KR20180047356A - a metal credit card of hybrid material way and manufacturing method metal credit card of hybrid material way - Google Patents

a metal credit card of hybrid material way and manufacturing method metal credit card of hybrid material way Download PDF

Info

Publication number
KR20180047356A
KR20180047356A KR1020160143345A KR20160143345A KR20180047356A KR 20180047356 A KR20180047356 A KR 20180047356A KR 1020160143345 A KR1020160143345 A KR 1020160143345A KR 20160143345 A KR20160143345 A KR 20160143345A KR 20180047356 A KR20180047356 A KR 20180047356A
Authority
KR
South Korea
Prior art keywords
metal
oxide
aluminum
card
aluminum plate
Prior art date
Application number
KR1020160143345A
Other languages
Korean (ko)
Other versions
KR101983028B1 (en
Inventor
이재희
Original Assignee
코나씨 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 코나씨 주식회사 filed Critical 코나씨 주식회사
Priority to KR1020160143345A priority Critical patent/KR101983028B1/en
Publication of KR20180047356A publication Critical patent/KR20180047356A/en
Priority to KR1020190059329A priority patent/KR102283971B1/en
Application granted granted Critical
Publication of KR101983028B1 publication Critical patent/KR101983028B1/en

Abstract

The present invention relates to a method for fabricating a metal card of a hybrid material, of which a high-durable metal sheet is attached to a high-decorative aluminum sheet to realize the metal card of high quality and functionality. The method includes the steps of: polishing the bottom surface of an aluminum sheet (11) by aluminum oxide or sand blast to form an oxide processed layer (12); polishing the bottom surface of a metal sheet (14) by aluminum oxide or sand blast to form an oxide processed layer (12); polishing the top surface of the metal sheet by aluminum oxide or sand blast to form an oxide processed layer (12); positioning, heating and pressing a hot-melting adhesive (13) between the oxide processed layers of the aluminum sheet and the metal sheet to form a card body (10); milling a surface of the aluminum sheet to form a shallow guide groove (21), and inserting and attaching an IC chip (20) in the guide groove; and machining the metal sheet by CNC and cutting the circumference of the card.

Description

하이브리드 소재의 메탈카드 제조방법 및 하이브리드 소재의 메탈카드{a metal credit card of hybrid material way and manufacturing method metal credit card of hybrid material way}METHOD FOR MANUFACTURING METAL CARD OF HYBRID MATERIAL AND HYBRID MATERIAL METHOD BACKGROUND OF THE INVENTION Field of the Invention [0001]

본 발명은 비철금속인 알루미늄 판재에 금속판재가 결합된 하이브리드 소재의 메탈카드 제조방법에 관한 것으로서, 더욱 상세하게는 금속광택이 뛰어나면서도 장식성이 높은 알루미늄 판재와 내구성이 좋으면서도 무게 감이 있는 금속판재가 결합되어 외관이 미려하여 고품위를 느낄 수 있고, 메탈카드의 중량 감을 느낄 수 있는 고품질 고기능성의 메탈카드를 구현한 수 있도록 한 발명에 관한 것이다.
The present invention relates to a method of manufacturing a metal card made of a hybrid material having a metal plate joined to an aluminum plate made of a nonferrous metal. More particularly, the present invention relates to an aluminum plate having excellent metallic luster and high decorative property, The present invention relates to a high-quality and high-performance metal card which can feel a high-quality appearance and feel a weight of a metal card.

일반적으로 신용카드는 현금을 대신하여 사용할 수 있을 뿐 아니라 근래에는 대용량의 정보를 수록할 수 있는 IC칩들이 내장된 스마트카드들이 개발되어 병원의 진료카드 및 각종 멤버카드 등으로 적극 활용된다.In general, credit cards can be used in place of cash, and in recent years, smart cards with integrated IC chips capable of storing large amounts of information have been developed and actively utilized as clinic cards and various member cards.

이중에서도 VIP 고객을 위하여 차별화 된 금속재질의 신용카드가 개발되어 있고, 금속카드는 금속광택이 표출되는 고품위의 신용카드를 구현하여 특수 고객들에 제공된다.Among them, differentiated metal credit cards have been developed for VIP customers, and metal cards are provided to special customers by implementing a high-quality credit card that displays metallic luster.

