KR20190101699A - Water-treatment membrane and Method of manufacturing the same - Google Patents

Water-treatment membrane and Method of manufacturing the same Download PDF

Info

Publication number
KR20190101699A
KR20190101699A KR1020180022018A KR20180022018A KR20190101699A KR 20190101699 A KR20190101699 A KR 20190101699A KR 1020180022018 A KR1020180022018 A KR 1020180022018A KR 20180022018 A KR20180022018 A KR 20180022018A KR 20190101699 A KR20190101699 A KR 20190101699A
Authority
KR
South Korea
Prior art keywords
ferrocene
cyclodextrin
reverse osmosis
water treatment
osmosis membrane
Prior art date
Application number
KR1020180022018A
Other languages
Korean (ko)
Other versions
KR102040272B1 (en
Inventor
곽승엽
이지영
Original Assignee
서울대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 서울대학교산학협력단 filed Critical 서울대학교산학협력단
Priority to KR1020180022018A priority Critical patent/KR102040272B1/en
Publication of KR20190101699A publication Critical patent/KR20190101699A/en
Application granted granted Critical
Publication of KR102040272B1 publication Critical patent/KR102040272B1/en

Abstract

A reverse osmosis membrane for water treatment provided in the present invention comprises: a membrane substrate; a linker portion formed on the membrane substrate; and a branched hydrophilic polymer-ferrocene-cyclodextrin complex connected to the membrane substrate through the linker portion. Cyclodextrin bonds can be made reversible by redox reactions, so that contaminant-attached cyclodextrin can be purified and reused. Since the regeneration of the reverse osmosis membrane for water treatment becomes possible, the service life of the reverse osmosis membrane becomes long.

Description

전기 자극을 통해 재생이 가능한 수처리 분리막 및 이의 제조 방법 {Water-treatment membrane and Method of manufacturing the same}Water treatment membrane which can be regenerated by electrical stimulation and its manufacturing method {Water-treatment membrane and Method of manufacturing the same}

본 발명은 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체가 링커에 의해 기재에 연결되어 있는 수처리용 역삼투 분리막 및 그의 제조방법에 관한 것이다.The present invention relates to a reverse osmosis membrane for water treatment in which a branched hydrophilic polymer-ferrocene-cyclodextrin complex is linked to a substrate by a linker, and a method for preparing the same.

분리막을 이용한 수처리 방법은 기존 기술들에 비해 적은 설치 공간, 우수한 처리용량, 낮은 운영비용으로 최근들어 분리막을 하수처리, 해수담수, 가정용, 의료용, 산업용 등 다양한 수처리 분야에 적용하는 사례가 증가하고 있다. 이들은 공경 크기에 따라 정밀여과(Microfiltration, MF), 한외여과(Ultrafiltration, UF), 나노여과(Nanofiltration, NF), 역삼투(Reverse osmosis, RO) 분리막으로 나뉘며, 이에 따라 필요 구동압력과 걸러낼 수 있는 물질의 종류가 달라진다. 그 중, 역삼투 분리막의 경우 작은 기공 크기로 1가 이온들을 효과적으로 제거하여 해수 담수로 가장 많이 쓰이는 방법이다. 가장 많이 쓰이는 역삼투 분리막은 폴리아마이드 역삼투 분리막(Polyamide reverse osmosis membrane, PA RO)으로 높은 압력에서도 견디게 하는 폴리설폰(polysulfon, PSF)층과 그 위에 얇은 두께의 폴리아마이드(Polyamide, PA)층으로 이루어져 있다. 높은 수투과도와 염 제거율을 가지지만 유기 오염물과 분리막 표면간에 상호작용이 형성되어 오염이 가속화 되며 이에 의해 수투과도 감소 등의 분리막 성능 저하가 발생한다는 단점이 있다. 이러한 분리막 오염을 저감시키기 위해 분리막 표면 친수성 고분자 코팅, 전하를 띄는 물질의 코팅 및 개질 등의 다양한 방법을 사용하고 있다. (Chem. Rev. 2010, 110, 2448-2471)In recent years, the use of membranes for water treatment has been increasing in applications such as sewage treatment, seawater desalination, household, medical, industrial, etc. due to the low installation space, excellent treatment capacity, and low operating cost. . They are divided into microfiltration (MF), ultrafiltration (UF), nanofiltration (NF), and reverse osmosis (RO) membranes according to pore size. The type of material present varies. Among them, reverse osmosis membranes are the most widely used method for seawater freshwater by effectively removing monovalent ions with small pore size. The most commonly used reverse osmosis membrane is a polyamide reverse osmosis membrane (PA RO), a polysulfon (PSF) layer that can withstand high pressures, and a thin polyamide (PA) layer on it. consist of. Although it has a high water permeability and salt removal rate, the interaction between organic contaminants and the surface of the separator is formed to accelerate the contamination, thereby reducing the membrane performance such as water permeability decrease. In order to reduce the contamination of the membrane, various methods such as coating of a hydrophilic polymer on the surface of the membrane, coating and modifying of a chargeable material are used. (Chem. Rev. 2010, 110, 2448-2471)

그러나 다양한 방법들에도 오염을 완전히 막을 수 없기 때문에 자극-감응성 물질의 도입을 통하여 분리막에 재생성을 주는 방법들이 시도되고 있다. 자극-감응성 물질 도입의 경우 특정 자극에 반응하여 가역적 결합을 하는 성질을 이용하여 분리막에 높은 회복 성능을 줄 수 있다. 대표적으로 열 감응성 딜스-알더 고리화첨가반응을 도입하여 고온조건에서 친수성층을 오염물질과 함께 제거하고 다시 적절한 온도에서 재차 도입하는 방법, 고분자 전해질을 층별로 도입하여 산성 조건에서 고분자 전해질의 전기적 척력을 이용하여 고분자 전해질 층을 오염물질과 떼어내는 방법이 있다. 산성과 고온의 환경의 경우 역삼투 분리막을 손상, 분해시켜 역삼투 분리막에 적용시키기 힘든 반면, 전기의 경우 물속에서 쉽고 빠르게 적용시킬 수 있다. However, since various methods cannot completely prevent contamination, methods for regenerating the separator through the introduction of a stimulus-sensitive material have been attempted. In the case of stimulus-sensitive material introduction, a high recovery performance can be given to the separator by using a property of reversible binding in response to a specific stimulus. Representatively, the thermally sensitive Diels-Alder cycloaddition reaction is used to remove the hydrophilic layer with contaminants at high temperature and re-introduced again at the appropriate temperature. There is a method of separating the polymer electrolyte layer from the contaminants using the. In the case of acid and high temperature environment, reverse osmosis membrane is damaged and decomposed and difficult to apply to reverse osmosis membrane, while electricity can be applied quickly and easily in water.

한편, 분리막 기재로 메타페닐렌 디아민 및 트리메실오익 클로라이드가 계면 중합되어 있는 폴리아미드 역삼투 멤브레인이 당업계에서 사용되어 왔으며, 상기 분리막 기재는 물 플럭스(water flux), 바이오물질 공격(biological attack)에 대한 안정성 및 기계적 강도 측면에서 바람직하지만, 오염문제(fouling)가 심각한 점이 지적되어 왔다. 이러한 오염문제는 수처리에 부가적인 에너지 투입을 필요로 하고, 오염물질 제거가 필요할 뿐만 아니라 수처리 분리막의 내구성을 떨어뜨리는 문제를 발생시킨다. 따라서, 수처리 분리막에 부착된 오염물질을 제거할 필요가 있다.Meanwhile, a polyamide reverse osmosis membrane having an interfacial polymerization of metaphenylene diamine and trimesyloick chloride as a separator substrate has been used in the art, and the separator substrate may be a water flux or a biological attack. Although desirable in terms of stability and mechanical strength, the fouling problem has been pointed out. This pollution problem requires additional energy input to the water treatment, not only removes pollutants, but also causes problems of deterioration of the water treatment membrane. Therefore, it is necessary to remove the contaminants attached to the water treatment membrane.

본 발명이 해결하고자 하는 과제는, 페로센-사이클로덱스트린 복합체를 도입한 분리막의 우수한 회복성능을 가지면서도 높은 내오염성능을 갖는 수처리 분리막 및 그 제조방법을 제공하기 위한 것이다.The problem to be solved by the present invention is to provide a water treatment separation membrane having a high fouling resistance while having excellent recovery performance of the separation membrane incorporating the ferrocene-cyclodextrin complex and a method of manufacturing the same.

