KR20160038212A - Composition for coating a surface and a seat cover for automobile applied the same - Google Patents
Composition for coating a surface and a seat cover for automobile applied the same Download PDFInfo
- Publication number
- KR20160038212A KR20160038212A KR1020140130628A KR20140130628A KR20160038212A KR 20160038212 A KR20160038212 A KR 20160038212A KR 1020140130628 A KR1020140130628 A KR 1020140130628A KR 20140130628 A KR20140130628 A KR 20140130628A KR 20160038212 A KR20160038212 A KR 20160038212A
- Authority
- KR
- South Korea
- Prior art keywords
- surface coating
- composition
- weight
- urethane
- beads
- Prior art date
Abstract
Description
본 발명은 표면코팅용 조성물 및 이를 적용한 자동차 시트에 관한 것이다.
The present invention relates to a composition for surface coating and an automobile seat to which the composition is applied.
일반적으로 염화비닐수지(PVC)는 저가이고, 열에 강하며, 연성 및 강성에 있어서 다양한 형태를 취할 수 있어서 바닥재, 의료장비, 전선 절연체, 인테리어시트, 간판 또는 실내외 장식시트의 원료로 사용될 수 있는 것으로, 예를 들어, 염화비닐수지는 자동차 시트의 원료로 사용될 수 있다.In general, vinyl chloride resin (PVC) is inexpensive, strong in heat, can take various forms in ductility and rigidity, and can be used as a raw material for flooring, medical equipment, wire insulator, interior sheet, , For example, vinyl chloride resin can be used as raw material for automobile seat.
그러나, 현재 자동차는 제2의 주거공간으로 부각되고 있는바, 자동차 시트가 차내에서 가장 많은 부분을 차지하고 있어, 자동차라는 공간에서 높은 수준을 유지할 수 있는 자동차 시트에 대한 소비자의 관심이 증대되고 있고, 차내의 깨끗한 환경을 보존하기 위한 높은 내마모성 및 내오염성과 같은 기본적인 물성이 향상되면서도, 우수한 촉감과 같은 부가적인 물성이 향상된 자동차 시트에 대한 연구의 필요성이 확대되고 있는 실정이다.However, since automobiles are now regarded as a second residential space, automobile seats occupy the largest portion in the automobiles, and consumers are increasingly interested in automobile seats that can maintain a high level in the automobile space, Background Art [0002] There is a growing need for research on automobile seats having improved physical properties such as superior tactile properties while improving basic properties such as high abrasion resistance and pollution resistance for preserving a clean environment in a vehicle.
또한, 자동차 시트의 표면코팅층을 형성함에 있어, 유기용매를 사용하게 되면 유기용매 사용으로 인한 휘발성 유기 화합물질(VOCs)에 따른 냄새물질의 발생에 따른 문제가 있다.
Further, when an organic solvent is used to form a surface coating layer of an automobile seat, there is a problem due to generation of odorous substances due to volatile organic compounds (VOCs) due to the use of an organic solvent.
본 발명은 말단에 이소시아네이트기를 가지는 카르복실기 함유 주제; 및 우레탄계 비드를 포함하는 표면코팅용 조성물 및 이를 적용한 촉감이 우수한 자동차 시트를 제공하고자 한다.The present invention relates to a carboxyl group-containing subject having an isocyanate group at the terminal thereof; And urethane beads, and a car seat having excellent tactile sensation using the same.
그러나, 본 발명이 이루고자 하는 기술적 과제는 이상에서 언급한 과제에 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 당업자에게 명확하게 이해될 수 있을 것이다.
However, the technical problem to be solved by the present invention is not limited to the above-mentioned problems, and other matters not mentioned can be clearly understood by those skilled in the art from the following description.
본 발명은 말단에 이소시아네이트기를 가지는 카르복실기 함유 화합물을 포함하는 주제; 및 우레탄계 비드를 포함하는 표면코팅용 조성물을 제공한다.The present invention relates to a subject comprising a carboxyl group-containing compound having an isocyanate group at the terminal thereof; And a composition for surface coating comprising urethane beads.
상기 우레탄계 비드는 450% 내지 900%의 신도를 갖을 수 있다.The urethane beads may have an elongation of 450% to 900%.
상기 우레탄계 비드는 25℃ 에서 50% 신장 변형시 탄성 회복률(Re)이 95% 내지 99%일 수 있다.The urethane-based beads may have an elastic recovery (Re) of 95% to 99% at 50% elongation at 25 ° C.
상기 우레탄계 비드는 입자크기가 1㎛ 내지 20㎛일 수 있다.The urethane beads may have a particle size of 1 탆 to 20 탆.
상기 주제는 평균 입경이 상이한 입자들을 포함하여, 이중 입자 크기 분포(bimodal particle size distribution)를 가질 수 있다. The subject may have bimodal particle size distributions, including particles with different average particle sizes.
상기 주제는 물이 첨가되어 수분산된 것일 수 있다.The subject may be water-dispersed and water-dispersed.
상기 주제는 폴리올 화합물, 카르복실기 함유 폴리올 화합물 및 말단에 적어도 2개의 이소시아네이트기를 가지는 이소시아네이트 화합물이 반응하여 형성된 프리폴리머(prepolymer)일 수 있다.The subject matter may be a prepolymer formed by reacting a polyol compound, a carboxyl group-containing polyol compound and an isocyanate compound having at least two isocyanate groups at the terminal thereof.
상기 프리폴리머는 폴리실록산 화합물이 추가로 반응하여 형성된 것일 수 있다.The prepolymer may be one in which a polysiloxane compound is further reacted.
상기 폴리실록산 화합물의 중량평균분자량은 200g/mol 내지 300g/mol일 수 있다.The weight average molecular weight of the polysiloxane compound may be from 200 g / mol to 300 g / mol.
상기 표면코팅용 조성물 총 100 중량부에 대하여, 상기 주제 30중량부 내지 60중량부 및 상기 우레탄계 비드 1 중량부 내지 10중량부를 포함할 수 있다.30 to 60 parts by weight of the subject and 1 to 10 parts by weight of the urethane based beads may be contained relative to 100 parts by weight of the total amount of the composition for surface coating.
이소시아네이트계 경화제를 추가로 포함할 수 있다.An isocyanate-based curing agent may be further included.
