KR20180017794A - Anode Active Materials for Magnesium Secondary Battery and Magnesium Secondary Battery Using Thereof - Google Patents

Anode Active Materials for Magnesium Secondary Battery and Magnesium Secondary Battery Using Thereof Download PDF

Info

Publication number
KR20180017794A
KR20180017794A KR1020160102175A KR20160102175A KR20180017794A KR 20180017794 A KR20180017794 A KR 20180017794A KR 1020160102175 A KR1020160102175 A KR 1020160102175A KR 20160102175 A KR20160102175 A KR 20160102175A KR 20180017794 A KR20180017794 A KR 20180017794A
Authority
KR
South Korea
Prior art keywords
negative electrode
active material
secondary battery
silicon
magnesium secondary
Prior art date
Application number
KR1020160102175A
Other languages
Korean (ko)
Inventor
송승완
뉴엔단티엔
김재람
Original Assignee
충남대학교산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 충남대학교산학협력단 filed Critical 충남대학교산학협력단
Priority to KR1020160102175A priority Critical patent/KR20180017794A/en
Publication of KR20180017794A publication Critical patent/KR20180017794A/en

Abstract

The present invention provides a novel negative electrode active material containing Si for a magnesium secondary battery. The negative electrode active material of the present invention has an electrochemical reaction activity with magnesium ions, is capable of reversible charging and discharging by reversible magnetization and demagnetization with magnesium ions, has high capacity and high stability, thereby being advantageous for commercialization.

Description

마그네슘 이차전지용 음극활물질 및 이를 포함하는 마그네슘 이차전지{Anode Active Materials for Magnesium Secondary Battery and Magnesium Secondary Battery Using Thereof}BACKGROUND OF THE INVENTION 1. Field of the Invention [0001] The present invention relates to an anode active material for a magnesium secondary battery, and an anode active material containing the magnesium secondary battery,

본 발명은 마그네슘 이차전지용 음극활물질 및 이를 포함하는 마그네슘 이차전지에 관한 것으로, 상세하게, 고효율을 가지며 안정적 구동이 가능한 마그네슘 이차전지용 음극활물질에 관한 것이다. The present invention relates to a negative electrode active material for a magnesium secondary battery and a magnesium secondary battery including the same. More particularly, the present invention relates to a negative active material for a magnesium secondary battery capable of stable operation with high efficiency.

휴대폰, 노트북을 비롯하여 전기자동차 등까지 이차전지의 활용 분야가 확대됨에 따라, 에너지 저장 장치의 고용량화에 대한 요구가 높아지고 있다.2. Description of the Related Art [0002] As the application fields of secondary batteries such as mobile phones, notebooks, and electric vehicles are expanded, demands for higher capacity of energy storage devices are increasing.

이에 따라, 차세대 이차전지로, 리튬 이차전지, 니켈-카드뮴 전지, 니켈-수소 전지 및 니켈 아연등의 종래 이차전지 대비 보다 친환경적이고, 안정성이 우수하며, 자원이 풍부하고, 저가와 고용량화가 가능하여 특히 중대형 전지로 활용 가능한 마그네슘 이차전지에 대한 연구가 이루어지고 있다. As a result, the next-generation secondary battery is more environmentally friendly, superior in stability, rich in resources, low in cost and high in capacity compared to conventional secondary batteries such as lithium secondary batteries, nickel-cadmium batteries, nickel-hydrogen batteries and nickel zinc Especially, a magnesium secondary battery which can be used as a middle- or large-sized battery has been studied.

마그네슘 이차전지는 마그네슘 이온이 양극 활물질에 삽입-탈리되며 전자를 이동시켜 충방전되는 이차전지이다. 마그네슘 이차전지에서 음극으로는 마그네슘 금속 판이, 양극으로는 Chevrel-phase 양극활물질 소재가, 전해액으로는 알킬 마그네슘 할라이드 전해질인 그리냐드 시약(Grignard solutions)이 상용화 가능성 측면에서 주목되고 있다.The magnesium secondary battery is a secondary battery in which magnesium ions are inserted into and separated from the cathode active material and charged and discharged by moving electrons. In the magnesium secondary battery, a magnesium metal plate is used as an anode, a chevrel-phase cathode active material is used as an anode, and Grignard solutions, which is an alkyl magnesium halide electrolyte as an electrolyte, are attracting attention in view of commercialization.

마그네슘 이차전지는 Chevrel-phase 양극활물질에 의해 가역적인 충방전 구현이 확보된 2000년대에 들어서야 실질적인 연구가 시작되었을 뿐이며, 현재 리튬 이온 전지의 절반 이하의 수준에 불과한 에너지 밀도만이 구현되는 수준으로, 새로운 활물질 소재, 전해질 물질, 집전체등의 개발이 절실히 요구되고 있다. In the 2000s, when the reversible charging and discharging was achieved by the Chevrel-phase cathode active material, the magnesium secondary battery only started to be practically studied. At present, only the energy density of less than half of the lithium ion battery is realized, Development of new active material, electrolytic material, current collector, and the like are urgently required.

그러나, 마그네슘 이차전지에 대한 대부분의 연구가 미국 등록특허 제6713213호나 일본 공개특허 제2007-188709호와 같이 전해질 분야나, 대한민국 공개특허 제2015-0033787호와 같이 양극활물질 분야에 집중되어 있으며, 마그네슘 이차전지의 음극 활물질에 대한 연구는 거의 미미한 실정이다.  However, most of the studies on magnesium secondary batteries are concentrated in the field of electrolytes as in U.S. Patent No. 6713213 or 2007-188709 and in the field of cathode active materials as disclosed in Korean Patent Laid-Open Publication No. 2015-0033787, The study on the anode active material of the secondary battery is almost insignificant.

미국 등록특허 제6713213호United States Patent No. 6713213 일본 공개특허 제2007-188709호Japanese Patent Application Laid-Open No. 2007-188709 대한민국 공개특허 제2015-0033787호Korea Patent Publication No. 2015-0033787

본 발명의 목적은 신규한 마그네슘 이차전지용 음극활물질 및 이를 포함하는 마그네슘 이차전지를 제공하는 것이다. An object of the present invention is to provide a novel negative electrode active material for a magnesium secondary battery and a magnesium secondary battery containing the same.

본 발명에 따른 음극활물질은 마그네슘 이차전지용 음극활물질이며, 실리콘(Si)을 함유한다.The negative electrode active material according to the present invention is an anode active material for a magnesium secondary battery and contains silicon (Si).

본 발명의 일 실시예에 따른 음극활물질에 있어, 상기 실리콘은 진성 반도체 실리콘(intrinsic silicon) 또는 n형 도펀트나 p형 도펀트로 도핑된 익스트린직(extrinsic) 실리콘일 수 있다.In the anode active material according to an embodiment of the present invention, the silicon may be intrinsic silicon or an extrinsic silicon doped with an n-type dopant or a p-type dopant.

본 발명의 일 실시예에 따른 음극활물질에 있어, 상기 n형 도펀트는 인(P), 비소(As) 및 안티몬(Sb)에서 하나 또는 둘 이상 선택되며, p형 도펀트는 붕소(B), 알루미늄(Al) 및 인듐(In)에서 하나 또는 둘 이상 선택될 수 있다.In the anode active material according to an embodiment of the present invention, the n-type dopant is selected from one or more of phosphorus (P), arsenic (As) and antimony (Sb) (Al) and indium (In).

본 발명의 일 실시예에 따른 음극활물질에 있어, 상기 실리콘은 막(film), 웨이퍼(wafer), 와이어(wire) 및 입자(particle)에서 하나 또는 둘 이상 선택되는 형상일 수 있다.In the negative electrode active material according to an embodiment of the present invention, the silicon may be a shape selected from one or more of a film, a wafer, a wire, and particles.

본 발명은 상술한 마그네슘 이차전지용 음극활물질을 포함하는 마그네슘 이차전지용 음극을 포함한다.The present invention includes a negative electrode for a magnesium secondary battery including the above-described negative electrode active material for a magnesium secondary battery.

