KR20170122553A - Natural insulation board possible fireproof and flame retardant using Fungus binder and method - Google Patents
Natural insulation board possible fireproof and flame retardant using Fungus binder and method Download PDFInfo
- Publication number
- KR20170122553A KR20170122553A KR1020160051684A KR20160051684A KR20170122553A KR 20170122553 A KR20170122553 A KR 20170122553A KR 1020160051684 A KR1020160051684 A KR 1020160051684A KR 20160051684 A KR20160051684 A KR 20160051684A KR 20170122553 A KR20170122553 A KR 20170122553A
- Authority
- KR
- South Korea
- Prior art keywords
- natural
- binder
- insulating board
- mushroom
- weight
- Prior art date
Abstract
Description
본 발명은 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드 및 이의 제조 방법에 관한 것으로서, 더욱 상세하게는 자연계에 있는 천연재료에 버섯균 혹은 고상종균과 같은 미생물을 바인더로 활용하여 천연 단열 보드를 제공함으로써, 환경호르몬이나 유해한 분진이 배출되지 않는 효과와 종래의 단열보드보다 가벼우며 탄력성이 좋고 더 견고한 천연 단열 보드를 제공할 수 있는 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드 및 이의 제조 방법에 관한 것이다.
The present invention relates to a natural insulating board which provides a fire-retardant and flame retardant function using mushroom germ as a binder, and a method of manufacturing the same. More particularly, the present invention relates to a natural insulating board using microorganisms such as mushroom bacteria or solid- , It is possible to provide a natural insulation board which is lighter than conventional insulation board and has more elasticity and more solid than conventional insulation board by providing natural heat insulating board and has fireproof and flame retardant function using mushroom germ as a binder And a method of manufacturing the same.
건축기술의 발달과 함께 단열재나 샌드위치판넬과 같은 건축내외장재의 기술도 많이 발전하여 그 종류도 무수히 많지만 대부분은 화재에 취약한 폴리우페탄발포체, 스티렌발포체같은 발포체 제품이 많고 화재에 다소 유리한 제품으로는 유리섬유나 암면 또는 석면 그리고 석고보드를 들 수 있다.In addition to the development of construction technology, the technology of interior and exterior materials such as insulation and sandwich panel has developed a lot, and many kinds of foam products such as polyurethane foam and styrene foam are vulnerable to fire. Fiber, rock or asbestos, and gypsum board.
다공성 물질을 발포시켜 제조하는 발포단열재의 경우는 인화성이 매우 높아서 점화원이 있을 경우 쉽고 빠르게 건물전체로 화재가 번지며 유독가스를 내기 때문에 많은 재산피해와 인명피해를 주고 있다.In the case of foamed insulation manufactured by foaming a porous material, the flammability is very high. Therefore, when there is an ignition source, a fire easily spreads throughout the building and poisonous gas is emitted.
유리섬유나 석면제품의 경우는 불연성 재료라는 측면에서는 화재로부터의 위험성에 유리하나 시공 중 유리가루나 석면가루가 날리어 작업자의 건강을 해치며 환경을 오염시킬 수 있다는 단점이 있다.In the case of glass fiber and asbestos products, it is advantageous in terms of nonflammable materials in terms of fire hazard. However, it is disadvantageous that glass or asbestos powder is blown during construction, which may harm the health of workers and pollute the environment.
석고보드의 경우에는 유리섬유와 마찬가지로 불연성 재료이므로 화재에는 유리하나 고온의 환경에서 재료 자체가 쉽게 터지고 깨지는 단점을 가지고 있다.In the case of gypsum board, since it is a nonflammable material like glass fiber, it is good for fire but it has the disadvantage that the material easily breaks and breaks in a high temperature environment.
또한, 화재 같은 고온의 환경에서 재료 자체가 쉽게 터지고 깨지는 단점을 가지고 있어 화재 직후에는 소방관이나 주변의 인근주민의 환경이 분진으로 인한 악성으로 변하고 화재 진압에 사용된 물이 하수로 흘러들어가 수질오염을 유발하고 있다.In addition, since the material itself easily breaks and breaks in a high temperature environment such as a fire, the environment of firefighters and surrounding residents turns to malicious due to dust immediately after the fire, and the water used for the fire suppression flows into the sewage, .
상기한 바와 같이, 종래의 건축내외장재들은 폐기시 건축폐기물법에 의한 폐기를 해야 하는 악성의 재료들로서 일반적인 처리로는 환경적인 측면에서 많은 폐해를 제공하게 된다.As described above, conventional architectural interior and exterior materials are malicious materials that must be disposed of by the construction waste method at the time of disposal.
그러나, 본 발명은 천연소재의 재료들만으로 구성되어 있고, 재료들을 결합하는 바인더 또한 자연계의 미생물을 이용하였으므로 자연으로 돌아가 유용한 퇴비로 식물의 양분으로 변화하므로 기존의 문제점들에서 벗어날 수가 있는 것이다.
However, since the present invention is made up only of natural materials, the binder that binds the materials also uses natural microorganisms, so it returns to nature and becomes a useful compost and changes into nutrients of plants.
본 발명의 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드 및 이의 제조 방법은 상기와 같은 종래 기술에서 발생하는 문제점을 해소하기 위한 것으로, 자연계에 있는 천연재료에 버섯균 혹은 고상종균과 같은 미생물을 바인더로 활용하여 천연 단열 보드를 제공하도록 하는데 있다.The present invention provides a natural insulating board and a method of manufacturing the same that provide a fire-retardant and flame-retardant function using a mushroom germ as a binder. The natural insulating board and the method for manufacturing the same provide a mushroom- And to provide a natural insulating board by using a microorganism such as a seed as a binder.
본 발명의 다른 목적은 천연 단열 보드에 무기질 도료를 이용하여 방수 처리와 발수 처리하거나, 은나노 코팅을 수행하여 항균 처리 및 곰팡이 제거를 수행함으로써, 기능성 단열보드를 제공하도록 하는데 있다.Another object of the present invention is to provide a functional insulating board by performing waterproofing treatment and water repellent treatment using a natural paint on a natural insulating board, or by performing antibacterial treatment and mold removal by performing silver nano coating.
본 발명의 또 다른 목적은 천연 단열 보드 상면에 폐면, 면실박을 형성시켜 결속력을 제공하도록 하는데 있다.
Another object of the present invention is to provide a bonding force by forming a closed face and a cotton foil on the upper surface of a natural insulating board.
