KR20180055338A - method of polyurea coating of precious slag ball for installation of artificial turf

Info

Publication number: KR20180055338A
Application number: KR1020160153083A
Authority: KR
Inventors: 김영남
Original assignee: 김영남
Priority date: 2016-11-17
Filing date: 2016-11-17
Publication date: 2018-05-25
Also published as: KR101876078B1

Abstract

The present invention comprises: a step of washing and treating the surface of PS balls, having a diameter of 0.8-4 mm, and then, sorting the balls; a moisture content measurement step of measuring moisture contained in the PS balls through a moisture content measurement device; a step of applying harmless and eco-friendly acrylic emulsion to the surface of the PS balls, and then, drying the balls at 60-80 degrees Celsius for 20-40 minutes; a step of coating the surface of the PS balls with harmless and eco-friendly polyurea, and then, drying the balls through a drying unit; a step of inspecting the quality of the coated surface of the PS balls and sorting the balls; and a step of packing the PS balls. As such, the present invention is capable of conveniently discharging and purifying water, left in an artificial turf stadium, and maintaining a pleasant condition by using PS balls, which are rounded without angular parts, as fillers for an artificial turf structure.

Description

인조잔디 포설용 PS볼의 폴리우레아 도막방법{method of polyurea coating of precious slag ball for installation of artificial turf} BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a polyurea coating method for a PS ball for artificial turf laying,

본 발명은 인조잔디 포설용 PS볼(Precious Slag Ball)의 폴리우레아 도막방법에 관한 것으로서, 더욱 상세하게는, 인조잔디 포설 구조체에 충전 사용되어 운동장의 쾌적한 환경을 제공하고, 인조잔디의 수명을 연장하며, 인체 및 자연환경에 유해하지 않고, 인조잔디 포설에 따른 설치비용을 절감할 수 있도록 한 PS볼에 있어서, 상기 PS볼을 선별한 후 함수율측정을 거쳐 아크릴에멀젼을 도포한 후 아크릴에멀젼을 도포층에 폴리우레아를 일정 두께로 도막하는 방법을 제공하는 것으로서, 인조잔디 포설에 적합한 PS볼을 제공할 수 있는 인조잔디 포설용 PS볼의 폴리우레아 도막방법에 관한 것이다.The present invention relates to a polyurea coating method of a PS ball for artificial turf laying, more particularly, to a method of polyurea coating for artificial lawn, which is filled with artificial turf laid structure to provide a pleasant environment of a playground, The present invention provides a PS ball which is not harmful to the human body and natural environment and can reduce the installation cost due to the artificial turf installation. The PS ball is selected, the acrylic emulsion is applied through water content measurement, The present invention relates to a polyurethane coating method for a PS ball for artificial turf laying which can provide a PS ball suitable for artificial turf laying.

일반적으로 인조잔디는 형태를 갖추어 인공적으로 만든 천연잔디의 대용품으로 미국에서 처음 제작된 이래 주로 스포츠 구장에 사용되었고 잔디의 생육이 불가능한 옥내 정원이나 일조시간이 극히 제한된 고층건물의 북쪽에 접한 옥외지역과 같은 곳에서 사용할 수 있다. Artificial turf is generally used as a substitute for artificial turf, which is used as a substitute for artificial turf since it was first produced in the United States. It has been used mainly as a sports ground and has been used as an outdoor garden facing the northern side of a high- Can be used in the same place.

상기 인조잔디는 항상 푸름을 유지하고 환경조건의 제한을 받지 않아 시공 후 관리가 용이하다. 인조잔디가 시공된 인조잔디 구장은 일반 천연잔디에 비해 초기 시공비가 많이 들지만, 계절에 관계없이 사용이 가능하고 유지관리의 편의성, 운동하기에 적합하도록 표면이 고른 점 등으로 인해 선호도가 높다. The artificial turf always maintains a green color and is not restricted by environmental conditions, so it is easy to manage after construction. Although artificial turf is constructed with artificial turf, the initial construction cost is higher than that of general natural turf. However, preference is high because it is possible to use regardless of the season, convenience of maintenance, and uniformity of surface for exercise.

