KR20160100066A - Ion Gel Smart Window and Manufacturing Method Thereof - Google Patents

Ion Gel Smart Window and Manufacturing Method Thereof Download PDF

Info

Publication number
KR20160100066A
KR20160100066A KR1020150022566A KR20150022566A KR20160100066A KR 20160100066 A KR20160100066 A KR 20160100066A KR 1020150022566 A KR1020150022566 A KR 1020150022566A KR 20150022566 A KR20150022566 A KR 20150022566A KR 20160100066 A KR20160100066 A KR 20160100066A
Authority
KR
South Korea
Prior art keywords
transparent electrode
electrochromic
electrochromic layer
electrolyte layer
layer
Prior art date
Application number
KR1020150022566A
Other languages
Korean (ko)
Other versions
KR101656466B1 (en
Inventor
김혜경
김세현
이소희
Original Assignee
영남대학교 산학협력단
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 영남대학교 산학협력단 filed Critical 영남대학교 산학협력단
Priority to KR1020150022566A priority Critical patent/KR101656466B1/en
Publication of KR20160100066A publication Critical patent/KR20160100066A/en
Application granted granted Critical
Publication of KR101656466B1 publication Critical patent/KR101656466B1/en

Abstract

The present invention relates to an ion gel smart window and a method of manufacturing the same. An ion gel smart window according to the present invention include a first transparent electrode member having electric conductivity and optical transmission; a first electrochromic layer provided at one side of the first transparent electrode member to change a color thereof as electrons move; an electrolyte layer provided at one side of the first transparent electrode member and including electrolyte for causing the first electrochromic layer to be changed in color; and a second transmission electrode member provided at one side of the electrolyte and having electric conductivity and optical transmission, wherein the electrolyte layer includes polymer and ionic liquid. As compared with those of a smart window of which the electrolyte layer is prepared of liquid, the stability of the smart window may be greatly improved and a decrease in the durability of the smart widow may be prevented.

Description

이온젤 스마트 윈도우 및 이의 제조방법{Ion Gel Smart Window and Manufacturing Method Thereof}TECHNICAL FIELD [0001] The present invention relates to an ion-gel smart window,

본 발명은 이온젤 스마트 윈도우 및 이의 제조방법에 관한 것으로, 보다 상세하게는 스마트 윈도우를 구성하는 주요부분 중 하나인 전해질층으로부터 전해질용액이 누출되지 않아서 안전성 및 수명이 증대되는 스마트 윈도우에 관한 것이다. The present invention relates to an ion-gel smart window and a manufacturing method thereof, and more particularly, to a smart window in which an electrolyte solution does not leak from an electrolyte layer, which is one of the main components of a smart window, thereby increasing safety and lifetime.

스마트 윈도우는 전기변색소자(Electrochromic Device : ECD)를 이용한 것으로 전장을 인가하여 전류의 흐름에 따라 색상이 변화하는 소자를 말한다. A smart window is an electrochromic device (ECD) that changes color according to current flow by applying electric field.

스마트 윈도우는 창문이나 거울 또는 디스플레이장치에 적용되어 광의 투과도나 반사도를 조절하는 용도로 주로 사용되고 있다. 스마트 윈도우는 전기화학적 산화/환원 반응에 의하여 물질의 색이 가역적으로 조절될 수 있는 것으로서, 산화 또는 환원시 수반되는 전자 이동에 의해 자외선이나 가시광선, 근적외선 영역에서의 에너지 흡수변화에 따라 색상을 가변시키게 된다. Smart windows are used in windows, mirrors or display devices to control the transmission and reflectivity of light. The smart window can reversibly control the color of a substance by an electrochemical oxidation / reduction reaction. It can change the color depending on the change of energy absorption in the ultraviolet ray, visible light, and near infrared region due to electron transfer accompanied by oxidation or reduction .

이러한 스마트 윈도우가 건축물 또는 자동차의 윈도우에 적용되면 겨울에는 실내로 최대한 태양광선이 들어올 수 있도록 투명하게 조절하고, 여름에는 태양광선을 차단하도록 하면 실내온도를 조절할 수 있으며 이에 따른 에너지도 절약할 수 있다. When such a smart window is applied to a window of a building or an automobile, it is possible to control the indoor temperature to be as transparent as possible in the winter, and to shut off the sunlight in the summer, so that the indoor temperature can be controlled and energy can be saved .

이러한 스마트 윈도우에 관련하여 종래 기술 중에는 대한민국등록특허 제10-1319443호(발명의 명칭 : 전기변색성 스마트 윈도우 필름. 이하 선행기술 1) 등이 있다. Related to this smart window, Korean Patent No. 10-1319443 (entitled " Electrochromic Smart Window Film, hereinafter referred to as Prior Art 1) "

선행기술 1에 따르면, 스마트 윈도우 필름의 두께를 얇게 제조할 수 있는 구조에 관한 기술이 개시되어 있으며, 이러한 선행기술을 이용하여 스마트 윈도우의 두께를 어느 정도 얇게 제조할 수 있었다. 하지만, 이러한 선행기술 1에 따르면, 액체전해질층을 포함하는 구조로 되어 있는데 이러한 경우 제조 공정상 리킹(leaking)이나 베이퍼(vapor)의 발생으로 인한 제품불량율이 문제되었다. 나아가 스마트 윈도우를 제조하더라도 액체전해질층으로부터 액체전해질이 누출이 되어 제품의 안정성이 떨어지고, 제품의 수명이 단축되는 문제점 또한 있었다. According to the prior art 1, a technique relating to a structure capable of manufacturing a thin thickness of a smart window film is disclosed, and the thickness of the smart window can be made thin to some extent using this prior art. However, according to the prior art 1, a structure including a liquid electrolyte layer is formed. In such a case, the product defective rate due to leaking or vapor generation is a problem in the manufacturing process. Furthermore, even when a smart window is manufactured, the liquid electrolyte leaks from the liquid electrolyte layer, resulting in a decrease in the stability of the product and a shortening of the service life of the product.

본 발명의 목적은 상기한 종래의 문제점을 해결하기 위한 것으로, 스마트 윈도우에서 액체전해질이 누출될 염려가 없는 스마트 윈도우를 제공함에 있다. SUMMARY OF THE INVENTION An object of the present invention is to provide a smart window in which a liquid electrolyte does not leak in a smart window.

상기와 같은 목적을 달성하기 위한 본 발명에 따른 이온젤 스마트 윈도우는 전기전도성과 빛에 대한 투과성 있는 제1투명전극체; 상기 제1투명전극체의 일측에 마련되며, 전자의 이동에 따라 변색되는 제1전기변색층; 상기 제1전기변색층의 일측에 마련되며, 상기 제1전기변색층이 전기변색을 일으킬 수 있도록 전해질로 이루어진 전해질층; 및 상기 전해질의 일측에 마련되며, 전기전도성과 빛에 대한 투과성이 있는 제2투명전극체;를 포함하되, 상기 전해질층은 고분자폴리머 및 이오닉리퀴드(ionic liquid)를 포함하여 이루어지는 이온젤(ion gel)인 것을 하나의 특징으로 할 수도 있다. According to an aspect of the present invention, there is provided an ion-gel smart window comprising: a first transparent electrode body that is electrically conductive and transparent to light; A first electrochromic layer provided on one side of the first transparent electrode body and discolored by the movement of electrons; An electrolyte layer provided on one side of the first electrochromic layer and made of an electrolyte so that the first electrochromic layer can cause electrochromism; And a second transparent electrode body provided on one side of the electrolyte and having electrical conductivity and light transmittance, wherein the electrolyte layer comprises an ionic gel comprising a polymer polymer and an ionic liquid, gel) may be a feature.

여기서, 상기 제1투명전극체 또는 상기 제2투명전극체는, ITO글라스(indium titanium oxide glass)인 것을 또 하나의 특징으로 할 수도 있다. Here, the first transparent electrode member or the second transparent electrode member may be an ITO glass (indium titanium oxide glass).

여기서, 상기 제1투명전극체 또는 상기 제2투명전극체는, 폴리에스테르, 폴리에틸렌테레프탈레이트, 폴리페닐렌설파이드, 폴리스티렌, 폴리아미드, 폴리카보네이트, 폴리메틸메타크릴레이트, 폴리에틸렌나프탈레이트, 폴리에틸렌 및 폴리프로필렌 중에서 어느 하나로 이루어진 고분자기재체로서 전기전도성을 갖는 물질로 코팅된 것을 또 하나의 특징으로 할 수도 있다. Here, the first transparent electrode member or the second transparent electrode member may be formed of a material selected from the group consisting of polyester, polyethylene terephthalate, polyphenylene sulfide, polystyrene, polyamide, polycarbonate, polymethyl methacrylate, polyethylene naphthalate, Propylene, and the like may be used as a polymer-based body made of any one of them.

여기서, 상기 제1전기변색층은,

Figure pat00001
또는
Figure pat00002
중에서 어느 하나를 포함하여 이루어진 것을 또 하나의 특징으로 할 수도 있다.Here, the first electrochromic layer may be formed,
Figure pat00001
or
Figure pat00002
May be any of the features described above.

여기서, 상기 전해질층과 상기 제2투명전극체 사이에 위치하며, 전자의 이동에 따라 변색되는 제2전기변색층; 을 더 포함하는 것을 또 하나의 특징으로 할 수도 있다. A second electrochromic layer disposed between the electrolyte layer and the second transparent electrode and being discolored by the movement of electrons; May be further included.

여기서, 상기 제2전기변색층은,

Figure pat00003
또는
Figure pat00004
중에서 어느 하나를 포함하여 이루어진 것을 또 하나의 특징으로 할 수도 있다. Here, the second electrochromic layer may be formed,
Figure pat00003
or
Figure pat00004
May be any of the features described above.

여기서, 상기 전해질층에 포함되는 상기 고분자폴리머는 PDVF(polyvinylidene fluoride-co-hexafluoropropylene), poly(styrene-block-ethyleneoxide-block styrene)(SOS) triblock copolymer 및 poly(ethylene oxide)-poly(propylene oxide) block copolymer 중에서 어느 하나인 것을 또 하나의 특징으로 할 수도 있다.Here, the polymeric polymer included in the electrolyte layer may be polyvinylidene fluoride-co-hexafluoropropylene (PDVF), styrene-block-ethyleneoxide-block styrene (SOS) triblock copolymer, poly (ethylene oxide) -poly (propylene oxide) block copolymer may be another feature of the present invention.