그러나, 종래의 금속카드들은 얇은 박막의 금속시트를 사용하거나 금속분말을 얇게 코팅하여 제작하는 것이므로 금속카드의 표면에 문양 및 문자의 형성이 어려웠고, 금속의 질감을 느낄 수 없었을 뿐 아니라 금속카드가 매우 가벼운 재질로 형성되어 금속이 갖는 중량 감을 느낄 수 없었다.However, since the conventional metal cards are manufactured by using a thin metal sheet or by thinly coating the metal powder, it is difficult to form a pattern and characters on the surface of the metal card, the metal texture can not be felt, It was made of a light material and could not feel the weight feeling of metal.

따라서, 금속판재로 제작된 금속카드의 중량과 질감을 느낄 수 있는 금속 신용카드의 제안이 절실히 요구되었다.Therefore, a proposal of a metal credit card capable of feeling the weight and texture of a metal card made of a metal plate has been urgently required.

종래에는 등록실용공보 제20-0382725호 "금속박막 플라스틱카드"(선행기술1) 및 공개특허공보 제10-2013-0051906호 "금속카드의 제조방법"(선행기술2)이 제안된 바 있다.In the related art, a registration method for a metal thin card (Prior Art 1) and a method for manufacturing a metal card (Prior Art 2) have been proposed in Japanese Patent Application Laid-Open No. 20-0382725 (Prior Art 1) and 10-2013-0051906.

상기 선행기술1은 합성수지 코어시트의 상,하부에는 코어시트 보다 작은 크기의 금속박막이 부착되어 둘레에는 여백이 형성되고, 코어시트의 상부면 여백에는 안테나코일이 둘레를 따라 설치되어 코어시트 내측에 고정된 IC칩과 연결되며, 코어시트의 상부에는 인쇄층이 형성된 상부 코팅지가 부착되고, 코어시트의 하부면에는 인쇄층이 형성된 하부 코팅지가 부착되어 차례로 적층된 상태에서 열 접착됨을 특징으로 하는 금속박막 플라스틱카드이다.In the prior art 1 , a metal thin film having a size smaller than that of the core sheet is attached to upper and lower portions of the synthetic resin core sheet, margins are formed around the core sheet, antenna coils are installed along the periphery of the upper surface of the core sheet, Wherein a top coated paper having a print layer formed thereon is attached to an upper portion of the core sheet and a lower coated paper having a print layer formed on a lower surface of the core sheet is thermally adhered in a stacked state, It is a thin plastic card.

상기 선행기술2는 안테나가 형성된 인레이시트를 포함하는 플라스틱 시트 복합체 및 금속 박막 복합체를 포함하는 금속 카드의 제조 방법에 있어서, 상기 금속 박막 복합체를 제조하는 단계는, 베이스 필름의 일면에 수지층을 형성하는 단계; 및 상기 수지층의 표면에 스퍼터링 증착 방식으로 200 ~ 1,000 Å 두께의 금속 박막을 형성하는 단계를 포함하는 금속카드의 제조 방법이다.The prior art 2 is a method of manufacturing a metal card including a plastic sheet composite and a metal thin film composite including an inlay sheet on which an antenna is formed, wherein the step of fabricating the metal thin film composite includes forming a resin layer on one surface of the base film ; And forming a metal thin film having a thickness of 200 to 1,000 angstroms on the surface of the resin layer by a sputtering deposition method.

그러나, 상기 선행기술1은 0.02∼0.1mm 정도의 두께를 갖는 얇은 호일 형태의 금속박막(薄膜)을 형성한 기술이고, 상기 선행기술2는 스터퍼링 증착에 의하여 미크론 단위의 얇은 금속박막을 형성한 기술이므로 금속재질이 갖는 중량 감을 느낄 수 없었으므로 결국 무늬만 금속을 표방할 뿐 메탈카드가 갖는 질감이나 무게를 구현할 수 없었다.
However, the prior art 1 is a technique in which a thin foil-shaped metal thin film having a thickness of about 0.02 to 0.1 mm is formed. In the prior art 2 , a thin metal thin film of micron unit is formed by the stir- It was impossible to feel the weight feeling of the metal material. Therefore, the texture and the weight of the metal card could not be realized because the pattern was only the metal.

