KR20190020536A - Meterial contaning loess, volcanic cluster, basalt and manufacturing method of the same - Google Patents
Meterial contaning loess, volcanic cluster, basalt and manufacturing method of the same Download PDFInfo
- Publication number
- KR20190020536A KR20190020536A KR1020170105605A KR20170105605A KR20190020536A KR 20190020536 A KR20190020536 A KR 20190020536A KR 1020170105605 A KR1020170105605 A KR 1020170105605A KR 20170105605 A KR20170105605 A KR 20170105605A KR 20190020536 A KR20190020536 A KR 20190020536A
- Authority
- KR
- South Korea
- Prior art keywords
- basalt
- loess
- volcanic
- powder
- solvent
- Prior art date
Abstract
Description
본 발명은 황토, 화산송이, 현무암을 포함하는 물질 및 물질의 제조방법 에 관한 것이다. The present invention relates to a method for producing materials and materials including loess, volcanic clusters, and basalt.
화산송이는 제주 전역에 광범위하게 분포하지만 그동안 특별한 활용 용도가 없어 방치된 실정이다. 제주 화산송이는 흡수량과 마모감량이 높고 품질이 일정하지 않아 건설재료로는 부적합하다는 인식이 지배적이다. 따라서 타일과 벽돌과 같이 치장용으로 제한적으로 사용되고 있다. 화산송이만을 주재료로 사용하는 경우 결합재의 양이 많아지고, 미립분의 부족으로 표면이 거칠고, 색채가 아름답지 못하다. 따라서, 미립분과 안료 역활을 하는 황토를 일정량 이상 혼합하면, 점성이 높아져서 결합재도 소량 소요되고, 황색의 아름다운 천연색을 나타낼 수 있다. 다만 황토를 기초로 생성된 건설자재는 비가 오는 경우 등 자연환경에 의해서 쉽게 손상될 수 있다. The volcanic pine mushroom is widely distributed throughout Jeju, but has been neglected since it has no special application. Jeju volcanic ash is dominant in that it is not suitable as a construction material because it has high absorption and abrasion loss and quality is not constant. Therefore, tiles and bricks are used for stapling. When only volcanic rocks are used as the main material, the amount of binder is increased, and the surface is rough due to lack of fine particles, and the color is not beautiful. Therefore, when a certain amount or more of yellow loess which acts as a fine powder and a pigment is mixed, the viscosity becomes high, and a small amount of binder is required, and a beautiful natural color of yellow can be exhibited. However, construction materials based on loess can be easily damaged by natural environments such as rain.
본 발명이 해결하고자 하는 과제는 황토, 화산송이, 현무암을 포함하는 물질 및 물질의 제조방법을 제공하는 것이다.The object of the present invention is to provide a method for producing materials and materials including loess, volcanic clusters and basalt.
본 발명이 해결하고자 하는 과제들은 이상에서 언급된 과제로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 통상의 기술자에게 명확하게 이해될 수 있을 것이다.The problems to be solved by the present invention are not limited to the above-mentioned problems, and other problems which are not mentioned can be clearly understood by those skilled in the art from the following description.
상술한 과제를 해결하기 위한 본 발명의 일 실시예에 따른 황토, 화산송이, 현무암을 포함하는 물질의 제조방법은, 상기 황토와 상기 화산송이를 분쇄하여 황토 가루와 화산송이 가루를 생성하는 단계; 용매에 상기 황토 가루와 상기 화산송이 가루를 용해시킨 침전용매를 생성하는 단계; 상기 침전용매에 현무암을 투입시키는 단계; 상기 현무암의 소정의 구멍에 상기 황토 가루 및 상기 화산송이 가루 중 적어도 하나가 침전되는 경우 현무암을 상기 침전용매로부터 분리시키는 단계; 침전물이 포함된 현무암을 높은 열에서 굽는 초벌 단계;를 포함하는 황토, 화산송이, 현무암을 포함한다.According to another aspect of the present invention, there is provided a method of manufacturing a material including a loess, a volcanic rock, and a basalt, the method comprising: crushing the loess and the volcanic rock to produce a mixture of loess and volcanic rock; Generating a precipitating solvent in which the yellow clay powder and the volcanic clay powder are dissolved in a solvent; Introducing a basalt rock into the precipitation solvent; Separating the basalt from the precipitation solvent when at least one of the loess powder and the volcanic clay powder is deposited in a predetermined hole of the basalt; Includes loess, volcanic clusters and basalt, including the basal stage of baking the basalt containing the sediment in high heat.