상기 표면 코팅용 조성물은 3차원 가교결합 반응에 의해 폴리머 사슬을 형성할 수 있다.The composition for surface coating may form a polymer chain by a three-dimensional crosslinking reaction.
소광제, 습윤제, 분산제, 왁스, 슬립제, 소포제 및 이들의 조합으로 이루어진 군으로부터 선택된 첨가제를 더 포함할 수 있다.A wetting agent, a dispersing agent, a wax, a slipping agent, an antifoaming agent, and combinations thereof.
본 발명의 일 구현예로, 상기 표면코팅용 조성물로 형성된 표면코팅층; 및 상기 표면코팅층 하부에 형성된 기재층을 포함하는 자동차 시트를 제공한다.In one embodiment of the present invention, a surface coating layer formed of the composition for surface coating; And a base layer formed below the surface coating layer.
상기 표면코팅층의 상부 표면에 다수의 돌출부가 형성된 것을 특징으로 할 수 있다.And a plurality of protrusions are formed on the upper surface of the surface coating layer.
상기 돌출부는 반구형 또는 반타원구형이고, 0.5㎛ 내지 10㎛의 높이를 가질 수 있다.The protrusion may have a hemispherical shape or a semi-elliptic shape, and may have a height of 0.5 탆 to 10 탆.
상기 표면코팅층은 상기 표면코팅용 조성물이 1㎛ 내지 20㎛로 도포 후 건조되어 형성될 수 있다.The surface coating layer may be formed by applying the surface coating composition at a thickness of 1 to 20 m, followed by drying.
상기 표면코팅층의 스퀵 지수는 0.2 이하일 수 있다.The Squeak index of the surface coating layer may be 0.2 or less.
상기 기재층은 폴리비닐클로라이드 수지, 폴리우레탄 수지, 열가소성 폴리올레핀 수지(Thermoplastic Polyolefins, TPO), 열가소성 폴리우레탄 수지(Thermoplastic Polyurethanes, TPU) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함할 수 있다.
The substrate layer may comprise one selected from the group consisting of polyvinyl chloride resins, polyurethane resins, thermoplastic polyolefins (TPO), thermoplastic polyurethanes (TPU), and combinations thereof.
본 발명에 따른 표면코팅용 조성물은 우레탄계 비드를 포함하는 것으로, 이를 적용한 자동차 시트는 우레탄계 비드로 인해 다수의 돌출부를 형성하는바, 내마모성 및 내오염성과 같은 기본적인 물성이 우수하면서도, 소프트한 촉감, 낮은 스퀵 지수에 따른 슬립성 및 불점착성과 같은 부가적인 물성 역시 우수하다.
The composition for surface coating according to the present invention includes urethane beads. The automobile sheet to which the present invention is applied has many protrusions due to urethane beads. It has excellent basic properties such as abrasion resistance and contamination resistance, Additional physical properties such as slip property and non-stick property according to Squeak index are also excellent.
도 1은 본 발명의 일 구현예에 따른 자동차 시트를 개략적으로 나타낸 단면도이다.
도 2는 실시예 1~2 및 비교예 1에 따른 자동차 시트의 스퀵 지수를 측정한 그래프이다.1 is a cross-sectional view schematically showing an automobile seat according to an embodiment of the present invention.
Fig. 2 is a graph showing the Squeak indices of automobile seats according to Examples 1 and 2 and Comparative Example 1. Fig.
본 발명자들은 자동차 시트 표면코팅용 조성물에 대해 연구하던 중, 말단에 이소시아네이트기를 가지는 카르복실기 함유 화합물을 포함하는 주제; 및 우레탄계 비드를 포함하는 표면코팅용 조성물을 자동차 시트에 적용함으로써, 물성을 향상시킬 수 있음을 확인하고 본 발명을 완성하였다.
The present inventors have studied a composition for coating a surface of an automobile seat, a subject comprising a carboxyl group-containing compound having an isocyanate group at the terminal thereof; And urethane-based beads are applied to an automobile seat, the present inventors have completed the present invention.
이하, 본 발명을 상세히 설명한다.
Hereinafter, the present invention will be described in detail.
표면코팅용 조성물Composition for surface coating
본 발명은 말단에 이소시아네이트기를 가지는 카르복실기 함유 화합물을 포함하는 주제; 및 우레탄계 비드를 포함하는 표면코팅용 조성물을 제공한다.
The present invention relates to a subject comprising a carboxyl group-containing compound having an isocyanate group at the terminal thereof; And a composition for surface coating comprising urethane beads.
구체적으로, 상기 주제는 말단에 이소시아네이트기를 가지는 카르복실기 함유 화합물을 포함하는 것으로, 상기 화합물의 주사슬 내 카르복실기를 함유한 것을 특징으로 한다. Specifically, the subject matter includes a carboxyl group-containing compound having an isocyanate group at the terminal thereof, and is characterized by containing a carboxyl group in the main chain of the compound.
구체적으로, 상기 주제는 평균 입경이 상이한 입자들을 포함하여, 이중 입자 크기 분포(bimodal particle size distribution)를 가질 수 있다. 이중 입자 크기 분포라 함은 상대적으로 평균 입경이 작은 제1 입자들 및 상대적으로 평균 입경이 큰 제2 입자들로 나뉘어진 상태의 분포를 말하는 것이다. 이와 같이, 상기 주제가 이중 입자 크기 분포를 가짐으로써, 제2 입자들 사이에 제1 입자들이 위치할 수 있어, 고충진밀도(high packing density)를 구현할 수 있는바, 내마모성 및 내오염성 효과를 보다 용이하게 구현할 수 있다.Specifically, the subject may have bimodal particle size distributions, including particles with different average particle sizes. The dual particle size distribution refers to a distribution in which particles are divided into first particles having a relatively small average particle diameter and second particles having a relatively large average particle diameter. As such, since the subject has a dual particle size distribution, the first particles can be positioned between the second particles, and high packing density can be realized, so that the abrasion resistance and stain resistance effect can be facilitated .
상기 주제는 물을 첨가하여 수분산될 수 있다. 여기서 물은 우레탄 수분산을 형성하기 위한 것으로 10 내지 50 중량부를 첨가할 수 있고, 2차 증류수인 초순수를 사용하는 것이 바람직하다. 상기 범위량의 물을 첨가하여 수분산시킴으로써, 수분산 폴리우레탄을 구현할 수 있다. 수분산 폴리우레탄이란 고분자(폴리우레탄)가 유기용매에 녹아있지 않고 물속에서 분산되어 있는 상태를 말하는 것으로, 용매를 물로 사용하기 때문에 휘발성 유기용매에 의한 독성 문제도 없고 안전하게 보관이 가능하다.