본 발명은 상기한 문제점을 감안하여 창안한 것으로서, 그 목적은 비철금속인 알루미늄판재와 금속판재가 결합되어 외관이 미려하면서도 메탈카드의 중량 감을 느낄 수 있는 고품위·고품질을 구현한 수 있는 하이브리드 소재의 메탈카드 제조방법 및 하이브리드 소재의 메탈카드를 제공함에 있는 것이다.
SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems, and its object is to provide a metal card of a hybrid material capable of realizing a high quality and high quality that can feel the weight feeling of a metal card while an aluminum plate and a metal plate are combined, And a metal card of a hybrid material.

상기한 목적을 달성하기 위한 본 발명의 특징은, 비철금속인 알루미늄판재(11)의 저면(底面)을 알루미늄 옥사이드(aluminum oxide)로 연마(硏磨)하거나 샌드브라스트(sand blast) 공법으로 거칠게 처리하여 옥사이드처리층(12)을 형성하는 단계; 스테인리스, 동(銅) 및 티타늄 중에서 어느 하나의 소재로 구성된 금속판재(14)의 상면(上面)을 알루미늄 옥사이드(aluminum oxide)로 연마(硏磨)하거나 샌드브라스트(sand blast) 공법으로 거칠게 처리하여 옥사이드처리층(12)을 형성하는 단계; 상기 알루미늄판재(11)와 금속판재(14)의 옥사이드처리층(12)들 사이에 핫멜트접착제(13)가 위치되도록 하여, 가열 및 가압하고 라미네이팅(laminating)하여 카드몸체(10)를 완성하는 단계; 상기 알루미늄판재(11)의 표면을 밀링(milling)가공을 하여 얕은 안내홈(21)을 형성한 후 안내홈(21)의 내부에는 IC칩(20)을 삽입하여 접착제로 부착하는 단계; 상기 알루미늄판재(11)와 금속판재(14)가 접합된 하이브리드 소재의 금속판재를 CNC로 가공하면서 카드의 외형을 따라 절단하여 메탈카드를 완성하는 단계를 포함하는 것을 특징으로 하는 하이브리드 소재의 메탈카드 제조방법에 의하여 달성될 수 있는 것이다.
In order to achieve the above object, a feature of the present invention is to polish the bottom surface of a non-ferrous metal plate 11 with aluminum oxide or to rough To form an oxide treatment layer (12); An upper surface of a metal plate 14 made of any one of stainless steel, copper and titanium is polished with aluminum oxide or roughly treated with a sand blast method To form an oxide treatment layer (12); A step of completing the card body 10 by placing the hot melt adhesive 13 between the aluminum plate material 11 and the oxide treatment layers 12 of the metal plate material 14 and heating and pressing the same and laminating ; A step of milling a surface of the aluminum plate 11 to form a shallow guide groove 21 and then inserting an IC chip 20 into the guide groove 21 and attaching the IC chip 20 with an adhesive; And cutting the metal sheet material of the hybrid material having the aluminum sheet material (11) and the metal sheet material (14) joined to each other along the outer shape of the card while CNC processing the metal sheet material to complete the metal card Can be achieved by a manufacturing method.

