KR20170045814A - High flame retardant resin composition and uses thereof - Google Patents
High flame retardant resin composition and uses thereof Download PDFInfo
- Publication number
- KR20170045814A KR20170045814A KR1020150145742A KR20150145742A KR20170045814A KR 20170045814 A KR20170045814 A KR 20170045814A KR 1020150145742 A KR1020150145742 A KR 1020150145742A KR 20150145742 A KR20150145742 A KR 20150145742A KR 20170045814 A KR20170045814 A KR 20170045814A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- resin composition
- flame retardant
- plasticizer
- Prior art date
Abstract
Description
본 발명은 고난연성 수지 조성물과 이를 이용한 절연체 및 전선에 관한 것으로, 상세하게는 베이스 수지인 중합도가 800~2,000인 폴리염화비닐(PVC) 수지 100 중량부에 대하여, 8~12 중량부의 삼산화안티몬(Sb2O3), 18~22 중량부의 붕산아연(Zinc Borate) 및 45~55 중량부의 하이드로 마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O)의 배합비를 갖는 난연제를 포함하는 것을 특징으로 하는 고난연성 수지 조성물과 이를 이용한 절연체 및 전선에 관한 것이다.The present invention relates to a high flame retardant resin composition and an insulator and a wire using the same. More specifically, the present invention relates to a high flame retardant resin composition comprising 8 to 12 parts by weight of antimony trioxide Sb 2 O 3), 18 ~ 22 parts by weight of a zinc borate flame retardant agent having the compounding ratio of the (zinc borate) and 45-55 parts by weight of a hydro-magnesite (hydromagnesite, Mg 4 (OH) 2 (CO 3) 3 and 3H 2 O) And an insulator and a wire using the resin composition.
종래 기술의 난연 전선의 도체 피복용 절연체로는 크게 할로겐계와 금속 수산화물을 이용한 비할로겐계 난연 재료의 두 가지가 널리 사용되고 있다. 할로겐계 난연 재료는 난연성이 우수하지만, 화재 시 유독성 기체를 방출하며, 독성 지수가 1.5 이하인 난연성 피복 재료를 구현하기 어려워 안전성, 환경 친화성 면에서 문제가 있다. 따라서 점차 엄격해지는 환경 규제 때문에 할로겐계 난연 전선의 사용은 앞으로 지양할 수밖에 없는 실정이다. Halogen-based flame retardant materials and halogen-based flame retardant materials using metal hydroxides are widely used as insulators for covering conductors of prior art flame retardant wires. The halogen-based flame retardant material is excellent in flame retardancy, but it has a problem in terms of safety and environmental friendliness since it is difficult to realize a flame retardant coating material having a toxicity index of 1.5 or less, which releases toxic gases in the event of a fire. Therefore, the use of halogen-based flame retardant wires is inevitable in the future due to the increasingly stringent environmental regulations.
금속 수산화물 등의 무기 난연제는 안전성 면에서는 할로겐계 난연제에 비해 우수하지만, 난연성이 높지 않기 때문에 원하는 난연성 수준에 이르기 위해서는 다량의 무기 난연제를 사용해야 한다. 과량의 금속 수산화물 난연제 때문에 압출 선속 등의 가공성이 떨어지고 전선의 물성이 저하되는 단점이 있다. 특히 이러한 무기 난연 전선은 유연성과 내마모성이 부족하다.Inorganic flame retardants such as metal hydroxides are superior to halogen-based flame retardants in terms of safety. However, since the flame retardancy is not high, a large amount of inorganic flame retardants must be used in order to achieve desired flame retardancy. An excessive amount of metal hydroxide flame retardant causes a drawback in that the processability such as an extruded flux and the like deteriorates and the physical properties of the wire deteriorate. In particular, these inorganic flame retardant wires lack flexibility and abrasion resistance.