본 발명의 다른 양태에서는 페로센-사이클로덱스트린 복합체가 사용되되, 높은 수 투과도를 갖고 친수성을 구비하여 오염 저감 성능을 증가시킨 수처리용 역삼투 분리막을 제공하기 위한 것이다. In another embodiment of the present invention, a ferrocene-cyclodextrin complex is used, and to provide a reverse osmosis membrane for water treatment having high water permeability and hydrophilicity to increase the pollution reduction performance.

본 발명의 다른 양태에서는 가지구조형 친수성 고분자에 페로센-사이클로덱스트린을 도입시켜 가지구조에 효율적으로 많은 양의 페로센-사이클로덱스트린 복합체를 도입하고 친수성 영향으로 오염 저감 성능을 가지는 수처리용 역삼투 분리막 및 그의 제조방법을 제공하기 위한 것이다.In another aspect of the present invention, by introducing a ferrocene-cyclodextrin into the branched hydrophilic polymer efficiently introduced into the branched structure a large amount of ferrocene-cyclodextrin complex and reverse osmosis membrane for water treatment having a pollution reduction performance by the hydrophilic effect and its preparation It is to provide a method.

본 발명의 제1 양태에 의하면, 분리막 기재; 상기 분리막 기재 상에 형성된 링커부; 및 상기 링커부를 통해 분리막 기재에 연결되어 있는 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체;를 포함하는 수처리용 역삼투 분리막이 제공된다.According to a first aspect of the present invention, a separator substrate; A linker portion formed on the separator substrate; And a branched hydrophilic polymer-ferrocene-cyclodextrin complex connected to the separator substrate through the linker portion. A reverse osmosis membrane for water treatment is provided.

본 발명의 제2 양태에 의하면, 상기 제1 양태에서 상기 가지구조형 친수성 고분자가 폴리에틸렌이민일 수 있다.According to a second aspect of the present invention, in the first aspect, the branched hydrophilic polymer may be polyethyleneimine.

본 발명의 제3 양태에 의하면, 상기 제1 양태 또는 제2 양태에서 상기 가지구조형 친수성 고분자와 페로센이 화학적으로 결합되어 있을 수 있다.According to the third aspect of the present invention, the branched hydrophilic polymer and ferrocene may be chemically bonded in the first or second aspect.

본 발명의 제4 양태에 의하면, 상기 제1 양태 내지 제3 양태중 어느 하나의 양태에서 상기 사이클로덱스트린과 페로센은 사이클로덱스트린 내에 페로센이 포접되어 물리적으로 결합되어 있을 수 있다.According to the fourth aspect of the present invention, in any one of the first aspect to the third aspect, the cyclodextrin and ferrocene may be physically bound by the inclusion of ferrocene in the cyclodextrin.

본 발명의 제5 양태에 의하면, (S1) 분리막 기재를 제공하는 단계; (S2) 상기 분리막 기재에 링커부를 형성시키고 페로센 카복스알데하이드와 가지구조형 친수성 고분자의 반응 생성물을 도입하는 단계; 및 (S3) 사이클로덱스트린을 도입하여 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체를 형성하는 단계;를 포함하는, 전술한 수처리용 역삼투 분리막의 제조 방법이 제공된다.According to a fifth aspect of the present invention, there is provided a method of preparing a separator substrate, the method comprising: providing a separator substrate (S1); (S2) forming a linker portion in the separator substrate and introducing a reaction product of ferrocene carboxaldehyde and a branched hydrophilic polymer; And (S3) introducing cyclodextrin to form a branched hydrophilic polymer-ferrocene-cyclodextrin complex. The method for preparing the reverse osmosis membrane for water treatment is provided.

본 발명의 제6 양태에 의하면, 상기 제5 양태에서 상기 링커부 도입을 위해 EDC(1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride)/NHS(N-hydroxysuccinimide) 반응이 수행될 수 있다.According to a sixth aspect of the present invention, in the fifth aspect, EDC (1-ethyl-3- (3-dimethylaminopropyl) carbodiimide hydrochloride) / NHS (N-hydroxysuccinimide) reaction may be performed to introduce the linker portion.

본 발명의 제7 양태에 의하면, (R1) 사이클로덱스트린에 오염물질이 부착된 분리막을 준비하는 단계; (R2) 페로센을 산화시켜 사이클로덱스트린을 오염물질과 함께 해리시키는 단계; 및 (R3) 페로센을 환원시켜 페로센과 사이클로덱스트린 복합체를 재형성시키는 단계;를 포함하는 전술한 수처리용 역삼투 분리막의 재생 방법이 제공된다.According to a seventh aspect of the present invention, (R1) preparing a separator having contaminants attached to a cyclodextrin; (R2) oxidizing ferrocene to dissociate the cyclodextrin with contaminants; And (R3) reducing the ferrocene to reconstitute the ferrocene and cyclodextrin complex. The regeneration method of the reverse osmosis membrane for water treatment is provided.

본 발명의 수처리용 역삼투 분리막은 가지구조형 친수성 고분자에 페로센-사이클로덱스트린을 도입시켜 친수성 고분자의 가지구조에 효율적으로 많은 양의 페로센-사이클로덱스트린 복합체가 도입될 수 있고 또한 친수성을 갖는 가지구조형 고분자가 사용됨에 따라 오염 문제를 저감시키는 효과를 갖는다. In the reverse osmosis membrane for water treatment of the present invention, ferrocene-cyclodextrin is introduced into the branched hydrophilic polymer so that a large amount of ferrocene-cyclodextrin complex can be efficiently introduced into the branched structure of the hydrophilic polymer, and the branched polymer having hydrophilicity As used, it has the effect of reducing pollution problems.

또한, 본 발명에 따른 수처리 역삼투 분리막은 산화환원 반응에 의해 사이클로덱스트린 결합이 가역적이 될 수 있으므로, 오염물질이 부착된 사이클로덱스트린을 정제하여 재사용할 수 있는 이점이 있다. 그 결과, 수처리용 역삼투 분리막의 재생이 가능하게 되므로, 역삼투 분리막의 사용연한이 길어지는 장점을 갖는다. In addition, the reverse osmosis membrane of the water treatment according to the present invention can be reversible cyclodextrin bond by the redox reaction, there is an advantage that can be reused by purifying the cyclodextrin attached to the contaminants. As a result, since the regeneration of the reverse osmosis membrane for water treatment is possible, the service life of the reverse osmosis membrane is long.