상기 방법으로 제조된 건축용 물질을 포함할 수 있다.And a building material prepared by the above method.
본 발명의 기타 구체적인 사항들은 상세한 설명 및 도면들에 포함되어 있다.Other specific details of the invention are included in the detailed description and drawings.
본 발명에 의하면 원적외선을 다량 방출하는 새집 증후군이 없는 높은 강도를 가진 천연 건설자재를 획득할 수 있는 효과가 있다.According to the present invention, it is possible to obtain a natural construction material having high strength without sick house syndrome that emits a large amount of far-infrared rays.
본 발명은 제조에 특별한 설비가 필요하지 않을 뿐만 아니라 제조공정이 단순하고, 먼지나 유해가스 또는 오염된 물이 발생하지 않으므로 작업환경이 열악하지 않으며, 제조과정에서 분진이나 악취 또는 유해가스나 폐수 등의 발생이 없어 환경을 오염하지 않고, 마감공정이 필요 없어 제조원가의 절감이 가능할 뿐만 아니라 사용시 인체에 유익한 원적외선이 다량으로 방출되어 피로회복과 신진대사의 증진이 가능하여 인체의 건강을 증진시키는데 도움을 줄 수 있고, 폐기시에도 인위적인 분해 없이 자연적인 폐기가 가능하여 환경을 오염시키지 않는 친환경적인 건축용 내장패널을 제공할 수 있는 유용한 효과를 갖는다.The present invention does not require special equipment for manufacturing, and the manufacturing process is simple, dust, noxious gas or contaminated water is not generated, so the working environment is not bad, and dust, odor or harmful gas or waste water It does not pollute the environment, it does not require a finishing process, and it can reduce the manufacturing cost. In addition, it releases a large amount of far-infrared ray which is beneficial to the human body during use, and thus it is possible to promote fatigue recovery and metabolism, And it is possible to provide an environmentally friendly building interior panel that does not pollute the environment because natural disposal is possible without artificial decomposition at the time of disposal.
본 발명의 효과들은 이상에서 언급된 효과로 제한되지 않으며, 언급되지 않은 또 다른 효과들은 아래의 기재로부터 통상의 기술자에게 명확하게 이해될 수 있을 것이다.The effects of the present invention are not limited to the above-mentioned effects, and other effects not mentioned can be clearly understood by those skilled in the art from the following description.
도 1은 본 발명의 일 실시예에 따른 물건 제조방법을 도시한 흐름도이다.
도 2는 본 발명의 다른 실시예에 따른 물건 제조방법을 도시한 흐름도이다.1 is a flowchart illustrating a method of manufacturing a product according to an embodiment of the present invention.
2 is a flowchart illustrating a method of manufacturing a product according to another embodiment of the present invention.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 첨부되는 도면과 함께 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나, 본 발명은 이하에서 개시되는 실시예들에 제한되는 것이 아니라 서로 다른 다양한 형태로 구현될 수 있으며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하고, 본 발명이 속하는 기술 분야의 통상의 기술자에게 본 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. BRIEF DESCRIPTION OF THE DRAWINGS The advantages and features of the present invention, and the manner of achieving them, will be apparent from and elucidated with reference to the embodiments described hereinafter in conjunction with the accompanying drawings. It should be understood, however, that the invention is not limited to the disclosed embodiments, but may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein, Is provided to fully convey the scope of the present invention to a technician, and the present invention is only defined by the scope of the claims.