여기서, 상기 전해질층에 포함되는 상기 이오닉리퀴드(ionic liquid)는, EMBI(1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide), 1-에틸-3-메틸이미다졸리움 헥사플로로포스포에이트(1-Ethyl-3-methylimidazolium hexafluorophosphoate) 및 1-에틸-3-메틸이미다졸리움 테트라플로로보레이트(1-Ethyl-3-methylimidazolium tetrafluoroborate) 중에서 어느 하나인 것을 또 하나의 특징으로 할 수도 있다. The ionic liquid contained in the electrolyte layer may be selected from the group consisting of 1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide, 1-ethyl-3-methylimidazolium hexafluorophosphate (1- Ethyl-3-methylimidazolium hexafluorophosphate) and 1-Ethyl-3-methylimidazolium tetrafluoroborate (1-ethyl-3-methylimidazolium tetrafluoroborate).

상기와 같은 목적을 달성하기 위한 본 발명에 따른 이온젤 스마트 윈도우 제조방법은 전기전도성과 빛에 대한 투과성이 있는 제1투명전극체의 일측 면에 전자의 이동에 따라 변색될 수 있는 제1전기변색층을 형성시키는 제1전기변색층형성단계; 상기 제1전기변색층형성단계에서 형성된 상기 제1전기변색층의 일측 면에 전해질층을 형성시키는 전해질층형성단계; 및 상기 전해질층형성단계에서 형성된 상기 전해질층의 일측에 전기전도성과 빛에 대한 투과성이 있는 제2투명전극체가 마련되는 제2투명전극체구비단계;를 포함하되, 상기 전해질층형성단계에서 형성되는 상기 전해질층은, 고분자폴리머 및 이오닉리퀴드(ionic liquid)를 포함하는 이온젤(ion gel)용액으로부터 형성되는 것을 하나의 특징으로 할 수도 있다.According to another aspect of the present invention, there is provided a method of manufacturing an ion-gel smart window, including: forming a first transparent electrode body having electrical conductivity and light transmittance, Forming a first electrochromic layer; An electrolyte layer forming step of forming an electrolyte layer on one side of the first electrochromic layer formed in the first electrochromic layer forming step; And forming a second transparent electrode body having a first transparent electrode body having electrical conductivity and light transmittance on one side of the electrolyte layer formed in the electrolyte layer forming step, The electrolyte layer may be formed of an ion gel solution including a polymer polymer and an ionic liquid.

여기서, 상기 제1전기변색층형성단계는, 상기 제1투명전극체의 일측 면을 제1전기변색소재용액으로 코팅시키는 제1코팅단계; 및 상기 제1코팅단계에서 코팅된 상기 제1전기변색소재용액을 건조시키는 제1건조단계; 를 포함하는 것을 하나의 특징으로 할 수도 있다.Here, the first electrochromic layer forming step may include: a first coating step of coating one side of the first transparent electrode material with a first electrochromic material solution; A first drying step of drying the first electrochromic material solution coated in the first coating step; May be included as one feature.

나아가, 상기 제1전기변색소재용액은,

Figure pat00005
또는
Figure pat00006
중 어느 하나와 디아이워터(D.I. water) 및 알콜을 포함하여 이루어진 용액인 것을 또 하나의 특징으로 할 수도 있다. Further, the first electrochromic material solution may contain,
Figure pat00005
or
Figure pat00006
(DI water) and an alcohol, and it may be another feature of the present invention.

여기서, 상기 전해질층형성단계 및 상기 제2투명전극체구비단계 사이에 이루어지는 단계로서, 상기 전해질층형성단계에서 형성된 상기 전해질층의 일측 면에 제2전기변색층을 형성시키는 제2전기변색층형성단계;를 더 포함하고, 상기 제2투명전극체구비단계에서, 상기 제2투명전극체는 상기 제2전기변색층의 일측 면에 마련되는 것을 또 하나의 특징으로 할 수도 있다. Here, a step between the electrolyte layer forming step and the second transparent electrode body forming step may include a step of forming a second electrochromic layer forming a second electrochromic layer on one side of the electrolyte layer formed in the electrolyte layer forming step Wherein the second transparent electrode body is provided on one side of the second electrochromic layer in the step of providing the second transparent electrode body.

나아가, 상기 제2전기변색층형성단계는, 상기 전해질층의 일측 면을 제2전기변색소재용액으로 코팅시키는 제2코팅단계; 및 상기 제2코팅단계에서 코팅된 상기 제2전기변색소재용액을 건조시키는 제2건조단계;를 포함하는 것을 또 하나의 특징으로 할 수도 있다. Further, the second electrochromic layer forming step may include: a second coating step of coating one side of the electrolyte layer with a second electrochromic material solution; And a second drying step of drying the second electrochromic material solution coated in the second coating step.

더 나아가, 상기 제2전기변색소재용액은,

Figure pat00007
또는
Figure pat00008
중 어느 하나와 디아이워터(D.I. water) 및 알콜을 포함하여 이루어진 용액인 것을 또 하나의 특징으로 할 수도 있다. Furthermore, the second electrochromic material solution may contain,
Figure pat00007
or
Figure pat00008
(DI water) and an alcohol, and it may be another feature of the present invention.

여기서, 상기 제2투명전극체구비단계 이전에 이루어지는 단계로서, 상기 제2투명전극체구비단계에서 마련될 상기 제2투명전극체의 일측 면에 전자의 이동에 따라 변색되는 제2전기변색층을 형성시키는 제2투명전극체준비단계;를 더 포함하고, 상기 제2투명전극체구비단계에서는, 상기 전해질층의 일측에 상기 제2투명전극체준비단계에서 상기 제2전기변색층이 형성된 상기 제2투명전극체를 부착시키는 것을 또 하나의 특징으로 할 수도 있다. Here, it is preferable that the step of forming the second electrochromic layer includes a step of forming a second electrochromic layer, which is discolored by the movement of electrons, on one side of the second transparent electrode body to be provided in the step of providing the second transparent electrode body, Forming a second transparent electrode body on the first transparent electrode body, and forming a second transparent electrode body on the second transparent electrode body, And attaching the two transparent electrode bodies may be another feature.

여기서, 상기 제2투명전극체구비단계 이후에, 상기 전해질층을 외부로부터 보호하기 위하여 상기 제1투명전극체와 상기 제2투명전극체 사이를 실링시키는 실링단계;를 더 포함하는 것을 또 하나의 특징으로 할 수도 있다. The sealing step may include sealing the first transparent electrode member and the second transparent electrode member to protect the electrolyte layer from the outside after the step of providing the second transparent electrode member, It can also be a feature.

여기서, 상기 전해질층형성단계는, 고분자폴리머를 용매에 혼합하여 고분자폴리머 용액을 형성시키는 A단계; 상기 A단계에서 혼합된 상기 고분자폴리머 용액에 이오닉리퀴드를 첨가하여 이온젤용액을 형성시키는 B단계; 상기 B단계에서 형성된 상기 이온젤용액을 상기 제1전기변색층의 표면에 코팅시키는 C단계; 및 상기 C단계에서 상기 제1전기변색층의 표면에 코팅된 상기 이온젤용액을 건조시키어 용매를 제거하는 D단계; 를 포함하는 것을 또 하나의 특징으로 할 수도 있다. Here, the electrolyte layer forming step may include a step A in which a polymer polymer solution is formed by mixing a polymer polymer with a solvent; A step B for adding an ionic liquid to the polymer polymer solution mixed in the step A to form an ionic gel solution; A step C of coating the surface of the first electrochromic layer with the ionic gel solution formed in step B; And D) drying the ionic gel solution coated on the surface of the first electrochromic layer in step C to remove the solvent; May be another feature of the present invention.

나아가, 상기 고분자폴리머는 PDVF(polyvinylidene fluoride-co-hexafluoropropylene), poly(styrene-block-ethyleneoxide-block styrene)(SOS) triblock copolymer 및 poly(ethylene oxide)-poly(propylene oxide) block copolymer 중에서 어느 하나인 것을 또 하나의 특징으로 할 수도 있다. Further, the polymer may be any one of polyvinylidene fluoride-co-hexafluoropropylene (PDVF), styrene-block-ethyleneoxide-block styrene (SOS) triblock copolymer and poly (ethylene oxide) -poly It may be another feature.

여기서, 상기 이오닉리퀴드(ionic liquid)는, EMBI(1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide), 1-에틸-3-메틸이미다졸리움 헥사플로로포스포에이트(1-Ethyl-3-methylimidazolium hexafluorophosphoate) 및 1-에틸-3-메틸이미다졸리움 테트라플로로보레이트(1-Ethyl-3-methylimidazolium tetrafluoroborate) 중에서 어느 하나인 것을 또 하나의 특징으로 할 수도 있다. The ionic liquid may be selected from the group consisting of 1-ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide, 1-ethyl-3-methylimidazolium hexafluorophosphoate ) And 1-ethyl-3-methylimidazolium tetrafluoroborate (1-Ethyl-3-methylimidazolium tetrafluoroborate).

여기서, 상기 제1투명전극체 또는 상기 제2투명전극체는, ITO글라스(indium titanium oxide glass)인 것을 또 하나의 특징으로 할 수도 있다. Here, the first transparent electrode member or the second transparent electrode member may be an ITO glass (indium titanium oxide glass).

여기서, 상기 제1투명전극체 또는 상기 제2투명전극체는, 폴리에스테르, 폴리에틸렌테레프탈레이트, 폴리페닐렌설파이드, 폴리스티렌, 폴리아미드, 폴리카보네이트, 폴리메틸메타크릴레이트, 폴리에틸렌나프탈레이트, 폴리에틸렌 및 폴리프로필렌 중에서 어느 하나로 이루어진 고분자기재체로서 전기전도성을 갖는 물질로 코팅된 것을 또 하나의 특징으로 할 수도 있다. Here, the first transparent electrode member or the second transparent electrode member may be formed of a material selected from the group consisting of polyester, polyethylene terephthalate, polyphenylene sulfide, polystyrene, polyamide, polycarbonate, polymethyl methacrylate, polyethylene naphthalate, Propylene, and the like may be used as a polymer-based body made of any one of them.

본 발명에 따른 이온젤 스마트 윈도우는 전해질층이 용액이 아닌 이온젤로 이루어지기 때문에 전해질용액이 누출 또는 누액되지 않는다. 따라서, 스마트 윈도우의 안정성과 안전성이 증대되고, 스마트 윈도우의 수명 단축을 억제하는 효과가 있다. In the ion-gel smart window according to the present invention, since the electrolyte layer is made of an ion gel rather than a solution, the electrolyte solution does not leak or leak. Therefore, the stability and safety of the smart window are increased, and the life span of the smart window is suppressed.

