KR20160067366A - Method of producing environmentally friendly water-based paint elastic waterproof coating composition - Google Patents
Method of producing environmentally friendly water-based paint elastic waterproof coating composition Download PDFInfo
- Publication number
- KR20160067366A KR20160067366A KR1020140172663A KR20140172663A KR20160067366A KR 20160067366 A KR20160067366 A KR 20160067366A KR 1020140172663 A KR1020140172663 A KR 1020140172663A KR 20140172663 A KR20140172663 A KR 20140172663A KR 20160067366 A KR20160067366 A KR 20160067366A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- water
- paint composition
- resistance
- powder
- Prior art date
Abstract
Description
본 발명은 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물 및 이의 제조방법에 관한 것으로, 더욱 상세하게는 콘크리트 재, 금속스틸 재, 목재, 플라스틱 재, 석재, 등의 표면에 마감도장재로 사용되고, 방수성, 방미성, 방식성, 방부성, 전기절연성, 내 화학성, 내 산성, 내알칼리성, 내식성, 내후 성, 신축성, 내구성, 내광성, 내염성, 부착성, 내노화성의 다양한기능성에 의하여 건설물의 내, 외장에서 발생하는 누수, 균열, 부풂, 파단, 풍압, 구멍 뚫림, 오염, 변색, 전기전류, 곰팡이세균번식, 라돈방출, 열에너지유실 , 소음, 부식, 부패를 방지하고, 투명한 백색조성물과 다양한색상의 유색조성물로 형성되고, 도장을 한 후에는 반질한탄성력의 경질성고무탄성도막이 형성되는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물 및 이의 제조방법에 관한 것이다.
More particularly, the present invention relates to a water-repellent, environmentally friendly, water-repellent, water-repellent paint composition for interior and exterior finishes of construction materials, and more particularly to a water- It is used in the construction of waterproofing materials by various functions such as waterproof property, water repellency, anticorrosive property, anticorrosive property, electrical insulation property, chemical resistance, acid resistance, alkali resistance, corrosion resistance, weather resistance, stretchability, durability, light resistance, , Prevents leakage, cracks, cracks, cracks, breakage, wind pressure, piercing, pollution, discoloration, electric current, fungus propagation, radon emission, thermal energy loss, noise, corrosion and decay, , And an eco-friendly elastic film for waterproof and weatherproofing of construction materials in which a hard rubber elastic film with a semi-elasticity is formed after coating is formed. And to a process for producing the same.
오늘날 건설물의 내, 외장의 마감재로 사용되는 콘크리트재, 금속스틸재, 목재, 플 라스틱재, 석재가 있으며, 그 외에 수성페인트와 유성페인트를 마감재용 도장재로 많이 사용되고 있다. 일반적으로 건설물의 마감재용으로 사용되는 하나의 도장재 로서, 중성수를 용제와 희석재로 사용되는 수성페인트는, 초기도장에서 냄새가 지 속적으로 장기간 발생하여 실내의 공기를 오염시키고, 방수성, 등의 기능성이 취약 하여 부패, 곰팡이세균번식, 박리, 크랙, 부풂, 오염과 분진의 발생으로 환경과 인 체의 건강이 저하되고, 재 도장을 해야 하는 원가상승의 원인이 되고 있으며, 다른 하나의 마감재용 도장재로 사용되는 유성페인트는 도장 후 발수성, 방식성, 내마모 성, 등의 기능성이 기후변화에 의하여 물성강도가 저감되어 박리, 크랙, 부풂, 오염 이 발생하여 다목적용도의 사용과 건설물 표면의 장기적인 보존은 한계가 있고, 더 욱 더 유기용매를 이용하여 용제와 희석재로 사용되고, 휘발성유기화합물과 중금속 물질, 등의 유해물질을 포함하고 있어 대기환경오염과 수질환경오염 및 인체의 건 강을 저해하는 요인으로 도출되고 있음을 많은 사람들이 알고 있으나, 현재에서도 상기와 같은 문제점과 요인을 해소 할 수 있는 다양한기능성과 다목적용도의 마감 재용 도장재가 없는 부재한 실정에서 기존의 수성페인트와 유성페인트를 사용할 수 밖에 없는 현실에 있다, Today, there are concrete, steel, wood, plastic, and stone used as finishing materials for interior and exterior of construction products. In addition, water-based paints and oil-based paints are widely used as coating materials for finishes. Water paint, which is generally used as a finishing material for construction materials, is used as a solvent and a diluent for neutral water. The water paint which is used as a solvent and diluent has a problem in that the odor is generated for a long time in the initial painting, Due to poor functionality, the environment and human health are reduced due to corruption, fungus breeding, peeling, cracks, cracks, pollution and dust generation, causing a cost increase to be repainted. The oil-based paint used as a coating material has many properties such as water repellency, anticorrosive property, abrasion resistance and the like after coating, because of the decrease of the physical strength due to the climate change, resulting in peeling, cracking, There is a limit to long-term preservation, and organic solvents are used as solvents and diluents, and volatile organic compounds and heavy metal substances, However, many people know that it is a factor that hinders the air pollution, water pollution, and the health of the human body. However, at present, various functionalities and versatile use finishes In the absence of recycled paint, it is inevitable to use existing water-based paints and oil-based paints.
따라서, 현재에서 요구되는 건설물의 내, 외장마감재용 도장재는 중성수를 용제와 희석재로 사용되고, 유해물질이 없고, 방수성, 방미성, 방식성, 방부성, 전기절연성, 내화학성, 내산성, 내알칼리성, 내식성, 내후성, 신축성, 내구성, 내광성, 내염성, 부 착성의 다양한기능성과 건설물의 내, 외장의 콘크리트재, 금속스틸 재, 목재, 플라 스틱재, 석재, 등의 표면에 다목적용도로 도장이 되고, 건설물의 내, 외장에서 발생 하는 누수, 균열, 부풂, 파단, 풍압, 구멍 뚫림, 오염, 변색, 충격, 부식, 부패, 분진방 지 및 전기전류흐름, 곰팡이세균번식, 방사능라돈방출, 열에너지유실, 소음을 방지 하고, 대기환경과 수질환경 및 인체의 건강을 보존하고, 건설물의 수명을 반영구적 으로 유지되는 무독성, 무취 성, 무해성의 수성페인트의 필요성이 주지되고 있다. Therefore, coating materials for interior and exterior finishing materials required in the current construction are used as neutralizing water as a solvent and diluent, and are free from harmful substances, and are excellent in water resistance, odor, anticorrosion, antistatic, electrical insulation, It is applied to the surface of various materials such as corrosion resistance, weather resistance, elasticity, durability, light resistance, salt resistance and adhesion and the surface of concrete, steel, wood, plastic, , Leakage, cracks, cracks, breakage, wind pressure, puncture, contamination, discoloration, impact, corrosion, decay, dust prevention and electric current flow, fungus propagation, radioactive radon emission, thermal energy loss , A need exists for a non-toxic, odorless and harmless water-based paint which can prevent noise, conserve the atmospheric environment, the water quality environment and the human health, and which is semi-permanently maintained for the life of the construction.
상기 주지된바와 같이 건설물의 표면에 도장재로 사용하는 수성페인트(에멀션수지)와 수용성 베이킹수지 도료, 등은 물을 용제로 하고 전색제로 합성고무수지, 알키 드수지, 멜라민수지, 아크릴수지, 아교, 카세인, 등을 사용한 수용성페인트가 있으나 , 내열성, 방수성 , 방식성, 탄성(신축성), 방미성, 절연성, 내화학성, 내구성, 내후성, 내마모성, 부착성의 다양한기능성의 결여로 금속스틸 재, 목재, 플라스틱재, 콘크리 트재의 마감도장재로 사용한 후에는 빗물과 기온변화 및 화학물질에 의한 누수, 균 열, 부풂, 파단, 풍압, 구멍 뚫림, 오염, 변색, 부식, 부패, 분진, 전기전류, 곰팡이 세 균번식, 방사능라돈방출, 에너지유실, 소음을 방지하지 못하고, 유해물질의 분진이 발생하여 대기환경과 수질환경 및 건강생활에 피해가 발생 할 수 있으며, 원가상승 의 원인이 될 수 있다.As is well known, water-based paint (emulsion resin) and water-soluble baking resin paint, which are used as a coating material on the surface of a construction material, are used as a solvent, and synthetic rubber resins, alkyd resins, melamine resins, acrylic resins, Water-based paints made of metal, steel, wood, plastics, etc. due to lack of various functions such as heat resistance, waterproofness, anticorrosion, elasticity (elasticity), transparency, insulation, chemical resistance, durability, weather resistance, abrasion resistance, After use as a finishing material for concrete and ash concrete, it is recommended to use it after rainwater and temperature changes and chemical leaks, cracks, cracks, breakage, wind pressure, puncture, contamination, discoloration, corrosion, decay, dust, It does not prevent propagation, radioactive radon emission, energy loss, and noise, and harmful substance dust can be generated, causing damage to the atmospheric environment, water quality environment and health life. This may cause.
또한, 기존의 에폭시페인트 및 변성알키드수지, 페놀수지, 멜라민변성아크릴수지, 아미노수지, 등의 페인트는 내수성 과 내구성 및 내마모성, 탄성도막, 등의 특성적인 기능성은 있으나. 다목적용도와 다양한기능성의 도장재로 사용하기에는 한계가 있으며, 화재에 취약하고 화재 시에 독가스발생 과 빗물산성화와 기온변화 및 화 학물질에 의한 빠른 노화현상으로 수축과 팽창이 반복적으로 발생하여, 크랙과 박 리 및 분진이 발생하고, 크랙의 틈새와 흡수로 스며든 빗물 및 화학물질, 등의 침 투로 내구성이 저감되어 페놀 계, VOC, 이소시에이트계, 아민계, 등의 유해성물질 의 분진과 표출로 대기환경과 수질환경을 오염시키는 단점과 건강질환의 발생 및 원가상승의 원인이 될 수 있다.In addition, conventional paints such as epoxy paint and modified alkyd resin, phenol resin, melamine modified acrylic resin, amino resin, etc. have the specific functionalities such as water resistance, durability, abrasion resistance and elastic film. It is limited to be used as a multi-purpose application and various functional coating materials, and it is vulnerable to fire, and it causes repetitive shrinkage and expansion due to poisonous gas, fire acidification, temperature change and rapid aging due to chemicals, Dirt and dust are generated and the durability is reduced due to cracks and penetration of rainwater and chemical substances which have penetrated into the absorption, and dust and appearance of harmful substances such as phenol, VOC, isocyte, amine, It can cause pollution of air environment and water quality environment, cause health diseases and increase cost.
한편 대한민국 특허 출원번호 10-2008-0068099호는 신축성이 우수한 수용성 도료조성물의 제조방법의 구성 재료들과 제조방법에 있어서, 소디움헥사메타포스 페이트, 폴리다이메틸실록세인, 벤지소시아졸린, 물, 프로필랜글리콜, 우레탄계를 교 반 한 후, 이산화티탄 5 ~ 20 중량 부를 첨가하여(S1단계), 교반한고, 메탈메타아크 릴레이트에멀션 30 ~ 100 중량 부를 첨가(S2단계)하고, 수산화암모늄과 우레탄계 증점제를 혼합 삼분하여 차례대로 첨가(S3단계)로 제조되는 우수한 수용성도료 조성물이 개시되어 있다. Korean Patent Application No. 10-2008-0068099 discloses a method for producing a water-soluble coating composition excellent in stretchability and a method for producing the water-soluble coating composition, which comprises the steps of mixing sodium hydroxymethosulfate, polydimethylsiloxane, benzisocyanurine, (Meth) acrylate emulsion is added (Step S2), followed by addition of ammonium hydroxide and urethane-based thickener (5 parts by weight) (Step S3). The water-soluble coating composition according to the present invention is prepared by mixing the above-mentioned components in an aqueous solution.
또한 대한민국 특허 출원번호 10-2008-0126491호는 수용성도료 조성물의 구성 재료들과 제조방법에 있어서, 카르복실기성분을 함유한 에멀션수지와 폴리우레탄디 스퍼션수지, 믹싱바인더용 pH조절 제 및 제1용제를 포함하는 믹싱바인더 중량 부, 폴리에스테르수지, 안료, 페이스트 조절용 pH 조절 제 및 제2용제를 포함하는 칼 라 페이스트 조성물 중량부로 이루어진 수용성도료 조성물이 개시되어 있다.Korean Patent Application No. 10-2008-0126491 discloses a water-soluble paint composition and a method for producing the water-soluble paint composition, which comprise an emulsion resin containing a carboxyl group component and a polyurethane dispersion resin, a pH adjuster for a mixing binder, , A polyester resin, a pigment, a pH adjusting agent for adjusting the paste, and a second solvent, based on the weight of the coloring composition.
대한민국 특허 등록번호 10-0882840호는 방수페인트조성물의 제조방법 및 그에 의하여 제조된 방수페인트 조성물의 구성 재료들과 제조방법이 개시된 바 있다. Korean Patent Registration No. 10-0882840 discloses a process for producing a waterproof paint composition and a constituent material of the waterproof paint composition and a manufacturing method thereof.