이상에서 상술한 제조과정에 의하여 완성된 본 발명의 하이브리드 소재 메탈카드는 알루미늄판재(11) 및 금속판재(14)에 형성된 옥사이드처리층(12)에 의하여 접착면에 이물질의 발생이 전혀 없고, 마찰력이 높은 거친 구조이므로 핫멜트접착제(13)의 접착이 매우 견고하게 이루어져 이질성을 갖는 2장의 금속판재가 매우 견고하게 접착되어 카드를 장기간 사용하더라도 분리되는 등의 폐단을 방지할 수 있는 동시에 상부에 위치한 알루미늄판재(11)가 갖는 비철금속의 특징에 의하여 금속광택이 뛰어나면서도 외관이 미려하여 장식성을 높여줄 수 있고, 하부에 결합된 금속판재에 의하여 내구성이 뛰어나면서도 메탈카드의 무게 감을 줄 수 있는 것으로서 고품위를 느낄 수 있는 고품질의 하이브리드 소재의 메탈카드를 제공할 수 있는 등의 이점이 있다.
The hybrid metal card of the present invention completed by the manufacturing process described above has no foreign matter generated on the bonding surface by the oxide treatment layer 12 formed on the aluminum plate 11 and the metal plate 14, Since the high coarse structure, the hot-melt adhesive 13 is very firmly adhered, so that the two metal plate materials having a heterogeneous property are adhered very firmly to prevent closure such as detachment even if the card is used for a long period of time, (11) is characterized by a non-ferrous metal, the metal luster is excellent, the appearance is good and the decorative property can be enhanced, and the metal plate combined with the lower metal plate provides excellent durability, It is possible to provide a metal card of a high-quality hybrid material that can be used.

도 1은 본 발명에 의한 하이브리드 메탈카드의 분해사시도,
도 2는 본 발명의 제조과정에 의하여 완성된 하이브리드 메탈카드의 사시도,
도 3a ∼ 도 3e는 본 발명에 의한 하이브리드 메탈카드의 제조과정을 순차적으로 나열한 제조공정 단면도.1 is an exploded perspective view of a hybrid metal card according to the present invention,
2 is a perspective view of a hybrid metal card completed by the manufacturing process of the present invention,
FIGS. 3A to 3E are cross-sectional views illustrating a manufacturing process of a hybrid metal card according to an embodiment of the present invention; FIG.

이하, 상기한 목적을 달성하기 위한 바람직한 실시예를 첨부된 도면에 의하여 상세히 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

실시예Example

비철금속인 알루미늄판재(11)의 저면(底面)을 알루미늄 옥사이드(aluminum oxide)로 연마(硏磨)하거나 샌드브라스트(sand blast) 공법으로 거칠게 처리하여 옥사이드처리층(12)을 형성하는 단계를 실시하였다.A step of polishing the bottom surface of the aluminum plate material 11 made of a nonferrous metal with aluminum oxide or roughening the surface with a sand blast technique to form the oxide treatment layer 12 Respectively.

상기 단계의 알루미늄 옥사이드(aluminum oxide)는 전기가마에서 보크사이트를 고온으로 가열 및 가압하여 생산한 알루미나를 사용하였으며, 그 화학적 성분은 산화알루미늄(Al2O3) 99.7중량%, 산화나트륨 (Na2O3) 0,25중량%, 산화철(Fe2O3)0.03중량%, 산화규소(Sio2) 0.02중량%로 구성되어 있으며, 그 특성은 높은 강도, 내열성, 내화학성 및 높은 인성으로 인하여 연마용 공구제작, 코팅, 세라믹, 랩핑, 표면처리, 도장전처리 그리고 고급 내화재료 등에 사용되는 것을 사용하였으며, 본 발명에서는 샌드브라스트(sand blast) 공법으로 알루미늄 옥사이드를 분사하여 알루미늄판재(11)의 하부면을 처리하였다.The aluminum oxide used in the above step was alumina produced by heating and pressurizing bauxite at a high temperature in an electric kiln. Chemical components thereof were 99.7 wt% of aluminum oxide (Al 2 O 3 ), sodium oxide (Na 2 O 3 ), 0.03% by weight of iron oxide (Fe 2 O 3 ), and 0.02% by weight of silicon oxide (Sio 2 ), and the characteristics thereof are excellent because of high strength, heat resistance, chemical resistance and high toughness In the present invention, aluminum oxide is sprayed by a sand blast method to form a lower part of the aluminum plate 11, Lt; / RTI >

이어서, 금속판재(14)의 상면을 알루미늄 옥사이드(aluminum oxide)로 연마(硏磨)하거나 샌드브라스트(sand blast) 공법으로 금속판재의 상면을 거칠게 처리하여 옥사이드처리층(12)을 형성하는 단계를 실시하였다.Then, the upper surface of the metal plate 14 is polished with aluminum oxide or the upper surface of the metal plate is roughened by a sand blast method to form the oxide treatment layer 12 Respectively.