또한 액체전해질을 이용하는 경우와 달리 본 발명에 따른 이온젤 스마트 윈도우의 경우 전해질이 젤 상태이기 때문에 리킹(leaking)이나 베이퍼(vapor)가 발생하지 않으므로 리킹이나 베이퍼로 인한 결함의 발생가능성이 억제된다. 또한 대면적화된 스마트 윈도우의 제조가 수월해 진다. 이와 같이 제조공정상에 있어서 제품생산수율 내지 생산성을 증대시키는 효과가 있다. Also, unlike the case of using a liquid electrolyte, in the case of the ion-gel smart window according to the present invention, leaking or vapor is not generated because the electrolyte is in a gel state, and thus the possibility of occurrence of defects due to leakage or vapor is suppressed. It also facilitates the production of large-sized smart windows. As described above, there is an effect of increasing the product yield and productivity at the top of the production process.

그리고, 잉크젯 프린팅 방법 등을 이용하여 이온젤의 전해질층을 형성시킬 수 있으므로 종래의 액체전해질을 이용하는 경우에 비해서 제조 공정상 좀 더 수월하게 제조할 수 있으며, 좀 더 다양한 형태(모양)을 갖는 스마트 윈도우의 제조가 가능하므로 보다 다양한 형태의 제품 디자인을 창출할 수 있다는 효과가 있다. Since the electrolyte layer of the ion gel can be formed by using an inkjet printing method or the like, it can be manufactured more easily in the manufacturing process than in the case of using a conventional liquid electrolyte, and a smart Since the window can be manufactured, it is possible to create more various types of product designs.

도 1은 본 발명의 실시 예에 따른 이온젤 스마트 윈도우를 개략적으로 나타낸 단면도이다.
도 2는 본 발명의 실시 예에 따른 이온젤 스마트 윈도우 제조방법을 개략적으로 나타낸 순서도이다.
도 3은 본 발명의 변형된 실시 예에 따른 이온젤 스마트 윈도우 제조방법을 개략적으로 나타낸 순서도이다.
도 4는 본 발명의 실시 예에 따른 이온젤 스마트 윈도우의 전압-전류의 특성을 개략적으로 나타낸 그래프이다.
도 5는 본 발명의 실시 예에 따른 이온젤 스마트 윈도우와 종래의 스마트 윈도우와의 투과도 차이를 개략적으로 나타낸 그래프이다.1 is a cross-sectional view schematically illustrating an ion-gel smart window according to an embodiment of the present invention.
2 is a flowchart schematically showing a method of manufacturing an ion-gel smart window according to an embodiment of the present invention.
FIG. 3 is a flowchart schematically showing a method of manufacturing an ion-gel smart window according to a modified embodiment of the present invention.
4 is a graph schematically illustrating voltage-current characteristics of an ion-gel smart window according to an embodiment of the present invention.
FIG. 5 is a graph schematically showing a difference in transmittance between an ion-gel smart window and a conventional smart window according to an embodiment of the present invention.

이하에서는 본 발명에 대하여 보다 구체적으로 이해할 수 있도록 첨부된 도면을 참조한 바람직한 실시 예를 들어 설명하기로 한다. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.

도 1은 본 발명의 실시 예에 따른 이온젤(ion gel) 스마트 윈도우를 개략적으로 나타낸 단면도이다. 1 is a schematic cross-sectional view of an ion gel smart window according to an embodiment of the present invention.

도 1을 참조하면, 본 발명의 실시 예에 따른 이온젤 윈도우는 제1투명전극체(110), 제1전기변색층(120), 전해질층(130) 및 제2투명전극체(150)을 포함하여 이루어지며, 좀 더 바람직하게는 제2전기변색층(140)을 더 포함하여 이루어진다. 1, an ion gel window according to an embodiment of the present invention includes a first transparent electrode member 110, a first electrochromic layer 120, an electrolyte layer 130, and a second transparent electrode member 150 And more preferably includes a second electrochromic layer 140.

제1투명전극체(110)는 전기전도성이 있으며, 빛에 대한 투과성이 있는 것이 바람직하다.It is preferable that the first transparent electrode member 110 is electrically conductive and has transparency to light.

제1투명전극체(110)로 이용될 수 있는 것에 대해 예를 들면, ITO글라스(Indium Titanium Oxide Glass)가 대표적이며, ITO글라스 이외에 고분자기재체를 들을 수 있다. ITO글라스에 대해서는 많이 알려져 있으므로 이에 대한 자세한 설명은 생략하기로 한다.For example, an ITO glass (Indium Titanium Oxide Glass) can be used as the first transparent electrode member 110, and a polymer-based substrate other than the ITO glass can be used. ITO glass is well known, so a detailed description thereof will be omitted.

ITO글라스 이외에도 전기전도성이 있는 고분자기재체가 제1투명전극체(110)로 사용될 수 있다. 즉, 고분자기재체의 일측 면(전기변색층, 전해질층(130)이 있는 방향측의 면을 말한다.)에 전기전도성을 주기 위하여 얇게 코팅처리를 하거나 은나노와이어층이 형성되어 있는 것이 바람직하다.In addition to the ITO glass, a polymer substrate having electrical conductivity may be used as the first transparent electrode member 110. That is, it is preferable that a thin coating treatment or a silver nano wire layer is formed in order to impart electrical conductivity to one side of the polymer base material (the side in the direction in which the electrochromic layer and the electrolyte layer 130 are present).

고분자기재체는 폴리에스테르(polyester), 폴리에틸렌테레프탈레이트(polyethyleneterephthalate ; PET), 폴리페닐렌설파이드(polyphenylenesulfide ; PPS), 폴리스티렌(polystyrene), 폴리아미드(polyamide), 폴리카보네이트(polycarbonate), 폴리메틸메타크릴레이트(polymethyl methacrylate ; PMMA), 폴리에틸렌나프탈레이트(polyethyleneaphthalate ; PEN), 폴리에틸렌(polyethylene ; PE) 및 폴리프로필렌(polypropylene ; PP) 중에서 선택되는 하나 또는 그 이상의 소재로서 80~300 마이크로미터 사이의 두께를 가지며 공기 대비 투과도가 85% 이상으로 이루어진 것이 바람직하며, 이에 꼭 국한되어야 하는 것은 아니다. The polymer-based substrate may be formed of at least one selected from the group consisting of polyester, polyethyleneterephthalate (PET), polyphenylenesulfide (PPS), polystyrene, polyamide, polycarbonate, One or more materials selected from the group consisting of polymethyl methacrylate (PMMA), polyethylene naphthalate (PEN), polyethylene (PE) and polypropylene (PP) It is preferable that the air permeability is not less than 85%, and the present invention is not limited thereto.

고분자기재층의 일측 면에 마련되는 은나노와이어층과 같이 투명한 전극층은 투명한 유리기판 또는 얇은 고분자 기판 위에 물리화학적인 방법으로 원자, 분자 또는 이온을 응축시킨 것으로, 가시광영역에서 투명하며, 전기전도도가 큰 것을 의미한다. 이러한 전극층은 광투과도와 전기전도도 이외에도 내열성, 내알칼리성, 식각특성, 전기화학적 안정성, 막표면형상, 부착강도, 부착경도, 막의 두께 등이 고려되는 것이 바람직하다.
Like the silver nanowire layer provided on one side of the polymer substrate layer, the transparent electrode layer is formed by condensing atoms, molecules or ions on a transparent glass substrate or a thin polymer substrate by a physicochemical method. The transparent electrode layer is transparent in a visible light region, . The electrode layer preferably has heat resistance, alkali resistance, etching property, electrochemical stability, film surface shape, adhesion strength, adhesion hardness, film thickness, etc. in addition to light transmittance and electrical conductivity.

다음으로, 제1전기변색층(120)은 제1투명전극체(110)의 일측에 마련된다. 그리고 전자의 이동에 따라 변색될 수 있는 것이 바람직하다. 여기에서 전자의 이동은 전기화학적으로 산화, 환원반응을 포함하여 의미한다. 그리고, 이러한 제1전기변색층(120)으로는

Figure pat00009
또는
Figure pat00010
으로 이루어진 것이 바람직하지만, 꼭 이에 국한되지 않는다. 제1전기변색층(120)은 유기변색물질이나 무기변색물질로 이루어질 수 있다. Next, the first electrochromic layer 120 is provided on one side of the first transparent electrode member 110. And it is preferable that it can be discolored by the movement of electrons. Here, the transfer of electrons means electrochemical oxidation and reduction reactions. As the first electrochromic layer 120,
Figure pat00009
or
Figure pat00010
But is not limited thereto. The first electrochromic layer 120 may be formed of an organic discoloring material or an inorganic discoloring material.

본 발명의 실시 예에서는 제1전기변색층(120)으로

Figure pat00011
또는
Figure pat00012
로 이루어진 것을 예시하였으며, 이러한 제1전기변색층(120)에 대해서는 종래에 알려진 방법으로 형성시킬 수도 있으므로 자세한 설명은 생략하기로 한다.
In the embodiment of the present invention, the first electrochromic layer 120
Figure pat00011
or
Figure pat00012
And the first electrochromic layer 120 may be formed by a conventionally known method, so that detailed description thereof will be omitted.

전해질층(Electrolyte)(130)은 제1전기변색층(120)의 일측에 마련되며, 제1전기변색층(120)이 전기변색을 일으킬 수 있도록 전해질로 이루어진다. 이러한 전해질층(130)은 고분자폴리머 및 이오닉리퀴드(ionic liquid)를 포함하여 이루어지는 이온젤(ion gel)인 것이 바람직하다. The electrolyte layer 130 is provided on one side of the first electrochromic layer 120 and is made of an electrolyte so that the first electrochromic layer 120 can cause electrochromism. The electrolyte layer 130 is preferably an ion gel including a polymer polymer and an ionic liquid.

여기서, 전해질층(130)에 포함되는 상기 고분자폴리머는 PDVF(polyvinylidene fluoride-co-hexafluoropropylene), poly(styrene-block-ethyleneoxide-block styrene)(SOS) triblock copolymer, poly(ethylene oxide)-poly(propylene oxide) block copolymer 중에서 어느 하나인 것이 바람직하다. The polymer polymer included in the electrolyte layer 130 may be at least one selected from the group consisting of polyvinylidene fluoride-co-hexafluoropropylene (PDVF), styrene-block-ethyleneoxide-block styrene (SOS) triblock copolymer, poly (ethylene oxide) -poly oxide block copolymer.