대한민국 특허 등록번호 10-1259773호는 건축물의 실내 마감재용 친환 경 수성페인트 조성물에 있어서, 유해물질을 흡착하기 위한 규조토 3 ~ 6 중량% 와 ; 탈취 효과를 강화시키기 위한 이산화티탄 7 ~ 12 중량%와 ; 실내의 공기로 부터 유래되는 유해한 균을 사멸시키는 항균제 마이크로캡슐 0.4 ~ 1.5 중량%와; 실내공기로 부터 유래되는 진균의 번식을 방지하는 방부제 0.1 ~ 0.5 중량%와; 수 성페인트 조성물의 각종 성분들을 서로 결합시키고 매끈한 표면을 형성하게 되는 무기바인더 30 ~ 40 중량%와; 수성페인트의 재료배합을 수행하고 작업성을 조절 할 수 있는 물 3 ~ 10 중량%와; 그리고 나머지는 수성페인트의 페이스물질로서 작업시에 두께를 형성하게 되는 규사로 제조된 조성물이 개시된 바 있다. Korean Patent Registration No. 10-1259773 discloses an environmentally friendly waterborne paint composition for indoor finishes of buildings, which comprises 3 to 6% by weight of diatomaceous earth for adsorbing harmful substances; 7 to 12% by weight of titanium dioxide for enhancing the deodorizing effect; 0.4 to 1.5% by weight of an antibacterial microcapsule for destroying harmful bacteria derived from indoor air; 0.1 to 0.5% by weight of an antiseptic to prevent the propagation of fungi derived from indoor air; 30 to 40% by weight of an inorganic binder which binds the various components of the aqueous paint composition together and forms a smooth surface; 3 to 10% by weight of water capable of performing the material blending of the aqueous paint and controlling the workability; And the balance being a face material of water-based paint, which forms a thickness upon working.
이와 같은 유해물질을 포함하고 다양한기능성과 다목적용도로 사용 할 수 없는 수성페인트와 유성페인트를 건설물의 내, 외장의 마감재용 도장재로 사용하고 있는 한, 근본적인 문제점을 해소 할 수 없는 것으로 평가되고 있다.
As long as water-based paints and oil-based paints that contain such harmful substances and can not be used for various functionalities and multipurpose applications are used as coating materials for interior and exterior finishes of construction products, it is estimated that the fundamental problem can not be solved.
본 발명은 상기한 종래 기술의 문제점을 해소하기 위해 안출된 것으로, 콘크리트재, 금속스틸재, 목재, 플라스틱재, 석재를 사용한 건설물의 내, 외장 의 벽체, 천장, 바 닥, 옥상, 지하실과 콘크리트구조물, 금속스틸 구조물, 교량, 터널, 수영장, 폐수장, 전선관, 하수관, 자동차, 비행기, 기차, 선박, 공장, 연구소, 노출콘크리트하우스, 콘크리트아파트, 전원주택, 수상목조주택, 벽돌집, 시멘트벽돌, 방음벽, 터널, 지하벙커, 금속외장의 빌딩, 전봇대, 글라스 울(glass wool), 발포스티로폼, 직물, 전봇대, 등의 표면에 미감재용 방수페인트 조성물로 사용되고, 누수, 균열, 부풂 , 파단, 풍압, 구 뚫림, 오염, 변 색, 전기전류, 곰팡이 세균 번식, 방사능 라돈방출, 열에너지유실, 소음, 부식, 부패, 화재를 방지하고, 시멘트몰탈과 무기질세립 제 및 난연재, 단열재, 재료와 각각 혼합하여, 방수난연 단열재, 층간바닥방수 충전 차음 몰탈재, 경량부력 방수콘크리트 알갱이, 부자, 부표, 구명주부, 보트, 방수전기 절연장갑, 방수텐트, 방수 우의, 방수난연 도료, 등의 자재들로 제조되고, 도장의 지촉시간과 완전 건조시간이 빠르고, 도장이 건조된 후에는 평탄하고 부드러운 신축성의 반질한(glossy) 무광택 과 광택의 방수성 경질탄성도막이 표면에 형성되어 잔도장물과 먼지, 기름떼, 등을 물과 비눗물로 세척이 되고, 중성수를 용제와 희석제로 사용하고, 휘발성유기화 합물(VOCs), 톨루엔, 포름알데히드, 중금속, 등의 유독성물질과 유해물질이 없어, 대기 오염과 수질오염 및 건강질환(아토피성질환 및 호흡기질환, 등)을 방지하고, 무독성 , 무취 성, 무해성의 투명한 백색조성물과 다양한색상의 유색조성물로 사용되는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법을 제공하는데 그 목적이 있다.
The present invention has been conceived to overcome the problems of the prior art described above, and it is an object of the present invention to provide a method of manufacturing a concrete structure, a steel material, a wood material, a plastic material, Concrete brick, brick house, brick house, brick house, brick house, brick house, brick house, brick house, bridge, tunnel, It is used as a waterproof paint composition for unrecognized surfaces such as soundproof walls, tunnels, underground bunkers, metal exterior buildings, electric poles, glass wool, foamed styrofoam, fabric, electric poles, It is used to prevent pitting, pollution, discoloration, electric current, fungus propagation, radioactive radon emission, thermal energy loss, noise, corrosion, corruption and fire, and to prevent cement mortar and inorganic fine particles and flame retardant, Waterproof flame retardant insulation material, interlayer bottom waterproof filling sound insulating mortar material, lightweight buoyancy waterproof concrete granule, rich, buoy, life-saving housewife, boat, waterproof electric insulating glove, waterproof tent, It is made of materials and has a fast touch time and complete drying time of the coating. After the coating is dried, a smooth, soft, elastic glossy, glossy, waterproof hard elastic coating is formed on the surface, Oil flocks and so on are washed with water and soapy water and neutral water is used as a solvent and diluent and there are no toxic and harmful substances such as volatile organic compounds (VOCs), toluene, formaldehyde, heavy metals, It prevents water pollution and health diseases (atopic diseases and respiratory diseases, etc.), and is used as a non-toxic, odorless, harmless transparent white composition and a colored composition of various colors To provide a set of water within the method of manufacturing an eco-friendly external finishing coating elastic water resistant water-based paint composition has the purpose.
본 발명의 일 실시예는, 프로필렌글리콜(propylene glycol), 부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체(butylacryl-2ethylhexylacrylatemethylmethacryl acid-acrylsilanecopolymer), 소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate-2Sodiumcarboxymethylcellulose), 콜로이달 실리카, 중성수를 혼합하여 이루어진 것을 특징으로 하는 수성페인트 조성물의 제조방법에 의해 달성된다. One embodiment of the present invention is a process for preparing a polyurethane resin composition comprising propylene glycol, butylacryl-2-ethylhexyl acrylate methyl methacrylate-acrylsilane copolymer (butylacryl-2ethylhexylacrylate methylmethacryl acid-acrylsilanecopolymer), sodium polyacrylate-2 sodium carboxymethyl Characterized in that the aqueous paint composition is prepared by mixing sodium polyacrylate-2 sodium carboxymethylcellulose, colloidal silica, and neutral water.
상기한 본 발명의 목적은, 스티렌 부타디엔 고무, 프로필렌글리콜(propyleneglyc ol), 부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체 (butylacryl-2ethylhexylacrylatemethylmethacrylic acid-acrylsilanecopolymer), 소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate-2Sodiumcarboxymethylcellulose), 콜로이달 실리카, 중성수를 혼합하여 이루어지는 것을 특징으로 하는 수성페인트 조성물의 제조방법에 의해 달성된다. It is an object of the present invention to provide a resin composition which is excellent in heat resistance and durability and which is excellent in heat resistance and durability when used in combination with other resins such as styrene butadiene rubber, propyleneglycol, butylacryl-2-ethylhexyl acrylate methyl methacrylate-acrylsilane copolymer (butylacryl-2-ethylhexylacrylate methylmethacrylic acid-acrylsilanecopolymer) 2 sodium carboxymethylcellulose, colloidal silica, and neutral water. The water-based paint composition according to claim 1,
상기한 본 발명의 목적은, 스티렌 부타디엔 고무, 프로필렌글리콜(propyleneglycol), 부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체(butylacryl-2ethylhexylacrylatemethylmethacryl acid-acrylsilan ecopolymer), 소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate- 2Sodiumcarboxymethylcellulose), 이산화티타늄, 백토분말, 조개분말, 탄산칼슘분말, 무기질분말, 무기질안료, 중성수, 콜로이달 실리카를 혼합하여 이루어지는 것을 특징으로 하는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법과 관련된다.
It is an object of the present invention to provide a resin composition which is excellent in heat resistance and durability due to the use of styrene butadiene rubber, propyleneglycol, butylacryl-2-ethylhexyl acrylate methyl methacrylate-acrylsilane copolymer (butylacryl-2-ethylhexylacrylate methylmethacrylate- 2 is a mixture of sodium polyacrylate-2 sodium carboxymethylcellulose, titanium dioxide, clay powder, shell powder, calcium carbonate powder, inorganic powder, mineral pigment, neutral water and colloidal silica. The present invention relates to a process for the preparation of water-repellent, water-repellent, and water-repellent paint compositions.
본 발명에 의한 친환경 탄성도막방수 수성페인트 조성물을 이용하여 건설물의 내, 외장에 사용 할 경우, 방수성, 내열성, 방식성, 방미성, 탄성(신축성), 전기절연성, 내화학성, 내구성, 내후성, 내마모성, 부착성, 내노화성의 다양한기능성에 의하여 건설물의 내, 외장에서 발생하는 누수, 균열, 부풂, 파단, 풍 압, 구멍 뚫림, 오염, 변색, 전기전류, 곰팡이세균번식, 방사능 라돈방출, 열에너지유 실, 소음, 부식, 부패를 방지하여 건설물의 수명을 반영구 적으로 보존하고, 대기환 경과 수질환경 및 도시환경을 개선하고 보호하는 장점이 있다. The water-repellent, heat-resistant, anticorrosive, water-repellent, elastic (stretchable), electrical insulating, chemical resistance, durability, weather resistance, and wear resistance of the water- , Cracks, cracks, breakage, wind pressure, piercing, pollution, discoloration, electric current, fungus propagation, radioactive radon emission, heat energy generated in interior and exterior of construction by various functionalities of adhesion, It has the advantage of preserving the life span of the construction by preventing thread, noise, corrosion and corruption, and improving and protecting the atmospheric environment, the water quality environment and the urban environment.
또한, 본 발명에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트조성물을 이용하여 건설물의 내, 외장에 사용 할 경우, 유기용매를 용제와 희석 재로 사용하지 않고, 유해성유기화합물(VOCs) 및 중금속물질을 포함하고 있지 않 아, 유해물질과 악취에 의한 대기환경오염과 수질환경오염 및 인체의 건강질환(아 토피성피부질환 및 호흡기질환, 등)을 방지하는 친환경 무독성, 무취 성, 무해 성의 장점이 있다. In addition, when the waterproof paint composition of the present invention is used for interior and exterior use of building waterproof paint compositions for interior and exterior finishes of construction materials, it is possible to use organic solvents (VOCs) And non-toxic, non-toxic, harmless, and toxic substances that do not contain heavy metals and prevent air pollution and environmental pollution caused by harmful substances and odors, and health diseases (athophilic skin diseases and respiratory diseases, etc.) There is an advantage of sex.
또한, 본 발명에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 건설물의 내, 외장에 사용할 경우, 콘크리트재, 금속스틸재, 목재, 플라스틱재, 석재, 글라스 울재, 발포 스티로폼재, 직물, 등의 표면에 방수성, 내열성, 방식성, 방미성, 탄성(신축성), 전기절연성, 내화학성, 내구성, 내후성, 내마 모성, 내염성, 부착성, 내노화성의 다양한기능성에 의하여 누수, 균열, 부풂, 파단, 풍압, 구멍 뚫림, 오염, 변색, 전기전류, 곰팡이세균번식, 방사능라돈방출, 열에너지 유실, 소음, 부식, 부패를 방지하는 다목적용도로 사용되어 반영구적으로 유지되는 원가절감의 장점이 있다. In addition, when the waterproof paint composition of the present invention is used for the interior and exterior of a building using the waterproof paint composition of the present invention, it can be used as a concrete material, a metal material, a wood material, a plastic material, a stone material, (Water repellency), electrical insulation, chemical resistance, durability, weather resistance, abrasion resistance, salt resistance, adherence, and aging resistance on the surfaces of the water-repellent, styrofoam, It is used for multipurpose applications to prevent cracks, cracks, breakage, wind pressure, puncture, pollution, discoloration, electric current, fungus propagation, radioactive radon emission, heat energy loss, noise, corrosion and corruption. There are advantages.
또한, 본 발명에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 건설물의 내, 외장에 사용할 경우, 색상선명도가 밝고, 평탄 하고 부드러운 신축성의 반질(glossy)한 무광택과 광택의 방수성경질탄성도막이 표면에 형성되어 잔도장물과 먼지, 기름 떼, 등을 물과 비눗물로 세척이 되고, 교량, 터널, 수영장, 폐수장, 전선관, 하수관, 자동차, 비행기, 기차, 선박, 공장, 연구소, 병 원, 노출콘크리트하우스, 콘크리트아파트, 전원주택, 수상목조주택, 벽돌집, 시멘트 벽돌, 방음벽, 터널, 지하벙커, 합 금속외장의 빌딩, 전봇대, 글라스 울(glass wool), 발포스티로폼, 직물, 전봇대, 등의 표면에 미감재용 탄성도막방수 수성페인트로 사 용 되고, 도장 후 빠른 지촉건조시간과 완전건조시간으로 설치마감도장시간이 단축 되어 공사기간 및 공사인건비를 줄이는 원가절감이 되는 장점이 있다. Further, when the waterproof paint composition of the present invention is applied to interior and exterior of a building using the waterproof paint composition of the present invention, it is possible to obtain a glossy, smooth, glossy, glossy and glossy Water, water, soil, water, water, water, water, water, water, water, soil, water, water, Building, electric poles, glass wool, foamed styrofoam, fabric, etc., which are used as building materials, laboratories, hospitals, exposed concrete houses, concrete apartments, powerhouses, water wooden houses, brick houses, cement bricks, soundproof walls, tunnels, It is used as a waterproof paint for waterproofing elastic coatings for unrecorded materials on the surface of electric poles, electric poles, etc., and shortens the time of installation finishing coating due to quick touch- There is an advantage of cost reduction by reducing labor period and construction labor cost.