본 발명에서 사용된 금속판재(14)는 스테인리스, 동(銅) 및 티타늄 중에서 어느 하나를 선택하여 사용하였다, 그러나, 상기 소재들의 합금을 사용할 수 있는 것으로서 비철금속인 알루미늄판재(11) 보다 중량이 무거운 소재를 사용하는 것이 바람직하다.The metal plate material 14 used in the present invention is selected from stainless steel, copper and titanium. However, it is possible to use the alloys of the above materials, It is preferable to use a material.

이어서, 상기 알루미늄판재(11)와 금속판재(14)의 옥사이드처리층(12)들 사이에 핫멜트(hot melt)접착제(13)가 위치되도록 하여, 가열 및 가압하는 라미네이팅(laminating) 단계를 실시하여 카드몸체(10)를 완성하였다.A hot melt adhesive 13 is then placed between the aluminum plate material 11 and the oxide treatment layers 12 of the metal plate material 14 to perform a laminating step of heating and pressing Thereby completing the card body 10.

상기 핫멜트 접착제는 에틸렌 초산비닐(EVA), 폴리아미드, 폴리에스테르, 아크릴 등을 주원료로 하는 열가소성 수지 접착제를 사용하였으며, 가열되면 용융되었 다가 식으면 급속히 경화되는 접착제를 사용하였다.As the hot melt adhesive, a thermoplastic resin adhesive mainly composed of ethylene-vinyl acetate (EVA), polyamide, polyester, acrylic, or the like was used, and an adhesive which melts when heated and rapidly hardens when cooled is used.

상기 단계에서는 알루미늄판재(11) 및 금속판재(14)에 형성된 옥사이드처리층(12)에 의하여 이물질의 발생이 없고, 마찰력이 높은 거친 구조이므로 핫멜트접착제(13)의 접착이 매우 강하게 이루어지는 견고한 구조의 카드몸체(10)를 완성할 수 있는 것으로서 이질성을 갖는 2장의 금속판재가 매우 견고하게 접착되어 카드를 장기간 사용하더라도 분리되는 등의 폐단을 방지할 수 있는 것이다.In this step, there is no generation of foreign matter by the oxide treatment layer 12 formed on the aluminum plate 11 and the metal plate 14, and since the coarse structure has a high frictional force, the adhesion of the hot melt adhesive 13 is very strong It is possible to complete the card body 10 and the two metal plate materials having heterogeneity are adhered very firmly to prevent closure such as disconnection even if the card is used for a long period of time.

이어서, 상기 알루미늄판재(11)의 표면을 CNC로 밀링(milling)가공하여 0.15∼0.3MM 깊이의 얕은 안내홈(21)을 형성하고, 안내홈(21)의 내부에 IC칩(20)을 삽입하여 접착제로 부착하는 단계를 실시하였다.The surface of the aluminum plate 11 is milled with CNC to form a shallow guide groove 21 having a depth of 0.15 to 0.3 mm and an IC chip 20 is inserted into the guide groove 21 And then adhered with an adhesive.

이어서, 상기 알루미늄판재(11)와 금속판재(14)가 접합된 하이브리드 소재의 카드몸체(10)를 CNC로 가공하면서 카드의 외형을 따라 절단하여 메탈카드의 제조를 완료하였다.Next, the card body 10 of the hybrid material in which the aluminum plate 11 and the metal plate 14 are joined is cut along the outer shape of the card while CNC processing is performed to complete the manufacture of the metal card.

전술한 제조과정에 의하여 완성된 본 발명의 하이브리드 소재의 메탈카드는, 알루미늄판재(11)의 저면에는 알루미늄 옥사이드(aluminum oxide)로 표면을 거칠게 처리한 옥사이드처리층(12)이 형성되고, 금속판재(14)의 상면에는 알루미늄 옥사이드로 거칠게 표면 처리한 옥사이드처리층(12)이 형성되며, 알루미늄판재(11)와 금속판재(14)의 옥사이드처리층(12)들 사이에는 핫멜트접착제(13)가 위치되어 열 접착된 구성으로 되어 있다.In the metal card of the hybrid material of the present invention completed by the above-described manufacturing process, the oxide treatment layer 12 roughly treated with aluminum oxide is formed on the bottom surface of the aluminum plate 11, A hot-melt adhesive 13 is formed between the aluminum plate 11 and the oxide-treated layers 12 of the metal plate 14. The hot- And are thermally adhered to each other.

