KR20180092538A - Tape for removal of optically clear adhesive on panel, method for preparing the same and method for separation and removal method of optically clear adhesive on panel using the tape - Google Patents
Tape for removal of optically clear adhesive on panel, method for preparing the same and method for separation and removal method of optically clear adhesive on panel using the tape Download PDFInfo
- Publication number
- KR20180092538A KR20180092538A KR1020170018353A KR20170018353A KR20180092538A KR 20180092538 A KR20180092538 A KR 20180092538A KR 1020170018353 A KR1020170018353 A KR 1020170018353A KR 20170018353 A KR20170018353 A KR 20170018353A KR 20180092538 A KR20180092538 A KR 20180092538A
- Authority
- KR
- South Korea
- Prior art keywords
- tape
- layer
- pressure
- sensitive adhesive
- transparent adhesive
- Prior art date
Abstract
Description
본 발명은 광학용투명접착제 제거용 테이프, 그의 제조방법 및 그를 이용한 광학용투명접착제의 제거방법에 관한 것이다.The present invention relates to a tape for removing an optical transparent adhesive, a method for producing the tape, and a method for removing an optical transparent adhesive using the tape.
터치스크린은 키보드나 마우스와 같은 입력장치를 사용하지 않고 화면의 특정 위치에 손가락이나 펜이 닿으면 그 위치를 인식하는 입력장치의 일종이다. 터치스크린 패널의 종류는 제조사 별로 다양하게 존재하고 있으나, 대표적으로 저항막 방식과 정전용량형 방식이 채용되고 있다. 터치스크린 패널은 기본적으로 프론트 윈도우(Front Window), 투명전극패턴(ITO), 및 터치했을 때의 위치값에 대한 저항값 또는 정전용량값의 변화를 제어장치로 처리해주는 회로(FPCB; Flexible Printed Circuit Board) 기판을 포함하는 구조를 갖는다. 상기 부품들은 광학용투명접착제(OCA; Optically Clear Adhesive) 또는 광학용투명접착레진(Optically Clear Resin, OCR)를 이용하여 합착됨으로써 터치스크린 패널을 형성한다.A touch screen is a type of input device that recognizes the position of a finger or a pen when a touch is made at a specific position on the screen without using an input device such as a keyboard or a mouse. Various types of touch screen panels exist depending on manufacturers, but resistive film type and capacitive type are typically used. The touch screen panel basically includes a front window, a transparent electrode pattern (ITO), and a circuit (FPCB: Flexible Printed Circuit (FPCB)) for processing a change in resistance value or capacitance value with respect to a position value when touched, Board) substrate. The parts are joined together using Optically Clear Adhesive (OCA) or Optically Clear Resin (OCR) to form a touch screen panel.
도 1은 이러한 터치스크린 패널의 부품의 합착 과정 및 불량발생의 예를 개략적으로 도시한 그림이다. 도 1을 참조하면, 터치스크린 패널은 제어칩(5)이 연결된 회로기판(3)이 일면에 부착된 투명전극패턴(2)과 프론트 윈도우(1) 사이에 광학용투명접착제(4)를 게재시켜 고진공프렛 합착이나 롤링합착을 하여 제조된다.FIG. 1 is a view schematically showing an example of the adhesion process of the components of the touch screen panel and the occurrence of defects. 1, a touch screen panel includes an optical transparent adhesive 4 between a transparent electrode pattern 2 attached on one surface of a circuit board 3 to which a
그러나, 합착 과정에서 기포가 생기거나 이물질이 포함되거나 합착 위치가 불량해지는 등 다양한 합착 불량이 발생하게 된다. 이러한 합착 불량을 줄이기 위해 제조사들은 고가의 장치로 진공 합착 및 롤러 합착을 하고 있으나, 제품에 따라 대략 20% 이상의 합착 불량이 발생하는 것으로 알려져 있다. 따라서, 터치스크린 패널 제조사들은 고가의 프론트 윈도우(예, 강화유리), ITO, FPCB 부품을 재생하는 것에 관심을 쏟고 있다.However, various lap joint failures occur such that bubbles are formed, foreign substances are contained, or cohesion positions become poor during the cementation process. In order to reduce the adhesion defect, the manufacturers have performed vacuum bonding and roller bonding with expensive devices, but it is known that the adhesion failure of about 20% or more occurs depending on the products. Accordingly, touch screen panel manufacturers are interested in playing expensive front windows (eg, tempered glass), ITO, and FPCB components.
그러나, 프론트 윈도우와 ITO 패턴필름을 합착하기 위한 광학용투명접착제는 접착성이 매우 강하여 합착 후에는 분리가 매우 어렵고, 분리한다고 하더라도 윈도우 면이나 ITO 필름면에 남아 있는 광학용투명접착제를 제거하는 것이 매우 어렵다.However, since the optical transparent adhesive for bonding the front window and the ITO pattern film is very strong, it is very difficult to separate after adhesion, and it is necessary to remove the optical transparent adhesive remaining on the window surface or the ITO film surface It is very difficult.
예컨대, 불량 터치스크린 패널이 생기면, 물리적인 방법을 이용하여 투명전극패턴으로부터 프론트 윈도우(1)를 분리하고, 이후 분리된 프론트 윈도우(1)에 남아 있는 광학용투명접착제(4)를 화학적 처리 과정을 거쳐 제거하게 되는데, 화학적 처리 과정에서 프론트 윈도우(1)의 손상 및 표면에 코팅되어 있는 실크막 및 로고부위, 렌즈코팅막의 손상문제가 발생하는 문제점이 있다.For example, when a bad touch screen panel is formed, the front window 1 is separated from the transparent electrode pattern using a physical method, and then the transparent adhesive 4 for optical use remaining in the separated front window 1 is subjected to a chemical treatment process There is a problem that damage to the front window 1 and damage to the silk film, the logo part, and the lens coating film coated on the surface occur in the chemical treatment process.
