KR20190086956A - Waterproof construction method that can detect leakage by using infrared device - Google Patents
Waterproof construction method that can detect leakage by using infrared device Download PDFInfo
- Publication number
- KR20190086956A KR20190086956A KR1020180005116A KR20180005116A KR20190086956A KR 20190086956 A KR20190086956 A KR 20190086956A KR 1020180005116 A KR1020180005116 A KR 1020180005116A KR 20180005116 A KR20180005116 A KR 20180005116A KR 20190086956 A KR20190086956 A KR 20190086956A
- Authority
- KR
- South Korea
- Prior art keywords
- leakage
- water
- construction method
- drying
- infrared device
- Prior art date
Abstract
Description
본 발명은 적외선기기를 이용하여 누수탐지가 가능한 방수 시공방법에 관한 것으로서, 건물의 천장 또는 벽체에 발생되는 누수를 탐지 시, 적외선기기를 이용하여 누수탐지하고 방수 처리하는 시공방법에 관한 것이다. BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a waterproof construction method capable of detecting water leakage by using an infrared device, and more particularly, to a construction method of detecting water leakage and waterproofing by using an infrared device when water leakage generated in a ceiling or a wall of a building is detected.
우선 종래의 기술을 살펴보면, First of all,
일반적으로 황토는 광물인 점토광물의 총칭으로 황색 내지 갈색의 일종의 무기산화물의 혼합물로서 가열시 다량의 원적외선을 방출하는 세라믹의 일종으로 볼 수 있다. In general, loess is a kind of clay mineral which is a kind of inorganic oxide of yellow to brown type, which is a kind of ceramics which emits a large amount of far-infrared rays upon heating.
이러한 황토는 특히 원적외선 방출에 의하여 인체의 생체 세포를 활성화하여 신진대사를 촉진하며, 탈취, 제습, 살균 등 정화하는 성분으로도 오래전부터 널리 사용되었음이 알려져있다. It is known that the loess is widely used as a component for purification of deodorization, dehumidification, sterilization and the like, by promoting the metabolism by activating the living body cells of the body by the far-infrared ray emission.
최근에는 이러한 유익한 천연재료인 황토를 이용하여 건축재로서 채용하여 사용하는 경향이 많아지고 있는 실정이고, 이러한 황토를 이용한 방수기술 또는 건축물에 시공되는 최근 출원된 기술을 몇 가지 살펴보도록 한다. In recent years, there has been a tendency to employ these beneficial natural materials, such as loess, as building materials, and a few of the recently applied technologies applied to waterproofing techniques or buildings using such loess are discussed.
황토를 이용한 시공방법의 일례로서 대한민국특허 공개번호 제2005-101055호에 개시된 내용을 살펴보면, 천연황토를 이용하여 건축구조물의 내 외벽면, 바닥면 또는 천정면을 시공한 후에 황토층의 건조과정에서 균열이 발생하는 문제를 해결하기 위해서 안출된 것으로 건축물의 표면에 초벌매개체가 되는 세멘콘크리트 또는 핸디 코트로 1차 도포 처리한 다음 2-3 ㎝ 두께의 천연황토 수화물을 도포, 처리하여 마감하는 시공방법에 관한 것이다. As an example of a construction method using loess, Korean Patent Laid-Open Publication No. 2005-101055 discloses a construction method in which after the interior or exterior wall surface, floor surface or ceiling surface of a building structure is constructed using natural loess, This is a method to solve the problem that occurs after applying the first coating with the semen concrete or handy coat which is the primitive medium on the surface of the building and then applying and treating the natural hull soil hydrate of 2-3 ㎝ thickness .
이러한 시공방법은 종래에 황토층의 균열을 방지하기 위해서 황토에 혼합하는 화학물질이나 무기 또는 유기접착제를 사용하지 않는 것을 장점으로 기재하고 있으나 천연황토를 도포하기 전에 내 외장 바탕에 사용하는 초벌 또는 재벌 도포재를 반드시 사용해야 하므로 건축비가 증대되는 문제가 있다. Such a construction method has conventionally described advantage of not using chemicals, inorganic or organic adhesives mixed in the loess soil in order to prevent cracking of the loess layer. However, in the case of applying the primer or conglomerate There is a problem that the construction cost is increased because the ash must be used.