한편, 내유성을 향상시키기 위하여 종래 기술에서 극성 작용기를 높은 비율로 함유하는 고분자 수지 또는 녹는점이 높은 결정성 수지를 사용한 도체 피복용 절연 재료를 선보인 바 있다. 그러나 결정성 수지는 상온에서 강성이 매우 높아 딱딱하므로 유연성이 낮으므로, 굴곡에 대한 내구성이 낮아 설치 후에도 파손 우려가 있다. 또한, 극성 작용기를 높은 비율로 함유하는 고분자 수지를 절연 재료로 사용한 전선은 동적 눌림에 대한 저항성이 낮아 변형이 쉽게 발생한다. On the other hand, in order to improve oil resistance, a polymeric resin containing a high proportion of polar functional groups or an insulating material for covering a conductor using a crystalline resin having a high melting point has been disclosed in the prior art. However, since the crystalline resin has a very high rigidity at room temperature, the flexibility is low since it is hard, so that the durability against bending is low, and there is a risk of breakage even after installation. In addition, a wire using a polymer resin containing a polar functional group at a high ratio as an insulating material has a low resistance to dynamic pressing, and therefore is easily deformed.
따라서 이러한 재료를 사용하면 유연한 전선을 얻지만 그러한 전선은 변형 우려가 있어 응력 또는 압력이 작용하는 부분에는 설치하기 어렵다는 단점이 있다.The use of these materials, however, has the disadvantage of being able to obtain flexible wires, but such wires are subject to deformation and are difficult to install in areas where stress or pressure is present.
상기한 문제점들을 보완하기 위하여, 다양한 연구들이 진행되어 왔으며, 그중에서도 전선에 사용되는 수지 조성물에 포함되는 재료의 성분 또는 함량을 조절하여 난연성을 증진시키고자 노력하였다. 일례로, 한국등록특허 제0737598호에 중합도가 800 내지 2,000인 폴리염화비닐(PVC) 수지를 기본수지로 사용하며, 상기 기본수지 100 중량부에 대해, 40 내지 80 중량부의 가소제; 50 내지 100 중량부의 난연제; 1 내지 10 중량부의 난연 보조제; 및 0.5 내지 20 중량부의 연기 억제제; 를 포함하여 이루어진 것을 특징으로 하는 저발연 고난연성 재료용 조성물과 이를 이용한 절연체 및 전선에 관한 기술이 개시되어 있으며, 한국등록특허 제1115679호에 염화비닐계 수지, 테레프탈산 에스테르 화합물을 포함하는 가소제, 칼슘-아연(Ca-Zn)계 안정제, 및 삼산화안티몬(Sb2O3)을 선택적으로 포함하는 난연제를 포함하여 이루어지는 것으로서, 특히 PVC 코팅 얀(yarn)에 적용되는 친환경성 염화비닐계 수지 조성물에 관한 기술이 개시되어 있고, 중국공개특허 제2013-10081760호에 폴리염화비닐(PVC) 92~100, 에어로질 10~16, 활석분 7~10, Wollastonite 분말 6~8, 3 (2-염소 에틸) 인산염 3~4, 2 신 지방 3~4, 에틸 아크릴레이트 2~3, 산화 폴리에틸렌 왁스 5-6, 이중 스테아린 아미드 1~3, 삼산화안티몬 2~4, 항산화제 1~2, 붕산아연 2~3, 3 염기성 황산납 1~2, 변성 첨가제 10~15를 포함하는 난연성 도어용 PVC 플라스틱 판재 및 그의 제조방법에 관한 기술이 개시되어 있으나, 본원 발명에 따르는 난연제 배합비를 갖는 고난연성 수지 조성물과 이를 이용한 절연체 및 전선에 관한 기술은 개시된 바 없다. In order to overcome the above-mentioned problems, various studies have been conducted. Among them, efforts have been made to improve the flame retardancy by controlling the content or the content of the material included in the resin composition used for the wire. For example, in Korean Patent No. 0737598, a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 2,000 is used as a base resin and 40 to 80 parts by weight of a plasticizer is added to 100 parts by weight of the base resin; 50 to 100 parts by weight of a flame retardant; 1 to 10 parts by weight of a flame retardant aid; And 0.5 to 20 parts by weight of a smoke inhibitor; A composition for a low flammability and high flame retardant material, and an insulator and a wire using the same are disclosed. Korean Patent No. 1115679 discloses a composition comprising a vinyl chloride resin, a plasticizer containing a terephthalic acid ester compound, calcium And a flame retardant selectively containing antimony trioxide (Sb 2 O 3 ), and more particularly to an environmentally friendly vinyl chloride resin composition applied to a PVC coated yarn (PVC) 92 to 100, aerosols 10 to 16, talc powder 7 to 10, wollastonite powder 6 to 8, and 3 (2-chloromethyl) are disclosed in Chinese Patent Laid-Open Publication No. 2013-10081760. Phosphate 3 ~ 4, 2 Shin fat 3 ~ 4, ethyl acrylate 2-3, oxidized polyethylene wax 5-6, double stearin amide 1-3, antimony trioxide 2-4, antioxidant 1-2, zinc borate 2-3 , Tribasic sulfuric acid lead (1 ~ 2), modified additives (10 ~ 15) Discloses a PVC plastic plate material for a flame-retardant door and a method of manufacturing the same. However, a highly flame retardant resin composition having a blending ratio of a flame retardant according to the present invention, and an insulator and a wire using the same, have not been disclosed.