The subject may be water dispersed by adding water. Here, water is used for forming a urethane water dispersion, and it is preferable to add 10 to 50 parts by weight of ultrapure water which is secondary distilled water. By adding water in the above range and dispersing it in water, a water-dispersed polyurethane can be realized. Water-dispersed polyurethane refers to a state in which a polymer (polyurethane) does not dissolve in an organic solvent but is dispersed in water. Since the solvent is used as a water, there is no toxicity problem caused by volatile organic solvents and it can be safely stored.
또한, 상기 주제는 폴리올 화합물, 카르복실기 함유 폴리올 화합물 및 말단에 적어도 2개의 이소시아네이트기를 가지는 이소시아네이트 화합물이 반응하여 형성된 프리폴리머(prepolymer)일 수 있다. 이때, 프리폴리머는 성형하기 쉽게 하기 위하여 중합반응을 중도 단계에서 중지시킨 비교적 중합도가 낮은 중합체를 의미한다. In addition, the subject matter may be a prepolymer formed by reacting a polyol compound, a carboxyl group-containing polyol compound and an isocyanate compound having at least two isocyanate groups at the terminal thereof. Here, the prepolymer means a polymer having a relatively low degree of polymerization in which the polymerization reaction is stopped in the middle stage in order to facilitate molding.
이때, 상기 프리폴리머는 폴리올 화합물 2당량, 카르복실기 함유 폴리올 화합물 1당량 및 말단에 적어도 2개의 이소시아네이트기를 가지는 이소시아네이트 화합물 4당량이 반응하여 형성될 수 있다.At this time, the prepolymer may be formed by reacting 2 equivalents of a polyol compound, 1 equivalent of a carboxyl group-containing polyol compound and 4 equivalents of an isocyanate compound having at least two isocyanate groups at its terminals.
상기 폴리올 화합물은 폴리에스테르계 폴리올, 락톤계 폴리올, 폴리카보네이트계 폴리올, 폴리에테르계 폴리올 및 이들의 조합으로 형성된 군으로부터 선택된 하나 이상의 화합물일 수 있다.The polyol compound may be at least one compound selected from the group formed by a polyester-based polyol, a lactone-based polyol, a polycarbonate-based polyol, a polyether-based polyol, and combinations thereof.
상기 카르복실기 함유 화합물은 하기 화학식 1일 수 있다:The carboxyl group-containing compound may be represented by the following Formula 1:
[화학식 1][Chemical Formula 1]
상기 말단에 적어도 2개의 이소시아네이트기를 가지는 이소시아네이트 화합물은 톨루엔 디이소시아네이트, 디페닐메탄 디이소시아네이트, 변성 디페닐메탄 디이소시아네이트, 나프탈렌 디이소시아네이트, 페닐렌 디이소시아네이트트, 헥사메틸렌 디이소시아네이트, 리신 이소시아네이트, 사이클로헥산 디이소시아네이트, 이소포론 디이소시아네이트, 메틸렌디페닐 이소시아네이트, 크실렌 디이소시아네이트, 테트라메틸크실렌 디이소시아네이트, 노르보넨 디이소시아네이트, 트리페닐메탄 트리이소시아네이트, 폴리페닐 폴리메틸렌 폴리이소시아네이트, 카보디이미드기를 포함하는 폴리이소시아네이트, 알로파네이트기를 포함하는 폴리이소시아네이트, 이소시아누레이트기를 포함하는 폴리이소시아네이트 및 이들의 조합으로 형성된 군으로부터 선택된 하나 이상의 화합물일 수 있다.The isocyanate compound having at least two isocyanate groups at the terminal thereof may be at least one selected from the group consisting of toluene diisocyanate, diphenylmethane diisocyanate, modified diphenylmethane diisocyanate, naphthalene diisocyanate, phenylene diisocyanate, hexamethylene diisocyanate, lysine isocyanate, cyclohexane di A polyisocyanate containing an isocyanate group, an isocyanate group, an isocyanate group, an isocyanate group, an isocyanate group, an isocyanate group, an isocyanate group, an isocyanate group, an isocyanate group, an isocyanate group, A polyisocyanate containing a phenate group, a polyisocyanate containing an isocyanurate group, and a combination thereof, These may be one or more compounds.
상기 반응으로 형성된 프리폴리머를 폴리우레탄 프리폴리머라 하며, 카르복실기에 의해 음이온성 프리폴리머인 것으로, 물이 첨가되어 용이하게 수분산될 수 있다.The prepolymer formed by the above reaction is referred to as a polyurethane prepolymer, which is an anionic prepolymer due to a carboxyl group, and water can be easily added and dispersed in water.
상기 프리폴리머는 폴리실록산 화합물이 추가로 반응하여 형성된 것일 수 있다.The prepolymer may be one in which a polysiloxane compound is further reacted.
상기 폴리실록산 화합물의 중량평균분자량은 200g/mol 내지 300g/mol일 수 있고, 말단에 하이드록시기를 가지는 폴리실록산 화합물일 수 있다. The weight average molecular weight of the polysiloxane compound may be 200 g / mol to 300 g / mol, and may be a polysiloxane compound having a hydroxyl group at the terminal.
상기 폴리실록산 화합물은 하기 화학식 2일 수 있다:The polysiloxane compound may be of the formula:
[화학식 2](2)
상기 화학식 2에서, R는 탄소수 1 내지 10의 포화 또는 불포화된 탄화수소 사슬이고, n은 1 내지 100의 정수이다.In the general formula (2), R is a saturated or unsaturated hydrocarbon chain having 1 to 10 carbon atoms, and n is an integer of 1 to 100.
상기 폴리실록산 화합물이 추가로 반응하여 형성된 프리폴리머 역시 음이온성 프리폴리머인 것으로, 물이 첨가되어 용이하게 수분산될 수 있다.The prepolymer formed by further reacting the polysiloxane compound is also an anionic prepolymer, and water can be easily added and dispersed in water.