다른 일례의 종래기술을 살펴보면, 대한민국 특허공개공보 제1999-42934호는 바닥면에 방수필름과 단열재를 시공하고 그 상부에 발열체를 부설한 다음 황토를 도포하고 황토에 무기질 또는 유기질 접착제를 혼합하여 이루어진 조성물을 발열체 상부에 도포 시공하는 기술에 관한 것이다. Korean Unexamined Patent Application Publication No. 1999-42934 discloses a method for producing a waterproof film and a heat insulating material on a bottom surface thereof, placing a heating element on the waterproof film, applying yellow clay and mixing an inorganic or organic adhesive to the clay The present invention relates to a technique for applying a composition onto an upper surface of a heating element.
이러한 시공방법은 발열체를 부설하고, 방수필름과 단열재를 별도로 시공하고 접착제가 함유된 황토로 시공하는 방법에 관한 것이나, 방수필름을 별도로 사용해야 하는 문제가 있다. Such a construction method relates to a method of laying a heating element, constructing a waterproof film and a heat insulating material separately, and installing the waterproof film with a yellow soil containing an adhesive, but there is a problem that a waterproof film must be separately used.
또 다른 일례의 황토를 이용한 시공방법으로 대한민국특허 공개공보 제1998-84228호에는 황토 시공후 수분 증발로 인한 수축균열을 방지하기 위해서 황토에 수화알칼리 실리케이트, 카소린, 디아로화나프탈렌, 설폰산 등을 첨가제로서 첨가한 방수제를 이용하여 시공하는 기술에 관한 것이다. As another example of a construction method using loess, Korean Patent Laid-Open Publication No. 1998-84228 discloses a method for preventing shrinkage cracking due to evaporation of water after application of a loess soil, comprising the steps of adding alkali earth silicate, calcine, diaronaphthalene, A waterproofing agent added as an additive.
이러한 시공방법은 황토에 고가의 실리케이트, 설폰산, 나프탈렌등의 화학제를 혼합 첨가하여 이루어진 것으로 시공 시 건축비가 상승하는 문제점이 있다. This construction method has a problem that the construction cost is increased when the construction is made by mixing the loess with high-priced chemicals such as silicate, sulfonic acid and naphthalene.
이에 종래에 등록번호 제10-0757929호의 ‘황토 방수 조성물 및 이를 이용하여 시공한 방수시공방법’과 등록번호 제20-0324973호의 ‘방수공사의 근적외선 융착공법 및 그 장치’가 개시되어 있지만, 상기한 문제점에 대해서는 여전히 개선되지 않고 있는 실정이다. Conventionally, the 'yellow clay waterproofing composition and the waterproofing construction method using it' of Registration No. 10-0757929 and the 'near infrared ray fusion method of waterproofing construction and its apparatus' of Registration No. 20-0324973 have been disclosed. The problem is still not improving.
본 발명은 상기한 종래 기술의 문제점을 해결하기 위하여 안출해낸 것으로서, 건물의 천장 또는 벽체에 발생되는 누수를 탐지함에 있어 적외선기기를 이용하여 누수부분과 누수량을 확인하고, 확인된 누수부분을 처리함에 있어 타공작업 후, 파이프를 삽입하여 물이 자연 배출되도록 하고, 자연배출에도 잔존 누수에 대해서는 발포제를 이용하여 방수하는 적외선기기를 이용하여 누수탐지가 가능한 방수 시공방법을 제공함에 주안점을 두고 기술적 과제로서 완성해낸 것이다. Disclosure of the Invention The present invention has been made to solve the problems of the prior art described above, and it is an object of the present invention to provide a method and apparatus for detecting leakages generated in a ceiling or a wall of a building using an infrared device, Therefore, it is a technical task to provide a waterproof construction method capable of detecting water leakage by inserting a pipe after the perforation work and allowing the water to be naturally discharged, and to use the infrared device for water leakage by using a foaming agent It is finished.