그리고, 전해질층(130)에 포함되는 상기 이오닉리퀴드(ionic liquid)는, EMBI(1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide), 1-Ethyl-3-methylimidazolium hexafluorophosphoate 및 1-Ethyl-3-methylimidazolium tetrafluoroborate 중에서 어느 하나인 것이 바람직하다. The ionic liquid contained in the electrolyte layer 130 may be at least one selected from the group consisting of 1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide, 1-Ethyl-3-methylimidazolium hexafluorophosphoate and 1-Ethyl-3-methylimidazolium tetrafluoroborate It is preferable to use any one of them.

전해질층(130)의 일측 면에는 제2전기변색층(140)이 마련되어 있는 것이 바람직하다. 제2전기변색층(140)은 제1전기변색층(120)에 대하여 설명의 편의상 구별하기 위하여 명칭을 조금 달리 했을 뿐 제1전기변색층(120)과 제2전기변색층(140)은 앞서 설명한 바와 같으며,

Figure pat00013
또는
Figure pat00014
으로 이루어지는 것이 바람직하다. 물론 이에 꼭 국한되어야하는 것은 아니며, 제2전기변색층(140)은 유기변색물질이나 무기변색물질로 이루어질 수도 있다. And the second electrochromic layer 140 may be provided on one side of the electrolyte layer 130. The first electrochromic layer 120 and the second electrochromic layer 140 may be formed in the same manner as the first electrochromic layer 120 and the second electrochromic layer 140 in order to distinguish the first electrochromic layer 120 from the first electrochromic layer 120, Lt; / RTI >
Figure pat00013
or
Figure pat00014
. Of course, the second electrochromic layer 140 may not be limited to the organic electrochromic material or the inorganic electrochromic material.

제2전기변색층(140)의 일측 면에는 제2투명전극체(150)가 마련된다. 제2투명전극체(150) 또한 제1투명전극체(110)에 대해서 설명의 편의상 구별하기 위하여 명칭을 달리 했을 뿐 제1투명전극체(110)와 제2투명전극체(150)에 대한 설명은 앞서 설명한 바와 같다. 따라서, 제2투명전극체(150)에 대한 더 이상의 설명은 생략하기로 한다.
A second transparent electrode member 150 is provided on one side of the second electrochromic layer 140. The description of the first transparent electrode member 110 and the second transparent electrode member 150 is omitted because the second transparent electrode member 150 is different from the first transparent electrode member 110 in order to distinguish the first transparent electrode member 110. [ As described above. Therefore, further description of the second transparent electrode member 150 will be omitted.

다음으로 도 2를 더 참조하여 본 발명의 실시 예에 따른 이온젤 스마트 윈도우의 제조방법에 대하여 설명하기로 한다. Next, a method of manufacturing an ion-gel smart window according to an embodiment of the present invention will be described with reference to FIG.

도 2는 본 발명의 실시 예에 따른 이온젤 스마트 윈도우의 제조방법을 개략적으로 나타낸 순서도이다. 2 is a flowchart schematically showing a method of manufacturing an ion-gel smart window according to an embodiment of the present invention.

도 2를 더 참조하면 본 발명의 실시 예에 따른 이온젤 스마트 윈도우의 제조방법은, 기본적으로 제1전기변색층형성단계(S110), 전해질층형성단계(S120) 및 제2투명전극체구비단계(S140)를 포함하여 이루어지며, 좀 더 바람직하게는 제2전기변색층형성단계(S130)를 더 포함하여 이루어진다. 여기서, 전해질층형성단계(S120)에서 형성되는 전해질층(130)은 고분자폴리머 및 이오닉리퀴드(ionic liquid)를 포함하는 이온젤용액으로부터 형성되는 것이 바람직하다.
2, a method of manufacturing an ion-gel smart window according to an embodiment of the present invention basically includes the steps of forming a first electrochromic layer (S110), forming an electrolyte layer (S120), and forming a second transparent electrode (S140), and more preferably, a second electrochromic layer forming step (S130). Here, the electrolyte layer 130 formed in the electrolyte layer forming step S120 is preferably formed from an ionic gel solution containing a polymeric polymer and an ionic liquid.

<<S110>><< S110 >>

제1전기변색층형성단계(S110)는 전기전도성과 빛에 대한 투과성이 있는 제1투명전극체(110)의 일측 면에 전자의 이동에 따라 변색될 수 있는 제1전기변색층(120)을 형성시키는 단계이다. In the first electrochromic layer forming step S110, a first electrochromic layer 120, which can be discolored according to the movement of electrons, is formed on one side of the first transparent electrode member 110 having electrical conductivity and light permeability .

여기서 제1투명전극체(110)는 후술할 제2투명전극체(150)와 설명의 편의상 구분할 수 있도록 임의적으로 명칭을 부여한 것이다. 제1투명전극체(110)는 전기전도성이 있는 것으로서 빛에 대한 투과성이 있는 것이 바람직하다. Here, the first transparent electrode member 110 is arbitrarily given a name so that it can be distinguished from the second transparent electrode member 150 to be described later for convenience of explanation. The first transparent electrode member 110 preferably has electrical conductivity and is transparent to light.

이러한 제1전기변색층형성단계(S110)는 제1코팅단계(S111) 및 제1건조단계(S113)를 포함하여 이루어진다.
The first electrochromic layer forming step S110 includes a first coating step S111 and a first drying step S113.

<<S111>><< S111 >>

제1코팅단계(S111)는 상기 제1투명전극체(110)의 일측 면을 제1전기변색소재용액으로 코팅시키는 단계이다. The first coating step S111 is a step of coating one side of the first transparent electrode member 110 with the first electrochromic material solution.

여기서, 제1투명전극체(110)로 이용될 수 있는 것으로는 ITO글라스(110)가 대표적이다. ITO글라스(110)는 빛에 대한 투과성이 있는 글라스의 표면에 ITO(Indium Titanium Oxide)층을 형성시켜서 글라스에 전기전도성을 부여한 것이다. Here, the ITO glass 110 is typically used as the first transparent electrode member 110. The ITO glass 110 is formed by forming an ITO (Indium Titanium Oxide) layer on the surface of a glass having transparency to light, thereby imparting electrical conductivity to the glass.

그리고, ITO글라스 이외에도 전기전도성이 있는 고분자기재체를 이용할 수도 있다. 여기서, 전기전도성이 있는 고분자기재체란 그 자체로서 전기전도성이 있는 것은 물론이고, 고분자기재체에 전기전도성을 주기 위하여 고분자기재체의 일측 면에 전기전도성 있는 물질로 얇게 코팅처리된 것 또한 포함하여 지칭하는 것이다.In addition to the ITO glass, a polymer-based material having electrical conductivity may also be used. Here, the electrically conductive polymer base material is not only electrically conductive but also includes a polymer base material which is thinly coated with an electrically conductive material on one side of the polymer base material to impart electrical conductivity to the polymer base material .

예를 들면, 고분자기재체에 은나노와이어를 포함하는 박막이 형성되어 있는 것을 들을 수 있다. 그리고, 고분자기재체는 폴리에스테르, 폴리에틸렌테레프탈레이트, 폴리페닐렌설파이드, 폴리스티렌, 폴리아미드, 폴리카보네이트, 폴리메틸메타크릴레이트 및 폴리에틸렌나프탈레이트 , 폴리에틸렌 및 폴리프로필렌 중에서 어느 하나 또는 둘 이상을 포함하여 이루어진 것이 바람직하다.
For example, it can be heard that a thin film including a silver nanowire is formed on a polymer base material. The polymer base material may be one or more selected from the group consisting of polyester, polyethylene terephthalate, polyphenylene sulfide, polystyrene, polyamide, polycarbonate, polymethyl methacrylate, polyethylene naphthalate, polyethylene and polypropylene .

그리고, 제1전기변색소재용액은,

Figure pat00015
또는
Figure pat00016
중 어느 하나와 디아이워터(D.I. water) 및 알콜(바람직하게는 이소프로필 알콜)을 포함하여 이루어진 용액인 것이 바람직하다. 여기서 제1전기변색소재용액은 후술할 제2전기변색소재용액과 설명의 편의상 구분될 수 있도록 명칭을 달리하여 설명하는 것이지만, 제1전기변색소재용액과 제2전기변색소재용액이 필히 서로 다른 소재로 이루어진 것이어야 하는 것은 아니다. Then, the first electrochromic material solution contains,
Figure pat00015
or
Figure pat00016
(DI water) and an alcohol (preferably, isopropyl alcohol). The solution of the first electrochromic material and the solution of the second electrochromic material are different from each other so that they can be distinguished from each other for convenience of explanation. It should not be.

Figure pat00017
또는
Figure pat00018
중 어느 하나를 디아이워터(D.I. water) 및 알콜(바람직핫게는 이소프로필 알콜)에 혼합하여 제1전기변색소재용액을 생성시킬 수 있다. 여기서 좀 더 구체적으로는
Figure pat00019
또는
Figure pat00020
중 선택되는 어느 하나와 디아이워터(D.I. water) 및 이소프로필알콜 사이의 질량비가 1:1:1이 되도록 혼합하여 제1전기변색소재용액을 생성시킬 수 있다.
Figure pat00017
or
Figure pat00018
Can be mixed with DI water and alcohol (preferably isopropyl alcohol) to produce a first electrochromic material solution. More specifically,
Figure pat00019
or
Figure pat00020
And a mixture of DI water and isopropyl alcohol in a mass ratio of 1: 1: 1 to produce a first electrochromic material solution.

이렇게 생성된 제1전기변색소재용액을 제1투명전극체(110)인 ITO글라스 혹은 고분자기재체의 일 면에 코팅처리한다. 제1전기변색소재용액으로 코팅하는 방법으로는 스프레이코팅(spray coating), 스핀(spin)코팅, 바코팅, 슬롯 다이(slot die) 코팅 등의 방법이 이용될 수도 있다.
The first electrochromic material solution thus produced is coated on one surface of the ITO glass or polymer-based material as the first transparent electrode member 110. As a method of coating with the first electrochromic material solution, methods such as spray coating, spin coating, bar coating, slot die coating and the like may be used.