종래 인조잔디는 최하부에 골재, 석분, 투스콘 등과 같은 물질이 형성되어 배수작용을 원활케 하는 지반층과, 지반층의 상부에 천연잔디의 형상과 유사하게 형성되는 잔디파일과, 상기 잔디파일을 견고하게 고정하는 고정층과, 고정층의 상부에 충전되어 잔디파일 사이사이를 채우는 모래 등의 규사층과, 규사층의 상부에 충전되어 탄성을 좋게하는 쿠션층으로 이루어지는 것이 통상적이었다.Conventional artificial turf has a ground layer formed at the lowermost portion such as aggregate, stone, and tusk cone to smooth drainage, a grass pile formed in the upper part of the ground layer similar to the shape of natural grass, And a cushion layer filled in the upper portion of the silica sand layer to improve the elasticity, as shown in Fig.

한편, 도 1은 종래 인조잔디 포설 구조체에 대한 단면도이다.1 is a cross-sectional view of a conventional artificial grass laid structure.

상기 도면에서 볼 수 있는 바와 같이, 종래 인조잔디 포설 구조체는, 표면을 관통하는 통공(11)이 형성된 바닥판(10)과, 합성수지사의 직모형태로 형성되어 상기 바닥판(10)의 통공(11)에 식재된 인조잔디 파일사(20)로 이루어져 지면 또는 지면에 포설된 완충패드 위에 포설되는 구성을 갖는다. 그리고 인조잔디 파일사 사이 사이에는 충전재인 모래 등의 규사(30)를 일정한 두께로 포설하고 그 위에 탄성을 좋게하는 쿠션층 즉, 고무분말(40)을 포설하여 완성된다.As shown in the figure, the artificial turf installation structure according to the related art includes a bottom plate 10 having a through hole 11 penetrating the surface thereof, and a through hole 11 of the bottom plate 10, The artificial lawn pile 20 is installed on a floor or a cushioning pad laid on the ground. And between the artificial turf pile yarns, a silk yarn 30 such as sand, which is a filler, is laid to a certain thickness and a cushion layer, that is, a rubber powder 40,

그런데, 종래 인조잔디 구조체는 아래와 같은 문제점을 갖는다.However, the conventional artificial turf structure has the following problems.

첫째, 규사는 그 크기가 한정되어 있지 않고 더군다나 날카로운 면을 가지기 때문에 운동시 슬라이딩 등을 하면 규사로 인해 피부가 손상된다는 문제가 있다.First, since the size of the silica sand is not limited and moreover it has a sharp surface, there is a problem that the skin is damaged due to the silica sand when sliding during the exercise.

둘째, 규사는 날카로운 면을 가지기 때문에 운동장에서 거친 운동을 하는 사용자의 움직임에 따른 자중에 날카로운 규사가 인조잔디 파일사을 파손하여 결과적으로 인조잔디의 수명을 단축시키는 문제점이 있다.Second, since the sandpaper has a sharp surface, the sharp grass sand on the weight due to the movement of the user who performs the rough motion on the playground breaks the artificial grass filament, which shortens the life of the artificial turf.

셋째, 규사는 비산먼지를 발생시키기 때문에 규사먼지가 인조잔디 구장에서 운동을 하는 사람의 호흡기로 유입되어 인체에 해로운 문제점이 있다.Third, because silica dust generates scattered dust, silica dust enters the respiratory system of a person exercising on artificial turf ground, which is harmful to the human body.

넷째, 규사가 일정한 크기를 갖지 않고 다양한 크기로 포설되기 때문에 운동장에서의 볼의 구름이 원활하지 않아 경기력의 저하 원인이 되는 문제점이 있다. Fourth, since the sandpaper is installed at various sizes without having a certain size, there is a problem that the ball is not smooth in the playground, which is a cause of deteriorating the performance.

또한 충전재로 사용되는 고무분말은 아래와 같은 문제점을 갖는다.Also, the rubber powder used as a filler has the following problems.

첫째, 고무분말은 시간이 흐르면 산화되어 먼지를 발생하고 따라서 고무분말 먼지가 인조잔디 구장에서 운동을 하는 사람의 호흡기로 유입되어 인체에 해롭다는 문제점과 아울러 피부에 접촉하면 다양한 종류의 피부병이 발생하는 문제점이 있다.First, the rubber powder is oxidized to generate dust over time, so that the rubber powder dust is harmful to the human body by flowing into the respiratory tract of a person exercising in the artificial grass field, and various kinds of skin diseases There is a problem.

