KR20160116100A - Method coating of fixture implant - Google Patents
Method coating of fixture implant Download PDFInfo
- Publication number
- KR20160116100A KR20160116100A KR1020150041615A KR20150041615A KR20160116100A KR 20160116100 A KR20160116100 A KR 20160116100A KR 1020150041615 A KR1020150041615 A KR 1020150041615A KR 20150041615 A KR20150041615 A KR 20150041615A KR 20160116100 A KR20160116100 A KR 20160116100A
- Authority
- KR
- South Korea
- Prior art keywords
- fixture
- implant
- coating
- acid
- surface treatment
- Prior art date
Abstract
Description
본 발명은 임플란트 표면처리시 골 유착 성능을 향상시킴과 동시에 픽스츄어 주위 잇몸에 염증(주위염)이 발생했을 경우 용이하게 치료할 수 있도록 한 코팅된 임플란트 픽스츄어에 관한 것이다.The present invention relates to a coated implant fixture which improves osseointegration performance during implant surface treatment and can be easily treated when inflammation (peripheral inflammation) occurs in the gum around the fixture.
특히, 본 발명은 픽스츄어 상단부에 칼슘포스페이트 코팅을 함으로써 임플란트 주위염 발생시 염산테트라싸이클린과 같은 항생제 처리를 통한 화학적인 치료방식을 적용하여 세균과 더불어 임플란트 픽스츄어 표면에 코팅된 칼슘포스페이트 코팅을 용해시켜 임플란트의 재골 유착이 가능토록 한 임플란트 픽스츄어 코팅방법에 관한 것이다. Particularly, according to the present invention, calcium phosphate coating is applied to the upper end of the fixture to apply a chemical treatment method by treating with antibiotics such as tetracycline hydrochloride in the case of periplasmic perimetry to dissolve calcium phosphate coating coated on the surface of the implant fixture together with bacteria, To an implant fixture coating method in which the bone graft can be made.
현대에는 치과 치료에 있어서 충치 또는 기타 사유에 의해 발치된 후 치아를 대체하기 위한 인공 치아로 임플란트가 사용되는 것이 일반적이다.In modern dental treatment, it is common that implants are used as artificial teeth to replace teeth after being caught by tooth decay or other reasons.
인공치아로 사용되는 임플란트는 인체에 전혀 해가 없는 재료를 사용하게 되며, 뼈와 잇몸이 없는 부분에 대해서 미용뿐만 아니라 기능까지 회복시키는 치료를 하게된다. 이런 임플란트를 이용한 치료로 인하여 기존의 치료 방법으로는 불가능했던 치료가 가능해져서, 더 편안하고 안정감 있는 회복으로 삶의 질을 높일 수 있는 장점이 있다.Implants used as artificial teeth will use materials that are harmless to the human body, and treat bone and gumless parts to restore beauty as well as function. These implants allow treatment that was not possible with conventional treatments, and thus have the advantage of improving the quality of life with a more comfortable and stable recovery.
일반적으로, 치과에서 사용하는 치과용 임플란트는 발치된 치아자리에 매식체를 골내에 식립하여 고정한 후, 자연치아 형태의 크라운을 결합하여 치아 기능을 수행하도록 하는 인공치아를 일컫는다. Generally, a dental implant used in a dentist refers to an artificial tooth that fixes and fixes a diaphragm in an extracted tooth position in the bone, and then performs a dental function by combining a natural tooth type crown.
또한 임플란트는 자연치아와 동일한 형상이며 충치가 발생하지 않으므로 반영구적으로 사용할 수 있다.Also, since the implant has the same shape as the natural tooth and does not cause tooth decay, it can be used semi-permanently.
이를 상세히 설명하면, 치과용 임플란트는 치조골에 식립되는 매식체와, 자연치아 형상의 크라운과, 상기 매식체와 크라운을 결합하는 어버트먼트로 이루어져 있는데, 상기 매식체는 골융합이 우수한 티타늄 또는 티타늄 합금으로 제조In detail, the dental implant is composed of an implant that is placed in the alveolar bone, a crown in the shape of a natural tooth, and an abutment that couples the implant to the crown. The implant has titanium or titanium alloy Manufactured in
된다.do.