본 명세서에서 사용된 용어는 실시예들을 설명하기 위한 것이며 본 발명을 제한하고자 하는 것은 아니다. 본 명세서에서, 단수형은 문구에서 특별히 언급하지 않는 한 복수형도 포함한다. 명세서에서 사용되는 "포함한다(comprises)" 및/또는 "포함하는(comprising)"은 언급된 구성요소 외에 하나 이상의 다른 구성요소의 존재 또는 추가를 배제하지 않는다. 명세서 전체에 걸쳐 동일한 도면 부호는 동일한 구성 요소를 지칭하며, "및/또는"은 언급된 구성요소들의 각각 및 하나 이상의 모든 조합을 포함한다. 비록 "제1", "제2" 등이 다양한 구성요소들을 서술하기 위해서 사용되나, 이들 구성요소들은 이들 용어에 의해 제한되지 않음은 물론이다. 이들 용어들은 단지 하나의 구성요소를 다른 구성요소와 구별하기 위하여 사용하는 것이다. 따라서, 이하에서 언급되는 제1 구성요소는 본 발명의 기술적 사상 내에서 제2 구성요소일 수도 있음은 물론이다.The terminology used herein is for the purpose of illustrating embodiments and is not intended to be limiting of the present invention. In the present specification, the singular form includes plural forms unless otherwise specified in the specification. The terms " comprises "and / or" comprising "used in the specification do not exclude the presence or addition of one or more other elements in addition to the stated element. Like reference numerals refer to like elements throughout the specification and "and / or" include each and every combination of one or more of the elements mentioned. Although "first "," second "and the like are used to describe various components, it is needless to say that these components are not limited by these terms. These terms are used only to distinguish one component from another. Therefore, it goes without saying that the first component mentioned below may be the second component within the technical scope of the present invention.
다른 정의가 없다면, 본 명세서에서 사용되는 모든 용어(기술 및 과학적 용어를 포함)는 본 발명이 속하는 기술분야의 통상의 기술자에게 공통적으로 이해될 수 있는 의미로 사용될 수 있을 것이다. 또한, 일반적으로 사용되는 사전에 정의되어 있는 용어들은 명백하게 특별히 정의되어 있지 않는 한 이상적으로 또는 과도하게 해석되지 않는다.Unless defined otherwise, all terms (including technical and scientific terms) used herein may be used in a sense that is commonly understood by one of ordinary skill in the art to which this invention belongs. In addition, commonly used predefined terms are not ideally or excessively interpreted unless explicitly defined otherwise.
공간적으로 상대적인 용어인 "아래(below)", "아래(beneath)", "하부(lower)", "위(above)", "상부(upper)" 등은 도면에 도시되어 있는 바와 같이 하나의 구성요소와 다른 구성요소들과의 상관관계를 용이하게 기술하기 위해 사용될 수 있다. 공간적으로 상대적인 용어는 도면에 도시되어 있는 방향에 더하여 사용시 또는 동작시 구성요소들의 서로 다른 방향을 포함하는 용어로 이해되어야 한다. 예를 들어, 도면에 도시되어 있는 구성요소를 뒤집을 경우, 다른 구성요소의 "아래(below)"또는 "아래(beneath)"로 기술된 구성요소는 다른 구성요소의 "위(above)"에 놓여질 수 있다. 따라서, 예시적인 용어인 "아래"는 아래와 위의 방향을 모두 포함할 수 있다. 구성요소는 다른 방향으로도 배향될 수 있으며, 이에 따라 공간적으로 상대적인 용어들은 배향에 따라 해석될 수 있다.The terms spatially relative, "below", "beneath", "lower", "above", "upper" And can be used to easily describe a correlation between an element and other elements. Spatially relative terms should be understood in terms of the directions shown in the drawings, including the different directions of components at the time of use or operation. For example, when inverting an element shown in the figures, an element described as "below" or "beneath" of another element may be placed "above" another element . Thus, the exemplary term "below" can include both downward and upward directions. The components can also be oriented in different directions, so that spatially relative terms can be interpreted according to orientation.
이하, 첨부된 도면을 참조하여 본 발명의 실시예를 상세하게 설명한다. Hereinafter, embodiments of the present invention will be described in detail with reference to the accompanying drawings.