대한민국 공개특허 제10-2011-0088772호는 터치스크린 패널의 일면을 가열하는 가열부; 상기 터치스크린 패널의 타면을 냉각하는 냉각부; 및 상기 가열부과 상기 냉각부의 온도를 제어하여 상기 접착층의 일면의 접착력이 와해되도록 하는 제어부를 포함하는 광학용투명접착제의 분리제거 장치 및 제거방법을 개시하고 있다. 그러나, 상기 방법은 복잡한 장치가 필요하며, 광학용투명접착제의 제거효과도 충분하지 않은 단점을 갖는다.Korean Patent Laid-Open Publication No. 10-2011-0088772 discloses a touch screen panel including a heating unit for heating one surface of a touch screen panel; A cooling unit for cooling the other surface of the touch screen panel; And a control unit for controlling the temperature of the heating unit and the cooling unit so that the adhesive force of one surface of the adhesive layer is broken. However, this method has a disadvantage in that a complex apparatus is required and the effect of removing the transparent adhesive for optical is not sufficient.
대한민국 등록특허 제10-1560286호는 감압성 접착제층을 포함하는 테이프를 이용하여 패널 상의 광학용투명접착제를 제거하는 방법을 개시하고 있으나 실제 공정에서 사용하는 경우 광학용투명접착제가 한번에 용이하게 제거되지 못하는 문제점이 있고, 특히 OCA필름을 합지하고 상당한 시간이 지났거나, 광학용투명접착레진(Optically Clear Resin, OCR)의 경우에는 상기 특허의 기술로 수차례 합지와 박리를 반복해야만 접착제 층이 완전히 박리된다는 문제점이 있다.Korean Patent No. 10-1560286 discloses a method of removing a transparent adhesive for optical use on a panel using a tape including a pressure-sensitive adhesive layer, but when used in an actual process, a transparent adhesive for optical use is not easily removed at once In particular, in the case of Optically Clear Resin (OCR), it is necessary to repeat the lapping and peeling a plurality of times with the technique of the above patent to completely separate the adhesive layer .
본 발명은 종래기술의 상기와 같은 문제를 해소하기 위하여 안출된 것으로서, 터치스크린 패널의 재생과정에서 프론트 윈도우 또는 터치스크린 패널로부터 효율적으로 광학용투명접착제 또는 광학용투명접착레진을 제거하는 방법을 제공하는 것을 목적으로 한다.Disclosure of the Invention The present invention is conceived to solve the above-described problems of the prior art, and provides a method for efficiently removing a transparent adhesive for optical or transparent adhesive resin for optical use from a front window or a touch screen panel in a process of reproducing a touch screen panel .
또한, 광학용투명접착제 또는 광학용투명접착레진의 제거 효과가 우수한 광학용투명접착제 제거용 테이프를 제공하는 것을 목적으로 한다.Another object of the present invention is to provide a tape for removing transparent adhesive for optical, which is excellent in the effect of removing optical transparent adhesive or optical transparent adhesive resin.
상기 목적 달성을 위하여 본 발명은 제1 이형필름층, 5㎛ ~ 50 ㎛ 두께의 엘라스토머층, 자외선 경화형 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층, 및 제2 이형필름층이 순차적으로 적층된 것을 특징으로 하는 광학용투명접착제 제거용 테이프를 제공한다.To achieve the above object, the present invention provides a pressure-sensitive adhesive composition comprising a first release film layer, an elastomer layer having a thickness of 5 to 50 탆, a pressure-sensitive adhesive layer containing an ultraviolet-curable photosensitive resin in an amount of 1 to 25% 2 release film layers are laminated in this order on a transparent substrate.
본 발명은,According to the present invention,
(a) 제1 이형필름 위에 엘라스토머를 도포하여 5㎛ ~ 50 ㎛ 두께의 엘라스토머층을 형성하는 단계;(a) applying an elastomer on the first release film to form an elastomer layer having a thickness of 5 탆 to 50 탆;
(b) 제2 이형필름 위에 자외선 경화형 감광성수지를 포함하는 점착제 조성물을 도포하여 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층을 형성하는 단계; 및(b) applying a pressure-sensitive adhesive composition containing a UV-curable photosensitive resin on the second release film to form a pressure-sensitive adhesive layer containing 1 to 25% by weight of the photosensitive resin based on the total weight of the pressure-sensitive adhesive layer; And
(c) 상기 엘라스토머층과 감압성 점착제층을 합지시키는 단계;를 포함하는 것을 특징으로 하는 광학용투명접착제 제거용 테이프의 제조방법을 제공한다.(c) bonding the elastomer layer and the pressure-sensitive adhesive layer to each other.