또한, 본 발명에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 건설물의 내, 외장에 사용할 경우, 기존의 마감재로 사용된 유성페인트 또는 수성페인트 및 에폭시페인트 위에 보수를 위한 재도장과 새로운 자재의 표면을 용이하게 도장이 되고, 도장하고 남은 도료를 재사용 하여 소비를 줄이는 원가절감이 되는 장점이 있다.
In addition, when the waterproof paint composition of the present invention is applied to interior and exterior of a building using the waterproof paint composition for environmentally resilient coating, water repellent paint or epoxy paint used as a conventional finishing material, The surface of the new material can be easily painted, and the cost can be reduced by reducing the consumption by reusing the remaining paint.
도 1은 본 발명의 제1실시예에 따른 수성페인트 조성물의 제조공정을 나타낸 흐름도,
도 2는 본 발명의 제2실시예에 따른 수성페인트 조성물의 제조공정을 나타낸 흐름도,
도 3은 본 발명의 제3실시예에 따른 수성페인트 조성물의 제조공정을 나타낸 흐름도,
도 4a은 본 발명에 따른 제조 실시예 1에 의한 수성페인트 조성물을 이용하여 시멘트벽돌위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진,
도 4b는 본 발명에 따른 제조 실시예 1에 의한 수성페인트 조성물을 이용하여 나무판재위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진,
도 5a는 본 발명에 따른 제조 실시예 2에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 CRC시멘트보드위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진,
도 5b는 본 발명에 따른 제조 실시예 2에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 목재판재위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진,
도 6a는 본 발명에 따른 제조 실시예 3에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 CRC시멘트보드위에 도장을 하여 백색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진,
도 6b는 본 발명에 따른 제조 실시예 3에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 목재판재위에 도장을 하여 백색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진,
도 6c는 상기 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 서울 목동에 위치한 아파트단지의 아파트건축물의 내, 외장에 도장한 사진,
도 6d는 상기 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물 을 이용하여 경기도 서종리에 위치한 드라이비트로 마감한 전원주택의 내, 외장에 도장한 사진,
도 6e는 상기 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물 을 이용하여 옥상의 목재데크위에 도장과 수영장의 내, 외장 및 금속스틸 방음벽에 도장하여 방수성능을 나타내는 실시예 1의 사진과 실시예 2의 사진 및 실시예 3의 사진,
도 6f는 상기 제조 실시예 1의 조성물과 실시예 2의 조성물 및 실시예 3의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 생산하여 공장 출하창고에서 보관 하고 있는 사진,
도 7은 콘크리트 벽돌 표면의 제1실시예(투명무광), 제2실시예((투명유광), 제3실시예(단청색)에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 나타낸 도면 대용 사진,
도 8은 목재패널 표면의 제1실시예(투명무광), 제2실시예((투명유광), 제3실시예(단청색의 검정색과 백색)에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 나타낸 도면 대용 사진,
도 9 및 도 10은 글라스울 표면에 제1실시예(투명무광)와 제3실시예(백색)에 의한 방염성능이 평가 된 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 나타낸 도면 대용 사진. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a flow chart showing a process for producing an aqueous paint composition according to a first embodiment of the present invention;
2 is a flow chart showing a process for producing an aqueous paint composition according to a second embodiment of the present invention,
3 is a flow chart showing a process for producing an aqueous paint composition according to a third embodiment of the present invention,
FIG. 4A is a photograph showing a transparent color by painting on a cement brick using the water-based paint composition according to Production Example 1 of the present invention,
FIG. 4B is a photograph showing a transparent color by coating on a wood plate using the water-based paint composition according to Production Example 1 of the present invention,
FIG. 5A is a photograph showing a transparent color by coating on a CRC cement board using an environmentally resilient, waterproof, waterproof paint composition for interior and exterior finish of a construction according to Production Example 2 of the present invention. Tested photos,
FIG. 5b shows a transparent color by coating on a wood plate using an environmentally-resilient, water-repellent, water-repellent, water-based paint composition for interior and exterior finishes of a construction product according to Example 2 of the present invention. One photo,
FIG. 6A is a photograph of a CRC cement board painted on a CRC cement board using an environmentally friendly waterproof paint composition for interior and exterior finish of a building according to the present invention, Tested photos,
FIG. 6B is a graph showing the results of a waterproof paint test for 24 hours by pouring water on a wood plate using a waterproof paint composition of an environmentally friendly elastic paint for interior and exterior finish of a construction according to the third embodiment of the present invention One photo,
FIG. 6c is a photograph showing the photographs of the interior and exterior of an apartment building in an apartment complex located in Mok-dong, Seoul, using an environmentally-resilient,
FIG. 6 (d) is a graph showing the results of photographs of interior and exterior paintings of dry house-finished powerhouses located in Sejong-ri, Gyeonggi-do using an environmentally resilient elastic coating waterproof paint composition for interior and exterior finishes of the above-
FIG. 6E is a photograph of Example 1 showing waterproof performance by painting an interior, exterior, and metal steel soundproof walls of a paint, a swimming pool, and a metal steel soundproofing wall on a wooden deck on the roof using the waterproof paint composition of the present invention A photograph of Example 2, a photograph of Example 3,
FIG. 6F is a photograph showing the composition of Example 1, the composition of Example 2, and the water-based paint composition of the present invention for the interior and exterior finish of the construction material,
7 is a view showing an example of a waterproof paint composition according to the first embodiment (transparent matte) of the concrete brick surface, the second embodiment (transparent luster), and the eco-friendly elastic coating waterproof aqueous paint composition for the interior and exterior finish of the construction by the third embodiment A photograph for a substitute drawing,
Fig. 8 is a view showing the construction of the eco-friendly elastic coating film for the interior and exterior finish of the construction material according to the first embodiment (transparent matte) of the surface of the wood panel, the second embodiment (transparent gloss), and the third embodiment (simple blue and white) A waterproof aqueous paint composition,
9 and 10 are views showing an environmentally friendly waterproof, waterproof aqueous paint composition for interior and exterior finishes of a construction material having evaluated flame retardancy by the first embodiment (transparent matte) and the third embodiment (white) on the surface of a glass wool Substitute photos.
이하 본 발명의 바람직한 실시예를 첨부된 도면을 토대로 상세하게 설명하면 다음과 같다.Hereinafter, preferred embodiments of the present invention will be described in detail with reference to the accompanying drawings.
하기에서 설명될 실시예는 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자가 발명을 용이하게 실시할 수 있을 정도로 상세하게 설명하기 위한 것이며, 이로 인해 본 발명의 기술적인 사상 및 범주가 한정되는 것을 의미하지는 않는다.It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed. It does not mean anything.
또한, 도면에 도시된 구성요소의 크기나 형상 등은 설명의 명료성과 편의상 과장되게 도시될 수 있으며, 본 발명의 구성 및 작용을 고려하여 특별히 정의된 용어들은 사용자, 운용자의 의도 또는 관례에 따라 달라질 수 있고, 이러한 용어들에 대한 정의는 본 명세서 전반에 걸친 내용을 토대로 내려져야 함을 밝혀둔다.
In addition, the sizes and shapes of the components shown in the drawings may be exaggerated for clarity and convenience of explanation, and the terms defined specifically in consideration of the configuration and operation of the present invention may vary depending on the intention or custom of the user, operator It should be noted that the definitions of these terms should be made on the basis of the contents throughout this specification.
본 발명은 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 제공한다. 본 발명은 유성페인트와는 다른 친환경 탄성도막방수 수성페인트 조성물 에 관한 것이므로, 그 자체의 성분이 유기용매를 필요로 하지 않으며, 대기환경 오염과 수질환경오염 및 인체에 해로운 휘발성유해물질을 포함하고 있지 않다.
The present invention provides an eco-friendly elastic coating waterproof aqueous paint composition for interior and exterior finishes of construction products. The present invention relates to an environmentally friendly water-repellent, water-repellent paint composition which is different from oil-based paints. Therefore, the composition of the present invention does not require an organic solvent and contains volatile harmful substances harmful to the environment, not.
본 발명에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성 물은 다목적용도와 다양한기능성을 동시에 수행 할 수 있도록 하기 위하여, 각각의 구성요소들을 기본적으로 무독성, 무취성, 무해성의 친환경 수용성중합체 합성고무 물질과 천연무기질물질 및 수소이온농도 7ph 정도의 중성수를 엄선하여 선정하였다.
The eco-friendly elastic coating waterproof aqueous paint composition for interior and exterior finish of a construction according to the present invention is characterized in that each component is basically composed of non-toxic, odorless and harmless eco-friendly water-soluble Polymer synthetic rubber materials, natural mineral substances and neutral water with a hydrogen ion concentration of about 7ph were carefully selected.
[제1실시예][First Embodiment]
본 발명의 제1실시예에 따른 수성페인트 조성물의 제조방법은, 도 1에 도시된 바와 같이, The method for producing an aqueous paint composition according to the first embodiment of the present invention, as shown in FIG. 1,
프로필렌글리콜(propylene glycol) 12 ~ 16 중량%; 12 to 16% by weight of propylene glycol;
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체(butylacryl-2ethylhexylacrylatemethylmethacryl acid-acrylsilanecopolymer) 18 ~ 25 중량%; Butyl acryl-2-ethylhexyl acrylate methyl acrylate-acryl silane copolymer (butylacryl-2ethylhexylacrylate methylmethacryl acid-acrylsilanecopolymer) 18 to 25% by weight;
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate-2Sodiumcarboxymethylcellulose) 12 ~ 15 중량%; 12 to 15% by weight of sodium polyacrylate-2 sodium carboxymethylcellulose (sodium polyacrylate-2 sodium carboxymethylcellulose);
콜로이달 실리카 13 ~ 17 중량%; Colloidal silica 13 to 17% by weight;
중성수 25 ~ 35 중량%;25 to 35% by weight of neutral water;
를 혼합하여 투명무광의 수성페인트 조성물이 제조된다.
To prepare a transparent matting aqueous paint composition.
프로필렌글리콜(propylene glycol)은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 유화분산성, 내광성, 방부성, 방미성(공기의살균, 곰팡이세균번식방지)을 강화시키기게 된다. Propylene glycol stably maintains the mixing and viscosity of the substance even when the temperature is changed, and strengthens the emulsion, dispersibility, light resistance, antiseptic properties, and smell resistance (sterilization of the air and prevention of growth of fungal bacteria).
프로필렌글리콜(propylene glycol)을 사용하는 이유는 친수성 유화제로서 온도변화에도 조성물의 유화안정성으로 점성을 안정되게 유지되고, 부패와 동결을 방지하고, 살균성에 의한 곰팡이세균번식방지와 내광성에 의한 노화를 방지하는 친수성의 수산이온 비전해질 제품이기 때문이다. Propylene glycol is used as a hydrophilic emulsifier because it keeps the viscosity stable due to the emulsion stability of the composition even when the temperature is changed, prevents decay and freezing, prevents fungus growth by bactericidal effect and prevents aging by light resistance Because it is a non-electrolytic product of hydrophilic acid.
또한 상기 프로필렌 글리콜은 전체 중량에 대해 12 중량%를 미달할 경우 유화안정성과 점성 및 기능성이 저감되고, 16 중량%를 초과할 경우에는 부착성이 저감되어 박리가 발생 할 수 있다.
If the propylene glycol is less than 12 wt% based on the total weight, the emulsion stability, viscosity and functionality are reduced. If the propylene glycol is more than 16 wt%, the adhesion is reduced and peeling may occur.
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체(butylacryl-2ethylhexylacrylatemethylmethacryl acid-acrylsilanecopolymer)는 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지시킬 수 있고, 도막의 방오성, 방식성, 내후성, 내열성, 전기절연성, 신장성과 균일한 경화성 및 부착력을 강화시키게 된다. Butyl acryl-2-ethylhexyl acrylate methyl acrylate-butylacryl-2ethylhexylacrylate methylmethacrylic acid-acrylsilanecopolymer can stably maintain the mixing and viscosity of the substance even when the temperature is changed, and the antifouling property, Weather resistance, heat resistance, electrical insulation, elongation, uniform curability and adhesion.
상기 부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체를 사용하는 이유는 소수성유화제로서 친수성물질과의 가교결합으로 온도변화에도 물질성분의 혼합결합을 안정되게 유지되고, 방오성, 방식성, 내후성, 내열성, 부착성의 기능성과 경질성의 비전해질 탄성고무도막형성이 되기 때문이다. The reason for using the butyl acryl-2-ethylhexyl acrylate methylmethacrylic acid-acrylsilane copolymer is that it is a hydrophobic emulsifier, which is crosslinked with a hydrophilic substance to stably maintain the mixing of the substance components even when the temperature changes, It is possible to form a non-electrolytic elastic rubber coating film having good weather resistance, heat resistance, adhesiveness and hardness.
또한 상기 부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체는 전체 중량에 대해 18중량%를 미달할 경우 도막의 탄성력과 점도조정기능이 저감되고, 25 중량%를 초과할 경우에는 점도가 높아지고 불균일한 혼합결합에 의하여 도장의 경화시간이 길어지면서, 건조 후에 울퉁불퉁한 자국이 발생 할 수 있다.
When the butyl acryl-2-ethylhexyl acrylate methylmethacrylate-acrylsilane copolymer is less than 18% by weight based on the total weight, the elasticity and viscosity adjusting function of the coating film is reduced. When the butyl acryl-2-ethylhexyl acrylate methyl methacrylate- As the viscosity increases and the curing time of the coating becomes longer due to nonuniform mixing bonding, rugged marks may occur after drying.