치과용 임플란트의 시술은 잇몸을 절개한 후 치조골을 노출시킨 상태에서 매식체를 식립한 다음, 다시 잇몸을 봉합한다. 이후 매식체와 치조골이 완전한 골융합이 이루어지게 되면 상기 매식체에 어버트먼트를 고정하고, 어버트먼트를 매개로 하여 자연치아 형태의 크라운을 결합하게 된다.Dental implants are prepared by cutting the gums and exposing the alveolar bone, placing the diaphragm and then sealing the gums again. Then, when complete phytoal fusion is achieved in each phakic and alveolar bone, the abutment is fixed to the phakic body and the natural tooth type crown is coupled through the abutment.
이와 같은 치과용 임플란트 시술의 성공여부는 티타늄 재질의 매식체와 치조골 사이에 완전한 골 융합이 이루어지는 여부에 따라 결정된다. The success of such a dental implant procedure depends on whether complete bone fusion occurs between the titanium material and the alveolar bone.
상기 매식체의 외부 표면에는 골 융합을 증진시키기 위한 방법으로서 SLA 등 다양한 표면처리가 수행되고 있다.Various surface treatments such as SLA have been performed on the outer surface of the plate to improve bone fusion.
임플란트 표면처리(Implant Surface Treatment) 방법으로는 machined surface와 TPS, HA coating의 시기를 거쳐 RBM시대를 기반으로 SLA, SLActive 및 Fluoride, 각종 이온주입 등 다양한 표면활성화 기술이 선보이고 있다. Implant surface treatment methods include various surface activation technologies such as SLA, SLActive, Fluoride, and various ion implantation based on the RBM era through machined surface, TPS, and HA coating.
RBM과 함께 각광받고 있는 표면처리법은 SLA(Sandblast Large grit Acid etch)로 이는 RBM처럼 입자로 sandblasting한 후 여러 종류의 산으로 처리하는 방식이다. 입자의 크기나 종류, 그리고 처리하는 산의 종류에 따라 여러 복잡한 공정이 필요하다. 따라서 같은 SLA라고 통칭하더라도 실상은 그 차이는 RBM과 SLA의 차이만큼이나 다양한 격차가 존재한다.Surface treatment with RBM is SLB (Sandblast Large grit Acid etch) which is sandblasted with particles like RBM and treated with various kinds of acids. Depending on the particle size and type, and the type of acid to be treated, several complicated processes are required. Therefore, even if the same SLA is collectively referred to, the difference exists as much as the difference between RBM and SLA.
RBM에서 SLA로 그리고 HA표면처리나 양극산화법과 같이 임플란트 표면을 물리 화학적인 방법으로 개선하여 임플란트 표면을 활성화하려는 연구개발 외에도 최근에는 골 형성 세포의 부착을 증진하는 합성펩타이드나 BMP-2등 골 형성 단백질 등을 임플란트 표면에 적용하여 골조직 반응을 향상시키기 위한 바이오 기술을 개발하고자 하는 다양한 시도를 진행하고 있으나 임상에 적용하기까지는 다소 시간이 필요할 것으로 판단된다.In addition to R & D efforts to improve the surface of implants by RBM to SLA and to improve the surface of implants by physicochemical methods such as HA surface treatment or anodic oxidation, recently, there has been developed a synthetic peptide or BMP- It has been tried various ways to develop biotechnology to improve bone tissue reaction by applying protein to the surface of implants. However, it takes some time to apply it to clinical application.
이와 같이 표면처리된 임플란트는 저작기능을 회복하기 위한 성공적 시술과정도 중요하지만, 시술 후 임플란트의 표면을 청결한 상태로 유지하는 것이 중요하다. 임플란트와 관련된 합병증의 원인으로는 보철적 요인, 수술적 요인, 염증성 요인 등이 있으며, 이들 중 염증적 요인이 주요 원인으로 보고되고 있다. 구강내로 노출된 매식체의 표면에는 세균들이 번식하기 쉬운 환경에 노출되어 있고, 이 세균들은 자연치아와 동일하게 치조골에 염증을 유발하여 치과 질환을 일으킨다.It is important to maintain the surface of the implant clean after the procedure, although the successful procedure for restoring the masticatory function is also important. Prosthetic factors, surgical factors, inflammatory factors, and inflammatory factors are the main causes of complications related to implants. The surface of each exposed diaphragm is exposed to an environment in which bacteria can breed easily, and these bacteria cause irritation of the alveolar bone in the same way as natural teeth, causing dental diseases.