본 발명은 또한,The present invention also relates to
광학용투명접착제가 합지된 패널을 준비하는 단계,Preparing a panel in which a transparent adhesive for optics is laminated,
제1 이형필름층, 5㎛ ~ 50 ㎛ 두께의 엘라스토머층, 자외선 경화형 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층, 및 제2 이형필름층이 순차적으로 적층된 광학용투명접착제 제거용 테이프를 준비하는 단계,Sensitive adhesive layer comprising a first release film layer, an elastomer layer having a thickness of 5 占 퐉 to 50 占 퐉, a pressure-sensitive adhesive layer containing an ultraviolet-curable photosensitive resin in an amount of 1 to 25% by weight based on the total weight of the pressure-sensitive adhesive layer, and a second release film layer Preparing a transparent adhesive removing tape for optical use,
상기 광학용투명접착제 제거용 테이프의 제2이형필름층을 제거하는 단계,Removing the second release film layer of the optical transparent adhesive removing tape,
상기 광학용투명접착제 제거용 테이프의 점착제층을 상기 패널의 광학용투명접착제의 표면에 합지하는 단계,Bonding a pressure-sensitive adhesive layer of the optical transparent adhesive removing tape to the surface of the optical transparent adhesive of the panel,
상기 광학용투명접착제 제거용 테이프가 합지된 패널을 자외선 경화기에 투입하여 자외선을 테이프방향에서 조사하는 단계, 및Irradiating ultraviolet rays in the direction of the tape by putting the panel in which the optical transparent adhesive removing tape is laminated in an ultraviolet curing device,
상기 광학용투명접착제 제거용 테이프의 제1이형필름층을 제거한 후에 테이프를 연신시켜 광학용투명접착제와 함께 제거하는 단계를 포함하는 패널의 광학용투명접착제 제거 방법을 제공한다.And removing the first release film layer of the optical transparent adhesive removing tape, and then stretching the tape to remove it together with the transparent adhesive for optical use.
본 발명의 광학용투명접착제 제거용 테이프의 점착제층은 열경화형 점착제 수지조성물에 자외선경화형 감광성수지조성물을 혼합하여 제조하였기 때문에 상기 테이프를 OCA 또는 OCR이 잔류하는 프로트 윈도우 또는 터치스크린 패널에 합지한 이후에 자외선 경화기를 통과시키면 이 과정에서 점착제층에 포함되어 있는 감광성수지와 OCA 또는 OCR 내의 미반응 감광성수지와의 화학적 결합이 이루어져 점착제층과 OCA 층이 일체화되므로 OCA 또는 OCR이 매우 용이하게 제거되는 효과가 있다.Since the pressure-sensitive adhesive layer of the tape for removing an optical transparent adhesive of the present invention is prepared by mixing an ultraviolet curable photosensitive resin composition with a thermosetting pressure-sensitive adhesive resin composition, the tape is laminated on a protrusion window or a touch screen panel in which OCA or OCR remains, , The chemical bond between the photosensitive resin contained in the pressure-sensitive adhesive layer and the unreacted photosensitive resin in the OCA or OCR is made so that the pressure-sensitive adhesive layer and the OCA layer are united with each other, so that OCA or OCR can be easily removed .
또한, 본 발명의 광학용투명접착제 제거용 테이프는 50㎛ 이하의 두께로 형성된 엘라스토머층을 포함하기 때문에 광학용투명접착제 제거에 매우 우수한 효과를 제공한다. In addition, since the tape for removing an optical transparent adhesive of the present invention includes an elastomer layer formed to a thickness of 50 탆 or less, it provides an excellent effect for removing a transparent adhesive for optical use.
또한, 본 발명의 광학용투명접착제 제거용 테이프의 제조방법에 의하면, 엘라스토머층을 이형필름 위에 코팅하여 감압성 점착제층과 합지시키므로, 공정수가 감소되며 엘라스토머층을 50㎛ 이하로 형성할 수 있어서 경제적 이점도 얻을 수 있다. Further, according to the method for producing a tape for removing an optical transparent adhesive of the present invention, since the elastomer layer is coated on the release film and bonded to the pressure-sensitive adhesive layer, the number of processes can be reduced and the elastomer layer can be formed to 50 탆 or less, You can also get benefits.
도 1은 터치스크린 패널의 부품의 합착 과정 및 불량발생의 예를 개략적으로 도시한 도면이며,
도 2는 본 발명의 광학용투명접착제 제거용 테이프의 일예를 도시한 단면도이며,
도 3 은 광학용투명접착제가 붙어 있는 재생용 프론트 윈도우 및 터치스크린 패널의 사진이며,
도 4는 본 발명의 광학용투명접착제 제거용 테이프의 감광성 수지와 터치스크린 패널의 OCA 내의 감광성 반응기의 반응을 도식화하여 나타낸 도면이며,
도 5는 본 발명의 광학용투명접착제 제거방법을 도식화한 도면이다.FIG. 1 is a view schematically showing an example of a process of attaching a component of a touch screen panel and generating a defect,
2 is a cross-sectional view showing an example of a tape for removing a transparent adhesive for optical use of the present invention,
3 is a photograph of a reproduction front window and a touch screen panel to which an optical transparent adhesive is attached,
4 is a diagram illustrating the reaction between a photosensitive resin of a tape for removing an optical transparent adhesive of the present invention and a photosensitive reactor in OCA of a touch screen panel,
Fig. 5 is a diagram illustrating a method for removing a transparent adhesive for optical use according to the present invention.
이하, 첨부된 도면을 참고하여 본 발명의 바람직한 실시예에 대하여 상세히 설명한다. 본 발명을 설명하기에 앞서 관련된 공지기능 및 구성에 대한 구체적 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우 그에 대한 설명은 생략하기로 한다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings. In the following description, well-known functions or constructions are not described in detail since they would unnecessarily obscure the gist of the present invention.
아래 설명과 도면은 당업자가 설명되는 장치와 방법을 용이하게 실시할 수 있도록 특정 실시예를 예시한다. 다른 실시예는 구조적, 논리적으로 다른 변형을 포함할 수 있다. 개별 구성 요소와 기능은 명확히 요구되지 않는 한, 일반적으로 선택될 수 있으며, 과정의 순서는 변할 수 있다. 몇몇 실시예의 부분과 특징은 다른 실시예에 포함되거나 다른 실시예로 대체될 수 있다.The following description and drawings illustrate specific embodiments in order that those skilled in the art can readily implement the described apparatus and method. Other embodiments may include other variations, both structurally and logically. Unless explicitly required, individual components and functions may be selected generally, and the order of the processes may vary. Portions and features of some embodiments may be included in other embodiments or may be replaced by other embodiments.