둘째, 고무분말은 시간이 흐르면 자연적인 기온 및 온도변화에 의해 녹아내리게 되고 따라서 녹은 고무분말은 운동자가 밟는 것에 의해 굳어져 빗물 배수가 용이치 않아 빗물이 인조잔디 운동장에 고이는 문제점과 아울러 인조잔디 파일사가 녹아내린 고무분말에 접착되어 고형화되는 것으로 인해 인조잔디의 역할이 불가능해진다는 문제점 있다.Secondly, the rubber powder melts due to the natural temperature and temperature change over time, and therefore, the molten rubber powder hardens by being treaded by the athlete, and the drainage of rainwater is insufficient, so that the rainwater accumulates in the artificial turf field, It is difficult to use the artificial turf because the rubber is adhered to the solidified rubber powder.

셋째, 고무분말에서 발생한 먼지 등이 빗물에 의해 유실되면 주변 자연환경을 손상시킨다는 문제점이 있다. Third, if the dust or the like generated in the rubber powder is lost by the rainwater, the surrounding natural environment is damaged.

결과적으로 종래 인조잔디 포설 구조체에 사용되는 규사 및 고무분말은 시간이 흐를수록 함께 혼합되어 상기와 같은 문제점을 발생하게 되고, 특히 종래 충전재는 운동자의 마찰에 의한 마모가 심해 장기간 사용할 수 없을 뿐만 아니라 사용기간도 짧아져 인조잔디의 유실보수 및 재시공하는데에 따른 비용을 발생시킨다.As a result, the silica sand and rubber powder used in the conventional artificial turf installation structure are mixed together with the lapse of time to cause the above problems. Particularly, the conventional filler has a problem of abrasion due to friction of the exerciser, The period of time is also shortened, resulting in the cost of repairing and reworking the artificial turf.

한편, 대한민국등록특허공보에 개시된 특허등록(10-1167279호 / 공고일자 2010. 07. 23)는 슬래그 볼을 이용한 인도 보도 및 자전거도로 포장시공방법에 관하 것이다.On the other hand, a patent registration (10-1167279 / publication date: 07. 23, 2010) disclosed in the Korean registered patent publication relates to a method of paving an Indian sidewalk and a bicycle road using a slag ball.

상기 종래 슬래그 볼을 이용한 인도 보도 및 자전거도로 포장시공방법에는 도로 시공면 및 프라이머 도포면에 PS 볼 및 우레탄 바인더 혼합 조성물을 골고루 포설하는 것이 기재되어 있다. 즉 도로면에 사용되는 PS 볼 및 우레탄 바인더 혼합 조성물은, 교반기에 PS 볼을 먼저 넣고, 주제와 경화제를 전동믹싱기를 사용하여 3분 이상 충분하게 믹싱하여 준비한 우레탄 바인더를 투입한 후, 2분 이상 충분하게 교반하여 제조하는 것이다. 그러나 이는 PS볼을 우레탄 바인더와 혼합한 후, 도로면에 포설하여 함께 경화시키는데 사용되는 것으로서 이는 공면의 수분 차단 및 PS볼 시공층의 접착력 향상을 위하여 시공전 우레탄 프라이머를 도포하는 것이기 때문에 이와 같은 우레탄 프라이머와 함께 경화된 다수의 PS볼은 인조잔디 포설 구조체에 사용할 수 없다는 문제점이 있다.In the method for paving roads and bicycle roads using the conventional slag balls, it is described that a PS ball and a urethane binder mixed composition are uniformly installed on the road construction surface and the primer application surface. That is, the PS ball and urethane binder mixed composition used for the road surface is prepared by first putting a PS ball into a stirrer, mixing a base and a hardener with a urethane binder prepared by mixing for 3 minutes or more by using an electric mixer, Followed by sufficient stirring. However, this is because PS balls are mixed with a urethane binder, and then used to cure the PS balls together with the road surface. This is because the urethane primer is applied before the application of water for interception of moisture in the co- A large number of PS balls cured together with the primer can not be used in artificial turf laying structures.