<<S113>><< S113 >>

다음으로 제1건조단계(S113)에서는 제1코팅단계(S111)에서 코팅된 제1전기변색소재용액을 건조시켜준다. 즉, 제1투명전극체(110)의 일측 면에 코팅처리된 제1전기변색소재용액을 건조시켜 줌으로써 제1전기변색층(120)이 안정적으로 제1투명전극체(110)의 일측 면에 형성된다. Next, in the first drying step (S113), the first electrochromic material solution coated in the first coating step (S111) is dried. That is, by drying the first electrochromic material solution coated on one side of the first transparent electrode member 110, the first electrochromic layer 120 can be stably deposited on one side of the first transparent electrode member 110 .

예를 들어 상온에서 섭씨 120도 이하의 온도 범위 내에서 10여분 동안 제1전기변색소재용액을 건조시켜서 제1전기변색층(120)을 형성시킨다.
For example, the first electrochromic material 120 is formed by drying the first electrochromic material solution for 10 minutes within a temperature range of 120 degrees Celsius or less at normal temperature.

<<S120>><< S120 >>

전해질층형성단계(S120)는 상기 제1전기변색층형성단계(S110)에서 형성된 상기 제1전기변색층(120)의 일측 면에 전해질층(130)을 형성시키는 단계이다. 여기서, 전해질층(130)은 고분자폴리머(macromolecule polymer) 및 이오닉리퀴드(ionic liquid)를 포함하는 이온젤(ion gel)용액으로부터 형성된다. The electrolyte layer forming step S120 is a step of forming the electrolyte layer 130 on one side of the first electrochromic layer 120 formed in the first electrochromic layer forming step S110. Here, the electrolyte layer 130 is formed from an ion gel solution containing a macromolecule polymer and an ionic liquid.

따라서, 전해질층형성단계(S120)는 고분자폴리머, 이오닉리퀴드 및 용매를 혼합하여 이온젤용액을 형성시키는 단계라고 할 수 있다.Accordingly, the electrolyte layer forming step (S120) may be a step of forming an ionic gel solution by mixing polymeric polymer, ionic liquid and solvent.

이러한 전해질층형성단계(S120)는 A단계 내지 D단계를 포함하여 이루어질 수 있다.
Such an electrolyte layer formation step (S120) may include steps A to D.

<<S121>><< S121 >>

A단계(S121)는 고분자폴리머를 용매에 혼합하여 고분자폴리머 용액을 형성시키는 단계이다. 여기서 고분자폴리머는 PDVF(polyvinylidene fluoride-co-hexafluoropropylene), poly(styrene-block-ethyleneoxide-block styrene)(SOS) triblock copolymer 및 poly(ethylene oxide)-poly(propylene oxide) block copolymer 중에서 어느 하나인 것이 바람직하다.
Step A (S121) is a step of mixing a polymeric polymer with a solvent to form a polymeric polymer solution. It is preferable that the polymer polymer is any one of polyvinylidene fluoride-co-hexafluoropropylene (PDVF), styrene-block-ethyleneoxide-block styrene (SOS) triblock copolymer and poly (ethylene oxide) -poly Do.

<<S123>><< S123 >>

B단계(S123)는 A단계(S121)에서 혼합된 상기 고분자폴리머 용액에 이오닉리퀴드를 첨가하여 이온젤용액을 형성시키는 단계이다. Step B123 is a step of forming an ionic gel solution by adding ionic liquid to the mixed polymer solution in step S121.

여기서 이오닉리퀴드(ionic liquid)는 EMBI(1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide), 1-에틸-3-메틸이미다졸리움 헥사플로로포스포에이트(1-Ethyl-3-methylimidazolium hexafluorophosphoate) 및 1-에틸-3-메틸이미다졸리움 테트라플로로보레이트(1-Ethyl-3-methylimidazolium tetrafluoroborate) 중에서 어느 하나인 것이 바람직하다. Wherein the ionic liquid is selected from the group consisting of 1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide, 1-Ethyl-3-methylimidazolium hexafluorophosphoate, -Ethyl-3-methylimidazolium tetrafluoroborate. The term &quot; ethyl-3-methylimidazolium tetrafluoroborate &quot;

예를 들면, 고분자폴리머와 아세톤을 혼합하고, 여기에 이오닉리퀴드로서 EMBI를 첨가하여 혼합함으로써 이온젤용액을 형성시킬 수 있다. 여기서 바람직하게는 고분자폴리머와 아세톤과 EMBI 사이의 질량비는 1:4:7 로 하여 이온젤용액을 형성시킬 수 있다.
For example, an ionic gel solution can be formed by mixing polymeric polymer and acetone, adding EMBI as an ionic liquid thereto, and mixing. Preferably, the ionic gel solution can be formed at a mass ratio of 1: 4: 7 between the polymer polymer, acetone and EMBI.

<<S125>><< S125 >>

C단계(S125)는 B단계(S123)에서 형성된 이온젤용액을 제1전기변색층(120)의 표면에 코팅시키는 단계이다. Step C125 is a step of coating the surface of the first electrochromic layer 120 with the ionic gel solution formed in step S123.

예를 들면, 이온젤용액을 제1전기변색층(120)의 표면에 스핀 코팅시키는 것이다. 이러한 경우 10초 동안 1500RPM의 회전속도로 스핀코팅 시킬 수 있다. 이와 같이 제1전기변색층(120)의 표면에 이온젤용액을 코팅함으로써 이온젤용액이 제1전기변색층(120)의 표면에 고르게 도포된다.
For example, the ionic gel solution is spin-coated on the surface of the first electrochromic layer 120. In this case, spin coating can be performed at a rotational speed of 1500 RPM for 10 seconds. By coating the surface of the first electrochromic layer 120 with the ionic gel solution as described above, the ionic gel solution is evenly applied to the surface of the first electrochromic layer 120.

<<S127>><< S127 >>

D단계(S127)는 C단계(S125)에서 제1전기변색층(120)의 표면에 코팅된 이온젤용액을 건조시키어 용매를 제거하는 단계이다. Step D127 is a step of drying the ionic gel solution coated on the surface of the first electrochromic layer 120 in step S125 to remove the solvent.

제1전기변색층(120)의 표면에 스핀코팅된 이온젤용액을 고온의 진공오븐에서 장시간 건조시킴으로써 용매를 제거시킬 수 있다. 예를 들면, 섭씨 70도의 온도로 진공오븐속에서 24시간 이상 건조시켜줌으로써 이온젤용액으로부터 용매를 제거시킬 수 있다. The solvent can be removed by drying the ionic gel solution spin-coated on the surface of the first electrochromic layer 120 in a high-temperature vacuum oven for a long time. For example, the solvent may be removed from the ionic gel solution by drying in a vacuum oven at a temperature of 70 degrees Celsius for at least 24 hours.

이와 같은 과정을 거치면서 전해질층(130)이 형성된다.
The electrolyte layer 130 is formed through this process.

<<S130>> << S130 >>

다음으로 제2전기변색층형성단계(S130)는 전해질층형성단계에서 형성된 전해질층(130)의 일측 면에 제2전기변색층(140)을 형성시키는 단계이다. 제2전기변색층형성단계(S130)는 전해질층형성단계(S120) 및 제2투명전극체구비단계(S140) 사이에 이루어질 수 있다. Next, the second electrochromic layer forming step S130 is a step of forming a second electrochromic layer 140 on one side of the electrolyte layer 130 formed in the electrolyte layer forming step. The second electrochromic layer forming step S130 may be performed between the electrolyte layer forming step S120 and the second transparent electrode forming step S140.

이러한 제2전기변색층형성단계(S130)는 제2코팅단계(S131) 및 제2건조단계(S133)를 포함하여 이루어진다.
The second electrochromic layer forming step (S130) includes a second coating step (S131) and a second drying step (S133).

<<S131>><< S131 >>

제2코팅단계(S131)는 전해질층(130)의 일측 면을 제2전기변색소재용액으로 코팅시키는 단계이다. 여기서 제2전기변색소재용액은

Figure pat00021
또는
Figure pat00022
중 어느 하나와 디아이워터(D.I. water) 및 알콜(바람직하게는 이소프로필 알콜)을 포함하여 이루어진 용액인 것이 바람직하다. The second coating step S131 is a step of coating one side of the electrolyte layer 130 with the second electrochromic material solution. Here, the second electrochromic material solution
Figure pat00021
or
Figure pat00022
(DI water) and an alcohol (preferably, isopropyl alcohol).

여기서 제2전기변색소재용액은 전술한 제1전기변색소재용액과 설명의 편의상 구분될 수 있도록 명칭을 달리하여 설명하는 것이지만, 제1전기변색소재용액과 제2전기변색소재용액이 필히 서로 다른 성분분으로 이루어진 것이어야 하는 것은 아니다. The solution of the first electrochromic material and the solution of the second electrochromic material may be different from each other for the sake of explanation. However, the solution of the first electrochromic material and the solution of the second electrochromic material must be different from each other It should not be done in minutes.

Figure pat00023
또는
Figure pat00024
중 어느 하나를 디아이워터(D.I. water) 및 알콜에 혼합하여 제2전기변색소재용액을 생성시킬 수 있다. 여기서 좀 더 구체적으로는
Figure pat00025
또는
Figure pat00026
중 선택되는 어느 하나와 디아이워터(D.I. water) 및 이소프로필알콜 사이의 질량비가 1:1:1이 되도록 혼합하여 제2전기변색소재용액을 생성시킬 수 있다.
Figure pat00023
or
Figure pat00024
Can be mixed with DI water and alcohol to produce a second electrochromic material solution. More specifically,
Figure pat00025
or
Figure pat00026
And a mixture of DI water and isopropyl alcohol in a mass ratio of 1: 1: 1 to produce a second electrochromic material solution.

이렇게 생성된 제2전기변색소재용액을 전해질층(130)의 일측 면에 코팅처리한다. 제2전기변색소재용액으로 코팅하는 방법으로는 스프레이코팅(spray coating), 스핀(spin)코팅, 바코팅, 슬롯 다이(slot die) 코팅 등의 방법이 이용될 수도 있다.
The second electrochromic material solution thus produced is coated on one side of the electrolyte layer 130. As a method of coating with the second electrochromic material solution, methods such as spray coating, spin coating, bar coating, slot die coating and the like may be used.

