 있게 된다.Atmospheric refractive index is 1.0, titanium dioxide (TiO 2 ) has a high refractive index of 2.55 ~ 2.76, silica (SiO 2 ) has a low refractive index of 1.46. Therefore, when light is incident on the live-film coating layer (ie, the inorganic coating composition of the present invention), some light is repeated by the silica particles after the refractive index is increased by the titanium dioxide particles dispersed and mixed therewith. Done. In addition, if the process is repeated many times, the refractive index eventually approaches 1.0, thereby greatly reducing the light reflection phenomenon of the coating layer.
본 발명의 폴리옥시프로필렌디아민(polyoxypropylenediamine)은 코팅층의 신율과 인장강도를 조절하고, 수분 안정성과 강도 증가를 위한 성분으로서, 그 조성비는 20 ~ 30 중량%로 구성되고, 바람직하게는 23 ~ 27 중량%로 구성될 수 있다.Polyoxypropylenediamine of the present invention is to control the elongation and tensile strength of the coating layer, and to increase the moisture stability and strength, the composition ratio is composed of 20 to 30% by weight, preferably 23 to 27% by weight It may consist of%.
폴리옥시프로필렌디아민의 함량이 20 중량% 미만이면 신율이 떨어져 실사필름 코팅재로써 적합하지 못하게 되고, 30 중량%를 초과하면 신율과 인장강도는 증가하나 내마모성이 떨어져 결국 코팅층의 내구성 및 수명 저하를 초래하게 된다.If the content of polyoxypropylene diamine is less than 20% by weight, the elongation is lowered, making it unsuitable as a film coating material. If the content of the polyoxypropylene diamine is exceeded, the elongation and tensile strength of the polyoxypropylene diamine is increased, but the wear resistance is decreased, resulting in a decrease in durability and life of the coating layer. do.
이하에서는, 본 발명의 무기질 도료 조성물의 실시예 및 그 측정결과에 대하여 설명하도록 한다.Hereinafter, the Example and the measurement result of the inorganic coating composition of this invention are demonstrated.
실시예Example 1 : 무기질 도료 조성물의 제조 및 코팅층 형성 1: Preparation of inorganic coating composition and coating layer formation
- 메틸트리메톡시실란(제품명:OFS-6070,다우코닝)과 γ-글리시독시프로필트리메톡시실란(제품명:OFS-6040,다우코닝)을 1:1 중량비로 혼합하고, 실리카 (MIL-U-SIL)와 이산화티타늄을 1:2 중량비로 혼합하고, 폴리옥시프로필렌디아민 25 중량%를 혼합하여 점도 125 cps at 25℃의 무기질 도료 조성물을 제조하였다.Methyltrimethoxysilane (product name: OFS-6070, Dow Corning) and γ-glycidoxypropyltrimethoxysilane (product name: OFS-6040, Dow Corning) are mixed in a 1: 1 weight ratio, and silica (MIL- U-SIL) and titanium dioxide were mixed in a 1: 2 weight ratio, and 25 wt% of polyoxypropylene diamine was mixed to prepare an inorganic coating composition having a viscosity of 125 cps at 25 ° C.
그리고, 제조된 무기질 도료 조성물을 필름재에 도포한 후 지촉건조 4시간, 고화건조 48시간, 완전경화 3일을 거쳐 코팅층을 형성하였다.Then, after coating the prepared inorganic coating composition on the film material, the coating layer was formed after 4 hours of dry touch, 48 hours of solidification and 3 days of complete curing.
측정결과 1 : 무기질 도료 조성물의 특성(1)Measurement Result 1: Properties of Inorganic Coating Composition (1)
실시예 1에 따른 무기질 도료 조성물을 통해 형성한 코팅층의 성능을 측정하였으며, 그 결과는 다음의 표 1과 같다.The performance of the coating layer formed through the inorganic coating composition according to Example 1 was measured, and the results are shown in Table 1 below.
표 1에 나타나듯이, 본 발명의 무기질 도료 조성물에 따른 코팅층은 경도, 내수성, 내염수성 및 내화학성이 우수하고, 도 4에서 나타나듯이 발수기능을 갖고 있어, 실사필름 코팅재로써 적합함을 알 수 있다.As shown in Table 1, the coating layer according to the inorganic coating composition of the present invention is excellent in hardness, water resistance, saline and chemical resistance, and has a water repellent function as shown in Figure 4, it can be seen that it is suitable as a realistic film coating material. .