상기 표면코팅용 조성물 총 100 중량부에 대하여, 상기 주제 30중량부 내지 60중량부를 포함하는 것이 바람직하나, 이에 한정되지 않는다. 이때, 주제가 30 중량부 미만인 경우, 본래 수분산성 폴리우레탄으로서 특성이 제대로 발휘되지 못하는 문제점이 있고, 주제가 60 중량부를 초과하는 경우, 나머지 성분으로 인한 특성이 제대로 발휘되지 못하는 문제점이 있다.
But it is not limited to 30 parts by weight to 60 parts by weight based on 100 parts by weight of the total amount of the composition for surface coating. At this time, when the content of the base is less than 30 parts by weight, the characteristics of the water-dispersible polyurethane can not be exhibited. When the content of the base exceeds 60 parts by weight, the characteristics due to the remaining components are not exhibited properly.
상기 우레탄계 비드는 소프트하면서도 탄성이 우수한 특징이 있는 입자인 것으로, 우레탄계 비드를 포함하는 표면코팅용 조성물을 자동차 시트에 적용하는 경우, 우레탄계 비드로 인하여 다수의 돌출부를 형성할 수 있고, 이로써 소프트한 촉감, 낮은 스퀵 지수에 따른 슬립성 및 불점착성과 같은 부가적인 물성을 확보할 수 있다.The urethane beads are soft and highly elastic. When a composition for surface coating comprising urethane beads is applied to an automobile seat, it is possible to form a large number of protrusions due to urethane beads, , Additional properties such as slipperiness and non-stickiness according to a low squeak index can be secured.
대다수의 우레탄계 비드는 표면코팅용 조성물 내 일부만 매몰되어 매몰되지 않은 부분이 노출된 상태로 다수의 돌출부를 형성하기 위한 것이고, 몇몇의 우레탄계 비드는 조성물 내 전부 매몰될 수도 있다.The majority of the urethane beads are intended to be buried only in a part of the composition for surface coating so as to form a plurality of projections with exposed portions uncovered, and some urethane-based beads may be completely buried in the composition.
상기 우레탄계 비드는 450% 내지 900%의 신도를 갖는 것이 바람직하나, 이에 한정되지 않는다. 이때, 신도라 함은 우레탄계 비드가 절단될 때까지 늘어나 길이를 우레탄계 비드의 원길이에 대한 백분율(%)로 나타낸 것을 말한다. The urethane beads preferably have an elongation of 450% to 900%, but are not limited thereto. In this case, the term "elongation" refers to the elongation of the urethane bead until it is cut, and the length is expressed as a percentage (%) of the urethane bead length.
또한, 상기 우레탄계 비드는 25℃ 에서 50% 신장 변형시 탄성 회복률(Re)이 95% 내지 99%인 것이 바람직하나, 이에 한정되지 않는다.It is preferable that the urethane bead has an elastic recovery rate (Re) of 95% to 99% at 50% elongation at 25 ° C, but is not limited thereto.
이와 같이, 우레탄계 비드가 상기 범위의 신도 및 탄성 회복률을 가짐으로써, 자동차 시트의 촉감 및 슬립성을 현저히 개선시킬 수 있다.As described above, the urethane-based bead has the elongation and elastic recovery rate in the above-mentioned range, whereby the tactile feeling and the slipperiness of the automobile seat can be remarkably improved.
또한, 상기 우레탄계 비드는 입자크기가 1㎛ 내지 20㎛인 것이 바람직하고, 1㎛ 내지 5㎛인 것이 더욱 바람직하나, 이에 한정되지 않는다. 이때, 우레탄계 비드가 상기 범위의 입자크기를 유지함으로써 스퀵 지수 측정시나 손으로 만질 때 닿는 표면적을 줄일 수 있는 이점이 있다. The urethane beads preferably have a particle size of 1 탆 to 20 탆, more preferably 1 탆 to 5 탆, but are not limited thereto. At this time, the urethane bead maintains the particle size within the above range, which has the advantage of reducing the surface area when measuring the Squeak index or touching with the hand.
이때, 입자크기라 함은 장축직경과 단축직경 각각의 평균값을 말하는 것이다. Here, the particle size refers to the average value of the major axis diameter and minor axis diameter, respectively.
상기 우레탄계 비드는 우레탄계 프리폴리머를 Emulsion중합법, Dispersion 중합법, Suspension 중합법, Seed 중합법 등을 통하여 제조될 수 있다. The urethane-based beads can be produced by emulsion polymerization, dispersion polymerization, suspension polymerization, Seed polymerization or the like using a urethane-based prepolymer.
상기 표면코팅용 조성물 총 100 중량부에 대하여, 상기 우레탄계 비드 1 중량부 내지 10 중량부를 포함하는 것이 바람직하나, 이에 한정되지 않는다. 이때, 우레탄계 비드가 1 중량부 미만인 경우 부드러운 감성이 제대로 재현되지 않는 문제점이 있고, 우레탄계 비드가 10 중량부를 초과하는 경우, 분산이 제대로 이루어지지 않고, 표면에 뿌옇게 뜬 현상인 백탁 현상이 발생해 미관상의 문제점이 있다.
But it is not limited thereto, but it is preferable to include 1 part by weight to 10 parts by weight of the urethane based beads with respect to 100 parts by weight of the total amount of the composition for surface coating. At this time, when the urethane bead is less than 1 part by weight, soft sensibility is not reproduced properly. When the urethane bead is more than 10 parts by weight, the dispersion is not properly performed and a whitish phenomenon, .
상기 표면코팅용 조성물은 이소시아네이트계 경화제를 추가로 포함할 수 있어, 주제 및 이소시아네이트계 경화제가 3차원 가교결합 반응에 의해 폴리머 사슬을 형성할 수 있다.The composition for surface coating may further include an isocyanate-based curing agent so that the subject and the isocyanate-based curing agent can form a polymer chain by a three-dimensional crosslinking reaction.
상기 3차원 가교결합이란 분자와 분자간에 공유 결합이나 이온 결합과 같은 완전한 화학 결합을 의미하는 바, 상기 폴리머 사슬은 상기 3차원 가교결합에 의해 망상구조의 분자를 포함할 수 있다. The three-dimensional crosslinking refers to a complete chemical bond such as a covalent bond or an ionic bond between a molecule and a molecule, and the polymer chain may include molecules of a network structure by the three-dimensional crosslinking.