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate-2Sodiumcarboxymethylcellulose)은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 고온성, 내염성, 내산성, 내알칼리성, 분산안정성, 거품안정성, 내마모성과 균 일한 경화성 및 부착력을 강화시키게 된다. Sodium Polyacrylate-2 Sodium Carboxymethylcellulose (Sodium Polyacrylate-2Sodium Carboxymethylcellulose) maintains the mixed binding and viscosity of the substance stably even under temperature changes, and has high temperature, salt resistance, acid resistance, alkali resistance, dispersion stability, Thereby enhancing abrasion resistance, uniform curability and adhesion.
상기 소듐폴리아크릴레이트-2카르복시메칠셀루로스나트륨을 사용하는 이유는 친수성 유화제로서, 온도변화에도 물질성분의 점성과 혼합결합을 안정되게 유지되고, 도막의 고온성, 내염성, 내산성, 내알칼리성, 분산안정성, 거품안 정성, 내마모성과 균일한 경화성 및 부착력의 기능성과 비전해질 물질로서 경질성 의 도막형성과 지촉건조시간 및 완전건조시간이 빠른 경화성 때문이다. The reason why sodium polyacrylate-2-carboxymethylcellulose sodium is used is that it is a hydrophilic emulsifier that stably maintains the viscosity and mixing of a substance component even with a change in temperature and that the coating film has high temperature resistance, salt resistance, acid resistance, Stability, foam stability, abrasion resistance, uniform curability and adhesive force, and the formation of a hard coating film as a non-electrolytic material, and quick drying time and drying time.
또한 소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨은 전체중량에 대해 12 중량% 를 미달할 경우에는 경화성이 저감될 수 있으며, 15 중량%를 초과할 경우에는 빠른 경화성으로 점성이 증가되고, 도막에 박리와 크랙이 발생 될 수 있다.
If sodium polyacrylate-2 sodium carboxymethylcellulose sodium is less than 12% by weight based on the total weight, the curability can be reduced. If it exceeds 15% by weight, the viscosity can be increased with fast curing property. Peeling and cracking may occur.
콜로이달 실리카는 친수성물질로서 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 방수성, 내열성, 내마모성, 충격성, 내노화성, 대전방지성과 도막의 균일한 경도를 강화시키게 된다. Colloidal silica is a hydrophilic substance, which keeps the mixing bond and viscosity of the material stably maintained even under a temperature change, and strengthens the waterproofness, heat resistance, abrasion resistance, impact resistance, aging resistance, antistatic property and uniform hardness of the coating film.
콜로이달 실리카를 사용하는 이유는 유해물질이 없는 친수성 콜로이달 실리카로서 온도변화에도 물질의 혼합결합 과 점성을 안정되게 유지되고, 분산성, 방수성, 내열성, 내마모성, 충격성, 대전방지성과 도막의 균질한 경도가 지속적으로 유지되기 때문이다.The reason why colloidal silica is used is that it is hydrophilic colloidal silica free from harmful substances, and the mixing bond and viscosity of the substance are stably maintained even under temperature change and the dispersibility, water resistance, heat resistance, abrasion resistance, impact resistance, This is because the hardness is kept constant.
또한 상기 콜로이달 실리카는 전체중량에 대해 13 중량% 를 미달할 경우에는 도막의 경도가 저하될 수 있으며, 17 중량%를 초과할 경우에는 조성물의 점성이 높아지고, 경화시간이 빠르게 진행되어 불규칙한 도막이 형성될 수 있다.
If the colloidal silica is less than 13% by weight based on the total weight of the colloidal silica, the hardness of the coating film may be lowered. If the colloidal silica exceeds 17% by weight, the viscosity of the composition increases and the curing time progresses rapidly, .
중성수를 사용하는 이유는 수소이온농도 7PH 정도의 물로서, 조성물의 점도와 건조시간 및 색상선명도를 조정하고, 용제와 희석재로 사용되기 때문이다. The reason for using neutral water is that water having a hydrogen ion concentration of 7PH is used as a solvent and a diluent because the viscosity, drying time and color sharpness of the composition are adjusted.
또한 중성수는 전체중량에 대해 25 중량% 를 미달할 경우에는 조성물의 혼합이 어렵고, 물질성분의 결합이 저하될 수 있으며, 35 중량%를 초과할 경우에는 불규칙한 도막이 형성 될 수 있다.
When the neutral water is less than 25 wt% based on the total weight, mixing of the composition is difficult and the bonding of the material components may be deteriorated. When the neutral water is more than 35 wt%, an irregular coating film may be formed.
[제2실시예][Second Embodiment]
본 발명의 제2실시예에 따른 수성페인트 조성물의 제조방법은, 도 2에 도시된 바와 같이, The method for producing an aqueous paint composition according to the second embodiment of the present invention, as shown in Fig. 2,
스티렌 부타디엔 고무 15 ~ 23 중량%; 15 to 23% by weight of styrene butadiene rubber;
프로필렌글리콜(propyleneglyc ol) 12 ~ 16 중량%; 12-16 wt% propylene glycol (ol);
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체 (butylacryl-2ethylhexylacrylatemethylmethacrylic acid-acrylsilanecopolymer) 12 ~ 25중량%; Butyl acryl-2-ethylhexyl acrylate methyl acrylate-butylacryl-2ethylhexylacrylate methylmethacrylic acid-acrylsilanecopolymer 12-25 wt%;
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate-2Sodiumcarboxymethylcellulose) 12 ~ 15 중량%; 12 to 15% by weight of sodium polyacrylate-2 sodium carboxymethylcellulose (sodium polyacrylate-2 sodium carboxymethylcellulose);
콜로이달 실리카 13 ~ 17 중량%와; 13 to 17% by weight colloidal silica;
중성수 25 ~ 35 중량%;25 to 35% by weight of neutral water;
를 혼합하여 투명유광의 수성페인트 조성물이 제조된다.
To prepare a clear, opaque water-based paint composition.
스티렌 부타디엔 고무(sbr : styrene butadiene rubber)는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성 물은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 방수성, 방미성, 방식성, 방부성, 전기절연성, 내화학성, 내유성, 내후성, 신장성과 부착력 및 탄성력을 강화시키기 위한 것이다. Styrene butadiene rubber (sbr: styrene butadiene rubber) is a waterproof, environmentally friendly waterproof paint composition for interior and exterior finishes of construction materials. The composition and viscosity of materials are kept stable even when the temperature changes, and the waterproofness, Resistance, electrical insulation, chemical resistance, oil resistance, weather resistance, stretchability, adhesion and elasticity.
스티렌 부타디엔 고무(Styrene Butadiene Rubber 현탁중합)를 사용하는 이유는 친수성유화제로서 친수성중합법에 의한 유화물질과 무기질물질과의 현탁중합에 의하여 온도변화에도 유화안정성으로 점성을 안정되게 유지되고, 도막의 방수 성, 방미성, 방식성, 방부성, 전기절연성, 내화학성, 내유성, 내후성, 신장성과 부착력 및 탄성력의 기능성이 강화되고, 비전해질의 보호콜로이드 합성고무액체로서, 도장 후에는 신장성과 경질성의 탄성고무도막형성이 되기 때문이다. Styrene Butadiene Rubber (Suspension Polymerization) is used because it is a hydrophilic emulsifier and its viscosity is stabilized by emulsion stability due to suspension polymerization by suspension polymerization between emulsified material and inorganic material by hydrophilic polymerization method. The coating composition of the present invention is a non-electrolytic protective colloidal synthetic rubber liquid having enhanced functionalities such as weatherability, antifouling property, anticorrosive property, antiseptic property, electrical insulation property, chemical resistance, oil resistance, weather resistance, stretchability and adhesion force and elasticity, .
스티렌 부타디엔 고무는 전체중량에 대해 15 중량%를 미달할 경우에는 조성물의 점성이 묽어지며, 부착성이 저감될 수 있으며, 23 중량%를 초과할 경우에는 조성물의 점성이 높아져 경화성이 빨라지고, 도장이 건조된 후에 부풂과 크랙이 발생될 수 있다. When the styrene-butadiene rubber is less than 15% by weight based on the total weight of the composition, the viscosity of the composition becomes thin and the adhesion can be reduced. When the content exceeds 23% by weight, the viscosity of the composition increases, Cracks may form after drying.
프로필렌 글리콜은 전체 중량에 대해 12 중량%를 미달할 경우 유화안정성과 점성 및 기능성이 저감되고, 16 중량%를 초과할 경우에는 부착성이 저감되어 박리가 발생 할 수 있다. If the amount of propylene glycol is less than 12 wt% based on the total weight, the emulsion stability and viscosity and functionality are reduced. If the amount is more than 16 wt%, the adhesion is reduced and peeling may occur.
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체는 전체 중량에 대해 12중량%를 미달할 경우 도막의 탄성력과 점도조정기능이 저감되고, 25 중량%를 초과할 경우에는 점도가 높아지고 불균일한 혼합결합에 의하여 도장의 경화시간이 길어지면서, 건조 후에 울퉁불퉁한 자국이 발생 할 수 있다.Butyl acryl-2-ethylhexyl acrylate methyl methacrylic acid-acrylic silane copolymer is less than 12% by weight based on the total weight, the elasticity and viscosity adjusting function of the coating film is reduced, and when it exceeds 25% by weight, As the hardening time of the coating becomes longer due to the high and non-uniform mixing bonding, rugged marks may occur after drying.
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨은 전체중량에 대해 12 중량% 를 미달할 경우에는 경화성이 저감될 수 있으며, 15 중량%를 초과할 경우에는 빠른 경화성으로 점성이 증가되고, 도막에 박리와 크랙이 발생 될 수 있다. When sodium polyacrylate-2 sodium carboxymethylcellulose sodium is less than 12% by weight based on the total weight, the curability may be reduced. When the content is more than 15% by weight, the viscosity increases with fast curing property, And cracks may occur.
콜로이달 실리카는 전체중량에 대해 13 중량% 를 미달할 경우에는 도막의 경도가 저하될 수 있으며, 17 중량%를 초과할 경우에는 조성물의 점성이 높아지고, 경화시간이 빠르게 진행되어 불규칙한 도막이 형성될 수 있다. When the colloidal silica is less than 13% by weight based on the total weight of the colloidal silica, the hardness of the coating film may be lowered. If the colloidal silica is more than 17% by weight, the viscosity of the composition increases and the curing time progresses rapidly to form an irregular coating film have.
한편 본 발명은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 점도와 건조시간 및 색상선명도를 조정시키기 위한 중성수 25 ~ 35 중량%가 포함된다. Meanwhile, the present invention includes 25 to 35% by weight of neutral water for adjusting the viscosity, drying time, and color sharpness, while maintaining stable mixing and viscosity of the material even under temperature changes.
중성수를 사용하는 이유는 수소이온농도 7PH 정도의 물로서, 조성물의 점도와 건조시간 및 색상선명도를 조정하고, 용제와 희석재로 사용되기 때문이다. The reason for using neutral water is that water having a hydrogen ion concentration of 7PH is used as a solvent and a diluent because the viscosity, drying time and color sharpness of the composition are adjusted.
또한 중성수는 전체중량에 대해 25 중량% 를 미달할 경우에는 조성물의 혼합이 어렵고, 물질성분의 결합이 저하될 수 있으며, 35 중량%를 초과할 경우에는 불규칙한 도막이 형성 될 수 있다.
When the neutral water is less than 25 wt% based on the total weight, mixing of the composition is difficult and the bonding of the material components may be deteriorated. When the neutral water is more than 35 wt%, an irregular coating film may be formed.
[제3실시예][Third Embodiment]
본 발명의 제3실시예에 따른 수성페인트 조성물의 제조방법은, 도 3에 도시된 바와같이, The method for producing an aqueous paint composition according to the third embodiment of the present invention, as shown in Fig. 3,
스티렌 부타디엔 고무(sbr : styrene butadiene rubber) 5 ~ 13 중량%; 5 to 13% by weight of styrene butadiene rubber (sbr);
프로필렌글리콜(propyleneglycol) 2 ~ 6 중량%; 2 to 6% by weight of propyleneglycol;
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체(butylacryl-2ethylhexylacrylatemethylmethacryl acid-acrylsilan ecopolymer) 8 ~ 15 중량%; 8 to 15% by weight of butylacryl-2-ethylhexyl acrylate methyl methacrylic acid-acrylsilane copolymer (butylacryl-2ethylhexylacrylate methylmethacryl acid-acrylsilane ecopolymer);
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate- 2Sodiumcarboxymethylcellulose) 2 ~ 5 중량%; 2 to 5% by weight of sodium polyacrylate-2 sodium carboxymethylcellulose (sodium polyacrylate-2 sodium carboxymethylcellulose);
이산화티타늄(Tio2) 0.1 ~ 0.6 중량%; 0.1 to 0.6% by weight of titanium dioxide (Tio2);
백토분말 12 ~ 15 중량%; 12 to 15% by weight of clay powder;
조개분말 2 ~ 4 중량%; 2 to 4% by weight of shell powder;
탄산칼슘분말 10 ~ 15 중량%; 10 to 15% by weight of calcium carbonate powder;
무기질분말 5 ~8 중량%; 5 to 8% by weight of an inorganic powder;
무기질안료 15 ~ 20 중량%; 15 to 20% by weight of an inorganic pigment;
중성수 15 ~ 25 중량%; 15 to 25% by weight of neutral water;
콜로이달 실리카 3 ~ 7 중량%Colloidal silica 3 to 7 wt%
을 혼합하여 단청색의 수성페인트 조성물이 제조된다.
To prepare a single blue aqueous paint composition.
스티렌 부타디엔 고무는 전체중량에 대해 5 중량%를 미달할 경우에는 조성물의 점성이 묽어지며, 부착성이 저감될 수 있으며, 13 중량%를 초과할 경우에는 조성물의 점성이 높아져 경화성이 빨라지고, 도장이 건조된 후에 부풂과 크랙이 발생될 수 있다. When the styrene-butadiene rubber is less than 5% by weight based on the total weight of the composition, the viscosity of the composition becomes thin and the adhesion can be reduced. When the content exceeds 13% by weight, Cracks may form after drying.