본 발명은 현무암, 황토, 화산송이를 주재로 하는 건축용 물질 및 그 물질 제조방법에 관한 것으로, 미리 설정된 크기로 절단된 다공성 천연 현무암에 황토와 화산송이의 가루를 소정 비율로 혼합한 물로 황토와 화산송이 가루를 현무암의 소정의 구멍에 침전시키고, 초벌을 하여 친환경 건축용 물질을 생성하는 발명에 관한 것이다. The present invention relates to a building material based on basalt, loess, and volcanic clusters, and a method for manufacturing the same. In a porous natural basalt cut into a preset size, water mixed with a mixture of loess and volcanic clusters at a predetermined ratio, The present invention relates to an invention for producing an environmentally friendly building material by sedimentation of clay powder in a predetermined hole of a basalt rock.
도 1은 본 발명의 일 실시예에 따른 물건 제조방법을 도시한 흐름도이다.1 is a flowchart illustrating a method of manufacturing a product according to an embodiment of the present invention.
도 1을 참조하면, 본 발명의 일 실시예로, 황토 및 화산송이 중 적어도 하나를 분쇄할 수 있다(S110). 황토 및 화산송이를 분쇄하면 황토 가루와 화산송이 가루가 생성될 수 있다. Referring to FIG. 1, in one embodiment of the present invention, at least one of loess and volcanic clusters may be crushed (S110). Crushing loess and volcanic clusters can produce yellow clay and volcanic clay.
생성된 황토 가루 및 화산송이 가루를 미리 정해진 비율로 용매에 녹여 침전용매를 생성할 수 있다(S120). 여기서 미리 정해진 비율은 황토 가루 1퍼센트에서 99퍼센트, 화산송이 가루 1퍼센트에서 99퍼센트에서 강도에 따라 자유롭게 조절 가능할 수 있다. The generated yellow loess powder and the volcanic clay powder may be dissolved in the solvent at a predetermined ratio to produce a precipitation solvent (S120). The predetermined ratio here is freely adjustable according to the strength at 1 to 99 percent of the loess powder and 1 to 99 percent of the volcanic crust powder.
침전 용매는 물과 같은 용매로 제한되지 않으며 기타 불순물이 많이 포함되지 않고 황토 가루와 화산송이 가루를 용해시킬 수 있는 다양한 용매일 수 있다. 침전용매에 현무암을 투입할 수 있다(S130). 현무암에는 소정의 구멍이 다량 포함되어 있을 수 있다. 이러한 소정의 구멍에 침전용매의 황토 가루 및 화산송이 가루가 침전될 수 있다. 침전이 완료되면 현무암을 분리시킬 수 있다(S140). 침전이 완료된 현무암에서 현무암의 비율은 70퍼센트에서 99.99퍼센트 일 수 있다. 침전이 완료된 현무암에서 황토 가루, 화산송이 가루의 비율은 0.01퍼센트에서 30퍼센트 일 수 있다. 침전물이 포함된 현무암을 고온에서 초벌할 수 있다(S150). 초벌 온도는 600도(C)에서 1000도(C)일 수 있다. The precipitation solvent is not limited to a solvent such as water, and may contain various impurities, and may be a variety of solvents that can dissolve the yellow clay and volcanic ash. Basalt can be added to the precipitation solvent (S130). The basalt may contain a large amount of pores. In this predetermined hole, yellow soil powder and volcanic clay powder of the precipitation solvent can be precipitated. When the precipitation is completed, the basalt can be separated (S140). The ratio of basalt to basalt in sedimentary basins can range from 70 percent to 99.99 percent. In the basalts where sedimentation has been completed, the ratio of loess and volcanic clay can be 0.01 to 30 percent. Basalt containing the sediment can be subjected to high temperature (S150). The initial temperature may be from 600 degrees C to 1000 degrees Celsius.
도 2는 본 발명의 일 실시예에 따른 물건 제조방법을 도시한 흐름도이다.2 is a flowchart illustrating a method of manufacturing a product according to an embodiment of the present invention.