한편, 경우에 따라서는 도 1 내지는 도 2에서 도시한 바와 같이, 알루미늄판재(11)의 표면에는 CNC 가공으로 입체 패턴을 이루는 문양(10a) 및 문자(10b)를 가공하는 단계가 더 포함되도록 구성하여 카드의 외관을 미려하게 형성하고, 문자정보를 나타낼 수 있도록 구성할 수도 있다. 이때, 카드의 표면에 형성되는 문자(10b)는 레이저가공으로 다양한 서체를 이루도록 정밀 가공하는 것이 바람직하다.On the other hand, as shown in Fig. 1 or Fig. 2, the surface of the aluminum plate 11 may further include a step of machining the pattern 10a and the character 10b forming a three-dimensional pattern by CNC machining So that the appearance of the card can be formed to be beautiful, and the character information can be displayed. At this time, the characters 10b formed on the surface of the card are preferably subjected to precision processing so as to form various fonts by laser processing.

경우에 따라서는 카드몸체(10)의 외부면에는 2액형 우레탄도료를 코팅한 후 경화시켜 메탈카드의 표면이 금속 느낌을 주면서도 보다 부드러운 느낌을 줄 수 있도록 스프레이 도장하여 처리할 수도 있다.In some cases, the outer surface of the card body 10 may be coated with a spray coating so that the surface of the metal card is coated with a two-component urethane coating and cured to provide a metal feel while providing a softer feel.

상기 2액형(二液型) 우레탄도료는 도료에서 주제(主劑)와 경화제의 혼합으로 일어난 가교 반응에 의해 그물눈 구조로 경화가 이루어지는 타입의 도료로 가교 반응은 온도가 높을수록 빨라지고, 40~80℃에서 건조되며, 열 경화형 도료와 같은 치밀한 그물눈 구조를 이루기 때문에 광택이 좋으면서도 경도, 가소성, 내마모성, 내 약품성, 내 오염성 등의 도막 성능이 우수한 특징이 있고 주제와 경화제의 배합비율 따라서 가죽의 표면과 같은 부드러운 감촉을 줄 수 있다.The two-part type (two-part) urethane paint is a type of paint which is cured in a net structure by a cross-linking reaction caused by a mixture of a main agent and a curing agent in the coating material. The crosslinking reaction accelerates at a higher temperature, ° C, and has a fine mesh structure similar to that of a thermosetting paint. Therefore, it is excellent in gloss and excellent in coating performance such as hardness, plasticity, abrasion resistance, chemical resistance and stain resistance, And the like.

또한, 경우에 따라서는 상기 알루미늄판재(11)의 표면에는 아노다이징(Anodizing) 처리에 의한 양극산화피막을 형성하고 염료를 착색(着色)한 후 열처리하는 건조단계를 실시하여 내식성, 내마모성이 양호하고 금속광택이 뛰어나면서도 장식성이 높은 미려한 카드를 구현할 수 있다.In some cases, an anodic oxidation film is formed on the surface of the aluminum plate 11, anodizing treatment is performed, and the dye is colored and then subjected to a heat treatment to obtain a metal plate having good corrosion resistance and abrasion resistance, It is possible to implement a beautiful card with high gloss and high decoration.

상기 알루미늄판재(11)의 표면을 아노다이징(Anodizing) 처리하는 과정은 다음과 같다.The process of anodizing the surface of the aluminum plate 11 is as follows.

먼저, 알루미늄판재(11)를 깨끗하게 세척한 후 황산 전해액이 담겨진 전해조(電解槽)에 넣고, 전해(電解)작업을 하여 성형물의 표면에 양극산화피막을 형성하는 단계를 실시하였다.First, the aluminum plate material 11 was cleaned and then placed in an electrolytic cell containing an electrolytic solution of sulfuric acid, and an electrolytic process was performed to form an anodic oxide film on the surface of the formed product.