본 발명은 상기와 같은 요구에 의해 도출된 것으로서, 본 발명의 고난연성 수지 조성물은 베이스 수지인 중합도가 800~2,000인 폴리염화비닐(PVC) 수지 100 중량부에 대하여, 25~40 중량부의 가소제; 9~15 중량부의 ESO계 가소제; 3~9 중량부의 안정제(stabilizer); 3~9 중량부의 아크릴계 수지; 8~12 중량부의 삼산화안티몬(Sb2O3), 18~22 중량부의 붕산아연(Zinc Borate) 및 45~55 중량부의 하이드로 마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O)를 포함하고, 상기 수지 조성물을 이용하여 제조한 전선의 난연성이 종래의 수지 조성물을 이용하여 제조한 전선보다 난연성이 우수하다는 것을 확인함으로써, 본 발명을 완성하였다.The present invention provides a highly flame-retardant resin composition comprising 25 to 40 parts by weight of a plasticizer based on 100 parts by weight of a polyvinyl chloride (PVC) resin having a degree of polymerization of 800 to 2,000 as a base resin; 9-15 parts by weight of an ESO plasticizer; 3 to 9 parts by weight of a stabilizer; 3 to 9 parts by weight of an acrylic resin; 8 to 12 parts by weight of antimony trioxide (Sb 2 O 3 ), 18 to 22 parts by weight of zinc borate and 45 to 55 parts by weight of hydro-magneite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O), and confirming that the flame retardancy of the wire produced by using the resin composition is superior to that of the wire made using the conventional resin composition, thereby completing the present invention.
상기 목적을 달성하기 위하여, 본 발명은 베이스 수지인 중합도가 800~2,000인 폴리염화비닐(PVC) 수지 100 중량부에 대하여, 25~40 중량부의 가소제; 9~15 중량부의 ESO계 가소제; 3~9 중량부의 안정제(stabilizer); 3~9 중량부의 아크릴계 수지; 8~12 중량부의 삼산화안티몬(Sb2O3), 18~22 중량부의 붕산아연(Zinc Borate) 및 45~55 중량부의 하이드로 마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O)를 포함하는 고난연성 수지 조성물을 제공한다.In order to attain the above object, the present invention provides a resin composition comprising: 25 to 40 parts by weight of a plasticizer, based on 100 parts by weight of a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 2,000 as a base resin; 9-15 parts by weight of an ESO plasticizer; 3 to 9 parts by weight of a stabilizer; 3 to 9 parts by weight of an acrylic resin; 8 to 12 parts by weight of antimony trioxide (Sb 2 O 3 ), 18 to 22 parts by weight of zinc borate and 45 to 55 parts by weight of hydro-magneite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O). ≪ / RTI >
또한, 본 발명은 상기 고난연성 수지 조성물을 이용하여 제조되는 것을 특징으로 하는 고난연성 절연체를 제공한다. Further, the present invention provides a highly flame-retardant insulator which is produced by using the above-mentioned flame-retardant resin composition.
또한, 본 발명은 상기 고난연성 절연체를 이용하여 피복된 것을 특징으로 하는 전선을 제공한다.Further, the present invention provides an electric wire coated with the high flame-retardant insulator.