프로필렌 글리콜은 전체 중량에 대해 2 중량%를 미달할 경우 유화안정성과 점성 및 기능성이 저감되고, 6 중량%를 초과할 경우에는 부착성이 저감되어 박리가 발생할 수 있다. When the propylene glycol is less than 2% by weight based on the total weight, the emulsion stability, viscosity and functionality are reduced, and when it is more than 6% by weight, the adhesion is reduced and peeling may occur.
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체는 전체 중량에 대해 8중량%를 미달할 경우 도막의 탄성력과 점도조정기능이 저감되고, 15 중량%를 초과할 경우에는 점도가 높아지고 불균일한 혼합결합에 의하여 도장의 경화시간이 길어지면서, 건조 후에 울퉁불퉁한 자국이 발생 할 수 있다.
Butyl acryl-2-ethylhexyl acrylate methyl methacrylic acid-acrylic silane copolymer is less than 8 wt% based on the total weight, the elasticity and viscosity adjusting function of the coating film is reduced, and when it exceeds 15 wt% As the hardening time of the coating becomes longer due to the high and non-uniform mixing bonding, rugged marks may occur after drying.
이산화티타늄은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 방식성, 내구성, 내염성, 내산성, 내알칼리성, 내마모성, 난연성과 발색지속력을 강화시키게 된다. Titanium dioxide maintains stable mixing and bonding of materials even when the temperature is changed, and enhances the corrosion resistance, durability, salt resistance, acid resistance, alkali resistance, abrasion resistance, flame retardancy and color sustainability of the coating film.
이산화티타늄(Tio2)을 사용하는 이유는 유해물질이 없는 천연무기질분말로서 온도변화에도 물질성분의 점성과 혼합결합을 안정되게 유지 되고, 도막의 방식성, 내구성, 내염성, 내산성, 내알칼리성, 내마모성, 난연성의 기능 성과 발색지속력이 유지되기 때문이다. 또한, 상기 이산화티타늄(Tio2)은 전체중량 에 대해 0.1 중량%를 미달할 경우에는 도막의 발색지속력이 저하될 수 있으며, 0.6 중량%를 초과할 경우에는 거품이 발생될 수 있다.
The reason why titanium dioxide (Tio2) is used is that it is a natural mineral powder without harmful substances, and the viscosity and mixing bond of the material ingredient is stably maintained even with temperature change, and the corrosion resistance, durability, salt resistance, acid resistance, alkali resistance, This is because the function of flame retardancy and sustainability of color development are maintained. If the amount of titanium dioxide (TiO 2) is less than 0.1% by weight based on the total weight, the color development sustainability of the coating film may be lowered, and if it exceeds 0.6% by weight, bubbles may be generated.
백토분말은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 방음성, 내구성, 내마모성, 내열성, 내산성, 내알칼리성, 방식성, 방미성, 내노화성, 방부성과 유해물질의 흡착, 라돈방출방지, 원적외선방출, 열에너지절감 및 은폐력과 경도를 강화시키기 위한 것이다. The white clay powder is stable in the mixing and viscosity of the material even under the temperature change and can be used for a long period of time. It can be used in a wide variety of applications such as soundproofing, durability, abrasion resistance, heat resistance, acid resistance, alkali resistance, anticorrosion, Emission prevention, far-infrared emission, thermal energy reduction, and to enhance hiding power and hardness.
백토분말를 사용하는 이유는 고령토라고도 불리는 300 메시 내지 400메시 크기의 유해물질이 없는 천연무기질분말로서, 도막의 방음성, 내구성, 내마모성, 내열성, 내산성, 내알칼리성, 방식성, 방미성, 내노화성, 방부성과 유해물질의 흡착, 라돈방출방지, 원적외선방출, 열에너지절감의 기능성과 건조시간 이 길수록 은폐력과 경도가 증강되고 안정되기 때문이다.The reason for using the clay powder is that it is a natural mineral powder having no harmful substance of 300 mesh to 400 mesh size, also called kaolinite. It is a natural mineral powder of a coating film and has excellent soundproofness, durability, abrasion resistance, heat resistance, acid resistance, alkali resistance, anticorrosive property, And the function and drying time of radiant emission prevention, radiant emission reduction, heat energy reduction, and hiding power and hardness are enhanced and stabilized as the drying time is longer.
또한, 상기 백토분말은 전체중량에 대해 12 중량% 를 미달할 경우에는 도막의 은폐력과 경도가 저하될 수 있으며, 15 중량%를 초과할 경우에는 조성물의 혼합이 어렵고, 중성수를 많이 투입하게 되어 도막이 불규칙하게 형성 될 수 있다.
If the amount of the clay powder is less than 12 wt% based on the total weight of the clay, the coating strength and hardness of the clay coat may be lowered. If the clay powder is more than 15 wt%, mixing of the composition is difficult and a large amount of neutral water is added The coating film may be irregularly formed.
조개분말은 온도변화에도 물질의 혼합 결합과 점성을 안정되게 유지되고, 도막의 방식성, 내노화성, 방부성, 난연성과 유해물질의 흡착, 라돈방출방지, 색상선명도를 강화시키기 위한 것이다. The shell powder maintains the mixing bond and viscosity of the substance stably even when the temperature changes, and is intended to enhance the anticorrosiveness, aging resistance, antifogging properties, flame retardancy and adsorption of harmful substances, prevention of radon emission, and color sharpness.
조개분말은 조개껍질을 분쇄하여 얻어지는 호분이라고도 불리는 유해 물질이 없는 천연무기질분말로서, 온도변화에도 물질의 점성과 혼합결합을 안정 되게 유지되고, 방식성, 난연성과 유해물질의 흡착, 라돈방출방지의 기능성과, 색상 선명도를 지속적으로 유지되기 때문이다. Shell powder is a natural mineral powder without harmful substance called crust which is obtained by crushing clam shell. It maintains stable viscosity and mixing bond of material even with temperature change. It is also used for anti-corrosiveness, adsorption of harmful substances, Functionality, and color sharpness.
또한, 상기 조개분말은 전체중량에 대해 2 중량%를 미달할 경우에는 기능성과 색상선명도의 지속성이 저감될 수 있으며, 4 중량%를 초과할 경우에는 원가상승이 발생될 수 있다.
If the shellfish powder is less than 2% by weight based on the total weight, the sustainability of functionality and color clarity can be reduced. If the shellfish powder is more than 4% by weight, a cost increase may occur.
탄산칼슘분말은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 내염성, 은폐성, 내열성, 경화성, 난연성, 내노화성과 경도 및 빛 반사확산력을 강화시키기 위한 것이다. The calcium carbonate powder is intended to stably maintain the mixing bond and viscosity of the material even when the temperature changes, and to enhance the salt resistance, hiding power, heat resistance, hardenability, flame retardancy, resistance to aging, hardness and diffuse reflection.
탄산칼슘분말를 사용하는 이유는 유해물질이 없는 천연 무기질분말로서, 온도변화에도 물질의 점성과 혼합결합을 안정되게 유지되고, 도 막의 내염성, 은폐성, 내열성, 경화성, 난연성, 내 노화성의 기능성과 햇빛 또는 전 등 빛에 의한 빛 반사확산력으로 물체와 주변이 밝아지기 때문이다. The reason why calcium carbonate powder is used is that it is a natural mineral powder free from harmful substances and the viscosity and mixing bond of the material is stably maintained even under a change of temperature and the function of salt resistance, Or because the object and its surroundings become brighter due to the diffuse reflection of the light by the light.
또한, 상기 탄산칼슘분말은 전체중량에 대해 10 중량% 를 미달할 경우에 는 도막의 빛 반사 확산력이 저감될 수 있으며, 15 중량%를 초과할 경우에는 점성 이 묽어지며, 침전물이 발생될 수 있다.
When the amount of the calcium carbonate powder is less than 10% by weight based on the total weight of the calcium carbonate powder, the light reflection diffusing power of the coating film may be reduced. When the content exceeds 15% by weight, the viscosity of the calcium carbonate powder may become thin, .
무기질분말은 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 내열성, 경화성, 난연 성과 은폐력 및 열에너지절감을 강화시키기 위한 것이다.The inorganic powder is intended to maintain the mixing bond and viscosity of the material stably and to enhance the heat resistance, hardenability, flame retardancy, hiding power and thermal energy of the coating film even when the temperature changes.
무기질분말은 석회, 규사 등의 유해물질이 없는 무기질 분말로서, 온도변화에도 물질의 혼합결합과 점성을 안정되게 유지되고, 도막의 은폐성, 내열성, 경화성, 난연성의 기능성과 경도를 높여주기 때문이다.The inorganic powder is an inorganic powder free from harmful substances such as lime and silica sand because it keeps the mixing bond and viscosity of the substance stably and changes the temperature to increase the hiding power, heat resistance, hardenability, flame retardancy and hardness of the coating .
또한 상기 무기질분말은 전체중량에 대해 5 중량% 를 미달할 경우에는 도막의 경도가 저감될 수 있으며, 8 중량%를 초과할 경우에는 도막에 박리와 크랙이 발생될 수 있다.
When the inorganic powder is less than 5 wt% based on the total weight of the inorganic powder, the hardness of the coated film may be reduced. When the inorganic powder is more than 8 wt%, peeling and cracks may occur in the coated film.
무기질 안료는 온도변화에도 물질의 혼합결합 과 점성을 안정되게 유지되고, 은폐성, 방미성, 방습성, 방식성, 분산성, 난연성, 내구성과 반영구적인 색상선명도를 강화시키기 위한 것이다. Mineral pigments are stably maintained in the mixing bond and viscosities of materials even at a temperature change, and are intended to enhance hiding power, anti-fogging property, moisture-proof property, anticorrosive property, dispersibility, flame retardancy, durability and semi-permanent color clarity.
무기질 안료를 사용하는 이유는 단청재료로 사용되는 유해물질이 없는 무기물착색제 물질로서, 온도변화에도 물질의 점성과 혼합결합을 안정되게 유지되고, 은폐성, 방미성, 방습성, 방식성, 분산성, 난연성, 내구성과 반영구적인 색상선명도가 높기 때문이다. The reason for using the inorganic pigment is that it is an inorganic coloring agent material which is used as a mono-coloring material and has no harmful substance, and the viscosity and mixing bond of the substance are stably maintained even under a change of temperature, and the hiding property, Flame retardancy, durability and semi-permanent color clarity.
무기질안료는 전체중량에 대해 15 중량% 를 미달할 경우에는 도막의 은폐력과 색상선명도가 저감될 수 있으며, 20 중량%를 초과할 경우에는 도막의 불규칙한 색상선명도와 원가상승이 발생 될 수 있다. If the content of the inorganic pigment is less than 15 wt% based on the total weight, the hiding power and color sharpness of the coating film may be reduced. If the inorganic pigment is more than 20 wt%, irregular color sharpness and cost increase of the coating film may occur.
중성수는 전체중량에 대해 15 중량% 를 미달할 경우에는 조성물의 혼합이 어렵고, 물질성분의 결합이 저하될 수 있으며, 25 중량%를 초과할 경우에는 불규칙한 도막이 형성 될 수 있다. When the neutralized water is less than 15% by weight based on the total weight, mixing of the composition is difficult and the bonding of the material components may be deteriorated. If the neutralized water is more than 25% by weight, an irregular coating film may be formed.
콜로이달 실리카는 전체중량에 대해 3 중량% 를 미달할 경우에는 도막의 경도가 저하될 수 있으며, 7 중량%를 초과할 경우에는 조성물의 점성이 높아지고, 경화시간이 빠르게 진행되어 불규칙한 도막이 형성될 수 있다.
If the colloidal silica is less than 3% by weight based on the total weight of the colloidal silica, the hardness of the coating film may be lowered. If the colloidal silica exceeds 7% by weight, the viscosity of the composition increases and the curing time progresses rapidly, have.
이하 본 발명에 따른 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 공정단계에 의하여 제조된 구체적인 실시예 및 그에 관한 실험 결과를 설명하기로 한다
Hereinafter, specific examples and experimental results of the eco-friendly elastic coating waterproof aqueous paint composition for interior and exterior finish of a construction according to the present invention will be described
[제조 실시예 1][Manufacturing Example 1]
1) 스티렌 부타디엔 고무 14.2 kg에 대하여 프로필렌글리콜 5.7 kg과 부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체 22.8 kg을 탱크에 순서대로 투입하여 상온에서 천천히 교반한다.1) To 14.2 kg of styrene-butadiene rubber, 5.7 kg of propylene glycol and 22.8 kg of butyl acryl-2-ethylhexyl acrylate methylmethacrylate-acrylsilane copolymer are added to the tank in order and slowly stirred at room temperature.
2) 소듐폴리아크릴레이트-2소듐카르복시메칠셀루로스나트륨 5.7 kg을 투입하여 상온에서 천천히 교반한다. 2) 5.7 kg of sodium polyacrylate-2 sodium carboxymethylcellulose sodium and stir gently at room temperature.
3) 콜로이달 실리카 8.5 kg을 투입하여 상온에서 천천히 교반한다.3) Add 8.5 kg of colloidal silica and stir gently at room temperature.
4) 중성수 42.8 kg을 투입하여 상온에서 천천히 교반하여 균일한 탄성도막방수 수성페인트 조성물 99.7 kg이 제조되었다. 4) 42.8 kg of neutral water was added and stirred slowly at room temperature to produce 99.7 kg of a uniform water-repellent paint composition.