이와 같이 임플란트 주위염 발생시 종래의 임플란트 표면처리는 골 유착 성능을 향상시키기 위해 표면의 거칠기를 높이는 방안으로 진행되고 있는데, 임플 란트 주위염의 원인이 되는 박테리아 부착 성능 또한 증대되기 때문에 임플란트 주위염이 발생시 표면에 붙은 박테리아를 완전히 제거하기 힘든 문제점이 있다.In this way, when the peripheral implant of the implant is developed, the conventional surface treatment of the implant is proceeding to increase the surface roughness in order to improve the osseointegration performance. Since the bacterial adhesion performance which is the cause of the periplasmic surface of the implant is also increased, There is a problem that it is difficult to completely remove the bacteria.
이 분야의 선행기술을 살펴보면, 등록특허 제10-1359100호(등록일자 2014년01월28일)의 "임플란트 표면처리 방법"은 임플란트의 매식체를 표면처리 하는 방법으로서, 임플란트 매식체 표면의 오염원을 물리적으로 제거하는 전처리 단계; 상기 전처리된 임플란트 매식체 표면을 세정하는 제1 세정단계; 세정된 임플란트 매식체 표면의 병원균을 소독하는 소독단계; 및 상기 소독이 완료된 임플란트 매식체 표면을 세정하는 제2 세정단계; 를 포함하여 이루어지고,In the prior art of this field, "Implant surface treatment method" of Registration No. 10-1359100 (registered on Jan. 28, 2014) is a method of surface treating each implant of implant, A preprocessing step of physically removing the substrate; A first cleaning step of cleaning the surface of the preprocessed implantable material; A sterilizing step of disinfecting pathogens on the surface of the cleaned implant matrix; And a second cleaning step of cleaning the disinfected surface of the implant plate; , ≪ / RTI >
상기 소독단계는 제1 소독단계와 제2 소독단계로 이루어지고, 상기 제1 소독단계는 클로로헥시딘 글루콘산염을 사용하고, 상기 제2 소독단계는 차아염소산을 사용하는 것을 특징으로 하는 임플란트 매식체의 표면처리 방법이 개시되었다.Wherein the sterilization step comprises a first sterilization step and a second sterilization step, wherein the first sterilization step uses chlorohexidine gluconate and the second sterilization step uses hypochlorous acid. A method of surface treatment of each sheet has been disclosed.
상기 선행기술은 임플란트를 환자의 발치 부분에 심기 전에 일플란트 매식체 표면을 소독하여 임플란트 이식 후 치주염등이 발생하는 것을 방지하도록 하고 있으나, 임플란트를 이식 후 임플란트가 심어진 주변 잇몸에 염증이 발생할 경우 별도의 치료가 필요하며, 심할 경우 임플란트 잇몸 치료를 위해 잇몸 주변에 주사등에 의한 약물을 침투시켜 치료하는 과정에서 골 유착 성능이 떨어지거나 시간이 걸리는 문제점이 있다. The prior art is designed to sterilize the surface of a plant before implanting the implant on the extraction site of a patient to prevent the occurrence of periodontal disease after implantation. However, when the implant is implanted, In the case of severe gingivitis, the osseointegration performance is deteriorated or takes a long time in the process of infiltrating the gum around the gum by injecting drugs.
본 발명은 상기와 같은 문제점을 해결하기 위한 것으로서, 발치 후 인공치아로 잇몸에 심어지는 픽스츄어 상단부에 칼슘 포스페이트 코팅을 함으로써 임플란트 주위염 발생시 염산테트라싸이클린과 같은 항생제 처리를 통한 화학적인 치료방식을 적용하여 세균과 더불어 임플란트 표면에 코팅된 칼슘포스페이트 코팅을 용해시켜 임플란트의 재골 유착을 가능토록 함을 목적으로 한 임플란트 픽스츄어 코팅방법에 관한 것이다. The present invention has been made to solve the above-mentioned problems, and it is an object of the present invention to provide a calcium phosphate coating on the upper part of a fixture, which is implanted in a gum with an artificial tooth after extraction to apply a chemical treatment method by treating antibiotics such as tetracycline hydrochloride, And an implant fixture coating method for dissolving a calcium phosphate coating coated on the surface of an implant so as to allow the bone to be bonded to the implant.