본 발명은 고난연성 수지 조성물과 이를 이용한 절연체 및 전선에 관한 것이다. 본 발명에 따른 고난연성 수지 조성물은 베이스 수지인 중합도가 800~2,000인 폴리염화비닐(PVC) 수지 100 중량부에 대하여, 25~40 중량부의 가소제; 9~15 중량부의 ESO계 가소제; 3~9 중량부의 안정제(stabilizer); 3~9 중량부의 아크릴계 수지; 8~12 중량부의 삼산화안티몬(Sb2O3), 18~22 중량부의 붕산아연(Zinc Borate) 및 45~55 중량부의 하이드로 마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O)를 포함하는 것이다. 본 발명에 따른 고난연성 수지 조성물은 난연제의 배합비에 의해 종래의 제품보다 난연성이 증진될 뿐만 아니라, 화재 시에도 PVC 수지가 열에 의해 녹에 흘러내리는 현상이 거의 나타나지 않는 효과가 있는 것이다. The present invention relates to a high flame retardant resin composition and an insulator and a wire using the same. The high flame retardant resin composition according to the present invention comprises 25 to 40 parts by weight of a plasticizer based on 100 parts by weight of a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 2,000 as a base resin; 9-15 parts by weight of an ESO plasticizer; 3 to 9 parts by weight of a stabilizer; 3 to 9 parts by weight of an acrylic resin; 8 to 12 parts by weight of antimony trioxide (Sb 2 O 3 ), 18 to 22 parts by weight of zinc borate and 45 to 55 parts by weight of hydro-magneite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O). The high flame retardant resin composition according to the present invention not only improves the flame retardancy by the blending ratio of the flame retardant agent but also hardly causes the PVC resin to flow down to the rust due to heat even during a fire.
본 발명은 베이스 수지인 중합도가 800~2,000인 폴리염화비닐(PVC) 수지 100 중량부에 대하여, 25~40 중량부의 가소제; 9~15 중량부의 ESO계 가소제; 3~9 중량부의 안정제(stabilizer); 3~9 중량부의 아크릴계 수지; 8~12 중량부의 삼산화안티몬(Sb2O3), 18~22 중량부의 붕산아연(Zinc Borate) 및 45~55 중량부의 하이드로 마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O)를 포함하는 고난연성 수지 조성물에 관한 것이다. The present invention relates to a resin composition comprising 25 to 40 parts by weight of a plasticizer based on 100 parts by weight of a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 2,000 as a base resin; 9-15 parts by weight of an ESO plasticizer; 3 to 9 parts by weight of a stabilizer; 3 to 9 parts by weight of an acrylic resin; 8 to 12 parts by weight of antimony trioxide (Sb 2 O 3 ), 18 to 22 parts by weight of zinc borate and 45 to 55 parts by weight of hydro-magneite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O). ≪ / RTI >
상기 삼산화안티몬(Sb2O3), 붕산아연(Zinc Borate) 및 하이드로 마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O)의 배합비율은 상기한 중량부를 사용하는 것이 바람직하지만, 그 중에서 1:2:5의 중량비인 것이 가장 바람직한 배합비율이다. 즉, 1:2:5의 중량비로 배합되었을 때의 난연성이 가장 우수한 것이다. The mixing ratio of the above antimony trioxide (Sb 2 O 3 ), zinc borate (Zinc Borate) and hydromagnesite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O) However, the most preferable mixing ratio is 1: 2: 5 by weight. That is, the flame retardancy is the most excellent when blended at a weight ratio of 1: 2: 5.
또한, 상기 가소제는 PVC 수지 조성물에 사용되는 가소제로서, 프탈산에스테르계(phthalates, DEHP, DINP, DBP 등), 인산계, 아디프산계(adipates, DHEA 등) 또는 세바트산 등의 지방산계, 에폭시계 등의 가소제를 사용할 수 있으며, 바람직하게는 프탈산에스테르계(phthalates, DEHP, DINP, DBP 등) 가소제이며, 가장 바람직하게는 DINP(diisononyl phthalate)인 것이지만 이에 제한하는 것은 아니다.The plasticizer is a plasticizer used in a PVC resin composition and may be a plasticizer such as phthalates, DEHP, DINP, DBP, phosphoric acid, adipates, DHAEA, sebacic acid, (DEHP, DINP, DBP, etc.) plasticizers, and most preferably DINP (diisononyl phthalate), but it is not limited thereto.