상기 탄성도막방수 수성페인트 조성물은 점성이 있는 맑고 투명한 백색의 액체이었고, 그 백색액체를 콘크리트재, 금속스틸재, 목재, 플라스틱재, 석재, 등의 표면에 도장한 후에는 빠르게 건조되고, 건조된 후에는 반질하고 경질한 탄성력의 고무탄성도막이 형성되고 무광택의 투명색을 띄고 있었다.
The water-repellent, water-repellent, water-repellent paint composition is a viscous, clear and transparent white liquid which is rapidly dried after being coated on the surface of concrete, steel, wood, plastic, stone, Thereafter, a rubber elastic coating film of a semi-rigid and rigid elastic force was formed and had a matte transparent color.
도 4a은 본 발명에 따른 제조 실시예 1에 의한 수성페인트 조성물을 이용하여 시멘트벽돌위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진이다.
FIG. 4A is a photograph showing a transparent color by coating on cement bricks using an aqueous paint composition according to Production Example 1 according to the present invention, and water resistance test for 24 hours by pouring water. FIG.
도 4b는 본 발명에 따른 제조 실시예 1에 의한 수성페인트 조성물을 이용하여 나무판재위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진이다.
FIG. 4B is a photograph showing a transparent color by coating on a wood plate using the aqueous paint composition according to Production Example 1 according to the present invention, and water resistance test for 24 hours by pouring water. FIG.
[제조 실시예 2][Manufacturing Example 2]
1) 스티렌 부타디엔 고무 18.3 kg에 대하여 부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체 21.1 kg을 탱크에 순서대로 투입하여 상온에서 천천히 교반한다. 1) To 18.3 kg of styrene butadiene rubber, 21.1 kg of butyl acryl-2-ethylhexyl acrylate methylmethacrylate-acrylsilane copolymer are put into the tank in order and slowly stirred at room temperature.
2) 소듐폴리아크릴레이트-2소듐카르복시메칠셀루로스나트륨 7 kg을 투입하여 상온에서 천천히 교반한다. 2) Add 7 kg of sodium polyacrylate-2 sodium carboxymethylcellulose and stir gently at room temperature.
3) 콜로이달 실리카 9.8 kg을 투입하여 상온에서 천천히 교반한다. 3) Add 9.8 kg of colloidal silica and stir gently at room temperature.
4) 중성수 35.2 kg을 교반기에 투입하여 상온에서 천천히 교반하여 균일한 탄성도막방수 수성페인트 조성물 99.8 kg을 얻었다,
4) Neutral water (35.2 kg) was added to a stirrer and stirred slowly at room temperature to obtain 99.8 kg of a uniform water-repellent, water-repellent paint composition.
상기 탄성도막방수 수성페인트 조성물은 점성이 있는 맑고 투명한 백색의 액체이었고, 그 백색액체를 콘크리트재, 금속스틸재, 목재, 플라스틱재, 석재, 등의 표면에 도장한 후에는 빠르게 건조되고, 건조된 후에는 반질하고 경질한 탄성력의 고무탄성도막이 형성되고 광택이 나는 유광의 투명색을 띄고 있었다.
The water-repellent, water-repellent, water-repellent paint composition is a viscous, clear and transparent white liquid which is rapidly dried after being coated on the surface of concrete, steel, wood, plastic, stone, Thereafter, a rubber elastic coating film of a semi-rigid and elastic elastic force was formed, and a translucent luster of glossy luster was observed.
도 5a는 본 발명에 따른 제조 실시예 2에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 CRC시멘트보드위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진이다.
FIG. 5A is a photograph showing a transparent color by coating on a CRC cement board using an environmentally resilient, waterproof, waterproof paint composition for interior and exterior finish of a construction according to Production Example 2 of the present invention. This is a test photo.
도 5b는 본 발명에 따른 제조 실시예 2에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 목재판재위에 도장을 하여 투명색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진이다.
FIG. 5b shows a transparent color by coating on a wood plate using an environmentally-resilient, water-repellent, water-repellent, water-based paint composition for interior and exterior finishes of a construction product according to Example 2 of the present invention. It's a picture.
[제조 실시예 3][Manufacturing Example 3]
1) 상기 제조 실시예 1에서 제조된 혼합물 10kg에 대하여 제조 실시예 2에서 제조된 혼합물 13kg을 투입하여 천천히 교반한다1) To 10 kg of the mixture prepared in Preparation Example 1, 13 kg of the mixture prepared in Preparation Example 2 was added and stirred slowly
2) 이산화티타늄 0.5 kg를 투입하여 천천히 교반한다. 2) Add 0.5 kg of titanium dioxide and stir slowly.
3) 백토분말 15 kg을 투입하여 천천히 교반한다. 3) Add 15 kg of white clay powder and stir slowly.
4) 조개분말 3.5 kg을 투입하여 천천히 교반한다. 4) Add 3.5 kg of shell powder and stir slowly.
5) 탄산칼슘분말 15 kg을 투입하여 천천히 교반한다. 5) Add 15 kg of calcium carbonate powder and stir slowly.
6) 무기질분말 8 kg을 투입하여 천천히 교반한다. 6) Add 8 kg of mineral powder and stir slowly.
7) 다양한색상의 무기질안료 중에서 선정한 백색의 무기질안료 20 kg을 투입하여 천천히 교반한다.7) Add 20 kg of selected white inorganic pigments from various colors of inorganic pigments and stir slowly.
8) 중성수 15 kg을 투입하여 상온에서 천천히 일정한 시간동안 교반한 다음, 다시 빠르게 교반하여 균일한 탄성도막방수 수성페인트 조성물 100kg을 얻었다. 8) 15 kg of neutral water was added, and the mixture was slowly stirred at room temperature for a certain period of time. Then, the mixture was rapidly stirred to obtain 100 kg of a water-based paint composition having a uniform elastic coating film.
상기 탄성도막방수 수성페인트 조성물은 점성이 있는 걸죽한 백색액체이었고, 그 백색액체를 콘크리트재, 금속스틸재, 목재, 플라스틱재, 석재, 등의 표면에 도장한 후에는 빠르게 건조되고, 건조된 후에는 더욱 더 반질하고 경도와 탄성력이 높은 고무탄성도막이 형성되고 광택이 나는 백색을 띄고 있었다. The water-repellent, water-repellent, water-repellent paint composition of the present invention was a viscous, waxy white liquid, which quickly dried after being coated on the surface of concrete, steel, wood, plastic, stone, etc., And the rubber elastic coating film having high hardness and elasticity was formed and had a glossy white color.
도 6a는 본 발명에 따른 제조 실시예 3에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 CRC시멘트보드위에 도장을 하여 백색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진이다. FIG. 6A is a photograph of a CRC cement board painted on a CRC cement board using an environmentally friendly waterproof paint composition for interior and exterior finish of a building according to the present invention, This is a test photo.
도 6b는 본 발명에 따른 제조 실시예 3에 의한 건설물의 내, 외장 마감재 용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 목재판재위에 도장을 하여 백색을 띄고 있고, 물을 부어 24시간 방수성능을 시험한 사진이다.
FIG. 6B is a graph showing the results of a waterproof paint test for 24 hours by pouring water on a wood plate using a waterproof paint composition of an environmentally friendly elastic paint for interior and exterior finish of a construction according to the third embodiment of the present invention It's a picture.
<건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 관한 건설용 도막방수재,"멤브레인 방수층 성능평가시험방법(KS F 2622-08)에 의한 실험과 "건설용 도막방수재 “성능평가시험방법(KS F 3211-08)에 의한 실험. 제조 실시예 3 >
<Performance evaluation test method of membrane waterproofing layer performance test method (KS F 2622-08) and performance evaluation test method of "Construction coating waterproofing material" for waterproof paint composition for environmentally friendly waterproofing paint for interior and exterior of construction materials (KS F 3211-08). Production Example 3>
상기 제조 실시예3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 건설용 탄성도막방수재 성능을 확인하기 위하여, 서울특별시 노원구 공릉길 232 서울과학기술대학교 건설기술연구소에 건설용 탄성도막방수재 성능시험을 의뢰(2014.3.10.) 하였다. In order to confirm the performance of the water-repellent material for construction of the waterproof paint composition for environmentally friendly waterproofing paint for indoor and outdoor use in the construction example 3, We requested the performance test of coating waterproofing material (October 3, 2014).
서울과학기술대학교 건설기술연구소에서는 KS규격 KS F 2622-08 "멤브레인 방수층 성능평가시험방법“에 의한 방수성시험(누수 유무), 패임저항성시험(누수 및 구멍뚫림, 유무), 충격저항성시험(누수 및 구멍?림 유무 관찰), 코너부저항성시험(코너부굳어짐과 파단의 유무 관찰), 풍압저항성시험(방수층 이상유무), 부풂저항성시험(절연부위확대 등의 변화유무)으로 선정하여 건설용도막방수재 성능시험을 진행하였다. The Institute of Construction Technology of the Seoul National University of Science and Technology has conducted a water resistance test (presence or absence of leakage), a damp resistance test (leakage and puncture), an impact resistance test (leakage and puncture) by KS standard KS F 2622-08 "Evaluation test method of membrane waterproofing layer" (Presence or absence of holes), corner resistance test (observation of presence or absence of corner portion hardening and fracture), wind pressure resistance test (existence of waterproof layer abnormality), brittle resistance test Performance tests were conducted.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 건설용도막 방수재 KS규격 KS F 2622-08 멤브레인 방수층 성능평가 시험방법에 의한 결과치(발급번호: 제1405-25. 2014.05.29.)는 “이상없음”으로 확인 되었다.Construction of waterproof paint composition for environmentally resilient coating waterproofing for interior and exterior finishing materials of building of the present invention Membrane waterproofing material KS standard KS F 2622-08 Membrane waterproofing layer Performance evaluation test result (Issued No. 1405-25, 2014.05.29 .) Was identified as "no abnormality".
또한, 상기 제조 실시예3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 건설용 탄성도막방수재 성능을 확인하기 위하여, 서울특별시 노원구 공릉길 232 서울과학기술대학교 건설기술연구소에 건설용 탄성도막방수재 성능시험을 의뢰(2014.3.10.) 하였다. Further, in order to confirm the performance of the water-repellent coating material for construction of the water-based paint composition for environmentally friendly water-repellent waterproof paint for interior and exterior finish of the construction according to Manufacturing Example 3, (Feb. 3, 2014) to request the performance test of elastic coating film.
서울과학기술대학교 건설기술연구소에서는 KS규격 KS F 3211-08 "건설용 도막방수재“에 의한 열화처리후의 인장 성능시험(인장강도비(가열처리(%), 알칼리처리(%), 산처리) 및 파단시의 신장율(가열처리(%), 알칼리처리(%), 산처리(%)), 신장시의 열화 성상 성능시험(가열처리).The Institute of Construction Technology of Seoul National University of Science and Technology has conducted a tensile strength test (tensile strength ratio (heat treatment (%), alkali treatment (%), acid treatment) after deterioration treatment with KS F 3211-08 "Construction coating waterproofing material" (%), Alkali treatment (%), acid treatment (%)) at the time of breakage, and deterioration performance test (heat treatment) at the time of elongation.
부착성능(N/㎣)(무처리 및 냉온반복처리 후(부착강도(N/㎣), 도막상태)), 내피로 성능시험(구멍?림, ?김, 파단이 없을 것), 인장성능(인장강도(N/㎣), 파단시의 신장율(%), 항장적(N/㎣)), 인열성능시험(인열강도(N/㎣)), 온도 의존성(인장강도비(%), 파단시의 물림부사이의 신장율(%)), 가열신축성상 성능시험(신축률(%))으로 선정하여 건설용도막방수재 성능시험을 진행하였다. Adhesion performance (N / ㎣) (No treatment and after cold / repeated treatment (Adhesion strength (N / ㎣), Coating film state)), Endothelial performance test (No puncture, Tensile strength (N / ㎣), elongation at break (%), tensile strength (N / ㎣)), tear performance test (tear strength (N / (%)), And the performance test for thermal expansion and contraction (expansion / contraction ratio (%)).
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 건설용도막 방수재 KS규격 KS F 3211-08 성능평가 시험방법에 의한 결과치(발급번호: 제1405-25. 2014.05.29.)는 “이상없음” 으로 확인 되었다.Construction of waterproof paint composition for waterproofing of environmentally resilient waterproofing coating for interior and exterior finishing materials of building of the present invention Film protection material KS standard KS F 3211-08 Performance evaluation test result (Issued No. 1405-25, 2014.05.29.) Was identified as "no abnormality".
도 6c는 상기 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 서울 목동에 위치한 아파트단지의 아파트건축물의 내, 외장에 도장한 사진이다.FIG. 6C is a photograph showing the interior and exterior of an apartment building in an apartment complex located in Mok-dong, Seoul, using an environmentally resilient, water-repellent, waterproof paint composition for interior and exterior finishing of the above construction.
상기 아파트건축물의 내, 외장에는 실시예 1의 조성물과 실시예 2의 조성물 및 실시예 3의 조성물을 이용하여 마감도장 하였다. The interior and exterior of the apartment building were finishing painted using the composition of Example 1, the composition of Example 2, and the composition of Example 3.
도 6d는 상기 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물 을 이용하여 경기도 서종리에 위치한 드라이비트로 마감한 전원주택의 내, 외장에 도장한 사진이다. FIG. 6D is a photograph of the interior and exterior of a power house with a dry bit located in Seojong-ri, Gyeonggi-do using an environmentally resilient elastic coating waterproof paint composition for interior and exterior finish of the construction.
상기 전원주택의 내, 외장에는 실시예 1의 조성물과 실시예 2 조성물 및 실시예 3의 조성물을 이용하여 마감도장 하였다. The interior and exterior of the power house were finishing painted using the composition of Example 1, the composition of Example 2, and the composition of Example 3.