본 발명의 목적을 달성하기 위한 것으로서, 치아의 발치부에 식립하기 위한 임플란트의 픽스츄어 표면에 잔류된 가공유를 세정하는 단계;To accomplish the object of the present invention, there is provided a method of cleaning a tooth of a tooth, comprising the steps of: cleaning the machining oil remaining on the surface of a fixture of an implant for placement on a tooth of a tooth;
상기 세정 후 픽스츄어 표면에 조대한 거칠기 부여를 위해 하이드록시 아파타이트를 이용한 블라스팅 표면처리 단계:A blast surface treatment step using hydroxyapatite to impart roughness to the surface of the fixture after the cleaning;
상기 블라스팅 후 픽스츄어 표면에 남아있는 블라스팅 물질 제거를 위해 60℃의 고온 질산에 담지하는 전처리 단계: A pretreatment step of carrying on the high temperature nitric acid at 60 DEG C for removing the blast material remaining on the surface of the fixture after the blasting,
상기 전처리 후 건조한 다음 픽스츄어 표면을 황산 및 염산을 이용하여 80℃ 이상 고온에서 산처리로 표면처리 하는 단계;Treating the surface of the fixture with sulfuric acid and hydrochloric acid at an elevated temperature of 80 ° C or higher;
상기 산 처리 후 건조한 다음 균일한 HA 코팅을 위해 알곤/산소 플라즈마를 이용하여 표면을 활성화시키는 단계;Activating the surface using an argon / oxygen plasma for drying after the acid treatment and then for uniform HA coating;
상기 표면처리된 픽스츄어 상단부 5㎜를 0.01∼0.2㎜ 두께로 칼슘포스페이트를 코팅하는 단계를 특징으로 한다.Coating the upper surface of the surface-treated fixture with calcium phosphate to a thickness of 0.01 to 0.2 mm at 5 mm.
본 발명은 픽스츄어 상단부 5㎜ 구간을 염산테스라싸이클린과 같은 항생제에 녹을 수 있는 칼슘포스페이트기 코팅된 것을 특징으로 한다. The present invention is characterized in that a 5 mm section of the upper end of the fixture is coated with a calcium phosphate group capable of dissolving in an antibiotic such as testraccycline hydrochloride.
이와 같이 된 본 발명은 발치부에 칼슘포스페이트가 코팅된 픽스츄어를 식립후 임플란트를 사용중에 임플란트 주위염이 발생시 염산테트라싸이클린과 같은 항생제 처리를 통한 화학적인 치료방식을 적용하여 세균과 더불어 픽스츄어 표면에 코팅된 칼슘포스페이트 코팅을 용해시켜 주위염을 치료하는 동시에 재골 유착이 가능토록 함으로 치료효과를 높일 수 있게 된다. According to the present invention as described above, a fixture coated with calcium phosphate is placed on a foot portion, a chemical treatment method is applied through treatment of an antibiotic such as tetracycline hydrochloride in the case of implant periplasty in the course of using the implant, It is possible to increase the therapeutic effect by allowing the calcium phosphate coating to dissolve the surrounding calcium salt while allowing the bone marrow adhesion.
도1은 본 발명의 임플란트 구성을 나타낸 예시 도이며,
도2는 본 발명의 픽스츄어 칼슘포스페이트 코팅 공정을 나타낸 것이다.1 is an exemplary view showing an implant construction of the present invention,
2 shows a process of coating a fixture calcium phosphate of the present invention.
이하 본 발명의 실시 예를 상세히 설명하면 다음과 같다.Hereinafter, embodiments of the present invention will be described in detail.