이에 본 발명은, 건물의 천장 또는 벽체에 발생되는 누수를 탐지하여 방수되도록 누수된 부분을 확인하는 누수확인단계와, 누수부분의 이물질을 박리하는 박리단계와, 박리된 부분의 표면을 매끄럽게 하는 그라인딩단계와, 누수부분을 방수 처리하는 누수처리단계와, 누수 처리 후 건조하는 건조단계 및 건조 후 도색하는 도색단계로 이루어지는 방수 시공방법에 있어서, 상기 누수확인단계에서는 적외선기기를 이용하여 누수부분과 누수량을 확인하고, 상기 누수처리단계에서는 누수부분에 타공작업 후 삽입하여 물을 배출하는 파이프가 구성되는 것을 특징으로 하는 적외선기기를 이용하여 누수탐지가 가능한 방수 시공방법을 그 기술적 특징으로 한다. Accordingly, the present invention provides a method of manufacturing a building, comprising: a leak checking step of detecting leakage of water generated in a ceiling or a wall of a building to confirm leakage of the leaked water; a peeling step of peeling foreign substances in the leaked portion; And a waterproofing method comprising a water leakage process step of waterproofing the water leakage part, a drying step of drying after the water leakage treatment, and a painting step of painting after drying, wherein in the water leakage confirmation step, And a pipe for discharging water by inserting the water after the puncturing operation is formed in the water leakage portion in the water leakage processing step. The waterproofing construction method capable of detecting leakage by using the infrared device.
본 발명에 따른 적외선기기를 이용하여 누수탐지가 가능한 방수 시공방법에 의하면, 천정 또는 벽체의 누수된 부분에 대한 누수탐지를 적외선기기를 이용하여 누수된 부분과 누수량을 손쉽게 확인할 수 있고, 방수 처리 시에는 누수된 위치 및 누수량에 따라 타공 후 파이프를 삽입하여 자연배출하거나 또는 페카와 발포제를 주입하여 추후 발생되는 누수를 미연에 방지할 수 있는 등 그 효과가 큰 발명이다. According to the waterproof construction method capable of detecting water leakage by using the infrared device according to the present invention, it is possible to easily detect water leakage and the leaked portion by using an infrared device for water leakage detection of a leaked portion of a ceiling or a wall, It is possible to insert the pipe after the piercing according to the leaking position and the amount of leaking water to discharge it naturally or to inject the plasticizer and the blowing agent to prevent the leakage which will occur in the future.
도 1은 본 발명인 방수 시공방법에 대한 작업흐름도
도 2는 본 발명인 방수 시공방법에 대한 다른 실시 예를 나타내는 작업흐름도1 is a flowchart of a waterproof construction method according to the present invention.
2 is a flowchart illustrating a waterproof construction method according to another embodiment of the present invention.
이하, 첨부되는 도면과 관련하여 상기 목적을 달성하기 위한 본 발명의 바람직한 구성 및 작용에 대하여 도 1, 도 2를 참고로 하여 설명하면 다음과 같다. Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings.
우선 본 발명을 설명하기에 앞서 그 구성을 도 1, 도 2를 참고하여 살펴보면, First, before describing the present invention, referring to FIG. 1 and FIG. 2,
본 발명인 방수 시공방법은 건물의 천장 또는 벽체에 발생되는 누수를 탐지하여 방수되도록 누수된 부분을 확인하는 누수확인단계와, 누수부분의 이물질을 박리하는 박리단계와, 박리된 부분의 표면을 매끄럽게 하는 그라인딩단계와, 누수부분을 방수 처리하는 누수처리단계와, 누수 처리 후 건조하는 건조단계 및 건조 후 도색하는 도색단계로 이루어지는 방수 시공방법에 있어서, 상기 누수확인단계에서는 적외선기기를 이용하여 누수부분과 누수량을 확인하고, 상기 누수처리단계에서는 누수부분에 타공작업 후 삽입하여 물을 배출하는 파이프가 구성된다. The waterproof construction method of the present invention is a waterproof construction method comprising: a water leakage checking step of detecting a water leakage generated in a ceiling or a wall of a building to identify a water leakage portion; a peeling step of peeling the foreign matter in the water leakage portion; A waterproofing method comprising a grinding step, a water leakage treatment step of waterproofing the water leakage part, a drying step of drying after the water leakage treatment, and a painting step of painting after drying, wherein in the water leakage confirmation step, And a pipe for discharging water by inserting the leaked portion after the puncturing operation is constituted.
상기 누수처리단계에서 파이프 삽입 후, 누수량에 따라 페카심기, 약액투입 및 발포제주입을 순차적으로 실행한다. After the piping is inserted in the leaking process step, the pesticide planting, the chemical liquid injection, and the blowing agent injection are sequentially executed in accordance with the leakage amount.