따라서 본 발명은 상기와 같은 종래 문제점을 해결하기 위하여 창안한 것으로서, 본 발명은 모나지 않도록 둥글게 가공되어 일정한 크기를 갖는 PS 볼만의 표면에 아크릴에멀젼과 폴이우레아를 도막함으로써, 인조잔디 포설 구조체에 충전용으로 사용함으로써, 운동장의 쾌적한 환경을 제공하여 경기력을 향상시키고, 인조잔디의 수명을 연장시키며 인체 및 자연환경에 유해하지 않으며, 인조잔디 포설에 따른 설치비용을 절감할 수 있는 인조잔디 포설용 PS볼의 폴리우레아 도막방법을 제공하는데 그 목적이 있다. SUMMARY OF THE INVENTION Accordingly, the present invention has been made to solve the above-mentioned problems occurring in the prior art, and it is an object of the present invention to provide an artificial turf installation structure in which acrylic emulsion and pole are coated with urea on the surface of a PS ball having a predetermined size, The artificial turf laying PS which can reduce the installation cost due to the installation of the artificial turf is not detrimental to the human body and the natural environment by providing the pleasant environment of the playground by improving the performance, And to provide a polyurea coating method for a ball.

상기 목적은 본 발명에 따라, 0.8mm ~ 4mm 크기의 지름을 갖는 PS볼을 세척 및 표면처리 후 선별하는 단계; 상기 선별단계 거친 상기 PS볼을 함수율측정기를 통해 상기 PS볼에 함유된 수분을 측정하는 함수율측정단계; 상기 함수율측정단계에서 선별된 PS볼의 표면에 인체에 무해하고 친환경적인 아크릴에멀젼을 스프레이 또는 디핑방법 중 선택된 어느 하나의 방법으로 도포한 후 건조수단에서 60℃ ~ 80℃의 온도에서 20~40분간 건조하는 단계; 상기 건조단계를 거친 PS볼의 표면에 인체에 무해하고 친환경적인 폴리우레아를 스프레이 방법으로 0.3mm ~ 0.9mm가 되도록 도막한 후 건조수단에서 60℃ ~ 80℃의 온도에서 20~40분간 건조하는 단계; 상기 도막 건조단계를 거친 PS볼의 도막품질검사단계 및 선별단계; 상기 단계를 통해 얻어진 PS볼의 포장단계로 이루어진 것을 특징으로 하는 인조잔디 포설용 PS볼의 폴리우레아 도막방법에 의해 달성된다.According to the present invention, the above object can be accomplished by a method of cleaning a PS ball having a diameter of 0.8 mm to 4 mm, A moisture content measuring step of measuring the water contained in the PS balls by using a water content meter; The acrylic emulsion harmless to the human body and applied to the surface of the PS balls selected in the water content measuring step is sprayed or dipped, Drying; Coating the surface of the PS ball having passed through the drying step so that the environmentally friendly polyurea is harmless to the human body with a spraying method of 0.3 mm to 0.9 mm and drying it at a temperature of 60 ° C to 80 ° C for 20 to 40 minutes ; A coating film quality inspection step and a screening step of the PS ball having been subjected to the coating film drying step; And a packaging step of the PS balls obtained through the above steps.

이상과 같은 본 발명은, 이상과 같은 도막방법으로 제공된 PS볼을 인조잔디 포설 구조체의 충전재로 사용함으로써, 유해물질 및 비산먼지가 없어 인체 및 자연환경을 저해하는 일이 없으며, 인조잔디 운동장에 고인 물을 쉽게 배수 및 정화하여 쾌적한 한경을 유지하는 이점이 있다. 그리고 본 발명은 PS볼이 모나지 않고 둥글기 때문에 인조잔디 파일사의 파손을 방지하며, PS볼은 자연기온에 녹아내리지 않기 때문에 인조잔디 운동장의 평탄성을 유지시키는 이점이 있다.As described above, the PS ball provided by the coating method as described above is used as a filler of the artificial turf installation structure, so that there is no harmful substances and scattered dust, and the human body and the natural environment are not hindered. There is an advantage that the water is easily drained and purified to maintain a pleasant environment. In addition, since the PS ball is round and round, the artificial grass filament is prevented from being damaged, and the PS ball is not melted in natural temperature, so that the flatness of the artificial turf ground is maintained.