측정결과 2 : 무기질 도료 조성물의 특성(2)Result of measurement 2: Properties of the inorganic coating composition (2)
실시예 1에 따른 무기질 도료 조성물의 TVOC, 폼알데히드의 방출량 및 중금속 검출 여부를 측정하였으며 그 결과는 도 1,2와 같다.TVOC, the release amount of formaldehyde and the detection of heavy metals of the inorganic coating composition according to Example 1 were measured and the results are shown in FIGS.
그리고, 실시예 1에 따른 무기질 도료 조성물의 내오염성을 측정하였으며 그 결과는 표 2 및 도 3과 같다.And, the contamination resistance of the inorganic coating composition according to Example 1 was measured, and the results are shown in Table 2 and FIG. 3.
참고로, 도 1 ~ 도 3의 측정은 한국화학융합시험연구원에 의뢰하였다.For reference, the measurement of FIGS. 1 to 3 was commissioned by the Korea Institute of Chemical Fusion Testing.
도 1,2에 나타나듯이, 본 발명에 따라 제조되는 무기질 도료 조성물은 인체에 유해한 TVOC, 폼알데히드 및 중금속(Pb, Cd, Hg, Cr(VI))을 포함하지 않는 친환경재임을 알 수 있다.As shown in Figures 1 and 2, it can be seen that the inorganic coating composition prepared according to the present invention is an environmentally friendly material that does not contain harmful TVOC, formaldehyde and heavy metals (Pb, Cd, Hg, Cr (VI)).
또한, 표 2 및 도 3에 나타나듯이 본 발명에 따라 제조되는 무기질 도료 조성물은 내오염성이 우수하여 실사필름 코팅재로써 적합함을 알 수 있다.In addition, as shown in Table 2 and Figure 3 it can be seen that the inorganic coating composition prepared according to the present invention is excellent in stain resistance and suitable as a realistic film coating material.
본 발명의 도료 조성물의 투명도를 더욱 높이고자할 경우, 이산화티타늄과 실리카를 미소캡슐 형태로 형성할 수 있으며, 상기 경우 이산화티타늄과 실리카로 이루어진 미소캡슐은 나노 사이즈로 제조되어 도료 조성물 내에 분산된 구조로 혼합 배치된다.In order to further increase the transparency of the coating composition of the present invention, titanium dioxide and silica may be formed in the form of microcapsules, and in this case, the microcapsules made of titanium dioxide and silica are manufactured in nano size and dispersed in the coating composition. Are placed into the mix.
이하에서는, 이산화티타늄(TiO2)과 실리카(SiO2)를 미소캡슐 형태로 형성하는 경우에 대하여 상세히 설명하도록 한다.Hereinafter, a case in which titanium dioxide (TiO 2 ) and silica (SiO 2 ) are formed in a microcapsule form will be described in detail.
도 5는 본 발명에 따른 이산화티타늄-실리카 미소캡슐의 개략적 단면도이다.도 5를 참조하면, 이산화티타늄(TiO2)과 실리카(SiO2)는 다수의 이산화티타늄 미립자(11)와 다수의 실리카 미립자(13)로 이루어진 코어물질과, 상기 코어물질을 감싸는 수지 재질의 외벽(15)을 포함하는 미소캡슐(10) 형태로 형성될 수 있다.5 is a titanium dioxide in accordance with the present invention - a schematic cross-sectional view of a silica microcapsule 5, a titanium dioxide (TiO 2) and silica (SiO 2) has a plurality of titanium dioxide particles 11 and the plurality of fine particles of silica It may be formed in the form of a microcapsule 10 including a core material (13) and an outer wall 15 of a resin material surrounding the core material.
그리고, 이와 같은 미소캡슐(10)은 200nm 이하의 평균직경을 갖도록 형성되어 분산 배치되어 있는 것을 특징으로 한다.The microcapsules 10 are characterized in that they are formed and dispersed so as to have an average diameter of 200 nm or less.