본 발명의 일 실시예에 따른 음극은 음극 집전체; 상기 음극 집전체 상 위치하는 음극활물질층을 포함하며, 상기 음극활물질층은 실리콘을 포함하는 음극활물질, 도전재 및 바인더를 함유할 수 있다.A cathode according to an embodiment of the present invention includes a cathode current collector; And a negative electrode active material layer positioned on the negative electrode collector, and the negative electrode active material layer may contain a negative electrode active material including silicon, a conductive material, and a binder.

본 발명은 상술한 음극을 포함하는 마그네슘 이차전지를 포함한다.The present invention includes a magnesium secondary battery including the above-described negative electrode.

본 발명의 일 실시예에 따른 마그네슘 이차전지에 있어, 상기 음극은 충전 상태 기준 MgxSi(0<x≤2인 실수)를 함유할 수 있다.In the magnesium secondary battery according to an embodiment of the present invention, the negative electrode may contain a charge state reference Mg x Si (0 <x? 2).

본 발명의 일 실시예에 따른 마그네슘 이차전지는 마그네슘 이온의 가역적인 삽입과 탈리가 가능한 전이금속화합물을 양극활물질로 포함하는 양극 및 전해액을 더 포함할 수 있다.The magnesium secondary battery according to an embodiment of the present invention may further include a cathode and an electrolyte including a transition metal compound capable of reversible insertion and desorption of magnesium ions as a cathode active material.

본 발명의 일 실시예에 따른 마그네슘 이차전지는 상기 음극과 양극 사이에 개재된 분리막을 더 포함할 수 있다.The magnesium secondary battery according to an embodiment of the present invention may further include a separation membrane interposed between the cathode and the anode.

본 발명의 일 실시예에 따른 마그네슘 이차전지에 있어, 상기 양극활물질은 보론 (B), 스칸듐(Sc), 타이타늄(Ti), 바나듐(V), 크로뮴(Cr), 망간(Mn), 철(Fe), 코발트(Co), 니켈(Ni), 구리(Cu), 아연(Zn), 실리콘 (Si), 주석 (Sn), 몰리브데넘(Mo), 나이오븀(Nb) 및 루테늄(Ru)에서 하나 이상 선택되는 원소의 산화물, 할로겐화물 또는 칼코젠화물을 포함할 수 있다.In the magnesium secondary battery according to an embodiment of the present invention, the cathode active material may be selected from the group consisting of boron (B), scandium (Sc), titanium (Ti), vanadium (V), chromium (Cr), manganese Fe, cobalt, nickel, copper, zinc, silicon, tin, molybdenum, niobium and ruthenium, Or oxides, halides or chalcogenides of the element (s) selected from one or more of the elements in the composition.

본 발명에 따른 음극활물질은 마그네슘 이온과 전기화학적 반응 활성을 가지며, 마그네슘 이온과의 가역적인 삽입(magnesiation)및 탈리(demagnesiation)가 이루어져 가역적인 충전 및 방전이 가능하고, 고용량 및 고안정성을 가지며, 상용화에 유리한 장점이 있다.The negative electrode active material according to the present invention has an electrochemical reaction activity with magnesium ions and is capable of reversible charging and discharging by reversible magnesiation and demagnetization with magnesium ions and has high capacity and high stability, There is an advantage in commercialization.

본 발명에 따른 마그네슘 이차전지는 탈 리튬 전지로, 상용화에 유리하며, 우수한 충방전 특성과 고용량 및 고안정성을 가지며, 중대형 에너지 저장장치 및 전기자동차 배터리등 다양한 분야에 응용 가능한 장점이 있다.  The magnesium secondary battery according to the present invention is a lithium lithium battery which is advantageous for commercialization, has excellent charge / discharge characteristics, high capacity and high stability, and is applicable to various fields such as medium and large-sized energy storage device and electric automobile battery.

도 1은 본 발명의 실시예에서 제조된 전기화학셀의 CV(cyclic voltammetry) 측정 결과를 도시한 도면이며,
도 2는 본 발명의 실시예에서 제조된 전기화학셀의 충방전 테스트 결과를 도시한 도면이다.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a graph showing a cyclic voltammetry (CV) measurement result of an electrochemical cell manufactured in an embodiment of the present invention,
FIG. 2 is a graph showing a charge / discharge test result of an electrochemical cell manufactured in an embodiment of the present invention. FIG.

이하 본 발명의 마그네슘 이차전지용 음극활물질 및 마그네슘 이차전지를 상세히 설명한다. 이때, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다. Hereinafter, the negative active material for a magnesium secondary battery and the magnesium secondary battery of the present invention will be described in detail. Hereinafter, the technical and scientific terms used herein will be understood by those skilled in the art without departing from the scope of the present invention. Descriptions of known functions and configurations that may be unnecessarily blurred are omitted.

본 출원인은 마그네슘 금속과 같이, 취급이 어렵고 상대적으로 고가인 판이나 박막 기반 금속 음극이 아닌, 입자 기반 음극의 구현이 가능하며, 넓은 비표면적을 가져 전기화학적 반응이 수행되는 활성 면적이 크고, 저비용으로 용이하게 제조 가능하면서도, 고용량 및 우수한 안정성을 가지며, 상용화에 유리한 새로운 음극활물질을 개발하기 위해 각고의 노력을 기울인 결과, 새로운 음극활물질을 발견하여 본 발명을 출원하기에 이르렀다. The present applicant has succeeded in realizing a particle-based negative electrode, which is not a plate or a thin-film-based metal negative electrode, which is difficult to handle and relatively expensive, such as magnesium metal, has a large specific surface area and has a large active area where an electrochemical reaction is performed, As a result of efforts to develop a new negative electrode active material having a high capacity and excellent stability and being advantageous for commercialization. As a result, a new negative active material has been discovered and the present invention has been filed.

본 발명에 따른 마그네슘 이차전지용 음극활물질은 실리콘(Si)을 함유한다. 상세하게, 본 발명에 따른 마그네슘 이차전지용 음극활물질은 반도체 실리콘(Si)을 함유하며, 음극활물질로 함유되는 실리콘은 진성 반도체 실리콘(intrinsic silicon), 불순물로 도핑된 실리콘인 익스트린직 실리콘(extrinsic silicon) 또는 이들의 혼합물을 포함할 수 있다.The negative active material for a magnesium secondary battery according to the present invention contains silicon (Si). In detail, the negative electrode active material for a magnesium secondary battery according to the present invention contains semiconductor silicon (Si), and the silicon contained in the negative active material includes intrinsic silicon, extrinsic silicon (Si) doped with impurities, ) Or mixtures thereof.

상세하게, 진성 반도체 실리콘(이하, 인트린직 실리콘)은 불순물이 의도적으로 도핑되지 않은 실리콘을 의미할 수 있으며, 순수한 실리콘을 의미할 수 있다. 일 예로, 순수한 실리콘은 99%, 구체적으로 99.9%, 보다 구체적으로 99.99% 이상의 순도를 갖는 실리콘을 의미할 수 있다. 이때, 인트린직 실리콘이 실리콘의 제조방법상 한계에 의해 갖는 불가피한 불순물을 포함할 수 있음은 물론이다.In detail, intrinsic semiconductor silicon (hereinafter referred to as &quot; intrinsic silicon &quot;) may mean silicon in which impurities are not intentionally doped, and may mean pure silicon. By way of example, pure silicon may mean silicon having a purity of 99%, specifically 99.9%, more specifically 99.99% or more. It goes without saying that the intrinsic silicon may include inevitable impurities due to limitations in the manufacturing method of silicon.