본 발명의 과제를 해결하기 위하여, 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드 제조 방법은,Disclosure of the Invention In order to solve the problems of the present invention, there is provided a method of manufacturing a natural insulating board, which provides a fire-
왕겨 20 ~ 35 중량부, 탄화왕겨 20 ~ 35 중량부, 톱밥 20 ~ 35 중량부를 준비하고, 볏집, 유독풀, 대나무잎, 탄화왕겨가루 중 어느 하나의 강도 보강재 10 ~ 20 중량부를 준비하는 내용물준비단계(S100)와; 상기 준비된 내용물을 물이 담긴 믹서기에 투입하여 함수율 65%로 만드는 수분조절단계(S200)와; 상기 함수율 65%인 내용물이 담긴 믹서기에 설탕 5 ~ 10 중량부를 투입하기 위한 당분제공단계(S300)와; 상기 믹서기를 동작시켜 믹싱하여 혼합물을 만든 후, 성형틀에 해당 혼합물을 투입하는 성형틀투입단계(S400)와; 압착성형기에 상기 성형틀을 투입하고, 500 ~ 1,000kg/㎠ 압력으로 가압하여 성형체를 만드는 성형체제조단계(S500)와; 상기 제조된 성형체가 포함된 성형틀을 멸균기에 투입하여 100 ~ 140℃의 온도에서 7 ~ 8시간 동안 멸균 처리하기 위한 멸균처리단계(S600)와; 상기 멸균 처리된 성형체가 포함된 성형틀을 크린룸에 투입하여 20 ~ 25℃의 온도로 10~20분 동안 냉각 처리하기 위한 냉각처리단계(S700)와; 상기 냉각 처리된 성형체가 포함된 성형틀을 60일 내지 90일 정도 종균 배양하고, 종균 배양 후 잘게 부순 후, 성형체에 배양된 버섯균 혹은 고상 종균을 투입하여 25 ~ 28℃의 온도로 3개월 정도 숙성시켜 바인딩하기 위한 천연바인딩처리단계(S800);를 포함하여 이루어짐으로써, 본 발명의 과제를 해결하게 된다.
20 to 35 parts by weight of rice husk, 20 to 35 parts by weight of carbonized rice husk and 20 to 35 parts by weight of sawdust are prepared and the contents are prepared to prepare 10 to 20 parts by weight of a reinforcement material of any one of rice straw, Step SlOO; A moisture controlling step (S200) of adding the prepared contents to a mixer containing water to make the water content 65%; A sugar supplying step (S300) for adding 5 to 10 parts by weight of sugar to a blender containing the contents having the moisture content of 65%; (S400) of operating a mixer to mix the mixture to form a mixture, and then injecting the mixture into a mold; (S500) of injecting the molding die into a compression molding machine and pressing the molding die at a pressure of 500 to 1,000 kg / cm < 2 > (S600) a sterilization treatment step (S600) for sterilizing the molding body containing the molded body at a temperature of 100 to 140 DEG C for 7 to 8 hours by charging the molding body into the sterilizer; A cooling treatment step (S700) for putting the molding frame containing the sterilized molded article into a clean room and performing cooling treatment at a temperature of 20 to 25 DEG C for 10 to 20 minutes; The molded mold containing the cooled molded article is cultured for about 60 to 90 days. After the seed culture, it is finely crushed, and the mushroom bacteria or solid phase bacteria cultured in the molded article are added thereto. And a natural binding processing step (S800) for binding by aging. The present invention solves the problems of the present invention.
본 발명에 의해, 자연계에 있는 천연재료에 버섯균 혹은 고상종균과 같은 미생물을 바인더로 활용하여 천연 단열 보드를 제공하도록 함으로써, 환경호르몬이나 유해한 분진이 배출되지 않는 효과와 종래의 단열보드보다 가벼우며 탄력성이 좋고 더 견고한 천연 단열 보드를 제공하게 된다.According to the present invention, by providing a natural heat insulating board by using microorganisms such as mushroom bacteria or solid phase bacteria as a binder in a natural material in a natural environment, it is possible to prevent the release of environmental hormones and harmful dust, Providing a more resilient and more rugged natural insulation board.
또한, 천연 단열 보드에 무기질 도료를 이용하여 방수 처리와 발수 처리하거나, 은나노 코팅을 수행하여 항균 처리 및 곰팡이 제거를 수행함으로써, 기능성 단열보드를 제공하게 된다.In addition, a functional insulating board is provided by performing waterproofing and water repellent treatment with a natural paint on a natural heat insulating board, or by performing antimicrobial treatment and mold removal by performing silver nano coating.
또한, 천연 단열 보드 상면에 폐면, 면실박을 형성시켜 결속력을 제공하도록 함으로써, 금이 가되, 부러지지 않는 효과를 제공하게 된다.In addition, by forming a closed face and a cotton foil on the upper surface of the natural insulating board to provide a binding force, it is possible to provide a cracked but non-breaking effect.
또한, 다공성 난연성 불연성의 천연소재들로 구성되어 건축내장재(벽체, 천정, 지붕하부)와 외장재(벽체단열층, 처마단열층)와 흡음재 또는 차음재로서 층간소음을 없애는 곳에 활용이 가능하며, 사람이 지나 다니는 곳에 잔디의 녹화를 위한 식생보드 또는 녹화보드로 이용이 가능하며, 이후 식생보드로 사용시 잔디의 번식 또는 활착이 끝나면 추후에 스스로 분해되어 잔디의 양분으로 변화하거나 자연계로 돌아가는 기능을 수행하는 효과를 제공하게 된다.It is made of porous, flame-retardant and nonflammable natural materials, and can be used in building interiors (wall, ceiling, roof bottom), exterior materials (wall insulation layer and insulation layer) and sound absorbing materials or sound insulating materials, It can be used as a vegetation board or a green board for greening of grass in the place, and when it is used as a vegetation board, when it is breeding or staking of grass when it is finished, it is decomposed by itself in the future, .
또한, 한 번의 시공 후 관리가 안 되는 곳의 자연분해를 유도할 수 있는 곳에서 사용한다면 친환경적으로 분해가 되고 폐기물로서 남지 않는 장점과 예를 들어, 가두리 양식장의 부력재로 활용한다면 스티로폼가루로 인한 해양의 환경 오염을 방지할 수 있게 된다.In addition, if it is used in a place where it is possible to induce the natural decomposition of the place where management is not possible after one time of construction, it is advantageous that it is decomposed in an environmentally friendly manner and is not left as waste. For example, if it is used as a buoyancy material of cage farm, It is possible to prevent environmental pollution.