도 6은 나노 배합액과 매크로 배합액의 비교 실험예로서, 도 6의 좌측 바이알 병에 담겨있는 시료는 미소캡슐을 120㎚의 평균직경 사이즈로 형성하여 액상수지에 혼합한 나노 배합액이고, 우측 바이알 병에 담겨있는 시료는 10㎛의 평균직경 사이즈로 이루어진 미소캡슐을 액상수지에 혼합한 매크로 배합액이다.6 is a comparative experimental example of a nano compounding solution and a macro compounding solution. The sample contained in the left vial bottle of FIG. 6 is a nano compounding solution in which microcapsules were formed in an average diameter of 120 nm and mixed in a liquid resin. The sample contained in the vial bottle is a macro compound solution in which a microcapsule having an average diameter of 10 μm is mixed with a liquid resin.
도 6의 비교 실험 예에서 명확히 나타나듯이, 좌측의 나노 배합액 시료는 투명하게 보이는 반면, 우측의 매크로 배합액 시료는 백색으로 불투명하게 보이는 것을 알 수 있다.As clearly shown in the comparative experimental example of FIG. 6, it can be seen that the sample of the nano compound solution on the left is transparent while the sample of the macro compound solution on the right is opaque white.
즉, 이산화티타늄-실리카 미소캡슐(10)을 가시광선의 파장보다 작은 나노 사이즈(바람직하게는 가시광선 파장 범위(400nm ~ 800nm)보다 1/4 이하로 작은 나노 사이즈)로 형성하게 되면 해당 시료로 입사되는 가시광선의 일부가 온전히 투과됨을 알 수 있다.That is, when the titanium dioxide-silica microcapsules 10 are formed in a nano size smaller than the wavelength of visible light (preferably nano size smaller than 1/4 of the visible light wavelength range (400 nm to 800 nm)), they enter the sample. It can be seen that some of the visible light is completely transmitted.
결국, 본 발명의 무기질 도료 조성물이 실사필름 위에 도포되면, 200nm 이하의 평균직경을 갖는 이산화티타늄-실리카 미소캡슐(10)이 혼합된 코팅층으로 형성된다.As a result, when the inorganic coating composition of the present invention is applied on the actual optical film, the titanium dioxide-silica microcapsules 10 having an average diameter of 200 nm or less are formed as a mixed coating layer.
그리고, 이산화티타늄-실리카 미소캡슐(10)이 코팅층(즉, 무기질 도료 조성물) 내에 존재하더라도 이 코팅층은 특정한 색(예컨대, 흰색)을 띠거나 불투명한 성질을 나타내지 않고 여전히 투명성을 발현할 수 있어 실사필름의 색감을 방해하지 않으면서 전술한 빛 반사 현상을 제거할 수 있게 된다.In addition, even if the titanium dioxide-silica microcapsules 10 are present in the coating layer (ie, the inorganic coating composition), the coating layer may still exhibit transparency without having a specific color (eg, white color) or exhibiting an opaque property. The aforementioned light reflection phenomenon can be eliminated without disturbing the color of the film.
이산화티타늄-실리카 미소캡슐(10)은 다수의 이산화티타늄 미립자(11)와 다수의 실리카 미립자(13)로 이루어진 코어물질을 준비한 후, 쉘 물질로 외벽(15)을 형성함으로써 대략 구형의 캡슐 형태가 제조된다.The titanium dioxide-silica microcapsules 10 prepare a core material composed of a plurality of titanium dioxide fine particles 11 and a plurality of silica fine particles 13, and then form an outer wall 15 with a shell material to form a substantially spherical capsule. Are manufactured.
미소캡슐(10)은 계면중합법 등의 화학적 방법, 비용매 첨가나 pH의 제어에 의해 외벽 물질의 용해도를 변화시켜 석출시키는 코아서베이션(coacervation), 가온·감압 등에 의해 외벽(15)물질의 용매를 제거하여 피막을 형성하는 계면침전법 등의 물리화학적 방법, 또는 분무건조법 등의 기계적 방법 등을 통해 제조할 수 있다.The microcapsules 10 are prepared by chemical methods such as interfacial polymerization, non-solvent addition or pH control to coarse the precipitates by varying the solubility of the outer wall material and depositing them. It may be produced by a physicochemical method such as an interfacial precipitation method or a mechanical method such as spray drying to remove a solvent to form a film.