익스트린직 실리콘(extrinsic silicon)은 3족 원소 및/또는 5족 원소로 의도적으로 도핑된 실리콘을 의미할 수 있다. 즉, 익스트린직 실리콘은 n형 도펀트(n-type dopant) 및/또는 p형 도펀트(p-type dopant)로 도핑된 실리콘을 의미할 수 있다. n형 도펀트로 도핑된 실리콘은 익스트린직 n형 실리콘으로, p형 도펀트로 도핑된 실리콘은 익스트린직 p형 실리콘으로, n형 도펀트와 p형 도펀트로 모두 도핑된 경우, 상대적으로 더 주가된 도펀트(즉, 상대적으로 도핑 농도가 더 높은 도펀트)의 타입과 동일한 타입의 익스트린직 실리콘으로 통칭될 수 있다. 익스트린직 실리콘의 경우, 마그네슘 이온에 대해 전기화학적인 활성을 가져, 가역적인 마그네슘화 및 탈마그네슘화가 발생하면서도, 음극활물질 자체의 저항을 감소시킬 수 있어 보다 유리하다.Extrinsic silicon may mean a silicon that is intentionally doped with a Group 3 element and / or a Group 5 element. That is, extrinsic silicon may refer to silicon doped with an n-type dopant and / or a p-type dopant. Silicon doped with an n-type dopant is extrinsic n-type silicon, and silicon doped with a p-type dopant is extrinsic p-type silicon. When doped with an n-type dopant and a p-type dopant, May be referred to as the same type of extinctional silicon as the type of dopant (i.e., the dopant with a relatively higher doping concentration). In the case of the extinosilicone, it has an electrochemical activity with respect to magnesium ions, and it is more advantageous to reduce the resistance of the negative electrode active material itself, while generating reversible magnesiumation and demagnetization.

본 발명의 일 실시예에 따른 마그네슘 이차전지용 음극활물질이 익스트린직 실리콘을 함유하는 경우, 도펀트의 도핑 농도(atoms/cm3)는 특별히 한정되는 것은 아니나, 1012 오더(order) 내지 1020 오더(order)의 범주일 수 있다. 구체적으로, 익스트린직 p형 실리콘의 p형 도펀트 도핑 농도(atoms/cm3)는 특별히 한정되는 것은 아니나 1x1012 내지 2x1020일 수 있다. 또한, 익스트린직 n형 실리콘의 n형 도펀트 도핑 농도(atoms/cm3)는 특별히 한정되는 것은 아니나 1x1014 내지 1x1020일 수 있다. In the case where the negative electrode active material for a magnesium secondary battery according to an embodiment of the present invention contains extrinsic silicon, the doping concentration (atoms / cm 3 ) of the dopant is not particularly limited, but may be in the range of 10 12 orders to 10 20 orders (order). Specifically, the doping concentration (atoms / cm 3 ) of the p-type dopant of the extrinsic p-type silicon is not particularly limited but may be 1 × 10 12 to 2 × 10 20 . The doping concentration (atoms / cm 3 ) of the n-type dopant in the ex trin n-type silicon is not particularly limited but may be 1 × 10 14 to 1 × 10 20 .

익스트린직 실리콘의 도펀트로, n형 도펀트는 인(P), 비소(As) 및 안티몬(Sb)에서 하나 또는 둘 이상 선택된 원소를 포함할 수 있으며, p형 도펀트는 붕소(B), 알루미늄(Al) 및 인듐(In)에서 하나 또는 둘 이상 선택되는 원소를 포함할 수 있다. 실질적으로, n형 도펀트는 인, 비소 또는 인과 비소일 수 있으며, p형 도펀트는 붕소일 수 있다.The n-type dopant may include at least one selected from phosphorus (P), arsenic (As) and antimony (Sb), and the p-type dopant may include boron (B), aluminum Al, and indium (In). Substantially, the n-type dopant can be phosphorus, arsenic or phosphorus and arsenic, and the p-type dopant can be boron.

결정학적으로, 마그네슘 이차전지용 음극활물질에 함유되는 실리콘은 단결정체, 다결정체, 비정질 또는 결정질과 비정질의 혼합상일 수 있다. Crystalline, the silicon contained in the negative electrode active material for a magnesium secondary battery may be a monocrystalline, polycrystalline, amorphous or a mixed phase of crystalline and amorphous.

형태적으로, 마그네슘 이차전지용 음극활물질에 함유되는 실리콘은 막(film), 웨이퍼(wafer), 와이어(wire) 및 입자(particle)에서 하나 또는 둘 이상 선택되는 형상일 수 있다. Formally, the silicon contained in the negative electrode active material for a magnesium secondary battery may be a shape selected from one or more of a film, a wafer, a wire and a particle.

구체적으로, 막 형상의 실리콘은 실리콘 단결정 막, 실리콘 다결정체 막, 비정질 실리콘 막, 비정질상과 결정질 상을 모두 포함하는 혼합상의 막을 포함할 수 있다. 막 형상의 실리콘은 박막(두께 5nm 내지 1000nm) 내지 후막(1000nm를 초과하는 두께)을 포함할 수 있으며, 실리콘과 상이한 이종 기재(일 예로, 집전체) 상 위치하는 코팅막 또는 적층막을 포함할 수 있다. 막 형상의 실리콘은 치밀 막 또는 다공 막일 수 있다. 다공막은 나노 다공 구조를 포함할 수 있으며, 치밀 막은 의도적으로 기공이 형성되지 않은 막을 의미할 수 있다. Specifically, the film-shaped silicon may include a silicon single crystal film, a silicon polycrystalline film, an amorphous silicon film, and a mixed-phase film including both an amorphous phase and a crystalline phase. The film-shaped silicon may include a thin film (thickness of 5 nm to 1000 nm) to a thick film (thickness of more than 1000 nm), and may include a coating film or a laminated film which is placed on a different substrate (for example, . The film-shaped silicon may be a dense film or a porous film. The porous membrane may include a nanoporous structure, and the dense membrane may mean a membrane that is not intentionally formed with pores.

구체적으로, 웨이퍼 형상의 실리콘은 실리콘(인트린직 또는 익스트린직) 단결정 웨이퍼 및/또는 실리콘(인트린직 또는 익스트린직) 다결정 웨이퍼를 포함할 수 있다.Specifically, the wafer-shaped silicon may include a silicon (extrinsic or extrinsic) single crystal wafer and / or a silicon (extrinsic or extrinsic) polycrystalline wafer.

구체적으로, 와이어 형상의 실리콘은 실리콘 나노와이어 및/또는 실리콘 나노튜브를 포함할 수 있다. 일 예로, 실리콘 나노와이어의 단축직경은 10nm 내지 100nm일 수 있으며, 종횡비(aspect ratio)는 5 내지 1000일 수 있으나, 이에 한정되지 않는다. 일 예로, 실리콘 나노튜브의 외경은 30 내지 400nm일 수 있으며, 외경과 내경의 차인 튜브 격벽 두께는 5nm 내지 50nm일 수 있고, 외경 기준 종횡비(aspect ratio)는 5 내지 1000일 수 있으나, 이에 한정되지 않는다. 와이어 형상의 실리콘은 단결정체, 다결정체, 비정질 또는 결정질과 비정질의 혼합상일 수 있으나, 이에 한정되지 않는다.Specifically, the wire-shaped silicon may include silicon nanowires and / or silicon nanotubes. In one example, the minor axis diameter of the silicon nanowire can be 10 nm to 100 nm, and the aspect ratio can be 5 to 1000, but is not limited thereto. For example, the outer diameter of the silicon nanotube may be 30 to 400 nm, the thickness of the tube partition wall, which is the difference between the outer diameter and the inner diameter, may be 5 nm to 50 nm, and the outer diameter reference aspect ratio may be 5 to 1000, Do not. The wire-shaped silicon may be a monocrystalline, polycrystalline, amorphous or mixed phase of crystalline and amorphous, but is not limited thereto.

구체적으로, 입자 형상의 실리콘은 입자뿐만 아니라, 입자들의 응집체를 포함할 수 있다. 입자 형상의 실리콘은 단결정체 입자, 다결정체 입자, 비정질 입자, 결정질과 비정질이 혼재하는 혼합상의 입자 또는 이들의 혼합물을 포함할 수 있다. 입자 형상의 실리콘의 입자 크기 분포는 유니 모달 분포, 바이모달 분포 또는 트라이모달 이상의 분포를 가질 수 있다. 입자 형상의 실리콘에서, 평균 입자 크기(직경)는 1 내지 50μm, 구체적으로 5 내지 20μm일 수 있으나, 이에 한정되는 것은 아니다. 입자 형상의 실리콘은 필라(pillar)와 같이 돌출된 표면 요철이 형성된 입자, 또는 다공성 입자, 또는 익스트린직 실리콘 쉘과 인트린직 실리콘 코어와 같은 코어쉘 입자등을 포함할 수 있으나, 이에 한정되는 것은 아니다.Specifically, the silicon in the form of particles may include aggregates of particles as well as particles. The particulate silicon may include monocrystalline grains, polycrystalline grains, amorphous grains, mixed phase grains in which crystalline and amorphous are mixed, or a mixture thereof. The particle size distribution of silicon in the form of particles may have a unimodal distribution, a bimodal distribution, or a distribution beyond the triimodal. In the particle-shaped silicon, the average particle size (diameter) may be 1 to 50 mu m, specifically 5 to 20 mu m, but is not limited thereto. The particulate silicon may include particles having protruded surface irregularities such as pillars or porous particles or core shell particles such as an extrinsic silicone shell and an intrinsic silicone core, no.