본 발명에서의 ESO(Epoxidized Soybean Oil)계 가소제는 PVC 수지와 난연제에 의해 강도가 떨어지는 것을 보완하는 효과가 있다. 아크릴계 수지를 포함함으로써, 가소제의 함량을 현저하게 줄일 수 있어 난연 효과를 증진시킬 뿐만 아니라, 배합물의 비산을 방지할 수 있으며, 압출 양을 향상시켜 생산량을 증가시키는 효과가 있다. The ESO (Epoxidized Soybean Oil) plasticizer according to the present invention has an effect of compensating for a decrease in strength due to PVC resin and flame retardant. By including the acrylic resin, the content of the plasticizer can be remarkably reduced, so that the flame retardant effect can be improved, the scattering of the compound can be prevented, and the amount of extrusion can be increased to increase the production amount.
상기 안정제는 무독성의 친환경 안정제인 Ca-Zn계 안정제 일 수 있으나, 이에 제한되지 않는다.The stabilizer may be a Ca-Zn stabilizer which is a non-toxic environmentally friendly stabilizer, but is not limited thereto.
또한, 본 발명은 상기 고난연성 수지 조성물을 이용하여 제조되는 것을 특징으로 하는 고난연성 절연체에 관한 것이다. Further, the present invention relates to a high flame-retardant insulator which is produced by using the above-mentioned flame-retardant resin composition.
또한, 본 발명은 상기 고난연성 절연체를 이용하여 피복된 것을 특징으로 하는 전선에 관한 것이다. Further, the present invention relates to an electric wire coated with the above flame-retardant insulator.
이하, 실시예를 이용하여 본 발명을 더욱 상세하게 설명하고자 한다. 이들 실시예는 오로지 본 발명을 보다 구체적으로 설명하기 위한 것으로 본 발명의 범위가 이들에 의해 제한되지 않는다는 것은 당해 기술분야에서 통상의 지식을 가진 자에게 있어 자명한 것이다. Hereinafter, the present invention will be described in more detail with reference to Examples. It is to be understood by those skilled in the art that these embodiments are merely illustrative of the present invention and that the scope of the present invention is not limited thereto.
실시예Example 1. 본원 발명에 따른 삼산화안티몬( 1. Antimony trioxide according to the present invention ( SbSb 22 OO 33 ), ), 붕산아연Zinc borate (( ZincZinc BorateBorate ) 및 ) And 하이드로Hydro 마그네사이트( Magnesite hydromagnesitehydromagnesite , , MgMg 44 (( OHOH )) 22 (CO(CO 33 )) 33 ㆍ3ㆍ 3 HH 22 OO )의 배합비가 1:2:5인 ) Is 1: 2: 5 고난연성High flammability 수지 조성물의 제조. Preparation of resin composition.
폴리염화비닐(poly vinyl chloride, PVC) 수지 100 중량부에 대하여, DINP 가소제 28 중량부, ESO계 가소제 12 중량부, 안정제(Ca-Zn계 안정제 : N080S) 6 중량부, 아크릴계 수지 6 중량부, 삼산화 안티몬(Sb2O3) 10 중량부, 붕산아연(Zinc Borate) 20 중량부, 및 하이드로마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O) 50 중량부를 포함하는 고난연성 수지 조성물을 제조하였다(표 1). , 28 parts by weight of a DINP plasticizer, 12 parts by weight of an ESO plasticizer, 6 parts by weight of a stabilizer (Ca-Zn stabilizer: N080S), 6 parts by weight of an acrylic resin, 100 parts by weight of a polyvinyl chloride (PVC) and containing antimony trioxide (Sb 2 O 3) 10 parts by weight of zinc borate (zinc borate) 20 parts by weight, and a hydro-magnesite (hydromagnesite, Mg 4 (OH) 2 (CO 3) 3 and 3H 2 O) 50 parts by weight A flame retardant resin composition was prepared (Table 1).
비교예Comparative Example 1. 삼산화안티몬( 1. antimony trioxide ( SbSb 22 OO 33 ), ), 붕산아연Zinc borate (( ZincZinc BorateBorate ) 및 ) And 하이드로Hydro 마그네사이트( Magnesite hydromagnesite, Mghydromagnesite, Mg 44 (OH)(OH) 22 (CO(CO 33 )) 33 ㆍ3ㆍ 3 HH 22 OO )의 배합비가 1.5:2.5:4.0인 ) Is 1.5: 2.5: 4.0 고난연성High flammability 수지 조성물의 제조. Preparation of resin composition.