코어물질은 코팅층(30)에 의해 반사되는 빛의 양을 감소시키기 위한 구성으로서, 다수의 이산화티타늄 미립자(11)와 다수의 실리카 미립자(13)를 포함한다.The core material is configured to reduce the amount of light reflected by the coating layer 30 and includes a plurality of titanium dioxide fine particles 11 and a plurality of silica fine particles 13.
외벽(15)은 수지로 형성되는 것을 특징으로 한다. 지용성 수지는 초기에 미립자 형태로 이루어진 코어물질의 외면을 둘러싸게 되고, 결국 코어물질은 이러한 외벽(15) 내부에 갇힌 상태로 존재하게 된다.The outer wall 15 is characterized in that formed of resin. The fat-soluble resin initially surrounds the outer surface of the core material, which is in the form of particulates, and eventually the core material remains trapped inside the outer wall 15.
외벽(15)은 수지 재질로 형성될 수 있고, 바람직하게는 투명한 지용성 고분자로 형성될 수 있다. 예컨대, 외벽은 아미노 레진, 폴리아미드 레진 및 포름알데하이드 레진 중에서 선택된 적어도 어느 하나의 지용성 수지로 형성될 수 있다.The outer wall 15 may be formed of a resin material, and preferably, may be formed of a transparent fat-soluble polymer. For example, the outer wall may be formed of at least one fat-soluble resin selected from amino resins, polyamide resins, and formaldehyde resins.
제조된 미소캡슐(10)은 세정이 필요한데, 세정은 순수, 이소프로필 알코올, 에틸렌 글리콜 등을 사용하여 수행될 수 있다. 미소캡슐(10)의 세정 후 미소캡슐 (10)을 수용액이나 세정액과 분리시키는 것이 필요한데, 이는 원심분리 (centrifugation)나 동결건조(Freeze Dry) 방법을 통해 수행될 수 있다.The prepared microcapsules 10 need cleaning, and the cleaning may be performed using pure water, isopropyl alcohol, ethylene glycol, and the like. After washing the microcapsules 10, it is necessary to separate the microcapsules 10 from the aqueous solution or the washing solution, which may be performed by centrifugation or freeze drying.
이와 같이 제조된 이산화티타늄-실리카 미소캡슐(10)을 나머지 조성물과 혼합 및 교반함으로써 본 발명의 실사필름 코팅용 무기질 도료 조성물이 제조될 수 있다.The inorganic coating composition for the actual film coating of the present invention may be prepared by mixing and stirring the titanium dioxide-silica microcapsules 10 prepared as described above with the remaining composition.
한편, 본 발명의 무기질 도료 조성물에 논슬립(Non-Slip) 기능을 부여하고자 할 경우, 본 발명의 무기질 도료 조성물은 코팅층의 표면에 미세 요철을 형성하기 위한 글래스 비드 내지 우레탄 칩을 더 포함할 수 있음은 물론이다.On the other hand, if you want to give a non-slip (Non-Slip) function to the inorganic coating composition of the present invention, the inorganic coating composition of the present invention may further include a glass bead to the urethane chip to form fine irregularities on the surface of the coating layer Of course.
전술한 바와 같은 본 발명의 무기질 도료 조성물을 이용하여 경관형 마감층을 시공할 수 있다. 이하에서는, 본 발명의 무기질 도료 조성물을 이용한 경관형 마감층 시공 방법에 대하여 설명하도록 한다.The landscape finish layer can be constructed using the inorganic coating composition of the present invention as described above. Hereinafter, to explain the landscape finish layer construction method using the inorganic coating composition of the present invention.
도 7은 본 발명에 따른 실사필름 코팅용 무기질 도료 조성물을 이용하여 건물 바닥면에 경관형 마감층을 시공한 모습을 보여주는 사진이다.Figure 7 is a photograph showing the construction of a landscape finish layer on the building floor using the inorganic coating composition for live-action film coating according to the present invention.
(1) 하도층 형성(1) forming the undercoat
인도, 자전거 도로, 실내 체육관, 아파트, 기타 건축물 등의 흙 포장도로 내지 바닥면, 또는 건축물 벽면에 본 발명의 무기질 도료 조성물을 도포하여 하도층을 형성한다.The undercoat layer is formed by applying the inorganic coating composition of the present invention to a dirt pavement or floor surface of a sidewalk, a bicycle road, an indoor gymnasium, an apartment, another building, or a building wall.