또한, 방화문의 내장재인 유리솜, 암면, 석면 등의 불연성 소재로서 사용하는 것의 대체품으로 사용이 가능하며, 용도에 따라 강도를 조절해 제작이 가능하므로 책상판재, 메모판, 바닥재, 부조, 노래방벽체, 포장박스 등으로 이용이 가능하게 된다.
In addition, it can be used as a substitute for non-combustible materials such as glass wool, rock wool, and asbestos, which are the interior materials of fire doors, and it can be manufactured by adjusting the strength according to the usage. So it can be used for desk board, memo board, flooring, Box or the like.
도 1은 본 발명의 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드 제조 방법을 나타낸 공정도.BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a process diagram showing a method for manufacturing a natural thermal insulation board that provides fire-retardant and flame retardant functions using mushroom germ as a binder of the present invention. FIG.
최근 단열 소재를 건축 내장재로 많이 이용하는데, 석면이나 환경호르몬 같은 물질로 인해 아토피 같은 병이 생기고 호흡기 질환, 불임, 발암성 물질로 인해 암 환자의 증가와 같은 병폐가 생기고 있기 때문에 이러한 발암물질을 포함한 환경 호르몬이 전혀 없는 친환경 소재의 다공성 물질로 단열재의 개발이 필요하게 되었다.Recently, insulation materials have been widely used as building interiors. Because of such diseases as asbestos and environmental hormones, diseases such as atopy, respiratory diseases, infertility, and carcinogenic substances, It is necessary to develop insulation material with porous material of eco-friendly material which has no environment hormone.
또한, 종래의 석면이나 암면 제품이나 유리솜 같은 부스러지는 소재들의 지하수로 유입되어 많은 병패를 양성하는 제품들은 폐기시킬 때 더욱 오염이 심하고 처리할 올바른 방법 또한 없기 때문에 건축폐기물법에 의하여 처리해야 한다.In addition, conventional waste products such as asbestos, rock wool, and glass wool that enter the ground water and produce many pieces of wastepaper should be handled by the Construction Waste Law because they are more polluted and there is no proper way to dispose of them.
본 발명의 과제를 해결하기 위하여, 불연 및 난연 기능을 제공하는 단열 보드 제조 방법은,In order to solve the problems of the present invention, a method of manufacturing an insulating board that provides a fire-
왕겨 20 ~ 35 중량부, 탄화왕겨 20 ~ 35 중량부, 톱밥 20 ~ 35 중량부를 준비하고, 볏집, 유독풀, 대나무잎, 탄화왕겨가루 중 어느 하나의 강도 보강재 10 ~ 20 중량부를 준비하는 내용물준비단계(S100)와; 상기 준비된 내용물을 물이 담긴 믹서기에 투입하여 함수율 65%로 만드는 수분조절단계(S200)와; 상기 함수율 65%인 내용물이 담긴 믹서기에 설탕 5 ~ 10 중량부를 투입하기 위한 당분제공단계(S300)와; 상기 믹서기를 동작시켜 믹싱하여 혼합물을 만든 후, 성형틀에 해당 혼합물을 투입하는 성형틀투입단계(S400)와; 압착성형기에 상기 성형틀을 투입하고, 500 ~ 1,000kg/㎠ 압력으로 가압하여 성형체를 만드는 성형체제조단계(S500)와; 상기 제조된 성형체가 포함된 성형틀을 멸균기에 투입하여 100 ~ 140℃의 온도에서 7 ~ 8시간 동안 멸균 처리하기 위한 멸균처리단계(S600)와; 상기 멸균 처리된 성형체가 포함된 성형틀을 크린룸에 투입하여 20 ~ 25℃의 온도로 10~20분 동안 냉각 처리하기 위한 냉각처리단계(S700)와; 상기 냉각 처리된 성형체가 포함된 성형틀을 60일 내지 90일 정도 종균 배양하고, 종균 배양 후 잘게 부순 후, 성형체에 배양된 버섯균 혹은 고상 종균을 투입하여 25 ~ 28℃의 온도로 3개월 정도 숙성시켜 바인딩하기 위한 천연바인딩처리단계(S800);를 포함하여 이루어지는 것을 특징으로 한다.20 to 35 parts by weight of rice husk, 20 to 35 parts by weight of carbonized rice husk and 20 to 35 parts by weight of sawdust are prepared and the contents are prepared to prepare 10 to 20 parts by weight of a reinforcement material of any one of rice straw, Step SlOO; A moisture controlling step (S200) of adding the prepared contents to a mixer containing water to make the water content 65%; A sugar supplying step (S300) for adding 5 to 10 parts by weight of sugar to a blender containing the contents having the moisture content of 65%; (S400) of operating a mixer to mix the mixture to form a mixture, and then injecting the mixture into a mold; (S500) of injecting the molding die into a compression molding machine and pressing the molding die at a pressure of 500 to 1,000 kg / cm < 2 > (S600) a sterilization treatment step (S600) for sterilizing the molding body containing the molded body at a temperature of 100 to 140 DEG C for 7 to 8 hours by charging the molding body into the sterilizer; A cooling treatment step (S700) for putting the molding frame containing the sterilized molded article into a clean room and performing cooling treatment at a temperature of 20 to 25 DEG C for 10 to 20 minutes; The molded mold containing the cooled molded article is cultured for about 60 to 90 days. After the seed culture, it is finely crushed, and the mushroom bacteria or solid phase bacteria cultured in the molded article are added thereto. And a natural binding treatment step (S800) for binding by aging.