이하의 설명에서 광학용투명접착제(OCA)를 예로 설명하나 이는 광학용투명접착레진(OCR)에도 동일하게 적용할 수 있다.In the following description, a transparent adhesive for optical (OCA) is described as an example, but the same can be applied to an optical transparent adhesive resin (OCR).
본 발명은 제1 이형필름층, 5㎛ ~ 50 ㎛ 두께의 엘라스토머층, 자외선 경화형 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층, 및 제2 이형필름층이 순차적으로 적층된 것을 특징으로 하는 광학용투명접착제 제거용 테이프를 제공한다.A pressure-sensitive adhesive layer comprising a first release film layer, an elastomer layer having a thickness of 5 탆 to 50 탆, an ultraviolet curable photosensitive resin in an amount of 1 to 25% by weight based on the total weight of the pressure-sensitive adhesive layer, Wherein the transparent adhesive tape for optical tape is laminated in order.
본 발명의 광학용투명접착제 제거용 테이프의 점착제층은 열경화형 점착제 수지조성물에 자외선경화형 감광성수지조성물을 혼합하여 제조된다. 한편, OCA는 다양한 형태의 자외선경화형 감광성수지로 이루어져 있는데 OCA의 제조공정 중에 약 3~5%의 감광성 수지는 반응을 하지 않고 OCA 점착층 내부에 잔류하고 있다.The pressure-sensitive adhesive layer of the tape for removing an optical transparent adhesive of the present invention is prepared by mixing an ultraviolet curable photosensitive resin composition with a thermosetting pressure-sensitive adhesive resin composition. On the other hand, OCA is composed of various types of ultraviolet curable photosensitive resin. During the manufacturing process of OCA, about 3 to 5% of the photosensitive resin remains in the OCA adhesive layer without reacting.
따라서 본 발명의 자외선 경화형 감광성수지를 포함하고 있는 OCA 제거용 테이프의 점착제층을 패널상의 OCA에 합지한 이후에 자외선 경화기를 통과시키면 상기 감광성수지의 이중결합 등과 OCA 내의 미반응 감광성수지와의 화학적 결합이 이루어져 점착제층과 OCA 층이 일체화되는 반응이 일어난다. 그 결과 패널의 OCA 가 본 발명의 광학용투명접착제 제거용 테이프와 함께 제거되는 것이다.Therefore, when the pressure-sensitive adhesive layer of the OCA removing tape containing the UV-curable photosensitive resin of the present invention is laminated on the OCA on the panel and then passed through an ultraviolet curing machine, the double bond of the photosensitive resin and the chemical bond A reaction occurs in which the pressure sensitive adhesive layer and the OCA layer are integrated. As a result, OCA of the panel is removed together with the optical transparent adhesive removing tape of the present invention.
상기 자외선 경화형 감광성 수지는 감압성 점착제층 총 중량 대비 1~25중량% 포함되는데, 자외선 경화혈 감광성 수지가 감압성 점착제층에 상기 함량으로 포함되는 경우, OCA내의 미반응 감광성 수지와의 반응에 적절하며, 또한 테이프의 신율이 적정한 범위가 되어, 결과적으로 OCA제거 특성이 우수하다.The ultraviolet curable photosensitive resin is contained in an amount of 1 to 25% by weight based on the total weight of the pressure sensitive adhesive layer. When the ultraviolet curing photosensitive resin is contained in the pressure sensitive adhesive layer in the above content, And the elongation of the tape is in an appropriate range, resulting in excellent OCA removal characteristics.
본 발명의 광학용투명접착제 제거용 테이프의 점착제층은 열경화형 아크릴계, 실리콘계 또는 고무계 점착제에 일정량의 자외선경화형 감광성 수지를 첨가하여 제조하는 것을 특징으로 한다.The pressure-sensitive adhesive layer of the tape for removing an optical transparent adhesive of the present invention is produced by adding a certain amount of a UV-curable photosensitive resin to a thermosetting acrylic, silicone or rubber adhesive.
본 발명의 점착제 층에 도입할 수 있는 자외선 경화형 감광성 수지는 다양한 구조와 분자량을 가지는 1관능기, 2관능기, 및 다관능기를 갖는 모노머 또는 올리고머 형태일 수 있고, 바람직하게는 다양한 관능기를 가지는 아크릴레이트계, 메타 아크릴레이트계, 에폭시아크릴레이트계, 폴리에스터아크릴레이트계, 우레탄아크릴레이트계 등일 수 있으나 이것으로 한정하는 것은 아니다.The ultraviolet curable photosensitive resin that can be introduced into the pressure-sensitive adhesive layer of the present invention may be in the form of a monomer or oligomer having a monofunctional group, a bifunctional group, and a polyfunctional group having various structures and molecular weights, , Methacrylate-based, epoxyacrylate-based, polyester acrylate-based, urethane acrylate-based, and the like, but the present invention is not limited thereto.