<<S133>><< S133 >>

다음으로 제2건조단계(S133)에서는 제2코팅단계(S131)에서 코팅된 제2전기변색소재용액을 건조시켜준다. 즉, 전해질층(130)의 일측 면에 코팅처리된 제2전기변색소재용액을 건조시켜 줌으로써 제2전기변색층(140)이 안정적으로 전해질층(130)의 일측 면에 형성된다. Next, in the second drying step (S133), the second electrochromic material solution coated in the second coating step (S131) is dried. That is, the second electrochromic layer 140 is stably formed on one side of the electrolyte layer 130 by drying the second electrochromic material solution coated on one side of the electrolyte layer 130.

예를 들어 상온에서 섭씨 120도 이하의 온도 범위 내에서 10여분 동안 건조시켜서 제2전기변색층(140)을 형성시킨다.
For example, the second electrochromic layer 140 is formed by drying for 10 minutes within a temperature range of room temperature to 120 degrees Celsius.

<<S140>><< S140 >>

다음으로 제2투명전극체구비단계(S140)는 전해질층형성단계(S120)에서 형성된 전해질층(130)의 일측에 전기전도성과 빛에 대한 투과성이 있는 제2투명전극체(150)가 마련되는 단계이다. 다시 말하자면, 제2투명전극체구비단계(S140)에서 제2투명전극체(150)는 전해질층(130)의 일측 면에 형성된 제2전기변색층(140)의 일측 면에 부착시킬 수 있다.Next, in the step of providing the second transparent electrode body (S140), a second transparent electrode member 150 having electrical conductivity and light permeability is formed on one side of the electrolyte layer 130 formed in the electrolyte layer forming step S120 . In other words, in the step of providing the second transparent electrode body (S140), the second transparent electrode member 150 may be attached to one side of the second electrochromic layer 140 formed on one side of the electrolyte layer 130.

여기서, 제2투명전극체(150)로 이용될 수 있는 것으로는 ITO글라스(150)가 대표적이다. ITO글라스는 빛에 대한 투과성이 있는 글라스의 표면에 ITO(Indium Titanium Oxide)층을 형성시켜서 글라스에 전기전도성을 부여한 것이다. Here, the ITO glass 150 is typical as the second transparent electrode member 150. An ITO glass is an ITO (Indium Titanium Oxide) layer formed on the surface of a glass having transparency to light, thereby imparting electrical conductivity to the glass.

그리고, ITO글라스 이외에도 전기전도성이 있는 고분자기재체를 이용할 수도 있다. 여기서, 전기전도성이 있는 고분자기재체란 그 자체로서 전기전도성이 있는 것은 물론이고, 고분자기재체에 전기전도성을 주기 위하여 고분자기재체의 일측 면에 전기전도성 있는 물질로 얇게 코팅처리된 것 또한 포함하여 지칭하는 것이다. In addition to the ITO glass, a polymer-based material having electrical conductivity may also be used. Here, the electrically conductive polymer base material is not only electrically conductive but also includes a polymer base material which is thinly coated with an electrically conductive material on one side of the polymer base material to impart electrical conductivity to the polymer base material .

예를 들면, 고분자기재체에 은나노와이어를 포함하는 박막이 형성되어 있는 것을 들을 수 있다. 그리고, 고분자기재체는 폴리에스테르, 폴리에틸렌테레프탈레이트, 폴리페닐렌설파이드, 폴리스티렌, 폴리아미드, 폴리카보네이트, 폴리메틸메타크릴레이트 및 폴리에틸렌나프탈레이트 , 폴리에틸렌 및 폴리프로필렌 중에서 어느 하나 또는 둘 이상을 포함하여 이루어진 것이 바람직하다.
For example, it can be heard that a thin film including a silver nanowire is formed on a polymer base material. The polymer base material may be one or more selected from the group consisting of polyester, polyethylene terephthalate, polyphenylene sulfide, polystyrene, polyamide, polycarbonate, polymethyl methacrylate, polyethylene naphthalate, polyethylene and polypropylene .

이상에서 설명한 바와 같이 제1전기변색층형성단계(S110)에서 제2투명전극체구비단계(S140)에 이르기까지의 단계를 거치면서 이온젤 스마트 윈도우가 제조될 수 있으며, 앞서 설명한 일 실시예에서 약간 변형된 실시 예 또한 가능하다.As described above, the ion-gel smart window can be manufactured through the steps from the first electrochromic layer forming step (S110) to the second transparent electrode forming step (S140). In the above-described embodiment A slightly modified embodiment is also possible.

이에 대하여 도 3을 더 참조하여 설명하기로 한다. This will be described with reference to FIG.

도 3은 본 발명의 변형된 실시 예에 따른 이온젤 스마트 윈도우 제조방법을 개략적으로 나타낸 순서도이다. 도 3에서 참조되는 바와 같이 본 발명의 변형된 실시 예에서는 앞서 설명한 실시 예에서와 크게 다르지 않다. 다만, 앞서 설명한 실시 예에서는 전해질층형성단계(S120) 이후 전해질층(130)의 일측 면에 제2전기변색층(140)을 형성시키었으나, 변형된 실시 예에서는 제2투명전극체(150)에 제2전기변색층(140)을 형성시킨 후, 제2전기변색층(140)이 형성된 제2투명전극체(150)를 전해질층(130)과 제1전기변색층(120)이 형성된 제1투명전극체(110)와 결합시켜서 이온젤 스마트 윈도우를 제조한다. FIG. 3 is a flowchart schematically showing a method of manufacturing an ion-gel smart window according to a modified embodiment of the present invention. As shown in FIG. 3, the modified embodiment of the present invention is not significantly different from the above-described embodiment. However, in the embodiment described above, the second electrochromic layer 140 is formed on one side of the electrolyte layer 130 after the electrolyte layer forming step S120. However, in the modified embodiment, The second electrochromic layer 140 is formed on the second electrochromic layer 140 and then the second electrochromic layer 140 is formed on the second electrochromic layer 140 to form the electrochromic layer 130 and the first electrochromic layer 120 1 transparent electrode body 110 to produce an ion-gel smart window.

따라서, 도 2 및 도 3에서 참조되는 바와 같이, 제1전기변색층형성단계(S110)의 제1코팅단계(S111)부터 전해질층형성단계(S120)의 D단계(S127)까지는 앞서 설명한 실시 예에서와 같으므로 이후부터 설명하기로 한다.
2 and 3, from the first coating step S111 of the first electrochromic layer forming step S110 to the D step S127 of the electrolyte layer forming step S120, And will be described later.

<<S1300>><< S1300 >>

제2투명전극체준비단계(S1300)는 제2투명전극체구비단계(S140)보다 먼저 이루어지는 단계로서 제2투명전극체구비단계(S140)에서 구비될 상기 제2투명전극체(150)의 일측 면에 전자의 이동에 따라 변색되는 제2전기변색층(140)을 형성시키는 단계이다. The second transparent electrode body preparation step S1300 is performed prior to the second transparent electrode body formation step S140 and may be performed at one side of the second transparent electrode body 150 to be provided at the second transparent electrode body formation step S140 Thereby forming a second electrochromic layer 140 which is discolored in accordance with the movement of electrons.

여기서 제2투명전극체(150)로 이용될 수 있는 것으로는 ITO글라스(150)가 대표적이다. ITO글라스는 빛에 대한 투과성이 있는 글라스의 표면에 ITO층을 형성시켜서 글라스에 전기전도성을 부여한 것이다. Here, the ITO glass 150 is typical as the second transparent electrode member 150. An ITO glass is an electrically conductive layer formed by forming an ITO layer on the surface of a glass having transparency to light.

그리고, ITO글라스 이외에도 전기전도성이 있는 고분자기재체를 이용할 수도 있다. 여기서, 전기전도성이 있는 고분자기재체란 그 자체로서 전기전도성이 있는 것은 물론이고, 고분자기재체에 전기전도성을 주기 위하여 고분자기재체의 일측 면에 전기전도성 있는 물질로 얇게 코팅처리된 것 또한 포함하여 지칭하는 것이다. 예를 들면, 고분자기재체에 은나노와이어를 포함하는 박막이 형성된 것을 들을 수 있다.
In addition to the ITO glass, a polymer-based material having electrical conductivity may also be used. Here, the electrically conductive polymer base material is not only electrically conductive but also includes a polymer base material which is thinly coated with an electrically conductive material on one side of the polymer base material to impart electrical conductivity to the polymer base material . For example, a thin film containing silver nanowires may be formed on a polymer base material.

이와 같은 제2투명전극체(150)의 일측 면에 제2전기변색층(140)을 형성시킨다. 여기서 제2전기변색층(140)을 형성시키기 위한 제2전기변색소재용액은 앞서 설명한 단계에서의 제2전기변색소재용액에 대한 설명과 같다. The second electrochromic layer 140 is formed on one side of the second transparent electrode member 150. Here, the second electrochromic material solution for forming the second electrochromic layer 140 is the same as the description of the second electrochromic material solution in the above-described step.

그리고, 제2투명전극체(150)에 제2전기변색소재용액을 코팅시켜서 제2전기변색층(140)을 형성시킨다.
Then, the second electrochromic material 140 is formed by coating the second electrochromic material solution on the second transparent electrode material 150.

<<S140>><< S140 >>

다음으로 제2투명전극체구비단계(S140)에서는 전해질층형성단계(S120)에서 형성된 전해질층(130)의 일측에 제2투명전극체준비단계((S1300)에서 제2전기변색층(140)이 형성된 제2투명전극체(150)를 부착시킨다. 즉, 전해질층(130)의 일측 면에 제2전기변색층(140)의 면이 접하여 도 1에 도시된 것과 같은 단면구조를 가질수 있게 결합시킨다는 것이다. Next, in the step of forming the second transparent electrode body (S140), a second transparent electrode layer preparation step (S1300) is performed on one side of the electrolyte layer 130 formed in the electrolyte layer formation step (S120) The surface of the second electrochromic layer 140 is in contact with one surface of the electrolyte layer 130 so that the surface of the second electrochromic layer 140 is in contact with the surface of the second electrochromic layer 140, .

이와 같이 제2투명전극체구비단계(S140)까지 거치면서 이온젤 스마트 윈도우가 제조될 수 있다.
As described above, the ion-gel smart window can be manufactured through the step of providing the second transparent electrode body (S140).

한 편,도 2 내지 도 3에 도시되지는 아니하였으나 제2투명전극체구비단계(S140) 이후에 상기 전해질층(130)을 외부로부터 보호하기 위하여 제1투명전극체(110)와 제2투명전극체(150) 사이를 실링시키는 실링단계를 더 포함할 수도 있다. Although not shown in FIGS. 2 to 3, in order to protect the electrolyte layer 130 from the outside after the step of providing the second transparent electrode body (S140), the first transparent electrode body 110 and the second transparent electrode body And a sealing step of sealing between the electrode bodies (150).