상기 전해단계는 알루미늄판재(11)를 양극으로 하여 황산용액이 담겨진 전해조(電解槽)에 전류를 흘러 넣으면 이때 발생되는 전하(電荷)에 의하여 알루미늄 판재의 표면에 산소를 발생시켜 두꺼운 산화피막을 형성하고, 양극산화피막은 다공질(多孔質) 및 섬유질로 형성되어 염료의 침투가 가능할 뿐 아니라 전기절연성이 높고, 내식성, 내마모성이 양호한 산화피막이 형성된다.In the electrolysis step, when an electric current flows into an electrolytic cell (electrolytic cell) containing a sulfuric acid solution with the aluminum plate 11 as an anode, oxygen is generated on the surface of the aluminum sheet material by the charge (charge) generated at this time to form a thick oxide film And the anodic oxide film is formed of porous and fibrous materials, so that it is possible not only to penetrate the dye but also to form an oxide film having high electrical insulation property and good corrosion resistance and abrasion resistance.

이어서, 다공질(多孔質)로 형성된 양극산화피막에 염료를 칠하여 색상을 입히는 염색단계를 실시한 후 염색이 완료된 알루미늄 판재(11)를 컨베이어를 통해 이송시키면서 60∼75℃의 온도로 열처리하는 건조단계를 실시하여 알루미늄판재(11)의 아노다이징 처리를 완성한 것이다.Next, a dyeing step of applying a color to the anodic oxidation coating formed with a porous material is performed, followed by a drying step of heat-treating the aluminum plate 11, which has been dyed, through a conveyor at a temperature of 60 to 75 ° C Thereby completing the anodizing treatment of the aluminum plate material 11. [

이상에서는 본 발명의 바람직한 실시예에 대하여 도시하고 또한 설명하였으나, 본 발명은 상기한 실시예에 한정되지 아니하며, 청구범위에서 청구하는 본 발명의 요지를 벗어남이 없이 당해 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 누구든지 다양한 변형 실시가 가능한 것은 물론이고, 그와 같은 변경은 기재된 청구범위 내에 있게 된다.
While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but many variations and modifications may be made without departing from the scope of the invention. It will be understood by those skilled in the art that various changes may be made and equivalents may be resorted to without departing from the scope of the appended claims.

10 : 카드몸체 11 : 알루미늄판재
11a : 문양 11b : 문자
12 : 옥사이드처리층 13 : 핫멜트접착제
14 : 금속판재 20 : IC칩
21 : 안내홈10: Card body 11: Aluminum plate
11a: Glyph 11b: Character
12: oxide treatment layer 13: hot melt adhesive
14: metal plate 20: IC chip
21: Guide groove

Claims (5)