본 발명은 또한The present invention also
(a) 제1 이형필름 위에 엘라스토머를 도포하여 5㎛ ~ 50 ㎛ 두께로 엘라스토머층을 형성하는 단계;(a) applying an elastomer on the first release film to form an elastomer layer having a thickness of 5 탆 to 50 탆;
(b) 제2 이형필름 위에 자외선 경화형 감광성수지를 포함하는 점착제 조성물을 도포하여 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층을 형성하는 단계; 및(b) applying a pressure-sensitive adhesive composition containing a UV-curable photosensitive resin on the second release film to form a pressure-sensitive adhesive layer containing 1 to 25% by weight of the photosensitive resin based on the total weight of the pressure-sensitive adhesive layer; And
(c) 상기 엘라스토머층과 감압성 점착제층을 합지시키는 단계;를 포함하는 것을 특징으로 하는 광학용투명접착제 제거용 테이프의 제조방법에 관한 것이다.(c) a step of laminating the elastomer layer and the pressure-sensitive adhesive layer to each other.
종래의 광학용투명접착제 제거용 테이프는 압출방식 등에 의해 기 제조된 엘라스토머 필름 위에 감압성 점착제를 도포하는 방식으로 제조되고 있다. 그러나, 상기와 같은 엘라스토머 필름은 현실적으로 50 ㎛ 미만의 두께를 가지는 것이 어렵다는 한계를 갖는다. The conventional tape for removing a transparent adhesive for optical is produced by applying a pressure-sensitive adhesive on an elastomer film produced by an extrusion method or the like. However, such an elastomer film has a limitation that it is practically difficult to have a thickness of less than 50 탆.
또한 본 발명의 발명자들은 광학용투명접착제 제거용 테이프에 포함되는 엘라스토머층의 두께가 50 ㎛를 초과하는 경우에는 상기 테이프의 연신률이 부족해지기 때문에 충분한 광학용투명접착제 제거 능력을 제공할 수 없음을 확인하였다. 즉 엘라스토머층의 연신성이 우수해야 점착층이 잘 떨어져 나오면서 광학용투명접착제를 용이하게 떼어 낼 수 있는데, 50 ㎛를 초과하는 경우에는 이러한 효과가 충분하지 못한 단점을 갖는다. Further, the inventors of the present invention have found that when the thickness of the elastomer layer included in the optical transparent adhesive removing tape exceeds 50 탆, the elongation rate of the tape becomes insufficient, Respectively. That is, the stretchability of the elastomer layer should be excellent so that the adhesive layer can be easily separated from the adhesive layer, and the transparent adhesive for optical use can be easily peeled off.
또한, 50 ㎛를 초과하는 경우 엘라스토머의 사용량이 증가하므로 경제적으로도 바람직하지 않다. On the other hand, if it exceeds 50 탆, the amount of the elastomer used increases, which is economically undesirable.
본 발명의 엘라스토머 필름은 연신율 및 경제적인 면에서 더욱 바람직하게는 5㎛ ~ 30 ㎛ 미만의 두께를 갖는다.The elastomer film of the present invention preferably has a thickness of from 5 탆 to less than 30 탆 in terms of elongation and economy.
본 발명의 제조방법에서 엘라스토머층은 이형필름 위에 엘라스토머를 콤마 코팅(COMMA Coating) 또는 슬롯 다이 코팅(Slot-Die Coating) 등의 공법을 이용하여 도포하는 방식으로 형성될 수 있다. 상기 방법에 따라, 종래기술과 달리, 엘라스토머층을 5㎛ ~ 50 ㎛ 의 두께로 형성하는 것이 가능해진다.In the manufacturing method of the present invention, the elastomer layer may be formed by applying an elastomer on a release film by using a method such as COMMA coating or slot die coating. According to the above-described method, unlike the prior art, it becomes possible to form the elastomer layer with a thickness of 5 占 퐉 to 50 占 퐉.
또한, 이러한 엘라스토머층의 형성방법에 따라 종래의 기술에서 기 제조된 엘라스토머 필름에 이형필름을 접착시킬 때 요구되는 접착공정을 생략하는 것도 가능하게 된다.Further, according to the method of forming such an elastomer layer, it is also possible to omit the adhesion step required when the releasing film is adhered to the elastomer film prepared in the prior art.
본 발명의 광학용투명접착제 제거용 테이프의 제조방법에 있어서, 상기 (c) 엘라스토머층과 감압성 점착제층을 합지시키는 단계는 엘라스토머층 및 감압성 점착제층 중 어느 한 층 이상이 자체적으로 갖는 접착력을 이용하여 수행될 수 있다. In the method for producing a tape for removing an optical transparent adhesive of the present invention, in the step (c) of laminating the elastomer layer and the pressure-sensitive adhesive layer, the adhesive force of at least one of the elastomer layer and the pressure- . ≪ / RTI >
즉, 상기 (a) 단계 및 (b) 단계에서 형성되는 엘라스토머층 또는 감압성 점착제층 중의 어느 한 층이 접착력을 갖는 상태에서 이들을 결합함으로써 별도의 접착제 없이 접착이 가능해진다.That is, any one of the layers of the elastomer layer or the pressure-sensitive adhesive layer formed in the step (a) and the step (b) can be bonded without a separate adhesive by bonding them in a state of having an adhesive force.
도 2는 본 발명의 광학용투명접착제 제거용 테이프의 일예를 도시하고 있다. 즉, 제1 이형필름층(10), 5㎛ ~ 50 ㎛의 두께의 엘라스토머층(20), 자외선 경화형 감광성수지를 포함하는 감압성 점착제층(30), 및 제2 이형필름층(40)이 이 순서로 적층된 것을 특징으로 하는 광학용투명접착제 제거용 테이프(100)을 도시하고 있다.Fig. 2 shows an example of a tape for removing a transparent adhesive for optical of the present invention. That is, the first
본 발명에서 상기 광학용투명접착제 제거용 테이프를 사용한 OCA 제거 방법은 다음과 같다.In the present invention, the OCA removal method using the optical transparent adhesive removal tape is as follows.