본 발명의 일 실시예에 따른 마그네슘 이차전지용 음극활물질은 가역적으로 마그네슘화(마그네슘 이온의 삽입) 및 탈마그네슘화(마그네슘 이온의 탈리)될 수 있으며, 구체적으로, 마그네슘 금속을 상대전극으로 한 전기화학 셀 기준 0.3 내지 0.5V 범위에서 탈마그네슘화가 발생할 수 있다. The negative electrode active material for a magnesium secondary battery according to an embodiment of the present invention can be reversibly magnesiumated (insertion of magnesium ions) and demagnesiumation (elimination of magnesium ions), and more specifically, electrochemical De-magnesiumation can occur in the range of 0.3 to 0.5 V on a cell basis.

상술한 바와 같이, 마그네슘 이차전지용 음극활물질은 실리콘을 함유할 수 있으나, 전지의 전기적 상태(충전 상태 및/또는 방전 상태)에 따라, 마그네슘 실리사이드(MgxSi)를 더 포함할 수 있다. As described above, the negative electrode active material for a magnesium secondary battery may contain silicon, but may further include magnesium suicide (Mg x Si) depending on the electrical state (charging state and / or discharging state) of the battery.

상세하게, 마그네슘 이차전지용 음극활물질은 전지의 음극으로 제조된 제조 직후 상태(즉, 전기적 충방전이 이루어지지 않은 상태)에서, 실리콘을 함유할 수 있으며, 일 예로, 음극활물질은 실리콘으로 이루어질 수 있다. 이러한 음극활물질을 포함하는 음극이 구비된 마그네슘 이차전지는 제조 직후의 전기적 상태가 방전상태일 수 있다. In detail, the negative electrode active material for a magnesium secondary battery may contain silicon in a state immediately after the battery is manufactured (i.e., in a state where no electric charge / discharge is performed), and the negative electrode active material may be made of silicon . A magnesium secondary battery having a negative electrode including such an anode active material may be in an electrically discharged state immediately after its manufacture.

이와 달리, 마그네슘 이차전지용 음극활물질은 전지의 음극으로 제조된 제조 직후 상태(즉, 전기적 충방전이 이루어지지 않은 상태)에서, 실리콘 및 마그네슘 실리사이드를 함유할 수 있으며, 일 예로, 음극활물질은 실리콘 및 마그네슘 실리사이드(MgxSi)로 이루어질 수 있다. 이러한 음극활물질을 포함하는 음극이 구비된 마그네슘 이차전지는 제조 직후의 전기적 상태가 충전상태일 수 있다. Alternatively, the negative electrode active material for a magnesium secondary battery may contain silicon and magnesium suicide in a state immediately after the battery is manufactured (that is, in a state where no electric charge / discharge is not performed) made of the negative electrode of the battery. And magnesium suicide (Mg x Si). A magnesium secondary battery having a negative electrode including such an anode active material may be in an electrically charged state immediately after its manufacture.

이와 달리, 마그네슘 이차전지용 음극활물질은 전지의 음극으로 제조된 제조 직후 상태(즉, 전기적 충방전이 이루어지지 않은 상태)에서, 마그네슘 실리사이드를 함유할 수 있으며, 일 예로, 음극활물질은 마그네슘 실리사이드로 이루어질 수 있다. 이러한 음극활물질을 포함하는 음극이 구비된 마그네슘 이차전지는 제조 직후의 전기적 상태가 충전상태일 수 있다. Alternatively, the negative electrode active material for a magnesium secondary battery may contain magnesium suicide in a state immediately after the battery is manufactured (that is, in a state where no electric charge and discharge is performed), and the negative electrode active material is made of magnesium suicide . A magnesium secondary battery having a negative electrode including such an anode active material may be in an electrically charged state immediately after its manufacture.

마그네슘 실리사이드는 마그네슘과 실리콘의 화합물을 의미할 수 있으며, 구체적으로, 마그네슘 실리사이드는 MgxSi(0<x≤2인 실수)를 의미할 수 있으며, 보다 구체적으로 마그네슘 실리사이드는 Mg2Si를 의미할 수 있다.The magnesium suicide may mean a compound of magnesium and silicon. Specifically, the magnesium suicide may mean Mg x Si (0 <x? 2), and more specifically, the magnesium suicide means Mg 2 Si .

이때, 음극활물질이 실리콘을 함유하여, 제조 직후 전지의 전기적 상태가 방전상태라 할지라도, 전지의 충전에 의해 실리콘에 마그네슘 이온이 삽입됨으로써, 실리콘의 일부 내지 전부가 마그네슘 실리사이드로 전환될 수 있음은 물론이다. In this case, even if the negative electrode active material contains silicon and the electric state of the battery is in a discharged state immediately after the production, magnesium ions are inserted into the silicon by charging the battery, so that some or all of the silicon can be converted to magnesium suicide Of course.

본 발명은 상술한 음극활물질을 포함하는 마그네슘 이차전지용 음극을 포함한다.The present invention includes a negative electrode for a magnesium secondary battery including the above-described negative electrode active material.

상세하게, 음극은 음극 집전체; 상기 음극 집전체 상 위치하며 음극활물질을 함유하는 음극활물질층을 포함할 수 있다. In detail, the negative electrode comprises a negative electrode collector; And a negative electrode active material layer positioned on the negative electrode collector and containing a negative electrode active material.

일 예로, 음극활물질이 실리콘 웨이퍼(또는 실리콘 막)인 경우, 음극은 실리콘 웨이퍼(실리콘 막)와 음극 집전체의 적층체일 수 있다. 이때, 적층체는 실리콘 웨이퍼(실리콘 막)와 집전체간의 물리적 적층을 포함하나, 이에 한정되는 것은 아니며, 실리콘 웨이퍼(실리콘 막)의 일 면에 전도성 막이 코팅(또는 증착)되어 웨이퍼(실리콘 막)와 일체로 형성된 적층체를 포함할 수 있다. 또한, 음극활물질이 실리콘 막인 경우 이러한 적층체는 음극 집전체 일 면에 실리콘이 코팅(또는 증착)되어 막을 형성함으로써, 음극 집전체와 일체로 형성된 경우를 포함할 수 있다.For example, when the negative electrode active material is a silicon wafer (or a silicon film), the negative electrode may be a laminate of a silicon wafer (silicon film) and an anode current collector. In this case, the layered product includes physical layering between a silicon wafer (silicon film) and a current collector, but is not limited thereto. A conductive film is coated (or vapor deposited) on one surface of a silicon wafer (silicon film) And a laminated body integrally formed with the substrate. In the case where the negative electrode active material is a silicon film, such a stacked body may include a case where silicon is coated (or deposited) on one surface of the negative electrode collector to form a film, thereby being integrally formed with the negative electrode collector.

이와 달리, 음극은 음극 집전체, 음극 집전체 상 위치하는 음극활물질층을 포함할 수 있으며, 음극활물질층은 실리콘을 포함하는 음극활물질, 도전재 및 바인더를 함유할 수 있다.Alternatively, the negative electrode may include a negative electrode current collector, a negative electrode active material layer positioned on the negative electrode collector, and the negative electrode active material layer may include a negative electrode active material including silicon, a conductive material, and a binder.

일 예로, 음극활물질이 실리콘 와이어 및/또는 실리콘 입자를 포함하는 경우, 음극은 음극 집전체 및 음극 집전체 상 위치하며 음극활물질, 도전재 및 바인더를 함유하는 음극활물질층을 포함할 수 있다.For example, when the negative electrode active material includes silicon wire and / or silicon particles, the negative electrode may include a negative electrode active material layer containing a negative electrode active material, a conductive material, and a binder, which are positioned on the negative electrode collector and the negative electrode collector.