상기 이소시아네이트계 경화제로는 톨루엔 디이소시아네이트, 디페닐메탄 디이소시아네이트, 변성 디페닐메탄 디이소시아네이트, 나프탈렌 디이소시아네이트, 페닐렌 디이소시아네이트트, 헥사메틸렌 디이소시아네이트, 리신 이소시아네이트, 사이클로헥산 디이소시아네이트, 이소포론 디이소시아네이트, 메틸렌디페닐 이소시아네이트, 크실렌 디이소시아네이트, 테트라메틸크실렌 디이소시아네이트, 노르보넨 디이소시아네이트, 트리페닐메탄 트리이소시아네이트, 폴리페닐 폴리메틸렌 폴리이소시아네이트, 카보디이미드기를 포함하는 폴리이소시아네이트, 알로파네이트기를 포함하는 폴리이소시아네이트, 이소시아누레이트기를 포함하는 폴리이소시아네이트 및 이들의 조합으로 형성된 군으로부터 선택된 하나 이상의 경화제가 사용될 수 있다. Examples of the isocyanate curing agent include toluene diisocyanate, diphenylmethane diisocyanate, modified diphenylmethane diisocyanate, naphthalene diisocyanate, phenylene diisocyanate, hexamethylene diisocyanate, lysine isocyanate, cyclohexane diisocyanate, isophorone diisocyanate , Polyisocyanates including methylene diphenyl isocyanate, xylene diisocyanate, tetramethyl xylene diisocyanate, norbornene diisocyanate, triphenyl methane triisocyanate, polyphenyl polymethylene polyisocyanate, carbodiimide group, poly At least one curing agent selected from the group formed by a polyisocyanate containing an isocyanurate group, an isocyanate group, an isocyanurate group, and combinations thereof may be used .
상기 표면코팅용 조성물 총 100 중량부에 대하여, 상기 경화제 1 중량부 내지 10 중량부를 포함하는 것이 바람직하나, 이에 한정되지 않는다. 이때, 경화제가 1 중량부 미만인 경우 경화가 제대로 이루어지지 않는 문제점이 있고, 경화제가 10 중량부를 초과하는 경우, 반응하지 않은 잔여 경화제가 조성물 내 잔존하여 상분리를 일으킬 문제점이 있다.
But it is not limited thereto, but it is preferable that the curing agent is included in an amount of 1 to 10 parts by weight based on 100 parts by weight of the total amount of the composition for surface coating. If the amount of the curing agent is less than 1 part by weight, curing may not be performed properly. If the amount of the curing agent is more than 10 parts by weight, unreacted residual curing agent may remain in the composition to cause phase separation.
상기 표면코팅용 조성물은 소광제, 습윤제, 분산제, 왁스, 슬립제, 소포제 및 이들의 조합으로 이루어진 군으로부터 선택된 첨가제를 더 포함할 수 있다. The composition for surface coating may further comprise an additive selected from the group consisting of a quencher, a wetting agent, a dispersing agent, a wax, a slip agent, a defoaming agent, and a combination thereof.
구체적으로, 상기 표면코팅용 조성물 고형분 100중량부에 대하여, 소광제, 습윤제, 분산제, 왁스, 슬립제, 소포제 및 이들의 조합으로 이루어진 군으로부터 선택된 첨가제를 0.1 중량부 내지 20 중량부 포함할 수 있다.
Specifically, 0.1 part by weight to 20 parts by weight of an additive selected from the group consisting of a quencher, a wetting agent, a dispersing agent, a wax, a slip agent, an antifoaming agent and a combination thereof may be added to 100 parts by weight of the solid content of the surface coating composition .
자동차 시트Car seat
또한, 본 발명은 상기 표면코팅용 조성물로 형성된 표면코팅층; 상기 표면코팅층 하부에 형성된 기재층을 포함하는 자동차 시트를 제공한다.
The present invention also relates to a surface coating layer formed of the composition for surface coating; And a base layer formed below the surface coating layer.
도 1은 본 발명의 일 구현예에 따른 자동차 시트를 도식화하여 나타낸 것으로, 도 1을 참조하면, 자동차 시트(100)는 표면코팅층(10) 및 기재층(20)을 포함할 수 있다.
1 is a schematic view of a car seat according to an embodiment of the present invention. Referring to FIG. 1, a
상기 표면코팅층(10)은 말단에 이소시아네이트기를 가지는 카르복실기 함유 주제; 및 우레탄계 비드를 포함하는 표면코팅용 조성물로 형성된 것으로, 구체적인 표면코팅용 조성물은 전술한 바와 같다. The surface coating layer (10) comprises a carboxyl group-containing subject having an isocyanate group at the terminal; And urethane beads. Specific compositions for surface coating are as described above.
상기 표면코팅층(10)의 상부 표면은 다수의 돌출부가 형성된 것을 특징으로 하는바, 상기 돌출부는 상기 우레탄계 비드가 상기 조성물 내 일부만 매몰되어 매몰되지 않은 부분이 노출된 상태로 형성된 것이다. The upper surface of the
상기 돌출부의 형상 및 높이는 상기 우레탄계 비드의 형상 및 크기에 따라 좌우되는 것으로, 상기 돌출부는 반구형 또는 반타원구형이고, 0.5㎛ 내지 10㎛의 높이를 가지는 것이 바람직하나, 이에 한정되지 않는다.The shape and height of the protrusions depend on the shape and size of the urethane beads. The protrusions are hemispherical or semi-spherical, and preferably have a height of 0.5 탆 to 10 탆, but are not limited thereto.
이와 같이 소프트하면서도 탄성이 우수한 우레탄계 비드가 다수의 돌출부를 형성함으로써, 다수의 돌출부로 인해 소프트하면서도 탄성이 우수한 표면적을 넓힐 수 있어, 자동차 시트의 촉감 및 슬립성을 현저히 개선시킬 수 있다.By forming a large number of protrusions with soft and highly elastic urethane beads, it is possible to widen the surface area with excellent softness and elasticity due to a large number of protrusions, thereby significantly improving the feel and slipperiness of the automobile seat.