즉, 광학용투명접착제가 합지된 패널을 준비하는 단계,That is, a step of preparing a panel in which a transparent adhesive for optics is laminated,
제1 이형필름층, 5㎛ ~ 50 ㎛ 두께의 엘라스토머층, 자외선 경화형 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층, 및 제2 이형필름층이 순차적으로 적층된 광학용투명접착제 제거용 테이프를 준비하는 단계,Sensitive adhesive layer comprising a first release film layer, an elastomer layer having a thickness of 5 占 퐉 to 50 占 퐉, a pressure-sensitive adhesive layer containing an ultraviolet-curable photosensitive resin in an amount of 1 to 25% by weight based on the total weight of the pressure-sensitive adhesive layer, and a second release film layer Preparing a transparent adhesive removing tape for optical use,
상기 광학용투명접착제 제거용 테이프의 제2이형필름층을 제거하는 단계,Removing the second release film layer of the optical transparent adhesive removing tape,
상기 광학용투명접착제 제거용 테이프의 점착제층을 상기 패널의 광학용투명접착제의 표면에 합지하는 단계,Bonding a pressure-sensitive adhesive layer of the optical transparent adhesive removing tape to the surface of the optical transparent adhesive of the panel,
상기 광학용투명접착제 제거용 테이프가 합지된 패널을 자외선 경화기에 투입하여 자외선을 테이프 방향에서 조사하는 단계, 및Irradiating ultraviolet rays in the direction of the tape by putting the panel in which the optical transparent adhesive removing tape is laminated in an ultraviolet curing device,
상기 광학용투명접착제 제거용 테이프의 제1이형필름층을 제거한 후에 테이프를 연신시켜 광학용투명접착제와 함께 제거하는 단계를 포함한다.Removing the first release film layer of the optical transparent adhesive removing tape, and then stretching the tape to remove it together with the optical transparent adhesive.
상기 자외선 램프는 예컨대, 고압수은램프와 메탈할라이드 램프 중에 선택하여 사용할 수 있으며 에너지는 800 ~ 1,200mJ/㎠ 일 수 있다.The ultraviolet lamp may be selected from, for example, a high-pressure mercury lamp and a metal halide lamp, and the energy may be 800 to 1,200 mJ / cm 2.
도 4에 본 발명의 광학용투명접착제 제거용 테이프의 감광성 수지와 터치스크린 패널의 OCA 내의 감광성 반응기의 반응을 도식화하였다.FIG. 4 illustrates the reaction between the photosensitive resin of the tape for removing optical transparent adhesive of the present invention and the photosensitive reactor in OCA of the touch screen panel.
도 5에 본 발명의 광학용투명접착제 제거방법을 도시하였다. 먼저, 제2 이형필름층이 박리된 감압성 점착제층(30)을 제거대상물인 프론트 윈도우 또는 터치스크린 패널 상의 광학용투명접착제에 접착시킨 후, 자외선을 조사하여 감압성 점착제층와 광학용투명접착제 사이에 결합이 일어나게 한다. 이후, 그의 일단부를 잡고 5도 ~ 60도를 형성하는 방향으로 당긴다. 이 때, 테이프는 부착면의 끝 부분부터 늘어나게 되는데, 테이프가 늘어나면서 작용하는 힘이 프론트 윈도우 또는 터치스크린 패널 상의 광학용투명접착제에 전달된다. 이때, 분리 제거용 테이프에 붙은 광학용투명접착제도 분리 제거용 테이프에 붙은 상태에서 함께 늘어나면서 연속적으로 제거된다.FIG. 5 shows a method of removing a transparent adhesive for optical use according to the present invention. First, the pressure-
본 발명에서 터치스크린 패널은 그 자체뿐만 아니라, 도 1 및 도 3에 도시된 바와 같이, 그 것을 구성하는 윈도우 패널(1)과 전극패턴 패널(2) 각각도 포함하는 개념으로 이해되어야 한다. 즉, 상기 터치스크린 패널이 재생을 위하여 분해된 후, 윈도우 패널(1)과 전극패턴 패널(2)에 붙어 있는 광학용투명접착제도 본 발명에 의해 용이하게 제거될 수 있다. The touch screen panel in the present invention should be understood not only in itself but also as a concept including each of the window panel 1 and the electrode pattern panel 2 constituting the touch screen panel as shown in Figs. That is, after the touch screen panel is disassembled for reproduction, the optical transparent adhesive for the window panel 1 and the electrode pattern panel 2 can be easily removed by the present invention.
이하에서, 실시예를 통하여 본 발명을 보다 상세히 설명한다. 그러나, 하기의 실시예는 본 발명을 더욱 구체적으로 설명하기 위한 것으로서, 본 발명의 범위가 하기의 실시예에 의하여 한정되는 것은 아니다. 하기의 실시예는 본 발명의 범위 내에서 당업자에 의해 적절히 수정, 변경될 수 있다. Hereinafter, the present invention will be described in more detail by way of examples. However, the following examples are intended to further illustrate the present invention, and the scope of the present invention is not limited by the following examples. The following examples can be appropriately modified and changed by those skilled in the art within the scope of the present invention.
제조예Manufacturing example 1. 점착제 코팅액의 제조 1. Preparation of pressure-sensitive adhesive coating liquid
고형분 기준으로 열경화형 점착제와 경화제를 아래 [표 1]의 조액표에 따라서 계량하고 혼합한 후 Mechanical Stirrer를 이용하여 15분간 혼합한다.The thermosetting pressure-sensitive adhesive and the curing agent are weighed and mixed according to the tabular table shown in Table 1 below, and then mixed using a mechanical stirrer for 15 minutes.