이러한 실링단계까지 실시하지 않아도 무방하지만, 미관상의 필요성 또는 이온젤 스마트 윈도우에 대한 보호성을 증진 시키는 차원에서 실링단계까지 실시하는 것 또한 가능하다. 실링하는 구체적인 방법은 통상의 스마트윈도우 제조방법에서 실링하여 마감처리하는 방법을 이용할 수 있다. It is not necessary to perform this sealing step, but it is also possible to carry out the sealing step in order to enhance the cosmetic necessity or the protection against the ion gel smart window. As a specific method for sealing, a method of sealing and finishing in a conventional smart window manufacturing method can be used.

이상에서와 같이 실시 예들을 들어 설명한 바와 같은 방법으로 본 발명에 따른 이온젤 스마트 윈도우를 제조할 수 있다.
As described above, the ion-gel smart window according to the present invention can be manufactured by the method described in the embodiments.

이와 같이 본 발명의 실시 예에 따른 이온젤 스마트 윈도우에 대하여 전압에 따른 전류의 특성을 도 4에 도시하였다. 도 4의 그래프에 나타난 바와 같이 전압에 따른 전류의 차이를 확인할 수 있었으며, 전류의 차이로부터 투과도의 차이를 알 수가 있다. 따라서 변색소자로서의 특성을 잘 나타내는지 여부를 알 수 있는데 도 4에 도시된 바와 같이 변색소자로서의 특성을 잘 나타내고 있다. FIG. 4 shows current characteristics of the ion gel smart window according to the embodiment of the present invention. As shown in the graph of FIG. 4, the difference of the current according to the voltage was confirmed, and the difference of the permeability was found from the difference of the current. Therefore, it can be known whether or not the characteristics as a color-changing element are well represented. As shown in Fig. 4, the characteristics as a color-changing element are well shown.

그리고 도 5에서는 본 발명의 실시 예에 따른 이온젤 스마트 윈도우와 통상의 액체전해질을 이용한 스마트 윈도우와의 투과도 차이를 나타낸 그래프이다. And FIG. 5 is a graph showing a difference in transmittance between a smart window using an ion gel smart window and a conventional liquid electrolyte according to an embodiment of the present invention.

도 5에서 참조되는 바와 같이 통상의 액체전해질에 비해서 본 발명에 따른 이온젤 스마트 윈도우의 경우에 더 높은 투과도를 나타내는 것을 알 수 있다.
As can be seen from FIG. 5, it can be seen that the ion gels according to the present invention exhibit higher transmittance than the conventional liquid electrolytes.

이상에서 설명한 바와 같이 본 발명에 따른 이온젤 스마트 윈도우는 전해질층이 용액이 아닌 이온젤로 이루어지기 때문에 전해질용액이 누출 또는 누액되지 않는다. 따라서, 스마트 윈도우의 안정성과 안전성이 증대되고, 스마트 윈도우의 수명 단축을 억제할 수 있다는 장점이 있다. As described above, the ionic gel smart window according to the present invention does not leak or leak the electrolyte solution because the electrolyte layer is made of an ionic gel rather than a solution. Accordingly, the stability and safety of the smart window are increased, and the shortening of the life of the smart window can be suppressed.

또한 액체전해질을 이용하는 경우와 달리 본 발명에 따른 이온젤 스마트 윈도우의 경우 전해질이 젤 상태이기 때문에 리킹(leaking)이나 베이퍼(vapor)가 발생하지 않으므로 리킹이나 베이퍼로 인한 결함의 발생가능성이 억제된다.또한 대면적화된 스마트 윈도우의 제조가 수월해 진다. 이와 같이 제조공정상에 있어서 제품생산수율 내지 생산성을 증대시킬 수 있다는 장점이 있다.Also, unlike the case of using a liquid electrolyte, in the case of the ion-gel smart window according to the present invention, leaking or vapor is not generated because the electrolyte is in a gel state, and thus the possibility of occurrence of defects due to leakage or vapor is suppressed. It also facilitates the production of large-sized smart windows. Thus, there is an advantage that the product production yield and productivity can be increased at the top of the manufacturing process.

그리고, 잉크젯 프린팅 방법 등을 이용하여 이온젤의 전해질층을 형성시킬 수 있으므로 종래의 액체전해질을 이용하는 경우에 비해서 제조 공정상 좀 더 편리하게 제조할 수 있으며, 좀 더 다양한 형태(모양)을 갖는 스마트 윈도우의 제조가 가능하므로 보다 다양한 형태의 제품 디자인을 창출할 수 있다는 장점이 있다.
In addition, since the electrolyte layer of the ion gel can be formed using an inkjet printing method or the like, it can be manufactured more conveniently in the manufacturing process than in the case of using a conventional liquid electrolyte, and a smart Since the window can be manufactured, it is possible to create more various product designs.

이상에서 설명된 바와 같이, 본 발명에 대한 구체적인 설명은 첨부된 도면을 참조한 실시 예들에 의해서 이루어졌지만, 상술한 실시 예들은 본 발명의 바람직한 실시 예를 들어 설명하였을 뿐이기 때문에, 본 발명이 상기의 실시 예에만 국한되는 것으로 이해되어져서는 아니되며, 본 발명의 권리범위는 후술하는 청구범위 및 그 등가개념으로 이해되어져야 할 것이다. While the present invention has been described in connection with what is presently considered to be practical exemplary embodiments, it is to be understood that the invention is not limited to the disclosed embodiments, but, on the contrary, It is to be understood that the scope of the present invention is to be construed as being limited only by the embodiments, and the scope of the present invention should be understood as the following claims and their equivalents.

110 : 제1투명전극체 120 : 제1전기변색층
130 : 전해질층 140 : 제2전기변색층
150 : 제2투명전극체110: first transparent electrode body 120: first electrochromic layer
130: electrolyte layer 140: second electrochromic layer
150: second transparent electrode body

Claims (21)