(2) 실사필름 부착(2) With live-action film
하도층 상에 시각적 디자인으로 제작된 실사필름 부착한다. 여기서, 실사필름은 컴퓨터 상에서 그래픽-툴로 그림을 그리거나 소정의 디자인 내지 작품을 스캔하여 얻은 디지털 그림정보(화소정보)를 그대로 또는 편집하여 부직포, 실크 등의 다양한 인쇄소재 상에 출력한 형태일 수 있다.The live-action film produced in the visual design is attached to the undercoat. Here, the live-action film may be a form that is output on various printed materials such as nonwoven fabric and silk by directly or editing digital drawing information (pixel information) obtained by drawing a graphic-tool on a computer or scanning a predetermined design or work. have.
(3) 상도층 형성(3) Top coat layer formation
실사필름의 부착이 완료되면, 해당 실시필름 위에 본 발명의 무기질 도료 조성물을 도포하여 코팅층(즉, 상도층)을 형성한 후, 이를 건조 및 경화시킴으로써 도 7과 같은 경관형 마감층의 시공이 완료된다.When the installation of the live-action film is completed, the inorganic coating composition of the present invention is applied to the corresponding film to form a coating layer (that is, a top coat layer), and then dried and cured to complete the construction of the landscape finish layer as shown in FIG. 7. do.
이와 같은 본 발명의 무기질 도료 조성물을 이용하여 경관형 마감층을 형성하면, 종래 유기 도료에서 발생되는 중금속, TVOC 및 HCHO 등의 독성 없이 내화학성, 내마모성, 내오염성, 발수성, 내후성 등이 뛰어난 코팅층을 구현할 수 있으면서 또한 도료를 투명하게 제조할 수 있게 되었다.When the landscape finish layer is formed using the inorganic coating composition of the present invention, a coating layer having excellent chemical resistance, abrasion resistance, fouling resistance, water repellency, weather resistance, etc. without toxicity of heavy metals, TVOC, HCHO, etc. generated in conventional organic paints It is also possible to realize the paint transparently.
이에 따라, 본 발명의 도료 조성물은 바닥, 벽면 등의 마감층의 상도층으로 사용할 수 있고, 특히 도료의 투명성으로 인해 다양한 그림 및 칼라 등의 시각적 디자인을 연출할 수 있으며, 더 나아가 빛 반사에 의해 실사필름의 그림/칼라 등의 외부연출 및 시인성이 저해되는 문제를 해결할 수 있어 마감층의 경관 효과를 극대화할 수 있게 되었다.Accordingly, the coating composition of the present invention can be used as a top coat layer of the finishing layer, such as floor, wall surface, and in particular, due to the transparency of the paint can produce a visual design, such as a variety of pictures and colors, and further due to light reflection It is possible to solve the problem that the external rendering and visibility of film and color are hindered, thereby maximizing the landscape effect of the finishing layer.
상기에서 본 발명의 바람직한 실시예가 특정 용어들을 사용하여 설명 및 도시되었지만 그러한 용어는 오로지 본 발명을 명확히 설명하기 위한 것일 뿐이며, 본 발명의 실시예 및 기술된 용어는 다음의 청구범위의 기술적 사상 및 범위로부터 이탈되지 않고서 여러가지 변경 및 변화가 가해질 수 있는 것은 자명한 일이다. 이와 같이 변형된 실시예들은 본 발명의 사상 및 범위로부터 개별적으로 이해되어져서는 안되며, 본 발명의 청구범위 안에 속한다고 해야 할 것이다.While the preferred embodiments of the present invention have been described and illustrated using specific terms, such terms are only for clarity of the present invention, and the embodiments and the described terms of the present invention are defined and the technical spirit and scope of the following claims. It is obvious that various changes and changes can be made without departing from the scope. Such modified embodiments should not be understood individually from the spirit and scope of the present invention, but should fall within the claims of the present invention.