본 발명의 임플란트 픽스츄어의 표면처리 방법은 제조 후 또는 사용 후의 임플란트 픽스츄어의 표면처리를 실시하게 되며, 표면처리 후 칼슘포스페이트 코팅을 실시하게된다. 이를 제조공정에 따라 설명하면 다음과 같다.The surface treatment method of the implant fixture of the present invention is a surface treatment of the implant fixture after or after the preparation, and calcium phosphate coating is performed after the surface treatment. The manufacturing process will be described as follows.
제 1 공정: 픽스츄어 가공 후 표면을 세척하는 단계Step 1: Cleaning the surface after the fixture processing
본 공정에서는 픽스츄어 가공 후 표면에 잔류된 절삭유와 같은 오염물질을 제거하기 위해 실시되는 세척단계로서, 화학적인 약품을 이용하여 초음파세척을 통해 세척을 진행한다. In this process, cleaning is performed to remove contaminants such as cutting oil remaining on the surface after the fixture processing, and the cleaning is performed by ultrasonic cleaning using a chemical agent.
제 2 공정: 표면거칠기 부여를 위한 블라스팅 표면처리 단계 Step 2: Blast surface treatment step for imparting surface roughness
상기 절삭유 세정 및 건조된 표면에 조대한 거칠기를 만들기 위해 200~600㎛ 크기의 HA(하이드록시아파타이트) 파우더를 4bar 이상의 고압의 압축공기를 이용하여 픽슈츄어 표면에 블라스팅을 하는 표면처리 단계이다. The surface of the fixture is subjected to blasting by using compressed air having a pressure of 4 bar or more and HA (hydroxyapatite) powder having a size of 200 to 600 μm to make roughness on the surface of the cutter.
제 3 공정: 균일한 마이크로 표면형상 확보를 위한 전처리 단계 Step 3: Pretreatment step for ensuring uniform micro-surface shape
상기 블라스팅 표면처리된 픽스츄어에 남아있는 블라스팅 파우더를 제거하여 산 처리시 균일한 표면형상을 확보하기 위해 50~60℃의 질산에서 20분간 처리하는 전처리 과정을 실시한다. The blasting powder remaining in the blast-surface-treated fixture is removed, and a pretreatment process is performed for 20 minutes in nitric acid at 50 to 60 ° C to secure a uniform surface shape at the time of acid treatment.
제 4 공정: 픽스츄어 산처리 단계 Step 4: Fixture acid treatment step
상기 질산처리 후 건조한 다음 픽스츄어 표면에 미세한 마이크로 형상 부여를 통해 표면적을 향상시키기 위한 80℃ 이상의 고온의 황산/염산 용액에 담지하는 표면처리를 실시한다.After the nitric acid treatment, the surface of the fixture is subjected to a surface treatment to be carried on a sulfuric acid / hydrochloric acid solution at a high temperature of 80 ° C or more to improve the surface area through fine micro-shape application to the surface of the fixture.
제 5 공정: 픽스츄어 세척 및 건조 단계 Step 5: Cleaning and drying the fixture
상기 산 처리 후 표면에 남아있는 산 성분을 충분히 세척하고 건조하는 과정을 거쳐야 한다. 세척 과정은 흐르는 물에서 수세 후 3회 이상의 초음파 세척을 실시하는데, 미세한 마이크로 표면에 묻어있는 산을 제거하기 위해 초음파 세척 시 증류수와 알코올을 이용하여 세척을 실시한다. The acid component remaining on the surface after the acid treatment is sufficiently washed and dried. In the cleaning process, ultrasonic cleaning is performed three times or more after the water rinsing in the flowing water. In order to remove the acid on the micro micro-surface, the ultrasonic cleaning is performed using distilled water and alcohol.
제 6 공정: 칼슘포스페이트 코팅 전처리 단계 Step 6: Calcium phosphate coating pretreatment step
본 공정에서 실시되는 픽스츄어의 표면처리는 픽스츄어 상단부 5㎜구간에 칼슘 포스페이스트 코팅을 실시하기 위한 표면 활성화 단계이다.The surface treatment of the fixture performed in this step is a surface activation step for applying calcium phosphide coating to the 5 mm section of the upper end of the fixture.