또한 본 발명은 PS볼이 마찰에 의한 마모가 발생하지 않고 침착되지 않아 경기력이 향상되며 장기간 사용 가능한 이점과 아울러 인조잔디의 포설 구조체가 단조로워 유지보수가 현저히 줄어들고 관리가 용이하며, PS볼의 자중에 의해 빗물에 유실되지 않으며, 빗물 등에 의해 세척되어 항상 신제품처럼 사용할 수 있는 효과가 있다. In addition, since the PS ball is not deposited due to abrasion due to friction, the performance is improved and the PS ball can be used for a long period of time. In addition, the artificial turf structure is monotonous and the maintenance is greatly reduced. It is not lost in rain water, it is cleaned by rainwater, etc., and can always be used as a new product.

도 1은 종래 인조잔디 포설 구조체에 대한 단면도이다.
도 2는 본 발명 인조잔디 포설용 PS볼의 폴리우레아 도막방법을 순차적으로 보인 블록도,
도 3은 본 발명에 따른 PS볼에 폴리우레아가 도막된 상태의 단면도,
도 4는 본 발명에 따른 PS볼을 인조잔디 포설 구조체에 충전한 상태를 보인 단면도이다.1 is a cross-sectional view of a conventional artificial turf laying structure.
2 is a block diagram sequentially showing a polyurea coating method of a PS ball for laying an artificial turf according to the present invention,
FIG. 3 is a cross-sectional view of a PS ball according to the present invention,
FIG. 4 is a cross-sectional view illustrating a state in which a PS ball according to the present invention is charged into an artificial turf laying structure.

이하에서는 첨부된 도면을 참고하여 본 발명에 대하여 상세히 설명한다.
Hereinafter, the present invention will be described in detail with reference to the accompanying drawings.

도 2는 본 발명 인조잔디 포설용 PS볼의 폴리우레아 도막방법을 순차적으로 보인 블록도 이다.FIG. 2 is a block diagram sequentially illustrating a polyurea coating method of a PS ball for laying an artificial turf according to the present invention.

상기 도면을 참고하여 본 발명에 따른 실시예를 설명한다.An embodiment according to the present invention will be described with reference to the above drawings.

[실시예][Example]

1. 0.8mm ~ 4mm 크기의 지름을 갖는 PS볼(300)을 세척 및 표면처리 후 합격과 불합격제품으로 선별하는 단계를 거치고(S10), 불합격된 PS볼(300)은 재처리 과정을 거쳐 다시 선별하는 단계를 거친다. 여기서 PS볼(300)은 표면이 모나지 않고 둥근 형상을 갖는 것이 인조잔디 포설 구조체에 포설하였을 때 사용자가 PS볼(300)로부터 신체를 보호할 수 있기 때문에 바람직하다. 1. The PS ball 300 having a diameter of 0.8 mm to 4 mm is washed and subjected to a surface treatment and a rejection step (S10), and the rejected PS ball 300 is reprocessed It goes through a selection step. Here, it is preferable that the PS ball 300 has a rounded shape without a surface, because the user can protect the body from the PS ball 300 when the PS ball 300 is installed on the artificial turf laying structure.

2. 선별단계 거친 PS볼(300)을 함수율측정기를 통해 PS볼(300)에 함유된 수분을 측정하는 함수율측정단계(S20)를 거치는데, 이는 PS볼(300)에 수분이 많을 경우 경화가 빨라 도막의 불량이 발생하기 때문이다.2. Selection Step The moisture content measuring step (S20) of measuring the moisture contained in the PS ball 300 is performed through the moisture content measuring device of the rough PS ball 300. This is because when the PS ball 300 is wet, This is because the coating film is defective quickly.

3. 함수율측정단계에서 선별된 PS볼(300)의 표면에 인체에 무해하고 친환경적인 아크릴에멀젼을 스프레이 또는 디핑방법 중 선택된 어느 하나의 방법으로 도포한 후 건조수단에서 60℃ ~80℃의 온도에서 20~40분간 건조하는 단계(S30)를 거친다. 여기서 아크릴에멀젼을 사용하는 이유는 경화시간을 줄이고, 완전한 경화를 할 수 있도록 돕는 역할을 하기 때문이다.3. An acrylic emulsion which is harmless to the human body and which is harmless to the human body is applied to the surface of the PS ball 300 selected in the water content measuring step by a spraying or dipping method and then dried at a temperature of 60 ° C to 80 ° C Followed by drying for 20 to 40 minutes (S30). The reason for using the acrylic emulsion here is to reduce the curing time and to help complete curing.