본원발명의 일 실시예에 따라, 음극활물질이 실리콘 와이어 및/또는 실리콘 입자를 포함하는 경우, 슬러리의 도포, 압연등, 통상의 이차전지 제조방법을 이용하여 음극의 제조가 가능함에 따라, 기 확립된 전지 제조공정으로 마그네슘 이차전지의 제조가 가능한 장점이 있다. 또한, 음극활물질이 도포된 집전체의 압연 및/또는 롤링(rolling)이 가능하여 전지 출력을 향상시킬 수 있고, 다양한 형상 및 구조의 전극으로 제조 가능한 장점이 있다. 또한, 음극활물질이 도전재 및 바인더등과 혼합되어 집전체 상 음극활물질층을 형성할 수 있으며, 이를 통해, 음극(집전체 및 음극활물질층)의 전기전도도, 물리적 강도 및 안정성을 증진시킬 수 있는 장점이 있다. 또한, 입자 및/또는 와이어상들의 음극활물질층을 형성할 수 있음에 따라, 동일 부피에서 전해액과의 반응 면적을 현저하게 향상시킬 수 있는 장점이 있다.According to one embodiment of the present invention, when the negative electrode active material includes a silicon wire and / or silicon particles, it is possible to manufacture a negative electrode using a conventional secondary battery manufacturing method such as slurry application and rolling, It is possible to manufacture a magnesium secondary battery by a manufacturing process of a battery. In addition, the current collector coated with the negative electrode active material can be rolled and / or rolled, thereby improving the output of the battery, and can be manufactured into electrodes having various shapes and structures. The negative electrode active material may be mixed with a conductive material, a binder, or the like to form a negative electrode active material layer on the current collector, thereby improving the electrical conductivity, physical strength and stability of the negative electrode (collector and negative electrode active material layer) There are advantages. Further, since the anode active material layer of the particles and / or the wires can be formed, the area of reaction with the electrolyte at the same volume can be remarkably improved.

음극의 바인더는 이차전지 분야에서 활물질층의 결착력을 향상시키기 위해 통상적으로 사용되는 고분자이면 족하다. 즉, 전해액과 화학적으로 반응하지 않으며 활물질간, 활물질과 도전재간, 활물질과 집전체간, 및 도전재와 집전체간을 결착시킬 수 있는 고분자이면 사용 가능하다. 구체적인 일 예로, 음극의 바인더는 폴리비닐리덴 플루오라이드, 폴리비닐리덴 플루오라이드-헥사플루오로프로필렌 공중합체, 폴리비닐리덴플루오라이드-트리클로로에틸렌 공중합체, 폴리메틸메타크릴레이트, 폴리테트라플루오로에틸렌, 폴리아크릴산, 폴리아크릴로니트릴, 폴리비닐피롤리돈, 폴리비닐아세테이트, 폴리에틸렌-비닐 아세테이트 공중합체, 폴리에틸렌옥사이드, 셀룰로오스 아세테이트, 셀룰로오스 아세테이트 부티레이트, 셀룰로오스 아세테이트 프로피오네이트, 시아노에틸풀루란, 시아노에틸폴리비닐알콜, 시아노에틸셀룰로오스, 시아노에틸수크로오스, 풀루란, 카르복실 메틸 셀룰로오스, 스티렌-부타디엔 공중합체, 아크릴로니트릴-스티렌-부타디엔 공중합체, 폴리이미드, 폴리테트라플루오로에틸렌 또는 이들의 혼합물등을 들 수 있으나, 이에 한정되는 것은 아니다. The binder of the negative electrode may be a polymer commonly used for improving the binding force of the active material layer in the secondary battery field. That is, any polymer that does not chemically react with the electrolytic solution and binds between the active material, between the active material and the conductive material, between the active material and the current collector, and between the conductive material and the current collector can be used. As a specific example, the binder of the negative electrode may be selected from the group consisting of polyvinylidene fluoride, polyvinylidene fluoride-hexafluoropropylene copolymer, polyvinylidene fluoride-trichlorethylene copolymer, polymethyl methacrylate, polytetrafluoroethylene , Polyacrylic acid, polyacrylonitrile, polyvinyl pyrrolidone, polyvinyl acetate, polyethylene-vinyl acetate copolymer, polyethylene oxide, cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, cyanoethylpullulan, cyano Styrene-butadiene copolymer, polyimide, polytetrafluoroethylene, or a copolymer thereof, which may be used in combination with one or more selected from the group consisting of polyvinyl alcohol, ethyl polyvinyl alcohol, cyanoethylcellulose, cyanoethyl sucrose, pullulan, carboxymethylcellulose, styrene-butadiene copolymer, acrylonitrile- Mixture, etc. It is, but is not limited to this.

음극의 도전재는 이차전지 분야에서 활물질층의 전기전도도를 향상시키기 위해 통상적으로 사용되는 전도성 물질이면 족하다. 구체적으로, 음극의 도전재는 카본 블랙, 아세틸렌 블랙, 케첸 블랙, 채널 블랙, 파네스 블랙, 램프 블랙, 서멀 블랙 또는 이들의 혼합물등의 전도성 탄소체; 탄소 섬유나 금속 섬유 등의 전도성 섬유; 탄소 나노 튜브나 그래핀 등의 전도성 나노구조체등을 일 수 있으나, 이에 한정되는 것은 아니다.The conductive material of the negative electrode may be a conductive material conventionally used for improving the electrical conductivity of the active material layer in the secondary battery field. Specifically, the conductive material for the negative electrode is a conductive carbon material such as carbon black, acetylene black, ketjen black, channel black, fines black, lamp black, thermal black or a mixture thereof; Conductive fibers such as carbon fibers and metal fibers; Conductive nanostructures such as carbon nanotubes and graphenes, but are not limited thereto.

음극의 집전체는 전도도가 우수하며 전지의 충방전시 화학적으로 안정한 물질이면 무방하다. 구체적으로, 음극의 집전체는 그라파이트, 그래핀, 티타늄, 구리, 플래티늄, 알루미늄, 니켈, 은, 금, 또는 카본나노튜브등의 전도성 물질일 수 있다. 음극 집전체는 전도성 물질의 포일(foil), 폼(foam), 박(film), 메쉬(mesh), 펠트(felt) 또는 다공성 박(perforated film) 형태일 수 있다. 그러나, 본 발명이 집전체의 형상 및 물질에 의해 한정될 수 없음은 물론이다.The collector of the negative electrode is excellent in conductivity and may be chemically stable when the battery is charged and discharged. Specifically, the current collector of the negative electrode may be a conductive material such as graphite, graphene, titanium, copper, platinum, aluminum, nickel, silver, gold, or carbon nanotubes. The anode current collector may be in the form of a foil, foam, film, mesh, felt or porous perforated film of conductive material. However, it goes without saying that the present invention can not be limited by the shape and material of the current collector.

음극활물질에 함유된 도전재 및 바인더의 함량은 안정적인 전기 전도가 이루어지며 구성 물질간 안정적인 결착이 이루어지는 정도면 무방하다. 일 예로, 음극활물질층 음극활물질 100 중량부에 대하여, 5 내지 50 중량부의 도전재 및 1 내지 20 중량부의 바인더를 함유할 수 있으나, 이에 한정되는 것은 아니다.  The content of the conductive material and the binder contained in the negative electrode active material is sufficient to ensure stable electrical conduction and stable binding between the constituent materials. For example, the negative electrode active material layer may contain 5 to 50 parts by weight of the conductive material and 1 to 20 parts by weight of the binder, based on 100 parts by weight of the negative electrode active material, but is not limited thereto.

본 발명은 상술한 음극활물질을 포함하는 마그네슘 이차전지를 제공한다.The present invention provides a magnesium secondary battery including the above-described negative electrode active material.

본 발명은 상술한 음극활물질을 함유하는 음극을 포함하는 마그네슘 이차전지를 제공한다.The present invention provides a magnesium secondary battery including a negative electrode containing the above-mentioned negative electrode active material.