한편, 부가적인 양상에 따라 상기 천연바인딩처리단계(S800) 이후에,On the other hand, according to an additional aspect, after the natural binding processing step (S800)
상기 숙성된 성형체가 포함된 성형틀을 건조기에 투입하여 50 ~ 60℃의 온도로 3시간 ~ 5시간 동안 건조한 후, 성형틀에서 성형체를 분리하여 천연 단열 보드를 획득하기 위한 천연단열보드획득단계(S900);를 더 포함하여 이루어지는 것을 특징으로 한다.A step of obtaining a natural heat insulating board for obtaining a natural heat insulating board by separating a molded body from a molding mold after the molding body containing the aged molded body is put into a dryer and dried at a temperature of 50 to 60 ° C for 3 hours to 5 hours (S900). ≪ / RTI >
한편, 다른 부가적인 양상에 따라, 상기 천연바인딩처리단계(S800) 이후에,On the other hand, according to another additional aspect, after the natural binding processing step (S800)
상기 숙성된 성형체가 포함된 성형틀을 건조기에 투입하여 50 ~ 60℃의 온도로 3시간 ~ 5시간 동안 건조한 후, 성형틀에서 성형체를 분리하여 천연 단열 보드를 획득하기 위한 천연단열보드획득단계(S900)와; 상기 획득된 천연 단열 보드에 무기질 도료를 이용하여 방수 처리와 발수 처리하기 위한 무기질도료처리단계(S1000)와; 상기 최종 처리된 천연 단열 보드를 절단기에 투입하여 일정한 규격으로 절단하기 위한 절단단계(S1100);를 더 포함하여 이루어지는 것을 특징으로 한다.A step of obtaining a natural heat insulating board for obtaining a natural heat insulating board by separating a molded body from a molding mold after the molding body containing the aged molded body is put into a dryer and dried at a temperature of 50 to 60 ° C for 3 hours to 5 hours S900); An inorganic paint treatment step (S1000) for water-repellent and water-repellent treatment of the obtained natural heat-insulating board using an inorganic paint; And a cutting step (S1100) for cutting the final heat-treated natural heat insulating board into a predetermined standard by feeding it into a cutter.
이때, 상기 무기질도료처리단계(S1000) 이후에,At this time, after the inorganic paint treatment step (S1000)
방수 처리와 발수 처리된 천연 단열 보드에 항균 처리 및 곰팡이 제거를 위하여 은나노 코팅을 수행하기 위한 은나노코팅단계(S1050);를 수행하는 것을 특징으로 한다.And a silver nano coating step (S1050) for performing silver nano coating for antibacterial treatment and fungus removal on the natural waterproofing and water-repellent board.
이때, 상기 무기질도료처리단계(S1000) 이후에, 결속력을 제공하기 위하여 폐면, 면실박 중 어느 하나를 골고루 뿌려주는 결속력강화단계를 수행하는 것을 특징으로 한다.In this case, after the inorganic paint treatment step (S1000), a binding force strengthening step for uniformly spraying either the closed face or the cotton foil is performed in order to provide binding force.
그리고, 상기의 제조 방법에 의해 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드를 제공하게 된다.In addition, the above-mentioned manufacturing method provides a natural insulating board that provides a fire-retardant and flame-retardant function utilizing mushroom germ as a binder.
이때, 상기 천연 단열 보드는,At this time,
부력재, 식생 블록 중 어느 하나에 적용되는 것을 특징으로 한다.Buoyant material, vegetation block, and the like.
이하, 상기와 같은 종래의 문제점을 개선하고자 본 발명을 개시하게 된 것이며, 본 발명인 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드 제조 방법에 대해 상세히 설명하면 다음과 같다.
Hereinafter, the present invention has been described in order to overcome the above-mentioned problems of the prior art, and a method of manufacturing a natural insulating board using the mushroom germ as a binder to provide a fireproof and flame retardant function will be described in detail.
1. 내용물준비단계(S100)1. Preparation of contents (S100)
왕겨 20 ~ 35 중량부, 탄화왕겨 20 ~ 35 중량부, 톱밥 20 ~ 35 중량부를 우선적으로 준비하게 된다.20 to 35 parts by weight of rice husk, 20 to 35 parts by weight of carbonized rice husk, and 20 to 35 parts by weight of sawdust are prepared in advance.
그리고, 볏집, 유독풀, 대나무잎, 탄화왕겨가루 중 어느 하나의 강도 보강재 10 ~ 20 중량부를 준비하게 된다.Then, 10 to 20 parts by weight of a reinforcing material selected from the group consisting of rice straw, poisonous grass, bamboo leaf and carbonized rice flour is prepared.
상기와 같이, 왕겨, 탄화왕겨, 톱밥 등과 같은 자연소재를 결속시키기 위하여(바인딩처리) 버섯 균을 사용하게 되는 것이다.As described above, in order to bind natural materials such as rice husks, carbonized rice husks, sawdust and the like (binding treatment), mushroom bacteria are used.
본 발명의 천연 단열 보드를 만드는데 왕겨를 사용하는 이유는 왕겨의 경우에 다공성 기공이 존재하고, 왕겨는 불에 타더라도 무기질 성분인 SiO2로 존재하여 불의 확산을 막게 된다. The reason for using the rice hulls to make the natural heat insulating board of the present invention is that the porous hulls exist in the case of rice hulls, and the rice hulls are present as SiO 2 , which is an inorganic component,
왕겨도 SiO2 성분을 함유하고 있는데, 별도의 탄화왕겨와 탄화왕겨가루를 넣어주는 이유는 미세조직 공간을 만들어 주기 위해서이다.The rice husks also contain the SiO 2 component, and the reason for putting separate carbonized rice husk and carbonized rice husk powder is to make a microstructure space.
또한, 톱밥을 사용하는 이유는 톱밥의 경우에는 나무를 갈아 만들어졌기 때문에 수분을 흡수하고 발수하는 기능을 제공하기 때문이며, 버섯균 혹은 고상 종균을 수월하게 활착시키기 위한 조건을 만들기 위한 것이다.
The reason for using sawdust is that, in the case of sawdust, it is made by grinding wood to provide water-absorbing and water-repellent function, and is intended to make conditions for easily activating mushroom bacteria or solid phase bacteria.
2. 수분조절단계(S200)2. Moisture regeneration step (S200)
상기 준비된 내용물을 물이 담긴 믹서기에 투입하여 함수율 65%로 조절하는 과정을 거치게 된다.
The prepared contents are put into a blender containing water to adjust the water content to 65%.
3. 당분제공단계(S300)3. Sugar providing step (S300)
상기 함수율 65%인 내용물이 담긴 믹서기에 설탕 5 ~ 10 중량부를 투입하여 버섯균 혹은 고상 종균이 번식할 수 있는 환경을 제공하게 되는 것이다.
5 to 10 parts by weight of sugar is added to the blender containing the contents having the moisture content of 65%, thereby providing an environment in which mushroom bacteria or solid phase bacteria can reproduce.
4. 성형틀투입단계(S400)4. Step of injecting mold (S400)
이후, 상기 믹서기를 동작시켜 물에 내용물과 설탕을 혼합하여 혼합물을 만든 후, 성형틀에 해당 혼합물을 투입하게 되는 것이다.Thereafter, the mixer is operated to mix the contents and sugar in water to prepare a mixture, and then the mixture is introduced into a molding mold.