4. 아크릴에멀젼 도포 및 건조단계를 거친 PS볼(300)의 표면에 인체에 무해하고 친환경적인 폴리우레아를 0.5mm가 되도록 도막하는 단계(S40)를 거치고, 건조수단에서 60℃ ~80℃의 온도에서 20~40분간 건조하는 단계(S30)를 거친 후, 도막상태를 선별하여 폴리우레아를 재도포하는 단계를 거친다. 4. A step (S40) of coating the surface of the PS ball 300, which has been subjected to the acrylic emulsion coating and drying step, so that the environmentally friendly polyurea is 0.5 mm thick, (S30) for 20 to 40 minutes, and then the coating state is selected to repaint the polyurea.

5. 도막단계를 거친 PS볼(300)의 도막품질검사단계 및 선별단계(S50)를 거친다.5. The coating film quality inspection step and the screening step (S50) of the PS ball 300 having undergone the coating step are performed.

6. 상기 단계를 통해 생산된 PS볼(300)의 포장하는 단계(S60)를 거친다.6. Step S60 of packaging the PS balls 300 produced through the above steps.

이상과 같은 실시예에 따라 생산된 PS볼(300)은 본 발명에 따른 인조잔디 포설 구조체용 PS볼(300)로의 사용이 효과적이다.
The PS ball 300 manufactured according to the above embodiment is effective for use in the PS ball 300 for the artificial lawn installation structure according to the present invention.

본 발명에 따라 생산된 PS볼(300)은 도 4에서 볼 수 있는 바와 같이, 통공이 형성된 바닥판(100)과, 합성수지사의 직모형태로 형성되어 바닥판(100)의 통공(101)에 마련된 인조잔디 파일사(200)와, 파일사 사이 사이에 충전된다.4, the PS ball 300 manufactured according to the present invention includes a bottom plate 100 with a through hole formed therein, a base plate 100 formed in a straight shape of synthetic resin and provided in the through hole 101 of the bottom plate 100, The artificial lawn pile yarn 200 and the pile yarn.

본 발명에 따른 PS볼(300)은 모나지 않도록 둥글게 가공된 것으로서 기존이 진조잔디 포설 구조체에 사용되던 모래 등의 규사와 달리 동일한 크기에서도 그 중량이 규사보다 크기 때문에 인조잔디 파일사(200) 사이에 포설되어도 바람 등에 의해 쉽게 비산되지 않는다.The PS ball 300 according to the present invention is rounded so that it is not rounded, and since the weight of the PS ball 300 is the same as that of the sand-like sand used in the conventional turf grass laying structure, Even if it is installed, it is not easily scattered by the wind.

상기 PS볼(300)은 지름 크기는 0.8mm ~4mm 크기로 제조하는 것이 바람직하나, 운동장의 용도에 따라 그 지름의 크기는 상기 지름의 크기 보다 작게 또는 크게 할 수 있을 것이다. 이에 다수의 PS볼(300)은 바닥판(100)에 마련된 인조잔디 파일사(200)의 전체 높이의 50~80%의 높이까지 충전한다.The diameter of the PS ball 300 is preferably 0.8 mm to 4 mm, but the diameter of the PS ball 300 may be smaller or larger than the diameter of the PS ball 300 depending on the application of the playground. The plurality of PS balls 300 are filled up to a height of 50 to 80% of the total height of the artificial grass filament yarn 200 provided on the bottom plate 100.

한편, 도 3은 본 발명에 따른 PS볼에 폴리우레아가 도막된 상태의 단면도이다. FIG. 3 is a cross-sectional view of a PS ball according to the present invention, in which polyurea is coated.