도 1은 본 발명의 일 양태에 따른 수처리용 역삼투 분리막의 제조 단계를 순차적으로 나타낸 것이다. 도 1에서 TFC PA RO는 박막 복합체 폴리아미드 역삼투(Thin Film Composite Polyamide Reverse osmosis)를 나타내고, RO는 역삼투를 나타내며, EDC는 N-(3-디메틸아미노프로필)-N'-에틸카보디이미드 하이드로클로라이드를 나타내고, NHS는 역삼투/N-하이드록시숙신이미드를 나타내며, b-FC는 페로센에 의해 개질된 가지구조형 친수성 고분자를 나타내고, CD는 사이클로덱스트린을 나타낸다.
도 2는 가지구조형 폴리에틸렌이민(b-PEI)과 페로센 카복스알데하이드(FcCHO)의 반응 및 그로부터 생성되는 생성물(b-FC)을 나타낸 것이다.
도 3은 본 발명의 일 양태에 따른 수처리용 역삼투 분리막에 막 오염물질이 부착된 상태(A), 오염 물질이 사이클로덱스트린과 함께 제거되는 상태(B) 및 사이클로덱스트린이 수처리 역삼투 분리막에 다시 도입된 상태(C)를 개략적으로 나타낸 것이다.
도 4는 페로센 카복스알데하이드 및 실시예 1 내지 4에서 페로센에 의해 개질된 가지구조형 폴리에틸렌이민의 특성을 FT-IR (Fourier-transform Infrared Spectroscopy) 분석하여 나타낸 그래프이다.
도 5는 페로센 카복스알데하이드 및 실시예 1 내지 4에서 페로센에 의해 개질된 가지구조형 폴리에틸렌이민의 특성을 H1NMR (Proton NuclearMagnetic Resonance) 분석하여 나타낸 그래프이다.
도 6은 실시예에서 사용된 분리막 기재 및 실시예 1 내지 4에서 제조된 본 발명에 따른 수처리용 역삼투 분리막을 FT-IR 분석법에 의해 나타낸 그래프이다.
도 7은 실시예에서 사용된 분리막 기재(TFC PA RO), 상기 분리막 기재에 페로센 개질된 가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 XPS(X-ray photoelectron spectroscopy) 분석하여 나타낸 그래프이다.
도 8은 실시예에서 사용된 분리막 기재(TFC PA RO), 상기 분리막 기재에 페로센 개질된 가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 FE-SEM 이미지로 나타낸 것이다.
도 9는 실시예에서 사용된 분리막 기재(TFC PA RO), 상기 분리막 기재에 페로센 개질된 가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 AFM(Atomic force microscope) 이미지로 나타낸 것이다.
도 10은 실시예에서 사용된 분리막 기재(TFC PA RO) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 사용하여 수투과 테스트 결과를 나타낸 그래프로, D.I. water cleaning은 증류수를 사용한 수투과 테스트를 나타내고, cleaning solution으로 Sodium hypochlorite solution (NaOCl) 용액을 사용하여 실시한 수투과 테스트를 나타낸 것이다.
Figure 1 shows in sequence the manufacturing step of the reverse osmosis membrane for water treatment according to an aspect of the present invention. In FIG. 1, TFC PA RO represents Thin Film Composite Polyamide Reverse osmosis, RO represents Reverse Osmosis, and EDC represents N- (3-dimethylaminopropyl) -N'-ethylcarbodiimide. Hydrochloride, NHS represents reverse osmosis / N-hydroxysuccinimide, b-FC represents branched hydrophilic polymer modified by ferrocene, and CD represents cyclodextrin.
Figure 2 shows the reaction of the branched polyethyleneimine (b-PEI) and ferrocene carboxaldehyde (FcCHO) and the resulting product (b-FC).
3 is a state in which membrane contaminants are attached to the reverse osmosis membrane for water treatment according to an embodiment of the present invention (A), the contaminants are removed together with the cyclodextrin (B), and the cyclodextrin is added to the reverse osmosis membrane in the water treatment. The state (C) introduced is schematically shown.
4 is a graph showing FT-IR (Fourier-transform Infrared Spectroscopy) analysis of the properties of ferrocene carboxaldehyde and branched polyethyleneimine modified by ferrocene in Examples 1 to 4;
FIG. 5 is a graph showing the characteristics of branched polyethyleneimine modified by ferrocene carboxaldehyde and ferrocene in Examples 1 to 4 by H 1 NMR (Proton Nuclear Magnetic Resonance) analysis.
6 is a graph showing the membrane substrate used in the Example and the reverse osmosis membrane for water treatment according to the present invention prepared in Examples 1 to 4 by FT-IR analysis.
7 is a membrane substrate (TFC PA RO) used in the examples, a form in which a ferrocene-modified branched polyethylene imine complex is bound to the membrane substrate (RO / b-Fc), and a ferrocene-branch further modified by cyclodextrin. X-ray photoelectron spectroscopy (XPS) analysis of the structure-bound polyethylene imine complex bound form (RO / b-Fc / CD).
FIG. 8 shows the separator substrate (TFC PA RO) used in the examples, the form in which the ferrocene-modified branched polyethylene imine complex is bound to the separator substrate (RO / b-Fc), and the ferrocene-branch further modified by cyclodextrins. The combined form of the structural polyethylene imine complex (RO / b-Fc / CD) is shown in the FE-SEM image.
9 is a separator substrate (TFC PA RO) used in the examples, a form in which a ferrocene-modified branched polyethylene imine complex is bound to the separator substrate (RO / b-Fc), and a ferrocene-branch further modified by cyclodextrin. The combined form of the structural polyethylene imine complex (RO / b-Fc / CD) is shown as an atomic force microscope (AFM) image.
10 shows the results of permeation test using the membrane substrate (TFC PA RO) used in the examples and the form in which the ferrocene-branched polyethylene imine complex was further modified by cyclodextrin (RO / b-Fc / CD). The DI water cleaning shows the water permeation test using distilled water and the water permeation test performed using Sodium hypochlorite solution (NaOCl) as a cleaning solution.

이하 본 발명의 구현예를 상세히 설명한다. 이에 앞서, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서, 본 명세서에 기재된 실시예에 기재된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.Hereinafter, embodiments of the present invention will be described in detail. Prior to this, terms or words used in the specification and claims should not be construed as having a conventional or dictionary meaning, and the inventors should properly explain the concept of terms in order to best explain their own invention. Based on the principle that can be defined, it should be interpreted as meaning and concept corresponding to the technical idea of the present invention. Therefore, the configurations described in the embodiments described herein are only one of the most preferred embodiments of the present invention and do not represent all of the technical ideas of the present invention, and various equivalents may be substituted for them at the time of the present application. It should be understood that there may be variations.

본원 명세서 전체에서, 어떤 부분이 다른 부분과 「연결」되어 있다고 할 때, 이는 「직접적으로 연결」되어 있는 경우뿐만 아니라 그 중간에 다른 매개체를 통해 「간접적으로 연결」되어 있는 경우도 포함한다. In the present specification, when a part is "connected" with another part, this includes not only the case where it is "directly connected" but also the case where it is "indirectly connected" through the other medium in between.

본원 명세서 전체에서, 어떤 부분이 어떤 구성 요소를 「포함한다」고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다. Throughout this specification, when a part "contains" a certain component, it means that it can further include other components, without excluding the other components unless otherwise stated.

본원 명세서 전체에서 사용되는 용어 「약」, 「실질적으로」 등은 언급된 의미에 고유한 제조 및 물질 허용 오차가 제시될 때 그 수치에서 또는 그 수치에 근접한 의미로서 사용되고 본원의 이해를 돕기 위해 정확하거나 절대적인 수치가 언급된 개시 내용을 비양심적인 침해자가 부당하게 이용하는 것을 방지하기 위해 사용된다. As used throughout this specification, the terms "about", "substantially," and the like are used to refer to, or in close proximity to, the numerical values of the preparations and material tolerances inherent in the meanings indicated, to aid the understanding of the present application. Or absolute figures are used to prevent unfair use of unscrupulous infringers.

본원 명세서 전체에서, 마쿠시 형식의 표면에 포함된 「이들의 조합(들)」의 용어는 마쿠시 형식의 표현에 기재된 구성 요소들로 이루어지는 군에서 선택되는 하나 이상의 혼합 또는 조합을 의미하는 것으로서, 상기 구성 요소들로 이루어지는 군에서 선택되는 하나 이상을 포함하는 것을 의미한다. Throughout this specification, the term "combination (s) thereof" included on the surface of the mark of the mark is used to mean one or more mixtures or combinations selected from the group consisting of the elements described in the mark of the mark type. It means to include one or more selected from the group consisting of the above components.

본원 명세서 전체에서, 「A 및/또는 B」의 기재는 「A 또는 B 또는 이들 모두」를 의미한다. Throughout this specification, description of "A and / or B" means "A or B or both."

본 발명의 일 측면에 따르면, 분리막 기재; 상기 분리막 기재 상에 형성된 링커부; 및 상기 링커부를 통해 분리막 기재에 연결되어 있는 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체;를 포함하는 수처리용 역삼투 분리막이 제공된다. According to an aspect of the invention, the membrane substrate; A linker portion formed on the separator substrate; And a branched hydrophilic polymer-ferrocene-cyclodextrin complex connected to the separator substrate through the linker portion. A reverse osmosis membrane for water treatment is provided.

본 발명의 다른 측면에 따르면, 상기 수처리용 역삼투 분리막은, (S1) 분리막 기재를 제공하는 단계; (S2) 상기 분리막 기재에 링커부를 형성시키고 가지구조형 친수성 고분자-페로센을 도입하는 단계; 및 (S3) 사이클로덱스트린을 도입하여 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체를 형성하는 단계;를 포함하는 공정에 의해 제조된다.According to another aspect of the invention, the reverse osmosis membrane for water treatment, (S1) providing a membrane substrate; (S2) forming a linker portion in the separator substrate and introducing a branched hydrophilic polymer-ferrocene; And (S3) introducing a cyclodextrin to form a branched hydrophilic polymer-ferrocene-cyclodextrin complex.

본 발명의 또 다른 측면에 따르면, (R1) 사이클로덱스트린에 오염물질이 부착된 분리막을 준비하는 단계; (R2) 페로센을 산화시켜 사이클로덱스트린을 오염물질과 함께 해리시키는 단계; 및 (R3) 페로센을 환원시켜 페로센과 사이클로덱스트린 복합체를 재형성시키는 단계;를 포함하는 수처리용 역삼투 분리막의 재생 방법이 제공된다.According to another aspect of the invention, (R1) preparing a separator having a contaminant attached to the cyclodextrin; (R2) oxidizing ferrocene to dissociate the cyclodextrin with contaminants; And (R3) reducing the ferrocene to reconstitute the ferrocene and cyclodextrin complex. There is provided a method for regenerating a reverse osmosis membrane for water treatment.