이후 자외선 경화형 모노머 또는 올리고머를 계량하여 투입하고 광개시제를 계량하여 투입한다.Then, the ultraviolet curing type monomer or oligomer is metered in and introduced, and the photoinitiator is metered in.
전체 고형분이 18중량%가 되도록 메틸에틸케톤(MEK):톨루엔(Toluene) 50:50 중량비 용액을 첨가하고 Mechanical Stirrer를 이용하여 45분 혼합한다.A solution of methyl ethyl ketone (MEK): toluene (Toluene) in a weight ratio of 50:50 was added thereto so that the total solid content was 18% by weight, and the mixture was stirred for 45 minutes using a mechanical stirrer.
제조예Manufacturing example 2. 테이프의 제조 2. Manufacture of tapes
제 1 이형필름 위에 엘라스토머를 20㎛ 코팅하고 90에서 3분간 건조 및 경화한다.The first release film is coated with 20 占 퐉 of an elastomer and dried and cured at 90 for 3 minutes.
제 2 이형필름 위에 상기 점착제 조성물을 20㎛ 코팅하고 90에서 3분간 건조 및 경화한다.The pressure-sensitive adhesive composition is coated on the second release film in a thickness of 20 μm and dried and cured at 90 ° C. for 3 minutes.
상기 엘라스토머 층과 점착제 층을 합지한다.The elastomer layer and the pressure-sensitive adhesive layer are laminated together.
(고형분 100% 기준)Acrylic adhesive
(Based on 100% solids)
(고형분 100% 기준)Acrylic pressure-sensitive adhesive hardener
(Based on 100% solids)
Satomer SR506NS / Isobomyl Acrylate / Mono-functionalSatomer SR506NS / Isobomyl Acrylate / Mono-functional
Satomer SR610NS / Polyethylene (600) Di-acrylate / Di-functionalSatomer SR610NS / Polyethylene (600) Di-acrylate / Di-functional
Satomer CN2203NS / Polyester Acrylate Oligomer / Di-functionalSatomer CN2203NS / Polyester Acrylate Oligomer / Di-functional
Satomer CN9007 / Aliphatic Urethane Acrylate / Di-functionalSatomer CN9007 / Aliphatic Urethane Acrylate / Di-functional
제조예Manufacturing example 3. 시험용 패널 제조 3. Test panel manufacture
고릴라 class에 cu-13302(50㎛) OCA필름을 Hot-roll Laminator를 이용하여 100, 1m/min, 2.5kgf/㎠로 Lamination시키고 120에서 24시간 aging 시켜 시험용 패널을 제조한다.Laminae of cu-13302 (50㎛) OCA film to the gorilla class using a hot-roll laminator at 100, 1m / min, 2.5kgf / ㎠ and aging for 120 to 24 hours to manufacture test panels.
비교실험예Comparative Experimental Example 1 및 2. OCA 제거 정도 시험 1 and 2. OCA Removal Test
상기 비교예 1 및 비교예 2에서 제조된 테이프의 제2이형필름층을 제거하고 시험용 패널의 OCA층에 합지한다. 제1이형필름층을 제거하고 25도 각도로 테이프를 연신하여 OCA를 제거한다. 그 결과를 표 2에 표시하였다.The second release film layer of the tape prepared in Comparative Example 1 and Comparative Example 2 was removed and lapped on the OCA layer of the test panel. The first release film layer is removed and the tape is stretched at an angle of 25 degrees to remove the OCA. The results are shown in Table 2.
실험예Experimental Example 1 및 2. OCA 제거 정도 시험 1 and 2. OCA Removal Test
상기 실시예 1 및 실시예 2에서 제조된 테이프의 제2이형필름층을 제거하고 시험용 패널의 OCA층에 합지하고 자외선 경화기를 이용하여 1,000mJ/㎠의 에너지를 테이프 방향에서 조사한다. 제1이형필름층을 제거하고 25도 각도로 테이프를 연신하여 OCA를 제거한다. 그 결과를 표 2에 표시하였다.The second release film layer of the tape prepared in Example 1 and Example 2 was removed and laminated to the OCA layer of the test panel, and an energy of 1,000 mJ / cm 2 was irradiated from the tape direction using an ultraviolet curing machine. The first release film layer is removed and the tape is stretched at an angle of 25 degrees to remove the OCA. The results are shown in Table 2.
비교예1의 경우에는 OCA가 박리되나 OCA의 점착제 층이 한번에 제거되지 않고 3회 라미와 박리과정을 반복해야만 제거되었다. 이에 반해 본발명의 테이프를 사용한 실시예 1과 2의 경우에는 OCA가 한번에 제거되었다.In the case of Comparative Example 1, the OCA was peeled off, but the adhesive layer of OCA was not removed at a time, but was removed only after repeating the lamination and peeling process three times. On the other hand, in the case of Examples 1 and 2 using the tape of the present invention, OCA was removed at once.
비교예 2의 경우는 2번의 라미와 박리과정을 반복해야만 제거되었다. 비교예 2 의 경우에는 점착제층의 자외선 경화형 감광성 수지의 함량이 높아서 테이프의 연신 정도가 실시예 1, 2 대비 다소 부족하여 박리력이 저하 되는 것으로 판단된다. In the case of Comparative Example 2, it was removed only by repeating the peeling process with two times of lamination. In the case of Comparative Example 2, the content of the ultraviolet curing type photosensitive resin of the pressure-sensitive adhesive layer was high and the degree of stretching of the tape was somewhat insufficient as compared with Examples 1 and 2, and the peeling force was judged to be lowered.