도 6e는 상기 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물 을 이용하여 옥상의 목재데크위에 도장과 수영장의 내, 외장 및 금속스틸 방음벽에 도장하여 방수성능을 나타내는 실시예 1의 사진과 실시예 2의 사진 및 실시예 3의 사진이다.FIG. 6E is a photograph of Example 1 showing waterproof performance by painting an interior, exterior, and metal steel soundproof walls of a paint, a swimming pool, and a metal steel soundproofing wall on a wooden deck on the roof using the waterproof paint composition of the present invention A photograph of Example 2 and a photograph of Example 3.
또한 상기 제조 실시예 1의 조성물과 제조 실시예 2 조성물 및 제조 실시예 3 의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 생산하여 판매하고 있다. Also, an eco-friendly elastic coating waterproof aqueous paint composition for the interior and exterior finish of the construction of the composition of Example 1, the composition of the preparation example 2 and the preparation example 3 is produced and sold.
도 6f는 상기 제조 실시예 1의 조성물과 실시예 2의 조성물 및 실시예 3의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 생산하여 공장 출하창고에서 보관 하고 있는 사진이다.FIG. 6F is a photograph showing the composition of Example 1, the composition of Example 2, and the waterproof paint composition of the eco-friendly elastic coating waterproofing aqueous paint for interior and exterior finishes of the construction material of Example 3 and stored in a factory warehouse.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 서울과학기술대학교 건설기술연구소에서 성능평가시험 결과치 (발급번호: 제1405-25. 2014.05.29.)에 대한 건설용 도막방수재 KS규격 KS F 2622-08에 의한 멤브레인 방수층 성능평가시험 결과 치와 건설용도막 방수재 KS 규격 KS F 3211-08에 의한 건설용 도막방수재 성능평가시험 결과치에 관한 최종적인 결과를 시험성적서의 형태로 하여 [표 1],[표 2]에 나타낸다.
Using the waterproof paint composition of the present invention for the interior and exterior finishing materials of the present invention, the waterproof paint composition of the present invention was used for the construction test for the performance evaluation test results (Issued No. 1405-25, 2014.05.29.) At the Institute of Construction Technology of Seoul National University of Science and Technology Membrane waterproofing layer performance evaluation test result by KS standard KS F 2622-08 KS standard Membrane waterproofing material performance test result according to KS standard KS F 3222-08 The final result of the performance evaluation test result of the construction waterproofing material according to KS F 3211-08 is shown in the form of test report Are shown in [Table 1] and [Table 2].
<건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 관한 내곰팡이성시험 과 염수분무성능시험(168h), 투수성시험, 중금속시험, 유해물질에 대한 성능시험. 제조 실시예 3><Fungicidal test and salt water spraying performance test (168h) on waterproof paint composition for environmentally resilient coatings for interior and exterior finishes of construction materials, water permeability test, heavy metal test, performance test on harmful substances. Production Example 3>
상기 제조 실시예 3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 곰팡이세균번식방지, 부식방지, 투수성(방수성), 중금속, 유해물질의 이상유무 및 검출확인을 확인하기 위하여, 서울특별시 영등포구 영등포동8가 88-2 한국화학융합시험연구원에 내곰팡이성과 염수분무시험(168h)후 녹발생유무 및 투수성, 중금속(Pb, Cd, Hg, Cr(VI)), 유해물질 포름알데히드에 대한 시험을 의뢰(2012.06.18.)하였다. In order to confirm the presence of the fungus in the water-repellent, water-repellent, corrosion-resistant, waterproof (waterproof), heavy metal, and harmful substances in the waterproof paint composition of the present invention, (Pb, Cd, Hg, Cr (VI)), Forms of harmful substances after the test for mycological and saline spray (168h) in Korea Chemical Fusion Test Institute 88-2, Yeongdeungpo-dong, Yeongdeungpo-gu, We commissioned the test for aldehyde (June 18, 2012).
한국화학융합시험연구원에서는 KS규격 KS M 6010시험방법에 의한 내곰팡이성 성능평가시험과 KS규격 KS D 9502시험방법에 의하여 염수분무시험(168h)후 녹발생 유무 성능평가시험 및 KS규격 KS F 4921시험방법에 의하여 투수성 유무 성능평가시험, KS규격 KS M ISO 3856-1 Pb, 3856-4 Cd, 3856-7 Hg, 3856-5 Cr(VI)시험방법에 의하여 중금속물질 검출성능평가시험, KS규격 US EPA 8315 A 시험방법에 의하여 유해물질 포름알데히드 검출성능평가시험을 진행하였다. The Korea Testing and Research Institute for Chemical Fusion Test was conducted to evaluate the performance of the fungicidal performance test using the KS standard KS M 6010 test method and the rust occurrence test after the salt spray test (168 h) according to the KS D 9502 test method and the KS standard KS F 4921 According to the test method, the performance test for the detection of heavy metals was carried out by the performance test of permeability, KS standard ISO 3856-1 Pb, 3856-4 Cd, 3856-7 Hg, 3856-5 Cr (VI) Specification US EPA 8315 A test method was used to evaluate the detection performance of toxic substance formaldehyde.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 한국화학융합시험연구원의 성능평가시험 결과치(성적서번호 TAK -008384. 시험 완료일자 2012.0723)에 의하여, 내곰팡이성의 결과치는 6, 이상없음 이고, 염수분무시험(168h)후 녹발생 유무의 결과 치는 이상없음 이고, 투수성 유무의 결과 치는 이상없음 이고, 중금속물질(Pb, Cd, Hg, Cr(VI)),의 결과치는 검출안됨이고, 유해물질 포름알데히드의 결과치는 검출안됨으로 확인 되었다. According to the performance evaluation test results (Test Report No. TAK-008384, Completion Date 2012.0723) of the Korea Chemical Fusion Test Institute for the waterproof paint composition for environmentally resilient coating waterproofing for interior and exterior finishing materials of the present invention, (Pb, Cd, Hg, Cr (VI)), and the result of the spray test (168h) after salt spraying showed no abnormality. And the result of toxic substance formaldehyde was not detected.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 한국화학융합시험연구원에서 성능평가시험 결과치 (성적서번호 TAK -008384. 시험 완료일자 2012.0723)에 대한 KS규격 KS M 6010시험방법에 의한 내곰팡이성 성능평가시험과 KS규격 KS D 9502시험방법에 의하여 염수분무시험(168h)후 녹발생 유무 성능평가시험 및 KS규격 KS F 4921시험방법에 의하여 투수성 유무 성능평가시험, KS규격 KS M ISO 3856-1 Pb, 3856-4 Cd, 3856-7 Hg, 3856-5 Cr(VI)성능평가시험 결과 치에 관한 최종적인 결과를 시험성적서의 형태로 하여 다음과 같이 나타낸다.The KS standard KS M 6010 test for the performance evaluation test results (Test Report No. TAK-008384. Completion date 2012.0723) at the Korea Chemical Fusion Test Institute using the waterproof paint composition of the environmentally resilient and elastic coating for interior and exterior finish of the present invention (KS D 9502 test method), the performance evaluation test of rust after salt spray test (168h) and the performance test of permeability by KS standard KS F 4921 test method, KS The final result of the performance evaluation test results in the form of test report is shown as follows.
<건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 관한 투수성과 내산성(H₂SO₄5%,168시간 침지)-균열 및 부풀음 유무 및 인장강도(N/㎣), 신장율(%)에 대한 성능시험. 제조 실시예 3><Permeability and acid resistance (H2SO4 5%, immersed for 168 hours) on waterproof paint composition for waterproofing of environmentally resilient coating film for building interior and exterior finishes - Performance test for cracking and swelling, tensile strength (N / ㎣) and elongation percentage . Production Example 3>
상기 제조 실시예3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 투수성(방수성) 과 산성물질의 저항성 및 인장강도, 신장율의 성능평가를 확인하기 위하여, 서울특별시 영등포구 영등포동8가 88-2 한국화학융합시험연구원에 투수성과 내산성(H₂SO₄5%,168시간 침지)-균열 및 부풀음 유무 및 인장강도(N/㎣), 신장율(%)에 대한 시험을 의뢰(2013.07.26.)하였다. In order to confirm the water permeability (waterproof property), resistance of the acidic material, tensile strength and elongation percentage of the environmentally resilient coating waterproofing aqueous paint composition for interior and exterior finish of the construction according to the preparation example 3, (88.2) Korea Testing and Research Institute for Chemical Engineering and Testing (KHNP) commissioned a test on permeability and acid resistance (H 2 SO 4 5%, 168 hours immersion) - Crack and swelling, tensile strength (N / ㎣) and elongation (%). Respectively.
한국화학융합시험연구원에서는 KS규격 KS F 4921시험방법에 의하여 투수성 성능평가시험과 KS규격 KS M ISO 2812-1 시험방법에 의하여 내산성(H₂SO₄5%,168시간 침지)-균열 및 부풀음 유무 성능평가시험 및 KS규격 KS F 3211 시험방법에 의하여 인장강도(N/㎣), 신장율(%)성능평가시험을 진행하였다. The Korea Testing and Research Institute for Chemical Fusion and Testing (KS F 4921) was used to evaluate the acid resistance (H 2 SO 4 5%, 168 hours immersion) by the permeability performance evaluation test and KS standard KS M ISO 2812-1 test method - (N / ㎣) and elongation percentage (%) according to the KS standard KS F 3211 test method.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 한국화학융합시험연구원의 성능평가시험 결과치(성적서번호 TAS -036441. 시험 완료일자 2013.08.12)에 의하여, 투수성 결과치는 이상없음이고, 내산성(H₂SO₄5%,168시간 침지)-균열 및 부풀음 유무의 결과치는 이상없음이고, 인장강도(N/㎣) 0.9 이고, 신장율(%) 890으로 확인되었다.According to the results of the performance evaluation test of the Korean Chemical Fusion Test Institute (Test Report No. TAS-036441, Completion Date 2013.08.12) on the waterproof paint composition for environmentally resilient coating waterproofing for the interior and exterior finish of the construction of the present invention, (N / ㎣) of 0.9 and elongation (%) of 890. The results are shown in Table 1. The results are shown in Table 1.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 이용하여 한국화학융합시험연구원에서 성능평가시험 결과치(성적서번호 TAS -036441. 시험 완료일자 2013.08.12)에 대한 KS규격 KS F 4921시험방법에 의하여 투수성 성능평가시험과 KS규격 KS M ISO 2812-1 시험방법에 의하여 내산성(H₂SO₄5%,168시간 침지)-균열 및 부풀음 유무 성능평가시험 및 KS규격 KS F 3211 시험방법에 의하여 인장강도(N/㎣), 신장율(%)성능평가시험 결과 치에 관한 최종적인 결과를 시험성적서의 형태로 하여 다음과 같이 나타낸 것이다.The KS standard KS F for the performance evaluation test results (Test Report No. TAS-036441, Date of Completion Test 2013.08.12) at the Korea Chemical Fusion Test Institute using the waterproof paint composition for environmentally resilient, (H 2 SO 4 5%, 168 hours immersion) - Performance evaluation test for cracking and swelling and KS standard KS F 3211 Test method by the test method of permeability test according to the test method and KS standard KS M ISO 2812-1 test method Tensile strength (N / ㎣), elongation (%) Performance evaluation The final result of the test results is shown in the form of test report as follows.
<건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 관한 촉진내후성후 초킹과 촉진내후성 황변도차 에 대한 성능시험. 제조 실시예1, 제조 실시예2, 제조 실시예3>
Performance test on accelerated weathering after chalking and accelerated weathering yellowing on the waterproof paint composition of eco - friendly elastic film for interior and exterior finishing materials of construction. Manufacturing Example 1, Manufacturing Example 2, Manufacturing Example 3>
상기 제조 실시예1, 제조 실시예2, 제조 실시예3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 노화에 의한 황변현상의 성능평가를 확인하기 위하여, 서울특별시 영등포구 영등포동8가 88-2 한국화학융합시험연구원에 촉진내후성 초킹과 촉진내후성 황변도차에 대한 시험을 의뢰(2014.08.21.)하였다.To confirm the performance evaluation of yellowing phenomenon caused by the aging of the water-based paint composition for environmentally resilient coating waterproofing for interior and exterior finishes of the construction products according to Production Example 1, Production Examples 2 and 3, Yeongdeungpo- And 88-2 Korea Chemical Fusion Test Research Institute (2014.08.21) commissioned a test for accelerated weathering chalking and accelerated weathering yellowing.
한국화학융합시험연구원에서는 KS규격 KS M 6010 시험방법에 의한 촉진내후성후 초킹 성능평가시험과 KS규격 KS M 6010 시험방법에 의하여 촉진내후성 황변도차 성능평가시험을 진행하였다. The Korea Testing and Research Institute for Chemical Fusion Test conducted the evaluation of accelerated weathering resistance and chalking performance by the KS M 6010 test method and the KS M 6010 test method.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 한국화학융합시험연구원의 성능평가시험 결과 치(성적서번호 TAK -008837. 시험 완료일자 2014.09.05)에 관한 최종적인 결과를 시험성적서의 형태로 하여 다음과 같이 나타낸 것이다.The final result of the performance evaluation test results of the Korea Chemical Fusion Test Institute for the waterproof paint composition of environmentally friendly elastic coating for the interior and exterior finishing materials of the present invention (Test Report No. TAK-008837, completion date 2014.09.05) In the form of test report, it is shown as follows.
<건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 관한 방염성능에 대한 성능시험. 제조 실시예3>Performance Tests on Flame Retardant Performance of Water - Resistant Water - Soluble Paint Composition with Eco - Elastic Elastic Coating for Interior and Exterior Finish of Construction. Production Example 3>
상기 제조 실시예3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 방염성능평가를 확인하기 위하여, 경기도 용인시 기흥구 지곡2동136번지 한국소방산업기술원에 방염성능대한 시험을 의뢰(2012. 06. 26. 접수번호 제1206320)하였다.In order to confirm the flame retardant performance evaluation of the waterproof paint composition for environmentally resilient coating waterproofing waterproofing paint for indoor and outdoor finishes of the construction according to the above Manufacturing Example 3, the fire-fighting performance test was commissioned to the Korea Fire & Disaster Management Institute, 136, Jigok 2 dong, Giheung- No. 26, 2012, No. 1206320).