상기 표면코팅층(10)은 상기 표면코팅용 조성물이 1㎛ 내지 20㎛, 바람직하게는 5㎛ 내지 10㎛로 도포 후 건조되어 형성될 수 있다. 구체적으로, 상기 표면코팅용 조성물이 상기 프라이머층 상부에 도포됨으로써, 두께가 1㎛ 내지 20㎛, 바람직하게는 5㎛ 내지 10㎛인 표면코팅층(10)을 형성할 수 있고, 표면코팅층(10)의 두께를 상기 범위내로 유지함으로써 상기 자동차 시트 표면의 유연성을 유지한 상태로 내마모성 및 내오염성을 동시에 확보할 수 있다.The
상기 표면코팅층(10)의 스퀵 지수는 0.2 이하인 것이 바람직하고, 0.02 내지 0.2인 것이 더욱 바람직하나, 이에 한정되지 않는다. 이때, 표면코팅층(10)이 상기 범위의 스퀵 지수를 유지함으로써, 슬립성이 현저히 우수하다.
The Squeak index of the
상기 기재층(30)은 폴리비닐클로라이드 수지, 폴리우레탄 수지, 열가소성 폴리올레핀 수지(Thermoplastic Polyolefins, TPO), 열가소성 폴리우레탄 수지(Thermoplastic Polyurethanes, TPU) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함할 수 있다. 예를 들어, 상기 기재층은 자동차 시트에 가장 많이 사용되는 폴리올레핀계 수지를 포함할 수 있고, 가죽, 인조가죽 등에 가장 많이 활용되는 폴리비닐클로라이드 수지 및 이를 포함하는 합성수지를 사용할 수 있다.
The substrate layer 30 may comprise one selected from the group consisting of polyvinyl chloride resins, polyurethane resins, thermoplastic polyolefins (TPO), thermoplastic polyurethanes (TPU), and combinations thereof. have. For example, the base layer may include a polyolefin-based resin most commonly used in an automobile seat, and a polyvinyl chloride resin most commonly used in leather, artificial leather, etc., and a synthetic resin containing the polyvinyl chloride resin may be used.
상기 표면코팅층(10) 및 기재층(20) 사이에 프라이머층(도면 미도시)을 추가로 포함할 수 있다. 상기 프라이머층으로는 우레탄 아크릴레이트 화합물을 포함하는 우레탄계 접착수지 또는 아크릴계 접착수지를 포함할 수 있다. 상기 우레탄계 접착수지는 우레탄 아크릴레이트 화합물을 포함하는바, 상기 우레탄 아크릴레이트 화합물은 상기 코팅층을 형성하는 표면코팅용 조성물과 성질이 유사하다 할 것이어서 코팅층과의 접착력이 우수하여 기재층과 코팅층과의 접착이 안정될 수 있게 한다.
A primer layer (not shown) may be additionally provided between the
따라서, 상기 기재층 상부에 전술한 표면코팅층을 부여함으로써, 내마모성 및 내오염성과 같은 기본적인 물성이 우수하면서도, 소프트한 촉감, 낮은 스퀵 지수에 따른 슬립성 및 불점착성과 같은 부가적인 물성 역시 우수한 자동차 시트를 제공할 수 있다.
Therefore, by providing the above-mentioned surface coating layer on the base layer, it is possible to provide a base material having excellent physical properties such as abrasion resistance and contamination resistance, as well as additional properties such as soft feel, slip property and non- Can be provided.
이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시한다. 그러나 하기의 실시예는 본 발명을 보다 쉽게 이해하기 위하여 제공되는 것일 뿐, 하기 실시예에 의해 본 발명의 내용이 한정되는 것은 아니다.
Hereinafter, preferred embodiments of the present invention will be described in order to facilitate understanding of the present invention. However, the following examples are provided only for the purpose of easier understanding of the present invention, and the present invention is not limited by the following examples.
[[ 실시예Example ]]
입자크기가 약 10㎛인 우레탄계 비드를 준비하였다. 이때, 우레탄계 비드는 약 700%의 신도를 갖고, 25℃에서 50% 신장 변형시 탄성 회복률(Re)이 약 97%이다.Urethane beads having a particle size of about 10 mu m were prepared. At this time, the urethane bead has an elongation of about 700% and an elastic recovery (Re) of about 97% at 50% elongation at 25 ° C.
폴리우레탄 프리폴리머(Bayhydrol® UH XP 2648/1) 50 중량부; 이소시아네이트계 경화제(IMPRAFIX® 2794) 2~3 중량부; 준비된 우레탄계 비드 3~6 중량부; 소광제로서 실리카 2~3 중량부; 습윤제 0.5 중량부; 분산제 0.5 중량부; 왁스 8 중량부; 및 슬립제 15~20 중량부를 혼합하고 초순수 15중량부 첨가하여 수분산시켜 120℃에서 가열하여 표면코팅용 조성물을 형성하였다.50 parts by weight of a polyurethane prepolymer (Bayhydrol 占 UH XP 2648/1); 2 to 3 parts by weight of an isocyanate-based curing agent (IMPRAFIX® 2794); 3 to 6 parts by weight of a urethane bead prepared; 2 to 3 parts by weight of silica as a quencher; 0.5 parts by weight of wetting agent; 0.5 parts by weight of dispersant; 8 parts by weight of wax; And 15 to 20 parts by weight of slip were added, and 15 parts by weight of ultrapure water was added thereto. The mixture was water dispersed and heated at 120 DEG C to form a composition for surface coating.
폴리비닐클로라이드 수지를 포함하는 인조가죽 상부에 우레탄계 접착수지를 도포하여 약 5~10㎛의 두께로 도포하여 표면코팅층을 형성한 후, 자동차 시트를 제조하였다. 이때, 표면코팅층 상부 표면에 우레탄계 비드가 조성물 내 일부만 매몰되어 매몰되지 않은 부분이 표면에 노출된 상태로 약 5㎛ 높이의 다수의 반구형 돌출부를 형성한다.
A urethane-based adhesive resin was applied to an upper portion of a synthetic leather containing a polyvinyl chloride resin and coated to a thickness of about 5 to 10 탆 to form a surface coating layer, and then an automobile seat was produced. At this time, urethane beads are buried in the composition on the upper surface of the surface coating layer to form a plurality of hemispherical protrusions having a height of about 5 탆 in a state where the unburied portions are exposed on the surface.
실시예Example 2 2
입자크기가 약 5㎛인 우레탄계 비드를 사용한 것을 제외하고는, 실시예 1과 동일한 방법으로 자동차 시트를 제조하였다.