전기전도성과 빛에 대한 투과성이 있는 제1투명전극체;
상기 제1투명전극체의 일측에 마련되며, 전자의 이동에 따라 변색되는 제1전기변색층;
상기 제1전기변색층의 일측에 마련되며, 상기 제1전기변색층이 전기변색을 일으킬 수 있도록 전해질로 이루어진 전해질층; 및
상기 전해질의 일측에 마련되며, 전기전도성과 빛에 대한 투과성이 있는 제2투명전극체;를 포함하되,
상기 전해질층은 고분자폴리머 및 이오닉리퀴드(ionic liquid)를 포함하여 이루어지는 이온젤(ion gel)인 것을 특징으로 하는 이온젤 스마트 윈도우.A first transparent electrode body having electrical conductivity and transparency to light;
A first electrochromic layer provided on one side of the first transparent electrode body and discolored by the movement of electrons;
An electrolyte layer provided on one side of the first electrochromic layer and made of an electrolyte so that the first electrochromic layer can cause electrochromism; And
And a second transparent electrode body provided on one side of the electrolyte and having electrical conductivity and transparency to light,
Wherein the electrolyte layer is an ion gel comprising a polymer polymer and an ionic liquid. 제 1항에 있어서,
상기 제1투명전극체 또는 상기 제2투명전극체는,
ITO글라스(indium titanium oxide glass)인 것을 특징으로 하는 이온젤 스마트 윈도우.The method according to claim 1,
Wherein the first transparent electrode member or the second transparent electrode member comprises a transparent electrode,
Characterized by being an ITO glass (indium titanium oxide glass). 제 1항에 있어서,
상기 제1투명전극체 또는 상기 제2투명전극체는,
폴리에스테르, 폴리에틸렌테레프탈레이트, 폴리페닐렌설파이드, 폴리스티렌, 폴리아미드, 폴리카보네이트, 폴리메틸메타크릴레이트, 폴리에틸렌나프탈레이트, 폴리에틸렌 및 폴리프로필렌 중에서 어느 하나로 이루어진 고분자기재체로서 전기전도성을 갖는 물질로 코팅된 것을 특징으로 하는 이온젤 스마트 윈도우. The method according to claim 1,
Wherein the first transparent electrode member or the second transparent electrode member comprises a transparent electrode,
A polymer-based material body made of any one of polyester, polyethylene terephthalate, polyphenylene sulfide, polystyrene, polyamide, polycarbonate, polymethyl methacrylate, polyethylene naphthalate, polyethylene and polypropylene, The ion gel smart window featuring. 제 1항에 있어서,
상기 제1전기변색층은,
Figure pat00027
또는
Figure pat00028
중에서 어느 하나를 포함하여 이루어진 것을 특징으로 하는 이온젤 스마트 윈도우.The method according to claim 1,
Wherein the first electrochromic layer comprises a first electrochromic layer,
Figure pat00027
or
Figure pat00028
Wherein the ionic gel comprises at least one of the following components. 제 1항에 있어서,
상기 전해질층과 상기 제2투명전극체 사이에 위치하며, 전자의 이동에 따라 변색되는 제2전기변색층; 을 더 포함하는 것을 특징으로 하는 이온젤 스마트 윈도우.The method according to claim 1,
A second electrochromic layer disposed between the electrolyte layer and the second transparent electrode and being discolored by the movement of electrons; Further comprising an ion-gel smart window. 제 1항에 있어서,
상기 제2전기변색층은,
Figure pat00029
또는
Figure pat00030
중에서 어느 하나를 포함하여 이루어진 것을 특징으로 하는 이온젤 스마트 윈도우.The method according to claim 1,
The second electrochromic layer may be formed,
Figure pat00029
or
Figure pat00030
Wherein the ionic gel comprises at least one of the following components. 제 1항에 있어서,
상기 전해질층에 포함되는 상기 고분자폴리머는 PDVF(polyvinylidene fluoride-co-hexafluoropropylene), poly(styrene-block-ethyleneoxide-block styrene)(SOS) triblock copolymer 및 poly(ethylene oxide)-poly(propylene oxide) block copolymer 중에서 어느 하나인 것을 특징으로 하는 이온젤 스마트 윈도우.The method according to claim 1,
The polymeric polymer contained in the electrolyte layer may be at least one selected from the group consisting of polyvinylidene fluoride-co-hexafluoropropylene (PDVF), styrene-block-ethyleneoxide-block styrene (SOS) triblock copolymer and poly (ethylene oxide) -poly Wherein the ion-gel smart window is an ion-gel smart window. 제 1항에 있어서,
상기 전해질층에 포함되는 상기 이오닉리퀴드(ionic liquid)는,
EMBI(1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide), 1-에틸-3-메틸이미다졸리움 헥사플로로포스포에이트(1-Ethyl-3-methylimidazolium hexafluorophosphoate) 및 1-에틸-3-메틸이미다졸리움 테트라플로로보레이트(1-Ethyl-3-methylimidazolium tetrafluoroborate) 중에서 어느 하나인 것을 특징으로 하는 이온젤 스마트 윈도우.The method according to claim 1,
The ionic liquid contained in the electrolyte layer may be an ionic liquid,
Ethyl-3-methylimidazolium hexafluorophosphoate, 1-ethyl-3-methylimidazolium bis (trifluoromethylsulfonylimide), 1-ethyl-3-methylimidazolium hexafluorophosphoate (1-Ethyl-3-methylimidazolium tetrafluoroborate). 전기전도성과 빛에 대한 투과성이 있는 제1투명전극체의 일측 면에 전자의 이동에 따라 변색될 수 있는 제1전기변색층을 형성시키는 제1전기변색층형성단계;
상기 제1전기변색층형성단계에서 형성된 상기 제1전기변색층의 일측 면에 전해질층을 형성시키는 전해질층형성단계; 및
상기 전해질층형성단계에서 형성된 상기 전해질층의 일측에 전기전도성과 빛에 대한 투과성이 있는 제2투명전극체가 마련되는 제2투명전극체구비단계;를 포함하되,
상기 전해질층형성단계에서 형성되는 상기 전해질층은,
고분자폴리머 및 이오닉리퀴드(ionic liquid)를 포함하는 이온젤(ion gel)용액으로부터 형성되는 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.A first electrochromic layer forming step of forming a first electrochromic layer capable of being discolored in accordance with the movement of electrons on one side of the first transparent electrode body having electrical conductivity and transparency to light;
An electrolyte layer forming step of forming an electrolyte layer on one side of the first electrochromic layer formed in the first electrochromic layer forming step; And
And forming a second transparent electrode body on the one side of the electrolyte layer formed in the electrolyte layer formation step, wherein the second transparent electrode body has electrical conductivity and transmittance to light,
Wherein the electrolyte layer formed in the electrolyte layer forming step comprises
Wherein the ionic gel is formed from an ion gel solution comprising a polymeric polymer and an ionic liquid. 제 9항에 있어서,
상기 제1전기변색층형성단계는,
상기 제1투명전극체의 일측 면을 제1전기변색소재용액으로 코팅시키는 제1코팅단계; 및
상기 제1코팅단계에서 코팅된 상기 제1전기변색소재용액을 건조시키는 제1건조단계; 를 포함하는 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.10. The method of claim 9,
The first electrochromic layer forming step may include:
A first coating step of coating one side of the first transparent electrode body with a first electrochromic material solution; And
A first drying step of drying the first electrochromic material solution coated in the first coating step; The method comprising the steps of: 제 10항에 있어서,
상기 제1전기변색소재용액은,
Figure pat00031
또는
Figure pat00032
중 어느 하나와 디아이워터(D.I. water) 및 알콜을 포함하여 이루어진 용액인 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.11. The method of claim 10,
Wherein the first electrochromic material solution comprises:
Figure pat00031
or
Figure pat00032
Wherein the solution is a solution containing any one of DI water and alcohol. 제 9항에 있어서,
상기 전해질층형성단계 및 상기 제2투명전극체구비단계 사이에 이루어지는 단계로서,
상기 전해질층형성단계에서 형성된 상기 전해질층의 일측 면에 제2전기변색층을 형성시키는 제2전기변색층형성단계;를 더 포함하고,
상기 제2투명전극체구비단계에서,
상기 제2투명전극체는 상기 제2전기변색층의 일측 면에 마련되는 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.10. The method of claim 9,
The step of forming the electrolyte layer, and the step of forming the second transparent electrode body,
A second electrochromic layer forming step of forming a second electrochromic layer on one side of the electrolyte layer formed in the electrolyte layer forming step,
In the step of forming the second transparent electrode,
Wherein the second transparent electrode body is provided on one side of the second electrochromic layer. 제 12항에 있어서,
상기 제2전기변색층형성단계는,
상기 전해질층의 일측 면을 제2전기변색소재용액으로 코팅시키는 제2코팅단계; 및
상기 제2코팅단계에서 코팅된 상기 제2전기변색소재용액을 건조시키는 제2건조단계;를 포함하는 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.13. The method of claim 12,
The second electrochromic layer forming step may include:
A second coating step of coating one side of the electrolyte layer with a second electrochromic material solution; And
And a second drying step of drying the second electrochromic material solution coated in the second coating step. 제 13항에 있어서,
상기 제2전기변색소재용액은,
Figure pat00033
또는
Figure pat00034
중 어느 하나와 디아이워터(D.I. water) 및 알콜을 포함하여 이루어진 용액인 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.14. The method of claim 13,
The second electrochromic material solution is a solution of
Figure pat00033
or
Figure pat00034
Wherein the solution is a solution containing any one of DI water and alcohol. 제 9항에 있어서,
상기 제2투명전극체구비단계 이전에 이루어지는 단계로서,
상기 제2투명전극체구비단계에서 마련될 상기 제2투명전극체의 일측 면에 전자의 이동에 따라 변색되는 제2전기변색층을 형성시키는 제2투명전극체준비단계;를 더 포함하고,
상기 제2투명전극체구비단계에서는,
상기 전해질층의 일측에 상기 제2투명전극체준비단계에서 상기 제2전기변색층이 형성된 상기 제2투명전극체를 부착시키는 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법. 10. The method of claim 9,
Wherein the step of forming the second transparent electrode body comprises:
Forming a second electrochromic layer on the one side of the second transparent electrode body, the second electrochromic layer being discolored by the movement of electrons, the second electrochromic layer being formed in the second transparent electrode body,
In the step of forming the second transparent electrode body,
And the second transparent electrode body on which the second electrochromic layer is formed is attached to one side of the electrolyte layer in the second transparent electrode body preparation step. 제 9항에 있어서,
상기 제2투명전극체구비단계 이후에,
상기 전해질층을 외부로부터 보호하기 위하여 상기 제1투명전극체와 상기 제2투명전극체 사이를 실링시키는 실링단계;를 더 포함하는 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.10. The method of claim 9,
After the step of forming the second transparent electrode body,
And sealing the first transparent electrode body and the second transparent electrode body in order to protect the electrolyte layer from the outside. 제 9항에 있어서,
상기 전해질층형성단계는,
고분자폴리머를 용매에 혼합하여 고분자폴리머 용액을 형성시키는 A단계;
상기 A단계에서 혼합된 상기 고분자폴리머 용액에 이오닉리퀴드를 첨가하여 이온젤용액을 형성시키는 B단계;
상기 B단계에서 형성된 상기 이온젤용액을 상기 제1전기변색층의 표면에 코팅시키는 C단계; 및
상기 C단계에서 상기 제1전기변색층의 표면에 코팅된 상기 이온젤용액을 건조시키어 용매를 제거하는 D단계;
를 포함하는 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.10. The method of claim 9,
Wherein the electrolyte layer forming step comprises:
(A) mixing the polymeric polymer with a solvent to form a polymeric polymer solution;
A step B for adding an ionic liquid to the polymer polymer solution mixed in the step A to form an ionic gel solution;
A step C of coating the surface of the first electrochromic layer with the ionic gel solution formed in step B; And
Drying the ionic gel solution coated on the surface of the first electrochromic layer in step C to remove the solvent;
The method comprising the steps of: 제 17항에 있어서,
상기 고분자폴리머는 PDVF(polyvinylidene fluoride-co-hexafluoropropylene), poly(styrene-block-ethyleneoxide-block styrene)(SOS) triblock copolymer 및 poly(ethylene oxide)-poly(propylene oxide) block copolymer 중에서 어느 하나인 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.18. The method of claim 17,
The polymer may be any one of polyvinylidene fluoride-co-hexafluoropropylene (PDVF), styrene-block-ethyleneoxide-block styrene (SOS) triblock copolymer, and poly (ethylene oxide) -poly A method for manufacturing an ion gel smart window. 제 17항에 있어서,
상기 이오닉리퀴드(ionic liquid)는,
EMBI(1-Ethyl-3-methylimidazolium bis trifluoromethylsulfonylimide), 1-에틸-3-메틸이미다졸리움 헥사플로로포스포에이트(1-Ethyl-3-methylimidazolium hexafluorophosphoate) 및 1-에틸-3-메틸이미다졸리움 테트라플로로보레이트(1-Ethyl-3-methylimidazolium tetrafluoroborate) 중에서 어느 하나인 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.18. The method of claim 17,
The ionic liquid,
Ethyl-3-methylimidazolium hexafluorophosphoate, 1-ethyl-3-methylimidazolium bis (trifluoromethylsulfonylimide), 1-ethyl-3-methylimidazolium hexafluorophosphoate (1-Ethyl-3-methylimidazolium tetrafluoroborate). 제 9항에 있어서,
상기 제1투명전극체 또는 상기 제2투명전극체는,
ITO글라스(indium titanium oxide glass)인 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법.10. The method of claim 9,
Wherein the first transparent electrode member or the second transparent electrode member comprises a transparent electrode,
Wherein the first electrode is an ITO glass (indium titanium oxide glass). 제 9항에 있어서,
상기 제1투명전극체 또는 상기 제2투명전극체는,
폴리에스테르, 폴리에틸렌테레프탈레이트, 폴리페닐렌설파이드, 폴리스티렌, 폴리아미드, 폴리카보네이트, 폴리메틸메타크릴레이트, 폴리에틸렌나프탈레이트, 폴리에틸렌 및 폴리프로필렌 중에서 어느 하나로 이루어진 고분자기재체로서 전기전도성을 갖는 물질로 코팅된 것을 특징으로 하는 이온젤 스마트 윈도우 제조방법. 10. The method of claim 9,
Wherein the first transparent electrode member or the second transparent electrode member comprises a transparent electrode,
A polymer-based material body made of any one of polyester, polyethylene terephthalate, polyphenylene sulfide, polystyrene, polyamide, polycarbonate, polymethyl methacrylate, polyethylene naphthalate, polyethylene and polypropylene, Wherein the method comprises the steps of:
KR1020150022566A 2015-02-13 2015-02-13 Ion Gel Smart Window Manufacturing Method KR101656466B1 (en)