실험예 6. 박리 각도별 시험Experimental Example 6 Test by peeling angle
상기 시험 결과에서 가장 결과가 양호한 실시예 1과 2의 조성 중에 자외선 경화형 모노머 및 올리고머의 함량 중에 중간값을 가지는 신규 실시예 3을 조액하여 필름을 코팅하고 Aging하여 테이프를 제작하였다.(표 3 참조)From the test results, the new Example 3 having the intermediate value among the contents of the ultraviolet curing type monomers and the oligomers was obtained from the compositions of Examples 1 and 2, which had the best results, and the film was coated and aged to produce a tape. )
(고형분 100% 기준)Acrylic adhesive
(Based on 100% solids)
(고형분 100% 기준)Acrylic pressure-sensitive adhesive hardener
(Based on 100% solids)
이 테이프를 이용하여 다양한 각도로 OCA를 박리하고 그 결과를 하기 표 4에 표시하였다.OCA was peeled at various angles using this tape, and the results are shown in Table 4 below.
비교예 1의 경우 15°~35°의 각도에서 1/3영역 정도만 OCA가 제거되지만, 실시예 3의 조성물을 이용한 테이프를 사용한 경우에서는 약 60°이하의 각도에서 전반적으로 OCA필름이 잘 제거됨을 볼수 있다. 즉, 종래의 기술을 사용한 비교예 1의 경우에는 작업자가 OCA제거필름의 박리 각도 조절을 잘 못 할 경우에 필름이 끊어지거나 박리가 잘 안될 경우가 발생하는데 반해서 본 발명의 점착층을 사용하여 테이프를 제조할 경우에는 작업자가 박리 각도에 둔감하게 빠르게 작업해도 OCA제거율이 상당히 양호한 것으로 판단된다.In the case of Comparative Example 1, the OCA was removed only in about 1/3 of the area at an angle of 15 ° to 35 °. However, in the case of using the tape using the composition of Example 3, the OCA film was well removed at an angle of about 60 ° or less can see. That is, in the case of Comparative Example 1 using the conventional technique, when the operator can not adjust the peeling angle of the OCA removal film, the film may be broken or peeling may not be performed easily, It is judged that the OCA removal rate is considerably good even if the operator works fast and insensitive to the separation angle.
10: 제1 이형필름층
20: 엘라스토머층
30: 감압성 점착제층
40: 제2 이형필름층
100: 광학용투명접착제 제거용 테이프10: first release film layer 20: elastomer layer
30: pressure-sensitive adhesive layer 40: second release film layer
100: Optical adhesive tape for removing transparent adhesive
Claims (4)
상기 감압성 점착제층은 열경화형 아크릴계, 실리콘계 또는 고무계 점착제에 일정량의 자외선경화형 감광성 수지를 첨가하여 제조하는 것을 특징으로 하는 광학용투명접착제 제거용 테이프.The method according to claim 1,
Wherein the pressure-sensitive adhesive layer is produced by adding a predetermined amount of ultraviolet curable photosensitive resin to a thermosetting acrylic, silicone or rubber adhesive.
(b) 제2 이형필름 위에 자외선 경화형 감광성수지를 포함하는 점착제 조성물을 도포하여 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층을 형성하는 단계; 및
(c) 상기 엘라스토머층과 감압성 점착제층을 합지시키는 단계;를 포함하는 것을 특징으로 하는 광학용투명접착제 제거용 테이프의 제조방법(a) applying an elastomer to a first release film to form an elastomer layer having a thickness of from 5 占 퐉 to 50 占 퐉;
(b) applying a pressure-sensitive adhesive composition containing a UV-curable photosensitive resin on the second release film to form a pressure-sensitive adhesive layer containing 1 to 25% by weight of the photosensitive resin based on the total weight of the pressure-sensitive adhesive layer; And
(c) a step of laminating the elastomer layer and the pressure-sensitive adhesive layer to each other; and
제1 이형필름층, 5㎛ ~ 50 ㎛ 두께의 엘라스토머층, 자외선 경화형 감광성수지를 감압성 점착제층 총 중량 대비 1~25중량% 포함하는 감압성 점착제층, 및 제2 이형필름층이 순차적으로 적층된 광학용투명접착제 제거용 테이프를 준비하는 단계,
상기 광학용투명접착제 제거용 테이프의 제2이형필름층을 제거하는 단계,
상기 광학용투명접착제 제거용 테이프의 점착제층을 상기 패널의 광학용투명접착제의 표면에 합지하는 단계,
상기 광학용투명접착제 제거용 테이프가 합지된 패널을 자외선 경화기에 투입하여 자외선을 테이프 방향에서 조사하는 단계, 및
상기 광학용투명접착제 제거용 테이프의 제1이형필름층을 제거한 후에 테이프를 연신시켜 광학용투명접착제와 함께 제거하는 단계를 포함하는 패널의 광학용투명접착제 제거 방법Preparing a panel in which a transparent adhesive for optics is laminated,
Sensitive adhesive layer comprising a first release film layer, an elastomer layer having a thickness of 5 占 퐉 to 50 占 퐉, a pressure-sensitive adhesive layer containing an ultraviolet-curable photosensitive resin in an amount of 1 to 25% by weight based on the total weight of the pressure-sensitive adhesive layer, and a second release film layer Preparing a transparent adhesive removing tape for optical use,
Removing the second release film layer of the optical transparent adhesive removing tape,
Bonding a pressure-sensitive adhesive layer of the optical transparent adhesive removing tape to the surface of the optical transparent adhesive of the panel,
Irradiating ultraviolet rays in the direction of the tape by putting the panel on which the optical transparent adhesive removing tape is laminated in an ultraviolet curing unit,
Removing the first release film layer of the optical transparent adhesive removing tape, and then stretching the tape to remove it together with the optical transparent adhesive,