먼저, 본 발명의 역삼투 분리막 기재를 구성하는 각 구성요소를 살펴본다.First, look at each component constituting the reverse osmosis membrane substrate of the present invention.

수처리용 역삼투 분리막의 분리막 기재로는 당해 기술분야에서 사용될 수 있는 모든 고분자 재료일 수 있다. 또한, 본 발명의 취지에 부합한다면 세라믹, 금속 등의 재료에도 제한없이 사용될 수 있다. The membrane substrate of the reverse osmosis membrane for water treatment may be any polymer material that can be used in the art. In addition, as long as it is in accordance with the spirit of the present invention can be used without limitation for materials such as ceramics, metals.

본 발명의 구체적인 일 실시양태에 있어서, 상기 고분자 재료는 폴리테트라플로오로에틸렌 (Polytetrafluoroethylene, PTFE), 폴리비닐리덴플루오라이드(Polyvinylidenefluoride, PVDF), 폴리설폰(Polysulfone, PSF), 폴리에테르설폰 (Polyethersulfone, PES), 폴리에스테르, 폴리아크릴로니트릴(Polyacrylonitrile, PAN), 폴리카보네이트(Polycarbonate, PC), 폴리에틸렌(Polyethylene, PE), 폴리프로필렌(Polypropylene, PP), 폴리염화비닐(Polyvinyl chloride, PVC), 셀룰로오스(Cellulose) 및 셀룰로오스 아세테이트(Cellulose acetate) 로 이루어진 군으로부터 선택되는 하나 또는 이 중 둘 이상을 포함할 수 있다. 또한, 상기 분리막 기재는 당업계에서 통상적으로 이루어지는 방식으로 화학적 및/또는 물리적으로 개질된 것일 수 있다. 예컨대, 폴리에스테르; 폴리설폰층; 및 메타페닐렌 디아민(MPD)과 트리메소일 클로라이드(TMC)가 계면 중합(interfacial polymerization)된 폴리아미드;가 순차적으로 적층되어 형성된 것일 수 있다.In one specific embodiment of the present invention, the polymer material is polytetrafluoroethylene (PTFE), polyvinylidene fluoride (PVDF), polysulfone (Polysulfone, PSF), polyethersulfone (Polyethersulfone, PES), polyester, polyacrylonitrile (PAN), polycarbonate (PC), polyethylene (PE), polypropylene (PP), polyvinyl chloride (PVC), cellulose It may include one or two or more selected from the group consisting of (Cellulose) and cellulose acetate (Cellulose acetate). In addition, the separator substrate may be chemically and / or physically modified in a manner conventionally made in the art. For example, polyester; Polysulfone layer; And polyamide having an interfacial polymerization of metaphenylene diamine (MPD) and trimesoyl chloride (TMC).

본 발명의 일 실시양태에 있어서, 상기 분리막 기재는 연신 처리된 고분자 필름일 수 있다. 또한, 상기 분리막 기재는 필름의 몸체 및 표면에 다수의 기공이 형성되어 있을 수 있으며, 상기 기공의 직경은 본 발명의 취지에 부합하는 한 특별히 제한되지 않으나, 1 nm 미만의 매우 작은 직경을 갖는 것일 수 있다. 상기 기공을 통해 여과수 등 처리물질이 분리막 기재를 통과하여 지날 수 있다. 수처리용 분리막은 단면구조가 대칭구조인 분리막에 비해 비대칭구조인 분리막이 유속 및 수투과도 등의 측면에서 여과 성능이 우수하다. 이러한 측면에서 본 발명의 구체적인 일 실시양태에 있어서 상기 고분자 분리막 기재는 미세 기공이 형성되어 있으며 바람직하게는 크기나 분포 면에서 균일한 공경 구조를 나타내는 표층 및 손가락형(finger-like) 또는 스폰지형 (sponge-like)의 기공 구조를 갖는 내부지지층을 포함할 수 있다. In one embodiment of the present invention, the separator substrate may be a stretched polymer film. In addition, the separator substrate may have a plurality of pores formed on the body and the surface of the film, the diameter of the pores is not particularly limited as long as it meets the spirit of the present invention, but having a very small diameter of less than 1 nm Can be. Through the pores, treated materials such as filtered water may pass through the membrane substrate. In the membrane for water treatment, the asymmetric membrane is superior in filtration performance in terms of flow rate and water permeability compared to the membrane having a symmetric cross-sectional structure. In this aspect, in one specific embodiment of the present invention, the polymer membrane base material has fine pores and is preferably a surface layer and a finger-like or sponge type having a uniform pore structure in terms of size or distribution ( It may include an inner support layer having a porous structure of the sponge-like).

또한, 분리막 기재로 사용할 수 있는 무기 재료는 알루미늄 산화물 (Alumina), 규소산화물(silica), 티타늄산화물(Titania) 중 적어도 어느 하나이거나, 이들을 혼합하여 사용할 수 있고, 분리막 기재로 사용할 수 있는 금속물질은 스텐리스 스틸(Stainless steel), 팔라듐 합금(Palladium alloy) 중 적어도 어느 하나이거나, 이들을 혼합하여 사용할 수 있다.In addition, the inorganic material that can be used as the separator substrate is at least one of aluminum oxide (silicon), silicon oxide (silica), titanium oxide (Titania), or a mixture thereof can be used, the metal material that can be used as the separator substrate At least one of stainless steel and a palladium alloy may be used, or a mixture thereof may be used.

상기 분리막 기재에는, 분리막 기재와, 후속 공정에서 도입될 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체를 연결시키기 위한 매개체로 링커부가 구비되어 있다. 즉, 분리막 기재 상에 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체가 직접 결합되어 있지 않다. 링커부에 의해 분리막 기재와 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체 사이에 공간이 확보될 수 있다. The separator substrate is provided with a linker portion as a medium for connecting the separator substrate and the branched hydrophilic polymer-ferrocene-cyclodextrin complex to be introduced in a subsequent step. That is, the branched hydrophilic polymer-ferrocene-cyclodextrin complex is not directly bonded on the separator substrate. The linker portion may secure a space between the separator substrate and the branched hydrophilic polymer-ferrocene-cyclodextrin complex.

상기 링커부에 가지구조형 친수성 고분자-페로센-사이클로덱스트린이 결합되어 있다. 보다 구체적으로, 가지구조형 친수성 고분자가 링커부와 결합되어 있으며, 가지구조형 친수성 고분자의 가지구조에 페로센이 화학적으로 결합되어 있고, 사이클로덱스트린과 페로센은 사이클로덱스트린 내에 페로센이 포접되어 물리적으로 결합되어 있다. A branched hydrophilic polymer-ferrocene-cyclodextrin is bound to the linker portion. More specifically, the branched hydrophilic polymer is bonded to the linker portion, ferrocene is chemically bonded to the branched structure of the branched hydrophilic polymer, and the cyclodextrin and ferrocene are physically bound by the inclusion of ferrocene in the cyclodextrin.

가지구조형 친수성 고분자는 가지구조를 가져 보다 많은 페로센과 결합될 수 있으며, 또한, 친수성을 가져 소수성 오염물질(hydrophobic foulant)의 흡착을 방지하는 역할을 할 수 있다. 이러한 가지구조형 고분자로는 금속 이온과 배위 결합을 형성할 수 있는 아민 작용기가 다수 포함된 것을 사용할 수 있다. 이의 구체적인 예로 상기 고차가지고분자로는 Hyperbranched poly(amido amine)(HPAMAM), Hyperbranched polyethyleneimine(PEI), Hyperbranched polyglycerol(HPG), Hyperbranched polyester(HPE), Hyperbranched polyethylene oxide(HPEO) 등을 예로 들 수 있다. 가지구조형 폴리에틸렌이민이 아민기로 인해 친수성을 구비하고 있고 반응성 말단 작용기 밀도가 높기 때문에 바람직하다.The branched hydrophilic polymer may have a branched structure and may be combined with more ferrocene, and may have a hydrophilic property to prevent adsorption of hydrophobic foulants. Such a branched polymer may be one containing a large number of amine functional groups capable of forming coordination bonds with metal ions. Specific examples thereof include hyperbranched poly (amido amine) (HPAMAM), Hyperbranched polyethyleneimine (PEI), Hyperbranched polyglycerol (HPG), Hyperbranched polyester (HPE), Hyperbranched polyethylene oxide (HPEO), and the like. The branched polyethyleneimine is preferred because it has hydrophilicity due to the amine group and high reactive terminal functional group density.