본 발명의 일 실시예에 따른 마그네슘 이차전지는, 실리콘(Si)을 함유하는 음극활물질을 포함하는 음극; 마그네슘 이온의 가역적인 삽입과 탈리가 가능한 전이금속화합물을 양극활물질로 포함하는 양극; 및 전해액을 포함할 수 있다. 이때, 마그네슘 이차전지는 제조 직후 상태, 방전 상태 또는 충전 상태일 수 있다. 이차전지가 충전 상태인 경우, 음극활물질에 포함된 실리콘은 마그네슘화에 의해 실리콘이 마그네슘 실리사이드(MgxSi)로 전환된 후에도 잔류하는 잔류 실리콘을 포함할 수 있다. A magnesium secondary battery according to an embodiment of the present invention includes a negative electrode including a negative active material containing silicon (Si); A positive electrode containing a transition metal compound capable of reversible insertion and desorption of magnesium ions as a positive electrode active material; And an electrolytic solution. At this time, the magnesium secondary battery may be in a state immediately after manufacture, a discharge state, or a charged state. When the secondary battery is in a charged state, the silicon contained in the negative electrode active material may include residual silicon remaining after the silicon is converted to magnesium silicide (Mg x Si) by magnesiumation.

구체적으로, 본 발명의 일 실시예에 따른 마그네슘 이차전지는, 인트린직 또는 익스트린직 반도체인 실리콘을 음극활물질로 포함하는 음극; 마그네슘 이온의 가역적인 삽입과 탈리가 가능한 전이금속화합물을 양극활물질로 포함하는 양극; 및 전해액을 포함할 수 있다. 이때, 마그네슘 이차전지는 제조 직후 상태 또는 방전 상태일 수 있다. Specifically, a magnesium secondary battery according to an embodiment of the present invention includes: an anode including an anode active material such as a stainless steel or an extrinsic semiconductor; A positive electrode containing a transition metal compound capable of reversible insertion and desorption of magnesium ions as a positive electrode active material; And an electrolytic solution. At this time, the magnesium secondary battery may be in a state immediately after manufacture or in a discharged state.

본 발명의 일 실시예에 따른 마그네슘 이차전지는 충전시 하기 반응식 1의 음극 반응을 가지며, 방전시 하기 반응식 2의 음극 반응을 가질 수 있다.The magnesium secondary battery according to an embodiment of the present invention has a negative electrode reaction of the following Reaction Formula 1 at the time of charging and may have a negative electrode reaction of the following Reaction Formula 2 at the time of discharging.

(반응식 1)(Scheme 1)

Si + 2Mg2+ + 4e- → Mg2SiSi + 2Mg 2+ + 4e - &gt; Mg 2 Si

(반응식 2)(Scheme 2)

Mg2Si → Si + 2Mg2+ + 4e- Mg 2 Si? Si + 2Mg 2+ + 4e -

본 발명의 일 실시예에 따른 마그네슘 이차전지에 있어, 양극의 양극활물질은 마이네슘 이온의 가역적인 삽입과 탈리가 가능한 물질이면 사용 가능하다. 구체적으로 마그네슘 이온의 가역적인 삽입과 탈리가 가능한 전이금속화합물일 수 있다. 구체적으로, 양극활물질은 보론 (B), 스칸듐(Sc), 타이타늄(Ti), 바나듐(V), 크로뮴(Cr), 망간(Mn), 철(Fe), 코발트(Co), 니켈(Ni), 구리(Cu), 아연(Zn), 실리콘 (Si), 주석 (Sn), 몰리브데넘(Mo), 나이오븀(Nb) 및 루테늄(Ru)에서 하나 이상 선택되는 원소의 산화물, 할로겐화물, 칼코겐화물 또는 이들의 혼합물일 수 있다. 예를 들어, 양극활물질은 Co3O4, MnO2, Mn2O3, Mn3O4, MgMnSiO4, MgVBO4, MgxFe2-xB2O5, MoO3, PbO2, Pb3O4, RuO2, V2O5, WO3, TiO2, TiS2, VS2, ZrS2, Mo3O4, Mo6S8, MoB2, TiB2, Cu2Se 또는 이들의 혼합물 등을 들 수 있으나, 이에 한정되는 것은 아니다.In the magnesium secondary battery according to an embodiment of the present invention, the positive electrode active material of the positive electrode may be used as long as it is a material capable of reversible insertion and desorption of the negative ion. Specifically, it may be a transition metal compound capable of reversible insertion and desorption of magnesium ions. Specifically, the positive electrode active material is selected from the group consisting of boron (B), scandium (Sc), titanium (Ti), vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), cobalt (Co) An oxide, a halide, or an oxide of one or more elements selected from copper (Cu), zinc (Zn), silicon (Si), tin (Sn), molybdenum (Mo), niobium (Nb), and ruthenium Chalcogenides, or mixtures thereof. For example, the positive electrode active material is Co 3 O 4, MnO 2, Mn 2 O 3, Mn 3 O 4, MgMnSiO 4, MgVBO 4, Mg x Fe 2-x B 2 O 5, MoO 3, PbO 2, Pb 3 O 4 , RuO 2 , V 2 O 5 , WO 3 , TiO 2 , TiS 2 , VS 2 , ZrS 2 , Mo 3 O 4 , Mo 6 S 8 , MoB 2 , TiB 2 , Cu 2 Se, But the present invention is not limited thereto.

양극 또한, 양극활물질을 함유하는 양극활물질층 및 양극 집전체를 포함할 수 있으며, 양극활물질층은 양극활물질, 바인더 및 도전재를 포함할 수 있다. The anode may also include a cathode active material layer containing a cathode active material and a cathode current collector, and the cathode active material layer may include a cathode active material, a binder, and a conductive material.

양극활물질층의 바인더, 도전재 및 양극의 집전체는 상술한 음극활물질층의 바인더, 도전재 및 음극의 집전체에서 상술한 바인더, 도전재 및 집전체와 동일 내지 유사할 수 있다. 양극활물질층에 함유된 도전재 및 바인더의 함량 또한, 안정적인 전기 전도가 이루어지며 구성 물질간 안정적인 결착이 이루어지는 정도면 무방하며, 음극활물질층과 독립적으로, 양극활물질 100 중량부에 대하여, 5 내지 50 중량부의 도전재 및 1 내지 20 중량부의 바인더를 함유할 수 있으나, 이에 한정되는 것은 아니다. The binder of the positive electrode active material layer, the conductive material and the current collector of the positive electrode may be the same as or similar to the binders, the conductive material and the current collector described above in the binder of the above-described negative electrode active material layer, the conductive material and the current collector. The content of the conductive material and the binder contained in the positive electrode active material layer may be such that the stable electrical conduction is performed and the stable binding between the constituent materials is achieved and that the amount of the conductive material and binder contained in the negative electrode active material layer is 5 to 50 By weight of a conductive material and 1 to 20 parts by weight of a binder, but is not limited thereto.

음극은 음극활물질, 도전재 및 바인더를 함유하는 슬러리를 집전체 상 도포 및 건조하여 제조될 수 있으며, 선택적으로 건조가 수행된 후 압착(rolling)이 더 수행될 수 있다. 이와 달리, 음극은 음극활물질, 도전재 및 바인더를 함유하는 혼합물을 압착한 압착체일 수 있다. The negative electrode can be produced by applying and drying a slurry containing a negative electrode active material, a conductive material and a binder on a current collector, and further, rolling can be further performed after drying is performed. Alternatively, the negative electrode may be a pressed member in which a mixture containing the negative electrode active material, the conductive material and the binder is squeezed.

양극 또한, 양극활물질, 도전재 및 바인더를 함유하는 슬러리를 집전체 상 도포 및 건조하여 제조되거나, 양극활물질, 도전재 및 바인더를 함유하는 혼합물을 압착하여 제조될 수 있다. 집전체 상 슬러리를 도포하여 양극을 제조하는 경우, 건조가 수행된 후 압착(rolling)이 더 수행될 수 있음은 물론이다.The anode can also be produced by applying and drying a slurry containing a cathode active material, a conductive material and a binder on a current collector, or by pressing a mixture containing a cathode active material, a conductive material and a binder. When the positive electrode is prepared by applying the current collector slurry, it is of course possible to further perform rolling after the drying is performed.