폴리염화비닐(poly vinyl chloride, PVC) 수지 100 중량부에 대하여, DINP 가소제 28 중량부, ESO계 가소제 12 중량부, 안정제(Ca-Zn계 안정제 : N080S) 6 중량부, 아크릴계 수지 6 중량부, 삼산화 안티몬(Sb2O3) 15 중량부, 붕산아연(Zinc Borate) 25 중량부, 및 하이드로마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O) 40 중량부를 포함하는 고난연성 수지 조성물을 제조하였다(표 1). , 28 parts by weight of a DINP plasticizer, 12 parts by weight of an ESO plasticizer, 6 parts by weight of a stabilizer (Ca-Zn stabilizer: N080S), 6 parts by weight of an acrylic resin, 100 parts by weight of a polyvinyl chloride (PVC) 15 parts by weight of antimony trioxide (Sb 2 O 3 ), 25 parts by weight of zinc borate and 40 parts by weight of hydro-magneite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O) A flame retardant resin composition was prepared (Table 1).
비교예Comparative Example 2. 삼산화안티몬( 2. Antimony trioxide ( SbSb 22 OO 33 ), ), 붕산아연Zinc borate (( ZincZinc BorateBorate ) 및 ) And 하이드로Hydro 마그네사이트( Magnesite hydromagnesite, Mghydromagnesite, Mg 44 (OH)(OH) 22 (CO(CO 33 )) 33 ㆍ3ㆍ 3 HH 22 OO )의 배합비가 2:2:4인 ) Is 2: 2: 4 고난연성High flammability 수지 조성물의 제조. Preparation of resin composition.
폴리염화비닐(poly vinyl chloride, PVC) 수지 100 중량부에 대하여, DINP 가소제 28 중량부, ESO계 가소제 12 중량부, 안정제(Ca-Zn계 안정제 : N080S) 6 중량부, 아크릴계 수지 6 중량부, 삼산화 안티몬(Sb2O3) 20 중량부, 붕산아연(Zinc Borate) 20 중량부, 및 하이드로마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O) 40 중량부를 포함하는 고난연성 수지 조성물을 제조하였다(표 1). , 28 parts by weight of a DINP plasticizer, 12 parts by weight of an ESO plasticizer, 6 parts by weight of a stabilizer (Ca-Zn stabilizer: N080S), 6 parts by weight of an acrylic resin, 100 parts by weight of a polyvinyl chloride (PVC) 20 parts by weight of antimony trioxide (Sb 2 O 3 ), 20 parts by weight of zinc borate (Zinc Borate), and 40 parts by weight of hydromagnesite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O) A flame retardant resin composition was prepared (Table 1).
시험예Test Example 1. 본 발명의 1. The present invention 일실시예에In one embodiment 따른 전선의 난연성능의 시험(국제전기표준회의 기구( Test of flame retardant performance of electric wire according to IECIEC ) 시험 규격에 준한다)) According to the test standard)
본 시험예 1에서는 본 발명의 수지 조성물이 고난연 산소지수와 VCTF Cat.A 시험방법을 만족하는지 여부를 확인하고자 하였다. In Test Example 1, it was tried to confirm whether the resin composition of the present invention satisfied the hot oxygen index and the VCTF Cat.A test method.
삼산화안티몬, 붕산아연 및 하이드로 마그네사이트의 배합 비율을 조정하여 가소성 물질이 불꽃에 탈 때, 거의 흘러 내림이 없고, 타고 남은 재가 떨어지지 않고, 뭉쳐서 산소공급이 원하지 않도록 할 수 있는지 여부를 판단하였다. The mixture ratio of antimony trioxide, zinc borate and hydro-magneite was adjusted to judge whether or not the abundant ashes did not fall off and the oxygen supply was not desired when the plastic material ran into the flame.
1) 적용범위: 불(fire)에 대한 전선의 난연 테스트1) Applicable scope: Flame retardant test of electric wire against fire
2) 시험편 준비: 완성품에서 3.5m 길이로 시험편을 준비하고, 연소할 수 있는 물질의 총 부피에 따라 다음 3가지로 분류한다(카테고리 A: 7ℓ/m, 카테고리 B: 3.5ℓ/m, 카테고리 C: 1.5ℓ/m).2) Preparation of test specimens: Prepare test specimens 3.5m long from the finished product and classify them according to the total volume of combustible materials (category A: 7ℓ / m, category B: 3.5ℓ / m, category C : 1.5 l / m).