도 2를 참조하면, 본 발명의 일 실시예로, 황토 및 화산송이 중 적어도 하나를 분쇄할 수 있다(S210). 황토 및 화산송이를 분쇄하면 황토 가루와 화산송이 가루가 생성될 수 있다. Referring to FIG. 2, in one embodiment of the present invention, at least one of loess and volcanic clusters may be crushed (S210). Crushing loess and volcanic clusters can produce yellow clay and volcanic clay.
생성된 황토 가루 및 화산송이 가루를 미리 정해진 비율로 섞어 현무암에 분사할 수 있다(S220). 여기서 미리 정해진 비율은 황토 가루 1퍼센트에서 99퍼센트, 화산송이 가루 1퍼센트에서 99퍼센트에서 강도에 따라 자유롭게 조절 가능할 수 있다. The generated yellow clay and volcanic clay can be blended at predetermined ratios and sprayed on the basalt (S220). The predetermined ratio here is freely adjustable according to the strength at 1 to 99 percent of the loess powder and 1 to 99 percent of the volcanic crust powder.
황토 가루 및 화산송이 가루가 분사된 현무암 구멍에 공기압을 투입할 수 있다(S230). 공기압의 강도는 스로틀을 통해 조절될 수 있다. 공기압이 현무암 구멍에 투입되면 현무암의 갈라진 틈새 사이로 황토 가루 및 화산송이 가루가 잘 스며들 수 있다.The air pressure can be applied to the basalt pores in which the loess powder and the volcanic dust are sprayed (S230). The intensity of the air pressure can be adjusted through the throttle. When air pressure is injected into the basalt pits, it can penetrate well into the cracks of the basalt.
공기압 투입이 완료된 경우 현무암을 진동시킬 수 있다(S240). 현무암이 진동되는 경우 현무암의 갈라진 틈새 사이로 황토 가루 및 화산송이 가루가 더욱 잘 스며들 수 있다. S220-S240과정은 반복하여 수행될 수 있다.When the air pressure input is completed, the basalt can be vibrated (S240). When basalt rocks, loess and volcanic dust can penetrate better through cracks in the basalt. Steps S220-S240 can be repeatedly performed.
황토 가루 및 화산송이 가루가 현무암에 미리 정해진 기준 이상 스며든 경우 현무암을 고온에서 초벌할 수 있다(S250). 초벌 온도는 600도(C)에서 1000도(C)일 수 있다.If the loess and the volcanic crust are soaked above basal standards, the basalt can be primed at high temperatures (S250). The initial temperature may be from 600 degrees C to 1000 degrees Celsius.
이상, 첨부된 도면을 참조로 하여 본 발명의 실시예를 설명하였지만, 본 발명이 속하는 기술분야의 통상의 기술자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로, 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며, 제한적이 아닌 것으로 이해해야만 한다. While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, You will understand. Therefore, it should be understood that the above-described embodiments are illustrative in all aspects and not restrictive.
Claims (2)
상기 황토와 상기 화산송이를 분쇄하여 황토 가루와 화산송이 가루를 생성하는 단계;
용매에 상기 황토 가루와 상기 화산송이 가루를 용해시킨 침전용매를 생성하는 단계;
상기 침전용매에 현무암을 투입시키는 단계;
상기 현무암의 소정의 구멍에 상기 황토 가루 및 상기 화산송이 가루 중 적어도 하나가 침전되는 경우 현무암을 상기 침전용매로부터 분리시키는 단계;
침전물이 포함된 현무암을 높은 열에서 굽는 초벌 단계;를 포함하는 황토, 화산송이, 현무암을 포함하는 물질의 제조방법.As a method for producing a material including loess, volcanic clay, and basalt,
Crushing the loess and the volcanic clusters to produce yellow loess and volcanic crust;
Generating a precipitating solvent in which the yellow clay powder and the volcanic clay powder are dissolved in a solvent;
Introducing a basalt rock into the precipitation solvent;
Separating the basalt from the precipitation solvent when at least one of the loess powder and the volcanic clay powder is deposited in a predetermined hole of the basalt;
A method for producing a material comprising loess, volcanic clay, and basalt comprising a basal stage of baking basalt containing precipitate in high heat.