10: 미소캡슐
11: 이산화티타늄 미립자
13: 실리카 미립자
15: 외벽10: microcapsules 11: titanium dioxide fine particles
13: silica fine particles 15: outer wall
Claims (8)
γ-글리시독시프로필트리메톡시실란 10 ~ 20 중량%;
이산화티타늄 20 ~ 30 중량%;
실리카 10 ~ 15 중량%; 및
폴리옥시프로필렌디아민 20 ~ 30 중량%를 포함하는 것을 특징으로 하는 실사필름 코팅용 무기질 도료 조성물.
10-20 wt% of methyltrimethoxysilane;
10 to 20% by weight of γ-glycidoxypropyltrimethoxysilane;
20 to 30% by weight titanium dioxide;
10-15 weight percent silica; And
Inorganic coating composition for a film coating, characterized in that 20 to 30% by weight of polyoxypropylene diamine.
상기 메틸트리메톡시실란과 상기 γ-글리시독시프로필트리메톡시실란은 중량비 기준으로 1:1 비율로 혼합되는 것을 특징으로 하는 실사필름 코팅용 무기질 도료 조성물.
According to claim 1,
The methyltrimethoxysilane and the γ-glycidoxypropyltrimethoxysilane are mixed in a 1: 1 ratio by weight ratio based on the inorganic coating composition for the actual film coating.
상기 이산화티타늄과 상기 실리카는 중량비 기준으로 2:1 비율로 혼합되는 것을 특징으로 하는 실사필름 코팅용 무기질 도료 조성물.
According to claim 1,
The titanium dioxide and the silica is an inorganic coating composition for a live film coating, characterized in that mixed in a 2: 1 ratio by weight.
상기 실사필름 코팅용 무기질 도료 조성물의 점도는 50 ~ 150 cps인 것을 특징으로 하는 실사필름 코팅용 무기질 도료 조성물.
According to claim 1,
The viscosity of the inorganic coating composition for the actual film coating is an inorganic coating composition for the actual film coating, characterized in that 50 ~ 150 cps.
상기 이산화티타늄 및 상기 실리카는,
다수의 이산화티타늄 미립자와 다수의 실리카 미립자로 이루어진 코어물질과, 상기 코어물질을 감싸는 수지 재질의 외벽을 포함하는 미소캡슐 형태로 형성되고,
상기 미소캡슐은,
200nm 이하의 평균직경을 갖도록 형성되어 분산 배치되어 있는 것을 특징으로 하는 실사필름 코팅용 무기질 도료 조성물.
According to claim 1,
The titanium dioxide and the silica,
Many titanium dioxide particles and many silica It is formed in the form of a microcapsule comprising a core material made of fine particles and an outer wall of a resin material surrounding the core material,
The microcapsules,
It is formed to have an average diameter of 200nm or less, the inorganic coating composition for a live-film coating, characterized in that the dispersing arrangement.
상기 외벽은 아미노 레진, 폴리아미드 레진 및 포름알데하이드 레진 중에서 선택된 적어도 어느 하나의 지용성 수지로 형성되는 것을 특징으로 하는 실사필름 코팅용 무기질 도료 조성물.
The method of claim 5,
The outer wall is an inorganic coating composition for the actual film coating, characterized in that formed of at least one fat-soluble resin selected from amino resin, polyamide resin and formaldehyde resin.
인도, 도로, 건축물의 바닥면 또는 건축물 벽면에 하도층을 형성하는 단계;
상기 하도층 위에 실사필름을 부착하는 단계;
상기 실사필름 위에 제1항 내지 제6항 중 어느 한 항의 무기질 도료 조성물을 도포하여 코팅층을 형성하는 단계; 및
상기 코팅층을 건조 및 경화시키는 단계;를 포함하는 것을 특징으로 하는 경관형 마감층 시공 방법.
As a finishing layer construction method,
Forming a subsurface layer on a sidewalk, a road, a bottom surface of a building, or a building wall;
Attaching a live-action film on the undercoat;
Forming a coating layer by applying the inorganic coating composition of any one of claims 1 to 6 on the optical film; And
Drying and curing the coating layer; Landscape finish layer construction method comprising a.
상기 하도층을 형성하는 단계는 제1항 내지 제6항 중 어느 한 항의 무기질 도료 조성물을 도포하여 형성하는 것을 특징으로 하는 경관형 마감층 시공 방법.The method of claim 7, wherein
The forming of the undercoat layer is a landscape finish layer construction method, characterized in that formed by applying the inorganic coating composition of any one of claims 1 to 6.