이 도면에서는 PS볼(300)은 외면 전체에 폴리우레아가 도막된 폴리우레아 도막층(302)이 형성되어 인조잔디 파일사(200) 사이에 PS볼(300)이 충전된다. 여기서 폴리우레아는 인체에 무해한 친환경적이면서 우수한 물성을 갖는 것으로서, 뛰어난 물리적 성질(인장, 인열, 내충격, 내마모성, 내구력 등)과 접착력, 방식성, 내약품성, 내산성, 내한성 등의 우수한 물성이 있다. 따라서 PS볼(300)에 도막하였을 때, 유해물질 및 비산먼지가 없어 인체 및 자연환경을 저해하는 일이 없으며, 인조잔디 운동장에 고인 물을 쉽게 배수 및 정화하여 쾌적한 환경을 유지한다. In this figure, a polyurea coating layer 302 having a polyurea coating is formed on the entire outer surface of the PS ball 300, and the PS ball 300 is filled between the synthetic grass pile yarns 200. Here, polyurea is an environmentally friendly and excellent physical property harmless to human body and has excellent physical properties such as excellent physical properties (tensile, tear, impact resistance, abrasion resistance, durability, etc.), adhesion strength, anticorrosion property, chemical resistance, acid resistance and cold resistance. Therefore, when the PS ball 300 is coated, there is no harmful substances and scattered dust, so that it does not hinder the human body and the natural environment. The artificial turf ground can easily drain and purify water to maintain a pleasant environment.

한편, 본 발명에 따른 PS볼(300)도 인체에 무해하고 친환경적이면서 모나지 않고 둥글기 때문에 인조잔디 파일사의 파손을 방지하며, PS볼(300)은 자연기온에 녹아내리지 않기 때문에 인조잔디 운동장의 평탄성을 유지시킨다. 특히 본 발명에서와 같이 폴리우레아 도막층(302)을 갖는 PS볼(300)은 종래 인조잔디 포설 구조체에 포설되는 규사 및 고무칩과 달리 내마모성을 갖기 때문에 기온 및 온도변화에 의해 녹아내리지 않아 인조잔디 파일사와 완벽하게 분리되므로 파일사의 변형 등이 방지된다.Meanwhile, since the PS ball 300 according to the present invention is harmless to the human body and is environmentally friendly and rounded without being rounded, the artificial turf pile yarn is prevented from being damaged and the PS ball 300 is not melted into natural temperature. . Particularly, as in the present invention, the PS ball 300 having the polyurea coating layer 302 has wear resistance, unlike silica sand and rubber chips, which are conventionally installed on artificial turf laying structures. Therefore, the PS ball 300 does not melt due to changes in temperature and temperature, Since it is completely separated from the file file, the file file is not deformed.

또한 본 발명에 따른 PS볼(300)이 마찰에 의한 마모가 발생하지 않고 침착되지 않아 경기력이 향상되며 장기간 사용 가능한 이점과 아울러 인조잔디의 포설 구조체가 단조로워 유지보수가 현저히 줄어들고 관리가 용이하며, PS볼(300)의 자중에 의해 빗물에 유실되지 않으며, 빗물 등에 의해 세척되어 항상 신제품처럼 사용할 수 있다. Further, since the PS ball 300 according to the present invention is not deposited due to friction, it is improved in performance and can be used for a long time. In addition, the artificial turf structure is monotonous, It is not lost to rainwater due to the weight of the ball 300, and can be always used as a new product by being cleaned by rainwater or the like.

이상과 같은 본 발명은, 모나지 않게 둥글게 가공된 PS볼(300)에 폴리우레아 도막층(302)을 갖기 때문에 인조잔디 파일사(200)에 사이 사이에 포설하여 충전재로 사용함으로써, 유해물질 및 비산먼지가 없고 인체 및 자연환경을 저해하는 일이 없으며, 인조잔디 운동장에 고인 물을 쉽게 배수 및 정화하여 쾌적한 환경을 유지한다. As described above, since the polyurea coating layer 302 is provided on the PS ball 300, which has been rounded without being rounded, it is installed between the artificial grass pile yarn 200 and used as a filler, There is no dust, no hindrance to the human body and the natural environment, and easy drainage and purification of artificial turf playground to maintain comfortable environment.