상기 건조단계 후, 누수확인단계를 진행하여 누수 확인 시, 노출된 페카와 발포제를 제거한다. After the drying step, the leak check step is performed to remove the exposed pecca and the foaming agent at the time of checking the leakage.
상기한 바와 같이 구성되는 본 발명을 더욱 상세하게 설명하면, The present invention, which is constructed as described above, will now be described in more detail.
우선, 종래의 방수 시공방법은 누수를 확인하는 누수확인단계와, 누수부분의 이물질을 박리하는 박리단계와, 박리된 부분의 표면을 매끄럽게 하는 그라인딩단계와, 누수부분을 방수 처리하는 누수처리단계와, 누수 처리 후 건조하는 건조단계 및 건조 후 도색하는 도색단계로 이루어진다. First, a conventional waterproofing method includes a water leakage confirmation step for confirming water leakage, a peeling step for peeling the foreign matter in the water leakage part, a grinding step for smoothing the surface of the peeling part, a water leakage processing step for waterproofing the water leakage part Drying step for drying after leakage treatment, and a painting step for coloring after drying.
상기 단계는 천정 또는 벽체의 누수된 부분을 탐사하여 방수하는 시공방법에 대해 일반적으로 사용되고 있는 단계이다. The above step is generally used for a construction method in which a leaked portion of a ceiling or a wall is explored and waterproofed.
이에, 본 발명인 방수 시공방법에 대해 설명하면, The waterproof construction method of the present invention will now be described.
누수확인단계에서는 적외선기기를 이용하여 누수부분과 누수량을 확인한다. In the leak detection step, the leakage part and the leakage amount are checked using an infrared device.
상기 적외선기기를 이용하게 되면, 누수 되지 않은 부분에는 붉은색으로 표시되고, 누수부분에 대해 파란색으로 표시된다. 이는 적외선기기를 이용하여 누수부분을 확인하기 위함이다. When the infrared device is used, red portions are displayed on the non-leaked portions, and blue portions are displayed on the leak portions. This is to confirm the leakage part using infrared device.
박리단계에서는 상기 누수확인단계에서 확인된 누수부분 및 그 주변에 대한 이물질을 박리한다. In the peeling step, the leaked water portion identified in the leak check step and the foreign matter to the periphery thereof are peeled off.
그라인딩단계에서는 박리된 부분 및 누수부분에 대해 표면을 매끄럽게 한다. 이때, 통상적으로는 그라인딩기기를 이용한다. In the grinding step, the surface is smoothed with respect to the peeled and leaked portions. At this time, a grinding machine is usually used.
누수처리단계에서는 누수부분을 확인 후, 상기 누수부분의 벽체에 타공작업을 진행한다. 이때, 타공하는 깊이는 천정 또는 벽체의 두께에 따라 달리 한다. In the leaking process step, after confirming the leaking portion, the leaking operation is performed on the wall of the leaking portion. At this time, the depth of perforation depends on the ceiling or wall thickness.
상기 타공작업이 완료되면, 타공부분에 누수된 물을 외부로 배출하는 파이프를 삽입한다. When the piercing work is completed, a pipe for discharging the water leaking out to the piercing hole is inserted.
상기 파이프는 5 ~ 10cm 정도의 깊이로 삽입하는데, 이는 누수된 부분의 위치 또는 누수정도에 따라 가변될 수 있는 깊이이다. The pipe is inserted at a depth of about 5 to 10 cm, which is a depth that can vary depending on the position of the leaked portion or the degree of leak.
상기 누수처리단계에서 타공부분에 파이프 삽입이 완료되면, 누수된 량에 따라 페카를 심고, 상기 페카의 내부로 약액을 투입한 후에 발포제를 주입하는 것을 순차적으로 실행한다. When the piping is completed in the perforated portion in the leaking process, the pesticide is planted according to the leaked amount, the chemical liquid is injected into the pecca, and then the foaming agent is injected sequentially.
건조단계에서는 상기 누수처리 후, 12 ~ 48시간 사이에 건조작업을 진행하게 되는데, 이때에는 자연건조를 실행한다. In the drying step, the drying operation is performed between 12 and 48 hours after the water leakage treatment. At this time, natural drying is performed.