가지구조형 폴리에틸렌이민을 사용하는 경우, 가지구조형 폴리에틸렌 이민의 분자량은 본 발명의 취지에 부합하는 한 특별히 제한되지 않으며, 예컨대, 1,000 내지 100,000 또는 10,000 내지 100,0000 범위의 중량평균분자량(Mw)을 가질 수 있다. 상기 범위에서 분자량이 클수록 친수성이 높아지고 수투과 테스트에서 좋은 성능을 나타낼 수 있다.When branched polyethyleneimine is used, the molecular weight of the branched polyethyleneimine is not particularly limited as long as it is in accordance with the spirit of the present invention, and may have, for example, a weight average molecular weight (Mw) in the range of 1,000 to 100,000 or 10,000 to 100,0000. Can be. The larger the molecular weight in the above range, the higher the hydrophilicity and the better the performance in water permeation test.

페로센은 2개의 사이클로펜타디에닐 고리에 철(Fe) 원자가 결합되어 있는 형태를 갖는 것으로, 가역적인 산화환원 양태(reversible redox behavior)를 나타내는 것을 특징으로 한다. 또한, 사이클로덱스트린, 특히 베타-사이클로덱스트린과 소수성 작용(hydrophobic interaction)에 의해 1:1 포접 결합체를 형성할 수 있다.Ferrocene has a form in which iron (Fe) atoms are bonded to two cyclopentadienyl rings, and is characterized by exhibiting a reversible redox behavior. It is also possible to form 1: 1 clathrate conjugates by hydrophobic interaction with cyclodextrins, in particular beta-cyclodextrins.

사이클로덱스트린으로는 알파 사이클로덱스트린, 베타 사이클로덱스트린, 감마 사이클로덱스트린, 델타 사이클로덱스트린 또는 이들의 혼합물을 사용할 수 있다. 이 중 낮은 높이의 뿔잘린 원기동(shallow truncated conical shape) 형상을 갖는 베타-사이클로덱스트린이 Host-guest 포접 복합체를 형성하기에 적합한 소수성 캐비티(hydrophobic cavity) 및 친수성 표면(hydrophilic surface)을 가기에 바람직하다.As the cyclodextrin, alpha cyclodextrin, beta cyclodextrin, gamma cyclodextrin, delta cyclodextrin or mixtures thereof can be used. Among these, beta-cyclodextrins having a low height of truncated conical shape are preferable for hydrophobic cavities and hydrophilic surfaces suitable for forming host-guest inclusion complexes. Do.

사이클로덱스트린은 각 크기에 맞는 유기 오염물질을 선택적으로 포집하여, 착체를 형성하여 제거할 수 있다. 상기 포집은 반데르발스 인력, 소수성 인력, CH-ð 상호작용과 같은 2차 결합에 의해 유기 오염물질과 포접착제를 형성(host-guest interaction)하여 이루어진다.Cyclodextrins can selectively trap organic contaminants for each size to form and remove complexes. The collection is accomplished by host-guest interaction with organic contaminants by secondary bonding such as van der Waals attraction, hydrophobic attraction, and CH-ð interaction.

이어서, 본 발명의 수처리용 역삼투 분리막의 제조방법의 일례를 하기에서 설명한다.Next, an example of the manufacturing method of the reverse osmosis membrane for water treatment of this invention is demonstrated below.

(S1) 분리막 기재를 제공한다.(S1) A separator base material is provided.

사용가능한 분리막 기재에 대한 내용이 상기에 기재되어 있다.Information on the separator substrates that can be used is described above.

(S2) 상기 분리막 기재에 링커를 형성시키고 페로센 카복스알데하이드와 가지구조형 친수성 고분자의 반응 생성물을 도입한다.(S2) A linker is formed on the separator substrate, and a reaction product of ferrocene carboxaldehyde and branched hydrophilic polymer is introduced.

상기 링커부를 형성시키기 위해, 분리막 기재를 -COOH 로 개질시키고, 상기 -COOH에 1-에틸-3(3-디메틸 아미노프로필)카보디이미드 (1-ethyl-3(3-dimethyl aminopropyl) carbodiimide, EDC) 및 히드록실석식이미드 (N-hydroxysuccinimide, NHS)의 EDC/NHS 반응을 순차적으로 수행할 수 있으나, 이에 한정되는 것은 아니다. 이 때, 분리막 기재에 형성되어 있는 -COOH 1몰 기준으로 동일한 몰의 EDC 및 NHS 각각이 첨가될 수 있다. 또는, 분리막 기재와 가지구조형 친수성 고분자를 매개시킬 수 있는 임의의 표면중합, 코팅 등의 다른 표면 개질 방법을 이용하여 링커부를 도입할 수 있다.In order to form the linker portion, the separator substrate is modified with -COOH, and 1-ethyl-3 (3-dimethyl aminopropyl) carbodiimide (1-ethyl-3 (3-dimethyl aminopropyl) carbodiimide, EDC is added to the -COOH. ) And hydroxyl-succinimide (N-hydroxysuccinimide, NHS) may be performed sequentially, but is not limited thereto. At this time, the same moles of EDC and NHS may be added based on 1 mole of -COOH formed in the separator substrate. Alternatively, the linker portion may be introduced using other surface modification methods such as surface polymerization and coating, which may mediate the separator substrate and the branched hydrophilic polymer.

가지구조형 친수성 고분자-페로센 복합체를 링커부를 통해 분리막 기재에 도입하기 위해, 먼저, 가지구조형 친수성 고분자-페로센 복합체를 준비한다. 가지구조형 친수성 고분자 1몰 기준으로 페로센 10 내지 100 몰 또는 12.5 내지 75몰을 사용할 수 있다. 페로센 함량이 상기 상한치보다 많으면 역삼투 분리막의 수 투과도가 지나치게 낮아지게 되고, 페로센 함량이 상기 하한치보다 적으면 사이클로덱스트린을 도입하는 효과가 미미하게 된다. 가지구조형 친수성 고분자와 페로센-카복스알데하이드의 반응은 각각을 유기용매, 예컨대, 메탄올 등을 용매로 사용하여 용액 상태로 만들고, 도 2에 도시된 바와 같이 환원 반응에 의해 이루어질 수 있다. 상기 환원 반응은 강환원제, 예컨대, 소듐 보로하이드라이드(NaBH4)를 이용하여 이루어질 수 있으나, 이에 한정되는 것은 아니다. In order to introduce the branched hydrophilic polymer-ferrocene complex into the separator substrate through the linker portion, first, the branched hydrophilic polymer-ferrocene complex is prepared. 10 to 100 moles or 12.5 to 75 moles of ferrocene may be used based on 1 mole of the branched hydrophilic polymer. If the ferrocene content is greater than the upper limit, the water permeability of the reverse osmosis membrane is too low, and if the ferrocene content is less than the lower limit, the effect of introducing cyclodextrin is insignificant. The reaction of the branched hydrophilic polymer with the ferrocene-carboxaldehyde may be achieved in a solution state by using an organic solvent, such as methanol, as a solvent, and by a reduction reaction as shown in FIG. 2. The reduction reaction may be performed using a strong reducing agent such as sodium borohydride (NaBH 4 ), but is not limited thereto.

가지구조형 친수성 고분자-페로센 복합체를 반응시켜 가지구조형 친수성 고분자-페로센 복합체가 링커부를 통해 연결된 분리막 기재가 수득된다. The branched hydrophilic polymer-ferrocene complex is reacted to obtain a separator substrate in which the branched hydrophilic polymer-ferrocene complex is connected through a linker portion.

(S3) 사이클로덱스트린을 도입하여 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체가 링커부를 통해 분리막 기재에 연결된 수처리용 역삼투 분리막이 수득되다.(S3) The cyclodextrin is introduced to obtain a reverse osmosis membrane for water treatment in which the branched hydrophilic polymer-ferrocene-cyclodextrin complex is connected to the separator substrate through a linker portion.

페로센과 동일한 몰(mol)의 사이클로덱스트린을 첨가하고, 초음파 처리하여 페로센-사이클로덱스트린 포접체를 형성시킴으로써 가지구조형 친수성 고분자-페로센-사이클로덱스트린 포접체가 구비된 수처리용 역삼투 분리막이 제공된다. 상기 초음파 처리는 약 24시간 내지 36시간 동안 수행될 수 있다.A reverse osmosis membrane for water treatment provided with a branched hydrophilic polymer-ferrocene-cyclodextrin clathrate is added by adding a mole of cyclodextrin equal to ferrocene and sonicating to form a ferrocene-cyclodextrin clathrate. The sonication may be performed for about 24 hours to 36 hours.