또한 본 발명은 PS볼(300)이 모나지 않고 둥글기 때문에 인조잔디 파일사(200)의 파손을 방지하며, PS볼(300)은 금속으로서 자연기온에 녹아내리지 않기 때문에 인조잔디 운동장의 평탄성을 유지시킨다. 그리고 본 발명은 PS볼(300)이 마찰에 의한 마모가 발생하지 않고 침착되지 않아 경기력이 향상되며 장기간 사용가능함과 아울러 인조잔디의 포설 구조체가 단조로워 유지보수가 현저히 줄어들고 관리가 용이하며, PS볼(300)의 자중에 의해 빗물에 유실되지 않으며, 빗물 등에 의해 세척되어 항상 신제품처럼 사용할 수 있다. 그리고 본 발명에 따른 PS볼(300)은 종래의 고무칩과 규사로 이루어져 인조잔디 포설 구조체로 사용되어 장기간이 지나면 함께 녹아 엉겨 붙어 결국 재활용하지 못하고 폐기처분되는 것과 달리, 인조잔디 포설 구조체로 사용된 후 일정한 기간이 지나면 폴리우레아가 도막된 PS볼(300) 만을 선별하여 세척 후 다시 폴리우레아를 재 도막하면 재사용할 수 있기 때문에 폐기에 따른 자연환경을 오염시키지 않는다. In addition, since the PS ball 300 is round and round, the artificial turf pile yarn 200 is prevented from being broken, and the PS ball 300 is not melted into natural temperature as a metal, so that the flatness of the artificial turf ground is maintained . In addition, since the PS ball 300 is not deposited due to abrasion due to friction, the performance is improved and the PS ball 300 can be used for a long period of time. In addition, the artificial turf structure is monotonous, 300), it can be used as a new product all the time because it is cleaned by rainwater or the like. The PS ball 300 according to the present invention is formed of a conventional rubber chip and silica sand so that it can be used as an artificial turf laying structure. After a long time, the PS ball 300 is melted and tangled together and eventually can not be recycled. After a certain period of time, after the PS ball 300 coated with polyurea is selectively cleaned, the polyurea may be re-coated again to prevent the pollution of the natural environment due to disposal.

이상에서와 같이 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이고 사전적인 의미로 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.As used herein, the terms and words used in the present specification and claims should not be construed in a conventional and dictionary sense, and the inventor shall properly define the concept of the term to describe its invention in the best possible way It should be construed as meaning and concept consistent with the technical idea of the present invention.

따라서 본 명세서에 기재된 실시 예와 도면에 도시된 구성은 본 발명의 바람직한 1 실시예에 불과할 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형 예들이 있을 수 있음을 이해하여야 한다.Therefore, the embodiments described in the present specification and the configurations shown in the drawings are merely preferred embodiments of the present invention, and not all of the technical ideas of the present invention are described. Therefore, various equivalents It should be understood that water and variations may be present.

100 : 바닥판
101 : 통공
200 : 인조잔디 파일사
300 : PS볼
302 : 폴리우레아 도막층100: bottom plate
101: Through hole
200: Artificial turf files
300: PS ball
302: polyurea coating layer

Claims

0.8mm ~ 4mm 크기의 지름을 갖는 PS볼을 세척 및 표면처리 후 선별하는 단계;
상기 선별단계 거친 상기 PS볼을 함수율측정기를 통해 상기 PS볼에 함유된 수분을 측정하는 함수율측정단계;
상기 함수율측정단계에서 선별된 PS볼의 표면에 인체에 무해하고 친환경적인 아크릴에멀젼을 스프레이 또는 디핑방법 중 선택된 어느 하나의 방법으로 도포한 후 건조수단에서 60℃ ~ 80℃의 온도에서 20~40분간 건조하는 단계;
상기 건조단계를 거친 PS볼의 표면에 인체에 무해하고 친환경적인 폴리우레아를 스프레이 방법으로 0.3mm ~ 0.9mm가 되도록 도막한 후 건조수단에서 60℃ ~ 80℃의 온도에서 20~40분간 건조하는 단계;
상기 도막 건조단계를 거친 PS볼의 도막품질검사단계 및 선별단계;
상기 단계를 통해 얻어진 PS볼의 포장단계로 이루어진 것을 특징으로 하는 인조잔디 포설용 PS볼의 폴리우레아 도막방법.

Selecting and cleaning the PS balls having a diameter of 0.8 mm to 4 mm after cleaning and surface treatment;
A moisture content measuring step of measuring the water contained in the PS balls by using a water content meter;
The acrylic emulsion harmless to the human body and applied to the surface of the PS balls selected in the water content measuring step is sprayed or dipped, Drying;
Coating the surface of the PS ball having passed through the drying step so that the environmentally friendly polyurea is harmless to the human body with a spraying method of 0.3 mm to 0.9 mm and drying it at a temperature of 60 ° C to 80 ° C for 20 to 40 minutes ;
A coating film quality inspection step and a screening step of the PS ball having been subjected to the coating film drying step;
Wherein the step of packaging the PS balls obtained through the above step is performed.