이때, 바람직하게는 상기 성형틀의 하면에 한지나 망사 또는 부직포를 깔고, 상기 혼합물을 투입하고, 혼합물 상면에 다시 한지나 망사 또는 부직포를 깔을 수도 있다.
At this time, it is also possible to apply a piece of paper, a mesh or a non-woven fabric to the lower surface of the mold, insert the mixture, and lay the paper, mesh or nonwoven fabric on the upper surface of the mixture.
5. 성형체제조단계(S500)5. Molding step (S500)
이후, 압착성형기에 상기 성형틀을 투입하고, 500 ~ 1,000kg/㎠ 압력으로 가압하여 성형체를 만들게 된다.
Thereafter, the above-mentioned molding die is put into a compression molding machine and pressed at a pressure of 500 to 1,000 kg / cm < 2 >
6. 멸균처리단계(S600)6. Sterilization treatment step (S600)
상기 제조된 성형체가 포함된 성형틀을 압착성형기에서 이격시켜 다시 멸균기에 투입하여 100 ~ 140℃의 온도에서 2 ~ 3시간 동안 멸균 처리하는 과정을 거치게 된다.
The molding die including the molded body is separated from the compression molding machine and then put into a sterilizer and sterilized at a temperature of 100 to 140 ° C for 2 to 3 hours.
7. 냉각처리단계(S700)7. Cooling process step (S700)
상기 멸균 처리된 성형체가 포함된 성형틀을 크린룸에 투입하여 20 ~ 25℃의 온도로 10~20분 동안 냉각 처리하는 과정을 거치게 된다.
The mold having the sterilized molded article is put into a clean room and cooled at a temperature of 20 to 25 ° C for 10 to 20 minutes.
8. 천연바인딩처리단계(S800)8. Natural binding treatment step (S800)
이후, 상기 냉각 처리된 성형체가 포함된 성형틀을 60일 내지 90일 정도 종균 배양하고, 종균 배양 후 잘게 부순 후, 성형체에 배양된 버섯균 혹은 고상 종균을 투입하여 25 ~ 28℃의 온도로 3개월 정도 숙성시켜 성형체를 바인딩하게 되는 것이다.
Thereafter, the mold having the cooled molded body is cultured for about 60 to 90 days, and after the seed culture, it is crushed and finely crushed. The mushroom bacteria or the solid phase bacteria cultured in the molded body are then added, And aged for about a month to bind the formed body.
한편, 천연재료 중 바인더를 고령토나 황토같은 무기질 성분으로 한다면 고열로 가열을 해야 하며, 무게가 무거워지고 잘 깨지는 문제를 가지게 된다.On the other hand, if the binder of the natural material is an inorganic component such as kaolin or loess, it must be heated with high heat, and the weight becomes heavy and it is broken well.
그러나, 상기한 버섯균을 이용하여 바인더로 사용하게 된다면 버섯균이 목질 화되어 질긴 재질로 변화하므로 잘 깨지지 않는 특성을 제공하게 되는 것이다.However, if the above-mentioned mushroom microorganism is used as a binder, the mushroom microorganism becomes ligneous and is changed into a solid material, so that it is not broken.
또한, 친환경 소재의 다공성 단열재를 제공할 수 있으므로 자연계에 소재로서 자연계에서 스스로 분해할 수 있는 장점을 제공하기 때문에 친환경적으로도 안정적인 처리가 가능한 장점을 제공하게 되는 것이다.
In addition, since it is possible to provide a porous insulation material of an environmentally friendly material, it provides advantages of being able to be decomposed by itself in nature as a material in a natural world, and thus it is possible to provide an environmentally-
한편, 상기 천연바인딩처리단계(S800) 이후에, 성형체가 포함된 성형틀을 건조기에 투입하여 50 ~ 60℃의 온도로 3시간 ~ 5시간 동안 건조한 후, 성형틀에서 성형체를 분리하여 천연 단열 보드를 획득하기 위한 천연단열보드획득단계(S900)를 거치게 된다.Meanwhile, after the natural binding treatment step (S800), the forming mold including the molded body is put into a dryer and dried at a temperature of 50 to 60 ° C for 3 hours to 5 hours. Then, the molded body is separated from the molding mold, (S900) for acquiring the natural heat insulation board for obtaining the natural heat insulation board.
상기의 과정은 균사의 밀도를 높이는 숙성기간을 거쳐 버섯 균을 약한 열로 건조하면 버섯균이 사멸되고, 이것을 건조시키면 친환경 다공성 단열보드가 완성되는 것이다.In the above process, when mushroom bacteria are dried in weak heat after aging to increase the density of hyphae, mushroom bacteria are killed, and when dried, the eco-friendly porous heat insulating board is completed.
이후, 최종 처리된 천연 단열 보드를 절단기에 투입하여 일정한 규격으로 절단하기 위한 절단단계(S1100)를 거쳐 최종적으로 규격화된 단열 보드를 완성하게 되는 것이다.Thereafter, the finally processed natural heat insulating board is inserted into the cutter, and a cutting step S1100 is performed to cut the same into a predetermined standard, thereby completing the finalized standardized heat insulating board.
한편, 상기 절단단계 이전에 획득된 천연 단열 보드에 무기질 도료를 이용하여 방수 처리와 발수 처리하기 위한 무기질도료처리단계(S1000)를 거칠 수도 있다.On the other hand, the natural insulating board obtained before the cutting step may be subjected to an inorganic paint treatment step (S1000) for waterproof treatment and water repellent treatment using an inorganic paint.
즉, 무기질 도료인 실리카 혹은 액상유리를 이용하여 도포하게 되면 방수 처리와 발수 처리를 수행하여 방수 기능과 발수 기능을 제공할 수 있게 되는 것이다.That is, when silica or liquid glass, which is an inorganic paint, is applied, it is possible to provide a waterproof function and a water repellent function by performing waterproof treatment and water repellent treatment.
한편, 상기 무기질도료처리단계(S1000) 이후에, 천연 단열 보드에 항균 처리 및 곰팡이 제거를 위하여 은나노 코팅을 수행하기 위한 은나노코팅단계(S1050)를 수행할 수도 있다.Meanwhile, after the step of treating the inorganic paint (S1000), a silver nano coating step (S1050) may be performed to perform a silver nano coating for antibacterial treatment and fungus removal on the natural heat insulating board.