칼슘 포스페이트 코팅은 습식의 졸-겔 코팅방식을 적용하게 되는데, SLA 표면처리 후 임플란트 표면은 소수성을 가지게 되어 균일한 코팅이 어렵게 되는 단점이 있다. 이를 보완하기 위해 본 발명에서는 SLA 표면에 균일한 HA 코팅을 확보하기 위해 플라즈마 클리닝을 이용한 티타늄 표면 활성화 공정을 도입하였다. 플라즈마 활성화 공정에서는 산소 또는 알곤 가스를 이용하여 상온의 3.0*10-3torr 이하의 진공 조건에서 20분 동안 플라즈마 클리닝 과정을 진행한다. In the calcium phosphate coating, a wet sol-gel coating method is applied. After the SLA surface treatment, the surface of the implant becomes hydrophobic, making uniform coating difficult. In order to compensate for this problem, a titanium surface activation process using plasma cleaning is introduced in order to ensure uniform HA coating on the SLA surface. In the plasma activation process, the plasma cleaning process is performed for 20 minutes under a vacuum condition of 3.0 * 10 -3 torr or less at room temperature using oxygen or argon gas.
제 7 공정: 칼슘 Step 7: Calcium 포스페이트Phosphate 코팅 단계 Coating step
상기 플라즈마 전처리 된 픽스츄어 표면에 졸-겔 방식을 이용한 칼슘 포스페이트 코팅을 위한 최종 표면처리 단계이다. 상기 표면처리 중 실시되는 코팅은 픽스츄어 상단부 5㎜를 1～50㎛ 두께로 칼슘포스페이트를 코팅한다.And a final surface treatment step for calcium phosphate coating using a sol-gel method on the surface of the plasma pretreated fixture. During the surface treatment, the upper end of the fixture is coated with calcium phosphate to a thickness of 1 to 50 탆.
상기 표면 처리용으로 코팅되는 칼슘포스페이트는 염산테스라싸이클린과 같은 항생제에 녹을 수 있는 것을 사용하여 차후 주위염이 발생될 경우 항생제를 사용하여 칼슘포스페이트를 용해시켜 주위염을 치료하는 동시에 골 유착 성능을 향상시킬 수 있게 된다. The calcium phosphate coated for surface treatment may be dissolved in an antibiotic such as testcycline hydrochloride. When the peripheral inflammation is generated, an antibiotic is used to dissolve calcium phosphate to treat the peripheral inflammation and improve the osseointegration performance .
이하 본 발명의 첨부도면을 설명하면 다음과 같다.Hereinafter, the present invention will be described in detail.
도1은 본 발명의 임플란트 구성을 나타낸 예시 도로서, 이는 본 발명에 적용되는 것이나 발치 부분에 심어지는 통상의 임플란트 구조를 설명하여 본 발명을 이해할 수 있도록 도시한 것이다.FIG. 1 is a view illustrating an implant structure of the present invention, which is applied to the present invention or a conventional implant structure implanted in an extraction region, so as to understand the present invention.
도1에서 알 수 있는 바와 같이 환자의 발치 부분에 픽스츄어(20)를 잇몸에 심고, 이의 픽스츄어(20) 중앙에 어버트먼트(30)를 심어 기둥을 형성한 후 이의 어버트먼트 상단부에 크라운(30)을 씌어 인공치안인 임플란트(10)가 완성된다.As shown in FIG. 1, the
도2는 본 발명의 픽스츄어 칼슘포스페이트 코팅 공정을 나타낸 것으로서, 임플란트의 픽스츄어의 표면처리 전처리 단계로서 픽스츄어 가공 후 표면에 남아있는 가공유를 세척하는 단계 → 표면거칠기 부여를 위한 블라스팅 단계 → 균일한 마이크로 표면형상 확보를 위해 블라스팅 물질을 제거하는 질산 전처리 단계 → 표면에 마이크로 미세 형상을 만들기 위한 염산/황산 표면처리 단계 → 산 처리 후 표면에 남아있는 산을 세척하는 단계 → 균일한 HA 코팅을 하기 위한 플라즈마 세척을 이용한 티타늄 활성화 표면처리 단계 → 픽스츄어 상단부 5mm구간에 칼슘포스테이트를 코팅하는 단계로 이루어진다.FIG. 2 shows the process of coating the fixture calcium phosphate of the present invention. In the pretreatment of the surface of the fixture of the implant, the process oil is cleaned after polishing the surface of the fixture, blasted for surface roughness, Nitric acid pretreatment step for removal of blast material to secure micro-surface shape → hydrochloric acid / sulfuric acid surface treatment step to make micro fine shape on the surface → washing of the acid remaining on the surface after acid treatment → homogeneous HA coating A step of activating the titanium activated surface by plasma cleaning, and a step of coating the calcium phosphate on the 5 mm section of the upper end of the fixture.