도색단계에서는 상기 건조단계 후, 12 ~ 24시간 사이에 도색작업을 진행하게 된다. In the painting step, the painting operation is performed between 12 and 24 hours after the drying step.
이때, 방수 시공한 부분의 상태에 따라 박리단계와 그라인딩단계를 진행한 후, 도색단계를 진행할 수도 있다. At this time, the peeling step and the grinding step may be performed according to the state of the waterproof part, and then the painting step may be performed.
상기한 방수 시공방법의 단계 중에서 상기 건조단계 후, 누수확인단계를 진행한다. After the drying step among the steps of the waterproofing method, the leakage checking step is performed.
이때, 누수확인은 상기 누수확인단계에서와 동일하게 진행하며, 누수 확인이 되지 않으면 도색단계로 넘어가지만, 잔존 누수가 확인 시에는 노출된 페카와 발포제를 제거한다. At this time, the leak check is performed in the same manner as in the leak check step. If the leakage is not confirmed, the process goes to the painting step. However, when the leakage is confirmed, the exposed peca and the blowing agent are removed.
상기에서 누수가 확인되어 페카와 발포제를 제거한 후에는 잔존누수에 대해 자연건조가 진행되도록 하고, 이후에는 도색단계로 넘어가게 된다. After the leakage is confirmed and the pecca and the foaming agent are removed, natural drying is progressed to the remaining water leakage, and then the painting is passed to the painting step.
이는 잔존누수의 양이 많지 않았을 상황이고, 타공된 부분이 페카와 발포제로 막힘 되어 있어 잔존누수가 외부로 표출되지 않을 상황임으로써, 잔존누수에 대해서는 자연건조가 되도록 하기 위함이다. This is because the remaining amount of leaking water is not so large, and the pierced portion is blocked by the fecal material and the foaming agent, so that the residual leaking water is not exposed to the outside.
상기와 같은 본 발명에 따르면, 천정 또는 벽체의 누수된 부분에 대한 누수탐지를 적외선기기를 이용하여 누수된 부분과 누수량을 손쉽게 확인할 수 있고, 방수 처리 시에는 누수된 위치 및 누수량에 따라 타공 후 파이프를 삽입하여 자연배출하거나 또는 페카와 발포제를 주입하여 추후 발생되는 누수를 미연에 방지할 수 있다. According to the present invention as described above, it is possible to easily check the leaked portion and the leaked water amount by using the infrared device, and to detect the leakage of the leaked portion of the ceiling or the wall by the infrared Or injecting a blowing agent and a plasticizer to prevent the leakage of water from occurring in the future.
Claims (3)
상기 누수확인단계에서는 적외선기기를 이용하여 누수부분과 누수량을 확인하고,
상기 누수처리단계에서는 누수부분에 타공작업 후 삽입하여 물을 배출하는 파이프가 구성되는 것을 특징으로 하는 적외선기기를 이용하여 누수탐지가 가능한 방수 시공방법.
A leak detecting step of detecting leaked water generated in a ceiling or a wall of a building and confirming a leaked portion to be waterproofed; a peeling step of peeling foreign substances in the leaked portion; a grinding step of smoothing the surface of the peeled portion; And a water-repellent coating method comprising a water-repellent treatment step of water-repellent treatment, a drying step of drying after leakage treatment, and a painting step of painting after drying,
In the leakage check step, the leakage portion and the leakage amount are confirmed by using an infrared device,
Wherein the water leakage processing step includes a pipe for discharging water by inserting the water leakage part after the piercing operation.
상기 누수처리단계에서 파이프 삽입 후, 누수량에 따라 페카심기, 약액투입 및 발포제주입을 순차적으로 실행하는 것을 특징으로 하는 적외선기기를 이용하여 누수탐지가 가능한 방수 시공방법.
The method according to claim 1,
Wherein the step of inserting the pipe is followed by the step of injecting the pesticide, the step of injecting the chemical liquid and the step of injecting the foaming agent according to the amount of water leakage.
상기 건조단계 후, 누수확인단계를 진행하여 누수 확인 시, 노출된 페카와 발포제를 제거하는 것을 특징으로 하는 적외선기기를 이용하여 누수탐지가 가능한 방수 시공방법.
The method according to claim 1,
The method according to any one of claims 1 to 3, further comprising the step of detecting a leakage of water after the drying step to remove the exposed peca and the foaming agent.