즉, 은나노 코팅을 통해 표면 처리를 하여 항균 기능과 곰팡이 제거가 가능하게 된다.In other words, surface treatment through silver nano coating enables antimicrobial function and mold removal.
또한, 상기 무기질도료처리단계(S1000) 이후에, 결속력을 제공하기 위하여 폐면, 면실박 중 어느 하나를 골고루 뿌려주는 결속력강화단계를 더 포함하여 이루어질 수 있는데, 이를 통해 결속력을 강화시켜 금이 가더라도 부러지지 않도록 할 수도 있을 것이다.Further, after the step (S1000) of treating the inorganic paint, it is possible to further include a binding force strengthening step of uniformly spraying any one of the closed face and the cotton cloth in order to provide a binding force. It may be possible to prevent it from being broken.
즉, 콘크리트의 견고성을 제공하기 위하여 철근을 삽입하는 공정을 수행하게 되는데, 이를 활용하여 철근 같은 역할을 하는 폐면, 면실박, 볏집 같은 천연소재를 깔거나, 길쭉하게 잘라 넣거나, 얇게 깍은 나무박판을 깔아 배양한다면 버섯균으로 이것을 바인딩 처리하여 견고한 합판으로도 제작이 가능하게 될 것이다.That is, a process of inserting reinforcing bars is performed in order to provide the rigidity of concrete. By using the reinforcing bars, it is possible to lay the natural materials such as the obtuse, the cotton, and the straw, which act like reinforcing bars, or cut them long, It will be able to bind it with mushroom germs and be able to make it with solid plywood.
그러면, 절단도 용이하고 못이나 피스 같은 것으로 부착하기가 용이하다.Then, cutting is easy and it is easy to attach such as nails or pieces.
그리고, 최종적으로 성형틀(금형 또는 몰드)에서 제품의 모양을 만드는 과정을 거쳐야 하기 때문에 어떠한 모양으로도 가능하고 다양한 무늬나 부착에 용이하도록 끼워질 수 있도록 더브테일 형태(
또한, 표면을 부조처럼 음각 또는 양각으로 금형 성형을 할 수가 있기 때문에 부조를 조각으로 만들어 조립하면 벽체나 천장을 장식하는 마감재로 사용이 가능하다.In addition, since the surface can be molded with embossed or embossed shapes like a relief, it can be used as a finishing material to decorate a wall or a ceiling by assembling a relief piece into a piece.
종래의 텍스는 다공성 기공을 만들기 위해 돌을 발포하여 다공성을 층으로 적층해 만들거나, 석고가 건조 후에 물이 있던 자리가 기공으로 남게 되는 것을 이용하여 석고보드를 만들고 있지만, 무게가 무겁고 잘 부서지는 특성을 가지고 있으며 특히, 수분에 취약하다는 단점을 가지고 있다.The conventional tex is made of a gypsum board by making a porous layer by foaming a stone to make a porous pore or by making a place where water is left as a pore after the gypsum is dried. However, the gypsum board is made by weight, And is particularly susceptible to moisture.
본 발명에서 종래의 내장재들과 차별화한 것은 자연계에 있는 천연재료와 미생물을 이용한 재료들의 결합방식으로서 환경호르몬이나 유해한 분진이 나오지 않는 장점을 가지고 있으며, 종래이 재료보다 가벼우며 탄력성이 좋고 더 견고하게 만들 수가 있는 장점을 제공하게 된다.The present invention distinguishes itself from the conventional interior materials in that natural materials and materials using microorganisms are combined with each other in nature and has an advantage of not emitting an environmental hormone or harmful dust and is made lighter than a conventional material, It will provide a number of advantages.
다만, 배양하고 건조하는 등의 제작 과정이 길어 인건 비용이 기존의 제품보다 많이 발생할 수는 있지만 농산물 부산물로서 만들기 때문에 원자재 값이 싸므로 가격 경쟁력은 오히려 월등할 수가 있을 것이다.However, since the production process such as cultivation and drying is long, the cost of labor can be higher than that of existing products, but since it is made as a by-product of agricultural products, the price of raw materials is cheap.
또한, 버섯균의 종류에 따라 균사가 목질화 되었을 때 더 질긴 것이 있는데, 예를 들자면, 느타리 버섯균사보다 표고버섯 균사가 목질화 되었을 때 더 질기고 표고버섯균보다 운지버섯이 더 질기다.Also, depending on the type of mushroom fungus, there is some tougher when the mycelium is lignified. For example, mushroom mycelia is more gruff than mushroom hyphae, and more fungus than shiitake mushroom.
배양 속도도 운지버섯이 표고버섯보다 빠르고 수분이 적어도 빠르게 진행되며 표고버섯은 배양 중에 다른 균(곰팡이종류)이 생기면 활착이 멈추고 끝나버리지만, 운지버섯은 진행도중에 같은 현상이 와도 곰팡이가 활동하지 못하는 건기에 배양을 이어서 나머지 빈 공간을 다 채우게 배양이 된다. The cultivation speed is faster than that of shiitake mushroom and the water is at least faster than that of shiitake mushroom. When the other mushroom (mold type) is produced during shiitake mushroom culture, the mushroom stops and ends with the action. However, It is cultured in the dry season to fill the remaining empty space.
그러므로, 어떤 버섯 균을 이용하느냐에 따라 제작 속도를 조절할 수 있으며, 목질화되는 강도가 높은 균을 잘 선택해야만 할 것이다.
Therefore, it is possible to control the production speed depending on which mushroom is used, and it is necessary to select a mushroom having high strength to be lignified.
이하에서 본 발명의 바람직한 실시예를 상세히 설명한다.Hereinafter, preferred embodiments of the present invention will be described in detail.
이하의 실시예들은 본 발명을 예증하기 위한 것으로 본 발명의 범위를 국한시키는 것으로 이해되어져서는 안될 것이다.
The following examples are intended to illustrate the invention and should not be construed as limiting the scope of the invention.
<실시예 1> 버섯균을 바인더로 활용한 천연 단열보드 제조<Example 1> Production of a natural thermal insulation board using mushroom germ as a binder
시중에서 왕겨 30 kg, 탄화왕겨 30kg, 톱밥 30kg을 구입하고, 볏집, 유독풀, 대나무잎, 탄화왕겨가루 중 강도 보강재로 대나무잎 10kg을 구입하여 준비한다.Purchase 30 kg of rice husks, 30 kg of carbonized rice husks, 30 kg of sawdust, and purchase 10 kg of bamboo leaves as reinforcement material in rice straw, poisonous grass, bamboo leaves and carbonized rice flour.