3) 시험 전처리 35SQ 이상: 케이블 외경의 ½ 간격으로 배열하나(20mm 이하) 케이블 배열 폭이 300mm 초과시는 사다리 앞뒤, 양쪽에 배열한다.3) Test pre-treatment 35SQ or more: Arranged at intervals of cable outer diameter (20mm or less). Arrange cables on both sides of the ladder when the cable arrangement width is over 300mm.
4) 불꽃의 인가 시간은 카테고리 A, B는 48분이고, 카테고리 C는 20분으로, 평가 기준은 버너의 불을 끈 후, 케이블을 닦고 까맣다거나 불꽃 영향을 입은 부분의 케이블 앞 또는 뒤에서 측정한 길이가 버너의 일부분(일치한 부분에서) 2.5m 이상일 경우 불합격이다. 본 발명에서는 카테고리 A를 기준으로 평가하였다. 4) The duration of the flame application is 48 minutes for categories A and B, and 20 minutes for category C. The evaluation criteria is that the burner is turned off and the cable is cleaned and the length measured in front of or behind the cable in the black or spark affected area If the part of the burner is more than 2.5m (from the matched part), it is rejected. In the present invention, evaluation was made on the basis of category A.
상기 실시예 1, 비교예 1 및 비교예 3의 조성물을 이용하여 제조한 전선의 산소지수는 모두 동일한 값을 나타냈으나, 본 시험예에서 실시한 안정성 시험 결과는 하기 표 2에 개시한 바와 같이, 본 발명의 실시예 1의 조성물을 이용하여 제조한 전선의 경우, 합격하였으나, 비교예 1 및 2의 조성물을 이용하여 제조한 전선의 경우, 불합격하였다. Although the oxygen indexes of the wires prepared using the compositions of Example 1, Comparative Example 1 and Comparative Example 3 were all the same, the stability test results obtained in this Test Example were as shown in Table 2, The wires manufactured using the composition of Example 1 of the present invention were acceptable, but the wires manufactured using the compositions of Comparative Examples 1 and 2 were rejected.
또한, 본 발명의 제품이 고난연성을 가지면서도 인장강도와 신장률이 종래 제품과 동일하거나 더 우수하다는 것을 확인하였고, 본 발명의 수지 조성물로 제품을 생산하는 과정에서 비산이 방지되고, 제품의 생산성도 증진되는 효과가 있다는 것을 확인하였다.It is also confirmed that the product of the present invention has a high flame retardancy and a tensile strength and an elongation at the same or better than that of the conventional product. In the course of producing the product with the resin composition of the present invention, scattering is prevented, It is confirmed that there is an effect of enhancing.
따라서, 본 발명에 따른 제품의 난연성능이 기존 제품에 비해 우수하다는 것을 확인할 수 있었다. Therefore, it was confirmed that the flame retardant performance of the product according to the present invention is superior to the conventional product.
Claims (5)
25~40 중량부의 가소제; 9~15 중량부의 ESO계 가소제; 3~9 중량부의 안정제(stabilizer); 3~9 중량부의 아크릴계 수지; 8~12 중량부의 삼산화안티몬(Sb2O3), 18~22 중량부의 붕산아연(Zinc Borate) 및 45~55 중량부의 하이드로 마그네사이트(hydromagnesite, Mg4(OH)2(CO3)3ㆍ3H2O)를 포함하는 고난연성 수지 조성물.Based on 100 parts by weight of a polyvinyl chloride (PVC) resin having a polymerization degree of 800 to 2,000 as a base resin,
25 to 40 parts by weight of a plasticizer; 9-15 parts by weight of an ESO plasticizer; 3 to 9 parts by weight of a stabilizer; 3 to 9 parts by weight of an acrylic resin; 8 to 12 parts by weight of antimony trioxide (Sb 2 O 3 ), 18 to 22 parts by weight of zinc borate and 45 to 55 parts by weight of hydro-magneite (Mg 4 (OH) 2 (CO 3 ) 3 .3H 2 O). ≪ / RTI >
An electric wire coated with the flame-retardant insulator according to claim 4.