본 발명은 수처리용 역삼투 분리막의 재생 방법을 제공한다. 상기 재생 방법은 하기 (R1) 내지 (R3)의 단계를 포함할 수 있다. The present invention provides a regeneration method of a reverse osmosis membrane for water treatment. The regeneration method may include the following (R1) to (R3).

(R1) 사이클로덱스트린에 오염물질이 부착된 분리막을 준비하는 단계;(R1) preparing a separator having contaminants attached to the cyclodextrin;

(R2) 페로센을 산화시켜 사이클로덱스트린을 오염물질과 함께 해리시키는 단계; 및(R2) oxidizing ferrocene to dissociate the cyclodextrin with contaminants; And

(R3) 페로센을 환원시켜 페로센과 사이클로덱스트린 복합체를 재형성시키는 단계. (R3) reducing ferrocene to reconstitute the ferrocene and cyclodextrin complex.

상기 방법은 수처리용 분리막 중 외부와 가장 빈번하게 접하게 되는 사이클로덱스트린에 오염물질이 부착되어 있는 구현예를 가정한 것이다. 이를 위해, (R1)에서 사이클로덱스트린에 오염물질이 부착된 분리막을 준비한다. 이 때, 상기 오염물질로는, 세틸 트리메틸 암모늄 클로라이드(CTAC)와 같은 양이온 계면활성제; 프탈레이트계 물질, 비스페놀류와 같은 내분비계 장애물질; 유기계열 살충제 물질; 이온성/비이온성 약물; 페놀류를 비롯한 방향족 화합물; 휘발성 황화합물; 휘발성 질소화합물; 휘발성 단쇄 지방산 및 카다베린(cadaverine), 메탄올(methanol), 에탄올(ethanol), 아세톤(acetone), 아세트알데하이드(acetaldehyde)를 들 수 있으나, 이에 한정되는 것은 아니다. The method assumes an embodiment in which a contaminant is attached to a cyclodextrin which is most frequently contacted with the outside of the separation membrane for water treatment. To this end, in (R1) to prepare a separation membrane with contaminants attached to the cyclodextrin. At this time, the contaminants include cationic surfactants such as cetyl trimethyl ammonium chloride (CTAC); Endocrine disruptors such as phthalate substances and bisphenols; Organic insecticides; Ionic / nonionic drugs; Aromatic compounds including phenols; Volatile sulfur compounds; Volatile nitrogen compounds; Volatile short-chain fatty acids and cadaverine (cadaverine), methanol (methanol), ethanol (ethanol), acetone (acetone), acetaldehyde (acetaldehyde), but is not limited thereto.

(R2) 단계는 수처리용 역삼투 분리막이 있는 물에 전기를 인가하는 등의 방식으로 페로센을 산화시켜 수행될 수 있다. 이로써 사이클로덱스트린이 페로센과의 결합으로부터 해리되어 수처리용 삼투압 분리막에서도 해리되고, 이 때 사이클로덱스트린에 부착된 오염물질이 함께 제거되는 효과를 갖는다. 해리된 사이클로덱스트린은 포집 장치 등을 통해 수거되어 오염물질을 제거한 후에 재사용할 수 있다. The step (R2) may be performed by oxidizing ferrocene by applying electricity to water having a reverse osmosis membrane for water treatment. As a result, the cyclodextrin is dissociated from the binding with ferrocene and is also dissociated in the osmotic membrane for water treatment. At this time, the contaminants attached to the cyclodextrin are removed together. Dissociated cyclodextrins can be collected via a collection device or the like to be reused after removing contaminants.

(R3) 단계는 사이클로덱스트린이 제거된 수처리용 역삼투 분리막에 깨끗한 사이클로덱스트린을 다시 도입시키는 단계이다. 오염물질이 부착되지 않은 사이클로덱스트린을 수처리용 역삼투 분리막이 있는 물에 첨가하고 카본 플레이트 전극을 사용하는 등의 방식으로 페로센을 환원시킨다. 이어서, 24 내지 36시간동안 초음파 처리하여 사이클로덱스트린과 페로센의 포접이 이루어지도록 함으로써 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체가 구비된 수처리용 역삼투 분리막이 수득된다.(R3) is a step of introducing the clean cyclodextrin back to the reverse osmosis membrane for water treatment in which the cyclodextrin was removed. Cyclodextrins free of contaminants are added to water with reverse osmosis membranes for water treatment and the ferrocene is reduced, for example, using a carbon plate electrode. Subsequently, the ultrasonic treatment for 24 to 36 hours to allow the inclusion of cyclodextrin and ferrocene to obtain a reverse osmosis membrane for water treatment equipped with a branched hydrophilic polymer-ferrocene-cyclodextrin complex.

이하, 본 발명의 이해를 돕기 위하여 실시예 등을 들어 상세하게 설명하기로 한다. 그러나 본 발명에 따른 실시 예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 하기 실시 예들에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시 예들은 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다. Hereinafter, examples and the like will be described in detail to help understand the present invention. However, the embodiments according to the present invention may be modified in various other forms, and the scope of the present invention should not be construed as being limited to the following embodiments. Embodiments of the present invention are provided to more fully describe the present invention to those skilled in the art.

실시예Example 1 One

가지구조형 폴리에틸렌이민(Mw 25,000; Degree of branching 약 0.38)을 메탄올에 용해시킨 용액에 페로센 카복스알데하이드를 용해시킨 메탄올 용액을 천천히 섞어주었다. 이 때 가지구조형 폴리에틸렌 이민 0.07 mmol 기준으로 페로센 카복스알데하이드 0.87mmol (12.5 당량)이 되도록 사용하였다. 페로센 카복스알데하이드와 같은 몰비의 NaBH4를 넣어주어 환원 반응을 유도하여 가지구조형 폴리에틸렌이민의 이민기에 페로센을 합성하였다. 합성한 고분자(가지구조형 폴리에틸렌이민-페로센 복합체, b-Fc)는 디에틸 에테르를 통해 미반응 물질들을 걸러주고 진공오븐에 넣어 수분이 없는 상태로 보관한다.The methanol solution in which ferrocene carboxaldehyde was dissolved was slowly mixed with a solution of branched polyethyleneimine (Mw 25,000; Degree of branching about 0.38) in methanol. At this time, 0.07 mmol (12.5 equivalents) of ferrocene carboxaldehyde was used based on 0.07 mmol of branched polyethylene imine. Ferrocene was synthesized by imine group of branched polyethyleneimine by inducing a reduction reaction by adding a molar ratio of NaBH 4 such as ferrocene carboxaldehyde. The synthesized polymer (branched polyethylenimine-ferrocene complex, b-Fc) is filtered through diethyl ether to filter out unreacted materials and stored in a vacuum oven in a dry state.

분리막 기재는 역삼투 특성을 갖는 것으로, 0.1 wt% EDC 용액에 담가 표면에 불안정한 O-acylisourea ester 중간체를 형성한 후, NHS를 추가하여 아민 반응성 NHS-ester 중간체를 부여하였다. The membrane substrate had reverse osmosis characteristics, soaked in 0.1 wt% EDC solution to form an unstable O-acylisourea ester intermediate on the surface, and NHS was added to give an amine-reactive NHS-ester intermediate.

분리막 기재를 물로 한번 세척한 후에 1g/L의 페로센으로 개질된 가지구조형 폴리에틸렌이민(b-Fc) 용액에 넣어 24시간 동안 반응시켜 b-Fc로 개질된 역삼투 분리막을 제조하였다. The membrane substrate was washed once with water, and then put into 1 g / L ferrocene-modified branched polyethyleneimine (b-Fc) solution to react for 24 hours to prepare a reverse osmosis membrane modified with b-Fc.

이렇게 개질된 역삼투 분리막을 사이클로덱스트린 용액에 담가주어 페로센과 반응시킴으로써 페로센-사이클로덱스트린 복합체가 합성된 가지구조형 폴리에틸렌이민(b-Fc/CD)으로 개질된 역삼투 분리막('RO/b-Fc1/CD')을 제작하였다.The modified reverse osmosis membrane ('RO / b-Fc1 /) was immersed in a cyclodextrin solution and reacted with ferrocene to modify the ferrocene-cyclodextrin complex into branched polyethyleneimine (b-Fc / CD). CD ').

실시예Example 2 2

가지구조형 폴리에틸렌 이민 0.07 mmol 기준으로 페로센 카복스알데하이드 1.75mmol (25 당량)이 되도록 사용하는 것을 제외하고 실시예 1과 동일한 방법으로 역삼투 분리막('RO/b-Fc2/CD')을 제작하였다.A reverse osmosis membrane ('RO / b-Fc2 / CD') was prepared in the same manner as in Example 1 except that the ferrocene carboxaldehyde was used at 1.75 mmol (25 equivalents) based on 0.07 mmol of branched polyethylene imine.