이후, 준비된 내용물을 물 65리터가 담긴 믹서기에 투입하여 함수율 65%로 만들게 된다.Then, the prepared contents are put into a mixer containing 65 liters of water to make the water content 65%.
이후, 믹서기에 설탕 5kg을 투입한 후, 믹서기를 동작시켜 믹싱하여 혼합물을 만든 후, 성형틀에 해당 혼합물을 투입하게 된다.Thereafter, 5 kg of sugar is put into a blender, and the blender is operated to mix the mixture to prepare a mixture.
이후, 압착성형기에 성형틀을 투입하고, 500kg/㎠ ~ 1,000kg/㎠ 압력으로 가압하여 성형체를 만들게 된다.Thereafter, the forming mold is put into a compression molding machine, and the molding is pressed at a pressure of 500 kg / cm 2 to 1,000 kg / cm 2 to form a molded body.
이후, 제조된 성형체가 포함된 성형틀을 멸균기에 투입하여 120℃의 온도에서 8시간 동안 멸균 처리하게 된다.
Thereafter, the mold with the formed molded article is put into a sterilizer and sterilized at a temperature of 120 캜 for 8 hours.
이후, 멸균 처리된 성형체가 포함된 성형틀을 크린룸에 투입하여 25℃의 온도로 20분 동안 냉각 처리하게 된다.Thereafter, the mold containing the molded article subjected to the sterilization treatment is put into a clean room and cooled at a temperature of 25 캜 for 20 minutes.
이후, 성형체가 포함된 성형틀을 70일 동안 종균 배양하고, 종균 배양 후, 잘게 부순 후, 성형체에 배양된 버섯균을 투입하여 28℃의 온도로 3개월 동안 숙성시켜 버섯균을 이용하여 종균 활착을 시키게 된다.Thereafter, the molding frame containing the molded body was cultured for 70 days, and after cultivation, the mushroom cultured in the molded body was added to the molded body, and aged at a temperature of 28 ° C for 3 months. .
즉, 천연 바인딩 처리 과정을 거치게 되는 것이다.That is, they are subjected to a natural binding process.
이후, 숙성된 성형체가 포함된 성형틀을 건조기에 투입하여 55℃의 온도로 3시간 동안 건조한 후, 성형틀에서 성형체를 분리하여 실시예1의 천연 단열 보드를 획득하게 된다.
Thereafter, the molding frame containing the aged molded body is placed in a dryer, dried at a temperature of 55 ° C for 3 hours, and then the molded body is separated from the molding frame to obtain the natural heat insulating board of Example 1.
<실시예 2> 무기질 바인더를 활용한 단열보드 제조<Example 2> Production of an insulating board using an inorganic binder
실시예1과 동일한 방법으로 단열보드를 제조하되, 버섯균 대신에 황토를 바인더로 사용하며, 내용물을 바인딩하기 위하여 최소 5kg을 준비하여 바인딩처리하였으며, 1,800℃의 온도로 가열하여 무기질 바인더 단열보드를 제조하였다.
A heat insulating board was prepared in the same manner as in Example 1 except that yellow earth was used as a binder instead of mushroom fungus and a minimum of 5 kg of binder was prepared to bind the contents and heated at 1,800 ° C to form an inorganic binder insulating board .
<실시예 3> 수지계열 바인더로 활용한 단열보드 제조≪ Example 3 > Production of an insulating board utilized as a resin-based binder
실시예1과 동일한 방법으로 단열보드를 제조하되, 버섯균 대신에 수지계열 바인더를 사용하며, 상온에서 수지계열 바인더 단열보드를 제조하였다.
A heat-insulating board was prepared in the same manner as in Example 1 except that a resin-based binder was used instead of mushroom fungus, and a resin-based binder insulating board was manufactured at room temperature.
상기한 실시예1, 실시예2, 실시예3에서 제조된 천연 단열 보드, 무기질 바인더 단열보드, 수지계열 바인더 단열보드의 무게는 무기질 바인더 단열보드가 천연 단열 보드 및 수지계열 바인더 단열보드보다 무겁고, 단단하기 때문에 탄력성이 없어 20kg/㎠ 압력으로 가압한 결과, 깨지는 문제점이 발생하였다.The weight of the natural insulating board, the inorganic binder insulating board, and the resin-based binder insulating board manufactured in Examples 1, 2, and 3 is such that the inorganic binder insulating board is heavier than the natural insulating board and the resin- It was not elastic because of its hardness. As a result of pressing at a pressure of 20 kg / cm2, a problem of breaking occurred.
따라서, 단열보드로 부적합함을 실험을 통해 알 수 있었다.Therefore, it was found through experiments that the board is not suitable as an insulating board.
또한, 상기 제조된 천연 단열 보드, 무기질 바인더 단열보드, 수지계열 바인더 단열보드에 화염방사기를 사용하여 화재시험 결과, 천연 단열 보드 및 무기질 바인더 단열보드의 경우에는 녹아내리거나 액체 상태의 연소물질을 발생시키지 않으며, 탄화 현상과 미량의 연기만을 발생시킬 뿐, 불씨가 남지 않아 소방 안전 기준에 최적임을 실험을 통해 확인할 수 있었다.As a result of the fire test using the flame radiator on the natural heat insulating board, the inorganic binder insulating board and the resin-based binder insulating board, the natural heat insulating board and the inorganic binder insulating board were melted or burned in a liquid state It is possible to confirm that it is optimal for fire safety standard because only carbonization phenomenon and only a small amount of smoke are generated and the fire is not left.
그러나, 수지계열 바인더 단열보드의 경우에는 다량의 유독 가스를 방출하며, 액체 상태의 연소물질을 발생시키면서 불씨가 남아 소방 안전 기준에 부적합함을 실험을 통해 확인할 수 있었다.However, in the case of the resin-based binder heat insulating board, it was confirmed through experiments that a large amount of toxic gas was emitted, and the flammable liquid was generated while generating the liquid state combustion material, thereby being incompatible with the fire safety standard.
상기한 실험예의 결과로 볼 때, 본 발명의 천연 단열 보드는 탄력성에서 우수하면서 소방 안전 기준에 최적의 조건을 만족시키고 있음을 알 수 있었다.As a result of the above experimental example, it can be seen that the natural heat insulating board of the present invention is excellent in elasticity and satisfies the optimum condition for the fire safety standard.