이와 같이 된 본 발명은 환자의 잇몸 발치부에 칼슘포스페이트를 코팅된 픽스츄어의 임플란트를 식립 후 사용시 임플란트 주위염이 발생시 염산테트라싸이클린과 같은 항생제 처방함으로 픽스츄어에 코팅된 칼슘포스페이트가 화학적인 반응에 의해 용해되어 잇몸으로 흘러들어가 주위염을 치료하는 동시에 재골 유착이 가능토록 함으로 치료효과를 높이는 동시에 임플란트 관리를 간단 용이하게 할 수 있는 새로운 치료방법을 제공하는 이점이 있다. In the present invention, when an implant of a fixture coated with calcium phosphate is placed on a tooth of a patient's gums, an antibiotic such as tetracycline hydrochloride is prescribed when the implant is periosteal, and the calcium phosphate coated on the fixture is dissolved The present invention provides a new treatment method that can improve the therapeutic effect and simplify the management of the implant by allowing the bone to be adhered while treating the periplasm while flowing into the gums.
Claims (4)
치아의 발치부에 식립하기 위한 임플란트의 픽스츄어 표면에 오염원을 세척하는 단계:
표면거칠기 부여를 위한 블라스팅 단계 및 균일한 마이크로 표면형상 확보를 위해 블라스팅 물질을 제거하는 질산 전처리 단계;
표면에 마이크로 미세 형상을 만들기 위한 염산/황산 표면처리 단계
산 처리 후 표면에 남아있는 산을 세척하는 단계:
균일한 HA 코팅을 하기 위한 플라즈마 세척을 이용한 티타늄 활성화 표면처리 단계:
픽스츄어 상단부 5mm 구간까지 1～50㎛ 두께로 칼슘 포스테이트를 코팅하는 단계를 특징으로 하는 임플란트 픽스츄어 코팅방법.
1. An implant fixture coating method for an artificial tooth,
A step of washing the contamination source on the surface of the fixture of the implant to be placed on the root of the tooth;
A blast step for imparting surface roughness and a nitric acid pretreatment step for removing blast material to obtain a uniform micro-surface shape;
Hydrochloric acid / sulfuric acid surface treatment step to make micro fine shape on surface
Washing the acid remaining on the surface after the acid treatment:
Titanium Activated Surface Treatment with Plasma Wash for Homogeneous HA Coating Step:
Coating a calcium forster to a thickness of 1 to 50 mu m up to an interval of 5 mm on the upper end of the fixture.
픽스츄어의 표면처리는 픽스츄어 상단부 5㎜구간에 SLA 표면처리 후 칼슘포스페이스트 또는 HA 코팅을 실시하고 픽스츄어 상단부 5㎜이하 구간에는 SLA 표면처리를 실시하는 것을 특징으로 하는 임플란트 픽스츄어 코팅방법.
The method according to claim 1,
Wherein the surface treatment of the fixture is performed by applying calcium phosphide or HA coating to the 5 mm upper end portion of the fixture after the SLA surface treatment and performing the SLA surface treatment to the upper end portion of the fixture of 5 mm or less.
픽스츄어 상단부 5㎜에 염산테스라싸이클린과 같은 항생제에 녹을 수 있는 칼슘포스페이트가 코팅된 것을 특징으로 하는 임플란트 픽스츄어 코팅방법.
The method according to claim 1,
Wherein the top end of the fixture is coated with calcium phosphate which is soluble in antibiotics such as 5-mm tessira cyclin.
An implant fixture according to claim 1, wherein the implant fixture is calcium phosphate-coated.