실시예Example 3 3

가지구조형 폴리에틸렌 이민 0.07 mmol 기준으로 페로센 카복스알데하이드 3.5 mmol (50 당량)이 되도록 사용하는 것을 제외하고 실시예 1과 동일한 방법으로 역삼투 분리막('RO/b-Fc4/CD')을 제작하였다.A reverse osmosis membrane ('RO / b-Fc4 / CD') was prepared in the same manner as in Example 1, except that 3.5 mmol (50 equivalents) of ferrocene carboxaldehyde was used based on 0.07 mmol of branched polyethylene imine.

실시예Example 4 4

가지구조형 폴리에틸렌 이민 0.07 mmol 기준으로 페로센 카복스알데하이드 5.25 mmol (75 당량)이 되도록 사용하는 것을 제외하고 실시예 1과 동일한 방법으로 역삼투 분리막('RO/b-Fc6/CD')을 제작하였다.A reverse osmosis membrane ('RO / b-Fc6 / CD') was prepared in the same manner as in Example 1 except that the ferrocene carboxaldehyde was used as 5.25 mmol (75 equivalents) based on 0.07 mmol of the branched polyethylene imine.

평가예Evaluation example

페로센 카복스알데하이드 및 실시예 1 내지 4에서 페로센에 의해 개질된 가지구조형 폴리에틸렌이민의 특성을 FT-IR (Fourier-transform Infrared Spectroscopy) 분석하였으며, 그 결과를 도 4에 나타내었다.Fourier-transform Infrared Spectroscopy (FT-IR) analysis of the ferrocene carboxaldehyde and branched polyethyleneimine modified by ferrocene in Examples 1 to 4 was performed, and the results are shown in FIG. 4.

또한, 페로센 카복스알데하이드 및 실시예 1 내지 4에서 페로센에 의해 개질된 가지구조형 폴리에틸렌이민의 특성을 H1NMR (Proton NuclearMagnetic Resonance) 분석하여 나타내었으며, 그 결과를 도 5에 나타내었다.In addition, the properties of ferrocene carboxaldehyde and branched polyethyleneimine modified by ferrocene in Examples 1 to 4 were shown by H 1 NMR (Proton Nuclear Magnetic Resonance) analysis, the results are shown in FIG.

상기 도 4와 도 5의 그래프로부터, 페로센이 성공적으로 가지구조형 폴리에틸렌이민에 합성되었음은 물론 페로센의 양을 조절함으로서 합성된 양을 확인할 수 있다. 보다 구체적으로, 도 5의 NMR에 페로센과 b-PEI 피크의 적분비에 의해 페로센과 b-PEI가 여러 조성비로 합성되었음을 확인할 수 있다. 이와 관련하여, b-Fc1과 b-Fc2의 경우에는 DLS(Dynamic Light Scattering)에 의한 크기 측정결과, 페로센 함량이 적어 기존의 가지구조형 폴리에틸렌이민과 비슷한 10 nm 내외의 크기를 갖는 것으로 나타난 반면, b-Fc4와 b-Fc6의 경우에는 소수성 페로센의 양이 증가함에 따라 뭉치는 힘이 커져 물속에서 각각 63.6 nm, 104.3 nm 크기를 갖게 되었다. 이와 같이 페로센 조성비가 증가할수록 카복실기에 결합된 b-FC 이외의 b-FC가 부가적으로 도입되며, 최종적으로 수득되는 역삼투 분리막의 수투과도를 감소시키는 결과를 가져온다. 이러한 점을 고려하여, 페로센 뭉침이 상대적으로 적으면서 하나의 페로센당 사이클로덱스트린을 상대적으로 많이 도입할 수 있는 RO/b-Fc2/CD가 수처리 분리막에 가장 바람직하다.From the graphs of FIGS. 4 and 5, ferrocene was successfully synthesized in the branched polyethyleneimine as well as the amount synthesized by controlling the amount of ferrocene. More specifically, it can be confirmed that ferrocene and b-PEI were synthesized in various composition ratios by the ratio of ferrocene and b-PEI peaks in the NMR of FIG. 5. In this regard, in the case of b-Fc1 and b-Fc2, the size measurement by DLS (Dynamic Light Scattering) showed that the ferrocene content was small and had a size of about 10 nm, similar to the existing branched polyethyleneimine, but b In the case of -Fc4 and b-Fc6, as the amount of hydrophobic ferrocene increased, the grouping force increased to 63.6 nm and 104.3 nm in water, respectively. As the ferrocene composition ratio increases as described above, b-FC other than b-FC bound to the carboxyl group is additionally introduced, resulting in a decrease in the water permeability of the finally obtained reverse osmosis membrane. In view of this, RO / b-Fc2 / CD which is relatively small in the aggregation of ferrocene and can introduce a relatively high amount of cyclodextrin per ferrocene is most preferred for the water treatment membrane.

본원 명세서에서 하나의 페로센당 도입되는 사이클로덱스트린 개수는 하기 수학식 1을 이용하여 계산할 수 있으나, 이에 한정되는 것은 아니다:In the present specification, the number of cyclodextrins introduced per one ferrocene may be calculated using Equation 1, but is not limited thereto.

Figure pat00001
Figure pat00001

상기 수학식 1에서, In Equation 1,

중량평균분자량(Mw) 25000의 b-FC에서 N 개수(Numberof N in b-PEI)는 약 582 이고,The number of N in b-PEI in the b-FC of the weight average molecular weight (Mw) 25000 is about 582,

사이클로덱스트린에서 C-O 개수(Number of C-O in CD)는 35이며,The number of C-O in CD in the cyclodextrin is 35,

사이클로덱스트린 강도(Intensity of cyclodextrin)은 하기 수학식 2를 이용하여 계산하고:Intensity of cyclodextrin is calculated using Equation 2:

Figure pat00002
Figure pat00002

b-FC 강도는 하기 수학식 3을 이용하여 계산한다:b-FC intensity is calculated using Equation 3:

Figure pat00003
Figure pat00003

실시예에서 사용된 분리막 기재 및 실시예 1 내지 4에서 제조된 본 발명에 따른 수처리용 역삼투 분리막을 FT-IR 분석하고, 그 결과를 도 6에 나타내었다.FT-IR analysis of the membrane substrate used in the Example and the reverse osmosis membrane for water treatment according to the present invention prepared in Examples 1 to 4, and the results are shown in FIG.

또한, 실시예에서 사용된 분리막 기재(TFC PA RO), 상기 분리막 기재에 페로센 개질된 가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 XPS(X-ray photoelectron spectroscopy) 분석하고 그 결과를 도 7에 나타내었다.In addition, the membrane substrate (TFC PA RO) used in the embodiment, the ferrocene-modified branched polyethylene imine complex conjugated form (RO / b-Fc) and the ferrocene-branched structure further modified by cyclodextrin used in the separator substrate Polyethylene imine complex bound form (RO / b-Fc / CD) was analyzed by X-ray photoelectron spectroscopy (XPS) and the results are shown in FIG. 7.

실시예에서 사용된 분리막 기재(TFC PA RO), 상기 분리막 기재에 페로센 개질된 가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 도 8에서 FE-SEM 이미지로 나타내었다.Membrane Substrate (TFC PA RO) used in the Examples, the form in which the ferrocene-modified branched polyethylene imine complex is bound to the separator substrate (RO / b-Fc) and the ferrocene-branched polyethylene imine further modified by cyclodextrin. The complex bound form (RO / b-Fc / CD) is shown in FE-SEM image in FIG. 8.

실시예에서 사용된 분리막 기재(TFC PA RO), 상기 분리막 기재에 페로센 개질된 가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 도 9에서 AFM(Atomic force microscope) 이미지로 나타내었다.Membrane Substrate (TFC PA RO) used in the Examples, the form in which the ferrocene-modified branched polyethylene imine complex is bound to the separator substrate (RO / b-Fc) and the ferrocene-branched polyethylene imine further modified by cyclodextrin. The combined form (RO / b-Fc / CD) is shown in Atomic force microscope (AFM) images in FIG. 9.

상기와 같이, 도 6 내지 도 9에서 FT-IR, XPS, FE-SEM, AFM을 이용하여 막 표면 개질에 따른 화학적 구조 및 표면 형태의 변화를 관찰힌 결과, 개질을 진행함에 따라 해당하는 작용기의 도입이 관찰되었으며 친수성 역시 증가하였고 AFM과 FE-SEM의 결과 합성 과정 중 막 손상이 일어나지 않음을 확인하였다. 이러한 분석으로 인해 역삼투 분리막이 b-FC/CD로 개질되는 것을 확인하였다.As described above, the changes in the chemical structure and the surface morphology of the membrane surface were observed using FT-IR, XPS, FE-SEM, and AFM in FIGS. 6 to 9. Introduction was observed and hydrophilicity was also increased, and the results of AFM and FE-SEM confirmed that no membrane damage occurred during the synthesis. This analysis confirmed that the reverse osmosis membrane was modified with b-FC / CD.