전해액은 마그네슘 이온을 함유하는 액체로, 마그네슘 이차전지에 통상적으로 사용되는 전해액이면 족하다. 전해액은 비수계 유기 전해액 또는 수계 전해액일 수 있다. 전해액은 전해질이 되는 마그네슘염 및 용매를 포함할 수 있다. 수계 전해액인 경우, 전해질은 Mg(OH)2, MgSO4, MgCl2, 또는 Mg(NO3)2등과 같은 수용성 마그네슘 염일 수 있다. 수계 전해액의 경우, 전해질 농도는 포화농도 또는 포화농도에 근접한 농도일 수 있다. 전해액이 비수계 전해액인 경우, 전해액은 그리냐드 시약계 기반 전해액일 수 있다. 구체적으로, 비수계 전해액인 경우, 전해질로서 이용가능한 마그네슘염은 RMgX(R은 탄소수 1 내지 10인 직쇄형이거나 분지형의 알킬기, 탄소수 1 내지 10인 직쇄형이거나 분지형의 아릴기, 또는 탄소수 1 내지 10인 직쇄형이거나 분지형의 아민기이며, 바람직하게는 메틸기, 에틸기, 부틸기, 페닐기, 또는 아닐린기이며, X 는 할로겐이고 바람직하게는 염소 또는 브롬), MgX2 (X는 할로겐이고 바람직하게는 염소 또는 브롬), R2Mg (R은 알킬기, 디알킬보론기, 디아릴보론기, 알킬카보닐기(예를 들면 메틸카보닐기(-CO2CH3)), 알킬설포닐기(예를 들면, 트리플루오로메틸설포닐기(-SO2CF3)) 등에서 하나 또는 둘 이상 선택될 수 있으나, 이에 한정되는 것은 아니다. 이때, 전해액은 AlCl3과 같은 첨가제를 더 포함할 수 있으나, 이에 한정되는 것은 아니다. 비수계 전해액의 용매는 디메틸에테르, 디에틸에테르, 디메틸 카보네이트, 디에틸 카보네이트, 에틸메틸 카보네이트, 디프로필 카보네이트, 메틸프로필 카보네이트, 에틸프로필 카보네이트, 에틸렌 카보네이트, 프로필렌 카보네이트, 부틸렌 카보네이트, 메틸 아세테이트, 에틸 아세테이트, n-프로필 아세테이트, 디메틸아세테이트, 메틸프로피오네이트, 에틸프로피오네이트, γ-부티로락톤, 데카놀라이드(decanolide), 발레로락톤, 메발로노락톤(mevalonolactone), 카프로락톤(caprolactone), 디부틸 에테르, 테트라글라임, 트리글라임, 디글라임, 폴리에틸렌글리콜디메틸에테르, 디메톡시에탄, 테트라하이드로퓨란, 2-메틸테트라하이드로퓨란, 2,2-디메틸테트라하이드로퓨란, 2,5-디메틸테트라하이드로퓨란, 시클로헥사논, 트리에틸아민, 트리페닐아민, 트리에텔포스핀옥사이드, 아세토니트릴, 디메틸포름아미드, 1,3-디옥솔란, 및 설포란(sulfolane)등에서 하나 또는 둘 이상 선택될 수 있으나, 이에 한정되는 것은 아니다. 다른 비수계 전해액의 일 예로, 상술한 바와 같은 비수계 전해액의 용매와 Mg(TFSI)2, Mg(FSI)2, Mg(PF6)2, Mg(ClO4)2 등에서 하나 또는 둘 이상 선택된 마그네슘 염을 함유하는 전해액을 들 수 있으나, 이에 한정되는 것은 아니다. The electrolytic solution is a liquid containing magnesium ions, which is an electrolytic solution ordinarily used in a magnesium secondary battery. The electrolytic solution may be a non-aqueous organic electrolytic solution or an aqueous electrolytic solution. The electrolytic solution may include a magnesium salt to be an electrolyte and a solvent. If the aqueous liquid electrolyte, the electrolyte may be a salt water-soluble magnesium such as Mg (OH) 2, MgSO 4 , MgCl 2, or Mg (NO 3) 2. In the case of an aqueous electrolyte, the electrolyte concentration may be a saturation concentration or a concentration close to the saturation concentration. When the electrolyte is a non-aqueous liquid electrolyte, the electrolyte may be a Grignard reagent-based electrolyte. Specifically, in the case of a non-aqueous liquid electrolyte, the magnesium salt that can be used as the electrolyte is RMgX (wherein R represents a linear or branched alkyl group having 1 to 10 carbon atoms, a linear or branched alkyl group having 1 to 10 carbon atoms, And X is halogen and preferably chlorine or bromine), MgX 2 (wherein X is halogen and preferably a halogen atom), and more preferably a halogen atom, (For example, chlorine or bromine), R 2 Mg (wherein R represents an alkyl group, a dialkylboron group, a diarylboron group, an alkylcarbonyl group (for example, methylcarbonyl group (-CO 2 CH 3 ) , And trifluoromethylsulfonyl group (-SO 2 CF 3 )). However, the present invention is not limited thereto, and the electrolyte solution may further include additives such as AlCl 3 . Non-aqueous electrolysis Methyl ethyl ketone, dimethyl carbonate, diethyl carbonate, ethyl methyl carbonate, dipropyl carbonate, methyl propyl carbonate, ethyl propyl carbonate, ethylene carbonate, propylene carbonate, butylene carbonate, methyl acetate, ethyl acetate, n -Propyl acetate, dimethyl acetate, methyl propionate, ethyl propionate,? -Butyrolactone, decanolide, valerolactone, mevalonolactone, caprolactone, dibutyl But are not limited to, ether, tetraglyme, triglyme, diglyme, polyethylene glycol dimethyl ether, dimethoxyethane, tetrahydrofuran, 2-methyltetrahydrofuran, 2,2-dimethyltetrahydrofuran, , Cyclohexanone, triethylamine, triphenylamine, triethylphosphine oxide, One or more selected from the group consisting of acetonitrile, dimethylformamide, 1,3-dioxolane, and sulfolane, but is not limited thereto. As an example of other non-aqueous liquid electrolytes, An electrolytic solution containing a solvent of an electrolytic solution and a magnesium salt selected from one or two or more selected from the group consisting of Mg (TFSI) 2 , Mg (FSI) 2 , Mg (PF 6 ) 2 and Mg (ClO 4 ) 2 , no.

본 발명의 일 실시예에 따른 마그네슘 이차전지는 분리막을 더 포함할 수 있으며, 분리막은 음극과 양극 사이에 위치하여 마이네슘 이온을 포함한 물질 이동은 원활히 이루어지면서도 음극과 양극의 전기적 단락을 원천적으로 차단하는 역할을 수행할 수 있다. 분리막으로는 종래에 이차전지에서 양극과 음극 사이에 개재되는 통상의 무기 분리막이나 유기 분리막이 사용될 수 있다. 무기 분리막으로는 글라스 필터 등을 들 수 있고, 유기 분리막으로는 다공성 고분자 필름등을 들 수 있다. 다공성 고분자 필름은, 예를 들어 에틸렌 단독중합체, 프로필렌 단독중합체, 에틸렌/부텐 공중합체, 에틸렌/헥센 공중합체 및 에틸렌/메타크릴레이트 공중합체 등과 같은 폴리올레핀계 고분자로 제조한 다공성 고분자 필름을 들 수 있다. The magnesium secondary battery according to an embodiment of the present invention may further include a separation membrane. The separation membrane is disposed between the cathode and the anode so that the material including the ionic material migrates smoothly, and the electrical short- It can play a role of blocking. As the separation membrane, a conventional inorganic separation membrane or an organic separation membrane interposed between an anode and a cathode in a conventional secondary battery can be used. Examples of the inorganic separation membrane include a glass filter and the organic separation membrane is a porous polymer membrane. Examples of the porous polymer film include a porous polymer film made of a polyolefin-based polymer such as an ethylene homopolymer, a propylene homopolymer, an ethylene / butene copolymer, an ethylene / hexene copolymer, and an ethylene / methacrylate copolymer .

본 발명의 일 실시예에 따른 마그네슘 이차전지는 이차전지 분야에서 통상적으로 사용되는 구조를 가질 수 있으며, 캔을 사용한 원통형, 각형, 파우치(pouch)형 또는 코인(coin)형 등일 수 있으나, 이에 한정되는 것은 아니다. The magnesium secondary battery according to an embodiment of the present invention may have a structure commonly used in the secondary battery field, and may be a cylindrical shape, a square shape, a pouch shape or a coin shape using a can, It is not.