A car sheet was produced in the same manner as in Example 1, except that a urethane bead having a particle size of about 5 탆 was used.
비교예Comparative Example 1 One
우레탄계 비드를 사용하지 않은 것을 제외하고는, 실시예 1과 동일한 방법으로 자동차 시트를 제조하였다.
An automobile seat was manufactured in the same manner as in Example 1, except that urethane-based beads were not used.
실험예Experimental Example : 물성 평가: Property evaluation
1. 내마모성 평가1. Abrasion resistance evaluation
실시예 1~2 및 비교예 1에 따른 자동차용 시트를 로터리식 마모시험기를 이용하여 내마모성을 평가하였다.
The automotive sheet according to Examples 1 to 2 and Comparative Example 1 was evaluated for abrasion resistance using a rotary abrasion tester.
2. 내오염성 평가2. Evaluation of stain resistance
실시예 1~2 및 비교예 1에 따른 자동차용 시트를 유니버셜형 마모 시험기(Universal Wear Tester)에 장착 한 후 상기 자동차 시트 상부에 Cotton Soil Test Cloth 조각을 올리고 5N의 일정한 하중을 가하였다. 순환속도를 1분에 25번 실시하였다. 상기 자동차 시트를 500Cycle 오염시켰다. 상기 오염된 자동차용 시트를 꺼내어 gray scale로 이뤄진 기준과 비교해서 육안으로 그 등급을 나누었다.
The sheets for automobiles according to Examples 1 and 2 and Comparative Example 1 were mounted on a Universal Wear Tester, and a piece of Cotton Soil Test Cloth was placed on the automobile seat and a constant load of 5 N was applied. The circulation rate was 25 times per minute. The car seat was contaminated for 500 cycles. The contaminated sheet for automobiles was taken out and compared with a gray scale standard to divide the grade visually.
3. 소프트한 정도 평가3. Evaluation of softness
실시예 1~2 및 비교예 1에 따른 자동차용 시트를 내부 전문가들이 손으로 직접 만져보아 상대적인 소프트한 정도를 평가하였다(우수 ○, 보통 △, 미흡 ×로 표시).
The automotive seat according to Examples 1 to 2 and Comparative Example 1 was evaluated by the internal experts by hand to evaluate the degree of relative softness (excellent ◯, normal △, insufficient ×).
4. 4. 스퀵Squeak (( SqueakSqueak ) 지수 평가) Exponential evaluation
실시예 1~2 및 비교예 1에 따른 자동차용 시트 각각을 하나는 디딤판 위에 고정시키고, 다른 하나는 아래쪽 원단에 맞닿게 놓은 다음 그 위에 일정무게의 추를 올린다. 이후, 도르래를 이용하여 추에 연결되어 있는 수평으로 연결되어 있는 끈을 수직인 만능재료시험기(Universal Testing Machine)와 연결하고, 만능재료시험기를 이용하여 일정속도로 추를 당기는데 힘의 편차(△F) 및 평균힘(Fa)을 측정하였고, △F/ Fa으로 스퀵 지수를 계산하였다.
Each of the automotive sheets according to Examples 1 to 2 and Comparative Example 1 was fixed on one of the treads and the other was placed on the bottom fabric, and a weight having a predetermined weight was placed thereon. Thereafter, a horizontally connected string connected to the weight is connected to a vertical universal testing machine using a pulley, and a force deviation (△ F) and average force (Fa) were measured, and the Squeak index was calculated by? F / Fa.
5. 5. 불점착성Non-stickiness 평가 evaluation
실시예 1~2 및 비교예 1에 따른 자동차용 시트 각각을 아래위로 포개어 양쪽 원단을 유리를 누른 다른 위쪽에 3N의 추로 누르고, 80℃의 온도에서 12시간 방치한 후, 25℃의 온도에서 30분 동안 방치하여 불점착성을 평가하였다(우수 ○, 보통 △, 미흡 ×로 표시).Each of the car seats according to Examples 1 to 2 and Comparative Example 1 was placed on top of each other, and both fabrics were pressed with a weight of 3N on top of the other side of the glass and pressed for 12 hours at a temperature of 80 DEG C, Minute, and the tackiness was evaluated (indicated as excellent ◯, normal △, insufficient ×).
도 2(a)는 실시예 1에 따른 자동차 시트의 스퀵 지수를 측정한 그래프를, 도 2(b)는 실시예 2에 따른 자동차 시트의 스퀵 지수를 측정한 그래프를, 도 2(c)는 비교예 1에 따른 자동차 시트의 스퀵 지수를 측정한 그래프를 각각 나타낸 것이다. 2 (b) is a graph in which the Squeak index of the automobile seat according to the second embodiment is measured, and FIG. 2 (c) is a graph showing the Squeak index And the Squeak indices of the automobile seat according to Comparative Example 1. Fig.
상기 표 1 및 도 2에서 보듯이, 실시예 1~2에 따른 표면코팅용 조성물은 우레탄계 비드를 포함하는 것으로, 이를 적용한 자동차 시트는 우레탄계 비드로 인해 다수의 돌출부를 형성하는바, 비교예 1에 따른 표면코팅용 조성물을 적용한 자동차 시트와 내마모성 및 내오염성과 같은 기본적인 물성이 동등한 수준을 유지하면서도, 비교예 1에 따른 표면코팅용 조성물을 적용한 자동차 시트에 비해, 소프트한 촉감, 낮은 스퀵 지수에 따른 슬립성 및 불점착성과 같은 부가적인 물성 현저히 우수함을 확인할 수 있었다.As shown in Table 1 and FIG. 2, the composition for surface coating according to Examples 1 and 2 includes urethane beads, and the automobile sheet to which the composition is applied has a plurality of protrusions due to urethane beads. In Comparative Example 1 Compared with the automobile seat to which the composition for surface coating according to Comparative Example 1 was applied, while maintaining the basic physical properties such as abrasion resistance and pollution resistance at the same level as that of the automobile seat to which the composition for surface coating according to Comparative Example 1 was applied It was confirmed that the additive properties such as slip property and non-stick property were remarkably excellent.
특히, 실시예 2에 따른 표면코팅용 조성물과 같이 입자크기가 약 5㎛인 우레탄계 비드를 사용한 경우에, 낮은 스퀵 지수에 따른 슬립성 및 불점착성이 매우 우수함을 확인할 수 있었다.