비철금속인 알루미늄판재(11)의 저면을 알루미늄 옥사이드(aluminum oxide)로 연마(硏磨)하거나 샌드브라스트(sand blast) 공법으로 거칠게 처리하여 옥사이드처리층(12)을 형성하는 단계;
스테인리스, 동(銅) 및 티타늄 중에서 어느 하나의 소재로 구성된 금속판재(14)의 상면을 알루미늄 옥사이드(aluminum oxide)로 연마(硏磨)하거나 샌드브라스트(sand blast) 공법으로 거칠게 처리하여 옥사이드처리층(12)을 형성하는 단계;
상기 알루미늄판재(11)와 금속판재(14)의 옥사이드처리층(12)들 사이에 핫멜트(hot melt)접착제(13)가 위치되도록 하고, 가열 및 가압하는 라미네이팅(laminating)하는 단계를 실시하여 카드몸체(10)를 완성하는 단계;
상기 알루미늄판재(11)의 표면을 밀링(milling)가공을 하여 얕은 안내홈(21)을 형성한 후 안내홈(21)의 내부에는 IC칩(20)을 삽입하여 접착제로 부착하는 단계;
상기 알루미늄판재(11)와 금속판재(14)가 접합된 하이브리드 소재의 금속판재를 CNC로 가공하면서 카드의 외형을 따라 절단하여 메탈카드를 완성하는 단계를 포함하는 것을 특징으로 하는 하이브리드 소재의 메탈카드 제조방법.
A step of polishing the bottom surface of the aluminum plate material 11 made of a nonferrous metal with aluminum oxide or roughening the surface with a sand blast technique to form an oxide treatment layer 12;
An upper surface of a metal plate 14 made of any one of stainless steel, copper and titanium is polished with aluminum oxide or roughly treated with a sand blast method, Forming a layer (12);
A hot melt adhesive 13 is placed between the aluminum plate material 11 and the oxide layer 12 of the metal plate material 14 and laminating is performed by heating and pressing, Completing the body 10;
A step of milling a surface of the aluminum plate 11 to form a shallow guide groove 21 and then inserting an IC chip 20 into the guide groove 21 and attaching the IC chip 20 with an adhesive;
And cutting the metal sheet material of the hybrid material having the aluminum sheet material (11) and the metal sheet material (14) joined to each other along the outer shape of the card while CNC processing the metal sheet material to complete the metal card Gt;
제 1항에 있어서,
상기 알루미늄판재(11)의 표면에는 CNC 가공으로 다양한 패턴을 이루는 문양(11a) 및 문자(11b)를 가공하는 단계가 더 포함되도록 구성한 것을 특징으로 하는 하이브리드 소재의 메탈카드 제조방법.
The method according to claim 1,
Further comprising the step of machining the pattern (11a) and the characters (11b) forming various patterns by CNC machining on the surface of the aluminum plate material (11).
제 1항에 있어서,
상기 카드몸체(10)의 외부면에는 2액형 우레탄도료를 코팅한 후 경화시키는 단계가 더 포함되어, 메탈카드의 표면이 부드러운 느낌을 줄 수 있도록 처리한 것을 특징으로 하는 하이브리드 소재의 메탈카드 제조방법.
The method according to claim 1,
The method of manufacturing a metal card of a hybrid material according to claim 1, further comprising a step of coating a two-component urethane paint on the outer surface of the card body (10) and then curing the surface of the card body .
제1항에 있어서, 상기 알루미늄판재(11)의 표면에는,
상기 알루미늄판재(11)를 깨끗하게 세척한 후 황산 전해액이 담겨진 전해조(電解槽)에 넣어, 전해(電解)작업을 실시하여 성형물의 표면에 양극산화피막을 형성하고, 염료를 착색(着色)한 후 열처리하는 건조단계를 실시하는 아노다이징(Anodizing) 처리 단계가 더 포함된 것을 특징으로 하는 하이브리드 소재의 메탈카드 제조방법.
2. The aluminum plate member according to claim 1,
After the aluminum plate 11 is thoroughly cleaned, the aluminum plate 11 is placed in an electrolytic bath containing an electrolytic solution of sulfuric acid, electrolytic (electrolytic) work is performed to form an anodic oxide film on the surface of the molded product, And an anodizing treatment step of performing a drying step of heat treatment.
알루미늄판재(11)의 저면에는 알루미늄 옥사이드(aluminum oxide)로 표면 처리한 옥사이드처리층(12)이 형성되고,
금속판재(14)의 상면에는 알루미늄 옥사이드로 표면 처리한 옥사이드처리층(12)이 형성되며,
알루미늄판재(11)와 금속판재(14)의 옥사이드처리층(12)들 사이에는 핫멜트접착제(13)가 위치되어 열 접착된 것을 특징으로 하는 하이브리드 소재의 메탈카드,An oxide layer 12, which is surface-treated with aluminum oxide, is formed on the bottom surface of the aluminum plate 11,
On the upper surface of the metal plate 14 is formed an oxide-treated layer 12 surface-treated with aluminum oxide,
A metal card of a hybrid material, characterized in that a hot melt adhesive (13) is placed between the aluminum plate material (11) and the oxide treatment layers (12) of the metal plate material (14)
KR1020160143345A 2016-10-31 2016-10-31 a metal credit card of hybrid material way and manufacturing method metal credit card of hybrid material way KR101983028B1 (en)