(실시예)(Example)

보론(B)이 도핑된 p-형 실리콘 웨이퍼(Siltron, 저항 25.2 - 42.5 Ωcm)의 작업전극, 마그네슘 금속 박(foil)의 기준전극 및 마그네슘 금속 박(foil)의 상대전극을 포함하는 3-전극 전기화학셀을 제조하였다. 이때, 테트라하이드로퓨란(THF)에 0.5M의 농도로 PhMgCl(Ph=페닐)이 용해된 액을 전해액으로 사용하였다. Electrode comprising a working electrode of a p-type silicon wafer doped with boron (B) (Siltron, resistance 25.2 - 42.5? Cm), a reference electrode of magnesium metal foil and a counter electrode of magnesium metal foil An electrochemical cell was fabricated. At this time, a liquid in which PhMgCl (Ph = phenyl) was dissolved in tetrahydrofuran (THF) at a concentration of 0.5M was used as an electrolytic solution.

도 1은 제조된 3-전극 전기화학셀을 0.001-0.6V의 전압 범위에서 0.3mV/s의 스캔 속도(scan rate)로 CV 측정한 결과이다. 도 1에서 알 수 있듯이, 실리콘으로 마그네슘이온이 삽입(magnesiation)-탈리 (demagnesiation)되며 실리콘이 전기화학적으로 환원-산화되는 것을 볼 수 있다. FIG. 1 shows a result of CV measurement of the prepared 3-electrode electrochemical cell at a scan rate of 0.3 mV / s in a voltage range of 0.001 to 0.6 V. FIG. As can be seen from FIG. 1, magnesium ions are magnesiation-demagnetized into silicon and silicon is electrochemically reduced-oxidized.

도 2는 제조된 3-전극 전기화학셀을 0.07-0.6V의 전압 범위에서 정전류 2μA로 충방전 테스트한 결과를 도시한 도면이다. 도 2에서 알 수 있듯이, 실리콘 음극은 마그네슘이온과의 전기화학적 반응에 활성을 보이며 충전(마그네슘이온 삽입, magnesiation)되고 약 0.4V에서 마그네슘이온 탈리(demagnesiation)에 의한 평탄면을 보이며 가역적으로 방전됨을 알 수 있다. 2 is a graph showing a result of charging / discharging test of a 3-electrode electrochemical cell manufactured with a constant current of 2 μA in a voltage range of 0.07 to 0.6 V. FIG. As can be seen from FIG. 2, the silicon anode exhibits an electrochemical reaction with magnesium ions and shows a flat surface due to charging (magnesium ion implantation, magnesiation) and magnesium ion demagnetization at about 0.4 V and reversibly discharges Able to know.

이상과 같이 본 발명에서는 특정된 사항들과 한정된 실시예 및 도면에 의해 설명되었으나 이는 본 발명의 보다 전반적인 이해를 돕기 위해서 제공된 것일 뿐, 본 발명은 상기의 실시예에 한정되는 것은 아니며, 본 발명이 속하는 분야에서 통상의 지식을 가진 자라면 이러한 기재로부터 다양한 수정 및 변형이 가능하다. While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, Those skilled in the art will recognize that many modifications and variations are possible in light of the above teachings.

따라서, 본 발명의 사상은 설명된 실시예에 국한되어 정해져서는 아니되며, 후술하는 특허청구범위뿐 아니라 이 특허청구범위와 균등하거나 등가적 변형이 있는 모든 것들은 본 발명 사상의 범주에 속한다고 할 것이다.Accordingly, the spirit of the present invention should not be construed as being limited to the embodiments described, and all of the equivalents or equivalents of the claims, as well as the following claims, belong to the scope of the present invention .

Claims (10)

실리콘(Si)을 함유하는 마그네슘 이차전지용 음극활물질.A negative electrode active material for a magnesium secondary battery containing silicon (Si). 제 1항에 있어서,
상기 실리콘은 진성 반도체 실리콘(intrinsic silicon) 또는 n형 도펀트나 p형 도펀트로 도핑된 익스트린직(extrinsic) 실리콘인 마그네슘 이차전지용 음극활물질.The method according to claim 1,
Wherein the silicon is an extrinsic silicon doped with intrinsic silicon or an n-type dopant or a p-type dopant. 제 2항에 있어서,
상기 n형 도펀트는 인(P), 비소(As) 및 안티몬(Sb)에서 하나 또는 둘 이상 선택되며, p형 도펀트는 붕소(B), 알루미늄(Al) 및 인듐(In)에서 하나 또는 둘 이상 선택되는 마그네슘 이차전지용 마그네슘 이차전지용 음극활물질.3. The method of claim 2,
The n-type dopant is one or more selected from phosphorus (P), arsenic (As) and antimony (Sb), and the p-type dopant is one or more selected from boron (B), aluminum (Al) Electrode active material for magnesium secondary battery selected for magnesium secondary battery. 제 1항에 있어서,
상기 실리콘은 막(film), 웨이퍼(wafer), 와이어(wire) 및 입자(particle)에서 하나 또는 둘 이상 선택되는 형상인 마그네슘 이차전지용 음극활물질.The method according to claim 1,
Wherein the silicon is a shape selected from one or more of a film, a wafer, a wire, and a particle, the negative electrode active material for a magnesium secondary battery. 제 1항 내지 제 4항 중 선택되는 어느 한 항에 따른 마그네슘 이차전지용 음극활물질을 포함하는 마그네슘 이차전지용 음극.A negative electrode for a magnesium secondary battery comprising a negative electrode active material for a magnesium secondary battery according to any one of claims 1 to 4. 제 5항에 있어서,
상기 음극은 음극 집전체; 상기 음극 집전체 상 위치하는 음극활물질층을 포함하며, 상기 음극활물질층은 실리콘을 포함하는 음극활물질, 도전재 및 바인더를 함유하는 마그네슘 이차전지용 음극.6. The method of claim 5,
The negative electrode comprising: a negative electrode collector; And a negative electrode active material layer positioned on the negative electrode collector, wherein the negative electrode active material layer contains a negative active material including silicon, a conductive material, and a binder. 제 5항에 따른 음극을 포함하는 마그네슘 이차전지.A magnesium secondary battery comprising a negative electrode according to claim 5. 제 7항에 있어서,
상기 음극은 충전 상태 기준 MgxSi(0<x≤2인 실수)를 함유하는 마그네슘 이차전지.8. The method of claim 7,
Wherein the negative electrode contains a charge state criterion Mg x Si (0 < x &lt; = 2). 제 7항에 있어서,
상기 마그네슘 이차전지는 마그네슘 이온의 가역적인 삽입과 탈리가 가능한 전이금속화합물을 양극활물질로 포함하는 양극 및 전해액을 더 포함하는 마그네슘 이차전지.8. The method of claim 7,
Wherein the magnesium secondary battery further comprises a positive electrode and an electrolyte containing a transition metal compound capable of reversible insertion and desorption of magnesium ions as a positive electrode active material. 제 9항에 있어서,
상기 양극활물질은 보론 (B), 스칸듐(Sc), 타이타늄(Ti), 바나듐(V), 크로뮴(Cr), 망간(Mn), 철(Fe), 코발트(Co), 니켈(Ni), 구리(Cu), 아연(Zn), 실리콘 (Si), 주석 (Sn), 몰리브데넘(Mo), 나이오븀(Nb) 및 루테늄(Ru)에서 하나 이상 선택되는 원소의 산화물, 할로겐화물 또는 칼코젠화물인 마그네슘 이차전지.
10. The method of claim 9,
The cathode active material may be at least one selected from the group consisting of boron (B), scandium (Sc), titanium (Ti), vanadium (V), chromium (Cr), manganese (Mn), iron (Fe), cobalt Halides or chalcogenides of one or more elements selected from among copper (Cu), zinc (Zn), silicon (Si), tin (Sn), molybdenum (Mo), niobium (Nb) and ruthenium Magnesium secondary battery as cargo.
KR1020160102175A 2016-08-11 2016-08-11 Anode Active Materials for Magnesium Secondary Battery and Magnesium Secondary Battery Using Thereof KR20180017794A (en)