상기와 같은 기능을 제공하는 천연 단열 보드는 흡음재 혹은 방음벽으로 활용할 수 있지만, 부력재, 식생 블록 중 어느 하나에 적용될 수 있게 된다.The natural heat insulating board providing the above functions can be used as a sound absorbing material or a soundproofing wall, but it can be applied to any one of a buoyant material and a vegetation block.
부력재로 사용될 경우에는 스티로폼 대체제로 사용이 가능할 것이며, 식생 블록으로 사용될 경우에는 무거운 종래의 블록 대체제로 사용이 가능할 거이다.When used as a buoyant material, it can be used as a substitute for styrofoam. When used as a vegetation block, it can be used as a heavy conventional block replacement agent.
또한, 건물 내장재로 활용할 경우에는 단열, 흡음, 방음 기능을 제공할 수 있을 것이며, 야외에서 활용할 경우에는 난연성 혹은 불연성 재료로 사용이 가능할 것이다.In addition, when used as a building interior material, it will be able to provide insulation, sound absorption and soundproofing function, and it can be used as a flame retardant or incombustible material when used outdoors.
이는 실리카 성분을 함유하고 있기 때문에 가능하다.This is possible because it contains a silica component.
또한, 불이 붙지 않으면서 화학 가스를 배출하지 않게 된다.In addition, the chemical gas is not discharged without being ignited.
이는 석유 화학 성분을 함유하고 있지 않기에 가능하며, 환경호르몬도 배출되지 않아 친환경 소재로 널리 활용할 수 있게 될 것이다.This is possible because it does not contain petrochemical components, and environmental hormones are not emitted, making it widely available as environmentally friendly materials.
상기와 같은 내용의 본 발명이 속하는 기술분야의 당업자는 본 발명의 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시 예들은 모든 면에서 예시된 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. It will be understood by those skilled in the art that the present invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. It is to be understood, therefore, that the embodiments described above are to be considered in all respects as illustrative and not restrictive.
본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위에 의하여 나타내어지며, 특허청구 범위의 의미 및 범위 그리고 그 등가 개념으로부터 도출되는 모든 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
The scope of the present invention is defined by the appended claims rather than the detailed description and all changes or modifications derived from the meaning and scope of the claims and their equivalents are to be construed as being included within the scope of the present invention do.
S100 : 내용물준비단계
S200 : 수분조절단계
S300 : 당분제공단계
S400 : 성형틀투입단계
S500 : 성형체제조단계
S600 : 멸균처리단계
S700 : 냉각처리단계
S800 : 천연바인딩처리단계S100: Contents preparation step
S200: moisture control step
S300: Sugar serving step
S400: Step of injecting mold
S500: Molding step
S600: sterilization treatment step
S700: Cooling process step
S800: natural binding processing step
Claims (2)
왕겨 20 ~ 35 중량부, 탄화왕겨 20 ~ 35 중량부, 톱밥 20 ~ 35 중량부를 준비하고, 볏집, 유독풀, 대나무잎, 탄화왕겨가루 중 어느 하나의 강도 보강재 10 ~ 20 중량부를 준비하는 내용물준비단계(S100)와;
상기 준비된 내용물을 물이 담긴 믹서기에 투입하여 함수율 65%로 만드는 수분조절단계(S200)와;
상기 함수율 65%인 내용물이 담긴 믹서기에 설탕 5 ~ 10 중량부를 투입하기 위한 당분제공단계(S300)와;
상기 믹서기를 동작시켜 믹싱하여 혼합물을 만든 후, 성형틀에 해당 혼합물을 투입하는 성형틀투입단계(S400)와;
압착성형기에 상기 성형틀을 투입하고, 500 ~ 1,000kg/㎠ 압력으로 가압하여 성형체를 만드는 성형체제조단계(S500)와;
상기 제조된 성형체가 포함된 성형틀을 멸균기에 투입하여 100 ~ 140℃의 온도에서 7 ~ 8시간 동안 멸균 처리하기 위한 멸균처리단계(S600)와;
상기 멸균 처리된 성형체가 포함된 성형틀을 크린룸에 투입하여 20 ~ 25℃의 온도로 10~20분 동안 냉각 처리하기 위한 냉각처리단계(S700)와;
상기 냉각 처리된 성형체가 포함된 성형틀을 60일 내지 90일 정도 종균 배양하고, 종균 배양 후 잘게 부순 후, 성형체에 배양된 버섯균 혹은 고상 종균을 투입하여 25 ~ 28℃의 온도로 3개월 정도 숙성시켜 바인딩하기 위한 천연바인딩처리단계(S800);를 포함하여 이루어지는 것을 특징으로 하는 버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드 제조 방법.
A method of manufacturing an insulating board to provide a fireproof and flame retardant function,
20 to 35 parts by weight of rice husk, 20 to 35 parts by weight of carbonized rice husk and 20 to 35 parts by weight of sawdust are prepared and the contents are prepared to prepare 10 to 20 parts by weight of a reinforcement material of any one of rice straw, Step SlOO;
A moisture controlling step (S200) of adding the prepared contents to a mixer containing water to make the water content 65%;
A sugar supplying step (S300) for adding 5 to 10 parts by weight of sugar to a blender containing the contents having the moisture content of 65%;
(S400) of operating a mixer to mix the mixture to form a mixture, and then injecting the mixture into a mold;
(S500) of injecting the molding die into a compression molding machine and pressing the molding die at a pressure of 500 to 1,000 kg / cm < 2 >
(S600) a sterilization treatment step (S600) for sterilizing the molding body containing the molded body at a temperature of 100 to 140 DEG C for 7 to 8 hours by charging the molding body into the sterilizer;
A cooling treatment step (S700) for putting the molding frame containing the sterilized molded article into a clean room and performing cooling treatment at a temperature of 20 to 25 DEG C for 10 to 20 minutes;
The molded mold containing the cooled molded article is cultured for about 60 to 90 days. After the seed culture, it is finely crushed, and the mushroom bacteria or solid phase bacteria cultured in the molded article are added thereto. And a natural binding treatment step (S800) for binding by aging. The method for producing a natural insulating board using the mushroom germ as a binder to provide fire retardant and flame retardant functions.
버섯균을 바인더로 활용한 불연 및 난연 기능을 제공하는 천연 단열 보드.
A process for producing a polyurethane foam comprising the steps of:
Natural insulation boards that provide fire-retardant and flame-retardant functions using mushroom germ as a binder.