한국소방산업기술원에서는 방염성능의 기준(KOFEIS 1001) 시험방법에 의한 잔염시간(10초이내), 잔진시간(30초이내), 탄화면적(50㎤ 이내), 탄화길이(20㎝ 이내), 접염회수(3회 이상) 성능평가 시험을 진행 하였다.The Korea Fire Protection Industrial Technology Institute (KFAS) has estimated the flame retardant performance (KOFEIS 1001) test method of residual flame time (within 10 seconds), residual time (within 30 seconds), carbonization area (within 50 cm), carbonization length (3 times or more) performance evaluation test.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 한국소방산업기술원의 성능평가시험 결과 치(성적서번호 제2012-07-2799 -008837. 시험 완료일자 2012.07.10)에 의하여, 이상없음으로 확인 되었다. According to the results of the performance evaluation test of the Korea Fire Fighting Industry Technical Institute for the waterproof paint composition for environmentally resilient and elastic coating for interior and exterior finishing materials of the present invention (Test Report No. 2012-07-2799 -008837. , And no abnormality.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 한국소방산업기술원의 성능평가시험 결과 치(성적서번호 제2012-07-2799 -008837. 시험 완료일자 2012.07.10)에 관한 최종적인 결과를 시험성적서의 형태로 하여 다음과 같이 나타낸 것이다.The performance evaluation test results of the Korea Fire Fighting Industry Technical Institute for the waterproof paint composition for environmentally resilient and elastic waterproofing of interior and exterior of construction materials of the present invention (Test Report No. 2012-07-2799 -008837. The final result is shown in the form of a test report as follows.
<건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 관한 시멘트보드(CRC) 중 라돈(radon)측정에 대한 성능시험. 제조 실시예3>Performance Tests for Radon Measurements in Cement Board (CRC) for Water - Resistant, Water - Soluble Paint Composition with Eco - Elastic Elastic Coating for Interior and Exterior Finishes of Construction. Production Example 3>
상기 제조 실시예3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 시멘트보드(CRC) 중 라돈(radon)측정 성능평가를 확인하기 위하여, 경기도 성남시 수정구 성남대로 1342 가천대학교 환경에너지공학과 연구소에 라돈(radon)측정성능에 대한 시험을 의뢰(2014.08.04.)하였다.In order to confirm the radon measurement performance of the cement board (CRC) of the environmentally resilient coating waterproofing aqueous paint composition for interior and exterior finishing materials of the construction example 3, The research institute requested a test on radon measurement performance (April 4, 2014).
가천대학교 환경에너지공학과 연구소에서는 실내공기질 관리기준에 의하여 다중이용시설 등의 실내질 관리법과 학교보건법에 의한 라돈 4.0Rn(pCi/ℓ) 이하, 에 대한 성능평가시험을 진행하였다.In the Institute of Environmental Energy Engineering, Gachon University, performance evaluation test was conducted on the indoor quality control law of multi - use facilities and less than 4.0Rn (pCi / ℓ) of radon by School Health Law according to indoor air quality management standard.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 가천대학교 환경에너지공학과 연구소의 성능평가시험 결과 치(시험 완료일자 2014.08.26)에 의하여, 시료번호 SA 1 : 0.18Rn(pCi/ℓ), SA 2 : 0.17Rn(pCi/ℓ), SA 3 : 0.11Rn(pCi/ℓ), 이상없음 으로 확인 되었다. According to the results of the performance evaluation test (Date of completion: 2014.08.26) of the Institute of Environmental Energy Engineering, Institute of Environmental Science and Engineering, Institute of Environmental Science and Technology, Gachon University for the waterproof paint composition for waterproofing of environmentally resilient coating films for interior and exterior finishes of the present invention, Sample No. SA 1: 0.18Rn pCi / l), SA 2: 0.17Rn (pCi / l) and SA 3: 0.11Rn (pCi / l).
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 가천대학교 환경에너지공학과 연구소의 성능평가시험 결과 치(시험 완료일자 2014.10.06)에 관한 최종적인 결과를 시험성적서의 형태로 하여 다음과 같이 나타낸 것이다.
The final results of the performance evaluation test results (date of completion of examination 2014.10.06) of the Institute of Environmental Energy Engineering, Gachon University on the waterproof paint composition for waterproofing of environmentally resilient and elastic coatings for interior and exterior finishes of the present invention are shown in the form of a test report As shown in FIG.
(다중이용시설 등의 실내 질 관리법과 학교보건법, 라돈 4.0 Rn(pCi/ℓ)이하) (Under the indoor quality control law and school health law of multipurpose facilities, less than 4.0 Rn (pCi / ℓ) of radon)
<건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 관한 전기절연저항에 대한 성능시험. 실시예1, 실시예2, 실시예3>
Performance Tests on Electrical Insulation Resistance of Eco - Friendly Elastic Coating Waterproofing Paint Composition for Interior and Exterior Finishes of Construction. Example 1, Example 2, Example 3>
상기 실시예1, 실시예2, 실시예3에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 전기절연저항성능평가를 확인하기 위하여, 1000V 절연저항계로 시험을 진행하였다.
In order to confirm the electric insulation resistance performance evaluation of the waterproof paint composition for environmentally resilient coating waterproofing paint for interior and exterior finish of the construction according to Examples 1, 2, and 3, the test was conducted with a 1000V insulation resistance meter.
본 발명의 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물에 대한 전기절연저항 성능평가시험 결과치(시험 완료일자 2014.08.21)에 관한 최종적인 결과를 시험성적서의 형태로 하여 다음과 같이 나타낸 것이다.
The final result of the electrical insulation resistance performance evaluation test (test completion date 2014.08.21) for the waterproof paint composition of the environmentally resilient coating waterproofing paint for interior and exterior finishing materials of the present invention is shown in the form of a test report as follows will be.
이상에서 본 발명에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물 및 그 사용에 의한 효과를 구체적으로 설명 하였으나, 이는 본 발명의 가장 바람직한 실시양태를 기재한 것일 뿐, 본 발명이 이에 한정되는 것은 아니며, 첨부된 특허청구에 의해서 그 범위가 결정되어지고 한정되어진다.
While the present invention has been particularly shown and described with respect to the preferred embodiments thereof, it should be understood that the present invention is not limited to the described embodiments. The scope of which is defined and limited by the appended claims.
도 7은 콘크리트 벽돌 표면의 제1실시예(투명무광), 제2실시예((투명유광), 제3실시예(단청색)에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 나타낸 도면 대용 사진이다. 7 is a view showing an example of a waterproof paint composition according to the first embodiment (transparent matte) of the concrete brick surface, the second embodiment (transparent luster), and the eco-friendly elastic coating waterproof aqueous paint composition for the interior and exterior finish of the construction by the third embodiment Fig.
도 8은 목재패널 표면의 제1실시예(투명무광), 제2실시예((투명유광), 제3실시예(단청색의 검정색과 백색)에 의한 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 나타낸 도면 대용 사진이다. Fig. 8 is a view showing the construction of the eco-friendly elastic coating film for the interior and exterior finish of the construction material according to the first embodiment (transparent matte) of the surface of the wood panel, the second embodiment (transparent gloss), and the third embodiment (simple blue and white) Water-proof paint composition according to the present invention.
도 9 및 도 10은 글라스울 표면에 제1실시예(투명무광)와 제3실시예(백색)에 의한 방염성능이 평가된 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물을 나타낸 도면 대용 사진이다. 9 and 10 are views showing an environmentally friendly waterproof, waterproof aqueous paint composition for interior and exterior finishes of a construction material having evaluated flame retardancy by the first embodiment (transparent matte) and the third embodiment (white) on the surface of a glass wool It is a substitute photograph.
화염으로 직접 20분~40분간 가열하였고 가열 후 사진에 보이는 바와 같이 불이 붙지 않는 방염성능이 확인되었다.
The flame was directly heated for 20 minutes to 40 minutes, and as shown in the photograph after the heating, flame retardant performance without flame was confirmed.
비록 본 발명이 상기 언급된 바람직한 실시예와 관련하여 설명되어졌지만, 발명의 요지와 범위로부터 벗어남이 없이 다양한 수정 및 변형이 가능한 것은 당업자라면 용이하게 인식할 수 있을 것이며, 이러한 변경 및 수정은 모두 첨부된 청구의 범위에 속함은 자명하다.
Although the present invention has been described in connection with the above-mentioned preferred embodiments, it will be apparent to those skilled in the art that various modifications and variations can be made without departing from the spirit and scope of the invention, It is obvious that the claims fall within the scope of the claims.
없음none
Claims (6)
부틸아크릴-2에틸실아크릴레이트메틸메타크릴산-아크릴실란공중합체(butylacryl-2ethylhexylacrylatemethylmethacryl acid-acrylsilanecopolymer) 18 ~ 25 중량%;
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate-2Sodiumcarboxymethylcellulose) 12 ~ 15 중량%;
콜로이달 실리카 13 ~ 17 중량%;
중성수 25 ~ 35 중량%;
를 혼합하여 이루어진 것을 특징으로 하는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법.12 to 16% by weight of propylene glycol;
Butylacryl-2ethylhexylacrylate methylmethacrylic acid-acrylsilanecopolymer 18-25% by weight; butyl acrylate-2 ethyl ethyl acrylate methyl methacrylate-acryl silane copolymer;
12 to 15% by weight of sodium polyacrylate-2 sodium carboxymethylcellulose (sodium polyacrylate-2 sodium carboxymethylcellulose);
Colloidal silica 13 to 17% by weight;
25 to 35% by weight of neutral water;
Wherein the water-repellent paint composition is a mixture of water and an organic solvent.
프로필렌글리콜(propyleneglyc ol) 12 ~ 16 중량%;
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체 (butylacryl-2ethylhexylacrylatemethylmethacrylic acid-acrylsilanecopolymer) 12 ~ 25중량%;
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate-2Sodiumcarboxymethylcellulose) 12 ~ 15 중량%;
콜로이달 실리카 13 ~ 17 중량%와;
중성수 25 ~ 35 중량%;
를 혼합하여 이루어지는 것을 특징으로 하는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법.15 to 23% by weight of styrene butadiene rubber;
12-16 wt% propylene glycol (ol);
Butyl acryl-2-ethylhexyl acrylate methyl acrylate-butylacryl-2ethylhexylacrylate methylmethacrylic acid-acrylsilanecopolymer 12-25 wt%;
12 to 15% by weight of sodium polyacrylate-2 sodium carboxymethylcellulose (sodium polyacrylate-2 sodium carboxymethylcellulose);
13 to 17% by weight colloidal silica;
25 to 35% by weight of neutral water;
Wherein the water-based paint composition is a mixture of water and an organic solvent.
프로필렌글리콜(propyleneglycol) 2 ~ 6 중량%;
부틸아크릴-2에틸헥실아크릴레이트메틸메타크릴산-아크릴실란공중합체(butylacryl-2ethylhexylacrylatemethylmethacryl acid-acrylsilan ecopolymer) 8 ~ 15 중량%;
소듐폴리아크릴레이트-2소듐카르복시메칠셀룰로오스나트륨(Sodiumpolyacrylate- 2Sodiumcarboxymethylcellulose) 2 ~ 5 중량%;
이산화티타늄(Tio2) 0.1 ~ 0.6 중량%;
백토분말 12 ~ 15 중량%;
조개분말 2 ~ 4 중량%;
탄산칼슘분말 10 ~ 15 중량%;
무기질분말 5 ~8 중량%;
무기질안료 15 ~ 20 중량%;
중성수 15 ~ 25 중량%;
콜로이달 실리카 3 ~ 7 중량%
을 혼합하여 이루어지는 것을 특징으로 하는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법.5 to 13% by weight of styrene butadiene rubber (sbr);
2 to 6% by weight of propyleneglycol;
8 to 15% by weight of butylacryl-2-ethylhexyl acrylate methyl methacrylic acid-acrylsilane copolymer (butylacryl-2ethylhexylacrylate methylmethacryl acid-acrylsilane ecopolymer);
2 to 5% by weight of sodium polyacrylate-2 sodium carboxymethylcellulose (sodium polyacrylate-2 sodium carboxymethylcellulose);
0.1 to 0.6% by weight of titanium dioxide (Tio2);
12 to 15% by weight of clay powder;
2 to 4% by weight of shell powder;
10 to 15% by weight of calcium carbonate powder;
5 to 8% by weight of an inorganic powder;
15 to 20% by weight of an inorganic pigment;
15 to 25% by weight of neutral water;
Colloidal silica 3 to 7 wt%
Wherein the water-based paint composition is a mixture of water and an organic solvent.
상기 백토분말은 고령토이며 300 메시 내지 400 메시 크기인 것을 특징으로 하는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법.The method of claim 3,
Wherein the white clay powder is kaolin and has a size of 300 mesh to 400 mesh. Description: FIELD OF THE INVENTION The present invention relates to a waterproof paint composition for environmental and residential use.
상기 조개분말은 조개껍질을 분쇄하여 얻어지는 호분인 것을 특징으로 하는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법.The method of claim 3,
Wherein the clamshell powder is a fume obtained by crushing the clamshells.
상기 무기질분말은 석회 또는 규사인 것을 특징으로 하는 건설물의 내, 외장 마감재용 친환경 탄성도막방수 수성페인트 조성물의 제조방법.
The method of claim 3,
Wherein the inorganic powder is lime or silica. 2. The method of claim 1, wherein the inorganic powder is lime or silica.