실시예에서 사용된 분리막 기재(TFC PA RO) 및 사이클로덱스트린에 의해 더 개질된 페로센-가지구조형 폴리에틸렌 이민 복합체가 결합된 형태(RO/b-Fc/CD)를 사용하여 이러한 분리막의 내오염성 측정을 위해 수투과 테스트를 수행하고, 그 결과를 도 10에 나타내었다. 수투과 테스트는 3번의 파울링 테스트 후 전기장을 주어 사이클로덱스트린 재생에 의한 수투과도 회복 성능을 평가하여 실시하였다. 상기 파울링 테스트는 역삼투 분리막 평가 장치 (dead-end 방식)을 이용하여 RO/b-Fc2/CD와 상용되는 역삼투 분리막에 20분간 순수한 물을 흘려주어 값을 고정시킨 후, 60 mg/L CTAC 용액(오염물질)을 100분간 흘려주어 수투과도의 상대적 감소량을 확인하였다. 그 후 막을 물 또는 세척 용액으로 세척시킨 후 다시 순수한 물을 흘려주어 회복된 수투과도를 확인함으로서 막의 내오염성을 확인하였으며, 이 실험을 3번 반복하여 진행하였다. 그 결과 RO/b-Fc2/CD의 경우 큰 친수성에 의해 오염물질에 대한 오염도가 적고 세척 후 높은 회복율을 나타내었다. 상기 재생실험은 3번 파울링 테스트가 진행된 오염된 막에 전기장을 가하여 사이클로덱스트린을 재생 시킨후, 다시 순수한 물을 흘려주어 수투과도의 회복율을 확인하였다.Measurement of fouling resistance of such membranes was carried out using a combination of the membrane substrate (TFC PA RO) used in the examples and the ferrocene-branched polyethylene imine complex further modified by cyclodextrin (RO / b-Fc / CD). A water permeation test was carried out for the purpose, and the results are shown in FIG. 10. The water permeation test was performed by evaluating the water permeability recovery performance by cyclodextrin regeneration by giving an electric field after three fouling tests. The fouling test uses a reverse osmosis membrane evaluation device (dead-end method) to fix the value by flowing pure water for 20 minutes to the reverse osmosis membrane commercially compatible with RO / b-Fc2 / CD, 60 mg / L CTAC solution (contaminant) was flowed for 100 minutes to confirm the relative decrease in water permeability. Thereafter, the membrane was washed with water or a washing solution, and then pure water was poured again to check the recovered water permeability to check the fouling resistance of the membrane. This experiment was repeated three times. As a result, in the case of RO / b-Fc2 / CD, due to the high hydrophilicity, the degree of contamination to pollutants was small and high recovery rate after washing was shown. The regeneration experiment was applied to the contaminated membrane subjected to the three fouling test to regenerate the cyclodextrin to regenerate the cyclodextrin, and then flowed again pure water to confirm the recovery rate of water permeability.

도 10에서 확인되는 바와 같이, 개질하지 않은 막에 비해 수투과도의 감소가 적었다. 개질되지 않은 막에 화학적 세척을 하는 경우 처음에는 높은 회복율을 보였지만 수투과 테스트를 진행함에 따라 회복성능이 감소한 반면, 개질된 막의 경우 계속 높은 회복성능을 보였다. 또한 막 오염이 충분히 진행된 후 표면의 사이클로덱스트린을 전기를 가해 제거하고 새로운 사이클로덱스트린을 도입하는 것으로 감소되었던 수투과도가 높은 수준으로 복구되는 것을 관찰하였다. 따라서 페로센-사이클로덱스트린 복합체가 도입된 가지구조형 폴리에틸렌이민으로 개질된 역삼투 분리막은 기존의 분리막에 비해 우수한 내오염성능과 회복성능을 가진다고 볼 수 있다.As can be seen in FIG. 10, there was less reduction in water permeability compared to unmodified membranes. Chemical cleaning of unmodified membranes initially showed high recovery rates, but recovery performance decreased with permeability tests, while modified membranes continued to exhibit high recovery performances. It was also observed that after membrane contamination had sufficiently progressed, the water permeability was reduced to a high level, which was reduced by applying electricity to remove the surface cyclodextrin and introducing a new cyclodextrin. Therefore, the reverse osmosis membrane modified with branched polyethyleneimine into which the ferrocene-cyclodextrin complex is introduced can be considered to have excellent fouling resistance and recovery performance compared to the conventional membrane.

Claims (7)

분리막 기재;
상기 분리막 기재 상에 형성된 링커부; 및
상기 링커부를 통해 분리막 기재에 연결되어 있는 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체;
를 포함하는 수처리용 역삼투 분리막.
Separator substrate;
A linker portion formed on the separator substrate; And
A branched hydrophilic polymer-ferrocene-cyclodextrin complex connected to the separator substrate through the linker portion;
Reverse osmosis membrane for water treatment comprising a.
제1항에 있어서,
상기 가지구조형 친수성 고분자가 폴리에틸렌이민인 것을 특징으로 하는 수처리용 역삼투 분리막.
The method of claim 1,
Reverse osmosis membrane for water treatment, characterized in that the branched hydrophilic polymer is polyethyleneimine.
제1항에 있어서,
상기 가지구조형 친수성 고분자와 페로센은 화학적으로 결합되어 있는 것을 특징으로 하는 수처리용 역삼투 분리막.
The method of claim 1,
The branched hydrophilic polymer and ferrocene are reverse osmosis membranes for water treatment, characterized in that chemically bonded.
제1항에 있어서,
상기 사이클로덱스트린과 페로센은 사이클로덱스트린 내에 페로센이 포접되어 물리적으로 결합되어 있는 것을 특징으로 하는 수처리용 역삼투 분리막.
The method of claim 1,
The cyclodextrin and ferrocene are reverse osmosis membrane for water treatment, characterized in that the ferrocene is contained in the cyclodextrin is physically bonded.
(S1) 분리막 기재를 제공하는 단계;
(S2) 상기 분리막 기재에 링커부를 형성시키고 페로센 카복스알데하이드와 가지구조형 친수성 고분자의 반응 생성물을 도입하는 단계; 및
(S3) 사이클로덱스트린을 도입하여 가지구조형 친수성 고분자-페로센-사이클로덱스트린 복합체를 형성하는 단계;를 포함하는
제1항에 기재된 수처리용 역삼투 분리막의 제조방법.
(S1) providing a separator substrate;
(S2) forming a linker portion in the separator substrate and introducing a reaction product of ferrocene carboxaldehyde and a branched hydrophilic polymer; And
(S3) introducing cyclodextrin to form a branched hydrophilic polymer-ferrocene-cyclodextrin complex; comprising
The manufacturing method of the reverse osmosis membrane for water treatment of Claim 1.
제5항에 있어서,
상기 링커부 도입을 위해 EDC(1-ethyl-3-(3-dimethylaminopropyl)carbodiimide hydrochloride)/NHS(N-hydroxysuccinimide) 반응이 수행되는 것을 특징으로 하는 수처리용 역삼투 분리막의 제조방법.
The method of claim 5,
EDC (1-ethyl-3- (3-dimethylaminopropyl) carbodiimide hydrochloride) / NHS (N-hydroxysuccinimide) reaction for the introduction of the linker portion is a method for producing a reverse osmosis membrane for water treatment.
(R1) 사이클로덱스트린에 오염물질이 부착된 분리막을 준비하는 단계; (R2) 페로센을 산화시켜 사이클로덱스트린을 오염물질과 함께 해리시키는 단계; 및 (R3) 페로센을 환원시켜 페로센과 사이클로덱스트린 복합체를 재형성시키는 단계;를 포함하는 제1항에 기재된 수처리용 역삼투 분리막의 재생 방법.(R1) preparing a separator having contaminants attached to the cyclodextrin; (R2) oxidizing ferrocene to dissociate the cyclodextrin with contaminants; Regenerating the ferrocene and cyclodextrin complex by reducing the ferrocene (R3); The method for regenerating the reverse osmosis membrane for water treatment according to claim 1.
KR1020180022018A 2018-02-23 2018-02-23 Water-treatment membrane and Method of manufacturing the same KR102040272B1 (en)