In particular, when the urethane bead having a particle size of about 5 탆 was used as the composition for surface coating according to Example 2, it was confirmed that the slip property and the non-adhesive property according to the low Squeak index were excellent.
전술한 본 발명의 설명은 예시를 위한 것이며, 본 발명이 속하는 기술분야의 통상의 지식을 가진 자는 본 발명의 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 쉽게 변형이 가능하다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.It will be understood by those skilled in the art that the foregoing description of the present invention is for illustrative purposes only and that those of ordinary skill in the art can readily understand that various changes and modifications may be made without departing from the spirit or essential characteristics of the present invention. will be. It is therefore to be understood that the above-described embodiments are illustrative in all aspects and not restrictive.
Claims (19)
우레탄계 비드를 포함하는
표면코팅용 조성물.
A subject containing a carboxyl group-containing compound having an isocyanate group at the terminal; And
Containing urethane beads
Composition for surface coating.
상기 우레탄계 비드는 450% 내지 900%의 신도를 갖는
표면코팅용 조성물.
The method according to claim 1,
The urethane beads have an elongation of 450% to 900%
Composition for surface coating.
상기 우레탄계 비드는 25℃ 에서 50% 신장 변형시 탄성 회복률(Re)이 95% 내지 99%인
표면코팅용 조성물.
The method according to claim 1,
The urethane-based beads have an elastic recovery (Re) of 95% to 99% at 50% elongation at 25 ° C
Composition for surface coating.
상기 우레탄계 비드는 입자크기가 1㎛ 내지 20㎛인
표면코팅용 조성물.
The method according to claim 1,
The urethane-based beads have a particle size of 1 탆 to 20 탆
Composition for surface coating.
상기 주제는 평균 입경이 상이한 입자들을 포함하여, 이중 입자 크기 분포(bimodal particle size distribution)를 가지는
표면코팅용 조성물.
The method according to claim 1,
The subject matter includes particles having different average particle diameters, and having a bimodal particle size distribution
Composition for surface coating.
상기 주제는 물이 첨가되어 수분산된 것인
표면코팅용 조성물.
The method according to claim 1,
The subject matter is water-dispersed and water-dispersed
Composition for surface coating.
상기 주제는 폴리올 화합물, 카르복실기 함유 폴리올 화합물 및 말단에 적어도 2개의 이소시아네이트기를 가지는 이소시아네이트 화합물이 반응하여 형성된 프리폴리머(prepolymer)인
표면코팅용 조성물.
The method according to claim 1,
The subject is a prepolymer formed by reacting a polyol compound, a carboxyl group-containing polyol compound and an isocyanate compound having at least two isocyanate groups at the terminal thereof
Composition for surface coating.
상기 프리폴리머는 폴리실록산 화합물이 추가로 반응하여 형성된 것인
표면코팅용 조성물.
8. The method of claim 7,
Wherein the prepolymer is formed by further reacting the polysiloxane compound
Composition for surface coating.
상기 폴리실록산 화합물의 중량평균분자량은 200g/mol 내지 300g/mol인
표면코팅용 조성물.
9. The method of claim 8,
The polysiloxane compound has a weight average molecular weight of 200 g / mol to 300 g / mol
Composition for surface coating.
상기 표면코팅용 조성물 총 100 중량부에 대하여, 상기 주제 30중량부 내지 60중량부 및 상기 우레탄계 비드 1 중량부 내지 10중량부를 포함하는
표면코팅용 조성물.
The method according to claim 1,
30 parts by weight to 60 parts by weight of the subject and 1 part by weight to 10 parts by weight of the urethane based beads, based on 100 parts by weight of the total composition for surface coating,
Composition for surface coating.
이소시아네이트계 경화제를 추가로 포함하는
표면코팅용 조성물.
The method according to claim 1,
Further comprising an isocyanate-based curing agent
Composition for surface coating.
상기 표면 코팅용 조성물은 3차원 가교결합 반응에 의해 폴리머 사슬을 형성하는
표면코팅용 수성 조성물.
12. The method of claim 11,
The composition for surface coating forms a polymer chain by a three-dimensional crosslinking reaction
Aqueous composition for surface coating.
소광제, 습윤제, 분산제, 왁스, 슬립제, 소포제 및 이들의 조합으로 이루어진 군으로부터 선택된 첨가제를 더 포함하는
표면코팅용 조성물.
The method according to claim 1,
A wetting agent, a dispersing agent, a wax, a slipping agent, an antifoaming agent, and combinations thereof.
Composition for surface coating.
상기 표면코팅층 하부에 형성된 기재층을 포함하는
자동차 시트.
A surface coating layer formed from the composition for surface coating according to any one of claims 1 to 13; And
And a base layer formed below the surface coating layer
Car seat.
상기 표면코팅층의 상부 표면에 다수의 돌출부가 형성된 것을 특징으로 하는
자동차 시트.
15. The method of claim 14,
And a plurality of projections are formed on the upper surface of the surface coating layer
Car seat.
상기 돌출부는 반구형 또는 반타원구형이고, 0.5㎛ 내지 10㎛의 높이를 가지는
자동차 시트.
16. The method of claim 15,
The protrusions are semispherical or semi-elliptic spherical, and have a height of 0.5 to 10 mu m
Car seat.
상기 표면코팅층은 상기 표면코팅용 조성물이 1㎛ 내지 20㎛로 도포 후 건조되어 형성된
자동차용 시트.
15. The method of claim 14,
The surface coating layer may be formed by applying the surface coating composition at a thickness of 1 탆 to 20 탆,
Car seat.
상기 표면코팅층의 스퀵 지수는 0.2 이하인
자동차 시트.
15. The method of claim 14,
The Squeak index of the surface coating layer is 0.2 or less
Car seat.
상기 기재층은 폴리비닐클로라이드 수지, 폴리우레탄 수지, 열가소성 폴리올레핀 수지(Thermoplastic Polyolefins, TPO), 열가소성 폴리우레탄 수지(Thermoplastic Polyurethanes, TPU) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함하는
자동차 시트
15. The method of claim 14,
Wherein the substrate layer comprises one selected from the group consisting of a polyvinyl chloride resin, a polyurethane resin, a thermoplastic polyolefin resin (TPO), a thermoplastic polyurethanes (TPU), and combinations thereof
Car seat